CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims priority from U.S. provisional patent application no.

62/170,237 that was filed on June 3, 2015, the entire contents of which are hereby

incorporated by reference.

REFERENCE TO GOVERNMENT RIGHTS

[0002] This invention was made with government support under 2010-DN-077-AR1042 awarded by the Department of Homeland Security. The government has certain rights in the invention.

BACKGROUND

[0003] Room -temperature semiconducting X-ray and y-ray detectors are crucial in a number of technologies, including biomedical imaging, national security and spectroscopy instrumentation; however, the high cost of commercial detectors has severely limited their broad application. Finding low cost room -temperature radiation detectors is a complex, multifaceted challenge. First of all, there is a limited number of potential detector materials due to the low availability of heavy element compounds possessing suitable optical band gaps (1.5 - 3.0 eV) and high resistivity. For example, the heavy chalcogenides, HgQ (Q = Se and Te), which are isostructural with CdTe and the rock salt Pb >, possess nearly zero or very narrow energy gaps. The second problem arises from the complex physics and chemistry of compound semiconductors in comparison to their elemental counterparts, such as Si and Ge. Third, many compounds with attractive bulk physical properties, such as a-HgS and Til, exhibit phase transitions hindering the growth of high quality single crystals. For compounds suitable for crystal growth, e.g. the commercial benchmark Cdo.9Zno _.1 Te (CZT), the detector material suffers from stoichiometric imbalance and Te phase precipitation rooted in its intrinsic chemical properties, which have prevented its low cost production.

SUMMARY

[0004] Methods and devices for detecting the incident gamma and/or x-ray radiation are provided. [0005] One embodiment of a method for the detection of gamma and/or x-ray radiation comprises the steps of: exposing a material comprising an inorganic compound having the formula A ₂ P ₂ X6, where A represents Pb or Sn and X represents S or Se, to incident gamma radiation, x-ray radiation, or a combination thereof, wherein the material absorbs the incident radiation and electron-hole pairs are generated in the material; and measuring at least one of the energy or intensity of the absorbed incident radiation by detecting the generated electrons and/or holes.

[0006] One embodiment of a detector for gamma and/or x-ray radiation comprises: a material comprising an inorganic compound having the formula A ₂ P ₂ X ₆ , where A represents Pb or Sn and X represents S or Se; a first electrode in electrical communication with the material; a second electrode in electrical communication with the material, wherein the first and second electrodes are configured to apply an electric field across the material; and a detector configured to measure a signal generated by electron-hole pairs that are formed when the material is exposed to incident gamma radiation, x-ray radiation, or a combination thereof.

[0007] Also provided are single crystals of Pb ₂ P ₂ Se ₆ having a surface area of at least 5 mm ² , wherein the single crystals do not contain any impurity at a concentration of greater than 2 ppm wt, other than impurities that are isoelectronic with Se or with Pb.

[0008] Other principal features and advantages of the invention will become apparent to those skilled in the art upon review of the following drawings, the detailed description, and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] Illustrative embodiments of the invention will hereafter be described with reference to the accompanying drawings.

[0010] FIG. 1. Crystal structure of Pb ₂ P ₂ Se ₆ .

[0011] FIG. 2. Temperature profile of a furnace used in the crystal growth of Pb ₂ P ₂ Se ₆ in Example 1.

[0012] FIG. 3 A. Differential thermal analysis of Pb ₂ P ₂ Se ₆ between 650°C and 850°C, measured at a rate 1 °C/min. FIG. 3B. DTA analysis of Pb ₂ P ₂ Se ₆ using two consecutive cycles of heating and cooling above 600°C. FIG. 3C. Thermal conductivity of Pb ₂ P ₂ Se ₆ up to 400°C, measured at a rate 1 °C/min. FIG. 3D. Heat capacity and thermal diffusivity of Pb ₂ P ₂ Se ₆ . [0013] FIG. 4. Electronic absorption spectrum obtained from UV-Vis diffuse reflectance measurement on ground Pb ₂ P ₂ Se ₆ crystals.

[0014] FIG. 5A. Electronic band structure of Pb ₂ P ₂ Se ₆ within the sX-LD A scheme. FIG. 5B. Projected partial density of states (PDOS).

[0015] FIG. 6. Electrical resistivity of Pb ₂ P ₂ Se6 with (circles) and without (squares) Ag x-ray.

[0016] FIG. 7A. Unresolved ⁵⁷ Co γ-ray spectroscopic responses of Pb ₂ P ₂ Se ₆ crystal samples. FIG. 7B. ⁵⁷ Co γ-ray spectroscopic responses of a Pb ₂ P ₂ Se ₆ single crystal wafer at 600V and 800V bias, compared to that of a SPEARS CZT detector. FIG. 7C. Partially resolved ⁵⁷ Co γ-ray spectra of Pb ₂ P ₂ Se6 crystals compared with that of a SPEAR detector (CZT), based on channel number. FIG. 7D. Partially resolved ⁵⁷ Co γ-ray spectra of Pb ₂ P ₂ Se ₆ crystals compared with that of a SPEAR detector (CZT), based on energy.

[0017] FIG. 8. Experimental powder X-ray diffraction pattern of Pb ₂ P ₂ Se6 compared to a simulated pattern.

[0018] FIG. 9. Schematic diagram of a vacuum sealing configuration.

[0019] FIG. 10A. Electronic band structure of Pb ₂ P ₂ S ₆ 160-atom supercells: defect-free. FIG. 10B. Electronic band structure of Pb ₂ P ₂ S6 160-atom supercells: containing one interstitial oxygen atom. FIG. IOC. Electronic band structure of Pb ₂ P ₂ S6 160-atom supercells: containing 1 oxygen atom replacing Se atom. Shades of bands reflect contribution from O p states.

[0020] FIG. 11. UV-Vis transmittance experiments measuring the band gap of Pb ₂ P ₂ Se6 samples with (PE1079) and without (PE1123) secondary phase precipitates.

[0021] FIG. 12A. The photo-electrical responses of two Pb ₂ P ₂ Se ₆ samples with observable precipitates. FIG. 12B. The photo-electrical responses of two Pb ₂ P ₂ Se ₆ samples without observable precipitates. These samples were illuminated by a 50 mW, 405 nm CW laser at room temperature.

[0022] FIG. 13 A. Power dependence at 15.5 K using 1.6 mW, on the photoluminescence spectra of a Pb ₂ P ₂ Se ₆ sample. FIG. 13B. Temperature dependence at 15.5 K using 1.6 mW, on the photoluminescence spectra of a Pb ₂ P ₂ Se6 sample.

[0023] FIG. 14A. Plot of integrated PL intensity vs. 1000/T collected using 1.6 mW laser power for excitation for the three peaks observed in Pb ₂ P ₂ Se ₆ . FIG. 14B. Plot of integrated FWHM vs. T collected using 1.6 mW laser power for excitation for the three peaks observed in Pb ₂ P ₂ Se ₆ . The solid lines are fittings of the data to Eq.1, while the dotted line is a guide to the eye.

[0024] FIG. 15. Thermodynamic stability of the Pb ₂ P ₂ Se ₆ phase determined from the calculated ranges of chemical potentials under thermodynamic equilibrium with competing phases.

[0025] FIG. 16. Temperature profile of a Bridgman growth measured at the tip and heel of a sample.

[0026] FIG. 17. A typical spectroscopic response from a Pb ₂ P ₂ Se ₆ sample under ⁵⁷ Co source radiation. The data were collected under 400V (bottom spectrum), 450V (second to bottom spectrum) and 500V (second to top spectrum) bias and compared to the background at 500V (top spectrum).

DETAILED DESCRIPTION

[0027] Methods and devices for detecting incident radiation, such as incident x-rays or gamma-rays, are provided. The methods and devices use high purity, high quality single- crystals of inorganic semiconductor compounds having the formula Α ₂ Ρ ₂ Χ ₆ , where A represents Pb or Sn and X represents S or Se, as photoelectric materials.

[0028] The compounds desirably have a band gap of at least 1.5 eV. This includes compounds having a band gap of at least 1.6 eV and further includes compounds having a bandgap of at least 1.8 eV. For example, in some embodiments the compounds have a band gap in the range from about 1.6 eV to about 3 eV. Methods of determining the bandgap of a material are described in the Examples.

[0029] Detector-grade materials comprising the compounds can be grown with high chemical purity and high crystal quality. For example, some embodiments of the materials do not contain any impurity element at a concentration of greater than 2 ppm wt., other than impurity elements that are isoelectronic with the A element or the X element in the inorganic compound. This includes embodiments of the materials that do not contain any impurity element at a concentration of greater than 1.5 ppm wt., other than impurity elements that are isoelectronic with the X element in the inorganic compound. Methods of making detector- grade materials are demonstrated in the Examples below, using Pb ₂ P ₂ 2 ₆ compounds as an illustration. The methods described in the Examples can be adapted to make detector-grade materials comprising the other inorganic semiconductor compounds, as well.

