FORMED FROM TETRAFLUOROPROPENE

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] The present application claims priority from US Provisional Application Serial No. 61/894,146, filed 22 October 2013, the disclosure of which is hereby incorporated herein by reference. The ' 146 Provisional Application is related to U.S. Application No, 13/645,444, filed on Oct. 4, 2012, U.S. Application No. 13/645,437, filed on Oct. 4, 2012, U.S. Provisional Application No. 61/543,780, filed on Oct. 5, 2011 , and U.S. Provisional Application No. 61/543,714, filed on Oct. 5, 2011, the contents of which are hereby incorporated herein by reference in their entirety.

FIELD OF THE INVENTION

[0002] The present invention generally relates to novel curable copolymers formed, at least in part, from teirafluoropropene. More specifically, the present invention relates to curable copolymers formed in part from monomelic material comprising 2,3,3,3-tetra- fluoropropene «Ί·\( Τ ( ^' 1 1 ·. "HFO-1234yf ') and/or 1,3,3,3-tetrafluoropropene "HFO-1234ze"), and to compositions and uses thereof. BACKGROUND OF THE INVENTION

[0003] Fluoropolvmers such as polytetrafluoroethylene (PTFE), polychlorotrifluoro- ethylene (PCTFE) and polyvinylidene fluoride (PVDF) are well known for having excellent thermal, chemical, and weather resistance, along with favorable properties like water and oil resistance. Unfortunately, the use of such fluoropolvmers in coatings is difficult owing to their poor solubility in industrial solvents such as xylene and butyl acetate— which are typically used in the coating industry. Instead, more exotic solvents must often be used, which not only affect the economics of a coating, but can also present environmental issues owing to, e.g., potential toxicity of the exotic solvents.

[0004] Accordingly, there is a need to formulate alternative coatings which have superior performance properties, yet can use economical industrial solvents and be

environmentally friendly.

[0005] Furthermore, polymerization of fluorinated polymers presents a number of challenges, e.g., as detailed in prior application Serial No. 13/645,437 (now U.S. Patent Publication No. 2013/0090439 AT), incorporated herein by reference. Although several types of polymerization methods to make tetrafluoropropene copolymers have been described in prior application Serial No. 13/645,437, Applicants have come to further appreciate that these polymerization methods have undesirable aspects or limitations, and/or that the polymers produced thereby can be formed with different and/or improved properties.

[0006] Accordingly, Applicants have come to appreciate a need to develop improved processes for making tetrafluoropropene copolymers having different and/or improved properties for uses in various applications. SUMMARY OF THE INVENTION

[0007] In accordance with a first aspect of the present invention, a curable

tluorocopolymer can be formed by solution copolymenzation of the monomers represented by (a), (b) and (c):

(a) 40 to 60 mol% of tetrafluoropropene;

(b) 5 to 45% of vinyl ether or vinyl ester or both of them, represented by formula CH ₂ =CR1-0(C=0) _X R2 and CH ₂ =CR3-OR4 respectively, wherein Rl and R3 is hydrogen or a methyl group, and wherein R2 and R4 is an unsubstituted straight-chain, branched- chain or alicyclic alkyl group having 1 to 12 carbon atoms; and

(c) 3 to 30 mol% of hydroxyalkyl vinyl ether, represented by formula€H?=C-R5-QR6, wherein R5 is hydrogen or a methyl group, and R6 is an unsubstituted straight-chain, branched- chain or alicyclic alkyl group having a hydroxyl groups,

[0008] In accordance with a second aspect of the present in vention, the tetrafluoropropene is selected from either or both of HFO-I234yf and HFO-1234ze. In accordance with the present invention, the applicants have found that environmentally friendly HFO- 1234yf and HFO-1234ze can each, and in combination, be employed advantageously as fluorinated monomers for the production of polymeric coatings.

[0009] In accordance with a third aspect of the present invention, a product containing the curable fluorocopoiymer has a solvent content of 15-50 %, and preferably, 15-25%, so as to provide a concentrated product which is economical to ship to the user of the product. DET AI LED DESCRIPTION OF THE INVENTION

[0010] In accordance with a preferred embodiment of the present invention, the 40-60 moI% tetrafluoropropene in the form of HFO-1234yf and/or HFO-1234ze is used as component (a), and most preferably, 45 to 55 mol%. If a mixture of HFO-1234yf and HFO-1234ze is used, the blending ratio of HFO-1234yf and HFO-1234ze is used can be any ratio, but preferably is 0.3 to 0.7: 0.7 to 0.3.

