This invention relates to curable compositions.

High continuous use temperature ("CUT") composite materials of cross-linked polyimide matrices reinforced with fibres, especially continuous fibres, are known. Such composite materials have been used for many applications, especially in the aerospace industry in which strength-to-weight ratios and high CUT are particularly important, eg in jet engine components.

A particularly useful polyimide matrix material for use in such composites has been developed by NASA. This family of polyimide materials is known by the designation PMR (ie polymerisable monomer reactants). The PMR materials are the subject of inter alia US-A-3528950, US-A-3745149 and US-A-7603055 and have been widely reviewed in the literature, for example T T Serafini and P Devigs, Applied Polymer Symposium No 22, 89-100, 1973; Ruth H Pater, SAMPE Journal, Nov/Dec 1981; T T Serafini, Proceedings of 5th International Conference on Composite Materials, 1007-1023, Metal Soc 1985, AIME; D Wilson, British Polymer Journal, 20_(5), 405-416, 1988; and D A Scola and J H Vontell, Chemtech 112-121, February 1989.

The PMR curable compositions initially comprise an aromatic diamine, an end cap monomer and an aromatic tetracarboxylic acid, its dianhydride or alkyl diester. In accordance with US-A-3745149, a useful combination of reactants is:-

a) compounds of formula:

0 0

\ /

Rl

/ \

R2- 0-C C-O-R ²

II II o o

wherein R ¹ is a tetravalent aryl radical and R ² is alkyl or hydrogen and at least two R ² are alkyl;

b) H2N-R ³ -NH ₂

wherein R- ⁵ is a divalent aryl radical; and

c) compounds of formula:-

0

II

R ² -0-C

\

R«

/

R2-O-C

wherein R ² is as defined in a) and at least one R ² is alkyl and R-+ is a divalent radical of the formula:-

wherein R-- is hydrogen or lower alkyl; the molar ratio of a:b:c being n:(n+l):2, wherein n has a value from 1 to 20.

A commercially-available PMR resin, derived from the monomers dimethyl ester of 3,3' ,4,4'-benzophenonetetracarboxylic acid (BTDE)/4,4'-methylenedianiline (MDA)/methyl ester of

5-norbornene-2,3-dicarboxylic acid (NE) has a CUT of up to 316°C in atmospheric air and is known by the designation PMR-15. The

"15" in the designation is derived from the formulated molecular weight (FMW) of the composition. The FMW, as described in the 1985 Serafini paper, is considered to be the average molecular weight of imidized prepolymer that could have been formed if an amide-acid prepolymer had been synthesised and it is derived from the formula:-

FMW = nMWβTDE + ⁽ⁿ +1)MWMDA + ²¹ * ^W NE - 2 ⁽ n + l ⁾ [MW{ _water } + ^■ ^{methanol}]

wherein MW stands for molecular weight. It is now common practise to denote the stoichiometry of a PMR curable composition by dividing the FMW by 100.

A primary drawback of PMR-15, as reported in section 9.4 of the 1988 Wilson paper, is the suspected carcinogenic character of MDA. Although said section 9.4 indicates MDA has been substituted by other, less toxic, diamines (eg ,4'-oxydianiline and l,l-bis(4-aminophenyl)-l-phenyl-2,2,2-trifluoroethane as reported by W B Alston, Proc. Conf. High Temperature Polymer Matrix Composites, NASA Lewis Research Centre, 187-205, March 1983, the combination of properties provided by MDA could not be matched. Other variants are disclosed in the references, for example

PMR-II derived from the monomers dimethyl ester of 4,4'-(hexa- fluoroispropylidene)bis(phthalic acid) (HFDE)/para-phenylene- diamine (p-PDA)/NE, and substitution of NE with aminostyrene, optionally with the addition of N-phenylnorbornene to improve processability, ie melt flow.

The reduced processibility of the curable composition resulting from substitution of MDA by p-PDA in PMR-II, thus enabling the enhanced thermal stability of p-PDA compared with MDA to be exploited, is offset by the increase in processibility afforded by the use of HFDE. However, a primary drawback of PMR-II is the cost of HFDE.

