| CLAIMS: 1. A chemically cross-linked aromatic polyimide polymer comprising a formula (I) wherein formula (I) is represented by the following formula: wherein R is selected from the group consisting of -H, -COCH3, and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of and mixtures thereof, and -R'- is selected from the group consistin and mixtures thereof; Yl is selected from the group consisting of and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH3, and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1 : 100 to 100: 1; and n'/m' is in a range of 1 : 100 to 100: 1. 2. A chemically cross-linked aromatic polyimide membrane comprising the chemically cross-linked aromatic polyimide polymer of claim 1. 3. An aromatic polyimide blend comprising a first aromatic polyimide comprising carboxylic acid groups comprising a plurality of repeating units of formula (II) wherein XI and X2 are selected from the group consisting of and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range of 1 : 100 to 100: 1, and preferably n/m is in a range of 1 : 10 to 5 : 1 and a second aromatic polyimide comprising hydroxyl groups comprises a plurality of repeating units of formula (III) wherein X3 and X4 are selected from the group consisting of and mixtures thereof, and -R'- is selected from the group consisting of CF3 CH3 o — ?— — ?— — i— — °— — s— CF3 CH3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH3, and mixtures thereof;; wherein Y3 is selected from the group consisting of and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1 : 100 to 100: 1, and preferably n'/m' is in a range of 1 : 10 to 5: 1. 4. The aromatic polyimide blend of claim 3 wherein said first polyimide polymer and said second polyimide polymer have a weight average molecular weight between 10,000 and 1,000,000 g/mol. 5. An aromatic polyimide blend membrane comprising the aromatic polyimide blend of claim 3. 6. A process for preparing a chemically cross-linked polyimide polymer membrane comprising making an aromatic polyimide blend membrane comprising a first aromatic polyimide polymer and a second aromatic polyimide polymer and then chemical cross- linking the said aromatic polyimide blend membrane by heating the said aromatic polyimide blend membrane at 100 to 300°C under an inert atmosphere, wherein the first aromatic polyimide comprises carboxylic acid groups comprising a plurality of repeating units of formula (II) wherein XI and X2 are selected from the group consisting of and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range of 1 : 100 to 100: 1, and preferably n/m is in a range of 1 : 10 to 5 : 1 and the second aromatic polyimide comprising hydroxyl groups comprising a plurality of repeating units of formula (III) wherein X3 and X4 are selected from the group consisting of and mixtures thereof, and -R'- is selected from the group consisting of CF3 CH3 o — ?— — ?— — i— — °— — s— CF3 CH3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH3, and mixtures thereof; wherein Y3 is selected from the group consisting of and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1 : 100 to 100: 1, and preferably n'/m' is in a range of 1 : 10 to 5: 1. 7. The process of claim 6 wherein said chemically cross-linked polyimide polymer membrane comprising a chemically cross-linked aromatic polyimide polymer comprises a formula (I) wherein R is selected from the group consisting of -H, -COCH3, and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of and mixtures thereof, and -R'- is selected from the group consistin and mixtures thereof; Yl is selected from the group consisting of and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH3, and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1:100 to 100:1; and n'/m' is alsoinarange of 1:100 to 100:1. 8. A process for separating at least one gas from a mixture of gases comprising a. providing a chemically cross-linked aromatic polyimide membrane comprising a formula (I) wherein R is selected from the group consisting of -H, -COCH3, and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of and mixtures thereof, and -R'- is selected from the group consistin and mixtures thereof; Yl is selected from the group consisting of and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH3, and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1 : 100 to 100: 1; and n'/m' is also in a range of 1 : 100 to 100: 1; b. contacting the mixture of gases to one side of the chemically cross-linked aromatic polyimide membrane to cause at least one gas to permeate said membrane; and c. removing from an opposite side of said chemically cross-linked aromatic polyimide membrane a permeate gas composition comprising a portion of said at least one gas that permeated said membrane. 9. The process of claim 8 wherein said at least two gases are a mixture of volatile organic compounds and atmospheric gas; a mixture of helium, nitrogen, carbon dioxide or hydrogen sulfide, or mixtures thereof in a natural gas stream; a pair of gases selected from the group consisting of nitrogen and oxygen, carbon dioxide and methane, hydrogen and methane, nitrogen and methane, or a mixture of carbon monoxide, helium and methane. 10. The process of claim 8 wherein said mixture of gases are selected from the group consisting of a mixture of iso and normal paraffins, a mixture of xylenes, a hydrocarbon vapor and hydrogen, a mixture of propylene and propane, and methane, carbon dioxide, oxygen, nitrogen, water vapor, hydrogen sulfide, and helium. |
AROMATIC POLYIMIDE MEMBRANE FOR SEPARATIONS
PRIORITY CLAIM OF EARLIER NATIONAL APPLICATION
[0001] This application claims priority to U.S. Application No. 13/929,864 filed
June 28, 2013.
BACKGROUND OF THE INVENTION
[0002] This invention relates to high hydrocarbon resistant chemically cross-linked aromatic polyimide membranes and methods for making and using these membranes.
[0003] In the past 30-35 years, the state of the art of polymer membrane-based gas separation processes has evolved rapidly. Membrane-based technologies have advantages of both low capital cost and high-energy efficiency compared to conventional separation methods. Membrane gas separation is of special interest to petroleum producers and refiners, chemical companies, and industrial gas suppliers. Several applications of membrane gas separation have achieved commercial success, including N2 enrichment from air, carbon dioxide removal from natural gas and from enhanced oil recovery, and also in hydrogen removal from nitrogen, methane, and argon in ammonia purge gas streams. For example, UOP's Separex™ cellulose acetate spiral wound polymeric membrane is currently an international market leader for carbon dioxide removal from natural gas.
