Description

The present invention relates to an organic light-emitting element which emits delayed fluorescence comprising specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives or 1 ,2,4-thiadiazole derivatives in the light-emitting layer, a light-emitting layer comprising the specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives or 1 ,2,4- thiadiazole derivatives, specific specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4- oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives and an organic light emitting element comprising the specific 1 ,2,4-azole derivatives as well as a light emitting layer comprising the specific 1 ,2,4-azole derivatives; the use of the specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives for electrophotographic photore- ceptors, photoelectric converters, sensors, dye lasers, solar cell devices and organic light emitting elements, and the use of the specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4- oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives for generating delayed fluorescence emission. The specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives and 1 ,2,4- thiadiazole derivatives exhibit TADF (thermally activated delayed fluorescence) characteristics, usually at 298 K.

TADF is an effective triplet-harvesting process that involves up-conversion of triplet (T-i) to sin- glet (Si) excited states.

Derivatives exhibiting TADF characteristics are characterized by having a sufficiently small energy gap between Si and Τ-ι (ΔΕ _δ τ) to enable up-conversion of the triplet exciton from T-i to Si. The present invention therefore relates to organic light emitting elements, which emit delayed fluorescence comprising the specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives as thermally activated delayed fluorescence (TADF) emitters (guests) and/or hosts. The organic light emitting elements show high electroluminescent efficiency.

The development of OLED luminescent materials is an important issue and these materials have been classified into two major categories. The first category concerns fluorescent materials, which can harvest only the singlet excitons (25%) that are generated by electrical excitation. The second category concerns phosphorescent materials, which can harvest the triplet excitons generated (75%). The branching ratio of singlet and triplet excitons is 1 : 3. Therefore, in recent devices, phosphorescent materials and their related technologies have been indispensable to obtain high EL efficiency. However, phosphorescent materials are generally based on organo- metallic compounds containing Ir or Pt. These metals are rather expensive and are dependent on limited global resources.

Recently, the alternative concept of thermally activated delayed fluorescence (TADF) as a third generation luminescent material, instead of the conventional fluorescent and phosphorescent materials was described by C. Adachi et al. in Adv. Mater., 2009, 21 , 4802; Appl. Phys. Lett., 201 1 , 98, 083302 and Chem. Commun., 2012, 48, 9580.

The TADF strongly depends on HOMO-LUMO separation in a single molecule. TADF materials have a sufficiently small energy gap between Si and Τ-ι (ΔΕ _δ τ) to enable up-conversion of the triplet exciton from T-i to Si. This small ΔΕ _δ τ enables TADF materials to realize 100% of the exci- ton formation generated by electrical excitation at Si.

AEST is the difference between the lowest excited singlet state Si and the lowest excited triplet state T-i of a molecule. In the case that the energy gap between Si and Τ-ι (ΔΕ _δ τ) is small enough to provide a thermal up-conversion of the triplet exciton from T-i to Si according to a Boltzmann distribution, or pursuant to the thermal energy k _B T, a thermally activated light emission from the Si state is allowed (TADF), based on the following equation: lnt(Si→S ₀ )/lnt(Ti→To) = k(SiVk(Ti)exp(-AE/k _B T)

wherein,

lnt(Si→So)/lnt(T ₁ →T ₀ ) is the intensity ratio of the emission from the Si state and the T-i state k _B is the Boltzmann constant

T is the absolute temperature

k(Si)/k(T-i) is the rate ratio of the transition processes from the singlet Si state and from the triplet T-i state in the electronic ground state So.

WO 2006/1 14377 A1 relates to electroluminescent devices comprising organic layers containing triazole compounds of formula (I) or (II):

(I) or (")

The triazole compounds are suitable components of organo-electroluminescent layers, according to the examples as a host component. According to the examples, the following triazole compounds are used as host materials in OLEDs: wherein Het is a substituent of formula (S1 -1 ) or (S1 -2)

The compounds are used as hosts with bipolar properties for phosphorescent as well as fluorescent emitters in light-emitting elements. Examples for compounds G1 are:

and

Q. Li et al., Dyes and Pigments 101 (2014) 142-148 concerns the synthesis of new bipolar host materials based on 1 ,2,4-oxadiazole for blue phosphorescent OLEDs. The following host materials are mentioned:

J. Jin et al., Chem. Mater. 2014 (26) 2388-2395 concerns bipolar host materials based on 1 ,2,4- thiadiazole for phosphorescent organic light-emitting diodes. The following host materials are mentioned:

CN 10358870 A relates to the design and synthesis of 3,5-diphenyl substituted 1 ,2,4-thiadiazole derivatives as well as the application of the 3,5-diphenyl substituted 1 ,2,4-thiadiazole derivatives in an organic electroluminescent device (OLED). The 3,5-diphenyl substituted 1 ,2,4-thiadiazole derivatives may be used in the light-emitting layer of an OLED as host or light-emitting material or in a transport layer of an OLED as hole or electron transport material. According to the examples in CN 10358870 A, the 3,5-diphenyl substituted 1 ,2,4-thiadiazole derivatives are used as host materials in OLEDs for phosphorescent green emitters. The following 3,5-diphenyl sub- stituted 1 ,2,4-thiadiazole derivatives are explicitly mentioned:

None oft the documents mentioned above mentions TADF (thermally activated delayed fluorescence) characteristics of the compounds disclosed.

An object of the present invention is to provide a highly efficient and practically useful organic light-emitting element and an organic material suitable for providing the organic light-emitting element.

It has surprisingly been found that certain specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4-oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives emit delayed fluorescence, usually at 298 K, and are useful for providing an organic light-emitting element having a high efficien- cy. The temperature of 298 K mentioned before means that the specifically substituted 1 ,2,4- triazole derivatives, 1 ,2,4-oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives of formulae (I) and (Ι') according to the present invention show delayed fluorescence at room temperature (298 K) and does not mean that the specifically substituted 1 ,2,4-triazole derivatives, 1 ,2,4- oxadiazole derivatives and 1 ,2,4-thiadiazole derivatives according to the present invention do not emit delayed fluorescence at lower temperatures and at higher temperatures.

Accordingly, the present invention relates to an organic light-emitting element, comprising a light-emitting layer comprising i) a compound of formula (I) as guest and a host material; or

ii) a compound of formula (I) as host and a fluorescent guest materi- al, wherein

wherein

X is O, S or N-Y ⁴ -R ⁴ ,

Y ¹ and Y ² and Y ⁴ are independently of each other a direct bond, CrC ₂ 5-alkylene, or C ₆ -Ci ₀ - arylene, which is unsubstituted or substituted by one or more groups R ³ ;

R ¹ and R ² are independently of each other hydrogen, deuterium, F, CI, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ , or a group of formula (Xa) or (Xd); preferably, R ¹ and R ² are independently of each other hydrogen, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₀ aryl group, which is unsubstituted or substituted by one or more groups R ³ , or a group of formula (Xa) or (Xd);

R ³ is deuterium, F, CI, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, or a C ₆ -Ci ₄ aryl group; preferably, R ³ is a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₀ aryloxy group, or a C ₆ -Ci ₄ aryl group;

R ⁴ is a CrC ₂₅ alkyl group, a C ₆ -Ci ₀ aryl group, which is unsubstituted or substituted by one or more roups R ³ , or a group of formula (Xa) or (Xd);

X ¹ is O, S, N(R ¹⁵ ), C(=0), C(R ¹⁶ )(R ¹⁷ ), B(R ¹⁸ ), or Si(R ¹⁹ )(R ²⁰ ); preferably, X ¹ is O, S, C(O), N(R ¹⁵ ), or C(R ¹⁶ )(R ¹⁷ );

R ¹⁰ , R ¹¹ , R ²¹ and R ²¹ are independently of each other hydrogen, deuterium, F, CI, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , or a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ; preferably, R ¹⁰ , R ¹¹ , R ²¹ and R ²¹ are independently of each other hydrogen, or a CrC ₂₅ alkyl group;

R ¹⁵ , R ¹⁶ , R ¹⁷ , R ¹⁸ , R ¹⁹ and R ²⁰ are independently of each other a C C ₂₅ alkyl group, or a C ₆ - Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ; wherein at least one group of formula (Xa), or (Xd) is present in the compound of formula (I), characterized in that it emits delayed fluorescence.

