Ink-jet printing (IJP) is a non-impact printing technique in which droplets of ink are ejected through a fine nozzle onto a substrate without bringing the nozzle into contact with the substrate.

There are many demanding performance requirements for dyes and inks used in IJP. For example they desirably provide sharp, non-feathered images having good water, light and ozone fastness and high optical density. The inks are often required to dry quickly when applied to a substrate to prevent smudging, but they should not form a crust over the tip of an ink-jet nozzle because this will stop the printer from working. The inks should also be stable to storage over time without decomposing or forming a precipitate which could block the fine nozzle.

A particular problem for photorealistic quality printing is that of light-fastness.

Prints are often exposed to daylight for long periods and there is a need for the image to have as good light-fastness as possible. However, at the same time ink-jet photorealistic quality prints have to compete with silver halide photography and so the dyes used in IJP inks cannot be unduly expensive. The colorants in the print reacting with atmospheric ozone can play a major role in poor light-fastness.

This invention relates to colorants suitable for use in ink-jet printing inks and ink-jet printing processes with improved ozone-fastness and light-fastness.

According to the present invention there is provided a process for coloration of a substrate comprising applying thereto by means of an ink jet printer a composition comprising a medium and a compound of Formula (1): Formula (1) wherein: A is optionally substituted aryl ; B is optionally substituted arylene ; and R'and R2 are each independently H or optionally substituted alkyl.

The ink-jet printer preferably applies the composition to the substrate in the form of droplets which are ejected through a small orifice onto the substrate. Preferred ink-jet printers are piezoelectric ink-jet printers and thermal ink-jet printers. In thermal ink-jet

printers, programmed pulses of heat are applied to the composition in a reservoir by means of a resistor adjacent to the orifice, thereby causing the composition to be ejected in the form of small droplets directed towards the paper during relative movement between the substrate and the orifice. In piezoelectric ink-jet printers the oscillation of a small crystal causes ejection of the composition from the orifice. Alternately the ink can be ejected by an electromechanical actuator connected to a moveable paddle or plunger as for example described in WO 00/48938 and WO 00/55089.

The substrate is preferably paper, plastic, a textile, metal or glass more preferably paper, an overhead projector slide or a textile material, especially paper.

Preferred papers are plain, coated or treated papers which may have an acid, alkaline or neutral character.

Preferably A is optionally substituted phenyl or optionally substituted naphthyl.

Preferably B is optionally substituted phenylen or optionally substituted naphthylene. More preferably A is optionally substituted phenyl and B is optionally substituted phenylen.

Preferred optional substituents which may independently be present on A or B are optionally substituted alkyl (preferably C, 4-alkyl), optionally substituted alkoxy (preferably C1 4-alkoxy), optionally substituted aryl (preferably phenyl), optionally substituted aryloxy (preferably phenoxy), polyalkylene oxide (preferably polyethylene oxide or polypropylene oxide), carboxy, phosphato, sulpho, nitro, cyano, halo, ureido, SOIF, hydroxy, ester, - NR3R4,-COR3,-CONR3R4,-NHCOR3, carboxyester, sulphone, and-SO2NR3R4 wherein R3 and R4 are each independently H or optionally substituted alkyl (especially C1 4-alkyl).

More preferably the optional substituents which may independently be present on A or B are each independently; methyl, ethyl, propyl, butyl, phenyl, methoxy, ethoxy, butoxy, carboxy, phosphato, sulpho, nitro, phenoxy, cyano, carboxyester, sulphone, sulphonamide, ureido, SO2NR3R4 or NHCOR3 groups wherein R3 and R4 are as hereinbefore defined.

When A is optionally substituted naphthyl or B is optionally substituted naphthylene then preferably A and/or B carry one or more (preferably 1 to 4) substituents selected from hydroxy, amino, sulpho and carboxy.

When A is optionally substituted phenyl or B is optionally substituted phenylen then preferably A and/or B carry at least one substituent selected from hydroxy, phosphato, amino, sulpho and carboxy. More preferably when A is optionally substituted phenyl or B is optionally substituted phenylen then A and B each independently carry at least one carboxy or sulpho substituent.

Preferably R'and R2 are each independently H or C, 4-alkyl, more preferably R' and R are H.

