| 1. | A method of treating a chrysotile asbestos containing cementitious material installed on a substrate in a building, to provide a fireproofing asbestos free building material thereon, comprising: (a) providing an admixture composition derived from admixing (i) water, (ii) at least about 30% by weight of phosphoric acid, and (iii) from about 0.1 to about 4% of a source of fluoride ions; (b ) applying said admixture composition to the chrysotile asbestos containing building material; (c) permitting said admixture composition to penetrate the building material and contact the chrysotile asbestos contained therein; (d) allowing said composition to remain in contact with the chrysotile asbestos containing building material for a sufficient period of time to reduce the amount of chrysotile asbestos contained therein to less than 1 % by weight. |
| 2. | The method of Claim 1, wherein the cementitious material is a gypsumcontaining cementitious building material in the form of a coating on a building component substrate. |
| 3. | The method of Claim 2, wherein said composition is applied in the form of a foam. |
| 4. | The method of Claim 2, wherein said composition further contains a metal corrosion inhibiting agent. |
| 5. | The method of Claim 2, wherein the acid is phosphoric acid present in a concentration of from about 30 to about 45 weight percent, and wherein the source of fluoride ions is a salt selected from the group consisting is a hexafluorosilicate or tetrafluoroborate salt of an alkali metal, alkaline earth metal, or ammonia, or mixtures of said salts present in a concentration of from about 0.5 to about 2 percent by weight based on the total weight of said composition. |
| 6. | The method of Claim 5, wherein said composition further contains a component capable of inhibiting corrosion of metals in contact therewith. |
| 7. | The method of Claim 1, 2, 3, 4, 5 or 6, wherein said composition is applied in an amount of from about 8 to about 20 parts by weight based on the weight of chrysotile asbestos contained in the building material being treated. |
| 8. | A composition capable of transforming an asbestoscontaining material to a cementitious material containing less than 1% by weight of chrysotile asbestos, comprising a mixture of (a) water, (b) phosphoric acid, and (c) a source of fluoride ions; wherein the phosphoric acid is present in a concentration of from at least about 30 weight percent of the composition and the source of fluoride ions is present in a concentration of from about 0.1 to about 4 weight percent of the composition. |
| 9. | A composition capable of transforming an asbestoscontaining material to a cementitious material containing less than 1 % by weight of chrysotile asbestos having fireproofing properites derived from admixing (a) water, (b) phosphoric acid, and (c) a source of fluoride ions; wherein the phosphoric acid is present in a concentration of at least about 30 weight percent of the composition and the source of fluoride ions is present in a concentration of from about 0.1 to about 4 weight percent of the composition. |
| 10. | The composition of Claim 8 or 9, wherein the source of fluoride ions is selected from an ammonium, alkali metal or alkaline earth metal hexafluorosilicate or tetrafluoroborate. |
| 11. | The composition of Claim 8 or 9, wherein the acid is present in a concentration of from about 30 to about 45 weight percent of the composition. |
| 12. | The composition of Claim 10, wherein the acid is present in a concentration of from about 30 to about 45 weight percent of the composition. |
| 13. | The composition of Claim 8 or 9, wherein the source of fluoride ions is present in a concentration of from about 0.5 to about 2 weight percent based on the weight of the composition. |
| 14. | The composition of Claim 10, wherein the source of fluoride ions is present in a concentration of from about 0.5 to about 2 weight percent based on the weight of the composition. |
| 15. | The composition of Claim 8 or 9, wherein said phosphoric acid is present in a concentration of from about 30 to about 45 weight percent and the source of fluoride ions is an alkali metal alkaline earth metal or ammonium hexafluorosilicate or mixtures thereof present in a concentration of from about 0.5 to about 2 weight percent based on the weight of the composition. |
| 16. | The composition of Claim 10, wherein said fluoride source is selected from ammonium hexafluorosilciate, magnesium hexafluorosilicate or sodium tetrafluoroborate or mixtures thereof. |
| 17. | The composition of Claim 8 or 9, wherein said mixture further contains a component capable of causing said composition to be in the form of a foam which is stable for at least about 1 minute. |
| 18. | The composition of Claim 10, wherein said mixture further contains a component capable of inhibiting corrosion of metals in contact therewith. |
| 19. | The composition of Claim 10, wherein said mixture further contains a component capable of causing said composition to be in the form of a foam which is stable for at least about 1 minute. |
| 20. | The composition of Claim 8 or 9, wherein said phosphoric acid is present in a concentration of from about 30 to about 45 weight percent and the source of fluoride ions is an alkali metal, alkaline earth metal, or ammonium tetrafluorosilicate or mixtures thereof present in a concentration of from about 0.5 to about 2 weight percent based on the weight of the composition. |
This invention was made with Government support under contract DE-
AC02-76CH00016 awarded by the Department of Energy. The Government has
certain rights to this invention.
