FISCHER, Verena (Aichegg 16, Schwanberg, A-8541, AT)
HAJEK, Karin (Willy-Haas-Str. 25, Alfter, 53347, DE)
SCHEIWE, Gerd (Berscheid 3, Rheinbach, 53359, DE)
HAFERKORN, Thomas (Brüder-Grimm-Str. 63, Ingelheim, 55128, DE)
V. WITZLEBEN, Moritz (Hitzelerstr. 97b, Köln, 50968, DE)
IHLE, Jan (Poststr. 11, Deutschlandsberg, A-8530, AT)
FISCHER, Verena (Aichegg 16, Schwanberg, A-8541, AT)
HAJEK, Karin (Willy-Haas-Str. 25, Alfter, 53347, DE)
SCHEIWE, Gerd (Berscheid 3, Rheinbach, 53359, DE)
HAFERKORN, Thomas (Brüder-Grimm-Str. 63, Ingelheim, 55128, DE)
V. WITZLEBEN, Moritz (Hitzelerstr. 97b, Köln, 50968, DE)
WHAT IS CLAIMED IS:
1. Feedstock for injection molding, comprising
- a ceramic filler convertible by sintering into a ceramic with a positive temperature coefficient of its electrical resistance,
- a matrix for binding the filler, the matrix having a melting point lower than the melting point of the ceramic filler, - metallic impurities, wherein the content of the impurities in the feedstock is lower than 10 ppm.
2. The feedstock of the preceding claim, wherein the ceramic filler comprises a material with a structure Bai- x - y M x D y Tii- a - b N a Mn b O 3 , wherein
x = 0 to 0 . 5 , y = 0 to 0 . 01 ; a = 0 to 0 . 01 and b = 0 to 0 . 01 ;
M comprises a cation of the valency two, D comprises a donor of the valency three or four and N comprises a cation of the valency five or six.
3. The feedstock of claim 1, wherein the sintered ceramic comprises a resistivity of 3 ωcm to 30000 ωcm at 25°C.
4. The feedstock of claim 1, comprising a content of the matrix of ≤ 20 percent by mass.
5. The feedstock of the preceding claim, wherein the matrix comprises a material which is chosen out of a group comprising wax, resins, thermoplastics and water soluble polymers.
6. The feedstock of the preceding claim, wherein the matrix additionally comprises at least one component which is chosen from lubricants, plasticizers and anti-oxidants .
7. The feedstock of claim 1, wherein the metallic impurities comprise metals chosen from Fe, Al, Ni, Cr, and W.
8. Method for preparing a feedstock for injection molding, comprising the steps of A) preparing a ceramic filler being convertible to a ceramic with a positive temperature coefficient of the electrical resistance by sintering,
B) mixing the ceramic filler with a matrix for binding the filler, C) producing a granulate comprising the filler and the matrix, whereby in steps A) , B) and C) , tools are employed having a low degree of abrasion such that a feedstock comprising less than 10 ppm of impurities caused by abrasion is prepared.
9. The method of the preceding claim, whereby in step A) base materials of the filler are mixed, calcinated, and ground to a powder.
10. The method of the preceding claim, wherein the base materials comprise BaCO 3 , Tiθ2 Mn-ion containing solutions and Y-ion containing solutions and at least one chosen out of the group SiO 2 , CaCO 3 , SrCO 3 , and Pb 3 O 4 .
11. The method of claim 8, wherein step B) is performed at a temperature in the interval from 40 0 C to 200 0 C.
12. The method of claim 8, wherein in step C) the mixture of the filler and the matrix is reduced to small pieces at room temperature or at an elevated temperature.
13. The method of claim 8, wherein in steps A), B) and C) tools are chosen from a group comprising a twin-roll mill, a single-screw extruder, a twin-screw extruder, a ball mill, a blade-type mixer.
14. The method of the preceding claim, wherein the surfaces of the tools contactable with the ceramic filler comprise a hard coating.
15. The method of the preceding claim, wherein the coating comprises tungsten carbide. |
FEEDSTOCK AND METHOD FOR PREPARING THE FEEDSTOCK
TECHNICAL BACKGROUND
Ceramic materials with a positive temperature coefficient of the electrical resistance (PTC-ceramics) may be processed into molded bodies. With conventional methods such as continuous casting or extrusion, bodies of simple geometries like discs or rectangles can be formed.
The following description relates to feedstocks for PTC- ceramics that can be processed into bodies of complex geometries .
