BIOBASED HYDROXYL OR CARBOXYL POLYESTER RESINS
Document Type and Number:
WIPO Patent Application WO/2016/038302
Kind Code:
A1
Abstract:
The invention concerns a polyester resin having a linear or branched structure and free of unsaturated fatty acids, which is hydroxylated or carboxylated and characterised in that it is made from: a) an acid component comprising: a1) at least one C4 to C6 carboxylic polyacid or anhydride, a2) at least one Cs to C54 carboxylic polyacid or anhydride, a3) optionally, at least one C2 to C22 saturated monoacid, b) an alcohol component comprising: b1) at least one biobased polyol having a functionality of at least 2, and at least one of the following two polyols b2) or b3): b2) at least one polyol different from b1) having a functionality of at least 2, b3) at least one polyol different from b1) and b2) having a functionality of at least 3. Said resin is more particularly 100% biobased. The invention also concerns a resin solution and a coating composition comprising said resin and the use of same in coatings having a high strength and made from renewable raw materials.

Inventors:
DELMAS GRÉGORY (FR)
RIONDEL ALAIN (FR)
COGORDAN FRANK (FR)
OZERAY HERVÉ (FR)
Application Number:
PCT/FR2015/052407
Publication Date:
March 17, 2016
Filing Date:
September 10, 2015
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
ARKEMA FRANCE (FR)
International Classes:
C08G63/12; C08G63/16; C08G63/668; C08G63/672; C08G63/66
Foreign References:
US20140371419A12014-12-18
US20020115817A12002-08-22
EP2325229A12011-05-25
EP2623538A12013-08-07
US20130197152A12013-08-01
Attorney, Agent or Firm:
Killis, Andréas (FR)
Download PDF:
Claims:
REVENDICATIONS

1 . Résine polyester de structure linéaire ou ramifiée et exempte d'acides gras insaturés, qui est hydroxylée ou carboxylée, éventuellement hydroxylée et carboxylée, caractérisée en ce qu'elle est à base de :

a) un composant acide a) comprenant :

a1 ) au moins un polyacide ou anhydride carboxylique en C4 à C6, de préférence de fonctionnalité fai allant de 2 à 4 et plus préférentiellement égale à 2 a2) au moins un polyacide ou anhydride carboxylique en Cs à Cs4, de préférence de fonctionnalité fa2 allant de 2 à 4 et plus préférentiellement égale à 2 a3) en option au moins un monoacide saturé en C2 à C22, éventuellement pouvant porter un groupement hydroxyle,

b) un composant alcool b) comprenant :

b1 ) au moins un polyol biosourcé de fonctionnalité fbi d'au moins 2, de préférence 2, porteur d'un motif 1 ,4:3,6 dianhydrohexitol

et au moins un des deux polyols b2) ou b3) suivants :

b2) au moins un polyol différent de b1 ) et de fonctionnalité fb2 d'au moins 2, de préférence 2, plus particulièrement un polyol en C3 à C36

b3) au moins un polyol différent de b1 ) et de b2 de fonctionnalité fb3 d'au moins 3, de préférence 3.

2. Résine selon la revendication 1 , caractérisée en ce que ledit motif de polyol b1 ) est l'isosorbide (1 ,4:3,6 dianhydro-D-sorbitol), l'isomannide (1 ,4:3,6 dianhydro-D-mannitol) ou l'isoidide (1 ,4:3,6 dianhydro-L-iditol).

3. Résine selon l'une des revendications 1 à 2, caractérisée en ce qu'une fraction d'au moins 50 %, de préférence d'au moins 75 % en poids de ladite résine est biosourcée.

4. Résine selon l'une des revendications 1 à 3, caractérisée en ce que ledit composant b) comprend b2) et b3) et qu'au moins 50 % en poids, de préférence au moins 75 % en poids dudit composant b) est biosourcé.

5. Résine selon l'une des revendications 1 à 4, caractérisée en ce que les composants a) et b) sont à 100 % biosourcés.

6. Résine selon l'une des revendications 1 à 5, caractérisée en ce que ledit polyol b2) est biosourcé et choisi parmi le 1 ,3 propylène diol ou le 1 ,2 propylène diol, le 1 ,4 butane diol ou les diols à base d'acides gras saturés.

7. Résine selon l'une des revendications 1 à 6, caractérisée en ce que ledit polyol b3) est biosourcé et choisi parmi le glycérol et ses dérivés éther-polyols, tels que les polyglycérols.

8. Résine selon l'une des revendications 1 à 7, caractérisée en ce que ledit polyacide a1 ) est un diacide aliphatique biosourcé choisi parmi : acide succinique, acide tartrique, acide citrique, acide malique, acide itaconique, acide glutarique, acide glutamique, acide fumarique, acide furanne dicarboxylique, acide tetrahydrofuranne 2,5 dicarboxylique et acide tetrahydrofuranne 3,5 dicarboxylique, de préférence acide succinique, acide itaconique, acide glutamique, acide fumarique, acide furane dicarboxylique, acide tetrahydrofuranne 2,5 dicarboxylique et acide tetrahydrofuranne 3,5 dicarboxylique.