RELATED APPLICATIONS This application is related to the following commonly assigned
applications, which have been filed simultaneously herewith and the disclosures of which have been incorporated herein by reference in their entirety:
(1) Serial number 08/721,854 (Docket No. 8903), entitled COMPOSITION
AND METHOD TO REMOVE ASBESTOS;
(2) Serial number 08/721 ,859 (Docket No. 9032), entitled COMPOSITION
AND METHOD TO REMOVE ASBESTOS;
(3) Serial number 08/721,858 (Docket No. 9161), entitled COMPOSITION
AND METHOD TO REMOVE ASBESTOS;
(4) Serial number 08/721,863 (Docket No. 9225), entitled COMPOSITION AND METHOD TO REMOVE ASBESTOS ;
(5) Serial number 08/721,857 (Docket No. 9166), entitled FOAM
COMPOSITION FOR TREATING ASBESTOS-CONTAINING MATERIALS
AND METHOD OF USING SAME; and
(6) Serial number 08/721 ,853 (Docket No. 9130), entitled CORROSION
INHIBITING COMPOSITION FOR TREATING ASBESTOS CONTAINING MATERIALS.
BACKGROUND OF THE INVENTION
This invention relates to methods and compositions for digesting the chrysotile form of asbestos ( "chrysotile asbestos") to provide a non-asbestos material while the chrysotile asbestos is a component of a gypsum-containing
cementitious composite, and especially to methods and compositions for the in-
place digestion of chrysotile asbestos present in composite material that i.s bonded to a support structure.
Chrysotile asbestos is a serpentine asbestos fibrous-like material consisting
of alternating layers of silica and magnesium oxide/hydroxide bound to each other through covalently shared oxygen. At least in part because of its availability and unique fire resistance and
thermal properties, chrysotile asbestos has been used commercially in a variety of
building products, including, for example, fire resistant roofing shingles, acoustical plasters, fire resistant and thermally insulating coating compositions and the like. In the formation of fire resistant coating compositions, found to be appropriate for
treatment by the present invention, small amounts of chrysotile asbestos were
mixed with a settable bonding material, such as calcium sulfate hemihydrate and, optionally, other materials such as vermiculite and the like. The composition was
then applied to a structure where it forms a hardened gypsum-containing coating. For example, such compositions found considerable use in multi-story buildings
wherein the gypsum-containing composition was applied as an adherent coating to
steel girders, floor support plates, concrete decking and the like to provide fire resistance and high-temperature thermal insulation properties which aid in
preventing damage and even possible collapse of such buildings in the event of
fire.
In recent years asbestos has been classified as a regulated material in the United States. Federal, state and local government agencies also have promulgated
regulations dealing with the use and disposal of asbestos-containing building
materials. The U.S. Environmental Protection Agency ("EPA") has defined
asbestos-containing material ("ACM") as a material containing therein greater than one percent (1%) asbestos. In accordance with various regulatory procedures,
various safeguards are employed to protect workers from inhaling asbestos fibers
during the removal or demolition activities. Such safeguards include, among others, requiring workers to wear approved respirator or breathing apparatus, as well as protective clothing, requiring any area in a building in which asbestos-
containing material is being removed to be isolated or enclosed from the remainder
of the building, and requiring the enclosed work area to be kept at a negative pressure by the use of special apparatus equipped with HEPA filters to prevent airborne asbestos fibers from leaving the work area. Such isolation of the work
area is an expensive and time consuming part of the process.
