USING LOW PURITY STARTING PRECURSORS

CROSS REFERENCE TO RELATED APPLICATIONS

[001] This application claims the benefit of and priority to the filing date of U.S provisional application Ser. No. 62/676,043 filed May 24, 2018, incorporated herein by reference in its entirety. This application is related to U.S. Application Serial No. 15/362,993 entitled LITHIATED TRANSITION METAL OXIDES, issued on October 3, 2017 as U.S. Patent, 9,780,356, incorporated herein by reference in its entirety. This application is also related to U.S. Application Serial No. 16/143,453 filed September 27, 2018, entitled ELECTROPLATING TRANSITIONAL METAL OXIDES, published on April 4, 2019 as U.S. Pat. Pub. 2019/0100850 Al, incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

[002] The present disclosure relates to a method for electroplating (or electrodeposition) a lithiated transition metal oxide composition using low purity starting conventional (e.g. LiOH) and unconventional precursors (e.g. Li ₂ S0 ₄ and LiCl). The final product i.e. lithiated transition metal oxides (LTMOs) can be used in fuel cells, structural components, super capacitors, metal- air, primary and secondary Li-ion batteries.

[003] Lithium ion batteries (LIBs) have spurred great interest in the realm of energy crisis owing to their high energy densities. They are comprised of a cathode, which host Li ions, a Li- ion containing electrolyte, a separator and an anode in which Li-ions can be intercalated / alloyed into and de-intercalated / de-alloyed from. [004] One of the widely used commercial methods to manufacture lithium ion active material uses the active material (i.e. graphite, LiCo0 ₂ ), which is mixed with conductive agent (e.g. super P, carbon black, acetylene black) and polymeric binder (e.g. polyvinylidene fluoride). These components are homogenized together in N-methyl pyrrolidone (NMP) to form a slurry. This slurry is cast on a two-dimensional substrate (typically Al or Cu foils) and dried. This widely used method has several critical drawbacks. The use of NMP as the carrier solvent during homogenation requires the recapture of this toxic solvent during drying, leading to additional initial capital costs as well as ongoing recurring costs. Furthermore, this coating process yields electrodes with high interfacial resistance between the poorly conductive active materials, and propensity to delaminate at high mass loading. Electroplated LTMOs can be synthesized and formed into electrodes, which is currently a multi-step process, in just one step (see U.S. Patent No. 9, 780,356 B2, Lithiated transition metal oxide, issued October 3, 2017 to Huigang Zhang, John D. Busbee, Hailong Ning, Thuy D. Dang, Kevin A. Arpin; and Electroplating lithium transition metal oxides, Huigang Zhang, Hailong Ning, John Busbee, Zihan Shen, Chadd Kiggins, Yuyan Hua, Janna Eaves, Jerome Davis, Tan Shi, Yu-Tsun Shao, Jian-Min Zuo, Xuhao Hong, Yanbin Chan, Shuangbao Wang, Peng Wang, Pengcheng Sun, Sheng Xu, Jinyun Liu, and Paul V. Braun, Science Advances, Vol. 3, no. 5, el602427, 2017). This method doesn’t use toxic NMP, and therefore, does not require the expensive solvent recapturing step required for traditional slurry casting methods.

[005] The synthesis of LTMOs, both industrially and academically, are produced at high temperature (800-1100 °C) (see U.S Patent No. 5,885,544, Lithium cobaltate based positive electrode-active material for lithium secondary cell and method of manufacturing same, issued March 23, 1999 to Nobuyuki Yamazaki, Kathuyuki Negishi, and Solid-State Redox Reactions of LiCo02 (R3m) for 4 Volt Secondary Lithium Cells, Tsutomu Ohzuku and Atsushi IJeda, ./. Electrochem. Soc., Vol. 141, No. 11, November 1994). As a result, high purity (> 99%) starting materials are required to ensure that there are no inclusions of secondary materials in the final product that can lead to performance degradation and safety issues. The fundamental mechanism of the electrodeposition process described herein enables the use of low purity starting materials, down to 50% purity, for a wide range of starting materials and impurities.

