FOR CURING

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit of priority of U.S. Application Serial No.

14/012355 filed on August 28, 2013 the content of which is relied upon and incorporated herein by reference in its entirety.

FIELD

[0002] This disclosure relates to adhesive and more particularly to radiation curable adhesive compositions used for attaching an optical element to a structure that is configured to support the optical element.

BACKGROUND

[0003] Radiation-curable adhesive compositions are employed in a variety of applications in which a durable, permanent bond or seal between parts is desired. The use of an adhesive provides a cost-effective alternative to mechanical mounts that imparts less stress on the parts being joined together. In many cases, it is possible to expose all portions of the curable adhesive composition to direct radiation, such as when the adhesive is positioned entirely within a gap between parts that are to be bonded together or sealed, or when at least one of the parts is transparent to radiation of the frequency (or wavelength) needed to cure (chemically harden) the adhesive composition. However, in many cases, it is not possible to directly expose all portions (i.e., the entire volume or mass) of the radiation-curable adhesive composition to radiation of a frequency (or wavelength) that will initiate curing of the adhesive composition (i.e., an actinic radiation), such as when at least a portion of the adhesive composition is disposed between parts comprised of a material that blocks the actinic radiation. Also, a light blocking coating may be applied over a surface of the optical element to obstruct or block radiation that would cause degradation of the adhesive. The unexposed portions of the adhesive composition may cure very slowly, resulting in unacceptably long fixing times. Accordingly, there has been a recognized need to provide structures and processes that facilitate rapid curing of those portions of a radiation-curable adhesive or sealant composition that cannot be exposed directly to the actinic radiation (e.g., along a straight line from the radiation source to the adhesive).

[0004] U.S. Patent Application Publication No. 2013/0090402 Al describes the use of a light-diffusing optical fiber that is coupled to an actinic light source and is at least partially disposed within a portion of a radiation-curable adhesive composition that is located in a region between parts (e.g., a holder and an optical element) that are to be joined together, which region is blocked from receiving radiation directly from an external source. While providing a workable solution to the problem of exposing a radiation-curable composition that is blocked from being irradiated by an external source to actinic radiation, this technique is relatively expensive due to the added steps of providing a light-diffusing optical fiber coupled to an actinic light source, and properly positioning the light-diffusing optical fiber within the adhesive composition to facilitate exposure of the composition to actinic radiation and rapid curing.

SUMMARY

[0005] Disclosed is a radiation-curable adhesive composition that is capable of scattering actinic radiation. More particularly, the composition allows sufficient scattering and redistribution of the actinic radiation to facilitate rapid curing of a portion of the composition that is blocked from receiving actinic radiation directly from an external source, and which is contiguous with a different portion of the composition that is not blocked from receiving actinic radiation directly from the external source.

[0006] The radiation-curable adhesive composition that is capable of scattering actinic radiation to facilitate rapid curing of a portion of the adhesive that is blocked from directly receiving actinic radiation may include a photocurable material and a structured optical particulate material dispersed throughout the photocurable material, wherein the structured optical particulate material is capable of scattering the actinic radiation throughout the photocurable material.

[0007] Also disclosed are optical devices having an optical element adhesively joined to a support structure using a cured adhesive composition as described herein, and processes for attaching an optical element to a support structure using a disclosed radiation-curable adhesive composition that is capable of scattering actinic radiation. BRIEF DESCRIPTION OF THE DRAWINGS

[0008] Figure 1 is a schematic diagram of a known optical device receiving actinic radiation from an external radiation source to induce curing of an adhesive disposed between a support structure and an optical element, with the close-up inset illustrating that the radiation does not reach a portion of the adhesive disposed directly beneath a coating that blocks light of a wavelength spectrum that causes degradation of the adhesive.

[0009] Figure 2 is an alternative close-up inset in which the adhesive composition of

Figure 1 is replaced with an adhesive composition containing a structured optical particulate material that is capable of scattering light throughout portions of the adhesive composition that are blocked or obstructed from receiving radiation directly.

[0010] Figure 3 is an alternative close-up inset in which the adhesive composition of

Figures 1 or 2 is replaced with an adhesive composition containing both a structured optical particulate material that is capable of scattering light through portions of the adhesive compositions that are blocked or obstructed from receiving radiation directly, and a second particulate material that is capable of absorbing radiation of a wavelength that is different from the wavelength of the curing radiation.

[0011] Figure 4 is a schematic illustration of a device in which adhesion between a mirrored optical element and a metal holder is improved by adding, to a radiation-curable adhesive, a structured optical particulate material that is capable of scattering light through portions of the adhesive compositions that are blocked or obstructed from receiving radiation directly.