9. Résine selon l'une des revendications 1 à 8, caractérisée en ce que ledit polyacide a2) est biosourcé et choisi parmi : l'acide azélaïque (Cg), acide sébacique (C10), acide undécane dioïque, acide dodécane dioïque ou dimères et trimères d'acides gras respectivement en C36 et C54.

10. Résine selon l'une des revendications 1 à 9, caractérisée en ce que ledit monoacide a3) est présent dans la composition de ladite résine et sélectionné parmi : acide acétique, acide pyruvique, acide lactique ou la colophane (acide abiétique et isomères en C20) ou un acide gras saturé en C12 à C22.

1 1 . Résine selon l'une des revendications 1 à 10, caractérisée en ce que ledit polyol b1 ) représente au moins 30 % en poids de ladite résine.

12. Résine selon l'une des revendications 1 à 1 1 , caractérisée en ce qu'elle a une fonctionnalité OH et/ou acide carboxylique correspondant à un indice de OH et/ou d'acide allant de 10 à 200 mg KOH/g.

13. Résine selon l'une des revendications 1 à 1 1 , caractérisée en ce qu'elle a une fonctionnalité carboxyl correspondant à un indice d'acide inférieur à 20, de préférence inférieur à 10 et plus préférentiellement inférieur à 5 et en particulier 0 mg KOH/g et une fonctionnalité en OH correspondant à un indice OH allant de 10 à 200, de préférence de 10 à 150, plus préférentiellement de 10 à 100 mg KOH/g.

14. Résine selon l'une des revendications 1 à 13, caractérisée en ce que sa masse moléculaire moyenne en nombre Mn varie de 500 à 20000, de préférence de 750 à 10000.

15. Résine selon l'une des revendications 1 à 14, caractérisée en ce que la Tg de ladite résine varie de -10°C à 100°C, de préférence de 10 à 50°C.

16. Solution de résine dans un solvant organique, caractérisée en ce qu'elle comprend au moins une résine telle que définie selon l'une des revendications 1 à 15.

17. Solution selon la revendication 16, caractérisée en ce que ledit solvant est sélectionné parmi les esters méthyliques ou esters éthyliques d'acides monocarboxyliques en C2 à C4 ou esters desdits acides monocarboxyliques avec des monoéthers méthoxy ou éthoxy de diols en C2 à C4, en particulier l'acétate de méthoxy propyle ou parmi diesters méthyliques ou éthyliques de diacides carboxyliques en C4 à C6, terpènes, polyhydroxyalcanoates, esters méthyliques ou éthyliques d'huiles d'acides gras ou esters d'acide lactique avec alcools en Ci à Cs.

18. Composition de revêtement, de préférence en milieu solvant organique, comprenant au moins une résine telle que définie selon l'une des revendications 1 à 15 ou une solution de résine telle que définie selon la revendication 16 ou 17.

19. Composition selon la revendication 18, caractérisée en ce qu'il s'agit d'une composition réticulable comprenant en plus de ladite résine au moins un agent réticulant, porteur de groupements réactifs avec les groupements hydroxyles et/ou carboxyles portés par ladite résine.

20. Composition selon la revendication 18 ou 19, caractérisée en ce que ledit agent réticulant est sélectionné parmi la mélamine ou un polyisocyanate, en particulier polyisocyanate bloqué ou un polyanhydride ou un polysilane, en particulier polysilane bloqué par alcoxy quand ladite résine est hydroxylée ou ledit agent réticulant est sélectionné parmi les polyépoxydes ou polyols quand ladite résine est carboxylée.

21 . Composition selon l'une des revendications 17 à 20, caractérisée en ce qu'il s'agit d'une composition de revêtement en milieu solvant organique, en particulier d'une composition de peinture ou de vernis, plus particulièrement pour surfaces métalliques.

22. Utilisation d'une résine telle que définie selon l'une des revendications 1 à 15 ou d'une solution de résine telle que définie selon la revendication 16 ou 17 dans les compositions de revêtements, en particulier dans les compositions de revêtements réticulables.

23. Utilisation selon la revendication 22, caractérisée en ce qu'il s'agit de compositions de revêtements à comportement « monocomposant » pour métal, en particulier pour revêtement de feuille métallique (« coil »).

24. Utilisation selon la revendication 22 ou 23, caractérisée en ce qu'il s'agit de revêtement primaire, une finition, un envers de bande ou un revêtement monocouche.