SUMMARY OF THE INVENTION

[006] In the present invention, a novel approach is described which aims to decrease the production cost of LTMOs by using low cost / low purity raw materials. In addition, the use of low purity precursors could enable various new raw material sources that are unusable, without considerable purification (and cost), for traditional LTMOs manufacturing. The purification of high purity raw materials to synthesize LTMOs typically requires the use of toxic chemicals and energy intensive processes, which in turn add considerable cost to the final price of the Li-ion battery. Up until now, all commercially available lithium metal oxide production methods such as solid state, wet, sol-gel etc. are required to use at least 98% purity Li and 95% purity transition metal precursors (see Ultrathin Coatings on Nano-LiCo0 ₂ for, Isaac D. Scott, Yoon Seok Jung, Andrew S. Cavanagh, Yanfa Yan, Anne C. Dillon, Steven M. George, and Se-Hee Lee, Nano Lett., 2011, 11 (2), pp 414 418) which are responsible for a significant portion of the final battery cost. In addition, conventional solid-state synthesis methods do not utilize Li ₂ S0 ₄ and LiCl precursors as Li source because their anions (S0 ₄ ² and CT) are not stable and react with LTMOs during high temperature heat treatment of LTMOs (see Improvement of Structural Stability and Electrochemical Activity of a Cathode Material LiNi0.7Co0.3O2 by Chlorine Doping, Xinlu Li, Feiyu Kang, Wanci Shen, Xinde Bai, Electrochemica Acta, 53, 2007, 1761- 1765). Due to this side reaction, conventional techniques to manufacture LTMOs utilize mainly LiOH.H ₂ 0, LiOH, Li ₂ C0 ₃ , LiN03, Li(CHOOCH3) as their Li source (see. Lithium Recovery from Aqueous Resources and Batteries: A Brief Review, Ling Li, Vishwanath G. Deshmane, M. Parans Paranthaman, Ramesh Bhave, Bruce A. Moyer, Stephen Harrison, Johnson Matthey Technol. Rev., 2018, 62, (2), 161-176). This patent application therefore demonstrates new routes to synthesize LTMOs with unconventional starting Li and transition metal precursors such as LiCl, Li ₂ S0 ₄ , and CoCl _2.

[007] Electroplating is an element specific technique that can be used to manufacture LTMOs as demonstrated by U.S. Patent No. 9, 780,356 B2 Lithiated transition metal oxide, issued October 3, 2017 to Huigang ZHANG, John D. BUSBEE, Hailong Ning, Thuy D. Dang, and Kevin A. Arpin, incorporated by reference herein in its entirety. The aim of the’356 patent was to describe the method of plating LTMOs from a molten salt eutectic without any disclosure as to the required raw material purity. The foundation of the current invention is to demonstrate the ability to use low purity starting materials from both conventional and unconventional Li and transition metal (TM) sources to create high purity LTMOs from a molten salt eutectic. To our knowledge, reports of the synthesis of high purity LTMOs from low purity raw materials (50% - 95%) have not been reported. The method described herein demonstrates that high purity LTMOs that perform as good as or in some cases better than traditional LTMOs can be synthesized and formed into an electrode from starting materials with purities as low as 50%. This technology should enable the direct use, or require only preliminary purifications, of some common ores (e.g., spodumene lithium-aluminum-silicate) and some common lithium containing brines. Low purity salts don’t require extensive multiple processing steps, energy expenditure, water consumption, and stringent high starting purity requirements. As a result, the financial cost is lower, the economic impact is lower and the processing speed is faster. Applicants have taken advantage of the previously patented technology by Xerion Advanced Battery Corp. (XABC) to overcome cost challenges associated with Li and TM refinement processes. The electroplating solution is non-aqueous and comprised of eutectic points of one of the several Li precursors (LiOH, Li ₂ S0 ₄ , LiCl ₃ , LiN0 ₃ , Lil, LiBr) with KOH being the major constituents of the eutectic bath. Depending on the desired final LTMO, a transition metal source (Co, Mn, Ni, Al, Fe, Cu, Zn, V, Ti) is also added to the eutectic bath.

