Title:
BIODEGRADABLE HYDROPHOBIC COMPOSITE MATERIALS AND PROCESS FOR THE PREPARATION THEREOF
Document Type and Number:
WIPO Patent Application WO/2014/057502
Kind Code:
A1
Abstract:
The present invention relates to biodegradable hydrophobic composite materials and a process for the preparation of said hydrophobic biodegradable materials from the seaweed polysaccharides through grafting reaction with vinylated monomers e.g. vinyl acetate. The said composites can be used as a substitute for synthetic ropes for varied applications including seaweed cultivation in the open sea. The results of cultivation experiments showed that ropes are suitable for cultivation of seaweeds in the sea environment, and exhibit higher biomass yield as compared to synthetic ropes. The prepared composites are very flexible and can be used for making handles for carry bags and for the preparation of biodegradable designs, bowls, pots, jars, gift items, stud caps and bracelets.

Inventors:
MEENA RAMAVATAR (IN)
GHOSH PUSHPITO KUMAR (IN)
CHEJARA DHARMESH (IN)
ESWARAN KARUPPANAN (IN)
SIDDHANTA ARUP KUMAR (IN)
PRASAD KAMALESH (IN)
CHAUDHARY JAI PRAKASH (IN)
Application Number:
PCT/IN2013/000617
Publication Date:
April 17, 2014
Filing Date:
October 11, 2013
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
COUNCIL SCIENT IND RES (IN)
International Classes:
C08B37/00; C08F251/00
Domestic Patent References:
WO2006059180A22006-06-08
WO2006059180A22006-06-08
Foreign References:
US6294202B12001-09-25
US20040171545A12004-09-02
US20050161857A12005-07-28
US20030118692A12003-06-26
JP2000093080A2000-04-04
Other References:
MISHRA ET AL: "Synthesis of graft copolymer (k-carrageenan-g-N,N-dimethylacrylamide) and studies of metal ion uptake, swelling capacity and flocculation properties", CARBOHYDRATE POLYMERS, APPLIED SCIENCE PUBLISHERS, LTD. BARKING, GB, vol. 71, no. 4, 14 December 2007 (2007-12-14), pages 524 - 534, XP022390890, ISSN: 0144-8617, DOI: 10.1016/J.CARBPOL.2007.06.021
THOMAS KARBOWIAK ET AL: "Effect of Plasticizers (Water and Glycerol) on the Diffusion of a Small Molecule in Iota-Carrageenan Biopolymer Films for Edible Coating Application", BIOMACROMOLECULES, vol. 7, no. 6, 1 June 2006 (2006-06-01), pages 2011 - 2019, XP055104116, ISSN: 1525-7797, DOI: 10.1021/bm060179r
Y MATVEEV ET AL: "The plasticizing effect of water on proteins, polysaccharides and their mixtures. Glassy state of biopolymers, food and seeds", FOOD HYDROCOLLOIDS, vol. 14, no. 5, 1 September 2000 (2000-09-01), pages 425 - 437, XP055104113, ISSN: 0268-005X, DOI: 10.1016/S0268-005X(00)00020-5
TRIVEDI J H ET AL: "Ceric-induced grafting of acrylonitrile onto sodium salt of partially carboxymethylated guar gum", CARBOHYDRATE POLYMERS, APPLIED SCIENCE PUBLISHERS, LTD. BARKING, GB, vol. 60, no. 1, 7 April 2005 (2005-04-07), pages 117 - 125, XP027721537, ISSN: 0144-8617, [retrieved on 20050407]
ATHAWALE V D ET AL: "Free radical graft copolymerization of methacrylamide onto agar", EUROPEAN POLYMER JOURNAL, PERGAMON PRESS LTD. OXFORD, GB, vol. 35, no. 7, 1 July 1999 (1999-07-01), pages 1237 - 1243, XP004172363, ISSN: 0014-3057, DOI: 10.1016/S0014-3057(98)00200-6
XIAOGUANG YING ET AL: "Stimuli-responsive recognition of BSA-imprinted poly vinyl acetate grafted calcium alginate core-shell hydrogel microspheres", JOURNAL OF APPLIED POLYMER SCIENCE, vol. 127, no. 5, 23 May 2012 (2012-05-23), pages 3898 - 3909, XP055103901, ISSN: 0021-8995, DOI: 10.1002/app.37730
GHOSH ET AL., POLYMER INTERNATIONAL, vol. 53, 2004, pages 339 - 343
POLYMER INTERNATIONAL., vol. 50, 2001, pages 1103 - 1108
Attorney, Agent or Firm:
DHAWAN, Ramesh, Chander (Plot No. B-28 Sector 32,Institutional Area, Gurgaon 1, Haryana, IN)
Download PDF:
Claims:
We Claim:

1. Hydrophobic biodegradable composites comprising:

[a] seaweed derived polysaccharides in the range of 30 to 80 wt%; [b] vinylated monomer in the range of 8 to 60 wt %; and

[c] plasticizer in the range of 2 to 15 wt%; wherein, the moisture content of said composites is in the range of 5 to 15 wt%.

2. The composites as claimed in claim 1, wherein the seaweed derived polysaccharides are selected from the group consisting of agar, agarose, alginate, and carrageenan.

3. The composites as claimed in claim 1, wherein the seaweed derived polysaccharides are either used alone or in combination.

4. The composites as claimed in claim 1 , wherein the seaweed derived polysaccharide is agar and/or agarose.

5. The composites as claimed in claim 1, wherein the vinylated monomer is vinyl acetate.

6. The composites as claimed in claim 1, wherein the plasticizer is selected from the group consisting of glycerol, ethylene glycol, and sorbitol. 7. The composites as claimed in claim 1, wherein the plasticizer is glycerol.

8. A process for the preparation of the composites as claimed in claim 1, the process comprising:

[a] dissolving 1 to 8 wt % of seaweed polysaccharides or their blends in distilled water by heating at a temperature in the range of 100 to 120 degree Celsius for 5 to 30 minutes to obtain a homogenous solution; [b] adding 0.01 to 0.10 wt% potassium persulphate to the homogeneous solution as obtained in step [a] under stirring followed by addition of 2 to 16 wt% vinylated monomers and heating at a temperature in the range of 60 to 85 degree Celsius in aqueous medium under reflux conditions for 3 to 7 hours under constant stirring to obtain a reaction mixture;

[c] adding 0.5 to 5.0 wt% plasticizers into the reaction mixture as obtained in step [b] and transferring the contents into desired hollow or tubular devices/moulds to obtain moulded composites;

[d] treating the moulded composites as obtained in step [c] with organic solvent at a temperature in the range of 20 to 30 degree Celsius to remove unreacted homopolymer followed by air drying to obtain desired hydrophobic biodegradable composites.

9. The process as claimed in claim 8, wherein the hollow or tubular devices/moulds are made of glass, plastic, steel, or wood.

10. The process as claimed in claim 8, wherein the organic solvent is selected from the group consisting of isopropyl alcohol, acetone, methanol, ethanol, ethyl acetate, and tetra hydro furan.

Description:
BIODEGRADABLE HYDROPHOBIC COMPOSITE MATERIALS AND PROCESS FOR THE PREPARATION THEREOF

FIELD OF THE INVENTION

The present invention relates to biodegradable hydrophobic composite materials and process for the preparation thereof In particular, the present invention relates to a process for the preparation of controlled/completely hydrophobic biodegradable composites that can be used for varied applications including seaweed cultivation in the open sea. The prepared composites can be sterilised in water without solubilisation, are flexible and can be used for numerous applications including carry bag handles, bowls, pots, gift items, studs, accessories for ornaments, etc. along with the advantage that they can be safely and easily disposed off in the environment.

BACKGROUND OF THE INVENTION

Conventionally, ropes are made out of coconut fibre and other natural materials. Such ropes are widely used in seaweed cultivation, but in general, the durability of the ropes is low in seawater. Ropes are also available- which are made up of synthetic/semi- synthetic fibres such as nylon, polyester, etc. Such ropes are routinely used in seaweed cultivation but their low/poor biodegradability is a great concern.

