Title:
CORROSION INHIBITOR
Document Type and Number:
WIPO Patent Application WO/2003/083173
Kind Code:
A2
Abstract:
The corrosion inhibitor blend of at least one corrosion inhibitor base (which may be a Mannich reaction product), a solvent selected from the group consisting of C1 acids and ester and salt derivatives thereof, and optionally a surfactant, has been found to be effective as a corrosion inhibitor for metals in acid media, particularly fluids containing halogen acids. The corrosion inhibitor has improved performance over similar or identical corrosion inhibitor composi­tions where an alcohol such as methanol is used as a solvent. Suitable, non­limiting possibilities for the solvent include, but are not necessarily limited to formic acid, format salts, methyl format, ethyl format, benzyl format, format salts of amines, inorganic format, and mixtures thereof.

Inventors:
WALKER MICHAEL L
Application Number:
PCT/US2003/009047
Publication Date:
October 09, 2003
Filing Date:
March 25, 2003
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BAKER HUGHES INC (US)
International Classes:
C09K8/54; C23F11/04; C23F11/14; (IPC1-7): C23F11/04
Foreign References:
US4493775A1985-01-15
EP0276879A11988-08-03
EP0869258A11998-10-07
EP0638663A21995-02-15
US6117364A2000-09-12
US4028268A1977-06-07
US3779935A1973-12-18
US5697443A1997-12-16
US3634270A1972-01-11
US3077454A1963-02-12
Attorney, Agent or Firm:
Littlefield, Stephen A. (Baker Petrolite Division Baker Hughes Incorporate, d, 12645 West Airport Boulevar, Sugar Land TX, US)
Download PDF:
Claims:
What is claimed is:
1. A corrosion inhibitor comprising: a. at least one corrosion inhibitor base selected from the group consisting of: i) a Mannich reaction product, and ii) a nitrogensubstituted heterocycle of 6 to 10 members quaternized with at least one alkyl or aryl halide ; and b. at least one first solvent selected from the group consisting of Ci acids and ester derivatives thereof and salts thereof.
2. The corrosion inhibitor of claim 1 where the Mannich reaction product comprises the product of reaction of (i) one mole of an ammonia derivative having at least one hydrogen attached to nitrogen and having no groups reactive under the conditions of reaction other than hydrogen, (ii) from 1.5 to 10 moles of a carbonyl compound having at least one hydrogen atom on the carbon atom adjacent to the carbonyl group, (iii) from 2 to 10 moles of an aldehyde different from the carbonyl compound, selected from the group consisting of aliphatic aldehydes having from 1 to 16 carbon atoms and aromatic aldehydes of the benzene series and having no functional groups other than aldehyde groups, and (iv) from 0.6 to 24 parts by weight based on (1), (2), and (3) of a fatty acid having from 1 to 20 carbon atoms at a temperature of from 150°F (66°C) to 250°F (121°C) for from 1 to 16 hours.
3. The corrosion inhibitor of claim 1 where the at least one first solvent is selected from the group consisting of formic acid, formate salts, methyl formate, ethyl formate, benzyl formate, formate salts of amines, inorganic formates, and mixtures thereof.
4. The corrosion inhibitor of claim 1 where the components are present in the following proportions: a. 10 to 60 volume % corrosion inhibitor base; and b. 3 to 50 volume % solvent, based on the total corrosion inhibitor.
5. The corrosion inhibitor of claim 1 further comprising a second solvent different from the first solvent present up to 50 volume %, based on the total corrosion inhibitor.
6. The corrosion inhibitor of claim 1 further comprising at least one surfactant.
7. The corrosion inhibitor of claim 6 where the at least one surfactant is an alcohol or an esterified alcohol that has been alkoxylated.
8. The corrosion inhibitor of claim 8 where the alcohol used to make the at least one surfactant has from 6 to 30 carbon atoms.
9. The corrosion inhibitor of claim 6 where the components are present in the following proportions: a. 10 to 60 volume % corrosion inhibitor base; b. 3 to 50 volume % solvent; and c. 5 to 50 volume % surfactant, based on the total corrosion inhibitor.
10. A method of inhibiting the corrosion of metals in the presence of a liquid medium containing at least one halogen acid comprising including in the fluid a corrosion inhibitor comprising a. at least one corrosion inhibitor base selected from the group consisting of: i) a Mannich reaction product, and ii) a nitrogensubstituted heterocycle of 6 to 10 members quaternized with at least one alkyl or aryl halide ; and b. at least one first solvent selected from the group consisting of Ci acids and ester derivatives thereof and salts thereof.
11. The method of claim 10 where the corrosion inhibitor comprises at least one Mannich reaction product comprises the product of reaction of (i) one mole of an ammonia derivative having at least one hydrogen attached to nitrogen and having no groups reactive under the conditions of reaction other than hydrogen, (ii) from 1.5 to 10 moles of a carbonyl compound having at least one hydrogen atom on the carbon atom adjacent to the carbonyl group, (iii) from 2 to 10 moles of an aldehyde different from the carbonyl compound, selected from the group consisting of aliphatic aldehydes having from 1 to 16 carbon atoms and aromatic aldehydes of the benzene series and having no functional groups other than aldehyde groups, and (iv) from 0.6 to 24 parts by weight based on (1), (2), and (3) of a fatty acid having from 1 to 20 carbon atoms at a temperature of from 150°F (66°C) to 250°F (121°C) for from 1 to 16 hours.