[008] One of the embodiments of this invention was demonstrated by synthesizing LiCo0 ₂ particles from a eutectic bath which contained low purity (85% purity) LiOH. In this example, the low purity LiOH material was prepared by mixing 98% purity LiOH (impurity 1 : 1 Li ₂ C0 ₃ & Li ₂ S0 ₄ per manufacturer) with other commonly found impurities that were specified by the manufacturer (namely Li ₂ S0 and Li ₂ C0 ₃ ). In addition to these major impurities there are other impurities present in Li ₂ S0 and Li ₂ C0 _3. These impurities are at the ppm level and can be following elements based on the specification sheet provided by the vendor: Ca, Cd, Co, Cr, Cu, Fe, K, Mg, Mn, Na, Ni, Pb, Zn, S0 -, Cl- and N0 _3. In this example, three-dimensional stainless- steel fibers (SSF), cobalt wire and Ni foil were used as the working electrode, reference electrode and counter electrode, respectively. These three electrodes are immersed into the molten salt and multiple 1.2V (versus cobalt wire reference electrode) potential pulses were applied. The pulse range is from 100 ps to 20s. (see U.S. Patent No. 9, 780,356 B2, Lithiated transition metal oxide, issued October 3, 2017 to Huigang Zhang, John D. Busbee, Hailong Ning, Thuy D. Dang, and Kevin A. Arpin incorporated by reference herein in its entirety). Various characterization methods were employed to verify the characteristics of the LTMO, and demonstrates the physical and electrochemical properties are identical and/or superior in some cases compared to material synthesized using conventional high temperature methods. This demonstrates that starting with 85% purity LiOH highly pure LCO can be made, which is elaborated in below. Applicants have also run elemental Sulphur analysis of the final LCO electrodes prepared from both 98% and 85% purity of Li ₂ S0 ₄ using X-ray florescence and did not find any Sulphur within the detection limit of the instrument. Extensions of this embodiment were also carried out using various purities of the lithium source while maintaining the standard purities of the two other bath constituents CoOH (97%) and KOH (85%). We successfully demonstrate that various purities of LiCl (85-50%) and LiS0 ₄ (85%), and finally various purities of the TMO (e.g. 85% CoOH) can be used in the method of the present invention. The details of the specific impurities will be found in the“Detailed Description of the Invention.”

BRIEF DESCRIPTION OF THE DRAWINGS

[009] Figure 1. Cyclic voltammetry of LiOH (98%)/KOH, LiOH (90%)/KOH, LiOH (85%) /KOH baths containing Co(OH) ₂ at 5mV/s scan rate at 260 °C.

[010] Figure 2. XRD patterns of electroplated LiCo0 ₂ powders obtained from LiOH (98%)/KOH, LiOH (90%)/KOH, LiOH (85%) /KOH eutectic baths containing Co(OH) _2.

[011] Figure 3. HRSEM figure of LiCo0 ₂ particles obtained from LiOH (98%)/KOH, LiOH (90%)/KOH, LiOH (85%) /KOH eutectic baths containing Co(OH) _2.

[012] Figure 4A. Discharge profiles of LiCo0 ₂ cathode active materials obtained from LiOH (98%)/KOH, LiOH (90%)/KOH, LiOH (85%) /KOH eutectic baths containing Co(OH) _2. The cells were cycled between 4.25 and 3 V at C/5 rate.

[013] Figure 4B. dQ/dV plot along with its charge-discharge profile for LiCo0 ₂ cathode obtained regular LiOH/KOH eutectic bath containing Co(OH) _2. [014] Figure 5. Cyclic voltammetry of LiCl (97%)/KOH, LiCl (85%)/KOH, LiCl (70%)/KOH, LiCl (50%)/KOH baths containing Co(OH) ₂ at 5mV/s scan rate at 320 °C.

[015] Figure 6. Discharge profiles of LiCo0 ₂ cathode active materials obtained from LiCl (97%)/KOH, LiCl (85%)/KOH, LiCl (70%)/KOH, LiCl (50%)/KOH baths containing Co(OH) ₂ at 320 °C. The cells were cycled between 4.25 and 3 V at C/5 rate.

[016] Figure 7. Cyclic voltammetry of Li ₂ S0 ₄ (98%)/KOH and Li ₂ S0 ₄ (85%)/KOH baths containing Co(OH) ₂ at 5mV/s scan rate at 350 °C.

[017] Figure 8. Discharge profiles of LiCo0 ₂ cathode active materials obtained from Li ₂ S0 (98%)/KOH and Li ₂ S0 (85%)/KOH baths containing Co(OH) ₂ at 350 °C. The cells were cycled between 4.25 and 3 V at C/5 rate.

[018] Figure 9. Cyclic voltammetry of LiOH/KOH baths containing 98% pure Co(OH) ₂ and 85% pure Co(OH) ₂ at 5mV/s scan rate at 260 °C.