[0011] A copolymer in accordance with the present invention may contain vinyl ether units, vinyl ether units, or a combination thereof as component (b). Preferably, 5 to 45 mol% is used, and most preferably, 25-45 mol% is used. Examples of vinyl ether include alky! vinyl ethers such as methyl vinyl ether, ethyl, propyl vinyl ether, n-butyl vinyl ether, isohutyl vinyl ether, hexyl vinyl ether, octyi vinyl ether, decyl vinyl ether and lauryl vinyl ether. Vinyl ethers including an alicyclic group can also be used, for example, cyclobutyl vinyl ether, cyclopentyl vinyl ether and cyclohexyl vinyl ether. Examples of vinyl esters include vinyl acetate, vinyl propionate, vinyl butyrate, vinyl pivalate, vinyl capronate, vinyl laurate, VEOVA-9 (vinyl versatate ester formed from a C9 carbocylic acid, produced by Momentive), VEOVA-10 (vinyl versatate ester formed from a CIO carbocylic acid, produced by Momentive) and vinyl cyclohexanecarboxylate.

[0012] Exampl es of the hydroxyalkyl vinyl ether of component (c) include bydroxyl- ethyl vinyl ether, hydroxypropyl vinyl ether, hvdroxybutyl vinyl ether, hydroxypentyl vinyl ether and hydroxy hexyl vinyl ether. Preferably 3 to 30 mol% is used, and most preferably, 5 to 20 mol % is used,

[0013] The fluorocopolymer is preferably produced in a solution polymerization system. Examples of solvents for solution polymerization include: esters, such as methyl acetate, ethyl acetate, propyl acetate and butyl acetate; ketones, such as acetone, methyl ethyl acetone and cyclohexanoiie; aliphatic hydrocarbons, such as hexane, cyclohexane, octane, nonane, decane, undecane, dodecane and mineral spirits; aromatic hydrocarbons, such as benzene, toluene, xylene, naphthalene, and solvent napthta; alcohols, such as methanol, ethanol, tert-butanol, iso-propanoi, ethylene glycol monoalkyl ethers; cyclic ethers, such as tetrahydrofuran, tetrahydropyran, and dioxane; fluorinated solvents, such as HCFC-225 and HCFC- 1.41b; dimethyl sulfoxide; and the mixtures thereof.

[0014] Preferably, polymerization is conducted in a range of -30°C to 150°C depending on the polymerization initiation source and type of the polymerization medium.

[0015] The copolymer of the present invention is preferably prepared by copolymerizing those monomers and having a number average molecular weight of 5000 to 50000, and more preferably 5000 to 10000. Preferably, the copolymer has a molecular weight distribution of 2 to 10, more preferably 2.5 to 8, and most preferably 3 to 6. When the number average molecular weight is less than 5000, the copolymer is inferior in weatherability and chemical resistance, and when more than 50000, high viscosities may cause operational difficulties.

[0016] The copolymer of the present invention has hydroxy 1 groups and it is curable with a curing agent such as melamine resin curing agent, urea resin curing agent, polybasic acid curing agent and a non-blocked polyisocyanate curing agent or a blocked

polyisocyanate curing agent which are used for conventional thermosetting acryl coating. Examples of melamine resin curing agents include hutylated melamine resin, methylated melamine resin, epoxymelamine resin and the like. Examples of non-blocked

