Title:
A CRACK RESISTANT LAYER WITH GOOD BEAM FATIGUE PROPERTIES MADE FROM AN EMULSION OF A POLYMER MODIFIED BITUMINOUS BINDER AND METHOD OF SELECTING SAME
Document Type and Number:
WIPO Patent Application WO/2010/099471
Kind Code:
A2
Abstract:
A method of selecting a crack resistant layer to be applied to an existing surface, the method comprising the steps of: selecting at least one emulsified bituminous binder to examine, where the emulsified bituminous binder comprises bitumen, one or more emulsifier, and one or more polymers, where the one or more polymers, the one or more emulsifier, or both include a sufficient amount of conjugated diene such that at least 2.5% of the weight of the emulsified bituminous binder residuum comprises conjugated diene, preferably at least 3.0%, more preferably at least 3.5%, and most preferably 4.0%; forming at least one bituminous mixture comprising the emulsified bituminous binder and an aggregate; testing each bituminous mixture for fatigue properties; and selecting a bituminous binder for use in the crack resistant layer. The method may further comprise the steps of testing the bituminous mixture for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and fracture energy properties, and/or testing the emulsified bituminous binder residuum for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and bituminous binder residuum fracture energy properties.

Inventors:
BARNAT, James J. (10527 South 92nd East Circle, Tulsa, OK, 74133, US)
VOPAT, Vince (5009 East 86th Place, Tulsa, OK, 74137, US)
Application Number:
US2010/025632
Publication Date:
September 02, 2010
Filing Date:
February 26, 2010
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
ROAD SCIENCE, L.L.C. (6502 South Yale Avenue, Tulsa, OK, 74136, US)
BARNAT, James J. (10527 South 92nd East Circle, Tulsa, OK, 74133, US)
VOPAT, Vince (5009 East 86th Place, Tulsa, OK, 74137, US)
International Classes:
E01C7/35; C09D109/00; C09D195/00; E01C7/00; E01C7/18
Domestic Patent References:
WO2007051703A12007-05-10
WO2005100479A12005-10-27
Foreign References:
EP0561472A11993-09-22
US20030149140A12003-08-07
US20040106705A12004-06-03
Attorney, Agent or Firm:
WILKINSON, Cassandra L. (Head, Johnson & Kachigian228 West 17th Plac, Tulsa OK, 74119, US)
Download PDF:
Claims:
WHAT IS CLAIMED IS: 1. A method of selecting a crack resistant layer to be applied to an existing surface, the method comprising the steps of: selecting at least one emulsified bituminous binder to examine, where the emulsified bituminous binder comprises bitumen, one or more emulsifier, and one or more polymers, where the one or more polymers, the one or more emulsifier, or both include a sufficient amount of conjugated diene such that at least 2.5% of the weight of emulsified bituminous binder residuum comprises conjugated diene; forming at least one bituminous mixture comprising the emulsified bituminous binder and an aggregate; testing each bituminous mixture for fatigue properties; and selecting a bituminous binder for use in the crack resistant layer.

2. The method of Claim 1 where at least 3.0% of the weight of the emulsified bituminous binder residuum comprises conjugated diene.

3. The method of Claim 1 where at least 3.5% of the weight of the emulsified bituminous binder residuum comprises conjugated diene.

4. The method of Claim 1 where at least 4.0% of the weight of the emulsified bituminous binder comprises residuum conjugated diene.

5. The method of Claim 1 where at least part of the conjugated diene included in the emulsified bituminous binder comes from latex.

6. The method of Claim 5 where the emulsified bituminous binder is formed by emulsifying a bituminous binder, and where the latex is added to the bituminous binder before emulsifϊcation, during emulsification, after emulsification, or combinations thereof.

7. The method of Claim 1 where selecting the emulsified bituminous binder for use in the crack resistant layer is based on mixture fatigue properties.

8. The method of Claim 7 where the testing of each bituminous mixture for fatigue properties comprises subjecting each bituminous mixture to a flexural beam fatigue test performed at 2,000 microstrains, 10 Hz, and 150C per ASTM D 7460-08.

9. The method of Claim 8 the flexural beam fatigue test results in at least 5,000 cycles to failure.

10. The method of Claim 8 the flexural beam fatigue test results in at least 10,000 cycles to failure.

11. The method of Claim 8 the flexural beam fatigue test results in at least 15,000 cycles to failure.

12. The method of Claim 1 further comprising the steps of testing the emulsified bituminous mixture for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and fracture energy properties.

13. The method of Claim 12 where the testing of the emulsified bituminous mixture for fracture energy comprises subjecting the emulsified bituminous mixture to a Semi-Circular Bend Test or a Disk-Shaped Compact Tension Test.

14. The method of Claim 13 where the fracture energy test is the Disk-Shaped Compact Tension Test and is performed at a temperature of - 100C and a rate of loading of 1.0 mm/min, in accordance with ASTM D 7313-07.

15. The method of Claim 14 where the fracture energy test results in a mixture fracture energy of greater than 600 J/m2.

16. The method of Claim 14 where the fracture energy test results in a mixture fracture energy of greater than 700 J/m2.

17. The method of Claim 14 where the fracture energy test results in a mixture fracture energy of greater than 800 J/m2.

18. The method of Claim 1 further comprising the steps of testing the emulsified bituminous binder residuum for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and bituminous binder residuum fracture energy properties.