[019] Figure 10. Discharge profiles of LiCo0 ₂ cathode active materials obtained from LiOH/KOH baths containing 98% pure Co(OH) ₂ and 85% pure Co(OH) ₂ at 260 °C. The cells were cycled between 4.25 and 3 V at C/5 rate.

[020] Figure 11. Cyclic voltammetry of LiOH/KOH baths containing 95% pure Co(SO) at 5mV/s scan rate at 260 °C.

[021] Figure 12. Discharge profiles of LiCo0 ₂ cathode active materials obtained from LiOH/KOH baths containing 98% pure Co(OH) ₂ and 95% pure Co(SO) at 260 °C. The cells were cycled between 4.25 and 3 V at C/5 rate.

DETAILED DESCRIPTION OF THE INVENTION [022] In general, the present invention relates to a method of forming a lithiated transition metal oxide comprising the steps of (a) immersing a working electrode into a non-aqueous electrolyte comprising a lithium source and a transition metal source, wherein the lithium and transition metal source are both of low purity; (b) electrodepositing a lithiated transition metal oxide onto a surface of the working electrode from the electrolyte at a temperature in excess of the melting temperature of the non-aqueous electrolyte; (c) removing the working electrode from the bath and; (d) rinsing the electrodeposited lithiated transition metal oxide.

[023] In a preferred embodiment, the electrodeposition is done by applying a constant voltage ranging from 0.6V to 1.4V versus Cobalt wire reference electrode or by applying constant current ranging from luA/cm2 to l00A/cm2, or applying a voltage and/or current pulses intermittently.

[024] In a preferred embodiment, the low purity lithium source is selected from the group consisting of LiOH, Li ₂ C0 ₃ LiF, LiCl, LiBr, Lil, LiN0 ₃ , LiN0 ₂ , Li ₂ S0 ₄ , and combinations thereof.

[025] In a preferred embodiment, the low purity transition metal source is selected from the group consisting of MnCl ₂ , MnS0 ₄ , Mn ₂ 0 ₃ , Mn0 ₂ , Mn ₃ 0 , CoO, Co ₂ 0 ₃ , Co ₃ 0 , CoOH ₂ , CoCl ₂ , CoS0 , and combinations thereof.

[026] The low purity lithium and transition metal sources have a purity ranging from about 50% to about 98% by weight, more preferably from about 50% to about 95% by weight, and most preferably from about 50% to about 85% by weight.

[027] Preferably the non-aqueous electrolyte comprises an inorganic molten salt, wherein at least 50%, and preferably 99% of the ions comprised by the inorganic molten salt electrolyte are inorganic ions. The inorganic molten salt electrolyte can comprise a hydroxide salt, a halide salt, a nitrate salt, a sulfate salt or a combination thereof. In a preferred embodiment, the inorganic molten salt electrolyte comprises a hydroxide salt selected from the group consisting of LiOH, KOH, NaOH, RbOH, and CsOH, a halide salt selected from the group consisting of LiCl, LiF, KF, KC1, NaCl, NaF, LiBr, NaBr, KBr, Li I, Nal, KI, a nitrate salt selected from the group consisting of L1NO3, NaN0 ₃ , and KN0 ₃ , a nitrite salt selected from the group consisting of LiN0 ₂ , NaN0 ₂ , KN0 ₂ , a Li ₂ S0 ₄ sulfate salt, and combinations thereof.

[028] In one embodiment, the inorganic molten salt electrolyte comprises a nitrite salt selected from the group consisting of LiN0 ₂ , NaN0 ₂ , KN0 ₂ , and combinations thereof.

[029] In another embodiment, the inorganic molten salt electrolyte comprises a hydroxide salt selected from the group consisting of LiOH, KOH, NaOH, CsOH, and combinations thereof.

[030] In another embodiment, the inorganic molten salt electrolyte comprises a Li ₂ S0 ₄ sulfate salt.

[031] The electrodeposited lithiated transition meal oxide is preferably conformally coated onto the working electrode. In a preferred embodiment, the working electrode is a three-dimensional porous nanostructured structure. The three-dimensional porous working electrode preferably has a void volume fraction (porosity) between 1% and 99%.

[032] The working electrode comprises an electrically conductive material selected from the group consisting of metals, metal alloys, metallic ceramics, electrically conductive carbon, electrically conductive polymers, and electrically conductive composite materials. In a preferred embodiment, the working electrode is a metal or metal alloy selected from the group consisting of aluminum, copper, chromium, cobalt, manganese, nickel, silver, gold, tin, platinum, palladium, zinc, tungsten, tantalum, rhodium, molybdenum, titanium, iron, zirconium, vanadium, and hafnium, and the alloys thereof. [033] In another preferred embodiment, the working electrode is a planar foil with thickness ranging from lum to lOOmm or a porous foam with porosity ranging from 1% to 99% porosity.

