Title:
COMBUSTION PROCESS FOR FUEL CONTAINING VANADIUM COMPOUNDS
Document Type and Number:
WIPO Patent Application WO/2014/016237
Kind Code:
A1
Abstract:
Oxycombustion process wherein low ranking, gaseous, liquid, solid, optionally solid melting hydrocarbon fractions are used as fuels, having a vanadium content in an amount by weight from 50 to 5,000 ppm or higher, for producing energy, wherein magnesium is added as oxide, or as a water- soluble salt, the combustor being refractored and isotherm or quasi isotherm, flameless, working at temperatures comprised between 1,250°C and 1,450°C and under pressurized conditions, wherein the oxidant is oxygen, the oxidant being used in admixture with water or steam such that the ratio by moles oxidant: (water-steam) is comprised between about 1:0,4 and about 1:3 or the oxidant is used in admixture with flue gases recycled from the flue gases outletting the energy recovery equipments, wherein the water amount is higher than 30% by volume, optionally by adding water, the molar ratio oxidant: (water/steam) in flue gases being comprised from about 1:0.4 to about 1:3; the low ranking hydrocarbon fraction containing vanadium is fed in admixture with water or steam, such that the amount of water/steam in the mixture is at least 30% by weight with respect to the hydrocarbon fraction.

Inventors:
MALAVASI MASSIMO PIETRO (IT)
DI SALVIA GRAZIA (IT)
BASSIGNANO ALVISE ACHILLE (IT)
TEDESCHI GIAMPIETRO (IT)
Application Number:
PCT/EP2013/065393
Publication Date:
January 30, 2014
Filing Date:
July 22, 2013
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
ITEA SPA (IT)
International Classes:
C10L1/12; F23L7/00
Domestic Patent References:
WO1995007408A11995-03-16
WO2005108867A12005-11-17
WO2004094904A12004-11-04
Foreign References:
US20070240425A12007-10-18
US4659339A1987-04-21
US2843200A1958-07-15
US2781005A1957-02-12
US3817722A1974-06-18
US20100255431A12010-10-07
US2884369A1959-04-28
US4116820A1978-09-26
US6013176A2000-01-11
US6372124B22002-04-16
US7947167B22011-05-24
US5358634A1994-10-25
US7264710B22007-09-04
Other References:
E. ROCCA: "Nickel Oxide as a New Inhibitor of Vanadium- induced Hot Corrosion of Superalloys-Comparison to MGO- based Inhibitor", J. MAT. CHEM., vol. 12, 2002, pages 3766 - 3772
Attorney, Agent or Firm:
SAMA, Daniele (Milano, IT)
Download PDF:
Claims:
CLAIMS

1. Oxycombustion process wherein low ranking, gaseous, liquid, solid, optionally solid melting hydrocarbon fractions used as fuels, having a vanadium content in an amount by weight from 50 to 5, 000 ppm or higher, wherein magnesium is added as oxide, or as a magnesium compound forming MgO in the combustion process, the combustor being refractored and isotherm or quasi- isotherm, flameless, operating at temperatures in the range 1 , 250 ° -1 , 450 °C and under pressurized conditions, wherein the oxidant is oxygen the oxidant being used in admixture with water or steam such that the ratio by moles oxidant: (water-steam) is comprised between about 1:0,4 and about 1:3 or the oxidant is used in admixture with recycled flue gases, coming from the flue gases outletting the energy recovery equipments, wherein the water/steam amount is higher than 30% by volume, optionally by adding water to the recycled flue gases, the molar ratio oxidant: (water/steam) in flue gases being as above; the hydrocarbon fraction being fed in admixture with water or steam, such that the amount of water/steam is at least 30% by weight with respect to the hydrocarbon fraction.

2. A process according to claim 1 wherein the pressure in the combustor is comprised from higher than or equal to 102 kPa to 5,000 kPa.

3. A process according to claims 1-2 wherein the pressure in the combustor is comprised from higher than or equal to 200 kPa to 3,500 kPa.

4. A process according to claims 1-3 wherein the oxidant is pure oxygen or technical oxygen, having an oxygen titre higher than 80% by volume.

5. A process according to claims 1-4 wherein tne ivig:v molar ratio is in the range 1:1 - 2:1.

6. A process according to claim 5 wherein the Mg:V molar ratio ranges from 1.25:1 to 1.75:1.

7. A process according to claims 1-6 wherein the combus- tor is operated at temperatures in the range 1300°- 1400°C.

8. A process according to claims 1-7 wherein the solid hydrocarbon fractions are selected from: asphaltene, petrolene, carbonaceous substances, Petcoke, carbona¬ ceous residues of petrochemical processes, heavy re¬ finery bottoms .

9. A process according to claims 1-8 wherein magnesium is added as magnesium sulphate dissolved in an aqueous solution .

10. A process according to claims 1-9 wherein the resi¬ dence time of the fuel in the combustor ranges from 0.5 seconds up to 30 minutes.

11. Flue gas obtainable with the process according to claims 1-10, wherein (data on a flue gas dry basis) :

- absent soot and IPA <10~4 mg/Nm3,

- fly ash lower than 10 mg/Nm3,

- T0C<1 ppm,

- magnesium, both as oxide and sulphate, <1 mg/Nm3,

- vanadium under the form of orthovanadates and pyro- vanadates ≤1 mg/Nm3;

- V205 <0.01 mg/Nm3,

- S03 ≤2 mg/Nm3,

- NiO <1 mg/Nm3

- NaV03 not detectable by XRD and SEM analysis of mi- croaggregates .

Description:
COMBUSTION PROCESS FOR FUEL CONTAINING VANADIUM COMPOUNDS

The present invention relates to combustion process of low ranking fuels containing vanadium amounts from 50 to 5, 000 ppm or higher, for obtaining flue gases showing, on a flue gas dry basis, a low content of fly ash, that is <10 mg/Nm 3 dry base, preferably <5 mg/Nm 3 , negligible incombus ¬ tible residues, that is with a TOC amount by weight <1 ppm, IPA (polyaromatic hydrocarbons, mainly pyrenes) <10 ~4 mg/Nm 3 , in particular soot absent, vanadium or its compounds being in amounts lower than 1 mg/Nm 3 , and the form of V2O 5 in amounts <0.01 mg/Nm 3 , and NaVC>3 being not detectable at XRD, further said flue gases not being able either to at ¬ tack the combustor building material and of the energy recovery equipments, or to cause efficiency reduction due to adhesive fouling of the equipments used for the energy re ¬ covery .

More preferably the present invention relates to the use for the production of energy of commercially low ranking hydrocarbon fractions, such as for example petrolene and asphaltene, containing high amounts of vanadium in com- bustors working at temperatures in the range 1250 0 -1450 °C, the combustors being a part of the energy recovery plants operating for 8,000 h/year or longer without interruptions for cleaning either the downhill energy recovery equipments or for substituting corroded parts or parts irremediably damaged by the sintered powders deposited by flue gases and without penalizing the punctual efficiency and the energy recovery; intrinsically adhesive compounds, in particular sulphates and soot being substantially absent/negiigiDie m the residual powders.

It is well known in the prior art that the refining processes of the various types of crude oils for the pro ¬ duction of commercial hydrocarbon fractions such as fuels, petrochemical loads, fuels for the production of energy, give heavy hydrocarbon fractions as by-products, in par ¬ ticular petrolene and asphaltene. These by-products cannot be directly used for the production of commercial hydrocar ¬ bon fractions and they find application for poorer and limited uses, for example road asphalts or they form particu ¬ lar fuels, for example Petcoke, pitches, vis-breaking resi ¬ dues suitable for the production of energy but only through very complex energy transformation plants, in order to overcome the negative effect, both technological and envi ¬ ronmental, that would arise when used in conventional hy ¬ drocarbon plants. In fact in heavy hydrocarbon fractions, carbon compounds, polyaromatic hydrocarbons for example as ¬ phaltene, high molecular weight linear or branched hydro ¬ carbons, for example petrolene, the compounds having chemi ¬ cal structures more difficult to be subjected to exhaustive combustion, are concentrated. For example, for Petcoke more complex plants are to be used, for example those used for fossil coal, that is with a number and complexity of equip ¬ ments increased, in particular in the flue gas post- treatment section. As a matter of facts this represents a commercial downgrading of the fuel, besides creating prob ¬ lems in term of higher operation costs and environmental impact .

Another way for using the above heavy fractions as fu ¬ els is to transform them, e.g. by gasification, followed by complex gas cleaning operations, in order to be able to use the gas obtained in conventional energy gas combustors, for example combined cycle turbogas . Alternatively, tne neavy fractions are subjected to complex catalytic reforming pro ¬ cesses to obtain higher commercial value hydrocarbon frac ¬ tions .

However these operations require significant invest ¬ ments and operative costs and dedicated plants. Of course the commercial downgrading of these fuels still remains due to some species concentrated in these fractions, for exam ¬ ple sulphur and nitrogen remaining after hydrogenation treatments in refinery, and present in crude oil chemically bound to high molecular weight molecules, preferably con ¬ centrate in the heavy hydrocarbon fraction. The behaviour of the incombustible ashes and of some heavy metals, in particular vanadium and nickel, is similar.