[0004] Polymers provide a range of properties including low cost, permeability, mechanical stability, and ease of processability that are important for gas separation. Glassy polymers (i.e., polymers at temperatures below their Tg) have stiffer polymer backbones and therefore let smaller molecules such as hydrogen and helium pass through more quickly, while larger molecules such as hydrocarbons pass through more slowly as compared to polymers with less stiff backbones. Cellulose acetate (CA) glassy polymer membranes are used extensively in gas separation. Currently, such CA membranes are used for natural gas upgrading, including the removal of carbon dioxide. Although CA membranes have many advantages, they are limited in a number of properties including selectivity, permeability, and in chemical, thermal, and mechanical stability.
[0005] The membranes most commonly used in commercial gas and liquid separation applications are asymmetric polymeric membranes and have a thin nonporous selective skin layer that performs the separation. Separation is based on a solution-diffusion mechanism. This mechanism involves molecular-scale interactions of the permeating gas with the membrane polymer. The mechanism assumes that in a membrane having two opposing surfaces, each component is sorbed by the membrane at one surface, transported by a gas concentration gradient, and desorbed at the opposing surface. According to this solution- diffusion model, the membrane performance in separating a given pair of gases (e.g., CO2/CH4, O2/N2, H2/CH4) is determined by two parameters: the permeability coefficient (abbreviated hereinafter as permeability or P^) and the selectivity ( ^/ ). The is the product of the gas flux and the selective skin layer thickness of the membrane, divided by the pressure difference across the membrane. The ^/ is the ratio of the permeability coefficients of the two gases (a A/B = PA/PB) where P^ is the permeability of the more permeable gas and Ρβ is the permeability of the less permeable gas. Gases can have high permeability coefficients because of a high solubility coefficient, a high diffusion coefficient, or because both coefficients are high. In general, the diffusion coefficient decreases while the solubility coefficient increases with an increase in the molecular size of the gas. In high performance polymer membranes, both high permeability and selectivity are desirable because higher permeability decreases the size of the membrane area required to treat a given volume of gas, thereby decreasing capital cost of membrane units, and because higher selectivity results in a higher purity product gas.
[0006] One of the components to be separated by a membrane must have a sufficiently high permeance at the preferred conditions or extraordinarily large membrane surface areas is required to allow separation of large amounts of material. Permeance, measured in Gas Permeation Units (GPU, 1 GPU=10"6 cm^ (STP)/cm^ s (cm Hg)), is the pressure normalized flux and equals to permeability divided by the skin layer thickness of the membrane.
Commercially available gas separation polymer membranes, such as CA, polyimide, and polysulfone membranes formed by phase inversion and solvent exchange methods have an asymmetric integrally skinned membrane structure. Such membranes are characterized by a thin, dense, selectively semipermeable surface "skin" and a less dense void-containing (or porous), non-selective support region, with pore sizes ranging from large in the support region to very small proximate to the "skin". However, fabrication of defect-free high selectivity asymmetric integrally skinned polyimide membranes is difficult. The presence of nanopores or defects in the skin layer reduces the membrane selectivity. The high shrinkage of the polyimide membrane on cloth substrate during membrane casting and drying process results in unsuccessful fabrication of asymmetric integrally skinned polyimide membranes using phase inversion technique.
[0007] In order to combine high selectivity and high permeability together with high thermal stability, new high-performance polymers such as polyimides (Pis),
poly(trimethylsilylpropyne) (PTMSP), and polytriazole were developed. These new polymeric membrane materials have shown promising properties for separation of gas pairs like C0 2 /CH 4 , 0 2 /N 2 , H 2 /CH 4 , and C 3 H 6 /C 3 H 8 . However, current polymeric membrane materials have reached a limit in their productivity-selectivity trade-off relationship. In addition, gas separation processes based on glassy polymer membranes frequently suffer from plasticization of the stiff polymer matrix by the sorbed penetrating molecules such as C0 2 or C 3 H 6 . Plasticization of the polymer is exhibited by swelling of the membrane structure and by a significant increase in the permeances of all components in the feed and decrease of selectivity occurring above the plasticization pressure when the feed gas mixture contains condensable gases. Plasticization is particularly an issue for gas fields containing high C0 2 concentrations and heavy hydrocarbons and for systems requiring two-stage membrane separation.
[0008] US 2005/0268783 Al, US 2009/0182097 Al, and US 2009/0178561 Al disclosed chemically cross-linked polyimide hollow fiber membranes prepared from two separate steps. Step one is the synthesis of a monoesterified polyimide polymer in a solution by treating a polyimide polymer containing carboxylic acid functional group with a small diol molecule at esterification conditions in the presence of dehydrating conditions. However, significant extra amount of diol was used to prevent the formation of biesterified polyimide polymer. Step two is the solid state transesterification of the monoesterified polyimide membrane at elevated temperature to form a cross-linked polyimide membrane.
[0009] Chemical cross-linking of polyimides using diamine small molecules was also disclosed. (J. MEMB . SCI., 2001, 189, 231-239) However, C0 2 permeability decreased significantly after this type of cross-linking. In addition, the thermal stability and hydrolytic stability of the diamine cross-linked polyimide were not improved.
[0010] Koros et al. disclosed decarboxylation-induced thermally cross-linked polyimide membrane. (J. MEMBR. SCI., 2011, 382, 212-221) However, decarboxylation reaction among the carboxylic acid groups on the carboxylic acid group-containing polyimide membrane occurred at temperatures higher than the glass transition temperature of the polyimide polymer. Such a high temperature resulted in densification of the substructure of the membrane and decreased membrane permeance.