polyisocyanate include 2,4- and 2,6-diisocyanatotoluene (TDI), diphenylmethane-2,4'- and/or -4,4'-diisocyanate (MDI), 1,6-hexaniethylene diisocyanate (HDI), 1-isocyanato- 3,3,5 -trimethyl- 5 -isocyanatomethyl cyclohexane (IPDI ), dicyclohexylmethane diisocyanate (H12MDI), 1 ,4-diisocyanatobutane, 2-methyI- 1 ,5-diisocyanatopentane, 1,5- dii.socyanato-2,2- dimethylpentane, 2,2,4- or 2,4,4-trimethyl-l ,6-diisocyanatohexane, 1 , 10-diisocyanato- decane, 1,3- and 1,4- diisocyanatocyclohexane, 1,3- a d 1,4-bis- (isocyanatomethyl)- cyclohexane, 4,4'-diisocyanatodicyciohexylrneth.ane, I -isocyanato-1 - methyl-4(3)- isocvanato- methylcyclohexane (IMCI), bis-(isocyanatomethyl)-norbomane, 1,3- and 1,4-bis- (2-isocyanato-prop-2-yl)-benzene (TMXDI), 1 ,5- diisocyanatonaphthalene, 2,4'-, 4,4'-diisocyanatodiphenylmethane, and their dimers, tri.rn.ers and polymers thereof. As to blocked poiyisocyanate, preferred blocking groups employed for blocking polyisocyanates include metal bisulfite, diethyl malonate (DEM) 3,5-dimethylpyrazole (DMP), methyl- ethylketoxime (ME O) e-caprolactam (e-CAP), diisopropylamine, dimethyl- pyrazole, methyl ethyl ketoxime (butanone oxime), malonic acid diethyl ester, secondary amines and triazole and pyrazole derivatives. When the curing is conducted at an ordinary temperature by using poiyisocyanate, it is possible to accelerate the curing by an addition of a conventional catalyst such as dibutyltin diiaurate

[0017] Various solvents can be used for the preparation of solution-type paints or coatings with the copolymer of the present invention. Preferred solvents include aromatic hydrocarbons such as xylene and toluene; alcohols such as n-butanol; esters such as butyl acetate; ketones such as methyl isobutyl ketone, and glycol ethers such as ethyl cellusolve and various commercial thinners. When t he copolymer of the present invention is used for producing a thermosetting composition for coating, a curing agent such as a melamine type curing agent, a urea type curing agent, a polybasic acid type curing agent, a poiyisocyanate type curing agent or the like is simultaneously mixed in the mixing step mentioned above to produce a one-pack type coating.

[0018] On the other hand, when the composition is a normal temperature setting type coating which uses a poiyisocyanate, the curing agent component is separately prepared to provide a two-pack type coating. In this case, the coating can be cured at room temperature for from several hours to several days, and has good properties by

controlling the type of isocyanate and catalyst and their amounts to be added, the concentration of the copolymer, the contents of the hydroxyalkyl vinyl ether in the copolymer, and the like.

[0019] When the copolymer of the present invention is used as resin for paint or coating, it is possible to form under a mild condition, a film having excellent hardness of finish and gloss, flexibility, chemical resistance, stain resistance and weathering resistance. Such films are useful not only as a coating for pre-coated galvanized steel, colored aluminum plate and aluminum frames, but also as an on-site paintable non-thermally dryabie paint. The paint or coating may be used for a number of substrates, including: metallic substrates; inorganic substrates such as glass, cement and concrete; organic substrates, for example, plastics (such as polyethylene, polypropylene, ethylene-vinyl acetate copolymer, nylon, aery] polyester ethylene-polyvinyl alcohol copolymer, vinyl chloride, vmylidene chloride) and wood materials. Specific applications for the paint or coating include, but are not limited to, the coating of aluminum swimming pools, the coating of colored glass intended for exterior use, and the coating of cement tile used for roofing.

[0020] The present invention is further illustrated by the following non-limiting examples.

EXAMPLE 1

[0021 ] 19.0 g of butyl acetate, 9.5 g of ethyl vinyl ether, 20.8 g of VEOVA-9, 8.0 g of hydroxybutyl vinyl ether, and 0.62 g of tert-butyl peroxypivalate were charged into a 300 ml stainless steel autoclave equipped with a stirrer. The mixture was solidified with liquid nitrogen, and deaerated to remove the dissolved air. Then, 50 g of 1,3,3,3- tetrafluoro- propene was added to the mixture, and the mixture was gradually heated to 65°C in an autoclave. The mixture was stirred for 18 hours. After the autoclave was cooled to room temperature, the unreacted monomers were purged and the autoclave was opened. Excess solvent was removed via evaporation. [0022] Yield 92%; Tg (glass transition temperature) of final copolymer = 15°C; Mn = 7348; Mw = 13789; Mw/Mn = 1.87; final polymer concentration = 74.7%; viscosity < 500 cps.

EXAMPLE 2

[0023] 20.0 g of butyl acetate, 9.1 g of ethyl vinyl ether, 6.0 g of vinyl acetate, 6.7 g of hydroxybutyl vinyl ether, and 0.4 g. of tert-Butyl peroxypivaiate were charged into a 300 ml stainless steel autoclave equipped with a stirrer. The mixture was solidified with liquid nitrogen, and deaerated to remove the dissolved air. Then, 40 g of 2,3,3,3- tetrafluoro- propene was added to the mixture, and the mixture was gradually heated to 65°C in an autoclave. The mixture was stirred for 18 hours. After the autoclave was cooled to room temperature, the unreacted monomers were purged and the autoclave was opened. Excess solvent was removed via evaporation.