[034] The thickness of the electrodeposited lithiated transition metal oxide preferably ranges from about lOnm to about 500p The electrodeposited lithiated transition metal oxide material can also be in the form of a powder, and wherein the powder can be scraped off.

[035] The electrodeposition is carried out at relatively low temperatures ranging from 100 °C to 600 °C. Preferably, the electrodeposition temperature is from about 300°C to about 500 °C.

[036] The electrodeposition can be carried out in an ambient or an inert atmosphere.

[037] In a preferred embodiment, the electrodeposited lithiated transition metal oxide is lithium cobalt oxide characterized by an XRD spectrum containing a doublet peak at approximately between 63 and 70 2Q degrees.

[038] Electroplating of a lithiated transition metal oxide was carried out using a 3 -electrode system where a working electrode, a counter (Ni foil), and a pseudo reference (Co metal) electrode were immersed into a eutectic solution, which is also called a molten salt, containing a transition metal and Li ions source. Preferably, the transition metal source comprises an oxide, hydroxide, halide or sulfate of at least one transition metal. The transition metal can be aluminum, copper, chromium, cobalt, manganese, nickel, silver, gold, tin, platinum, zinc, tungsten, tantalum, rhodium, molybdenum, titanium, iron, zirconium, vanadium, hafnium, and the alloys thereof. The Li source can be LiOH, Li ₂ S0 ₄ , LiCl, Lil, LiBr, L1NO3, LiN0 ₂ , LiNO and mixtures thereof.

[039] The eutectic system can provide a relative low synthesis temperature (100° - 800° C). The eutectic temperature is known as the melting point which is lower than any composition made up of the mixture. Above the eutectic temperature, the liquid phase is generally called molten salt. For electrodepositing on a working electrode, a molten salt system should have low temperature to protect the working electrode and possess high solubility of transition metal sources. Low-temperature molten salt is usually selected by checking the eutectic points in the phase diagrams. Molten salt bath is prepared with at least one of chemicals including hydroxides (KOH, NaOH, RbOH, CsOH etc), halides (KF, KC1, NaCl, NaF, NaBr, KBr, Nal, KI, AlCl ₃ etc), nitrate (NaN0 ₃ , KN0 ₃ ), nitrite (NaN0 ₂ , KN0 ₂ ), and sulfates (Na ₂ S0 ₄ , K ₂ S0 ₄ ). The Ni crucible was used as the reaction vessel and glass lid was used to hang the abovementioned electrodes into the eutectic solution. All three electrodes were connected to a power supply which provides sufficient voltage or current densities where electrochemically active lithiated transition metal oxide materials were produced. These materials are of great interest to the Li-ion battery industry. Figure 1 shows the cyclic voltammetries (CVs) of several KOH/LiOH molten salt systems containing different percentages of LiOH impurities (98%, 90% and 85%) which all of the baths contain CoOH ₂ species as Co source. The 90% and 85% pure LiOH powders were prepared by grinding appropriate percentages of Li ₂ C0 ₃ and Li ₂ S0 with 98% pure LiOH. As can be seen from CV profiles, in all cases Co ²⁺ ions start to be oxidized at relatively similar potentials i.e. 0.7V. All three profiles in Figure 1 resemble each other suggesting that there are most likely no electrochemically active impurities present during electroplating. The sharp increase in current appearing above 1.2V is due to the oxidation of OH- groups originating from KOH and LiOH salts which are the major components of the molten salt. To further support this, the inset figure in Figure 1 also shows the CV of the KOH/LiOH bath without the presence of Co source which demonstrates that there is only one oxidation peak which corresponds to anion oxidation. The potentials shift after Co oxidation is minor which could be due to the water content of the molten salt. As seen in Figure 1 (inset) the eutectic bath is stable for plating LiCo0 ₂ nano-flakes to 1.4 V vs. Co/Co ²⁺ . We found the optimum voltage pulse to be 1.2V versus Co reference electrode. All voltage values are reported versus Co/Co ²⁺ pseudo reference electrode. As can be seen from Figure 2, all LiCo0 ₂ powders have very similar XRD patterns irrespective of the starting material impurity percentages. They all possess R3m phase of layered structure and have similar lattice parameters. Every diffraction peak can be assigned to Joint Committee on Powder Diffraction Standards (JCPDS) card no 50-0653 indicating that the materials made from these impure starting materials are crystallographically identical to standard lithium cobalt oxide. Of particular importance, the presence of the doublet peak in all patterns around 65-70 2Q degrees suggest that layered feature of the crystal structure is preserved regardless of the impurity percentages. High resolution scanning electron microscopy images exhibited in Figure 3 shows that the LiCo0 ₂ particles have very similar morphological features. This set of images demonstrates that the raw material impurities present in LiOH do not affect the morphology of the final product.