It is well known that vanadium is a constituent of porphirins, typical substances of the orogenesis of fossil hydrocarbons and generally present in the various types of crude oils in proportion to the content of polyaromatic hy ¬ drocarbons. During the refining processes the bonded vana ¬ dium is concentrated in the heavy hydrocarbon fractions. This certainly reduces the problems in obtaining valuable commercial fractions by removing vanadium, but conversely, the problems related with the use of the heavy hydrocarbon fractions are further worsened. For example an average oil having an 105-110 API grade may contain vanadium in very variable contents depending on the extraction well, generally of the order of 50-100 ppm. However, in heavy fractions deriving from this crude oil, vanadium concentration can rise up to 200-300 ppm. When the heavy fraction, or the heavy oil are subjected to a separation process of asphal- tene for obtaining upgraded oil, the vanadium is further increased in these fractions. For example in the asphaltene fraction the vanadium concentration can rise up to 500-700 ppm.

It is also known that in the residues from catalytic con ¬ version/gasification/reforming treatments of heavy hydrocarbon fractions vanadium can be of the order of some thou ¬ sands of ppm.

It is also known that vanadium represents a remarkable problem for the health of human beings as well as for the environmental impact, and also a technological problem in industrial plants for its aggressiveness towards the vari ¬ ous materials used, as insulating refractories, steels, high performance alloys (special steels) .

Various methods for reducing the negative effects of vanadium in plants for transforming fuels into energy are known in the prior art. See for example USP 2,843,200 that describes a process for reducing the corrosive effect of the vanadium containing fractions, by injecting into the combustor an inhibitor formed by finely subdivided precipi ¬ tate of hydrate calcium silicate, or the inhibitor is uni ¬ formly mixed with the fuel. In the background of this pat ¬ ent it is stated that the fly ashes, obtained by burning residual fuel oils containing substantial amounts of vana ¬ dium compounds, have an important corrosive effect on the building materials of the downhill energy recovery plants, for example there is a catastrophical oxidation of the tur ¬ bine blades. The corrosive effect is deemed to be due to the presence of V 2 O 5 , formed during the combustion of resid ¬ ual fuel oils containing vanadium. This compound attacks various metals, their alloys and other building materials. The corrosive effect progressively increases with the flue gas temperature. Furthermore, the flue gas ashes containing vanadium form a hard and sticky material that deposits on the downhill equipment walls by thickening them and besides corroding them. By using the additive described in this patent, the fly ashes containing vanadium do not aanere any longer to the metal materials of the downhill equipments, but they deposit as non adherent easily removable powders. However it is noticed that the corrosive effect on the various materials of the plants is only delayed. In this patent it is taught to operate the combustor at relatively low working temperatures, of no more than about 750°C (1,350°F, 732°C in the examples) . One drawback of the proc ¬ ess is that the burning residues in fly ashes are in high amounts with consequent adhesive fouling of the downhill equipments. USP 2,781,005 describes the use of magnesium- and zinc-based inhibiting additives, both as oxides and as compounds generating oxides at the combustion temperatures, for the use of low grade residual fuel oils containing va ¬ nadium. The effect of the combustion flue gases at tempera ¬ tures comprised between 600° and 800°C on the energy recov ¬ ery equipments, for example the blades of a turbine, are also described. The operative example is carried out at 650°C. The additives are fed into the combustor, optionally mixed with the fuel. In this way the corrosion is of the same level that takes place in the absence of vanadium. The composition of the zinc and magnesium oxides is such to lead to the formation of orthovanadates M 3 V 2 O 8 with contem ¬ poraneous disappearance of V 2 O 5 from flue gases. In the pat ¬ ent it is stated that when the added amount of the additive is lower than that indicated, the corrosion is not substantially reduced, probably due to the presence of free V 2 O 5 in flue gases. The drawback of the additives used in this patent is the same of the preceding patent. USP 3,817,722 describes the reduction both of the corrosion and of the fouling from sticky fly ashes on the walls of the downhill energy recovery equipments obtainable by adding compounds producing silica and magnesium oxide as silicon and magne- sium sources, such to provide a ratio by weignt iU2/i v igu higher than 2:1, preferably higher than 3:1, in the combustion of fossil fuels containing vanadium and alkaline met ¬ als. At least two parts by weight of magnesium/one part of vanadium and at least two parts by weight of silicon/one part of alkaline metals must be present. The higher the Si0 2 /MgO ratio, the better the benefits in terms of inhibi ¬ tion of the corrosion and fly ash deposition. When the sodium content is high, SiC^/MgO ratios even of 6:1 can be reached. In the patent it is reported that the low cost fu ¬ els, that is those containing vanadium, and optionally also alkaline metals and sulphur compounds, are difficult to be treated. In the background it is stated that the use of silica was already known for controlling the fly ash de ¬ posit on the energy recovery downhill equipments.

Other patents of the prior art describe the use of MgO and S1O 2 in the ratio 1/1 to 2/1. However, if combustion temperatures higher than 760°C as indicated in the prior art are used, corrosion and fly ash deposit take place. Therefore the additives effective at these temperatures are ineffective at temperatures higher than 760°C due to the occurrence of melting phenomena of fly ashes, with impact on corrosion and fouling. Si0 2 has been shown effective in modifying the fly ash nature and in preventing the fouling on the downhill energy recovery equipments and in inhibiting corrosion. In this way the ash melting temperature is increased so as to eliminate the presence of corrosive liq ¬ uid phases. However this is true for temperatures up to 700°C. At temperatures in the range 815°-870°C corrosion and fouling of the fly ash will occur again. In other words, the use of the prior art additives is quite ineffec ¬ tive in low cost/low ranking fuels containing vanadium at combustion temperatures higher than 800 °C. Systems for reaching temperatures higher tnan aoout 760°C are based on the fuel pre-treatment through washing with water to remove the alkaline metals and then adding magnesium sulphate in a ratio by weight Mg/V 3/1. The draw ¬ back of this treatment is that a substantial fouling of the turbine blades of the downhill energy recovery equipments occurs with a progressive decrease of energy production. In practice the ratio magnesium/vanadium can be at most 3/1- 3.5/1 for a good balance between the protection from corro ¬ sion and minimal energy production losses. However turbine operations must be interrupted for blade cleaning, carried out by washings. As a matter of fact one part of the modi ¬ fied ashes deposits on the turbine blades which must be stopped and subjected to washings with water. These clean ¬ ing operations require about 6 hours, therefore these treatments can be only carried out on turbines that can be cyclically stopped. It has also been tried to perform the washings by using milled nutshells for speeding up the op ¬ eration, however with a little advantage. In the prior art, in order to improve the resistance to corrosion, attention has been paid to the building materials, by using special steels, in particular alloys containing nickel and cobalt. However the apparent improvement at temperatures of 400°- 500°C is not maintained at temperatures higher than 700°C. Consequently the equipments show a remarkably reduced work ¬ ing life in comparison with those wherein fuels not containing vanadium are used. The additive disclosed in USP 3,817,722 (supra) allows to carry out combustion up to temperatures of about 815°C as shown in the examples. The drawback of this additive is the high ratio SiC^/MgO at least of 6:1, requested for obtaining a lower corrosion. Another drawback of that additive is that the corrosion phenomena are reduced but not eliminated. The temperature of 815°C must not be exceeded, in order to avoid corrosions from melting ashes. Besides, when sulphur is present, MgSC^ is also formed, that subtracts magnesium to the mentioned reactions. Magnesium sulphate is adhesive to the walls of the downhill equipments, thus lowering the energy recovery efficiency. Magnesium is used also in the cases of fuel gasification for producing synthesis gas to be used in boilers or in combined cycles, with effects similar to those provided by the above described art in direct combus- tors using low ranking fuels to produce hot flue gases. However also in these cases, before using synthesis gases in high yield thermodynamic cycles it is necessary to pro ¬ vide powder removal, by forming solid currents of problem ¬ atic disposal (Vanadium cake) , and further complex opera ¬ tions to remove residual vanadium, present in the form of an ultrafine particulate.