It is an object of the invention to provide useful PMR curable compositions in which MDA is absent.

The object of the invention is achieved by the provision of a PMR curable composition in which the aromatic diamine comprises m-phenylenediamine or a mixture of p-phenylenediamine and m-phenylenediamine.

In particular, in accordance with the invention, a curable composition comprises:-

a) at least one aromatic tetracarboxylic acid, its dianhydride or alkyl diester;

b) a diamine selected from the group consisting of p-phenylenediamine and m-phenylenediamine wherein the diamine is selected such that the molar ratio of p-phenylenediamine to m-phenylenediamine is in the range

0:100 to 95:5; and

c) compounds of formula:-

R ² -0-C C

wherein R ² are alkyl or hydrogen and at least one R ² is alkyl and R ⁴ is a divalent radical of the formula:-

wherein R-5 is hydrogen or lower alkyl; and, optionally,

d) a viscosity modifier;

wherein the molar ratio of a:b:c is n:(n+l):2, wherein n has a value from 1 to 20, more particularly from 1 to 10, especially from 1.5 to 6.5 and wherein, optionally, at least some of c) is replaced by:-

e) a component selected from the group consisting of a mono aromatic amine, acid, ester or anhydride having vinyl or ethynyl functionality;

wherein, when said component e) is present and is an amine, the molar ratio of a:b is adjusted to provide sufficient component a) to react with component e).

Preferably, component a) of the curable composition is at least one aromatic tetracarboxylic acid, its dianhydride or alkyl diester selected from the group consisting of 3,3' ,4,4'-benzo- phenonetetracarboxylic acid, 4,4'-(hexafluoroisopropylidene)bis- (phthalic acid) and 2,2' ,3,3'-diphenyltetracarboxylic acid, their dianhydrides or alkyl, preferably methyl, diesters; and especially is the dialkyl ester of the corresponding tetracarboxylic acid.

Preferably, component c) of the curable composition is a mono alkyl, preferably methyl, ester of 5-norbornene-2,3-di- carboxylic acid.

One preferred curable composition according to the invention comprises:-

from the group consisting of 3,3' , , '-benzophenonetetra- carboxylic acid and 2,2' ,3,3'-diphenyltetracarboxylic acid;

b) a mixture of p-phenylenediamine and m-phenylenediamine in the molar ratios 95:5 to 70:30, preferably 90:10 to 75:25, more particularly 85:15 to 75:25, especially substantially 80:20; and

c) a mono alkyl, preferably methyl, ester of 5-norbornene-2,3- dicarboxylic acid; and, optionally,

d) a viscosity modifier ;

wherein the molar ratio of a:b:c is n:(n+l):2, wherein n has a value from 1 to 20, more particularly from 1 to 10, especially from 1.5 to 6.5 and wherein, optionally, at least some of c) is replaced by:-

e) a mono aromatic amine having vinyl or ethynyl functionality;

wherein, when component e) is present, the molar ratio of a:b is adjusted to provide sufficient component a) to react with component e) .

Preferably, component d) of the curable composition is selected from the group consisting of mono- or bis-nadimides derived respectively from mono, unsubstituted or halo-substituted, amines and unsubstituted diamines of formula H2N-Ph-(X-Ph) _a -NH2 wherein Ph is 1,3-phenylene or 1,4-phenylene, X is a direct bond, -CO-, -S0-.-S02-, -0-, -CR ⁶ 2 wherein R ⁶ is _H, -CH3 or -CF3 and a is an integer from 0 to 5, preferably from 0 to 2 and especially is 0 or 1.

