CATALYTIC COMPOSITIONS

INTRODUCTION

[0001 ] The present invention relates to catalytic compositions. More particularly, the present invention relates to catalytic compositions comprising constrained geometry complexes associated with a catalytic support material. The present invention also relates to the use of catalytic compositions in the polymerisation of alkenes.

BACKGROUND OF THE INVENTION

[0002] It is well known that ethylene (and a-olefins in general) can be readily polymerized at low or medium pressures in the presence of certain transition metal catalysts. These catalysts are generally known as Zeigler-Natta type catalysts.

[0003] A particular group of these Ziegler-Natta type catalysts, which catalyse the polymerization of ethylene (and a-olefins in general), comprise an aluminoxane activator and a metallocene transition metal catalyst. Metallocenes comprise a metal bound between two η ⁵ - cyclopentadienyl type ligands. Generally the r -cyclopentadienyl type ligands are selected from rf-cyclopentadienyl,

[0004] At the time of their conception, constrained geometry complexes (CGCs) represented one of the first major departures from metallocene-based catalysts. In structural terms, CGCs feature a ττ-bonded ligand linked to one of the other ligands on the same metal centre, in such a manner that the angle subtended by the centroid of the ττ-system and the other ligand from the metal centre is smaller than in comparable complexes wherein the ττ-bonded ligand and the other ligand are not linked. To date, research in the field of CGCs has centred around ansa- bridged cyclopentadienyl amido complexes, with such catalysts presently featuring heavily in the industrial preparation of CGC-derived polymers.

[0005] In spite of the advances made using ansa-bridged cyclopentadienyl amido-based complexes, there remains a need for CGCs, or compositions comprising them, having improved characteristics. In particular, there remains a need for CGCs having improved catalytic properties and/or GCGs suitable for preparing polymers having desirable characteristics. Such improved catalytic properties may include enhanced catalytic activity, better co-monomer incorporation and improved stability. Desirable polymer characteristics may include particular polymer molecular weights, polydispersities and melt indices.

[0006] The present invention was devised with the foregoing in mind. SUMMARY OF THE INVENTION

[0007] According to a first aspect of the present invention, there is provided a catalytic composition comprising a compound of formula (I) as defined herein associated with solid polymethylaluminoxane.

[0008] According to a further aspect of the present invention, there is provided a use of a composition as defined herein in the polymerisation of ethylene and optionally one or more (3- 10C)alkene.

[0009] According to a further aspect of the present invention, there is provided a polymerisation process comprising the step of:

a) polymerising ethylene and optionally one or more (3-10C)alkene in the presence of a composition as defined herein.

DETAILED DESCRIPTION OF THE INVENTION

Definitions

[0010] The term "(m-nC)" or "(m-nC) group" used alone or as a prefix, refers to any group having m to n carbon atoms.

[0011 ] The term "alkyl" as used herein includes reference to a straight or branched chain alkyl moieties, typically having 1 , 2, 3, 4, 5 or 6 carbon atoms. This term includes reference to groups such as methyl, ethyl, propyl (n-propyl or isopropyl), butyl (n-butyl, sec-butyl or tert- butyl), pentyl (including neopentyl), hexyl and the like. In particular, an alkyl may have 1 , 2, 3 or 4 carbon atoms.

[0012] The term "alkenyl" as used herein include reference to straight or branched chain alkenyl moieties, typically having 2, 3, 4, 5 or 6 carbon atoms. The term includes reference to alkenyl moieties containing 1 , 2 or 3 carbon-carbon double bonds (C=C). This term includes reference to groups such as ethenyl (vinyl), propenyl (allyl), butenyl, pentenyl and hexenyl, as well as both the cis and trans isomers thereof.

[0013] The term "(3-10C)alkene" as used herein includes reference to any alkene having 3-10 carbon atoms that is capable of being copolymerised with ethylene. Straight and branching aliphatic alkenes are included (e.g. 1 -hexene or 1 -octene), as are alkenes comprising an aromatic moiety (e.g. styrene). [0014] The term "alkynyl" as used herein include reference to straight or branched chain alkynyl moieties, typically having 2, 3, 4, 5 or 6 carbon atoms. The term includes reference to alkynyl moieties containing 1 , 2 or 3 carbon-carbon triple bonds (C≡C). This term includes reference to groups such as ethynyl, propynyl, butynyl, pentynyl and hexynyl.

[0015] The term "alkoxy" as used herein include reference to -O-alkyl, wherein alkyl is straight or branched chain and comprises 1 , 2, 3, 4, 5 or 6 carbon atoms. In one class of embodiments, alkoxy has 1 , 2, 3 or 4 carbon atoms. This term includes reference to groups such as methoxy, ethoxy, propoxy, isopropoxy, butoxy, tert-butoxy, pentoxy, hexoxy and the like.

[0016] The term "aryl" as used herein includes reference to an aromatic ring system comprising 6, 7, 8, 9 or 10 ring carbon atoms. Aryl is often phenyl but may be a polycyclic ring system, having two or more rings, at least one of which is aromatic. This term includes reference to groups such as phenyl, naphthyl and the like.

[0017] The term "aryl(m-nC)alkyl" means an aryl group covalently attached to a (m- nC)alkylene group. Examples of aryl-(m-nC)alkyl groups include benzyl, phenylethyl, and the like.

[0018] The term "halogen" or "halo" as used herein includes reference to F, CI, Br or I. In a particular, halogen may be F or CI, of which CI is more common.

[0019] The term "substituted" as used herein in reference to a moiety means that one or more, especially up to 5, more especially 1 , 2 or 3, of the hydrogen atoms in said moiety are replaced independently of each other by the corresponding number of the described substituents. The term "optionally substituted" as used herein means substituted or unsubstituted.

