COATING CARBON STEEL TUBING WITH IRON SULFIDE
Document Type and Number:
WIPO Patent Application WO/2018/169938
Kind Code:
A1
Abstract:
Treating carbon steel tubing includes contacting the carbon steel tubing with a first treatment solution including a salt; corroding the carbon steel tubing with the salt to yield a corroded surface on the carbon steel tubing; contacting the corroded surface on the carbon steel tubing with a second treatment solution comprising sulfide ions; and forming an iron sulfide layer on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions in the second treatment solution with iron in the carbon steel tubing. In some cases, the first treatment solution also includes sulfide ions, and the iron sulfide layer is formed by contacting the carbon steel tubing with the first treatment solution.

Inventors:
CHANG FAKUEN FRANK (SA)
CHEN TAO (SA)
WANG QIWEI (SA)
Application Number:
PCT/US2018/022150
Publication Date:
September 20, 2018
Filing Date:
March 13, 2018
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
SAUDI ARABIAN OIL CO (SA)
ARAMCO SERVICES CO (US)
International Classes:
C09K8/54; C23F11/16
Foreign References:
US5188179A1993-02-23
Other References:
YINGRUI ZHANG ET AL: "Corrosion Monitoring Under Iron Sulfide Deposit: Testing Method Development", CORROSION 2014, 9 March 2014 (2014-03-09), XP055471382
H.A. NASR-EL-DIN ET AL: "Iron Sulfide Scale: Formation, Removal and Prevention", INTERNATIONAL SYMPOSIUM ON OILFIELD SCALE, 30 January 2001 (2001-01-30), XP055471377, DOI: 10.2118/68315-MS
Attorney, Agent or Firm:
BRUCE, Carl E. et al. (US)
Download PDF:
Claims:
WHAT IS CLAIMED IS:

1. A method of treating carbon steel tubing, the method comprising:

contacting the carbon steel tubing with a first treatment solution comprising a salt;

corroding the carbon steel tubing with the salt to yield a corroded surface on the carbon steel tubing;

contacting the corroded surface on the carbon steel tubing with a second treatment solution comprising sulfide ions; and

forming an iron sulfide layer on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions in the second treatment solution with iron in the carbon steel tubing.

2. The method of claim 1, wherein the carbon steel tubing is located in a subterranean formation.

3. The method of claim 1 or claim 2, wherein treating the carbon steel tubing occurs in situ.

4. The method of any one of the above claims, wherein the first treatment solution and the second treatment solution are the same solution, and contacting the carbon steel tubing with the first treatment solution and contacting the corroded surface on the carbon steel tubing with the second treatment solution occur at the same time.

5. The method of any one of the above claims, wherein a temperature of the first treatment solution is at least 100°F.

6. The method of any one of the above claims, wherein a temperature of the first treatment solution is at least 150°F.

7. The method of any one of the above claims, comprising contacting the carbon steel tubing with the first treatment solution for at least five hours.

8. The method of any one of the above claims, comprising contacting the carbon steel tubing with the first treatment solution for at least ten hours.

9. The method of any one of the above claims, comprising contacting the carbon steel tubing with the first treatment solution for at least fifteen hours.

10. The method of any one of the above claims, comprising contacting the carbon steel tubing with the first treatment solution for at least twenty hours.

11. The method of any one of the above claims, wherein salt includes at least one of sodium, magnesium, potassium, ammonium, and calcium.

12. The method of any one of the above claims, wherein the salt includes at least one of chloride, phosphate, carbonate, and bicarbonate.

13. The method of any one of the above claims, wherein a concentration of the salt in the first treatment solution is at least 100,000 ppm by weight.

14. The method of claim 13, wherein the concentration of the salt in the first treatment solution is at least 150,000 ppm by weight.

15. The method of claim 14, wherein the concentration of the salt in the first treatment solution is at least 200,000 ppm by weight.

16. The method of any one of the above claims, wherein a concentration of the sulfide ions in the second treatment solution is at least 50 ppm by weight.

17. The method of claim 16, wherein the concentration of the sulfide ions in the second treatment solution is at least 100 ppm by weight.

18. The method of claim 17, wherein the concentration of the sulfide ions in the second treatment solution is at least 150 ppm by weight.