12. The method of claim 10 where in the corrosion inhibitor, the at least one first solvent is selected from the group consisting of formic acid, formate salts, methyl formate, ethyl formate, benzyl formate, formate salts of amines, inorganic formates, and mixtures thereof.
13. The method of claim 10 where the components of the corrosion inhibitor are present in the following proportions: a. 10 to 60 volume % corrosion inhibitor base; and b. 3 to 50 volume % solvent, based on the total corrosion inhibitor.
14. The method of claim 10 where the corrosion inhibitor further comprises a second solvent different from the first solvent, and the second solvent is present up to 50 volume %, based on the total corrosion inhibitor.
15. The method of claim 10 where the corrosion inhibitor further comprises at least one surfactant.
16. The method of claim 15 where in the corrosion inhibitor, the at least one surfactant is an esterified alcohol that has been alkoxylated.
17. The method of claim 16 where in the surfactant, the alcohol used to make the at least one surfactant has from 6 to 30 carbon atoms.
18. The method of claim 15 where the components of the corrosion inhibitor are present in the following proportions: a. 10 to 60 volume % corrosion inhibitor base; b. 3 to 50 volume % solvent ; c. 5 to 50 vol. % surfactant; and based on the total corrosion inhibitor.
19. The method of claim 10 where the amount of corrosion inhibitor in the liquid ranges from 0.1 to 3.0% volume %.
20. A fluid for contacting a metal surface, the fluid comprising A. at least one halogen acid; and B. a corrosion inhibitor comprising: a. at least one corrosion inhibitor base selected from the group consisting of: i) a Mannich reaction product, and ii) a nitrogensubstituted heterocycle of 6 to 10 members quaternized with at least one alkyl or aryl halide ; and b. at least one first solvent selected from the group consisting of Ci acids and ester derivatives thereof and salts thereof.
21. The fluid of claim 20 where in the corrosion inhibitor, the Mannich reaction product comprises the product of reaction of (i) one mole of an ammonia derivative having at least one hydrogen attached to nitrogen and having no groups reactive under the conditions of reaction other than hydrogen, (ii) from 1.5 to 10 moles of a carbonyl compound having at least one hydrogen atom on the carbon atom adjacent to the carbonyl group, (iii) from 2 to 10 moles of an aldehyde different from the carbonyl compound, selected from the group consisting of aliphatic aldehydes having from 1 to 16 carbon atoms and aromatic aldehydes of the benzene series and having no functional groups other than aldehyde groups, and (iv) from 0.6 to 24 parts by weight based on (1), (2), and (3) of a fatty acid having from 1 to 20 carbon atoms at a temperature of from 150°F (66°C) to 250°F (121°C) for from 1 to 16 hours.
22. The fluid of claim 20 where in the corrosion inhibitor, the at least one first solvent is selected from the group consisting of formic acid, formate salts, methyl formate, ethyl formate, benzyl formate, formate salts of amines, inorganic formate, and mixtures thereof.
23. The fluid of claim 20 where in the corrosion inhibitor, the components are present in the following proportions: a. 10 to 60 vol. % corrosion inhibitor base; and b. 3 to 50 vol. % solvent.
24. The fluid of claim 20 where the amount of corrosion inhibitor in the liquid ranges from 0.1 to 22 volume %.
25. The fluid of claim 20 where the corrosion inhibitor further comprises a second solvent different from the first solvent, and the second solvent is present up to 50 volume %, based on the total corrosion inhibitor.
26. The fluid of claim 20 where the corrosion inhibitor further comprising at least one surfactant.
27. The fluid of claim 26 where in the corrosion inhibitor, the at least one surfactant is an esterified alcohol that has been alkoxylated.
28. The fluid of claim 27 where in the surfactant, the alcohol used to make the at least one surfactant has from 3 to at least 22 carbon atoms.
29. The fluid of claim 26 where in the corrosion inhibitor, the components are present in the following proportions: a. 10 to 60 vol. % corrosion inhibitor base; b. 3 to 50 vol. % solvent; and c. 5 to 50 vol. % surfactant.
30. The fluid of claim 20 where the amount of corrosion inhibitor in the liquid ranges from 0.1 to 22 volume %.
Description:
CORROSION INHIBITOR Field of the Invention The invention relates to methods and compositions for inhibiting corro- sion of metals, and, in one aspect, more particularly relates to methods and compositions for inhibiting corrosion of metals in acid environments where the acid contains halogen, such as hydrochloric acid, hydrofluoric acid, and the like.