[0011] US 7,485,173 disclosed UV cross-linked mixed matrix membranes via UV radiation. The cross-linked mixed matrix membranes comprise microporous materials dispersed in the continuous UV cross-linked polymer matrix.
[0012] US 4,931,182 and US 7,485,173 disclosed physically cross-linked polyimide membranes via UV radiation. The cross-linked membranes showed improved selectivities for gas separations. However, it is hard to control the cross-linking degree of the thin selective layer of the asymmetric gas separation membranes using UV radiation technique, which will result in very low permeances although the selectivities are normally very high.
[0013] The present invention discloses a new type of high hydrocarbon resistant chemically cross-linked aromatic polyimide membranes and methods for making and using these membranes.
SUMMARY OF THE INVENTION [0014] The present invention is for a chemically cross-linked aromatic polyimide polymer and a membrane made from this polymer. The polymer comprises a formula (I)
wherein R is selected from the group consisting of -H, -COCH 3 ,
and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consistin
and mixtures thereof; Yl is selected from the group consisting of
-6-
and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1:100 to 100:1; and n'/m' is also in a range of 1:100 to 100:1. Preferably, n/m is in a range of 1:10 to 5:1; and n'/m' is also in a range of 1:10 to 5:1.
[0015] These polymers are made from a blend of a first aromatic polyimide comprising carboxylic acid groups comprising a plurality of repeating units of formula (II)
wherein XI and X2 are selected from the group consisting of
and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of
and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range of 1 : 100 to 100: 1, and preferably n/m is in a range of 1 : 10 to 5: 1, and a second aromatic polyimide comprising hydroxyl groups comprises a plurality of repeating units of formula (III)
wherein X3 and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consisting of
CF 3 CH 3 o
— ?— — ?— — i— — °— — s —
CF 3 CH 3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof;; wherein Y3 is selected from the group consisting of
and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1 : 100 to 100: 1, and preferably n'/m' is in a range of 1 : 10 to 5: 1.
[0016] The invention further comprises a process for preparing this polymer comprising blending the first aromatic polyimide polymer and the second aromatic polyimide polymer and then chemical cross-linking the blend polyimide polymer membrane by heating the membrane at 100 to 300°C under an inert atmosphere.
[0017] The polymer of the invention may be fabricated into any known membrane configuration or form. The process of preparing the membrane may further involve coating a high permeability material onto the membrane such as a polysiloxane, a fluoro-polymer, a thermally curable silicone rubber, or a UV radiation curable epoxy silicone.
[0018] The first aromatic polyimide may be selected from the group consisting of poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-2,4,6- trimethyl-m-phenylenediamine) polyimide derived from a polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,5-diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-3,3',5,5'-tetramethyl-4,4'-methylene dianiline) polyimide derived from a polycondensation reaction of 3,3',4,4'-diphenylsulfone
tetracarboxylic dianhydride with a mixture of 3,5-diaminobenzoic acid and 3,3 ',5,5'- tetramethyl-4,4 '-methylene dianiline; poly(3, 3 ',4,4 '-benzophenone tetracarboxylic dianhydride-pyromellitic dianhydride-3,5-diaminobenzoic acid-2,4,6-trimethyl-m- phenylenediamine) polyimide derived from a polycondensation reaction of 3,3',4,4'- benzophenone tetracarboxylic dianhydride and pyromellitic dianhydride with 3,5- diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; poly(3, 3 ',4,4 '-benzophenone tetracarboxylic dianhydride-pyromellitic dianhydride-3,5-diaminobenzoic acid-3,3',5,5'- tetramethyl-4,4' -methylene dianiline) polyimide derived from a polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride and pyromellitic dianhydride with 3,5- diaminobenzoic acid and 3,3',5,5'-tetramethyl-4,4'-methylene dianiline; poly(3,3',4,4'- benzophenone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-3,3',5,5'-tetramethyl- 4,4'-methylene dianiline) polyimide derived from a polycondensation reaction of 3,3',4,4'- benzophenone tetracarboxylic dianhydride with 3,5-diaminobenzoic acid and 3,3',5,5'- tetramethyl-4 ,4 '-methylene dianiline; poly (pyromellitic dianhydride-3,5-diaminobenzoic acid-3,3 ',5,5 '-tetramethyl-4,4 '-methylene dianiline) polyimide derived from a
polycondensation reaction of pyromellitic dianhydride with 3,5-diaminobenzoic acid and 3 ,3 ' ,5 ,5 ' -tetramethyl-4,4 ' -methylene dianiline; poly(3 ,3 ' ,4,4 ' -benzophenone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-2,4,6-trimethyl-m-phenylenediamine) polyimide derived from a polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 3,5-diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; and poly(pyromellitic dianhydride -3,5-diaminobenzoic acid -2,4,6-trimethyl-m- phenylenediamine) polyimide derived from a polycondensation reaction of pyromellitic dianhydride with 3,5-diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine.