25. Utilisation selon la revendication 22 ou 23, caractérisée en ce qu'il s'agit de revêtements en poudre.

26. Utilisation selon la revendication 22, caractérisée en ce qu'il s'agit de revêtements « bicomposants ».

27. Revêtement caractérisé en ce qu'il résulte de l'utilisation d'au moins une résine telle que définie selon l'une des revendications 1 à 15 ou d'une solution de résine telle que définie selon la revendication 16 ou 17 ou d'une composition de revêtement telle que définie selon l'une des revendications 18 à 21.

Description:
RESINES POLYESTERS HYDROXYLES OU CARBOXYLES BIOSOURCEES

L'invention concerne une résine polyester de structure linéaire ou ramifiée et exempte d'acides gras insaturés, laquelle est hydroxylée ou carboxylée à base de matières premières renouvelables, en particulier au moins à base de polyol biosourcé spécifique, une composition de revêtement comprenant ladite résine et son utilisation dans les revêtements ayant une durabilité élevée et à base de matières premières renouvelables, en particulier pour revêtements de feuilles métalliques.

Les résines polyesters fonctionnalisées sans huile sont bien connues pour les applications de revêtements pourfeuilles métalliques connus sous le terme anglais « coils ».

Des résines polyesters polyols à base de composants d'origine renouvelable dits également « biosourcés » pour application dans les revêtements de feuilles métalliques sont déjà décrits dans WO 2012/042153 et en particulier des résines sans huile. Ces résines polyesters sont à base de colophane. Cependant, comme telles, elles ont besoin d'amélioration en termes de durabilité et de résistance au jaunissement.

B. A. Noordover et al décrit dans J. Biomacromolecules, 2006, 7, 3406-3416 des co- et terpolyesters basés sur l'isosorbide et l'acide succinique et d'autres monomères d'origine renouvelable comme le 2,3 butanediol ou 1 ,3 propanediol ou l'acide citrique.

Aucune présence de polyacides de chaîne plus longue en au moins Cs n'est mentionnée ou suggérée.

La présente invention cherche à mettre au point des nouvelles résines polyesters hydroxylées ou carboxylées, sans huile et exempte de tout résidu d'acide gras insaturé ayant une durabilité et résistance au jaunissement et un compromis dureté/flexibilité améliorées concernant le revêtement obtenu, en particulier pour application sur feuilles de métal.

Le premier objet de la présente invention concerne ladite résine de polyester linéaire ou ramifié qui est hydroxylé et/ou carboxylé à base d'une composition spécifique avec des matières premières renouvelables et en particulier à base d'un polyol biosourcé spécifique.

Est également couverte la solution de ladite résine dans un solvant organique. Un autre objet de l'invention concerne une composition de revêtement comprenant ladite résine et en particulier une composition réticulable de revêtement.

Fait également partie de l'invention l'utilisation de ladite résine dans lesdites compositions de revêtement et finalement le revêtement qui en résulte.

Donc, le premier objet de l'invention concerne une résine polyester de structure linéaire ou ramifiée et exempte d'acides gras insaturés, qui est hydroxylée ou carboxylée, éventuellement hydroxylée et carboxylée, laquelle résine est à base de : un composant acide a) comprenant :

a1 ) au moins un polyacide ou anhydride carboxylique en C 4 à C6, de préférence de fonctionnalité f a i allant de 2 à 4, plus préférentiellement égale à 2 a2) au moins un polyacide ou anhydride carboxylique en Cs à Cs 4 , de préférence de fonctionnalité f a 2 allant de 2 à 4, plus préférentiellement égale à 2 a3) en option, au moins un monoacide saturé en C2 à C22, éventuellement pouvant porter un groupement hydroxyle

un composant alcool b) comprenant :

b1 ) au moins un polyol biosourcé de fonctionnalité fbi d'au moins 2, de préférence

2, porteur d'un motif 1 ,4:3,6 dianhydrohexitol

et au moins un des deux polyols b2) ou b3) suivants :

b2) au moins un polyol différent de b1 ) et de fonctionnalité fb2 d'au moins 2, de préférence 2, plus particulièrement un polyol en C3 à C36

b3) au moins un polyol différent de b1 ) et de b2) de fonctionnalité fb3 d'au moins 3, de préférence 3.

Selon une option particulière, les deux polyols b2) et b3) peuvent être présents.

Le terme « résine exempte d'acides gras insaturés » signifie, selon la présente invention, l'absence de tout acide gras insaturé ou d'huile d'acide gras insaturé sous forme incorporée chimiquement dans la structure de ladite résine ou sous forme libre (non incorporée chimiquement).

Ledit polyacide a1 ) inclut dans sa couverture des acides comme l'acide aconitique issu de la canne à sucre, en C6 et de fonctionnalité f a i = 3. Le polyacide a1 ) peut aussi porter un groupement parmi hydroxyle comme l'acide citrique avec fai = 3 et porteur en plus d'une fonction hydroxyle ou malique avec f a i = 2 et porteur d'un hydroxyle ou l'acide glutamique avec f a i = 2 et porteur d'un groupement aminé.

