SUITABLE FOR HOT COMESTIBLE APPLICATIONS

FIELD

[0001] The present application relates to microencapsulated materials, such as for use in hot foods and beverages, and methods for their manufacture. More particularly, the microencapsulated materials include functional ingredients in an enteric matrix further coated with enteric materials which are suitable for use in hot foods and beverages and which release functional ingredients in a user's intestines.

BACKGROUND

[0001J Enteric delivery of functional materials in food applications has been limited.

Enteric delivery systems are commonly utilized when the functional materials or medicaments are known to be sensitive to certain conditions such that they become less effective or if the functional materials cause problems for the user, such as stomach problems with aspirin.

Further, enteric delivery systems are commonly utilized when the functional materials or medicaments are known to be sensitive to low pH or have undesirable flavor and /or taste characteristics which cannot be effectively masked by other methods.

[0002] Generally, enteric delivery, as most common in pharmaceutical practice, is accomplished by coating tablets and gel capsules. However, those particular delivery methods are not well suited for food applications. In particular, neither tablets nor capsules are sized to be integrated into most existin food products.

[0003] An alternative process for enteric delivery is microencapsulation. However, one issue with microencapsulation is the recovery rate, or microencapsulation efficiency of the process. Generally, a certain significant percentage of the material to be microencapsulated is not captured. The uncaptured material may be recovered for reuse, recycled, or a percentage of the uncaptured material remains adhered to the outer surface of the microencapsulated particulates,

[0Q04J In the situation where uncaptured material remains adhered to the

microencapsulated particles, the product tends to have a taste profile associated with the uncaptured material, which is often undesirable. This is particularly true when the uncaptured material includes oxidizable triglycerides such as unsaturated and polyunsaturated lipids, oxidizable flavors and essential oils, or other organic compounds that may naturally have strong undesirable taste and/ or flavor. For example, functional ingredients, such as essential oils, are known to possess health benefits and protect against intestinal parasites. However, one limitation of incorporating essential oils into foods and beverages is their strong pungent smell and taste.

[0005] Further, there have been a number of previous attempts at developing enteric delivery of functional ingredients, such as essential oils, for use at ambient and cold

temperature. In one form, these materials may be provided in the form of powdered beverages. However, such systems fail to provide protection and taste masking at a temperature above about 35°C as the enteric delivery system fails at elevated temperatures. For example, as the powdered beverage is hydrated and heated to form a hot beverage, the enteric materials used to contain the functional ingredients degrade, thereby releasing the functional ingredients prematurely, such as when the beverage is being prepared and /or when the beverage is introduced into a user's mouth, in this regard, the user may perceive any undesirable taste profiles of the functional ingredient. Moreover, if the functional ingredient is susceptible to degradation, such as in the user's stomach, the functional ingredient may not provide sufficient delivery of the desired beneficial effects.

SUMMARY

[0006] it has unexpectedly found that microencapsulated materials may be manufactured which are suitable for use in higher temperature foods and beverages, while still providing acceptable enteric delivery properties. For example, functional ingredients, such as essential oils may be microencapsulated into an enteric matrix. Further, a coating of an enteric material may be applied.

[0007] in one form, a microencapsulated composition for use in hot foods and beverages is provided. The composition includes a core, a first coating and a second coating. The core includes a functional ingredient and a enteric material to microencapsulate the functional ingredient within a matrix of the enteric material. The enteric material includes sodium caseinate and soy protein. The first coating substantially surrounds the core and includes zein. The second coating substantially surrounds the first coating and includes ethylcellulose. {0008] According to one form, the enteric material consists essentially of sodium caseinate and soy protein,

[0009] In accordance with one form, the core includes about 1 to about 80 wt.% of sodium caseinate and about 1 to about 80 wt.% soy protein, each on a dry basis of the core ingredients,

[0010] In one form, the composition has a moisture content of less than about 5 wt.%.

[0011] According to one form, the composition comprises about 1 to about 70 wt.% sodium caseinate and about 1 to about 70 wt.% soy protein, each on a dry basis of the total composition ingredients.

[0012] In accordance with one form, the composition comprises about 1 to about 19 wt,% zei on a dry basis of the total composition ingredients.

[0013] In one form, the composition comprises about 1 to about 19 wt.% ethyleellulose on a dry basis of the total composition ingredients.

[0014] .According to one form, the functional ingredient comprises essential oils.

[0015] In accordance with one form, a method of forming a multi-coated precipitate of a microencapsulated composition for use in hoi foods and beverages is provided. The method includes the steps of: agitating a combination of water and an enteric material at an appropriate pH to solubilize the enteric material, the enteric material including soy protein and sodium caseinate; adding a functional ingredient to the combination; mixing the combination and the functional ingredient to create an emulsion; titrating the emulsion with a cross-linking or precipitating agent in an amount effective to form a particulate precipitate including a matrix of the enteric material microencapsulating the functional ingredient; separating and drying the particulates; coating the particulate precipitate with a first coating including zein to form a coated particulate precipitate; and coating the coated precipitate with a second coating including ethyleellulose to form a multi-coated particulate precipitate.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] FIG. 1 is a diagrammatic representation of an enteric material including a core and a plurality of coatings; [0017] FIG. 2 is a process flow diagram illustrating one form of a method for producing enteric materials;

[0018] FIG. 3 is a graph illustrating the release of functional components from various core materia! combinations while at a pH of approximately 5.3;

[0019] FIG. 4 is a graph illustrating the release of functional components from various core material combinations while at a pH of approximately 6.3; and

[0020] FIG. 5 is a graph illustrating in vitro digestion and release of functional components from various core material combinations over time.

