FIELD

This disclosure relates generally to coated pigments and coating systems including the coated pigments, and particularly, to the design of polymer coated pigments and methods of producing the coated pigments, and to the design of coating systems including the coated pigments.

BACKGROUND

Pigments, resins, and solvents are major components of pigmented paints and inks. While resins are mainly responsible for the film formation and adhesion between coatings and substrates, pigments are widely used in paint/ink industries to impart aesthetic effects or protective functions to the coated substrates. The properties of pigmented paint/inks and the performances of the final coating are greatly affected by the dispersion of the pigments and their interaction with resin, solvent, and other components of the paints/inks. However, due to the complicated interactions among these ingredients, proper dispersion of pigments in their vehicles and optimal characteristics of the paints/inks are desirable.

Incorporation of pigments into inks and coatings is typically achieved by dispersing dry pigments into liquid resin systems. In order to achieve optimum hiding power or color strength, extensive shear has to be applied during the mixing process to break the pigment agglomerates or aggregates down into primary particles. The pigment particles also need to be stable in the paint/ink system during the storage as re-aggregation of the pigment particles or separation of pigment from the bulk of paint/ink system will reduce the performance of the paint/ink system.

The addition of pigment to the paint/ink system often has complicated implication to the performance of paint/ink systems. For example, the interaction between pigment surfaces and resin polymer chains can alter the viscosity profiles of the ink/paint systems. Depending on their application conditions, paints or inks have their distinctive preferred rheology profiles. The viscosity of the paint/ink products depends greatly not only on the size, shape, concentration, and dispersion of pigment particles, but also on the interactions between pigment particles and other components of the resin systems. On the other hand, incompatibility between resin and pigments often results in flocculation and separation of pigments from the resin systems, reducing the hiding power and aesthetics of the final coatings.

The interactions between pigments and other paint/ink ingredients are complex, and extensive efforts are required to understand these interactions and how these interactions affect the properties and performances of the final products. For these purposes, dispersants have been extensively used in coating formulations to help the dispersion of pigments and extend shelf life of the resulting paints/inks. Numerous pigment pre-treatment methods have been utilized to increase the pigment compatibility in the resin system and to improve pigment dispersion, control system viscosity, and maintain stability of the paint/ink systems. The surface of the pigment can be treated with surface active reagents that can be either physically absorbed onto the pigment surfaces or chemically bonded to the pigment surfaces. Examples of such surface active reagents include fatty acids, organophosphorous compounds, and silane coupling reagents. Polymeric materials that contain surface active groups also have been extensively studied as pigment dispersants. Research also has been conducted to encapsulate pigments into polymer or inorganic matrixes to improve their dispersion in paint/ink systems.

Pigments can react and/or interact with other ingredients of the paints/inks. In these cases, to increase storage stability and to enhance the final performance of paints/inks, it is desirable to separate these ingredients from one another and mix them together only immediately prior to the application of the paints/inks. However, due to the complex nature of these coating materials, commercial paints/inks are generally supplied as finished products with all ingredients and processed to their final application form by their manufactures. Therefore, despite extensive efforts to mitigate the undesirable reactions and interactions among different ingredients, commercial paints/inks generally have limited shelf-lives. For example, aluminum pigments, which are widely used in paint/ink industries to generate metallic effects, can readily react with water and liberate hydrogen gas. Not only will the erosion of aluminum reduce the metallic luster of the final coating, excessive hydrogen buildup inside the container will impose great hazards during storage, shipping, and handling. With current industrial focus shifts from solvent-borne to water-borne to minimize volatile organic contents (VOC), extensive industrial efforts have been diverted to mitigate the reaction between aluminum pigments and water and to elongate the shelf-stability of the final products.

The interaction between pigment and other coating components also affect the final coating properties such as adhesion, weathering, chemical resistance, and aesthetics. For example, pigments tend to migrate to the surface of coating if they are incompatible with the resin matrix. In these cases, pigments have less adhesion to the film and are exposed to the external environments. As a result, the final coating will have limited scratch resistance and be prone to discoloration.

Therefore, due to the complex interactions between pigments and the rest of the paint/ink systems, extensive considerations have to be made during the paint/ink formulation processes. For instance, depending on the compatibility of the pigments and the rest of the paint/ink systems, extensive research would be needed to identify suitable additives and to develop proper processes to achieve the desirable properties of the paint/inks. SUMMARY

A coated pigment that can include polymer encapsulations which act as a pigment dispersant and film forming agent, coating systems that can include the coated pigment and methods for producing the coated pigment and the coating system are described. The polymer encapsulations of the coated pigments can allow the coated pigments that are included in the coating system to be dispersed with or without the addition of any other dispersants and/or resins. Thus, the disclosed coated pigments can simplify the process of making coating systems. The disclosed coated pigments also can extend the shelf-life of the coating systems, and can provide a final coating with enhanced pigment orientation and aesthetics.