More particularly, component d) of the curable composition is at least one compound of formula:-

a) at least one Cj_ to C4 alkyl, preferably methyl, diester of an aromatic tetracarboxylic acid selected from the group consisting of 3,3' ,4,4'-benzophenonetetracarboxylic acid and ,4'-(hexafluoroisopropylidene)bis(phthalic acid) and, optionally, a minor proportion of 2,2' ,3,3'-diphenyltetra- carboxylic acid;

b) a diamine selected from the group consisting of p-phenylene¬ diamine and m-phenylenediamine wherein the diamine is selected such that the molar ratio of p-phenylenediamine to m-phenylenediamine is in the range 0:100 to 95:5, preferably 5:95 to 60:40, more preferably 10:90 to 55:45, especially substantially 20:80; and

c) a mono alkyl, preferably methyl, ester of 5-norbornene-2,3- dicarboxylic acid; and, optionally,

d) a viscosity modifier ;

wherein the molar ratio of a:b:c is n:(n+l):2, wherein n has a value from 1 to 20, more particularly from 1 to 10, especially from 1.5 to 6.5 and wherein, optionally, at least some of c) is replaced by:-

e) a mono aromatic amine having vinyl or ethynyl functionality;

wherein, when component e) is present, the molar ratio of a:b is adjusted to provide sufficient component a) to react with component e) . Another preferred curable composition according to the invention comprises:-

a) at least 10 mole Z of a Ci to C4 alkyl, preferably methyl, diester of 4,4'-(hexafluoroisopropylidene)bis(phthalic acid) and, optionally, at least one Ci to C4 alkyl, preferably methyl, diester of an aromatic tetracarboxylic acid selected

wherein R ⁷ is selected from the group consisting of bis(phenyl)- methane and 1,3-phenylene and R ⁸ is selected from the group consisting of phenyl and 4-fluorophenyl. Preferably, component d) is present in the curable composition in an amount not more than 102, preferably not more than 52, especially substantially 22, by weight based on the weight of components a), b) and c). Preferably, component d) is present in the curable composition in an amount of at least 12 by weight of components a), b) and c).

Preferably, component e) of the curable composition is selected from the group consisting of 3-aminostyrene, 4-amino- styrene, 3-ethynylaniline, 4-ethynylaniline and 3- or 4-allyl- substituted or ethynyl-substituted phthalic mono-alkyl, preferably methyl, ester or anhydride. More preferably, component e) is 4-aminostyrene.

Preferred curable compositions according to the invention have a FMW between 1200 and 6000, more preferably between 1200 and 3500.

Preferably, the curable composition according to the invention further comprises fibre reinforcement. Although the fibres may be any suitable fibres such as glass, carbon or organic polymers, preferably, the fibres are carbon fibres, especially graphite fibres. Graphite fibres which have been found to be especially useful in the invention are those supplied by Amoco under the trade designations T650-35 and T650-42; those supplied by BASF under the trade designation Celion G35-500; those supplied by Toray under the trade designation T800-HB; and those supplied by Hercules under the trade designation IM 8. The fibres may be short or chopped fibres, typically of mean fibre length not more than 20 mm, for example about 6mm.

When the fibres of the reinforcement are in the form of a woven fabric, structures may be quasi-isotropic or between anisotropic and quasi-isotropic.

The invention will now be illustrated by reference to the following Examples and to the accompanying drawings, in which:-

Figure 1 is a graphical representation of weight loss data generated in the TOS evaluation of Samples 1 to 5 in

Example 1;

Figure 2 is a graphical representation of weight loss data generated in the TOS evaluation of Samples 1 and 14 to

16 as described in Example 4; and

Figures 3(a) and 3(b) are respectively the imidization/cure cycle and post cure cycle used to make the laminates of

Example 9. In the Examples, the following components, methods and tests were used:-

Esters dimethyl ester of 3,3' ,4,4'-benzophenonetetracarboxylic acid BTDE dimethyl ester of 4,4'-(hexafluoroisopropylidene)bis(phthalic acid) - HFDE dimethyl ester of 2,2' ,3,3'-diphenyltetracarboxylic acid - BPDE dimethyl ester of 3,3' ,4,4'-diphenylethertetracarboxylic acid ODPE dimethyl ester of 3,3' ,4,4'-diphenylsulphonetetracarboxylic acid

- DSDE diethyl ester of pyromellitic acid - PMDE

Diamines

4,4'-methylenedianiline - MDA p-phenylenediamine - p-PDA m-phenylenediamine - m-PDA

Alternatively, and preferably, the fibres are continuous and may, for example, be unidirectionally-disposed fibres or a woven fabric. Combinations of both short and/or chopped fibres and continuous fibres may be utilised. The fibres may be sized or unsized.