It is known in the prior art, see the article by E. Rocca e al. "Nickel Oxide as a New Inhibitor of Vanadium- induced Hot Corrosion of Superalloys-Comparison to MGO- based Inhibitor". J. Mat. Chem.. 2002, 12, 3766-3772, that the use of fuels containing vanadium and sodium causes ash accumulation along the flue gas path. These ashes give rise to fouling and corrosion along the gas path as a result of the formation of reactive compounds having a low melting point. The additive used in this publication is formed by NiO-MgO usable up to 850 ° -1 , 000 °C . The formation of nickel orthovanadate drastically reduces the corrosion and the de ¬ posit of ashes. The MgO effect on ashes is to stabilize va ¬ nadium under the form of mixed sodium and magnesium orthovanadate NaMg 4 (V0 4 )3. However the favoured transformation of MgO to sulphate due to the sulphur present in the fuel implies feeding amounts of magnesium in excess in order to form a mixed orthovanadate, the excess being found in the flue gases as magnesium sulphate, whose adhesiveness is well known, to give compact deposits on the walls of the energy recovery equipments, with the known inconveniences. The publication concludes that NiO is an effective alterna ¬ tive to MgO to reduce the corrosion due to vanadium. In the publication it is stressed that chromium oxides and alumi ¬ num oxide give the corresponding orthovanadates . However these compounds in the molten state generate corrosion, the more important the higher the amount of sodium present. The MgO addition as inhibitor leads to the formation of mixed orthovanadate, that gives, as it is stated, a limited cor ¬ rosion, but it increases the amount of ashes, due to the ratio in excess magnesium/vanadium, that are also adhesive. In the publication it is pointed out that, differently from the magnesium orthovanadate, nickel orthovanadate is insen ¬ sitive to the presence of sodium. The mixed sodium and mag ¬ nesium vanadates aMg 4 ( V0 4 )3, even though they are refrac ¬ tory and inert, are low-melting and together with the mixed sulphates a6Mg( S 0 4 ) 4 , low-melting too (melting point around 500°C), are liquid at the operating temperatures of the en ¬ ergy recovery equipments, and cause the ash sintering and fouling of the downhill equipment walls.

It is also known in the prior from the above mentioned publication and from patent application US 2010/0255431, that the species of vanadium particularly large spectrum aggressive on materials is the alkaline methavanadate MeV0 3 , wherein Me is sodium or potassium. It is also known that vanadium can be transformed into compounds such as nickel and magnesium orthovanadates ( M3 ( V0 4 )2) and magnesium pyro- vanadates (Mg ^Ov) , chemically and thermally very stable. They are completely inert and non aggressive towards the building materials and besides they are free from any cata ¬ lytic activity in undesired parallel reactions such as the conversion of SO 2 into SO 3 in an oxidizing environment, at temperatures in the range 250°-700°C (i.e. in the range of interest for the thermal recovery of hot flue gases) . How ¬ ever the transformation reactions of vanadium to orthova- nadates are slow and not quantitative and are inhibited by the presence of iron (for example Fe 2 <0 3 in the formation of nickel orthovanadate), subjected to competitive interfer ¬ ences (for example Na 2 <0, Na 2 SC>4, on magnesium orthovanadate to give metavanadate) , and furthermore negatively affected by the presence of sulphur (magnesium preferably consumed to sulphate) , without being possible to eliminate the ag ¬ gressive species aV0 3 , and with formation of submicronic corpuscular vanadium oxide, difficult to remove from flue gases. In particular the patent application describes a process for operating a thermal plant comprising a combus ¬ tion chamber and a turboexpander , fed with a fuel containing vanadium, sulphur and optionally sodium, wherein boron and magnesium are fed in amounts such that the molar ratio of sodium , of magnesium and of boron b=E>20 3 /V20 5 is such that m≥3+2b-s and m≤3+3b-s and b ranges from 0.5 to 3.5, preferably from 1 to 3, so that the com ¬ bustion products mainly comprise magnesium orthovanadate, boron and magnesium mixed oxide and optionally sodium bo ¬ rate. With the used additive there is a lower corrosion and an increase of the ash melting temperature so as to avoid the formation of corrosive and sticky liquid ashes. In this way the combustor can be operated at temperatures higher than those of the prior art, up to 1140°C. In the examples the combustion temperature is of 1090°C up to 1120°C. The additive of this process allows less frequent turbine cleaning compared to the additives mentioned in the preced ¬ ing prior art. Likewise important is the combustion tem ¬ perature risen up to 1140°C, therefore with higher thermo- dynamic efficiencies of the industrial cycle and less stops for cleaning. By passing, it is observed that the math- ematic formulation for the above mentioned quantitative ex ¬ pression of the additives could also consider the case of negative values of m when s takes high values. At any rate it is pointed out that the drawback of this process is that fly ashes are still in high amounts and the frequency of the plant stops for the equipment cleaning is still high (fouling only reduced) . According to this patent applica ¬ tion it is necessary to operate at temperatures not higher than those indicated to avoid both the melting of the mixed oxide mixtures, potentially aggressive, but especially their sintering to give particularly thick deposits difficult to be removed from the downhill energy recovery equipments and in particular from the turbine blades. In summary this patent application describes the use of mixed oxides MgOE y O z wherein E is an element of the group Ilia, IVa, Illb, IVb, VIII or of the Lanthanide series. The second ox ¬ ide E y O z can be selected from the group comprising B 2 O 3 , AI 2 O 3 , Fe 2 <0 3 , S1O 2 , preferably B 2 O 3 , as exemplified. With this additive high-melting, friable, refractory and not sticky ashes are obtained, that can be easily removed by dry cleaning or washing with water. The ratios that are to be used between magnesium oxide and the second oxide are given by the above reported equations. The use of these mixed ox ¬ ides is shown effective in protecting magnesium from the interference of sulphur (to give sulphate) through the fa ¬ voured transformation into mixed borate, and in subtracting sodium from the formation of the dangerous sodium metava- nadate, with the purpose of increasing the ash melting temperature as said above, starting from molar ratios magne ¬ sium/vanadium (MgO/V 2 0s) of 7 (while the stoichiometric would be 3) , up to a molar ratio of 9, in order to obtain the maximum increase (1140°C) of the melting tempera ¬ ture/sintering of the fly ash and avoid the presence of corrosive liquid fly ash. Although the obtained ashes are indicated to be not very sticky (marked difference with re ¬ spect to the sticky ashes of MgSC^) and not melting (and not adhesive up to a temperature of 1,140°C), nevertheless the drawback of the mentioned additives resides in the fact that in order to render vanadium inert, high dosages of MgO are used, to which B 2 O 3 is added (molar ratio B 2 O 3 /V 2 O 5 equal to 3) . Therefore, even if the described additive represents for some aspects an improvement as for the higher combus ¬ tion temperature, up to 1140°C, and for the less sticky ashes (zeroing of Mg sulphate), it however implies high dosages (as a sum of MgO and of B 2 O 3 ) of additives, then found in significant amounts as fly ashes in flue gases, with the well known problems for the technological use of flue gases.

The poor performances of the described prior art, as regards to the additives of vanadium containing fuels, have led towards other solutions, such as the direct pretreat- ment of the fuel in order to activate reactions to elimi ¬ nate the effects of the corrosion due to vanadium.

See for example USP 2,884,369 wherein the fractions containing heavy metals and vanadium are treated with active coal having a high surface area to remove iron, nickel and vanadium at temperatures up to about 400 °C. This tem ¬ perature is specific for the selective removal of the pol ¬ luting metals and such to avoid cracking of the heavy hydrocarbon oil.

Another type of pre-treatment is reported in USP 4,116,820, that describes a process for removing heavy met ¬ als such as nickel and vanadium from heavy hydrocarbon oils by pre-treatment with acidified active coals, carried out at temperatures from 370° to 450°C.

USP 6,013,176 describes a process for removing heavy metals from mineral oil by using hydroxides and carbonates of metals of the first and second group, in the presence of a gas containing oxygen and of a phase transfer agent at temperatures from 100°C to 180°C.

USP 6,372,124 describes a process for purifying hydro ¬ carbons wherein an absorbing material formed (% by weight) by 50-96% alumina and 50-4% calcium oxide and magnesium ox ¬ ide, wherein the ratio by weight CaO:MgO ranges from 90:10 to 50:50 is used, the surface area being greater than 100 m 2 /g, the pretreatment being carried out at a temperature between 20 and 450°C.

USP 7,947,167 describes a method for purifying low- grade fuels from vanadium, nickel and other metals, by con ¬ tacting heavy hydrocarbon fractions with an absorbing agent having a high surface area, such as for example alumina, aluminum hydrate, molybdenum oxide, petroleum coke, activated coal, zeolites, clays, silicates, inorganic oxides or combinations thereof.

USP 5,358,634 describes a process for removing metals from heavy oils by treatment with hydrogen on active coal at temperatures from 260° to 649°C and pressure from 0 to 272 atm.

USP 7,264,710 describes a process for removing vana ¬ dium by treatment of heavy hydrocarbon fractions in the presence of water in supercritical conditions, and of an oxidizing agent. The process is operated at temperatures comprised between 350°-600°C, obtaining the reforming of the hydrocarbon phase and the oxidation of vanadium, which is removed in the presence of a scavenger (calcium or iron), with which vanadium forms mixed oxides.

In general the fuel pre-treatments described in the prior art are effective to remove vanadium-nicKei m tne light fractions (fuel requalification) , but less effective to treat heavy hydrocarbon oils (asphaltenes, petrolenes) when the C/H ratio increases. These pre-treatments repre ¬ sent however a remarkable increase of the complexity of the integral process of using these fuels and they require dedicated plants.