[0020] It will, of course, be understood that substituents are only at positions where they are chemically possible, the person skilled in the art being able to decide (either experimentally or theoretically) without inappropriate effort whether a particular substitution is possible. For example, amino or hydroxy groups with free hydrogen may be unstable if bound to carbon atoms with unsaturated (e.g. olefinic) bonds. Additionally, it will of course be understood that the substituents described herein may themselves be substituted by any substituent, subject to the aforementioned restriction to appropriate substitutions as recognised by the skilled person.

Compositions of the invention

[0021 ] As described hereinbefore, the present invention provides a catalytic composition comprising a compound of formula (I) shown below associated with solid polymethylaluminoxane:

R ₁ is (1 -6C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more groups selected from (1 -4C)alkyl;

wherein each R ₂ is independently selected from (1 -3C)alkyl;

R _a and R _b are independently hydrogen, (1 -6C)alkyl, aryl and aryl(1 -2C)alkyl, either or which may be optionally substituted with one or groups selected from (1 - 2C)alkyl;

X is scandium, yttrium, lutetium, titanium, zirconium or hafnium

each Y is independently halo, hydrogen, a phosphonated, sulfonated or borate anion, or a (1 -6C)alkyl, (2-6C)alkenyl, (2-6C)alkynyl, (1 -6C)alkoxy, aryl or aryloxy group which is optionally substituted with one or more groups selected from (1 -6C)alkyl, halo, nitro, amino, phenyl, (1 -6C)alkoxy, -C(0)NR _x R _y or -Si[(1 -4C)alkyl] ₃ ;

wherein R _x and R _y are independently (1 -4C)alkyl.

[0022] The compositions of the invention offer a number of advantages when compared with CGCs currently favoured by industry. In particular, the compositions of the invention have been shown to be as much as six times more catalytically active in the homopolymerisation of ethylene than analogous compositions employing the ansa-bridged cyclopentadienyl amido CGC currently preferred in industry. Furthermore, the compositions of the invention are noticeably more productive than industrial standard catalysts when ethylene is polymerised in the presence of hydrogen, or another alkene (e.g. 1 -hexene of styrene).

[0023] In an embodiment, R ₁ is (1 -5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more groups selected from (1 -3C)alkyl, wherein each R ₂ is independently selected from (1 -4C)alkyl.

[0024] In an embodiment, R ₁ is (1 -5C)alkyl, -Si(R ₂ ) ₃ or phenyl, either of which is optionally substituted with one or more groups selected from (1 -3C)alkyl, wherein each R ₂ is independently selected from (1 -3C)alkyl. [0025] In another embodiment, R ₁ is (2-5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -4C)alkyl, wherein each R ₂ is independently selected from (1 -2C)alkyl.

[0026] In another embodiment, R ₁ is (2-5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -3C)alkyl, wherein each R ₂ is independently selected from (1 -2C)alkyl.

[0027] In another embodiment, R ₁ is (2-5C)alkyl or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -4C)alkyl.

[0028] In another embodiment, R ₁ is (2-5C)alkyl or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (2-4C)alkyl.

[0029] In another embodiment, R ₁ is methyl, ethyl, iso-propyl, iso-butyl, n-butyl, sec-butyl, tert- butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl, di-isopropylphenyl, tert-butylphenyl or n- butylphenyl.

[0030] In another embodiment, R ₁ is methyl, ethyl, iso-propyl, iso-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl or di-isopropylphenyl.

[0031 ] In another embodiment, R ₁ is (1 -5C)alkyl.

[0032] In a particularly suitable embodiment, R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted with a (1 -4C)alkyl group.

[0033] In a particularly suitable embodiment, R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted at the 4-position with a (1 -4C)alkyl group.

[0034] In a particularly suitable embodiment, R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted at the 4-position with n-butyl or tert-butyl.

[0035] In a particularly suitable embodiment, R ₁ is tert-butyl or iso-propyl.

[0036] In a particularly suitable embodiment, R ₁ is tert-butyl.

[0037] In another embodiment, R _a and R _b are independently selected from hydrogen, (1 - 4C)alkyl, phenyl and benzyl.

[0038] In another embodiment, R _a and R _b are independently selected from hydrogen, (1 - 3C)alkyl, phenyl and benzyl.

[0039] In another embodiment, R _a and R _b are independently selected from hydrogen or (1 - 3C)alkyl.

[0040] In another embodiment, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl. [0041 ] In another embodiment, X is titanium, zirconium or hafnium. Suitably, X is zirconium or titanium. More suitably, X is titanium.

[0042] In another embodiment, each Y is independently halo, hydrogen, or a (1 -4C)alkyl group which is optionally substituted with one or more groups selected from (1 -4C)alkyl, halo, nitro, amino, phenyl and (1 -4C)alkoxy.

[0043] In another embodiment, each Y is independently halo, hydrogen, or a (1 -4C)alkyl group which is optionally substituted with one or more groups selected from (1 -4C)alkyl, halo and phenyl.

[0044] In another embodiment, each Y is independently halo, hydrogen, or (1 -4C)alkyl.

[0045] In another embodiment, each Y is independently halo. Suitably, at least one Y group is chloro. More suitably, both Y groups are chloro.

[0046] In an embodiment, the compound of formula (I) has a structure according to formula (la) below:

wherein

R ₁ , R _a , R _b , X and Y are each independently as defined in any of the paragraphs provided hereinbefore.

[0047] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein R ₁ is (2-5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -4C)alkyl, wherein each R ₂ is independently selected from (1 -2C)alkyl.

[0048] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, n-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl, di-isopropylphenyl, tert-butylphenyl or n- butylphenyl. [0049] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl or di-isopropylphenyl. Suitably, R ₁ is methyl, ethyl, iso- propyl, iso-butyl, sec-butyl, tert-butyl or neopentyl. Even more suitably, R ₁ is tert-butyl.

[0050] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted with a (1 -4C)alkyl group.

[0051 ] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein R _a and R _b are independently selected from hydrogen or (1 -3C)alkyl. Suitably, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl.

[0052] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein X is titanium or zirconium.

[0053] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein X is titanium.