Background of the Invention It is well known that steel surfaces will corrode in the presence of acid environments. While the rate at which corrosion will occur depends on a number of factors, such as the steel alloy itself, the strength and type of acid, the temperature of the environment, the length of contact, etc. , some sort of corrosion invariably occurs. Alloy technology has provided materials to withstand the incidental contact of steel with acid, but the corrosion problem is particularly aggravated when there is no choice but to contact steel with acid, as in the case of chemical processing where acids are employed. In instances where the acid is not required to remain pure and where the contact is inevitable, attention has turned toward providing corrosion inhibitors in the acid medium itself to prevent corrosion of the steel surfaces that it must come into contact with, yet still deliver the acid to its ultimate destination. It would be advantageous if a new corrosion inhibitor were discovered that would be an improvement over the presently known systems. For example, a corrosion inhibitor providing a large corrosion inhibiting effect for a small proportion used would be advantageous.

Specific environments in which an improved corrosion inhibitor would be appreciated include industrial cleaning and hydrocarbon recovery operations.

With respect to oil and gas production, it is well known that during the produc- tion life of an oil or gas well, the production zone within the well may be chemi- cally treated or otherwise stimulated to enhance the economical production life- time of the well. A common way of doing this is by acid fracturing or matrix acidizing, whereby a highly acidic solution, generally having a pH of less than

about 1, but which may be as high as about 6.9 is injected into the well. Spent acid in return fluids may have a pH of around 3 to 6.9. Because of the acidic nature of the treatment fluid, the production or workover conduit which is utilized in the well in such applications encounters considerable acidic corrosion, in the forms of surface pitting, embrittlement, loss of metal component and the like. Halogen acids are commonly used in these fluids.

In earlier years of producing subterranean wells, the vast majority of pro- duction and workover conduits comprised carbon steels. These steels were utilized either temporarily or permanently in the well, and treatment and/or stim- ulation fluids were introduced through them into the well. Recently, due pri- marily to the drilling and completion of many subterranean wells through forma- tions which contain high concentrations of corrosive fluids such as hydrogen sulfide, carbon dioxide, brine, and combinations of these constituents, the pro- duction and workover conduits for use in the wells have been made of high alloy steels. The high alloy steels include chrome steels, duplex steels, stainless steels, martensitic alloy steels, ferritic alloy steels, austenitic stainless steels, precipitation-hardened stainless steels, high nickel content steels, and the like.

Various corrosion inhibitors are known, to which are added other compo- nents, such as intensifiers, surfactants, oil wetting components, and the like.