[0030] The high quality, low impurity nature of the compounds is reflected in their high electrical resistivities. For example, some embodiments of the compounds have an electrical resistivity at 23 °C of at least 10 ⁹ Ω · cm. This includes compounds having an electrical resistivity at 23° C of at least 10 ¹⁰ Ω · cm and further includes compounds having an electrical resistivity at 23° C of at least 10 ¹¹ Ω · cm. Methods of determining the electrical resistivity of a material are described in the Examples.

[0031] In some embodiments of the methods and devices, the inorganic compound is a lead chalco-phosphate compound having the chemical formula Pb ₂ P ₂ (¾ (where Q = S or Se) or its isostructural tin chalco-phosphates having the chemical formula Sn ₂ P ₂ g ₆ (where Q = S or Se).

[0032] The two isostructural Pb ₂ P ₂ 2 ₆ compounds crystallize in the .P2i/c space group with a = 6.606 k, b = 7.464 A, c =11.346 A, β= 124.10° for Pb ₂ P ₂ S ₆ and a = 6.910 A, b = 1.670 A, c =11.816 A, β = 124.35° for Pb ₂ P ₂ Se ₆ . As illustrated in FIG. 1, the Pb ₂ P ₂ Se ₆ is a salt of Pb ²⁺ cations with ethane-like [P ₂ Se ₆ ] ^4" anions. The Pb ₂ P ₂ S ₆ and Pb ₂ P ₂ Se ₆ display yellow and dark red color, respectively, reflecting their large optical band gaps. Although both Pb ₂ P ₂ S ₆ and Pb ₂ P ₂ Se ₆ have attractive optical properties, the selenide with an average atomic number (Z) of 39.8 and a density of 6.14 g em ^"3 is more suitable for high energy x-ray and y-ray applications. The attenuation coefficient of Pb ₂ P ₂ Se ₆ is greater than that of CZT, especially in the high energy region, which relaxes the requirement of high mobility -life time product (μτ) for an effective γ-ray detector. For example, for ¹³⁷ Cs radiation at 662 keV, the attenuation length is 2.3 cm for CZT and only 1.8 cm for Pb ₂ P ₂ Se ₆ . In this case, the necessary distance for the charge carriers to travel to the electrodes is shorter in a Pb ₂ P ₂ Se ₆ detector reducing the probability of trapping.

[0033] In addition to their bulk physical properties, another attractive feature of the present inorganic compounds as detector materials is their potential for low cost production. Compared to the commercial benchmark, CZT - an alloy of cadmium telluride and zinc telluride, the stoichiometric ternary compounds, A ₂ P ₂ X ₆ , with their simpler phase diagrams, have fewer technological and engineering challenges in terms of crystal growth and scale up development. More importantly, the elements in the compounds are abundant and widely used, while their robust chemical and physical properties allows them to be easily extracted, isolated and purified. The availability of high purity starting materials implies less

complicated purification processes.

[0034] One aspect of the invention provides devices for the detection of incident radiation. In some embodiments the devices comprise: a material comprising an inorganic compound, of the type described herein, wherein the material is capable of absorbing incident radiation and generating electron-hole pairs; a first electrode in electrical communication with the material; and a second electrode in electrical communication with the material. In such devices the first and second electrodes are configured to apply an electric field across the material. The devices can further comprise one or more additional electronic components configured to measure a signal generated by the electron-hole pairs that form upon exposure of the material to the incident radiation. The incident radiation can comprise wavelengths in the gamma region of the electromagnetic spectrum (i.e., wavelengths in the range from about 1 x 10 ^~10 to about 2 ^χ 10 ^~13 meters), in the x-ray region of the electromagnetic spectrum (i.e., wavelengths in the range from about 0.01 to 10 nanometers), or both.

[0035] Unless otherwise indicated, the quantitative chemical and physical properties recited herein refer the values of those properties at room temperature and atmospheric pressure.

EXAMPLES

[0036] Example 1. Basic Method of Pb^P^Se^ Growth and Processing

[0037] This example demonstrates the crystal growth and optical and electrical properties, as well as the y-ray response of Pb ₂ P ₂ Se6 single crystals. Other physical properties of this compound, such as thermal behavior and mechanical properties are also discussed with respect to its utility as a low cost detector material.

[0038] Synthesis, Crystal Growth and Process

[0039] The Pb ₂ P ₂ Se6 compound was prepared from as-purchased commercial elements without any further purification. The samples for exploratory crystal growth experiments and bulk physical property measurements (thermal, hardness) were prepared from lower purity starting materials (99.99%, wt), while the samples subjected to electrical measurements and gamma-ray detection tests were grown from high purity elements (99.999%+, wt). As starting materials, lead metal, red phosphorus and elemental selenium are chemically robust and physically stable substances, so they can be handled in the ambient environment. Although no additional purification was performed on the commercial starting materials, other than the removal of the surface oxide on the lead rods, great care was taken during the sample preparation to minimize the materials' exposure to possible sources of impurities, such as surfaces and containers. Following the same guideline, the synthesis and crystal growth of Pb ₂ P ₂ Se ₆ were performed in one single ampoule to reduce the chance of contamination.

[0040] Studies of Pb ₂ P ₂ Se6 for other applications have demonstrated the growth of large single crystals by the Bridgman method. (See, I. Martynyuk-Lototska, O. Mys, B.

Zapeka, M. Kostyrko, A. Grabar, R. Vlokh, Appl. Opt. 2014, 53, B103 and O. Mys, I.

Martynyuk-Lototska, A. M. Kostruba, A. Grabar, R. Vlokh, Ukr. J. Phys. Opt. 2012, 13, 177.) The Pb ₂ P ₂ Se6 compound exhibits a rather high melting point at 798°C, which creates a challenge for Bridgman crystal growth in terms of maintaining stable temperature zones. (See, I. P. Prits, M. V. Potorij, Y. V. Voroshilov, Ukr. Khim. Zh. 1989, 55, 135.) A high temperature two-zone furnace was selected for the Bridgman growth in order to achieve the desired temperature stability. Because of the relatively short zones of the furnace (hot and cold zones were 125 mm long), a large thermal stress was created when the bottom of the crystal started to quickly cool down as it moved out of the heated part of the cold zone (see FIG. 2 for the temperature profile). Such a situation is more pronounced when growing longer crystal ingots (> 100mm). The large thermal stress caused multiple cleavages perpendicular to the growth direction. These cleavages were spaced closer to the bottom of the ingot, indicating a greater temperature change towards the bottom the furnace.

[0041] The above-discussed crystal growth process yielded sizable, crack-free segments of crystal ingots with good reproducibility. These ingots were subsequently cut and polished into detector samples. A Pb ₂ P ₂ Se6 single crystal wafer less than 1 mm thick appeared transparent under intense incandescent light. When examined under polarized light, the sample exhibited uniform color change upon rotation, illustrating its single crystalline nature.

[0042] Thermal and Mechanical Properties

[0043] Although the crystal growth technique was simple at this stage, it was able to produce sizable, high quality crystal ingots of Pb ₂ P ₂ Se ₆ because of its well behaved thermal properties. The Differential Thermal Analysis (DTA) analysis performed on the

polycrystalline Pb ₂ P ₂ Se6 sample revealed only one endothermic peak at 812°C and one exothermic peak at 778°C (FIG. 3 A), indicating a congruent melting behavior (see FIG. 3B for the full, two heat/cool cycle DTA analysis). The discrepancy between the DTA data and the reported melting point is likely caused by the fast heating and cooling rate (l°C/min) used during the DTA analysis. (See, I. P. Prits, M. V. Potorij, Y. V. Voroshilov, Ukr. Khim. Zh. 1989, 55, 135.) The intense and sharp exothermic peak observed at 778°C implies the Pb ₂ P ₂ Se ₆ system favors a highly crystalline form upon solidification. As a result, during the crystal growth process, a large amount of heat needs to be conducted away from the liquid- solid interface through the just-formed crystalline material.

[0044] The thermal conductivity of an as grown Pb ₂ P ₂ Se6 single crystal along the growth direction was measured up to 400°C (FIG. 3C, for heat capacity and thermal diffusivity see FIG. 3D). It is worth noting that the Pb ₂ P ₂ Se ₆ exhibited an almost temperature- independent thermal conductivity between room temperature (i.e., -23 °C) and 300°C, in agreement with earlier measurements. (See, V. M. Rizak, K. Al'-Shoufi, I. M. Rizak, I. P. Prits, Y. M. Vysochanskii, V. Y. Slivka, Ferroelectrics 1994, 155, 323.) At temperatures above 300°C, the thermal conductivity of Pb ₂ P ₂ Se ₆ increased slightly with rising temperature. At 400°C, the thermal conductivity of Pb ₂ P ₂ Se ₆ was 0.90 ± iW m ^'1 ! ^'1 , which is comparable to that of CZT (1 W m^ K ^"1 ) and higher than that of TIBr (0.52W m ^"1 K ^"1 ). (See, M. E.