[0054] In another embodiment, the compound of formula (I) has a structure according to formula (la), wherein each Y is independently halo, hydrogen, or (1 -4C)alkyl.

[0055] In an embodiment, the compound of formula (I) has a structure according to formula (lb) below:

wherein

R ₁ , R _a , R _b and X are as defined in any of the paragraphs provided hereinbefore.

[0056] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein R ₁ is (2-5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -4C)alkyl, wherein each R ₂ is independently selected from (1 -2C)alkyl. [0057] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, n-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl, di-isopropylphenyl, tert-butylphenyl or n- butylphenyl.

[0058] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl or di-isopropylphenyl. Suitably, R ₁ is methyl, ethyl, iso- propyl, iso-butyl, sec-butyl, tert-butyl or neopentyl. Even more suitably, R ₁ is tert-butyl.

[0059] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted with a (1 -4C)alkyl group.

[0060] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein R _a and R _b are independently selected from hydrogen or (1 -3C)alkyl. Suitably, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl.

[0061 ] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein X is titanium or zirconium.

[0062] In another embodiment, the compound of formula (I) has a structure according to formula (lb), wherein X is titanium.

[0063] In an embodiment, the compound of formula (I) has a structure according to formula (lc) below:

wherein

R ₁ , R _a , R _b and Y are each independently as defined in any of the paragraphs provided hereinbefore. [0064] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein R ₁ is (2-5C)alkyl, -Si(R ₂ )3 or phenyl, either of which is optionally substituted with one or more (e.g. 2 or 3) groups selected from (1 -4C)alkyl, wherein each R ₂ is independently selected from (1 -2C)alkyl.

[0065] n another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, n-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl, di-isopropylphenyl, tert-butylphenyl or n- butylphenyl.

[0066] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein R ₁ is methyl, ethyl, iso-propyl, iso-butyl, sec-butyl, tert-butyl, neopentyl, trimethylsilyl, phenyl, mesityl, xylyl or di-isopropylphenyl. Suitably, R ₁ is methyl, ethyl, iso- propyl, iso-butyl, sec-butyl, tert-butyl or neopentyl. Even more suitably, R ₁ is tert-butyl.

[0067] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein R ₁ is n-butyl, tert-butyl, iso-propyl, or phenyl substituted with a (1 -4C)alkyl group.

[0068] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein R _a and R _b are independently selected from hydrogen or (1 -3C)alkyl. Suitably, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl.

[0069] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein each Y is independently halo, hydrogen, or (1 -4C)alkyl.

[0070] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein each Y is independently halo. Suitably, at least one Y group is chloro. More suitably, both Y groups are chloro.

[0071 ] In another embodiment, the compound of formula (I) has a structure according to formula (Ic), wherein at least one Y group is chloro and the other is (1 -4C)alkyl.

[0072] In an embodiment, the compound of formula (I) has a structure according to formula (Id) below:

wherein

R _a , R _b and Y are each independently as defined in any of the paragraphs provided hereinbefore.

[0073] In another embodiment, the compound of formula (I) has a structure according to formula (Id), wherein R _a and R _b are independently selected from hydrogen or (1 -3C)alkyl. Suitably, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl.

[0074] In another embodiment, the compound of formula (I) has a structure according to formula (Id), each Y is independently halo, hydrogen, or (1 -4C)alkyl.

[0075] In another embodiment, the compound of formula (I) has a structure according to formula (Id), wherein each Y is independently halo. Suitably, at least one Y group is chloro. More suitably, both Y groups are chloro.

[0076] In another embodiment, the compound of formula (I) has a structure according to formula (Id), wherein at least one Y group is chloro and the other is (1 -4C)alkyl.

[0077] In an embodiment, the compound of formula (I) has a structure according to formula (le) below:

wherein R _a and R _b are each independently as defined in any of the paragraphs provided hereinbefore.

[0078] In another embodiment, the compound of formula (I) has a structure according to formula (le), wherein R _a and R _b are independently selected from hydrogen or (1 -3C)alkyl. Suitably, R _a and R _b are both methyl or ethyl, or one of R _a and R _b is methyl and the other is propyl.

[0079] In a particularly suitable embodiment, the compound of formula (I) has any of the following structures:

[0081 ] The compound of formula (I) may be associated with the solid polymethylaluminoxane support material by one or more ionic or covalent interactions. It will be understood that any minor structural modifications to the compound of formula (I) arising from it being associated with the solid polymethylaluminoxane support material are within the scope of this invention. For example, without wishing to be bound by theory, the compound of formula (I) may be associated with solid polymethylaluminoxane as illustrated in figure 6 (i.e. by replacement of one of the Y groups with a bond to oxygen on the surface of the solid polymethylaluminoxane).

[0082] The terms "solid MAO" and "solid polymethylaluminoxane" are used synonymously herein to refer to a solid-phase material having the general formula -[(Me)AIO] _n -, wherein n is an integer from 4 to 50 (e.g. 10 to 50). Any suitable solid polymethylaluminoxane may be used.

[0083] There exist numerous substantial structural and behavioural differences between solid polymethylaluminoxane and other (non-solid) MAOs. Perhaps most notably, solid polymethylaluminoxane is distinguished from other MAOs as it is insoluble in hydrocarbon solvents and so acts as a heterogeneous support system. The solid polymethylaluminoxane useful in the compositions of the invention are insoluble in toluene and hexane.

[0084] In contrast to non-solid (hydrocarbon-soluble) MAOs, which are traditionally used as an activator species in slurry polymerisation or to modify the surface of a separate solid support material (e.g. Si0 ₂ ), the solid polymethylaluminoxanes useful as part of the present invention are themselves suitable for use as solid-phase support materials, without the need for an additional activator. Hence, compositions of the invention comprising solid polymethylaluminoxane are devoid of any other species that could be considered a solid support (e.g. inorganic material such as Si0 ₂ , Al ₂ 0 ₃ and Zr0 ₂ ). Moreover, given the dual function of the solid polymethylaluminoxane (as catalytic support and activator species), the compositions of the invention comprising solid MAO may contain no additional catalytic activator species.

