The present invention relates to the field of"constrained geometry catalyst" systems based on Group Illb metals of the Periodic Table. It also relates to their synthesis and their use in olefin polymerisation.

"Constrained geometry catalysts" (CGC) are half-sandwich complexes bearing hetero-bifunctional cyclopentadienyl-amido ligands. They have attracted much attention owing to several reasons: - replacing of a cyclopentadienyl moiety in linked bis (cyclopentadienyl) ligands by a less electron-donating amido group results in the formation of ansa- metallocene-like complexes with higher Lewis acidity; and therefore potentially enhanced catalytic activity towards Lewis basic substrates.

- there are many more possibilities to design new catalytic geometries by selecting appropriate substituents on the cyclopentadienyl ring, on the bridging atom and on the heteroatom of the side chain.

The synthesis and polymerisation abilities of cyclopentadienyl-amido complexes of group III metals (Sc, Y, Yb, Lu) have been described for example in Shapiro et al.

(P. J. Shapiro, W. D. Cotter, W. P. Schaefer, J. A. Labinger, J. E. Bercaw; in J. Am.

Chem. Soc. , 1994,116, 4623. ) or in Hultzsch et al. (K. C. Hultzsch, P. Voth, K.

Beckerle, T. P. Spaniol, J. Okuda; in Organometallics, 2000,19, 228. ), or in Tian et al. (S. Tian, V. M. Arredondo, C. L. Stern, T. J. Marks; in Organometallics, 1999, 18,2568.), or in Mu et al. (Y. Mu, W. Piers, M.-A. MacDonald, M. J. Zaworotko; in Can. J. Chem. , 1995,73, 2233. ) or in Arndt and Okuda (S. Arndt, J. Okuda, in Chem. Rev. , 2002,102, 1953. )

All these publications however were limited to lantanide compounds with combined cyclopentdienyl-amido ligands. None has addressed the field of fluorenyl-amido ligands.

It is an object of the present invention to-prepare in good yield bridged half- sandwich metallocene components based on fluorenyl-heteroatom ligands and based on Group Illb metals of the Periodic Table.

It is another aim of the present invention to prepare catalyst components efficient in the controlled polymerisation of styrene.

It is a further aim of the present invention to prepare catalyst components capable of preparing polymethylmethacrylate.

More generally, the present invention aims at preparing catalyst systems efficient in the controlled polymerisation of polar or non polar monomers.

Accordingly, the present invention discloses a metallocene catalyst component based on a Group Illb metal of the Periodic Table and a bridged constrained geometry fluorenyl-based ligand.

In a first embodiment, the present invention discloses a metallocene catalyst component of the general formula [ (Flu-SiR2-N-R') M (R") (L) n] m (I) wherein Flu is a fluorenyl, substituted or unsubstituted, M is a Group Illb metal of the Periodic Table, SiR2 is a structural bridge between N and Flu (9-position) imparting stereorigidity to the component wherein each R is the same or different

and is an alkyl having from 1 to 20 carbon atoms, R'is hydrogen or is of the form ZR$3 wherein Z is C or Si and R$ is a hydrocarbyl having from 1 to 20 carbon, R"is hydrogen, or a hydrocarbyl having from 1 to 20 carbon atoms, said hydrocarbyl possibly containing one or more Si atoms, or is a halogen, L is a co-ordinating solvent, n is 0,1 or 2, and m is 1 or 2.

The substituents on the fluorenyl are not particularly limited, they can be the same or different and are of the form ZR$3 as defined here-above; they include particularly hydrocarbyls having from 1 to 20 carbon atoms. Preferably, they are located at positions 3 and 6, or at positions 4 and 5, or at positions 2 and 7 and more preferably, they are the same.

M is preferably yttrium, lanthanum or a member of the lanthanide series.

Throughout this description, the term"lanthanide series"means the rare earth series of elements having atomic numbers of from 58 to 71. In the lanthanide series M is preferably neodymium, samarium. More preferably, M is yttrium.

Preferably, N is substituted and more preferably, the substituent is tert-butyl.

