PROCESSING

BACKGROUND

Technical Field

[0Θ01] This disclosure generally relates to wafer manufacturing, such as wafer manufacturing involving thin film deposition.

Background Art

[0002] Semiconductor manufacturing, like many types of manufacturing, strives to produce more products faster and at higher quality. Over the years, semiconductor manufacturing has become highly automated and is performed in a series of photolithographic and chemical processing steps. These steps can generally be categorized as wafer processing, die preparation, integrated circuit (IC) packaging and IC testing. Of particular relevance is the step of chemical vapor deposition (CVD) or atomic layer deposition (ALD), which is part of wafer processing.

[0003] CVD and ALD are often used to create a thin film on a semiconductor wafer. A gas precursor, often two gas precursors, are released above the substrate surface of the wafer to decompose and/or react on the surface. A growth film can be created by repeatedly exposing the surface to the volatile precursors. With ALD, a purge gas is usually injected between applications of reactant to force the reactive precursor (and/or any byproducts) out of the reaction chamber to ensure nothing unexpected remains in the chamber prior to the next reaction.

[0004] Wafers may be processed one at a time or in a batch process. The term single wafer processing generally means that only one wafer at a time is processed at a given step; the term does not typically mean that only one wafer is being manufactured at a time. In contrast, batch processing can be beneficial when one is looking to produce a large number of identical wafers, perhaps for a computer chip to be sold to the general public, such as for a graphics card or a central processing unit. However, batch processing may impose additional constraints, such as the need for parallel machinery to process all of the wafers during a given step.

[0005] Wafer manufacturing is concerned with producing results that are uniform and repeatable. This is particularly true for batch manufacturing, because higher volumes are being manufactured and a lack of uniformity may lead to a reduced yield, lowered specifications (to allow for higher variability in manufacturing), and difficulty in ramping up production. Because annual sales of semiconductor chips have risen to $200-300 billion per year and continue to grow, even small improvements to manufacturing uniformity can be quite valuable.

[0006] Therefore, a need exists for improved processing of wafers.

SUMMARY

[0007] Systems, apparatuses and method embodiments for batch processing of semiconductor wafers are described herein.

[0008] In an embodiment, an apparatus comprises a vertical arrangement of wafers configured for batch processing. The wafers include at least a first wafer and a second wafer. An injection module is configured to direct gas parallel to a plane of the first wafer. The injection module has an opening configured such that the gas projected from the opening is dispersed substantially evenly proximate to an edge of the first wafer.

[0009] In an embodiment, a method comprises configuring a vertical arrangement of wafers for batch processing. The wafers include at least a first wafer and a second wafer. Ga is projected from an injection module, parallel to a plane of the first wafer, such that the gas disperses substantially evenly proximate to an edge of the first wafer.

[0010] Further features and advantages, as well as the structure and operation of various embodiments, are described in detail below with reference to the accompanying drawings. It is noted that the disclosure is not limited to the specific embodiments described herein. Additional embodiments will be apparent to persons skilled in the relevant art based on the teachings contained herein.

BRIEF DESCRIPTION OF THE DRAWINGS/FIGURES

[0 11] The features and advantages of embodiments of the present invention will become more apparent from the detailed description set forth below when taken in conjunction with the drawings. In the drawings, like reference numbers generally indicate identical, functionally similar, and/or structurally similar elements. The drawing in which an element first appears is indicated by the leftmost digit(s) in the corresponding reference number. [0012] FIG. 1 is a perspective view of an apparatus for batch wafer manufacturing, according to an embodiment.

[0013] FIG. 2 illustrates an issue with a semiconductor manufacturing apparatus after one injection.

[0014] FIG. 3 depicts a timing diagram for injecting gases for batch wafer manufacturing.

[0015] FIG. 4 illustrates an issue with a semiconductor manufacturing apparatus after six injections.

[0016] FIG. 5A is a top view of an apparatus for batch wafer manufacturing with a single angled injector, according to an embodiment.