[040] In one example, l20g of KOH, 20g LiOH, and 5g CoOH ₂ are added to the bath and monitored that they are dissolved thoroughly. The color of the melt changed from transparent color to blue as the divalent Co ²⁺ ions are coordinated by hydroxide ions. This is followed by immersing the 3-electrode lid into the molten salt. Afterwards, 1.2V (versus cobalt wire reference electrode) potential pulses were applied. The pulse range is from lps to 20s where a SSF, Ni foil and Co wire are used as working, counter, and pseudo reference electrodes, respectively. Between pulses, there was an open circuit voltage period (ranging from lps to 60 minutes). This resting period allows ions to move into the voids of SSF thereby conformal deposition is achieved. Number of deposition cycles (duty cycle refers to on/off time) determines the loading of the sample. Constant voltage or current densities will also lead to the formation of the metal oxide however the electroplated material will not cover the 3D substrate conformally. Nevertheless, one can use this method to obtain powder form of the lithiated metal oxide. By simply changing the transition metal to a Mn source, one can also produce Li _x Mn _y O _z material.

[041] After electroplating LiCo0 ₂ on the working electrode, the electrode quickly is rinsed with deionized water thoroughly to ensure no residual KOH or LiOH salts remain. Since CoOH ₂ is not soluble in water, a chelating agent, such as citric acid, would help to dissolve Co ²⁺ . If CoOH ₂ traces are not removed, during heat treatment this would form Co ₃ 0 ₄ particles that are not formed during electroplating. Removal of Co ²⁺ ions can be simply done by immersing the lithiated transition metal oxide electrode into an approximately 0.4M citric acid aqueous solution for 1 minute.

[042] In one experiment, we employed stainless steel fibers (SSF) as the 3D scaffold working electrode. The plating procedure is as follows: 1.2V (versus Co/Co ²⁺ ) voltage pulses for ls on- time followed by 2 minutes rest between each voltage pulses. This ensured ions to diffuse inner pores of 3D scaffold leading to conformal LCO plating. Approximately, 20 cycles of these pulse plating procedures resulted in a 2mAh/cm ² loaded electrodes with around l45mAh/g specific capacities, standard values in the literature. The electrochemical performances of the LiCo0 ₂ electrodes were tested and discharge profiles of LiCo0 ₂ obtained from different purity of LiOH precursor were plotted in Figure 4A. The coin cell was constructed with LiCo0 ₂ cathode deposited onto SSF versus Li foil and separated with a commercially available 20um polymer separator. The electrolyte was a traditional LiPF ₆ dissolved in organic solvents. All of the LiCo0 ₂ electrodes in Figure 4A delivered very identical capacities (~l45mAh/g) and voltage profiles resemble each other well. This electrochemical data further proves that neither 85% nor 90% pure LiOH have any negative effect on the characteristic of LiCo0 ₂ electrochemical discharge profile. Figure 4B exhibits charge-discharge capacities of the LiCo0 ₂ electrode obtained from a regular molten salt bath. The plateaus indicated with the circles in Figure 4B are indicative of a high level of crystallinity. During charging at 4.06V and 4.18V regions, a phase transformation takes place concomitant with the removal of Li ions from monoclinic and hexagonal phases, respectively (see Microemulsion-based synthesis and electrochemical evaluation of different nanostructures of LiCo02 prepared through sacrificial nanowire templates, Gautam Ganapati Yadav, Anand David, Huazhang Zhu, James Caruthers and Yue Wu, Nanoscale, 2014, 6, 860). These regions are considered a direct correlation with the quality of LiCo0 ₂ powders. Good crystallinity is desired as it is responsible for good performance characteristics like lifetime and high temperature storage resistance.