Plus particulièrement, ledit motif porté par ledit polyol b1 ) est l'isosorbide (1 ,4:3,6 dianhydro-D-sorbitol), l'isomannide (1 ,4:3,6 dianhydro-D-mannitol) ou l'isoidide (1 ,4:3,6 dianhydro-L-iditol).

Selon une préférence particulière, une fraction d'au moins 50 %, de préférence d'au moins 75 % en poids de ladite résine est biosourcée.

Une résine ou un produit biosourcé signifie qu'il comprend une matière première d'origine non fossile qui est renouvelable et d'origine végétale ou animale.

La caractéristique de « biosourcé » d'un produit ou résine ou d'une matière première utilisée comme composant dudit produit, telle qu'un polyacide, un polyol ou un acide gras peut être déterminée par détermination du taux de carbone 14 C, lequel atteste l'origine renouvelable du carbone dudit composant comme tel ou incorporé dans un produit final après réaction (qui ne modifie en rien ce taux). En effet, un composant biosourcé est un composant dans lequel le carbone provient du dioxyde de carbone (CO2) fixé par photosynthèse à partir de l'atmosphère terrestre. La teneur fixe spécifique en carbone 14 C est la signature d'un composant biosourcé qui se différencie de celui correspondant à un composant d'origine fossile. Cette teneur peut être déterminée selon ASTM D 6866 (ASTM D 6866-06) ou ASTM D 7026 (ASTM D 7026-04), en particulier par spectrométrie de masse selon ASTM D6866-06.

Selon un cas particulier, ledit composant b) comprend b2) et b3) et au moins 50 % en poids, de préférence au moins 75 % en poids dudit composant b) est biosourcé.

Plus particulièrement, les composants a) et b) peuvent être à 100 % biosourcés.

Selon une autre option particulière, ledit polyol b2) est biosourcé et choisi parmi le 1 ,3 propylène diol ou le 1 ,2 propylène diol, le 1 ,4 butane diol ou les diols à base (signifiant dérivés) d'acides gras saturés. De tels diols peuvent avoir une chaîne en C12 à C36.

Encore plus particulièrement, ledit polyol b3) peut être biosourcé et choisi parmi le glycérol et ses dérivés éther-polyols, tels que les polyglycérols (dérivés oligomères de glycérol).

Dans le cas où la fonctionnalité d'un des composants cités est supérieure à 2, de préférence la fonctionnalité moyenne en nombre du mélange des composants a) + b) ne dépasse pas 2. Ledit polyester est donc de structure linéaire ou ramifiée et par définition il ne peut comporter de structure réticulée, laquelle est ainsi par définition exclue. L'homme du métier sait en particulier choisir les proportions et les fonctionnalités de composants réactifs ainsi que le taux de conversion des fonctions réactives, afin d'éviter toute réticulation ou gélification chimique du système réactif. Cette question ne peut se poser que quand l'un des composants réactifs (a) et (b) est de fonctionnalité moyenne supérieure à 2 pour obtenir une structure ramifiée. Il est possible de contrôler la structure sans aucune réticulation possible, en ajustant les proportions des composants a) et b) de sorte que la fonctionnalité moyenne en nombre (par mole de composant réactant) sur l'ensemble des composants réactifs (a + b) ne dépasse pas 2 ou si elle dépasse 2 de limiter le taux de conversion bien avant le point de gel (gélification) prédictible soit par l'expérimentation soit par le calcul selon la relation de Macosko-Miller et/ou par addition progressive du composant le moins fonctionnalisé sur le composant le plus fonctionnalisé sous agitation efficace (maintenu en excès de fonctions réactives par l'addition progressive du deuxième composant réactif). La relation de Macosko-Miller citée ci-haut est telle que définie selon Macromolecules, vol. 9, pages 199-21 1 (1976) et est considérée comme bien connue de l'homme du métier. Pour plus de clarté, nous rappelons ci-dessous cette relation qui relie le rapport critique r c des fonctions réactives pour deux composants réactifs A et B au point de gel, r c = fonctions de A/fonctions B, avec la fonctionnalité moyenne de A qui est ÎA, et celle de B qui est ÎB avec le taux critique de conversion au point de gélification x g suivant : r c * x g 2 = 1 / [(f B -1 ) * (f A -1 )]

Ledit polyacide a1 ) peut être en particulier un diacide aliphatique biosourcé choisi parmi : acide succinique, acide tartrique, acide citrique, acide malique ou acide itaconique, acide glutarique, acide glutamique, acide fumarique, acide furanne dicarboxylique, acide tetrahydrofuranne 2,5 dicarboxylique et acide tetrahydrofuranne 3,5 dicarboxylique et de préférence parmi : acide succinique, acide itaconique, acide glutamique, acide fumarique, acide furane dicarboxylique, acide tetrahydrofuranne 2,5 dicarboxylique et acide tetrahydrofuranne 3,5 dicarboxylique.

