HALOGEN FREE FLAME RETARDANT POLYAMIDE COMPOSITION

FIELD OF THE INVENTION

The present invention relates to the field of halogen free flame retardant non reinforced polyamide composition and to moulded articles and articles made therefrom.

BACKGROUND OF THE INVENTION

Polyamide resins possess excellent mechanical properties, moldability, and chemical resistance and have therefore been used in automotive parts, electric/electronic components, mechanical components, and many other applications. Articles made from polyamide resins possess extremely desirable physical properties.

However, in certain applications, it is desirable that polyamide resin compositions be flame retardant and meet the UL-94 standard for a high degree of flame retardance.

This requirement has promoted research into a variety of methods for imparting flame retardance to polyamide resins. A common method of imparting flame retardance to thermoplastic resin compositions involves incorporating a halogenated organic compound such as brominated polystyrene as a flame retardant along with an antimony compound that acts as a synergist for the flame retardant. However, the use of

halogenated flame retardants has certain drawbacks in that these materials tend to decompose or degrade at the temperatures used to mold polyamide compositions. The degradation products can implicate potential health and environmental effects due to the gases that are released.

Consequently, there has been a trend away from using halogenated compounds or mixtures containing them to impart flame retardance.

The use of non-halogenated flame retardants such as phosphate or phosphinate compounds with triazine derivatives has been proposed in U.S. patent No. 6,031 ,032 but these flame retardants are unstable at high temperatures and can decompose or degrade during molding, leading to detrimental effects on the electrical properties of a compounded polyamide resin composition containing these flame retardants, especially under conditions of high humidity. Thus, effective non-halogenated flame retardants that have good heat stability and that do not have a detrimental effect upon a resin's properties, in particular electrical properties, are desirable. U.S. patent 5,773,556 discloses compositions comprising polyamide and phosphinate or diphosphinate. U.S. patent 6,255,371 , however, discloses compositions comprising polymers such as polyamide or polyester, with a flame retardant comprising phosphinate or diphosphinate and melamine derivatives such as condensation products of melamine and/or reaction products of melamine with phosphoric acid and/or reaction products of condensation products of melamine with phosphoric acid and/or a mixture of these. U.S. patent 7,294,661 discloses compositions comprising aromatic polyamides and phosphinates as flame retardants but the elongation at break for such compositions is not sufficient for applications in electrical and electronic parts (E/E), in particular for terminal blocks where the material is snap fitted on a metallic rail and where that material would break during assembly if it does not possess a sufficient elongation at break.

U.S. patent publication 2011/0275743 A1 discloses a flame retardant thermoplastic resin comprising a phosphinic acid salt, a compound having an ortho-substituted hydroxyl caboxylamide, and optionally a one or more poshporous compounds including phosphate compounds.

Based on the foregoing discussion, an object of the present invention is to provide a flame resistant polyamide resin composition capable of yielding articles that possess excellent flame retardance and good physical properties.

It is an object of the invention to provide compositions and articles made thereof with good chemical resistance, electrical insulation, high temperature resistance and mouldability.

It is a further object of the invention to provide compositions and articles made thereof with a UL94 flammability rating of V0 at 0.8 mm and even a V0 rating at 0.4 mm.

It is another object of this invention to provide compositions and articles made thereof with a minimum elongation at break of 5%. These and other objects, features and advantages of the present invention will become better understood upon having reference to the following description of the invention.

SUMMARY OF THE INVENTION

Disclosed herein is a flame retardant polyamide composition comprising:

(A) one or more semi-aromatic polyamide, and

(B) a flame retardant mixture comprising:

b1 ) at least one flame retardant comprising a material selected from the group consisting of phosphinates of the formula (I); disphosphinates of the formula (II); polymers of (I); polymers of (II); and mixtures of two or more thereof

wherein R1 and R2 are independently selected from hydrogen, linear or branched C1 -C6 alkyl groups, and aryl groups; R3 is a linear or branched C1-C10-alkylene group, a C6-C10-arylene group, an -alkylarylene group or an - arylalkylene group; M is selected from the group consisting of calcium, magnesium, aluminum, zinc and mixtures thereof; m is 2 to 3; n is 1 or 3; and x is 1 or 2, and b2) a phosphoric ester flame retardant of formula (III)

wherein R4 and R5 each independently represent a hydrogen atom or a methyl group and n represents a number of 1 to 5.

In one preferred embodiment, the flame retardant polyamide composition of the present invention do not contain glass fibers.

