Title:
FLUORINATED ACRYLATE BLOCK COPOLYMERS WITH LOW DYNAMIC SURFACE TENSION
Document Type and Number:
WIPO Patent Application WO/2013/124421
Kind Code:
A1
Abstract:
The present invention relates to a composition, comprising a binder resin, a block copolymer which comprises at least a block A and a block B, wherein the block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, a vinyl aromatic compound, or any mixture thereof, the block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I): H2C=C(R1)(C(0)ORF-1), wherein R1 is H or methyl; and RF-1 is an organic residue containing a perfluorinated C4-6 alkyl group, a fluorinated alpha-olefm having the following formula (II): H2C=CH(RF-2) (II) wherein RF-2 is an organic residue containing a perfluorinated C4-6 alkyl group, i.e. -(CF2)3-5-CF3 or any mixture thereof.

Inventors:
THOMSON MARY (DE)
KNISCHKA RALF (DE)
AUSCHRA CLEMENS (DE)
ENGELBRECHT LOTHAR (DE)
Application Number:
PCT/EP2013/053567
Publication Date:
August 29, 2013
Filing Date:
February 22, 2013
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BASF SE (DE)
International Classes:
C08L53/00; C09D7/47; C08L27/12; C08L33/14; C08L33/16; C08L75/04; C09D11/00; C09D133/16; C09D153/00; C09J133/16; C09J153/00
Domestic Patent References:
WO2007078819A22007-07-12
WO2003027159A22003-04-03
WO2003033603A12003-04-24
WO2005059048A12005-06-30
WO2009103613A12009-08-27
WO1998001478A11998-01-15
WO1999005099A11999-02-04
WO1999031144A11999-06-24
WO1998058974A11998-12-30
WO1996030421A11996-10-03
Foreign References:
US20040254268A12004-12-16
GB2335190A1999-09-15
GB2361235A2001-10-17
Other References:
See also references of EP 2817370A1
Attorney, Agent or Firm:
MAIWALD PATENTANWALTS GMBH (Elisenstr. 3 / Elisenhof, Munich, DE)
Download PDF:
Claims:
Claims

A composition, comprising

a binder resin,

a block copolymer which comprises at least a block A and a block B, wherein

the block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, a vinyl aromatic compound, or any mixture thereof,

the block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I):

wherein

Rl is H or methyl; and

RF-I is an organic residue containing a perfluorinated

C4-6 alkyl group,

a fluorinated alpha-olefm having the following formula (II):

H2C=CH(RF_2) (II)

wherein Rp_2 is an organic residue containing a perfluorinated C4-6 alkyl group,

or any mixture thereof.

The composition according to claim 1, wherein Rp_i and RF_2, which can be the same or different, have the following formula (III):

-(R2)x-(CF2)3-5-CF3 (III)

wherein x is 0 or 1; and R2 is a divalent non- fluorinated Ci_4 alkylene group.

3. The composition according to claim 1 or 2, wherein the block B of the block copolymer has an average number of monomer units which are derived from the fluorinated (meth)acrylic ester compound of formula (I) and/or from the fluorinated alpha-olefm of formula (II) of at least 0.25.

The composition according to one of the preceding claims, wherein the block A of the block copolymer has an average number of monomer units which are derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound, of at least 5.

The composition according to one of the preceding claims, wherein the block copolymer has a number average molecular weight Mn of from 1000 to 100,000 g/mol; and/or wherein the block copolymer has a polydispersity index PDI of less than 1.90.

The composition according to one of the preceding claims, wherein the block copolymer comprises the monomer units derived from the fluorinated (meth)acrylic ester of formula (I) and/or from the fluorinated alpha-olefm of formula (II) in an amount of from 0.1 wt% to 70 wt%; and/or wherein the block copolymer has a fluorine content of from 0.05 wt% to 35 wt%.

The composition according to one of the preceding claims, wherein the block copolymer is obtained by a controlled free radical polymerization, which is preferably selected from nitroxide-mediated controlled polymerization (NMP), atom transfer radical polymerization (ATRP), or reversible addition- fragmentation chain transfer polymerization (RAFT.

The composition according to one of the preceding claims, wherein two neighbouring blocks are directly linked to each other.

The composition according to one of the preceding claims, wherein two neighbouring blocks are linked to each other via a linking group LG, the linking group LG preferably having the following formula (VII):

wherein the INi ' and IN2' groups, which can be the same or different, are derived from initiator fragments INi and IN2 of the controlled free radical polymerization, and Y' is a divalent group covalently linked to the INi ' and IN2' groups or represents a covalent bond between the ΙΝ and IN2' groups.

10. The composition according to one of the preceding claims, wherein the

amount of the block copolymer, relative to the total composition, is from 0.05 wt% to 15 wt%.

11. The composition according to one of the preceding claims, wherein the block copolymer is a gradient block copolymer.

12. The composition according to one of the preceding claims, wherein the block copolymer is obtained by nitroxide-mediated controlled radical

polymerization (NMP).