SUMMARY
A feedstock for injection molding is provided. The feedstock comprises a ceramic filler convertible by sintering into a ceramic with a positive temperature coefficient of its electrical resistance (PTC-ceramic) . The feedstock comprises a matrix for binding the filler, the matrix having a melting point lower than the melting point of the ceramic filler. Additionally, the feedstock comprises metallic impurities, the content of which in the feedstock is lower than 10 ppm.
The feedstock is suited to producing bodies containing a PTC- ceramic by injection molding. The feedstock may be processed to create a high variety of injection molded bodies for a variety of applications where the features of PTC-ceramics are needed. The PTC-ceramic has a low resistivity at room temperature, in particular at 25°C. When plotting the resistance of such a PTC-ceramic against temperature in a so called resistance-temperature-curve, the resistance starts to increase at a certain characteristic reference temperature. At temperatures above this reference temperature the resistance of the ceramic shows a steep slope with increasing temperature. Thus, when applying a voltage to a body
containing the PTC-ceramic, the body is heated. To maintain these electrical features of the PTC-ceramic, impurities, especially metallic impurities, are preferably reduced or avoided in the feedstock which is later processed into the PTC-ceramic.
A method for preparing a feedstock for injection molding is also proposed. The method comprises the preparation of a ceramic filler convertible by sintering to a PTC-ceramic. The ceramic filler is mixed with a matrix for binding the filler and the mixture comprising filler and matrix is processed into a granulate. During the preparation of the feedstock, tools contactable with the feedstock are used which have a low degree of abrasion such that a feedstock comprising less than 10 ppm abrasion caused impurities is obtained.
The method enables preparing a feedstock with a low content of impurities. As a result of the at least nearly absent impurities, when the feedstock is injection molded, its electrical properties such as low resistivity and / or steep slope of the resistance-temperature curve are maintained in the molded ceramic body.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 shows the content of metallic impurities of differently prepared feedstocks.
Fig. 2 shows the relation between metallic impurities and resistivities of injection molded bodies prepared from different feedstocks.
Fig. 3 shows resistance-temperature curves of molded bodies prepared from different feedstocks.
DETAILED DESCRIPTION
In one embodiment an injection moldable feedstock with a ceramic filler, a matrix for binding the filler and with a content of less than 10 ppm of metallic impurities comprises a ceramic filler based on Bariumtitanate (BaTiOs) , which is a ceramic of the perovskite-type (ABO3) . The ceramic comprises the structure
Bai-x-yMxDyTii-a-bNaMnbOs
wherein the parameters are defined preferably as follows:
x = 0 to 0.5; y = 0 to 0.01; a = 0 to 0.01 and b = 0 to 0.01.
In this structure M stands for a cation of the valency two, such as for example Ca, Sr or Pb, D stands for a donor of the valency three or four, for example Y, La or rare earth elements, and N stands for a cation of the valency five or six, for example Nb or Sb.
Hence, a high variety of ceramic materials can be used, whereby the composition of the ceramic may be chosen in dependence of the required electrical features of the later sintered ceramic.
The ceramic filler of the feedstock can be converted into a PTC-ceramic with low resistivity and a steep slope of the resistance-temperature curve.
The resistivity of a PTC-ceramic made from such a feedstock can comprise a range from 3 ωcm to 30000 ωcm at 25°C in dependence of the composition of the ceramic filler used and the conditions under which the feedstock is sintered.
- A -
The reference temperature T b at which the resistance begins to increase comprises a range from -30 0 C to 340 0 C. As higher amounts of impurities could impede the electrical features of the molded PTC-ceramic the content of the metallic impurities in the feedstock is lower than 10 ppm.
The feedstock is injection moldable since the melting point of the matrix is lower than the melting point of the ceramic filler. Thus, bodies of complex geometries can be produced by injection molding of the feedstock, for example bodies comprising bulges, protrusions, surface cavities or grooves or bodies comprising flanges or ribs.
According to one embodiment, the matrix in the feedstock comprises a content of ≤ 20 percent by mass, preferably a content of ≤ 12 percent by mass. This content reduces costs and burnout time of the matrix when it is removed before or during sintering. Further, the low amount of matrix material in the feedstock helps control dimensional variations during the burnout and to reduce shrinkage of the feedstock while it is sintered.