[0019] The second aromatic polyimide may be selected from the group consisting of poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,3'-dihydroxy-4,4'-diamino- biphenyl-2,4,6-trimethyl-m-phenylenediamine) polyimide derived from the polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,3'- dihydroxy-4,4'-diamino-biphenyl and 2,4,6-trimethyl-m-phenylenediamine; poly[2,2'-bis- (3,4-dicarboxyphenyl) hexafluoropropane dianhydride-3,3'-dihydroxy-4,4'-diamino-biphenyl] polyimide derived from the polycondensation reaction of 2,2'-bis-(3,4-dicarboxyphenyl) hexafluoropropane dianhydride with 3,3'-dihydroxy-4,4'-diamino-biphenyl; poly(3,3',4,4'- diphenylsulfone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino-biphenyl - 3,3',5,5'-tetramethyl-4,4'-methylene dianiline) polyimide derived from the polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,3'- dihydroxy-4,4'-diamino-biphenyl and 3,3 ',5,5 '-tetramethyl-4,4' -methylene dianiline;
poly(3,3',4,4'-benzophenone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino- biphenyl -2,4,6-trimethyl-m-phenylenediamine) polyimide derived from the
polycondensation reaction of 3,3',4,4'-benzophenone tetracarboxylic dianhydride with 3,3'- dihydroxy-4,4'-diamino-biphenyl and 2,4,6-trimethyl-m-phenylenediamine; poly(3 ,3 ' ,4,4 ' - benzophenone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino-biphenyl -3,3',5,5'- tetramethyl-4,4' -methylene dianiline) polyimide derived from the polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 3,3'-dihydroxy-4,4'-diamino- biphenyl and 3,3',5,5'-tetramethyl-4,4'-methylene dianiline; poly(3,3',4,4'-benzophenone tetracarboxylic dianhydride -2,2-bis(3-amino-4-hydroxyphenyl)-hexafluoropropane-3,3',5,5 '- tetramethyl-4,4' -methylene dianiline) polyimide derived from the polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 2,2-bis(3-amino-4- hydroxyphenyl)-hexafluoropropane and 3,3 ',5,5 '-tetramethyl-4,4 '-methylene dianiline.
[0020] The invention also involves a process for separating at least one gas from a mixture of gases comprising providing the chemically cross-linked aromatic polyimide blend membrane of formula (I) contacting the mixture of gases to one side of the chemically cross- linked aromatic polyimide membrane to cause at least one gas to permeate said membrane; and removing from an opposite side of said chemically cross-linked aromatic polyimide membrane a permeate gas composition comprising a portion of said at least one gas that permeated said membrane.
DETAILED DESCRIPTION OF THE INVENTION
[0021] The present invention generally relates to chemically cross-linked aromatic polyimide polymers and high hydrocarbon resistant chemically cross-linked aromatic polyimide membranes for gas, vapor, and liquid separations, as well as methods for making and using these polymers and membranes. [0022] The chemically cross-linked polyimide polymers and the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention compris a plurality of repeating units of formula (I), wherein formula (I) comprises a first aromatic polyimide comprising carboxylic acid groups cross-linked with a second aromatic polyimide comprising hydroxyl groups via covalent ester bonds. The chemically cross-linked polyimide polymers and the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention comprise aromatic polyimide polymer chain segments where at least part of these polymer chain segments are cross-linked to each other through direct covalent ester bonds. The formation of inter- polymer chain cross-linked covalent ester bonds results in good mechanical stability, excellent resistance to hydrocarbon and high concentration of CO2. More importantly, the chemically cross-linked aromatic polyimide membrane described in the present invention showed high selectivity and high permeability for a variety of gas separation applications such as CO2/CH4, H2/CH4, and He/Cffy separations. For example, a cross-linked poly[2,2'- bis-(3,4-dicarboxyphenyl) hexafluoropropane dianhydride-3,3'-dihydroxy-4,4'-diamino- biphenyl] polyimide (abbreviated as poly(6FDA-HAB)) blended with poly(3,3',4,4'- diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-3,3',5,5'-tetramethyl- 4,4'-methylene dianiline) polyimide poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-3,3',5,5'-tetramethyl-4,4'-methylene dianiline) polyimide (abbreviated as poly(DSDA-DBA-TMMDA)) membrane has CO2 permeance of 8.04 Barrers and high CO2/CH4 selectivity of 45.4 for CO2/CH4 separation. This chemically cross-linked membrane has ¾ permeance of 33.5 Barrers and H2/CH4 selectivity of 189 for H2/CH4 separation. This chemically cross-linked membrane also has He permeance of 41.8 Barrers and He/CH4 selectivity of 236 for He/CH4 separation.
[0023] Formula (I) is represented by the following formula:
wherein R is selected from the group consisting of -H, -COCH 3 ,
and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consistin
and mixtures thereof; Yl is selected from the group consisting of
and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1:100 to 100:1; and n'/m' is also in a range of 1:100 to 100:1. Preferably, n/m is in a range of 1:10 to 5:1; and n'/m' is also in a range of 1:10 to 5:1.
[0024] The first aromatic polyimide comprising carboxylic acid groups described in the present invention comprises a plurality of repeating units of formula (II).
wherein XI and X2 are selected from the group consisting of
and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of
and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range ofl:100to 100:1, and preferably n/m is in a range ofl:10to5:l
[0025] The second aromatic polyimide comprising hydroxyl groups comprises a plurality of repeating units of formula (III).
wherein X3 and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consisting of
CF 3 CH 3 o
— ?— — ?— — i— — °— — s —
CF 3 CH 3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof;; wherein Y3 is selected from the group consisting of
and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1 : 100 to 100: 1, and preferably n'/m' is in a range of 1 : 10 to 5: 1.
[0026] The first and second aromatic polyimide polymers used for making the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the current invention have a weight average molecular weight in the range of 10,000 to 1,000,000 g/mol, preferably between 70,000 to 500,000 g/mol.
[0027] The weight ratio of the first aromatic polyimide polymer to the second aromatic polyimide polymer in the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the current invention is in a range of 10: 1 to 1 : 10.