Generally, prior art methods for handling asbestos-containing building
materials have taken several approaches. One approach has been to chemically alter asbestos fibers before using them in building products. This approach is
discussed, for example, in U.S. patents 4,328,197 and 4,401 ,636, both to Flowers,
and in U.S. patent 4,474,742 to Graceffa et al.
Greceffa et al (U.S. 4,474,742) teach treatment of asbestos with hydroxamic acid and iron chelating agents to remove the iron present in the asbestos based on
their presumption that the iron is the harmful component. In the Flowers patents
(U.S. 4,328,197 and U.S. 4,401 ,636), one is taught to contact asbestos fibers with an aqueous solution of a weak base/strong acid or a strong base/weak acid salt of manganese, chromium, cobalt, iron, copper or aluminum or mixtures thereof, to
convert the asbestos fibers into a metal-micelle product. In general, the process
contemplated by Flowers is effected by preparing a slurry of asbestos fibers in an aqueous solution of the appropriate salt, effecting the conversion of the asbestos
fibers to metal-micelle fibers in the slurry, and recovering the metal-micelle fibers
from the slurry for use in the subsequent preparation of the desired fiber-containing
end product.
Another approach is to treat previously formed asbestos-containing building materials by encapsulating the materials to thereby prevent the asbestos fibers from
becoming airborne. A resinous encapsulating coating material typically would be
applied by spraying, brushing or troweling. Care must be taken when using encapsulating methods so as not to physically damage the building material being
encapsulated. Encapsulation is a containment method and, thus, the encapsulated material remains in place during the life of the building.
A number of removal techniques have been proposed, and each has its advantages and disadvantages. For example, it has been proposed to simply scrape
or chip away at dry untreated asbestos-containing material and to collect the
scrapings for discard. This technique, which is referred to as dry removal, is
generally considered unacceptable by regulatory agencies since it provides no safeguards against the release of airborne asbestos particles.
Dry vacuum methods have been attempted to overcome the problem of dry
removal by incorporating an exhaust filtering system to prevent pollution to the
outside environment and by using sealed containers for storing and discarding the collected asbestos-containing material. One of the disadvantages of this dry vacuum method is that the bond between the dry building material and the
underlying surfaces on which it is coated may be stronger than the vacuum
capabilities of the equipment. In those cases, it is necessary to dislodge at least a portion of the asbestos-containing material by scraping or chipping, which has the same limitations as the dry removal process described above.
Wet removal processes have been developed as a means for reducing the problems associated with the various dry removal techniques. Wet removal generally involves wetting a building material with water or water-surfactant
solution to soften it and to thereby facilitate its removal. Wet removal clearly
represents an improvement over dry removal. However, the use of water as a
softening agent is not entirely satisfactory because water penetrates slowly, does
not completely wet most building materials, and tends to run off the surfaces being
treated.
Over the past several years, wet removal techniques have been improved by
devising more effective wetting and/or softening compositions. Recent U.S. patents which relate to such improved wet removal techniques include, for
example, U.S. patent 4,347, 150 to Arpin; U.S. patent 4,693,755 to Erziner; and
U.S. patent 5,258,562 to Mirick et al.
The Arpin patent discloses a technique for wetting and removing friable insulating materials from an underlying substrate using a two-part wetting system.
The first component comprises an aqueous alkali metal silicate dispersion blended
with a cationic or nonionic surfactant and the second component comprises a mixture of an acrylic latex and a reagent that is reactive with the alkali metal
silicates in the first part. The two parts are stored separately and are mixed shortly
before use to form a stripping composition which facilitates the removal of the
building material while encapsulating the individual asbestos fibers contained
therein. The removed material must be handled as an asbestos-containing material.