The disclosed coated pigments can include polymer chains or polymer networks that are attached to the pigment surfaces. In one embodiment of the disclosed coating system, the coating system can include the disclosed coated pigments and a solvent. In one example, once a suitable solvent is added to the coated pigments, the attached polymer chains or polymer networks can swell and the coated pigments can become readily dispersed into the solvent. The swollen polymer chains or polymer networks can provide steric hindrance and/or electrostatic repulsion, and can serve as dispersants to stabilize the coated pigments in the final paint/ink system. Unlike conventional dispersants whose affinity to the pigment surfaces are greatly influenced by the solution environments, the attached polymer chains of the disclosed coated pigments can provide robust stabilization for the dispersion, and can allow expanded formulation windows for the paint and ink systems.

In another embodiment of the coated pigment, polymers or polymer networks can be included in amount sufficient to provide film forming capabilities! Conventional paints rely on an external resin or binder for the film formation. In these conventional systems, a sufficient amount of binder is needed to wet the pigments and the amount of pigment used needs to be low enough to keep the pigment volume concentration (PVC) below a critical PVC. In one example of the disclosed system, paints or inks can be directly formed via dispersing polymer

encapsulated pigments into a solvent without the addition of external resins. Upon the evaporation of solvents and other volatile contents, the attached polymer on the surfaces of the pigments can directly adhere the pigment to one another. This can result in a film formation and promotion of the adhesion between the coating and the substrate that is being coated.

In one embodiment of the disclosed coating system, the disclosed coating system can simplify the paint/ink preparation process by not requiring the use of an external binder, grinding aid and dispersants in the paint formulation. In this instance, paints/inks can be made simply by adding a solvent to the disclosed coated pigments with minimal shearing and stirring. Through simplifying the paint/ink composition and reducing processing requirements, the likelihood of undesirable interactions can be decreased and the shelf-life of the resulting paint/ink can be extended. In addition, since polymers can be chemically bonded to the pigments and the amount of grafted polymer required to achieve good film forming capabilities can be small, high pigment loading can be achieved in the final coating. Compared with conventional coatings, the disclosed system can include the disclosed coated pigments with pigments that are aluminum, glass and mica flakes, and can result in coatings that can achieve improved pigment orientation and enhanced aesthetics. BRIEF DESCRIPTION OF THE DRAWINGS

Fig. 1 illustrates one embodiment of the disclosed coated pigment.

Fig. 2 shows the disclosed coating system applied on a plastic of a) poly(methyl methacrylate), b) acrylonitrile butadiene styrene and c) polystyrene.

Fig. 3 shows the results of a cross-hatch adhesion test of the resin-less coating of polystyrene coated Silberline Sparkle Silver® Premium 695.

Fig. 4 shows the scanning electron microscopy graph of the surface of the resin-less coating of poly(methyl methacrylate) coated Silberline Sparkle Silver® Premium 695 on poly (methyl methacrylate) panel.

DETAILED DESCRIPTION

A coated pigment that can have polymers that are dispersants and film forming reagents attached to the pigment, a coating system that can include the coated pigment, and a method for producing the coating system are described. The concepts of the coating system described herein will be described with respect to a paint or ink system. However, in appropriate circumstances, it is to be realized that the concepts can be applied to other types of systems as well.

Resins and pigments can be usually key components in coating systems such as paint/ink systems. The term "resins" herein can mean polymers that are commonly added in the art as dispersing, film forming and/or adhesive agents to coating formulations such as inks and paints. Resins can be, for example, alkyd, polyester, polyamide, polyimide, silicone, phenolic, urea, melamine, epoxy, polyurethane, polyolefines, polyvinyl, and polyacrylic resins. The term "pigments" herein can mean transparent, metallic, white or colored, mineral or organic particles of any form, which are insoluble in a liquid medium and are suitable for use in ink and paint compositions. Resins, as film forming reagents, can be responsible for the mechanical properties of a coating system and adhesion of the film formed by the coating system to the substrates. The pigments can provide hiding power and impart aesthetics to the coating. The inventors have found that by attaching polymers that are dispersants and film forming agents to pigments, a coating system that includes such a coated pigment does not require any additional components other than a solvent to disperse the pigments and form a film that has good adhesion to the substrate.

In one embodiment, the disclosed coating system can be a resin-less system. The term "resin-less" can mean that besides the polymers or polymer networks that are grafted on the surface of the pigments, no additional dispersants and/or resins are required in the final paint/ink formulation for formation of the coating film. The term "additional dispersants and/or resins" herein can mean polymers that are separate from the polymer chains that are attached to the surface of the pigment, and are commonly added in the art as dispersing, film forming and/or adhesive agents to coating formulations such as inks and paints. The additional resins, for example, can be alkyd, polyester, polyamide, polyimide, silicone, phenolic, urea, melamihe, epoxy, polyurethane, polyolefines, polyvinyl, and polyacrylic resins. Examples of the additional dispersants can be found in Organic coatings: science and technology, third edition (New York: John Wiley & Sons, 2007), pages 440 and 446, which is incorporated herein by reference.

In one example, the disclosed coating system can include the disclosed coated pigments and a solvent or a solvent mixture. The term "solvent or a solvent mixture" herein can mean a liquid that carries the components of the final coating so they can be applied to a substrate and then is removed by evaporation, treating, etc. In one example, the disclosed coating system can include the coated pigments and the solvent or the solvent mixture only. In one implementation, the polymers can be added in an amount sufficient to form a film and adhere the film to a substrate when the coating system is applied onto the substrate. The substrate to which the coating system is applied can be any substrate to which paints or inks are applied, including, but not limited to, plastic, metal, etc.