Rodriguez, J. J. Alvarado-Gil, I. Delgadillo, O. Zelaya, H. Vargas, F. Sanchez-Sinencio, M. Tufino- Velazquez, L. Banos, Phys. Status Solidi A 1996, 158, 67 and R. J. Gummow, I.

Sigalas, Int. J. Thermophys. 1987, 8, 607.) With a further improved Bridgman technique, the higher thermal conductivity of Pb ₂ P ₂ Se6 in combination with its congruent melting behavior promises better single crystal yield and faster growth speeds, which are highly desirable material attributes for cost-effective bulk crystal production.

[0045] Another attractive property of a Pb ₂ P ₂ Se6 crystal is its mechanical hardness. For soft materials, waferization and mechanical polishing performed during detector fabrication could introduce more defects that deteriorate its performance. Micro-indentation

measurements revealed a Knoop hardness of 106 ± 3kg- mm ^"2 for Pb ₂ P ₂ Se ₆ , which is significantly harder than CZT (60-80kg mm ^"2 ) and TIBr (12kg mm ^"2 ). (See, A. Owens, A. Peacock, Nucl. Instrum. Methods Phys. Res., Sect. A 2004, 531, 18; S. Adachi, Properties of Group-IV, III-V and II-VI Semiconductors, John Wiley & Sons, Ltd, 2005 and A. V.

Churilov, G. Ciampi, H. Kim, W. M. Higgins, L. J. Cirignano, F. Olschner, V. Biteman, M. Minchello, K. S. Shah, J. Cryst. Growth 2010, 312, 1221.) The superior hardness

demonstrates that simpler post-growth processes and device fabrication methods can be implemented for the development of Pb ₂ P ₂ Se ₆ .

[0046] Optical Properties and Electronic Structure Calculations [0047] The optical band gap of Pb ₂ P ₂ Se6 was determined to be 1.88 eV by UV-Vis diffuse reflectance spectroscopy using ground crystals (FIG. 4). (See, S. Johnsen, Z. Liu, J. A. Peters, J.-H. Song, S. Nguyen, C. D. Malliakas, H. Jin, A. J. Freeman, B. W. Wessels, M. G. Kanatzidis, J. Am. Chem. Soc. 2011, 133, 10030). The observed optical band gap of Pb ₂ P ₂ Se ₆ was found in agreement with the ~ 2eV indirect band gap predicted by the electronic structure calculations (FIG. 5A). Interestingly, the theoretical calculations also revealed dominant contributions of Pb and Se based orbitals to the density of state (DOS, FIG. 5B) at the vicinity of the Fermi level. Although the tetravalent phosphorus atoms play a limited role in the direct Pb-Se bonds, they produce strong covalent P-Se bonding in the [P ₂ Se6] ^4" cluster, which in turn modulates Pb-Se bond strength to define the observed large band gap.

[0048] Electronic Transport and Detector Properties

[0049] The room temperature electrical resistivity of Pb ₂ P ₂ Se ₆ was in the range of 1 ^χ 10 ¹⁰ Ω-cm. This value is comparable to CZT and well above the threshold requirement of 10 ⁸ — 10 ⁹ Ω-cm for effective room temperature y-ray detector materials. With such a high resistivity, a Pb ₂ P ₂ Se ₆ detector is expected to exhibit low dark current, so that higher bias can be applied to increase detector resolution and decrease readout time.

[0050] In addition to the high resistivity, when the Pb ₂ P ₂ Se6 samples were subjected to 40kV/10mA Ag X-ray radiation, they produced a threefold increase in current under a 400V bias (FIG. 6). This observation illustrates the good photo-conductivity properties of Pb ₂ P ₂ Se ₆ under hard radiation.

[0051] In terms of the detector performance, the Pb ₂ P ₂ Se6 compound was still at a very early stage of development. The crystallinity and purity of the Pb ₂ P ₂ Se6 samples can vary depending on their position in a multi cm long crystal ingot. In general, the tip part (first to solidify) of a Bridgman-grown crystal ingot exhibited lower crystallinity due to the competition between multiple seeds. The heel portion (last to solidify) of the same crystal ingot, on the other hand, retained more impurities. As a result, the spectroscopic performances of the extracted single crystal samples depended on their positions along the ingot.

Nevertheless, it was found that Pb ₂ P ₂ Se ₆ samples can exhibit spectroscopic responses under gamma-radiation (FIG. 7A), with resolvable spectroscopic features. FIG. 7B presents two pulse height spectra of ⁵⁷ Co y-radiation generated by a Pb ₂ P ₂ Se6 single crystal wafer at 600V (top) and 800V (bottom) bias. At 600V, the Pb ₂ P ₂ Se ₆ wafer produced a ⁵⁷ Co y-ray spectrum with resolved features that are comparable to those in a CZT-generated spectrum. At an increased bias of 800V, the spectrum from the same Pb ₂ P ₂ Se ₆ sample became more convoluted, while a shift of peak maxima (position in detector channel number) could be observed, elucidating the sample's response to the change in bias voltage.

[0052] In addition to these responses, several Pb ₂ P ₂ Se ₆ crystals were able to generate partially resolved ⁵⁷ Co y-ray spectra. FIGs. 7C and 7D demonstrate two pulse height of a ⁵⁷ Co source which emits 14.4, 122.1, and 136.5 keV y-rays with relative intensities of 0.11, 1, and 0.12, respectively. The spectrum in FIG. 7C shows two major peaks matching the 122.1, and 136.5 keV lines of the ⁵⁷ Co spectrum from CZT, while other minor features were too weak to be identified. In FIG. 7D, the Pb ₂ P ₂ Se ₆ sample resolved the main peak at and 122.1 keV with a resolution of -10 keV FWHM. Due to the relatively low resolution, the 136.5 keV radiation was only partially resolved as a shoulder of the 122.1 keV signal. The typical Compton scattering feature at - 80 keV was also recorded and found to match those recorded by typical CZT detectors. (See, G. R. Gilmore, Practical Gamma-Ray Spectrometry, John Wiley & Sons, Ltd, 2008.) The small peak at - 98 keV could be attributed to the Pb atom escape line, which is intrinsic to the composition. The broad peak between 30 and 40 keV is believed to be related to a breakdown current formed under the large electric field, which also contributes to the high background at low energy. The 14.4 keV γ-radiation signal may be convoluted with the large background forming a broad shoulder feature.

[0053] The spectroscopic response at different applied voltages allowed for the evaluation of the mobility-lifetime products of electron carriers using a methodology developed by Ruzin et al, which employs a mollified Hecht equation (equation (a)). (See, A. Ruzin, Y.

Nemirovsky, J. Appl. Phys. 1997, 82, 4166 and K. Hecht, Z. Physik 1932, 77, 235.) This method is based on spectroscopy measurements of the X- or y-ray photons. The mobility- lifetime products for electrons was derived from the analysis of the maximal charge collection efficiency (CCE) under each bias voltage applied to the sample, specifically, the channel location that had the maximum photon counts under a given bias voltage. By varying the applied bias voltage V, the maximum response count channel Ch(V) varied accordingly. The charge collection efficiency (CCE) is linked to parameter J ⁷ , the bias voltage applied to the sample as:

CCEiV) = (a),

where J (0.171 cm) is the thickness of the sample. With negative bias applied to the surface facing the radiation source, electron carriers were collected and the maximum response count channel under the 122.1 keV characteristic peak was recorded. By using the maximum centroid channel numbers Chi (9910) and Chi (12747) under the two bias voltages, VI = 400 V, and V2 = 600 V, and equation (a), the estimated lifetime mobility product of the sample was 3.5xl0 ^"5 cm ² /V for electron carriers. Multiplying by the applied external electric field under 600 V bias, 600 V/ 0.171 cm = 3509 V/cm, the drift length was estimated to be 1.23 mm under 600 V bias. Under 400 V bias, it was estimated to be 0.82 mm. The parameter Const is the maximum channel corresponding to the limit reachable, estimated to be 23,618. This method was tested by measuring a CZT sample under a ⁵⁷ Co radiation source. The mobility lifetime product for electron carriers of the CZT sample (4x4x2 mm ³ ) from eV Products was measured using the same method. Two bias voltages, 200 V and 300 V, were used. The value was estimated to be 5.8x l0 ^"3 cm ² /V , which is in good agreement with previous measurements.