[0028] Some examples of the first aromatic polyimide polymer described in the current invention may include, but are not limited to: poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-2,4,6-trimethyl-m-phenylenediamine) polyimide derived from the polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride (DSDA) with a mixture of 3,5-diaminobenzoic acid (DBA) and 2,4,6-trimethyl- m-phenylenediamine (TMPDA); poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride- 3,5-diaminobenzoic acid -3,3 ',5 ,5 '-tetramethyl-4,4' -methylene dianiline) polyimide derived from the polycondensation reaction of DSDA with a mixture of DBA and 3,3 ',5,5'- tetramethyl-4,4 '-methylene dianiline (TMMDA); poly(3,3',4,4'-benzophenone
tetracarboxylic dianhydride-pyromellitic dianhydride-DBA-TMPDA) polyimide derived from the polycondensation reaction of 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA) and pyromellitic dianhydride (PMDA) with DBA and TMPDA; poly(BTDA- PMDA-DBA-TMMDA) polyimide derived from the polycondensation reaction of BTDA and PMDA with DBA and TMMDA; poly(BTD A-DB A-TMMD A) polyimide derived from the polycondensation reaction of BTDA with DBA and TMMDA; poly(PMDA- DB A-TMMD A) polyimide derived from the polycondensation reaction of PMDA with DBA and TMMDA; poly(BTDA-DBA-TMPDA) polyimide derived from the polycondensation reaction of BTDA with DBA and TMPDA; poly(PMDA- DBA-TMPDA) polyimide derived from the polycondensation reaction of PMDA with DBA and TMPDA.
[0029] Some examples of the second aromatic polyimide polymer described in the current invention may include, but are not limited to: poly(DSDA-3,3'-dihydroxy-4,4'- diamino-biphenyl-TMPDA) polyimide derived from the polycondensation reaction of DSDA with a mixture of 3,3'-dihydroxy-4,4'-diamino-biphenyl (HAB) and TMPDA; poly [2,2 '-bis- (3,4-dicarboxyphenyl) hexafluoropropane dianhydride-3,3'-dihydroxy-4,4'-diamino-biphenyl] polyimide derived from the polycondensation reaction of 2,2'-bis-(3,4-dicarboxyphenyl) hexafluoropropane dianhydride (6FDA) with HAB; poly(DSDA-HAB-TMMDA) polyimide derived from the polycondensation reaction of DSDA with a mixture of HAB and TMMDA; poly(BTDA-HAB-TMPDA) polyimide derived from the polycondensation reaction of BTDA with HAB and TMPDA; poly(BTDA-HAB-TMMDA) polyimide derived from the polycondensation reaction of BTDA with HAB and TMMDA; poly(BTDA-2,2-bis(3-amino- 4-hydroxyphenyl)-hexafluoropropane-TMMDA) polyimide derived from the
polycondensation reaction of BTDA with 2,2-bis(3-amino-4-hydroxyphenyl)- hexafluoropropane (APAF) and TMMDA.
[0030] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention can be fabricated into any convenient geometry such as flat sheet (or spiral wound), tube, or hollow fiber. [0031] The present invention provides a method for the production of high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane by: 1) fabricating a blend aromatic polyimide polymer membrane from a first aromatic polyimide containing carboxylic acid functional groups and a second aromatic polyimide containing hydroxyl functional groups; 2) chemical cross-linking of the blend aromatic polyimide polymer membrane by heating the membrane at 100 to 300°C under an inert atmosphere, such as argon, nitrogen, or vacuum. In some cases, a membrane coating step is added after step 1) and before step 2) by coating the selective layer surface of the blend aromatic polyimide polymer membrane with a thin layer of high permeability material such as a polysiloxane, a fluoro-polymer, a thermally curable silicone rubber, or a UV radiation curable epoxy silicone.
[0032] The invention provides a process for separating at least one gas from a mixture of gases using the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention, the process comprising: (a) providing a high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention which is permeable to said at least one gas; (b) contacting the mixture on one side of the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention to cause said at least one gas to permeate the membrane; and (c) removing from the opposite side of the membrane a permeate gas composition comprising a portion of said at least one gas which permeated said membrane.
[0033] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention is especially useful in the purification, separation or adsorption of a particular species in the liquid or gas phase. In addition to separation of pairs of gases, the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention may, for example, be used for the desalination of water by reverse osmosis or for the separation of proteins or other thermally unstable compounds, e.g. in the pharmaceutical and biotechnology industries. The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention may also be used in fermenters and bioreactors to transport gases into the reaction vessel and transfer cell culture medium out of the vessel. Additionally, the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention may be used for the removal of microorganisms from air or water streams, water purification, ethanol production in a continuous fermentation/membrane pervaporation system, and in detection or removal of trace compounds or metal salts in air or water streams. [0034] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention is especially useful in gas separation processes in air purification, petrochemical, refinery, and natural gas industries. Examples of such separations include separation of volatile organic compounds (such as toluene, xylene, and acetone) from an atmospheric gas, such as nitrogen or oxygen and nitrogen recovery from air. Further examples of such separations are for the separation of He, CO2 or H2S from natural gas, ¾ from N2, CH4, and Ar in ammonia purge gas streams, ¾ recovery in refineries, olefin/paraffin separations such as propylene/propane separation, xylene separations, iso/normal paraffin separations, liquid natural gas separations, C2+ hydrocarbon recovery. Any given pair or group of gases that differ in molecular size, for example nitrogen and oxygen, carbon dioxide and methane, hydrogen and methane or carbon monoxide, helium and methane, can be separated using the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention. More than two gases can be removed from a third gas. For example, some of the gas components which can be selectively removed from a raw natural gas using the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described herein include carbon dioxide, oxygen, nitrogen, water vapor, hydrogen sulfide, helium, and other trace gases. Some of the gas components that can be selectively retained include hydrocarbon gases. When permeable components are acid components selected from the group consisting of carbon dioxide, hydrogen sulfide, and mixtures thereof and are removed from a hydrocarbon mixture such as natural gas, one module, or at least two in parallel service, or a series of modules may be utilized to remove the acid components. For example, when one module is utilized, the pressure of the feed gas may vary from 275 kPa to 2.6 MPa (25 to 4000 psi). The differential pressure across the membrane can be as low as 70 kPa or as high as 14.5 MPa (10 psi or as high as 2100 psi) depending on many factors such as the particular membrane used, the flow rate of the inlet stream and the availability of a compressor to compress the permeate stream if such compression is desired. Differential pressure greater than 14.5 MPa (2100 psi) may rupture the membrane. A differential pressure of at least 0.7 MPa (100 psi) is preferred since lower differential pressures may require more modules, more time and compression of intermediate product streams. The operating temperature of the process may vary depending upon the temperature of the feed stream and upon ambient temperature conditions.