In another embodiment, the disclosed coating system can include coated pigments that are encapsulated with smooth and robust polymer coating of controlled thickness. To obtain stable coated pigment dispersions, the polymer chains or networks can be adhered to the surface of the pigment under process conditions. The polymer encapsulation can be stabilized through chemical bonds between polymer chains/networks and the pigments. In one implementation, the polymer encapsulation can be composed of polymer chains, where the polymer chains have one end covalently bonded or strongly adsorbed to the surface of a pigment. One example of the disclosed coated pigment will now be described. With reference to Fig. 1, a coated pigment 10 can include a pigment 12 having a surface 12a. The surface 12a can be coated with a coating 14 that has multiple layers 14a, 14b. In the illustrated embodiment shown in Fig. 1, the coating 14 can include two layers 14a, 14b, but in appropriate circumstances, the coating 14 can have one layer or more than two layers, Each of the layers 14a, 14b can include polymer chains 16. The composition of the polymer chains 16 in each of the layers may be the same or different. The polymer chains 16 can be strongly attached to the surface 12a of the pigment 12. The term "attached" can mean that the polymer chains 16 are chemically or physically adhered to the surface 12a of the pigment 12. The coating 14 can also include inter- chain cross-links 18 that link the polymer chains 16.

The pigment can be, but is not limited to, metal oxides, metal oxide encapsulated materials, silica, borosilica, silica coated materials, mica, glass, iron or aluminum. In one example, the coated pigment 10 utilized can include a pigment having a thickness in a range from 0.5 nm to 500 μιχι. In another example, the thickness of the pigment can be in a range from 20 nm to 100 μπι. In yet another example, the thickness of the pigment can be in a range from 50 nm to 1 μιη. In yet another example, the size of the pigment can be in a range from 100 nm to 5000 μη . In yet another example, the size of the pigment can be in a range from 500 nm to 100 um. In yet another example, the size of the pigment can be in a range from 1 μηι to 50 μηι.

The strong interactions between the polymer chains 16 and the surface 12a of the pigment 12 can provide robustness and stability of the coating. The term "robustness and stability of the coating" herein can mean the survivability of coated pigments under circulation test, chemical resistance and other process conditions.

Moreover, uneven coating on the pigments surface can disrupt orientation of the pigments and result in poor aesthetic performance. On the other hand, the surfaces of the disclosed coated pigment 10 can be smooth so as to allow maximal contact among a plurality of coated pigments 10 and good film formation.

In general, the disclosed coating system can include a plurality of the coated pigments 10 and there can be several steps involved in the manufacture of the disclosed coating system. First, pigments can be encapsulated with polymers. In one example, the polymer encapsulated pigments can be easily dispersed in solvents. The polymer encapsulated pigments are kept in wet form and stored, for example, as concentrated pastes or slurry. Additional solvent can be added at any time to achieve desired coated pigment concentration prior to the application of the coating system. When the coating system is applied onto a substrate, the solvent can evaporate so as to form a film. In one example, the thickness of the film that is formed on the substrate can be between 1 and 10 μηι. In another example, the thickness of the film that is formed on the substrate can be between 2.5 and 3 μιη. In yet another example, the thickness of the film that is formed on the substrate can be 2.5 μηι. Good adhesion between the film and the substrate can be achieved by physical or chemical interactions between the polymers included in the coated pigments and the substrate. While the entanglement among polymer chains grafted from different coated pigments can result in good film mechanical properties, the polymer chains can be further modified with functional groups and allow the formation of cross-linked networks on the pigments.

In one embodiment, surface-initiated polymerization can be used to fabricate a thick polymer coating on the pigment. In this process, initiator moieties, which are defined as functional groups that can initiate polymerization of polymerizable monomers, are first immobilized on the surfaces of the pigments. Then, with subsequent polymerization, thick polymer chains can be grown from the surfaces of the pigment.

The coating thickness can be readily controlled simply by varying the reaction time. In addition, other factors including, but not limited to, monomer concentration, polymerization time, solvent, and catalyst can be used to control the thickness of the coating as well. The average polymer coating thickness, which can be measured by direct observation via

transmission electron microscopy, ranges from a few nanometers to more than 100 nm.

Two factors, grafting density and average molecular weight of polymer chains, also can determine coating thickness. The molecular weight of the polymer chains can be adjusted by tuning the polymerization conditions such as polymerization time, monomer concentration, solvent, reaction temperature, and catalysts. Varying the grafting density can be achieved by controlling the initiator area density on the surfaces of the platelets. Using controlled/living radical polymerization, such as atom transfer radical polymerization (U.S. Patent 5,763,548), itroxide mediated polymerization (U.S. Patent 6,353,107), and reversible addition- fragmentation chain transfer polymerization (U.S. Patent 7,205,362), polymer chains can be grown at similar rates from surfaces, thereby leading to a coating with a uniform structure on the surface of the substrates.

Moreover, by eliminating unbounded initiators in solution, most polymer chains formed are anchored to platelet surfaces. As a result, there can be minimal amounts of unbounded polymer chains in solution. The polymerization mixture can retain low viscosity throughout the reaction process with or without the addition of solvent. Simple purification procedures can readily separate polymer encapsulated platelets from the other components in the reaction solution.