19. The method of Claim 18 where the testing of the bituminous binder residuum for fracture energy comprises testing a single edge notch beam tested at 0.1 mm/sec at -3O0C, calculated by ASTM D 5045-99 where the dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm where the samples were conditioned at test temperature for 18 to 20 hours before testing.

20. The method of Claim 19 where the fracture energy test results in a bituminous binder residuum fracture energy of greater than 40 J/m2 where the samples were conditioned at test temperature for 18 to 20 hours before testing.

21. The method of Claim 19 where the fracture energy test results in a bituminous binder residuum fracture energy of greater than 50 J/m2 where the samples were conditioned at test temperature for 18 to 20 hours before testing.

22. The method of Claim 19 where the fracture energy test results in a bituminous binder residuum fracture energy of greater than 60 J/m2 where the samples were conditioned at test temperature for 18 to 20 hours before testing.

23. The method of Claim 12 further comprising the steps of testing the bituminous binder residuum for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties, mixture fracture energy properties, and bituminous binder fracture energy properties.

24. The method of Claim 1 further comprising the steps of testing the bituminous mixture for permeability and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and permeability.

25. The method of Claim 24 where the bituminous mixture is tested for permeability in accordance with ASTM D 3637.

26. The method of Claim 25 where the permeability is greater than 8 cm2.

27. The method of Claim 1 where the bituminous mixture has a Hveem stability of greater than 21 per ASTM D 1560.

28. The method of Claim 1 where the bituminous mixture has greater than 1% air voids.

29. The method of Claim 1 where the emulsified bituminous binder further comprises additives.

30. The method of Claim 29 where the additives comprise cross-linking agents, accelerators, extenders, fluxing agents, or combinations thereof.

31. The method of Claim 1 where the aggregate comprises a hard and inflexible mineral aggregate, a hard and inflexible man-made aggregate, or a combination thereof.

32. The method of Claim 1 where the bituminous mixture further comprises recycled materials.

33. The method of Claim 32 where the recycled materials are reclaimed asphalt pavement, glass, ground rubber tires, ceramics, metals, or mixtures thereof.

34. A crack resistant layer to be applied to an existing surface, where the layer comprises: an aggregate; and an emulsified bituminous binder, wherein the bituminous binder is comprised of bitumen and one or more polymers, where the one or more polymers include a sufficient amount of conjugated diene such that at least 2.5% of the weight of emulsified bituminous binder residuum comprises conjugated diene, and where the bituminous binder is emulsified to form an emulsified bituminous binder; where the emulsified bituminous binder and the aggregate are mixed and form a bituminous mixture wherein the mixture has a flexural beam fatigue resistance of at least 5,000 cycles at 2000 microstrains at 10 Hz when tested 150C per ASTM D 7460-08.

35. The crack resistant layer of Claim 34 where at least 3.0% of the weight of the emulsified bituminous binder residuum comprises conjugated diene.

36. The crack resistant layer of Claim 34 where at least 3.5% of the weight of the emulsified bituminous binder residuum comprises conjugated diene.

37. The crack resistant layer of Claim 34 where at least 4.0% of the weight of the emulsified bituminous binder residuum comprises conjugated diene.

38. The crack resistant layer of Claim 34 where at least part of the conjugated diene comprising the bituminous binder residuum comes from latex.

39. The method of Claim 38 where the latex is added to the bituminous binder before emulsification, during emulsification, after emulsification, or combinations thereof.

40. The crack resistant layer of Claim 34 where the layer exhibits beam fatigue properties of at least 10,000 cycles to failure when subjected to a flexural beam fatigue test at 2000 microstrains at 10 Hz when tested 150C per ASTM D 7460-08.

41. The crack resistant layer of Claim 34 where the layer exhibits beam fatigue properties of at least 15,000 cycles to failure when subjected to a flexural beam fatigue test at 2000 microstrain at 10 Hz when tested 150C per ASTM D 7460-08.

42. The crack resistant layer of Claim 34 where the bituminous mixture exhibits desirable fracture energy properties when subjected to testing for such fracture energy properties.

43. The crack resistant layer of Claim 42 where the bituminous mixture is tested for fracture energy properties with a Semi-Circular Bend Test or a Disk-Shaped Compact Tension Test.

44. The crack resistant layer of Claim 43 where the fracture energy test is performed at a temperature of -1O0C and a rate of loading of 1.0 mm/min., in accordance with ASTM D 7313-07.

45. The crack resistant layer of Claim 44 where the bituminous mixture's fracture energy properties are desirable if the fracture energy test results in a mixture fracture energy of greater than 600 J/m2.

46. The crack resistant layer of Claim 44 where the bituminous mixture's fracture energy properties are desirable if the fracture energy test results in a mixture fracture energy of greater than 700 J/m2.

47. The crack resistant layer of Claim 44 where the bituminous mixture's fracture energy properties are desirable if the fracture energy test results in a mixture fracture energy of greater than 800 J/m2.

48. The crack resistant layer of Claim 34 where the emulsified bituminous binder residuum has a fracture energy of greater than 40 J/m2 when a single edge notch beam is tested at 0.1 mm/sec, at -3O0C, calculated by ASTM D 5045-99 where the dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm where the samples were conditioned at test temperature for 18 to 20 hours before testing.

