Title:
COMPOSITIONS CONTAINING POLYANION, ETHOXYLATED CATIONIC POLYMER AND PHYLLOSILICATES FOR IMPROVED OXYGEN BARRIER COATINGS
Document Type and Number:
WIPO Patent Application WO/2017/017146
Kind Code:
A1
Abstract:
Described is an aqueous composition comprising (a) at least one polyanion, (b) at least one ethoxylated cationic polymer, and (c) at least one phyllosilicate. The composition can be used for providing oxygen barrier properties to a polymer film.

Inventors:
PIETSCH INES (DE)
ROSCHMANN KONRAD (DE)
DEETER GARY (US)
MCGUIRE MEAGHAN (US)
FELLER RUSSELL KENNETH (US)
BREU JOSEF (DE)
KALO HUSSEIN (DE)
Application Number:
PCT/EP2016/067918
Publication Date:
February 02, 2017
Filing Date:
July 27, 2016
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BASF SE (DE)
International Classes:
C09D133/06; C08J7/043; C08J7/048; C08K3/34; C08L79/02
Foreign References:
JP2013059930A2013-04-04
Attorney, Agent or Firm:
BASF IP ASSOCIATION (DE)
Download PDF:
Claims:
Claims

Aqueous composition comprising

(a) at least one polyanion,

(b) at least one ethoxylated cationic polymer, and

(c) at least one phyllosilicate.

Aqueous composition according to claim 1 , wherein the aqueous composition contains

(a) from 10 to 90 wt.%, referring to solids content, of the polyanion; and

(b) from 10 to 90 wt.%, referring to solids content, of the ethoxylated cationic polymer; and

(c) from 5 to 75 wt.%, referring to solids content, of the phyllosilicate.

Aqueous composition according to any of the preceding claims, wherein the polyanion (a) and the ethoxylated cationic polymer (b) are dissolved in the aqueous composition and wherein the polyanion (a) is a polymer comprising acid groups neutralized with at least one base selected from the group consisting of inorganic bases and monovalent organic bases and said polymer comprising acid groups having a weight average molecular weight of preferably at least 10000 g/mol prior to neutralization and wherein said ethoxylated cationic polymer (b) has a weight average molecular weight of preferably at least 2500 g/mol.

Aqueous composition according to any of the preceding claims, wherein the weight ratio of the polyanion (a), calculated without neutralizing agent, to the ethoxylated cationic polymer (b) is from 10:1 to 10:5 and wherein the weight ratio of the sum of polyanion (a) and ethoxylated cationic polymer (b) to phyllosilicate (c) is preferably from 95:5 to 50:50.

Aqueous composition according to any of the preceding claims, wherein the polyanion is selected from polymers capable of being produced from monomers selected from the group consisting of monoethylenically unsaturated C3 to C10 carboxylic acids, vinylsulfonic acid, styrenesulfonic acid, acrylamidomethylpropanesulfonic acid, vinylphosphonic acid, and salts of these acids, preferably acrylic acid, methacrylic acid, maleic acid, itaconic acid.

Aqueous composition according to any of the preceding claims, wherein the polyanion (a) is neutralized polyacrylic acid or a neutralized copolymer of acrylic acid and maleic acid, the weight average molecular weight of the anionic polymer (a) is from 10,000 to 200,000 g/mol.

Aqueous composition according to any of the preceding claims, wherein the degree of ethoxylation of the ethoxylated cationic polymer (b) is from 40: 1 to 1 : 10, and the weight average molecular weight of the ethoxylated cationic polymer (b) is preferably from 2500 to 3 million g/mol.

8. Aqueous composition according to any of the preceding claims, wherein the phyllosilicate is selected from exfoliated organically modified smectites. 9. Aqueous composition according to any of the preceding claims, wherein the phyllosilicate is a natural or synthetic phyllosilicate with an aspect ratio of more than 400, preferably more than 1000 or more than 10.000.

10. Aqueous composition according to any of the preceding claims, wherein the phyllosilicate is a synthetic smectite of the formula

[Mn/vaiency]inter [M'm M"0]oct [Si4]tet do Y2 , wherein

M are metal cations of oxidation state 1 to 3 or H+,

M' metal cations of oxidation state 2 or 3,

M" are metal cations of oxidation state 1 or 2,

X are di-anions and

Y are mono-anions,

m for metal atoms M' of oxidation state 3 is≤2.0

and m for metal atoms M' of oxidation state 2 is≤3.0,

o is≤1 .0 and

the layer charge n is from greater or equal 0.01 to lower or equal 2.0.

1 1 . Aqueous composition according to any of the preceding claims, wherein the phyllosilicate is surface-modified with at least one organic compound having at least one group selected from amino groups and ammonium groups.

12. Aqueous composition according to any of the preceding claims, wherein the phyllosilicate is hydrothermally produced or is produced by high-temperature melt synthesis and subsequent exfoliation and/or delamination. 13. Aqueous composition according to any of the preceding claims, wherein the ethoxylated cationic polymer (b) is selected from ethoxylated vinylimidazolium polymers, ethoxylated diallyl dimethyl ammonium halide polymers, ethoxylated vinylamine polymers, ethoxylated ethylene imine polymers, ethoxylated dialkylaminoalkyl acrylate polymers, ethoxylated di- alkylaminoalkyl methacrylate polymers, ethoxylated dialkylaminoalkyl acrylamide poly- mers and ethoxylated dialkylaminoalkyl methacrylamide polymers.

14. Aqueous composition according to any of the preceding claims, wherein the ethoxylated cationic polymer (b) is an ethoxylated polyalkylenimine or an ethoxylated polyamine of the general formula I

in which the variables are each defined as follows:

R represents identical or different, linear or branched C2-Ci2-alkylene radicals or an theralkyl unit of the following formula: in which the variables are each defined as follows:

R10, R11, R12 represent identical or different, linear or branched C2-C6-alkylene radicals, preferably ethylene, and

d is an integer having a value in the range of from 0 to 50, preferably 1 to 5;

represents a continuation of the ethoxylated polyalkylenimines or ethoxylated polyam- ines by branching;

is an alkylenoxy unit of the formula II, wherein the alkylenoxy units may be in any order

II

in which the variables are each defined as follows:

R1 represents 1 ,2-propylene, 1 ,2-butylene, 1 ,2-isobutylene and/or 1 ,2-pentene;

R2 represents hydrogen and/or Ci-C22-alkyl and/or C7-C22 aralkyl, preferably C1-C6- alkyl;

m is an integer having a value in the range of from 5 to 50;

n is an integer having a value in the range of from 0 to 40;

y and z are each from 0 to 150, where the sum of y+z is at least 1 ;

wherein the number of ethyleneoxy groups is more than 50% of all alkylenoxy groups.

15. Aqueous composition according to any of the preceding claims, wherein the ethoxylated cationic polymer (b) is an ethoxylated polyethyleneimine. 16. A polymer film, coated with an aqueous composition according to any of the preceding claims. 17. Polymer film according to the preceding claim, wherein the oxygen transmission rate of the coated film is less than 40% of the oxygen transmission rate of the uncoated film, measured at 25 °C and 75% relative humidity.

18. Polymer film according to any of claims 16 to 17, wherein the material of the polymer film is selected from polyethylene terephthalate, oriented polypropylene, polyethylene, casted polypropylene, biodegradable aliphatic-aromatic copolyesters, metalized polyethylene terephthalate, metalized oriented polypropylene and polyamide and wherein the thickness of the coating layer after drying is preferably from 0.2 to 50 μηη.

19. A package comprising a polymer film according to any of claims 16 to 18.

A method of forming a polymeric film with enhanced oxygen barrier properties comprising: applying an aqueous composition according to any of claims 1 to 15 to at least one side of a polymer film and drying said composition to form a barrier coating on the polymer film.

21 . Use of the composition according to any of claims 1 to 15 for providing oxygen barrier properties.

Description:
Compositions containing polyanion, ethoxylated cationic polymer and phyllosilicates for improved oxygen barrier coatings

Description

The invention relates to aqueous compositions comprising (a) at least one polyanion, (b) at least one ethoxylated cationic polymer, and (c) at least one phyllosilicate. The compositions can be used for providing oxygen barrier properties to polymer films. When products that are susceptible to oxidation or are sensitive to oxygen are packaged it is important that the packaging materials used have oxygen-barrier properties, i.e. that they have minimum oxygen transmission or minimum oxygen permeability. Polymer films used as packaging materials and made e.g. of polyolefins, such as polyethylene, or of oriented polypropylene, or of polyesters, e.g. polyethylene terephthalate, generally have relatively high oxygen permea- bility when they are used in uncoated form. Various measures have therefore been proposed for increasing the oxygen-barrier properties of these packaging materials.