In one example, a coupling reagent that includes an initiator can be used to functionalize pigment surfaces with initiator moieties. The initiator has a chemical structure X-R-Y, where X denotes a surface active group, Y denotes an initiator moiety, and R denotes a spacer. The initiator moieties can be anchored to the pigment upon the reaction between surface active groups and functional groups that are present on surfaces of the pigments.

In another example, an initiator can be immobilized on pigment surfaces through a multiple step process. In one instance, the multiple step process can be a two-step process. In this instance, a surface active molecule, X-Rl-A, is first applied to the surface of a pigment. While functional group X immobilizes the molecules to the surfaces, functional group A can allow further chemical reactions on pigment surfaces and lead to the initiator moiety, Y, to be on the surfaces of the pigment.

The surface active group X can be, but is not limited to, mono-, di-, and tri- alkoxylsilanes, mono-, di- and tri-halosilanes, carboxylic acid, phosphonic acid and other chemical groups that have strong affinity to metal, metal oxide or silica surfaces. In case of trialkoxysilane and trihalosilane, the intermolecular condensation among organosilane molecules can lead to the formation of high density robust coating of such molecules. In some instances, the selection of X can be dependent upon the type of pigment utilized. For example, silanes can be used to modify the surface of silica, alumina, and glass, while molecules with carboxylic acid can be used to functionalize surfaces of iron oxide. The initiator moiety Y can be any functional group that initiates controlled radical polymerization. The initiator moiety Y can be, but is not limited to, an activated halogen atom, alkoxyamine, dithioester, dithiocarbamates, trithiocarbonates and xanthates, organic peroxides, and azo compounds.

A variety of polymerization methods, such as radical polymerization, controlled radical polymerization, anionic polymerization, and cationic polymerization, have been used to grow polymer encapsulation from surfaces. In one implementation, controlled radical polymerizations can be used to grow polymer chains with controlled structures from surfaces. In one example of the coated pigment, the polymeric chains can include homopolymers, random copolymers, gradient copolymers, block polymers, grafted copolymers, star copolymers or any combination thereof. In one implementation, the polymer chains can include cross-links to form a polymer network coating on the pigment.

In one example, after the initiator is immobilized on the surface of the platelet, the platelet can be purified via filtration to remove any unbounded coupling reagents before proceeding to the polymerization reaction. In another example where the existence of free coupling reagent in solution does not significantly increase the solution viscosity or adversely alter other process conditions in the following polymerization, the reaction solution can be used directly without further purification.

The initiator-immobilized platelets then can be dispersed in a monomer solution. The monomer solution can include one type of monomer or mixtures of different types of monomers. Examples of monomers that can be used include, but is not limited to, styrenes, (meth)acrylates, (meth)acrylamides, (meth)acrylic acids, acrylonitrile, vinylpyridines, maleimides, vinyl acetate, vinyl chloride, vinylidene chloride and isoprene. Following dispersion of the initiator immobilized platelets into the monomer solution, polymerization from surfaces can lead to the formation of polymer chains that are attached to the platelet. Because of its small size, initiator molecules can be immobilized on the surface of the platelet with high area density. Therefore, this approach can allow the synthesis of polymer coatings with high grafting density. As polymerization from the surface of the platelet follows the same mechanism as solution polymerization, monomers that can be polymerized in solution polymerization can be directly adopted into the disclosed method.

Living or controlled radical polymerization, such as atom transfer radical polymerization, nitroxide mediated polymerization, and reversible addition-fragmentation chain transfer polymerization, can allow synthesis of polymers with controlled molecular weight,

polydispersity, and architectures from many different types of monomers. By using living polymerization, the disclosed method can allow the thickness of the coating to be controlled from a few nanometers up to hundreds of nanometers and further allows the structure of polymer coating on platelets to be controlled. Transmission electron microscopy can be used to directly observe the coating thickness and uniformity on particle or platelet surfaces. In one example, the coating thickness of each of the coated platelets can be substantially uniform. In this instance, the average and standard deviation of coating thickness can be calculated from transmission electron microscope pictures from more than 10 different coated platelets at a magnification between x20,000 and χΙΟΟ,ΟΟΟ. As shown in Figure 4, the standard deviation of the coating thickness on the platelets can vary less than 15% of the average coating thickness, where the scale bar is 100 nm.

The living nature of the controlled radial polymerization can be used in the disclosed method also enables the synthesis of a multilayered coating on the platelet. In one example, a second monomer or a second set of monomers can be added to the reaction flask after a predetermined reaction time. In another example, after the end of the first polymerization, the platelets can be separated from the reaction mixtures, purified, and then subjected to a second polymerization with a second monomer or second set of monomers. In both cases, a second layer of coating can be formed with a composition that is different from that of the first layer. In the latter approach, the method can allow the synthesis of a second layer with a completely different composition. The above steps can be repeated any number of times and in any different combinations to provide a multilayered coating.