[0054] Conclusion

[0055] The heavy metal chalco-phosphate, Pb ₂ P ₂ Se ₆ , is a suitable semiconductor for X- ray and/or y-ray detectors. Here, procedures for bulk synthesis, crystal growth and sample processing have been described. Large single crystals of Pb ₂ P ₂ Se ₆ with high resistivity were grown by vertical Bridgman method and subsequently waferized and processed for physical property measurements and y-ray detector testing. The optical band gap of bulk Pb ₂ P ₂ Se ₆ is 1.88 eV, and is indirect in nature as indicated by the electronic structure calculations. The Pb ₂ P ₂ Se ₆ crystal samples exhibited relatively low mobility-lifetime products, but despite this, they exhibited good photo-current response towards 40 keV Ag X-ray and were able to produce a resolved ⁵⁷ Co y-ray spectrum.

[0056] The Pb ₂ P ₂ Se ₆ compound is a useful cost-effective hard radiation detector material because of its robust chemical and physical properties. The availability and stability of the starting materials allows for a simple preparation of functioning detector samples. Its thermal behavior implies less technological and engineering challenges in terms of crystal growth and scale up. Finally, the good mechanical hardness of Pb ₂ P ₂ Se ₆ enables easy adaption to existing post-growth processes and detector fabrication techniques

[0057] Experimental section [0058] Synthesis and Crystal Growth: Polycrystalline samples of Pb ₂ P ₂ Se6 were prepared from lead metal (rod, Alfa Aesar, various purity), selenium (shots, Alfa Aesar, various purity) and red phosphorous (pieces, Alfa Aesar, various purity). During the sample preparation, lead metal was etched with 5% HN0 ₃ solution then rinsed with pure ethanol in order to remove the surface oxide. Sixty grams of stoichiometric starting materials were loaded into tapered fused silica ampoules (13 mm ID, 1 mm wall thickness and 200 mm in length) and sealed under vacuum (~10 ^~4 Torr). The samples were heated to 950°C over 72 hours and held at the maximum temperature for 12 hours before they were cooled to room temperature over 12 hours.

[0059] The as obtained polycrystalline samples, with their original silica ampoules intact, were subsequently used for single crystal growth in a modified vertical two-zone Bridgman furnace equipped with a geared dropping mechanism. The temperature of the hot zone was 850°C, while the cold zone was 650°C. The crystal growth was carried out with a lowering rate of 0.5 mm per hour. Once the samples were completely lowered into the cold zone, they were annealed in situ at 650°C for 24. Finally, the grown crystals were cooled to room temperature over 24 hours. The temperature gradient in the two-zone Bridgman furnace was estimated to be 30°C/cm. Segmented crystal ingots were obtained from the crystal growth. The solid crystal ingots naturally fracture in the direction perpendicular to the thermal gradient, forming smaller segments toward the tip of the tapered ampoule and largest segments (up to 25 mm long) at the heel part. The compositions and phase purity of the Pb ₂ P ₂ Se ₆ crystals were verified by powder X-ray diffraction (FIG. 8).

[0060] X-ray Diffraction studies: -ray powder diffraction experiments were conducted on a silicon-calibrated CPS 120 Inel powder X-ray diffractometer with radiation. The data were collected in an angular range of 0-120° 2Θ with a scan step 0.029°. Experimental powder XRD patterns were compared to the simulated diffraction pattern based on the reported the single crystal structure. (See, H. Yun, J. A. Ibers, Acta Crystallogr., Sect. C: Cry st. Struct. Commun. 1987, 43, 2002.) The powder XRD patterns showed good agreement with the calculated XRD patterns from the single crystal models. To verify the crystal structure, single-crystal X-ray diffraction was performed at 298(2) K on extracted Pb ₂ P ₂ Se ₆ single crystals with a Stoe image plate diffraction system (IPDS) II diffractometer using graphite- monochromated Mo Ka radiation (λ = 0.71073). Data process and numerical absorption corrections were performed using Stoe X-Area software. (See, STOE & Cie GmbH, Darmstadt 2006.) Structures were solved by direct methods and refined by full-matrix least-squares on F (all data) using the SHELXTL software suite. (See, G. M. Sheldnck, University of Gottingen, Gottingen, Germany 1997.) The crystallographic and structural information is summarized in Tables 1, 2 and 3.

Table 1. Crystallographic refinement data for Pb ₂ P ₂ Se6 at 298(2) K

Formula Pb ₂ P ₂ Se ₆

Formula Mass (amu) 950.08

Space group P2 c

a (A) a = 6.902(1)

b (A) b = 7.655(2)

c (A) c = 11.791(3)

a (°) 90

b (°) 124.33(2)

g (°) 90

Volume (A ³ ) 514.4(2)

Z 2

Crystal size (mm) 0.20x0.18x0.15

p (calculated) (g/cm^) 6.134

Absorption coefficient (mm ^~ l) 54.153

F(000) 796

Θ (deg) 3.98-33.40

Index ranges -10 < h < 10, -11 <k < 11, -18 < 1 < li

Reflections collected 9916

Independent reflections 1980

Completeness to Θ = 33.40° 99.2 %

Data / Restraints / Parameters 1980 / 0 / 46

GOF on F ² 1.184

R/wR (I > 2σ(Ι)) 0.0494/0.0829

R/wR (all data) 0.0658/0.0868

Largest diff peak and hole (e. A ^~ 3) 1.564 and -2.714

Table 2. Atomic positions and isotropic displacement factors for Pb ₂ P ₂ Se ₆

Atom X y z Wyckoff U _eq (A ² ) Occupancy

Pb 0.28642(7) 0.38694(5) 0.24862(4) 4e 0.0249(1) 1

Sel 0.1272(2) 0.0027(1) 0.23349(8) 4e 0.0137(2) 1

Se2 0.2193 (2) 0.7020(1) 0.04232(8) 4e 0.0142(2) 1

Se2 0.3883 (2) 0.1925(1) 0.05433(8) 4e 0.0158(2) 1

P 0.6227(4) 0.39246(3) 0.06340(2) 4e 0.0105(3) 1

Table 3. Selected Bond Lengths (A) and Angles (°) for Pb ₂ P ₂ Se ₆ .

Atoms Value

Bond Lengths

Pb - Se 3.108(1)

3.109(1)

3.127(1)

3.166(1)

3.199(1)

3.268(1)

P - P 2.227(4)

P - Se 2.190(2)

2.185(2)

2.183(2)

Angles

Se - P - Se 115.46(9)

114.4(1)

109.45(9)

Se - P - P 106.4(1)

102.9(1)

107.3(1)

[0061] Waferization and polishing: The larger Pb ₂ P ₂ Se ₆ crystal segments were cut into wafers of 1-2 mm thick in the direction perpendicular to the growth direction using a Struers Accutom-50 waferizing saw equipped with a 300//m wide diamond-impregnated blade. The sample surface was polished by hand with successively finer grit SiC grinding papers up to 3 /mi particle size. Then the fine polishing was achieved mechanically with 0.05 mi suspended AI2O3 slurry. After polishing, the processed Pb ₂ P ₂ Se ₆ crystals exhibited mirror like smooth surfaces. The processed samples were usually irregular shaped due to fracturing occurred during polishing. The average surface area of the wafers ranged from 3 mm><3 mm up to 5 mmx 10 mm, while the thickness varied between 1 mm to 2 mm.

[0062] Differential Thermal Analysis: Differential thermal analysis (DTA) was performed on a Shimadzu DTA-50 thermal analyzer. Around 20 mg of ground crystalline samples were sealed in a fused silica ampoule under vacuum. A similar amount of α-Α1 ₂ 0 ₃ powder sealed in a separated ampoule was used as a reference. The samples were heated and cooled to a maximum temperature of 900°C. A heating/cooling rate of 5°C/min was used up to 600°C, while a slower rate of l°C/min was used between 600°C to 900°C. The melting and crystallization points were taken as the temperatures of the endothermic and exothermic peaks, respectively.

[0063] Optical Characterization: In order to determine the optical band gap of Pb ₂ P ₂ Se ₆ , optical diffuse reflectance measurements were employed. The measurements were performed at room temperature using a Shimadzu UV-3101-PC double-beam, double-monochromator spectrophotometer. Data were collected in the range of 200-2500 nm with BaS0 ₄ as a 100% reflectance standard. The finely ground crystalline sample was spread on a compacted substrate of BaS0 ₄ powder. The generated reflectance versus wavelength data was converted to absorbance data using the Kubelka-Munk equation so the optical band gap can be estimated. (See, S. P. Tandon, J. P. Gupta, Phys. Status Solidi B 1970, 38, 363.)