WO 07/002322 describes coated polymer films with oxygen-barrier properties. The coating composition is a solution of a maleic acid/acrylic acid copolymer and of a vinyl alcohol/vinyl- amine copolymer. After the coating process, the two copolymers of the coating composition crosslink on the polymer film. WO 98/31719 describes coating compositions for barrier coatings. The compositions comprise an ethylenically unsaturated acid monomer and a polyamine, comprising an incorporated crosslinking agent. After the coating process, crosslinking takes place via initiation of a free-radical-induced polymerization reaction. WO 201 1/023587 describes the use of specific polyelectrolyte complexes for providing an oxygen barrier to packaging materials made of polymer films. The polymer film is either coated with an aqueous dispersion comprising a dispersed polyelectrolyte complex previously produced by water-in-water emulsion polymerization, or the polymer film is coated with a composition comprising a polyelectrolyte complex produced from anionic polymer and from cationic surfactant, or the polymer film is coated with at least three alternating layers, where respectively one of two adjacent layers comprises an anionic polyelectrolyte component and the other of two adjacent layers comprises a cationic polyelectrolyte component, and polyelectrolyte complexes form at the opposite, adjacent interfaces of the alternating layers. WO 2013/182444 describes the use of aqueous polyanion- polyethyleneimine solutions for producing polymer films with oxygen-barrier properties. Packag- ing films known hitherto with oxygen-barrier properties are not yet entirely satisfactory, especially when used in high humidity atmosphere. For example the barrier coating described in

WO 201 1/023587 needs an additional moisture-protection system for protecting the barrier from humidity. The gas permeability effects of polymer/clay nanocomposite materials that consist of inorganic platelet-shaped fillers in polymer matrices are known (G. Choudalakis, A.D. Gotsis, European Polymer Journal 45 (2009) 967-984). Barrier materials based on phyllosilicates are described in WO 201 1/089089, WO 2012/175427 and WO 2012/175431 . Oxygen barrier compositions comprising specific organic polymers and specific inorganic materials such as clay or nanofillers are described for example in WO 2009/130200, US 2004/0225066 or WO 03/055792.

It was an object of the present invention to provide further improved compositions and processes which permit production of polymer films with good oxygen-barrier properties, in particular good oxygen-barrier properties in high humidity environments without the need for additional protective coatings.

The invention provides an aqueous composition comprising

(a) at least one polyanion,

(b) at least one ethoxylated cationic polymer, and

(c) at least one phyllosilicate.

The invention also provides the use of the aqueous composition for providing oxygen barrier properties to a polymer film.

The invention also provides a coated polymer film comprising an oxygen barrier coating obtainable via the use according to the invention as described herein, wherein at least one side of the polymer film has been coated with the aqueous composition according to the invention. The oxygen barrier properties can be measured by the permeability test described in the examples. The term oxygen-barrier property means that oxygen transmission rate (OTR) has been reduced in comparison with an uncoated substrate. The oxygen transmission rate of polymer films coated according to the invention is preferably less than 20%, in particular less than 10%, or less than 5%, e.g. from 1 to 3%, of the value for the uncoated polymer film measured at 23°C and 0% relative humidity; and preferably less than 40% or less than 30 % or less than 20% measured at 25 °C and 75% relative humidity.

The amount of polyanion (a) in the aqueous composition is preferably from 10 to 90 wt.%, more preferably from 20 to 80 wt.%, referring to solids content.

The amount of ethoxylated cationic polymer (b) in the aqueous composition is preferably from 10 to 90 wt.%, more preferably from 20 to 80 wt.%, referring to solids content.

The amount of phyllosilicate (c) in the aqueous composition is preferably from 5 to 75 wt.%, more preferably from 5 to 50 wt.% and even more preferably from 5 to 30 wt.%, referring to solids content.

The weight ratio of the polyanion (calculated without neutralizing agent) to the ethoxylated cationic polymer is preferably from 10:1 to 10:9, more preferably from from10:2 to 10:5. The weight ratio of the sum of polyanion (a) and ethoxylated cationic polymer (b) to phyllosilicate (c) is preferably from 95:5 to 50:50, more preferably from 95:5 to 70:30 and even more preferable from 90:10 to 75:25. The concentration of the sum of polyanion and ethoxylated cationic polymer in the aqueous composition, is preferably at least 1 % by weight, in particular at least 5% by weight and up to 50% by weight or up to 60% by weight, for example from 1 to 50% by weight or from 5 to 40% by weight.

Preferably, the polyanion (a) and the ethoxylated cationic polymer (b) are dissolved in the aqueous composition. Preferably the polyanion is a polymer comprising acid groups neutralized with at least one base selected from the group consisting of inorganic bases and monovalent organic bases and said polymer comprising acid groups having a weight average molecular weight of at least 10000 g/mol prior to neutralization; and the ethoxylated cationic polymer has preferably a weight average molecular weight of at least 2500 g/mol or of at least 10000 g/mol.

The average molecular weight can be determined by gel permeation chromatography with polymethyl methacrylate as standard (DIN 55672-2:2008:06).

The polyanion is a polymer comprising neutralized acid groups, also named anionic polymer. Anionic polymers are polymers having anionic or acidic groups, in particular organic polymers having carboxylate, phosphate, or sulfate groups or the corresponding acid groups. The term "anionic polymer" also comprises the corresponding polymers with acid groups, as long as they are at least partially neutralized by monovalent bases when used in the aqueous composition according to the invention.

Examples of suitable anionic polymers are those formed by free-radical polymerization of ethy- lenically unsaturated anionic monomers capable of free-radical polymerization. The term "anion- ic monomer" comprises monomers with at least one anionic or acidic group, wherein the acidic group can be neutralized by a base. The group of anionic polymers also comprises copolymers made of at least one anionic monomer and of one or more than one different non-ionic, non- acidic copolymerizable monomer(s). The polyanion can also be synthesized by polymerization of one or more non-ionic monomers such as acid derivatives like for example ethylenically un- saturated acid esters, followed by a hydrolysis to obtain an anionic polymer. Suitable non-ionic monomers can be alkyi acrylates, alkyi methacrylates (e.g. tert-butyl acrylate, ethyl acrylate etc.) or ethylenically unsaturated acid anhydrids such as maleic anhydride.

Examples of ethylenically unsaturated anionic monomers that can be used are monoethylenical- ly unsaturated C3 to C10 or C3 to C5 carboxylic acids, such as acrylic acid, methacrylic acid, eth- acrylic acid, crotonic acid, maleic acid, fumaric acid, itaconic acid; or monoethylenically unsaturated sulfonic acids such as vinylsulfonic acid, styrenesulfonic acid, acrylamidomethylpropane- sulfonic acid; or monoethylenically unsaturated phosphonic acids such as vinylphosphonic acid or ((meth)acryloyloxy)alkyl phosphonic acids with up to 10 C-atoms in the alkyi group (e.g. 2- (methacryloyloxy)ethyl phosphonic acid); or phosphoalkyl (meth)acrylates with up to 10 C- atoms in the alkyi group (e.g. phosphoethyl methacrylate;; and salts of these acids such as the alkali-metal salts, alkaline-earth-metal salts, or ammonium salts of these acids. Among the anionic monomers preferably used are acrylic acid, methacrylic acid, maleic acid, itaconic acid and 2-acrylamido-2-methylpropanesulfonic acid. Particular preference is given to aqueous solutions of polymers based on acrylic acid. The anionic monomers can either be polymerized alone to give homopolymers or else can be polymerized in a mixture with one another to give copolymers. Examples of these are the homopolymers of acrylic acid, homopolymers of methacrylic acid, copolymers of acrylic acid and maleic acid, copolymers of acrylic acid and methacrylic acid, and copolymers of methacrylic acid and maleic acid. Preferably, the polyanion is selected from polymers capable of being produced from monomers selected from the group consisting of monoethylenically unsaturated C3 to C10 carboxylic acids, vinylsulfonic acid, styrenesulfonic acid, acrylamidomethylpropanesulfonic acid, vinylphosphonic acid, and salts of these acids, pref- erably acrylic acid, methacrylic acid, maleic acid, itaconic acid. Most preferably the polyanion is a polyacrylic acid or a copolymer of acrylic acid and maleic acid.

However, the anionic monomers can also be polymerized in the presence of at least one other ethylenically unsaturated monomer. These monomers can be nonionic or can bear a cationic charge. Examples of nonionic comonomers are acrylamide, methacrylamide, N-C1 to C3-alkyl- acrylamides, N-vinylformamide, styrene, acrylic esters of monohydric alcohols having from 1 to 20 carbon atoms, e.g. in particular methyl acrylate, ethyl acrylate, isobutyl acrylate, and n-butyl acrylate, methacrylic esters of monohydric alcohols having from 1 to 20 carbon atoms, e.g. methyl methacrylate and ethyl methacrylate, and also vinyl acetate and vinyl propionate.

Suitable cationic monomers which can be copolymerized with the anionic monomers are dial- kylaminoethyl acrylates, dialkylaminoethyl methacrylates, dialkylaminopropyl acrylates, dialkyl- aminopropyl methacrylates, dialkylaminoethylacrylamides, dialkylaminoethylmethacrylamides, dialkylaminopropylacrylamides, dialkylaminopropylmethacrylamides, diallyldimethylammonium chloride, vinylimidazole, and also the respective basic monomers neutralized with acids and/or quaternized. Individual examples of cationic monomers are dimethylaminoethyl acrylate, dime- thylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, dime- thylaminopropyl acrylate, dimethylaminopropyl methacrylate, diethylaminopropyl acrylate, and diethylaminopropyl methacrylate, dimethylaminoethylacrylamide, dimethylaminoethylmethacryl- amide, dimethylaminopropylacrylamide, dimethylaminopropylmethacrylamide, diethylami- noethylacrylamid, and diethylaminopropylacrylamide.