Preferably compounds of Formula (1) have 1,2 or 3 water-dispersing substituents.

Preferred water-dispersing substituents are polyalkylene oxides, sulpho, phosphato and carboxy, more preferably sulpho and carboxy.

Preferred polyalkylene oxide groups are poly (C2-3-alkylene oxide) groups, more preferably polyethylene glycol and polypropylene glycol, preferably having from 1 to 20 glycol units and terminated with a hydroxy or C1 4-alkoxy group.

Preferably the compounds of Formula (1) are water-soluble.

Preferably the compounds of Formula (1) do not contain groups reactive towards textiles.

It is also preferred that compounds of Formula (1) are disazo.

In view of the foregoing preferences, a preferred compound of Formula (1) is of Formula (2) as hereinafter described.

Any acid or basic groups on the compound are preferably in the form of a salt.

Thus the Formulae shown herein include the compounds in free acid and in salt form.

Preferred salts are alkali metal salts, especially lithium, sodium and potassium, ammonium and substituted ammonium salts (including quaternary amines such as ((CH3) 4N+) and mixtures thereof. Especially preferred are salts with sodium, lithium, ammonia and volatile amines, more especially sodium salts. The compounds may be converted into a salt using known techniques.

The compounds of Formula (1) and (2) may exist in tautomeric forms other than those shown in this specification. These tautomers are included within the scope of the present invention.

Preferably the composition comprises: (a) from 0.01 to 30 parts of a compound of Formula (1) as hereinbefore defined, preferably of Formula (2) as hereinafter described; and (b) from 70 to 99.99 parts of a medium; wherein all parts are by weight and the number of parts of (a) + (b) =100.

Preferably the medium is a liquid medium.

The number of parts of component (a) is preferably from 0.1 to 20, more preferably from 0.5 to 15, especially from 1 to 5 parts. The number of parts of component (b) is preferably from 99.9 to 80, more preferably from 99.5 to 85, especially from 99 to 95 parts.

The composition may of course contain further ingredients in addition to (a) and (b).

Preferably component (a) is completely dissolved in component (b). Preferably component (a) has a solubility in component (b) at 20°C of at least 10%. This allows the preparation of liquid concentrates which may be used to prepare more dilute inks and also reduces the chance of component (a) precipitating if evaporation of the liquid medium occurs during storage.

Preferred liquid media include water, a mixture of water and organic solvent and organic solvent free from water.

When the liquid medium comprises a mixture of water and organic solvent, the weight ratio of water to organic solvent is preferably from 99: 1 to 1: 99, more preferably from 99: 1 to 50: 50 and especially from 95: 5 to 80: 20.

It is preferred that the organic solvent present in the mixture of water and organic solvent is a water-miscible organic solvent or a mixture of such solvents. Preferred water- miscible organic solvents include C, _6-alkanols, preferably methanol, ethanol, n-propanol, isopropanol, n-butanol, sec-butanol, tert-butanol, n-pentanol, cyclopentanol and cyclohexanol ; linear amides, preferably dimethylformamide or dimethylacetamide ; ketones and ketone-alcohols, preferably acetone, methyl ether ketone, cyclohexanone and diacetone alcohol ; water-miscible ethers, preferably tetrahydrofuran and dioxane; diols, preferably diols having from 2 to 12 carbon atoms, for example ethylene glycol, propylene glycol, butylen glycol, pentylene glycol, hexylene glycol and thiodiglycol and oligo-and poly-alkyleneglycols, preferably pentane-1,5-diol, diethylene glycol, triethylene glycol, polyethylene glycol and polypropylene glycol ; triols, preferably glycerol and 1,2,6-hexanetriol; mono-C,. 4-alkyl ethers of diols, preferably mono-C,. 4-alkyl ethers of diols having 2 to 12 carbon atoms, especially 2-methoxyethanol, 2- (2-methoxyethoxy) ethanol, 2- (2-ethoxyethoxy)-ethanol, 2- [2- (2-methoxyethoxy) ethoxy] ethanol, 2- [2- (2-ethoxyethoxy)- ethoxy]-ethanol and ethyleneglycol monoallylether ; cyclic amides, preferably 2-pyrrolidone, N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, caprolactam and 1,3-dimethylimidazolidone; cyclic esters, preferably caprolactone ; sulphoxides, preferably dimethyl sulphoxide and sulpholane. Preferably the liquid medium comprises water and 2 or more, especially from 2 to 8, water-miscible organic solvents.