49. The crack resistant layer of Claim 34 where the emulsified bituminous binder residuum has a fracture energy of greater than 50 J/m2 when a single edge notch beam is tested at 0.1 mm/sec, at -300C, calculated by ASTM D 5045-99 where the preferred dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm where the samples were conditioned at test temperature for 18 to 20 hours before testing.

50. The crack resistant layer of Claim 34 where the emulsified bituminous binder residuum has a fracture energy of greater than 60 J/m2 when a single edge notch beam is tested at 0.1 mm/sec, at -300C, calculated by ASTM D 5045-99 where the preferred dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm where the samples were conditioned at test temperature for 18 to 20 hours before testing.

51. The crack resistant layer of Claim 34 where the bituminous mixture's permeability is greater than 8 cm2 when tested in accordance with ASTM D 3637.

52. The crack resistant layer of Claim 34 where the bituminous mixture has a Hveen stability of greater than 21 per ASTM D 1560.

53. The crack resistant layer of Claim 34 where the bituminous mixture has greater than 1% air voids.

54. The crack resistant layer of Claim 34 further comprising additives.

55. The crack resistant layer of Claim 54 where the additives comprise cross-linking agents, accelerators, extenders, fluxing agents, or combinations thereof.

56. The crack resistant layer of Claim 34 where the aggregate comprises a hard and inflexible mineral aggregate, a hard and inflexible man-made aggregate, or a combination thereof.

57. The crack resistant layer of Claim 34 where the mixture further comprises recycled materials.

58. The crack resistant layer of Claim 57 where the recycled materials are reclaimed asphalt pavement, glass, ground rubber tires, ceramics, metals, or mixtures thereof.

Description:
A CRACK RESISTANT LAYER

WITH GOOD BEAM FATIGUE PROPERTIES MADE FROM AN

EMULSION OF A POLYMER MODIFIED BITUMINOUS BINDER

AND METHOD OF SELECTING SAME

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application is a continuation-in-part of U.S. patent application Serial No. 12/395,318 titled A Crack Resistance Layer With Good Beam Fatigue Properties and Method of Selecting Same filed February 27, 2009.

BACKGROUND

1. Field of the Invention.

[0002] The present invention relates to a crack resistant layer with good beam fatigue properties and a method of selecting same. More particularly, the present invention relates to a bituminous binder with a critical amount of conjugated diene, which allows for enhanced fatigue resistant properties in a crack resistant layer.

2. Description of the Related Art.

[0003] When pavements deteriorate, they may be overlaid with hot mix asphalt (HMA) to repair them. When designing an overlay, the rate of crack propagation through the overlay, the rate of deterioration of the reflective crack, and the amount of water that can infiltrate through the cracks must be considered. One disadvantage with such HMA overlays is that cracks in the old pavement reflect through the new overlay. To relieve this reflective cracking, thicker overlays may be placed. Another disadvantage with these overlays is that they typically have a low strain tolerance and a low resistance to reflective cracking.

[0004] To improve traditional HMA overlays, asphalt binders that display the ability to undergo creep or stress relaxation at low temperatures may be used. Such bituminous binders minimize the potential for thermal and reflective cracking. However, the disadvantage with such bituminous binders is that they are highly ductile and have a low shear modulus at high temperatures, and thus roads created with them tend to rut. Asphalts with high shear modulus that resist rutting at high temperatures may also be used. However, such binders tend to be brittle at low temperatures, and thus roads created with them tend to crack. Typical asphalt bituminous binders formulated for pavement applications usually display either high shear modulus at high temperatures or high ductilities at low temperatures but not both.

[0005] A typical highway HMA surface mixture has about 3% to 5% air voids and a fatigue life of only about 500 cycles when tested at 15 0 C with a strain amplitude of 2,000 microstrains and frequency of 10 Hz using a 4-point bending beam apparatus. The best surface mixture with about 3% to 5% air voids has a fatigue life of only about 2,000 to 5,000 cycles when tested at 15 0 C with a strain amplitude of 2,000 microstrains and frequency of 10 Hz using a 4-point bending beam apparatus. Other mixtures with air voids greater than 5% to 7% may have a fatigue life of only about 500 to 1,500 cycles when tested at 15 0 C with a strain amplitude of 2,000 microstrains and frequency of 10 Hz using a 4-point bending beam apparatus.

[0006] Blankenship et al, US Patent No. 6,830,408, which is incorporated herein by reference, attempts to solve the foregoing problems through the use of an interlayer that is placed on the cracked road underneath the overlay. The interlayer includes a mixture of aggregate and bituminous binder, preferably polymer modified asphalt, and is used to delay or stop the occurrence of cracking, control crack severity, reduce overlay thickness, and enhance waterproofing capabilities. The interlayer is highly strain tolerant and substantially impermeable.

[0007] The bituminous binder used in the interlayer of the '408 patent includes bitumen, one or more polymers, and, optionally, a cross-linking agent to effect vulcanization of the polymer in the bitumen. Limitations on the characteristics of the bituminous binder and interlayer are set forth in the '408 patent. In particular, the '408 patent specifies that the percentage of air voids in the interlayer must be between 2.0% and 4.0%. This produces a flexural beam fatigue performance of at least 100,000 cycles to failure.

