JP2005256078A |
To provide a clear enameled stainless steel having the metallic luster intrinsic of stainless steel and also having excellent scratch resistance and oil soiling resistance.The clear enameled stainless steel sheet is provided with a clear...
|
JP2005248189A |
To obtain an enamelled Al-plated stainless steel having excellent adhesion of enamel, and further having satisfactory workability and designing properties.A thermal expansion difference ΔE=(1 to 4)×10-6/°C is imparted between the ther...
|
JP2005227133A |
To provide a manufacturing method for a porcelain enamel steel sheet capable of preventing lowering of a yield, by detecting and judging a defect brought to a blister defect and by removing it.This manufacturing method for the porcelain ...
|
JP3681149B2 |
To obtain a pyrogenous material composed of mainly MoSi2, which has excellent pest resistivity and of which performance does not deteriorate over a long period of time. Content of a nonconforming component is reduced which spreads spaces...
|
JP2005200726A |
To provide an enameled steel sheet with an elaborated design, by distributing surface enamel layers 3 like an island shape.The enameled steel sheet having surface enamel layers 3 distributed like the island shape is formed by the steps o...
|
JP3664538B2 |
To provide a ferritic stainless steel sheet having a surface form high in adhesion with a coating film by continuous production. This ferritic stainless steel sheet excellent in adhesion with a coating film is the one in which pits are c...
|
JP3664537B2 |
To produce a stainless steel sheet having a surface from high in adhesion with an inorganic coating film by continuous production. An austenitic stainless steel sheet in which spherical pits are compactly formed on the surface of the ste...
|
JP3645331B2 |
To provide a method for producing an enameled member capable of reproducing an extremely delicate photographic picture using a photographic transfer sheet. A photographic transfer sheet is stuck with water on the sticking part 3 of an en...
|
JP3620404B2 |
Methods and apparatuses for efficiently forming a homogeneous glass layer having uniform thickness and a homogeneous metal layer having uniform thickness are provided. A workpiece is accommodated in a screened container which is rotatabl...
|
JP2005022927A |
To provide a pottery and an enameled article having antibacterial properties and antibacterial activities, which contains an antibacterial agent which is not deactivated by urine or tap water, safe for human body, and harmless for enviro...
|
JP2005008974A |
To provide a porcelain enameled material which persistently shows high photocatalytic functions while maintaining the characteristics of porcelain enamel such as gloss, acid resistance and alkali resistance, and to provide a method for e...
|
JP2004358846A |
To provide a coated metal sheet having a composite layer coating film of an enamel layer 2/photocatalyst layer 3, which is excellent in coating film adhesion and photocatalytic activity, formed thereto.In the enamel/photocatalyst composi...
|
JP2004532908A |
An enameling composition comprising an enamel sinter and a heat hardening resin consists of a powder of a substance free from any solvent for the resin. ?>Independent claims are also included for the following: ?>(a) the production o...
|
JP2004256917A |
To provide a composite material and a cooking container having an antibacterial action manufactured from the composite material.The composite material is composed of a base body made of a ground metal whose surface is at least partially ...
|
JP3557868B2 |
When machine works such as a honing processing, nicking processing or mirror finishing are applied on the surface 10a of the facing member of watches and clocks composed of Ti and Ti alloy, a layer of Ti oxide is formed to cause surface ...
|
JP3557869B2 |
|
JP2004522546A |
An object of the present invention is to provide a method for sintering a bioactive glass or a bioactive glass complex. The method of the present invention is characterized in that its sintering is carried out using localized electromagn...
|
JP3524349B2 |
To improve an antibacterial effect by baking a substrate bake layer on the surface of a raw metal sheet, applying and baking the glaze containing a glass material, a pigment, and an antibacterial agent on the substrate bake layer to form...
|
JP3521618B2 |
To provide a steel sheet for porcelain enameling excellent in adhesion even if being subjected to repeated firing. This steel sheet for porcelain enameling excellent in adhesion has a compsn. contg., by weight, ≤0.005% C, 0 to 0.05% Si...
|
JP2004107754A |
To provide a plated steel sheet for enameling in which a low-carbon Al-killed steel sheet, a high-oxygen steel sheet, a Ti-added steel sheet, an Nb-added steel sheet or a B-added steel sheet can be used and by which excellent workability...
|
JP2004107755A |
To provide a steel sheet for porcelain enameling by which excellent adhesion of enamel can be obtained by only one-coat enameling using a Ti-added steel sheet, its manufacturing method, an enameled product and its manufacturing method.Co...
|
JP2004107753A |
To provide a steel sheet for porcelain enameling in which excellent adhesion of enamel can be obtained by one-coat enameling using a Ti-added steel sheet, and to provide its manufacturing method, an enameled product and its manufacturing...
|
JP2004084011A |
To provide a steel sheet to be enameled, which is highly strengthened when baked after being enameled, without deteriorating formability and enameling properties, and to provide an enameled and baked steel sheet.The steel sheet to be ena...
|
JP2004050764A |
To provide a self-cleaning material which can sufficiently exhibit a self-cleaning effect without an increase in cost, and is excellent in safety, hygienic properties, and environment protection, and to provide its manufacturing method.A...