Preferably, R"is hydrogen or an alkyl or an aryl or an allyl or a halogen, and m is 1 when R"is an alkyl or an aryl or an allyl, m is 2 when R"is hydrogen or a halogen.

When R"is a halogen, it is preferably Cl, l, or Br.

The co-ordinating solvent is typically an ether such as for example tetrahydrofuran (THF), dimethoxyether (DME) or diethyl oxide (Et20).

In order to be active in polymerization, compounds of type (I), wherein R"is a halogen must be alkylated first with an adequate reagent. Typical reagents can be

selected from LiR, R MgX, Mg R*z, Al R* 3, Al R* nX3-n, [Li] + [AIR* nX3-nl-and methylalumoxane (MAO), wherein R* is an alkyl, aryl or allyl having from 1 to 20 carbon atoms and X is a halogen, preferably Cl. This list should not be considered as limitative.

In a second embodiment, the present invention discloses a metallocene catalyst component of the general formula [(Flu-SiR2-N-R') 2 M]- [Q (L) p] + (II) wherein all symbols are as defined in formula (I), Q is an alkali, an earth alkali or a Group IIIa metal of the Periodic Table and p is from 2 to 4.

Q is preferably Li, Na, Mg or AI.

When the ion-pair in complex 11 is fully dissociated, p is 4 and when the ion-pair is partially associated, p is 2 or 3.

The present invention discloses a first method, based on a salt metathesis reaction method for preparing the catalyst components (I) or (II) that comprises the steps of: a) suspending MX3 (THF) n in an ether; b) suspending a deprotonated dilithium salt [Flu-SiR2-N-R'] Li2 in the same or another ether; c) carrying out the salt metathesis reaction of suspensions a) and b) at a temperature of from-80 °C to 60 °C. d) recrystallising the crude product obtained in c) after evaporation of volatiles from an ether or a mixture of an ether and an hydrocarbon at a temperature of from-60 to-0°C ; e) retrieving a crystalline powder of formula (I) or (II)

In another embodiment of the present invention, complex (I) wherein R"is a halogen, can comprise the additional step of alkylation with an alkylating agent to give complex (I) wherein R"is a hydrocarbyl as defined above.

Suitable alkylating agent can be selected from LiR+, R+MgX, MgR+2, AIR+3, AIR+nX3- n and [Li]+[AlR+nX3-n]- wherein R+ is an alkyl, an aryl or an allyl having from 1 to 20 carbon atoms and X is a halogen, preferably cl.

The present invention discloses a second method, based on an alkane elimination reaction, for preparing specifically the catalyst component [ (Flu-SiR2-N-R') M (R") (L) n] m (I) wherein R"is specifically a hydrocarbyl having from 1 to 20 carbon atoms, said hydrocarbyl possibly containing one or more Si atoms, that comprises the steps of reacting the triscarbyl complex M (R") s (L) n, either presynthesised or generated in situ, with one equivalent of the diproteo ligand (FluH-SiR2-NH-R').

The triscarbyl complex M (R") 3 (L) n is preferably generated in situ as the reaction product of MCI3 (THF) n and 3 equivalents of LiR". The reaction temperature for the preparation of complex (I) is of from 0 °C up to 75 °C and preferably of from 40 to 50 °C. For the second method of preparation described here-above, M is preferably Yttrium and the bridge SiR2, is preferably a dialkyl silyl.

These two methods can comprise the additional step of hydrogenolising carbyl complex (I) to prepare complex [ (Flu-SiR2-N-R) M (H) (L) n] m (I) Suitable hydrogenolising agents can be selected from dihydrogen or an hydrosilane, e. g. phenylsilane. The reaction is preferably carried out at room temperature at about 25 °C and at atmospheric pressure in an hydrocarbon

solvent, e. g. benzene or toluene. The reaction product is insoluble in both polar (ethers) and non-polar (hydrocarbons) solvents.

The present invention further discloses a catalyst system based upon any one or more of catalyst components of formulas (I) and/or (II) and a suitable activating agent and/or a transfer agent.