Especially preferred water-miscible organic solvents are cyclic amides, especially 2- pyrrolidone, N-methyl-pyrrolidone and N-ethyl-pyrrolidone ; diols, especially pentane-1,5-diol, ethyleneglycol, thiodiglycol, diethyleneglycol and triethyleneglycol ; and mono-C14-alkyl and C, -alkyl ethers of diols, more preferably mono-C14-alkyl ethers of diols having 2 to 12 carbon atoms, especially 2-methoxy-2-ethoxy-2-ethoxyethanol.

Although not necessary, further colorants may be added to the composition medium to modify the shade and performance properties of the composition. Examples of such colorants include C. I. Direct Yellow 86,132,142 and 173; C. I. Direct Blue 199, and 307; C. I.

Food Black 2; C. I. Direct Black 168 and 195; C. I. Acid Yellow 23; and any of the dyes used in ink-jet printers sold by Seiko Epson Corporation, Hewlett Packard Company, Canon Inc.

& Lexmark International. Addition of such further colorants can increase overall solubility leading to less kogation (nozzle blockage) for the resultant composition.

It particularly preferable to add C. l. Direct Yellow 173 to the composition.

Examples of further suitable liquid media comprising a mixture of water and one or more organic solvents are described in US 4,963,189, US 4,703,113, US 4,626,284 and EP 4,251,50A.

When the liquid medium comprises organic solvent free from water, (i. e. less than 1% water by weight) the solvent preferably has a boiling point of from 30° to 200°C, more preferably of from 40° to 150°C, especially from 50 to 125°C. The organic solvent may be water-immiscible, water-miscible or a mixture of such solvents. Preferred water-miscible organic solvents are any of the hereinbefore described water-miscible organic solvents and mixtures thereof. Preferred water-immiscible solvents include, for example, aliphatic hydrocarbons; esters, preferably ethyl acetate; chlorinated hydrocarbons, preferably CH2CI2 ; and ethers, preferably diethyl ether; and mixtures thereof.

When the liquid medium comprises water-immiscible organic solvent, preferably a polar solvent is included because this enhances solubility of the dye in the liquid medium.

Examples of polar solvents include C14-alcohols. In view of the foregoing preferences it is especially preferred that where the liquid medium is organic solvent free from water it comprises a ketone (especially methyl ethyl ketone) and/or an alcohol (especially a Cl-4- alkanol, more especially ethanol or propanol).

The organic solvent free from water may be a single organic solvent or a mixture of two or more organic solvents. It is preferred that when the medium is organic solvent free from water it is a mixture of 2 to 5 different organic solvents. This allows a medium to be selected which gives good control over the drying characteristics and storage stability of the composition.

Liquid media comprising organic solvent free from water are particularly useful where fast drying times are required and particularly when printing onto hydrophobic and non-absorbent substrates, for example plastics, metal and glass.

Preferably the composition has been filtered through a filter having a mean pore size below 1011m, more preferably below 3Am, especially below 2pm, more especially below 1 um. This filtration removes particulate matter which could otherwise block the fine nozzles found in many ink-jet printers.

Preferably the composition contains less than 500ppm, more preferably less than 250ppm, especially less than 100pm, more especially less than 10ppm in total of halide ions.

The composition preferably has a total concentration of divalent and trivalent metal ions of below 1000, more preferably below 500, especially below 100, more especially below 20 and particularly below 10 parts per million by weight relative to the total weight of the composition (other than any divalent and trivalent metal ions bound to a component of the ink). Pure compositions of this type may be prepared by using high purity ingredients and/or by purifying the composition after it has been prepared. Suitable purification techniques are well known, e. g. ultrafiltration, reverse osmosis, ion exchange and combinations thereof.

Thus a particularly preferred composition is one which contains less than 1000ppm divalent and trivalent metal ions (other than any divalent and trivalent metal ions

bound to a component of the ink) and which has been filtered through a filter having a mean pore size below 1011m.