|
JP3475258B2 |
PURPOSE: To form a ceramic coating film having a low coefft. of thermal expan sion and excellent in heat resistance and electric insulating property on the surface of a metallic material at a lower temp. than the temp. at which an MgO co...
|
JP2003342755A |
To provide various vitreous-layer-coated aluminum-alloy cast products in which vitreous layer coating is made possible by a new aluminum-alloy casting method or regulation of an aluminum-alloy composition. An inorganic mold-coating mater...
|
JP3471415B2 |
PURPOSE: To produce a stainless steel sheet for enameling good in adhesion by constituting a stainless steel of specified wt.% of C, Cr, Al and Fe and forming an oxidized film excellent in adhesive strengths bath to a metallic matrix and...
|
JP2003293172A |
To provide a method for coating application of glaze which enables anyone to easily, exactly and stably apply the glaze for beading to prescribed positions and an apparatus for coating application of the glaze.The method for coating appl...
|
JP2003524076A |
The invention concerns a method which consists in: providing a protective treatment against corrosion to the initial sheet metal using an aqueous emulsion containing colloids based on acrylic and/or methacrylic polymer; a step which cons...
|
JP2003221688A |
To provide a process for manufacturing a porcelain enamel steel sheet having a porcelain enamel surface sufficiently smooth for practical use at a low cost, without deteriorating the original characteristics of porcelain enamel having ex...
|
JP3432399B2 |
To improve volume resistivity by incorporating a frit and a metallic fiber having a specific diameter, length and shape ratio of (length)/(diameter) in a specific quantity to the frit. The diameter of the metallic fiber to be used is pre...
|
JP2003212594A |
To provide a frit for porcelain enamel and a porcelain enamel product at a low cost.This production method of the frit for porcelain enamel features that waste glass cullet is pulverized and the frit for porcelain enamel is produced. The...
|
JP2003212599A |
To suppress unfavorable rise of viscosity in aqueous slurry using frit which easily changes in the lapse of time.At first, the frit is dry-pulverized to prescribed grain size in a dry state corresponding to usage purpose of the slurry. A...
|
JP3431658B2 |
PURPOSE: To obtain the joined body of heat-resistant alloy excellent in electrical insulation, high-temp. strength, normal-temp. strength and heat resistance cycle property. CONSTITUTION: The opposed surfaces of the heat-resistant alloy ...
|
JP2003192471A |
To provide a method for forming a glaze layer to impart excellent antibacterial mildew-proof property on the surface of a pottery or a substrate of an enamel product.A water-based slurry containing a silver-containing substance and a gla...
|
JP3414523B2 |
PURPOSE: To thin an enameled panel, to facilitate the cutting of the panel into desired shape and size and to reduce the production cost and weight. CONSTITUTION: A glaze having high contents of boron oxide, nickel oxide and copper oxide...
|
JP2003138388A |
To easily apply metallic tone decoration to a porcelain enamel face, to form a uniform coating of mica having heat resistance on a porcelain enamel face, to remarkably improve the heat resistance of porcelain enamel, and therefore, to ob...
|
JP2003138387A |
To provide a durable, heat resistant porcelain enamel-coated stainless steel heating cooker which can easily be washed though food materials such as meat and fish are roasted thereon by the direct heating of a grill or a salamander with ...
|
JP3402430B2 |
To obtain a panel for building material excellent in not only weather resistance and corrosion resistance but the hardness of a coating film and anti- staining property by mixing an inorganic base clear specified in the content of an ino...
|
JP3400259B2 |
To improve wear resistance by incorporating fine grains of silica and/or alumina into a specified composite film. This hydrophilic film is produced by a following method. Namely, the composite sol soln. contg. a titania sol capable of be...
|
JP3395826B2 |
To improve adhesion of porcelain enamel by forming an Al-Zn alloy plating layer on the surface of a steel sheet, providing a porcelain enamel coating layer as an outermost layer, and further providing an interposition layer between the p...
|
JP3394188B2 |
To assure sufficient post bendability, to prevent a ground surface from being visible through and to impart glass to the surface by forming an enamel layer contg. a prescribed amt. of pigments on at least one surface of a substrate and a...
|
JP3390349B2 |
To surface-treat the inner-container internal surface of inner/outer double containers uniformly and for easy cleaning resulting from no possibility that the surface will have contents sticking to it, smell and foul, improve the outer ap...
|
JP2003054988A |
To provide a product having a glass layer which can display high antibacterial ability without causing rise in product cost and deterioration of appearance. The product has the glass layer 10 made of silicate glass on a surface of a base...
|
JP3372820B2 |
|
JP3373067B2 |
PURPOSE: To automate the pretreatment of the specimen of enameling steel sheet and to improve the working environment by allowing a twin-shaft robot controlled in an evacuated casing to move the specimen and dip the specimen in a treatin...
|
JP3368173B2 |
To provide a process for producing an enamel plate capable of reproducing extremely fine photographic images by using a photographic transfer sheet. In the case where holes 9 for hanging by hooks are formed on a base metallic plate 3 to ...
|
JP3366904B2 |
|
JP3364441B2 |
|
JP2002363774A |
To provide a porcelain enameling material for a kitchen which has excellent durability even in use for parts in the vicinity of a stove and within a grill which are continuously exposed to high temperatures, water, salt or the like, and ...
|