The need was therefore felt to have available a combus ¬ tion process allowing the direct use of low ranking hydro ¬ carbon fractions and fuel residues containing vanadium, in amounts (by weight) from 50 to 5, 000 ppm or higher, at high combustion temperatures higher than 1140°C, without the known drawbacks due to the vanadium aggressiveness towards the plant materials, wherein the addition of remarkable amounts of additives were not necessary and in any case without the production of flue gases with high fly ash concentrations so as to carry out the technological use of the hot combustion flue gases in the energy recovery plants for at least 8,000 h/year, without dangerous emissions of heavy metals in the environment, without substantially attack ¬ ing/corroding the combustor refractories and the build ¬ ing material of the downhill equipments in the case of thermal recovery by production of steam or heat, without substantially having residual and aggressive ashes in the case of use of pressurized hot flue gases coming out from the combustor in turbo-machinery for the energy recovery, that is obtain flue gases having a low content of fly ashes, preferably <10 mg/Nm 3 flue gas dry basis, negligible incombustible residues i.e. with a TOC concentration <1 ppm by weight, IPA<10 ~4 ppm by wt, in particular soot-free, va ¬ nadium or its compounds being in amount lower than 1 mg/Nm 3 flue gas dry basis, and at any rate not detectable at the XRD as aV03, and at any rate as V 2 O 5 in amounts <0.01 mg/Nm 3 flue gas dry basis, said flue gases being not aggressive to the plant building material or such as to reduce the energy recovery efficiency due to adhesive fouling on the walls of the plants used for the heat exchange in the section down ¬ hill of the combustor.

The Applicant has surprisingly and un expectedly found the solution to the above technical problem, that is a com ¬ bustion process capable to chemically transform vanadium quantitatively into not aggressive inert species.

An object of the present invention is an oxycombustion process of low ranking gaseous, liquid, solid, optionally melting solid hydrocarbon fractions used as fuels, having a vanadium content in amounts by weight from 50 to 5,000 ppm or higher, wherein magnesium is added as oxide or as a water-soluble salt, or as a magnesium compound forming MgO in the combustion process, the combustor being refractored, isotherm or quasi-isotherm, flameless, operating at temperatures in the range 1 , 250 ° -1 , 450 °C, under pressurized conditions, wherein the oxidant is oxygen, the oxidant be ¬ ing used in admixture with water or steam such that the ratio by moles oxidant: (water/steam) being comprised between about 1:0.4 and about 1:3, or the oxidant is used in admix ¬ ture with recycled flue gases, coming from the flue gases outletting the energy recovery equipments, the water/steam amount being higher than 30% by volume, optionally by add ¬ ing water to the recycled flue gases, the molar ratio oxi ¬ dant: (water/steam) in the flue gases being as above; the hydrocarbon fraction being fed in admixture with water or steam, the amount of water/steam being least 30% by weight with respect to the fed hydrocarbon fraction.

Preferably the pressure used in the combustor is com ¬ prised from higher than or equal to about 102 kPa to about 5,000 kPa, preferably higher than or equal to about uu K a and up to about 3,500 kPa.

The oxygen is pure oxygen or technical oxygen, that is having an oxygen titre higher than 80% by volume. The complement to 100% being formed by inert gases and/or nitro ¬ gen .

Technical oxygen is obtained from air by cryogenic distillation, or by differential absorption on zeolites, or by separation with ceramic membranes at high temperature, etc. Technical oxygen is available on the market.

In the oxycombustion process technical oxygen having an oxygen content >98.5% by volume is preferably used. Gen ¬ erally also oxygen having 92-94% titre VSA (vacuum swing absorption) and 88-92% VPSA (vacuum pressure swing absorption) can be used. The oxygen in the process of the invention is normally used in excess with respect to the stoichiometric amount required for the reaction. Values from 1% to 3% molar of unconverted oxygen are preferably present in flue gases.

A combustor works under quasi isothermal conditions when the temperature in degrees Celsius in all its inner zones varies at most of ± 5% with respect to the base com ¬ bustion temperature. This means that in practice the com ¬ bustor does not show significant cold zones.

As the magnesium compound forming MgO during combus ¬ tion, both the water-soluble salts, for example MgSC^, and the corresponding water insoluble salts are used. The lat ¬ ter are fed to the combustor as an aqueous suspension.

Preferably the molar ratio Mg:V is in the range 1:1- 2:1, more preferably from 1.25:1 to 1.75:1.

Soot generally means an organic fuel material under the form of aggregates, having particle sizes from 10 nm up to about 10 μιη, more in detail oxygen-rich organic macro- molecules based on carbon and hydrogen (hydrocarbon macro- molecules partially degraded by oxidation reactions], re ¬ sidual in flue gases owing an incomplete combustion.

By alkaline metals (Ma) the metals of the first group of the periodic system, generally sodium, are meant.

When alkaline metals are present in the fuel and the molar ratio Ma:V is preferably lower than or equal to 1:3, mixed and inert orthovanadates of Ma, in particular of Na and Mg, are formed. In the presence of Ma it is preferable to oper ¬ ate with a magnesium excess near to the upper limit of the above indicated Mg:V range. In the case of the Ma amount significantly higher than the above reported molar ratio range Ma:V, preferably a pretreatment of the fuel is car ¬ ried out, consisting of alkaline metal desalting, in order to bring the content of these metals within the above indi ¬ cated values. These methods are well known in the prior art .

When other heavy metals different from vanadium are present in the starting fuel, as for example nickel, iron and cobalt, they are transformed in the combustor into the corresponding oxides.

The Applicant has unexpectedly and surprisingly found that the above oxides promote the transformation of vana ¬ dium compounds into orthovanadates which, as said, are sta ¬ ble and non aggressive. The amount of these metals present in the fuel substitutes equimolar amount of the magnesium used to convert vanadium into orthovanadates.

The amount of water or steam to be mixed with the fuel preferably is not higher than 80-90% by weight with respect to the weight of the hydrocarbon fraction. Above this limit the added amount of water can significantly affect the thermal recovery efficiency. Preferably the combustor oper ¬ ates at temperatures in the range 1300 ° -1400 °C . Among solid fuels, hydrocarbon solids brought to melt ¬ ing/liquefaction by heating and fed to the combustor as viscous liquids, can also be used.

Solid fuels can also be fed after gasification into the combustor of the invention.

Examples of solid low ranking hydrocarbon fractions that can be used are the following: asphaltene, petrolene, carbonaceous substances (in general compounds having high values of the ratio carbon/hydrogen) , Petcoke, carbonaceous residues (ex. POX, partially oxidated hydrocarbons) of the petrochemical processes, refinery vis-breaking bottoms.

Preferably magnesium is added as the corresponding magnesium sulphate dissolved in an aqueous solution.

The added magnesium amount depends on the content of vanadium in the fuel. As said, the molar ratio Mg:V ranges from 1:1 to 2:1 but it can also reach about 4:1. Higher amounts can be used. The upper limit can also be 10:1 or higher without bringing any substantial advantage for the combustion process, with an increase in operative costs.

The isotherm and flameless combustors are known in the prior art, see for example patent application WO 2005/108867 and WO 2004/094904 in the name of the Applicant, herein incorporated by reference.

In the process of the invention the fuel residence time in the combustor preferably ranges from 0.5 seconds up to 30 minutes, more preferably from 2 to 10 seconds. It is possible to use also longer times, if desired.

At the bottom of the combustor, there is a tank for collecting molten ashes, dripping therein in liquid state. In the tank ashes are cooled, for example in a water bath and transferred in a vitrified solid state into static separators (settlers) .

When the flue gases obtained in the combustion process of the invention are used to produce energy by steam produc ¬ tion, or to generate heat for other applications, the flue gases outletting the combustor are cooled in a mixer by mixing them with cold recycled flue gases (from thermal recov ¬ ery) , in ratio hot flue gases/cold flue gases such that the final temperature of the gaseous mixture is about 1,100 K. The decrease of temperature obtained in this way, by strict recycling of flue gases outletting the thermal recovery plant, takes places without enthalpic cycle penalizations (isoenthalpic operation) and has no impact on the energy characteristics of the produced steam, since the technologi ¬ cal maximum temperature of the superheated steam temperature SH, acceptable by steam turbines is of 903 K. Therefore this does not imply any penalization of the yields of the trans ¬ formation cycle from thermal energy to mechanical/electrical energy through Rankine cycle, and allows to obtain a net ad ¬ vantage of using equipments for thermal recovery with wall heat exchange between flue gases and water/steam, built with materials of common use for the same service in conventional power plants .

The refractories of the internal combustor lining of the invention are made of conventional material, preferably of alumina type with the addition of about 10% chromium and about 4% zirconium.

The flue gases corresponding to the net gaseous product of combustion can be removed from the circuit under pressure by lamination (i.e. throttling) to atmospheric pressure. The conventional post-treatments to remove the residual ashes and acidity are carried out, for example by filtration on a bag filter and neutralization by washing with alkalies (lime milk) . When CO 2 has to be recovered, if the fuel produces little chemical water (reaction) , a preferred solution is to operate neutralization (washing) under pressure. Preferably, the part of the flue gases corresponding to the net gaseous product of the combustion is withdrawn down ¬ stream the mixer and expanded to yield mechanical work, and then sent to a thermal recovery unit and the atmospheric post-treatment of flue gases. The expansion can be carried out directly through a turboexpander made of conventional building materials, as flue gases are substantially free from fly ashes and have a temperature of about 1100 K.