The encapsulation can be composed of chains or networks of polymer or copolymers of a variety of monomers. Examples of monomers that can be used in the disclosed method include, but are not limited to, acrylonitrile, styrene, divinylbenzene, 4-methylstyrene, 3-methylstyrene, 2-methylstyrene, 4-vinylanisole, 4-fluorostyrene, 2-fluorostyrene, 3 -fluoro styrene, 4- chloromethylstyrene, 4-(tert-butyl)styrene, 3-chlorostyrene, methyl methacrylate, methyl acrylate, ethyl methacrylate, ethyl acrylate, n-propyl acrylate, n-propyl methacrylate, iso-propyl methacrylate, iso-propyl acrylate, n-butyl acrylate, n-butyl methacrylate, sec-butyl acrylate, sec- butyl methacrylate, tert-butyl acrylate, tert-butyl methacrylate, tert-amyl methacrylate, n-hexyl acrylate, n-octyl methacrylate, 2-ethylhexyl acrylate, n-decyl methacrylate, iso-decyl acrylate, iso-decyl methacrylate, undecyl methacrylate, n-dodecyl acrylate, n-dodecyl methacrylate, 1 - hexadecyl methacrylate, stearyl acrylate, stearyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, 3,3,5-trimethylcyclohexyl methacrylate, benzyl acrylate, benzyl methacrylate, pentabromophenyl acrylate, pentabromophenyl methacrylate, pentafluorophenyl acrylate, pentafluorophenyl methacrylate, phenyl acrylate, phenyl methacrylate, 1,1,1,3,3,3- hexafluoroisopropyl acrylate, lH,lH,2H,2H-heptadecafluorodecyl acrylate, 1H,1H,2H,2H- heptadecafluorodecyl methacrylate, lH,lH,3H-hexafluorobutyl acrylate, 1H,1H,3H- hexafluorobutyl methacrylate, lH,lH,3H-tetrafluoropropyl methacrylate, 1H,1H,5H- octafluoropentyl acrylate, lH,lH,5H-octafluoropentyl methacrylate, 1H,1H,7H- dodecafluoroheptyl methacrylate, ΙΗ,ΙΗ-heptafluorobutyl acrylate, 2,2,2-trifluoroethyl acrylate, 2,2,2-trifluoroethyl methacrylate, hexafluoro-iso-propyl methacrylate, pentafluorophenyl acrylate, pentafluorophenyl methacrylate, methacrylamide, acrylamides, 4-vinyl pyridine, N,N- dimethylaminoethyl methacrylate, Ν,Ν-diethylaminoethyl methacrylate, glycidyl methacrylate, 2 -hydroxy ethyl acrylate, and 2 -hydroxy ethyl methacrylate, glycidyl acrylate, 4-vinylaniline, 3- vinylaniline, N-iso-propylacrylamide, Ν,Ν-diethylacrylamide, N,N-dimethylacrylamide, poly(ethylene glycol) methacrylate, poly(ethylene glycol) acrylate, poly(ethylene glycol) methyl ether methacrylate, poly(ethylene glycol) ethyl ether methacrylate, poly(ethylene glycol) methyl ether acrylate, 1,10-decanediol dimethacrylate, 1,3-butanediol dimethacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, 1,4-diacryloylpiperazine, 1,4-phenylene diacrylate, 1,5-pentanediol dimethacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, 1,9- nonanediol dimethacrylate, 2,2-bis(4-methacryloxyphenyl)propane, 2,2-bis[4-(2- acryloxyethoxy)phenyl]propane, 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane, 2,2-dimethylpropanediol dimethacrylate, diethylene glycol diacrylate, diethylene glycol dimethacrylate, dipropylene glycol dimethacrylate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, ethylene glycol dimethacrylate, ethylene glycol dimethacrylate, N, N' ethylene bisacrylamide, N,N'-methylenebisacrylamide, Ν,Ν'-hexamethylenebisacrylamide, N,N- diallylacrylamide, tetraethylene glycol dimethacrylate, trans- 1,4-cyclohexanediol dimethacrylate, triethylene glycol diacrylate, triethylene glycol dimethacrylate, triethylene glycol dimethacrylate, 1,1,1-trimethylolpropane triacrylate, 1,1,1-trimethylolpropane trimethacrylate, dipentaerythritol pentaacrylate, pentaerythritol tetraacrylate, pentaerythritol triacrylate, poly(ethylene glycol) diacrylate, and poly(ethylene glycol) dimethacrylate.

In one instance, the thickness of the polymer encapsulation can define the amount of the polymer loading on the pigment and can affect the pigment-to-binder (P B) ratio of the final coating. In one example, the disclosed coating system can have a high P/B ratio. Since the pigments can be evenly encapsulated in the polymers, the disclosed coating system can be prepared with a much higher P/B ratio than that of conventional paint/ink systems. In this instance, the coating system can be prepared with a P/B ratio of up to 10, as compared to conventional paints/inks, which have P/B ratios that are typically less than 1. For example, for paints made from Silberline Sparkle Silver Premium® 695, which can include an aluminum pigment of average particle size of 12 μηι, conventional paints/inks can have typical P/B ratios of less than 1 , whereas the disclosed coating system can be prepared with a P/B ratio of 5 or higher.