The present invention is also directed to the use of compounds of formula (I) for generating de- layed fluorescence emission.

Thermally activated delayed fluorescence (TADF, E-type delayed fluorescence) is a promising way to obtain a high efficiency of exciton formation by converting spin-forbidden triplet excitons up to the singlet level by the mechanism of reverse intersystem crossing (RISC). In a TADF emitter, the upconversion mechanism uses the vibronic energy that, at sufficiently high temperatures (usually about 298 K), allows all of the excitons in an OLED to eventually produce light through singlet decay.

E-type delayed fluorescence is defined herein as a process in which the first excited singlet state (Si) becomes populated by a thermally activated radiationless transition from the first excited triplet state (Ti).

The present invention is also directed to an organic light-emitting element, comprising a compound of formula (I) in the light-emitting layer, characterized in that it emits delayed fluores- cence.

The organic light-emitting element preferably offers an external quantum efficiency of more than 5%, especially more than 10%. Further, the organic light-emitting element of the present invention shows reduced efficiency roll-off characteristics at high luminance.

The compound of formula (I) has preferably a difference between excited singlet energy (Si) and excited triplet energy (T^ ((ΔΕ _δ τ) of 0.5 eV or less, more preferably AE _S T of 0.35 eV or less, i.e. of 0.01 to 0.5 eV, especially 0.01 to 0.35 eV. In the meaning of the present invention, an organic light-emitting element, comprising a light- emitting layer comprising a compound of formula (I), characterized in that it emits delayed fluorescence, is preferably an organic light-emitting element, comprising a light-emitting layer comprising a compound of formula (I), wherein the compound of formula (I) has a difference between excited singlet energy (Si) and excited triplet energy (Τ-ι) (ΔΕ _δ τ) of 0.5 eV or less, more preferably AE _ST of 0.35 eV or less, i.e. a AE _ST of 0.01 to 0.5 eV, especially 0.01 to 0.35 eV.

The determination of ΔΕ _δ τ can be carried either by quantum mechanical calculations (for example TD-DFT (time dependent density functional theory) calculations, for example with commercially available Gaussian 09 or ADF Amsterdam Density Functional software programs; for ex- ample as described in Adv. Mater. 2008, 20, 3325-3330) or experimentally. Experimental determination of AE

i)

AEST can be determined based on the information given in the following formula:

lnt(Si→S ₀ )/lnt(Ti→To) = k(SiVk(Ti)exp(-AE/k _B T).

The intensites lnt(Si→S ₀ ) and lnt(Ti→T ₀ ) can be determined spectroscopically by a spectrophotometer. A graph of the logarithmic intensity ratios lnt(Si→S ₀ )/lnt(T ₁ →T ₀ ) measured at different temperatures versus the reciprocal of the absolute temperature T generally shows a straight line. The measurement is carried out in a temperature range from room temperature (300 K) to 77 K to 4.2 K (the temperature can be adjusted by means of a cryostat). The respective transitions (Si→So) and (Ti→T ₀ ) (band intensities) can be identified since the triplet transition is at lower energy than the singlet transition and increases in intensity with decreasing temperature. The measurements are usually performed in oxygen-free dilute solutions (about 10 ^"2 molL ^"1 ) or thin films of the respective compounds or doped films comprising the corresponding compounds.

The slope of the straight line mentioned above is -AE/k _B T _. With k _B = 1 .380 10 ^"23 JK ^"1 = 0.695 cm ^{" 1} K ^"1 , AEST can be determined. ii)

AEST can also be determined by measuring the temperature dependency of the emission decay as known by a person skilled in the art. iii)

An approximate estimation of AE _S T can be achieved by recording the fluorescence and phosphorescence spectra at low temperature (for example 77 K or 4.2 K using a cryostat). AE _S T then corresponds to an approximation of the energy difference between the high-energy rising edges of the fluorescence or phosphorescence band.

The compounds of formula (I) contain - when X is O or S - one or two groups of formula (Xa) and/or (Xd).

The compounds of formula (I) contain - when X is N-Y ⁴ -R ⁴ - one, two or three groups of formula (Xa) and/or (Xd).

In the compounds of formula (I), the residues and symbols have the following meanings:

X is O, S or N-Y ⁴ -R ⁴ . Y ¹ and Y ² and Y ⁴ are independently of each other a direct bond, CrC ₂ 5-alkylene, or C ₆ -Ci ₀ - arylene, which is unsubstituted or substituted by one or more groups R ³ ; preferably a direct bond, or a C ₆ -Ci ₀ arylene group which is unsubstituted or substituted by one or more C C ₂₅ alkyl groups. Examples of C ₆ -Ci ₀ arylene groups are phenylene and naphthylene. Preferred C ₆ - C-ioarylene groups are 1 ,3-phenylene and 3,6-naphthylene, which may be unsubstituted or substituted by one or more CrC ₈ alk l groups. Y ¹ and Y ² and Y ⁴ are more preferably a direct

bond, or a group of formula

R ¹ and R ² are independently of each other hydrogen, deuterium, F, CI, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ , or a donor group of formula (Xa) or (Xd); preferably, R ¹ and R ² are independently of each other hydrogen, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₀ ar l group, which is unsubstituted

or substituted b one or more groups R ³ , or a group of formula (Xa),

more preferably, R ¹ and R ² are inde endently of each other hydrogen, a C ₆ -Ci ₀ aryl group, or a

group of formula (Xd); most referably, R ¹ and R ² are are independently of each other hydrogen, or a group of formula

R ³ is deuterium, F, CI, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, or a C ₆ -Ci ₄ aryl group; preferably, R ³ is a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, or a C ₆ -Ci ₄ aryl group; more preferably, R ³ is a CrC ₂₅ alkyl group or a CrC ₂₅ alkoxy group.

R ⁴ is a CrC ₂₅ alkyl group, a C ₆ -Ci ₀ aryl grou which is unsubstituted or substituted by one or

more roups R , or a group of formula (Xa),

or (Xd); preferably, R ⁴ is hydrogen, a C ₆ -Ci ₀ aryl group, or or a group of formula (Xa) or (Xd).

X ¹ is O, S, N(R ¹⁵ ), C(=0), C(R ¹⁶ )(R ¹⁷ ), B(R ¹⁸ ), or Si(R ¹⁹ )(R ²⁰ ); preferably, X ¹ is O S, C(O),

N(R ¹⁵ ), or C(R ¹⁶ )(R ¹⁷ ); more preferably, X ¹ is O, S, C(CH ₃ )(CH ₃ ), C(=0), or

R ¹⁰ , R ¹¹ , R ²¹ and R ²¹ are independently of each other hydrogen, deuterium, F, CI, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , or a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ; preferably, R ¹⁰ , R ¹¹ , R ²¹ and R ²¹ are independently of each other hydrogen, or a CrC ₂₅ alkyl group.