The basic monomers can have been completely or only to some extent neutralized or quaternized, for example to an extent of from 1 to 99% in each case. Preferred quaternizing agent used for the basic monomers is dimethyl sulfate. However, the monomers can also be quaternized with diethyl sulfate or with alkyl halides, such as methyl chloride, ethyl chloride, or benzyl chloride. The amount used of the cationic monomers is at most such that the resultant polymer bears a net charge which is anionic at pH < 6.0 and a temperature of 20°C. The excess of anionic charge in the resultant amphoteric polymers is, for example, at least 5 mol%, preferably at least 10 mol%.

The amounts of the non-anionic, non-acidic comonomers used in the production of the anionic polymers are such that the resultant polymers are preferably water-soluble when diluted with water at pH above 7.0 and at a temperature of 20°C, and have an anionic net charge. Examples of the amount of non-anionic, non-acidic comonomers, based on the total amount of monomers used in the polymerization reaction, are from 0 to 99% by weight, preferably from 1 to 75% by weight, or an amount in the range from 1 to 25% by weight.

Examples of preferred copolymers are copolymers made of from 25 to 90% by weight of acrylic acid and from 75 to 10% by weight of acrylamide. It is preferable to polymerize at least one eth- ylenically unsaturated C3 to C5 carboxylic acid in the absence of other monoethylenically unsaturated monomers. Particular preference is given to homopolymers of acrylic acid, obtainable via free-radical polymerization of acrylic acid in the absence of other monomers; or to copolymers of acrylic acid and maleic acid.

In one embodiment, the anionic polymer comprises 2-acrylamido-2-methylpropanesulfonic acid (AMPS). It is preferable to copolymerize acrylic acid with AMPS. The amount of AMPS here can be, for example, from 0.1 to 15 mol% or from 0.5 to 10 mol%, based on the amount of all of the monomers.

The polymerization reaction for making the anionic polymer can also be conducted in the presence of at least one crosslinking agent. This then gives copolymers with higher molar mass than when the anionic monomers are polymerized in the absence of any crosslinking agent. Cross- linking agents used can comprise any of the compounds that have at least two ethylenically unsaturated double bonds within the molecule. Examples of crosslinking agents are triallyl- amine, the triallyl ether of pentaerythritol, the tetraallyl ether of pentaerythritol, methylenebis- acrylamide, Ν,Ν'-divinylethyleneurea, allyl ethers comprising at least two allyl groups, or vinyl ethers having at least two vinyl groups, where these ethers derive from polyhydric alcohols, e.g. sorbitol, 1 ,2-ethanediol, 1 ,4-butanediol, trimethylolpropane, glycerol, diethylene glycol, and from sugars, such as sucrose, glucose, mannose; other examples are dihydric alcohols which have from 2 to 4 carbon atoms and which have been completely esterified with acrylic acid or with methacrylic acid, e.g. ethylene glycol dimethacrylate, ethylene glycol diacrylate, butanediol di- methacrylate, butanediol diacrylate, diacrylates or dimethacrylates of polyethylene glycols with molecular weights from 300 to 600, ethoxylated trimethylenepropane triacrylates or ethoxylated trimethylenepropane trimethacrylates, 2,2-bis(hydroxymethyl)butanol trimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, and triallylmethylammonium chloride. If cross- linking agents are used in the production of the solutions of the invention, examples of the re- spective amounts used of crosslinking agent are from 0.0005 to 5.0% by weight, preferably from 0.001 to 1 .0% by weight, based on the entirety of monomers used in the polymerization reaction, provided that the polymer remains water-soluble at pH > 7. Crosslinking agents preferably used are the triallyl ether of pentaerythritol, the tetra allyl ether of pentaerythritol, N,N ' -divinyl- ethylene urea, allyl ethers of sugars such as sucrose, glucose or mannose, where these ethers comprise at least two allyl groups, and triallylamine, and also mixtures of these compounds.

If at least one anionic monomer is polymerized in the presence of at least one crosslinking agent, it is preferable to produce crosslinked copolymers of acrylic acid and/or methacrylic acid by polymerizing acrylic acid and/or methacrylic acid in the presence of the triallyl ether of pentaerythritol, the tetraallyl ether of pentaerythritol, Ν,Ν ' -divinylethyleneurea, allyl ethers of sugars such as sucrose, glucose or mannose, where these ethers comprise at least two allyl groups, and triallylamine, and also mixtures of these compounds. Preferably the amounts of crosslinking agents used in the polymerization reaction are limited to an extent so that the resultant anionic polymers are soluble in aqueous solution at pH > 7.0.

The weight average molecular weight of the polymer comprising acid groups prior to neutralization is preferably at least 10000 g/mol, more preferably at least 30000 g/mol, for example from 10000 to 200000 g/mol or from 30000 to 150000 g/mol.

In one embodiment of the invention the polyanion (a) is neutralized polyacrylic acid or a neutralized copolymer of acrylic acid and maleic acid and the weight average molecular weight of the anionic polymer (a) is from 10000 to 200000 g/mol or from 30000 to 150000 g/mol.

The acid groups of the polyanion are partially or completely neutralized with at least one base selected from the group consisting of inorganic bases and monovalent organic bases base. A monovalent organic base is an organic compound with a single basic group, e.g. a single amino group. Bases are for example NaOH, KOH, Ca(OH)2, Ba(OH)2, sodium carbonate, potassium carbonate, trisodium phosphate, ammonia or primary, secondary or tertiary organic amines.

Preferred bases are ammonia, sodium hydroxide and triethanol amine. Most preferred are volatile bases such as ammonia.

The degree of neutralization of the polyanion is preferably from 30 to 100%, more preferably from 50 to 100%, based on the total molar amount of acidic groups of the anionic polymer.

The aqueous composition comprises at least one ethoxylated cationic polymer (b). The cationic polymers are preferably water-soluble, i.e. they have at least 1 g/l solubility in water at 20°C. Cationic polymers are polymers having cationic groups, in particular organic polymers having quaternary ammonium groups. Cationic polymers as defined herein also include polymers having primary, secondary, or tertiary amine groups, which can be protonated either by acids comprised within the reaction medium or by acid groups of the anionic polymer, thus being converted to cationic groups. The amine groups or ammonium groups of the cationic polymer can be present in the form of substituents or as a portion of the polymer chain. They can also be a por- tion of an aromatic or non-aromatic ring system.

Examples of suitable ethoxylated cationic polymers are those from the following group:

(a) ethoxylated polymers comprising vinylimidazolium units,

(b) ethoxylated polydiallyldimethylammonium halides,

(c) ethoxylated polymers comprising vinylamine units,

(d) ethoxylated polymers comprising ethyleneimine units,

(e) ethoxylated polymers comprising dialkylaminoalkyl acrylate units and/or comprising dial- kylaminoalkyl methacrylate units, and (f) ethoxylated polymers comprising dialkylaminoalkyl acrylamide units and/or comprising dialkylaminoalkyl methacrylamide units.

(g) ethoxylated polymers comprising imidazole and epichlorhydrine units Examples of ethoxylated cationic polymers are

(a) ethoxylated homopolymers of vinylimidazolium methosulfate and/or ethoxylated copolymers of vinylimidazolium methosulfate and N-vinylpyrrolidone,

(b) ethoxylated polydiallyldimethylammonium chlorides,

(c) ethoxylated polyvinylamines,

(d) ethoxylated polyethyleneimines,

(e) ethoxylated polydimethylaminoethyl acrylate, ethoxylated polydimethylaminoethyl methacrylate, ethoxylated copolymers of acrylamide and dimethylaminoethyl acrylate, and ethoxylated copolymers of acrylamide and dimethylaminoethyl methacrylate, where the basic monomers can also be present in the form of the salts with mineral acids, or in quater- nized form, and

(f) ethoxylated polydimethylaminoethylacrylamide, ethoxylated polydimethylaminoethyl- methacrylamide, and ethoxylated copolymers of acrylamide and dimethylaminoethyl- acrylamide. The basic monomers can also be present in the form of the salts with mineral acids, or in quaternized form. The weight average molecular weights M w of the ethoxylated cationic polymers are preferably at least 500, or at least 1000 or at least 2000 or at least 2500 and preferably up to 3 million or up to 1 million, preferably up to 500 000, or up to 100 000. It is preferable to use the following as ethoxylated cationic polymers:

(a) ethoxylated homopolymers of vinylimidazolium methosulfate and/or ethoxylated copolymers of vinylimidazolium methosulfate and N-vinylpyrrolidone with weight average molecular weight M w of from 500 to 500 000 in each case,

(b) ethoxylated polydiallyldimethylammonium chlorides with weight average molecular weight Mw of from 1000 to 500 000,

(c) ethoxylated polyvinylamines with weight average molecular weight M w of from 500 to 1 million, and

(d) ethoxylated polyethyleneimines with weight average molecular weight M w of from 500 to 1 million.

The copolymers listed under (a) of ethoxylated vinylimidazolium methosulfate and N-vinylpyrrolidone comprise by way of example from 10 to 90% by weight of copolymerized

N-vinylpyrrolidone. Instead of N-vinylpyrrolidone it is possible to use, as comonomer, at least one compound from the group of the ethylenically unsaturated C3 to C5 carboxylic acids, particu- lar examples being acrylic acid or methacrylic acid, or to use the esters of these carboxylic acids with monohydric alcohols comprising from 1 to 18 carbon atoms, e.g. methyl acrylate, ethyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, methyl methacrylate, ethyl methacrylate, or n-butyl methacrylate. By way of example, synthesis of suitable copolymers (a) is described in WO 2005/049674 (copolymers 1 , 2, 3) or in WO 2005/049676 (copolymer 1 ).