[0024] Yield 91%; Tg of final copolymer = 1 1 °C; Mn - 5314; Mw = 12646; Mw Mn = 2.38; final polymer concentration = 73.8%; viscosity < 600 cps.

EXAMPLE 3

[0025] 20.0 g of butyl acetate, 8.0 g of ethyl vinyl ether, 17.4 g of VEOVA-9, 6.7 g. of hydroxybutyl vinyl ether, and 0.63 g. of tert-butyl peroxypivaiate were charged into a 300 ml stainless steel autoclave equipped with a stirrer. The mixture was solidified with liquid nitrogen, and deaerated to remove the dissolved air. Then, 60 g of 1,3, 3,3- tetrafiuoro- propene was added to the mixture, and the mixture was gradually heated to 65°C in an autoclave. The mixture was stirred for 18 hours. After the autoclave was cooled to room temperature, the unreacted monomers were purged and the autoclave was opened. Excess solvent was removed via evaporation. [0026] Yield 93%; Tg of final copolymer = 32°C; Mn = 7136; Mw = 24103; Mw/Mn = 3.37; final polymer concentration = 81.1%; viscosity < 700 cps.

EXAMPLE 4

[0027] 20.0 g of butyl acetate, 8.2 g of ethyl vinyl ether, 22.3 g of VEOVA-9, 3.4 g of hydroxybutyl vinyl ether, and 0.66 g of tert-butyl peroxypivalate were charged into a 300 ml stainless steel autoclave equipped with a stirrer. The mixture was solidified with liquid nitrogen, and deaerated to remove the dissolved air. Then, 50 g. of 1,3,3, 3- tetrafluoro- propene was added to the mixture, and the mixture was gradual!)' heated to 65°C in an autoclave. The mixture was stirred for 18 hours. After the autoclave was cooled to room temperature, the unreacted monomers were purged and the autoclave was opened. Excess solvent was removed via evaporation.

[0028] Yield 85%,; Tg of final copolymer = 12°C; Mn = 4640; Mw = 8079; Mw Mn = 1.74; final polymer concentration = 78.1%; viscosity < 600 cps.

EXAMPLE 5

[0029] 30.0 g of butyl acetate, 7.6 g of ethyl vinyl ether, 18.4 g of VeoVa-9, 6.7 g of hydroxybutyl vinyl ether, and 0.60 g of tert-butyl peroxypivalate were charged into a 300 ml stainless steel autoclave equipped with a stirrer. The mixture was solidified with liquid nitrogen, and deaerated to remove the dissolved air. Then, 60 g of 1 ,3,3,3- tetrafluoro- propene was added to the mixture, and the mixture was gradually heated to 65°C in an autoclave. The mixture was stirred for 18 hours. After the autoclave was cooled to room temperature, the unreacted monomers were purged and the autoclave was opened. Excess solvent was removed via evaporation.

[0030] Yield 82%,; Tg of final copolymer = 22°C; Mn = 7640; Mw = 17620; Mw/Mn = 2.31 ; final polymer concentration = 71.7%; viscosity < 600 cps. APPLICATION EXAMPLE

[0031 ] 26, 1 g of the resulting copolymer was dissolved in 17.9 g of butyl acetate, and then blended with 22.3 g of titanium oxide. The mixture was mixed for 1 hour by a paint shaker, then subsequently mixed with 14.8 g of DESMODUR BL4265, and 0.3 g of dibutyl tin dilaurate (1 % concentration). The mixture was then used to coat an aluminum substrate. About 72 hours later, the physical properties of the surface were tested.

[0032] The gloss (ISO 2813) of the surface = 70 (20°C); Hardness (Pencil Test; ASTM D3363) = 3H; Flexibility ( ASTM D4145) = 3T; Adhesion (ASTM D3359) - 5B.

[0033] From the foregoing, it will be appreciated that although specific examples have been described herein for purposes of illustration, various modifications may be made without deviating from the spirit or scope of this disclosure. It is therefore intended that the foregoing detailed description be regarded as illustrative rather than limiting, and that it be understood that it is the following claims, including all equivalents, that are intended to particularly point out and distinctly claim the claimed subject matter.