[0017] FIG. 5B is a perspective view of the apparatus of FIG. 5 A.

[0018] FIG. 6 A is an apparatus for batch wafer manufacturing with multiple injectors, according to an embodiment.

[0019] FIG. 6B is a perspective view of the apparatus of FIG. 6A.

[0020] FIG. 7A is a top view of an apparatus for batch wafer manufacturing with various injector opening shapes, according to an embodiment.

[0021] FIG. 7B is a perspective view of the apparatus of FIG. 7 A.

[0022] FIG. 8 A is a top view of a cutaway pipe with an injector opening that has a tapered angle, according to an embodiment.

[0023] FIG. 8B is a top view of an apparatus similar to FIG. 8A, but with an injector opening that has a rounded edge, according to an embodiment.

[0024] FIG. 8C is a top view of an apparatus similar to FIG. 8B, but with an injector opening that has a different rounded edge, according to an embodiment.

[0025] FIG. 9A is a top view of an apparatus for batch wafer manufacturing with a rectification wing, according to an embodiment.

[0026] FIG. 9B is a perspective view of the apparatus of FIG. 9A.

[0027] FIG. 9C is a perspective view of an apparatus similar to FIG. 9B, but with two rectification wings per wafer, according to an embodiment.

[0028] FIG. 1 OA is a top view of an apparatus for batch wafer manufacturing with a nozzle, according to an embodiment.

[0029] FIG. 10B is a perspective view of the apparatus of FIG. 1 OA.

[0030] FIG. 1 1A is a top view of an apparatus for batch wafer manufacturing with multiple pipes and injectors, according to an embodiment.

[0031} FIG. 1 IB is a perspective view of the apparatus of FIG. 1 1 A. [0032] FIG. 12 is a flowchart of a method for batch wafer manufacturing, according to an embodiment.

DETAILED DESCRIPTION

[0033] One difference between batch processing and single wafer processing is how gas is deposited onto the wafer. In single wafer processing, where one wafer at a time is processed, it may be convenient and effective to inject gas from above the wafer, directed at the center of the wafer, such that the gas disperses as it falls to cover the wafer. However, this is not possible in batch processing, where the wafers are generally in a vertical stack (one way to arrange wafers vertically is to load the wafers into a cassette, also known as a boat. The wafer boat may then be moved around a clean room to allow for processing of the wafers). This vertical arrangement means that the gas injectors must be located outside the stack of wafers, i.e., outside of the boat.

[0034] Accordingly, in batch processing, gas is injected from outside the circumference of the wafer boat. However, when doing so, it is unlikely that the gas will evenly and completely cover the wafers. One approach to solve this problem is to spin the wafers during the gas injecting, such that the gas is distributed around the wafer. By rotating the wafers six times, for example, six injections of gas can deposited onto the wafers. Purge gases may be injected in the same manner as reaction gases.

[0035] FIG. 1 depicts a batch processing apparatus 100 for silicon wafers 102. Each wafer 102, which may also be known as a slice or substrate, is often made from silicon crystal. Other wafers 102 may be made from other semiconductor materials, such as gallium arsenide, and combinations such as silicon on insulator. Wafers 102 may be used for purposes other than integrated circuits, such as creating diamonds through chemical vapor deposition. Wafers 102 may be 25.4 millimeters (1 inch) - 300 millimeters in diameter, with 450 mm diameter wafers in early testing. The invention is not limited to the above examples.

[0036] Apparatus 100 includes a pipe 104 that runs vertically alongside the stack of wafers 102. The pipe 104 has a series of injectors 106. The injectors 106 are formed as holes, or openings, in the pipe 104. The pipe 104, or tube, may be formed of quartz (primarily because quartz is impervious to the reaction gases, but also for its strength). The injectors 106 may also be formed of or from quartz. [0037] Gas 108 may flow through pipe 104 and injectors 106 to exit over the wafers 102.