The Erzinger patent exemplifies a wet method for removing asbestos-
containing materials from a substrate. This patent discloses applying a
composition containing a cellulosic polymer to the asbestos-containing material, allowing the cellulosic polymer-containing composition time to penetrate and wet
the asbestos-containing material, removing the wet material from the underlying
substrate by mechanical forces, and collecting the removed material for discard.
The Mirick et al patent is centered on the concept of removing asbestos
fiber containing building material by applying a dilute aqueous solution of an acid,
which may include a separate source of fluoride ions such as an alkali metal or
ammonium salt of hydrofluoric acid, to the building material for the purpose of
conditioning the material to aid in its removal while partially converting the asbestos fibers. The building material, after having been treated with the dilute
acid solution, preferably is removed for further treatment and/or discard. Mirick
et al further contemplate that the wet building material, once removed, can then be
digested by immersing the material into a bath of an acid solution, preferably with heating and agitation, until all of the asbestos material has been destroyed.
The problems of wet removal techniques include the requirements of
physical removal and handling of the wet asbestos-containing material. In
addition, the removed material must be further treated to destroy the remaining asbestos component if the material is to be discarded as a non-asbestos-containing
material.
In the process described in Mirick et al, in which a combination of acid and fluoride source is used, the formed solution generates excessive hydrogen fluoride noxious gas while in storage and during application which presents a health hazard to the applicator. The Office of Safety and Health Administration ("OSHA") has
set an upper permissible exposure limit of three (3) parts per million of hydrogen fluoride in the atmosphere.
U.S. Patent 5,472,562 to Ziger relates to etch baths containing a
combination of phosphoric acid, nitric acid and hydrofluoric acid to selectively
remove silicon nitride from an integrated circuit having a silicon substrate. This reference discloses that various soluble silicon compounds can be used as part of the etch bath. However, the concentration of the acids and the soluble silicon
compound to be used is not disclosed; nor is there any suggestion of using the etch
bath in applications other than integrated circuit manufacture. While there have been improvements in the treatment and handling of asbestos-containing building materials in recent years, the search continues for still
further improvements.
SUMMARY OF THE INVENTION
It is an object of the invention to provide an improved composition for digesting chrysotile asbestos to provide non-asbestos material.
It is another object of the invention to provide an improved composition
and method for treating gypsum-containing cementitious building materials which
contain chrysotile asbestos to transform the building materials to non-asbestos materials (i.e., materials which contain less than 1 % chrysotile asbestos), while
they are part of the building environment and supported on an underlying substrate.
Another object is to treat a building material which contains gypsum,
chrysotile asbestos and, optionally, other fillers such as vermiculite, while part of a building structure, to transform the building material to a non-regulated material,
without removing the building material from its underlying substrate and without
substantially impairing the physical integrity and heat insulating properties of the
building material.
An additional object is to provide a composition which is capable of
treating a chrysotile asbestos containing gypsum material while part of a building
structure to transform the building material to a non-regulated material which
exhibits enhanced toughness while retaining its heat-insulating properties.
A still further object is to provide a treating composition which fulfills the
objects stated above without generating hydrogen fluoride gas in excess of present
OSHA limits during storage and use.
In accordance with the invention, these and other objects and advantages
are achieved by the present composition and method for transforming chrysotile
asbestos material to non-asbestos material. The composition comprises a unique combination of water, a high concentration of phosphoric acid , and a catalytic amount of a fluoride ion source. The present composition is applied to the building materials in a manner which permits absorption of from about 8 to 20 parts by
weight of treating composition per part by weight of chrysotile asbestos in the
material being treated.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
The present invention is intended for the treatment of gypsum-containing
cementitious materials which contain chrysotile asbestos fibers to transform the building materials to non-asbestos materials having enhanced toughness and,
thereby, a desired product for retention as a building material. The present
invention is especially useful for digesting chrysotile asbestos fibers contained in
gypsum-based building materials that have been previously applied to the structural
components, such as steel beams, decking and the like of buildings as coatings thereon to provide fire and heat resistance thereto. The process of the present
invention provides an asbestos-free coating which retains its integrity and fire and
heat resistance properties on the substrate. Finally, the present invention provides a preferred composition which can digest chrysotile asbestos fibers without
generating noxious hydrogen fluoride under both storage and use conditions.