An especially preferred composition is one which contains less than 1000ppm divalent and trivalent metal ions (other than any divalent and trivalent metal ions bound to a component of the ink), less than 500ppm halide ions and which has been filtered through a filter having a mean pore size below 10jim.

The liquid medium may also of course contain further additives which are conventionally used in ink-jet printing inks, for example viscosity and surface tension modifiers, corrosion inhibitors, biocides, kogation reducing additives and surfactants which may be ionic or non-ionic.

A second aspect of the present invention provides a substrate, especially paper, an overhead projector slide, a textile material, a plastic, glass and metal, printed by a process according to a first aspect of the invention. Preferably the substrate is paper.

Preferred papers are plain, coated or treated papers which may have an acid, alkaline or neutral character.

According to a third aspect of the invention there is provided a composition comprising a compound of Formula (1), as hereinbefore defined, and a medium which comprises a mixture of water and organic solvent or organic solvent free from water wherein said composition has a total concentration of divalent and trivalent metal ions of below 1000 parts per million by weight relative to the total weight of the composition (other than any divalent and trivalent metal ions bound to a component of the ink) and/or has less than 500ppm halide ions and/or has been filtered through a filter having a mean pore size below 10 pu.

The composition preferably has a total concentration of divalent and trivalent metal ions of below 500, more preferably below 100, especially below 20 and more especially below 10 parts per million by weight relative to the total weight of the composition (other than any divalent and trivalent metal ions bound to a component of the ink).

Preferably the composition has been filtered through a filter having a mean pore size below 3pm, more preferably below 2pm and especially below 1 pm.

Preferably the composition contains less than 250ppm, more preferably less than 1 OOppm and especially less than 10pmin total of halide ions.

Preferably the compound of Formula (1) is of Formula (2) as hereinafter defined.

Preferred mixtures of water and organic solvent and organic solvent free from water are as described in the first aspect of the invention.

Compositions according to the third aspect of the invention are preferably prepared using high purity ingredients and/or by purifying the composition after it has been prepared.

Suitable purification techniques are well known, e. g. ultrafiltration, reverse osmosis, ion exchange and combinations thereof (either before or after they are incorporated in a composition according to the present invention). This purification results in the removal of

substantially all of the inorganic salts and by-products resulting from its synthesis. Such purification assists in the preparation of a low viscosity aqueous solution suitable for use in an ink jet printer.

Preferably the composition is an ink-jet printing ink or a liquid dye concentrate.

Concentrates are useful as a means for transporting colorant and so minimising costs associated with drying the compound and transporting excess liquid.

A fourth aspect of the invention provides a compound of Formula (1) provided it comprises at least one carboxy group or of Formula (2) or Formula (3): Formula (2) Formula (3) wherein: X is a water-dispersing substituent; p is 1 to 5 ; q is 0 to 4 ; D is optionally substituted napthyl ; E is optionally substituted phenylen ; and R'and R2 are each independently H or optionally substituted alkyl.

Preferably each X independently is sulpho or carboxy.

Preferably p is 1 or 2.

Preferably q is 0 or 1.

D preferably carries at least one water-dispersing substituent, more preferably D carries at least one sulpho and/or one carboxy.

A fifth aspect of the present invention provides an ink jet printer cartridge comprising a chamber and a composition wherein the composition is in the chamber and the composition is as described in the third aspect of the present invention.

The invention is further illustrated by the following Examples in which all parts and percentages are by weight unless otherwise stated.

Example 1 Preparation of:

C. I. Acid Yellow 9 (4g) was dissolved in water (150mut) at pH 6. The solution was cooled to 0-5°C and concentrated hydrochloric acid (5ml) was added followed by sodium nitrite (0.8g) and the suspension was stirred for 30 minutes at 5°C. Sulphamic acid (0.5g) was then added and the mixture poured into a beaker containing barbituric acid (1.3g) dissolved in water (150ml) at 5°C. The pH was adjusted to between pH 5-6 with 2 mol dm-3 sodium hydroxide solution. After stirring for 2 hours the reaction was complete. The precipitate was collected by filtration, washed with a small amount of water, and dried to give a yellow solid which when dissolved in water had a Xmax=417nm and Emax=40, 000 dm3 mol-'cm-'.