[043] In another example, Figure 5 shows the cyclic voltammetries (CVs) of several KOH/LiCl molten salt systems containing different percentages of LiCl impurities (97%, 85% 70% and 50%) in which all of the baths contain CoOH ₂ species as Co source. The bath temperature was set to 320 °C and the plating procedure was as follows: 1.2V (versus Co/Co ²⁺ ) voltage pulses for ls on-time followed by 2 minutes rest between each voltage pulses. This ensured ions to diffuse inner pores of 3D scaffold, SSF working electrode, leading to conformal LCO plating. Approximately, 20 cycles of these pulse plating procedures resulted in a 2mAh/cm ² loaded electrodes with around l45mAh/g specific capacities, bode well with the standard values in the literature. The 85%, 70% and 50% pure LiCl powders were prepared by mixing appropriate percentages of NaCl, KC1 and CaCl with 97% pure LiCl. These impurities were selected as LiCl is usually refined through brines which contain alkali chloride ions heavily (see Extraction of lithium from primary and secondary sources by pre-treatment, leaching and separation: A comprehensive review, Pratima Meshram, B.D. Pandey, T.RMankhand , Hydrometallurgy 150 (2014) 192 208). The weight percentages of the impurities were set as NaCl/KCl/CaCl w/w 1/0.5/0.5, respectively. The Pt foil working electrode is employed to evaluate if there are any side reactions stemming from impurities of LiCl precursors. As can be seen from CV profiles, in all cases Co ²⁺ ions oxidize at relatively similar potentials i.e. 0.6V. All three profiles in Figure 1 resemble each other suggesting that there are most likely no electrochemically active impurities present during electroplating. The intensity of the oxidation peak around IV could correspond to complexed [Co(OH) ₆ ] ⁴ and appears to decrease as the impurity percentages increase due to some cation hindrance. This however does not affect the final product as will be discussed below. From these results the eutectic bath is stable for plating LiCo0 ₂ up until 1.4 V vs. Co/Co ²⁺ . We find the optimum voltage pulse to be 1.2V versus Co reference electrode. All voltage values are reported versus Co/Co ²⁺ pseudo reference electrode. As can be seen from Figure 6, discharge capacities of LiCo0 ₂ electrodes obtained from different impurity ranges of LiCl delivered identical values which was around l45mAh/g. The voltage profiles also resembled each other suggesting that NaCl, KC1 and CaCl impurities do not have adverse effect on LiCo0 _2.

[044] In another example, Figure 7 shows the CVs of two K0H/Li ₂ S0 ₄ molten salt systems containing different percentages of Li ₂ S0 ₄ impurities (98% and 85%) in which both of the baths contain CoOH ₂ species as Co source. The bath temperature was set to 350 °C and the plating procedure was as follows: 1.2V (versus Co/Co ²⁺ ) voltage pulses for ls on-time followed by 2 minutes rest between each voltage pulses. This ensured ions to diffuse inner pores of 3D scaffold, SSF working electrode, leading to conformal LCO plating. Approximately, 20 cycles of these pulse plating procedures resulted in a 2mAh/cm ² loaded electrodes with around l45mAh/g specific capacities, standard values in the literature. The 85% pure Li ₂ S0 powders were prepared by mixing appropriate percentages of Al ₂ 0 ₃ and Si0 ₂ with 98% pure Li ₂ S0 _4. Al ₂ 0 ₃ and Si0 ₂ were reported as common impurities of Li ₂ S0 ₄ in literature. These impurities were selected as Li ₂ S0 is usually refined through an ore which contains spodumene, known as lithium- aluminum-silicate (see Extraction of lithium from primary and secondary sources by pre treatment, leaching and separation: A comprehensive review, Pratima Meshram, B.D. Pandey, T.R.Mankhand, Hydrometallurgy 150 (2014) 192 208). The weight percentages of the impurities were set as Al ₂ 0 ₃ /Si0 ₂ w/w 1/1, respectively. In addition to these two major impurities there are other impurities present in Li ₂ S0 _. These impurities are at the ppm level and consisted of the following elements: Ca, Cd, Co, Cr, Cu, Fe, K, Mg, Mn, Na, Ni, Pb, Zn and C1-. The Pt foil working electrode is employed to evaluate if there are any side reactions stemming from impurities of Li ₂ S0 precursors. As can be seen from CV profiles, in all cases Co ²⁺ ions start to oxidize at relatively similar potentials i.e. 0.6V. All three CV profiles in Figure 7 resemble each other suggesting that no electrochemically active impurities are present during electroplating. From these results the eutectic bath is stable for plating LiCo0 ₂ nano-flakes to 1.4 V vs. Co/Co ²⁺ . We find the optimum voltage pulse to be 1.2V versus Co reference electrode. All voltage values are reported versus Co/Co ²⁺ pseudo reference electrode. As can be seen from Figure 8, discharge capacities of LiCo0 ₂ electrodes obtained from different impurity ranges of Li ₂ S0 delivered identical values which is around l45mAh/g. The voltage profiles also resembled each other suggesting that Al ₂ 0 ₃ and Si0 ₂ impurities and other ppm level of impurities do not have adverse effect on LiCo0 _2.

