WO/2016/098707A1
Provided is a bonding wire characterized by comprising: a core material that comprises at least one of Ga, In and Sn in a total of 0.1-3.0 at.%, the remainder comprising Ag and inevitable impurities; and a coating layer that is formed on...  
WO/2016/097205A1
The invention provides a system and method of reconditioning a SMA or NTE material based core for use in an energy recovery device comprising the step of heating the core for a period of time above a certain temperature to configure the ...  
WO/2016/091550A1
The invention relates to a method for continuously solution heat-treating aluminium alloy sheet by continuously moving heat-treatable 7000-series aluminium alloy sheet through a continuous heat-treatment furnace arranged to heat the movi...  
WO/2016/093349A1
Provided are an oriented copper sheet in which a cubic crystal texture is developed to a high degree, higher strength than a conventional material having the same crystal texture is obtained, and high breaking elongation is obtained, a c...  
WO/2016/094464A1
The present invention relates to the reduction of artificial aging time of 7xxx series alloys. Currently, the artificial aging times for typical 7xxx series alloy can be as long as 24 hrs. The current invention allows for a significant r...  
WO/2016/091719A3
The present invention relates to a wire, comprising a copper core comprising: al.silver in an amount in the range of from 0.05 to 1.3 wt.%; or a2. Palladium, and further at least one element selected from silver and gold, wherein the amo...  
WO/2016/091824A1
The invention relates to a method for producing electrode foils (1) for capacitors (10), said method comprising the steps of: A) providing a metal foil (1); B) transferring microstructures (2) located on a punch to a main surface of the ...  
WO/2016/088825A1
This aluminum alloy electrical wire includes an aluminum alloy wire, the aluminum alloy wire comprising an aluminum alloy including 0.11-1.03 atomic% of Mg, 0.10-0.90 atomic% of Si, and 0.005-0.25 atomic% of Ni, the remainder comprising ...  
WO/2016/088887A1
The present invention provides e.g. an aluminum alloy wire material having improved plating properties without particular deterioration in mechanical characteristics. This aluminum alloy wire material has a composition comprising 0.1-1.0...  
WO/2016/089145A1
The present invention relates to a method for manufacturing Alloy 690 ordered alloy to be used in a steam generator tube serving as a heat exchanger in a nuclear power plant (hereinafter, referred to as NPP), and Alloy 690 ordered alloy ...  
WO/2016/090026A1
New 6xxx aluminum alloy strips having an improved combination of properties are disclosed. The new 6xxx new aluminum alloy strips are rolled to a target thickness in-line via at least a first rolling stand and a second rolling stand. In ...  
WO/2016/088889A1
Provided is an aluminum alloy wire material that can achieve both good vibrational characteristics and good bending fatigue characteristics while ensuring high electrical conductivity and a moderately low proof strength, even when the wi...  
WO/2016/088888A1
The present invention provides an aluminum alloy wire rod, etc., having high strength and excellent impact resistance used in electric wiring which is not readily broken and is also usable in small-diameter wire. This aluminum alloy wire...  
WO/2016/084118A1
The purpose of the present invention is to provide a high-performance permanent magnet. Provided is a permanent magnet, comprising: a composition represented by a composition formula of RpFeqMrCutCo100-p-q-r-t (wherein R is at least one ...  
WO/2016/083454A1
The invention relates to a heat exchanger (10), in particular for motor vehicles, with at least one exchanger tube (12) of an aluminium alloy and with at least one component (14, 16) connected fluidically to the exchanger tube (12), wher...  
WO/2016/084243A1
A hot-rolled α+β titanium alloy sheet obtained from, in mass%, Al: 4.7-5.5%, Fe: 0.5-1.4%, N: not more than 0.03%, Si: 0.15-0.40% with a Si/O ratio of 0.80-2.80, [O]eq in equation (1) being 0.13% to less than 0.25%, and the balance fro...  
WO/2016/084980A1
The titanium alloy member has a base material part, and a surface hardening layer formed on the surface layer of the base material part, the cross-sectional hardness of the base material part being 330 HV to less than 400 HV, and the cro...  