Reference may be made to the publication of Ghosh et al. (Polymer International, 53, 339-343; 2004) wherein it has been stated that grafting of vinyl acetate onto the low density polyethylene (LDPE)-starch blend films makes them suitable for printing and packaging applications. They used commercially available blend films made of synthetic polymer and starch under inert atmosphere using hazardous chemicals (e.g. HN0 3 ) during process, and used for printing and packaging applications. It is pertinent to mention here that the said reference does not mention the use of seaweed phycocolloids for making biodegradable hydrophobic composites for aqueous applications including seaweed cultivation. Reference may be made to US6294202B1, wherein disclosed is a process for making water-insoluble biodegradable composition containing polyanionic polysaccharides and hydrophobic bioabsorbable polymers to prepare film, foam, mesh matte, or to cast on top of any surface. It is pertinent to mention here that the said reference reports the formation of compositions containing polyanionic polysaccharides and hydrophobic bioabsorbable polymers or copolymers. However, there is no report on the formation of biodegradable hydrophobic composites based on seaweed polysaccharides for novel applications including seaweed cultivation in sea water.

Reference may be made to US20040171545A1 , wherein synthetic protein copolymers with plastic and elastic properties, and methods producing the copolymers, are disclosed. The process producing synthetic protein copolymer comprising at least one hydrophilic block and at least one hydrophobic block. It is pertinent to mention here that the said reference reports the formation of synthetic protein copolymers with plastic and elastic properties and does not describe any composition or process for the preparation of biodegradable hydrophobic composites based on seaweed phycocolloids for potential applications including seaweed cultivation.

Reference may be made to US20050161857A1 , wherein recited is a method of producing a polymeric fibre (poly caprolactone) comprising: dissolving at least one fibre forming polymer in a solvent so as to form a polymer solution, and feeding the polymer solution under gravity through an orifice directly into a non-solvent to cause formation of a polymeric fibre in the non-solvent. It is. pertinent to mention here that the said reference reports the formation of polymeric fibres from the synthetic polymer (e.g. poly-caprolactone) and does not describe any composition or process for the preparation of biodegradable hydrophobic composites based on seaweed phycocolloids. Reference may be made to US20030118692A1, wherein reported is a method for the preparation of biodegradable elastomeric material from glycerol and diacid like malonic acid, succinic acid, adipic acid, glutaric acid, pimelic acid etc. to prepare different shapes of particles, tubes, spheare, strand, coiled strands capillary network, film, fibers, mesh and sheet. It is pertinent to mention here that the said reference reports the formation of biodegradable elastomeric materials using glycerol and diacids and does not describe any composition or process for the preparation of biodegradable hydrophobic composites based on seaweed phycocolloids for novel applications including seaweed cultivations in sea water.

Reference may be made to JP20OO-O9308O, wherein disclosed is the use of polysaccharides like polyvinyl alcohol, polyvinyl pyrrolidone, sodium alginate, etc. in preparation of antibacterial and antifungal agent composition, which is soluble when used. It is pertinent to mention here that the said reference reports the formation of soluble materials and does not describe any composition or process for the preparation of biodegradable hydrophobic composites which are insoluble in water.

Reference may be made to Polymer International. 2001 50: 1 103- 1 108, wherein use of poly(vinyl alcohol) and κ-carrageenan in preparation of films based on polyvinyl alcohol)/ -carrageenan blends and their gelling properties is reported. However, there is no report on the formation of hydrophobic materials including ropes and other materials in this article.

Reference may be made to WO 2006059180 A3, wherein use of inexpensive semi- refined kappa carrageenan as a seaweed polysaccharide in preparation of tough, biodegradable films with improved performance over films obtained from refined kappa carrageenan is disclosed. However, these films are highly moisture sensitive and readily soluble in water and thus cannot be applied in activities such as seaweed cultivation in open sea water environment.

In short, it may be summarized that the hitherto reported prior art shows that the polymeric composites prepared from purely petrochemical substances or entirely natural substance have some inherent drawbacks. Totally synthetic polymeric materials have problems of degradation, while natural polymeric materials are highly moisture sensitive and not suitable for aqueous applications owing to their solubility. For instance, seaweed derived phycocolloids such as agar, carrageenans, agarose, alginate are excellent gel formers and used as thickeners, but are highly moisture sensitive. Further, due to their high solubility in water and hydrophilic nature, these can be used only for the formation of films and are not good for aqueous applications because the hitherto reported composites made from them readily solubilise in water. In order to be eco-friendly as well as suitable for applications in water the composites must be hydrophobic.

Therefore, the inventors of the present invention realized that there exists a dire need to solve the issues discussed above and provide a composite through copolymerisation technique, to obtain controlled/completely hydrophobic biodegradable materials. It is evident from the prior art that there are no examples wherein polymers derived from seaweeds are utilised for preparation of hydrophobic composite materials which can be used for varied aqueous applications including seaweed cultivation in the sea water conditions.

OBJECTIVE OF THE INVENTION The main object of the present invention is to provide composite materials which are biodegradable as well as water resistant i.e. exhibit hydrophobicity.

Another object of the present invention is to provide a process for the preparation of such hydrophobic biodegradable composites.

Still another object of the invention is to provide said hydrophobic composites using hydrophilic natural polymers and synthetic organic monomers.

Yet another object of the invention is to prepare ropes from the developed composites in a manner such that they are suitable for seaweed cultivation, are durable during use and at the same time, can be made to biodegrade in the soil/sea bottom.

Still another object of the invention is to provide a process for the preparation of the said composites wherein hydrophobicity is imparted by introducing vinylated monomers through chemical interventions. SUMMARY OF THE INVENTION

The present invention relates to biodegradable hydrophobic composite materials and process for the preparation thereof. The invention further relates to the preparation of hydrophobic biodegradable composites from natural polymers such as the seaweed polysaccharides through grafting reaction with vinylated monomers e.g. vinyl acetate. The developed composites can be moulded in the form of ropes, which can be used as a substitute of synthetic ropes for varied applications including seaweed cultivation in the open sea. The results of cultivation experiments showed that the prepared ropes are suitable for cultivation of seaweeds in the sea environment, and yield higher biomass as compared to the braiders or nylon ropes. These ropes are very flexible and can also be used for making handles for carry bags, small ladies bags, and small school children bags. In addition, they can also be used for the preparation of designs on bowls, pots, jars and gift items like rings and bracelets.

In an embodiment, the present invention provides a process which uses agar, agarose, alginate and carrageenan alone as the seaweed polymers or uses combination of agar, agarose, alginate and carrageenan as the seaweed polymers.

In another embodiment, the present invention provides a process which makes the hydrophilic polymers hydrophobic so as to tolerate seawater conditions.

In still another embodiment, the present invention provides a process which imparts such hydrophobicity through grafting of vinylated monomers.

In yet another embodiment, the present invention provides a process which imparts complete hydrophobicity through grafting of vinyl acetate and other such monomers.

In still another embodiment, the present invention provides a process which tests the durability and efficacy of these composites in seawater and dry conditions. In yet another embodiment, the present invention provides a process which demonstrates the biodegradability of the composites in soil. In a further embodiment of the present invention, the ropes are prepared from seaweed polymer in a manner such that they are suitable for the preparation of biodegradable handles for carry bags.

In another embodiment of the present invention, the ropes are prepared from seaweed polymer in a manner such that they are suitable for the preparation of biodegradable bowls, pots or jars for storage of food and non-food items.

In still another embodiment of the present invention, the ropes are prepared from seaweed polymer in a manner such that they are suitable for the preparation of biodegradable flower pots or jars for decoration. In yet another embodiment of the present invention, the ropes are prepared from seaweed polymer in a manner such that they are suitable for the preparation of designs on traditional items such as belts, bags and other small modern and fashionable items.

In still another embodiment of the present invention, the ropes are prepared from seaweed polymer in a manner such that they are suitable for the preparation of colored biodegradable ropes.