[0064] Thermal Conductivity: A selected single crystal wafer (6mmx6mmx2mm) was subjected to thermal conductivity measurement. A thin layer of graphite coating was applied to the sample to minimize errors from the emissivity of the material. Total thermal conductivity, /c, was calculated using the following equation:

K = aC _p d, (b) where a, C _p and d are the thermal diffusivity coefficient, the specific heat and the density, respectively. The thermal diffusivity coefficient (a) was measured using the laser flash diffusivity method in a Netzsch LFA457 Laser Flash Apparatus, while the specific heat capacity (C _p ) of Pb ₂ P ₂ Se ₆ was indirectly derived using a standard (Pyroceram 9606) in the range of 300-673K. A Cowan model with pulse correction was applied to the analysis of the thermal diffusivity data, where cooling cycles gave reproducible values for each sample. [0065] Hardness measurements: A Pb ₂ P ₂ Se ₆ single crystal was analyzed via the micro- indentation measurements using a Struers Duramin 5 automated micro hardness tester equipped with a Knoop tip. Indentations were made with a 25 g load for 5 seconds at random locations on the surface of a fine polished Pb ₂ P ₂ Se ₆ crystal wafer. The indentations were subsequently evaluated using a calibrated, built-in high resolution microscope to extract the Knoop hardness values for each indentation trace. (See, F. Knoop, C. G. Peters, W. B.

Emerson, J. Res. Natl. Bur. Stand. (U. S.) 1939, 23, 39.)

[0066] Transport and Detector Property Measurements: Direct current resistivity was measured in the dark using a Keithley 6517b electrometer. Colloidal graphite paint was used to connect copper wires to the surfaces of the Pb ₂ P ₂ Se ₆ wafer samples. During the

measurements, the voltage was swept from -400V to 400V with a dwell time of 30s.

Photoconductivity was measured in parallel with an Ag X-ray tube source (40kV, 10mA) illuminating the sample.

For the detector property measurement, Pb ₂ P ₂ Se ₆ single crystal wafers 1 -2 mm thick were exposed to a 1.0 mCi ⁵⁷ Co source. In each measurement, the sample was placed in an eV-480 test fixture which was connected to an eV-550 preamplifier box. A positive bias between 400V and 800 V was applied to a crystal wafer to maintain an electric field up to ~8 ^χ 10 ⁵ Vm ^" \ A SPEAR detector with a 5 x5 x5 mm CZT crystal was used as a reference and it was operated at a bias voltage of 1000 V. For the Pb ₂ P ₂ Se ₆ samples, the signals were transferred to an ORTEC amplifier (Model 572A) with a gain of 200-1000 and shaping time of 0.5-6 zs, while the signal from the commercial CZT detector was amplified with a gain of 1000 and shaping time of 0.5 zs. The processed signals was subsequently evaluated by a dual 16K input multichannel analyzer (Model ASPEC-927) and read into the MAESTRO-32 software. The detailed measurement parameters are summarized in Table 4, with respect to the spectra in FIGs 7A-7D.

Table 4. Co gamma-ray measurement parameters with respect to the spectra in FIGs.

Sample Thickness Voltage Shaping Collection

Polarity Gain

code (mm) (V) Time ( _j us) Time (s)

PE1077c3 1.5 400 1000 6 400

PE1077c4 1.5 400 1000 6 8000

Positive

PE1088c2 1.1 800 200 6 1000

PE1077c6 1.8 600-800 1000 6 7500 PE1072c2 1.3 400 30

PE1067U 1.7 600

[0067] Electronic Structure Calculations: The electronic band structure of Pb ₂ P ₂ Se6 was determined using the projector augmented wave method as implemented in the Vienna Ab initio Simulation Package. (See, P. E. Blochl, Phys. Rev. B: Condens. Matter Mater. Phys. 1994, 50, 17953; G. Kresse, J. Hafner, Phys. Rev. B: Condens. Matter Mater. Phys. 1993, 47, 558 and G. Kresse, J. Furthmiiller, Physical Review B 1996, 54, 11169.) Energy cut off for the plane wave basis was set to 350 eV and the 5 ^χ 5 ^χ 3 Monkhorst-Pack grid was used for momentum space integrations in a self-consi stent calculation. (See, H. J. Monkhorst, J. D. Pack, Phys. Rev. B: Condens. Matter Mater. Phys. 1976, 13, 5188.) In order to predict a band gap correctly, the hybrid functional was employed within the Heyd-Scuseria-Ernzerhof formalism. (See, J. Heyd, G. E. Scuseria, M. Ernzerhof, J. Chem. Phys. 2003, 118, 8207.) Spin-orbit coupling was included in a non-collinear scheme.

[0068] Example 2. Enhanced Method of Pb?P?Sefi Growth and Processing

[0069] In order to further develop the Pb ₂ P ₂ Se6 as a hard radiation detector, it was desirable to improve the reproducibility of the detector material quality. For instance, a higher phase uniformity within an ingot enables the study of the distributions of impurities, defects, and secondary phases along the growth direction. In addition, better reproducibility across the growth runs would result in identification of the crucial processes affecting the final sample quality. This example reports refined synthesis, crystal growth and post-growth processes developed to produce Pb ₂ P ₂ Se ₆ with improved electrical and optical properties, as well as reproducible responses to γ-ray radiation. The impact of stoichiometry control on the optical and electrical properties of the detector samples was elucidated by a series of comparative measurements.

[0070] Synthesis and Crystal Growth

[0071] The Pb ₂ P ₂ Se ₆ samples were synthesized from lead metal (rod, Alfa Aesar, 99.9999% wt.), selenium (pellets, Stanford Advanced Materials, 99.99999% wt.) and red phosphorous (pieces, Alfa Aesar, 99.999%) wt.). The as-purchased lead was etched with 5%> HNO ₃ solution then rinsed with pure ethanol in order to remove the surface oxide. The Pb rod was cut into a section of -10 g. This practice minimized the contamination of the Pb metal from cutting and handling. Red phosphorus and elemental selenium were weighed with respect to the exact mass of the lead metal. [0072] The silica ampoules and plugs (silica rods fitted to ampoule) used for synthesis and crystal growth were first etched with a 2% HF solution in HN0 ₃ in order to remove any surface layer of metallic impurities. The ampoules and plugs were subsequently rinsed with deionized water and 200 proof ethanol. The tubes and the plugs were then baked in a furnace at 1000°C for 20 hours to remove organic contamination. The furnace was cooled to 200°C after the baking process.

[0073] The baked silica ampoules/plugs were immediately used for sample loading in a moisture controlled, Class 1000 clean room (30% humidity at 25°C). For each synthesis, up to 30 grams of stoichiometric starting materials were loaded into tapered fused silica ampoules (13 mm ID, 1 mm wall thickness and 250 mm in length). After loading the starting materials, the silica plugs (12 mm Φ, 100 cm long) were inserted to rest directly on top of the raw materials.

[0074] The loaded sample ampoules were subjected to a bake-out procedure under vacuum using a setup shown schematically in FIG. 9. This setup was composed of a DC- powered heating tape and a graphite tube. While the DC-powered heating tape provided the thermal energy, the high thermal conductivity of the graphite tube ensured the temperature uniformity. The starting materials were baked at 85°C under a vacuum of ~10 ^"4 Torr for 2 hours before the ampoules were sealed. The loaded samples were sealed under vacuum by flame starting at the top of the silica plug.

[0075] For the initial material synthesis, the sealed samples were heated to 850°C over 72 hours and held at the maximum temperature for 48 hours before they were cooled to room temperature over 12 hours. The polycrystalline samples were directly subjected to crystal growth in a modified vertical two-zone Bridgman furnace equipped with a computer controlled linear stage. The temperature of the hot zone was 850°C, while the cold zone was 650°C. The crystal growth was carried out with a lowering rate of 1 mm per hour. Once the samples were completely in the cold zone, they were annealed in situ at 650°C for 24 hrs. Finally, the grown crystals were cooled to room temperature over 24 hours. The temperature gradient in the two-zone Bridgman furnace was estimated to be 8°C/cm. Crack-free crystal ingots were obtained from the crystal growth.

[0076] Post-growth Processes and Detector Fabrication

[0077] The Pb ₂ P ₂ Se ₆ single crystals obtained from the Bridgman growth procedure were cut into 2 mm thick wafers perpendicular to the growth direction using a Struers Accutom-50 waferizing saw equipped with a 300 μηι wide diamond-impregnated blade. The sample wafers were ground to <1 mm thick by hand on a 1200 grit SiC sand paper before they were hand polished on 4000, 8000, and 12000 grit sand papers. The final fine polishing was performed mechanically with a 0.05 /mi suspended A1 ₂ 0 ₃ slurry. The residue of the polishing slurry was removed by sonicating the wafers in toluene. The processed Pb ₂ P ₂ Se ₆ crystal wafers were 0.3-0.8 mm thick and exhibited smooth, mirror like surfaces.