U. S. Pat. No. 2,758, 970 describes derivatives of rosin amines, which are represented by the formula : where R is a radical selected from the group consisting of abietyl, hydroabietyl, and dehydroabietyl, Y is the group CH2R,, X is a radical selected from the group consisting of hydrogen and CH2R1, and Ri represents alpha ketonyl groups. These rosin amines are noted as useful in reducing the rate of corrosion of metals such as magnesium, aluminum and zinc when they are exposed to the action of a corrosive material such as hydrochloric acid.

Further, U. S. Pat. No. 3,077, 454 describes compositions for inhibiting corrosion made by combining certain active hydrogen containing compounds

with organic ketones having at least one hydrogen atom on the carbon atom alpha to the carbonyl group and an aldehyde selected from the group consisting of aliphatic aldehydes containing from 1 to 16 carbons, and aromatic aldehydes of the benzene series, having no functional groups other than aldehyde groups, and a fatty acid.

Additionally, Mannich base and thiourea inhibitor compositions and methods of inhibiting the acid attack by aqueous hydrofluoric acid on ferrous metal surfaces, and in particular highly reactive ferrous metal surfaces, are described in U. S. Pat. Nos. 3,992, 313 and 4,104, 303.

There remains a need for new corrosion inhibitor and methods of use therefore which would work in halogen acid environments for a wide variety of metals, particularly iron alloys such as steels.

Summary of the Invention Accordingly, it is an object of the present invention to provide a composi- tion of matter effective in the inhibition of corrosion in halogen acid environ- ments.

It is another object of the present invention to provide a corrosion inhibi- tor composition for minimizing corrosion in halogen acid situations, which com- positions may be easily made.

Still another object of the invention is to provide a halogen acid corrosion inhibitor that has improved performance as compared with conventional corro- sion inhibitors.

In carrying out these and other objects of the invention, there is provided, in one non-limiting embodiment of the invention, a corrosion inhibitor having at least one corrosion inhibitor base selected from the group consisting of Mannich reaction products and nitrogen-substituted heterocycles of 6 to 10 members quaternized with at least one alkyl or aryl halide, and at least one first solvent selected from the group consisting of C, acids and ester derivatives thereof and salts thereof. At least one surfactant may be optionally present. An additional, second solvent may also be optionally present.

The invention also concerns methods of inhibiting the corrosion of metals in the presence of liquids containing at least one halogen acid and the

corrosion inhibitor of this invention. The corrosion of the metal is inhibited as compared with a liquid otherwise identical but absent the corrosion inhibitor of this invention. Additionally, the invention includes fluids for contacting metal surfaces that have had their corrosion inhibition improved by the corrosion inhibitor of this invention.

Brief Description of the Drawings The single Figure is a chart comparing the corrosion loss in Ibst2 (kg/m2) for a corrosion inhibitor of this invention with a conventional corrosion inhibitor as a function of temperature.

Detailed Description of the Invention It has been discovered that useful halogen acid corrosion inhibitor may be provided by the use of at least one corrosion inhibitor base selected from the group consisting a Mannich reaction product and a nitrogen-substituted heterocycle of 6 to 10 members quaternized with alkyl halides, at least one solvent, and optionally at least one surfactant. The solvent is a Ci acid or derivative thereof, particularly ester derivatives thereof.

In one non-limiting embodiment of the invention, the Mannich reaction products may include, but are not necessarily limited to, the materials of U. S.

Pat. Nos. 3,077, 454; 5,366, 643; and 5,591, 381. The products of U. S. Pat. No.

3,077, 454 can be made with approximately a 50% yield, and they require the presence of a fatty acid, such as a tall oil fatty acid, in one non-limiting embodi- ment. The text of this patent is incorporated by reference herein. More specifi- cally, the Mannich reaction product may be the product of reaction of (i) one mole of an ammonia derivative having at least one hydrogen attached to nitrogen and having no groups reactive under the con- ditions of reaction other than hydrogen, (ii) from 1.5 to 10 moles of a carbonyl compound having at least one hydrogen atom on the carbon atom adjacent to the carbonyl group, (iii) from 2 to 10 moles of an aldehyde different from the carbonyl compound selected from the group consisting of aliphatic

aldehydes having from 1 to 16 carbon atoms and aromatic aldehydes of the benzene series and having no functional groups other than aldehyde groups, and (iv) from 0.6 to 24 parts by weight based on (1), (2), and (3) of a fatty acid having from 1 to 20 carbon atoms at a temperature of from about 150°F (66°C) to about 250°F (121 OC) for from about 1 to 16 hours.