In yet another embodiment of the present invention, the biodegradable ropes with controlled /complete hydrophobicity may be obtained from agar, agarose, carrageenans and alginate as well as their hybrid blends and more particularly agar and agarose.

In still another embodiment of the present invention, the microwave/conventional/autoclave heating is carried out at a temperature in the range of 100 to 120 degree Celsius for a period of 10 to 30 minutes to dissolve the seaweed polysaccharides or their blends and more particularly 15 minutes to obtain a homogeneous solution.

In yet another embodiment of the present invention, the autoclave treatment is done at a temperature in the range of 100 to 120 degree Celsius to dissolve the seaweed polysaccharides or their blends for 10 to 30 minutes and more particularly 25 minutes to obtain a homogeneous solution. In still another embodiment of the present invention, the water soluble initiator potassium persulphate (KPS) is added to the polymer mixture in the range of 0.01% to 0.04 wt% for the formation of active sites for grafting and more particularly 0.02 wt%.

In yet another embodiment of the present invention, the water soluble initiator potassium persulphate (KPS) is added to the polymer mixture at a temperature in the range of 60 to 90 degree Celsius under stirring.

In still another embodiment of the present invention, the vinylated monomer is added in the polymer and initiator KPS mixture in the range of 2 to 16 wt% and more particularly 6 wt%. In yet another embodiment of the present invention, the vinylated monomer is added in the polymer and initiator KPS mixture in the temperature range of 60 to 85 degree Celsius under stirring for grafting with polymers present in the reaction mixture, more particularly at 80 degree Celsius.

In still another embodiment of the present invention, the biodegradable composites with complete/controlled hydrophobicity is obtained by grafting of agar, agarose, carrageenan and alginate as well as their hybrids with vinylated monomers, preferably vinyl acetate.

In yet another embodiment of the present invention, the biodegradable composites with complete hydrophobicity is obtained by grafting of agar or agarose as well as their hybrids with vinyl acetate.

In still another embodiment of the present invention, the additive glycerol is added in the temperature range of 60 to 90 degree Celsius under stirring to inhibit the brittleness of the resulting ropes.

In yet another embodiment of the present invention, the resulting molded composites are treated with organic solvents to remove the excess amount of unreacted monomer as well as water under ambient conditions. In still another embodiment of the present invention, the organic solvent used is selected from the group consisting of acetone, methanol, ethanol, iso-propyl alcohol, ethyl acetate and tetra hydro furan (THF).

In yet another embodiment of the present invention, the solvent treated composites are dried in air followed by an optional oven drying at 50 degree Celsius for 2 hours.

In still another embodiment of the present invention, the seaweed polysaccharides are chemically hydrophobised to have the controlled/complete hydrophobicity.

In yet another embodiment of the present invention, the biodegradable composites prepared from agar or agarose or carrageenans or their blends are suitable for seaweed cultivation in open sea water environment.

In still another embodiment of the present invention, the quality of biodegradable composites is same after recovering from the sea water environment after 45 days or after first harvest of the seaweed.

In yet another embodiment of the present invention, the biodegradable composites prepared from seaweed polysaccharides or their blends are suitable for the preparation of biodegradable carry bags handles, bowl, pots, designs, ornaments accessories, etc.

In still another embodiment of the present invention, the quality of biodegradable composites in the form of handles, bowl, pots, designs, ornaments accessories, etc. is same after storing in ambient conditions or using longer time up to more than one year. In yet another embodiment of the present invention, the biodegradable composites are easy to dispose off in the open environment.

BRIEF DESCRIPTION OF ACCOMPANYING DRAWINGS

Figure 1 illustrates the biodegradable hydrophobic or controlled hydrophobic composites based colored ropes or rods, suitable for making decorative items, coloured handles for carry bags, ornaments accessories, etc. Figure 2 illustrates (a) cultivation of Kappaphycus alvarezii on the biodegradable hydrophobic ropes by the raft method, (b) cultivated plant in biodegradable hydrophobic composites based ropes of Examples 15 and 16, and (c) cultivated plant in synthetic ropes. The plant growth was higher in biodegradable ropes compared to synthetic ropes.

Figure 3 illustrates (a) flexibility property of biodegradable ropes, (b) empty carry bag with handle of ropes of Examples 14-20, and (c) 5 kg weight in carry bag with handles of ropes of Examples 14-20.

Figure 4 illustrates leather belt with beautiful designs made of biodegradable composites ropes of Examples 14-31.

Figure 5 illustrates stud caps made of biodegradable composites ropes of Examples 14-3 1.

Figure 6 illustrates bowl/basket made of biodegradable composites rope of Examples 14-31. Figure 7 illustrates storage of vegetables in bowl/basket made of biodegradable composites ropes of Example 38.

Figure 8 illustrates storage of bakery items in bowl/basket made of biodegradable composites ropes of Example 38.

Figure 9 illustrates decorative pot/jar made of biodegradable composites ropes of Examples 14-31.

Figure 10 illustrates flowers in decorative pot/jar made of biodegradable composites ropes of Example 41.

Figure 11 illustrates hand belts/bracelet made of biodegradable composites ropes of Examples 14-31.

Figure 12 illustrates the drying of cloths on biodegradable composites ropes of Examples 15 and 16. DETAILED DESCRIPTION OF THE INVENTION

The seaweed derived phycocolloids used for the purposes of the present invention are selected from agar bacteriological (product code: 0140132), agarose (product code: 01401 1) and alginate (product code: 1947295) which were commercially procured from M/s Sisco Research Laboratories (SRL) Pvt. Ltd. Mumbai - 400 093, Maharashtra, India, and semi refined carrageenan (product code: Aqua gel 250) which was commercially procured from M/s Aquagri Processing Pvt. Ltd., New Delhi, India.

The present invention relates to biodegradable composite materials of controlled hydrophobicity exhibiting high mechanical strength and good flexibility. The invention also describes a facile, eco-friendly and one-step process for the preparation of the said materials from the seaweed polysaccharides and their blends through chemical reaction with vinylated monomers like vinyl acetate, acrylamide and acetonitrile. According to a non-limiting exemplary embodiment, the said process comprises: dissolving 1 to 10 wt% of seaweed polysaccharides namely agar, carrageenans, alginate, agarose or their blends in distilled water by microwave heating at 100 degree Celsius for 5 to 15 minutes or by autoclaving at 120 degree Celsius for 30 minutes to obtain a homogenous solution, adding 0.01 to 0.10 wt% of potassium persulphate ( PS) under stirring to said solution followed by addition of 2 to 16 wt% vinylated monomers, heating the reaction mixture in aqueous medium under reflux conditions at 60 to 85 degree Celsius for 3 to 7 hours with constant stirring, adding 0.5 to 2.0 wt% of plasticizers selected from glycerol, sorbitol, ethylene glycol or other polyols into the reaction mixture and transferring the contents to the desired hollow or tubular devices/moulds made of glass or metal to obtain the desired moulded composites in various shapes, treating the resulting moulded composites with organic solvent at a temperature in the range of 20 to 30 degree Celsius so as to remove the unreacted homopolymer followed by air drying under ambient conditions to yield the desired biodegradable hydrophobic composites suitable for multifarious applications including seaweed cultivation in the open seawater environment. EXAMPLES

The following examples are given by way of illustration and therefore should not be construed to limit the scope of the present invention.

EXAMPLE 1 Seaweed phycocolloid (SP) agarose (2 wt%) was dissolved in water by microwave

(MW) heating at 100 degree Celsius for 15 minutes. To this, 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 4 wt% acrylamide

(AAm). The reaction mixture was heated in aqueous medium under reflux conditions at

80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PAAm-composite (la). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 1: Effect of different reaction parameters and other variables in Example 1.

Seaweed AAm KPS Plasticizer Remarks/Observations

phycocolloi (wt%) (wt%)

(wt%)

d (wt%)

Agar 4 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PAAm-composite (lb). It was observed (2) that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi- 4 0.02 0.5 This produced water sensitive biodegradable composites refmed named as SRC/PAAm-composite (Ic). It was observed carrageenan that the prepared composites were not hydrophobic and

(SRC) thus not suitable to be used for applications such as seaweed cultivation.