Furthermore, to ensure proper film formation and good adhesion of the coating, the polymer chains in the encapsulation can be of reasonable length and have certain flexibility so that the rearrangement of polymer chains will provide enough physical entanglement and/or expose enough chemical reaction sites to the pigments or the polymer chains from other coated pigment encapsulations. The term "flexibility" herein can mean that the polymer chains of the polymer coating can readily rearrange their configuration such that the polymer chains can follow the surfaces of other coated pigments and thereby increase the contact areas between the coating surfaces.

In another instance, the polymer chains can be attached to the surface of the substrates so as to provide robustness and stability of the coating. The term "robustness and stability" herein can mean the survivability of the coated substrates under circulation test, repeated solvent wash and typical reaction conditions. In these instances, the polymer chains can have the flexibility to maximize their contact with color pigments and greatly enhance the adhesion between the color pigments and the surfaces of the coated substrates.

In one embodiment of the disclosed coating system, the coating system can include a plurality of the coated pigments 10 and a solvent or solvent mixture only. A coating system of this embodiment can be prepared simply by dispersing the plurality of coated pigments 10 in a solvent or a solvent mixture. The amount of the coated pigments in the coating system can be from 10% to 70%. Optionally, the amount of the solvent in the coating system can range from 25% to 85%.

In one example, the solvent or solvent mixture utilized can be a good solvent of the polymer segments on surfaces of the encapsulation and as such, can prevent the collapse of polymer chains and pigment particles from agglomeration. The solvent or solvent mixture used in the disclosed colored system can be water, lower alcohols, hydrocarbons, ethers, esters, ketones, glycol ethers, pyrrolidones, sulfoxides, and mixtures thereof. Examples of a solvent that can be used include butanol, ethyl acetate, butyl acetate, xylene, toluene, propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, and N-methylpyrrolidone and methyl ethyl ketone.

In yet another embodiment, the plurality of coated pigments 10 can be dispersed in systems conventionally used in the art of paints and inks to achieve optimal adhesion and/or reduce the amount of external resin required in the formulation. In this embodiment, the composition of the polymer encapsulation can be adjusted to enhance the dispersion of the pigments, promote adhesion between the pigments and the rest of the coating, and/or provide barrier function to protect pigments.

Without being bound to theory, the mechanical properties of the coating film can originate from the physical entanglement of the polymer chains of different coated pigments 10. In one occurrence, the film integrity can be further strengthened by introducing reactive sites on the encapsulation 14 and the formation of cross-linked networks after the application of coated system to a substrate. Similarly, the adhesion between the coating film and the coated pigment can be of chemical or physical origin.

The reduction of binder in the final coating also can affect the aesthetics of the final coating products. In another occurrence, increased coated pigment loading in the coating system can lead to chroma or opacity enhancement of the final coating. For effect pigments, it is known that excessive resin in paint/ink will disrupt orientation of pigment. In one example, since the coating system can be formed with a high P/B ratio and the coated pigments can be evenly embedded in the polymer encapsulation, the final orientation of the coated pigments, and therefore the aesthetics of the coating, can be greatly improved as compared to conventional methods.

The polymer encapsulation also can be designed to provide the coated pigments with superior stability in the coating systems and in the film that has been formed on a substrate. For example, Al pigments can be susceptible to the attack of water, which can degrade Al and generate hydrogen gas that can impose hazards during shipping and storage. In one example, incorporation of a hydrophobic coating on an aluminum pigment can effectively retard the penetration of water to the surface of Al flakes and thereby enhance the stability of the disclosed coating system. For the same reason, the final coating system can have better water resistance as compared to a conventional coating system made from pigments without polymer encapsulation.

Further, conventional paints/inks typically can require certain viscosity criteria that need to be met prior to application. For example, in ink applications, the amount of pigment loading can be limited by the viscosity of the ink mixtures. Excessive pigment loadings can often result in increased viscosity and reduced printability. In resin-less inks, due to the high pigment to binder ratio, significant amount of pigments can be dispersed in the solvent without significantly increasing the ink viscosity. In one example, the disclosed coating system optionally does not require a viscosity criteria. In one instance, the coating system can be applied in low viscosity. In this instance, since the coating system can include a lower percentage of resin as compared to conventional paints/inks, the disclosed coating system can solidify in a much shorter period of time when applied onto a substrate as compared to that of conventional paints/inks. Another advantage is that since the resin-less paints/inks can contain relatively small amounts of resin as compared to conventional coating systems, the resin-less coating can be dried in a much shorter period of time than conventional coating systems.

Yet another advantage is that because optionally no external resin or optionally no dispersant is required in the disclosed coating system, the disclosed system can allow great ease during the formulation process. For instance, the coated pigments 10 can be stored in a slurry form. Bulk solvents can be added immediately prior to the application of the coating system.

The resin less system can be applied using standard coating/printing methods.

Application methods for the resin-less paint include, but are not limited to, spray and dip coating. Application methods for the resin-less ink include, but are not limited to, gravure, flexo and offset printing.

In one embodiment of an article, the article includes a coating the can contain the disclosed coating system.

EXAMPLES

Example 1 - Preparation of polystyrene coated Al pigment

480 g aluminum paste (Silberline Sparkle Silver® Premium 695, 75.28% nonvolatile), 1200 mL toluene, and 3 mL 3-(trimethoxysilylpropyl)-2-bromo-2-methylpropionate were added to a 2 L reaction flask equipped with a mechanic stirrer and a condenser. The reaction mixture was heated up and was kept under reflux for 24 hours. Once the reaction time was complete, the mixture was cooled down to room temperature. The flakes were vacuum filtered. Two washes of toluene were applied.