Example 2 Preparation. of: Sulphuric acid (20moi) was stirred at 0-10°C and sodium nitrite (0.8g) added step wise. 4- Amino-3', 5'-dicarboxyazobenzene (4g) was then added, followed by a 86: 14 acetic: propionic acid mixture (20ml). The mixture was stirred at between 0 to10°C for 1 hour. The resulting suspension was then added to a stirred solution of barbituric acid (1.3g), sulphamic acid (0.5g) and water (150ml) at between 0 to10°C. The pH was adjusted to between pH 5-6 with 2mol dm-3 sodium hydroxide solution and the solution stirred for 2 hours to complete the reaction. Sodium chloride was added to precipitate the title product. This precipitate was collected by filtration and dried to give a yellow solid which when dissolved in water had a #max=425nm and #max=31, 000 dm3 mol-'cm-'.

Example 3 Preparation of:

3- (4-amino-phenylazo)-naphthalene-1, 5-disulphonic acid (13g) was dissolved in water (300ml) at pH 7. Sodium nitrite (1.8g) was added. The solution was cooled to 0-5°C and concentrated hydrochloric acid (8ml) was added and the suspension was stirred for 30 minutes at 5°C. Sulphamic acid (0.5g) was then added and the mixture poured into a beaker containing barbituric acid (3.6g) and dissolved in water (1 50ml) at 5°C. The pH was adjusted to between pH 5-6 using sodium carbonate solution. After stirring for 2 hours the reaction was complete. The resultant precipitate was collected by filtration, washed with a small amount of water, and dried to give a yellow solid which when dissolved in water had a #max=4200nm and Emax=31, 000 dm3 3mol-'cm-'.

Example 4 Preparation of: 3-(4-amino-2-methoxyphenylazo) benzene sulphonic acid (9.5g) was dissolved in water (300moi) at pH 7. Sodium nitrite (2. 0g) was added. The solution was cooled to 0-5°C and concentrated hydrochloric acid (1 Oml) was added and the suspension was stirred for 60 minutes at 5°C. Sulphamic acid (0.5g) was then added and the mixture was poured into a beaker containing barbituric acid (3.8g) dissolved in water (150mol) at 5°C. The pH was adjusted to between pH 5-6 with sodium carbonate solution. After stirring for 2 hours the reaction was complete. The resultant precipitate was collected by filtration, washed with a small amount of water, and dried to give a yellow solid which when dissolved in water had a XmaX=432nm and Emax=34, 000 dm3 3mol-'cm-'.

Example 5 Preparation of:

The method for the preparation of Example 4 above was employed to synthesise the above dye except that in place of 3- (4-amino-2-methoxyphenylazo) benzene sulphonic acid there was used 3- (4-amino-3-methoxyphenylazo) benzene sulphonic acid. A yellow solid was produced which, when dissolved in water, had a #max=446nm and Emax=36, 000 dm3mol-'cm-'.

Example 6 Preparation of: The method for the preparation of the Example 4 above was used to synthesise the above dye except that in place of 3- (4-amino-2-methoxyphenylazo) benzene sulphonic acid there was used 3- (4-amino-2, 5-dimethylphenylazo) benzene-1,4-disulphonic acid. A yellow solid which when dissolved in water had a #max=441nm and Emax=34, 000 dm3 mol-1 cm Example 7 Preparation of Ink 1 Ink 1 was prepared by dissolving the compound of Example 1 (3 g) in 100 mi of a liquid medium consisting of 2-pyrrolidone/thiodiglycol/SurfynolTM 465 in a weight ratio of 5: 5: 1.

Example 8 Preparation of Ink 2 Ink 2 was prepared by dissolving the compound of Example 1 (1.5 g) and 1.5 g of Fast Yellow 2 in 100 ml of a liquid medium consisting of 2-pyrrolidone/thiodiglycol /Surfynol 465 in a ratio of 5: 5: 1.

Example 9 Preparation of Ink 3 Ink 3 was prepared by dissolving the compound of Example 4 (3 g) in 100 ml of a liquid medium consisting of 2-pyrrolindone/thiodiglycol/SurfynolTM 65 in a ratio of 5: 5: 1.