The matrix may, according to one embodiment, comprise materials chosen out of a group comprising wax, resins, thermoplastics and water soluble polymers. For example, low molecular weight polyethylene, polystyrene, paraffin, microcrystalline waxes, several copolymers and celluloses may be contained in the matrix. Additionally, the matrix may comprise at least one more component chosen out of a group comprising lubricants, plasticizers and anti-oxidants . For example, phthalate plasticizers or stearic acids as lubricant may be contained in the matrix.
The metallic impurities in the feedstock may comprise Fe, Al, Ni, Cr and W. Their content in the feedstock, in combination with one another or each respectively, is less than 10 ppm
due to abrasion from tools employed during the preparation of the feedstock.
A method for preparing a feedstock for injection molding is described, comprising the steps A) preparing a ceramic filler being convertible to PTC-ceramic by sintering, B) mixing the ceramic filler with a matrix for binding the filler, and C) producing a granulate comprising the filler and the matrix.
The method comprises using tools having such a low degree of abrasion that a feedstock comprising less than 10 ppm of impurities caused by said abrasion is prepared. Thus, preparation of injection moldable feedstocks with a low amount of abrasion caused metallic impurities is achieved without the loss of desired electrical features of the molded PTC-ceramic .
In step A) base materials of the filler can be mixed, calcinated and ground to a powder. During the calcination which can be performed at temperatures of about 1100 0 C for around two hours a ceramic material of the structure Bai- X - yMxDyTii- a - b N a Mn b Os with x = 0 to 0.5, y = 0 to 0.01, a = 0 to 0.01 and b = 0 to 0.01 is formed, where M stand for a cation of the valency two, D a donor of the valency three or four and N a cation of the valency five or six. This ceramic material is ground to a powder and dried to obtain the ceramic filler.
As base materials, BaCC>3, Tiθ2, Mn-ion containing solutions and Y-ion containing solutions, for example MnSO 4 and YO3 / 2, and at least one out of the group of Siθ2, CaCθ3, SrCC>3, and Pb3θ 4 may be used to prepare the ceramic filler. From these base materials a ceramic material of a composition such as (Bao, 329oCao, ososSro, o969Pbo, 1306Y0, 005 ) ( Tio, 5O2Mno, 0007 ) Oi, 5045 can be prepared, for example. A sintered body of this ceramic material has a characteristic reference temperature T b of
122°C and - depending on the conditions during sintering - a resistivity range from 40 to 200 ωcm.
According to an implementation of the method, step B) is performed at a temperature of 40 0 C to 200 0 C. First, the ceramic filler and the matrix are mixed at room temperature, after which this cold mixture is put into a hot mixer which is heated to temperatures of 100 0 C to 200 0 C, preferably between 120 0 C to 170 0 C, for example 160 0 C resulting in a mechanical mixing of the ceramic filler and the matrix. Then, the mixture of the ceramic filler and the matrix which binds the filler is homogenized in a twin-roll mill to a homogenous consistency at elevated temperatures of 40 0 C to 160 0 C. Other kneading / crushing devices as mixer or mixing devices may be used.
A twin-roll mill preferably consists of two counter-rotating differential speed rollers with an adjustable nip and imposes intense shear stresses on the ceramic filler and the matrix as they pass through the nip. Further, a single-screw or a twin-screw extruder as well as a ball mill or a blade-type mixer may be used for preparing the mixture containing the matrix and the ceramic filler.
In step C) , the mixture of matrix and ceramic filler can be cooled to room temperature and reduced to small pieces by crushing. In a further embodiment, the mixture of the matrix and the ceramic filler can be reduced to small pieces by cutting the mixture at elevated temperatures resulting from the heating applied in method step B) . The mixture hardens when it is cooled and by reducing it to small pieces a granulate of feedstock material is formed.
According to an implementation of the method, the tools used in method steps A) , B) and C) comprise coatings of a hard material. The coating may comprise any hard metal, such as, for example, tungsten carbide (WC) . Such a coating reduces
the degree of abrasion of the tools when in contact with the mixture of ceramic filler and matrix and enables the preparation of a feedstock with a low amount of metallic impurities caused by said abrasion. Metallic impurities may be Fe, but also Al, Ni or Cr. When the tools are coated with a hard coating such as WC, impurities of W may be introduced into the feedstock. However, these impurities have a content of less than 50 ppm. It was found that in this concentration, they do not influence the desired electrical features of the sintered PTC-ceramic.