In another preferred embodiment, the flame retardant polyamide composition consisting of:

(A) one or more semi-aromatic polyamide, and

(B) a flame retardant mixture comprising:

b1 ) from at or about 10 to 30 weight percent based on the total weight of the flame retardant polyamide composition of at least one flame retardant comprising a material selected from the group consisting of phosphinates of the formula (I); disphosphinates of the formula (II); polymers of (I); polymers of (II); and mixtures of two or more thereof

wherein R1 and R2 are independently selected from hydrogen, linear or branched C1 -C6 alkyl groups, and aryl groups; R3 is a linear or branched C1-C10-alkylene group, a C6-C10-arylene group, an -alkylarylene group or an - arylalkylene group; M is selected from the group consisting of calcium, magnesium, aluminum, zinc and mixtures thereof; m is 2 to 3; n is 1 or 3; and x is 1 or 2, and

b2) from at or about 0.5 to 3 weight percent based on the total weight of the flame retardant polyamide composition of an phosphate ester flame retardant of formula (III)

wherein R4 and R5 each independently represent a hydrogen atom or a methyl group and n represents a number of 1 to 5

and

(C)from at or about 0.05 to 10 weight percent based on the total weight of the flame retardant polyamide composition of additives wherein the sum of component a) to c) amounts to 100 weight percent.

Preferably, the semi-aromatic polyamide is at least one

independently selected from the group consisting of PA6T/66, PA6T/XT, PA6I/6T, PA66/6I/6T, PA6T/6I and their copolymers and combinations thereof.

Also described herein are molded articles comprising the flame retardant polyamide composition described herein, preferably the molded articles are selected from the group consisting of connector housings, breaker housings and contactor housings, in particular electrical connector, and even more preferably the molded articles are terminal blocks.

Also disclosed herein is the use of the flame retardant polyamide composition according to the present invention for making insulated wires and/or cables.

The flame retardant polyamide composition according to the present invention and articles made thereof comply with the a UL94 flammability rating of V0 at 0.8 mm and even at 0.4 mm.

The flame retardant polyamide compositions according to the present invention and articles made thereof have an elongation at break of more than 5% measured according to ISO 527-2/1 A/50.

DETAILED DESCRIPTION OF THE INVENTION

The following definitions are to be used to interpret the meaning of the terms discussed in the description and recited in the claims.

As used herein, the article "a" indicates one as well as more than one and does not necessarily limit its referent noun to the singular.

As used herein, the terms "about" and "at or about" mean that the amount or value in question may be the value designated or some other value that is approximately or about the same. The phrase is intended to convey that similar values promote equivalent results or effects according to the invention.

As used herein, the term "melting point" in reference to a polyamide refers to the melting point of the pure resin as determined with differential scanning calorimetry (DSC) at a scan rate of 10°C/min in the first heating scan, wherein the melting point is taken at the maximum of the

endothermic peak. In customary measurements of melting behavior of blends of polymers, more than one heating scans may be performed on a single specimen, and the second and/or later scans may show a different melting behavior from the first scan. This different melting behavior may be observed as a shift in temperature of the maximum of the endothermic peak and/or as a broadening of the melting peak with possibly more than one peaks, which may be an effect of possible transamidation in the case of more than one polyamides. However, when selecting polyamides in the scope of the current invention, always the peak of the melting endotherm of the first heating scan of the single polyamide is used. As used herein, a scan rate is an increase of temperature per unit time. Sufficient energy must be supplied to maintain a constant scan rate of 10°C/min until a temperature of at least 30°C and preferably at least 50°C above the melting point is reached.

Semi-aromatic Polyamides

Polyamides are condensation products of one or more dicarboxylic acids and one or more diamines, and/or one or more aminocarboxylic acids, and/or ring-opening polymerization products of one or more cyclic lactams. Polyamides may be fully aliphatic or semi-aromatic and are described hereafter.

The term "semi-aromatic" describes polyamides that comprise at least some monomers containing aromatic groups, in comparison with "fully aliphatic" polyamide which describes polyamides comprising aliphatic carboxylic acid monomer(s) and aliphatic diamine monomer(s). The one or more semi-aromatic polyamides (A) may be derived from one or more aliphatic carboxylic acid components and aromatic diamine components such as for example m-xylylenediamine and p-xylylenediamine, it may be derived from one or more aromatic carboxylic acid components, such as terephthalic acid, and one or more aliphatic diamine components, it may be derived from mixtures of aromatic and aliphatic dicarboxylic acid components and mixtures of aromatic and aliphatic diamine components, it may be derived from mixtures of aromatic and aliphatic carboxylic acids and aliphatic diamines or aromatic diamines, it may be derived from aromatic or aliphatic carboxylic acids with mixtures of aliphatic and aromatic diamines.