The curable composition according to the invention may also contain other fillers such as toughening agents such as thermoplastics optionally having reactive groups; aggregates such as glass beads; polytetrafluoroethylene; graphite; boron nitride; mica; talc; vermiculite; nucleating agents; and stabilisers. The total of such materials and the fibre reinforcement should be such that the curable composition contains at least 202 by volume of reinforcing fibres and/or fillers. The percentages of fibres and such other materials are calculated on the total composition after curing.

The invention also includes composite materials comprising plies of fibre-reinforced curable compositions according to the invention laminated together by heat and pressure, for example by autoclave, compression moulding or by heated rollers, at a temperature above the curing temperature of the curable composition.

When the fibres of the reinforcement are continuous and unidirectional, the resulting multi-ply laminate may be anisotropic in which the fibres are oriented essentially parallel to one another or quasi-isotropic in each ply of which the fibres are oriented at an angle, conveniently 45° as in most quasi-isotropic laminates but possibly for example 30° or 60° or 90° or intermediately, to those in the plies above and below. Orientations which are between anisotropic and quasi-isotropic, and combination laminates, may be used. Suitable laminates contain at least four, preferably at least eight, plies. The number of plies is dependent on the application for the laminate, for example the strength required, and laminates containing thirty-two or even more, for example several hundred, plies may be desirable. There may be aggregates, as mentioned above, in interlaminar regions.

End Caps mono methyl ester of 5-norbornene-2,3-dicarboxylic acid - NE p-aminostyrene - PAS

The esters were prepared by refluxing the corresponding dianhydride or anhydride as the case may be with the appropriate alcohol for 2 hours.

Viscosity Modifiers N-phenylnadimide - NPN

4-fluoro-N-phenylnadimide - F-NPN 4,4'-methylenedianilinebisnadimi.de, ie

MDA-bisnadimide

m-phenylenediaminebisnadimide

- m-PDA-bisnadimide

The viscosity modifiers were readily prepared by converting the appropriate amine with nadic anhydride by stirring in acetone at room temperature followed by cyclodehydration of the resultant amic acid to the required imide using sodium acetate and acetic anhydride in refluxing acetone. These preparations are readily exemplified with reference to the preparation of NPN which was prepared as follows. A solution

of 5-norbornene-2,3-dicarboxylic anhydride (196.99g, 1.20 mole) in 400ml of acetone was formed by gently heating the ingredients in a reaction flask. Aniline (109.35ml, 1.20 mole) was then added to the flask dropwise, the temperature of the reaction mixture being maintained at ambient by means of an ice/water bath. The reaction mixture was then stirred at ambient temperature for a further 2 hours. A precipitated white product (N-phenylnadic acid) was filtered off and washed on the filter with a minimum quantity of acetone. The washed and filtered product was dried in a vacuum oven at 60°C (yield = 812).

The N-phenylnadic acid (249.59g, 0.47 mole) was slurried with 400ml of acetone in a reaction flask. Sodium acetate (32.82g, 0.40 mole) and acetic anhydride (136ml, 1.44 mole) were then added to the flask. The temperature of the reaction mixture was then increased until a gentle reflux of the acetone was achieved. The temperature of the reaction mixture was maintained at reflux for a further 3 hours and was then cooled to ambient temperature and slowly added to a vigorously-stirred ice/water mixture. The resultant precipitated white product (NPN) was then filtered off, washed several times with warm distilled water and dried at 60°C in a vacuum oven (yield = 652).

Thermal Oxidative Stability

A number of the Examples are concerned with the thermal oxidative stability (TOS) of samples under isothermal aging conditions. The TOS of the samples was assessed by locating a sample in an aluminium cup and periodically measuring weight loss during isothermal ageing of the sample at the ageing temperature, eg 350°C, in an air circulating oven at ambient pressure. The isothermal ageing was taken over approximately 500 hours.