R ¹⁵ , R ¹⁶ , R ¹⁷ , R ¹⁸ , R ¹⁹ and R ²⁰ are independently of each other a C C ₂₅ alkyl group, or a C ₆ - Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ; preferably, R ¹⁵

and R ¹⁸ are inde endently of each other a group of formula or

; and R ¹⁶ , R ¹⁷ , R ¹⁹ and R 32 ^u 0 are independently of each other hydrogen, or a CrC ₂₅ alkyl group; R and R are independently of each other hydrogen, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₀ aryloxy group, or a C ₆ -Ci ₀ aryl group; preferably hydrogen.

The roup of formula Xa) is preferably a group of formula (Xa), wherein X ¹ is O, S,

The group of formula (Xd) is preferably a group of formula (Xd), wherein R ²¹ and R ²¹ are hydrogen.

The roup of formula (Xa) or (Xd) is more preferably a group of formula

In particularly preferred compounds of formula (I) the residues have the following meanings: R ¹ and R ² are independently of each other hydrogen, C C ₂₅ alkyl group, a C ₆ -Ci ₀ aryl group, or a group of formula (Xa) or (Xd);

R ⁴ is a CrC ₂₅ alkyl group, a C ₆ -Ci ₀ ar l group, or a group of formula (Xa) or (Xd);

X ¹ is O, S, C(CH ₃ )(CH ₃ ), C(=0), or ; and R ¹⁰ , R ¹¹ , R ²¹ and R ^{21 '} are independently of each other hydrogen, or a Ci-C ₂₅ alkyl group;

wherein at least one group of formula (Xa), or (Xd) is present in the compound of formula (I).

Specific examples of compounds of formula (I) are shown below:

Specific examples of the compounds of formula (I), wherein X is N-Y ⁴ -R ⁴ are the following compounds of formula (la):

Among compounds of formula (la) those are referred which are substituted especially by

grou s (Xa) and/or (Xd) of formula

, such as, for example, compounds

(A-1 ), (A-2), (A-5), (A-6), (A-10), (A-11 ), (A-12), (A-15), (A-16), (A-20), (A-21 ), (A-22), (A-25), (A-26), (A-30), (A-31 ), (A-32), (A-35), (A-36), (A-40), (A-41 ), (A-42), (A-45), (A-46), (A-50), (A- 51 ), (A-52), (A-55), (A-56), (A-60), (A-61 ), (A-62), (A-65), (A-66), (A-70), (A-71 ), (A-72), (A-73), (A-75), (A-76), (A-78), (A-81 ) (A-82), (A-83), (A-84), (A-85), (A-86), (A-87), (A-88), (A-89), (A- 90), (A-91 ), (A-92), (A-93), (A-94), (A-99), and (A-100). The most preferred examples are (A-1 ), (A-2), (A-5), (A-6), (A-11 ), (A-12), (A-15), (A-16), (A- 21 ), (A-22), (A-25), (A-26), (A-31 ), (A-32), (A-35), (A-36), (A-41 ), (A-42), (A-45), (A-46), (A-51 ), (A-52), (A-55), (A-56), (A-61 ), (A-62), (A-65), (A-66), (A-72), (A-73), (A-76), (A-82), (A-83), (A- 84) and (A-85). Specific examples of the compounds of formula (I), wherein X is O are the following compounds of formula (lb):



Among compounds of formula lb) those are preferred which are substituted especially by donor

groups of formula

and , such as, for example, compounds (B-1 ), (B-2), (B-5), (B-6), (B-10), (B-21 ), (B-22), (B-25), (B-26), (B-30), (B-31 ), (B-32), (B-35), (B-36), (B-40), (B-75), (B-76), (B- 78), (B-81 ), (B-82), (B-83), (B-86), (B-87), (B-88), (B-89), (B-90), (B-92), (B-93), (B-99), and (B-100).

The most preferred examples are (B-1 ), (B-2), (B-5), (B-6), (B-21 ), (B-22), (B-25), (B-26), (B- 31 ), (B-32), (B-35), (B-36), (B-76), (B-82) and (B-83).

Specific examples of the compounds of formula (I), wherein X is O are the following compounds of formula (lc):



Amon compounds of formula (Ic) those are preferred which are substituted especially by donor

(C-21 ), (C-22), (C-25), (C-26), (C-30), (C-31 ), (C-32), (C-35), (C-36), (C-40), (C-75), (C-76), (C- 81 ) (C-82), (C-83), (C-86), (C-87), (C-88), (C-89), (C-90), (C-92), (C-93), (C-99), and (C-100).

The most preferred examples are (C-1 ), (C-2), (C-5), (C-6), (C-21 ), (C-22), (C-25), (C-26), (C- 31 ), (C-32), (C-35), (C-36), (C-76), (C-82), and (C-83).

CrC ₂₅ alkyl, preferably CrCi ₈ alkyl is typically linear or branched, where possible. Examples are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec. -butyl, isobutyl, tert. -butyl, n-pentyl, 2-pentyl, 3- pentyl, 2,2-dimethylpropyl, 1 ,1 ,3,3-tetramethylpentyl, n-hexyl, 1 -methylhexyl, 1 ,1 ,3,3,5,5- hexamethylhexyl, n-heptyl, isoheptyl, 1 ,1 ,3,3-tetramethylbutyl, 1 -methylheptyl, 3-methylheptyl, n-octyl, 1 ,1 ,3,3-tetramethylbutyl and 2-ethylhexyl, n-nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, or octadecyl. CrC ₈ alkyl is typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec. -butyl, isobutyl, tert. -butyl, n-pentyl, 2-pentyl, 3-pentyl, 2,2- dimethyl-propyl, n-hexyl, n-heptyl, n-octyl, 1 ,1 ,3,3-tetramethylbutyl and 2-ethylhexyl. CrC ₄ alkyl is typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec. -butyl, isobutyl, tert. -butyl.

CrC ₂₅ alkoxy groups, preferably CrCi ₈ alkoxy groups are straight-chain or branched alkoxy groups, e.g. methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, tert-butoxy, am- yloxy, isoamyloxy or tert-amyloxy, heptyloxy, octyloxy, isooctyloxy, nonyloxy, decyloxy, un- decyloxy, dodecyloxy, tetradecyloxy, pentadecyloxy, hexadecyloxy, heptadecyloxy and octade- cyloxy. Examples of CrC ₈ alkoxy are methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec- butoxy, isobutoxy, tert.-butoxy, n-pentyloxy, 2-pentyloxy, 3-pentyloxy, 2,2-dimethylpropoxy, n- hexyloxy, n-heptyloxy, n-octyloxy, 1 ,1 ,3,3-tetramethylbutoxy and 2-ethylhexyloxy, preferably C C ₄ alkoxy such as typically methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, isobutoxy, tert.-butoxy.

C ₆ -Ci ₀ aryl, which optionally can be substituted, is typically phenyl, naphthyl, especially 1 - naphthyl, or 2-naphthyl,or biphenylyl, which may be unsubstituted or substituted by one, or more CrC ₈ alkyl, Ci-C ₈ alkoxy and/or C ₆ -Ci ₀ aryloxy groups, especially Ci-C ₈ alkyl, Ci-C ₈ alkoxy groups.

