To provide a manufacturing method of a cold-rolled steel plate excellent in sliding characteristic and die galling resistance, and the cold-rolled steel plate.

After executing the hot rolling and the cold rolling, the oxidation treatment is executed in the atmosphere containing 0.05% O2 and/or 0.10% H2O, and the reduction treatment is successively executed in the atmosphere containing 1.0-100% H2. Fe-based oxides are formed on a surface by executing the oxidation treatment. Thereafter, by reducing the oxides, a cold-rolled steel plate is obtained, wherein reduced Fe is present on its surface. In the oxidation treatment, the steel plate is preferably heated to 400-900C, and the steel plate is further heated at the temperature raising rate of 5C/sec in the temperature range of 400-650C.