Ledit polyacide a2) peut être également biosourcé et choisi parmi : l'acide azélaïque (Cg), acide sébacique (C10), acide undécane dioïque, acide dodécane dioïque ou dimères et trimères d'acides gras respectivement en C36 et C54. La présence de ce diacide a2) et sa proportion par rapport à a1 ) sont des facteurs importants pour jouer sur le compromis dureté/flexibilité du revêtement final et ajuster le rapport dureté/flexibilité, l'augmentation du taux de a2) améliore la flexibilité. Inversement, la dureté du revêtement augmente avec le taux de a1 ).

De préférence, le rapport molaire a1 )/a2) varie de 2 à 8 et plus préférentiellement de 3 à 7.

Selon un mode particulier, ledit monoacide a3) est présent dans la composition de ladite résine et sélectionné parmi : l'acide acétique, l'acide pyruvique, l'acide lactique ou la colophane (acide abiétique et isomères en C20) ou un acide gras saturé en C12 à C22.

Selon un mode particulier et préféré de ladite résine, ledit polyol b1 ) représente au moins 30 % en poids de ladite résine, ce poids de « ladite résine » signifiant ici « par rapport au poids total des composants a) + b) utilisés pour ladite résine ».

Plus particulièrement, le taux du polyol b1 ) en % mol/mol sur l'ensemble du composant alcool b) varie de 40 à 80 et de préférence de 55 à 65.

Le taux correspondant au polyol b2) peut varier de 0 à 50 et de préférence de 25 à

35.

Le taux molaire du polyol b3) peut varier de 0 à 20 et de préférence de 5 à 15. Concernant la fonctionnalité OH ou carboxy, éventuellement OH et carboxy de ladite résine, elle peut correspondre à un indice de OH et/ou d'acide allant de 10 à 200 mg KOH/g. Plus particulièrement, ladite résine peut avoir une fonctionnalité carboxy correspondant à un indice d'acide inférieur à 20, de préférence inférieur à 10 et plus préférentiellement inférieur à 5 et en particulier 0 mg KOH/g et une fonctionnalité en OH correspondant à un indice OH allant de 10 à 200, de préférence de 10 à 150, plus préférentiellement de 10 à 100 mg KOH/g. L'indice OH est déterminé selon ISO 2554. L'indice d'acide est déterminé selon ISO 21 14.

La résine selon l'invention peut donc être fonctionnalisée OH ou carboxy ou OH et carboxy, de préférence dans ce dernier cas avec une fonctionnalité OH prédominante, c'est-à-dire à plus de 90 % de groupements fonctionnels étant OH.

Concernant la masse moléculaire moyenne en nombre Mn de ladite résine, elle peut varier de 500 à 20000 et de préférence de 750 à 10000. Cette masse moléculaire Mn est déterminée par calcul à partir de l'indice de fonctionnalité (en mg KOH/g) et de la fonctionnalité moyenne f r de ladite résine qui représente le nombre moyen de fonctions OH et/ou acide carboxy, calculé à partir du bilan matière (proportions molaires) et de la fonctionnalité connue des composants a) et b) utilisés.

La Tg de ladite résine peut varier de -10°C à 100°C et de préférence de 10 à 50°C. Ladite Tg est déterminée par mesure DSC au 2 ème passage à 10°C/min.

Le deuxième objet de l'invention concerne une solution de résine dans un solvant organique, laquelle solution comprend au moins une résine telle que définie ci-haut selon l'invention. Plus particulièrement, ledit solvant peut être sélectionné parmi les esters méthyliques ou esters éthyliques d'acides monocarboxyliques en C2 à C 4 ou esters desdits acides monocarboxyliques avec des monoéthers méthoxy ou éthoxy de diols en C2 à C 4 , en particulier l'acétate de méthoxy propyle ou parmi diesters méthyliques ou éthyliques de diacides carboxyliques en C 4 à C6, terpènes, polyhydroxyalcanoates, esters méthyliques ou éthyliques d'huiles d'acides gras ou esters d'acide lactique avec alcools en Ci à Cs.

La résine de l'invention peut être préparée par réaction entre les composants acide a) et alcool b) comme définis ci-dessus et selon les étapes successives suivantes :

i) réaction de l'ensemble du composant acide a) avec ledit composant b1 ) dudit composant alcool b) jusqu'à une conversion d'au moins 85 %, de préférence 100 % dudit composant b1 ), suivie de

ii) réaction du produit issu de l'étape i) avec le reste dudit composant alcool b), comprenant au moins un des polyols b2) ou b3) comme définis ci-haut,

les réactions desdites étapes i) et ii) ayant lieu en solution dans au moins un solvant organique pouvant former un azéotrope avec l'eau. Le rapport carboxy/OH dans la première étape i) peut varier de 1 ,1 à 2,1 , de préférence de 1 ,2 à 2.