The metallic impurities of the feedstock may be detected by chemical analyzing methods, for example by inductively coupled plasma (IPC) spectrometry. IPC-spectrometry is a technique for elemental analysis which is applicable to most elements over a wide range of concentrations. Most elements of the periodic table can be analyzed. Samples have to be dissolved prior to analysis.
Figure 1 shows the content C (in ppm) of the metallic impurities Im including Al, Ni, Cr and Fe of differently prepared feedstocks, respectively.
Granulate R is a reference granulate prepared for dry pressing without homogenizing it under high shear rates.
Thus, granulate R contains no or very few metallic impurities due to the preparation method without any abrasion of the tools .
Feedstock Fl was prepared for injection molding with tools made of steel which were not coated with any abrasion preventing coating.
Feedstocks 2a, 2b and 3 were prepared for injection molding with tools comprising surface coatings which prevent abrasion leading to metallic impurities. In the preparation of the feedstock F3, all tools were coated with the hard metal WC,
whereas in the preparation of feedstocks F2a and F2b the tools were coated only partially such that the feedstock has been in contact with the steel of the tools during some method steps.
The reference granulate R has very low amounts of metallic impurities as it was not mixed with a matrix under high shear rates .
The feedstock Fl was prepared under high shear rates but without any coating of the tools used for mixing the ceramic filler with the matrix. It showed high amounts of Al (about 175 ppm) and Fe (about 55 ppm) . The high content of Al was considered to arise from a cleaning step of the tools with AI2O3 before homogenizing the feedstock; the content of Fe was found to be caused by abrasion of the tools. The development of methods with a coating of WC on the surfaces of the tools reduces the amount of metallic impurities in the feedstock.
In feedstocks F2a, F2b and F3, almost all metallic impurities have a lower content of Fe than the content A (10 ppm), which is the highest allowable content for maintaining the desired electrical features of the later sintered PTC-ceramic. To avoid the use of AI2O3 for cleaning the tool and reducing the content of Aluminium (Al) in the feedstock, the tool may preferably be cleaned with the same material as the material of the feedstock itself prior to preparing the injection moldable feedstock.
Figure 2 shows the relation between metallic impurities of Al and Fe Im A i + Fe (in ppm) in a sintered PTC-ceramic and the resistivity p (in ωcm) prepared from different feedstocks. The sintering of the feedstocks can be performed at temperatures of about 1250 0 C to 1400 0 C, preferably of about 1300 0 C to 1350 0 C in air. Temperature, cooling, pressure, atmosphere and the cooling rate during the sintering process
can be varied to influence the characteristics of the PTC- ceramic .
Figure 2 shows a clear relation between p and Im A i +Fe . The higher the amount of the impurities, the higher is the resistivity of the sintered ceramic. Thus, feedstock Fl which was prepared without WC-coating of the surface of the tool or tools leads to a ceramic with a resistivity of more than 2500 ωcm. In contrast, when the feedstock was prepared with a WC coating of the surface of the tools, such as with feedstocks F2b or F3, p of the sintered PTC-ceramic is about as low as in PTC-ceramics which are obtained by granulate prepared for dry pressing (granulate R) .
In Figure 3, resistance-temperature curves of PTC-ceramics are shown whereby the resistivity p in ωcm is plotted against the temperature T in 0 C. The PTC-ceramic made of the reference granulate R by dry pressing has a low resistivity of 20 ωcm for temperatures under 122 0 C which is the characteristic reference temperature T b . For temperatures above 122°C, a steep slope or derivative of the resistance with higher temperatures is shown. Such behaviour of the ceramic can also be achieved with an injection molded PTC- ceramic from a feedstock prepared with the above mentioned method (feedstock F3) . For temperatures above the characteristic reference temperature T b (122°C in this case), the resistance of the feedstock increases by about four orders of magnitude. Feedstocks with higher amounts of metallic impurities such as Fl or F2b have a higher resistivity at temperatures less than T b = 122°C and the slope at temperatures above T b is flatter. This can be an undesired feature in applications making use of PTC-ceramics. The higher resistivity and reduced slope above T b was found to be due to abrasions during the preparation process of the respective feedstocks.
Thus, the presented feedstock enables the preparation of PTC- ceramics with desired electrical features and which can be processed by injection molding to a large variety of complex geometries. Further, the method of the preparation of a feedstock for injection molding leads to obtaining feedstocks with low amounts of impurities.
Next Patent: ROLL PRESS WITH SYMMETRICAL ROLL CENTRING