Preferably, the one or more semi-aromatic polyamides (A) are formed from one or more aromatic carboxylic acid components and one or more aliphatic diamine components. The one or more aromatic carboxylic acids can be, for example, terephthalic acid or mixtures of terephthalic acid and one or more other carboxylic acids, such isophthalic acid, substituted phthalic acid such as for example 2-methylterephthalic acid and unsubstituted or substituted isomers of naphthalenedicarboxylic acid, wherein the carboxylic acid component contains at least 55 mole-% of terephthalic acid (the mole-% being based on the carboxylic acid mixture). Preferably, the one or more aromatic carboxylic acids are selected from terephthalic acid, isophthalic acid and mixtures thereof and more preferably, the one or more carboxylic acids are mixtures of terephthalic acid and isophthalic acid, wherein the mixture contains at least 55 mole-% of terephthalic acid. More preferably, the one or more carboxylic acids is 100% terephthalic acid. Furthermore, the one or more carboxylic acids can be mixed with one or more aliphatic carboxylic acids, like adipic acid; pimelic acid; suberic acid; azelaic acid; sebacic acid and dodecanedioic acid, adipic acid being preferred. More preferably the mixture of terephthalic acid and adipic acid comprised in the one or more carboxylic acids mixtures of the one or more semi-aromatic polyamide (A) contains at least 55 mole-% of terephthalic acid. The one or more semi-aromatic polyamides (A) described herein comprises one or more aliphatic diamines that can be chosen among diamines having four or more carbon atoms, including, but not limited to tetramethylene diamine,

hexamethylene diamine, octamethylene diamine, decamethylene diamine, 2-methylpentamethylene diamine, 2-ethyltetramethylene diamine, 2- methyloctamethylene diamine; trimethylhexamethylene diamine, bis(p- aminocyclohexyl)methane; and/or mixtures thereof. Preferably, the one or more diamines of the one or more semi-aromatic polyamides (A) described herein are selected from hexamethylene diamine, 2-methyl pentamethylene diamine and mixtures thereof, and more preferably the one or more diamines of the one or more semi-aromatic polyamides (A) are selected from hexamethylene diamine and mixtures of hexamethylene diamine and 2-methyl pentamethylene diamine wherein the mixture contains at least 50 mole-% of hexamethylene diamine (the mole-% being based on the diamines mixture).

Examples of semi-aromatic polyamides (A) useful in the flame retardant composition described herein are commercially available under the trademark Zytel ^® HTN from E. I. du Pont de Nemours and Company,

Wilmington, Delaware.

Preferred semi-aromatic polyamides (A) have a melting point of at least 280°C, and comprise a semiaromatic polyamide selected from the group consisting of poly(£-caprolactam/tetramethylene terephthalamide) (PA6/4T), poly(£-caprolactam/hexamethylene terephthalamide) (PA6/6T), poly(£-caprolactam/decamethylene terephthalamide) (PA6/10T), poly(£- caprolactam/dodecamethylene terephthalamide) (PA6/12T),

poly(hexamethylene decanediamide/hexamethylene terephthalamide) (PA610/6T), poly(hexamethylene dodecanediamide/hexamethylene terephthalamide) (PA612/6T), poly(hexamethylene

tetradecanediamide/hexamethylene terephthalamide) (PA614/6T), poly(£- caprolactam/ hexamethylene isophthalamide/hexamethylene

terephthalamide) (PA6/6I/6T), poly(2-methylpentamethylene

hexanediamide/hexamethylene hexanediamide/hexamethylene

terephthamide) (PA D6/66/6T), poly(hexamethylene terephthamide/2- methylpentamethylene terephthamide) (PA 6Ί7ΧΤ), poly(hexamethylene hexanediamide/hexamethylene terephthamide (PA66/6T),

poly(hexamethylene terephthamide/ hexamethylene isophthamide

(PA6T/6I), poly(hexamethylene hexanediamide/hexamethylene

terephthamide/ hexamethylene isophthamide (PA66/6T/6I),

poly(decamethylene decanediamide/decamethylene terephthalamide) (PA1010/10T) poly(decamethylene decanediamide/dodecamethylene decanediamide/ decamethylene terephthalamide/dodecamethylene terephthalamide (PA1010/1210/10T/12T), poly(11- aminoundecanamide/tetramethylene terephthalamide) (PA11/4T), poly(11- aminoundecanamide/hexamethylene terephthalamide) (PA11/ 6T), poly(11 -aminoundecanamide/decamethylene terephthalamide)