Preferably, the effective operating temperature of the membranes of the present invention will range from -50° to 150°C. More preferably, the effective operating temperature of the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane of the present invention will range from -20° to 100°C, and most preferably, the effective operating temperature of the membranes of the present invention will range from 25° to 100°C.
[0035] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention are also especially useful in gas/vapor separation processes in chemical, petrochemical, pharmaceutical and allied industries for removing organic vapors from gas streams, e.g. in off-gas treatment for recovery of volatile organic compounds to meet clean air regulations, or within process streams in production plants so that valuable compounds (e.g., vinylchloride monomer, propylene) may be recovered. Further examples of gas/vapor separation processes in which the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention may be used are hydrocarbon vapor separation from hydrogen in oil and gas refineries, for hydrocarbon dew pointing of natural gas (i.e. to decrease the hydrocarbon dew point to below the lowest possible export pipeline temperature so that liquid hydrocarbons do not separate in the pipeline), for control of methane number in fuel gas for gas engines and gas turbines, and for gasoline recovery. The high hydrocarbon resistant chemically cross- linked aromatic polyimide membrane described in the present invention may incorporate a species that adsorbs strongly to certain gases (e.g. cobalt porphyrins or phthalocyanines for C"2 or silver (I) for ethane) to facilitate their transport across the membrane.
[0036] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention also has immediate application to concentrate olefin in a paraffin/olefin stream for olefin cracking application. For example, the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention can be used for propylene/propane separation to increase the concentration of the effluent in a catalytic dehydrogenation reaction for the production of propylene from propane and isobutylene from isobutane. Therefore, the number of stages of a
propylene/propane splitter that is required to get polymer grade propylene can be reduced. Another application for the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention is for separating isoparaffin and normal paraffin in light paraffin isomerization and MaxEne™, a process for enhancing the concentration of normal paraffin (n-paraffin) in the naphtha cracker feedstock, which can be then converted to ethylene.
[0037] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention can also be operated at high temperature to provide the sufficient dew point margin for natural gas upgrading (e.g, CO2 removal from natural gas). The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention can be used in either a single stage membrane or as the first or/and second stage membrane in a two stage membrane system for natural gas upgrading.
[0038] The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention may also be used in the separation of liquid mixtures by pervaporation, such as in the removal of organic compounds (e. g., alcohols, phenols, chlorinated hydrocarbons, pyridines, ketones) from water such as aqueous effluents or process fluids. A membrane which is ethanol-selective would be used to increase the ethanol concentration in relatively dilute ethanol solutions (5-10% ethanol) obtained by fermentation processes. Another liquid phase separation example using the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention is the deep desulfurization of gasoline and diesel fuels by a pervaporation membrane process similar to the process described in US 7,048,846, incorporated by reference herein in its entirety. The high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention that are selective to sulfur- containing molecules would be used to selectively remove sulfur-containing molecules from fluid catalytic cracking (FCC) and other naphtha hydrocarbon streams. Further liquid phase examples include the separation of one organic component from another organic component, e.g. to separate isomers of organic compounds. Mixtures of organic compounds which may be separated using the high hydrocarbon resistant chemically cross-linked aromatic polyimide membrane described in the present invention include: ethylacetate-ethanol, diethylether- ethanol, acetic acid-ethanol, benzene-ethanol, chloroform-ethanol, chloroform-methanol, acetone-isopropylether, allylalcohol-allylether, allylalcohol-cyclohexane, butanol- butylacetate, butanol-l-butylether, ethanol-ethylbutylether, propylacetate-propanol, isopropylether-isopropanol, methanol-ethanol-isopropanol, and ethylacetate-ethanol-acetic acid. EXAMPLES
[0039] The following examples are provided to illustrate one or more preferred embodiments of the invention, but are not limited embodiments thereof. Numerous variations can be made to the following examples that lie within the scope of the invention.
EXAMPLE 1
Preparation and evaluation of cross-linked aromatic polyimide membrane from poly(6FDA-HAB) and poly(DSDA-DBA-TMMDA) aromatic polyimides
[0040] 4.0 g of poly(6FDA-HAB) polyimide synthesized from poly condensation reaction of 6FDA and HAB monomers and 1.0 g of poly(DSDA-DBA-TMMDA) polyimide synthesized from polycondensation reaction of DSDA dianhydride with DBA and TMMDA diamines with a DBA to TMMDA molar ratio of 1 : 1 were dissolved in 12.0 g of NMP and 10.0 g of 1,3-dioxolane solvents. The mixture was mechanically stirred for 2 hours to form a homogeneous casting dope. The resulting homogeneous casting dope was allowed to degas overnight. The poly(6FDA-HAB)/poly(DSDA-DBA-TMMDA) blend membrane was prepared from the bubble free casting dope on a clean glass plate using a doctor knife with a 20-mil gap. The membrane together with the glass plate was then put into a vacuum oven. The solvents were removed by slowly increasing the vacuum and the temperature of the vacuum oven. Finally, the membrane was heated at 200°C under vacuum for 48 hours to completely remove the residual solvents. The dried poly(6FDA-HAB)/poly(DSDA-DBA- TMMDA) blend membrane was heated at 300°C under N 2 for 10 min to cross-link poly(6FDA-HAB) with poly(DSDA-DBA-TMMDA) via esterification reaction between the carboxylic acid groups on poly(DSDA-DBA-TMMDA) and the hydroxyl groups on poly(6FDA-HAB) to form the cross-linked poly(6FDA-HAB)/poly(DSDA-DBA-TMMDA) aromatic polyimide membrane.