19. The method of claim 18, wherein the concentration of the sulfide ions in the second treatment solution is at least 200 ppm by weight.

20. The method of any one of the above claims, wherein a thickness of the iron sulfide layer on the carbon steel tubing is at least 10 μιτι.

21. The method of any one of the above claims, wherein the iron sulfide layer forms a hydrophobic coating on the carbon steel tubing.

22. The method of any one of the above claims, wherein a pH of the first treatment solution is in a range of 2 to 10.

23. The method of any one of the above claims, wherein a pH of the second treatment solution is in a range of 3 to 8.

24. The method of any one of claims 1 through 21, wherein the first treatment solution and the second treatment solution are the same, and the pH of the treatment solution is in a range of 2 to 10.

25. A method of treating carbon steel tubing, the method comprising:

contacting the carbon steel tubing with a treatment solution comprising sulfide ions and a salt;

corroding the carbon steel tubing with the salt to yield a corroded surface on the carbon steel tubing; and

forming an iron sulfide layer on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions with iron in the carbon steel tubing.

26. The method of claim 25, wherein the carbon steel tubing is located in a subterranean formation.

27. The method of claim 25 or claim 26, wherein treating the carbon steel tubing occurs in situ.

28. The method of any one of claims 25 through 27, wherein a temperature of the treatment solution is at least 100°F.

29. The method of any one of claims 25 through 28, wherein a temperature of the treatment solution is at least 150°F.

30. The method of any one of claims 25 through 29, comprising contacting the carbon steel tubing with the treatment solution for at least five hours.

31. The method of any one of claims 25 through 30, comprising contacting the carbon steel tubing with the treatment solution for at least ten hours.

32. The method of any one of claims 25 through 31, comprising contacting the carbon steel tubing with the treatment solution for at least fifteen hours.

33. The method of any one of claims 25 through 32, comprising contacting the carbon steel tubing with the treatment solution for at least twenty hours.

34. The method of any one of claims 25 through 33, wherein salt includes at least one of sodium, magnesium, potassium, ammonium, and calcium.

35. The method of any one of claims 25 through 34, wherein the salt includes at least one of chloride, phosphate, carbonate, and bicarbonate.

36. The method of any one of claims 25 through 35, wherein a concentration of the salt in the treatment solution is at least 100,000 ppm by weight.

37. The method of claim 36, wherein the concentration of the salt in the treatment solution is at least 150,000 ppm by weight.

38. The method of claim 37, wherein the concentration of the salt in the treatment solution is at least 200,000 ppm by weight.

39. The method of any one of claims 25 through 38, wherein a concentration of the sulfide ions in the treatment solution is at least 50 ppm by weight.

40. The method of claim 39, wherein the concentration of the sulfide ions in the treatment solution is at least 100 ppm by weight.

41. The method of claim 40, wherein the concentration of the sulfide ions in the treatment solution is at least 150 ppm by weight.

42. The method of claim 41, wherein the concentration of the sulfide ions in the treatment solution is at least 200 ppm by weight.

43. The method of any one of claims 25 through 42, wherein a thickness of the iron sulfide layer on the carbon steel tubing is at least 10 μιτι.

44. The method of any one of claims 25 through 43, wherein the iron sulfide layer forms a hydrophobic coating on the carbon steel tubing.

45. The method of any one of claims 25 through 44, wherein a pH of the treatment solution is in a range of 2 to 10.

Description:
COATING CARBON STEEL TUBING WITH IRON SULFIDE

CLAIM OF PRIORITY

This application claims priority to U.S. Patent Application No. 62/471,143 filed on March 14, 2017, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

This document relates to methods for coating carbon steel tubing with iron sulfide in oilfield applications, in particular to reduce corrosion and surface scaling.

