| CLAIMS 1. A method for producing a fiber based product, c h a r a c t e r i z e d in that the method com¬ prises the steps of: a) applying a binder composition over at least one surface of at least one fiber based sub¬ strate, which binder composition is prepared by using at least polymerizable substance, crosslinking agent, and colorant, wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a correspond¬ ing binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units; b) determining the distribution of the applied binder composition over the entire at least one surface of the at least one fiber based substrate; and c) based on the determination in step b) ei¬ ther accepting the treated at least one fiber based substrate for the production of the fiber based prod¬ uct or rejecting the treated at least one fiber based substrate from the production of the fiber based prod¬ uct . 2. The method of claim 1, wherein in step c) the treated at least one fiber based substrate is ac¬ cepted for the production of the fiber based product when the applied binder composition is uniformly distributed over the entire surface, as visually deter¬ mined . 3. The method of claim 1, wherein in step c) the treated at least one fiber based substrate is ac¬ cepted for the production of the fiber based product when the contrast value is 50% or less, wherein the contrast value is determined as (Ds-Dt) /Ds · 100%, where- in Ds is the reflection density of the binder composi¬ tion and Dt is the reflection density of the surface of the at least one fiber based substrate having the binder composition applied thereon, as measured by reflection densitometry. 4. The method of any one of claims 1 - 3, wherein the colorant is used in an amount such that the difference between the color of the binder compo¬ sition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is preferably at least 5 units, more preferably at least 7 units, and even more preferably at least 10 units. 5. The method of any one of claims 1 - 4, wherein the colorant is used in an amount such that the difference between the color of the binder compo¬ sition and the color of a corresponding binder compo- sition prepared without the use of the colorant, as measured on a Gardner scale, is 3 - 18 units, prefera¬ bly 10 - 18 units, and more preferably 14 - 17 units. 6. The method of any one of claims 1 - 5, wherein the fibers of the fiber based substrate are synthetic or natural fibers. 7. The method of any one of claims 1 - 6, wherein the fiber based substrate is a veneer. 8. The method of claim 7, wherein step a) comprises applying 80 - 250 g, and more preferably 100 - 200 g of binder composition per square meter of veneer . 9. The method of any one of claims 1 - 6, wherein the fiber based substrate is a wood chip, pa¬ per, cardboard, or cotton. 10. The method of any one of claims 1 - 6, wherein the fiber based substrate comprises organic fibers, inorganic fibers, plastic fibers, glass fi¬ bers, carbon fibers, or any combination thereof. 11. The method of any one of claims 1 - 10, wherein the polymerizable substance, the crosslinking agent and the colorant are polymerized. 12. The method of any one of claims 1 - 11, wherein the colorant is a phenolic compound, prefera¬ bly a wood-based phenolic compound, and more prefera¬ bly lignin or tannin. 13. The method of any one of claims 1 - 12, wherein the colorant is lignin and wherein the lignin has a weight average molecular weight of 500 - 10000 g/mol, and preferably of 2000 - 8000 g/mol. 14. The method of any one of claims 1 - 13, wherein the colorant is lignin and wherein the poly- dispersity index of lignin is 1.5 - 15, preferably 2 - 13, and more preferably 3 - 9. 15. The method of any one of claims 1 - 12, wherein the colorant is tannin and wherein the tannin has a weight average molecular weight of 1000 - 4000 g/mol, and preferably of 1300 - 3000 g/mol. 16. The method of any one of claims 1 - 12 or 15, wherein the colorant is tannin and wherein the polydispersity index of tannin is 1 - 6, preferably 1.1 - 4, and more preferably 1.5 - 3. 17. The method of any one of claims 1 - 11, wherein the colorant is flavone dye, iso-quinoline dye, polyene colorant, pyran colorant, chromene dye, naphthochinone dye, chinone dye, anthrachinone dye, chromene dye, benzophyrone dye, indigoid dye or indole colorant . 18. A method for producing a binder composition, c h a r a c t e r i z e d in that the method com¬ prises the step of: - preparing the binder composition by using at least polymerizable substance, crosslinking agent, and colorant, wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a correspond- ing binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units. 19. The method of claim 18, wherein the col¬ orant is used in an amount such that the difference between the color of the binder composition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is preferably at least 5 units, more preferably at least 7 units, and even more preferably at least 10 units. 20. The method of any one of claims 18 - 19, wherein the colorant is used in an amount such that the difference between the color of the binder compo¬ sition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is 3 - 18 units, prefera- bly 10 - 18 units, and more preferably 14 - 17 units. 21. The method of any one of claims 18 - 20, wherein the step of preparing the binder composition comprises the step of polymerizing the polymerizable substance, the crosslinking agent and the colorant. 22. The method of any one of claims 18 - 21, wherein the colorant is a phenolic compound, prefera¬ bly a wood-based phenolic compound, and more prefera¬ bly lignin or tannin. 23. The method of any one of claims 18 - 22, wherein the colorant is lignin and wherein the lignin has a weight average molecular weight of 500 - 10000 g/mol, and preferably of 2000 - 8000 g/mol. 24. The method of any one of claims 18 - 23, wherein the colorant is lignin and wherein the poly- dispersity index of lignin is 1.5 - 15, preferably 2 - 13, and more preferably 3 - 9. 25. The method of any one of claims 18 - 22, wherein the colorant is tannin and wherein the tannin has a weight average molecular weight of 1000 - 4000 g/mol, and preferably of 1300 - 3000 g/mol. 26. The method of any one of claims 18 - 22 or 25, wherein the colorant is tannin and wherein the polydispersity index of tannin is 1 - 6, preferably 1.1 - 4, and more preferably 1.5 - 3. 27. The method of any one of claims 18 - 21, wherein the colorant is flavone dye, iso-quinoline dye, polyene colorant, pyran colorant, chromene dye, naphthochinone dye, chinone dye, anthrachinone dye, chromene dye, benzophyrone dye, indigoid dye or indole colorant . 28. A binder composition obtainable by the method of any one of claims 18 - 27. 29. A fiber based product, c h a r a c t e r ¬ i z e d in that the fiber based product comprises at least one fiber based substrate having a binder compo¬ sition applied over at least one surface of the at least one fiber based substrate, which binder composi¬ tion is prepared by using at least polymerizable sub¬ stance, crosslinking agent, and colorant, wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units. 30. The fiber based product of claim 29, wherein the colorant is used in an amount such that the difference between the color of the binder compo¬ sition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is preferably at least 5 units, more preferably at least 7 units, and even more preferably at least 10 units. 31. The fiber based product of any one of claims 29 - 30, wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a correspond- ing binder composition prepared without the use of the colorant, as measured on a Gardner scale, is 3 - 18 units, preferably 10 - 18 units, and more preferably 14 - 17 units. 32. The fiber based product of any one of claims 29 - 31, wherein the fiber based substrate is a wood board and wherein the binder composition is at least partly absorbed into the at least one surface of the at least one wood board. 33. The fiber based product of any one of claims 29 - 32, wherein the applied binder composition is uniformly distributed over the entire at least one surface of the at least one fiber based substrate, as visually determined. 34. The fiber based product of any one of claims 29 - 32, wherein the contrast value is 50% or less, and wherein the contrast value is determined as (Ds-Dt) /Ds · 100%, wherein Ds is the reflection density of the binder composition and Dt is the reflection densi¬ ty of the surface of the at least one fiber based sub¬ strate having the binder composition applied thereon, as measured by reflection densitometry. 35. The fiber based product of any one of claims 29 - 34, wherein the fiber based substrate is a veneer . 36. The fiber based product of any one of claims 29 - 35, wherein the fiber based product is plywood and wherein the average wood failure of the plywood is above 60 %, preferably above 70 %, and more preferably above 80 %. 37. The fiber based product of any one of claims 35 - 36, wherein 80 - 250 g, and more prefera¬ bly 100 - 200 g of binder composition is applied per square meter of veneer. 38. The fiber based product of any one of claims 29 - 34, wherein the fiber based substrate is a wood chip. 39. The fiber based product of any one of claims 29 - 34, wherein the fiber based substrate com- prises organic fibers, inorganic fibers, plastic fi¬ bers, glass fibers, carbon fibers, or any combination thereof . 40. The fiber based product of any one of claims 29 - 39, wherein the binder composition is obtained by the method of any one of claims 18 - 27. |
FIELD OF THE INVENTION
The invention relates to a method for produc ¬ ing a fiber based product, a method for producing a binder composition, a binder composition and a fiber based product.