(PA11/10T), poly(11-aminoundecanamide/dodecamethylene

terephthalamide) (PA11/12T), poly(12- aminododecanamide/tetramethylene terephthalamide) (PA12/4T), poly(12- aminododecanamide/hexamethylene terephthalamide) (PA12/6T), poly(12-aminododecanamide/decamethylene terephthalamide)

(PA12/10T), and poly(dodecamethylene

dodecanediamide/dodecamethylene dodecanediamide/dodecamethylene terephthalamide)) (PA1212/12T), and their copolymers and combinations. Particularly preferred semi-aromatic polyamides are selected from the group consisting of PA66/6T, PA6T/XT, PA6T/6I, and their

combinations and copolymers.

The flame retardant polymer composition of the present invention may also be a blend of one or more semi-aromatic polyamides described above with one or more homopolymers, copolymers, terpolymers, or higher polymers that are derived fully aliphatic polyamides.

Examples of aliphatic polyamide homopolymers, copolymers, or terpolymers that may be blended with the semi-aromatic polyamides of the present invention include polyamide 6, polyamide 66, polyamide 610, polyamide 612, polyamide 46, polyamide 66/6 copolymers, polyamide 66/68 copolymers, polyamide 66/610 copolymers, polyamide 66/612 copolymers, polyamide 66/10 copolymers, polyamide 66/12 copolymers, polyamide 6/68 copolymers, polyamide 6/610 copolymers, polyamide 6/612 copolymers, polyamide 6/10 copolymers, polyamide 6/12

copolymers, polyamide 6/66/610 terpolymers, polyamide 6/66/69 terpolymers, polyamide 6/66/11 terpolymers, polyamide 6/66/12

terpolymers, polyamide 6/610/11 terpolymers, polyamide 6/610/12 terpolymers, and polyamide 6/66/PACM where PACM refers to bis-p- (aminocyclohexyl)methane)] terpolymers.

Flame retardants

Flame retardance in the flame retardant polyamide compositions described herein is imparted by flame retardant mixtures also referred herein as flame retardant compositions.

These flame retardant mixtures (B) comprise a flame retardant b1 ) which is a phosphinate of the formula (I) (i.e. a monophosphinate) and/or a diphosphinate of the formula (II) and/or polymers of (I) and/or (II),

wherein R ₁ and R ₂ are identical or different and are hydrogen, linear or branched C ₁ -C ₆ alkyl groups, and/or aryl groups; R ₃ is a linear or branched C ₁ -C ₁₀ -alkylene group, a C ₆ -C ₁₀ -arylene group, an alkylarylene group or arylalkylene group; M is calcium, magnesium, aluminum, and/or zinc; m is 2 to 3; n is 1 or 3; and x is 1 or 2.

R ₁ and R ₂ may be identical or different and are preferably hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, n-pentyl and/or phenyl. R3 is preferably methylene, ethylene, n-propylene, isopropylene, n-butylene, tert-butylene, n-pentylene, n-octylene, n- dodecylene, or phenylene or naphthylene, or methylphenylene, ethylphenylene, tert-butylphenylene, methylnaphthylene, ethylnaphthylene or tert-butylnaphthylene, or phenylmethylene, phenylethylene,

phenylpropylene or phenylbutylene. M is preferably aluminum or zinc.

By polymers of the compounds of formulas (I) and (II) is meant species containing oligomers or condensation products of the phosphinate and diphosphinate anion moieties.

Preferred phosphinates are metal salts of organic phosphinates, such as metal salts of methylethylphosphinates and diethylphosphinates. More preferred are aluminum methylethylphosphinate, aluminum diethylphosphinate, zinc methylethylphosphinate, and zinc

diethylphosphinate. More preferably, the flame retardant is aluminum phosphinate, magnesium phosphinate, calcium phosphinates and/or zinc phosphinate and still more preferably, the flame retardant is aluminum phosphinate, aluminum diethyl phosphinate and/or zinc diethyl

phosphinate.