32.3 g initiator modified Al paste (containing 20 g of nonvolatile), 0.423 g CuBr, 200 mL

Styrene, and 190 mL PM Acetate were added to a 500 mL reaction flask equipped with a mechanical stirrer and a heating mantle: The solution was degassed with nitrogen and heated to

80°C under constant stirring. In a separated flask, pentamethyldiethylenetriamine (PMDETA) was degassed with nitrogen for 30 min. Then 0.83 mL of degassed PMDETA was transferred to the reaction flask with a nitrogen purged syringe. After 4 hours of polymerization, the reaction was stopped. The pigments were purified with centrifugation. Thermal gravimetric analysis confirmed polymer composed 15.86% of the dried pigments. The pigments were stored as wet paste in PM acetate.

Example 2 - Resin-less paint of polystyrene coated Al from Example 1

Resin-less paint of pigment made in Example 1 was prepared by diluting wet paste with PM acetate. The final paint has pigment weight concentration of 10.1%. Paint was siphon sprayed onto the plastic panel of polystyrene, poly(methyl methacrylate) and acrylonitrile butadiene styrene (ABS). The sprayed panel was further dried in oven. Example 3 - Preparation of poly(methyl methacrylate) coated Al pigment

4.8 kg aluminum paste (Silberline Sparkle Silver® Premium 695, 75.68% nonvolatile), 12 L PM acetate, and 16 mL 3-(trimethoxysilylpropyl)-2-bromo-2-methylpropionate were added to a 20 L reaction flask equipped with a mechanic stirrer and a condenser. The reaction mixture was heated up and was kept under reflux for 6 hours. Once the reaction time was complete, the mixture was cooled down to room temperature. The flakes were vacuum filtered. Two washes of PM acetate were applied.

61.6 g initiator modified Al paste (containing 40 g of nonvolatile), 0.106 g CuBr, 200 mL methyl methacrylate, and 180 mL PM Acetate were added to a 500 mL reaction flask equipped with a mechanical stirrer and a heating mantle: The solution was degassed with argon and heated to 80°C under constant stirring. In a separated flask, pentamethyldiethylenetriamine (PMDETA) was degassed with argon for 30 min. Then 0.16 mL of degassed PMDETA was transferred to the reaction flask with a argon purged syringe. After 4 hours of polymerization, the reaction was stopped. The pigments were purified with centrifugation. Thermal gravimetric analysis confirmed polymer composed 20.19%) of the dried pigments. The pigments were stored as wet paste in PM acetate.

Example 4 - Resin-less paint of poly(methyl methacrylate) coated Al from Example 3 Resin-less paint of pigment made in Example 3 was prepared by diluting the wet paste with PM acetate. The final paint has pigment weight concentration of 5.8%. Paint was siphon sprayed onto the plastic panel of poly (methyl methacrylate) and ABS. The sprayed panel was further dried in oven.

Example 5 - Article including the resin-less system

The resin-less paint prepared in accordance with Example 4 was applied onto (a) poly(methyl methacrylate), (b) acrylonitrile butadiene styrene and (c) polystyrene panels. The coatings were formed via siphon spray of the resin-less paints. The results are shown in Figure 2.

Example 6 - Cross-hatch adhesion test

Cross-hatch adhesion test of the coating in Example 4 was conducted in accordance with ASTM D3359 standards. The results are shown in Figure 3. As shown in Figure 3, the coating prepared with the disclosed method can provide good performance in a standard cross-hatch adhesion test.

Example 7 - Scanning electron microscopy of the resin-less coating

The resin-less paint coated poly(methyl methacrylate) panel in Example 5 was analyzed with scanning electron microscopy. The results are shown in Figure 4. Figure 4 shows superior orientation of the pigments, which allows superior aesthetics of the coating.

Aspects:

1. A coating system, comprising:

a plurality of coated pigments; and

a solvent or a solvent mixture,

wherein each of the coated pigments includes

a pigment having a surface, and a coating surrounding the pigment, the coating including polymer chains, the polymer chains surrounding the surface of the pigment being attached to the surface of the pigment, and

wherein the polymer chains of the plurality of the coated pigments are present in an amount sufficient to form a film and adhere the film to a substrate when the coating system is applied onto the substrate.

2. The coating system of any of the aspects, wherein the system does not include any additional dispersants and/or resins other than those that are attached to the surface of the pigment.

3. The coating system of any of the aspects, wherein the coating has at least one layer, and the at least one layer includes polymer chains, and the polymer chains are substantially uniform in structure.

4. The coating system of any of the aspects, wherein the coating has a plurality of layers, each layer including the polymer chains, the polymer chains in each layer being substantially uniform in structure. 5. The coating system of any of the aspects, wherein the pigment includes at least one selected from the group consisting of metal oxides, metal oxide encapsulated materials, silica, borosilica, silica coated materials, mica, glass, iron and aluminum.

6. The coating system of any of the aspects, wherein the coating includes an inner passivation layer and an outer dispersion layer.