Gas injectors 106 may inject the gas 108 parallel to a horizontal plane 1 10 of the wafers 102 (such horizontal plane 110 being parallel to the surfaces of wafers 102) such that the gas 108 falls down onto the wafers 102. Some of the gas 108 may continue across the wafers 102 and down to an exhaust 1 12.

[0038] In the embodiment of FIG. 1 , an injector module 1 I4A includes the injector

106 A. An injector module 1 14 establishes the path that the gas 108 takes from the pipe 104 to the wafer 102. In the example of FIG. 1, each injector module 1 14 comprises only injector 106. A more detailed discussion of injector modules 114 can be found in the description of the embodiment of FIG. 9A, wherein the injector module 1 14 includes more than just injector 106.

[0039] In a first embodiment shown in FIG. 2, the gas injector 106A disperses gas 108A towards the center 202 A of the wafer 102A. The gas 108 A is dispersed with an angle of approximately 40° relative to the plane 1 10 of wafer 102A. As depicted, the gas 108A is most concentrated near the injector 106A and dilutes (or disperses) as the gas 108A crosses the wafer 102 A.

[0040] FIG. 3 depicts a timing diagram 302 for injecting gases 108 where batch processing apparatus 100 is an atomic layer deposition apparatus. Vertical dashed lines separate each cycle, labeled 1 ^st , 2 ^nd and 3 ^rd . As discussed below, FIG. 4 shows the gas distribution over wafer 102A after six cycles. FIG. 3 depicts that the 1 ^st cycle is divided into four parts, where reaction gas A is released into the chamber, followed by purge gas, then gas B, and so forth. As depicted, the process repeats each cycle.

[0041] Atomic layer deposition (ALD) is a process to deposit conformal thin films onto a surface, such as a wafer 102. ALD deposits films by repeatedly exposing a growth surface to precursors. Because ALD deposits a set amount of material for each reaction, ALD is self-limiting. ALD is similar to chemical vapor deposition, except that ALD exposes the surface to precursors one at a time, i.e., it breaks a reaction in half. Keeping precursors separate allows for a thinner film to be deposited. ALD separates the precursors by using a purge gas in between the precursors. ALD is sometimes known as "molecular layering."

[0042] FIG. 4 depicts a second embodiment for dispersing gas 108 to wafers 102. In

FIG. 4, the injector 106A has injected gas 108A six times (per timing diagram 302), such that the six injections have overlapped each other as the gas 108 A from each injection settled on the wafer 102 A. The sum of the settled gas 108 A has formed a six pointed gas blob on the wafer 102A. In this embodiment, gas 108A was injected a first time, and then the wafer 102A was rotated, and this was repeated 5 more times. In FIG. 4, gas 108 A was dispersed with an angle of approximately 90° along the plane 110 of wafer 102A. As also depicted in FIG. 4, the settled gas 108 A is more concentrated towards the edge 402 A of wafer 102 A than at the center 202 A of wafer 102 A. However, there is area near the edge 402A that has not been exposed to gas 108A. In sum, the embodiments of FIGS. 2 and 4 do not result in full and even coverage of gas 108 on wafers 102. In the following, additional embodiments are described that solve these shortcomings and result in more even and complete gas 108 dispersal over wafers 102.

[0043] FIG. 5A depicts an embodiment similar to FIG. 2. In FIG. 5A, however, the injector 106 A is angled away from the center 202 A of the wafer 102 A. One advantage of directing the injector 106A away from the center 202 A and towards the edge 402A of the wafer 102A is that the gaps in gas dispersion seen in FIG. 4 are more likely to be mitigated.

[0044] FIG. 5B illustrates how the techniques of FIG. 5A may be applied to a vertical arrangement of wafers 102. FIG. 5B shows that an injector 106 may be angled towards the edge 402 either by rotating the pipe 104 (e.g., installing the pipe 104 such that the injector holes 106 are at the specified angle relative to the centers 202 of the wafers 102), or by building the injectors 106 such that the injectors 106 are angled away from the centers 202 when the pipe is installed in a standard fashion.