Glass Transition Temperature (Tg)

The Tg of samples was determined using dynamic mechanical thermal analysis (DMTA) (E' onset) under nitrogen and at a heating rate of 2°C/min. The DMTA was done using a single

cantilever method wherein the sample is clamped at one end and is oscillated at a frequency of 10Hz.

Neat Resin Examples

Curable compositions of alkyl diester/diamine/end cap in the molar ratios n:n+l:2 were converted into PMR prepolymer moulding powders using the following method which is exemplified by a PMR-15 composition:- BTDE (4.03g), MDA (3.06g) and NE (1.96g) were dissolved in methanol (30ml). The resultant solution was placed on a hot block (120°C) to evaporate the methanol. When the majority of the methanol had evaporated off, the residue was placed in an air circulating oven (120°C) until the remaining methanol had evaporated and partial imidisation was initiated. The resultant solid material was crushed into a fine powder, the oven temperature was increased to 200°C and held for 1 hour to complete imidisation. The imidised material was then ground into a fine powder suitable for moulding.

When part or all of the end cap is an amine, eg PAS, the molar ratio of alkyl diester and diamine is adjusted so that there is sufficient alkyl diester present to react with the amine. When all of the end cap is amine, the molar ratios of alkyl diester/diamine/end cap are n+l:n:2. Processability

Samples of the imidised moulding powders were assessed for processability by using rheometrics to determine the complex viscosity I*. Typical conditions used to evaluate the powder samples, which were compressed into 25mm diameter discs prior to rheological evaluation, using a RMS 800 rheometer manufactured by Rheometrics Limited were:-

Initial Temperature 200°C - 260°C Final Temperature 350°C

Heating rate 2.0°C/min

Strain rate 1.02

Oscillation 10 rads/sec Data Points One every 10 sec,

NB The actual temperature range scanned varied depending upon the moulding powder melt temperature and cure temperature.

Two moulding cycles were used depending on whether the end caps of the imidised material were derived from NE (nadic ends) or PAS (styrene ends). The methods are given below:-

Nadic-ended Prepolymers

Imidised moulding powder (2.5g) was poured into the female section of a matched metal mould (40mm x 10mm) and the male section was inserted. The mould was placed in an air circulating oven (280°C-300°C) and left for 5-10 minutes. The preheated mould was then placed between the platens of a press (preheated to 320°C). After 15 minutes, pressure was applied and gradually increased up to a maximum of 6.1 MPa (depending upon the formulation) . The temperature and pressure were held constant for 1-2 hours to complete curing. The mould was then cooled under pressure to below 150°C and removed from the press. The resultant neat resin plaque was removed from the mould.

The plaque was post cured at an appropriate temperature in an air circulating oven for 24 hours at ambient pressure.

Styrene-ended Prepolymers

Imidised moulding powder (2.5g) was poured into the female section of a matched metal mould (40mm x 10mm) and the male section was inserted. The cold mould was placed between the platens of a press (preheated to 302°C), held for 15 minutes and then a pressure of 0.6 MPa was applied. The pressure was held for 30 minutes following which the press temperature was increased to 350°C. The temperature was held constant for 1 hour during which period the pressure was increased to 2.5 MPa. The temperature was then increased to 371°C and held for a further 1 hour with the pressure maintained at 2.5 MPa. The mould was then

cooled under pressure to below 150°C and removed from the press. The resultant neat resin plaque was removed from the mould.

The plaque was post cured at an appropriate temperature in an air circulating oven for 24 hours at ambient pressure.

In fibre-reinforced samples:-

G_ _c was determined in accordance with the Protocols for

Interlaminar Fracture Testing of Composites, ESIS Protocol,

Co-ordinator P Davies, FREMER, Plouzane, France, May 1992 - specimen dimensions 25 x 145 x 3 mm; and SBSS was determined using ASTM D2344-84 - specimen dimensions 25 x 10 x 3 mm.