In a still more preferred solution for the energy recovery by turbomachinery, the part of flue gases corresponding to the net gaseous product of the combustion is directly withdrawn at the outlet of the combustor, and sent to conventional turbomachines that, owing to suitable engineering modifications of cooling/protection of the metal surfaces by a steam layer, can operate with flue gases up to a tempera ¬ ture of 1,300°C, with a distinct advantage of yield of the power cycle. In fact, in this way it is possible to combine a cycle of the Joule-Bryton type, with the combustor pressurized for example at 1, 500 kPa releasing the hot flue gases with a flow rate equal to the net product of the combustion, directly to a turboexpander, with a Rankine cycle that with ¬ draws heat from the recycled hot gases. In this way, starting from low ranking fuels, yields of transformation from thermal energy to electric energy higher than 55% can for example be reached.

The process of the present invention allows therefore the possibility to use even the above indicated low ranking fuels containing vanadium for high energy efficiency plants having a low environmental impact. These fuels otherwise are not in practice usable in conventional energy plants as they require very complex and expensive plants and in any case op ¬ erating with lower yields.

In the process of the invention the vanadium is recov- ered in a substantially quantitative way from low ranKing ny- drocarbon fractions. Vanadium is isolated as orthovanadate and pyrovanadate, among them nickel orthovanadate, together with other melting ashes, under the form of vitrous, inert beads of easy handling, having a high concentration of useful V and Ni metals largely used in metallurgy.

By the process of the invention the Applicant has sur ¬ prisingly and unexpectedly found the following advantages:

- speeding up of the reactions, also those lazy according to the prior art, up to the quantitative conversion of V 2 O 5 into orthovanadates/pyrovanadates under gas flow condi ¬ tions ;

- segregation of vanadates (both orthovanadates and pyrova- nadates) under the form of liquefied ashes, collected on the refractored walls of the combustor and dripped to the bottom of the combustor, solidified in slags having a vit ¬ reous appearance (beads) , available as a concentrate of V and Ni for recovery in metallurgy;

- the nickel, that on a molar basis is present in these fu ¬ els in an amount in general lower with respect to vanadium, is transformed into nickel orthovanadate and it is avail ¬ able concentrated for the recovery from vitrous slags;

- absence of chemical attack on the refractories of the combustor, also for the conventional ones having an alumina basis, such as for example alumina additivated of about 10% chromium and about 4% zirconium, manufactured in high fired bricks ;

- SO 3 is reduced to negligible values (lower than about 2 mg/Nm 3 of flue gas dry basis) and absence of the aggressive sulphuric condensates on the metal walls of the thermal re ¬ covery equipments, - the combustion is exhaustive, in combustion fumes soot is absent, TOC <1 ppm and with IPA (polyaromatic hydrocarbons, mainly pyrenes) <10 ~4 mg/Nm 3 flue gas dry basis.

The flue gases outletting the combustor operated with the process of the invention, sent the heat recovery sec ¬ tion, besides being substantially soot-free and with IPA and TOC within the above indicated very low limits, sur ¬ prisingly and unexpectedly have given the following results at the analytical characterization:

- fly ash <100 mg/Nm 3 , preferably <50 mg/Nm 3 flue gas dry basis ,

- concentration of magnesium in flue gases, both in the form of oxide and sulphate <1 mg/Nm 3 flue gas dry basis, therefore negligible both for the corrosion and for the fouling of the wall surfaces of the equipments downhill of the combustor,

- vanadium, under the form of inert orthovanadates , (generally of Ni and Mg) and under the form of inert pyrova- nadates, (generally of Mg) in amounts, expressed as vana ¬ dium, ≤1 mg/Nm 3 flue gas dry basis; furthermore V 2 O 5 (in ¬ cluding the submicron particulate) <0.01 mg/Nm 3 flue gas dry basis ,

- SO 3 ≤2 mg/Nm 3 flue gas dry basis,

- NiO ≤1 mg/Nm 3 flue gas dry basis.

NaVC>3 not detectable by XRD and SEM analyses of microaggre- gates .

These features of the process of the present invention are maintained, surprisingly and unexpectedly, even for very high inletting concentrations of heavy metals (Cr, V, Ni) , by using fuels containing for example up to 5, 000 ppm by wt of vanadium and 2, 000 ppm by wt of nickel, and with fuels difficult to be converted such as for example asphal- tenes, residual carbonaceous ashes. The effect to have flue gases with the described char ¬ acteristics implies the reduction of fouling from sticky compounds on the walls of the equipments downhill of the combustor to levels that do not influence their efficiency for a time comparable to the operating factor of a non critical industrial plant (8,000 h/year). More specifically it is deemed that the absence of fouling is due both to the low content of organic non combustible residues and to the likewise low content of magnesium sulphate.

Besides the absence of fouling, the transformation re ¬ actions of vanadium into orthovanadates and pyrovanadates obtainable with the process of the invention, combined with very reduced residual amounts of SO 3 in flue gases, allow, as said, an high operating factor. It has been found by the Applicant, surprisingly and unexpectedly, that there are no corrosion phenomena of the building materials (steel and the stainless alloys and high performance stainless alloys) from both vanadium and the sulphuric acid condensates in the equipments downhill of the combustor.

The process of the present invention allows to de ¬ crease the emissions of the regulated substances (organic compounds, heavy metals) and to reduce, by simplifying them, the unit operations for the post-treatment of the flue gases, as indicated above. In practice only filtration on a bag filter is carried out, with the filtrate recycled to the plant feeding, and neutralization (DeSO x ) of the flue gas sent to the stack.

Morein detail, by DeSO x it is meant the equipment wherein sulphur oxides in flue gases are neutralized.

According to a non binding theory, the Applicant thinks that under the operating conditions of the combus ¬ tion process according to the present invention the following reactions take place: - the flameless combustion conditions decouple/remove part of the catastrophic parameters (non linear parameters) that confer a chaotic character to the oxidation phenomena of the conventional flames. This allows the expansion of the oxidative phenomena to the whole combustor volume in an or ¬ derly and predeterminable way with consequent exhaustive oxidation of the fuel species without soot formation, and the IPA are reduced to insignificant values,

- the high and uniform temperature in the combustor favours the disassociation of the alkaline metal and magnesium sul ¬ phates, to give the corresponding oxides:

M x S0 4 → M x O + S0 3 (being M=Ma with x=2, being M=Mg with x=l) and the reaction of SO 3 to give SO 2 :

S0 3 → S0 2 + ½ 0 2

- magnesium is entirely available as MgO oxide and it is in a sufficient amount to quickly and exhaustively react with V 2 O 5 coming from the thermal oxidation of vanadium contained in the starting low ranking fuels e.g. in porphirins, as there are no competitive reactions wherein the magnesium oxide can be involved. A stable and chemically inert magne ¬ sium orthovanadate is formed:

3MgO +V 2 O 5 → Mg 3 V 2 0 8

and magnesium pyrovanadate:

2MgO + V 2 0 5 → Mg 2 V 2 0 7

V 2 O 5 reacts quantitatively without being it necessary to re ¬ spect a definite stoichiometry Mg-V, as both the positive and negative deviations from the stoichiometric amount of the orthovanadate are absorbed by the formation of pyrova- nadates when the Mg amount is in defect and when the Mg amount is in excess, mixed oxides are formed according to the reaction:

zMgO + yMpOq → (MgO) z - (M p O q ) y wherein M is a metal different from Mg, z and y are inte ¬ gers, that mix with melted orthovanadates ,

- nickel, present as NiO oxide at the temperatures at which the combustor is operated, quickly combines with V 2 O 5 to give a very stable and inert orthovanadate according to the reaction :

3NiO + V 2 0 5 → Ni 3 V 2 0 8

This reaction is influenced only by the presence of high concentrations of iron oxides in the inletting ashes, that are competitive in the formation of vanadates, but of no practical effect on the vanadium content in the flue gases outletting the combustor.

Furthermore, in the preferred temperature range and for a suitable residence time, preferably ≥2 sec, in the combustor, the formed chemical species melt together with the non combustible ashes (mixture of oxides) contained in the fuel and are subjected to liquid coalescence so to col ¬ lapse as drops on the combustor walls, accumulating in a substantially quantitative way (> 99% with respect to the ash balance) at the combustor bottom.

Without being bound to any theory, it is believed that with the process of the invention the condition is achieved that reactants and products, normally subjected to an al ¬ most not controllable complexity of multiple reaction paths, multiplied by a multiplicity of operating condi ¬ tions, in the present invention are only those above indi ¬ cated and therefore very well controllable under flameless conditions (volume combustion) , without significant forma ¬ tion of other species downstream the combustor, as the residual fraction of pollutants in the outletting flue gases is very low; and mainly (the following data are referred to 1 Nm 3 flue gas dry basis) :

- fly ash residue <100 mg/Nm 3 wherein: - Mg <1 mg/Nm ,

- S0 3 ≤2 mg/Nm 3 ,

- orthovanadates and pyrovanadates, expressed as V <1 mg/Nm 3 and V 2 0 5 <0.01 mg/Nm 3 .