13. The composition according to one of the preceding claims, wherein the block copolymer is obtained by nitroxide-mediated controlled polymerization using a polymerization regulator compound which is selected from one of the following formulas (IV), (V) and (VI) or based on the corresponding stable free nitroxyl radicals in conjunction with a radical source:

(IV)

wherein

R is hydrogen, Ci_i8alkyl which is uninterrupted or interrupted by one or more oxygen atoms, cyanoethyl, benzoyl, glycidyl, a monovalent radical of an aliphatic carboxylic acid having 2 to 18 carbon atoms, of a

cycloaliphatic carboxylic acid having 7 to 15 carbon atoms, or an α,β- unsaturated carboxylic acid having 3 to 5 carbon atoms or of an aromatic carboxylic acid having 7 to 15 carbon atoms;

Rioi is Ci_i2alkyl, Cs-7cycloalkyl, C7-8aralkyl, C2_i8alkanoyl,

C3-5alkenoyl or benzoyl;

Rio2 is Ci-isalkyl, C5-7cycloalkyl, C2_8alkenyl, which can be unsubstituted or substituted by a cyano, carbonyl or carbamide group, or is glycidyl, a group of the formula -CH2CH(OH)-Z or of the formula -CO-Z or -CONH-Z wherein Z is hydrogen, methyl or phenyl;

G6 is hydrogen,

G5 is hydrogen or Ci_4alkyl,

Gi and G3 are methyl, G2 and G4 are ethyl or propyl, or Gi and G2 are methyl and G3 and G4 are ethyl or propyl; and

X is selected from -CH2-phenyl, CH3CH-phenyl, (CH3)2C-phenyl, (C5_6Cycloalkyl)2CCN, (CH3)2CCN,

-CH2CH=CH2, CH3CH-CH=CH2 , (Ci_4alkyl)CR20-C(O)-phenyl,

(Ci_4)alkyl-CR20-C(O)-(Ci_4)alkoxy, (Ci_4)alkyl-CR20-C(O)-(Ci_4)alkyl, (Ci_4)alkyl-CR20-C(O)-N-di(Ci_4)alkyl, (Ci_4)alkyl-CR20-C(O)-NH(Ci_4)alkyl, (Ci_4)alkyl-CR2o-C(0)-NH2, wherein R20 is hydrogen or (Ci_4)alkyl.

14. The composition according to one of the preceding claims, wherein the

composition is a coating composition, an ink composition, or an adhesive composition, or a combination thereof. 15. Use of the block copolymer according to one of the claims 1 to 14 as an anti- cratering and/or leveling and/or substrate wetting agent in a coating compositions, an ink composition or an adhesive compositions.

Description:
Fluorinated acrylate block copolymers with low dynamic surface tension

The present invention relates to a composition which comprises a block copolymer having fluorinated monomer units and to the use of said block copolymer as substrate wetting, anti-cratering and/or leveling agent for coating, ink and/or adhesive compositions.

Smooth and crater free surfaces are important for almost all coating, ink and adhesive applications; they provide not only a visually appealing film but serve also as a protective barrier for the substrate as well as homogenous bondstrength throughout the film.

When e.g. the coating is not homogenous and some parts of the surface are only thinly, or not all, coated it leads to poor protection of the substrate. As a result, substrate wetting, anti cratering and leveling agents are added to all sorts of coatings. These difficulties in application of coating resin, particularly in liquid systems, occur particularly when the surface tension of the liquid system is high and the surface tension of the substrate, or contaminants on the substrate, is much lower. The addition of substrate wetting and anti cratering additives reduces both the dynamic and static surface tension of the liquid coating, leading to smoother film formation.

As long as the viscosity of the coating formulation is low, sufficient substrate wetting and leveling can be achieved with commercially available additives. Large problems can be observed in the cases of high solids coatings, powdered coatings and high speed coating processes. There is a strong demand for substrate wetting and anti- cratering additives with a very low dynamic surface tension, which can provide smooth and uniform films in these highly demanding applications.

The same reasoning applies also for inks and adhesives.

Long chain perfluoro chemicals, typically with perfluorinated chains of length C8 and longer, are used as anti-cratering and leveling agents for coating compositions but are known to form very environmentally persistent degradation products, including perfluoro-octanoic acid (PFOA). Thus, there is a need for alternatives which do not form such environmentally persistent degradation products. However, any improvement in degradation properties should not be achieved at the expense of properties which are relevant for leveling agents such as low dynamic surface tension. In general, the effect on dynamic surface tension reduction is believed to decrease with the order of the perfluorinated unit.

WO 2005/059048 describes coating compositions containing leveling agents prepared by nitroxide mediated polymerization. Monomer units may be substituted by fluoro or perfluoro.

WO 2009/103613 describes the use of short perfluorinated chains in copolymers prepared by nitroxide mediated polymerization for the use of leveling agents. It is an object of the present invention to provide a polymeric leveling and anti- cratering agent which does not form environmentally very persistent degradation products such as perfluoro-octanoic acid but still enables manufacturing of coating, ink or adhesive compositions having very low dynamic surface tension. According to a first aspect of the present invention, the object is solved by providing a composition, comprising

a binder resin,

a block copolymer which comprises at least a block A and a block B, wherein the block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a

(meth)acrylamide, a vinyl aromatic compound, or any mixture thereof, the block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I):

wherein

Rl is H or methyl; and

R F - I is an organic residue containing a perfluorinated C 4 _ 6 alkyl group, i.e. -(CF 2 ) 3 - 5 -CF 3 ,

a fluorinated alpha-olefm having the following formula (II):

H 2 C=CH(R F _ 2 ) (II)

wherein Rp_ 2 is an organic residue containing a perfluorinated C 4 _ 6 alkyl group, i.e. -(CF 2 ) 3 _ 5 -CF 3

or any mixture thereof.