[0008] The problem with such interlayers is that, in order to get such a fatigue life and retard the progression of reflective cracks in the pavement, these interlayers sacrifice a degree of their load bearing capacity, as measured in the Hveem stabilometer, and typically have Hveem stabilities of about 18-21. In order to compensate for their low stability, these interlayers are placed below the top layers of a pavement structure so that they are not exposed to direct traffic loads. Thicker top layers help to improve the total structural stability but are costly. Still further, the top layers of the pavement structure cannot completely compensate for the low load bearing capacity of the interlayer.

[0009] Blankenship et al, US Application No. 10/631,149, which is incorporated herein by reference, attempts to solve this problem through the use of a highly strain tolerant, substantially moisture impermeable, hot mix reflective crack relief interlayer. The interlayer includes a polymer modified bituminous binder mixed with a dense fine aggregate mixture that is made primarily from manufactured sand. This results in increased stability and improved load bearing capacity. Limitations on the characteristics of the bituminous binder and interlayer are set forth in the '149 application. In particular, the '149 application specifies that the percentage of air voids in the interlayer must be between 1.0% and 5.0%, preferably 2.0% to 4.0%, and most preferably about 3.0%. This produces a flexural beam fatigue performance of at least 50,000 cycles to failure, preferably 80,000 and most preferably 100,000.

[0010] The problem with this interlayer is that it is impermeable. When such an interlayer is placed on Portland Cement Concrete (PCC) or another paved surface, the interlayer has the potential to trap vapor underneath it. As changes occur in climatic and environmental conditions, this causes the PCC to release moisture or vent. The interlayer then rises, creating a blister. This causes overlays on top of this interlayer also to rise and blister.

[0011] Blankenship et al., US Patent Number 7,479,185, which is incorporated herein by reference, attempts to solve this problem through the use of a layer that remains substantially moisture impervious and retains its ability to retard the formation of reflective cracks while having increased vapor permeability. This layer may be an interlayer, but also may be a base layer or an overlay.

[0012] Limitations on the characteristics of the bituminous binder and layer are set forth in the ' 185 patent. In particular, the '185 patent specifies that the percentage of air voids in the layer must be at least 3.0%, preferably at least 4.0%, more preferably at least 4.5%, even more preferably at least 5.0%, and most preferably at least 7.0%. This produces a flexural beam fatigue performance of at least 5,000 cycles to failure, preferably at least 35,000 cycles to failure, and most preferably at least 100,000 cycles to failure. The '185 patent notes that there is typically an inverse relationship between the air voids in a bituminous mixture and fatigue resistance of that mixture. However, the bituminous mixture of the '185 patent may be made by creating a very large amount of air voids in an aggregate structure and then filling a large portion of those voids with bitumen. The total amount of air voids is critical. Too many air voids will limit fatigue resistance and too few air voids will compromise permeability.

[0013] The problem with the ' 185 layer is the narrow operating window. The perfect aggregate structure is required to produce the skeletal structure that meets the requirements of fatigue resistance, strength, and permeability. Local aggregates may not be suitable requiring more costly aggregate sources to be used. Tight tolerances at the hot mix plants creates off- specification product that impacts costs. Additionally, a very high asphalt content is required, which increases costs dramatically.

[0014] The current art uses mixture volumetric properties and film thickness to achieve acceptable beam fatigue properties. The '408 patent to Blankenship requires air voids in a tight and low range, extremely high binder film thicknesses, and extremely low DP's (dust to effective binder ratio). The '149 application greatly limits aggregate properties to effect acceptable beam fatigue properties. The '185 patent allows for higher air void content but also requires a higher binder film thickness. Hence, the current art is void of any binder property that affects beam fatigue properties.

[0015] In each of the foregoing, polymer is used in the bituminous binder. Methods of preparing polymer modified bitumen is described in Maldonado et al., US Patent No. 4,242,246, and Maldonado et al., US Patent No. 4,330,449, both of which are incorporated herein by reference.

[0016] As is known in the art and used herein, emulsification of asphalt refers to forming an emulsion of asphalt and water. Emulsification basically requires that the asphalt and any desired performance-enhancing additives be combined with an emulsifying agent in an emulsification mill along with about 20 to 70 percent by weight of water. Asphalt emulsions are desirable in many applications because an emulsion may be applied at lower temperatures than hot-mix asphalts because the water acts as a carrier for the asphalt particles. For example, hot-mix asphalts, which are mixes of asphalt, aggregate, and a single polymer, are commonly applied at a temperature of 140° C to 232° C to achieve the requisite plasticity for application. In comparison, an asphalt emulsion typically may be applied at 54° C to 77° C to achieve the same working characteristics. Once applied, the water evaporates, leaving the asphalt. Also, emulsified asphalt products generally do not use or release the environmentally-harmful volatile organic compounds normally associated with asphalts diluted with light carrier solvents such as diesel fuel, naphtha, and the like.

[0017] Notwithstanding the foregoing, there remains a need for a crack resistant layer with low air voids and good beam fatigue properties that does not suffer from the drawbacks of the layers of the Blankenship patent and applications. Accordingly, it would be desirable to provide an emulsion of a bituminous binder for a crack resistant layer with greater than 1% air voids and greater than 5,000 cycles to failure, that is stable, that does not require special aggregate structure or excessive asphalt content, and that may be used as a base layer, interlayer, or overlay.