BACKGROUND OF THE INVENTION
Modern production processes in wood industry have a very high production speed. This brings about high requirements for the reliability and effective ¬ ness of quality control during the processes. It is well known that the traditional ways to monitor prod ¬ uct defects during e.g. plywood production result in high reject rates of the final product due to the de ¬ lay between the actual production and availability of quality testing results thereof. For glued or impreg ¬ nated products the main sources of defects are related to the binder and its interaction with the substrate. Already small differences between different glue batches (e.g. viscosity or molecular weight distribu ¬ tion) or in the properties of the substrate (e.g. moisture content or density) will significantly change the adsorption and absorption behavior of the binder on and into the substrate. Consequently, gluing phase is the most challenging part in plywood production process. Problems in gluing can usually be seen only after hot pressing when it is already too late.
The inventors of the present invention have recognized a need for better systems to monitor the quality of the glued substrates on which binder compo ¬ sition has been applied. The current invention relates to a new method for producing a fiber based product, comprising a way to monitor the uniformity of the ap- plied binder composition. PURPOSE OF THE INVENTION
The purpose of the invention is to provide a new type of method for producing a fiber based product and to provide a method for producing a binder compo- sition which allows for easy on-line monitoring of defects immediately after the gluing phase. The purpose of the invention is also to provide a new binder composition and a fiber based product.
SUMMARY
The method for producing a fiber based prod ¬ uct according to the present invention is characterized by what is presented in claim 1.
The method for producing a binder composition according to the present invention is characterized by what is presented in claim 18.
The binder composition obtainable by the method according to the present invention is charac ¬ terized by what is presented in claim 28.
The fiber based product according to the pre ¬ sent invention is characterized by what is presented in claim 29.
BRIEF DESCRIPTION OF THE DRAWINGS
The accompanying drawing, which is included to provide a further understanding of the invention and constitutes a part of this specification, illus ¬ trates embodiments of the invention and together with the description helps to explain the principles of the invention. In the drawing:
Fig. 1 is a flow chart illustration of a method according to one embodiment of the present in ¬ vention . DETAILED DESCRIPTION OF THE INVENTION
The present invention relates to a method for producing a fiber based product comprising the steps of:
a) applying a binder composition over at least one surface of at least one fiber based sub ¬ strate, which binder composition is prepared by using at least polymerizable substance, crosslinking agent, and colorant, and wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a correspond ¬ ing binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units;
b) determining the distribution of the applied binder composition over the entire at least one surface of the at least one fiber based substrate; and c) based on the determination in step b) ei ¬ ther accepting the treated at least one fiber based substrate for the production of the fiber based prod ¬ uct or rejecting the treated at least one fiber based substrate from the production of the fiber based prod ¬ uct .
The inventors of the present invention sur- prisingly found out that adding a colorant into the binder composition in the amount according to the present invention facilitates determination of the dis ¬ tribution of the binder composition applied on a surface of the fiber based substrate. Especially, the in- ventors found out an efficient way to immediately check the distribution before proceeding into other production steps of fiber based product. This enhances the production process, because if the binder composi ¬ tion is uniformly applied over the desired surface of the fiber based substrate, the strength of the fiber based product is good. Information on the distribution on the binder composition at the early stage of the production of the fiber based product significantly reduces e.g. wood waste during the production process.
The present invention further relates to a method for producing a binder composition comprising the step of preparing the binder composition by using at least polymerizable substance, crosslinking agent, and colorant, wherein the colorant is used in an amount such that the difference between the color of the binder composition and the color of a correspond- ing binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units.
The corresponding binder composition is a reference binder composition. The corresponding binder composition is prepared in the corresponding way as the binder composition according to the present invention, except that the colorant is excluded. In case the preparation of the binder composition according to the present invention includes adding the colorant in- to a previously produced composition comprising cross- linking agent polymerized with polymerizable sub ¬ stance, the corresponding binder composition is prepared in the same way as the binder composition ac ¬ cording to the present invention, except that the col- orant is not added into the corresponding binder com ¬ position. In case the preparation of the binder composition according to the present invention includes polymerizing the polymerizable substance, the cross- linking agent and the colorant, the colorant is re- placed, in the preparation of the corresponding binder composition, with the same amount of a polymerizable substance before the polymerization step.
The present invention further relates to a binder composition obtainable by the method according to the present invention.
The present invention further relates to a fiber based product comprising at least one fiber based substrate having a binder composition applied over at least one surface of the at least one fiber based substrate, which binder composition is prepared by using at least polymerizable substance, crosslink- ing agent, and colorant, wherein the colorant is used in an amount such that the difference between the col ¬ or of the binder composition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is at least 3 units.