The present invention is directed to treating composition which is an
aqueous solution or dispersion of a high concentration of phosphoric acid and a catalytic amount of a source of fluoride ions, as fully described hereinbelow.
The acid component of the present composition may comprise phosphoric
acid as the sole acid. However, phosphoric acid may be used in combination with small amounts of up to about 20% by weight of the total acid content, of other
inorganic acids, inorganic acid salts or mixtures thereof. In addition, small
amounts (up to about 5%, preferably up to about 2%, by weight of the acid
content) can be in the form of an organic acid.
The acid component is employed in the present compositions in high
concentrations of at least about 30% by weight based on the weight of the treating compositions, up to the saturation point of the acid in the aqueous system. It is
preferred that the acid component be present in from about 30% to about 45% by
weight based on the total weight of the treating composition.
The present treating compositions must contain at least one source of
fluoride ions, typically a fluorine-containing salt which is soluble in the aqueous
treating compositions in the amounts described hereinbelow. Fluorine-containing
salts which may be used in the present treating compositions include, for example, the fluorides, bifluorides, fluoroborates and fluorosilicates of ammonia, alkali
metals and alkaline earth metals. Mixtures of such salts also may be used. The
preferred fluorine-containing salts are hexafluorosilicates and tetrafluoroborates, more specifically, ammonium hexafluorosilicate, magnesium hexafluorosilicate, and sodium tetrafluoroborate.
It has unexpectedly been found that by employing a preferred composition
of the present invention which contains high concentrations of phosphoric acid in combination with a catalytic amount of a hexafluorosilicate or tetrafluoroborate salt, the treating compositions of the present invention can be stored and used to
transform chrysotile asbestos-containing building materials to non-asbestos
materials while in place in a building environment without generating noxious hydrogen fluoride gas in amounts which are unacceptable for commercial application, as exemplified by OSHA standards. This represents a major
improvement over prior art asbestos treating compositions which rapidly generate
large quantities of hydrogen fluoride gas when used, thus creating a dangerous
work area.
The catalytic amount of the fluorine-containing salt in the present treating
compositions is very small relative to the concentration of the phosphoric acid.
Concentrations of the fluorine-containing salt should be in the range of from about 0.1% to about 4% by weight based on the total weight of the treating composition,
with concentrations of from about 0.5% to about 2% by weight being preferred.
It has been found that the present treating compositions, regardless of which
fluorine-containing salts employed, are particularly useful for treating building materials which contain gypsum in combination with chrysotile asbestos, since the use of the present composition results in the digestion of the chrysotile asbestos to
provide a non-regulated material (i.e., a material containing less than 1% by weight
asbestos) while permitting the gypsum building material to remain in place as part of the building structure, retain its integrity and provide the heat insulating
properties for which it was initially intended.
It has been unexpectedly found that the present treating composition can be
readily used to transform chrysotile asbestos containing cementitious building materials into non-asbestos building material without degradation of the building
material. It has been further unexpectedly found that the present treating
composition causes the resultant building material to exhibit heat insulating and
fireproofing properties as well as toughness which is equal to or greater than that of the initial untreated material.
It has been unexpectedly found that the present compositions, particularly
those which employ a hexafluorosilicate or tetrafluoroborate salt as the source of fluoride ions, do not produce hydrogen fluoride in excessive amounts while in
storage nor directly or indirectly cause generation of HF gas when in contact with
chrysotyile asbestos. For this reason, only a small, essentially catalytic amount of
the source of fluoride ions needs to be used in the treating compositions.
The present treatment composition may be readily applied to chrysotile asbestos containing cementitious coatings in any manner so that from about 8 to 20
parts by weight, preferably 9 to 15 parts by weight, of the aqueous treating
composition is applied per part by weight of the chrysotile asbestos in the material being treated. The amount to be applied will depend on the amount of chrysotile
asbestos initially present in the material, the concentration of the acid in the
treating composition and the thickness and absorptive capacity of the material
being treated. The exact amount can be readily determined by small scale application and testing.