La fonctionnalité de ladite résine est réglée par la nature du composant a) ou b) étant en excès global stœchiométrique.

Un troisième objet de l'invention concerne une composition de revêtement, de préférence une composition de revêtement en milieu solvant organique, laquelle composition comprend au moins une résine telle que définie ci-haut selon l'invention ou (comprend) une solution de résine telle que définie ci-avant. De préférence, ladite composition est une composition réticulable comprenant en plus de ladite résine au moins un agent réticulant, porteur de groupements réactifs avec les groupements hydroxyles et/ou carboxyles portés par ladite résine.

Quand ladite résine est hydroxylée, ledit agent réticulant peut être sélectionné parmi : la mélamine ou un polyisocyanate, en particulier polyisocyanate bloqué ou un polyanhydride ou un polysilane, en particulier polysilane bloqué par alcoxy et quand ladite résine est carboxylée, ledit agent réticulant peut être sélectionné parmi les polyépoxydes ou les polyols.

Comme polyols agents réticulants convenables quand ladite résine est carboxylée, on peut citer tous polyols monomères ou oligomères de structure aliphatique ou cycloaliphatique. Comme exemples de polyols monomères aliphatiques, on peut citer le triméthylol propane ou le glycérol ou le pentaérythritol ou le ditrimethylolpropane ou dipentaérythritol, ces polyols pouvant éventuellement être alcoxylés. D'autres polyols pouvant convenir sont des oligomères polyols acryliques, polyéthers polyols ou polyesters polyols. Des oligomères polyesters polyols convenables comme agents réticulants quand ladite résine est carboxylée sont également les résines polyesters hydroxylées telles que définies selon la présente invention.

Plus particulièrement, ladite composition de revêtement est entièrement biosourcée avec ladite résine et ledit agent réticulant étant tous deux biosourcés, de préférence à 100 % biosourcés.

Dans le cas possible où la résine porte des fonctions à la fois hydroxyles et carboxy, un mélange d'agent réticulants correspondant respectivement à chaque fonctionnalité de ladite résine peut être utilisé et éventuellement avec deux étapes d'addition pour éviter la coréaction éventuelle entre les deux agents réticulants.

De préférence, la fonctionnalité OH ou carboxy est prédominante ou unique et ledit agent réticulant est spécifique pour fonctionnalité OH seulement ou spécifique pour fonctionnalité carboxy seulement. Selon une option particulièrement préférée, ladite composition est une composition de revêtement en milieu solvant organique et en particulier une composition de peinture ou de vernis, plus particulièrement pour surfaces métalliques. Plus préférentiellement, lesdites surfaces métalliques sont sous forme de feuilles métalliques (en anglais « coils »).

Un autre objet de l'invention concerne l'utilisation d'une résine telle que définie ci- haut ou (l'utilisation) d'une solution d'une telle résine dans les compositions de revêtements, en particulier dans les compositions de revêtements réticulables. Une telle utilisation concerne en particulier les compositions de revêtements à comportement « monocomposant » pour métal et en particulier pour revêtement de feuille métallique. Une composition à comportement « monocomposant » se caractérise par le fait qu'elle est stable au stockage et qu'elle n'est réticulable que par activation thermique, caractéristique qui est indispensable dans ce but.

Selon une option particulière, ladite utilisation concerne un revêtement primaire, une finition, un envers de bande ou un revêtement monocouche. Le terme « un envers de bande » signifie ici un revêtement appliqué sur la face « envers » ou « cachée » de la feuille métallique (bande).

Une autre utilisation potentielle de ladite résine concerne les revêtements en poudre, en particulier réticulables. Ladite résine peut être carboxylée et l'agent réticulant peut être un polyépoxyde ou un polyol à base de cyanurate, en particulier le trihydroxyéthyl cyanurate.

Selon une autre option, ladite utilisation concerne des revêtements

« bicomposants ». Lesdites compositions de revêtements bicomposants sont réticulables à basse température et sans besoin d'activation thermique. En fait, dans ce cas, ladite résine en présence dudit agent réticulant réagit aussitôt mélangée audit agent. Par conséquent, une telle composition est préparée juste avant l'utilisation et n'est donc pas stable au stockage, aboutissant après mélange et réaction de ladite résine avec ledit agent réticulant, à une structure réticulée de manière irréversible.

Finalement, l'invention concerne un produit fini, en particulier un revêtement, lequel résulte de l'utilisation d'au moins une résine telle que définie ci-haut ou d'une solution de telle résine ou d'une composition de revêtement telle que définie ci-haut selon la présente invention.