[0041] The cross-linked poly(6FDA-HAB)/poly(DSDA-DBA-TMMDA) aromatic polyimide membrane became insoluble in any organic solvents.
[0042] The cross-linked poly(6FDA-HAB)/poly(DSDA-DBA-TMMDA) aromatic polyimide membrane is useful for a variety of gas separation applications such as CO2/CH4, H2/CH4, and He/CH4 separations. The membrane was tested for CO2/CH4, H2/CH4, and He/CH4 separations at 50°C under 791 kPa (100 psig) pure single feed gas pressure. The results show that this chemically cross-linked membrane has CO2 permeance of 8.04 Barrers and high CO2/CH4 selectivity of 45.4 for CO2/CH4 separation. This chemically cross-linked membrane has ¾ permeance of 33.5 Barrers and H2/CH4 selectivity of 189 for H2/CH4 separation. This chemically cross-linked membrane also has He permeance of 41.8 Barrers and He/CH4 selectivity of 236 for He/CFL } separation.
EXAMPLE 2
Preparation of cross-linked aromatic polyimide membrane from poly(DSDA-HAB-TMMDA) and poly(DSDA-DBA-TMMDA) aromatic polyimides
[0043] 2.5 g of poly(DSDA-HAB-TMMDA) polyimide synthesized from
polycondensation reaction of DSDA dianhydride with HAB and TMMDA diamines with a HAB to TMMDA molar ratio of 1 :2 and 2.5 g of poly(DSDA-DBA-TMMDA) polyimide synthesized from polycondensation reaction of DSDA dianhydride with DBA and TMMDA diamines with a DBA to TMMDA molar ratio of 1 :3 were dissolved in 12.0 g of NMP and 10.0 g of 1,3-dioxolane solvents. The mixture was mechanically stirred for 2 hours to form a homogeneous casting dope. The resulting homogeneous casting dope was allowed to degas overnight. The poly(DSDA-HAB-TMMDA)/poly(DSDA-DBA-TMMDA) blend membrane was prepared from the bubble free casting dope on a clean glass plate using a doctor knife with a 20-mil gap. The membrane together with the glass plate was then put into a vacuum oven. The membrane was heated at 200°C under vacuum for 48 hours to completely remove the residual solvents. The dried poly(DSDA-HAB-TMMDA)/poly(DSDA-DBA-TMMDA) blend membrane was heated at 300°C under N 2 for 10 min to cross-link poly(DSDA-HAB- TMMD A)/poly(D SD A-DB A-TMMD A) via esterification reaction between the carboxylic acid groups on poly(DSDA-DBA-TMMDA) and the hydroxyl groups on poly(DSDA-HAB- TMMDA) to form the cross-linked poly(DSDA-HAB-TMMDA)/poly(DSDA-DBA- TMMDA) aromatic polyimide membrane.
SPECIFIC EMBODIMENTS [0044] While the following is described in conjunction with specific embodiments, it will be understood that this description is intended to illustrate and not limit the scope of the preceding description and the appended claims.
[0045] A first embodiment of the invention is a chemically cross-linked aromatic polyimide polymer comprising a formula (I) herein formula (I) is represented by the following formula
wherein R is selected from the group consisting of -H, -COCH 3 ,
and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consistin
and mixtures thereof; Yl is selected from the group consisting of
and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1 : 100 to 100: 1; and n'/m' is in a range of 1 : 100 to 100: 1. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the first embodiment in this paragraph wherein a chemically cross-linked aromatic polyimide membrane comprises the chemically cross-linked aromatic polyimide polymer.
[0046] A second embodiment of the invention is an aromatic polyimide blend comprising a first aromatic polyimide comprising carboxylic acid groups comprising a plurality of repeating units of formula (II)
wherein XI and X2 are selected from the group consisting of
and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of
and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range of 1 : 100 to 100: 1, and preferably n/m is in a range of 1 : 10 to 5 : 1 and a second aromatic polyimide comprising hydroxyl groups comprises a plurality of repeating units of formula (III)
wherein X3 and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consisting of
CF 3 CH 3 o
— ?— — ?— — i— — °— — s —
CF 3 CH 3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof;; wherein Y3 is selected from the group consisting of
and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1100 to 1001, and preferably n'/m' is in a range of 110 to 51. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the second embodiment of this invention wherein the first polyimide polymer and the second polyimide polymer have a weight average molecular weight between 10,000 and 1,000,000 g/mol. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the second embodiment of this invention wherein an aromatic polyimide blend membrane comprises the aromatic polyimide blend of this paragraph.