The flame retardant b1 ) is usually in the form of particles which may have any particle size distribution, as commonly understood and used by those having skill in the field, but preferably the phosphinate and/or diphosphinates that comprise component b1 ) have particle sizes (D50 value) of less than or equal to 100 microns and more preferably less than or equal to 50 microns. The D50 value corresponds to a particle size below which 50 weight percent of the particles lie, wherein the particle size distribution is measured by the technique of laser diffraction from a suspension of particles in a solvent using a particle size analyzer,

Mastersizer 2000 from Malvern. This test method meets the requirements set forth in ISO 13320.

Preferably, the flame retardant mixtures (B) comprise a flame retardant b1 ) in an amount from at or about 10 to at or about 30 weight percent, more preferably from at or about 15 to at or about 25 weight percent, and even more preferably from at or about 18 to at or about 20 weight percent, the weight percentage being based on the total weight of the flame retardant polyamide composition.

The flame retardant mixtures (B) described herein comprise a phosphate ester flame retardant b2) of formula (III).

wherein R4 and R5 each independently represent a hydrogen atom or a methyl group and n represents a number of 1 to 5.

Preferably, R4 and R5 represent a hydrogen atom. The phosphate ester flame retardant b2) may be a mixture of the monomers or oligomers of compound of formula (III) i.e. a mixture of compounds wherein n is equal to 1 and n is equal to 2, 3, 4 or 5.

Phosphate ester flame retardants of the present invention may be obtained.for instance, according to the processes described in U.S. patent application US 2011/0084242.

Preferred phosphate ester flame retardant b2) are the ones with CAS number 1003300-73-9 available from Adeka Palmarole.

Preferably, the flame retardant mixtures (B) comprise a phosphate ester flame retardant b2) in an amount from at or about 0.5 to at or about 3 weight percent, more preferably from at or about 0.75 to at or about 1.5 weight percent, the weight percentage being based on the total weight of the flame retardant polyamide composition.

Additives

The flame retardant compositions of the present invention may further contain other additives that can be selected from the group consisting of stabilizers, processing agents, metal deactivators,

antioxidants, UV stabilizers, heat stabilizers, flame retardant synergists, dyes and/or pigments and other additives in addition to the components mentioned previously.

Examples of antioxidants include phenolic antioxidants, thioether antioxidants, and phosphite antioxidants.

Flame retardant synergists may also be optionally included in the composition in conventional amounts and as understood by those having skill in the field. Examples include silicone, metal oxides such as silica, boehmite, aluminum oxide, iron oxide, titanium oxide, manganese oxide, magnesium oxide, zirconium oxide, zinc oxide, molybdenum oxide, cobalt oxide, bismuth oxide, chromium oxide, tin oxide, antimony oxide, nickel oxide, copper oxide and tungsten oxide, metal powder such as aluminum, iron, titanium, manganese, zinc, molybdenum, cobalt, bismuth, chromium, tin, antimony, nickel, copper and tungsten, and metal salts such as zinc borate, zinc metaborate, barium metaborate, zinc carbonate, zinc stannate, magnesium carbonate, calcium carbonate, and barium carbonate. Preferred synergists are boehmite (aluminum hydroxide oxide (AIO(OH))), aluminum oxide, zinc borate, zinc stannate and mixtures thereof.

Synergists will preferably be present in up to about 10 weight percent or more preferably in about 0.5 to about 8 weight percent, or yet more preferably in about 1 to about 6 weight percent, based on the total weight of the flame retardant polyamide composition.

The flame retardant polyamide compositions of the present invention are melt-blended and can be manufactured by any known manufacturing methods. The component materials may be mixed to homogeneity using a melt-mixer such as a single or twin-screw extruder, blender, kneader, Banbury mixer, etc. to give a resin composition. Or, part of the materials may be mixed in a melt-mixer, and the rest of the materials may then be added and further melt-mixed until homogeneous.

The articles of the present invention may be formed from the flame retardant polyamide compositions of the invention by any known means such as injection molding, blow molding, extrusion, or thermoforming. Examples of articles that may be formed from the flame retardant polyamide compositions of the present invention are housings, electrical connectors and connector housings and cases, breaker housings, terminal blocks and contactor housings.

EXAMPLES

The invention is further illustrated by certain embodiments in the examples below which provide greater detail for the compositions, uses and processes described herein.