Les exemples suivants sont présentés à titre d'illustration de l'invention et de ses performances et ne limitent en rien sa portée. Partie Expérimentale

1 ) Matières premières utilisées

Tableau 1 : matières premières utilisées

* biosourcé

** mélange d'esters méthyliques d'acide adipique, glutarique et succinique

2) Préparation de la résine (mode opératoire exemple 1 selon l'invention)

Dans un réacteur de 3 litres, chauffé électriquement, équipé :

d'une colonne à distiller du type Vigreux surmontée d'un séparateur Dean Stark, d'une canne plongeante pour introduire l'azote, d'une sonde de température,

on charge :

582 g d'isosorbide,

246,8 g d'acide sébacique,

- 380,9 g d'acide succinique,

0,13 g de Fascat ® 4100 (acide butyl stannoique).

Sous débit d'azote, on chauffe jusqu'à 150°C et on introduit 50,62 g de méthyl isobutyl cétone (MIBK) comme (solvant) entraîneur azéotropique. On chauffe ensuite, jusqu'à 220°C tout en éliminant l'eau de la réaction sous forme d'hétéroazéotrope avec la MIBK jusqu'à atteindre un indice d'acide constant de 165 mg KOH/g correspondant à un taux de conversion de l'isosorbide de 99,5 %. La durée de cette première étape est de 8 h. On refroidit à 180°C et on introduit dans le réacteur 55,7 g de glycérol. Le milieu réactionnel est porté à 220°C toujours sous azote, jusqu'à obtenir un indice d'acide <10 mg KOH/g. Le réacteur est refroidi à 150°C et on ajoute 617,57 g de méthoxy propyl acétate (MPA) en tant que solvant de dilution de la résine. A 90°C, le réacteur est vidangé et l'extrait sec est ajusté par ajout de 68,62 g de MPA.

Les caractéristiques finales du produit sont :

Coloration : 3 Gardner (méthode ISO 4630)

Extrait Sec : 60 % (méthode ISO 3251 )

Viscosité Brookfield à 25°C (méthode ISO 3219) : 4350 mPa.s

Indice d'acide : 8 mg KOH/g (méthode ISO 21 14)

Indice OH (fonctionnalité essentielle) (mg KOH/g) : 70 (méthode ISO 2554)

Isosorbide mesuré par analyse RMN du carbone 13 : 0,1 % dans la résine solvantée, ce qui correspond à un taux de conversion finale de l'isosorbide de 99,7 %.

Exemple 2 comparatif

On reproduit l'exemple 1 mais cette fois sans acide sébacique.

Au cours de cet essai, le polyester final obtenu est insoluble dans le PMA et il faut rajouter du Dibasic ester fourni par Invista qui est un mélange d'esters méthyliques dérivés de l'acide adipique, de l'acide succinique et de l'acide glutarique, de composition respective en poids (en pourcentage massique) :

di méthyl ester de l'acide adipique : 0,1 - 22 %,

di méthyl ester de l'acide succinique : 0,1 - 98 %

diméthyl ester de l'acide glutarique : 0,3 - 99 %

Les caractéristiques finales du produit sont : Coloration : 3 Gardner (méthode ISO 4630)

Extrait Sec : 48 % (méthode ISO 3251 ) pour un ratio MPA/DBE de 67/33

Viscosité Brookfield à 25°C (méthode ISO 3219) : 800 mPa.s

Indice d'acide : 8 mg KOH/g (méthode ISO 21 14)

Indice OH (fonctionnalité essentielle) (mg KOH/g) : 70

Isosorbide mesuré par analyse RMN du carbone 13 : 0,09 % dans la résine solvantée, ce qui correspond à un taux de conversion finale de l'isosorbide de 99,5 %.

3) Application des résines dans des peintures satinées pour feuille métallique

3.1 ) Formulation de peintures satinées

Tableau 2 : Compositions et matières premières utilisées

Composant Parties Réf Fonction Nom Chimique Fournisseur en poids composant

sur 1000

Résine exemple 209 (1 ) Liant Résine

1 hydroxylée selon

(partie 1 ) l'invention

PMA 25,5 (2) Solvant Méthoxy propyl BASF (partie 1 ) acétate

Disperbyk ® -161 5,5 (3) Dispersant Copolymère bloc BYK

TÎ02-KRONOS 243 (4) Pigment Oxyde de Titane KRONOS 2360

Silice Aerosil ® 2,5 (5) Additif Silice EVONIK R972 rhéologique

Résine exemple 220 (1 ) Liant Résine

1 (partie 2) hydroxylée selon

invention

PMA (partie 2) 31 (2) Solvant Méthoxy propyl BASF acétate

Silice SYLOID ® 30 (6) Agent Silice Grâce ED 40 matant

CYMEL ® 303 LF 46 (7) Agent Mélamine Allnex réticulant méthylée Catalyst PTSA 7,5 (8) catalyseur Acide p-toluène Aldrich sulfonique (12,5 %

dans butanol)