C ₆ -Ci ₀ aryloxy, which optionally can be substituted by one, or more Ci-C ₈ alkyl and/or

Ci-C ₈ alkoxy groups, is typically phenoxy, 1 -naphthoxy, or 2-naphthoxy. her relates to a specific compound of formula (Ι'), wherein

X is O, S, N-Y ^4' -R ⁴ or N-Y ^{4 "} -R ⁴ ,

Y ¹ and Y ² are independently of each other a direct bond, CrC ₂ 5-alkylene, or C ₆ -Ci ₀ -arylene, which is unsubstituted or substituted by one or more groups R ³ ;

Y ⁴ is a direct bond, CrC ₂ 5-alkylene;

Y ⁴ is C ₆ -Cio-arylene, which is unsubstituted or substituted by one or more groups R ³ ;

R ¹ and R ² are independently of each other hydrogen, deuterium, F, CI, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ , or a group of formula (Xa) or (Xd);

R ³ is deuterium, F, CI, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, or a C ₆ -Ci ₄ aryl group;

R ⁴ is a C C ₂₅ alkyl group, a C ₆ -Ci ₀ aryl group, which is unsubstituted or substituted by one or more groups R ³ , or a group of formula (Xa) or (Xd);

X ¹ is O, S, N(R ¹⁵ ), C(=0), C(R ¹⁶ )(R ¹⁷ ), B(R ¹⁸ ), or Si(R ¹⁹ )(R ²⁰ ), or

when X is N-Y ^{4 "} -R ⁴ ,

X ¹ is N(R ¹⁵ ), C(=0), C(R ¹⁶ )(R ¹⁷ ), B(R ¹⁸ ), or Si(R ¹⁹ )(R ²⁰ ),

R ¹⁰ , R ¹¹ , R ²¹ and R ²¹ are independently of each other hydrogen, deuterium, F, CI, a CrC ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₄ aryloxy group, which is unsubstituted or substituted by one or more groups R ³ , or a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ;

R ¹⁵ , R ¹⁶ , R ¹⁷ , R ¹⁸ , R ¹⁹ and R ²⁰ are independently of each other a C C ₂₅ alkyl group, or a C ₆ - Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ;

R ¹⁵ is a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ ; wherein at least one group of formula (Xa) or (Xd) is present in the compound of formula (I).

Preferred and particularly preferred residues and groups X, X ¹ , Y ¹ , Y ² , R ¹ , R ² , R ³ , R ⁴ , R ¹⁰ , R ¹¹ , R ²¹ , R ^21' , R ¹⁵ , R ¹⁶ , R ¹⁷ , R ¹⁸ , R ¹⁹ and R ²⁰ for the specific compounds of formula (Ι') are the same residues as mentioned concerning the compounds of formula (I) mentioned above.

Y ⁴ is a is a direct bond, CrC ₂₅ -alkylene, preferably a direct bond; and

Y ⁴ is C ₆ -Cio-arylene, which is unsubstituted or substituted by one or more groups R ³ (R ³ is de- fined above); preferably a C ₆ -Ci ₀ arylene group which is unsubstituted or substituted by one or more CrC ₂₅ alkyl groups. Examples of C ₆ -Ci ₀ arylene groups are phenylene and naphthylene. Preferred C ₆ -Ci ₀ arylene groups are 1 ,3-phenylene and 3,6-naphthylene, which may be unsubstituted or substituted by one or more CrC ₈ alkyl groups. More preferably, Y ⁴ is a group

of formula

X ¹ in the specific compounds of formula (Γ), wherein X is N-Y ⁴ -R ⁴ , is N(R ¹⁵ ), C(=0), C(R ¹⁶ )(R ¹⁷ ), B(R ¹⁸ ), or Si R ¹⁹ )(R ²⁰ ), preferably C(=0), N(R ¹⁵ ), or C(R ¹⁶ )(R ¹⁷ );

more preferably, C(CH ₃ )(CH ₃ ), C(=0), or

R in the specific compounds of formula (Γ) is a C ₆ -Ci ₄ aryl group, which is unsubstituted or substituted by one or more groups R ³ , preferably a C ₆ -Ci ₀ aryl group, which is unsubstituted or

substituted b one or more groups R ³ , more preferably a group of formula or

, wherein R and R are independently of each other hydrogen, a C C ₂₅ alkyl group, a CrC ₂₅ alkoxy group, a C ₆ -Ci ₀ aryloxy group, or a C ₆ -Ci ₀ aryl group;

most preferably phenyl.

The group (Xa) in the specific compounds of formula (Γ), wherein X is N-Y ⁴ -R ⁴ , is therefore most referably:

Specific examples of compounds of formula (Ι') are:

Specific examples of the compounds of formula (Ι'), wherein X is N-Y ⁴ -R ⁴ or N-Y ⁴ -R ⁴ " are the following compounds of formula (1 'a):

(A-1 ), (A-2), (A-3), (A-4), (A-5), (A-6), (A-7), (A-8), (A-9), (A-10), (A-13), (A-15), (A-16), (A-17), (A-18), (A-19) (A-20), (A-23), (A-25), (A-26), (A-27), (A-28), (A-29), (A-30), (A-33), (A-35), (A- 36), (A-37), (A-38), (A-39), (A-40), (A-43), (A-45), (A-46), (A-47), (A-48), (A-49), (A-50), (A-51 ), (A-52), (A-53), (A-54), (A-55), (A-56), (A-57), (A-58), (A-59), (A-60), (A-61 ), (A-62), (A-63), (A- 64), (A-65), (A-66), (A-67), (A-68), (A-69), (A-70), (A-71 ), (A-72), (A-73), (A-74), (A-75), (A-76), (A-77), (A-78), (A-79), (A-80), (A-81 ), (A-82), (A-83), (A-86), (A-87), (A-88), (A-89), (A-90), (A- 94), (A-95), (A-96), (A-97), (A-98), (A-99), and (A-100).

Among compounds of formula (la) those are referred which are substituted especially by

grou s (Xa) and/or (Xd) of formula

, such as, for example, compounds

(A-1 ), (A-2), (A-5), (A-6), (A-10), (A-15), (A-16), (A-20), (A-25), (A-26), (A-30), (A-35), (A-36), (A-40), (A-45), (A-46), (A-50), (A-51 ), (A-52), (A-55), (A-56), (A-60), (A-61 ), (A-62), (A-65), (A- 66), (A-70), (A-71 ), (A-72), (A-73), (A-75), (A-76), (A-78), (A-81 ) (A-82), (A-83), (A-86), (A-87), (A-88), (A-89), (A-90), (A-94), (A-99), and (A-100).

The most preferred examples are (A-1 ), (A-2), (A-5), (A-6), (A-15), (A-16), (A-25), (A-26), (A- 35), (A-36), (A-45), (A-46), (A-51 ), (A-52), (A-55), (A-56), (A-61 ), (A-62), (A-65), (A-66), (A-72), (A-73), (A-76), (A-82), and (A-83).

Specific examples of the compounds of formula (Ι'), wherein X is O are the following compounds of formula (I'b):

(B-1 ), (B-2), (B-3), (B-4), (B-5), (B-6), (B-7), (B-8), (B-9), (B-10), (B-21 ), (B-22), (B-23), (B-24), (B-25), (B-26), (B-27), (B-28), (B-29), (B-30), (B-31 ), (B-32), (B-33), (B-34), (B-35), (B-36), (B- 37), (B-38), (B-39), (B-40), (B-75), (B-76), (B-77), (B-78), (B-79), (B-80), (B-81 ), (B-82), (B-83), (B-84), (B-85), (B-86), (B-87), (B-88), (B-89), (B-90), (B-92), (B-93), (B-95), (B-96), (B-97), (B- 98), (B-99) and (B-100). Among compounds of formula 1 'b) those are preferred which are substituted especially by do

nor roups of formula

and such as, for example, compounds

(B-1 ), (B-2), (B-5), (B-6), (B-10), (B-21 ), (B-22), (B-25), (B-26), (B-30), (B-31 ), (B-32), (B-35), (B-36), (B-40), (B-75), (B-76), (B-78), (B-81 ), (B-82), (B-83), (B-86), (B-87), (B-88), (B-89), (B- 90), (B-92), (B-93), (B-99), and (B-100).