[0045] FIG. 6A depicts another embodiment to disperse gas 108 over a wafer 102A.

FIG. 6A depicts two injectors 106A1 and 106A2 that direct gas over wafer 102A. In some embodiments, a similar amount of gas 108 is collectively projected through the two injectors 106A1 and 106A2 as would have been delivered through a single injector 106 A (see, for example, FIG. 5 A). In the embodiment of FIG. 6A, gas 108 A may not travel as far across wafer 102 A relative to the embodiment of FIG. 2 because there is less gas 108A to disperse through each injector hole 106A1, 106A2, or because there is less pressure on the gas 108A (as the combined size of the injector openings is larger). In an embodiment, more than two injector holes are used, such as a horizontal line of small holes on pipe 104, to release gas 108A.

[0046] FIG. 6B illustrates how the technique of FIG. 6A may be applied to a vertical arrangement of wafers 102.

[0047] FIG. 7A depicts another embodiment, wherein injector 106A has an oval opening or a rectangular opening, as opposed to the circular openings illustrated in FIG. 1. One advantage of either an oval or a rectangular shaped opening is that either, if placed with the long side parallel to plane 1 10, allows gas 108A to escape such that it more evenly distributes over the wafer 102A because the gas 108A exits the injector 106A with a wider, or more obtuse, angle. FIG. 7B illustrates how the technique of FIG. 7A may be applied to a vertical arrangement of wafers 102.

[0048] FIGS. 8A-8C show embodiments of the injector 106. In particular, FIG. 8A is a top view of a cutaway of the pipe 104 and the injector 106 A. FIG. 8 A uses dotted lines 802 to indicate the gas projection angle of injector 106 of FIG. 2 (wafer 102A, while not drawn to scale, is shown to depict the angle of projection of injector 106).

[0049] Tapered angle 804 in FIG. 8A illustrates how an injector opening may be modified to alter the shape or direction of dispersed gas 108. In the embodiment of FIG. 8 A, the tapering is approximately 45°.

[0050] In the embodiment of FIG. 8B, the injector 106A has a rounded edge 806. A rounded edge 806 may have a similar effect on gas 108 A dispersion as a directed angle 804. In particular, rounded edge 806 may curve through, for example, a half circle, as in FIG. 8B, or a quarter circle, as in FIG. 8C.

[0051] FIG. 9A illustrates another embodiment where the injector module 1 14A includes the injector 106A and a rectification wing 902. The injector 106A is coupled to the rectification wing 902 to disperse gas 108 A over wafer 102 A. According to the embodiment of FIG. 9A, gas 108A follows a path from the pipe 104 through the injector 106A, contacts the rectification wing 902, and then settles on the wafer 102A. The rectification wing 902 is a deflector because it serves to deflect at least some of the gas 108 A after exiting opening 106. In certain embodiments, the rectification wing 902 is configured to deflect all of the gas 108A from the injector 106A. In other embodiments, the rectification wing 902 is configured to deflect a portion of the gas 108A from the injector 106A. In certain embodiments, where there is more than one injector 106 (as shown in FIGS. 6 A and 6B, for example), there may be symmetric rectification wings 902 for each injector 106A1 and 106A2. In other embodiments, there may be a rectification wing 902 for one injector 106A1 but not for another injector 106A2. Rectification wings 902 may be made from materials, such as quartz, that are commonly used to manufacture pipes 104 or other components with the appropriate strength and inertness.

[0052] FIG. 9B illustrates how the technique of FIG. 9A may be applied to a vertical arrangement of wafers 102. In this embodiment, rectification wings 114 are placed off center, relative to the injectors 106, in order to direct more gas 108 towards the edges 402 of the wafers 102 in the opposite direction from the rectification wings 114. Each of the rectification wings 902 are identical and have been placed identically. In other embodiments, rectification wings 902 may be placed differently, or made from different materials.