[0078] The polished samples were preserved under toluene until metallization. Detectors were fabricated by depositing 50 nm of gold on the top and bottom surfaces of each wafer sample using an electron beam evaporator (Auto 500, BOC Edwards) to form parallel-plate device geometries. The detector devices for electrical and γ-ray spectroscopy measurements were made by mounting a sample wafer on to a glass slide with copper stripes, where copper wires were connected to the gold electrodes and copper stripes by colloidal silver paint.

[0079] Single Crystal Bandgap

[0080] The transmittance spectra of Pb ₂ P ₂ Se ₆ single crystals were recorded in the 450-850 nm wavelength range (1.45-2.75 eV) at room temperature using a Perkin Elmer LAMBDA 1050 spectrophotometer equipped with an integrating SpectralonR sphere. The samples were polished to 0.39 mm thickness using the described procedure. The samples are too thick to accurately measure the absorption coefficient (a) due to a significant contribution from light scattering within the bulk on the crystal. However, the measurement yields an accurate bandgap and the transparency of the various samples can be compared.

[0081] Photoluminescence (PL) Measurements

[0082] The excitation source for the PL measurements was the 405 nm line from a CW semiconductor diode laser (Excelsior One-405, Spectra-Physics) with the beam diameter of -1.2 mm. The laser has a constant power of 50 mW, which was varied by using a series of neutral optical density filters. The signal-to-noise ratio was increased using an optical chopper and a lock-in amplifier (SR810, Stanford Research Systems). The PL signals were resolved by a 0.75 m SPEX grating monochromator equipped with a Hamamatsu photomultiplier tube (R928 PMT). The datasets were collected at a rate of 0.5 nm s ^"1 , such that a single PL spectrum in the 650-900 nm range can be obtained within 10 mins. A 405 nm bandpass filter with a FWHM of 10 nm (Thorlabs, Inc.) was used to deliver a narrower laser line to the sample. The PL signals were focused using a series of lenses placed between the closed-cycle He cryostat (SHI cryogenics DE-202) and the entrance slit of the monochromator. The scattered and reflected laser light was filtered using a 650 nm sputtered edgepass filter (Thorlabs, Inc) placed in front of the entrance slit of the monochromator (slit widths = 200 microns). Either CRY-CON (Air Products and Chemicals) or Apiezon N grease was used to mount the samples on a vertical stage. The grease was applied to the back of the sample and was not excited by the laser beam.

[0083] Electronic Transport and Detector Property Measurements

[0084] In a typical measurement of I-V characteristics, the applied voltage was swept from 0 V to 300 V using a high voltage power supply (PS300, Stanford Research Systems) and a current meter (Model 2636 A, Keithley) measured the current with a dwell time of 10-15 sec. Photoconductivity (σ^) was measured by using a CW 405 nm laser source for excitation (50 mW, 1.2 mm laser spot diameter). A qualitative measurement of photosensitivity was conducted using a custom-made setup. A detector device with a 0.4 mm thickness wafer was put inside a guarded dark box, which was connected to a Keithley source-meter (model 6517b). The sample was exposed to ambient visible light with an ON-OFF state. A 400V bias voltage was applied while the resulting photocurrent was recorded as a function of time.

[0085] For the detector response measurement, Pb ₂ P ₂ Se ₆ detector devices were exposed to a 0.25// Ci ⁵⁷ Co source. In each measurement, the fabricated detector device connected to an eV-550 preamplifier was placed in a customized sample box. Depending on the thickness of the sample wafer, a positive bias between 400V and 800 V was applied. The maximum electric field maintained on a device was ~2 ^χ 10 ⁵ Vm ^"1 . The detector signals were amplified (ORTEC 572A amplifier) with a gain of 200 and shaping time of 6 /s. The electronic signals were subsequently measured by a dual 16 K input multichannel analyzer (Model ASPEC- 927) and read using MAESTRO-32 software. A SPEAR CZT detector operated under a similar electric field condition was used as a reference device.

[0086] Thermodynamic Stability and Electronic Structure Calculations

[0087] First-principles total energy calculations within the density functional theory framework were employed to investigate the thermodynamic stability, electronic structure, and defect properties of Pb ₂ P ₂ Se ₆ . The projector augmented wave (PAW) method as implemented in the VASP code was employed. (See, Kresse, G.; Hafner, J. Physical Review B 1993, 47, 558 and Kresse, G; Furthmuller, J. Physical Review B 1996, 54, 11169.) The energy cut off for the plane wave basis was set to 350 eV and a regular &-point mesh generated according to the Monkhorst-Pack scheme with the density of 50 (A°) ^_1 was used for Brillouin zone sampling. (See, Monkhorst, H. J.; Pack, J. D. Physical Review B 1976, 13, 5188.) The exchange-correlation contribution to the potential was included using the generalized gradient approximation (GGA) within the Perdew-Burke-Ernzerhof (PBE) functional. (See, Perdew, J. P.; Burke, K.; Ernzerhof, M. Phys. Rev. Lett. 1996, 77, 3865.) To describe the isolated defects and impurities, 2><2><2 supercells containing 160 atoms and a 3 x3 x3 &-point mesh were utilized. The internal atomic positions of the defect structures were fully relaxed until the residual forces on atoms were less than 0.01 eV/A while the lattice parameters of the supercells remained fixed.

[0088] Reduction of Oxygen

[0089] The Glow Discharge Mass Spectrometry (GD-MS) analysis performed on the Pb ₂ P ₂ Se ₆ single crystal samples grown from the as-purchased materials revealed less than 5 ppm total impurity (Table 5). According to the GD-MS analysis of the Pb ₂ P ₂ Se6, the major impurities were alkaline metals (Na, K), Cu, Si and S. The alkaline metals likely came from the silica ampoule used for synthesis and crystal growth, which should be significantly reduced by using low-alkaline quartz products. The copper impurity (0.23 ppm) was introduced during the Se mining and refining processes. The most dominant impurity, sulfur at 3 ppm, is isoelectronic with Se, thus should have limited impact on the electronic transport properties of Pb ₂ P ₂ Se ₆ .

Table 5. Glow Discharge Mass Spectrometry (GD-MS) impurity analysis of a Pb ₂ P ₂ Se6 single crystal samples. Only the impurity elements above the detection limit are listed.

Concentration

Element

(ppm wt.)

Na 0.16

Si 0.21

S 3

K 1.7

0.23

Cu

[0090] Although the GD-MS analysis showed reasonably low impurity content, the concentration of oxygen in the Pb ₂ P ₂ Se ₆ samples remained unknown. The final oxygen and moisture level inside the sample ampoule should be very low after a prolonged evacuation (~2 hours) at a pressure of ~10 ^"4 Torr. However, even the small amount of remaining oxygen and moisture can have detrimental effects on the crystal quality due to the rapid reactivity with the lead metal to form lead oxide. Lead oxide can fuse with the silica ampoule wall to form spots or film of lead glass resembling "watermarks" on the silica wall. During the crystal growth of Pb ₂ P ₂ Se ₆ , the spots of Pb on the glass tube act as parasitic nucleation centers introducing competing grains from the ampoule wall. Furthermore, the interaction between these Pb spots and the crystal ingot prevented the release of the ingot from the ampoule. A small amount of oxygen/moisture can cause a strong "sticking" effect between the ampoule and the crystal ingot. Such a chemical reaction between the oxides in the Pb ₂ P ₂ Se ₆ melt and the ampoule wall is also suspected to introduce the Si impurity into the crystal system. Most importantly, oxygen impurity is well known for its detrimental effect on the transport properties of many semiconductors.

[0091] First-principles electronic structure calculations of oxygen defects were carried out using the supercell approach in order to understand the effect of oxygen on the electronic properties of Pb ₂ P ₂ Se6. Oxygen interstitials and oxygen substitutional defects were considered. Owing to its significantly smaller atomic radius, oxygen prefers to occupy interstitial positions rather than substitute other atoms in the structure (66 nm, compared with 107, 120, and 146 nm for P, Se, and Pb, respectively). There are four unique interstitial sites in the Pb ₂ P ₂ Se6 unit cell that O atoms can occupy. Among substitutional positions, O replacing Se is strongly preferred energetically over other substitutions. The effect of oxygen on the electronic properties of Pb ₂ P ₂ Se ₆ was analyzed based on the comparison of the calculated electronic band structures for pure and defected supercells.