The following materials were used to prepare the flame retardant polyamide compositions described herein and the compositions of the comparative examples. Polyamide 6T XT Polyamide 6T/XT, refers to a

copolyamide of terephtalic acid, hexamethylenediamine, and 2-methyl- pentamethylenediamine having a typical inherent viscosity (IV) of about 0.88, according to ASTM D2857 method, and a melting point of about 300 ^° C, available from E.I. DuPont de Nemours and Company, Wilmington, Delaware.

Polyamide 6T/66 Polyamide 6T/66 refers to a

copolyamide made from terephtalic acid, adipic acid and hexamethylenediamine wherein the two acids are used in a 55:45 molar ratio; having a melting point of about 310°C and an inherent viscosity (IV), according to ASTM D2857, typically about 1.07, available from E.I. DuPont de Nemours and Company, Wilmington, Delaware.

Flame retardant 1 Aluminium diethylphosphinate having a

D50 from 20 to 40 μm, Exolit® OP1230 available from Clariant

Flame retardant 2 refers to phosphoric acid, mixed esters with 1 ,1'-bisphenyl]-4,4'-diol and phenol, CAS number 1003300-73-9, ADK

STAB® FP800 available from Adeka Palmarole.

Flame retardant 3 Aluminium diethylphosphinate having a

D90 max of 7.506 microns, Exolit® OP935 available from Clariant

Flame retardant synergist Boehmite BMT33, available from Kawai

Sekkai Kogyo

Impact modifier refers to a blend of impact modifiers comprising an ethylene-octene copolymer consisting of 72 weight percent ethylene and 28 weight percent 1-octene commercially available as Engage® 8180, available from Dow Chemical Co., Midland, Ml and being grafted with maleic anhydride to give an average maleic anhydride level of approximately 1%.

As required for the manufacturing process and well-known to those skilled in the art, the polyamide contained up to 2 weight percent of heat stabilizers, UV stabilzers, antioxidants and lubricants.

Compounding

The components were dry blended and then compounded with a screw speed of 300 rpm using a twin-screw extruder. The barrel temperatures were about 320 °C. Upon exiting the extruder, the molten polymer was quenched in a water bath and pelletized.

Production of test samples

Test specimen have been prepared using an injection moulding machine (Billion H470-150T Select Dixit II, diameter 32mm, ratio L D 19) at a melt temperature of 325°C and a mold temperature of 100°C.

Measurement of properties

Except for flammability, all properties have been measured on dry as moulded (DAM) samples. Tensile properties (tensile modulus, stress at break and elongation at break) have been measured using ISO 527-2/1 A/50. Values in the exemples are average values of 10 specimens,

Notched Charpy was measured using ISO 179-1/1 eA and

Unnotched Charpy was measure using ISO 179-1/1 ell. Values in the exemples are average values of 10 specimens.

Comparative tracking index (CTI) was measured using IEC 60112 on 4mm ISO bars. Values in the exemples are average values of 5 specimens.

Flammability testing was done according to UL-94 (20 mm Vertical Burning Test) using 0.4mm or 0.8mm thick test pieces, which are then conditioned for either 48 hours at 23 °C and 50% relative humidity or 168 hours at 70 °C. Values in the examples are average values of 10 specimens.

In Table 1 , comparative examples C1 , C2, C3 show that impact modifiers are efficient to improve elongation at break of unreinforced and flame retardant composition of PA6T/66 but reduce its flammability performances. It shows that it is not possible to achieve 5% elongation at break while maintaining UL-V0 flammability performances even at 0.8mm.

In Table 2, comparative examples C4, C5 and C6 show that increasing the flame retardant level in unreinforced and flame retardant composition of PA6T/66 containing impact modifier does not allow to achieve UL-V0 but reduces the elongation at break.

In Table 3, examples E1, E2 and E3 show that the addition of phosphate ester increases elongation at break of unreinforced and flame retardant composition of PA6T/XT containing impact modifier.

In Table 4, examples E4, E5 and E6 and comparative examples C7 and C8 show that the addition of phosphate ester increases elongation at break of unreinforced and flame retardant composition of PA6T/66. The increase of elongation at break varies with the amount of phosphate ester and is higher for example E4 which contains the highest level of phosphate ester.

Example E4 and comparative examples C7 and C8 show that the addition of phosphate ester in unreinforced and flame retardant composition of PA6T/66 improves the flammability performances of the composition and allows to achieve UL-VO at 0.4mm and 0.8mm without use of any flame retardant synergist (e.g. boehmite).