Example 1

Curable compositions based on MDA, NE and selected esters were prepared to evaluate the ester component (excluding fluorine-containing esters) of the composition with respect to TOS. The compositions were formulated to give a FMW = 1500. The esters used, together with their Tg data, are given in Table 1 below. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 350°C. Samples of the moulded compositions were then subjected to TOS evaluation at 350°C. The weight loss data generated were plotted, see Figure 1, from which it is apparent that Samples 1 (PMR-15 control) and 2 contain the most stable esters.

TABLE 1

SAMPLE NO ESTER Tg (°C)

1 BTDE (PMR-15 control) 332

2 BPDE 350

3 PMDE 370

4 DSDE

5 ODPE 280

The processibilities of the samples were also assessed.

Sample 1 (PMR-15 control) had a minimum tf) * of approximately 70

Pa.s. Samples 4 and 5 had comparable processibility to Sample 1 but Samples 2 and 3 did not flow under the rheological conditions used.

Example 2

Curable compositions based on BTDE, NE and, as diamines, p-PDA and m-PDA and mixtures thereof were prepared to evaluate the diamine component of the composition with respect to TOS. The compositions were formulated to give a FMW = 1500. A PMR-15 control (Sample 1) was also prepared. The compositions were converted into moulding powders which were moulded into plaques. Compositions containing 1002 p-PDA proved to be unmouldable. The plaques were post cured at 350°C. Samples of the moulded compositions were then subjected to TOS evaluation at 350°C for approximately 500 hours and Tg determination. The samples tested, their TOS 500 hour data and Tg data are given in Table 2 below.

The processibilities of the samples were also assessed. Only Samples 13 to 15 flowed sufficiently under the rheological conditions used to to be assessed. Sample 15 had a minimu A * of approximately 850 Pa.s; and Samples 13 and 14 had a minimum /I* of approximately 5700 Pa.s. Example 3 Curable compositions based on a PMR-II composition, ie HFDE, NE and p-PDA and such compositions in which a part of the p-PDA is replaced by m-PDA were prepared to evaluate the TOS of the cured compositions. The compositions were formulated to give a FMW = 3000. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 350°C. The PMR-II formulation shows only a small weight loss when subjected to isothermal aging at 316°C and 350°C but a more significant weight loss at 371°C. Accordingly, samples of the moulded compositions were subjected to TOS evaluation at 371°C for approximately 500 hours. The Tg of the samples was also determined. The samples tested, their TOS 500 hour data and

Tg data, including for comparison Sample 1 data (ie PMR-15) are given in Table 3 below.

The processibilities of the samples were also assessed.

Sample 16, ie PMR-II-30, had a minimum^* of approximately 2200 Pa.s (cf PMR-15 minimum/)* of 70 Pa.s; Sample 17 had a minimum/7* of approximately 240 Pa.s; and Sample 18 had a minimum^* of approximately 220 Pa.s.

TABLE 2

SAMPLE NO p-PDA:m-PDA WEIGHT LOSS (2) Tg (°

1 - 51.4 332

6 95:5 47.2 -

7 90:10 35.1 -

8 85:15 32.1 >350

9 80:20 22.5 -

10 70:30 21.1 381

11 50:50 14.8* ¹ 362

12 40:60 14.9 350

13 30:70 30.0 352

14 20:80 18.5 337

15 0:100 36.9 346

*1 - Estimated value at 500 hours from weight loss v time plot extending up to 575 hours.

Example 4

The TOS weight loss data at 350°C for approximately 500 hours for Samples 1 (PMR-15), 14 (BTDE/NE/p-PDA:m-PDA 20:80), 15

(BTDE/NE/ p-PDA:m-PDA 0:100) and 16 (PMR-II-30) are plotted in

Figure 2. As can be seen, the TOS of Sample 14 is approaching that of Sample 16.