A polymer of group (b) that can be used with preference is ethoxylated polydiallyldimethyl- ammonium chloride. Other suitable ethoxylated polymers are copolymers of diallyldimethyl- ammonium chloride and dimethylaminoethyl acrylate, copolymers of diallyldimethylammonium chloride and dimethylaminoethyl methacrylate, copolymers of diallyldimethylammonium chloride and diethylaminoethyl acrylate, copolymers of diallyldimethylammonium chloride and dimethyl- aminopropyl acrylate, copolymers of diallyldimethylammonium chloride and dimethylaminoethyl- acrylamide, and copolymers of diallyldimethylammonium chloride and dimethylaminopropyl- acrylamide. The copolymers of ethoxylated diallyldimethylammonium chloride comprise, in co- polymerized form by way of example from 1 to 50 mol%, mostly from 2 to 30 mol%, of at least one of the comonomers mentioned. An exemplary synthetic protocol is given in WO

2005/049676 (copolymer 3). Ethoxylated polymers (c) comprising vinylamine units are obtainable via polymerization of N-vinylformamide, if appropriate in the presence of comonomers, and hydrolysis of the vinyl- formamide polymers with elimination of formyl groups to form amino groups. The degree of hydrolysis of the polymers can by way of example be from 1 to 100%, mostly being in the range from 60 to 100%. The average molecular weights M w are up to 1 million. Subsequent alkoxyla- tion as described in EP 1290071 (cf. example 2) yields the inventive ethoxylated polymers (c).

Polymers of group (d) comprising ethyleneimine units, for example polyethyleneimines, are commercially available products sold under the tradename Sokalan ® or Lupasol ® , examples being Sokalan ® HP 20 or Lupasol ® SC-61 B. These cationic polymers are polymers of ethylene- imine which are produced via polymerization of ethyleneimine in an aqueous medium in the presence of small amounts of acids or of acid-forming compounds, examples being halogenat- ed hydrocarbons, e.g. chloroform, carbon tetrachloride, tetrachloroethane, or ethyl chloride, or are condensates of epichlorohydrin and compounds comprising amino groups, examples being mono- and polyamines, e.g. dimethylamine, diethylamine, ethylenediamine, diethylenetriamine, and triethylenetetramine, or ammonia. By way of example, they have weight average molecular weights M w of from 500 and up to 3 million or up to 1 million, preferably from 1000 to 500 000.

This group of cationic polymers also includes graft polymers of ethyleneimine on compounds having a primary or secondary amino group, examples being polyamidoamines made of dicar- boxylic acids and of polyamines. The ethyleneimine-grafted polyamidoamines can also, if appropriate, be reacted with bifunctional crosslinking agents, for example with epichlorohydrin or with bischlorohydrin ethers of polyalkylene glycols.

Ethoxylated cationic polymers of group (e) that can be used are polymers comprising dialkyla- minoalkyl acrylate units and/or comprising dialkylaminoalkyl methacrylate units. These monomers can be used in the polymerization reaction in the form of the free bases, but are preferably used in the form of the salts with mineral acids, such as hydrochloric acid, sulfuric acid, or phosphoric acid, or else in quaternized form. An example of a quaternizing agent that can be used is dimethyl sulfate, diethyl sulfate, methyl chloride, ethyl chloride, cetyl chloride, or benzyl chloride. These monomers are used together with suitable ethoxylated (meth)acrylates (e.g. Bisomer ® MPEG 350 MA, Bisomer ® MPEG 550 MA, Bisomer ® S7W, Bisomer ® S10W or Bi- somer ® S20W) or other vinyl monomers (e.g. Pluriol ® A10R, Pluriol ® A1 1 R, Pluriol ® A46R) to produce either binary or multiple copolymers. Examples of suitable additional comonomers are acrylamide, methacrylamide, N-vinylformamide, N-vinylpyrrolidone, methyl acrylate, ethyl acry- late, methyl methacrylate, and mixtures of the monomers mentioned.

Ethoxylated cationic polymers of group (f) are polymers comprising dimethylaminoethyl acryla- mide units or comprising dimethylaminoethyl methacrylamide units, which preferably comprise the basic monomers in the form of the salts with mineral acids, or in quaternized form. As with cationic polymers of group (e), these materials can be either binary or multiple copolymers with suitable alkoxylated vinyl monomers. Examples are copolymers of dimethylaminoethyl acrylamide which has been completely quaternized with dimethyl sulfate or with benzyl chloride, ho- mopolymers of dimethylaminoethyl methacrylamide which has been completely quaternized with dimethyl sulfate, with methyl chloride, with ethyl chloride, or with benzyl chloride, and copolymers of acrylamide and dimethyl-sulfate-quaternized dimethylaminoethyl acrylamide. Manufacture of such copolymers is exemplified in WO 2005/049676 (copolymer 4). The following cationic polymers are preferably used in the production of the aqueous composition of the invention:

(a) ethoxylated homopolymers of vinylimidazolium methosulfate and/or copolymers of vinyl- imidazolium methosulfate and N-vinylpyrrolidone with average molecular weight M w of from 1000 to 100 000 in each case,

(b) ethoxylated polydiallyldimethylammonium chlorides with average molecular weight M w of from 2000 to 100 000, and/or

(c) ethoxylated polyvinylamines with average molecular weight M w of from 1000 to 500 000.

The polyvinylamines are preferably used in the form of the salts with sulfuric acid or hydrochloric acid and

(d) ethoxylated polyethyleneimines with weight average molecular weight M w of from 500 to 1 million.

Polymers that can be used as ethoxylated cationic polymers are not only those polymers composed solely of cationic monomers but also amphoteric polymers, with the proviso that the net charge that they bear is cationic. By way of example, the excess of cationic charge in the amphoteric polymers is at least 5 mol%, preferably at least 10 mol%, and mostly in the range from 15 to 95 mol%. Examples of amphoteric polymers having an excess of cationic charge are

copolymers of acrylamide, dimethylaminoethyl acrylate and acrylic acid, comprising at least 5 mol% more dimethylaminoethyl acrylate than acrylic acid as comonomer;

- copolymers of vinylimidazolium methosulfate, N-vinylpyrrolidone, and acrylic acid, comprising at least 5 mol% more vinylimidazolium methosulfate than acrylic acid as comonomer; hydrolyzed copolymers of N-vinylformamide and of an ethylenically unsaturated C3 to C5 carboxylic acid, preferably acrylic acid or methacrylic acid, with at least 5 mol% higher con- tent of vinylamine units than units of ethylenically unsaturated carboxylic acids; and copolymers of vinylimidazole, acrylamide, and acrylic acid, where the pH has been selected in such a way that the amount of vinylimidazole cationically charged is at least 5 mol% more than the amount of copolymerized acrylic acid.

Basic polymers are preferably used in the form of the salts with mineral acids or with organic acids, such as formic acid or acetic acid.

Embodiments of the invention are the use of polyelectrolyte complexes formed from

* homopolymers of acrylic acid and ethoxylated polymers comprising vinylimidazolium units;

* homopolymers of acrylic acid and ethoxylated homopolymers having vinylimidazolium units;

* homopolymers of acrylic acid and ethoxylated copolymers of monomers having vinylimidazolium units and of vinyllactams, in particular vinylpyrrolidone;

* copolymers of acrylic acid with 2-acrylamido-2-methylpropanesulfonic acid and ethoxylated polymers comprising vinylimidazolium units;

* copolymers of acrylic acid with 2-acrylamido-2-methylpropanesulfonic acid and ethoxylated homopolymers having vinylimidazolium units;

* copolymers of acrylic acid with 2-acrylamido-2-methylpropanesulfonic acid and ethoxylated copolymers of monomers having vinylimidazolium units and of vinyllactams, in particular vi- nylpyrrolidone

* homopolymers of acrylic acid and ethoxylated polyethylene imine.

Preferred ethoxylated cationic polymers are in particular cationic polymers selected from the group consisting of ethoxylated polymers comprising vinylimidazolium units, ethoxylated polydi- allyldimethylammonium halides, ethoxylated polymers comprising vinylamine units, ethoxylated polymers comprising ethyleneimine units, ethoxylated polymers comprising dialkylaminoalkyi acrylate units, ethoxylated polymers comprising dialkylaminoalkyi methacrylate units, ethoxylated polymers comprising dialkylaminoalkylacrylamide units, and ethoxylated polymers comprising dialkylaminoalkyi methacrylamide units.

The cationic polymers can be prepared for example by radical polymerization of suitable monomers. Suitable cationic monomers which may be copolymerized with non-cationic monomers are dialkylaminoethyl acrylates, dialkylaminoethyl methacrylates, dialkylaminopropyl acrylates, dialkylaminopropyl methacrylates, dialkylaminoethylacrylamides, dialkylaminoethylmethacryla- mides, dialkylaminopropylacrylamides, dialkylaminopropylmethacrylamides, diallyldime- thylammonium chloride, vinylimidazole, and also the respective basic monomers neutralized with acids and/or quaternized. Individual examples of cationic monomers are dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, dimethylaminopropyl acrylate, dimethylaminopropyl methacrylate, diethyla- minopropyl acrylate, and diethylaminopropyl methacrylate, dimethylaminoethylacrylamide, di- methylaminoethylmethacrylamide, dimethylaminopropylacrylamide, dimethylaminopropyl- methacrylamide, diethylaminoethylacrylamid, and diethylaminopropylacrylamide. The basic monomers can have been completely or only to some extent neutralized and, respectively, quaternized, for example to an extent of from 1 to 99% in each case. Preferred quaterniz- ing agent used for the basic monomers is dimethyl sulfate. However, the monomers can also be quaternized with diethyl sulfate or with alkyl halides, such as methyl chloride, ethyl chloride, or benzyl chloride.