The most preferred examples are (B-1 ), (B-2), (B-5), (B-6), (B-21 ), (B-22), (B-25), (B-26), (B- 31 ), (B-32), (B-35), (B-36), (B-76), (B-82) and (B-83).

Specific examples of the compounds of formula (Ι'), wherein X is O are the following compounds of formula (1 'c):

(C-1 ), (C-2), (C-3), (C-4), (C-5), (C-6), (C-7), (C-8), (C-9), (C-10), (C-21 ), (C-22), (C-23), (C-24), (C-25), (C-26), (C-27), (C-28), (C-29), (C-30), (C-31 ), (C-32), (C-33), (C-34), (C-35), (C-36), (C- 37), (C-38), (C-39), (C-40), (C-75), (C-76), (C-77), (C-78), (C-79), (C-80), (C-81 ), (C-82), (C-83), (C-84), (C-85), (C-86), (C-87), (C-88), (C-89), (C-90), (C-92), (C-93), (C-95), (C-96), (C-97), (C- 98), (C-99) and (C-100).

Among compounds of formula 1 'c) those are preferred which are substituted especially by do

nor groups of formula

and , such as, for example, compounds

(C-1 ), (C-2), (C-5), (C-6), (C-10), (C-21 ), (C-22), (C-25), (C-26), (C-30), (C-31 ), (C-32), (C-35), (C-36), (C-40), (C-75), (C-76), (C-81 ) (C-82), (C-83), (C-86), (C-87), (C-88), (C-89), (C-90), (C- 92), (C-93), (C-99), and (C-100).

The most preferred examples are (C-1 ), (C-2), (C-5), (C-6), (C-21 ), (C-22), (C-25), (C-26), (C- 31 ), (C-32), (C-35), (C-36), (C-76), (C-82), and (C-83).

In addition, the present invention is directed to an organic light emitting element, comprising the specific compound of the formula (Ι').

Further, the present invention is directed to an organic light-emitting element comprising the light-emitting layer comprising the specific compound of formula (Ι'). For the specific compounds of formula (Ι') the preferences specified above apply.

The specific compounds of formula (Ι') or the compounds of formula (I) can be used as host in combination with a fluorescent guest material in the emitting layer of an organic EL element. Known fluorescent materials are usable as the fluorescent guest material. Examples of the fluo- rescent guest material include a bisarylamino naphthalene derivative, an aryl-substituted naphthalene derivative, a bisarylamino anthracene derivative, an aryl-substituted anthracene derivative, a bisarylamino pyrene derivative, an aryl-substituted pyrene derivative, a bisarylamino chrysene derivative, an aryl-substituted chrysene derivative, a bisarylamino fluoranthene derivative, an aryl-substituted fluoranthene derivative, an indenoperylene derivative, a pyrromethene boron complex compound, a compound having a pyrromethene skeleton or a metal complex thereof, a diketopyrrolopyrrole derivative, and a perylene derivative. Examples are 2,5,8,1 1 - tetra-tert-butylperylene (TBPe), 9,10-bis[N,N -di-(p -tolyl)-amino]anthracene (TTPA), 2,8-di-tert - butyl-5,1 1 -bis(4-tert -butylphenyl)-6,12- diphenyltetracene (TBRb) and dibenzo{[f,f ]-4,4',7,7'- tetraphenyl}diindeno[1 ,2,3- cd :1 ',2',3'-lm ]perylene (DBP). In case of using the specific com- pound of formula (Ι') or the compounds of formula (I) as host material, the content of the compound of formula (Ι') or the compound of formula (I) in the light-emitting layer preferably falls within the range of 51 to 99 wt%, more preferably 80 to 99 wt%, based on the total weight of the light-emitting layer. The present invention therefore further relates to the organic light-emitting element as mentioned above, comprising a light-emitting layer comprising a specific compound of formula (Ι') as host and a guest material. For the specific compounds of formula (Ι') the preferences specified above apply.

Alternatively, the specific compounds of formula (Ι') as well as the compounds of formula (I) can be used as guest in combination with a host material in the light-emitting layer of an organic EL element. Said guest compounds are preferably present in the light-emitting layer in an amount of 1 to 50 wt%, more preferably 1 % by weight to 25% by weight, most preferably 6% to 15% by weight, based on the total weight of the light emitting layer.

The compound of formula (I), respectively the specific compound of formula (Ι'), i.e. the organic light-emitting material, has preferably a difference between excited singlet energy and excited triplet energy ((AE _S T) of 0.5 eV or less, more preferably AE _S T of 0.35 eV or less, i.e. of 0.01 to 0.5 eV, especially 0.01 to 0.35 eV. The compound of formula (I) or the specific compounds of formula (Ι') may be used alone in the light-emitting layer as organic light-emitting material. However, as necessary, for the purpose of, for example, confining, in the organic light-emitting mate- rial, singlet excitons and triplet excitons generated in the organic light-emitting material, the organic light-emitting material of the present invention and an organic compound which has a higher value of at least any one of excited singlet energy and excited triplet energy than those of the organic light-emitting material and serves as a host material are preferably used in the light- emitting layer. At least any one of the excited singlet energy (Si _h ) and excited triplet energy (T _1h ) of the host compound is preferably higher by 0.1 eV or more, particularly preferably higher by 0.2 eV or more than the excited singlet energy (Si _g ) and excited triplet energy (T _1g ) of the organic light-emitting material of the present invention. That is, it is preferred that one or both of (Si _h ) - (Si _g ) > 0.1 eV and (T _1h ) - (T _1g ) > 0.1 eV be satisfied and it is more preferred that one or both of (Si _h ) - (Si _g ) > 0.2 eV and (T _1h ) - (T _1g ) >0.2 eV be satisfied. In case of using the compound of formula (I) or the specific compound of formula (Ι') as guest material, the content of the compound of formula (I) or the specific compound of formula (Ι') in the light-emitting layer preferably falls within the range of 1 to 50 wt%, more preferably 1 to 25 wt%, most preferably 6 to 1 5 wt%, based on the total weight of the light emitting layer. The present invention therefore further relates to the organic light-emitting element mentioned above, comprising a light-emitting layer comprising a specific compound of formula (Ι') as guest and a host material.

For the specific compounds of formula (Ι') the preferences specified above apply.

The organic EL element (organic light-emitting element) of the present invention usually has, as essential layers, an anode, a hole-transporting layer, a light-emitting layer, and a cathode.

Further, the organic EL element of the present invention may have - in addition to the usually essential layers - , as layers other than the usually essential layers, an electron-transporting layer, an electron-injecting layer, an electron-blocking layer, a hole-blocking layer, and an exci- ton element layer. In addition, the hole-transporting layer may be a hole-injecting/transporting layer having a hole-injecting function and the electron-transporting layer may be an electron- injecting/transporting layer having an electron-injecting function.

An example for an organic EL element comprises therefore at least the following layers: an an- 5 ode, a hole-transporting layer, a light-emitting layer, an electron-transporting layer, and a cathode.

The organic EL element of the present invention may comprise in this order: a substrate, an anode, a hole-injecting layer, a hole-transporting layer, a light-emitting layer, an electroni c) transporting layer and a cathode. Alternatively, the cathode, the electron-transporting layer, the light-emitting layer, the hole-transporting layer, and the anode may be laminated on the substrate in the stated order.

Substrate

15 The organic EL element of the present invention is preferably supported by a substrate. The substrate is not particularly limited and may be any substrate which is conventionally used in an organic EL element. For example, a substrate formed of glass, transparent plastic, quartz, or the like may be used.

