Title:
HIGH-DUCTILITY HIGH-CARBON STEEL WIRE
Document Type and Number:
WIPO Patent Application WO/2007/139234
Kind Code:
A1
Abstract:
A high-ductility high-carbon steel wire which is less apt to break during drawing
and is used for steel cords, etc. It is a high-carbon steel wire produced by hot
rolling and having a carbon content of 0.7% or higher. It comprises 95% or more
pearlite structure, and the pearlite in a central part of the hot-rolled wire
has a maximum pearlite block grain diameter of 65 µm or smaller. The high-ductility
high-carbon steel wire may have a tensile strength in the range of {248+980×(C
mass%)}±40 MPa and have a reduction of area of {72.8-40×(C mass%)}
% or more. The high-ductility high-carbon steel wire may be characterizedin
that the average grain diameter of those pearlite blocks in the central part of
the hot-rolled wire which are defined by ferrite grain boundaries having a difference
in orientation of 9 degrees of more, as measured with an EBSP apparatus, is 10-30
µm.
More Like This:
Inventors:
NISHIDA SEIKI (JP)
YAMASAKI SHINGO (JP)
DEMACHI HITOSHI (JP)
MUROGA NARIYASU (JP)
OHASHI SHOUICHI (JP)
NAKAMURA KENICHI (JP)
KOSAKA MAKOTO (JP)
KOMIYA NOBUYUKI (JP)
SAHARA SUSUMU (JP)
YAMASAKI SHINGO (JP)
DEMACHI HITOSHI (JP)
MUROGA NARIYASU (JP)
OHASHI SHOUICHI (JP)
NAKAMURA KENICHI (JP)
KOSAKA MAKOTO (JP)
KOMIYA NOBUYUKI (JP)
SAHARA SUSUMU (JP)
Application Number:
PCT/JP2007/061497
Publication Date:
December 06, 2007
Filing Date:
May 31, 2007
Export Citation:
Assignee:
NIPPON STEEL CORP (JP)
NISHIDA SEIKI (JP)
YAMASAKI SHINGO (JP)
DEMACHI HITOSHI (JP)
MUROGA NARIYASU (JP)
OHASHI SHOUICHI (JP)
NAKAMURA KENICHI (JP)
KOSAKA MAKOTO (JP)
KOMIYA NOBUYUKI (JP)
SAHARA SUSUMU (JP)
NISHIDA SEIKI (JP)
YAMASAKI SHINGO (JP)
DEMACHI HITOSHI (JP)
MUROGA NARIYASU (JP)
OHASHI SHOUICHI (JP)
NAKAMURA KENICHI (JP)
KOSAKA MAKOTO (JP)
KOMIYA NOBUYUKI (JP)
SAHARA SUSUMU (JP)
International Classes:
B21B3/00; C22C38/00; C22C38/04; C22C38/54
Foreign References:
JP2001181790A | 2001-07-03 | |||
JP2004137597A | 2004-05-13 | |||
JP2004091912A | 2004-03-25 | |||
JP2003082434A | 2003-03-19 | |||
JPS61261436A | 1986-11-19 | |||
JPH0360900B2 | 1991-09-18 | |||
JP2000006810A | 2000-01-11 | |||
JP3681712B2 | 2005-08-10 |
Other References:
TAKAHASHI ET AL., THE JOURNAL OF THE JAPAN INSTITUTE OF METALS, vol. 42, 1978, pages 702
"Quantitative Microscopy", 1968, MCGRAW HILL PUBLISHERS
See also references of EP 2025769A4
"Quantitative Microscopy", 1968, MCGRAW HILL PUBLISHERS
See also references of EP 2025769A4
Attorney, Agent or Firm:
AOKI, Atsushi et al. (Toranomon 37 Mori Bldg.5-1, Toranomon 3-chom, Minato-ku Tokyo 23, JP)
Download PDF:
Previous Patent: PROCESS FOR PRODUCING EXHAUST GAS PURIFICATION CATALYST
Next Patent: MOLDINGS OF POLYLACTIC ACID COMPOSITIONS
Next Patent: MOLDINGS OF POLYLACTIC ACID COMPOSITIONS