- alkaline metavanadates , generally NaV03, not detectable in ashes by XRD techniques and SEM analysis of the microaggre- gates .

In the outletting flue gases there is no significant presence of chemical species capable to give undesired side reactions, such as for example V 2 O 5 , SO 3 , MgSC^ and there have been inactivated the chemical species that could re ¬ generate downstream of the combustor the undesired species

(the mass effect is missing) , even at decreasing tempera ¬ tures but for relatively longer residence times, for exam ¬ ple, the reaction of magnesium oxide to give again sulphate

(sticky ashes) , and the subsequent reactions of the magne ¬ sium sulphate with magnesium pyrovanadate to form again SO 3 .

Still according to a not binding theory the Applicant thinks that in the process of the invention besides the positive effects above said, it has to be taken into con ¬ sideration the quenching effect on the combustion flue gases of cold recycled flue gases (after heat recovery) . That is a first rapid decrease of the flue gas temperature down to 1100 K (much lower temperature than the normal con- vectives of the prior art) takes place, that brings to the kinetic quenching of the possible post-reactions among the species formed in the combustor and residual in the flue gases in the temperature range between 1,700 and 1,100K

(from the combustor to the quencher) .

In the temperature range from 1,100 to 520 K, unavoid ¬ able for proceeding to the heat energy recovery, it is instead critical to have the total conversion of V 2 O 5 , that is the absence of V 2 O 5 in the flue gases. Otherwise, in the range 1,000-800K the conversion of SO 2 to SO 3 , catalyzed by V 2 O 5 , would take place and thus the reappearance of this chemical species responsible for the disastrous sulfur cor ¬ rosion on the thermal recovery equipments.

In this connection it can be added, according to a non binding theory, that the formation of V 2 O 5 particles under gas flow conditions can be hypothesized also on the basis of experimental elements (see methodology (la) in the exam ¬ ples) .

Undoubtedly the chemistry and physical chemistry of the vanadium oxides is made very complicated by the inter ¬ actions with other metal oxides always present in fu ¬ els/industrial processes, with masking effects difficult to overcome also with the most sophisticated characterizations of the flue gases. However blank tests (without interfer ¬ ences) can be carried out. Methodology (la) (see the exam ¬ ples) points out that vanadium alone, at temperatures of 1300-1400°C, gives rise to interaction with the alumina of the tubular reactor (shown by a soft colouring) and however in quantitative low amounts. Vanadium is transformed pre ¬ vailingly into V 2 O 5 particles (submicron sizes), not filter ¬ able on a 0.1 ym filter, not wettable, and that cannot be removed with the usual scrubbing processes, even by using acid solutions and with high oxidizing power in conventional high efficiency contactors (drexels) . Only with a very high contact surface, by using large size drexels, a satisfactory percentage of removal of the introduced vana ¬ dium, equal to 70-80%, can be obtained, by using a working solution acidified with nitric acid at pH 0.5 and brought to an oxidation potential of 1.4 eV with hydrogen peroxide.

Always according to a not binding theory, in the prior art the complex interactions of V 2 O 5 with other oxides do not allow to remove from the population of chemical species containing vanadium, outletting from the combustors, V 2 O 5 particles and sodium metavanadate . On the contrary, the quantitative conversion of V 2 O 5 , surprisingly and unexpect ¬ edly, is obtained with the process of the present inven ¬ tion. The solutions proposed by the prior art are not ef ¬ fective in reducing the attack of vanadium on the materials of the downhill equipments, as it is shown by the presence of vanadium downstream of the flue gas cleaning processes, even after several and complex operations carried out down ¬ hill of the combustion/gasification processes, as in the case of combined cycle turbogas, operated with synthesis gases from gasification.

On the contrary, with the process of the invention, surprisingly and un expectedly, as said, the V 2 O 5 amount is <0.01 mg/Nm 3 flue gas dry basis, i.e. practically below the analytical sensitivity limit, (see the examples, methodolo ¬ gies (la) and (lb)) and the typical traces of V 2 0 5 are not detectable by the EDX and SEM characterizations. Likewise sodium metavanadate is not detectable in the accumulated powders collected on the sampling filter.

It has also surprisingly and unexpectedly found that by increasing the pressure in the pressurized oxycombustion process of the present invention, even without substan ¬ tially modifying the total amount of the residual ashes in the flue gases outletting the combustor, the vanadate con ¬ centration is instead reduced. For example, the temperature being equal, by operating at a pressure of 11 barg (bar gauge - relative pressure) the total amount of the residual ashes is slightly reduced with respect to that obtained at the pressure of 3 barg, while for vanadium (orthovanadates and pyrovanadates ) under the same conditions a significant reduction of about 1/3 is obtained. In addition to the analytical characterization data that, as seen, exclude the presence in flue gases of unde- sired chemical species (MgO, V 2 O 5 and aVOs) up to the sen ¬ sitivity limit of the analysis method, a confirmation of their substantial absence comes from the analysis of the materials used in the plant after many working cycles, for example of 2,000 h/year. Inspection of the internal sur ¬ faces of the combustor (refractories) and of the surfaces of the downhill equipments reveals that no degradation has occurred. This is a further confirmation of the absence of aggressive species as evidenced by the chemical characteri ¬ zation of the outletting flue gases. Therefore there is no interaction of the residual vanadium with these materials (for example carbon steel (CS) and stainless steel (AISI 304) in the whole range of the working temperatures, from 750°C of AISI 304, from 380°C of CS, down to the room tem ¬ perature .

Furthermore the obtainment of flue gases substantially free from aggressive species directly at the outlet of the combustor, the disappearance of corrosive phenomena on the materials, of erosive phenomena from powders, and of foul ¬ ing of the surfaces, allows on the whole to arrange the process flow rates of the flue gases necessary for:

- attemperation of the combustor, in conditions of oxycom- bustion (low ranking) heavy hydrocarbon fractions having a high calorific value, with recycled flue gases collected in a strict loop downstream of the heat recovery,

- quenching the flue gases outletting the combustor, in order to lower temperature to values (700-800°C) compatible with the use of conventional materials in the heat recovery equipments, by direct flue gas recycle, at strict loop and directly under the process pressure, without carrying out cleaning operations or removing undesired species, obtain- ing the maximum thermodynamic efficiency and tne minimum increase both in operating and fixed costs.

As already said, the process of the present invention allows, surprisingly and unexpectedly, to treat hydrocarbon fractions having a very variable vanadium content, also in a range of some orders of magnitude, allowing the removal of V2O 5 and of NaVC>3 from the flue gases downstream of the combustor, therefore without no corrosion in the downhill equipments and without no sintered or sticky fly ashes that adhere to the walls of these equipments owing to the acti ¬ vation of specific mechanisms (stoichiometric, quantita ¬ tive) easily adjustable to the most different typologies of vanadium content of fuels. Unexpectedly and surprisingly with the process of the invention there are no penaliza ¬ tions in the efficiency of the energy recovery equipments since the cleaning of the surfaces of the downhill equip ¬ ments during a working period even prolonged in time, for example higher than 8,000 h/year, is not required.

For amounts of vanadium higher than 5,000 ppm, vanadium concentrations from about 6,000 to 8.000 ppm are meant.

The amounts of additive used range from 0.5% to 2%. If desired, also higher values can be used.

The following examples are merely given for illustra ¬ tive purposes and are not limitative of the present inven ¬ tion.

EXAMPLES

Characterization

Analytical methods

Characterization of the particulate in flue gases

The particulate contained in the combustion flue gases is collected by means of an impactor of the Andersen Mark III type equipped with: one pre-separator (cyclone) capable to remove particles having an aerodynamic diameter greater than 10 ym, screens for impactor Andersen for particulate PM 10, by using a sampling flow of 14 liter/min, and filters able to separate fractions having particle diameter, respectively, of 10-9 μιη; 9-5.8 μιη; 5.8-4.7 μιη; 4.7-3.3 μιη; 3.3-2.1 μιη; 2.1-1.1 μιη; 1.1-0.7 μπι; 0.7-0.4 μπι.

The particulate having particle sizes lower than 0.4 μιτι, that is not retained in the last stage of the impactor Ander ¬ sen, is filtered on mica filter for analysis with the atomic force microscope by means of a pneumatic actuator that col ¬ lects, by thermophoretic effect, a sufficient and statisti ¬ cally significant amount of particles. The gaseous flow out- letting the impactor is then conveyed into a condensation system of the combustion steam, wherein the sub micron particulate is collected, together with a part of the particu ¬ late having a diameter lower than 10 nm, in an amount comprised between 1% and 10% by weight of the original particle population having nanometric sizes. The sampling step makes available particle fractions that are then subjected to the chemico-physical analysis by scanning electronic microscopy (SEM) and to the X-ray analysis. The chemical analysis of the single particles is carried out with a microscope SEM PHILIPS XL30, equipped with a thin window EDX system for the microanalysis by energy dispersion spectrometry, by using an automatic system capable to automatically detect the particles when a determined threshold is exceeded.