SUMMARY OF THE INVENTION

[0018] In general, in a first aspect, the present invention relates to a method of selecting a crack resistant layer to be applied to an existing surface, the method comprising the steps of: selecting at least one emulsified bituminous binder to examine, where the emulsified bituminous binder comprises bitumen, one or more emulsifier, and one or more polymers, where the one or more polymers, the one or more emulsifier, or both include a sufficient amount of conjugated diene such that at least 2.5% of the bituminous binder residuum weight comprises conjugated diene, preferably at least 3.0%, more preferably at least 3.5%, and most preferably 4.0%; forming at least one bituminous mixture comprising the emulsified bituminous binder and an aggregate; testing each bituminous mixture for fatigue properties; and selecting a bituminous binder for use in the crack resistant layer. At least part of the conjugated diene included in the emulsified bituminous binder may come from latex, which may be added before emulsification, during emulsification, after emulsification, or combinations thereof. The testing of each bituminous mixture for fatigue properties may comprise subjecting each bituminous mixture to a flexural beam fatigue test performed at 2,000 microstrains, 10 Hz, and 15 0 C per ASTM D 7460-08. Such a flexural beam fatigue test may result in at least 5,000 cycles to failure, preferably at least 10,000 cycles to failure, and most preferably at least 15,000 cycles to failure.

[0019] The method may further comprise the steps of testing the bituminous mixture for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and fracture energy properties. The testing of the bituminous mixture for fracture energy may comprise subjecting the bituminous mixture to a Semi-Circular Bend Test or a Disk-Shaped Compact Tension Test. The fracture energy test may be the Disk-Shaped Compact Tension Test performed at a temperature of -1O 0 C and a rate of loading of 1.0 mm/min, in accordance with ASTM D 7313-07, and may result in a mixture fracture energy of greater than 600 J/m 2 , preferably greater than 700 J/m 2 , and most preferably greater than 800 J/m 2 .

[0020] The method may further comprise the steps of testing the emulsified bituminous binder residuum for fracture energy and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and bituminous binder fracture energy properties. Testing of the emulsified bituminous binder residuum for fracture energy may comprise testing a single edge notch beam tested at 0.1 mm/sec at -3O 0 C, calculated by ASTM D 5045-99 where the dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm (all dimensions + or - 1%), which may result in a bituminous binder fracture energy of greater than 40 J/m 2 , preferably greater than 50 J/m 2 , and most preferably greater than 60 J/m 2 . The preferred testing device is an RSA III Dynamic Mechanical Analyzer from TA Instruments, Inc of New Castle, DE.

[0021] The method may further comprise the steps of testing the bituminous mixture for permeability and selecting the emulsified bituminous binder for use in the crack resistant layer based on fatigue properties and permeability. The bituminous mixture may be tested for permeability in accordance with ASTM D 3637, which may result in permeability greater than 8 cm 2 .

[0022] The bituminous mixture may have a Hveem stability of greater than 21 per ASTM D 1560 and may have greater than 1% air voids. The emulsified bituminous binder may further comprise additives, such as cross-linking agents, accelerators, extenders, fluxing agents, or combinations thereof. The aggregate may comprise a hard and inflexible mineral aggregate, a hard and inflexible man-made aggregate, or a combination thereof. The bituminous mixture may further comprise recycled materials, such as reclaimed asphalt pavement, glass, ground rubber tires, ceramics, metals, or mixtures thereof. [0023] In a second aspect, the invention relates to a crack resistant layer having the properties set forth above.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] The present invention relates to an emulsion of a bituminous binder for use in a crack resistant layer. The layer may be used to resurface a distressed pavement surface, and may be used as a base layer, an interlayer, or an overlay. Use of such a layer is described in the Description of Related Art section above and in the Blankenship patents and application. The bituminous binder is such that the crack resistant layer has good beam fatigue properties. A method of selecting such a bituminous binder is also provided herein.

[0025] The layer is formed from a bituminous mixture, which is comprised of an emulsion of a bituminous binder and an aggregate. The bituminous binder includes bitumen, one or more polymers, and, optionally, other additives, including but not limited to cross- linking, accelerators, extenders, fluxing agents, and/or other similarly appropriate additives suitable for use in bituminous binders.