[0085] In an embodiment, the solid polymethylaluminoxane is prepared by heating a solution containing MAO and a hydrocarbon solvent (e.g. toluene), so as to precipitate solid polymethylaluminoxane. The solution containing MAO and a hydrocarbon solvent may be prepared by reacting trimethyl aluminium and benzoic acid in a hydrocarbon solvent (e.g. toluene), and then heating the resulting mixture.

[0086] In an embodiment, the solid polymethylaluminoxane is prepared according to the following protocol:

The properties of the solid polymethylaluminoxane can be adjusted by altering one or more of the processing variables used during its synthesis. For example, in the above-outlined protocol, the properties of the solid polymethylaluminoxane may be adjusted by varying the Al:0 ratio, by fixing the amount of AIMe ₃ and varying the amount of benzoic acid. Exemplary Al:0 ratios are 1 :1 , 1 .1 :1 , 1 .2:1 , 1 .3:1 , 1 .4:1 and 1 .6:1 . Suitably the Al:0 ratio is 1 .2:1 or 1 .3:1 . Alternatively, the properties of the solid polymethylaluminoxane may be adjusted by fixing the amount of benzoic acid and varying the amount of AIMe ₃ .

[0087] In another embodiment, the solid polymethylaluminoxane is prepared according to the following protocol:

[0088] In the above protocol, steps 1 and 2 may be kept constant, with step 2 being varied. The temperature of step 2 may be The duration of step 2 may be from 12 to 28 hours (e.g. 12, 20 or 28 hours). The duration of step 2 may be from 5 minutes to 24 hours. Step 3 may be conducted in a solvent such as toluene.

[0089] In an embodiment, the aluminium content of the solid polymethylaluminoxane falls within the range of 36-41 wt%.

[0090] The solid polymethylaluminoxane useful as part of the present invention is characterised by extremely low solubility in toluene and n-hexane. In an embodiment, the solubility in n-hexane at 25°C of the solid polymethylaluminoxane is 0-2 mol%. Suitably, the solubility in n-hexane at 25°C of the solid polymethylaluminoxane is 0-1 mol%. More suitably, the solubility in n-hexane at 25ºC of the solid polymethylaluminoxane is 0-0.2 mol%. Alternatively or additionally, the solubility in toluene at 25°C of the solid polymethylaluminoxane is 0-2 mol%. Suitably, the solubility in toluene at 25ºC of the solid polymethylaluminoxane is 0-1 mol%. More suitably, the solubility in toluene at 25ºC of the solid polymethylaluminoxane is 0-0.5 mol%. The solubility in solvents can be measured by the method described in JP- B(KOKOKU)-H07 42301 .

[0091 ] In a particularly suitable embodiment, the solid polymethylaluminoxane is as described in US2013/0059990, WO2010/055652 or WO2013/146337, and is obtainable from Tosoh Finechem Corporation, Japan.

[0092] In an embodiment, the mole ratio of solid polymethylaluminoxane to the compound of formula (I) is 50:1 to 500:1 . Suitably, the mole ratio of solid polymethylaluminoxane to the compound of formula (I) is 75:1 to 400:1 . More suitably, the mole ratio of solid polymethylaluminoxane to the compound of formula (I) is 100:1 to 300:1 .

Preparation of compositions of invention

[0093] The compounds of formula (I) may be synthesised by any suitable process known in the art. Particular examples of processes for the preparing compounds of formula (I) are set out in the accompanying examples.

[0094] Suitably, a compound of formula (I) is prepared by:

(i) reacting a compound of formula A:

(wherein R ₁ , R _a and R _b are each as defined hereinbefore and M is Li, Na or K) with a compound of the formula

(wherein X is as defined hereinbefore and Y' is halo (particularly chloro or bromo)) in the presence of a suitable solvent to form a compound of formula (Γ):

and optionally thereafter:

(ii) reacting the compound of formula la above with MY" (wherein M is as defined above and Y" is a group Y as defined herein other than halo), in the presence of a suitable solvent to form the compound of the formula (I") shown below

[0095] Suitably, M is Li in step (i) of the process defined above.

[0096] Suitably, the compound of formula B is provided as a solvate. In particular, the compound of formula B may be provided as X(Y') ₄ .THFp, where p is an integer (e.g. 2).

[0097] Any suitable solvent may be used for step (i) of the process defined above. A particularly suitable solvent is toluene or THF.

[0098] If a compound of formula (I) in which Y is other than halo is required, then the compound of formula (Γ) above may be further reacted in the manner defined in step (ii) to provide a compound of formula (I").

[0099] Any suitable solvent may be used for step (ii) of the process defined above. A suitable solvent may be, for example, diethyl ether, toluene, THF, dichloromethane, chloroform, hexane DMF, benzene etc.

[00100] Compounds of formula A may generally be prepared by:

(i) Reacting a compound of formula C:

(wherein M is lithium, sodium, or potassium) with one equivalent of a compound having formula D shown below:

(wherein R _a and R _b are as defined hereinbefore)

to form the compound of the formula E shown below:

(ii) Reacting the compound of formula E with a compound of formula F shown below:

(wherein R ₁ is as defined hereinbefore, and wherein Li may be substituted for K or Na).

[00101] Compounds of formulae A and F can be readily synthesized by techniques well known in the art.

[00102] Any suitable solvent may be used for step (i) of the above process. A particularly suitable solvent is THF.

[00103] Similarly, any suitable solvent may be used for step (ii) of the above process. A suitable solvent may be, for example, toluene, THF, DMF etc.

[00104] A person of skill in the art will be able to select suitable reaction conditions (e.g. temperature, pressures, reaction times, agitation etc.) for such a synthesis.