[0092] The calculated electronic band structure of defect-free Pb ₂ P ₂ Se6, plotted along the lines between the high-symmetry points in the Brillouin zone (BZ), is shown in FIG. 10A. The band structure of a supercell has a larger number of bands compared with that of a primitive unit cell due to band downfolding. The main features of the supercell such as character and width of the band gap and the character of the states near the band edges, however, remain unchanged. The calculated band structure shows that Pb ₂ P ₂ Se6 is an indirect band gap material with the PBE band gap of 1.60 eV (FIG. 10A). This calculated value is slightly underestimated compared with the measured value of 1.88 eV. Underestimation of band gaps is a known issue of DFT calculations employing exchange-correlation functionals based on the local density approximation, such as PBE. The band gap value corrected by the calculations employing hybrid functional scheme is 2.0 eV, as reported in a previous work. (See, Wang, P. L.; Liu, Z.; Chen, P.; Peters, J. A.; Tan, G.; Im, J.; Lin, W.; Freeman, A. J.; Wessels, B. W.; Kanatzidis, M. G. Adv. Fund. Mater. 2015, 25, 4874.) The band structure of Pb ₂ P ₂ Se ₆ with an interstitial O atom (Oi _nt ) shows that the presence of oxygen leads to the formation of two new electronic levels within the band gap (FIG. 10B): a deep level located near the middle of the gap, and a shallow acceptor level near the valence band maximum (VBM). To demonstrate that these levels are in fact due to oxygen, the site-resolved and orbital -projected wavefunction character of each band was calculated (FIG. 10B). The new levels were mostly comprised of Op states, while contribution of oxygen to most of the other bands was very small. Similar behavior was observed for oxygen in other interstitial positions and in different charge states. These results confirm that Oi _nt impurities are detrimental to the electronic and detector properties of Pb ₂ P ₂ Se ₆ because they can act as deep-level traps that could be responsible for nonradiative recombination of carriers due to carrier capture.

[0093] The band structure of Pb ₂ P ₂ Se ₆ was also calculated with an oxygen atom substituting one of the Se atoms (FIG. IOC). In stark contrast to the interstitial oxygen calculation, O-for-Se substitution (Os _e ) did not create any levels within the band gap and mostly contributed to the bands that are located 2-3 eV below the valence band. The changes to the band structure were largely due to a slight distortion of the structure around the defect. This distortion led to the removal of band degeneracy and a minor shift of the resulting non- degenerate bands with respect to each other. Subsequently, the bands became much denser but there is no change in the character and width of the bands near the band edges. Since O and Se are electronic analogues belonging to the same group in the Periodic Table, O-for-Se substitution did not change the character of chemical bonding in this system. Therefore, the Os _e defect was electrically inert and will not have any detrimental effect on the detector properties of Pb ₂ P ₂ Se6.

[0094] The results of the first-principles calculations suggest that the detrimental effect of oxygen on the electronic properties of Pb ₂ P ₂ Se ₆ can be avoided by reducing its level below the level of Se vacancies. In such a case, oxygen will occupy Se vacancy positions rather than interstitial ones, becoming electrically benign. Thermodynamic stability calculations show that Se vacancies are the prevalent native defects and have the lowest formation energy and therefore are easily created [see discussion below]. Se-poor growth conditions promote Se- vacancy formation and can further facilitate oxygen removal by trapping it at the Se-vacancy sites.

[0095] In addition to the oxygen contamination in the starting materials, moisture adsorbed onto the inner wall of the silica ampoules was found to be a major source of oxygen. A baked silica tube can adsorb enough moisture on its inner surface within a few hours to cause noticeable "sticking" between crystal and the growth ampoule. Thus, the silica ampoules were immediately used for sample loading after baking. Other experimental procedures, such as metal etching and vacuum baking of raw materials, were also

implemented to further reduce the oxygen content. Due to the elusive nature of the oxygen impurity, the reduction of the oxygen levels could not be quantified. However, a clear elimination of the "water-mark" like oxide film accompanied by an improved release of ingots from the ampoules was observed. The successful reduction of oxygen impurity, together with a better stoichiometry control, resulted in the improved optical and electrical properties in the Pb ₂ P ₂ Se6 samples.

[0096] Secondary Phase and Stoichiometric Control

[0097] In addition to the difficulties encountered with oxygen and moisture

contamination, the Pb ₂ P ₂ Se ₆ crystals were plagued with secondary phase precipitation. The precipitate can be clearly observed under an optical microscope in a transmission mode. To further understand the nature of the observed precipitation, single crystal wafers of Pb ₂ P ₂ Se6 with and without precipitates were subjected to UV-Vis transmittance spectroscopy.

Compared to the precipitate-free Pb ₂ P ₂ Se ₆ crystal, a sample with a black secondary phase exhibited a similar band gap value while displaying a much lower transmittance to light (FIG. 11). Hence, the black precipitation in the crystal can be attributed to a secondary phase unrelated to the Pb ₂ P ₂ Se ₆ matrix and has a no impact on its optical band gap.

[0098] In addition to the poor optical transparency below the bandgap, the Pb ₂ P ₂ Se ₆ samples with secondary phase inclusions also exhibited poor electrical properties and photo response (FIG. 12A) in comparison to the samples without visible precipitates (FIG. 12B). Although both samples possessed similar electrical resistance under low bias voltages, a nonlinear current-voltage behavior was observed for the sample with a secondary phase in the dark as well as under laser radiation. Such an observation is consistent with an electrical breakdown behavior under applied voltage. In contrast, the sample without secondary precipitates displayed more linear current-voltage characteristics over a larger voltage range. More importantly, a large photo response to the 405 nm laser radiation was also observed for the Pb ₂ P ₂ Se6 sample free of secondary phase.

[0099] Photolumine scent (PL) Properties

[00100] PL properties of several grown Pb ₂ P ₂ Se ₆ single crystals from different growth runs were investigated. For the uniform and transparent samples a broad PL emission was observed in the 1.5-1.8 eV range at 15 K, comprised of three peaks centered at 1.52, 1.62 and 1.75 eV (FIGs. 13 A and 13B). Samples with no response to γ radiation and visible

precipitation, however, showed no near-band edge PL at low temperature. In most of these cases, green localized luminescence centers were observed. Exploration of a sample cut from the heel of an ingot suggests that the green "dots" are caused by the presence of a small amount of lead oxide, which collects in the tip of the tube and exhibits green PL emission.

[00101] It is well known that the PL intensity (I) is proportional to L ^k , where L is the laser power and the exponent k describes the nature of the observed transition. (See, Schmidt, T.; Lischka, K.; Zulehner, W. Phys. Rev. B 1992, 45, 8989.) Excitonic transitions show l values in the 1 < k < 2 range, while free-to-bound and donor-acceptor pair (DAP) transitions are characterized by the value of k < 1. The power dependence on the PL intensity of the three peaks was investigated at 15.5 K (FIG. 13 A). The intensity of the peaks decreased with decreasing laser power, such that the plots of log (PL intensity) vs. log (laser power) were linear with the corresponding values of & of 1.1 ± 0.2, 0.48 ± 0.09, and 0.5 ± 0.2 for peaks centered at 1.52, 1.62, and 1.75 eV, respectively . Therefore, the peaks centered at 1.62 and 1.75 eV were due to DAP recombination, while that at 1.52 eV was due to a bound exciton. The two lower energy peaks (1.52 eV and 1.62 eV) exhibited a blueshift with increasing laser power, while the peak at 1.75 eV appeared to redshift. In addition, a slight peak broadening was observed with increasing laser power for the peaks at 1.52 and 1.75 eV, while the full width at half maximum (FWFDVI) of the peak at 1.62 eV did not vary significantly.

[00102] To determine activation energies of the defect levels, the dependence of PL intensity on temperature was examined. The Arrhenius plots of the dependence of the integrated PL intensity on temperature for a DAP and excitonic emissions are described by Eq. 1 and Eq. 2, respectively, where 1(0) is the extrapolated zero-temperature intensity, k _B , (pi, φ ₂ , C] and C ₂ are constants, E _a is the thermal activation energy of a defect level and E] is the thermal ionization energy of a bound exciton.

7(0)

/(Γ) = _{1 +} ^ _{l T} 3/2 ₊ ^ _{2 T} 3/2 _exp (1) [00103] Plots of integrated PL intensity vs. 1000/T revealed that the peak centered at 1.75 eV underwent rapid thermal quenching, precluding determination of its activation energy (FIG. 14A). The fitting parameters for peaks centered at 1.52 and 1.62 eV to Eq. 2 and Eq. 1, respectively, are given in Table 6. Activation energies of E _\ = 1 1 ± 2 and E _a = 15 ± 7 meV were obtained, which were the same within error. The error is due to the fact that the PL emission was weak, and thermal quenching limits the temperature range at which the signals could be detected. In addition to the activation parameters, the temperature dependent data revealed that the DAP peak at 1.62 eV blueshifted and broadened with increasing

temperature, while the excitonic peak at 1.52 eV redshifted and became narrower (FIG. 14B). The redshift and an increase in full width at half maximum (FWUM) were expected due to the temperature-dependent bandgap widening and thermal broadening, respectively.

However, the blueshift and peak narrowing were unexpected.