In one embodiment of the present invention the polymerizable substance is a compound selected from the class of phenols. In one embodiment of the present invention the polymerizable substance is se- lected from a group consisting of phenol, cresol, res- orcinol and combinations thereof. In one embodiment of the present invention the polymerizable substance is phenol. In one embodiment of the present invention the polymerizable substance is selected from a group con- sisting of bio-based hydroxyphenols and their deriva ¬ tives .
In one embodiment of the present invention the crosslinking agent is selected from a group of al ¬ dehydes. In one embodiment of the present invention the group of aldehydes comprises an aldehyde, a deriv ¬ ative of an aldehyde, an aldehyde forming compound and any combination thereof. In one embodiment of the pre ¬ sent invention the derivative of an aldehyde is hexa- methylenetetramine or trioxane. In one embodiment of the present invention the crosslinking agent is se ¬ lected from a group consisting of an aromatic alde ¬ hyde, glyoxal, furfuryl alcohol, caprolactam and gly ¬ col compounds. The aromatic aldehyde can be furfuryl aldehyde. In one embodiment of the present invention the crosslinking agent is an aldehyde, and preferably formaldehyde, paraformaldehyde or a combination there ¬ of. In one embodiment of the present invention at least one catalyst is used for the production of the binder composition. In one embodiment of the present invention the catalyst is a base. In one embodiment of the present invention the catalyst is an alkali or an alkali earth hydroxide. In one embodiment of the pre ¬ sent invention the catalyst comprises a salt or a hy ¬ droxide of an alkali metal. In one embodiment of the present invention the catalyst is selected from a group consisting of sodium hydroxide, potassium hydroxide and any mixture thereof. In one embodiment of the present invention the catalyst is an organic amine .
In one embodiment of the present invention, the at least one surface of at least one fiber based substrate is any part of the total surface area of the fiber based substrate. In one embodiment of the pre ¬ sent invention, the at least one surface of at least one fiber based substrate is half of the total surface area of the fiber based substrate. In one embodiment of the present invention, the at least one surface of at least one fiber based substrate means various shapes on the surface of the fiber based substrate. In one embodiment of the present invention, the shape is a stripe or multiple stripes. In one embodiment of the present invention, the shape is a spot or multiple spots. By "the entire at least one surface" of the at least one fiber based substrate, it is meant the en ¬ tire surface over which the binder composition has been applied. In other words, "the entire at least one surface" is not necessarily the total surface area of the fiber based substrate.
In one embodiment of the present invention the treated at least one fiber based substrate is, in step c) , accepted for the production of the fiber based product when the applied binder composition is uniformly distributed over the entire surface, as vis ¬ ually determined.
In one embodiment of the present invention the treated at least one fiber based substrate is, in step c) , accepted for the production of the fiber based product when the contrast value is 50% or less, wherein the contrast value is determined as (D s - D t )/D s -100%, wherein D s is the reflection density of the binder composition and D t is the reflection densi- ty of the surface of the at least one fiber based sub ¬ strate having the binder composition applied thereon, as measured by reflection densitometry.
Reflection densitometry is the practice of characterizing the amount of light absorption of mate- rials by measuring reflectance and calculating and re ¬ porting reflection density. Reflection density (D) is the light-absorbing property of a material, expressed as the logarithm of the reciprocal of the reflectance factor (R) . Higher reflection density is an indication of more light absorbed. Reflection density is calcu ¬ lated as follows: D = logio (1/R) = -logio (R) · Reflec ¬ tion density of the fiber based substrate over which binder composition has been applied, is measured by using a reflection densitometer or spectrodensitometer according to ASTM standard test method for reflection density of printed matter (D7305-08a (Reapproved 2013) ) . Over a restricted range, the reflection densi ¬ ty readings from a densitometer are approximately pro ¬ portional to the binder composition film thickness, i.e. the uniformity of the applied binder composition.
Reflection densitometry can be used to determine whether the applied binder composition film is uniform by measuring the reflection density over a wide area. Multiple reflection density measurements are taken in specified positions on the surface over which binder composition has been applied in order to determine an average result. For example, five meas- urements are taken, one in each corner 25 mm from the edge of the surface over which the binder composition has been applied and one in the middle of the surface. The mean of the five readings is calculated. The con- trast between the fiber based substrate over which the binder composition has been applied and the binder composition is determined. The contrast value is a measure of the uniformity of the binder composition layer on the surface of the fiber based substrate. A contrast value of 50% or less is acceptable.
In one embodiment of the present invention the colorant is used in an amount such that the dif ¬ ference between the color of the binder composition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is preferably at least 5 units, more preferably at least 7 units, and even more pref ¬ erably at least 10 units.
In one embodiment of the present invention the colorant is used in an amount such that the dif ¬ ference between the color of the binder composition and the color of a corresponding binder composition prepared without the use of the colorant, as measured on a Gardner scale, is 3 - 18 units, preferably 10 - 18 units, and more preferably 14 - 17 units. The dif ¬ ference between the color of the binder composition and the color of a corresponding binder composition could also be higher than 18 units, but the upper lim ¬ it of the Gardner scale is 18 units.
In one embodiment of the present invention the fibers of the fiber based substrate are synthetic or natural fibers. Synthetic fibers are made from syn ¬ thesized polymers or small molecules. Natural fibers are made from plant, animal and mineral sources. In one embodiment of the present invention the fibers of the fiber based substrate are wood based natural fi ¬ bers . In one embodiment of the present invention the fiber based substrate is a veneer. In one embodi ¬ ment of the present invention the fiber based sub ¬ strate is wood or wood containing material. In one em- bodiment of the present invention the fiber based sub ¬ strate is a cellulose based timber product. In one em ¬ bodiment of the present invention the fiber based sub ¬ strate is a gluelam product.
In one embodiment of the present invention the binder composition is applied over at least one surface of at least two veneers and the at least two veneers are glued together with the binder composi ¬ tion. In one embodiment of the present invention at least two veneers are glued together with the binder composition under the influence of hot pressing.
In one embodiment of the present invention the veneer is made of softwood. In one embodiment of the present invention the veneer is made of hardwood.
In one embodiment of the present invention the veneer is selected from a group consisting of pine veneer, poplar veneer, beech veneer, spruce veneer, and birch veneer. In one embodiment of the present in ¬ vention the veneer is spruce veneer or pine veneer. In one embodiment of the present invention the veneer is birch veneer.