A perfluorinated C 4 _ 6 alkyl group is represented by the formula -(CF 2 ) 3 _ 5 -CF 3 .

Preferably, R F _ I and R F _ 2 , which can be the same or different, have the following formula (III):

-(R 2 ) X -(CF 2 ) 3 _ 5 -CF 3 (III)

wherein x is 0 or 1; and R 2 is a divalent non- fluorinated Ci_ 4 alkylene group, which can be substituted or unsubstituted. In a preferred embodiment, R 2 in formula (III) is -(CH 2 ) 1-4 -; such as -CH 2 -; -CH2-CH2-; -CH2-CH2-CH2-; or -CH2-CH2-CH2-CH2-

In a preferred embodiment, the fluorinated (meth)acrylic ester compound of formula (I) is selected from 3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoroctyl acrylate,

3,3,4,4,5 ,5, 6,6, 6-nonafluorhexyl-acrylate, or mixtures thereof.

Preferred fluorinated alpha-olefms of formula (II) include e.g.

3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoro-l-octene,

3,3,4,4,5,5,6,6,6-nonafluoro-l-hexene, or any mixture thereof.

The block B may consist of monomer units derived from the fluorinated

(meth)acrylic ester compound of formula (I) or from the fluorinated alpha-olefm of formula (II). Alternatively, the block B may contain two or more different monomer units.

If the block copolymer contains two or more blocks of type "B", they may differ in block length (i.e. different number of monomer units), but preferably have the same arrangement or sequence of monomer units.

Preferably, the block B of the block copolymer has an average number of monomer units which are derived from the fluorinated (meth)acrylic ester compound of formula (I) and/or from the fluorinated alpha-olefm of formula (II) of at least 0.25, more preferably at least 0.5, or at least 1.

If the average number of monomer units of a specific block is below 1 , this means that, statistically, not every polymer chain contains monomer units of said block. However, when using the block copolymer of the present invention, a reduced dynamic surface tension is still obtained at such low amount of fluorinated monomer units. In a preferred embodiment, the block B of the block copolymer has an average number of monomer units which are derived from the fluorinated (meth)acrylic ester compound of formula (I) and/or from the fluorinated alpha-olefm of formula (II) of from 0.25 to 40, more preferably 0.5 to 30, even more preferably 1 to 20.

Preferably, block A comprises monomer units derived from a compound selected from Ci_i 8 (meth)acrylates, more preferably C 1 -10 (meth)acrylates, especially methyl(meth)acrylate (MMA), ethyl(meth)acrylate, n-butyl(meth)acrylate, iso- butyl(meth)acrylate, t-butyl(meth)acrylate, 2-ethylhexyl(meth)acrylate,

isodecyl(meth)acrylate, hydroxyl- functional (meth)acrylates like 2- hydroxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate, acid functional

(meth)acrylic monomers like acrylic acid or methacrylic acid, sulphonic acid containing monomers like 2-acrylamido-2-methylpropane sulfonic acid (AMPS) , amino functional (meth)acrylates like dimethylaminoethylmethacrylate (DMAEMA), epoxy functional (meth)acrylates like glycidylmethacrylate (GMA), (meth)acrylates containing siloxane groups, vinyl aromatic compounds such as styrene, or any mixture thereof. The block A may consist of monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound.

Alternatively, the block A may contain two or more different monomer units.

If the block copolymer contains two or more blocks of type "A", they may differ in block length (i.e. different number of monomer units), but preferably have the same arrangement or sequence of monomer units. Preferably, the block A of the block copolymer has an average number of monomer units which are derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound, of at least 5, more preferably at least 10, even more preferably at least 15. In a preferred embodiment, the block A of the block copolymer has an average number of monomer units which are derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound, of from 5 to 1000, more preferably from 10 to 500, even more preferably from 15 to 300.

Preferably, the block copolymer has a number average molecular weight Mn of from 1000 to 100,000 g/mol, more preferably from 2,000 to 50,000 g/mol, even more preferably 3,000 to 25,000 g/mol. Other appropriate Mn ranges that can be used in the present invention are e.g. from 3,000 to 100,000 g/mol, or from 4,000 to 100,000 g/mol, or from 6,000 to 50,000 g/mol.

Preferably, the block copolymer comprises the monomer units derived from the fluorinated (meth)acrylic ester of formula (I) and/or from the fluorinated alpha-olefm of formula (II) in an amount of from 0.1 wt% to 70 wt%, more preferably from 0.5 wt% to 50 wt%, even more preferably from 1 wt% to 25 wt%.

Preferably, the block copolymer has a fluorine content of from 0.05 wt% to 35 wt%, more preferably from 0.25 wt% to 25 wt%, even more preferably from 0.5wt% to 17 wt%.