Table 6. Fitting parameters of the plots of integrated PL intensity vs. T to Eq. 1 (1.62 eV peak) and

Eq. 2 (1.52 eV peak).

Parameter 1.52 eV peak 1.62 eV peak

1 (0) (a.u.) 0.16 + 0.02 0.30 + 0.03

<Pi - 0.005 + 0.002

Φ2 - 0.1 + 0.1

E _a (meV) - 15 + 7

C 1000 + 800 -

E (meV) 1 1 + 2 -

[00104] Thermodynamic Stability

[00105] Due to the detrimental effect of the secondary phase precipitates on the optical and electrical properties of Pb ₂ P ₂ Se ₆ , its formation conditions were studied by first-principles total energy calculations of thermodynamic stability. The growth of Pb ₂ P ₂ Se ₆ can be limited by the existence of competing phases such as binary phases and other ternary compounds in the Pb- P-Se system. Pure and precipitate-free Pb ₂ P ₂ Se ₆ can only be grown in a limited range of chemical potentials of its components. A set of linear equation (Eq. 3 - Eq. 5) balancing heat of formation (AH _F ) of Pb ₂ P ₂ Se ₆ with AH _F of the competing phases and with the chemical potentials Αμ _α of elemental components describes the region where Pb ₂ P ₂ Se ₆ can be stabilized:

2Αμ _η + 2Αμ _Ρ + 6Αμ _β = AH _F (Pb ₂ P ₂ Se ₆ ) (3)

Αμ _α ≤ 0 (4) n _Pb A^ _Pb + η _Ρ Δμ _Ρ + η _5θ Δμ _5θ < H _F (competing phases) (5)

[00106] The following phases are known to exist in the Pb-P-Se system: PbSe (3 structural forms), PbSe ₂ , PSe, P ₄ Se ₃ (2 structural forms) and P ₄ Se ₅ . The calculated region of

thermodynamic stability of Pb ₂ P ₂ Se ₆ is presented in FIG. 15 in the form of stability phase diagram. The shaded region in the diagram corresponds to the range of chemical potentials that allow the growth of Pb ₂ P ₂ Se ₆ without formation of other competing phases. The extreme points of this region, marked by circles, correspond to Pb-poor, P-poor, or Se-poor growth conditions. The stability region of Pb ₂ P ₂ Se ₆ is sufficiently wide, which suggests that this compound can be grown precipitate-free even if there is a substantial variance in growth conditions. The Pb-poor condition results in P-Se binaries which are not stable at the melting point of Pb ₂ P ₂ Se ₆ (798°C), but may still form and precipitate after cooling. However, both P- poor and Se-poor conditions promote the formation of other Pb-Se phases, which are known to be stable at high temperature. The thermodynamic stability of native defects was also calculated. Results indicated that selenium vacancies (Vs _e ) are the most dominant defects but are, however, electronically inactive.

[00107] To determine the nature of the secondary phase precipitation in Pb ₂ P ₂ Se _6, a decomposition test was performed as follows. A piece of an as grown Pb ₂ P ₂ Se ₆ single crystal sample was first heated under a temperature gradient in a single zone tube furnace heated to 600°C. A temperature gradient was created by placing a long silica ampoule in the furnace such that the end containing the Pb ₂ P ₂ Se ₆ single crystal was heated by the furnace while the empty end was exposed to room temperature. After heating the Pb ₂ P ₂ Se ₆ sample for 48 hours, a significant amount of black/red materials were deposited at the colder end of the tube. The Pb ₂ P ₂ Se ₆ sample at the right side of the tube was heated below melting temperature, while the decomposition products were transported to the cold end of the tube along the temperature gradient. Analysis of the decomposition products by energy dispersive spectroscopy (EDS) revealed that the Pb ₂ P ₂ Se ₆ sample had completely decomposed into the most

thermodynamically stable lead-selenium binary, PbSe. The more volatile phosphorus and selenium were driven by the temperature gradient to the cold end of the tube to form P-Se binary glass. The dark precipitates observed in the poor quality samples of Pb ₂ P ₂ Se ₆ were PbSe binary resulting from the loss of volatile P and Se.

[00108] In addition to the decomposition experiment, a series of controlled experiments were performed where the Pb ₂ P ₂ Se ₆ single crystal samples were subjected to different temperature gradients. The experiments indicated that the ternary Pb ₂ P ₂ Se6 phase went through a congruent vapor transport between 900°C and 650°C without decomposition, indicating a critical temperature around 650°C. Below this temperature the decomposition of the ternary becomes favorable. Owing to these experiments, the temperature profile of the Bridgman growth procedure was optimized such that no part of the sample ampoule was cooled below 650°C through the growth. A typical temperature profile of a Bridgman growth is shown in FIG. 16. The temperatures at the tip and heel part of the ampoule were measured by two separated thermocouples during the crystal growth.

[00109] Detector Properties

[00110] Subsequent studies on Pb ₂ P ₂ Se6 of Example 1 revealed that the detector response could be variable due to lack of reproducibility in the synthesis and crystal growth processes. A slight compositional deviation or higher oxygen content usually could render the entire crystal ingot unresponsive to any radiation (ambient light, visible laser, X-ray and γ-ray). By improving the experimental procedures, Pb ₂ P ₂ Se6 single crystals can be consistently obtained with a γ-ray detection response. FIG. 17 shows a typical spectroscopic response for a ⁵⁷ Co source from a Pb ₂ P ₂ Se ₆ sample. These spectra showed clearly distinguishable peaks that were responsive to the change of bias voltage.

[00111] The mobility -lifetime products of electron carriers in these samples were estimated using the maximal charge collection efficiency (CCE) under each bias voltage applied to the sample. (See, Ruzin, A.; Nemirovsky, Y. J. Appl. Phys. 1997, 82, 4166.) The details of this method were presented in Example 1 and in a previous report. (See, Wang, P. L.; Liu, Z.; Chen, P.; Peters, J. A.; Tan, G.; Im, J.; Lin, W.; Freeman, A. J.; Wessels, B. W.; Kanatzidis, M. G. Adv. Funct. Mater. 2015, 25, 4874.) At the current stage of development the electron mobility-lifetime product (μτ _ε ) of the Pb ₂ P ₂ Se ₆ detectors are in the range of l x lO ^"5 cm ² /V.

[00112] Concluding remarks

[00113] In order to produce more consistently high quality single crystal samples of Pb ₂ P ₂ Se ₆ for hard radiation detection investigations, the experimental procedures of synthesis and crystal growth were improved and further standardized. Two major factors affecting the reproducibility, oxygen contamination and off stoichiometry, were mitigated. The first- principles electronic band structure calculation of Pb ₂ P ₂ Se ₆ shows that the presence of Oi _nt atoms leads to the formation of two new electronic levels within the band gap: a deep level located near the middle of the gap, and a shallow acceptor level near the valence band maximum. In addition, total energy DFT calculations of the heat of formation (AH _F ) of Pb ₂ P ₂ Se ₆ indicated that the region of thermodynamic stability was sufficiently wide. This suggested that this compound could be grown precipitate-free even if there was a substantial variance in growth conditions. The impact of oxygen on the quality of the Pb ₂ P ₂ Se ₆ crystal ingot was observed through the chemical reaction between oxide species and the silica ampoule, while the nature of the off stoichiometry was studied experimentally. Furthermore, experimental procedures and crystal growth conditions were implemented to improve the electrical and optical properties of the single crystal based on an understanding of the phase stability of the Pb ₂ P ₂ Se ₆ system. PL studies indicated that luminescence was only observed from samples which showed response to γ-ray radiation. Crystals of low quality showed green PL centers attributed to PbO precipitates. The higher quality Pb ₂ P ₂ Se ₆ single crystals exhibited two peaks due to DAP recombination centered at 1.62 eV and 1.75 eV, and one excitonic peak at 1.52 eV. The refined synthesis and crystal growth processes provided Pb ₂ P ₂ Se ₆ samples with excellent optical transparency and high electrical resistivity, as well as good photoluminescent and photoconductive properties. Importantly, these samples showed spectroscopic responses to ⁵⁷ Co γ-ray radiation leading to an estimation of the μτ _ε product in the range of l x lO ^"5 cm ² /V.

[00114] The word "illustrative" is used herein to mean serving as an example, instance, or illustration. Any aspect or design described herein as "illustrative" is not necessarily to be construed as preferred or advantageous over other aspects or designs. Further, for the purposes of this disclosure and unless otherwise specified, "a" or "an" means "one or more".

[00115] The foregoing description of illustrative embodiments of the invention has been presented for purposes of illustration and of description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The embodiments were chosen and described in order to explain the principles of the invention and as practical applications of the invention to enable one skilled in the art to utilize the invention in various embodiments and with various modifications as suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto and their equivalents.