When further occupancy of the building or treated area is planned, the
present treating composition, preferably, should further contain agents which will inhibit the corrosion of metallic substrate materials (e.g. steel beams, galvanized corrugated decking, steel pipes and the like) to which the material being treated is attached and/or in vicinity thereof. It has been found that certain specific materials
are useful as corrosion inhibiting agents for a broad spectrum of metals when part
of the present acidic treating composition. These agents, and their incorporation in acidic treating compositions such as that described herein which digests chrysotile
asbestos to provide non-asbestos material and the utilization to transform the
asbestos-containing cementitious material to a non-regulated material are fully
described in a concurrently filed, copending application, U.S. Serial Number 08/721 ,853, (Docket No. 9130), entitled CORROSION INHIBITING
COMPOSITION FOR TREATING ASBESTOS-CONTAINING MATERIALS,
the teachings of which are incorporated herein in its entirety by reference.
The method of the present invention transforms chrysotile asbestos- containing material into a material which contains very little, if any, chrysotile
asbestos when measured, for example, by polarizing light microscopy, X-ray
diffraction, or other conventional method. The resultant treated material contains less than one percent (1%), and normally less than one-half of one percent (0.5%) chrysotile asbestos in the overall structure of the resultant material. Thus, the
material treated by the present composition results in a product which meets the U.
S. governmental standards of a non-regulated asbestos-free material which may be safely handled by ordinary means. Further, it has been unexpectedly found that the
present composition and method provides this transformation without causing a
degradation of the cementitious material and, thereby, permits the material to
remain in place and to continue to provide the functions of fire resistance, etc. for which it was initially installed.
The chrysotile asbestos contained in the cementitious material is
substantially completely digested to a non-asbestos product while in place and part
of the cementitious material. Typically, at least about eighty five percent, and
preferably at least about ninety percent, of the chrysotile fibers are digested by the
present composition and method to provide a non-regulated product without
causing degradation of the cementitious material and, thereby, not requiring
removal of the material nor detracting from the properties of the cementious coating material.
All that is necessary to achieve the digestion of the chrysotile asbestos
fibers in accordance with the present invention is to wet the material containing the
chrysotile fibers with the treating composition, for example, by spraying or brushing the material with the treating composition. In the case of asbestos-
containing building materials, such as fireproofing materials coated on girders,
beams and floor support plates, this can be done by spraying the treating
composition in the form of a solution, dispersion, gel or foam (e.g., a foam which is stable for at least about 1 minute, and preferably for at least about 60 minutes) directly onto the asbestos-containing material, preferably while it is in place in the
building environment. It is unnecessary to disturb the asbestos-containing materials since the treating compositions typically will penetrate into the building materials and contact the asbestos fibers contained therein. In those cases where it is desirable to increase the rate of penetration of the treating composition into the
building material, one or more wetting agents may be added to the treating
composition. For example, an anionic surfactant, such as linear alkyl sulfonates, sodium lauryl sulfates, polyalkoxy carboxylates, or a non-ionic surfactant, such as
alcohol alkoxylates, alkyl phenol ethoxylates, polyoxyethylene esters and
polyalkylene oxide block copolymers, can be added to the treating composition in
conventional amounts, e.g., in amounts of up to about 5 % by weight based on the total weight of the composition, to increase the rate of penetration of the treating composition into the building material and the resultant wetting of the asbestos
fibers. Excellent wetting has been achieved in most cases, however, with the
treating composition alone, without additional wetting agents. The present treating composition should be applied to the gypsum-
containing cementitious building material in manners which permit a total
application of from about 100 to 200% by weight, preferably from about 125 to about 175% by weight, of the subject composition based on the weight of the cementitious building material. The exact amount will depend on the
concentration of the chrysotile asbestos contained in the building material being
treated.