The present invention discloses a process for polymerisation comprising the steps of: a) introducing a catalyst system based on any one or more of catalyst components of formulas (I) and/or (II) in the reactor, b) optionally introducing an activating agent or a transfer agent in the reactor, c) feeding a monomer and an optional comonomer, d) maintaining the system under polymerisation conditions, e) retrieving the desired polymer.

The optional activating agent includes Lewis acids having an ionising action and having a low or no co-ordinating capability. Typically, all the activators used with the metals Group IV of the Periodic Table can be used in the present invention.

Suitable aluminium-containing activating agents comprise an alumoxane an aluminium alkyl or an alkylaluminate [Li] + [AIR* nX3-nl- The alumoxanes that can be used in the present invention are well known and preferably comprise oligomeric linear and/or cyclic alkyl alumoxanes represented by the formula (III) : for oligomeric linear alumoxanes ; and formula (IV)

for oligomeric cyclic alumoxanes, wherein n is 1-40, preferably 10-20; m is 3-40, preferably 3-20; and R is a Cl-C8 alkyl group, preferably methyl. Generally, in the preparation of alumoxanes from, for example, aluminium trimethyl and water, a mixture of linear and cyclic compounds is obtained.

Suitable boron-containing activating agents may comprise a triphenylcarbenium boronate, such as tetrakis-pentafluorophenyl-borato-triphenylcarbenium as described in EP-A-0427696: or those of the general formula below, as described in EP-A-0277004 (page 6, line 30 to page 7, line 7): Other preferred activating agents include hydroxy isobutylaluminium and a metal aluminoxinate.

Alkylating agents of the type MgR=2 can also be used as activating agents, wherein each R= is the same or different and is a hydrocarbyl having from 1 to 20 carbon atoms, and optionally containing one or more Si atoms The transfer agents comprise for example H2 and hydrosilanes of the formula HSiR"'3 wherein each R"'is the same or different and is either an H atom or a hydrocarbyl having from 1 to 20 carbon atoms. They are selected in accordance with the monomer to be polymerised.

The monomers that can be used in the present invention include non polar monomers such as for example ethylene, alpha-olefins, styrene and polar monomers such as for example (meth) acrylates or dienes. Preferably, styrene and methyl methacrylate have been used.

The catalyst system of the present invention may be employed in any type of homo- or co-polymerisation method, provided that the required catalytic activity is not impaired. In a preferred embodiment of the present invention, the catalyst system is employed in a bulk polymerisation process or in a solution polymerisation process, which is homogeneous, or in a slurry process, which is heterogeneous. In a solution process, typical solvents include THF or hydrocarbons having from 4 to 7 carbon atoms such as heptane, toluene or cyclohexane. In a slurry process, it is necessary to immobilise the catalyst system on an inert support, particularly a porous solid support such as talc, inorganic oxides and resinous support materials such as polyolefin. Preferably, the support material is an inorganic oxide in its finely divided form.

Suitable inorganic oxide materials that are desirably employed in accordance with this invention include group IIA, IIIA, IVA, or IVB metal oxides such as silica, alumina and mixtures thereof. Other inorganic oxides that may be employed, either alone or in combination with the silica or alumina, are magnesia, titania, zirconia, and the like. Other suitable support materials, however, can be employed, for

example, finely divided functionalised polyolefins such as finely divided polyethylene.

Preferably, the support is a silica support having a surface area of from 200- 700 m2/g and a pore volume of from 0.5-3 ml/g.

The polymerisation temperatures range from-20 °C up to 100 °C.

The present invention also covers the polymers obtainable by polymerisation in the presence of the catalysts components described hereabove.

LIST OF FIGURES.

Figure 1 represents the crystal structure of the molecule [3, 6-di-tBu-C13H6- SiMe2-NtBu] Y (CH2SiMe3) (THF) 2 (1).

Figure 2 represents the 1H NMR spectrum of complex [3, 6-di-tBu-C13H6-SiMe2- NtBu] Y (CH2SiMe3) (THF) 2 (1) in C6D6 at 25 °C.