DETAILED DESCRIPTION OF THE DISCLOSED EMBODIMENTS

[0012] The radiation-curable adhesive compositions employed in the various embodiments and aspects of this disclosure are flowable compositions that can be exposed to radiation (e.g., ultraviolet radiation or electron beam) to cause the composition to solidify and harden by chemical reactions such as polymerization and/or cross-linking employing any of a variety of different chemistries. These photocurable compositions may comprise a combination of small molecules (e.g., monomers), oligomers and polymers, and for example include radiation-curable epoxy, oxetane, vinyl ethers, propenyl ether, crotyl ether, allyl ether, propargyl ether, maleate ester, fumarate ester, cinnamate ester, styrenic, acrylamide, methacrylamide, acrylate, methacrylate, maleimide and thiol-ene based resin compositions.

[0013] The term "adhesive composition" as used herein and in the claims is meant to encompass sealants and potting compositions having an adhesive quality (i.e., the ability to bond to a surface of a support structure and to an optical element held on the support structure).

[0014] Dispersed in the photocurable liquid is a structured optical particulate material that is capable of collecting and scattering radiation, including at least radiation of a frequency (or wavelength) that is capable of inducing curing of the photocurable liquid. The structured optical particulate material can be uniformly distributed in the photocurable liquid using a mechanical mixing apparatus. Generally, the small particle size of the structured optical material, combined with the viscosity of the photocurable material, as well as the relatively small difference in the density (or specific gravity) of the structured optical material as compared to the photocurable material prevents rapid settling, allowing storage of the adhesive composition for a reasonable period before remixing is needed prior to use.

[0015] Factors that affect the light scattering properties of the structured optical material include particle size and asphericity, the wavelength of the actinic radiation that is to be scattered, the ratio of the refractive index of the structured optical material relative to the refractive index of the photocurable liquid, and surface roughness of the structured optical particulate material. The structured optical particulate material could be any particulate material capable of transmitting and/or reflecting the actinic radiation capable of inducing photocure. The particulate could be organic (e.g., synthetic or natural polymers, etc.) or inorganic (e.g., glass, ceramic, glass-ceramic, minerals, etc.). The particles may be regular in shape (e.g., spheroid or cylindrical), fibrous, or can be irregular in shape as in the particles obtained from grinding. An example of a structured optical material that may be used is fused silica microspheres. Such particles can have a diameter of from about 30 to about 300 microns. Other structured optical materials may include glass or polymer microspheres or aspherical particles (e.g., spheroid or cylindrical).

[0016] The amount of structured optical material that may be incorporated into the adhesive composition is not particularly limited. In general, the particulate structured optical material is added in an amount that is sufficient to improve adhesion by scattering curing radiation to portions of the adhesive that would not otherwise be exposed to the curing radiation, while avoiding excessive amounts of the structured optical particulate material that would adversely affect adhesive properties or the cohesive strength of the cured composition. Exemplary amounts are 0.01% to 50%, 0.1% to 30%, 0.5% to 25%, 1% to 20%, 2% to 15% and 5% to 10% of the total weight of the adhesive composition.

[0017] In certain aspects of this disclosure, the structured optical material can be selected to absorb light of a wavelength that is different from that of the actinic radiation that causes curing of the photocurable liquid material. More particularly, the absorbed wavelength can be a wavelength or wavelength spectrum or range that has a degradative effect on the cured adhesive composition. Alternatively, a second particulate material can be dispersed in the adhesive composition to absorb degradative radiation.

[0018] Figure 1 illustrates a known optical device 312 having an optics mount or support structure 310 having a central aperture 316 defined by an inner ring 320, which is defined in part by a lip 330 configured to receive an optical element 300 that is ultimately secured to the support structure by a reacted photocurable adhesive material 270. An actinic radiation source 150 is used to direct radiation 152 to the photocurable material 270 to induce curing thereof. A lens 180 can be placed between source 150 and the device 312 during its assembly to shape the illumination pattern so that light 152 is directed toward surface 271 of photocurable material 270 and covers a sufficiently large area of the bondline. If the element 300 has been processed on one or more of its surfaces (e.g., bottom surface 304 or side surface 302) with a coating 301 or other treatment that blocks transmission of the curing (actinic) radiation, or is made of a material that does not transmit the curing radiation, the portion 270B of adhesive 270 that is not directly illuminated by radiation 152 from source 150 will not cure at an appreciable rate. As a result, the bond between structure 310 and element 300 may be less than adequate for a substantial time until portion 270B has cured without benefit of radiation 152.