DETAILED DESCRIPTION

[0021] Disclosed is a microencapsulated composition including a functional ingredient and a method for manufacture. Generally,, the composition includes one or more enteric materials as well as one or more coatings that can be used in combination to delay the release of the functional ingredient prior to dissolution in the intestine. Such a combination of features may be suitable for use in a comestible which can be prepared as a hot comestible, such as a hot beverage. As used herein, the term "hot comestible" i cludes foods, drinks arid the like which are prepared and/or served at a temperature in a range of about 25 to about 80°C. In one form, the temperature range is from about 40 to about 70°C.

[0022] Generally, it should be u derstood that the term ' ^" 'matrix" refers to a type of encapsulation that is somewhat different from traditional "true encapsulation" which has a single functional material coated by the encapsulating material. Matrix encapsulation is generally directed to a three dimensional material which may be spherical, semi-spherical and the like, with multiple active particulates, liquids and/or solids distributed and/or embedded throughout the matrix particle. For example, in one form, the matrix includes a plurality of oil droplets are dispersed throughout the matrix material. ^' Therefore, the matrix particle may include a plurality of oil droplets dispersed in the matrix material. In one form, the matrix may stabilize and/or protect the functional ingredients within. The matrix particle may then be encapsulated with one or more coatings.

[0023] As shown in. FIG. 1, one form of a microencapsulated material 10 is shown. In one form, the microencapsulated material 10 includes a core 12, a first coating 14 and a second coating 16, It should be noted that the microencapsulated material 10 may include any number of coatings suitable for providing a composition which is suitable for use in hot comestibles. Further, it should be noted that the microencapsulated material 10 may take a variety of shapes, including irregular shapes.

[0024] The core 12 generally may include a number of different components, such as a functional ingredient, a non-active carrier,, one or more enteric materials and the like.

According to one form, the selection of materials for the core 12 may be such that the core 12, by itself, has enteric properties. For example, the core 12 may include functional ingredients such as essential oils, non-active carriers such as lipids and enteric materials such as soy protein and sodium caseinate. According to one form, the core includes about 1 to about 80 wt.% soy protein and about 1 to about 80 wt.% sodium caseinate, both on a dry weight basis of the core ingredients. In another form, the core includes about 20-60 wt.% of each of the soy protein and sodium caseinate. In one form, soy protein may be provided in an amount of about 1 to about 70 wt. % relative to the o verall microencapsulated material 10 and the sodium caseinate may be provided in an amount of about 1 to about 70 wt. % relative to the overall microencapsulated material 10. In another form, the overall microencapsulated material 10 may include 10-60 wt.% of each of the soy protein and sodium caseinate. Further, the core 12 may include a ratio of about 1:2.5 to about 1:3.5 of the functional ingredient to the combination, of the soy protein and sod i u m ca se i nate.

[0025] Other materials may be included in the core 12 as will be discussed below in more detail and as found in the examples provided herein. The core 12 may take a variety of forms, including, but not limited to core capsules. In one form, the core 12 may have enteric properties, but may not provide sufficient protection for the core 12, such as when used in a hot comestible.

[0026] The first coating 14 may include a variety of different materials, including, but not limited, to enteric materials. For example, in one form, the first coating 14 includes zein.

According to another form, the first coating 14 includes an aicohol-based zein (which generally refers to a binary solvent of alcohol and water). The first coating 14 may be provided in a variety of amounts and thicknesses as desired. For example, in one form, the first coating 14 includes about 1 to about 25 wt. % zein on a dry basis of the total composition. In another form. the first coating 14 includes zein such that zein is provided in an amount of about 5 to about 19 wt% relative to the total microencapsulated material 10. It should be noted that other materials may be included in the first coating 14 as will be described below in more detail and as found in the examples provided herein.

[0027] The second coating 16 may also include a variety of different materials, including, but not limited to enteric materials. For example, in one form, the second coating 14 includes ethyiceJlulose. The second coating 16 may be provided in a variety of amounts and thicknesses as desired. For example, in one form, the second coating 16 includes about 1 to about 25 w ethyiceliuiose on a dry weight basis of the total composition. In another form, the second coating 16 includes ethyiceliuiose such that ethyiceliuiose is provide in an amount of about 5 to about 19 w % relative to the microencapsulated material 10. It should be noted that other materials may be included in the second coating 16 as will be described below in more detail and as found in the examples provided herein. In one form, the second coating has a melt point of greater than about 10G°C

[0028] in one form, the composition a)' be composed of core capsules containing proteins such as sodium caseinate and soy prepared at their isoelectric point. The core microcapsules may then be coated with a unique combination of food grade, enteric polymers. According to one form, the first coating is prepared from a binary solvent (alcohol/ water) based zein solution, and the second coating is also prepared from a binary solvent (alcohol/ water) based ethyiceliuiose (EC). It is believed that the combination of the two coatings with the core materials may be used to provide improved taste/ flavor masking, especially when used in hot comestibles. For exa le, ethyiceliuiose generally may be used as a very good moisture barrier as it is relatively insoluble in water, and has a high glass transition temperature (Tg) of greater thai about 100°C. In addition to the excellent moisture barrier and high Tg, ethyiceliuiose may also f unction to provide a delayed release of the functional ingredient, in other words, ethyiceliuiose may be provided as the second coating, such as an outermost coating, to thereby provide thermal protection and also protection when the comestible is being prepared due to its solubility properties.