Preferably, the block copolymer has a polydispersity index PDI (i.e. Mw/Mn) of less than 1.90, more preferably of less than 1.60, even more preferably of less than 1.40, or even less than 1.30. The polydispersity index PDI may depend on the number of blocks being present and their arrangement in the block copolymer. If the block copolymer is linear with one block of A and one block of B, PDI may preferably be less than 1.40, more preferably less than 1.30. If the block copolymer is linear with one block of A and two blocks of B, or alternatively with one block of B and two blocks of A, PDI may preferably be less than 1.60, more preferably less than 1.50.

The block copolymer is preferably obtained by a controlled free radical

polymerization (sometimes also referred to as "controlled radical polymerization").

Methods of "controlled free radical polymerization" are generally known to the skilled person.

In a preferred embodiment, the controlled free radical polymerization is selected from nitroxide-mediated controlled polymerization (NMP), atom transfer radical polymerization (ATRP), or from reversible addition- fragmentation chain transfer polymerization (RAFT). These polymerization methods and variants thereof are generally known to the skilled person. The reversible addition- fragmentation chain transfer polymerisation RAFT using chain transfer agents which react by reversible addition- fragmentation chain transfer is described, for example, in WO-A-98/01478, WO-A-99/05099, WO-A-99/31144, and WO 2009/103613. RAFT describes a method of polymer synthesis by radical polymerization in the presence of a free radical source and using chain transfer agents which react by reversible addition- fragmentation chain transfer. The chain transfer agent is, for example,

2-phenylprop-2-yl dithiobenzoate (Ph-C(CH 3 ,CH 3 )-S-C(S)-Ph) or benzyl dithioacetate Ph-CH 2 -S-C(S)-CH 3 as described in WO 98/01478, carbamates such as benzyl 1-pyrrolecarbodithioate, as described in

W099/31144;

alkylxanthates such as ethyl a(0-ethylxanthyl propionate), as described in WO 98/58974.

WO 96/30421 discloses a controlled polymerisation process of ethylenically unsaturated polymers, such as styrene or (meth)acrylates, by employing the Atomic Transfer Radical Polymerisation (ATRP) method. This method produces defined oligomeric homopolymers and copolymers, including block copolymers. Initiators are employed, which generate radical atoms, such as » C1, in the presence of a redox system of transition metals of different oxidation states, e.g. Cu(I) and Cu(II), providing "living" or controlled radical polymerisation.

Details about nitroxide-mediated controlled polymerization are described e.g. in WO 2005/059048 and WO 2009/103613. The initiator compounds described therein can be used in the present invention as well.

More preferably, the controlled radical polymerization is selected from nitroxide- mediated controlled polymerization (NMP) and atom transfer radical polymerization (ATRP), even more preferably from NMP.

In a preferred embodiment, the controlled radical polymerization is a nitroxide- mediated controlled polymerization, which preferably uses a polymerization regulator system based on polymerization regulator compounds being preferably selected from one of the following formulas (IV), (V) and (VI) or based on the corresponding stable free nitroxyl radicals in conjunction with a radical source:

wherein

R is hydrogen, Ci_i 8 alkyl which is uninterrupted or interrupted by one or more oxygen atoms, cyanoethyl, benzoyl, glycidyl, a monovalent radical of an aliphatic carboxylic acid having 2 to 18 carbon atoms, of a cycloaliphatic carboxylic acid having 7 to 15 carbon atoms, or an α,β-unsaturated carboxylic acid having 3 to 5 carbon atoms or of an aromatic carboxylic acid having 7 to 15 carbon atoms;

Rioi is Ci_i 2 alkyl, C5- 7 cycloalkyl, C 7 - 8 aralkyl, C 2 -i 8 alkanoyl, C3- 5 alkenoyl or benzoyl;

Rio2 is Ci-isalkyl, C 5 - 7 cycloalkyl, C 2 _ 8 alkenyl, which can be unsubstituted or substituted by a cyano, carbonyl or carbamide group, or is glycidyl, a group of the formula -CH 2 CH(OH)-Z or of the formula -CO-Z or -CONH-Z wherein Z is hydrogen, methyl or phenyl;

G 6 is hydrogen,

G 5 is hydrogen or Ci_ 4 alkyl,

Gi and G3 are methyl,

G 2 and G 4 are ethyl or propyl, or Gi and G 2 are methyl and G3 and G4 ethyl or propyl; and

X is selected from -CH 2 -phenyl, CH 3 CH-phenyl, (CH 3 ) 2 C-phenyl, (C 5 _ 6cycloalkyl) 2 CCN, (CH 3 ) 2 CCN,

-CH 2 CH=CH 2 , CH 3 CH-CH=CH 2 , (Ci_ 4 alkyl)CR 20 -C(O)-phenyl, (Ci_ 4 )alkyl- CR 20 -C(O)-(Ci_ 4 )alkoxy, (Ci_ 4 )alkyl-CR 20 -C(O)-(Ci_ 4 )alkyl, (Ci_ 4 )alkyl-CR 20 - C(0)-N-di(Ci_ 4 )alkyl, (Ci_ 4 )alkyl-CR 20 -C(O)-NH(Ci_ 4 )alkyl, (Ci_ 4 )alkyl-CR 20 - C(0)-NH 2 , wherein R 20 is hydrogen or (Ci_ 4 )alkyl; and

wherein any of the alkyl groups can be unsubstituted or substituted, e.g. by one or more functional groups such as hydroxyl, amino, carboxylic acid, halide, cyano, and/or carbonyl.