For each of the identified particles the morphological parameters are determined by measuring the intensities of the lines typical of the X ray spectrum and converting into the corresponding atomic concentrations.

Analysis of the metals

The analysis is carried out by induction-plasma spectroscopy by using an ICP device (inductive coupled plasma) -OES (Thermo Electron Corporation) .

For the solid phases, the compounds are analyzed by XRD (X- Rays Diffraction), combined with ICP.

Chemical potential (eV)

The potential of the solutions has been determined with a potentiometer .

Soot analysis

Soot analysis is carried out by SEM microscopy.

Partially combusted fuel molecules tend to aggregate them ¬ selves into clusters (microaggregates ) of different size and very irregular shape.

These particles, called cenospheres and plerospheres , are representative of soot (also known as Diesl Particles, or Black Carbon) and are clearly identifiable at SEM micro ¬ scope .

Result evaluation

By Andersen Probe, SEM, and EDX analysis cenospheres and plerospheres are not detectable. If present, they are below the sensitivity limits of these analytical methods.

Other analytical methods that have been used are reported under example 1.

The other methods used in the example are of common prac ¬ tice and well known to the skilled in this art.

For example the flue gases from the reactor are detected by a set of fast response analysis unit (T95, 1.5 seconds), specifically developed by Fisher-Rosemount able of monitor ¬ ing both the bulk compounds, CO 2 , and the "micro" compounds CO, NO, NO 2 , SO 2 , and TOC (total organic content, hydrogen flame detector) . The analytical units analyze the gases at a frequency of 10 Hertz. The original signal is recorded, skipping the data smoothing software. The closed cycle flue gases of the reactor are monitored in parallel, as soon as they are laminated to atmospheric pressure by a group or F IR sensors which detect H 2 0, C0 2 , CO, NO, N0 2 , HC1 with a response time of 40 seconds.

EXAMPLE 1

In a tank equipped with tracings and steam heat exchanger, an oil fraction obtained from the refinery operations of an heavy oil is loaded and collected on the bottom of the vis- breaking section.

At the calorimetry characterization, the hydrocarbon fraction shows a LHV (Low Heating Value) value of 39,350 kJ/kg. The material subjected to pyrolysis at the temperature of 605°C has an incombustible ash amount of 0.67% by weight. The analysis by optical ICP (ICP-OES) shows that the ashes are mainly formed of alumina and silica and to a lower extent of calcium.

Sodium is in concentration of 1.41% by weight in the ashes. The ashes contain also heavy metals, among which the following ones:

Nickel 42 ppm weight

Vanadium 287 ppm weight

By a gear pump fuel is fed to a 5 MW flameless thermal com- bustor, using as comburent (oxidant) oxygen having a titre 93% by volume, operated at 1,650 K and at the pressure of 5 barg (600 kPa) , and inserted in a demonstration plant. The fuel flow rate determined by a Coriolis type fluxmeter is 8.2 kg/min. The injection into the combustor is carried out by means of a nozzle by using pressurized steam for the disper ¬ sion (dispersion only, not atomization) of the inletting jet. The steam sent to the nozzle head comes from the heat recov ¬ ery steam generator, and it is laminated at 13-14 bar, fed at the flow-rate of 65 kg/h, added of water at a rate of 95 kg/h, dispersed in the steam through an atomizer.

Oxygen having a titre 99.85% vol. is fed at a flow-rate of 18.2 Nm 3 /min. The used oxygen comes from a cryogenic storage plant equipped with an evaporator. Oxygen is mixed with compressed air added at the flow-rate of 2.4 Nm 3 /min. The gase ¬ ous mixture is introduced into the current of the recycled flue gases fed to the combustor to attemper it.

By means of a second injection nozzle a solution of magnesium sulphate 0.2 M, is fed at a rate of 0.33 litres/min.

The demonstration plant has equipments according to the art .

The flue gases outletting the combustor are cooled in a quencher by mixing with recycled flue gases to a final tem ¬ perature of about 1, 050 K, and sent to the heat recovery equipment (steam generator train, with superheater SH, evaporator EVA and final heat recovery ECO) . Downhill of the heat recovery equipment the flue gases, having the tem ¬ perature of about 520 K, are divided in recycle flue gases (sent to the combustor and to the quencher) compressed by means of a blower and in produced flue gases sent to the FGT section (flue gas post-treatment) after lamination from the pressure of the process to a pressure slightly higher than the atmospheric one.

The produced superheated steam SH (400°C, 40 barg) is quan- titated by a calibrated flange before being sent to the condenser .

In the FGT section, the flue gases are filtered on a bag filter with a vermiculite powder precoat, then neutralized with a Venturi type contactor by means of lime milk (DeSO x ) , before being sent to the stack.

In by pass the section for the sampling of heavy metals is available, that operates by the Andersen impactor (see above) , located between the bag filter and the Venturi type contactor .

The analytical equipment for controlling stack emissions is formed of an analyzer battery in continuum, operating on a current continuously sampled from the recycled gases after removal (Peltrier) of moisture, consisting of:

FTIR for the determination of SOx, CO, besides TOC

NDIR for the mass components,

HFID (hydrogen flame detector) for the continuous analysis of TOC (total organic content) , and

zirconium probe for oxygen.

In by pass with the stack flue gas powders are sampled for determining total powders and heavy metals (methodologies according to the European regulations) .

In the same way, but with a batch modality, flue gases are sampled for 8 hours for determining dioxins, furans, PBC (polychlorobiphenyls ) , IPA.

An analytical unit is arranged for the batch sampling of the flue gases for specific determinations on the powders (vanadium and besides nickel, magnesium) , in the following positions of the process.

Point 1. downstream the combustor, in detail downstream the quencher .

Point 2. downstream the bag filter.

Point 3. downstream the DeSO x (at the stack) .

Powder determination in flue gas is carried out by using the following devices in sequence, (see methodologies (la) and (lb) (see below)): quartz fiber filter (particle size cut 0.1 μιη) , condenser positioned in a thermostated bath at 12 °C, a drexel filled with water (drexel 1) , a drexel filled with acid (drexel 2) , and, as last a drexel having a high contact time, filled with an aqueous solution pH 0.5 acidified with nitric acid and brought to an oxidizing power of 1.4 EV by means of hydrogen peroxide, and a litre-counter of the ex ¬ tracted uncondensable fractions.

The run of the combustion process lasted 600 h (25 days) . At the end the plant is disassembled at some specific points for collecting powder samples, for the core sampling of the refractory coatings, for the extraction of the metal specimen (various metals and alloys) for characterization.

Point 3.

Determinations in continuum during the run on the flue gas sent to the stack.

Among the values of the analytical determinations, the fol ¬ lowing (values expressed in mg/Nm 3 of flue gas dry basis) are pointed out:

average peak value

CO 2.3 11

TOC <0.1 0.6

The average values of the batch analytical determinations at the stack (see above) (8 determinations, 5 of which in the first week) for parachlorodibenzodioxins/furans (PCDD/F) and polyaromatic hydrocarbons (I PA) were as it follows (referred to flue gas dry basis) :

PCDD/F ng I-TEQ/Nm 3 0.0003

IPA μg/ m 3 <0.05

On the flue gas powders, the following average values have been determined, expressed as mg/Nm 3 flue gas dry basis, of total powders, Ni, Mn and V, respectively:

Total powders 1.2

Heavy metals

Ni 0.008

Mn 0.002

V <0.001

All the other metals having regulated emissions, each <0.001 mg/Nm 3 . The flow rate of the produced flue gases, on a dry basis, calculated by the flow-rate determinations and the composi ¬ tion analyses is of 940 Nm 3 /h, including a flow-rate of about 50 Nm 3 /h of air used for fluxing the analytical instruments and other items .

The batch analyses of the powders in the other sampling points of the process for the characteristic components (V, Ni, Mg) have given the following average results expressed in mg/Nm 3 flue gas dry basis.

Point 1.

Downstream of the combustor:

Filter

The powders present in the flue gases have been collected on a ceramic fiber filter (size cut 0.1 μιη) , dried and weighed. In order to take into account the total volume of dried flue gas of 400 litres, as determined by the volumetric counter, the dry powder amount was multiplied by the factor 1/0.4=2.5, to obtain the corresponding value expressed as mg/Nm 3 flue gas dry basis:

Total powders 88

Condenser

In the condenser the water present in combustion fumes is condensed to a dew point of 18 °C. 263 ml of condensate are collected on a total dried flue gas volume of 400 litres.

The amount of each heavy metal found in the condensate is multiplied by the coefficient 0.236/0.4=0.6575, to give the corresponding amount expressed as mg/Nm 3 flue gas dry basis: Ni 0.91

Mg 0.002

V 0.02

(the solution has pH 1.1)

Drexel 1 + drexel 2 content

In each of the two drexels the solution amount was of 30 ml. These solutions were pooled and the amount of each heavy metal, expressed as Mg/Nm 3 flue gas dry basis, was calculated by multiplying the found analytical value by the coefficient 0.06/0.4=0.15. The following values are obtained:

Ni 0.02

Mg 0.03

V <0.001.