Example 5 Curable compositions were formulated to determine the effect of replacing NE with PAS in PMR-II compositions and the effect of

1B FMW on such compositions and on compositions based Sample 15 above in TOS evaluations of the cured compositions. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 350°C. The samples tested, together with Samples 1, 15 and 16, TOS 500 hour/350°C data and TOS 600 hour/371°C data are given in Table 4 below. Example 6

Curable compositions of p-PDA and PAS together with HFDE (Sample 21A) and mixtures of HFDE and BTDE, with a formulated FMW of 3000, were formulated to evaluate TOS of the cured compositions. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 371°C. The samples tested, Tg, TOS 500 hour/350°C data and TOS 500 hour/371°C data are given in Table 5 below. The samples did not melt and flow under the rheological test conditions.

TABLE 3

SAMPLE NO p-PDA:m-PDA WEIGHT LOSS (2) Tg (°C)

AT 371°C

1 - 100* ² 332

16 100:0 36.2 342

17 80:20 26.0 328

18 60:40 44.8 -

19 40:60 51.6 —

*2 - PMR-15 is almost completely decomposed after approximately 300 hours at 371°C.

Example 7

Curable compositions of HFDE and PAS together with p-PDA (Sample 21A) and mixtures of p-PDA and m-PDA, with a formulated

FMW of 3000, were formulated to evaluate TOS of the cured

compositions. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 371°C. The samples tested, Tg, TOS 500 hour/350°C data and TOS 500 hour/371°C data are given in Table 6 below. The samples did not melt and flow under the rheological test conditions but excellent melt flow was observed during compression moulding of the samples.

TABLE 4

SAMPLE NO MONOMERS FMW WEIGHT LOSS WEIGHT LOSS (2) 350°C (2) 371°C

1 BTDE/MDA/NE 1500 52 100* ³

15 BTDE/m-PDA/NE 1500 37 -

20 HFDE/p-PDA/NE 1500 22 64

21 HFDE/p-PDA/PAS 1500 21.5 54

15A BTDE/m-PDA/NE 3000 20.5 _

16 HFDE/p-PDA/NE 3000 10 -

21A HFDE/p-PDA/PAS 3000 6.0 to 9.27* ⁴ -

* ³ - At approximately 300 hours.

Example 8

Curable compositions based on Sample 14, ie BTDE/NE/p-PDA:m-PDA 20:80, were formulated, FMW of 1500, together with a viscosity modifier. The compositions were converted into moulding powders which were moulded into plaques. The plaques were post cured at 350°C. The samples tested, together with Samples 1 and 14, TOS 500 hour/350°C data and^Λ * (minimum) data are given in Table 7 below.

TABLE 5

SAMPLE NO HFDE:BTDE WEIGHT LOSS WEIGHT LOSS Tg (°C) RATIO (2) 350°C (2) 371°C

21A 100:0 6.0 to 9. 27* ⁴ 20.69 316

22 80:20 9.58 25.48 320

23 60:40 10.60 34.58 332

24 40:60 8.01 24.41 410* ⁵

25 20:80 7.14 24.35 402* ⁵

* ⁴ - Several samples gave values within this range. * ⁵ - Not a sharp break in E' .

TABLE 6

SAMPLE NO p-PDA:m-PDA WEIGHT LOSS WEIGHT LOSS Tg (°C) RATIO (2) 350°C (2) 371°C

21A 100:0 9.27 20.69 316

26 90:10 8.72 19.32 333

27 80:20 9.42 21.13 344

28 70:30 9.07 22.27 363

29 50:50 7.54 19.64 359

30 0:100 9.02 18.07 339

Example 9

Selected fibres (12k tows) were impregnated with a number of curable compositions using conventional PMR prepregging techniques, ie monomers in methanol, to form prepregs. The curable compositions were of alkyl diester/diamine/end cap in the molar ratios n:n+l:2 together with a viscosity modifier present in a weight 2 based on the weight of the alkyl diester/diamine/end cap. All of the compositions used a mixture of p-PDA and m-PDA as the diamine, NE as the end cap and NPN as the viscosity modifier. A PMR-15 control composition, Sample 41,

was also used. Further details of the fibres and the compositions are given in Table 8 below.