The above polymerization regulator compounds as well as their corresponding stable free nitroxl radicals and their preparation are described in GB 2 335 190 and

GB 2 361 235.

As known to the skilled person, controlled free radical polymerization may involve using an initiator fragment IN for initiating the radical polymerization. The initiator fragment can be released from a polymerization regulator compound IN-E, e.g. from one of those described above. In formulas (IV) to (VI), radical X represents the initiator fragment IN, whereas the nitroxide radical would represent the group E. The block copolymer can be a diblock copolymer, a triblock copolymer, or multiblock copolymer.

The block copolymer can be linear, or branched (such as star-shaped, comb-shaped, etc.).

In the present invention, the term "block copolymer" also includes a gradient and/or tapered block copolymer. This type of structured copolymer is also generally known to the skilled person. In a gradient or tapered block copolymer, there is a gradient compositional transition between blocks A and B.

In a preferred embodiment, a block can also be defined as a region of the polymer chain that is richer in fluorinated monomer than another block. In the block copolymer of the present invention, two neighbouring blocks can be directly linked to each other. Alternatively, two neighbouring blocks can be linked to each other via a linking group LG, e.g. -A-LG-B- ; -B-LG-B- ; -A-LG-A-

The linking group LG can be any divalent group which may form a covalent bond to blocks A and B. Appropriate linking groups are known to the skilled person.

In a preferred embodiment, the linking group LG has the following formula (VII):

wherein the INi ' and IN 2 ' groups, which can be the same or different, are derived from the initiator fragments INi and IN 2 of the controlled free radical polymerization, and Y' is a divalent group covalently linked to the INi ' and IN 2 ' groups or represents a covalent bond (e.g. σ-bond or π-bond) between the ΙΝ and IN 2 ' groups. Preferably, the initiator fragments INi and IN 2 are the same and, consequently, the ΙΝ and IN 2 ' groups are the same as well.

The divalent group Y' can be derived from a compound Y having at least two functional groups which may react with the initiator fragments INi and IN 2 .

Appropriate compounds having at least two functional groups are e.g. diisocyanate compounds (such as toluene diisocyanate), aliphatic polyisocyanates or isocyanurate compounds. The linking group LG of formula (VII) can be obtained by using, in the controlled free radical polymerization, an initiator fragment IN having at least one functional group, such as hydroxyl, amino, carboxylic acid, halide, cyano, and/or carbonyl. After having initiated controlled free radical polymerization, the initiator fragment IN is covalently bonded to one end of the polymer chain. In the presence of a compound Y having two functional groups, a chemical reaction between said compound Y and two IN groups of two different polymer chains may take place, thereby bonding these polymer chains to each other via a linking group of formula (VII). The block copolymer of the present invention may contain only one block A, or may contain two or more blocks of A. The blocks may have the same number of monomer units or may differ in block length (i.e. different number of monomer units). The block copolymer of the present invention may contain only one block B, or may contain two or more blocks of B. The blocks may have the same number of monomer units or may differ in block length (i.e. different number of monomer units).

If the block copolymer contains at least two blocks of A and at least two blocks of B, the block copolymer may comprise the following structural element: -B-A-LG-A-B- or -A-B-LG-B-A- wherein LG is the linking group described above, which is preferably of formula (VII). Preferably, the amount of the block copolymer, relative to the total composition, is from 0.05 wt% to 15 wt%, more preferably from 0.075 wt% to 10 wt% and most preferred from 0.1 wt% to 5 wt%.

The binder resin can be selected from those commonly used for coating

compositions. Appropriate binder resins are known to the skilled person.

The binder resin can be selected from solvent based resins, water based resins, emulsion polymers, solution polymers, or any mixture thereof. The binder resins comprise all kinds of crosslinking mechanism and coating systems based on one-component multi-component systems, e.g. thermosetting resins, room temperature curable resins, radiation-curable resins. Also included are physically drying coating systems like thermoplastic acrylic resins. The resins comprise state of the art polymer chemistry used in coatings, inks and adhesives: e.g. saturated polyesters, unsaturated polyesters, polyacrylates, styrene- acrylic resins, polyurethanes, epoxy resins, nitrocellulose resins, hybrid systems like polyester/polyurethanes, polyacrylate/poly- urethanes, alkyd/melamine,

polyester/CAB/melamine, polyacrylate/CAB/melamine, etc. Preferred binder resins comprise powder coating resins, i.e. resin systems which are solid at room

temperature and do not include a liquid carrier, e.g. thermosetting powder coatings or radiation curable powder coatings like polyester/PRIMID, polyester/TGIC, epoxy- functional polyacrylates with acidic crosslinker components, etc. The weight ratio the block copolymer to binder resin can be varied over a broad range. Preferably, the weight ratio of block copolymer to binder resin is within the range of from 0.001 to 0.5 more preferably from 0.005 to 0.3 even more preferably from 0.01 to 0.1.

Preferably, the composition is a coating composition, an ink composition or an adhesive composition.