Figure 3 represents the 13C NMR spectrum of complex ( [3,6-di-tBu-C13H6-SiMe2- NtBu] Y (CH2SiMe3) (THF) 2 (1) in C6D6 at 25 °C.

Figure 4 represents the'H NMR spectrum of complex [3, 6-di-tBu-C13H6-SiMe2- NtBu] Y (CH2SiMe3) (THF) 2 (1) in C6D6 at-70 °C.

Figure 5 represents the 1H NMR spectrum of complex [{(tbu2-C13H6)-SiMe2- NtBu} 2Y]-[Li (THF) 4] + (2) in THF-d8 at 25 °C.

Figure 6 represents the 13C NMR spectrum of complex [{(tBu2-C13H6)-SiMe2- NBu} 2YnU (THF) 4] + (2) in THF-ds at 25 °C.

Figure 7 represents the crystal structure of the molecule [{3,6-di-tBu-C13H6- SiMe2-NtBu} 2La]- [Li (OEt2) 2] (4) Figure 8 represents the crystal structure of the molecule [(3,6-di-tBu-C13H6- SiMe2-NtBu) Nd (µ-Cl)(THF)]2 (5).

EXAMPLES.

Synthesis of [3, 6-di-tBu-C13H6-SiMe2-NtBu]Y(CH2SiMe3) (THF) 2 (1).

(a) NMR scale reaction : An NMR tube equipped with a teflon valve was charged with Y [CH2SiMe3)] 3 (THF) 2 (32.4 mg, 0.065 mmol) and 3, 6-di-tBu-Ci3H6H-SiMe2- NHtBu (26.7 mg, 0.065 mmol) and benzene-d6 (#0. 6 mL) was condensed in at- 196 °C. The tube was stopped with valve and heated to room temperature.

Progress of the reaction was monitored periodically by'H NMR spectroscopy.

(b) Preparative scale reaction : Anhydrous YC13 (338 mg, 1.73 mmol) was slurried in THF (15 mL) and stirred at 80 °C for 1 h. The solvent was removed in vacuo and the solid residue was suspended in pentane (20 mL). The suspension was cooled to-78 °C, a solution of LiCH2SiMe3 (5.2 mL of a 1M solution in pentane, 5.2 mmol) was added, and the suspension was stirred at 0 °C for 2 h. The suspension was filtered and the white solid was extracted with pentane (2 x 10 mL). LiCl was filtered off and a solution of 3, 6-di-tBu-C13H6H- SiMe2-NHtBu (578 mg, 1.42 mmol) in pentane (30 mL) was added at 0 °C. The reaction mixture was warmed to room temperature and stirred for 30 h. The

solution was filtered and concentrated in vacuo. The crude product was [C13H6- SiMe2-NtBu] Y (CH2SiMe3) (THF) 2 (1) (0.63 g, 68 %). The 1H NMR spectrum of complex (1) is represented in Figure 2 and gave the following results : (benzene- d6, 200 MHz, 25 °C) : 8 8. 34 (d, 2H, 4JHH = 2.0 Hz, 4,5-H), 7.97 (d, 2H, 3JHH = 8.3 Hz, 1,8-H), 7.57 (dd, 2H, JHH = 2.0, 8.3 Hz, 2,7-H), 3.0 (m, 8H, a-CH2, THF) 1.61 (s, 9H, NCCH3), 1.50 (s, 18H, CCH3 (Flu)), 1.17 (m, 8H, P-CH2, THF), 0.78 (s, 6H, SiCH3), 0.00 (s, 9H, CH2SiCH3),-0. 89 (d, JYH = 3.3 Hz, 2H, YCH2). The 13C NMR of complex (1) is represented in Figure 3 and gave the following results. (benzene-d6, 75 MHz, 25 °C) : J 140.7, 139.4, 130.3, 123.9, 117.8, 116.7, 115.5 (C-1, -2,-3,-4,-5,-6,-7,-8), 82.2 (C-9), 69.7 (a-THF), 54.3 (NCCH3), 36.4 (NCCH3), 34.7 (Flu-CCH3), 32.3 (Flu-CCH3), 30.2 (d, 1J (Y, C) = 45.2 Hz, YCH2), 25.1 (P-THF), 6.2 (SiCH3), 4.6 (CH2SiCH3). The 1H NMR spectrum of complex (1) (benzene-d6, 200 MHz,-70 °C) is represented in Figure 3. The NMR spectroscopy thus indicates that on the NMR time scale, complex (1) is symmetric in benzene at 25 °C, but appears dissymmetric at a temperature lower than-30 °C.