In one embodiment of the present invention step a) comprises applying 80 - 250 g, and more pref ¬ erably 100 - 200 g of binder composition per square meter of veneer. The amount of binder composition ap- plied per square meter of veneer according to the pre ¬ sent invention results in good contact between the binder composition and the veneer, which leads to a good strength and wood failure value of the fiber based product.
In one embodiment of the present invention the fiber based substrate is a wood chip, paper, card ¬ board, or cotton. Wood chip is a piece of wood formed by cutting or chipping large pieces of wood. The size of wood chips may vary.
In one embodiment of the present invention the fiber based substrate comprises organic fibers, inorganic fibers, plastic fibers, glass fibers, carbon fibers, or any combination thereof. In one embodiment of the present invention the fiber based substrate comprises or consists of mineral wool. In one embodi ¬ ment of the present invention the fiber based sub- strate comprises or consists of rock wool. In one em ¬ bodiment of the present invention the fiber based sub ¬ strate comprises or consists of rubber, polyamide, or polyester. In one embodiment of the present invention the fiber based substrate comprises or consists of vulcanized fiber.
In one embodiment of the present invention the polymerizable substance, the crosslinking agent and the colorant are polymerized. In one embodiment of the present invention the step of preparing the binder composition comprises the step of polymerizing the polymerizable substance, the crosslinking agent and the colorant. In one embodiment of the present inven ¬ tion the binder composition according to the present invention is prepared by forming an aqueous composi- tion comprising colorant, polymerizable substance and crosslinking agent, and by allowing polymerization reactions to take place between these reactant compo ¬ nents under the influence of heating the composition. In one embodiment of the present invention the binder composition according to the present invention is prepared by mixing colorant with a previously produced composition comprising crosslinking agent polymerized with polymerizable substance.
In one embodiment of the present invention the aqueous composition comprising at least polymerizable substance and crosslinking agent is heated at a temperature of 30 - 95 °C for allowing polymerization reactions to take place, until a binder composition with a viscosity value of 80 - 1200 cp is formed.
In one embodiment of the present invention the aqueous composition comprising at least polymeriz- able substance, crosslinking agent, and colorant is heated at a temperature of 30 - 95 °C for allowing polymerization reactions to take place, until a binder composition with a viscosity value of 80 - 1200 cp is formed .
In one embodiment of the present invention the colorant is a phenolic compound, preferably a wood-based phenolic compound, and more preferably lig- nin or tannin. Wood-based phenolic compounds, espe ¬ cially lignins and tannins, have a similar chemical structure as the PF resin. Therefore, a homogeneous dispersion of components is formed, in which at least part of the components are solubilized. The formation of a homogeneous dispersion minimizes phase separation of the components.
In this specification, unless otherwise stat ¬ ed, the expression "lignin" should be understood as lignin originating from any suitable lignin source. The lignin may include essentially pure lignin. By the expression "essentially pure lignin" should be under- stood as at least 90 % pure lignin, preferably at least 95 % pure lignin. In one embodiment of the pre ¬ sent invention the essentially pure lignin comprises at most 10 %, preferably at most 5 %, of other compo ¬ nents. Extractives and carbohydrates such as hemicel- luloses can be mentioned as examples of such other components. In one embodiment of the present invention the lignin contains less than 10 weight-%, preferably less than 6 weight-%, and more preferably less than 4 weight-% of carbohydrates. The amount of carbohydrates present in lignin can be measured by high performance anion exchange chromatography with pulsed amperometric detector (HPAE-PAD) in accordance with standard SCAN- CM 71.
In one embodiment of the present invention the ash percentage of lignin is less than 7.5 weight- %, preferably less than 5 weight-%, and more prefera ¬ bly less than 3 weight-%. The ash content can be de ¬ termined by carbonifying and quickly burning a lignin sample so that alkali salts are not melted before the organic matter has been burned (e.g. 20-200°C for 30 minutes, after which temperature is adjusted to 200- 600°C for 1 h, and thereafter adjusting the temperature to 600-700°C for 1 hour), and finally the lignin sample is ignited at 700°C for lh. Ash content of a lignin sample refers to the mass that remains of the sample after burning and ignition, and it is presented as per cent of the sample's dry content.
In one embodiment of the present invention the lignin is selected from a group consisting of kraft lignin, steam explosion lignin, biorefinery lignin, supercritical separation lignin, hydrolysis lignin, flash precipitated lignin, biomass originating lignin, lignin from alkaline pulping process, lignin from soda process, lignin from organosolv pulping and combinations thereof. In one embodiment of the present invention the lignin is wood based lignin. The lignin can originate from softwood, hardwood, annual plants or from a combination thereof.
In one embodiment of the present invention the lignin is Kraft lignin. By "kraft lignin" is to be understood in this specification, unless otherwise stated, lignin that originates from kraft black liq ¬ uor. Black liquor is an alkaline aqueous solution of lignin residues, hemicellulose, and inorganic chemi ¬ cals used in a kraft pulping process. The black liquor from the pulping process comprises components origi ¬ nating from different softwood and hardwood species in various proportions. Lignin can be separated from the black liquor by different, techniques including e.g. precipitation and filtration. Lignin usually begins precipitating at pH values below 11 - 12. Different pH values can be used in order to precipitate lignin fractions with different properties. These lignin fractions differ from each other by molecular weight distribution, e.g. Mw and Mn, polydispersity, hemicel- lulose and extractive contents. The molar mass of lig ¬ nin precipitated at a higher pH value is higher than the molar mass of lignin precipitated at a lower pH value. Further, the molecular weight distribution of lignin fraction precipitated at a lower pH value is wider than of lignin fraction precipitated at a higher pH value. The precipitated lignin can be purified from inorganic impurities, hemicellulose and wood extrac ¬ tives using acidic washing steps. Further purification can be achieved by filtration.
In one embodiment of the present invention the lignin is flash precipitated lignin. The term "flash precipitated lignin" should be understood in this specification as lignin that has been precipitat ¬ ed from black liquor in a continuous process by de ¬ creasing the pH of a black liquor flow, under the influence of an over pressure of 200 - 1000 kPa, down to the precipitation level of lignin using a carbon dioxide based acidifying agent, preferably carbon dioxide, and by suddenly releasing the pressure for precipitat ¬ ing lignin. The method for producing flash precipitated lignin is disclosed in patent application FI 20106073. The residence time in the above method is under 300 s. The flash precipitated lignin particles, having a particle diameter of less than 2 μπι, form agglomerates, which can be separated from black liquor using e.g. filtration. The advantage of the flash pre- cipitated lignin is its higher reactivity compared to normal kraft lignin. The flash precipitated lignin can be purified and/or activated if needed for the further processing .