The polymerization reaction can also be conducted in the presence of at least one crosslinking agent. This then gives copolymers with higher molar mass than when the anionic monomers are polymerized in the absence of any crosslinking agent. Incorporation of a crosslinking agent into the polymers moreover gives reduced solubility of the polymers in water. As a function of the amount of copolymerized crosslinking agent, the polymers become insoluble in water, but are swellable in water.

Crosslinking agents used can comprise any of the compounds that have at least two ethyleni- cally unsaturated double bonds within the molecule. Examples of crosslinking agents are trial- lylamine, the triallyl ether of pentaerythritol, the tetraallyl ether of pentaerythritol, methylene- bisacrylamide, Ν,Ν'-divinylethyleneurea, allyl ethers comprising at least two allyl groups, or vinyl ethers having at least two vinyl groups, where these ethers derive from polyhydric alcohols, e.g. sorbitol, 1 ,2-ethanediol, 1 ,4-butanediol, trimethylolpropane, glycerol, diethylene glycol, and from sugars, such as sucrose, glucose, mannose; other examples are dihydric alcohols which have from 2 to 4 carbon atoms and which have been completely esterified with acrylic acid or with methacrylic acid, e.g. ethylene glycol dimethacrylate, ethylene glycol diacrylate, butanediol di- methacrylate, butanediol diacrylate, diacrylates or dimethacrylates of polyethylene glycols with molecular weights from 300 to 600, ethoxylated trimethylenepropane triacrylates or ethoxylated trimethylenepropane trimethacrylates, 2,2-bis(hydroxymethyl)butanol trimethacrylate, pentae- rythritol triacrylate, pentaerythritol tetraacrylate, and triallylmethylammonium chloride. If cross- linking agents are used in the production of the dispersions of the invention, examples of the respective amounts used of crosslinking agent are from 0.0005 to 5.0% by weight, preferably from 0.001 to 1.0% by weight, based on the entirety of monomers used in the polymerization reaction. Crosslinking agents preferably used are the triallyl ether of pentaerythritol, the tetraallyl ether of pentaerythritol, Ν,Ν ' -divinylethyleneurea, allyl ethers of sugars such as sucrose, glucose or mannose, where these ethers comprise at least two allyl groups, and triallylamine, and also mixtures of these compounds.

The aqueous composition preferably comprises at least on ethoxylated polyethyleneimine. Poly- ethyleneimines are polymers comprising ethyleneimine units. They are preferably branched. The polyethyleneimines can be used neutralized in the form of the salts with suitable acids but are preferably used in unneutralized form.

In one embodiment of the invention, the polyethyleneimine is selected from highly branched or dendritic polyethyleneimines. Highly branched polyethyleneimines are characterized by their high degree of branching (DB). The DB can be determined by 13 C-NMR-spectroscopy, preferably in D2O, and is defined as:

DB = D +T/(D+T+L) wherein D (dendritic) correlates to the amount of tertiary amine groups, L (linear) correlates to the amount of secondary amine groups and T (terminal) correlates to the amount of primary amine groups. Highly branched polyethyleneimines according to the invention have a DB of preferably from 0.1 to 0.95, or from 0.25 to 0.9, more preferred from 0.30 to 0.80 and especially preferred of at least 0.5. Dendritic polyethyleneimines have a structural and molecular uniform constitution (DB = 1 ).

The weight average molecular weight of the ethoxylated polyethylene imines is preferably at least 2500 g/mol, more preferably at least 10000 g/mol, for example from 2500 to 3 million g/mol or from 10000 to 2 million g/mol or from 10000 to 500000 g/mol. The charge density of the polyethylene imines is preferably from 1 to 35 meq/g, more preferably from 5 to 25 meq/g. Charge density can be measured by titration of aqueous solutions of the polyethyleneimine with potassium polyvinyl sulfate (KPVS) at pH 4.5 with toluidine blue as indicator. Suitable polyethyleneimines are polymers of ethyleneimine which are produced via polymerization of ethyleneimine in an aqueous medium in the presence of small amounts of acids or of acid-forming compounds, examples being halogenated hydrocarbons, e.g. chloroform, carbon tetrachloride, tetrachloroethane, or ethyl chloride, or are condensates of epichlorohydrin and compounds comprising amino groups, examples being mono- and polyamines, e.g. dimethyl- amine, diethylamine, ethylenediamine, diethylenetriamine, and triethylenetetramine, or ammonia.

This group of cationic polymers also includes graft polymers of ethyleneimine on compounds having a primary or secondary amino group, examples being polyamidoamines made of dicar- boxylic acids and of polyamines. The ethyleneimine-grafted polyamidoamines can also, if appropriate, be reacted with bifunctional crosslinking agents, for example with epichlorohydrin or with bischlorohydrin ethers of polyalkylene glycols.

In one embodiment, the polyethyleneimine is cross-linked. Any crosslinking agent with at least two functional groups capable of forming covalent bonds with amine groups of the polyethyleneimine can be used for crosslinking. Suitable crosslinking agents are for example alkyldialdehyds with preferably 3 to 20 C-atoms such as glutaraldehyd (1 ,5-pentanedial).

The aqueous composition may comprise water as the only solvent or it may comprise a mixture of water and water miscible organic solvents such as methanol, ethanol, acetone or tetrahydro- furan. Preferably water is the only solvent. The pH is preferably from 6 to 12, more preferably from 7 to 10.

Ethoxylated polyethylene imines are described in WO 09/060059, WO 06/108856, WO

15/028191 and the literature cited therein.

The degree of ethoxylation of the ethoxylated cationic polymer (b) is preferably from 40:1 to 1 :10, preferably from 30:1 to 2:1 based on the weight amount of CH2CH20-units to the other polymer components.

The term "ethoxylated" in the at least one ethoxylated cationic polymer (b) refers to alkoxylated polymers in general and does not exclude respective copolymers of ethylene oxide with other epoxides like propylene oxide, butylene oxide or styrene oxide. Such copolymers may be either random or exhibit block-like structure. The amount of ethylene oxide in such copolymers is preferably more than 70 mol%, more preferably more than 80 mol% and even more preferable more than 90 mol%. Most preferable, homopolymers of ethylene oxide are employed. Ethoxylated cationic polymers can be made by methods generally known in the art, for example 1 ) copolymerization of cationic monomers with polyethylene glycol-functional (PEG-functional) monomers, for example one or more of the following PEG-functional monomers:

X = 0, S

with n = number of ethylene oxide units, preferably from 2 to 50

2) grafting of cationic polymers (e.g. polyethylene imine) by reaction with ethylene oxide

3) grafting of (meth)acrylic ester copolymers by trans-esterification or trans-amidation with suitable polyethylenoxide compounds such as for example

HO-(CH 2 CH 2 0) n -R, or

with R = alkyl, preferable C1 - to C4 alkyl such as methyl, ethyl, propyl, n-butyl;

n = number of ethylene oxide units, preferably from 2 to 70

- ring opening of maleic acid anhydride copolymers and esterification or amidation with the above-mentioned polyethylene oxide compounds.

Preferred ethoxylated polyalkylenimines or ethoxylated polyamines are of the general formula I in which the variables are each defined as follows: R represents identical or different, linear or branched C2-Ci2-alkylene radicals or an etheralkyl unit of the following formula:

in which the variables are each defined as follows:

R 10 , R 11 , R 12 represent identical or different, linear or branched C2-C6-alkylene radicals, preferably ethylene, and

d is an integer having a value in the range of from 0 to 50, preferably 1 to 5;

B represents a continuation of the ethoxylated polyalkylenimines or ethoxylated polyamines by branching

E is an alkylenoxy unit of the formula II, wherein the alkylenoxy units may be in any order

II

in which the variables are each defined as follows:

R 1 represents 1 ,2-propylene, 1 ,2-butylene, 1 ,2-isobutylene and/or 1 ,2-pentene;

R 2 represents hydrogen and/or Ci-C22-alkyl and/or C7-C22 aralkyl, preferably C1-C6- alkyl;

m is an integer having a value in the range of from 5 to 50;

n is an integer having a value in the range of from 0 to 40;

y and z are each from 0 to 150, where the sum of y+z is at least 1 ;

wherein the number of ethyleneoxy groups is more than 50%, preferably more than 70%, or more than 80% or 100% of all alkylenoxy groups.

R is preferably linear or branched C2-C6-alkylene, more preferred ethylene.

The aqueous composition contains at least one phyllosilicate. Phyllosilicates are a subgroup of silicate minerals. Phyllosilicates are sheet silicate materials (layered silicates), formed by parallel sheets of silicate tetrahedra with S12O5 or a 2:5 ratio. The tetrahedral layers alternate with octahedron layers. In the octahedral layers are cations surrounded by hydroxide ions and / or oxygen in octahedral coordination. The actual layers themselves are usually charged negatively and the charges are partially offset by additional cations in the interstices of the respective lay- ers. These additional cations are to be distinguished from the foregoing cations in the octahedral layers. Many phyllosilicates may be well swollen in water and / or dispersed. This process is called exfoliation (or synonymously delamination).