Because of the high concentration of phosphoric acid in the treating
compositions of the invention and the catalytic presence of fluorine-containing
salt, the desired asbestos transformation may be achieved by a single application
of the treating composition on the building material while it is in place in the building environment. However, in some cases it may be necessary or desirable to
make successive applications, preferably without any intermediate drying step,
until the desired degree of digestion of the chrysotile asbestos fibers is achieved.
The preferred manner of applying the subject treating composition to the material is by applying the composition in the form of a foam directly onto the major free surface(s) of the building material. As the material to be treated is in the
form of a coating on a substrate building component, usually one major surface is
exposed and free for application of the subject composition. Spraying of the aqueous treating composition may require successive applications, preferably
without any intermediate drying step(s) between applications. Application of a
foamed aqueous treating composition provides an extended contact time and a
pseudo-encapsulation of the material being treated while the transformation is occurring. The formation of the foamed composition and its specific utilization in
the instant method of transforming chrysotile asbestos-containing building
materials to non-asbestos materials is fully described in concurrently filed,
copending U.S. application Serial Number 08/721 ,857, (Docket No. 9166), entitled
FOAM COMPOSITION FOR TREATING ASBESTOS-CONTAINING MATERIALS AND METHOD OF USING SAME, the text of which is
incorporated herein in its entirety by reference.
It has been found that when a chrysotile asbestos-containing material is
transformed in place in accordance with the present invention, the physical integrity and adherence of the resulting non-asbestos material to the underlying
substrate are such that it may be left in place to perform the fireproofing or other
function for which the asbestos-containing material was originally installed. The resultant material subsequently may be treated by spraying or the like with a mild
alkaline solution, such as sodium bicarbonate, calcium carbonate, sodium
carbonate, magnesium hydroxide or the like in order to neutralize any remaining
acid in the material.
The method of the invention, as applied to the abatement of asbestos in
buildings, may typically include the step of removing any obstructions, such as
interior partitions, ceilings and column covers, to expose the asbestos-containing
material to be treated. This will enable the sampling and testing of the material to determine its composition and other relevant characteristics, thereby facilitating the selection of an optimum asbestos treatment composition and treatment procedure
in accordance with the present invention. The treatment composition is then applied directly to the asbestos-containing material while in place in amounts described above to provide a non-regulated material. The resultant material may be
further treated with a neutralizing agent.
One of the advantages of the invention is that it enables building materials to be treated in place without destroying their physical integrity and adherence to their substrate such that the materials may be left in place to perform their
originally intended function after the asbestos has been transformed to non-
asbestos material.
The following examples are intended to illustrate the invention without
imposing limits on the scope of the invention, as defined by the claims appended
hereto. All parts and percentages are by weight unless otherwise indicated.
EXAMPLE 1
Several phosphoric acid solutions were prepared by mixing concentrated (85%) phosphoric acid and water. To each solution a weighed quantity of
ammonium bifluoride was added. These solutions were added to a simulated
fireproofing material which contained 0.7 parts chrysotile asbestos, 1.5 parts vermiculite and 3.8 parts of gypsum. The weight ratio of solution to material was
1.5. The mixture was allowed to remain in contact with the simulated fireproofing
material for three days in a closed plastic container. After three days, the mixture
was filtered, washed with water, dried and analyzed for chrysotile asbestos by X- ray diffraction. The composition of the various solutions and the results of the
analyses are shown in Table 1.
TABLE 1
85% H 3 PO (parts) NH 4 HF (parts) H ? O (parts) Residual Chrysotile (%)
5.0 0.1 4.0 0.15
4.75 0.1 4.25 0.15
4.50 0.1 4.50 0.23
4.25 0.1 4.75 0.15
4.0 0.1 5.0 0.23
3.75 0.1 5.25 0.23
3.5 0.1 5.5 0.15
3.25 0.1 5.75 0.23
The results show that substantially complete transformation of chrysotile
asbestos within the treated material was achieved to provide a material having less
than about 0.2 percent by weight asbestos and, thus, produces a non-regulated
material.