Anode

Preferably used as the anode in the organic EL element is one using, as an electrode substance, any of a metal, an alloy, an electrically conductive compound, and a mixture thereof with a high work function (4 eV or more). Specific examples of such electrode substance include metals such as Au and conductive transparent materials such as Cul, indium tin oxide (ITO), Sn0 ₂ , and ZnO. Further, a material capable of producing an amorphous transparent conductive film such as IDIXO (In ₂ 0 ₃ -Zn0) may be used. In the production of the anode, it is possible to form any of those electrode substances into a thin film by a method such as vapor deposition or sputtering, and then form a pattern having a desired shape by a photolithographic method. Alternatively, in the case of using a coatable substance such as an organic conductive compound, it is also possible to employ a wet film-forming method of a printing mode, a coating mode, or the like.

Cathode

Meanwhile, preferably used as the cathode is one using, as an electrode substance, any of a 35 metal (referred to as electron-injecting metal), an alloy, an electrically conductive compound, and a mixture thereof with a low work function (4 eV or less). Specific examples of such electrode substance include sodium, a sodium-potassium alloy, magnesium, lithium, a magnesium/copper mixture, a magnesium/silver mixture, a magnesium/aluminum mixture, a magnesium/indium mixture, an aluminum/aluminum oxide (Al ₂ 0 ₃ ) mixture, indium, a lithium/aluminum 40 mixture, and a rare earth metal. Of those, from the viewpoints of electron-injecting property and durability against oxidation and the like, a mixture of an electron-injecting metal and a second metal, which has a work function value higher than that of the electron-injecting metal and is a stable metal, such as a magnesium/silver mixture, a magnesium/aluminum mixture, a magnesi- um/indium mixture, an aluminum/aluminum oxide (Al ₂ 0 ₃ ) mixture, a lithium/aluminum mixture, or aluminum is suitable. It should be noted that a case where any one of the anode and the cathode of the organic EL element is transparent or translucent in order to transmit emitted light is advantageous because light emission luminance is improved.

Light-emitting layer

The light-emitting layer is a layer which emits light after excitons have been generated through the recombination of holes and electrons injected respectively from an anode and a cathode. The light-emitting layer preferably includes an organic light-emitting material and a host materi- al. As the organic light-emitting material, there may be used one kind or two or more kinds selected from the compounds of formula (I), respectively selected from the specific compounds of formula (Ι'). In order that the organic EL element of the present invention exhibits high luminous efficiency, it is important to confine, in the organic light-emitting material, singlet excitons and triplet excitons generated in the organic light-emitting material. Accordingly, it is preferred to use a host material in addition to the organic light-emitting material in the light-emitting layer. As the host material, there may be used an organic compound having a higher value of at least any one of excited singlet energy and excited triplet energy than those of the organic light-emitting material of the present invention. This allows singlet excitons and triplet excitons generated in the organic light-emitting material of the present invention to be confined in the molecule of the organic light-emitting material of the present invention and allows the luminous efficiency to be exhibited sufficiently. In the organic EL element of the present invention, light is emitted from the organic light-emitting material of the present invention included in the light-emitting layer.

In case of using the host material below, the content of the organic light-emitting material of the present invention in the light-emitting layer falls preferably within the range of 1 to 50 wt%, more preferably 1 to 25 wt%, most preferably 6 to 15 wt%, based on the total weight of the light emitting layer.

The host material in the light-emitting layer is preferably an organic compound which has a hole-transporting ability and/or an electron-transporting ability, prevents an emission wavelength from becoming longer, and has a high glass transition temperature.

The host material may be a polymer, for example poly(N-vinylcarbazole) or polysilane. The host material may, however, be a small molecule, for example 4,4-N,N-dicarbazolebiphenyl

(CDP=CBP , 2,6-bis(N-carbazolyl)phe -Di(9H-carbazol-9-yl)biphenyl (mCBP),

(PYD2), (DPEPO),

3-yl)-1 ,3,5-triazine (T2T))

or tertiary aromatic amines, for example TCTA.

However, as mentioned above, the compounds of formula (I) as well as the specific compounds of formula (Ι') can alternatively be used as host in combination with a fluorescent guest material in the emitting layer of an organic EL element. Known fluorescent materials are usable as the fluorescent guest material. Suitable fluorescent materials are mentioned above.

Injecting layer

The injecting layer refers to a layer to be provided between an electrode and an organic layer for the purposes of reducing a driving voltage and improving a light emission luminance. The injecting layer includes a hole-injecting layer and an electron-injecting layer, and may be provided between the anode and the light-emitting layer or the hole-transporting layer, and between the cathode and the light-emitting layer or the electron-transporting layer. The injecting layer may be provided as necessary.

Customarily used hole injection materials include CuPc, MTDATA, or dipyrazino[2,3-f:2',3'- hjquinoxaline-2,3,6,7,10,1 1 -hexacarbonitrile (HAT-CN). Polymeric hole-injection materials can be used such as poly(N-vinylcarbazole) (PVK), polythiophenes, polypyrrole, polyaniline, self- doping polymers, such as, for example, sulfonated poly(thiophene-3-[2[(2- methoxyethoxy)ethoxy]-2,5-diyl) (Plexcore ^® OC Conducting Inks commercially available from Plextronics), and copolymers such as poly(3,4-ethylenedioxythiophene)/poly(4- styrenesulfonate) also called PEDOT/PSS.

Lithium-comprising organometallic compounds such as 8-hydroxyquinolatolithium (Liq), CsF, NaF, KF, Cs ₂ C0 ₃ or LiF may be applied between the electron transport layer and the cathode as an electron injection layer in order to reduce the operating voltage. Blocking layer

The blocking layer is capable of blocking charges (electrons or holes) and/or excitons present in the light-emitting layer from diffusing to the outside of the light-emitting layer. The electron- blocking layer may be arranged between the light-emitting layer and the hole-transporting layer, and blocks electrons from passing through the light-emitting layer toward the hole-transporting layer. Similarly, the hole-blocking layer may be arranged between the light-emitting layer and the electron-transporting layer, and blocks holes from passing through the light-emitting layer toward the electron-transporting layer. The blocking layer may also be used for blocking excitons from diffusing to the outside of the light-emitting layer. That is, the electron-blocking layer and the hole-blocking layer may each have a function of an exciton-blocking layer as well. The electron-blocking layer or exciton-blocking layer as used herein is meant to include a layer having a function of an electron-blocking layer and an exciton-blocking layer in one layer.

Hole-blocking layer

The hole-blocking layer has a function of the electron-transporting layer in a broad sense. The hole-blocking layer has a role in blocking holes from reaching the electron-transporting layer while transporting electrons. This can improve the probability of recombination of electrons and holes in the light-emitting layer. As a material for the hole-blocking layer, a material for the electron-transporting layer to be described below may be used as necessary. Electron-blocking layer

The electron-blocking layer has a function of transporting holes in a broad sense. The electron- blocking layer has a role in blocking electrons from reaching the hole-transporting layer while transporting holes. This can improve the probability of recombination of electrons and holes in the light-emitting layer.

Exciton-blocking layer

The exciton-blocking layer refers to a layer for blocking excitons, which are generated by the recombination of holes and electrons in the light-emitting layer, from diffusing to a charge- transporting layer. The insertion of this layer allows excitons to be efficiently confined in the light-emitting layer, which can improve the luminous efficiency of an element. The exciton- blocking layer may be inserted on any of the anode side and the cathode side of the adjacent light-emitting layer, and may be simultaneously inserted on both of the sides. That is, when the exciton-blocking layer is provided on the anode side, the layer may be inserted between the hole-transporting layer and the light-emitting layer so as to be adjacent to the light-emitting layer. When the exciton-blocking layer is inserted on the cathode side, the layer may be inserted between the light-emitting layer and the cathode so as to be adjacent to the light-emitting layer. Further, the hole-injecting layer, the electron-blocking layer, and the like may be provided be- tween the anode and the exciton-blocking layer adjacent to the anode side of the light-emitting layer, and the electron-injecting layer, the electron-transporting layer, the hole-blocking layer, and the like may be provided between the cathode and the exciton-blocking layer adjacent to the cathode side of the light-emitting layer. In the case of providing the blocking layer, it is preferred that at least any one of the excited singlet energy and excited triplet energy of a material to be used as the blocking layer be higher than the excited singlet energy and excited triplet energy of a light-emitting material.