[0029] Zein may be used as the first coating, which in an inner coating that is otherwise protected by ethyiceliuiose as the second coating. The zein may be used to provide a more controlled enteric release of the functional ingredient at the desired pH when ingested by the user.

[0030] As used herein, "functional ingredient" generally refers to any non-polar, wafer insoluble or immiscible liquid, such as essential oils, functional oils, oil solubles and any other functional material,

[0031] The functional ingredient can include any mixture of hydrophobic liquids and solids, such as solids mixed or combined therewith or dissolved or solubilized therein, As an example, functional ingredients can be selected to include materials which are desired to be released in the small intestine rather than the stomach due to pH sensitivity. As an example, the functional ingredient can include compositions described in U.S. Patent Publication No. 2008/0145462 to Enan. For instance, the f unctional ingredient includes about 25 to about 35% by weight para-cymene, about 1 to about 10% by weight linalool, about 1 to about 10% by weight alpha-pinene, about 35 to about 45% by weight thymol, and about 20 to about 30% by weight soybean oil.

[0032] In particular, the functional ingredient described herein can include an essential oil blend which possesses anti-parasitic properties. n one embodiment., the essential oil blend is organic compounds blended with food grade oil, i.e. soybean, oil. Further, the organic compounds can include thymol and linalool. In a further embodiment, the organic compounds include alpha-pinene and para-cymene. One exemplary blend of an essential oil includes, by- weight, about 17.5 percent soybean oil, about 8 percent alpha-pinene (liquid), about 44 percent para-cymene (liquid), about 5 percent linalool (liquid) and about 25,5 percent thymol (crystal). In another embodiment, the functional ingredient may also include modified forms of the hydrophobic liquid, as described in provisional Patent Application Serial No. 61/4.22,439, filed December 13, 2010, which is incorporated herein in its entirety b reference. In yet another embodiment, the hydrophobic liquid includes esters, such as esters of linalool and thymol, as described in Application Serial No. 12/479,444, filed Tune 5, 2009, which is incorporated herein in its entirety by reference. Another exemplary form includes about 10 wt.% para-cymene, 5 wt.% alpha-pinene, 15 wt. %. linalyl acetate, and about 70 wt.% th myl octanoate.

[0033] The functional ingredient: can include a portion which is modified, such as by esterification, and can comprise from about 1 to about 99 percent of the functional ingredient by weight. In some approaches, the modified functional ingredient can include from at least about 10 percent of the functional ingredient by weight and, in other approaches, about 30 percent by weight, in another embodiment, the modified functional ingredient can include from about 25 to about 65 percent of the functional ingredient by weight.

[0034] In one embodiment, the blend of non-active carrier and functional ingredient can include, by weight, about 15 to about 30 percent canola oil, about 1 to about 10 percent alpha pinene, about 5 to about 25 percent para-cymene, about 5 to about 20 percent linalyl ester and about 20 to about 60 percent thymyl ester. In other approaches, the blend of non-active carrier and functional ingredient can include, by weight, about 20 to about 25 percent canola oil, about 2 to about 7 percent alpha pinene, about 10 to about 20 percent para-cymene, about 7 to about 15 percent l inalyl ester and about 35 to about 50 percent thymyl ester.

[0035] By one approach, the selected esterified form of the functional ingredient may have increased functionality due to an increased rate of hydrolysis over the parent form after ingestion and release from the enteric matrix in an intestinal tract. Esters may be obtained from natural sources or synthesized using any suitable chemical or biochemical reactions between functional ingredients, such as thymol and linaiool, and organic or inorganic oxoacids that yield esters. Suitable oxoacids may include carboxylic acid, amino acids, phosphoric acid, sulfuric acid, and nitric acid. The hydroxy! group can be derived from, a homogenous source (e.g., thymol) or mixed source (thymol and linaiool). Exemplar}'- monocarboxylic acids include, but are not limited to, acetic, propionic, butyric, pentanoic, hexanoic, octanois, decanoic, stearic, lactic, cinnamic, pyruvic, benzoic, and gluconic acids. Exemplary tricarboxylic acids include, but are not limited to, oxalic, malorue, maleic, fumaric, tartaric, succinic, glutaric, giucaric, adipic, pimelic, suberic, azelak, and sebacic acids. Exemplary tricarboxylic acids, include, but are not limited to, citric and isocitric acids. Other exemplary esters that may be formed by reactions of terpenes with oxoacids include dithymoJ succinate, dithymoJ adipate, and dithymol sebacate.

[0036] In another form, the modified functional ingredient can include an ester formed, regardless of chemical or biochemical reaction approach for its preparation, between terpene esters and other esters. In particular, the functional group can be formed using transesterifkation. For example,, the functional grou can include an ester formed by reacting thymol acetate with methyl octanoate or tripalmitin.