[00105] Once prepared, the compound of formula (I) may be associated with the solid polymethylaluminoxane by any suitable means. For example, the compound of formula (I) may be associated with the solid polymethylaluminoxane by contacting the compound of formula (I) with the solid polymethylaluminoxane in a suitable solvent (e.g. toluene) with heating, and then isolating the resulting coloured solid. Uses of the compositions

[00106] As described hereinbefore, the present invention also provides a use of a composition as defined herein in the polymerisation of ethylene and optionally one or more (3- 10C)alkene.

[00107] The compositions of the invention may be used as catalysts in the preparation of a variety of polymers, including polyalkylenes (e.g. polyethylene) of varying molecular weight, and copolymers. Such polymers and copolymers may be prepared by heterogeneous slurry- phase polymerisation of a monomer-containing feed stream.

[00108] In an embodiment, when the optional one or more (3-10C)alkene is not included, the compositions of the invention may be used to prepare polyethylene homopolymers.

[00109] In another embodiment, the optional one or more (3-10C)alkene (which may be an a- olefin) is one or more (3-8C)alkene. Suitably, the quantity of the one or more (3-8C)alkene in the monomer feed stream is 0.05-10 mol%, relative to the quantity of ethylene monomers. More suitably, the one or more (3-8C)alkene is selected from 1 -hexene, 1 -octene and styrene. Hence, the composition of the present invention are useful as catalysts in the preparation of copolymers such as poly(ethylene-co-hexene), poly(ethylene-co-octene) and poly(ethylene-co- styrene).

[00110] In a particularly suitable embodiment, the compositions of the invention are used to copolymerise ethylene and styrene.

[00111] In a particularly suitable embodiment, the compositions of the invention are used to copolymerise ethylene and 1 -hexene.

[00112] In another embodiment, in addition to ethylene and the optional one or more (3- 10C)alkene, the polymerisation is also conducted in the presence of hydrogen. Hydrogen acts to control the molecular weight of the growing polymer or copolymer. When hydrogen is used alongside ethylene and the optional one or more (3-10C)alkene in the feed stream, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.5:1 . Suitably, when hydrogen is used alongside ethylene and the optional one or more (3-10C)alkene, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.1 :1 . More suitably, when hydrogen is used alongside ethylene and the optional one or more (3-10C)alkene, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.05:1 . When compared with analogous compositions employing the ansa-bridged cyclopentadienyl amido CGC currently preferred in industry, the compositions of the present invention show only a marginal decrease in catalytic productivity with increasing quantity of hydrogen in the feed stream. [00113] As described hereinbefore, the present invention also provides a polymerisation process comprising the step of:

a) polymerising ethylene and optionally one or more (3-10C)alkene in the presence of a composition as defined herein.

[00114] The compositions of the invention may be used as catalysts in the preparation of a variety of polymers, including polyalkylenes (e.g. polyethylene) of varying molecular weight, and copolymers. Such polymers and copolymers may be prepared by heterogeneous slurry- phase polymerisation of a monomer-containing feed stream.

[00115] In an embodiment, step a) is conducted at a temperature of 30-120 °C. Suitably, step a) is conducted at a temperature of 40-80 °C.

[00116] In another embodiment, step a) is conducted at a pressure of 1 -10 bar.

[00117] In another embodiment, step a) is conducted in a suitable solvent (e.g. hexanes or heptane).

[00118] In another embodiment, step a) is conducted in the presence of a compound suitable for scavenging moisture and oxygen. Exemplary moisture and oxygen scavengers include alkylaluminium compounds, including triethylaluminium (TEA), tnisobutylaluminium (TIBA) and methylaluminoxane (MAO). Suitably, the moisture/oxygen scavenger is triisobutylaluminium (TIBA) or methylaluminoxane (MAO).

[00119] In another embodiment, step a) may be conducted for between 1 minute and 5 hours. Suitably, step a) may be conducted for between 5 minutes and 2 hours.

[00120] In another embodiment, when the optional one or more (3-10C)alkene is not included, the process yields polyethylene homopolymer.

[00121 ] In another embodiment, the optional one or more (3-10C)alkene is one or more (3- 8C)alkene. Suitably, the quantity of the one or more (3-8C)alkene in the monomer feed stream is 0.05-10 mol%, relative to the quantity of ethylene monomers. More suitably, the one or more (3-8C)alkene is selected from 1 -hexene, 1 -octene and styrene. Hence, the process may be used to prepare copolymers such as poly(ethylene-co-hexene), poly(ethylene-co-octene) and poly(ethylene-co-styrene).

[00122] In a particularly suitable embodiment, step a) comprises copolymerising ethylene and styrene in the presence of a composition as defined herein.

[00123] In a particularly suitable embodiment, step a) comprises copolymerising ethylene and 1 -hexene in the presence of a composition as defined herein. [00124] In another embodiment, in addition to ethylene and the optional one or more (3- 1 0C)alkene, the polymerisation is also conducted in the presence of hydrogen. Hydrogen acts to control the molecular weight of the growing polymer or copolymer. When hydrogen is used alongside ethylene and the optional one or more (3-10C)alkene in the feed stream, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.5:1 . Suitably, when hydrogen is used alongside ethylene and the optional one or more (3-1 0C)alkene, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.1 :1 . More suitably, when hydrogen is used alongside ethylene and the optional one or more (3-1 0C)alkene, the mole ratio of hydrogen to total alkenes in the feed stream is 0.001 :1 to 0.05:1 . When compared with analogous compositions employing the ansa-bridged cyclopentadienyl amido CGC currently preferred in industry, the compositions of the present invention show only a marginal decrease in catalytic productivity with increasing quantity of hydrogen in the feed stream.

EXAMPLES

Fig. 7 shows the slurry polymerisation of ethylene using solid (black

square), solid MAO/ ^Et2 SB( ^tBu N, l*)TiCI ₂ (black circle) and solid (black

triangle). Polymerisation conditions: 2 bar of ethylene, 10 mg of catalyst, 30 minutes,

= 200, 1 50 mg of TIBA and 50 mL hexanes.