[0053] FIG. 9C illustrates a different way that the technique of FIG. 9A may be applied to a vertical arrangement of wafers 102. In FIG. 9C, the injector modules 114 each comprises two rectification wings 902. The rectification wings 902 are installed symmetrically to each other, relative to the injector 106, though this may be different in other embodiments. One advantage to non-symmetric rectification wings 114 is that each of two rectification wings 114 may direct gas 108 in different directions.

[0054] FIG. 10A illustrates an embodiment wherein the opening 106A is coupled to a nozzle 1002. Nozzle 1002 may be a jet, laminar, spray or other device that directs, or forms, a spray. In certain embodiments, nozzles 1002 may be made from materials, such as quartz, that are commonly used to manufacture pipes 104 or other components with the appropriate strength and inertness. In certain embodiments, multiple injectors 106 may have identical nozzles 1002, as illustrated in FIG. 10B, or different injectors 106 may have different nozzles 1002.

[0055] FIG. 11A illustrates an embodiment with two pipes 104, each with an injector module 114 comprising an injector 106.

[0056] In the embodiment of FIG. 11 A, wafer 102 A is rotated when gas 108 is projected from injectors 106A1 and 106A2. By rotating the wafer 102A while simultaneously projecting gas 108, it is possible to achieve overlap of the gas over the wafer.

[0057] Two injectors 106A1 and 106A2 in two pipes 104 allow gas dispersal over a wafer 102 with less need for wafer rotation.

[0058] FIG. 1 IB illustrates how the technique of FIG. 1 1 A may be applied to a vertical arrangement of wafers 102. In one embodiment, pipes 104 A and 104B may each carry as much gas 108 as the pipe 104 in FIG. 2. In another embodiment, each pipe 104A and 104B may carry half as much gas 108 as in FIG. 2 (half as much because there are two pipes 104A and 104B, but the same amount of gas 108). Other embodiments may use three or more pipes 104.

[0059] FIG. 12 illustrates an exemplary method 1200 to disperse gas 108 over semiconductor wafers 102 in batch processing. [0060] In step 1202, a vertical arrangement of wafers 102 is configured for batch processing.

[0061] In step 1204, gas 108 is projected to the wafers 102. The gas 108 is projected from injection modules 1 14, parallel to a plane of the wafers 102, such that the gas 108 disperses substantially evenly proximate to an edge 402 of the wafers 102.

[0062] Any of the embodiments disclosed herein may be combined with one another.

For example, the multiple injectors 106 of FIG. 11A may be combined with the nozzles 1002 of FIG. 10A. In another embodiment, the nozzles 1002 of FIG. 10A may be combined with the rectification wings 902 of FIG. 9A. In another embodiment, a nozzle 1002 may be provided with a rectangular opening. In a variation of FIG. 7A, an injector 106 may have an opening that is partially rectangular and partially oval. For example, a non-symmetric opening (such as a semicircle opening integrally coupled to an oval or rectangular opening) may allow an injector 106 to disperse gas 108 in a manner that provides a higher proportion of the gas 108 to land near the edge 402 of the wafer 102 than would otherwise. Further, two or more embodiments may be combined. For example, one apparatus 100 may employ an angled injector 106, as in FIG. 5 A, with a tapered angle 804, as in FIG. 8, such that at least part of the gas 108 will be redirected by a rectification wing 902.

[0063] It is to be appreciated that the Detailed Description section, and not the Summary and Abstract sections, is intended to be used to interpret the claims. The Summary and Abstract sections can set forth one or more but not all exemplary embodiments as contemplated by the inventors, and thus, are not intended to limit the appended claims in any way.

[0064] Embodiments have been described above with the aid of functional building blocks illustrating the implementation of specified functions and relationships thereof.

Alternate boundaries can be defined so long as the specified functions and relationships thereof are appropriately performed.

[0065] The breadth and scope of the present disclosure should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.