Exemplary compositions include a solvent-based coating composition, a water-based coating composition, a high solids coating composition, a powder coating

composition, a solvent-borne ink composition, a water-borne ink composition, a UV- curable ink composition, or a UV-curable coating composition, or combinations thereof. According to a further aspect, the present invention is directed to the use of the block copolymer described above as an anti-cratering and/or leveling and/or substrate wetting agent in coating compositions, ink compositions, or adhesive compositions.

As the block copolymer of the present invention provides a significant reduction in dynamic surface tension, it is preferably used as an anti-cratering and/or leveling agent in challenging coating systems, such as high solids coatings, powder coatings, solvent-borne inks, water-borne inks, UV inks, UV coatings and/or in high speed coating processes. According to a further aspect, the present invention is directed to the use of the block copolymer described above for reducing dynamic surface tension in a coating composition, ink composition or adhesive composition, such as high solids coating compositions and powder coating compositions, ink compositions such as solvent- borne inks, water-borne inks, UV inks, UV coatings. Preferably, the term "reducing dynamic surface tension" means that dynamic surface tension is lower if compared to a random but otherwise identical copolymer.

Examples I. Measuring methods

If not indicated otherwise, parameters defined in the present application are measured by the measuring methods described below:

Number average molecular weight Mn, polydispersity index PDI

Mn and PDI are measured by gel permeation chromatography (GPC) with polystyrene standards. The eluent is THF.

Amount of F (in wt%) and amount of fluorine-containing monomer units (in wt%) in the block copolymer

Determined by 1H NMR, 400 MHz. II. Preparation Examples Inventive Example 1

Synthesis of a linear A-B Block-copolymer of n-Butyl Acrylate (nBA) and

3.3.4.4.5.5.6.6.7.7.8.8.8-Tridecafluoroctyl Acrylate (TFOA

Synthesis of A block

In a 5000 mL glass reactor with overhead mechanical stirrer, condenser, metering pumps, computerized temperature control and data acquisition, the following A- blocks are synthesized.

GK3023-360 (10 units nBA)

1816.70 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), 150.00 g of the initiator compound NOR 1 (317.48 g/mol) and 271.38 g of ethyl acetate (EtAc, Mw 88.11 g/mol) are mixed together, purged with N 2 and reacted for 3 h at 120°C. Residual monomer and ethyl acetate is distilled off at 105°C and 20 mbar.

Yield: 33.3%; GPC (THF, PS-Standard, Mn = 1706 g/mol, PDI = 1.26, liquid)

GK3023-264 (20 units)

1211.13 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 60.00 g of the initiator compound NOR 1 (317.48 g/mol) are mixed together, purged with N 2 and reacted for 3.5 h at 115°C. Residual monomer is distilled off at 105°C and 20 mbar.

Yield: 42.83%; GPC (THF, PS-Standard, Mn = 2435 g/mol, PDI = 1.36, viscous liquid) GK3023-335 (35 units)

1383.92 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), 40.00 g of the initiator compound NOR 1 (317.48 g/mol) and 206.70 g of ethyl acetate (EtAc, Mw 88.11 g/mol) are mixed together, purged with N 2 and reacted for 3 h at 120°C. Residual monomer and ethyl acetate is distilled off at 105°C and 20 mbar.

Yield: 38.3%; GPC (THF, PS-Standard, Mn = 3649 g/mol, PDI = 1.44, viscous liquid)

GK3023-387 (75 units)

1211.13 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 60.00 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 and reacted for 1.5 h at 115°C. A feed of 2422.26 g of nBA is fed to the reactor over 3 hours. At 125°C, the reaction continues for a further 4.5 h. Residual monomer is distilled off at 105°C and 20 mbar. Yield: 50.36%; GPC (THF, PS-Standard, Mn = 9650 g/mol, PDI = 1.21, viscous liquid)

Synthesis of B block

Mw =418.15

In a 5 -necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table) and B g of 3,3,4,4, 5,5, 6,6, 7,7, 8,8,8- Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128°C. Residual monomer is distilled off at 105°C and 20 mbar. The polymer is characterized by GPC (THF and with PS-Standards; note: the refractive index of TFOA is negative) and 1H-NMR (in CDCI3).

c Polymerization at 115°C for 2 hours.

Comparative Example 2

Synthesis of a linear, low polydispersity, random copolymer of n-Butyl Acrylate (nBA) and 3.3.4.4.5.5.6.6.7.7.8.8.8-Tridecafluoroctyl Acrylate (TFOA)

GK3479-027

Mw =418.15

In a 5 -necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, C 65.70 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), D 3.70 g of

3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafiuoroctyl Acrylate (TFOA, Mw 418.15 g/mol) and E 2.50 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 3-4 hours at 125°C. Residual monomer is distilled off at 95°C and 10 mbar. The polymer is characterized by GPC (THF and with PS- Standards) and 1H-NMR (in CDC1 3 ). wt.%