WO/2016/080155A1
The present invention provides: an alloy material which comprises palladium and 10.2-50.0 mass% iridium, the alloy material being an improvement over conventional palladium alloys, having improved X-ray impermeability and better machinab...  
WO/2016/074423A1
A magnesium alloy and a preparation method and a use thereof. The magnesium alloy contains: 0.8-1.4 weight% of a rare earth element, 0.01-0.2 weight% of R, 0.8-1.5 weight% of Mn, 0-0.01 weight% of Fe, 0-0.01 weight% of Cu, 0-0.01 weight%...  
WO/2016/077044A1
This application discloses an aluminum alloy, processes for preparing the aluminum alloy, processes for fabricating metal parts, such as automotive panels, comprising the aluminum alloy, and the automotive parts fabricated from the alumi...  
WO/2016/074424A1
A magnesium alloy and a preparation method and a use thereof. The magnesium alloy contains: 2-3.5 weight% of Ce, 0.01-0.2 weight% of R, 0.8-1.5 weight% of Mn, 0-0.01 weight% of Fe, 0-0.01 weight% of Cu, 0-0.01 weight% of Ni, 0-0.01 weigh...  
WO/2016/076263A1
The present invention comprises an aluminium alloy clad material obtained by cladding a sacrificial material on one surface of a core material and cladding an Al-Si or Al-Si-Zn brazing material on the other surface, wherein: the core mat...  
WO/2016/071971A1
Provided is a solder material with which the thickness of an oxide film is controlled to a certain value or lower before solder melting and which exhibits oxidation resistance during and after solder melting. A Cu core ball 1A includes a...  
WO/2016/072304A1
A method for manufacturing an electric wire in which an insulation coating is provided on the outer periphery of a conductor is provided with: a step for readying a conductor material wire that has been subjected to a solution treatment;...  
WO/2016/072339A1
The present invention is a pipe which is constituted of a copper alloy and has a grooved inner surface and which is for use in heat exchangers, characterized in that the copper alloy contains 0.004-0.040 mass% P, with the remainder compr...  
WO/2016/071257A1
An aluminium alloy forged product obtained by following steps: a) casting a billet from a 6xxx aluminium alloy comprising: Si: 0.7-1.3 wt. %; Fe : ≤ 0.5 wt. %; Cu: 0.1-1.5 wt. %; Mn: 0.4-1.0 wt. %; Mg: 0.6-1.2 wt. %; Cr: 0.05-0.25 wt.%...  
WO/2016/069695A1
The present invention relates to aluminum alloy products that can be riveted and possess excellent ductility and toughness properties. The present invention also relates to a method of producing the aluminum alloy products. In particular...  
WO/2016/067045A1
A process of preparing sheet metal alloy material for forming is disclosed. The process comprises hot rolling (42) a metal alloy material, wherein the metal alloy material is at a temperature above that at which precipitates form in the ...  
WO/2016/070158A1
A method for increasing the strength of metals or metal components includes selecting a wrought metal or powder metal sample having a mass equal to or greater than a final mass of a component to be formed. If the sample is wrought metal,...  
WO/2016/068293A1
This aluminum alloy substrate for a magnetic disk contains 0.5-24.0 mass% of Si and 0.01-3.00 mass% of Fe and comprises the balance being Al and inevitable impurities. The aluminum alloy substrate for a magnetic disk has a smooth and hig...  
WO/2016/066706A1
The present invention relates to a ball-game racket comprising a stringing that has at least one string including a superelastic material.  
WO/2016/063768A1
The present invention provides a superelastic alloy containing: 8.0-20.0 mass% of essential additive elements of Au and at least one of Cr and Mo, and an optional additive element of Ta; and, as the remaining portion, Ti and unavoidable ...  
WO/2016/063839A1
To improve the erosion resistance of a processing member for low-melting-point molten metals such as aluminum having a low melting point by suppressing the occurrence of cracks in a surface protective layer or separation of a coating lay...  
WO/2016/063876A1
This 5000 series aluminium alloy sheet, which has an Mg solid solution amount and subgrain area ratio configured to a specified range, has no shortage in pressure resistance strength after filling with a beverage takes place, has excelle...  