[0019] Figure 2 shows an alternative close-up inset of an assembly or device similar to that shown in Figure 1, using an adhesive composition comprising a structured optical particulate material 400 dispersed throughout photocurable composition 270. Structured optical particulate material 400 transmits curing radiation 152 to region 270B of photocurable composition 270 that is blocked from receiving curing radiation 152 directly via a scattering mechanism.

[0020] Structured optical particulate material 400 acts as a waveguide for curing radiation 152 to redirect radiation to areas in the photocurable composition 270 (e.g., adhesive, sealant or potting composition) that would otherwise be obstructed from receiving radiation 152 from source 150.

[0021] Figure 3 shows a slightly modified alternative close-up inset of an assembly or device similar to that shown in Figures 1 and 2, using an adhesive composition that contains a structured optical particulate material 400 dispersed throughout composition 270 and a second particulate material 410 that absorbs radiation at a wavelength or wavelength spectrum or range that is different from the wavelength or wavelength spectrum or range of the curing radiation. The purpose of second particulate material 410 is to absorb radiation (e.g., ultraviolet radiation, usually of a wavelength shorter than that of the operating wavelengths used in the device 312) that would cause degradation of the cured product of adhesive composition 270. Thus, according to some embodiments, an adhesive composition includes: (a) a photocurable material; and (b) a structured optical particulate material dispersed throughout the photocurable material, the structured optical particulate material being capable of scattering radiation of a first wavelength throughout the photocurable material. In some exemplary embodiments the structured optical particulate material is fused silica microspheres. In some embodiments the structured optical material is capable of absorbing light of a second wavelength. In some embodiments the adhesive composition further includes a second particulate material that absorbs radiation of a second wavelength

[0022] Figure 4 schematically illustrates a device 512 using an ultraviolet radiation- curable adhesive composition 570 to bond a mirror 500 to a metal holder 510. The mirrored surface prevents direct illumination of the bondline from the curing radiation 552 emitted from radiation source 550. A small portion 580 of adhesive composition 570 that extends outwardly beyond the outer diameter of mirror 500 is exposed to radiation 552 and is redirected by structured optical particulate material in adhesive composition 570 to the larger portion of adhesive composition 570 that is obstructed from receiving radiation 552 directly from source 550. [0023] Pushout force testing to determine the force needed to break an adhesive bondline between an optical element and a holder in an arrangement similar to that described above and illustrated in Figure 4 demonstrate that light scattered by the structured optical particulate material (e.g., fused silica microspheres) facilitates a complete cure of a bondline shielded from direct illumination by a coating, which cure is equivalent to an otherwise identical arrangement in which the bondline is not shielded and receives direct illumination. This result demonstrates that addition of the structured optical particulate filler facilitates radiation induced curing at obstructed portions of the adhesive composition that would not otherwise cure within an acceptable timeframe.

[0024] Thus, according to some embodiments an one optical device comprises: (a) a support structure configured to retain an optical element; (b) an optical element positioned on the support structure; and (c) a cured adhesive composition disposed between a surface of the support structure and a surface of the optical element to adhesively bond the optical element to the support structure, the cured adhesive composition having a cross-linked polymer matrix material and a structured optical particulate material dispersed throughout the matrix. The cured adhesive composition may be disposed in a region between the optical element and the support structure that is not within a direct illumination path. For example, cured adhesive composition may be disposed in a region between the optical element and the support structure that is shielded from a direct illumination path by a coating applied to a surface of the optical element.

[0025] According to some embodiments a process for adhesively attaching an optical element to a support structure includes the following steps: (a) positioning the optical element on the support structure with the photocurable adhesive composition disposed between a surface of the support structure and a surface of the optical element; and (b) directing at the photocurable adhesive composition radiation of a wavelength suitable to cause curing of the photocurable adhesive composition. According to some embodiments the process further comprises the step of applying a surface treatment or coating to a portion of the surface of the optical element before directing the radiation at the photocurable adhesive composition, wherein the surface treatment or coating shields at least a region of the adhesive composition from receiving the radiation along a direct illumination path. The optical member may be, for example, a lens or mirror. According to some embodiments of the process the photocurable adhesive composition has structured optical material situated therein and the structured optical material is capable of absorbing light of a second wavelength. A second particulate material that absorbs radiation of a second wavelength may also be situated within the photocurable adhesive composition.

[0026] The optical elements fixed to the support structures of the devices disclosed herein can be reflective elements such as a mirror, refractive elements such as a refractive lens, or diffractive elements such as refractive gratings or lenses.

[0027] The described embodiments are preferred and/or illustrated, but are not limiting. Various modifications are considered within the purview and scope of the appended claims.