BACKGROUND

Carbon steel tubing is widely used as well completion material in oil and gas wells in oilfield applications. Corrosion of carbon steel tubing and scaling on carbon steel tubing in the presence of water is a common problem in oil and gas wells. The presence of corrosive materials, such as carbon dioxide and hydrogen sulfide, exacerbates the problem. Carbon steel tubing often fails due to corrosion, including sour general corrosion and sour pitting corrosion. In addition, scaling on carbon steel tubing in contact with hard water creates technical problems in oil and gas production, including pipe or valve blockage, under deposit corrosion, and unscheduled equipment shutdown. Corrosion resistant alloys and surface coatings have been used to mitigate the failure of carbon steel tubing. However, corrosion resistant alloys are expensive, and surface coatings have limitations related to temperature stability, abrasion resistance, offline treatment, and manufacturing requirements.

SUMMARY

In a first general aspect, treating carbon steel tubing includes contacting the carbon steel tubing with a first treatment solution including a salt; corroding the carbon steel tubing with the salt to yield a corroded surface on the carbon steel tubing;

contacting the corroded surface on the carbon steel tubing with a second treatment solution comprising sulfide ions; and forming an iron sulfide layer on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions in the second treatment solution with iron in the carbon steel tubing.

Implementations of the first general aspect may include one or more of the following features. l In some implementations, the carbon steel tubing is located in a subterranean formation. Treating the carbon steel tubing may occur in situ.

In some implementations, the first treatment solution and the second treatment solution are the same solution, and contacting the carbon steel tubing with the first treatment solution and contacting the corroded surface on the carbon steel tubing with the second treatment solution occur at the same time.

In some implementations, a temperature of the first treatment solution is at least 100°F or at least 150°F. The carbon steel tubing may be contacted with the first treatment solution for at least 5 hours, at least 10 hours, at least 15 hours, or at least 20 hours.

In some implementations, the salt includes at least one of sodium, magnesium, potassium, ammonium, and calcium. In some implementations, the salt includes at least one of chloride, phosphate, carbonate, and bicarbonate. A concentration of the salt in the first treatment solution is typically at least 100,000 ppm by weight, at least 150,000 ppm by weight, or at least 200,000 ppm by weight.

In some implementations, a concentration of the sulfide ions in the second treatment solution is at least 50 ppm by weight, at least 100 ppm by weight, at least 150 ppm by weight, or at least 200 ppm by weight.

In some implementations, a thickness of the iron sulfide layer on the carbon steel tubing is at least 10 μιτι.

In some implementations, the iron sulfide layer forms a hydrophobic coating on the carbon steel tubing.

A pH of the first treatment solution is typically in a range of 2 to 10. A pH of the second treatment solution is typically in a range of 3 to 8. In some

implementations, the first treatment solution and the second treatment solution are the same, and the pH of the first treatment solution is in a range of 2 to 10.

In a second general aspect, treating carbon steel tubing includes contacting the carbon steel tubing with a treatment solution comprising sulfide ions and a salt;

corroding the carbon steel tubing with the salt to yield a corroded surface on the carbon steel tubing; and forming an iron sulfide layer on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions with iron in the carbon steel tubing. Implementations of the second general aspect may include one or more of the following features.

In some implementations, the carbon steel tubing is located in a subterranean formation. Treating the carbon steel tubing may occur in situ.

In some implementations, a temperature of the treatment solution is at least 100°F or at least 150°F. The carbon steel tubing may be contacted with the treatment solution for at least 5 hours, at least 10 hours, at least 15 hours, or at least 20 hours.

In some implementations, the salt includes at least one of sodium, magnesium, potassium, ammonium, and calcium. In some implementations, the salt includes at least one of chloride, phosphate, carbonate, and bicarbonate. A concentration of the salt in the treatment solution is typically at least 100,000 ppm by weight, at least 150,000 ppm by weight, or at least 200,000 ppm by weight. A concentration of the sulfide ions in the treatment solution is typically at least 50 ppm by weight, at least 100 ppm by weight, at least 150 ppm by weight, or at least 200 ppm by weight.

In some implementations, a thickness of the iron sulfide layer on the carbon steel tubing is at least 10 μιτι.

In some implementations, the iron sulfide layer forms a hydrophobic coating on the carbon steel tubing.

A pH of the treatment solution is typically in a range of 2 to 10.