WO/2016/060117A1
To provide: a method for producing an aluminum alloy member, which exhibits excellent formability during a forming process and is capable of producing an aluminum alloy member that has high strength and high proof stress; and an aluminum...  
WO/2016/059707A1
This Cu-Ni-Si alloy contains 2.2-3.2 mass% Ni, 0.4-0.8 mass% Si, and 0.1-1.0 mass% Zn and the remainder is configured from Cu and unavoidable impurities. The mass ratio of Ni to Si is 4.0-5.5. The number of particles having a particle di...  
WO/2016/060444A1
A copper alloy material with high strength, high thermal resistance, high corrosion resistance, and excellent bending processability, and a method of producing the same are disclosed. The copper alloy material includes 5.0 to 40.0 wt% of...  
WO/2016/059950A1
A magnesium alloy which contains, in mass%, from 1% to 12% (inclusive) of Al and from 0.1% to 5% (inclusive) of Mn, and which is provided with a structure wherein particles of a compound containing Al and Mn are dispersed. The average pa...  
WO/2016/056612A1
Provided is a sputtering target characterized by containing 20-40 at% of Te, 5-20 at% of Cu, 5-15 at% of Zr, and the remainder comprising Al, and having a sputtering target structure composed of an Al phase, a Cu phase, a CuTeZr phase, a...  
WO/2016/056491A1
A method for altering the surface of a metal is provided with which it is possible to obtain a metallic product excellent in terms of surface hardness, heat resistance, corrosion resistance, resistances to high-temperature oxidation, hig...  
WO/2016/056607A1
 A titanium encapsulation structure which is a titanium material provided with a packaging material formed from a pure titanium material, and a filler packed into the packaging material, the internal pressure of the packaging material ...  
WO/2016/056240A1
The present invention provides a superplastic-forming aluminium alloy plate that has excellent properties for superplastic forming, such as blow forming, and that has excellent surface properties after forming. Provided is a superplastic...  
WO/2016/051099A1
The invention concerns a sheet 0.5 to 9 mm thick, having an essentially recrystallised granular structure made from an aluminium alloy comprising 2.8 to 3.2 % by weight of Cu, 0.5 to 0.8 % by weight of Li, 0.1 to 0.3 % by weight of Ag, 0...  
WO/2016/052941A1
The present invention relates to a titanium alloy which is capable of nonlinear elastic deformation and simultaneously has super-high strength, super-low elastic modulus and stable super-elastic properties. The titanium alloy according t...  
WO/2016/052789A1
The present invention relates to a titanium alloy exhibiting nonlinear elastic deformation and having super-high strength, ultra-low elastic modulus, and stable superelasticity, said titanium alloy comprising: niobium (Nb); zirconium (Zr...  
WO/2016/052551A1
A Ni-based alloy pipe, the chemical composition of the base metal of which is, in mass%, C: not more than 0.15%, Si: not more than 1.0%, Mn: not more than 2.0%, P: not more than 0.030%, S: not more than 0.030%, Cr: 10.0-40.0%, Ni: 50.0-8...  
WO/2016/052423A1
 Provided is an Ni-based alloy for use in an aircraft engine or gas turbine for power generation, wherein the Ni-based superheat-resistant alloy has good mechanical characteristics at high temperature. The alloy comprises, in mass%, C:...  
WO/2016/051864A1
This copper alloy material contains Cu and Fe, and is composed of a Cu-Fe alloy. The Fe content in this copper alloy material is from 20% by mass to 50% by mass (inclusive). This copper alloy material has a structure that contains a Cu p...  
WO/2016/051060A1
The invention relates to a wrought product made of aluminum alloy having the composition, in percentage by weight, of Mg: 4.0-5.0; Li: 1.0-1.8; Mn: 0.3-0.5; Zr: 0.05-0.15; Ag: ≤ 0.5; Fe: ≤ 0.1; Ti: <0.15; Si: ≤ 0.05; other elements...  
WO/2016/052445A1
The purpose of the present invention is to provide a two-phase alloy which is a metallic material suitable even for use in highly corrosive environments with a temperature range as in oil wells and which has high corrosive resistance equ...  