{0037] Alternatively, it is anticipated that the functional ingredient can include other modified compounds. In one form, the modified functional group can include any glycoside formed by chemical or biochemical reaction between the hydroxy! group (s) of a terpene and a single sugar group (monosaccharide) or several sugar groups (oligosaccharide). For example, thymol and/ or linalool glycosides can be the modified functional ingredient. The sugar group can Include any glycoside with the glycone portion composed of mono, di, tri , and/ or polysaccharides of any kind and the aglycone portion being any hydro y-terpene (e.g., thymol, linalool). The sugar group can also include reducing sugars and /or non-reducing sugars. Exemplary sugars include, but are not limited to, glucose, fructose, galactose, ribose, sucrose, mannose, maltose, lactose, and cellobiose.

[0038] In another form, it is anticipated that the functional group can include any ionic or nonionic salt or complex formed involving a hydroxy-terpene and another chemical species. For example, thymol and linalool salts or complexes can be the modified functional ingredient. One example may be sodium and/ or potassium salts. In another form, the modified functional ingredient may include thymol salts that do not have fixed stoichiometrics. For example, thymol salts may be prepared as partial or mixed salts having different ratios of cations and thymol comprising one or more specific cations (Na+, K , Mg++, etc.) to prepare solid- complexes. The solidified complexes may or may not be obtained in crystalline form. The salt or complex may be formed by any suitable method, but in some cases is formed by a chemical reaction, or association between one or more hydroxy-terpene and one or more alkaline reagent. Exemplary alkaline reagents may include, but are not limited to, alkaline hydroxide, oxide, or carbonate. The salt or complex can include any alkali metal, alkaline earth metal, or transition metal element, or combination thereof. Suitable salts or complex for use in foods may include those formed from sodium, potassium, lithium, calcium, magnesium, iron, manganese, zinc, and aluminum. Other exemplary salts include any mono, di, or trivalent salt of thymol, including sodium thymolate (e.g., sodium thymoxide) and any mono, di, or trivalent salt of phenol, includ n calcium phenoxide. [0039] Furthermore, the functional ingredient may include various forms of modification that are combined. For example, a portion of the modified functional ingredient composition may i ciucie one or more of salts, glycosides, complexes and esterified forms of one or more essential oils.

[0040] Modifications to the functional ingredient may include a variety of forms that modify the perceived taste arid/or organoleptic properties of the functional ingredient. For example, the modification, may cause a change to the flavor and/ or taste threshold of the functional ingredient. In one form, the modification causes a change to the volatility and/or vapor pressure of the modified functional ingredient with respect to the non-modified, parent form of the functional ingredient. In. particular, the organoleptic properties of the modified form may include a higher taste threshold. As a result, in some cases a modified functional ingredient on the surface of the enteric matrix may produce a less undesirable flavor profile than the presence of unmodified functional ingredients. Further, the modifications may include salt, glycoside, complex and /or esterification of the functional ingredient.

[0041] When ingested and released in the intestinal tract, the modified form of the functional ingredient reverts back, at least in. pari, into the parent form and provides the same functional benefits as if the parent functional ingredient was microencapsulated and consumed, In one form, the modified functional ingredient hydrolyzes from the modified form back into the parent, non-modified form of the functional ingredient during digestion.

[0042] in some approaches, the functional ingredient described herein can include compounds which possess functional properties, such as anti-parasitic, anti-protozoan, and anti-fungal. In one embodiment, the organic compounds further include alpha-pinene and para-cymene.

10043] Other suitable examples of a materials which may be included in the core include unsaturated and polyunsaturated OMEGA 3, other unsaturated and polyunsaturated lipids or fatty acids and triglycerides thereof, beta-carotene, and oil soluble vitamins, stomach irritants, or any other hydrophobic materials that are either sensitive to acidic pH conditions or impart strong undesirable taste. [0044] Due to the low water solubility and/or increased hydrophobicity, an ester may have higher microencapsulation efficiency, such as described above., than non-esterified parent compounds, such as thymol and linalool. Preferably, the efficiency increases about 50 to about 200 percent: over the efficiency observed when using non-esterified functional ingredients, more preferably about 100 to about 150 percent. Further, esters have a higher olfactory perception threshold than the parent compounds, such that amount of esters necessary to be perceived is more than the amount of non-esterified thymol and linalool.

[0045] Methods are provided for microencapsulating one or more function ingredients therein. One method for microencapsulating a functional ingredient is generally described in FIG. 2. As shown in FIG. 2, water, an enteric material and optionally an emulsifier are subjected to agitation until the enteric material and emulsifier are combined with the water to form a solution, such as at step 20. Generally, the emulsifier and enteric material can. be added to the water together or separately, with either being added first. In some cases, the pH of the solution is generally greater than 7, and generally greater than about 7.1 to about 9. In other cases, a base, such as sodium, ammonium or potassium hydroxide, carbonates, bicarbonates and combinations thereof, can be added to the solution to maintain the pH greater than 7, and in yet other cases from greater than 7 to about 9 to maintain dissolution of the enteric polymers in water substantially free of organic solvents.

[0046] The functional ingredient is then added to the enteric material solution, such as at step 30. 'The enteric material solution containing the functional ingredient is then mixed, such as at step 40. In one form, the materials are agitated or mixed to form an emulsion. By one approach, "agitation" or ^" 'agitated" generally refers to the use of a top mixer with impeller or a rotor /stator mixing device operating at a speed of less than about 10,000 RPM. Other mixing devices may also be employed.