The nitrogen-substituted heterocycles of 6 to 10 members quaternized with alkyl halides are also commonly referred to as coal tar based quats. These materials are typically quinolines, pyridines and the like quaternized with alkyl and/or aryl halides, where the alkyl or aryl group may range from methyl to ben- zyl (Ci to C6). Naphthyl quinoline quats are included in this group. Further infor- mation may be found with reference to U. S. Pat. No. 2,814, 593, incorporated by reference herein, which discusses benzyl chloride quats of quinoline.

The surfactant suitable for use in the method of this invention may be, in one non-limiting embodiment, an esterified alcohol that has been alkoxylated.

In a particularly preferred embodiment, the alkoxylation is achieved by reaction with ethylene oxide. Propylene oxide and butylen oxide may also be used, as well as combinations thereof, such as a combination of ethylene oxide and pro- pylene oxide. Suitable alcohols have from about 6 to about 30 carbon atoms, preferably from about 12 to about 22 carbon atoms, and may have more than one hydroxyl group, in one non-limiting embodiment from 1 to 6 hydroxyl groups, and in another non-limiting embodiment from 1 to 3 hydroxyl groups.

Particular alcohols expected to be useful in preparing the surfactants for the compositions of this invention include, but are not necessarily limited to, sorbitol, glycerol, ethylene glycol, alkylphenols, and mixtures thereof. In a particularly preferred embodiment of the invention, the surfactant is made by esterifying sorbitol with one mole of tall oil and then reacting the product thereof with ethylene oxide until the desired properties are obtained. The desired properties include, but are not necessarily limited to, facilitating, improving and assisting the corrosion inhibitor base and the solvent in contacting any metal in contact with the fluid being inhibited. A suitable amount of ethylene oxide may

range from about 3 to about 60 moles, preferably from about 12 to about 40 moles in another non-limiting embodiment of the invention, and from about 3 to about 30 mules in yet another non-limiting embodiment.

It is expected that formic acid will be the solvent of choice, although other materials are expected to function equivalently. These materials include, but are not necessarily limited to ester derivatives of Ci acids, and salts of these acids or ester derivatives. In particular, the solvent may include, but is not necessarily limited to, formate salts, methyl formate, ethyl formate, benzyl formate, formate salts of amines, inorganic formates and mixtures thereof.

These inventive solvents unexpectedly and surprisingly give better results than conventional solvents such as unmodified or unreacted alcohols, which in one embodiment of the invention are preferably absent. However, it may be desirable in some embodiments to use conventional solvents as a second solvent such as low carbon number alcohols, e. g. isopropyl alcohol (IPA) for other reasons, including, but not necessarily limited to pour point depression.

These conventional solvents may be optionally present in the corrosion inhibitor in proportions from about 0 to about 50 volume % in one non-limiting embodiment, and from 0 to about 30 volume % in an alternate non-limiting embodiment.

In still another non-limiting embodiment of the invention, the proportions of the various components in the corrosion inhibitor composition may range from about 10 to about 60 vol. % corrosion inhibitor base, from about 5 to about 50 vol. % surfactant, and from about 3 to about 50 vol. % solvent. In a preferred embodiment of the invention, the corrosion inhibitor composition may range from about 10 to about 50 vol. % corrosion inhibitor base, from about 10 to about 50 vol. % surfactant, and from about 10 to about 40 vol. % solvent. In one particularly preferred embodiment of the invention, the corrosion inhibitor includes about 20% to 40% corrosion inhibitor base, about 20% to 40% surfactant, and about 10% to 40% solvent.

The halogen acid environments where the invention is useful encompass acid environments where the acid includes, but is not limited to, hydrochloric acid, hydrofluoric acid, formic acid, acetic acid, and mixtures thereof. The composition of this invention has been found to have excellent

stability, thus avoiding degradation over time. These corrosion inhibitors will be cost effective and provide excellent corrosion control.

The acid corrosion inhibitor may be combined with any suitable acidic injection medium, including but not necessarily limited to, such media as down- hole acidizing fluids and compositions; 15% and 28% concentrations of HCI, 15-5% acetic acid/HCI blend. It aids corrosion control at elevated temperatures and pressures with the inventive inhibitor.