Hole blocker materials typically used are 2,6-bis(N-carbazolyl)pyridine (mCPy), 2,9-dimethyl- 4,7-diphenyl-1 ,10-phenanthroline (bathocuproin, (BCP)), bis(2-methyl-8-quinolinato)-4- phenylphenylato)aluminum(lll) (BAIq), phenothiazine S,S-dioxide derivates and 1 ,3,5-tris(N- phenyl-2-benzylimidazolyl)benzene) (TPBI), TPBI also being suitable as electron-transport material. Further suitable hole blockers and/or electron conductor materials are 2,2',2"-(1 ,3,5- benzenetriyl)tris(1 -phenyl-1 -H-benzimidazole), 2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1 ,3,4- oxadiazole, 8-hydroxyquinolinolatolithium, 4-(naphthalen-1 -yl)-3,5-diphenyl-4H-1 ,2,4-triazole, 1 ,3-bis[2-(2,2'-bipyridin-6-yl)-1 ,3,4-oxadiazo-5-yl]benzene, 4,7-diphenyl-1 ,10-phenanthroline, 3- (4-biphenylyl)-4-phenyl-5-tert-butylphenyl-1 ,2,4-triazole, 6,6'-bis[5-(biphenyl-4-yl)-1 ,3,4-oxa- diazo-2-yl]-2,2'-bipyridyl, 2-phenyl-9,10-di(naphthalene-2-yl)anthracene, 2,7-bis[2-(2,2'-bipyridin- 6-yl)-1 ,3,4-oxadiazo-5-yl]-9,9-dimethylfluorene, 1 ,3-bis[2-(4-tert-butylphenyl)-1 ,3,4-oxadiazo-5- yljbenzene, 2-(naphthalene-2-yl)-4,7-diphenyl-1 ,10-phenanthroline, tris(2,4,6-trimethyl-3- (pyridin-3-yl)phenyl)borane, 2, 9-bis(naphthalene-2-yl)-4,7-diphenyl-1 ,10-phenanthroline, 1 - methyl-2-(4-(naphthalene-2-yl)phenyl)-1 H-imidazo[4,5-f][1 ,1 Ojphenanthroline,

Hole-transporting layer

The hole-transporting layer is formed of a hole-transporting material having a function of transporting holes. The hole-transporting layer may be provided in a single layer or a plurality of layers.

The hole-transporting material has any of hole-injecting or -transporting property and electron- blocking property, and may be an organic material or an inorganic material. An applicable known hole-transporting material is exemplified by a triazole derivative, an oxadiazole derivative, an imidazole derivative, a carbazole derivative, an indolocarbazole derivative, a polyarylal- kane derivative, a pyrazoline derivative, a pyrazolone derivative, a phenylenediamine derivative, an arylamine derivative, an amino-substituted chalcone derivative, an oxazole derivative, a styrylanthracene derivative, a fluorenone derivative, a hydrazone derivative, a stilbene derivative, a silazane derivative, an aniline-based copolymer, or a conducting polymeric oligomer, particularly a thiophene oligomer. However, preferably used are a porphyrin compound, an aromatic tertiary amine compound, and a styrylamine compound, and more preferably used is an aromatic tertiary amine com molecules are selected

phenyl-N-(4-phenylphenyl)-N-[4-

[4-(N-[4-(4-phenylphenyl)phenyl]anilino)phenyl]phenyl]ani line), (4- phenyl-N-(4-phenylphenyl)-N-[4-[4-(4-phenyl-N-(4-phenylpheny l)anilino)phenyl]phenyl]aniline),

(4-phenyl-N-[4-(9-phenylcarbazol-3-yl)phenyl]-N-(4-phenyl phenyl)aniline),

(1 ,1 ',3,3'-tetraphenylspiro[1 ,3,2-benzodiazasilole-2,2'-3a,7a-dihydro-1 ,3,2-

benzodiazasilole]), (N2,N2,N2',N2',N7,N7,N7',N7'-octakis(p- tolyl)-9,9'-spirobi[fluorene]-2,2',7,7'-tetramine), 4,4'-bis[N-(1 -naphthyl)-N-phenylamino]biphenyl (a-NPD), N,N '-diphenyl-Ν,Ν '-bis(3-methylphenyl)-[1 ,1 '-biphenyl]-4,4 '-diamine (TPD), 1 ,1 bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC), N,N '-bis(4-methylphenyl)-N,N '-bis(4- ethylphenyl)-[1 ,1 '-(3,3 '-dimethyl)biphenyl]-4,4 '-diamine (ETPD), tetrakis(3-methylphenyl)- Ν,Ν,Ν ' ,Ν '-2,5-phenylenediamine (PDA), a-phenyl-4-N,N-diphenylaminostyrene (TPS), p- (diethylamino)benzaldehyde diphenylhydrazone (DEH), triphenylamine (TPA), bis[4-(N,N- diethylamino)2-methylphenyl](4-methylphenyl)methane (MPMP), 1 -phenyl-3-[p- (diethylamino)styryl]5-[p-(diethylamino)phenyl]pyrazoline (PPR or DEASP), 1 ,2-trans-bis(9H- carbazol9-yl)-cyclobutane (DCZB), Ν,Ν,Ν ' ,Ν '-tetrakis(4-methylphenyl)-(1 ,1 '-biphenyl)-4,4 ' -diamine (TTB), fluorine compounds such as 2,2',7,7'-tetra(N,N-di-tolyl)amino9,9-spirobifluorene (spiro-TTB), N,N'-bis(naphthalen-1 -yl)-N,N'-bis(phenyl)9,9-spirobifluorene (spiro-NPB) and 9,9- bis(4-(N,N-bis-biphenyl-4-yl-amino)phenyl-9Hfluorene, benzidine compounds such as Ν,Ν ' - is(naphthalen-1 -yl)-N,N ' -bis(phenyl)benzidine and porphyrin compounds such as copper

used such as poly(N-vinylcarbazole) (PVK), polythiophenes, polypyrrole, polyaniline, self-doping polymers, such as, for example, sulfonated poly(thiophene-3-[2[(2-methoxyethoxy)ethoxy]-2,5- diyl) (Plexcore® OC Conducting Inks commercially available from Plextronics), and copolymers such as poly(3,4-ethylenedioxythiophene)/poly(4-styrenesulfonate) also called PEDOT/PSS.

Electron-transporting layer

The electron-transporting layer is formed of a material having a function of transporting electrons. The electron-transporting layer may be provided in a single layer or a plurality of layers.