Example 10 Ink-jet Printing Inks 1 to 3 were ink-jet printed onto a variety of papers using a Hewlett Packard DeskJet 550cam. The CIE colour co-ordinates of each print (a, b, L, Chroma"C"and hue "h") were measured using a Xrite 98T" Spectrodensitometer with 0°/45° measuring geometry with a spectral range of 400-700nm at 20nm spectral intervals, using illuminant C with a 2° (CIE 1931) observer angle and a density operation of status T. No less than 2 measurements were taken diagonally across a solid colour block on the print with a size greater than 10mm x 10mm. The properties of the resultant prints are shown in Table 1.

Table 1 Ink paper % Depth L a b C h Ink 1 X AcidTM 100% 82 16 84 85 79 Ink 1 X AcidTM 50% 86 7 72 72 85 Ink 1 Hp Printing TM 100% 81 16 82 83 79 Ink 1 Hp Printing TM 50% 85 7 66 66 84 Ink 1 HR101 TM 100% 81 17 97 99 80 Ink 1 HR101TM 50% 86 6 78 78 86 Ink 1 Epson PU TM 100% 87 3 96 96 88 Ink 1 Epson PU 50% 90-3 69 69 93 Ink 1 Hp PremiumTM 100% 84 13 94 95 82 Ink 1 Hp PremiumTM 50% 87 4 72 73 87 Ink 1 Kodak Picture 100% 84 14 90 91 81 Ink 1 Kodak Picture 50% 87 6 72 72 86 Ink 2 X AcidTM 100% 84 11 81 82 83 Ink 2 X AcidTM 50% 87 3 67 68 87 Ink 2 Hp Printing TM 100% 84 9 79 80 83 Ink 2 Hp Printing TM 50% 87 2 65 65 88 Ink 2 HR101TM 50% 87 1 79 79 89 Ink 2 HR101 TM 50% 90 -4 49 49 94 Ink 2 Epson PM TM 100% 88 1 97 97 89 Ink 2 Epson PM TM 50% 91 -6 72 72 95 Ink 2 Hp PremiumTM 100% 85 9 101 102 85 Ink 2 Hp Premium TM 50% 88 1 78 78 89 Ink 2 Kodak PictureTM 100% 85 10 98 98 84 Ink 2 Kodak PictureTM 50% 88 1 79 79 89 Ink 3 X AcidTM 100% 70 40 73 83 61 Ink 3 X AcidTM 60% 76 29 66 72 66 Ink 3 Hp Printing TM 100% 69 40 70 81 60 Ink 3 Hp Printing TM 50% 75 30 59 66 63 Ink 3 HR101 TM 100% 69 44 88 98 64 Ink 3 HR101 TM 50% 76 30 73 79 68 Ink 3 Epson PM TM 100% 75 32 96 101 71 Ink 3 Epson PMTM 50% 82 16 76 78 78 Ink 3 Hp PremiumTM 100% 69 43 94 103 66 Ink 3 Hp PremiumTM 50% 76 29 75 80 69 Ink 3 Kodak PIctureTM 100% 70 43 89 99 64 Ink 3 Kodak PictureTM 50% 77 29 74 79 68

Light Fastness To evaluate light fastness the prints were irradiated in an Atlas Ci35 Weatherometer for 100 hours. The results are shown in Table 2 where degree of fade is expressed as hE where a lower figure indicates higher light fastness. AE is defined as the overall change in the CIE colour co-ordinates L*, a*, b* of the print and is expressed by the equation hE = (AL2+ ß a2+ Ab2) 0s Table 2 Ink | Paper | hE Ink1 X AcidTM 15 Ink1 HP Printing 21 Ink1 HR101TM 38 Ink1 Epson PM 14 Ink1 HP Premium 17 Ink1 Kodak Picture 39 Ink2 X Acid 16 Ink 2 HP Printing 20 Ink2 HR101TM 30 Ink 2 Epson PM 13 Ink 2 HP Premium 17 Ink 2 Kodak Picture T39 Ink 3 X Acid 16 Ink 3 HP Printing 22 Ink nk3HR101 57 Ink 3 Epson PMTm 8 Ink 3 HP PremiumTM 11 Ink 3 Kodak Picture T45

Ozone Fastness Inks 1 to 3 were printed onto the substrate shown using a Canon 4300 IJ printer.