Other optional ingredients may be used with the corrosion inhibitor of this invention, and may include, but are not necessarily limited to, any acetylenic compound such as acetylenic alcohols ; cinnamaldehyde ; a nitrogen compound, such as a quaternary ammonium compound; solvents such as alcohols or ketones; and aromatic hydrocarbons or mixtures thereof, as are known to those skilled in the art. For example, teachings from acid corrosion inhibitors as made and described in U. S. Pat. Nos. 3,514, 410 ; 3,404, 094; 3,107, 221; 2,993, 863; and 3,382, 179; may be utilized in accordance with the present invention. All of these patents are hereby incorporated by reference. In one embodiment, the corrosion inhibitor contains at least one acetylenic alcohol having from 3 to 10 carbon atoms.

Examples of acetylenic compounds that may be used include propargyl alcohol (2-propyn-1-ol), hexynol, dimethyl hexynol, diethyl hexynediol, dimethyl hexynediol, ethyl octynol, dimethyl octynediol, methyl butynol, methyl pentynol, ethynyl cyclohexynol, 2-ethyl hexynol, phenyl butynol, and ditertiary acetylenic glycol.

Other acetylenic compounds which can be employed in accordance with the present invention include, but are not limited to, butynediol ; 1-ethynylcyclo- hexanol ; 3-methyl-1-nonyn-3-ol ; 2-methyl-3-butyn-2-ol ; also 1-propyn-3-ol ; 1- butyn-3-ol ; 1-pentyn-3-ol ; 1-heptyn-3-ol ; 1-octyn-3-ol ; 1-nonyn-3-ol ; 1-decyn-3- ol ; 1- (2, 4, 6-trimethyl-3-cyclohexenyl)-3-propyne-1-ol ; and in general acetylenic compounds having the general formula :

wherein R'is-H,-OH, or an alkyl radical ; R2 is-H, or an alkyl, phenyl, substi- tuted phenyl or hydroxyalkyl radical ; and R3 is-H or an alkyl, phenyl, substituted phenyl or hydroxyalkyl radical.

The nitrogen or ammonia compounds that can be optionally employed in accordance with the present invention, may include, but are not limited to, those amines having from 1 to 24 carbon atoms in each alkyl moiety as well as the six-membered heterocyclic amines, for example, alkyl pyridines, crude quinolines and mixtures thereof. This includes such amines as ethylamine, diethylamine, triethylamine, propylamine, dipropylamine, tripropylamine, mono-, di-and tripentylamine, mono-, di-and trihexylamine and isomers of these such as isopropylamine, tertiary-butylamine, etc. This also includes alkyl pyridines having from one to five nuclear alkyl substituents per pyridine moiety, such alkyl substituents having from one to 12 carbon atoms, and preferably those having an average of six carbon atoms per pyridine moiety, such as a mixture of high boiling tertiary-nitrogen-heterocyclic compounds, such as HAP (high alkyl pyri- dines), Reilly 10-20 base and alkyl pyridines H3. Other nitrogen compounds include the crude quinolines having a variety of substituents.

The corrosion inhibitor may also contain a number of other constituents, such as fatty alcohol adducts, nonyl phenol adducts and tallow amine adducts, tall oil adducts, such as surfactants. Oil wetting components, such as heavy aromatic solvents, may also be present. In another non-limiting embodiment of the invention, the corrosion inhibitor contains at least one saturated alcohol having from 1 to 5 carbon atoms, and at least one alkyl phenol or alkoxylated alkyl phenol having from 15 to 24 carbon atoms.

In another non-limiting embodiment of the invention, the corrosion inhibi- tor has an absence of a source of molybdat ions. In yet another non-limiting embodiment of the invention, the corrosion inhibitor has an absence of cinna- aldehyde or substituted cinnamaldehyde.

It will be appreciated that the halogen acid corrosion inhibitor of this invention may be used with conventional corrosion inhibitors as described above and below, and in any application where a steel surface, such as stain- less steel, high alloy or other steel, is exposed to an acid environment. While the specific implementation of this invention is described in the context of the oil patch, the invention may certainly find uses in other applications where it is desirable to reduce corrosion, such as chemical processes that necessarily require the contact of acids with conduits, fittings, and other equipment, such as industrial cleaning applications.