[0047] After mixing, the materials are then acid titrated to precipitate out the functional ingredient microencapsulated with the enteric material, such as at step 50, in a matrix core structure that is generally tiny droplets of functional ingredients substantially homogeneously dispersed in the matrix material. Next, the first coating is applied to the microencapsulated functional ingredient, as shown in step 60. After the first coating is applied, a second coating may be applied, such as shown in step 70. It should be noted that additional coatings may be included beyond the first and second coatings. Optionally, the coatings may include a small amount of a suitable plasticizer, such as one that is soluble/ misdble in water.

[0048] As shown at step 50, the material is titrated with add in an amount effective to decrease the pH below the isoelectric or solubility point of the enteric materials causing phase separation and inducing precipitation of the enteric material out of solution with the functional being microencapsulated therein, thus creating a slurry of an aqueous solution and precipitate. The slurry includes a particulate precipitate having a particle size from about 1 to about 1.000 micrometers, in some cases about 10 to about 500 micrometers, and in yet other cases from about 75 to about 250 micrometers, in some approaches, precipitation occurs at a pH ranging from about 3 to about 6.5, and in other approaches from about 3 to about 5, and in one approach at a pH of about 4.5. in the method illustrated in FIG. 2, in order to maintain the enteric properties of the particulate precipitate, the fine, stable emulsion of sodium caseinate and soy protein may be titrated with an acid to a pH correspondi ng to the insolubility at the isoelectric point of sodium caseinate, such as about 4.4 to about 4.6. In some approaches, the slurry may be allowed to settle, resulting in a clear division of the liquid or supernatant and the settled particulate,

[0049] While not wishing to be limited by theory, it is believed that as the pH of the emulsion drops below the solubility point, enteric materials, such as soy protein and sodium caseinate may cross-link to like particles or to one another to form a matrix, the hydrophobic liquid being microencapsulated within the matrix. As a result of the cross-linking, the functional ingredient is homogeneously dispersed throughout the matrix. The matrix further provides a seal for the functional ingredient. As a result, the impact of the functional ingredient on the organoleptic qualities of the finished product is generally correlated to any functional ingredient remaining adhered to the outer surface of the enteric material that is not coated.

[0050] The acid used for step 50 can be any acid, including, but not limited to, food grade acid. In one approach, the acid is a weak food grade acid. For example, the acid may be citric acid.

[0051] As noted above, the composition of the enteric material affects the dissolution rate and the protection provided by the enteric matrix. As a result, the rate and amount of acid addition varies based on the enteric matrix materials used, [0052] To reclaim the precipitate, the slurry may be optionally filtered to produce a wet cake, then washed and dried to produce a dried cake, in some approaches, the particulate and the supernatant are both filtered to produce a cake, then washed and dried to provide a dried cake. In another approach, the shiny or supernatant and particulate are filtered to provide a wet cake. The wet cake is then washed, refiitered and rewashed prior to drying. In some approaches, the surface oil on the outer surface of the particulate precipitate is less than about 1 percent by weight of the final product.

[0053] Each solution to prepare the first and second outer coatings can include about 5 percent to about 20 percent enteric material and about 1. percent to about 3 percent plasticizer including, but not limited to, glycerin and other suitable plasticizers, The final, coated microencapsulated particles can include between about 1 to about 15 percent by weight of each of the first and second coatings.

[0054] The coating materials can be applied to the enteric matrix by mixing, spraying or other suitable application. In one approach, the coating materials are first solubilized in water. A base can optionally be added to the solubilized outer coating material to increase the pH to greater than 7, in some cases between about 7.1 and about 12. The solubilized material can then be atomized and sprayed onto the uncoated particulate product.

[0055] In some instances, the first and second coatings each have coating thicknesses of about 1 micrometer to about 5 micrometers. If desired, the coated matrix particles can then be sieved to meet the desired particle size.

[0056] Additional processing steps after the second coating may also be included. For example, such steps may include drying and/ or otherwise removing moisture from the coated microcapsules to form a material having less than about 10%, and, in some forms, less than 5% moisture.

[Θ057] In one instance, the coating materials are applied by spraying a fine mist of the respective coating onto fluidized core capsules to create a uniform particle coating. Such a process can include top and/or bottom spraying. In one form, such a process can combine simultaneous layer coating with instant drying. [0058J Other steps may also be included, such as grinding the dried material to form a powder. Further, other intermediate steps may also be included in the process. For example, such steps may include, but are not limited to, washing the microencapsulated material to remove unencapsula ed functional ingredients, pH adjustments and the like. In one embodiment, a surface oil remover may be added to aid in removing residual surface oil from the precipitate, as described in co-pending Application Serial No. 12/479,433, filed June 5, 2009, which is incorporated herein in its entirety by reference. Further, the surface oil remover can also be added at an point in the preparation after acid titrating.

[0059] Further, the powder can be pulverized to red uce the particle size of the powder precipitate, and then further dried to a moisture content of less than about 5 percent, such as with a fluidized bed dryer. By one approach, the resultant particles have a particle size ranging from about 1 to about 1000 micrometers, in some approaches from about 10 to about

500 micrometers, and in other approaches from about 75 to about 250 micrometers.

[0060] When drying the powder, the temperature may be maintained between about 25°C to about 70°C n some approaches between about 35°C to about 60°C and in other approaches between about 35°C and about 45°C, During other processing steps, the temperature may be maintained between abou 4°C to about 40°C, in some cases about: 4°C to about 30°C, and in other cases from about 15°C to about 28°C.