An X-ray diffraction study of monocrystals of complex (1) revealed that the fluorenyl moiety is bonded via an unusual exocyclic 713-fashion, which involves the bridgehead carbon atom of the central ring (C (9A) ) and the two adjacent carbon atoms of one six-membered ring (C (9), C (1)), wherein the carbon atoms are numbered as displayed in Figure 1, which represents the structure of molecule (1).

There are two THF molecules coordinated per metal atom in molecule (1) as compared with 14-electron mono-solvated [-C5Me4-SiMe2- NtBu] Y (CH2SiMe3) (THF) complex described by Hultzsch et aL (K. C. Hultzsch, P.

Voth, K. Beckerle, T. P. Spaniol, J. Okuda; in Organometallics, 2000,19, 228. ).

Also, molecule (1) can be considered formally as a 14-electron complex and coordination number of the yttrium atom is 6. Both coordinated THF ligands are not

equivalent according to X-ray data; the difference between the two Y-O distances is 0.05 A, suggesting that one THF molecule could be involved in dissociative processes.

Salt Metathesis Reaction between [3, 6-di-tBu-C13H6-SiMe2-NtBulLi2 and YCl3(THF)n. Preparation of [ (tBu2-C13H6)-SiMe2-NtBu}2Y]-[Li (THF) 4] + (2). To a solution of tBu2-C13H6H-SiMe2-NHtBu (108 mg, 0.265 mmol) in diethylether (20 mL) at-10 °C was added under vigorous stirring two equiv. of"BuLi (0.33 mL of a 1.6 M solution in hexane, 0.530 mmol). The reaction mixture was allowed to warm to ambient temperature and stirred for 8 h. To the resulting orange solution of the dilithium salt in ether cooled to-20 °C was added a suspension of YC13 THF-adduct (prepared from 52.0 mg, 0. 265 mmol of YCI3) in ether (30 mL). The mixture was vigorously stirred and warmed to room temperature; the color turned yellow after 30-40 min. The yellow solution was decanted from precipitate, volatiles were removed in vacuo and the resulting residue was washed with pentane (2 x 20 mL) to give a yellow powder (101.2 mg). The'H NMR spectrum of crude complex (2) shows the existence of two species in solution and gave the following results. (THF- d8, 200 MHz, 25 °C) : 1st product: 57. 90 (d, 2H, 4JHH= 2.1 Hz, 4,5-H), 7.69 (d, 2H, 3JHH = 8. 6 Hz, 1, 8-H), 6.90 (dd, 2H, JHH = 2. 1, 8. 6 Hz, 2,7-H), 1. 36 (s, 18H, CCH3 (Flu)), 1.20 (s, 9H, NCCH3), 0.38 (s, 6H, SiCH3) ; 2""product : 67. 83 (m, 2H, 4JHH = 2.1 Hz, 4,5-H), 7.54 (d, 2H, 3JHH= 8.6 Hz, 1, 8-H), 6.84 (dd, 2H, JHH = 2.1, 8.6 Hz, 2,7-H), 1.35 (s, 18H, CCH3 (Flu)), 1.11 (s, 9H, NCCH3), 0.40 (s, 6H, SiCH3).