Fig. 8 shows an SEM image of the PE synthesised using solid MAO/ ^Me2 SB( ^tBu N,l*)TiCI ₂ . Polymerisation conditions: 2 bar of ethylene, 1 0 mg of catalyst, 70 °C, 30 minutes,

200, 150 mg of TIBA and 50 mL hexanes.

Fig. 9 shows the ethylene uptake rate for the slurry polymerisation of ethylene using solid MAO/ ^Me2 SB( ^tBu N, l*)TiCI ₂ for hydrogen response (a)) and copolymerisation of ethylene and 1 - hexene (b)). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 10 shows GPC traces for the slurry polymerisation of ethylene using solid for hydrogen response (a)) and copolymerisation of ethylene and 1 - hexene (b)). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 1 1 shows the productivity of polymerisation for various polymerisation conditions (homopolymerisation of ethylene; addition of hydrogen in homopolymerisation of ethylene; copolymerisation of ethylene and 1 -hexene; and copolymerisation of ethylene with styrene) using Solid (black column) and Solid (white

column). Productivities are in parentheses. Polymerisation conditions: 8 bar of ethylene, 25- 50 mg of catalyst, TEA and 1000 mL hexane.

Fig. 12 shows the productivity of ethylene homopolymerisation with and without hydrogen using Solid (black square) and Solid (black circle).

Polymerisation conditions: Polymerisation conditions: 8 bar of ethylene, 25-50 mg of catalyst,

Fig. 25 shows the slurry polymerisation of ethylene of a range of time using solid (black square), solid ( ) (black left triangle), solid (black triangle) and solid (black circle). Polymerisation conditions: 2 bar of ethylene, 10 mg of catalyst, 70 °C, [AI] ₀ /[Ti] ₀ = 200, 150 mg of TIBA and 50 mL hexanes.

Fig. 26 shows the ethylene uptake rate for the slurry polymerisation of ethylene using solid for a) hydrogen response: no hydrogen (black square), 1 psi hydrogen (black circle) and 2 psi hydrogen (black triangle) and b) copolymerisation of ethylene and 1 - hexene: no 1 -hexene (black square), 125 μΙ_ 1 -hexene (black circle) and 250 μΙ_ 1 -hexene (black triangle). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 27 shows GPC traces for the slurry polymerisation of ethylene using solid MAO/ ^Me2 SB( ^tBu N,l ^* )TiCl2 for a) hydrogen response and b) copolymerisation of ethylene and 1 - hexene (b)). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 28 shows GPC traces of polyethylenes synthesised using a)

Et ₂ sB( ^tBu N,l ^* )TiCl2. Polymerisation conditions: 10 mg of catalyst, 50 mL hexanes, 2 bar, 30 minutes, and 150 mg TIBA.

Fig. 29 shows Slurry-phase ethylene polymerisation uptake (left) and GPC traces (right) with with no hydrogen (black square), 1 psi hydrogen (black circle) and

2 psi hydrogen (black triangle). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 30 shows slurry-phase ethylene polymerisation activities (left) and GPC traces (right) with solid with no H ₂ (black square) and 2 psi H ₂ (black circle), and with solid

MAO/ ^Me2 SB( ^tBu N,l ^* )TiCI ₂ with no H ₂ (black triangle) and 2 psi H ₂ (down triangle). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 31 shows slurry-phase ethylene polymerisation activities (left) and GPC traces (right) with solid with no 1 -hexene (black square) and 250 μί 1 -hexene (black

circle), and with solid MAO/ ^Me2 SB( ^tBu N,l ^* )TiCI ₂ with no 1 -hexene (black triangle) and 250 μί 1 - hexene (black down triangle). Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 32 shows CEF traces with solid

Polymerisation conditions: 8 bar of ethylene, 0.05 mg of catalyst, 80 °C, 10 μηιοΙ of TIBA and 5 mL heptane.

Fig. 33 shows SEM images of the polyethylenes synthesised using solid solid and solid M

Polymerisation conditions: 2 bar of ethylene, 10 mg of catalyst, 70 °C, [AI] ₀ /[Ti] ₀ = 200, 150 mg of TIBA and 50 mL hexanes.

Fig. 34 shows scale up slurry-phase polymerisation using solid MAO/ ^Me2 SB( ^tBu N,r)TiCl2 at various H ₂ loading and copolymerisation. Polymerisation conditions: 8 bar of ethylene, 25- of TEA and 1000 mL hexanes.

[00126] Having regard to Scheme 1 shown below, ligands useful in the preparation of the were synthesised by the following procedure: In a large Schlenk, 1 equivalent of greenish oil hexamethylindene (lnd ^# )H (3.0 g, 15.0 mmol) was dissolved in 100 mL pentane to afford a greenish solution. 1 .1 equivalent of "BuLi (1 1 .0 mL, 16.4 mmol, 2.5 M in Hexanes) was added dropwise (over 30 minutes) unto the previous solution cooled to 5 ºC (ice/water bath). The solution turned slightly yellow/ green. The reaction was left stirring at 23 °C for 18 h. After 18 h, the Schlenk contains off-white solid ((lnd ^# )Li) and dark orange solution. The pentane was pumped away to afford off-white solid. THF (30 mL) was added unto the solid to afford a red solution, then this solution was added dropwise (over 15 minutes) unto a previously cooled (to 5 °C) solution of 3.0 equivalent of dichlorodimethylsilane (5.8 g, 5.5 mL, 44.9 mmol) in THF (20 mL) or another dichlorodialkylsilane. The red solution of (lnd ^# )Li instantly decolourised when reacting with the previous solution. After 15 minutes, the yellow solution was stirred for 2 h at 23 °C. Then, the THF was dried to afford lnd ^* SiMe2CI as an oil. Finally, 1 .1 equivalent of LiNH'Bu (1 .3 g, 16.4 mmol) in THF (20 mL) was added at once unto a solution of lnd ^* SiMe ₂ CI in THF (40 mL) cooled at to 5 °C (ice/water bath). The solution was stirred for 18 h, then dried, extracted with 2 χ 20 mL of pentane and finally dried to afford ^Me2 Si( ^tBu N,l ^* )H ₂ as an oil in quantitative yield.