C (g of D (g of E (g Yield Mn a wt% F in

Product PDI a TFOA

nBA) TFOA) NORl) (%) (g/mol) b polymer b

GK3479-

65.70 3.70 2.50 60.14 3724 1.20 8.02 4.73 027

GK3479-

62.00 7.40 2.50 61.80 4031 1.23 14.27 8.42 026

GK3479-

58.00 11.40 2.50 60.71 3814 1.25 19.46 11.48 024

GK3479-

47.79 2.67 2.50 44.87 2217 1.30 12.55 7.41 022

GK3479-

45.06 5.40 2.50 47.76 2298 1.27 17.73 10.46 021

GK3479-

42.38 8.08 2.50 46.11 2296 1.28 21.53 12.70 020

a by GPC with polystyrene standards

b by H 1 NMR

Comparative Example 3

Synthesis of random copolymer of n-Butyl Acrylate (nBA) and

3.3.4.4.5.5.6.6.7.7.8.8.8-Tridecafluoroctyl Acrylate (TFOA) by free radical polymerization

GK3365-133

In a 5 -necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, 50.00 g of sec-Butanol (Mw 74.12 g/mol) is purged with N2 for 30 minutes and heated to 100°C. A pre-mixed feed of A 5.00 g of 3,3,4,4,5,5,6,6,7,7,8,8,8- Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol), B 88.54 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and C 6.46 g of tert-butyl Peroxy-2-ethylhexanoate (tBpOEH, Mw 216.32 g/mol) is fed to the reactor over 3 hours. After the completion of the feed, the reaction continues to react for a further 3 hours. The solvent is distilled off at lOOoC and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and 1H-NMR (in CDC1 3 ). B (g of A (g of C (g of Mn a wt.% wt% F in

Product PDI a

nBA) TFOA) tBpOEH) (g/mol) TFOA b polymer b

GK3365-

88.54 5.00 6.46 2065 1.56 5.35 2.95 133

GK3365-

83.54 10.00 6.46 2072 1.56 10.69 5.90 134

GK3365-

78.54 15.00 6.46 2043 1.50 16.04 8.85 135

GK3365-

88.54 5.00 3.00 2604 1.70 5.35 2.95 136

Inventive Example 4

Synthesis of a linear B-A-B Block-copolymer of n-Butyl Acrylate (nBA, A-block) and 3.3.4.4.5.5.6.6.7.7.8.8.8-Tridecafluoroctyl Acrylate (TFOA, B-block

Synthesis of A (interior) block

NOR 2 n-BA

Mw =342.48 Mw =128.17

In a 5000 mL glass reactor with overhead mechanical stirrer, condenser, metering pumps, computerized temperature control and data acquisition, the following A- blocks-precursors are synthesized. GK3023-389 (75 units)

2165.22 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 80.00 g of the initiator compound NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 1.5 h at 115°C. A feed of 1624.54 g of nBA was fed to the reactor over 5 hours. At 125°C, the reaction continues for a further 2 h. Residual monomer is distilled off at 105°C and 20 mbar.

Yield: 50.29%; GPC (THF, PS-Standard, Mn = 10740 g/mol, PDI = 1.19, viscous liquid)

GK3023-287 (15 units) 2944.4 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 180 g of NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 3.5 h at 115°C. Residual monomer is distilled off at 105°C and 20 mbar.

Yield: 28.84%; GPC (THF, PS-Standard, Mn = 2172 g/mol, PDI = 1.25, viscous liquid)

GK3023-010 (35 units) In a 2000 mL glass reactor with overhead mechanical anchor stirrer, condenser and metering pumps 561.36 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 50.00 g of NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 2 h at 115°C. A feed of 748.48 g of nBA is fed to the reactor over 6 hours. At 120°C, the reaction continues for a further 6 h. Residual monomer is distilled off at 105°C and 20 mbar. Yield: 49.67%; GPC (THF, PS-Standard, Mn

liquid)

Coupling to synthesize difunctional A-blocks

In a 5 -necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, F g of Poly-nBA precursors (see table) and G g of tolylene-2,4-diisocyanate (TDl, Mw 174.16 g/mol) are mixed together and purged with N2 for 30 minutes. The inner temperature is raised to 60°C and a few drops of dibutyltin dilaurate (DBTL, Mw 631.56, 10% solution in butyl acetate) are added. The coupling reaction continues for 4 hours at 60°C. The polymer is characterized by GPC (THF and with PS-Standards and 1H-NMR (in CDC1 3 ).

Synthesis of B block In a 5 -necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, H g of di- functional poly nBA (see table) and I g of 3,3,4,4, 5, 5,6, 6,7, 7, 8,8,8- Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128°C. Residual monomer is distilled off at 105°C and 20 mbar. The polymer is characterized by GPC (THF and with PS-Standards; note: the refractive index of TFOA is negative) and 'H-NMR (in CDCls).

a by GPC with polystyrene standards

b based on solids content

c Polymerized with a maximum temperature of 115°C in 1 hour.

d Polymerized with a maximum temperature of 115°C in 22 hours.

Inventive Example 5

Synthesis of a linear A-B Block-copolymer of n-Butyl Acrylate (nBA) and

3,3,4,4,5, 5, 6,6,6-Nonafluorhexyl Acrylate (NNFHA) Synthesis of A block

The same A-blocks as those described in Example 1 are used as the starting block for the chain extension with NFHA monomer.