The crude product was recrystallized from Et2O : THF: pentane (-0. 5: 1: 3) to give yellow crystals (88.2 mg, 55 %). The 1H NMR of recrystallized complex (2) is represented in Figure 5 and gave the following results that show the presence of a sole species. (THF-d8, 300 MHz, 25 °C) : #7. 94 (d, 2H, 4JHH = 1.8 Hz, 4,5-H), 7.72 (d, 2H, 3JHH = 8.3 Hz, 1,8-H), 7.13 (dd, 2H, JHH = 1. 8, 8.3 Hz, 2,7-H), 1.43 (s, 9H, NCCH3), 1.36 (s, 18H, CCH3 (Flu)), 0.27 (s, 6H, SiCH3). The 13C NMR spectrum of

complex (2) is represented in Figure 6 and gave the following results. (THF-d8, 75 MHz, 25 °C) : 8 144. 6,137. 8,133. 7,121. 1 (C-1,-8), 120.0 (C-2, -7), 115.5 (C-4, -5), 79.0 (C-9), 54.7 (NCCH3), 36.9 (NCCH3), 35.4 (Flu-CCH3), 33.2 (Flu-CCH3), 6.2 (SiCH3).

Salt Metathesis Reaction between [3, 6-di-tBu-C3H6-SiMe2-NtBu] Li2 and LaCl3 (THF)". Preparation of [{(tBu2-C13H6)-SiMe2-NtBu}2La]-[Li (THF) 4] + (3). The same procedure than that described above was carried out from the LaOs THF- adduct (prepared from 186 mg, 0.758 mmol of LaCis) and tBu2-C13H6H-SiMe2- NHtBu (310 mg, 0.760 mmol) to yield a yellow microcrystalline solid (440 mg). NMR of the crude complex showed the presence of two species in solution and gave the following results. 1H NMR (THF-d8, 200 MHz, 25 °C) : lst product: # 7. 93 (d, 2H, 4JHH = 2.0 Hz, 4,5-H), 7.73 (dd, 2H, JHH = 0.5, 8.6 Hz, 1,8-H), 6.94 (dd, 2H, JHH = 2.1, 8. 6 Hz, 2,7-H), 1.41 (s, 18H, CCH3 (Flu)), 1.25 (s, 9H, NCCH3), 0.43 (s, 6H, SiCH3) ; 2nd product: # 7. 83 (m, 2H, 4JHH = 2.1 Hz, 4,5-H), 7.54 (d, 2H, JHH = 8.6 Hz, 1,8-H), 6.84 (dd, 2H, JHH = 2. 1,8. 6 Hz, 2, 7-H), 1.35 (s, 18H, CCH3 (Flu)), 1.16 (s, 9H, NCCH3), 0.45 (s, 6H, SiCH3). Recrystallization of the crude product from THF-pentane (-1 : 4) mixture gave pale-orange crystals (0.38 g, 77 %). NMR of the recrystallized complex showed the presence of a sole species in solution and gave the following results NMR (Fig. 5.) (THF-d8, 300 MHz, 25 °C) : # 7. 82 (d, 2H, 4JHH = 1. 8 Hz, 4,5-H), 7.53 (d, 2H, 3JHH = 8.2 Hz, 1,8-H), 6.84 (dd, 2H, JHH = 1.8, 8.2 Hz, 2,7-H), 1.35 (s, 18H, CCH3 (Flu)), 1.19 (s, 18H, NCCH3), 0.39 (s, 6H, SiCH3). 13C NMR (THF-d8, 75 MHz, 25 °C) : # 144. 4,131. 4,127. 7,119. 5 (C-1,-8), 118.5 (C-2, -7), 114.9 (C-4, -5), 84.4 (C-9), 50.7 (NCCH3), 35.5 (Flu-CCH3), 35.4 (NCCH3), 34.1 (Flu-CCH3), 6.9 (SiCH3). Anal. Calcd for C70H110N2O4LiSi2La : C, 67.49 ; H, 8.90 ; N, 2.25. Found : C, 67.31 ; H, 8.37 ; N, 2.40.