10061] According to one form, the core is substantially free of organic solvents. As used herein, "substantially free of organic solvent" generally refers to an amount of added organic solvent, such as isopropanol or ethanol or an other organic solvent, which is less than the amount of organic solvent required to enable solubilization of the enteric material under the processing conditions. Preferably, the amount of added organic solvent is less than about 0.1 percent by weight of the combination of wafer, emulsifier and enteric material. As used herein, "organic solvent" generally refers to a non-aqueous, hydrocarbon-based liquid.

[0062J The enteric material used herein is any food grade enteric polymer, or a

combination or two or more food grade enteric polymers. In one form, the enteric material is a caseinate, such as sodium caseinate, soy protein or a combination thereof. [0063] Other enteric materials that may he included in the core include shellac and zein. The shellac can be provided as an alkaline (pH > 7) aqueous solution, such as a water-based solution having a solid content of about 25 percent by weight or it can he prepared from refined, bleached and dewaxed shellac powder. The shellac is substantially free of organic solvent, although it may contain, trace amounts of organic solvents, such as isopropyl alcohol (such as can be included in commercial products),, to act as a carrier for other ingredients in the shellac solution, such as methyl and propyl p ra bens. Preferably, the prepared shellac solution does not contai any added organic solvents.

[0064] In one approach, the enteric material consists essentially of soy protein and sodium caseinate. It should be noted that soy protein and sodium caseinate may not be thought of as traditional enteric materials. However, when the soy protein and sodium caseinate are prepared near their isoelectric points, the materials take on enteric functionality such that they would be considered enteric materials.

[0065] The enteric matrix material and optional emulsifier may be solubilized in. water, in one form alkaline water, substantially free of an organic solvent. However, it has been discovered that the combination of the soy protein and sodium caseinate provides an emulsif i cation capability so that the addition of an emulsifier is not required in this approach. . Further, the combination of soy protein and sodium, caseinate improves stability of the resulting microencapsulated functional ingredient over the duratio of the shelf life of the

microencapsulated functional ingredient. In one approach, the so protein and sodium caseinate are solubilized separately in separate aqueous solutions and then combined in a single solution. In some cases, a desired ratio of soy protein to sodium caseinate ranges from about 1:60 to about 60:1 in other cases the ratio ranges from about 1:10 to about 10:1 and in yet other cases the ratio ranges from about 2:1 to about 1:2

[0066] The emulsifier described herein is any food grade emulsifier. In one form, the emulsifier is polysorbate, polyglycerol ester, sucrose stearate, sucrose esters, proteins, lecithins or combinations thereof.

[0067] The methods described herein combine water, an optional emulsifier, the enteric materials and the functional ingredient in a manner effective to microencapsulate the functional ingredient in the enteric materials. Generally, the methods use water in amounts from about 50 percent to about 95 percent of the combination by weight and, in some approaches, from about 70 to about 95 percent, and, in other approaches, from about 80 to about 90 percent. The optional emulsifier is generall less than about 5 percent of the combination by weight, in some instances from about 0.01 to about 1 percent by weight, and, in other instances, about 0.01 to about 0.1 percent by weight of the combination. The enteric material ranges from about 3 percent to about 35 percent by weight, in some approaches from about 3 to about 23 percent, and, in other approaches, from about 10 percent to about 15 percent by weight of the combination. The functional ingredient generally is in amounts of about 1 to about 15 percent by weight of the combination, and in other approaches, about: 3 to about 6 percent b weight, as measured in a wet state prior to titration.

|0Θ68] The microencapsulated hydrophobic liquid produced by the above described methods may have an increased payload. Payload generally refers to the weight percentage of the functional ingredients in relation to the final particulate product. The totai payload generally refers to the total weight percentage of all the encapsulated functional ingredients, including the any carrier oil, in relation to the final particulate product. Therefore, an increase in payload corresponds to an increase in functional ingredient per a given amou t of enteric matrix.

[0069] In one form, the product created by the methods described herein may be used for delivery in a powdered soft drink (PSD) beverage. Further, the product created by the methods described herein may be used in a variety of other drinks, such as hot beverages, including, but not limited to, tea, coffee, hot chocolate, and other hot beverages. Other exemplary uses of the product include other food products, such as biscuits, bars, snacks, instant meals and the like.

[0070] Advantages and embodiments of the methods described herein are further illustrated by the following Examples. However, the particular conditions, processing schemes, materials, and amounts thereof recited in these Examples, as well as other conditions and details, should not be contrasted to unduly limit this method. All percentages are by weight unless otherwise indicated, EXAMPLES

[0071] Example 1: This example illustrates one method of preparing microcapsules stable in a hot beverage at temperature of up to 70°C. The core microcapsules are prepared with a 1:1 combination of soy and caseinate proteins. The core material was prepared as found below in Table 1.

[0072] Table 1. Summary of enteric ingredients in core composition.

[0073] Initially, the soy protein and sodium caseinate powder were added to water with overhead mixing. The powders were added slowly with the mixing gradually increasing from low to high speed. Low speed was used initially to avoid excess foaming. The materials were mixed for approximately 30 minutes.

[0074] Next, 5% NaOH solution was added slowly white mixing until the mixture reaches a pH of approximately 9.0. The conditions for the step are as follows: initial pH : 6.90; final pH : 8.99; amount of 5% NaOH - 295.0g.