In one embodiment of the present invention the lignin is separated from pure biomass. The separa- tion process can begin with liquidizing the biomass with strong alkali followed by a neutralization process. After the alkali treatment the lignin can be precipitated in a similar manner as presented above. In one embodiment of the present invention the separa- tion of lignin from biomass comprises a step of enzyme treatment. The enzyme treatment modifies the lignin to be extracted from biomass. Lignin separated from pure biomass is sulphur-free.
In one embodiment of the present invention the lignin is steam explosion lignin. Steam explosion is a pulping and extraction technique that can be ap ¬ plied to wood and other fibrous organic material.
By "biorefinery lignin" is to be understood in this specification, unless otherwise stated, lignin that can be recovered from a refining facility or pro ¬ cess where biomass is converted into fuel, chemicals and other materials.
By "supercritical separation lignin" is to be understood in this specification, unless otherwise stated, lignin that can be recovered from biomass us ¬ ing supercritical fluid separation or extraction technique. Supercritical conditions correspond to the tem ¬ perature and pressure above the critical point for a given substance. In supercritical conditions, distinct liquid and gas phases do not exist. Supercritical wa ¬ ter or liquid extraction is a method of decomposing and converting biomass into cellulosic sugar by em ¬ ploying water or liquid under supercritical condi ¬ tions. The water or liquid, acting as a solvent, ex- tracts sugars from cellulose plant matter and lignin remains as a solid particle. In one embodiment of the present invention the lignin is hydrolysis lignin. Hydrolysed lignin can be recovered from paper-pulp or wood-chemical process ¬ es .
In one embodiment of the present invention the lignin originates from an organosolv process. Or- ganosolv is a pulping technique that uses an organic solvent to solubilize lignin and hemicellulose .
In one embodiment of the present invention, the lignin is alkalated lignin. In one embodiment of the present invention, alkalated lignin is prepared before the preparation of the binder composition according to the present invention.
In one embodiment of the present invention alkalated lignin is prepared using the following method, comprising the steps of:
i) forming, under heating at a temperature of 30 - 98 °C, an aqueous dispersion comprising alkali and lignin, wherein the alkali comprises a hydrox- ide of an alkali metal; and
ii) heating the dispersion formed in step a) at a temperature of 50 - 95 °C .
In one embodiment of the present invention the alkali is selected from a group consisting of so- dium hydroxide, potassium hydroxide and a mixture thereof. In one embodiment of the present invention the alkali is sodium hydroxide. In one embodiment of the present invention the concentration of alkali is 5 - 50 weight-%, and preferably 10 - 25 weight-% based on the total weight of the dispersion in step i) . In one embodiment of the present invention the concentra ¬ tion of lignin in step i) is 10 - 50 weight-%, prefer ¬ ably 20 - 50 weight-%, and more preferably 20 - 45 weight-% based on the total weight of the dispersion in step i) . In one embodiment of the present invention step i) is carried out preferably at a temperature of 30 - 80 °C, and more preferably at a temperature of 30 70 °C . In one embodiment of the present invention step i) is carried out preferably at a temperature of 71 - 94 °C. In one embodiment of the present invention step ii) is carried out for 15 minutes - 24 hours, preferably for no longer than 5 hours, and more pref ¬ erably for 0.5 - 1,5 hours.
Alkalated lignin has an increased reactivity as compared to untreated lignin or so-called raw lig ¬ nin. Without limiting the invention to any specific theory about why step i) and step ii) results in a more reactive lignin being formed, it is to be consid ¬ ered that these steps result in the macromolecular structure of lignin being opened whereby the steric hindrances that usually disable reactive groups in lignin structures are removed. These steps, or a so- called alkalation process, may also add charged groups to the lignin macromolecule . The advantage of using alkalated lignin e.g. for producing a binder composition is that the compatibility and reaction behavior is much better than in a normal case, where non- treated lignin has been used in the cooking or poly ¬ merizing stage.
In one embodiment of the present invention the tannin used originates from any wood species. Tan- nin may originate from e.g. bark or heartwood. Quebra ¬ cho tree, beech tree and wattle tree are presented as examples of possible sources of tannin.
In one embodiment of the present invention the tannin used originates from softwood bark. In one embodiment of the present invention the tannin is sep ¬ arated from softwood bark of debarking units in sawmills or pulp mills. The separation process can be combined with an ethanol extraction process, a hot wa ¬ ter extraction process, a hot steam extraction process or a water-ethanol extraction process of softwood bark . In one embodiment of the present invention the tannin is condensed tannin. Condensed tannin has a high dry content and is therefore suitable to be used in the present invention. The dry matter content of condensed tannin may vary between 40 - 100 % and is suitably between 60 - 90 % and preferably between 70 - 80 %. Tannin with such dry matter content can easily be dispersed, whereby a good reactivity with the other reactant components is achieved. The tannin may also be hydrolysable tannin.
In one embodiment of the present invention the colorant is lignin and the lignin has a weight av ¬ erage molecular weight of 500 - 10000 g/mol, and pref ¬ erably of 2000 - 8000 g/mol.
In one embodiment of the present invention the colorant is lignin and the polydispersity index of lignin is 1.5 - 15, preferably 2 - 13, and more pref ¬ erably 3 - 9. The polydispersity index range of 3 - 9 results in less variation in the preparation of the binder composition and thus makes it easier to control the preparation of the binder composition.
In one embodiment of the present invention the colorant is tannin and the tannin has a weight av ¬ erage molecular weight of 1000 - 4000 g/mol, and pref- erably of 1300 - 3000 g/mol.
In one embodiment of the present invention the colorant is tannin and the polydispersity index of tannin is 1 - 6, preferably 1.1 - 4, and more prefera ¬ bly 1.5 - 3. The polydispersity index range of 1.5 - 3 results in less variation in the preparation of the binder composition and thus makes it easier to control the preparation of the binder composition.
When lignin or tannin of the weight average molecular weight range and polydispersity index range according to the present invention is used as a colorant, the binder composition partly penetrates into the veneer and partly stays on the surface of the veneer. Thus, the strength of the plywood prepared from the veneer is good.
The molecular weight of the lignin or tannin can be determined by using a high-performance size- exclusion chromatography.