[00127] Figures 1 and 2 respectively show the ¹ H NMR spectra for the ligands

[00128] Once the ligand has been prepared, the

were formed according to Scheme 2 shown below by the following procedure: 2.2 equivalents of "BuLi (2.7 mL, 6.7 mmol, 2.5 M in hexanes) was added dropwise, over 5 minutes, unto a solution of 1 equivalent of in THF (40 mL) cooled to 5 °C. The

solution quickly turned red. The reaction was stirred for 2 h at 25 °C. Then the solvent was dried and the sticky orange solid was washed with 2 ^χ 50 mL of pentane to afford a yellow solid in quantitative yields. Benzene (40 mL) was added into a Schlenk containing 1 equivalent of equivalent of TiCI ₄ .THF ₂ (978 mg, 2.9 mmol), the solution turned dark red. The reaction was stirred for 17 h at 25 °C. Then, the solution was thoroughly dried and the dark red solid was extracted with 2 ^χ 50 mL pentane. The pentane solution was concentrated to 20 mL and put in -30 °C freezer. A 1 ^st crop of was isolated in 26% yield (335 mg), the solution was put back in a -30 °C freezer.

[00129] Figures 3 and 4 respectively show the ¹ H NMR spectra for the CGCs and Figure 5 shows the molecular structure of

Example 2 - Synthesis of solid polymethylaluminoxane catalytic compositions

[00130] The solid polymethylaluminoxane used in this Example may be prepared via an adaptation of the optimised procedure in Kaji et al. in the US 8,404,880 B2 embodiment 1 (Scheme 3). For brevity, each synthesised solid polymethylaluminoxane is represented as solid MAO(Step 1 Al:0 ratio/Step 2 temperature in °C,time in h/Step 3 temperature in °C,time in h). Hence, the synthesis conditions outlined in Scheme 3 below would yield solid MAO(1 .2/70,32/1 00, 12).

Scheme 3 - Synthesis of solid MAOd .2/70.32/100.12)

[00131] A Rotaflo ampoule containing a solution of trimethyl aluminium (2.139 g, 2.967 mmol) in toluene (8 mL) was cooled to 15 ºC with rapid stirring, and benzoic acid (1 .509 g, 1 .239 mmol) was added under a flush of N ₂ over a period of 30 min. Effervescence (presumably methane gas, MeH) was observed and the reaction mixture appeared as a white suspension, which was allowed to warm to room temperature. After 30 min the mixture appeared as a colourless solution and was heated in an oil bath at 70 ºC for 32 h (a stir rate of 500 rpm was used). The mixture obtained was a colourless solution free of gelatinous material, which was subsequently heated at 100 ºC for 12 h. The reaction mixture was cooled to room temperature and hexane (40 mL) added, resulting in the precipitation of a white solid which was isolated by filtration, washed with hexane (2 x 40 mL) and dried in vacuo for 3 h. Total yield = 1 .399 g (71 % based on 40 wt% Al).

[00132] Having regard to figure 6, once the solid polymethylaluminoxane is prepared, different quantities of the were supported on it (the

different quantities being represented by varying aluminium to titanium ratios). In the glovebox, the solid polymethylaluminoxane and the complex are weighed out in a Schlenk tube. Toluene (50 mL) is added to the Schlenk and the reaction mixture swirled at 60 °C for one hour. The coloured solid is allowed to settle from the clear, colourless solution which is decanted, and the solid is dried in vacuo ( The product (solid ₂ and

solid is scraped out in the glovebox in quantitative yield.

[00133] Aside from the solid and solid

compositions of the invention, a comparator composition was

prepared by supporting the commercially-available ansa-bridged permethylcyclopentadienyl amido CGC shown below on solid polymethylaluminoxane using the same procedure.

Example 3 - Polymerisation studies

Ethylene homopolymerisation

[00134] The catalytic activity of the solid ( , ) and solid compositions of the invention was compared with that of the solid comparator composition in the slurry polymerisation of ethylene. Figure 7 shows that the solid

compositions of the invention demonstrated catalytic activities that were on average 4-6 times higher than for the comparator composition solid

[00135] Figure 8 shows an SEM image for a polyethylene synthesised using the solid composition of the invention. The SEM shows that the polyethylene has generally good morphology

Addition of hydroqen/co-monomer

Using solid

[00136] The solid compositions of the invention was assessed for its ability to polymerise ethylene in the presence of H ₂ (as molecular weight modifier) and 1 - hexene (as co-monomer).

[00137] Table 1 below shows the effect of increasing H ₂ pressure on the characteristics of polyethylene prepared using the solid of the invention. Table 2 below shows the effect of increasing 1 -hexene content on the characteristics of polyethylene prepared using the solid ^{M B} of the invention.

[00138] Figure 9a shows the ethylene uptake rate during ethylene polymerisation using solid as a function of increasing H ₂ pressure. Figure 9b shows the ethylene

uptake rate during ethylene-hexene copolymerisation using solid as a function of increasing hexane content. Figure 10a shows GPC traces for ethylene polymerised using solid under different H ₂ pressures. Figure 10b shows GPC traces

for ethylene polymerised using solid with varying 1 -hexene co-

monomer content.

[00139] Table 1 and figure 9a show that despite a small decrease, solid continues to be extremely active in ethylene polymerisation even under

2 psi of hydrogen. Figure 9b right shows that solid is an extremely

good incorporator of 1 -hexene, using all the co-monomers very rapidly.

[00140] Table 1 and Figure 10a shows very high molecular weight for the initial homopolymerisation, and a decrease in molecular weight with increasing hydrogen. Table 2 and Figure 10b shows very high molecular weight for the initial homopolymerisation with similar for the copolymerisation.

[00141] The catalytic performance of the solid ( ) composition of the invention was compared with that of the solid comparator

composition in a variety of different ethylene polymerisation conditions.