[0026] The polymer used in the bituminous binder may be any elastomer, plastomer, or other polymer suitable for use in bitumen, including but not limited to those described in the Maldonado and Blankenship patents and application, and containing at least a critical amount of conjugated diene. The critical amount of conjugated diene is at least 2.5%, preferably at least 3.0%, more preferably at least 3.5%, and most preferably 4.0%. Such high amounts of conjugated diene have not previously been used in similar layers because of the high cost of such a relatively large polymer content, the difficulty to process, the difficulty to handle the bituminous mixture, and the unknown favorable attributes of high levels of conjugated diene. Surprisingly, it has been found that increasing the amount of conjugated diene above the critical amount produces a layer with improved fatigue resistance of any asphalt-aggregate mixture. Thus, the life of the layer is increased, making the layer cost effective despite the large polymer content. [0027] Emulsifϊcation materials used with the polymer modified bituminous binder are those traditionally known by those skilled in the art, such as cationic emulsifying agents, anionic emulsifying agents, nonionic emulsifying agents, amphoteric emulsifying agents, zwitterionic emulsifying agents, and combinations thereof. Typical cationic emulsified polymer modified bituminous binders can be made using known emulsifying agents such as primary amines, diamines, ethoxylated amines, propoxylated amines, imidazolene amines, and the like. Typical anionic emulsified polymer modified bituminous binders can be made using emulsifying agents known by those skilled in the art, such as salts produced from lignin-based, Vinsol-based, or tall oil-based raw materials. Similarly, nonionic emulsified polymer modified bituminous binders can be made using known nonionic emulsifying agents such as oxylated nonolphenols. Typical zwitterionic emulsifying agents include, but are not limited to, families like Sulfobetanes and Sultanes of the general formula RN (CH3)2(CH2) x Sθ3. It should be understood and appreciated that this is not an exhaustive list of emulsifying agents that can be used. Rather, any emulsifying agent that is known in the art capable of emulsifying the polymer modified bituminous binder of the present invention can be used.

[0028] Satisfactory emulsified embodiments of the present invention include from about 20 percent to about 80 percent by weight polymer modified bituminous binder with about 80 percent to about 20 percent by weight water, emulsifying agent, and emulsion additives. For special applications, such as thin film resurfacing, a greater or lesser amount of water may be used. Generally, the amount of water used is that amount which will give the emulsified mixture the desired flow characteristics to allow proper placement and curing of the emulsion. Quantity and type of emulsifying agent typically is dictated by the ultimate use of the emulsion. Tests indicate that the quantity and type of emulsifying agents suitable for use with the present invention are consistent with existing asphalt and asphalt-polymer emulsions known in the art.

[0029] The aggregate may be hard and inflexible mineral aggregates, such as sand, stone, lime, Portland cement, kiln dust, or mixtures thereof; man made hard and inflexible aggregates, such as wet bottom boiler slag, blast furnace slag, or mixtures thereof; or any other appropriate aggregate. The structure of the aggregate may be any of those described in the Blankenship patent and applications, or may be any other appropriate structure. The aggregate need not include manufactured sand, as required by the ' 149 Blankenship application.

[0030] Recycled materials, such as reclaimed asphalt pavement, glass, ground rubber tires, ceramics, metals, or mixtures thereof, or any other appropriate recycled material may be incorporated into the mixture. Any conjugated diene from a recycled vulcanizate is not considered as part of the bituminous binder and is not included in the critical amount of conjugated diene as part of this invention.

[0031] The bituminous mixture formed from the appropriate amount of conjugated diene bituminous binder and the aggregate may meet any local standards for traditional bituminous mixture properties such as VMA, VFA, density, dust to binder ratio, and the like. However, the Hveem stability per ASTM D 1560 should be greater than 21 and the bituminous mixture should have greater than 1% air voids. The bituminous mixture with suitable crack resistance will have a beam fatigue of greater than 5,000 cycles to failure, more preferably at least 10,000 cycles to failure, and most preferably at least 15,000 cycles to failure; a mixture fracture energy of greater than 600 J/m 2 , more preferably greater than about 700 J/m 2 , and most preferably greater than about 800 J/m 2 ; and a bituminous binder fracture energy of greater than 40 J/m 2 , more preferably greater than about 50 J/m 2 , and most preferably greater than about 60 J/m 2 . [0032] Generally, the method of selecting the bituminous binder for use in the crack resistant layer involves mixing an emulsion of a bituminous binder and an aggregate to form a bituminous mixture, forming a specimen layer from the bituminous mixture, and testing the specimen layer to determine beam fatigue. If the beam fatigue is sufficient, the bituminous binder is appropriate for use in the crack resistant layer. If not, another bituminous binder must be used with higher conjugated diene content, and the process must begin again. Additionally or alternately, the bituminous mixture itself may be tested for fracture energy. Additionally or alternately, the bituminous binder may be tested for fracture energy. In both instances, if the fracture energy is sufficient, the bituminous binder is appropriate for use in the crack resistant layer. If not, another bituminous binder must be used and the process must begin again. The bituminous mixture may also additionally or alternately be tested for permeability, where the bituminous binder is appropriate only if the permeability is sufficient, and if not, another must be selected.

[0033] To produce the emulsified polymer modified bituminous binder, the binder, polymer, and/or any additives are first mixed to form a polymer modified bituminous binder, which is heated to a predetermined temperature that will produce acceptable flow characteristics. Once the polymer modified bituminous binder is heated to the predetermined temperature, the polymer modified bituminous binder is introduced into an emulsification mill with the emulsifying agents, emulsion additives, and/or water. Introducing the heated polymer modified bituminous binder into the emulsification mill allows the final emulsion temperature to be maintained within acceptable limits. Generally, acceptable limits for the final combined temperature of the emulsified polymer modified bituminous binder are less than about 100 0 C so as to prevent flash boiling of the water. It should be understood and appreciated that emulsification temperatures can exceed the boiling point of the aqueous phase with pressure and heat exchange equipment. The mill operates to slice the polymer- binder mix finely and mix it with the water, emulsifier, and emulsion additives to form an emulsion. The emulsifying agent acts to stabilize the resulting emulsion so as to prevent agglomeration of the asphalt prior to placement. The emulsion additives described herein for use in emulsification can be any additive for providing the emulsified polymer modified bituminous binder with predetermined properties. Examples of additive include, but are not limited to, sulfur containing compounds, thickeners, or other rheology modifiers, tackifiers, flow improvers, pH adjusting chemicals, stabilizers and the like.