(2) Alginate 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PAAm-composite (Id). It (2) was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 2

Experiments of Example 1 were repeated taking seaweed phycocolloid agarose (4 wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30 minutes. To this, 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 8 wt% acrylamide (AAm). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PAAm- composites (Ha). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 2: Effect of different reaction parameters and other variables in Example 2.

Seaweed AAm KPS Plasticiz Remarks/Observations

phycocoll (wt%) er

(wt%)

oid (wt%) (wt%)

Agar 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PAAm-composite (lib). It was observed that (4) the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi- 0.02 This produced water sensitive biodegradable composites refined named as SRC/PAAm-composite (lie). It was observed that carrageen the prepared composites were not hydrophobic and thus not an (SRC) suitable to be used for applications such as seaweed cultivation.

(4) W

Alginate 8 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate PAAm-composite (lid). It (4)

was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 3

Experiments of Example 1, were repeated taking seaweed phycocolloid agarose (6 wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30 minutes. To this 0.02 wt% potassium persulphate ( PS) was added under stirring, followed by addition of 16 wt% acrylamide (AAm). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PAAm- composites (Ilia). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 3: Effect of different reaction parameters and other variables in Example 3.

Seaweed AAm KPS Plasticiz Remarks/Observations

phycocoll er

(wt%) (wt%)

oid (wt%) (wt%)

Agar 16 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PAAm-composite (Illb). It was observed that

(6)

the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation. Serrti- 16 0.02 0.5 This produced water sensitive biodegradable composites refined named as SRC/PAAm-composite (IIIc). It was observed that carrageen the prepared composites were not hydrophobic and thus not an (SRC) suitable to be used for applications such as seaweed cultivation.

(6)

Alginate 16 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PAAm-composite (Hid). It was

(6)

observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 4

Experiments of Example 1, were repeated taking seaweed phycocolloid agarose (2 wt%) which was dissolved in water by microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by the addition of 4 wt% acrylonitrile (ACN). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PACN- composites (IVa). It was observed that the prepared composite was not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 4: Effect of different reaction parameters and other variables in Example 4.

Seaweed ACN KPS Plasticizer Remarks/Observations

phycocolloi , 0 „ (wt%) . (wt%)

d (wt%) Agar 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PACN-composite (IVb). (2)

It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi- 0.02 0.5 This produced water sensitive biodegradable refined composites named as SRC PACN-composite (IVc). carrageenan It was observed that the prepared composites were (SRC) not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

(2)

Alginate 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PACN-composite (2)

(IV d). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 5

Experiments of Example 2, were repeated taking seaweed phycocolloid agarose (4 wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30 minutes. To this 0.02 wt% potassium persulphate ( PS) was added under stirring, followed by addition of 8 wt% acrylonitrile (ACN). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PACN- composites (Va). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation. Table 5: Effect of different reaction parameters and other variables in Example 5.

Seaweed ACN KPS Plasticizer Remarks/Observations

phycocolloid ( wt o /0 ) (wt%) (wt%)

(wt%)

Agar 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PACN-composite (Vb). It was observed that (4)

the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 0.02 0.5 This produced water sensitive biodegradable composites carrageenan named as SRC/PACN-composite (Vc). It was observed that

(SRC) the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed

(4)

cultivation.

Alginate 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PACN-composite (Vd). It (4)

was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 6

Experiments of Example 3, were repeated taking seaweed phycocolloid agarose (6

wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30

minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring,

followed by addition of 16 wt% acrylonitrile (ACN). The reaction mixture was heated

in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant

stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then

transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PACN- composites (Via). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 6: Effect of different reaction parameters and other variables in Example 6.

Seaweed ACN PS Plasticiz Remarks/Observations

phycocol (wt%) er

(wt%)

loid (wt%)

(wt%)

Agar 16 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PACN-composite (VIb). It was observed that

(6)

the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi- 16 0.02 0.5 This produced water sensitive biodegradable composites refined named as SRC/PACN-composite (Vic). It was observed that carrageen the prepared composites were not hydrophobic and thus not an (SRC) suitable to be used for applications such as seaweed cultivation.

(6)

Alginate 16 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PACN-composite (VId). It was (6)

observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 7

Experiments of Example 1, were repeated taking seaweed phycocolloid agarose (2

wt%) which was dissolved in water by microwave heating at 100 degree Celsius for 15

minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring,

followed by the addition of 2 wt% polyvinyl alcohol (PVA). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes.

The resulting moulded composites were treated with organic solvent at a temperature of

25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PVA-composites

(Vila). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 7: Effect of different reaction parameters and other variables in Example 7.

Seaweed PVA KPS Plasticizer Remarks/Observations

phycocolloid , 0/ . (wt%) (wt%)

(wt%)

Agar 2 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PVA-composite (Vllb). It

(2)

was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 2 0.02 This produced water sensitive biodegradable carrageenan composites named as SRC/PVA-composite (VIIc). It

(SRC) was observed that the prepared composites were not hydrophobic and thus not suitable to be used for

(2)

applications such as seaweed cultivation.

Alginate 2 0.02 This produced highly water sensitive biodegradable composites named as Alginate/PVA-composite

(2)

(Vlld). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 8

Experiments of Example 2, were repeated taking seaweed phycocolloid agarose (4 wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30 minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 8 wt% PVA. The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the

desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting

moulded composites were treated with organic solvent at a temperature of 25 degree

Celsius to remove the unreacted homopolymer followed by air drying. This produced

water sensitive biodegradable composites named as Agarose/PVA-composites (Villa).

It was observed that the prepared composites were not hydrophobic and thus not

suitable to be used for applications such as seaweed cultivation.

Table 8: Effect of different reaction parameters and other variables in Example 8.

Seaweed PVA PS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PVA-composite (VHIb). It was observed (4)

that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 0.02 0.5 This produced water sensitive biodegradable composites carrageenan named as SRC/PVA-composite (VIIIc). It was observed that

(SRC) the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed

(4)

cultivation.

Alginate 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PVA-composite (Vllld). It (4)

was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 9

Experiments of Example 3, were repeated taking seaweed phycocolloid agarose (6

wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30

minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring,

followed by addition of 16 wt% PVA. The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the heated reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree

Celsius to remove the unreacted homopolymer followed by air drying. This produced water sensitive biodegradable composites named as Agarose/PVA-composites (IXa). It was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Table 9: Effect of different reaction parameters and other variables in Example 9.

Seaweed PVA PS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%) (wt%)

(wt%)

Agar 16 0.02 0.5 This produced water sensitive biodegradable composites named as Agar/PVA-composite (IXb). It was observed (6)

that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 16 0.02 0.5 This produced water sensitive biodegradable composites carrageenan named as SRC/PVA-composite (IXc). It was observed

(SRC) that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as

(6)

seaweed cultivation.

Alginate 16 0.02 0.5 This produced highly water sensitive biodegradable composites named as Alginate/PVA-composite (IXd). It (6)

was observed that the prepared composites were not hydrophobic and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 10

Experiments of Example 1 , were repeated taking seaweed phycocolloids agarose (2 wt%) which was dissolved in water by microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by the addition of 2 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h under constant stirring and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced improved hydrophobicity of the composites named as

Agarose/PVAc-composites (Xa). It was observed that the prepared composites are very brittle and non-flexible in nature thus not suitable to be used for applications such as seaweed cultivation.

Table 10: Effect of different reaction parameters and other variables in Example 10.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloi , {%) (wt%) (wt%)

d (wt%)

Agar 2 0.02 NIL This produced improved hydrophobicity of the composites named as Agar/PVAc-composites (Xb). It

(2)

was observed that the prepared composites are very brittle and non-flexible in nature thus not suitable to be used for applications such as seaweed cultivation.