Synthesis of [ {tBu-C13H6-SiMe2-NtBu}2La]-[Li(Et2O)2]+ (4). To a solution of tBu2- C1sH6H-SiMe2-NHtBu (340 mg, 0.834 mmol) in diethylether (30 mL) at-10 °C was added under vigorous stirring two equiv. of"BuLi (1.0 mL of a 1.6 M solution in hexane, 1.66 mmol). The reaction mixture was allowed to warm to ambient temperature and stirred for 8 h. To the resulting orange solution of the dilithium salt in ether cooled to-35 °C in glovebox was added a powder of LaCis (THF) 15 (295 mg, 0.834 mmol). The mixture was vigorously stirred and warmed to room temperature; the color turned orange-yellow after 20 min. The yellow solution was decanted from precipitate and concentrated in vacuo. Hexane (ca. 2-3 mL) was added to the ether solution and orange-yellow crystals started to grow to get in the next 10 h microcrystals of molecule (4) (0. 30 g, 33 %). H NMR (THF-d8, 200 MHz, 60 °C) : 57. 79 (d, 4H, 4JHH = 2.0 Hz, 4,5-H), 7.25 (d, 4H, JHH = 8.4 Hz, 1,8-H), 7.00 (dd, 4H, JHH = 2.0, 8. 4 Hz, 2,7-H), 3.36 (q, 8H, CH20CH3), 1.51 (s, 18H, NCCH3), 1.36 (s, 36H, CCH3 (Flu)), 1. 08 (t, 12H, CH20CH3), 0.17 (s, 12H, SiCH3).

Synthesis of [{tBu2-13H6-SiMe2-NtBu}Nd(µ-Cl)(THF)]2 (5). The same procedure as that described above was carried out from the NdCLl3 THF-adduct (prepared from 156 mg, 0.623 mmol of NdCI3) and tBu2-C13H6H-SiMe2-NHtBu (255 mg, 0.623 mmol) to yield molecule (5) as a yellow microcrystalline solid (0.45 g, 77%).

Crystallization of the reaction mixture from an Et20-hexane mixture gave green crystals of molecule (5) suitable for X-ray diffraction (0.15 g, 26%).

Reaction of [3, 6-di-tBu-Ci3H6-SiMe2-NtBu] Y (CH2SiMe3) (THF) 2 (1) with PhSiH3 or H2 to produce Y-hydride (6). Method A. To a solution of [C13H8-SiMe2- NtBu] Y (CH2TMS) (THF) 2 (0. 100 g, 0.137 mmol) in benzene (5 mL) was added phenylsilane (85) J. L, 0.688 mmol) at 25 °C. The mixture was stirred for 1 h at this temperature. The yellow precipitate formed was filtrated, washed with benzene (2 mL) and dried in vacuo to give 0.070 g of a pale-yellow microcrystalline product

insoluble in THF and hydrocarbons. Method B. A solution of [C13H8-SiMe2- NtBu] Y (CH2TMS) (THF) 2 (0.125 g, 0.172 mmol) in benzene (5 mL) was exposed in hydrogene atmosphere (1 atm, 25 °C) for 12 hours to yield after similar workup 30 mg of a pale-yellow insoluble product.

Polymerization.

Polymerisation of methyl methacrylate (MMA) and styrene have been carried out with complexes (1), (2) and (6). Complexes (1) and (2) were prepared as disclosed here-above. Complex (6) is an Y-hydride complex. Complex (2) reacts smoothly with bulk MMA at room temperature and 50 °C to give atactic PMMA of narrow molecular weight distribution (MWD). The molecular weight distribution is defined by the polydispersion index D that is the ratio Mw/Mn of the weight average molecular weight Mw over the number average molecular weight Mn. Alkyl complex (1) initiates sluggishly polymerization of MMA and styrene. The polymerization results are displayed in Table I.

TABLE 1.

MW Temp. Conv. zip Tacticity Complex Condit Monomer D °C % 103 rr mr mm 2 Bulk MMA 25 26 250 2.85 26 40 34 2""50 65 216 3.60 21 40 39 <BR> <BR> <BR> <BR> <BR> <BR> 1 ;"25 Traces <BR> <BR> <BR> <BR> <BR> <BR> <BR> <BR> <BR> 1"50 Traces 1 Toluene 25 2 not sol-29 29 42 1 " " 50 2 not sol-32 29 40 6 Toluene 25 13 19 2.8 33 26 41 1 Bulk Styrene 25 Traces 1 " " 50 3 455 1.81 Reaction conditions: MMA/[metal] = 200-500, t = 12 h.