Embodiments described herein advantageously inhibit or prevent tubing corrosion and surface scaling in carbon steel tubing by forming a chemically bonded iron sulfide protective layer on the carbon steel tubing. The iron sulfide layer is hydrophobic, and therefore reduces scale formation on the carbon steel tubing. In addition, coating carbon steel tubing with iron sulfide is achieved in situ, and the iron sulfide layer can be repaired and maintained as needed by repeating the in situ process. Operation costs are reduced by reducing the corrosivity of the carbon steel tubing and reducing the frequency of treatment for scale removal, and capital expenditures are reduced by increasing the durability of the carbon steel tubing.

BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 depicts an exemplary system for forming an iron sulfide layer on carbon steel tubing in situ. FIG. 2 is a flowchart showing operations in a first exemplary process for forming an iron sulfide layer on carbon steel tubing in situ.

FIG. 3 is a flowchart showing operations in a second exemplary process for forming an iron sulfide layer on carbon steel tubing in situ.

DETAILED DESCRIPTION

Reference will now be made in detail to certain embodiments of the disclosed subject matter. While the disclosed subject matter will be described in conjunction with the enumerated claims, it will be understood that the exemplified subject matter is not intended to limit the claims to the disclosed subject matter.

Corrosion and surface scale formation in oil and gas wells can be reduced by forming a hydrophobic layer of iron sulfide on carbon steel tubing in situ. The layer of iron sulfide inhibits or prevents contact of the surface of the carbon steel tubing with produced water, thereby reducing corrosion of the carbon steel tubing and formation of additional iron sulfide on the surface of the carbon steel tubing.

Forming a layer of iron sulfide on the carbon steel tubing can be achieved in situ by corroding the surface of the carbon steel tubing to expose ferrous ions, and contacting the exposed ferrous ions with sulfide ions. The ferrous ions and sulfide ions react chemically to yield iron sulfide, thereby forming a layer of iron sulfide on the surface of the carbon steel tubing. The iron sulfide is hydrophobic, and may be in the form of a continuous layer on the carbon steel tubing, thereby forming a barrier between the carbon steel tubing and water flowing through the tubing.

FIG. 1 depicts exemplary system 100 for forming an iron sulfide layer on carbon steel tubing in subterranean formation 102. A treatment solution from source 104 is pumped via pump 106 through line 108 to wellhead 110, and enters carbon steel tubing 112 in wellbore 114. Carbon steel tubing 112 is typically production steel tubing. The treatment solution is typically an aqueous solution including sulfide ions and one or more salts. The carbon steel tubing is contacted with the treatment solution for a length of time, thereby corroding the carbon steel tubing and exposing ferrous ions on the surface of the carbon steel tubing. In some embodiments, contacting the carbon steel tubing with the treatment solution includes flowing the treatment solution through the carbon steel tubing. The sulfide ions react with the exposed ferrous ions to yield a layer of iron sulfide on the surface of the carbon steel tubing. Thus, the iron sulfide forms a protective layer on the surface of the carbon steel tubing. In some embodiments, a thickness of the iron sulfide layer is in a range of 10 μιτι to 1000 μιτι.

The treatment solution includes one or more salts. Examples of suitable cations in the salts include sodium, magnesium, potassium, ammonium, and calcium. Examples of suitable anions in the salts include chloride, phosphate, carbonate, and bicarbonate. A total concentration of the salt in the treatment solution is at least 100,000 ppm by weight. In some embodiments, a total concentration of the salt in the treatment solution is at least 150,000 ppm by weight or at least 200,000 ppm by weight. In certain embodiments, a total concentration of the salt in the treatment solution is in a range of 5,000 ppm by weight to 300,000 ppm by weight. In certain embodiments, a concentration of the sulfide ions in the treatment solution is in a range of 50 ppm by weight to 50,000 ppm by weight. In some embodiments, a pH of the treatment solution is in a range of 2 to 10.

In some embodiments, the carbon steel tubing is contacted with the treatment solution for at least five hours, at least ten hours, at least fifteen hours, or at least twenty hours. In certain embodiments, the carbon steel tubing is contacted with the treatment solution for a length of time in a range between 5 hours and 48 hours. In some embodiments, a temperature of the treatment solution in contact with the carbon steel tubing is at least 100°F or at least 150°F. In certain embodiments, a temperature of the treatment solution is in a range of 100°F to 200°F, or 125°F to 175°F.