EXAMPLE 2
Five 5" x 5" fire-proofing test panels of the composition described in example 1 were prepared on galvanized steel backing. These panels were treated with a phosphoric acid conversion agent compositions composed of a solution
made up in the proportions of 3.5 parts of 85% phosphoric acid, 0.15 parts of
ammonium hexafluorosilicate and 5.5 parts of water. The weight ratio of
conversion agent to fire-proofing was 1.5: 1. After allowing to remain undisturbed for four days, small core samples (~10g) were removed and analyzed for chrysotile asbestos by x-ray diffraction. The results showed that all samples contained less
than 0.5% chrysotile. These panels were then fire-tested by a modified ASTM E-
1 19 procedure. All samples passed the test.
EXAMPLE 3
The procedure described in Example 1 was repeated except that ammonium
hexafluorosilicate was used instead of ammonium bifluoride. The concentrations used and the results obtained are summarized in the Table 3 below.
TABLE 3 85% H ,PO (g) (NH 4 ) z SiF 6 (g) H O(g) Residual
Chrysotile(%)
3.25 0.12 5.75 0.38
3.25 0.14 5.75 0.26
3.25 0.15 5.75 0.26
3.25 0.20 5.75 0.14
3.50 0.12 5.50 0.35
3.50 0.14 5.50 0.22
3.50 0.15 5.50 0.22
3.50 0.20 5.50 0.14
The results show that the resultant product can be obtained which is
substantially free of asbestos. The resultant material is therefore a non-regulated
material having less than 1 % chrysotile asbestos.
EXAMPLE 4
This example shows MgSiF substituted for (NH ) 2 SiF . The procedure
described in Example 3 was repeated with the exception that MgSiF g »6H 2 O was
used as the fluoride source. The results are summarized in the table below.
TABLE 4
85% H z PO 4 (g) MgSiFfi" »6H,O(ε) H 2 O (g) Residual
Chrvsotile(%)
3.25 0.20 5.75 0.49
3.25 0.26 5.75 0.38
3.50 0.20 5.50 0.50
3.50 0.26 5.50 0.28
The results show that the resultant product can be obtained which is substantially free of asbestos. The resultant material is therefore a non-regulated
material having less than 1% chrysotile asbestos.
EXAMPLE 5
Fireproofing coatings were formed as 5' x 5' test panels by forming a coating composed of 3.8 parts gypsum, 1.5 parts vermiculite and 0.7 chrysotile
asbestos onto a galvanized steel plate. Each panel was treated with an aqueous
composition composed of a high concentration of an acid or acid salt component and a fluoride source in amounts and identity stated in Table 5 below. The
compositions were applied to each panel in a weight ratio of 1.5 based on the
weight of the coating. Prior to the testing, the coatings were allowed to remain in
place for five days after application of the digestion compositions. Each panel was tested to determine the amount of residual chrysotile
asbestos, if any, contained in the fireproofing composition.
Each panel was tested for fireproofing properties according to a procedure of subjecting the panels to a gas flame using the temperature cycle of ASTM-E-1 19 and observing if the coating remained adhered to the metal substrate after a sixty
minute test period.
TABLE 5
Acid I.D./Conc. (%) Fluoride I.D./Conc. (%) Pass/Fail
H 3 PO 4 (33) (NH 4 ) 2 SiF 6 (1.6) 3/0
H 3 PO 4 (31) NH 4 HF 2 (1.1) 1 1/0
H 3 PO 4 (17) NH 4 HF 2 (2) 2/0
H 2 SO 4 (15)
NH 4 HSO 4 (50) NH 4 HF 2 (1.2) 2/13
NH 4 HSO 4 (33) NH 4 HF 2 (1.6) 0.2
NaHSO 4 (54) NH 4 HF 2 (2.3) 0.2
H 3 PO 4 (8) NH 4 HF 2 (2) 3/5
H 2 SO 4 (23)
Each of the test panels provided a non-regulated (less than 1% residual
asbestos) coating material substantially free of asbestos. The panels treated with
the high content phosphoric acid, in comparison to panels treated with other
compositions, provided fireproofing which remained adherent to the substrate and which were a tough material capable of withstanding mechanical impact and the
like.