In one embodiment of the present invention, the molecular weight of the lignin or tannin is determined by using a high-performance size-exclusion chro ¬ matography in the following manner: Two parallel meas- urements are carried out. 0.1 M NaOH is used as an el- uent . Calibration is done using Na-polystyrene sul ¬ fonate standards having a molecular weight of 1100 - 73900 g/mol. For quality control, standard quality kraft lignin and PSS molecular weight standard are used. The columns used are PSS MCX precolumns, 1000 A and 100 000 A separation columns filled with sulfonat ¬ ed styrene-divinylbenzene copolymer matrix. Isocratic run program is used. The run time is 45 minutes. The injection volume is 50 μΐ . The flux is 0.5 ml per mi- nute . The temperature is 25 °C . As a result of the chromatography, number average molecular weight (Mn) , weight average molecular weight (Mw) , peak molecular weight (Mp) and polydispersity index (PDI) values can be reported.
The polydispersity index (PDI) can be deter ¬ mined by size-exclusion high-performance liquid chro ¬ matography (SEC-HPLC) . The polydispersity index (PDI) is a measure of the distribution of molecular mass in a given polymer sample. The PDI is calculated as the weight average molecular weight divided by the number average molecular weight. PDI indicates the distribu ¬ tion of individual molecular masses in a batch of pol ¬ ymers. The higher the polydispersity index of color ¬ ant, the wider the molecular weight distribution range of the colorant.
In one embodiment of the present invention the colorant is flavone dye, iso-quinoline dye, poly- ene colorant, pyran colorant, chromene dye, naph- thochinone dye, chinone dye, anthrachinone dye, chromene dye, benzophyrone dye, indigoid dye or indole colorant .
In one embodiment of the present invention the fiber based substrate is a wood board and the binder composition is at least partly absorbed into the at least one surface of the at least one wood board .
In one embodiment of the present invention the applied binder composition is uniformly distributed over the entire at least one surface of the at least one fiber based substrate, as visually deter ¬ mined .
In one embodiment of the present invention the contrast value is 50% or less, and the contrast value is determined as (D s -D t ) /D s · 100%, wherein D s is the reflection density of the binder composition and D t is the reflection density of the surface of the at least one fiber based substrate having the binder com ¬ position applied thereon, as measured by reflection densitometry .
In one embodiment of the present invention the fiber based product is plywood and the average wood failure of the plywood is above 60 %, preferably above 70 %, and more preferably above 80 %. Wood fail ¬ ure is a measure of the strength of the binder compo ¬ sition. Wood failure is determined in accordance with standard EN314-1.
In one embodiment of the present invention 80
- 250 g, and more preferably 100 - 200 g of binder composition is applied per square meter of veneer.
In one embodiment of the present invention the fiber based substrate is a wood chip.
In one embodiment of the fiber based product, the binder composition is obtained by the method ac ¬ cording to the present invention. The embodiments of the invention described hereinbefore may be used in any combination with each other. Several of the embodiments may be combined to ¬ gether to form a further embodiment of the invention.
The methods, the binder composition or the fiber based product, to which the invention is relat ¬ ed, may comprise at least one of the embodiments of the invention described hereinbefore.
An advantage of the method according to the present invention is that the method allows for a sim ¬ ple and fast determination of the distribution of the binder composition over a surface of the fiber based substrate during the production process of fiber based products. This is due to the high contrast between the color of the binder composition and the color of the fiber based substrate. Consequently, the method en ¬ hances the overall production process of fiber based products. The distribution of the binder composition can be determined on-line, which assists in detecting the gluing or impregnation defects. As a result, the amount of e.g. wood waste is reduced. The method also improves the quality of the final product, because the uniformity of the binder composition film applied on the fiber based substrate affects the final product strength.
EXAMPLES
Reference will now be made in detail to the embodiments of the present invention, an example of which is illustrated in the accompanying drawing.
The description below discloses some embodi ¬ ments of the invention in such a detail that a person skilled in the art is able to utilize the invention based on the disclosure. Not all steps of the embodi- ments are discussed in detail, as many of the steps will be obvious for the person skilled in the art based on this specification. Figure 1 illustrates a method according to one embodiment of the present invention for producing a fiber based product.
Before applying the binder composition over at least one surface of at least one fiber based sub ¬ strate, the binder composition is prepared. At least polymerizable substance, crosslinking agent and color ¬ ant are used for the preparation of the binder compo ¬ sition. Also other components can be used for the preparation of the binder composition. The colorant is used in such an amount that it results in at least 3 units difference between the color of the binder com ¬ position and the color of a corresponding reference binder composition. The reference binder composition is prepared under the same reaction conditions and us ¬ ing the same component amounts as the binder composi ¬ tion according to the present invention, except that the colorant is excluded from the preparation of the reference binder composition. The color of the binder composition and the reference binder composition are measured on a Gardner scale.
The binder composition prepared as described above is then applied over at least one surface of at least one fiber based substrate. The binder composi- tion may be applied over the total surface area of the fiber based substrate. The binder composition may also be applied over certain areas on the surface of the fiber based substrate. Such areas may be shaped like stripes, spots, or any other shape.
After the application of the binder composition over the surface of the fiber based substrate, the distribution of the applied binder composition over the entire surface that was intended to be cov ¬ ered is determined. The determination can be done vis- ually. The determination can also be done by determining the contrast value as described in the description above . The treated fiber based substrate is then ei ¬ ther accepted for the production of the fiber based product or rejected from the production of the fiber based product, based on the determination step de ¬ scribed above.
EXAMPLE 1 - Preparing a binder composition.
In this example a lignin phenol formaldehyde (LPF) binder composition was produced.
The following components and their amounts were used:
In this example, and examples 2 and 7, the molecular weight distribution of lignin was determined by SEC-HPLC and the weight average molecular weight of the lignin used in these examples was 4000 - 6000 g/mol. The polydispersity index of the lignin used in these examples was determined by SEC-HPLC and the pol ¬ ydispersity index of the lignin used in these examples was 4 - 6.
Firstly, a synthetic phenol formaldehyde (PF) binder composition was produced by polymerizing phenol and formaldehyde in the presence of water and sodium hydroxide (NaOH) cL S cL C3.talyst. Formaldehyde was added in a stepwise manner to an aqueous phenol composition and thereafter the temperature of the formed composi ¬ tion was increased up to 80 - 90 °C . The composition was cooked at this temperature until a viscosity value of 295 cP was reached. The viscosity was measured at 25 °C using a rotary viscometer. To this composition, the lignin used as a colorant was physically mixed.
The lignin may also be alkalated lignin. Al- kalated lignin can be prepared as described in Example 2.
The molecular weight distribution of the formed binder composition was determined by SEC-HPLC. According to the results, the weight average molecular weight of the formed binder composition was 900 10000 g/mol.
The polydispersity index of the formed binder composition was determined by SEC-HPLC. According to the results, the polydispersity index of the formed binder composition was 7.