[045] In another example, Figure 9 shows the CVs of two KOH/LiOH molten salt systems containing different purity percentages of Co(OH) ₂ impurities (98% and 85%) in which the bath temperature was set to 260 °C and the plating procedure was as follows: 1.2V (versus Co/Co ²⁺ ) voltage pulses for ls on-time followed by 2 minutes rest between each voltage pulses. This ensured ions to diffuse inner pores of 3D scaffold, SSF working electrode, leading to conformal LCO plating. Approximately, 20 cycles of these pulse plating procedures resulted in a 2mAh/cm ² loaded electrodes with around l45mAh/g specific capacities, standard values in the literature. The 85% pure Co(OH) ₂ powders were prepared by mixing 98% Co(OH) ₂ powders with the appropriate percentages of C0SO ₄ and Mg(OH) ₂ , commonly found impurities in Co(OH) ₂ (see Processing Considerations for Cobalt Recovery from Congolese Copperbelt Ores, B Swartz, S. Donegan, S. Amos, Hydrometallurgy Conference 2009, The Southern African Institute of Mining and Metallurgy, 2009 ). The weight percentages of the C0SO ₄ and Mg(OH) ₂ impurities were 1/1. The Pt foil working electrode is employed to evaluate if there are any side reactions stemming from impurities of Co(OH) ₂ precursors. As can be seen from CV profiles, in all cases Co ²⁺ ions are started to be oxidized at relatively similar potentials i.e. 0.6V. All three CV profiles in Figure 9 resemble each other suggesting that no electrochemically active impurities are present during electroplating. From these results the eutectic bath is stable for plating LiCo02 nano-flakes to 1.4 V vs. Co/Co ²⁺ . We find the optimum voltage pulse to be 1.2V versus Co reference electrode. All voltage values are reported versus Co/Co ²⁺ pseudo reference electrode. As can be seen from Figure 10, discharge capacities of LiCo0 ₂ electrodes obtained from different impurity ranges of Co(OH) ₂ delivered identical values which is around l45mAh/g. Voltage profiles, an indication of structural integrity, also resembled each other suggesting that CoS0 and Mg(OH) ₂ impurities and other ppm level of impurities do not have adverse effect on LiCo0 _2.

[046] In another example, Figure 11 shows the CVs of two KOH/LiOH molten salt systems containing low purity (95% pure) percentage of Co(SO) in which the bath temperature was set to 260 °C and the plating procedure was as follows: 1.2V (versus Co/Co ²⁺ ) voltage pulses for ls on-time followed by 2 minutes rest between each voltage pulses. This ensured ions to diffuse inner pores of 3D scaffold, SSF working electrode, leading to conformal LCO plating. Approximately, 20 cycles of these pulse plating procedures resulted in a 2mAh/cm ² loaded electrodes with around l45mAh/g specific capacities, standard values in the literature. The Pt foil working electrode is employed to evaluate if there are any side reactions stemming from impurities of Co(SO) ₄ precursors. As can be seen from CV profiles, in all cases Co ²⁺ ions are started to be oxidized at relatively similar potentials i.e. 0.6V. CV profile in Figure 11 resemble CoOH ₂ based eutectic bath suggesting that CoS0 ₄ can also be utilized as Co source. As can be seen from Figure 12, discharge capacities of LiCo0 ₂ electrodes obtained from different Co source, namely CoOH ₂ and CoS0 delivered identical values which is around l45mAh/g. Voltage profiles, an indication of structural integrity, also resembled each other suggesting that using either CoOH ₂ or CoS0 do not have adverse effect on LiCo0 _2.