[0075] Next, approximately 240g of an essential oil blend was added slowly to the vortex. The essential oil blend included the following composition 10 wt.% para-cymene, 5 wt.% alpha- pinene, 15 wt.% linalyl acetate, and about 70 wt.% thymyi octanoate. The material was left to mix for 5 minutes, Therefore, the mixture contained a ratio of about 2,91:1 of the enteric materials (soy protein and sodium caseinate) relative to the essential oil blend.

[0076] After .mixing,, the composition was homogenized at 500/5000 psi in a two-stage homogerdzer. Before homogenizing the mass was approximately 8462.0g while after homogenizing the mass was approximately 8374.2g.

[0077] After homogenizing, the material was titrated with 12% citric acid solution to pH 4.5. The material was then left to mix for 5 - 10 minutes. The conditions for this step are as follows: initial pH : 8,86; final pH : 4.50; amount of 12% citric acid solution = 545.2g. [0078] After titrating with acid, the material is dewatered by pressing the precipitate at 40 psi for 30 minutes. Next, the pressed cake is ground using food processor and then spread in a fl uid bed drier to dry at approximately 60°C. The initial moisture prior to drying was 53.12%. After drying in the fluid bed drier for about 1 hour, the moisture content was below 5%. Final moisture ; 3.74%,

[0079] Next, the dried material is finely ground. The ground material was then sifted to collect a fraction between 100 - 250 μηι. The materials was reground and resifted.

[0080] After grinding, the material is coated. Two layers of coating were applied to the microcapsules. The first coat was zein, and the second coat was ethylcellulose. Coating was performed in a bench mini-Glatt fluid bed coater with a Wuster insert and bottom spray. The compositions of the coatings are shown below in ^' Tables 2 and 3.

[0081] Table 2. Zein coating— Coating solution at 10% zein

Ethanol 200 proo f 157.5g 1 DI Water — ^" 67.5g ί

Zein Powder 25g !

Total 250g j

Table 3- Ethylcellulose coating - - Coating solution at 8.33% EC:

Ethanol 200 proof 247. ¾ j

DI Water 27.5g

EC 4 Standard 12.5g j

EC 10 Standard 12.5g 1

Total ..300S J

[0083] As shown above, EC 4 and EC 10 refer to the viscosities of the respective ethylcellulose materials. For example, when hydrated in a solvent at room temperature, EC 4 has a viscosity of 4 cps while EC 10 has a viscosity of 10 cps. In one form, the viscosity and molecular weight may play a role in the processabiiity and/or functionality. Lower viscosity (lower molecular weight) allows the preparation of high concentrations of coating solutions where the high molecular weight provides a better functionality. Combining the two may allow for achieving both results. {0084] For coating, 200g of the core capsules were loaded into a Mini-Glatt fluid bed coater with a Wurster insert. The powder was fluidized at 0.1-0.3 Bar, Met temperature was set at 60°C. Once the product was warmed up to target temperature of about 30-35°C, the coating material was pumped in at a pump speed of 9 (about 1.2-2.0ml /minute), and nozzle atomization pressure set to 1.5 bars. Coating continued until all of coating solution was applied to achieve 10% for each of the coatings on dry weight basis. At the end, the powder was cooled to ambient temperature and collected for further evaluation.

[0085] Example 2: Example 2 was prepared to compare a core material prepared with just sodium caseinate and not including soy protein in a pilot plant. Approximately 8 060g of RO water was used to hydrate 8540g of sodium caseinate powder. In a vacushear vessel, water was loaded and a vacuum was pulled to maintain the mixing under negative pressure (vacuum) to minimize foaming of the caseinate solution. The caseinate powder was suctioned in slowly while mixing using an overhead mixer. Mixing continued under vacuum until all of caseinate powder was hvdrated. Mixing continued for extra 10 minutes. Caseinate solution was transferred into an open tank using an overhead mixer.

[0086] Next, 2928g of an essential oil blend including 10 wt.% para-cymene, 5 wt.% aipha- pinene, 15 wt.% linaiyi acetate, and about 70 wt.% thymyl octanoate was added slowly to the mixing caseinate solution to create a coarse emulsion. Once complete, the coarse emulsion was pumped through a single stage high pressure homogenize.!' at 8000 psi. A fine emulsion, was collected in. an open tank using an overhead mixer. Therefore, the mixture contained a ratio of about 2.91:1 of the enteric materials (sodium caseinate) relative to the essential oil blend.

[0087] Next, acid titration was performed using 12% citric acid which was pumped into the tank with mixing until solutio reached a pH of 4.5. At this H, the caseinate precipitated out with the essential oils entrapped within the enteric material, forming a slurry.

[0088] The formed slurry was filtered by using a filter bag at 40 psi and the filter cake was collected for further processing. Next,, the cake was coarse ground using a Fitz mill, and then, loaded into a Uni-Glatt fluid bed dryer. The coarse ground material was dried to a moisture below 5% in the fluid bed drier. [0089] The dried powder was reground using a Hammer Mill (Bourmister), then collected powder was sifted and product in the range of 75-250 μχη was collected, and large size material was re-ground and sifted again. The finely ground material was then coated as per Example 1.

[0090] Example 3: Example 3 was prepared to compare a core material prepared with just soy protein and not including sodium caseinate. The composition of the core is provided in Table 4 below.

[00 1J Table 4. Summary of enteric components in core composition.