[0034] Emulsified polymers, or more technically correct polymer dispersions like latex products, are also suited to provide sufficient amounts of conjugated diene to the bituminous binder. These polymer dispersions may be premixed with the binder, co-milled during the emulsification process, post added to the bituminous emulsion, added directly to the mixture, and combinations thereof. Latex products like natural rubber, SBR (styrene- butadiene rubber), Neoprene (chloroisoprene), and the like are suitable and within the scope of the invention.

[0035] Combinations of polymer sources like modified asphalt and latex products, various points of addition like pre-emulsification, co-emulsification, post emulsification, and combinations thereof are also suitable so long as the sum total of the conjugated diene content is sufficient to create a crack resistant layer.

[0036] The bituminous mixture produced from the emulsion of a bituminous binder and aggregate should meet the criteria set forth above, and should be mixed in sufficient quantities that the bituminous mixture meets the criteria set forth above. In particular, the emulsion of bituminous binder should include a polymer comprising at least 2.5%, preferably at least 3.0%, more preferably at least 3.5%, and most preferably at least 4.0% conjugated diene based on the weight of the polymer modified bitumen. Furthermore, the emulsion of bituminous binder should be formed in such a way that the bituminous mixture is formed in such a way that the specimen layer formed therefrom has at least 1% air voids and a Hveem stability of at least 21.

[0037] The specimen layer may be tested for fatigue, preferably using a beam fatigue test, most preferably using a flexural beam fatigue test. A flexural beam fatigue test determines the number of times a specimen may be flexed before it cracks. The test may be performed using any appropriate parameters. For example, the test may be performed at 2,000 microstrains, 10 Hz, and 15 0 C per ASTM D7460-08. An appropriate bituminous binder should result in a layer having at least 5,000 cycles to failure, preferably at least 10,000 cycles to failure, and most preferably at least 15,000 cycles to failure when tested at 2,000 microstrains, 10 Hz, and 15 0 C per ASTM D 7460-08.

[0038] The bituminous mixture may be tested for mixture fracture energy using any appropriate test, such as a Semi-Circular Bend Test or a Disk-Shaped Compact Tension Test, and also using any appropriate parameters. For example, when tested using a Disk-Shaped Compact Tension Test performed at a temperature of -1O 0 C, a rate of loading of 1.0 mm/min, and in accordance with ASTM D 7313-07, an appropriate bituminous binder should result in a bituminous mixture with a mixture fracture energy of greater than about 600 J/m 2 , more preferably greater than about 700 J/m 2 , and most preferably greater than about 800 J/m 2 .

[0039] The bituminous binder may likewise be tested for fracture energy using any appropriate test and any appropriate parameters. For example, when testing a single edge notch beam at 0.1 mm/sec at -30 0 C calculated by ASTM D 5045-99 where the preferred dimensions of the single edge notched beam are B = 6.0 mm, W = 9.5 mm, A = 4.9 mm, and L = 44.0 mm, an appropriate bituminous binder should result in a bituminous binder fracture energy of greater than about 40 J/m 2 , more preferably greater than about 50 J/m 2 , and most preferably greater than about 60 J/m 2 . [0040] The bituminous mixture may be tested for permeability in accordance with ASTM D 3637, in which case, an appropriate bituminous binder should result in a permeability of greater than about 8 cm 2 .

[0041] Mixture volumetric properties and/or binder film thicknesses do not need to be strictly controlled to achieve desired properties. The system can be optimized by choosing the lowest conjugated diene content that achieved the desired mixture and/or binder properties. The type of mixture, either coarse or fine, large aggregate or small, high or low air voids content, can be brought into acceptable levels of a crack resistant layer by selecting a binder with the appropriate conjugated diene content.

EXAMPLE 1 :

[0042] Eight polymer modified bituminous binders were created, four by heating a Suncor PG64-22 bituminous binder, adding polymers, mixing sufficiently to disperse the polymers within the bituminous binder, and adding a sufficient amount of sulfur to cross-link. The other four were created by the same process but with Suncor PG58-28 bituminous binder instead of PG64-22 bituminous binder. The polymers used were Solprene 1205 with about 75% conjugated diene, and Solprene 111OL with about 80% conjugated diene available from Dynasol. Binders 1 through 8 are described in Tables 1 and 2.

Table 1

Table 2

[0043] The eight bituminous binders were used to form eight bituminous mixtures, which in turn were used to form eight specimen layers. Mixture gradation and general volumetric properties are set forth in Table 3.

Table 3

[0044] The layers were tested at 2,000 microstrains, 10 Hz, and 15 0 C per ASTM D 7460-08 for flexural beam fatigue. The results are set forth in Table 4:

Table 4

[0045] As can be seen from Table 4, a higher percentage of conjugated diene resulted in a higher number of cycles to failure. A logarithmic correlation coefficient (r 2 ) between Beam Fatigue and conjugated diene content was 0.961 and 0.862 for the PG58-28 and PG64- 22 binders respectively. The correlation surprisingly demonstrates the positive effect of conjugated diene on beam fatigue properties. If acceptable beam fatigue properties are not achieved, another binder must be chosen with higher conjugated diene content.