Semi- 2 0.02 NIL This produced improved hydrophobicity of the refined composites named as SRC/PVAc-composites (Xc). It carrageenan was observed that the prepared composites are very (SRC) brittle and non-flexible in nature thus not suitable to be used for applications such as seaweed cultivation.

(2)

Alginate 2 0.02 NIL This produced improved hydrophobicity of the composites named as Alginate/PVAc-composites (Xd).

(2)

It was observed that the prepared composites are very brittle and non-flexible in nature thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 11

Experiments of Example 2, were repeated taking seaweed phycocolloid agarose (4 wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30 minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 8 wt% VAc. The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring and then transferred into the desired hollow vessels/devices/moulds to obtain the desired

shapes. The resulting moulded composites were treated with organic solvent at a

temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air

drying. This produced water non sensitive biodegradable composites named as

Agarose/PVAc-composites (XIa). It was observed that the prepared composites were

brittle, non-flexible and were not suitable to be used for applications such as seaweed

cultivation.

Table 11 : Effect of different reaction parameters and other variables in Example 1 1.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid ( (wt%) (wt%)

(wt%)

Agar 8 0.02 NIL This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (Xlb). It was (4)

observed that the prepared composites were brittle, non- flexible and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 0.02 NIL This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XIc). It was

(SRC) observed that the prepared composites were brittle, non- flexible and thus not suitable to be used for applications

(4)

such as seaweed cultivation.

Alginate 0.02 NIL This produced highly water non sensitive biodegradable composites named as Alginate/PVAc-composite (Xld). It (4)

was observed that the prepared composites were brittle, non- flexible and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 12

Experiments of Example 3, were repeated taking seaweed phycocolloid agarose (6

wt%) which was dissolved in water by autoclave heating at 120 degree Celsius for 30

minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring,

followed by addition of 16 wt% VAc. The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring and then transferred into the desired hollow vessels/devices/moulds to obtain the desired

shapes. The resulting moulded composites were treated with organic solvent at a

temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air

drying. This produced water non sensitive biodegradable composites named as

Agarose/PVAc-composites (Xlla). It was observed that the prepared composites were

brittle, non-flexible and were not suitable to be used for applications such as seaweed

cultivation.

Table 12: Effect of different reaction parameters and other variables in Example 12.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%>

(wt%)

(wt%)

Agar 16 0.02 NIL This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (Xllb). It was (6)

observed that the prepared composites were brittle, non- flexible and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 16 0.02 NIL This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XIIc). It was

(SRC) observed that the prepared composites were brittle, non- flexible and thus not suitable to be used for applications

(6)

such as seaweed cultivation.

Alginate 16 0.02 NIL This produced highly sensitive to water biodegradable composites named as Alginate/PVAc-composite (Xlld). It (6)

was observed that the prepared composites were brittle, non-flexible and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 13

Vinyl acetate 10 wt% was added in 100 ml distilled water. To this 0.02 wt% potassium

persulphate (KPS) was added under stirring. The reaction mixture was heated in

aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant

stirring. The reaction mixture was then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting polymers were treated with organic solvent at room temperature. These produced polymers named as PVAc (XIII), which dispersed in water, exhibited low strength, and were highly sensitive to organic solvents. Findinss from examples 1 to 13

Examples 1 to 9 demonstrated that vinylated reagents like AAm, ACN, and PVA produced composites (la to IXd), which were water sensitive and thus, were not suitable to be used for water applications such as seaweed cultivation and other similar applications. In addition, Examples 10 to 12 further demonstrated that vinyl acetate used as reagent produced composites (Xa to Xlld) with improved hydrophobicity compared to the parent seaweed phycocolloids, which are non-flexible, brittle in nature, and thus not suitable to be used for seaweed cultivation and other potential applications. These findings also revealed that a suitable plasticizer needs to be added to improve the flexibility and smoothness of these composites. Example 13 further demonstrated that vinyl acetate alone used as reagent produced hydrophobic PVAc (XIII) polymers, which are highly sensitive to organic solvents, and hence are not suitable to be used for seaweed cultivation and other applications.

EXAMPLE 14

Experiments of Example 10, were repeated taking agarose (2 wt%) which was dissolved in water by microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium persulphate (KPS) was addedunder stirring, followed by addition of 5 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XlVa), which are of low strength and thus not suitable to be used for applications such as seaweed cultivation. Yield of composites: 2.5 - 5.0 g, containing agarose 40-80 wt%, PVAc 12- 45 wt%, glycerol 2-10 wt% and moisture 5-10 wt% [Optimum yield is 5 ± 0.5 g, composition: Seaweed phycocolloids = 40 ± 2 wt%, PVAc = 45 ± 2 wt%, glycerol 5 ±

1 wt% and moisture 10 ± 1 wt%].

Table 14: Effect of different reaction parameters and other variables in Example 14.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XlVb). It (2)

was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XIVc). It (SRC) was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(2)

suitable to be used for applications such as seaweed cultivation.

Alginate This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XlVd). (2)

It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 15

Experiments of Example 11, were repeated taking agarose (4 wt%) which was dissolved

in water by microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt%

potassium persulphate (KPS) was added under stirring, followed by addition of 10 wt%

vinyl acetate (VAc). The reaction mixture was heated in aqueous medium under reflux

conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XVa). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for applications such as seaweed cultivation. Yield of composites: 4.8 - 11.2 g, containing agarose 35-86 wt%, PVAc 10-61 wt%, glycerol 5- 12 wt% and moisture 7-10 wt% [Optimum yield is 11.2 ± 0.5 g, composition: Seaweed phycocolloids = 36 ± 2 wt%, PVAc = 50 ± 2 wt%, glycerol 5 ± 1 wt% and moisture 8 ±

1 wt%].

Table 15: Effect of different reaction parameters and other variables in Example 15.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid , 0/ . (wt%) (wt%)

(wt%)

Agar 10 0.02 0.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XVb). It

(4)

was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation.

Semi-refined 10 0.02 0.5 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XVc). It

(SRC) was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(4)

suitable to be used for applications such as seaweed cultivation.

Alginate 10 0.02 0.5 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XVd).

(4)

It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation. EXAMPLE 16

Experiments of Example 12, were repeated taking agarose (6 wt%) which was dissolved in water by microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 12 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XVIa). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for applications such as seaweed cultivation. Yield of composites: 7.5 - 14.1 g, containing agarose 42-80 wt%, PVAc 13-40 wt%, glycerol 2- 8 wt% and moisture 5-10 wt% [Optimum yield is 14.1 ± 0.5 g, composition: Seaweed phycocolloids = 43 ± 2 wt%, PVAc = 42 ± 2 wt%, glycerol 7 ± 1 wt% and moisture 8 ±

1 wt%].

Table 16: Effect of different reaction parameters and other variables in Example 16.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid , 0/ . (wt%) (wt%)

(wt%)

Agar 12 0.02 0.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XVIb). It

(6)

was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation. Semi-refined 12 0.02 0.5 This produced water non sensitive biodegradable carrageenan composites named as SRC PVAc -composite (XVIc). It (SRC) was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(6)

suitable to be used for applications such as seaweed cultivation.

Alginate 12 0.02 0.5 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XVId).

(6)

It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

Examples 15 and 16 further demonstrated that seaweed phycocolloids namely agarose and agar (4 and 6 wt%) with VAc produced water non sensitive biodegradable composites (XVa,b and XVIa,b). It was observed that the prepared composites (XVa,b

and XVIa,b) were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation.

EXAMPLE 17

Experiments of Example 15, were repeated taking hybrid of agarose and semi-refined

carrageenans in 1 : 1 w/w ratio (4 wt%) which was dissolved in water by microwave

heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium persulphate

( PS) was added under stirring, followed by addition of 8 wt% vinyl acetate (VAc). The

reaction mixture was heated in aqueous medium under reflux conditions at 80 degree

Celsius for 5 h with constant stirring. 0.5 wt% glycerol was added into the reaction

mixture and then transferred into the desired hollow vessels/devices/moulds to obtain

the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed

by air drying. This produced water non sensitive biodegradable composites named as

Agarose/SRC/PVAc-composites (XVIIa). It was observed that the prepared composites

were hydrophobic biodegradable with high strength and thus suitable to be used for applications such as seaweed cultivation. Yields and compositions of the prepared

composites are in the range as given in the Example 15.