A thickness and density of the iron sulfide layer may be controlled by selecting a concentration of salt in the treatment solution, a concentration of sulfide ions in the treatment solution, a pH of the treatment solution, a temperature of the treatment solution, a pressure of the environment under which the treatment solution contacts the carbon steel tubing, or a combination thereof. In some embodiments, the treatment solution includes an additive, such as a catalyst or a polymer, selected to promote formation of a uniform iron sulfide layer.

In some embodiments, the treatment solution is provided to the carbon steel tubing as a first treatment solution and a second treatment solution. In one exemplary embodiment, the first treatment solution from source 104 and the second treatment solution from source 104' is pumped via pump 106 through line 108 to wellhead 1 10, and enters carbon steel tubing 112 in wellbore 1 14. The first treatment solution typically includes the salt and the second treatment solution typically includes the sulfide ions. The first treatment solution and the second treatment solution may be provided to carbon steel tubing 112 at the same time or sequentially. If the first treatment solution and the second treatment solution are provided sequentially, the first treatment solution is typically provided prior to the second treatment solution.

The first treatment solution includes one or more salts. Examples of suitable cations in the salts include sodium, magnesium, potassium, ammonium, and calcium. Examples of one or more suitable anions in the sa;ts include sulfate, chloride, phosphate, carbonate, and bicarbonate. A total concentration of the salt in the first treatment solution is at least 100,000 ppm by weight. In some embodiments, a total concentration of the salt in the first treatment solution is at least 150,000 ppm by weight or at least 200,000 ppm by weight. In certain embodiments, a total

concentration of the salt in the first treatment solution is in a range of 5,000 ppm by weight to 300,000 ppm by weight. In some embodiments, a pH of the first treatment solution is in a range of 2 to 10.

In some embodiments, a concentration of the sulfide ions in the second treatment solution is in a range of 3000 ppm by weight to 150,000 ppm by weight. In some embodiments, a pH of the second treatment solution is in a range of 3 to 8.

In some embodiments, the carbon steel tubing is contacted with the first treatment solution, the second treatment solution, or both for at least five hours, at least ten hours, at least fifteen hours, or at least twenty hours. In certain embodiments, the carbon steel tubing is contacted with the treatment solution for a length of time in a range between 5 hours and 48 hours. In some embodiments, a temperature of the treatment solution in contact with the carbon steel tubing is at least 100°F or at least 150°F. In certain embodiments, a temperature of the treatment solution is in a range of 100°F to 350°F.

An iron sulfide layer formed on carbon steel tubing may crack or thin over time. The iron sulfide layer can be replenished by re-treating the carbon steel tubing with the treatment solution. When the well is a sour well, hydrogen sulfide from the sour flowing stream may react with exposed iron on the surface of the carbon steel tubing to seal a crack or thin region in the iron sulfide layer.

FIG. 2 is a flowchart showing operations in an exemplary process 200 for forming a layer of iron sulfide on a carbon steel tubing in situ. In 202, carbon steel tubing is contacted with the treatment solution and under conditions described with respect to FIG. 1. In 204, the carbon steel tubing is corroded with the salt to yield a corroded surface on the carbon steel tubing. In 206, an iron sulfide layer is formed on the surface of the carbon steel tubing by chemically bonding the sulfide ions with the iron in the carbon steel tubing.

FIG. 3 is a flowchart showing operations in an exemplary process 300 for forming a layer of iron sulfide on a carbon steel tubing in situ. In 302, the carbon steel tubing is contacted with the first treatment solution and under conditions described with respect to FIG. 1. In 304, the carbon steel tubing is corroded with the salt to yield a corroded surface on the carbon steel tubing. In 306, the corroded surface on the carbon steel tubing is contacted with the second treatment solution and under conditions described with respect to FIG. 1. In 308, an iron sulfide layer is formed on the corroded surface of the carbon steel tubing by chemically bonding the sulfide ions in the second treatment solution with iron in the carbon steel tubing.