The phyllosilicate may be natural or synthetic. They have an aspect ratio of preferably at least 50, more preferably more than 400, or more than 1000 and most preferably more than 10000. The mode of barrier action of phyllosilicates is due to their high aspect ratio (ratio of width to thickness). The starting clay materials are layered structures which can be exfoliation and de- laminated in a known manner which - in an idealized case - leads to individual platelets with thicknesses of preferably greater or equal 10nm, ideally about 1 nm corresponding to a single clay layer.

The layer charge is preferably from 0.01 to 2.0 per formula unit, preferably from 0.3 to 0.95 and ideally from 0.4 to 0.6. The phyllosilicates may be modified or unmodified. Preference is given to modified phyllosilicates.

The phyllosilicates may be selected from montmorillonite, bentonite, kaolinite, mica, hectorite, fluorohectorite, saponite, beidellite, nontronite, stevensite, vermiculite, fluorovermiculite, hal- loysite, volkonskoite, suconite, magadite, sauconite, stibensite, stipulgites, attapulgites, illites, kenyaite, smectite, allevardite, muscovite, palygorskite, sepiolite, silinait, grumantite, revdite, zeolites, fuller's earth, natural or synthetic talc and mica, or of synthetic origin, such as permut- ites. Most preferred are exfoliated, organically modified smectites. These phyllosilicates are composed of packets of face to face stacking of individual silicate layers or sheets. The thickness of the sheets is typically about 1 nm and the longest length of the sheets is typically from 50 to 1000 nm or even longer, resulting in aspect ratios of 50 to 1000. As described by Breu et al. (Nanoscale 2012, 4, 5633-5639), aspect ratios of more than 10000 can be realized for synthetic clays.

Preferred are montmorillonite (aluminium magnesium silicate), hectorite (magnesium lithium silicate) clays, with synthetic fluorohectorite being the most preferred. Also preferred are exfoliated smectite types. Preferred synthetic phyllosilicates are synthetic smectites. Preferred synthetic smectites are those of the formula

[M n /vaiency] inter [M' m M" 0 ] oct [Si 4 ] tet do Y2 , wherein

M are metal cations of oxidation state 1 to 3, or H + ,

M' metal cations of oxidation state 2 or 3,

M" are metal cations of oxidation state 1 or 2,

X are di-anions and

Y are mono-anions,

m for metal atoms M' of oxidation state 3 is≤2.0

and m for metal atoms M' of oxidation state 2 is≤3.0,

o is≤1 .0 and

the layer charge n is from 0.01 to 2.0 , preferably from 0.3 to 0.95 and ideally from 0.4 to 0.6. M preferably has oxidation state 1 or 2. M is particularly preferably Li + , Na + , Mg 2+ , or a mixture of two or more of those ions. M is most particularly preferably Na + or Li + .

M' is preferably Mg 2+ , Al 3+ , Zn 2+ , Fe 2+ , Fe 3+ or a mixture of two or more of those ions.

M" is preferably Li + , Mg 2+ or a mixture of those cations.

Y is preferably OH " or F " , particularly preferably F " .

According to a particularly preferred embodiment of the invention, M is Li + , Na + , H + or a mixture of two or more of those ions, M' is Mg 2+ , M" is Li + , and Y is F " . A synthesis procedure of suitable synthetic layered silicates is described in M. Stoter et al., Langmuir 2013, 29, 1280-1285. A method for producing suitable and preferred phyllosilicates having high aspect ratios is described in WO 201 1/089089. Synthetic phyllosilicates may be prepared by high-temperature melt synthesis, followed by exfoliation and/or delamination to give phyllosilicate platelets having a high aspect ratio, e.g. as described in WO 201 1/089089 or in WO 2012/175431 . By means of this process it is possible to obtain phyllosilicate platelets having an average aspect ratio greater than 400. A further advantage of the phyllosilicate platelets obtainable by this process is that, unlike natural montmorillonites and vermiculites, which are more or less yellowish-brown in colour, they are colourless. This allows colourless composite materials to be produced therefrom.

Suitable phyllosilicates may also be produced hydrothermally, for example hydrothermally produced smectite such as Optigel® SH. It is well known to produce hectorite synthetically via hy- drothermal processing. For example, U.S. Patent Nos. 3,954,943 and 3,586,478 teach the synthesis of fluorine containing hectorite by a hydrothermal process. WO 2014/164632 teaches suitable synthetic zinc hectorite via hydrothermal preparation.

Preferably, the phyllosilicates are surface-modified with at least one organic compound having at least one group selected from amino groups and ammonium groups. Different type of cationic modification can be used to replace metal cations (e.g. sodium cations) from the surface of the delaminated phyllosilicates. The surface modification can provide stabilization of the delaminat- ed or exfoliated phyllosilicates and compatibilization with polymers (a) and (b).

Cationic modification means that an organic moiety has been strongly attached to the phyllosilicate by a treatment of subjecting the phyllosilicate to an ion exchange process whereby inor- ganic cations present in the phyllosilicate are replaced by organic cations comprising, but not limited to, either an organic group bonded to a cationic salt group, such as quaternary ammonium, phosphonium, pyridinium or the like, or an organic compound containing a cationic amine salt. The phyllosilicates are made organophilic by ion-exchanging organic or polymeric molecules between the inorganic layers, e.g. according to a process as described in U.S. Pat. No.

5,578,672. By way of example, mention may be made of the organophilic clays described in U.S. Pat. No. 6,1 17,932. Preferably, the clay is modified with an organic substance by ionic bonding with an onium ion having preferably 4 carbon atoms or more. If the number of carbon atoms is less than 4, the organic onium ion might be too hydrophilic and therefore the compatibility with the polymer matrix may decrease. By way of example of organic onium ion, mention may be made of hexylammonium ions, octylammonium ions, 2-ethylhexylammonium ions, do- decylammonium ions, laurylammonium ions, octadecylammonium (stearylammonium) ions, dioctyldimethylammonium ions, trioctylammonium ions, distearyldimethylammonium ions, stea- ryltrimethylammonium ions and ammonium laurate ions. It is recommended to use a clay having the highest possible surface of contact with the polymer, Other examples of organic onium ions or their precursors used for cationic modification may be selected from amino acids like glycine, alanine, lysine, ornithine or their derivatives; e.g. L-lysine monohydrochloride or Ν,Ν,Ν-trimethylglycine hydrochloride (= betaine); from amino alcohols like ethanol amine, Ν,Ν'-dimethyl ethanolamine, Ν,Ν'-dimethylamino ethoxyethanol, diethanol amine, triethanolamine, 2-amino-2-(hydroxymethyl)-1 ,3-propandiol (= TRIS); or from alkoxylated amines or amides like ethoxylated ethylene diamine (e.g. Mazeen® 184, Tetronic® 90R4,

Tetronic ©904 or Tetronic® 1 107), ethoxylated fatty amines (e.g. Lutensol® FA 12, Lutensol® FA 12K), ethoxylated fatty acid amides (e.g. Lutensol® FSA 10) or polyether amines like Jef- famine® M-600, M-1000, M-2005 or M-2070 from the Jeffamine® M-series or Polyamine D-230, D-400, D-2000, T-403 or T-5000 from BASF. Preferred modifiers are betaine, TRIS, lysine, alkoxylated ethylene diamines or ethoxylated fatty amines.

The cationic exchange capacity of the phyllosilicates is preferably from 50 and 200 milliequiva- lents per 100 g. The proportion of organic onium ion is advantageously from 0.3 to 3, preferably from 0.3 to 2 equivalents of the ion exchange capacity of the clay.

One embodiment of the invention is a polymer film coated with an aqueous composition as described above, in particular a polymer film comprising an oxygen barrier coating obtainable via the use of an aqueous composition as described above, wherein at least one side of the polymer film has been coated with an aqueous composition comprising

(a) at least one polyanion,

(b) at least one ethoxylated polyethyleneimine, and

(c) at least one phyllosilicate.

The oxygen transmission rate of the coated film is preferably less than 40% of the oxygen transmission rate of the uncoated film, measured at 25 °C and 75% relative humidity.

The aqueous composition used for the coating process can comprise further additives or auxiliaries, e.g. thickeners for adjusting rheology, wetting aids, or binders. Preferred polymer film substrates are polymer films which are suitable for packaging.

Preferred polymer films are made of oriented polypropylene or polyethylene, where the polyethylene can be produced from ethylene either by the high-pressure polymerization process or by the low-pressure polymerization process. Examples of other suitable polymer films are made of polyester, such as polyethylene terephthalate, and films made of polyamide, polystyrene and polyvinyl chloride. In one embodiment, the polymer film is biodegradable, e.g. made of biodegradable aliphatic-aromatic copolyesters and/or polylactic acid, an example being Ecoflex® films or Ecovio® films. Examples of suitable copolyesters are those formed from alkanediols, in particular C2 to C8 alkanediols, e.g. 1 ,4-butanediol, and from aliphatic dicarboxylic acids, in particular C2 to C8 dicarboxylic acids, e.g. adipic acid, and from aromatic dicarboxylic acids, e.g. terephthalic acid. Preferred polymer film materials are selected from polyethylene terephthalate, oriented polypropylene, casted polypropylene, polyethylene, biodegradable aliphatic- aromatic copolyesters, metalized polyethylene terephthalate, metalized oriented polypropylene and polyamide.