Table 17: Effect of different reaction parameters and other variables in Example 17.

Hybrid KPS Plasticizer Remarks/Observations

Seaweed (wt%) (wt%)

phycocolloids

(wt%)

Agarose/Agar 0.02 0.5 This produced water non sensitive biodegradable composites named as Agarose/Agar/PVAc-composite (4)

(XVIIb). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation.

Agarose/Algin 0.02 0.5 This produced water non sensitive biodegradable ate composites named as Agarose/ Alginate/PVAc-composite

(XVIIc). It was observed that the prepared composites

(4)

having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 18

Experiments of Example 16, were repeated taking hybrid of agarose and semi-refined

carrageenan (SRC) in 1 : 1 w/w ratio (6 wt%) which was dissolved in water by

microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium

persulphate (KPS) was added under stirring, followed by addition of 13 wt% vinyl

acetate (VAc). The reaction mixture was heated in aqueous medium under reflux

conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was

added into the reaction mixture and then transferred into the desired hollow

vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites

were treated with organic solvent at a temperature of 25 degree Celsius to remove the

unreacted homopolymer followed by air drying. This produced water non sensitive

biodegradable composites named as Agarose/SRC/PVAc-composites (XVIIIa). It was

observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation. Yields and compositions of the prepared composites are in the range as

given in the Example 16.

Table 18: Effect of different reaction parameters and other variables in Example 18.

Hybrid VAc KPS Plasticizer Remarks/Observations

Seaweed (wt%) (wt%)

(wt%)

phycocolloids

(wt%)

Agarose/Agar 13 0.02 0.5 This produced water non sensitive biodegradable composites named as Agarose/Agar/PVAc-composite (6)

(XVIIIb). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation.

Agarose/ Algin 13 0.02 0.5 This produced water non sensitive biodegradable ate composites named as Agarose/Alginate/PVAc- composite (XVIIIc). It was observed that the prepared

(6)

composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 19

Experiments of Example 15, were repeated taking hybrid of agar and semi-refined

carrageenan (SRC) in 1 : 1 w/w ratio (4 wt%) which was dissolved in water by

microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium

persulphate (KPS) was added under stirring, followed by addition of 11 wt% vinyl

acetate (VAc). The reaction mixture was heated in aqueous medium under reflux

conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was

added into the reaction mixture and then transferred into the desired hollow

vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites

were treated with organic solvent at a temperature of 25 degree Celsius to remove the

unreacted homopolymer followed by air drying. This produced water non sensitive

biodegradable composites named as Agar/SRC/PVAc-composites (XlXa). It was observed that the prepared composites were hydrophobic biodegradable with high

strength and thus suitable to be used for potential applications such as seaweed

cultivation. Yields and compositions of the prepared composites are in the range as given in the Example 15. Table 19: Effect of different reaction parameters and other variables in Example 19.

Hybrid VAc KPS Plasticizer Remarks/Observations

Seaweed ' %) (wt%) (wt%)

phycocolloids

(wt%)

Agar/ Alginate 11 0.02 0.5 This produced water non sensitive biodegradable

^ composites named as Agar/Alginate/PVAc-composite

(XlXb). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 20

Experiments of Example 16, were repeated taking hybrid of agar and semi-refined

carrageenan (SRC) in 1 : 1 w/w ratio (6 wt%) which was dissolved in water by

microwave heating at 100 degree Celsius for 15 minutes. To this 0.02 wt% potassium

persulphate (KPS) was added under stirring, followed by addition of 9 wt% vinyl

acetate (VAc). The reaction mixture was heated in aqueous medium under reflux

conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt% glycerol was

added into the reaction mixture and then transferred into the desired hollow

vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites

were treated with organic solvent at a temperature of 25 degree Celsius to remove the

unreacted homopolymer followed by air drying. This produced water non sensitive

biodegradable composites named as Agar/SRC/PVAc-composites (XXa). It was

observed that the prepared composites were hydrophobic biodegradable with high

strength and thus suitable to be used for potential applications such as seaweed

cultivation. Yields and compositions of the prepared composites are in the range as

given in the Example 16. Table 20: Effect of different reaction parameters and other variables in Example 20.

Hybrid Seaweed VAc KPS Plasticize Remarks/Observations

phycocolloids (w t% ( wt %) r (wt%)

(wt%) j °

Agar/Alginate 9 0.02 0.5 This produced water non sensitive biodegradable

^ composites named as Agar/Alginate/PVAc -composite

(XXb). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 21

The experiments of Examples 15 and 16 were repeated taking 7 wt% agarose. To this

0.04 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 14 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt%

glycerol was added into the reaction mixture and then transferred into the desired

hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded

composites were treated with organic solvent at a temperature of 25 degree Celsius to

remove the unreacted homopolymer followed by air drying. This produced water non

sensitive biodegradable composites named as Agarose/PVAc-composites (XXI a & a').

It was observed that the prepared composites were hydrophobic biodegradable with

high strength and thus suitable to be used for applications such as seaweed cultivation.

[Optimum yields (11.4 ± 0.2 g) and compositions of composites with 4 wt% agarose:- containing agarose = 36 ± 2 wt%, PVAc = 50 ± 2 wt%, glycerol 5 ± 1 wt% and moisture

8 ± 1 wt%; while optimum yields (14.3 ± 0.2 g) and compositions of composites with 6

wt% agarose is: agarose = 40 ± 2 wt%, PVAc = 49 ± 2 wt%, glycerol 5 ± 1 wt% and

moisture 6 ± 1 wt%].

Table 21 : Effect of different reaction parameters and other variables in Example 21.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid ( w t%) ( wt %) (wt%) (wt%)

Agar This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXIb & (7)

b'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation.

Semi-refined This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXIc & (SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and

(7)

thus not suitable to be used for applications such as seaweed cultivation.

Alginate This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXI (7)

d & d'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 22

The experiments of Examples 15 and 16 were repeated taking 5 wt% agarose. To this

0.08 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 5 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt%

glycerol was added into the reaction mixture and then transferred into the desired

hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded

composites were treated with organic solvent at a temperature of 25 degree Celsius to

remove the unreacted homopolymer followed by air drying. This produced water non

sensitive biodegradable composites named as Agarose/PVAc-composites (XXIIa & a')

It was observed that the prepared composites were hydrophobic biodegradable with

lower strength than the composites (XVa and XVIa) prepared in Examples 15 and 16

and thus not suitable to be used for applications such as seaweed cultivation. [Optimum

yields (11.0 ± 0.5 g) and compositions of composites with 4 wt% agarose: containing agarose = 35 ± 2 wt%, PVAc = 51 ± 2 wt%, glycerol 5 ± 1 wt% and moisture 8 ± 1 wt%; while optimum yields (13.9 ± 0.5 g) and compositions of composites with 6 wt%

agarose is: agarose = 39 ± 2 wt%, PVAc = 50 ± 2 wt%, glycerol 5 ± 1 wt% and moisture

6 ± 1 wt%]. Table 22: Effect of different reaction parameters and other variables in Example 22.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 2-16 0.08 0.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXIIb &

(5)

b')- It was observed that the prepared composites were hydrophobic biodegradable with lower strength than the composites (XVb and XVIb) prepared in Examples 15 and 16 and thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 2-16 0.08 0.5 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXIIc & (SRC) c'). It was observed that the prepared composites were hydrophobic biodegradable with lower strength than the

(5)

composites (XVc and XVIc) prepared in Examples 15 and 16 and thus not suitable to be used for applications such as seaweed cultivation.