In the implementation of the invention in the production of fluids from subterranean reservoirs, a fluid is introduced through a high alloy steel member or conduit positioned within the well. The fluid is an acidic injection medium and includes an acid corrosion inhibitor. The invention also encompasses a method of treating a well for enhancement of production within a production zone by introduction into the steel conduit of the acid corrosion inhibitor composition of this invention.

The fluid which is contemplated for use in one aspect of the present invention for treatment of a subterranean well for enhancement of production will be aqueous based; that is, it will be formed using sea water available at the well location, a brine, tap water or similar fluid. The amount of fluid used for the treatment will vary, of course, from well to well, and will be based upon the par- ticular application at hand, and the amount thereof is not particularly critical to the method of the present invention. It will be appreciated that one of ordinary skill in the art of corrosion inhibition will be able to adapt the teachings of this invention to applications outside the realm of oil and gas recovery, such as the area of chemical processing, with only routine experimentation.

The expected treatment fluid in an oil production environment is expected to have as a primary additive an acidic injection medium, which may be any compatible acid, including but not limited to hydrochloric acid, hydrofluoric acid, other mineral acids, other halogen acids, and mixtures thereof. The fluid with the acid injection medium therein should have a pH of no greater than about 6.9. Acidizing fluids can have pH of less than 1 when mixed with produced fluids which may have a pH as high as 6.9.

The treatment fluid also contemplates incorporation of other acid corro- sion inhibitors, which typically will be provided in treatment concentrations of from about 1,000 ppm, based upon the weight of the entire treatment fluid to about 60,000 ppm of such weight. Most often, the total amount of corrosion inhibitors will range from about 1,000 to 30,000 ppm. The treatment level of the acid corrosion inhibitor will depend upon the particular physical characteristics of the well, the high alloy steel conduit, temperature and pressure considerations, the selected acidic injection medium, and the like.

In particular, it will be appreciated that the treatment level of the acid cor- rosion inhibitor of this invention will vary depending upon a wide variety of com- plex, interrelated parameters including, but not limited to, the particular physical characteristics of the system or well, the nature of the steel, temperature and pressure considerations, the acid and strength thereof in the system, and the like. Nevertheless, to give a sense of the typical proportions that might be used, non-limiting effective amounts of the corrosion inhibitor ranges from about 0.1 to about 10 gpt (gallons of inhibitor per thousand gallons of acid), depending on the acid strength. (This could also be expressed as 0.1 to 10 Ipt-liters per thousand liters of acid. ) The treatment level also depends upon the temperature and exposure time, with the following being non-limiting, representative examples: 1-3 gpt (1-3 Ipt) at ambient to 200°F (93°C) in 15% HCI and 6 hours exposure; 1-5 gpt (1-5 Ipt) at ambient to 200°F (93°C) in 28% HCI and 6 hours exposure; 3-10 gpt (3-10 Ipt) at 200 to 250° (93 to 121°C) in 15% HCI and 6 hours exposure; and 5-15 gpt (5-15 Ipt) at 200 to 250° (93 to 121°C) in 28% HCI and 6 hours exposure.

Twenty (20) gpt (20 Ipt) of corrosion inhibitor intermediate is commonly used in acid systems at or above 250°F (121°C) in one non-limiting embodiment. Pro- portions of 2-4 gpt (2-4 Ipt) may be suitable in some environments (N-80 steel test coupons) at up to 270°F (132°C). In another non-limiting embodiment of

the invention, the amount of corrosion inhibitor based on the liquid being inhibited ranges from about 0.1 to about 22 volume %, preferably from about 3 to about 6 volume%. It will be appreciated that these treatment levels will be different for other mineral acids and other halogen acids.

The invention will be described further in the following illustrative Exam- ples, which are non-limiting and serve only to further illuminate the invention.