The color difference of the binder composi ¬ tion formed as described above and the corresponding binder composition formed similarly except without the addition of lignin, was determined on Gardner scale as described in Example 3. According to the results, the color difference was 10 units, as measured on Gardner scale .
The binder composition formed as above indi ¬ cated was further used for the production of fiber based product.
EXAMPLE 2 - Preparing a binder composition.
In this example a LPF binder composition was produced .
The following components and their amounts were used:
Material Concentration (%) Mass (g)
NaOH 50 103
Water 136
Kraft lignin 73 145
Formaldehyde 37 268 Phenol I 90 I Hi
Firstly, alkalated lignin was prepared as follows. Water and part of the sodium hydroxide (65 g) were mixed and heating of the mixture was started. Then lignin was dispersed slowly into the mixture of sodium hydroxide and water with agitation and simultaneously the temperature was increased up to 60 °C . When all of the lignin had been dispersed, the disper ¬ sion was heated at a temperature of about 76 °C for about 1 hour.
Then the phenol was added in a stepwise man ¬ ner to the above formed composition containing alkalated lignin, followed by the addition of the first part of the formaldehyde (125 g) also in a stepwise manner. The formed composition was then cooked at a temperature of 70 - 80 °C for allowing the reactant components therein to react with each other. During this step of cooking the composition, the second part of the formaldehyde (143 g) was added to the composi- tion. After adding formaldehyde into the composition, the composition was cooked for ten more minutes, after which the last part of catalyst, NaOH (38 g) , was add ¬ ed to the composition. Again, the composition was allowed to cook at a temperature of about 80 - 90 °C for about 2 hours and 47 minutes, after which the process was ended by cooling down the reaction composition.
The molecular weight distribution of the formed binder composition was determined by SEC-HPLC. According to the results, the weight average molecular weight of the formed binder composition was 11000 - 12000 g/mol.
The polydispersity index of the formed binder composition was determined by SEC-HPLC. According to the results, the polydispersity index of the formed binder composition was 8. The color difference of the binder composi ¬ tion formed as described above and the corresponding binder composition formed similarly except without the addition of alkalated lignin, was determined on Gard- ner scale as described in Example 3. In the corre ¬ sponding binder composition, alkalated lignin was replaced with the same amount of phenol before the polymerization step. According to the results, the color difference was 17 units, as measured on Gardner scale.
The binder composition formed as above indi ¬ cated was further used for the production of fiber based product. EXAMPLE 3 - Coloring of PF binder composition with lignin and the analysis of color change on Gardner scale .
The aim of this test was to create a method to evaluate the color of a reference binder composi ¬ tion (phenol formaldehyde binder composition, PF bind ¬ er composition) and in addition to evaluate the color change in the binder composition induced by the addi ¬ tion of lignin or alkalated lignin (lignin phenol for- maldehyde binder composition, LPF binder composition) .
The LPF binder composition (sample 8) was prepared as described in Example 2. The PF binder com ¬ position (sample 0, reference) was prepared in a cor ¬ responding manner except that alkalated lignin was re- placed with the same amount of phenol before the polymerization step.
The binder compositions were diluted with wa ¬ ter to a concentration of 1 g (dry mass of binder composition)/!. Diluted binder composition was placed in a test tube and the color of the dilution was visually determined by comparing the color of the dilution with the color of Gardner laboratories reference samples. Alkalated lignin or non-alkalated lignin (dry lignin) were then added to diluted PF binder composi ¬ tion according to table 2 in a concentration of 10 g/1. The lignin content of alkalated lignin was 30 %. The samples and their description are presented in ta ¬ ble 1.
The solution was then also diluted to a con ¬ centration of 1 g/1. The color of the solution was visually determined by comparing the color of the so- lution with the color of Gardner laboratories reference samples. The color of the binder composition with or without lignin addition is presented in table 2.
Table 1. Samples and their description
Samp1e Dry Phenol Added Added Lignin/ Value binder in alkala ¬ dry Phenol on compo ¬ diluted ted lig(%) Gard ¬ sition samp1e lignin nin ner
(g) (g) (g) (g) scale
0 1 0.5 0 0 0 <1
1 1 0.5 0.17 0 10 3
2 1 0.5 0.5 0 30 5 3 1 0.5 0.83 0 50 10
4 1 0.5 1.67 0 100 13
5 1 0.5 3.33 0 200 18
6 1 0.5 0 0.1 20 3
7 1 0.5 0 0.15 30 6
8 1 0.5 0 0 50 18
According to the results, the addition of lignin changed the color of the diluted binder compo ¬ sition. The change was noted immediately after the ad- dition of alkalated lignin and when dry lignin powder was dispersed in binder composition. Further according to the results, the addition of dry or alkalated lig ¬ nin gave similar response on Gardner scale. Samples 1 and 6 were not accepted for production of fiber based product, because the difference of the color of the binder composition and the color of the corresponding reference binder composition (sample 0) was less than 3 units. EXAMPLE 4 - Coloring of PF binder composition with tannic acid and the analysis of color change on Gard ¬ ner scale.
The aim of this test was to evaluate the col- or change in binder composition induced by addition of tannic acid.
The PF binder composition was prepared as de ¬ scribed in Example 1.
Binder composition was diluted with water to a concentration of 1 g (dry mass of resin) /l. Diluted binder composition was placed in a test tube and the color of the dilution was visually determined by com ¬ paring the color of the dilution with the color of Gardner laboratories reference samples.
Tannic acid (CAS: 1401-55-4, C76 H52 046), which is a specific type of tannin, was then added to diluted PF binder composition according to table 3. To 1 g of binder composition 0, 1, 2 or 4 g of tannic acid was added and the solution was mixed. The molecular weight distribution of the tannic acid was determined by SEC-HPLC and the weight average molecular weight of the tannic acid used was 1700 g/mol. The polydispersi ¬ ty index of the tannic acid used in this example was determined by SEC-HPLC and the polydispersity index of the tannic acid used was 1.5.
The solution was then diluted to a concentra ¬ tion of 1 g/1. The color of the solution was visually determined by comparing the color of the solution with the color of Gardner laboratories reference samples. The color of the binder composition with or without tannic acid addition is presented in table 3. The dry matter content (DMC) of the binder composition was de ¬ termined by heating the sample at a temperature of 60 °C for 6 hours . Table 3. Tannic acid amounts and the results of the color measurement
According to the results, the addition of tannic acid changed the color of the diluted binder composition. The change was noted immediately after the addition of tannic acid into the binder composi ¬ tion. Sample 1 was not accepted for production of fi ¬ ber based product, because the difference of the color of the binder composition and the color of the corre ¬ sponding reference binder composition (sample 0) was less than 3 units. EXAMPLE 5 - Coloring of PF binder composition with flavone dye quercitrin and the analysis of color change on Gardner scale.
