To provide a non-heat treated steel for induction hardening in which melting cracks caused in the case heating temperature for performing induction hardening is made high can be suppressed, and further, which can impart high fatigue strength to a machine structural component such as a crank shaft.
The non-heat treated steel for induction hardening has a composition containing 0.35 to 0.45% C, >0.30 to 0.70% Si, 1.00 to 1.50% Mn, ≤0.030% P, 0.010 to 0.035% S, 0.10 to 0.30% Cr, 0.005 to 0.050% Al, 0.100 to 0.200% V and 0.0040 to 0.0200% N, wherein the value expressed by expression: [80C