TABLE I Corrosion Inhibitor Comparison Ib/ft (kg/m) Example Blend Solvent Test 1 Test 2 Test 3 Test 4 Comp. 1 TFT MeOH 0.222 0.099 0.264 0.610 (1.08) (0.483) (1.29) (2.98) Comp. 2 Formula A MeOH 0.277 0.164 0.150 0.553 (1.35) (0.801) (0.732) (2.70) Inv. 3 Formula B Formic Acid 0.056 0.050 0.032 0.120 (0.273) (0.244) (0.156) (0.586) Inv. 4 Formula C Formic Acid 0.105 0.053 0.025 0.168 (0.513) (0.259) (0.122) (0.820) Notes to Table l : All tests were conducted on N-80 tubing steel for the conditions described in the Tests using 2.0% inhibitor. The corrosion base material is that described in U. S. Pat. No. 3,077, 454, discussed previously.

Test 1 : 15% HCI, 6 hrs. at 2000 psi (1.4 x 104 kPa) (nitrogen) or 3000 psi (2.1 x 104 kPa) (kerosene) 300°F (149°C).<BR> <P>Test 2: 15% HCI, 2 hrs. at 2000 psi (1.4 x 104 kPa) (nitrogen) or 3000 psi (2.1 x<BR> 104 kPa) (kerosene) 325°F (163°C).<BR> <P>Test 3: 28% HCI, 6 hrs. at 2000 psi (1. 4 x 104 kPa) (nitrogen) or 3000 psi (2.1 x<BR> 104 kPa) (kerosene) 250°F (121°C).<BR> <P>Test 4: 28% HCI, 6 hrs. at 2000 psi (1.4 x 104 kPa) (nitrogen) or 3000 psi (2.1 x 104 kPa) (kerosene) 275°F (135°C).

TFT is a conventional acetylenic alcohol containing inhibitor corrosion inhibitor of known performance containing about 30 vol. % methanol solvent.

Formula A and Formula B are identical except that formula A use methanol as solvent and is offered as a comparison to formula B which is an example of the invention using formic acid solvent.

It will be appreciated that the inventive corrosion inhibitor of Example 3 gives noticeably improved corrosion inhibition as contrasted with the compara- tive Examples 1 and 2. For instance, the 0.056 Ib/ft2 (0.273 kg/m2) result for Test 1 of Example 3 is about five times better than the 0.222 Ib/ft2 (1. 08 kg/m2) of Example 1 or the 0.277 Ib/ft2 (1.35 kg/m2) of Example 2. Similar comparisons can be made for the other Tests. The inventive corrosion inhibitor is consistently better for all Tests. Formula C of Inventive Example 4 was similar to Formula B of Inventive Example 3 except that a surfactant was not used.

With the exception of Test 1, the results are comparable to Example 3. It is surprising and unexpected that the addition of an acid, such as formic acid, and ester derivatives thereof, would reduce corrosion in the HCI environment of these Examples.

EXAMPLE 5 The corrosion loss of corrosion inhibitors of Inventive Example 3 and Comparative Example 1 are compared in the Figure chart as a function of tem- perature. It should be remembered that the corrosion loss scale of the y-axis is a logarithmic scale. This data, presented below in Table II, was collected using N-80 tubing steel in 15% HCI. It may be seen that the corrosion inhibitor of Inventive Example 3 far outperforms that of Comparative Example 1.

TABLE II Comparison of Corrosion Inhibitors of Inventive Example 3 with Comparative Example 1 on N-80 in 15% HCI Inventive Example 3 Comparative Example 1 Temperature Corrosion Loss Corrosion Loss °F (°C) Ibst'kg/m Ibs/ft2 kg/m' 200 (93) 0. 006 0. 029 0. 007 0. 034 225 (107) 0. 013 0. 063 0. 023 0. 112 250 (121) 0. 023 0. 112 0. 065 0. 317 275 (135) 0. 039 0. 190 0. 140 0. 683 300 (149) 0. 061 0. 298 0. 373 1. 820 325 (163) 0. 037 0. 181 0. 187 0. 913

Many modifications may be made in the present invention without departing from the spirit and scope thereof that are defined only by the appended claims. For example, certain components per se, or combinations of components thereof other than those specifically set out herein may be found by one of routine skill in the art to be particularly advantageous, e. g. different combinations of corrosion inhibitor bases with certain solvents and/or different combinations of surfactants. Additionally, certain proportions of reactants may produce corrosion inhibitors having particular efficacy.