Drexel 3

The solution volume in drexel 3 was of 60 ml. By making the calculation as for the heavy metal content of Drexel 1+ Drexel 2, the following amounts of heavy metals were found: Ni <0.001

Mg <0.001

V <0.001

Part of the solid collected on the filter has been set aside, and the collected fractions pooled and the following analyses have been carried out: the determination of the absolute com ¬ position by ICP-OES, the determination of the phases composi ¬ tions by XRD, the SEM visualization of the micro aggregates. At the analysis XRD neither V 2 O 5 or NaV03 phases are detected. At the SEM analysis the typical rods of V 2 O 5 are absent.

SO 3 concentration, measured on spot samples of recycled flue gases, is comprised between 0.5 and 1.5 mg/Nm 3 flue gas dry basis .

The vitrous slags discharged from the settler and collected in bath, accumulated during the run 600 hours, amount to slightly less than 2 t. The analysis on samples drawn from different bags show that they contain variable amounts of silico-aluminates . The vanadium percentage is on the average 4% by weight and nickel 0.5% by weight.

The inspection performed at the end of the run on the disas ¬ sembled parts of the plant shows that there are no sticky powders and that the residues deposited in dead zones are in a negligible amount. The DCS data of the process parameters indicative of the heat exchange efficiency show that during the run efficiency has remained substantially constant, in line with the preceding observations.

The collected powders have been analyzed at XRD and SEM. Nei ¬ ther V 2 O 5 nor aV03 phases have been detected.

Specific characterizations of V 2 O 5 of example 1 carried out in a gas flow reactor - methodology (la)

In a tubular reactor having a 50 mm diameter, made of high purity alumina, thermostatted in an oven at 1400°C, a gase ¬ ous current of CO 2 and O 2 is fed in a molar ratio 90:10 at a rate of 6.3 Nlitre/min.

Through a Venturi type feeder, an injector disperses in the air flow an aerosol of a 0.1 M vanadium aqueous solution (a solution of VOSO 4 , vanadylsulphate) at the flow rate of 20 ml/h, for 8 hours.

The gases outletting the tubular reactor are quenched with a metal "finger" cooled with water, passed on a glass fiber filter with a 0.1 μιη particle size cut and are then intro ¬ duced into a flask (condenser) placed in a thermostated bath at 18°C, wherein the excess moisture is condensed. A battery of three drexel type vessels, connected in series, i.e. in succession, drexel 1, drexel 2, drexel 3, is joined by a tube to the outlet of the condenser. In each vessel (drexel) the gas bubbles through a steady aqueous phase, so that the contact liquid/gas takes place with an high effi ¬ ciency. The first vessel (drexel 1) joined to the con ¬ denser, contains 30 ml of demineralized water, the second one (drexel 2) contains 60 ml of acidified water at pH 0.5 with nitric acid, the third and last one (drexel 3) con ¬ tains 300 ml of acidified water at pH 0.5 with nitric acid and brought to an oxidation potential of 1.4 eV by addition of hydrogen peroxide. After 8 hours the aerosol feeding is stopped and the reactor is kept under a weak flow of dry air at the temperature of 1300°C for 16 hours.

The operation is repeated three times, as a whole 0.048 gmoles of vanadium, equal to about 2.5 g of vanadium, are fed .

At the end of the test the tubular reactor is disassembled and broken into fragments. By XDR analysis of these frag ¬ ments it is found that a penetration of V 2 O 5 , quantitatively (ICP) not very significant, has taken place in the reactor walls .

The condenser is disassembled and the internal surface of the flask, after removal of the condensate from the bottom of the flask, is cleaned by means of a spatula and then with a washing acid aqueous solution. The washing solution is then pooled with the condensate liquid phase. The final volume of the condensate liquid phase is found to be 430 cc. This phase is subjected to ICP analysis. Likewise, the solution of drexel 1 is subjected to ICP analysis.

The vanadium concentration in the analyzed samples is <0.01 yg/litre .

The liquid phase contained in drexel 2 is analyzed by ICP. The vanadium concentration is <0.01 μg/litre.

It is noted that the addition of Drexels 1 and 2 has no im ¬ pact on the vanadium mass balance, as the vanadium concentration is below the analytical sensitivity limit.

In Drexel 3 the vanadium concentration is of 1.6 mg/litre, equal to a collected vanadium amount of 0.016 gmoles.

By multiplying the amount in g/litre by the volume of the solution (0.3 litre) it is found that the vanadium amount in the drexel is of 0.48 g, that is about 20% of the inlet- ting vanadium.

Second part of the methodology (la) By operating under the same conditions as in the first part but with the following modifications:

halving the flow rate of the vanadium solution and of the transport gas,

by providing in drexel 3 a solution volume of 450 cc with a more efficient dispersion and a longer contact time, thus with a very high efficiency, the concentra ¬ tion of the recovered vanadium is 1.98 g/litre.

The mass balance closing value is >70%, that results more acceptable, the corpuscolar nature of V 2 O 5 generated in the reaction gas flow can be shown.

Specific characterizations of V 2 O 5 of example 1 carried out in a gas flow reactor - methodology (lb))

In a tubular reactor of the same type as that used in the methodology (la), a gaseous current of CO 2 and O 2 is fed in a molar ratio 90:10, at a flow rate of 6.3 Nlitre/min and SO 2 analytical grade directly from a bomb at a flow rate of 0.01 Nlitre/min.

Through a Venturi type feeder, an injector disperses in the oxygen flow an aerosol of an aqueous solution obtained by mixing:

0.1 M VOSO 4 (vanadylsulphate) ,

0.125 M MgSC (water-soluble magnesium sulphate),

to have a molar ratio magnesium: vanadium 1:1.25, the flow rate being 20 ml/hour.

The experiment lasts 8 hours.

The gases outletting the tubular reactor are cooled as de ¬ scribed in methodology (la), then they are sent on a glass fiber filter with a 0.1 μιη particle size cut and in se ¬ quence, to the same equipments described in the methodology (la) second part as regards the high efficiency drexels. The test is carried out with the same modalities and times described in the methodology (la) for a total feeding of 0.048 gmoles of vanadium (about 2.5 g) .

At the end of the test the tubular reactor is disassembled and reduced into fragments. The surfaces of the fragments forming the internal wall of the tubular reactor, that during the test have been into contact with the vanadylsul- phate aerosol, at the visual inspection look dark-coloured, with a more evident thickness especially in the part of the external tube outletting the oven. However the XDR analysis on these fragments does not show vanadium penetration. The analysis of the dark surface layer carried out by XRD, shows the presence only of the phases magnesium orthova- nadate and magnesium pyrovanadate.

The solid deposit on the filter is analyzed by XRD, com ¬ bined with ICP analysis. The weight of the collected solid is 47 mg. Upon dissolution in an aqueous phase, by ICP it is found that the amount of vanadium in the collected solid is 15.6 mg .

The condenser is disassembled, the internal surface care ¬ fully washed with an aqueous acid solution, that is then weighed and pooled with the condensate collected at the bottom of the condenser. The volume of the recovered solu ¬ tion is of 425 cc.

The ICP analysis shows that magnesium and vanadium are pre ¬ sent at molar ratios MG/V intermediate between the stoichi- ometry of magnesium orthovanadate and magnesium pyrova ¬ nadate. In the collected fraction 0.9 mg of vanadium are present .

Likewise, the liquid phase contained in drexel 1 is sub ¬ jected to ICP analysis. The vanadium concentration, meas ¬ ured by ICP, results below the sensitivity analytical limit (<0.01 g/litre) . The same for the liquid phases of both drexel 2 and drexel 3, respectively.

The closing mass balance for the vanadium is 96%, taking also into account of the material deposited on the alumina tubular reactor and on the cold finger.

EXAMPLE 2 comparative

The same 5 MWt demonstration unit is used with the same mo ¬ dalities reported in example 1, but the fuel is fuel oil Bun- ker-C containing 41 ppm of vanadium. The fuel feeding rate is 7.8 kg/min .

The combustion is carried out without the addition of addi ¬ tives (MgO) , for a run of 120 hours.

At the end, after cooling and disassembling the parts of the equipments, the ashes deposited on the walls of the heat re ¬ covery steam generator and in the elbows of the flue gas pip ¬ ing are collected.

the ICP-OES analysis of these ashes shows that the vanadium amount is 2.6% by weight.

By XRD it is also possible to identify in the ashes the phases of V 2 O 5 and of aV03 and, by SEM, the typical rods of V2O5.

At the bottom of the economizer (ECO) , on the surfaces of the heat exchange tubes iron sulphates are present.

The specimens of alloyed material (AISI 304H) are found al ¬ ready degraded on the surface by formation of nickel va ¬ nadates (nickel deriving from the alloyed material) .