The thickness of the polymer film can be in the range from 5 to 200 μηη, in the case of films made of polyamide from 5 to 50 μηη, in the case of films made of polyethylene terephthalate from 10 to 100 μηη, in case of oriented polypropylene form 10 to 100 μηη, in the case of films of polyvinyl chloride about 100 μηη, and in the case of films made of polystyrene about 30-75 μηη.

Preferably, the oxygen barrier coating on the polymer film is pore-free, which can be analyzed by atomic force microscopy (AFM) or scanning electron microscope (SEM). One object of the invention is a method of forming a polymeric film with enhanced oxygen barrier properties comprising:

- applying an aqueous composition according to the invention as described above to at least one side of the polymer film, and

- drying said composition to form a barrier coating on the polymer film.

The aqueous composition can be applied by typical coating machinery to a backing film made of a plastic. If materials in the form of webs are used, the aqueous composition is usually applied from a trough by way of an applicator roll and rendered uniform with the aid of an air knife. Other suitable possibilities for applying the coating use the reverse gravure process, or spray pro- cesses, or a spreader system that uses a roll, or other coating processes known to the person skilled in the art. The aqueous composition can also be applied in a multi-coating process, wherein a first coating is followed by a second or more coating. A preferred coating method is spray coating, e.g. airbrush coating. Other suitable coating processes are the known intaglio printing and relief printing processes. Instead of using different inks in the printing-ink units, the process here by way of example uses a printing process for application of the aqueous polymer solution. Printing processes that may be mentioned are the flexographic printing process as a relief printing process known to the person skilled in the art, the gravure process as an example of intaglio printing, and offset print- ing as an example of flatbed printing. Modern digital printing, inkjet printing, electrophotography and direct imaging can also be used.

In order to achieve a further improvement in adhesion on a polymer film, the backing film can be previously subjected to corona treatment. Examples of the amounts applied to the sheet materials are preferably from 0.2 to 50 g (polymer, solid) per m 2 , preferably from 0.5 to 20 g/m 2 or from 1 to 15 g/m 2 . In order to achieve a further improvement in adhesion on a polymer film, a pre-coating or a primer can be applied on the polymer film before coating the oxygen barrier onto the substrate. Such primers can be based on polyurethane dispersions, polyurethane solutions, solvent-free or solvent based reactive polyurethane, polyethylene imine, polyacrylates or other primers known to the person skilled in the art.

Once the aqueous coating composition has been applied to the sheet substrates, the solvent is evaporated. For this, by way of example, in the case of continuous operation, the material can be passed through a drying tunnel, which can have an infrared irradiation apparatus. The coated and dried material is then passed over a cooling roll and finally wound up. The thickness of the dried coating is preferably from 0.2 to 50 μηη, particularly preferably from 0.5 to 20 μηη, most preferred from 1 -15 μηη.

The substrates coated with the aqueous coating composition exhibit excellent oxygen-barrier action, in particular in high humidity environments. The coated substrates can be used for ex- ample as means of packaging, preferably for packaging foods. The coatings have very good mechanical properties and exhibit, for example, an extraordinary flexibility.

The oxygen barrier coating can also be used as a barrier coating against other substances. Such substances can be carbon dioxide, nitrogen, bisphenol A (BPA), mineral oil, fat, alde- hydes, grease, plasticizer, photoinitiators or aroma substances.

In order to obtain specific additional surface properties or specific coating properties of the coated polymer films, for example good printability, or further improved sealing and non- blocking properties, or good water-resistance, it can be advantageous to overcoat the coated substrates with topcoat layers which provide these desired additional properties. The substrates precoated with the aqueous coating composition according to the invention can readily be over- coated. For the overcoating process, one of the processes mentioned above can be repeated, or repeated coating can be carried out in a continuous process without any intervening wind-up and unwind of the foil. The location of the oxygen barrier layer can thus be in the interior of the system, and the surface properties are then determined by the topcoat layer. The topcoat layer has good adhesion to the oxygen-barrier layer. Due to the good humidity resistance, it is in particular not necessary to apply an additional moisture-protection coating to ensure that the oxygen-barrier layer is effective even at relatively high humidity levels. In one embodiment, a polymer film of the invention comprises in addition to the oxygen barrier coating at least one additional layer made from materials selected from the group consisting of polyacrylates, polyvinylidene chloride (PVDC), waxes, epoxy resins, UV curable acrylates and polyurethanes. In one embodiment of the invention a polymer film of the invention as described above is laminated with at least one additional material wherein the at least one additional material is selected from polyethylene terephthalate, oriented polypropylene, polyethylene, casted polypropyl- ene, biodegradable aliphatic-aromatic copolyesters, metalized polyethylene terephthalate, met- alized oriented polypropylene, polyamide, paper and board.

Another object of the invention is a package comprising a polymer film according to the invention as described above.

Another object of the invention is the use of an aqueous composition according to the invention as described above for providing oxygen barrier properties.

Examples

Measurement of oxygen-barrier action:

Oxygen transmission rate (OTR) is determined on coatings on polymer films at a relative humidity (RH) level of 75% and at a temperature of 25 °C.

Measurements are done with synthetic air (21 % oxygen; results are extrapolated for 100% oxy- gen.

Carrier material: polymer film of PET (polyethylene terephthalate) with a thickness of 50 μηη. OTR of the uncoated film: 27,4 ± 0,2 cm 3 /(m 2* d).

The determination method is based on ASTM D3985 - 05, using a coulometric sensor. Each sample is measured twice and the mean result is calculated.

OTR are obtained on a Mocon OX-TRAN 2/21 XL instrument with a lower detection limit of 0.0005 cm 3 m- 2 day- 1 bar 1 .

Water vapour transmission rates (WVTR) were measured on a Mocon PERMATRAN-W model 333 at 25 °C and a relative humidity of 75% RH. The lower detection limit of the device was 0.05 g m- 2 day- 1 .

Polymer samples:

PEI1 33 wt.% aqueous solution of polyethyleneimine, Mw = 750000 g/mol;

charge density 17 meq/g, pH = 1 1

PEIE ethoxylated polyethyleneimine, 80 wt.% in water; Mw = 13000 g/mol

molar ratio of ethylene oxide units to ethyleneimine units = 20:1 (degree of ethoxyla- tion = 20.5 : 1 )

PAA polyacrylic acid, Mw = 100000 g/mol ; 35 wt% in water,

PPE1 polyelectrolyte complex made from PAA and PEIE in a weight ratio of 70 30, pH 4.3

PPE2 polyelectrolyte complex made from PAA and PEIE in a weight ratio of 90 10, pH 4.2

PPE3 polyelectrolyte complex made from PAA and PEIE in a weight ratio of 70 30, pH 3.3

Phyllosilicates:

Na-hect synthetic sodium fluorohectorite

L-hect hectorite modified with L-lysine

BT-hect hectorite modified with betaine

Tris-hect hectorite modified with 2-Amino-2-(hydroxymethyl)-1 ,3-propanediol (TRIS)

Modification agents:

L-lysine: (S)-2,6-Diaminohexanoic acid monohydrochloride C6H14N2O2.HCI,

reagent grade≥ 98%, Sigma-Aldrich GmbH, Germany.

Betaine: Ν,Ν,Ν-trimethylglycine (anhydrous), C5H11 NO2, Alfa Aesar GmbH, Germany

TRIS: 2-Amino-2-(hydroxymethyl)-1 ,3-propanediol, C4H11 NO3, reagent grade > 99.9 %,

Sigma-Aldrich GmbH, Germany. The pH of 0.5 M solution of TRIS was adjusted to 5.75 with hydrochloric acid.

The type of phyllosilicate used in the examples is exfoliated smectite type with layer charge of 0.5 per formula unit (p.f.u.). The synthesis procedure of the used phyllosilicate is described in M. Stoter, D. A. Kunz, M. Schmidt, D. Hirsemann, H. Kalo, B. Putz, J. Senker, J. Breu, Langmuir 2013, 29, 1280-1285. The phyllosilicate is a synthetic sodium fluorohectorite (Na-hect) and has a cation exchange capacity of 127 meq/100 g. The chemical formula is:

[Nao.5.xH 2 0] int [Mg2.5Lio.5] oct [Si4] te ioF2

Modification of the sodium fluorohectorite:

Different type of cationic modification where used to replace sodium cations from the surface of the delaminated layered silicate. Modification provides stabilization of the delaminated layered silicates and compatibilization of the layered silicate with the polymer matrix within the suspen- sion and in the drying step of film-formation.

Example 1 : Modifying delaminated Na-hect

In a 50 ml centrifuge tube 0.25 g of Na-hect was suspended in 30 ml of distillate water. For the surface modification of the Na-hect a 125% of CEC (cation exchange capacity) of the modifica- tion agent (after dissolved in 5 ml distillate water) was added and placed into an overhead shaker for 12 h. Afterward the modified Na-hect was centrifuged at 10000 rpm, the separated supernatant was discarded and the modified Na-hect was re-suspended in distillate water and again a 125% of CEC of the modification agent (after dissolved in 5 ml distillate water) was added and placed into an overhead shaker for 12 h to ensure complete surface modification of Na-hect. At last the modified Na-hect was centrifuged at 10000 rpm and the separated supernatant was discarded and the modified Na-hect was washed with distilled water washed until the conductivity of the separated supernatant was below 25 μβ.