Alginate 2-16 0.08 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXIId (5)

& d'). It was observed that the prepared composites were hydrophobic biodegradable with lower strength than the composites (XV d and XVI d) prepared in Examples 15 and 16 and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 23

The experiments of Examples 15 and 16 were repeated taking 4 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 9 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 1.5 wt% glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded

composites were treated with organic solvent at a temperature of 25 degree Celsius to

remove the unreacted homopolymer followed by air drying. This produced water non

sensitive biodegradable composites named as Agarose/PVAc-composites (XXIIIa & a').

It was observed that the prepared composites were hydrophobic biodegradable with

high strength and thus suitable to be used for applications such as seaweed cultivation.

Yields and compositions are according to the composites prepared in Examples 15 and

16.

Table 23: Effect of different reaction parameters and other variables in Example 23.

Seaweed VAc KPS Plasticizer Remarks/Observations

(wt%)

Ph [o?d C01 (wt%) (wt%)

(wt%)

Agar 9 0.02 1.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXIIIb & b'). It was (4) observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi- 9 0.02 1.5 This produced water non sensitive biodegradable composites refined named as SRC/PVAc-composite (XXIIIc & c'). It was carrageen observed that the prepared composites having improved an (SRC) hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

(4)

Alginate 9 0.02 1.5 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXIIId & d')- It was (4) observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 24

The experiments of Examples 15 and 16 were repeated taking 4 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 14 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 3.0 wt% glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XXI Va & a').

It was observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation.

Yields and compositions are according to the composites prepared in Examples 15 and

16.

Table 24: Effect of different reaction parameters and other variables in Example 24.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid ( wt %) (wt%) (wt%)

(wt%)

Agar 14 0.02 3.0 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXIVb & (4)

b'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi-refined 14 0.02 3.0 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXIVc & (SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(4)

suitable to be used for applications such as seaweed cultivation.

Alginate 14 0.02 3.0 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXIVd

(4)

& d'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 25

The experiments of Examples 15 and 16 were repeated taking 6 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 12 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 5.0 wt%

glycerol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XXVa & a').

It was observed that the prepared composites were hydrophobic biodegradable and leaching of plasticizer make them slippery and weaken thus not suitable to be used for applications such as seaweed cultivation. Yields and compositions are according to the composites prepared in Examples 15 and 16.

Table 25: Effect of different reaction parameters and other variables in Example 25.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid ( wt % \ (wt%) (wt%)

(wt%)

Agar 12 0.02 5.0 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXVb &

(6)

b'). It was observed that the prepared composites were hydrophobic biodegradable and leaching of plasticizer make them slippery and weaken thus not suitable to be used for applications such as seaweed cultivation. Semi-refined 12 0.02 5.0 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXVc &

(SRC) c'). It was observed that the prepared composites were hydrophobic biodegradable and leaching of plasticizer

(6)

make them slippery and weaken thus not suitable to be used for applications such as seaweed cultivation.

Alginate 12 0.02 5.0 This produced water non sensitive biodegradable composites named as Alginate/PVAc -composite (XXVd

(6)

& d'). It was observed that the prepared composites were hydrophobic biodegradable and leaching of plasticizer make them slippery and weaken thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 26

The experiments of Examples 15 and 16 were repeated taking 4 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 12 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt%

sorbitol was added into the reaction mixture and then transferred into the desired hollow

vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the

unreacted homopolymer followed by air drying. This produced water non sensitive

biodegradable composites named as Agarose/PVAc-composites (XXVIa & a'). It was

observed that the prepared composites were hydrophobic biodegradable with high

strength and thus suitable to be used for applications such as seaweed cultivation. Yields

and compositions are according to the composites prepared in Examples 15 and 16.

Table 26: Effect of different reaction parameters and other variables in Example 26.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%) Agar 12 0.02 0.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXVIb &

(4)

b'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi-refined 12 0.02 0.5 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXVIc &

(SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and

(4)

thus not suitable to be used for applications such as seaweed cultivation.

Alginate 12 0.02 0.5 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXVI

(4)

d & d')- It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 27

The experiments of Examples 15 and 16 were repeated taking 6 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 14 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 1.5 wt%

sorbitol was added into the reaction mixture and then transferred into the desired hollow

vessel s/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites (XXVIIa & a'). It was observed that the prepared composites were hydrophobic biodegradable with high

strength and thus suitable to be used for applications such as seaweed cultivation. Yields and compositions are according to the composites prepared in Examples 15 and 16. Table 27: Effect of different reaction parameters and other variables in Example 27.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 14 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXVTIb &

(6)

b'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi-refined 14 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXVIIc & (SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(6)

suitable to be used for applications such as seaweed cultivation.

Alginate 14 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXVII (6)

d & d'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 28

The experiments of Examples 15 and 16 were repeated taking 6 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 10 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 3.0 wt%

sorbitol was added into the reaction mixture and then transferred into the desired. hollow

vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites

were treated with organic solvent at a temperature of 25 degree Celsius to remove the

unreacted homopolymer followed by air drying. This produced water non sensitive

biodegradable composites named as Agarose/PVAc-composites (XXVIIIa & a'). It was

observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation. Yields and compositions are according to the composites prepared in Examples 15 and 16.

Table 28: Effect of different reaction parameters and other variables in Example 28.

Seaweed VAc KPS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 10 This produced water non sensitive biodegradable composites named as Agar PVAc-composite (XXVIIIb &

(6)

b'). It was observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation.

Semi-refined 10 This produced water non sensitive biodegradable carrageenan composites named as SRC PVAc-composite (XXVIIIc & (SRC) c'). It was observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable

(6)

to be used for applications such as seaweed cultivation.

Alginate 10 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXVIII (6)

d & d'). It was observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 29

The experiments of Examples 15 and 16 were repeated taking 4 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition of 8 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 0.5 wt%

ethylene glycol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree

Celsius to remove the unreacted homopolymer followed by air drying. This produced

water non sensitive biodegradable composites named as Agarose/PVAc-composites (XXIXa & a'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for applications such as seaweed cultivation. Yields and compositions are according to the composites prepared in Examples 15 and 16.

Table 29: Effect of different reaction parameters and other variables in Example 29.

Seaweed VAc KPS Plasticiz Remarks/Observations

phycocolloid (wt%) er

(wt%)

(wt%)

(wt%)

Agar 0.02 0.5 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXIXb &

(4)

b'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi-refined 0.02 0.5 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXIXc & (SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(4)

suitable to be used for applications such as seaweed cultivation.

Alginate 0.02 0.5 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXIXd & (4)

d'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 30

The experiments of Examples 15 and 16 were repeated taking 8 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 10 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium

under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 1.5 wt%

ethylene glycol was added into the reaction mixture and then transferred into the desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting moulded composites were treated with organic solvent at a temperature of 25 degree

Celsius to remove the unreacted homopolymer followed by air drying. This produced water non sensitive biodegradable composites named as Agarose/PVAc-composites

(XXXa & a'). It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for applications such as seaweed cultivation. Yields and compositions are according to the composites prepared in Examples 15 and 16.

Table 30: Effect of different reaction parameters and other variables in Example 30.

Seaweed VAc PS Plasticizer Remarks/Observations

phycocolloid (wt%) (wt%)

(wt%)

(wt%)

Agar 10 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXXb &

(8)

b')- It was observed that the prepared composites were hydrophobic biodegradable with high strength and thus suitable to be used for potential applications such as seaweed cultivation

Semi-refined 10 This produced water non sensitive biodegradable carrageenan composites named as SRC/PVAc-composite (XXXc & (SRC) c'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not

(8)

suitable to be used for applications such as seaweed cultivation.

Alginate 10 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXXd (8)

& d'). It was observed that the prepared composites having improved hydrophobicity and low strength and thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 31 The experiments of Examples 15 and 16 were repeated taking 8 wt% agarose. To this

0.02 wt% potassium persulphate (KPS) was added under stirring, followed by addition

of 10 wt% vinyl acetate (VAc). The reaction mixture was heated in aqueous medium under reflux conditions at 80 degree Celsius for 5 h with constant stirring. 3.0 wt% ethylene glycol was added into the reaction mixture and then transferred into the

desired hollow vessels/devices/moulds to obtain the desired shapes. The resulting

moulded composites were treated with organic solvent at a temperature of 25 degree

Celsius to remove the unreacted homopolymer followed by air drying. This produced

water non sensitive biodegradable composites named as Agarose/PVAc-composites

(XXXIa & a'). It was observed that the prepared composites were hydrophobic

biodegradable and slippery thus not suitable to be used for applications such as seaweed

cultivation. Yields and compositions are according to the composites prepared in

Examples 15 and 16.