Each prepreg had a resin content of 35±5 wt 2. Each prepreg sample was then laid up as [0]24 150 mm x 100 mm laminates in a matched metal mould and imidised and cured using a compression moulding cycle shown in Figure 3(a). The resultant consolidated laminates were post cured at ambient pressure in an air circulating oven using the cycle shown in Figure 3(b). The resultant laminates were isothermally aged (average of 5 samples), and tested to determine Gι _c and short beam shear strength (SBSS), the results of which are also given in Table 8.

Ultrasonic C-scan examination of the consolidated laminates demonstrated the laminates had a very low void content.

TABLE 7

SAMPLE MODIFIER 2 w/w a.s) WEIGHT LOSS

NO ] MODIFIER (2)

1 - _ 70 51.4

14 - - 5700 18.5

31 NPN 2 143 20.9

32 NPN 4 170 20.5

33 NPN 6 82 24

34 NPN 10 49 -

35 F-NPN 2 309 23.4

36 MDA- ■BISNADIMIDE 2 370 19.8

37 MDA- -BISNADIMIDE 4 200 17

38 MDA- -BISNADIMIDE 6 200 24

39 MDA- -BISNADIMIDE 10 140 -

40 m-PDA-BISNADIMIDE 2 287 22.3

TABLE 8

SAMPLE NO MONOMERS MODIFIER FMW 2 WT LOSS 2 WT LOSS G _lc (KJ/m ^z ) SBSS

DIESTER p-PDA:m-PDA WT 2 AT : 316°C AT 350°C INITIATION PROPAGATION (MPa) RATIO

41 PMR-15 CONTROL 1500 2.6 26.1 0.23 0.26 94.5 (2.6) 42 BTDE 20:80 2 1300 2.6 18.3 0.2 0.5 84.5 (12.2) 43 BTDE 20:80 2 1500 1.6 13.5 44 BTDE 20:80 2 1500 1.6 15.1 0.17 0.53 80.3 (4.1) 45 BTDE 20:80 1.1 1500 2.9 12.8 46 BTDE 20:80 3 1800 2.0 17.5 0.32 0.67 90.0 (4.1) 47 BTDE 30:70 2 1300 2.5 20.8 0.30 0.87 94.8 (6.2) 48 BTDE 30:70 4 1500 - - 0.17 0.60 94.8 (11.1) 49 BTDE/HFDE 20:80 4 2000 _ 12.6

70:30

Note 1 With the exception of Sample 43 which used AS4 fibres from Hercules, all of the other samples used

G30-500 fibres available under the trade name Celion. Note 2 The SBSS results show the standard deviations in brackets.

Example 10

Curable compositions based on various selected esters and mixtures thereof together with NE, p-PDA/m-PDA mixtures and 22 w/w of NPN were formulated (various FMW) . The compositions were converted into moulding powders and moulded into plaques. The plaques were posted cured at 350°C for 10 hours. The samples tested, TOS data at 316°C and 350°C (approximately 500 hours) and ή* minimum data are given in Table 9 below.

TABLE 9

SAMPLE DIESTES MONOMERS F FMMWW 2 WT LOSS 2 WT LOSS

NO p-PDA:m-PDA AT 316°C* ⁷ AT 350°C* ⁷ 1

50 BTDE 20:80 1500 4.2 19.7 234

51 DSDE 20:80 1500 10.5 84.6 73

52 ODPE 20:80 1500 4.1 28.7 156

53 PMDE 20:80 1500 40.6 90.2 *6

54 BPDE 20:80 1500 15.6 35.1 *6

55 HFDE 20:80 1500 5.4 13.1 16

56 HFDE 20:80 2000 4.4 12.0 560

57 HFDE 50:50 2000 3.7 8.9 1070

58 HFDE/BPDE 20:80 1500 3.9 12.7 63 30:70

59 HFDE/BPDE 20:80 1500 4.5 13.7 38 70:30

* ⁶ - Samples did not melt and flow under the rheological test conditions.