Definitions

In this document, the terms "a," "an," or "the" are used to include one or more than one unless the context clearly dictates otherwise. The term "or" is used to refer to a nonexclusive "or" unless otherwise indicated. The statement "at least one of A and B" has the same meaning as "A, B, or A and B." In addition, it is to be understood that the phraseology or terminology employed in this disclosure, and not otherwise defined, is for the purpose of description only and not of limitation. Any use of section headings is intended to aid reading of the document and is not to be interpreted as limiting; information that is relevant to a section heading may occur within or outside of that particular section.

Values expressed in a range format should be interpreted in a flexible manner to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. For example, a range of "about 0.1% to about 5%" or "about 0.1 % to 5%" should be interpreted to include not just about 0.1 % to about 5%, but also the individual values (for example, 1%, 2%, 3%, and 4%) and the sub-ranges (for example, 0.1 % to 0.5%, 1.1% to 2.2%, 3.3% to 4.4%) within the indicated range. The statement "about X to Y" has the same meaning as "about X to about Y," unless indicated otherwise. Likewise, the statement "about X, Y, or about Z" has the same meaning as "about X, about Y, or about Z," unless indicated otherwise. The term "about" can allow for a degree of variability in a value or range, for example, within 10%, within 5%, or within 1 % of a stated value or of a stated limit of a range.

The term "fluid" refers to gases, liquids, gels, slurries with a high solids content, and critical and supercritical materials.

The term "subterranean formation" refers to any material under the surface of the earth, including under the surface of the bottom of the ocean. For example, a subterranean formation can be any section of a wellbore and any section of a subterranean petroleum- or water-producing formation or region in fluid contact with the wellbore. In some examples, a subterranean formation can be any below-ground region that can produce liquid or gaseous petroleum materials, water, or any section below-ground in fluid contact therewith. For example, a subterranean formation can be at least one of an area desired to be fractured, a fracture, or an area surrounding a fracture, and a flow pathway or an area surrounding a flow pathway, where a fracture or a flow pathway can be optionally fluidly connected to a subterranean petroleum- or water-producing region, directly or through one or more fractures or flow pathways.

Example

In one example, aqueous treatment solutions A, B and C were prepared.

Aqueous treatment solution A contained 62,700 ppm sodium by weight, 22,000 ppm calcium by weight, 1 , 180 ppm magnesium by weight, 139,000 ppm chloride by weight, and 25 ppm sulfate by weight. Aqueous treatment solution B contained 62,700 ppm by weight sodium, 22,000 ppm calcium by weight, 1 ,180 ppm magnesium by weight, 139,000 ppm chloride by weight, 25 ppm sulfate by weight, and 100 ppm sulfide by weight. Aqueous treatment solution C contained 62,700 ppm by weight sodium, 22,000 ppm calcium by weight, 1 ,180 ppm magnesium by weight, 139,000 ppm chloride by weight, 25 ppm sulfate by weight, and 200 ppm sulfide by weight. The sodium, sulfide, and chloride was provided in the form of sodium sulfate, sodium sulfide, calcium chloride, magnesium chloride, and sodium chloride.

Aqueous treatment solution A was a control (no sulfide), and aqueous treatment solutions B and C had different amounts of sulfide (100 ppm and 200 ppm by weight, respectively). Test coupons 1, 2, and 3 (dimensions 3.03 x 1.00 cm x 0.44 cm) were immersed in aqueous treatment solutions A, B, and C, respectively, at 176°F for 22 hours. After 22 hours, test coupon 1 showed a weight loss of 2 mg, test coupon 2 showed a weight loss of 0.2 mg, and test coupon 3 showed a weight gain of 0.3 mg. The change in weight of test coupons 2 and 3 is due to corrosion (weight loss) as well as the formation of iron sulfide on the surface (weight gain). A dense black iron sulfide film was observed on the surfaces of test coupons 2 and 3 during the 22 hour test period. The iron sulfide film formed on the surfaces of test coupons 2 and 3 (15 μιτι and 20 μιτι, respectively) worked as a protective film and reduced further corrosion on the test coupons, resulting weight loss of no more than 10% of that of test coupon 1, on which no protective iron sulfide film was formed.

OTHER EMBODIMENTS

It is to be understood that while embodiments have been described in conjunction with the detailed description thereof, the foregoing description is intended to illustrate and not limit the scope of the invention, which is defined by the scope of the appended claims. Other aspects, advantages, and modifications are within the scope of the following claims.