[0092] Soy powder was hydrated in water with overhead mixing with the soy powder being added slowly, starting with low to high speed. The composition was allowed to mix for 30 minutes. Next, 5% NaOH solution was added slowly while mixing to pH 9.0. Final pH : 8.99; Amount of 5% NaOH - 184.5g. The functional ingredient was added next with 240g of an essential oil blend including 10 wt.% para-cymene, 5 wt. alpha-pinene, 15 wt.% linalyl acetate, and about 70 wt.% thymyl octanoate, being added to the vortex. The solution was left to mix for 5 minutes. The solution was then homogenized at 500/5000 psi. Therefore, the mixture contained a ratio of about 2,91:1 of the enteric materials (soy protein) relative to the essential oil blend ,

[0093] Next, the homogenized solution was titrated with 12% citric acid solution to pH 4,5 and left to mix for 5 - 10 minutes. Final pH : 4.54; Amount of 12% citric acid solution■ 468.3g.

[0094] The resulting precipitate was dewatered by pressing at 40 psi for 30 minutes. The dewatered material was then coarse ground using a food processor and dried. The initial moisture was 56.64% and the final moisture was less than 5%. The same coatings as in Example 1 were then applied.

[0095] Example 4: A similar solution and method as in Example 2 was prepared, except the enteric materials for the core capsules were prepared with a combination of caseinate and shellac (60% caseinate: 40% shellac). Therefore, the mixture contained a ratio of about 2.91:1 of the enteric materials (sodium caseinate and shellac) relative to the essential oil blend. The remaining steps were approximately the same with the same coatings as in Example 1.

[0096] Referring to FIGS, 3-4, the compositions from Examples 1-4 were compared at various pH levels to show the release profiles of the contained functional ingredients. As seen in FIGS, 3 and 4, Example 1, prepared with both soy protein and sodium caseinate in the core had significantly improved performance compared to soy protein alone, sodium caseinate alone and sodium caseinate with shellac. Better performance is shown by a lower % release of the functional ingredient. It should be noted that the total amount of enteric materials in the respective cores were the same. In other words, the total loading of sodium caseinate and soy protein in Example 1 was equivalent to the sodium caseinate in Example 2, the soy protein in Example 3 and the sodium caseinate and shellac in Example 4,

[0097] As seen in FIGS. 3 and 4, both of the examples with just soy protein or fust sodium caseinate had inferior performance compared to the sample with sodium caseinate and soy- protein. This was unexpected as the performance of the combination of soy protein and sod ium caseinate would not be expected to be any better than the equivalent loading of the best performing of the two components when used separately. In other words, sodium caseinate, when used at the set loading, had improved performance compared to soy protein at the same loading and it is unexpected that by replacing a portion, of the better performing sodium caseinate with the inferior performing soy protein, the resulting combination had improved performance over more of both components when used individually.

[0098] Example 5: Example 5 was prepared to evaluate compositions prepared in a hot- beverage, A powdered chocolate type beverage was used as the main beverage material . Water was healed to boil, and then 200ml was poured into a glass. 20g of the powdered chocolate beverage was mixed in. Microcapsules prepared according to Examples 1-4 were each dry- blended with sugar (about 0.5 capsules and 4.5g sugar), The capsules/ sugar blend was added to chocolate beverage at different temperatures to compare any effect temperature may have. The hot beverage was allowed to cool down to drinkable temperature (about 40°C), and taste and analyzed. The preparation was done at two different pH conditions of pH 6,3, and lower phi of 5.3 through the addition of lactic acid. [0099] The amount of essential oil released into the beverage correlates with taste. The higher the amount of essential oil released, the stronger the off taste. It is believed that the taste threshold is estimated at a range of 0.5-1.0%. Release was significantly lower at pH 5.3 than at pH 6.3. Of the microcapsules used, the best results were achieved with the soy and caseinate core combination which showed significantly lower release, even at 70°C. Further, in an informal panel, it was concluded that the product prepared with capsules from Example 1, soy and sodium caseinate, provided the cleanest taste profile. No objectionable off-tastes or flavors were noted.

[00100] E amgle _. 6: The samples from Examples 1-4 were prepared and used in an in vitro digestion model for Example 6 to determine their enteric performance. Capsules were first incubated in gastric juices for 30 minutes, and then in intestinal fluids for 24 hours. Analysis of % release of the functional i ngredients was carried out at 30 minutes for the gastric release, 30 minutes post gastric, arid then every 2 hours in intestinal fluid for up to 6 hours, and then at 24 hours.

[00101] The results are illustrated in FIG. 5. As found in FIG. 5, the sodium caseinate and soy protein core provided suitable release during digestion, After the composition is initially ingested, the material passes through the stomach and eventually on to the intestines, where it is desired that the enteric material release the functional ingredient for delivery. Therefore, the overall composition should provide protection during ingestion and when in the stomach, having a lower release of the functional ingredients as shown in FIGS. 3 and 4, but should also provide proper release of the functional ingredients in the intestines, as found in FIG. 5.

Therefore, as found in FIGS. 3-5, Example 1, prepared with soy protein and sodium caseinate in the core, had improved performance and a lower release during preparation of the comestible and ingestion while maintaining the desired release characteristics in the intestines.

[00102] While the compositions and methods have been particularly described with specific reference to particular process and product embodiments, it will be appreciated that various alterations, modifications, and adaptations may be based on the present disclosure, and are intended to be within the spirit of this disclosure.