To improve appearance and weatherability by forming a specific hot-melt adhesive layer on a base material layer composed of a vinyl chloride type resin film having a specific compsn.
A film with a thickness of 50-300μm composed of a vinyl chloride resin compsn. prepared by adding 10-40 pts.wt. of a plasticizer, 1-10 pts.wt. of phosphoric ester, 0.1-3 pts.wt. of an ultraviolet absorber, 5-50 pts.wt. of titanium oxide and 0.1-3 pts.wt. of a metal salt of org. phosphoric partial ester represented by formula I or II (wherein M is one or more metal element selected from a group consisting of zinc, calcium, barium, magnesium and strontium and R1, R2, R3, R4 and R5 are respectively a 1-22C alkyl group, an aralkyl group, an alkylaryl group or an ether bond-containing hydrocarbon group) to 100 pts.wt. of a vinyl chloride resin is set to a base material layer. A hot-melt adhesive layer with a thickness of 5-100μm composed of chlorinated polypropylene with chlorine content of 15-35wt.% is formed on the single surface of the base material layer.