Example 2: Mixing of polyanion (PAA) with ethoxylated polyethyleneimine (PEIE) in a 70:30 weight ratio to form polyelectrolyte complex (PPE1 )

8 g of the solution of PAA in water with 35 wt% solid content was mixed with 2.5 ml of a 3M solution of NH3 in water and then 1 .5 g of a 80 wt.-% (solution in water) of PEIE was added. 5 ml of distilled water was added to the mixture and mixed via magnetic stirring for 4h.

pH: 4.3

A mixture of the resulting PPE1 was coated on a PET substrate with speed blade 18 mm/s. The film was dried at 80 °C for 24 h and the OTR and WVTR were measured (see table 1 ). Example 3: Suspension of modified phyllosilicate Na-hect with a matrix polyelectrolyte complex (PPE1 ) with weight ratio 50:50.

Example 3a: Modification with betain (BT-hect50):

The amount of a Na-hect modified with BT according to procedure illustrate in example 1 was added to the required amount of PPE1 to produce a suspension with 50 wt.% (based on inorganic material, i.e. without modification agent) of phyllosilicate layer silicate in the final solid matrix (the amount of modification agent was calculated on the side of polymer). The final suspension ready to coating has a solid content of 2 wt%.

The suspension was deposited on PET foils using doctor-blading with speed of blade 18 mm/s. The film was dried at 80 °C for 24h and the OTR and WVTR were measured (see table 1 ).

Example 3b Modification with TRIS (Tris-hect50):

The procedure of example 3a was applied to prepare nanocomposites using TRIS as modification of Na-hect.

The coated film was dried at 80 °C for 24h and the OTR and WVTR were measured at 25°C and 75%RH (see table 1 ).

Example 3c: Modification with L-lysine (L-hect)

The procedure of example 3a was applied to prepare nanocomposite using L-lysine as modification of Na-hect with various amounts of L-hect:

Example 3c: 50 wt.-% inorganic material (L-hect50)

Example 3d : 10 wt.-% inorganic material (L-hect10)

Example 3c2: 20 wt.-% inorganic material (L-hect20)

Example 3c3: 30 wt.-% inorganic material (L-hect30)

Example 3c4: 40 wt.-% inorganic material (L-hect40) The coated film was dried at 80 °C for 24h and the OTR and WVTR were measured at 25°C and 75%RH (see table 1 ).

Example 4: Mixing of polyanion (PAA) with ethoxylated polyethyleneimine (PEIE) in a 90:10 weight ratio to form polyelectrolyte complex (PPE2)

12.86 g of the solution of PAA in water with 35 wt% solid content was mixed with 4.2 ml of 3M solution of NH3 in water, then 5 ml of distilled water were added and the mixture was mixed via magnetic stirring for 30 min. Then 0.63 g of 80 wt.-% solution in water of PEIE was added. The whole mixture was then homogenized via magnetic stirring for 4 h.

pH: 4.2

A mixture of the resulting PPE2 was coated on a PET substrate with blade speed of 18 mm/s. The film was dried at 80 °C for 24 h (see table 1 ). Example 4a1 : PPE2 + BT-hect

The procedure of example 3a was applied to prepare nanocomposites using betaine as modification of Na-hect and PPE2 (example 4) as polymer matrix. The amount of inorganic silicate material was 10 wt.-% of phyllosilicate in final solid matrix.

The coated film was dried at 80 °C for 24h and the OTR and WVTR were measured at 25°C and 75%RH (see table 1 ).

Example 4a2: PPE2 + L-hect

The procedure of example 3a was applied to prepare nanocomposites using L-lysine as modification of Na-hect and PPE2 (example 4) as polymer matrix. The amount of inorganic silicate material was 10 wt.-% of phyllosilicate in final solid matrix.

The coated film was dried at 80 °C for 24h and the OTR and WVTR were measured at 25°C and 75%RH (see table 1 ).

Example 5 PPE3

8 g of the solution of PAA (35 wt% solid content in water) was mixed with 0.75 ml of 3M solution of NH3 in water and then 1.5 g of a 80 wt.-% solution in water of PEIE was added. 5 ml of dis- tilled water was added to the mixture and mixed via magnetic stirring for 4h.

pH: 3.3

A mixture of the resulting PPE3 was coated on a PET substrate with speed blade 18 mm/s. The film was dried at 80 °C for 24 h and the OTR and WVTR were measured (see table 1 ).

Example 5a1 PPE3 + L-hect

The procedure of example 3a was applied to prepare nanocomposites using L-lysine as modification of Na-hect and PPE3 (example 5) as polymer matrix. The amount of inorganic silicate material was 20 wt.-% of phyllosilicate in final solid matrix.

The coated film was dried at 80 °C for 24h and the OTR and WVTR were measured at 25°C and 75%RH (see table 1 ).

Example 6 (comparative):

Suspension of modified phyllosilicate Na-hect with a matrix polyelectrolyte complex of PAA and not-ethoxylated PEI 1.

The procedure of example 3a was applied to prepare nanocomposite using L-lysine as modification of Na-hect and using 100 parts by weight PAA and 40 parts by weight of PEI1 instead of PEIE.

Example 7 (comparative): PAA + L-hect (100:20)

The procedure of example 3a was applied to prepare nanocomposite using L-lysine as modification of Na-hect and using 100 parts by weight PAA only, i.e. without PEIE. The amount of inorganic silicate material was 20 wt.-% of phyllosilicate in final solid matrix. Example 8 (comparative): PAA + L-hect (100:50)

The procedure of example 3a was applied to prepare nanocomposite using L-lysine as modifi- cation of Na-hect and using 100 parts by weight PAA only, i.e. without PEIE. The amount of inorganic silicate material was 50 wt.-% of phyllosilicate in final solid matrix.

Table 1 : Oxygen barrier and water vapor barrier measurement results

pH Thickness OTR VWTR

Film

[Mm] [cm 3 nr 2 day 1 bar 1 ] [g nr 2 day 1 ]

Uncoated PET -

50 27.4 (± 0.2) 4.67 substrate (comp.)

Ex. 2

4.3 8 25.4 (± 0.1 ) 4.27 PPE1 (comp.)

0.1 1 (± 0.01 ) 0.34

Ex. 3a BT-hect50 4.5 - 5 3

0.010 1 > 0.08 1 >

Ex 3b T-hect50 4.5 - 5 2.5 0.54 (± 0.03) 0.53

0.2 (± 0.02) 0.30

Ex. 3c L-hect50 4.5 - 5 2.4

0.020 1 > 0.08 1 >

Ex. 3d L-hect10 4.5 2 10.2 1 .5

Ex. 3c2 L-hect20 4.7 2 8.38 1 .21

Ex. 3c3 L-hect30 4.8 1 -2 6.41 0.90

Ex. 3c4 L-hect40 5 1 -2 4.65 0.77

Ex. 4

4.2 8 21.4 3.2 PPE2 (comp.)

Ex. 4a 1

4.5 2 8.02 2.95 PPE2 + BT-hect

Ex. 4a2

4.5 2 8.23 1 .4 PPE2 + L-hect

Ex. 5 PPE3

3.3 13-14 22.78 2.96 (comp.)

Ex. 5a 1 3.5 4 0.82 0.53 PPE3 + L-hect

Ex. 6 (comp.) No stable No stable

No stable formulation

PAA/PEI + L-hect formulation formulation

Ex. 7 (comp.)

PAA + L-hect 3-4 14,6 3,8

100:20

Ex. 8 (comp.)

PAA + L-hect 1 -2 10,3 2,1

100:50

1) Film dried for 48 hours

Example 9: Modification with L-lysine (L-hect50) for spray coating

The procedure of example 3a was applied to prepare nanocomposite using L-lysine as modifi- cation of Na-hect and PPE1. The final formulation contained 20 wt.-% of inorganic material, based on solids with a total solids content of 2 wt.-%.

Example 10: Modification with L-lysine (L-hect50) for spray coating

Same composition as Example 9, but with a total solids content of 1 wt.-%.

The compositions of examples 9 and 10 were spray coated on a PET substrate (optimont® BOPET-film; 100μηι) and the OTR and WVTR were measured (see table 2).

Spray coating parameters:

55 cycles (example 9); 1 10 cycles (example 10)

Spray device: SATAjet® 4000 LAB HVLP 1 ,0 mm

Carrier gas: air; inlet pressure 4 bar; outlet pressure 2-4 bar

Flow rate carrier gas: about 450 l/min at 2,5 bar

Flow rate suspension: 60 ml/min

Uniaxial application

Treadmill speed 1 m/sec

Drying: 60 sec at 60 °C with 250 W I R lamps

Table 2: Oxygen barrier and water vapor barrier measurement results for spray coated samples

Coating thickness OTR WVTR

Film

[Mm] [cm 3 nr 2 day 1 bar 1 ] [g nr 2 day 1 ]

Uncoated PET

0 1 1.5 1 .8

substrate 100 μηη

Ex. 9 2-3 6.68 · 10- 3 < 0.005

Ex. 10 4-6 7.19 · 10- 4 < 0.005