[00142] Figure 1 1 shows the productivity of polymerisation for various polymerisation conditions (homopolymerisation of ethylene; addition of hydrogen in homopolymerisation of ethylene; copolymerisation of ethylene and 1 -hexene; and copolymerisation of ethylene with styrene) using solid (black column) and solid

(white column). The results show that in all polymerisation conditions, the solid composition of the invention afforded higher productivities than the solid comparator composition.

[00143] Figure 12 and Table 3 below compares the catalytic performance of the solid composition of the invention and the solid

comparator composition in when ethylene is polymerised with and without hydrogen.

[00144] Table 3 and figure 12 demonstrate that an increase in hydrogen feed results, as expected, in a decrease in productivities for both catalysts. However, importantly, when the results for solid were directly compared, the solid composition of the invention afforded significantly

higher productivities than those observed with the solid comparator

composition.

[00145] With regard to Scheme 3 shown below, ligands useful in the preparation of the were synthesised by the following procedure: In a large Schlenk, 1 equivalent of greenish oil hexamethylindene (lnd ^# )H (3.0 g, 15.0 mmol) was dissolved in 100 mL pentane to afford a greenish solution. 1 .1 equivalent of "BuLi (1 1 .0 mL, 16.4 mmol, 2.5 M in hexanes) was added dropwise (over 30 minutes) unto the previous solution cooled to 5 ºC (ice/water bath). The solution turned slightly yellow/ green. The reaction was left stirring at 23 °C for 18 h. After 18 h, the Schlenk contains off-white solid ((lnd ^# )Li) and dark orange solution. The pentane was pumped away to afford off-white solid. THF (30 mL) was added unto the solid to afford a red solution, then this solution was added dropwise (over 15 minutes) unto a previously cooled (to 5 °C) solution of 3.0 equivalent of dichlorodimethylsilane (5.8 g, 5.5 mL, 44.9 mmol) in THF (20 mL). The red solution of (lnd ^# )Li instantly decolourised when reacting with the previous solution. After 15 minutes, the yellow solution was stirred for 2 h at 23 °C. Then, the THF was dried to afford lnd ^* SiMe ₂ CI as an oil. 1 equivalent of RNHLi (R = Vr (0.21 g), ⁿ Bu (0.27 g), 4-'BuPh (0.50 g), and 4- ⁿ BuPh (0.50 g)) and lnd ^* SiMe ₂ CI (1 .00 g, 3.40 mmol) were dissolved in THF (50 mL) cooled to 5 °C (ice/water bath). The solution was stirred for 2 h at 23 °C, then dried, and the product extracted in 2 χ 20 mL of pentane and dried to yield as an oil in a quantitative yield.

[00146] Figures 13, 14, 15 and 16 respectively show the ¹ H NMR spectra for the ligands

[00147] Following the preparation of the proligand

was synthesised according to the procedure shown in Scheme 4: 2.2 equivalents of "BuLi (3.0 mL, 6.7 mmol, 2.5 M in hexanes) was added dropwise to a solution of ^Me2 SB( ^R N,l ^* )H ₂ in the reaction mixture was stirred for 30 minutes at 23 °C. The reaction mixture was then dried under vacuum, and the solid product was washed with pentane (2 x 25 mL) and dried to yield a yellow solid ^Me2 SB( ^R N, r)Li ₂ . 40 mL of benzene was added to a Schlenk containing 1 equivalent of ^Me2 SB( ^R N,l ^* )Li ₂ (R= iPr (0.35 g, 1 .07 mmol), nBu (0.56 g, 1 .65 mmol), 4-tBuPh (1 .00 g, 2.40 mmol), 4-nBuPh (1 .00 g, 2.40 mmol)) and 1 equivalent of TiCI ₄ .2THF (0.36 g, 0.55 g, 0.80 g, 0.80 g respectively). The solution turned a dark red and was stirred for 23 h. The reaction mixture was then dried under vacuum, and the product was extracted in pentane. The pentane solution was placed in a - 30 °C freezer and a red solid was afforded in all cases.

Example 5 - Synthesis of solid polymethylaluminoxane catalytic compositions

[00149] The CGCs prepared in Example 4 were supported on solid polymethylaluminoxane according to the protocol discussed in Example 2. The resulting compositions (solid Example 6 - Further polymerisation studies

Ethylene homopolymerisation

[00150] The catalytic activity of the solid compositions of the invention

prepared in Example 5 were compared in the slurry phase polymerisation of ethylene. Figures 25 and 26 (demonstrating temperature and time dependence on polymerisation activity) demonstrate that all of the solid MAO/CGC compositions of the invention show ethylene polymerisation activity, with aniline-based CGC compositions tending to have a lower activity than aliphatic CGC compositions.

Addition of hydroqen/co-monomer

[00151] The effect of hydrogen addition on the ability of solid to

polymerise ethylene was investigated. The results are outlined in Table 4 below, and in figure 26a.

[00152] The effect of comonomer addition (1 -hexene) on the ability of solid MAO/ ^Me2 SB( ^iPr N,l ^* )TiCI ₂ to polymerise ethylene was investigated. The results are outlined in Table 5 below, and in figure 26b.

[00153] The effect of hydrogen/comonomer addition on the ability of other compositions of the invention to polymerise ethylene was investigated. Figure 28 shows that solid and solid gave ultra-high molecular weight

polyethylenes at 50 ºC (Mv above 800 kDa) and moderate molecular weight polyethylenes at 80 °C (At around 280 kDa). Figure 29 shows solid demonstrated good

response towards hydrogen with relatively high molecular weights and solid

M show very high activities followed by quick deactivation with increasing

1 -hexene addition (figure 32). The CEF demonstrated very high incorporation of the comonomer (figure 33).

[00154] While specific embodiments of the invention have been described herein for the purpose of reference and illustration, various modifications will be apparent to a person skilled in the art without departing from the scope of the invention as defined by the appended claims.