[0046] Each bituminous layer was tested for mixture fracture energy and was tested at a temperature of -1O 0 C, a rate of loading of 1.0 mm/min, and in accordance with ASTM D 7313-07. The results are set forth in Table 5:

Table 5

[0047] A logarithmic correlation coefficient (r 2 ) between Mixture Fracture Energy and conjugated diene content was 0.973 and 0.955 for the PG 58-28 and PG64-22 binders respectively. Similarly, the correlation surprisingly demonstrates the positive effect of conjugated diene on mixture fracture energy properties. If acceptable mixture fracture energy properties are not achieved, another binder must be chosen with higher conjugated diene content.

[0048] Each Binder was evaluated for Bituminous Binder Fracture Energy and tested 0.1 mm/sec at -3O 0 C per ASTM D 5045-99. The results are set forth in Table 6:

Table 6

[0049] As can be seen from Table 6, a higher percentage of conjugated diene resulted in a higher binder fracture energy. A linear correlation coefficient (r 2 ) between conjugated diene content and Binder Fracture Energy was 0.980 and 0.993 for the PG58-28 and PG64-22 binders respectively. The correlation surprisingly demonstrates the positive effect of conjugated diene on binder fracture energy properties. If acceptable mixture binder fracture energy properties are not achieved, another binder must be chosen with higher conjugated diene content.

EXAMPLE 2:

[0050] Four polymer modified bituminous binders were created, each by heating a PG64-22 bituminous binder, adding polymers, mixing sufficiently to disperse the polymers within the bituminous binder, and adding a sufficient amount of sulfur to cross-link. The polymers used were Solprene 1205 with about 75% conjugated diene available from Dynasol and Solprene 411 with about 70% conjugated diene available from Dynasol. The first bituminous binder was a control and contained no conjugated diene. The second bituminous binder contained 1.7% Solprene 1205 and 0.3% Solprene 411, resulting in 1.49% total conjugated diene based on the weight of the polymer modified bituminous binder. The third bituminous binder contained 3.4% Solprene 1205 and 0.6% Solprene 411, resulting in 2.97% total conjugated diene based on the weight of the polymer modified bituminous binder. Finally, the fourth bituminous binder contained 5.1% Solprene 1205 and 0.9% Solprene 411, resulting in 4.46% total conjugated diene based on the weight of the polymer modified bituminous binder. Binders 9 through 12 of are described in Tables 7.

Table 7

[0051] The four bituminous binders were used to form bituminous mixtures, which in turn were used to form eight specimen layers. Mixture gradation and general volumetric properties are set forth in Table 8 and 9.

Table 8

Table 9 [0052] Each bituminous layer was tested for mixture fracture energy and was tested at a temperature of -1O 0 C, a rate of loading of 1.0 mm/min, and in accordance with ASTM D 7313-07. The results are set forth in Table 10:

Table 10

[0053] A logarithmic correlation coefficient (r 2 ) between Mixture Fracture Energy and conjugated diene content was 0.903 and 0.922 for the 9.5 mm and 4.75 mm mixtures respectively. The correlation not only demonstrates the positive effect of conjugated diene on mixture fracture energy properties, it also demonstrates the ability of the binder alone to control mixture fracture energy by increasing the conjugated diene content until acceptable properties are achieved.

[0054] Each Binder was evaluated for Bituminous Binder Fracture Energy and tested 0.1 mm/sec at -3O 0 C per ASTM D 5045-99. The results are set forth in Table 11 :

Table 11

[0055] As can be seen from Table 11, a higher percentage of conjugated diene resulted in a higher binder fracture energy. A linear correlation coefficient (r 2 ) between conjugated diene content and Binder Fracture Energy was 0.981. The correlation demonstrates the positive effect of conjugated diene on binder fracture energy properties.

ALTERNATE MIXTURES: [0056] A variety of alternate mixtures may be used to form the crack resistant layer described herein, so long as the amount of conjugated diene and the fatigue properties meet the requirements set forth above, as well as the fracture energy properties if such properties are considered. For example, every state and the Federal Highway Administration have target levels for various types of mixes. These target levels may be used, and the crack resistant properties of the mixture may be optimized by varying the level of conjugated diene content using the method set forth above. The charts below set forth three alternate mixtures, as required by the Texas Department of Transportation (Alternate Mixture #1), the Oklahoma Department of Transportation (Alternate Mixture #2), and the New Jersey Department of Transportation (Alternate Mixture #3).

* % Air Voids = (100 - 98) = 2.0%

Alternate Mixture #1

Alternate Mixture #2

http://www.state.nj.us/transportation/eng/specs/2007/spec900 .shtmSt90202031

Alternate Mixture #3

[0057] From the above description, it is clear that the present invention is well adapted to carry out the objects and to attain the advantages mentioned herein as well as those inherent in the invention. While presently preferred embodiments of the invention have been described for purposes of this disclosure, it will be understood that numerous changes may be made which will readily suggest themselves to those skilled in the art and which are accomplished within the spirit of the invention disclosed and claimed.