An electron-transporting material (may also serve as a hole-blocking material) has only to have a function of transporting electrons, which are injected from the cathode, to the light-emitting layer. An applicable electron-transporting layer is exemplified by a nitro-substituted fluorene derivative, a diphenylquinone derivative, a thiopyran dioxide derivative, carbodiimide, a fluo- renylidenemethane derivative, an anthraquinodimethane derivative, an anthrone derivative, or an oxadiazole derivative. In addition, in oxadiazole derivative, a thiadiazole derivative in which an oxygen atom of an oxadiazole ring is substituted by a sulfur atom, or a quinoxaline derivative having a quinoxaline ring known as an electron-withdrawing group may also be used as the electron-transporting material. In addition, a polymer material obtained by introducing any of those materials into a polymer chain, or a polymer material including any of those materials in a polymer main chain may also be used. Suitable electron-transporting materials comprise 1 ,3,5- tris(N-phenyl-2-benzylimidazolyl)benzene (TPBi),

metals chelated with oxinoid compounds, such as tris(8-hydroxyquinolato)aluminum (Alq ₃ ), compounds based on phenanthroline such as 2, 9-dimethyl-4,7-diphenyl-1 ,10-phenanthroline (DDPA = BCP), 4,7-diphenyl-1 ,10-phenanthroline (Bphen), 2,4,7,9-tetraphenyl-1 ,10- phenanthroline, 4,7-diphenyl-1 ,10-phenanthroline (DPA) or phenanthroline derivatives disclosed in EP1786050, in EP1970371 , or in EP1097981 , and azole compounds such as 2-(4- biphenylyl)-5-(4-t-butylphenyl)-1 ,3,4-oxadiazole (PBD) and 3-(4-biphenylyl)-4phenyl-5-(4-t- butylphenyl)-1 ,2,4-triazole (TAZ). Examples of possible element structures are shown below:

ITO (100nm) / -NPD (35nm) / CBP: 6 % by weight compound of formula (I), respectively of the specific compound of formula (Ι') (15nm) / TPBi (65nm) / LiF (0.8nm) / Al (80nm)

ITO (100nm) / a -NPD (40nm) / mCP / PPT: 6 % by weight compound of formula (I), respective- ly of the specific compound of formula (Ι') (20nm) / PPT (40nm) / LiF (0.8nm) / Al (80nm)

ITO (30-1 OOnm) / a -NPD (60nm) / mCP: 6 % by weight compound of formula (I), respectively of the specific compound of formula (Ι') (20nm) / Bphen (40nm) / MgAg (1 OOnm) / Ag (20nm) ITO (30-1 OOnm) / a -NPD (60nm) / PYD2: 6 % by weight compound of formula (I), respectively of the specific compound of formula (Ι') (20nm) / Bphen (40nm) / MgAg (1 OOnm) / Al (20nm)

ITO/a-NPD (35 nm)/6 % by weight compound of formula (I), respectively of the specific compound of formula (Ι'): CBP (15 nm)/TPBi (65 nm)/LiF (0.8 nm)/AI (80 nm)

ITO (1 OOnm) / HAT-CN (1 Onm) / Tris-PCz (30nm) / CBP: 3, 6, 10, or 15 % by weight compound of formula (I), respectively of the specific compound of formula (Ι') (30nm) / BPY-TP2 (40nm) / LiF (0.8nm) / AI (100nm) ITO (100nm) / a -NPD (35nm) / CBP (10nm) / DPEPO: 6 to 12 % by weight compound of formula (I), respectively of the specific compound of formula (Ι') (15nm) / DPEPO (1 Onm) / TPBi (65nm) / LiF (0.5nm) / Al (80nm) ]

ITO: indium/tin oxide; a -NPD: 4,4'-bis[N-(1 -naphthyl)-N-phenylamino]biphenyl;

CBP: 4,4'-N,N'-dicarbazolebiphenyl; TPBi: 1 ,3,5-tris(N-phenyl-2-benzylimidazolyl)benzene;

The organic EL element emits light when an electric field is applied between an anode and a cathode of the resultant element.

The organic EL element of the present invention may be applied to any of a single element, an element formed of a structure with arrangement in an array fashion, and a structure in which an anode and a cathode are arranged in an X-Y matrix fashion.

The organic light-emitting element according to the present invention is characterized in that it emits light by delayed fluorescence.

According to the present invention, there is provided an element having significantly improved luminous efficiency as compared to a conventional element using light emission from a singlet state by incorporating the organic light-emitting material having a specific skeleton of the present invention into the light-emitting layer which emits delayed fluorescence. The element can exhibit excellent performance when being applied to a full-color or multi-color panel. The element may also be utilized in a backlight, lighting, and the like. The above compounds of formula (I) and the above specific compounds of formula (Ι') can be used in electrophotographic photoreceptors, photoelectric converters, sensors, dye lasers, solar cell devices and organic light emitting elements. The present invention therefore further relates to the use of the compounds of formula (I) and the specific compounds of formula (Ι') for elec- trophotographic photoreceptors, photoelectric converters, sensors, dye lasers, solar cell devices and organic light emitting elements.

The present invention further relates to the use of the compounds of formula (I) and the specific compounds of formula (Ι') for generating delayed fluorescence emission.

The compounds of formula (I) and the specific compounds of formula (Ι') of the present invention can be synthesized using copper catalyzed Ullmann conditions or palladium catalyzed Buchwald-Hartwig conditions. Suitable benzobisoxazole, benzobisthiazole and benzobisimidaz- ole base skeletons are either commercially available, or can be obtained by processes known to those skilled in the art. Reference is made to JP10340786, KR201 10085784A and

KR101 160670.

The following examples are included for illustrative purposes only and do not limit the scope of the claims. Unless otherwise stated, all parts and percentages are by weight.

Examples

Example 1

I

a) 4-Bromobenzonitrile (56 mmol) and Ethanol (35 g) are placed in a 100ml flask. While stirring, Acetyl chloride (448 mmol) is slowly added. The mixture is stirred at room temperature overnight (15 hours). After the reaction is completed, Ethanol is removed by evaporation, then the residue is washed with Diethyl ether. White solid is obtained by drying in vacuum. (Yield: 84.4 %) The product is used for the next reaction without further purification,

b) The product from example 1 a (11 .3 mmol), Triethylamine (24.9 mmol), 4-Bromobenzoyl chloride (11 .3 mmol) and 35 ml of dichloromethane are placed in a 100 ml flask. The mixture is stirred at -15°C to room temperature overnight (15 hours). After the reaction is completed, dichloromethane is removed by evaporation, then the residue is washed with warm Tetrahydrofu- ran. White solid is obtained by drying in vacuum. (Crude, Yield: 105%). The product is used for the next reaction without further urification.

c) The product from example 1 b (11 .3 mmol), phenylhydrazine (12.5 mmol), and 70 ml of tetrachloromethane are placed in a 100 ml flask. The mixture is stirred at room temperature over- night (15 hours). After the reaction is completed, tetrachloromethane is removed by evaporation. The crude product is purified by column chromatography with dichloromethane / hexane = 1/30- 1/1 as eluent. Beige solid is obtained by drying in vacuum, (yield: 16.5%). ¹ H-NMR (ppm, CDCIs): 8.09 (dd, 2H), 7.59 (dd, 2H), 7.52-7.39 (m, 9H)

d) The product from example 1 c (0.66 mmol), phenoxazine (1.35 mmol),

Tris(dibenzylideneacetone) dipalladium (0.013 mmol), tri-tert-buthylphosphine (0.026 mmol), sodium t-buthoxide (1.98 mmol) and 7 ml of toluene are placed in a 50 ml flask. The mixture is stirred at 110°C overnight and cooled. The mixture is filtered and the solid is washed with hex- ane, subsequently purified by column chromatography with dichloromethane / hexane = 1/5 as eluent. Pale yellow solid is obtained by drying in vacuum, (yield: 81 .4%). The product is subsequently purified using zone sublimation. ¹ H-NMR (ppm, CDCI ₃ ): 8.47 (d, 2H), 7.80 (d, 2H), 7.52 (m, 5H), 7.47 (d, 2H), 7.38 (d, 2H), 6.68 (m, 12H), 6.01 (dd, 2H), 5.94 (dd, 2H)

An organic light-emitting diode prepared comprising a light-emitting layer comprising the pound A-1 emits light with a high external quantum efficiency.