The printed substrate was then assessed for ozone stability using an ozone test cabinet from Hampden Test Equipment. The test was carried out for two and a half hours at 40°C and 55% relative humidity in the presence of 400 parts per hundred million of ozone. Fastness of the printed ink to ozone was judged by the difference in the optical density before and after exposure to ozone using an Xrite 983 Spectrodensitometer.

Thus, the lower the loss of % OD the greater the ozone fastness. Results are shown below in Table 3 and these clearly demonstrate that inks based on dyes of this invention display good ozone fastness.

Table 3

Ink Paper OD % loss of OD Ink 1 HR101TM 0.85 23% Ink 1 Epson PMTM 0.74 24% Ink 1 HP PremiumTM 0.99 1% Ink 1 Kodak PictureT" 0. 96 4% Ink2 HR101TM 1.02 12% Ink2 Epson PM 1. 01 8% Ink2 HP Premium 1. 13 0 Ink2 Kodak PictureTM 1.17 3% Ink3 HR101TM 0.68 40% Ink3 Epson PMTM 1.03 10% Ink3 HP PremiumTM 1.31 -9% Ink3 Kodak Picture 1. 12 3%

Inks and ink-iet printing The compounds described in Examples 1 and 2 may be formulated into inks by dissolving in a suitable liquid medium and filtering the solution through a 0.45pm filter.

For example a suitable ink comprises 3.5 parts of the compound in 96.5 parts of a liquid medium consisting of: 5 parts 2-pyrrolidone 5 parts thiodiglycol 2 parts Surfyno Tm 465 (a non-ionic surfactant available from Air Products Inc.) ; and 88 parts water.

When ink-jet printed on to paper, the inks provide prints which are a bright yellow shade with a high water-fastness, good light-fastness, ozone-fastness and a high optical density.

Further Inks The inks described in Tables I and 11 may be prepared wherein the Dye described in the first column is the compound made in the above example of the same number.

Numbers quoted in the second column onwards refer to the number of parts of the relevant ingredient and all parts are by weight. The inks may be applied to paper by thermal or piezo ink-jet printing.

The following abbreviations are used in Table and)) : PG = propylene glycol DEG = diethylene glycol NMP = N-methyl pyrollidone DMK = dimethylketone IPA = isopropanol MEOH = methanol 2P = 2-pyrollidone MIBK = methylisobutyl ketone P12 = propane-1, 2-diol BDL = butane-2, 3-diol CET= cetyl ammonium bromide PHO = Na2HP04 and TBT = tertiary butanol TDG = thiodiglycol TABLE I Example Dye Water PG DEG NMP DMK NaOH na IPA MEOH 2P MIBK Content 1 2.0 80 5 6 4 5 2 3.0 90 5 5 0.2 1 10.0 85 3 3 3 5 1 2 2.1 91 8 1 1 3.1 86 5 0.2 4 5 2 1.1 81 9 0.5 0.5 9 1 2.5 60 4 15 3 3 6 10 5 4 2 5 65 20 10 1 2.4 75 5 4 5 6 5 2 4.1 80 3 5 2 10 0.3 1 3.2 65 5 4 6 5 4 6 5 2 5.1 96 4 1 10.8 90 5 5 2 10.0 80 2 6 2 5 1 4 3 1.8 80 5 15 4 2.6 84 11 5 1 3.3 80 2 10 2 6 1 12.0 90 7 0.3 3 1 5.4 69 2 20 2 1 3 3 1 6.0 91 4 5 TABLE II Example Dye Water PG DEG NMP CET TBT TDG BDL PHO 2P PI2 Content 1 3.0 80 15 0.2 5 2 9.0 90 5 1.2 5 1 1.5 85 5 5 0.15 5.0 0.2 2 2.5 90 6 4 0.12 1 3.1 82 4 8 0.3 6 2 0.9 85 10 5 0.2 1 8.0 90 5 5 0.3 2 4.0 70 10 4 1 4 11 1 2.2 75 4 10 3 2 6 1 10.0 91 6 3 1 9.0 76 9 7 3.0 9.95 5 2 5.0 78 5 11 6 2 5.4 86 7 1 2.1 70 5 5 5 0.1 0.2 0.1 5 0.1 5 1 2.0 90 10 1 2 88 10 1 5 78 12 5 1 8 70 2 8 15 5 1 10 80 8 12 10 80 10