Synthesis of B block

In a 5-necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table) and B g of 3,3,4,4,5 ,5, 6,6,6-Nonafluorhexyl Acrylate (NFHA. Mw 318.13 g/mo 1) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128°C. Residual monomer is distilled off at 105°C and 20 mbar. The polymer is characterized by GPC (THF and with PS- Standards; note: the refractive index of NFHA is negative) and 1H-NMR (in CDCI3).

by GPC with polystyrene standards

by H 1 NMR

Comparative Example 6

Synthesis of a linear, low polydispersity, random copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA)

GK3 '47 7 9-202

C9H7F9O2 In a 5 -necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, C 50.86 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), D 9.70 g of 3,3,4,4,5 ,5, 6,6,6-Nonafluorhexyl Acrylate (NFHA, Mw 318.13 g/mol) and E 3.00 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 3-4 hours at 125°C. Residual monomer is distilled off at 95°C and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and

by GPC with polystyrene standards

by H 1 NMR Comparative Example 7 Synthesis of random copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,6- Nonafluorhexyl Acrylate (NFHA) by free radical polymerization

GK3365-207 In a 5 -necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, 50.00 g of sec-Butanol (Mw 74.12 g/mol) is purged with N2 for 30 minutes and heated to 100°C. A pre-mixed feed of A 5.00 g of 3,3,4,4,5,5,6,6,6- Nonaf uorhexyl Acrylate (NFHA, Mw 318.13 g/mol), B 88.54 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 6.46 g of tert-butyl Peroxy-2-ethylhexanoate (tBpOEH, Mw 216.32 g/mol) is fed to the reactor over 3 hours. After the completion of the feed, the reaction continues to react for a further 3 hours. The solvent is distilled off at 100°C and 10 mbar. The polymer is characterized by GPC (THF and with PS- Standards) and 1H-NMR (in CDC1 3 ).

Inventive Example 8 Synthesis of a linear A-B Block-copolymer of n-Butyl Acrylate (nBA) and

3.3.4.4.5.5.6.6.7.7.8.8.8-Tridecafluor-l-octene (TFO)

Synthesis of A block

The same A-blocks as those described in Example 1 are used as the starting block for the chain extension with TFO monomer.

Synthesis of B block

In a 5 -necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table), B g of 3, 3,4,4,5, 5,6,6, 7,7, 8,8, 8-Tridecafluor-l- octene (TFO, Mw 346.09 g/mol) and C g of toluene are mixed together, purged with N2 for 30 minutes and polymerized for 6 hours at reflux (106-110°C). Residual monomer and solvent is distilled off at 120°C and 20 mbar to >99%. The polymer is characterized by a mass balance of the distillate.

III. Application Exampl

Static surface tension:

Static surface tension is measured using an OCA 20 (Dataphysics) at concentrations from 1 - 10 w% in xylene using the hanging-drop method.

Table 1.1 Si atic surface tension

At comparable amounts of TFOA w% (GK3479/022 as a comparative example and GK3479-042 as an inventive example), a much lower static surface tension in xylene are clearly observed (28.98 mN/m and 25.93 mN/m respectively at 1 w% in xylene).

Dynamic surface tension:

(i) With block B containing fluorinated (meth)acrylic ester derived units Dynamic surface tension is measured using a bubble pressure tensiometer (Sita) at concentrations of 0.25 % 0,5 w% in the A component of a solventbased 2K-PU. Bubble life times are measured from 80 msec up to 10 sec.

A component 2K PU:

Table 2.1 2K-PU Component A

Efka 2018N is a commercially available defoamer.

At a very short bubble life time, a clear advantage (lower dynamic surface tension values) could be observed looking at same w% F-Monomer and 0.5 w% addition levels. Inventive examples GK3479/047 GK3479/042 GK3494/026 GK3494/027

DST at 80 ms, 0,5

w% addition level 73,1 63,3 56,2 55,2

w% TFOA 3,7 10,2 14,9 24,9

(ii) With block B containing fluorinated alpha-olefm derived units

Dynamic surface tension is measured using a bubble pressure tensiometer (Sita) at concentrations of 0.1 % 1.0 w% in the A component of a solventbased 2K-PU. Bubble life times are measured from 80 msec up to 10 sec. In the following test series the commercial leveling additive EFKA 3600N is used a reference.

A component 2K PU:

Table 2.1 2K-PU Component A

At a very short bubble life time, a clear advantage (lower dynamic surface tension values) could be observed compared to the commercial benchmark at 0.25 w% addition levels. Inventive examples GM800-012 GM800-013

DST at 80 ms, 0,25

w% addition level 72.4 70.9

Comparative

examples Efka 3600N

DST at 80 ms, 0,25

w% addition level 80.3

The results are also shown in Figure 1.

Anticratering test:

The formulation, according to table 3.1, is treated for about one hour on the roll bench and finally shaken by hand until homogenous. The amount of component A indicated in table 3.2 is added in 20 ml glass jar with the appropriate amount of component B. The sample is immediately shaken by hand until homogenous and applied on a PET foil. A draw down of the mixture with 75 μιη wire bar at speed 20 mm/ sec is prepared. The sample is checked for craters and haze on the panels after drying over night.

Table 3.1 2K- 'U Component A

Table 3.2 2K-PU Component B

Mixing ratio: A: B=100:35 (36 round) Table 3.3 Anticrater performance in 2K-PU

a Blank contains no additive.

1 indicates no craters and 8 indicates many craters.