PMA (partie 3) 154 (2) solvant Méthoxy propyl BASF acétate

Solvarex ® 9 24 (9) solvant Hydrocarbure Total aromatique

Crayvallac ® 2 (10) Agent Polyester Arkema Flow 200 d'étalement

Total 1000

3.2) Mode opératoire de préparation des peintures satinées

Dans un bêcher de 1 litre thermostaté à température ambiante, on introduit dans l'ordre indiqué les composés suivants (1 ) (partie 1 ), (2) (partie 1 ), (3), (4) et (5). Ce mélange est mis sous agitation à l'aide d'un agitateur type Dispermat, puis dispersé pendant 30 minutes à 3500 tours/min. On ajoute ensuite le reste (partie 2) du liant (1 ), le reste (partie 2) du solvant (2) et le composé (6). La dispersion est poursuivie pendant 15 minutes à 2500 tours/min. Toujours sous agitation à 1000 tours/min, on ajoute les composés (7) et (8). La viscosité de la peinture est ajustée grâce à l'ajout de (2) (partie 3) et (9). Enfin, on ajoute toujours sous agitation à 1000 tours/min le composé (10).

Les caractéristiques de la peinture satinée obtenue sont présentées au tableau 3 ci- dessous.

Tableau 3 : caractéristiques de la peinture satinée

Exemple 1 selon Exemple 2

Caractéristique Méthode de mesure

l'invention comparatif

Densité (g/cm 3 ) NF EN ISO 281 1 -1 1 ,27 1 ,32

Solide en poids (%)

ISO 3251 58,3 57,5 ES

Solide en volume

ratio volume sec / volume total 44,2 44,7 (%)

calcul grammes solvant par

COV (g/l) * 530 558

litre de peinture calcul ratio volume pigments /

volume pigments + volume

CPV (%) ** 22,8 22,7

liant (calculé sur matière

sèche)

Viscosité Cône plan

ISO 2884-1 520 520 à 25°C (m. Pas)

*COV : Composés Organiques Volatiles

**CPV : Concentration Pigmentaire Volumique

3.3) Feuille métallique utilisée, conditions d'application de la peinture satinée et conditionnement avant tests d'évaluation

La tôle utilisée pour les essais est une tôle en acier galvanisée de 0,5 millimètre d'épaisseur prétraitée avec une solution de chromate.

La peinture est appliquée à l'aide d'un applicateur type Bar Coater. Deux types d'application sont réalisés :

- revêtement de finition (« top coat »)

revêtement direct sur la tôle métallique (« direct to métal »)

L'épaisseur du revêtement de finition et du revêtement direct sur la tôle métallique est de 20 μηι.

Dans le cas du revêtement de finition (« top coat »), la peinture est appliquée sur une tôle métallique enduite déjà d'un revêtement primaire compatible de 5 μηη d'épaisseur. L'épaisseur totale du revêtement est de 25 μηη en incluant le revêtement primaire (top coat de 20 μηι).

La tôle ainsi revêtue est introduite dans un four à 385°C. La réticulation avec la mélamine s'effectue à un pic de température sur le métal (appelé PMT) de 232°C pendant 35 secondes.

La peinture, en tant que revêtement direct sur le métal et appliquée sur un primaire en tant que revêtement dé finition, est ensuite évaluée suivant divers tests de performances, après conditionnement des panneaux d'essais (tôle peinte) dans une salle climatisée à 23°C ± 2 avec l'humidité contrôlée à 50 % ± 5 %. ) Tests d'évaluation des performances des peintures

Tableau 4 : Tests utilisés

) Résultats et conclusion

.1 ) Revêtement direct sur le métal (application DTM)

Tableau 5 : résultats obtenus en revêtement direct sur métal

Exemple 1 Exemple 2 selon l'invention comparatif

Test d'emboutissage (mm) 4,5 2,8

Test d'adhérence 0 entre 0 et 1

Test de pliage 5 T > 6 T

Dureté PERSOZ (s) 207 233 Revêtement de finition sur primaire (« top coat »)

Tableau 6 : résultats obtenus en revêtement de finition

Le polyester polyol à base de matières premières d'origine biosourcée, objet de l'invention, permet de préparer des revêtements pour feuille de métal présentant des propriétés applicatives intéressantes avec notamment un bon compromis entre dureté et test de pliage.

L'exemple 1 , selon l'invention, réalisé avec acide sébacique conduit à une peinture beaucoup plus flexible (résultat du test de pliage) avec un niveau de dureté très satisfaisant pour l'application visée.