Table 31: Effect of different reaction parameters and other variables in Example 31.

Seaweed VAc( {CPS Plasticizer Remarks/Observations

phycocoll wt%) (wt%) (wt%)

oid

(wt%)

Agar 10 0.02 3.0 This produced water non sensitive biodegradable composites named as Agar/PVAc-composite (XXXIb & b')- It was (8)

observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation.

Semi- 10 0.02 3.0 This produced water non sensitive biodegradable composites refined named as SRC/PVAc-composite (XXXIc & c'). It was observed carrageen that the prepared composites were hydrophobic biodegradable an (SRC) and slippery thus not suitable to be used for applications such as seaweed cultivation.

(8)

Alginate 10 0.02 3.0 This produced water non sensitive biodegradable composites named as Alginate/PVAc-composite (XXXId & d')- It was (8)

observed that the prepared composites were hydrophobic biodegradable and slippery thus not suitable to be used for applications such as seaweed cultivation.

EXAMPLE 32

The hydrophobic biodegradable composites prepared in Examples 14-31 were treated

with color reducing food grade dyes namely Brilliant Blue FCF, Allura Red AC , and

Tartrazine, etc. to obtain desired colored ropes for making decorative or attractive

household items (Fig. 1).

EXAMPLE 33

Reaction mixtures obtained in Examples 14-20 were tested for their biodegradability

using moist soil test after casting in the form of films and ropes. The films got degraded

within 20-45 days; whiles ropes took longer duration in the range of 90 to 600 day to

degrade completely. This Example revealed that materials obtained in the above

Examples are biodegradable and eco-friendly.

EXAMPLE 34

The hydrophobic biodegradable composites prepared in Examples 15 and 16 were used

for seaweed cultivation in seawater environment. For this, Kappaphycus alvarezii was

collected from south east coast (Thoniturai, 79 o 10'29"E-9°16'21 "N), Mandapam-623

519, Tamil Nadu, India, and was cultivated at Thoniturai, 79°10'29"E-9°16'21 "N on

the biodegradable hydrophobic ropes prepared from the composites of Examples 15 and

16 and fixed with planting rope (8 mm diameter which was Garware polypropylene

rope). The plant was allowed to grow in open sea water and periodical observations

were made to ensure the acclimatization of the biodegradable rope in marine

environment. It was observed that the growth of the plants was normal and was

comparable with plants grown by common methods adopted for commercial cultivation

of Kappaphycus using 0.5 mm dia braider for tie-tie method. After 35 days the total

biomass and daily growth rate (DGR%) were 480 grams and 4.48% respectively in the biodegradable ropes. The same plant was also grown in braider as well as on the

combination of braider and biodegradable ropes, and the total biomass was observed to

be 390 (DGR 3.88%) and 425.5 (DGR 4.13%), respectively, which was lesser as

compared to seaweed phycocolloids based ropes (Table 32 & Fig. 2). Table 32. Performance of hydrophobic ropes during seaweed cultivation (Kappap ycus

alvarezii) in the open Sea at Mandapam, Tamil Nadu.

Sr. No. Braider Braider & Biodegradable rope Biodegradable rope

Initial weight (gm) 100.0 100.0 100.0

Fresh weight after 35 days 390.0 425.5 480.0

DGR%/day 3.88 4.13 4.48

EXAMPLE 35

The hydrophobic biodegradable composites prepared in Examples 14-20 were used as

handles of carry bags, which have capacity to carry 2-5 kg weight (Fig. 3). Seaweed

polysaccharides based handles offers superior feeling when carrying bags compared to

synthetic handles. No adverse effects were observed on using handles of ropes prepared

in Examples 14-20 up to 3 months. After 3 months there is no considerable effect on the

performance and quality of biodegradable ropes. These are eco-friendly and easy to

dispose off in the open environment.

EXAMPLE 36

The hydrophobic biodegradable composites prepared as per the procedure of Example

14-31 were used as biodegradable design e.g. in designing belts, bags and other leather

or cloth items (Fig. 4). It offers very smooth and soft feeling while wearing belts with

biodegradable design compared to synthetic handles. Even after 2 months, there was no

considerable change in the performance and quality of these designs. EXAMPLE 37

The hydrophobic biodegradable composites prepared as per the procedure of Example 14-31 were used as biodegradable cap of studs (Fig. 5). Stud cap of biodegradable ropes offers superior feeling when worn in ear compared to synthetic one. Even after 2 months there was no adverse effect or any allergic effect on the skin of the ear.

EXAMPLE 38

The hydrophobic biodegradable composites prepared as per the procedure of Example 14-31 were used for the preparation of biodegradable bowl, which has capacity to carry 2-5 kg weight (Fig. 6). It was observed that it offer attractive look while in use of keeping vegetables and fruits in biodegradable bowl compared to synthetic. Even after 9 months there was no considerable change in the performance and quality of the biodegradable bowls.

EXAMPLE 39

The bowl prepared as per Example 38 was used as biodegradable bowl for storage of vegetable and fruits items, which has the capacity to carry 2-5 kg weight (Fig. 7). It was observed that it offers attractive look in house when vegetable and fruits were kept in biodegradable bowl as compared to synthetic. Even after 9 months there was no considerable change in the performance and quality of the biodegradable bowls.

EXAMPLE 40 The bowl prepared as per Example 38 was used as biodegradable bowl for storage of biscuits, chips and other food packets, which has the capacity to carry 2-5 kg weight (Fig. 8). It was observed that it offers attractive look in house when biscuit and chips and other food packets were kept in biodegradable bowl as compared to synthetic. Even after 9 months there was no considerable change in the performance and quality of the biodegradable bowls. EXAMPLE 41

The hydrophobic biodegradable composites prepared as per the procedure of Examples 14-20 were used as biodegradable flower pots/jars, which provided good looks and feeling (Figs. 9 and 10). It was observed that it offers attractive look in house when flowers were kept in biodegradable pots/jars. Even after 11 months there was no considerable change in the performance and quality of the biodegradable flower pots/jars.

EXAMPLE 42

The hydrophobic biodegradable composites prepared in Examples 14-31 were used for making biodegradable gift items including hand belts (Fig. 11). It was observed that it offered attractive look in hands. Even after 6 months there was no adverse effect on the skin as well as the performance and quality of the biodegradable hand belts.

EXAMPLE 43

The hydrophobic biodegradable composites prepared in Examples 15 and 16 were used for drying of cloths in environmental conditions (Fig. 12). It was observed that it offered attractive look in houses and no rusting was observed even after 3 months of use. After 3 months there was no adverse change on the smoothness as well as on the performance and quality of the hydrophobic biodegradable composites.

ADVANTAGES OF THE INVENTION

• Recognizing the fact that seaweed cultivation inevitably requires use of ropes and that non-biodegradability of available ropes can pose a serious environmental threat where cultivation is undertaken on a very large scale, leading to massive problem of pollution with the generated solid waste, the present invention provides a solution to said problem by providing biodegradable hydrophobic composites which can be moulded in form of ropes that can be well used for seaweed cultivation. • By blending monomers such as vinyl acetate onto the seaweed polymers it is possible to impart enhanced hydrophobicity to the prepared composites without compromising excessively on their biodegradability, especially in soil.

• The prepared biodegradable hydrophobic composites exhibit high thermal stability which allows them to be sterilized at high temperature for wider applications such as in pharmaceutical applications.

• The prepared biodegradable hydrophobic composites exhibit stability in water up to 90 degree Celsius which may be used for wider aqueous applications such as cultivation of seaweeds in open sea water.