7. The coating system of any of the aspects, wherein the coating includes inorganic and organic colorants. 8. The coating system of any of the aspects, wherein the coating includes inter-chain cross-links.

9. The coating system of any of the aspects, wherein the solvent is selected from the group consisting of water, lower alcohols and/or mixtures thereof.

10. The coating system of any of the aspects, wherein the coating system is an ink or paint system.

11. The coating system of any of the aspects, wherein the pigment-to-binder ratio is between 1 to 10.

12. The coating system of any of the aspects, wherein the substrate is plastic or metal.

13. A method of producing the coating system of any of the aspects, consisting of: mixing the plurality of coated pigments with the solvent or the solvent mixture.

14. An article comprising:

a coating that comprises the coating system of any of the aspects.

15. A method of applying a coating composition, comprising:

applying the coating system of any of the aspects onto a substrate.

16. The coating system of any of the aspects, wherein the colored system does not include alkyd, polyester, polyamide, polyimide, silicone, phenolic, urea, melamine, epoxy, polyurethane, polyolefmes, polyvinyl, and polyacrylic resins.

17. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from 0.5nm to 500 microns. 18. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from 20nm to 100 microns.

19. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from 50nm to 1 micron.

20. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from lOOnm to 5000 microns. 21. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from 500nm to 100 microns.

22. The coating system of any of the aspects, wherein each of the coated pigments includes a pigment having a thickness in a range from 1 micron to 50 microns.

23. The coating system of any of the aspects, wherein the polymers of the coated pigments provide robustness and stability of the film.

24. The coating system of any of the aspects, wherein the surface of each of the coated pigments is smooth.

25. The coating system of any of the aspects, wherein the coating system is configured such that when the coating system is applied on the substrate, the film that is formed has a thickness of 1 to 10 microns.

26. The coating system of any of the aspects, wherein the coating system is configured such that when the coating system is applied on the substrate, the film that is formed has a thickness of 2.5 to 3 microns. 27. The coating system of any of the aspects, wherein the coating system is configured such that when the coating system is applied on the substrate, the film that is formed has a thickness of 2.5 microns.

28. The article of aspect 14, wherein the coating has a thickness of 1 to 10 microns.

29. The article of aspect 14, wherein the coating has a thickness of 2.5 to 3 microns.

30. The article of aspect 14, wherein the coating has a thickness of 2.5 microns.

31. The coating system of any of the aspects, wherein a coating thickness of each of the coated pigments ranges from a few nanometers to more than 100 nm.

32. The coating system of any of the aspects, wherein each of the coated pigments is obtained by modifying the surface of each of the substrates so that an initiator is immobilized to the surface of each of the substrates.

33. The coating system of any of the aspects, wherein the immobilized initiator contains a surface active group, a spacer and an initiator moiety.

34. The coating system of any of the aspects, wherein the surface active group is at selected from mono-, di-, and tri-alkoxylsilanes, mono-, di- and tri-chlorosilanes, carboxylic acid, organophosphorous compounds, and other chemical groups that have strong affinity to metal, metal oxide or silica surfaces.

35. The coating system of any of the aspects, wherein the initiator moiety is selected from a halogen atom, alkoxyamine, dithioester, dithiocarbamates, trithiocarbonates, xanthates organic peroxides, and azo compounds. 36. The coating system of any of the aspects, wherein each of the pigments is functionalized via silica or metal oxide encapsulation.

37. The coating system of any of the aspects, wherein a coating thickness of each of the coated pigments is substantially uniform such that when an average and standard deviation of the coating thickness are calculated from transmission electron microscope pictures from more than 10 different coated pigments at a magnification between x20,000 and xl 00,000, the standard deviation of the coating thickness on the substrates varies less than 15% of the average coating thickness, where the scale bar is 100 nm.

38. The coating system of any of the aspects, wherein a pigment-to-binder of the coating system is 5 or higher.

39. The coating system of any of the aspects, wherein a pigment-to-binder of the coating system is 5 to 10.

40. The coating system of any of the aspects, wherein the polymers have flexibility such that the polymer chains can readily rearrange their configuration so as to increase contact areas between the coating surfaces.

41. The coating system of any of the aspects, wherein the coating system includes the coated pigments in an amount of 10 to 70% by weight.

42. The coating system of any of the aspects, wherein the coating system includes the coated pigments in an amount of 25 to 85% by weight.

43. The coating system of any of the aspects, wherein the solvent is selected from the group consisting of water, lower alcohols, ethers, esters, ketones, glycol ethers, pyrrolidones, sulfoxides and/or mixtures thereof. 44. The coating system of any of the aspects, wherein the solvent is selected from the group consisting of butanol, ethyl acetate, butyl acetate, xylene, toluene, propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, N-methylpyrrolidone and methyl ethyl ketone.

45. The coating system of any of the aspects, wherein the coating system does not require a viscosity criteria.

While the disclosed coated pigments and methods have been described in conjunction with a preferred embodiment, it will be apparent to one skilled in the art that other objects and refinements of the disclosed coated pigments and methods may be made within the purview and scope of the disclosure.

The disclosure, in its various aspects and disclosed forms, is well adapted to the attainment of the stated objects and advantages of others. The disclosed details are not to be taken as limitations on the claims.