The aim of this test was to evaluate the col- or change in binder composition induced by the addi ¬ tion of flavone dye quercitrin.
The PF binder composition was prepared as de ¬ scribed in Example 1.
Binder composition was diluted with water to a concentration of 1 g (dry mass of resin) /l. Diluted binder composition was placed in a test tube and the color of the dilution was visually determined by com ¬ paring the color of the dilution with the color of Gardner laboratories reference samples.
Quercitrin dye (CAS: 522-12-3) was then add ¬ ed to diluted PF binder composition according to table 4. To 1 g of binder composition 0, 0.5, 1 or 2 g of quercitrin dye was added and the solution was mixed.
The solution was then diluted to a concentra- tion of 1 g/1. The color of the solution was visually determined by comparing the color of the solution with the color of Gardner laboratories reference samples. The color of the binder composition with or without quercitrin dye addition is presented in table 4.
Table 4. Quercitrin dye amounts and the results of the color measurement
Samp1e Dry binder Binder Diluted Added Value composition compo ¬ binder queron
(g) sition composi ¬ citrin Gardner
DMC tion (g) dye (g) scale
(%) 0 1 45.8 2.2 0 <1
1 1 45.8 2.2 0.5 3
2 1 45.8 2.2 1 5
3 1 45.8 2.2 2 8
According to the results, the addition of quercitrin dye significantly changed the color of the diluted binder composition. The change was noted imme- diately after the addition of quercitrin dye into the binder composition. Sample 1 was not accepted for pro ¬ duction of fiber based product, because the difference of the color of the binder composition and the color of the corresponding reference binder composition (sample 0) was less than 3 units.
Instead of quercitrin dye, any other colorant, such as iso-quinoline dye, polyene colorant, py- ran colorant, chromene dye, naphthochinone dye, chi- none dye, anthrachinone dye, chromene dye, benzo- phyrone dye, indigoid dye or indole colorant, may sim ¬ ilarly be used as the colorant.
EXAMPLE 6 - The use of a binder composition for producing plywood.
The binder composition of Example 1 or Example 2 was used in the production of plywood. Spruce veneer was used.
The binder composition was applied over the surface of at least one side of the veneers. The dis ¬ tribution of the applied binder composition over the surface of the veneer was determined as follows. The reflection density (D t ) of the surface, on which the binder composition was applied, was measured by re- flection densitometry according to ASTM standard test method for reflection density of printed matter (D7305-08a (Reapproved 2013) ) . Five separate measure ¬ ments were taken in each corner and in the middle of the surface over which the binder composition had been applied. The mean of the five measurements were calcu ¬ lated. The reflection density of the binder composi ¬ tion (D s ) was also measured by reflection densitome- try. The contrast value was determined as (D s - D t )/D s -100%. The contrast value was 20% when the binder composition of Example 1 was used, and 15% when the binder composition of Example 2 was used. The contrast value was found acceptable and the treated veneers were accepted for the production of plywood.
The accepted veneers were used in plywood production in the following manner. The wood veneers were joined together by the binder composition to form plywood. The wood veneers with the binder composition were pressed by hot-pressing technique. The plywood hot-pressing temperature used was about 130°C. For de ¬ termining the optimum hot-pressing time needed for the different plywood, the temperature rise of the inner ¬ most glue line of the plywood panel was followed. The hot-pressing time was the time it took to reach 100°C, plus two minutes for curing the binder composition.
EXAMPLE 7 - Preparing a binder composition and applying the binder composition on rock wool.
First, a LPF binder composition was produced. The following components and their amounts were used.
Material Concentration (%) Mass (g)
NaOH 50 110
Water 225
Lignin 70 170
Formaldehyde 37 1090
Phenol 90 535
Urea 100 110
Borax 100 45
Boric acid 100 25 Firstly, water, sodium hydroxide, phenol and lignin were mixed. Then, borax was added to the dis ¬ persion and the components were allowed to react for one hour at 50 °C . Formaldehyde was then added and the dispersion was heated at a temperature of 65 °C for 2.5 hours. The dispersion was then allowed to cool to 40 °C and boric acid and urea were added, respective- ly.
The lignin may also be alkalated lignin. Al- kalated lignin can be prepared as described in Example 2.
The molecular weight distribution of the formed binder composition was determined by SEC-HPLC. According to the results, the weight average molecular weight of the formed binder composition was 5000 6500 g/mol.
The polydispersity index of the formed binder composition was determined by SEC-HPLC. According to the results, the polydispersity index of the formed binder composition was 7.5.
The color difference of the binder composi ¬ tion formed as described above and the corresponding binder composition formed similarly except without the addition of lignin, was determined on Gardner scale as described in Example 3. In the corresponding binder composition, lignin was replaced with the same amount of phenol before the polymerization step. According to the results, the color difference was 16 units, as measured on Gardner scale.
The binder composition formed as above indi ¬ cated was then applied on rock wool as follows. Mix ¬ ture of volcanic stones and coke were fed to a fur ¬ nace. The melt was allowed to run out of the bottom of the furnace onto the spinning machine, where fibers of rock wool were spun to give rock wool with a fiber - like structure. The spinning was continued while minor amounts of binder composition prepared as above and oil were sprayed on the individual fibers of rock wool, i.e. the fiber based substrate, in order to ap ¬ ply the binder composition on rock wool. The rock wool fibers, on which the binder composition was applied, were then collected on a belt conveyor.
The distribution of the applied binder compo ¬ sition over the entire surface of the rock wool fibers was determined by visually detecting that the surface of the fibers was colored. According to the visual de ¬ termination the rock wool was accepted for the produc ¬ tion of the fiber based product, i.e. a cured rock wool mat. EXAMPLE 8 - Applying a binder composition on wood chips .
The binder composition of Example 1 or Example 2 was applied on wood chips.
The binder composition was applied over at least one surface of the wood chip. The distribution of the applied binder composition over the entire surface of the wood chip was determined as described in Example 5.
The contrast value was 30% when the binder composition according to Example 1 was used and 15% when the binder composition according to Example 2 was used. The contrast value was found acceptable and the treated wood chips were accepted for the production of fiber based product.
It is obvious to a person skilled in the art that with the advancement of technology, the basic idea of the invention may be implemented in various ways. The invention and its embodiments are thus not limited to the examples described above; instead they may vary within the scope of the claims.