[0047] A third embodiment of the invention is a process for preparing a chemically cross- linked polyimide polymer membrane comprising making an aromatic polyimide blend membrane comprising a first aromatic polyimide polymer and a second aromatic polyimide polymer and then chemical cross-linking the aromatic polyimide blend membrane by heating the aromatic polyimide blend membrane at 100 to 300°C under an inert atmosphere, wherein the first aromatic polyimide comprises carboxylic acid groups comprising a plurality of repeating units of formula (II)
wherein XI and X2 are selected from the group consisting of
and mixtures thereof, and wherein XI and X2 can be the same or different from each other; wherein Yl is selected from the group consisting of
and mixtures thereof; wherein n and m are independent integers from 2 to 500; and wherein n/m is in a range of 1 : 100 to 100: 1, and preferably n/m is in a range of 1 : 10 to 5: 1 and the second aromatic polyimide comprising hydroxyl groups comprising a plurality of repeating units of formula (III)
wherein X3 and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consisting of
CF 3 CH 3 o
— ?— — ?— — i— — °— — s —
CF 3 CH 3 O and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof;; wherein Y3 is selected from the group consisting of
and mixtures thereof; wherein n' and m' are independent integers from 2 to 500, and wherein n'/m' is in a range of 1 : 100 to 100: 1, and preferably n'/m' is in a range of 1 : 10 to 5: 1. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph wherein the aromatic polyimide blend membrane is fabricated by blending a first aromatic polyimide polymer and a second aromatic polyimide polymer wherein the first aromatic polyimide comprises carboxylic acid groups and the second aromatic polyimide comprises hydroxyl groups. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph further comprising coating a high permeability material onto the aromatic polyimide blend membrane. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph wherein the high permeability material comprises a polysiloxane, a fluoro-polymer, a thermally curable silicone rubber, or a UV radiation curable epoxy silicone. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph wherein the chemically cross-linked polyimide polymer membrane comprising a chemically cross-linked aromatic polyimide polymer comprises a formula (I)
wherein R is selected from the group consisting of -H, -COCH 3 ,
and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consistin
and mixtures thereof; Yl is selected from the group consisting of
and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1 : 100 to 100: 1; and n'/m' is also in a range of 1 : 100 to 100: 1. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph wherein the first aromatic polyimide is selected from the group consisting of poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid-2,4,6-trimethyl-m-phenylenediamine) polyimide derived from a polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,5- diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; poly(3,3',4,4'- diphenylsulfone tetracarboxylic dianhydride-3,5-diaminobenzoic acid -3,3',5,5'-tetramethyl- 4,4'-methylene dianiline) polyimide derived from a polycondensation reaction of 3,3',4,4'- diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,5-diaminobenzoic acid and 3 ,3 ' ,5 ,5 ' -tetramethyl-4,4 ' -methylene dianiline; poly(3 ,3 ' ,4,4 ' -benzophenone tetracarboxylic dianhydride-pyromellitic dianhydride-3,5-diaminobenzoic acid -2,4,6-trimethyl-m- phenylenediamine) polyimide derived from a polycondensation reaction of 3,3',4,4'- benzophenone tetracarboxylic dianhydride and pyromellitic dianhydride with 3,5- diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; poly(3, 3 ',4,4 '-benzophenone tetracarboxylic dianhydride - pyromellitic dianhydride -3,5-diaminobenzoic acid -3,3',5,5'- tetramethyl-4,4' -methylene dianiline) polyimide derived from a polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride and pyromellitic dianhydride with 3,5- diaminobenzoic acid and 3,3',5,5'-tetramethyl-4,4'-methylene dianiline; poly(3,3',4,4'- benzophenone tetracarboxylic dianhydride -3,5-diaminobenzoic acid -3,3',5,5'-tetramethyl- 4,4'-methylene dianiline) polyimide derived from a polycondensation reaction of 3,3',4,4'- benzophenone tetracarboxylic dianhydride with 3,5-diaminobenzoic acid and 3,3',5,5'- tetramethyl-4,4' -methylene dianiline; poly(pyromellitic dianhydride - 3,5-diaminobenzoic acid -3,3 ',5,5 '-tetramethyl-4,4 '-methylene dianiline) polyimide derived from a
polycondensation reaction of pyromellitic dianhydride with 3,5-diaminobenzoic acid and 3 ,3 ' ,5 ,5 ' -tetramethyl-4,4 ' -methylene dianiline; poly(3 ,3 ' ,4,4 ' -benzophenone tetracarboxylic dianhydride -3,5-diaminobenzoic acid -2,4,6-trimethyl-m-phenylenediamine) polyimide derived from a polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 3,5-diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine; and poly(pyromellitic dianhydride -3,5-diaminobenzoic acid -2,4,6-trimethyl-m- phenylenediamine) polyimide derived from a polycondensation reaction of pyromellitic dianhydride with 3,5-diaminobenzoic acid and 2,4,6-trimethyl-m-phenylenediamine. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the third embodiment in this paragraph wherein the second aromatic polyimide is selected from the group consisting of poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino-biphenyl-2,4,6-trimethyl-m-phen ylenediamine) polyimide derived from the polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,3'-dihydroxy-4,4'-diamino-biphenyl and 2,4,6-trimethyl-m-phenylenediamine; poly [2,2 ' -bis-(3 ,4-dicarboxyphenyl) hexafluoropropane dianhydride-3,3'-dihydroxy-4,4'-diamino-biphenyl] polyimide derived from the
polycondensation reaction of 2,2'-bis-(3,4-dicarboxyphenyl) hexafluoropropane dianhydride with 3,3'-dihydroxy-4,4'-diamino-biphenyl; poly(3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino-biphenyl -3,3 ',5,5 '-tetramethyl-4,4'-methylene dianiline) polyimide derived from the polycondensation reaction of 3,3',4,4'-diphenylsulfone tetracarboxylic dianhydride with a mixture of 3,3'-dihydroxy-4,4'-diamino-biphenyl and 3 ,3 ' ,5 ,5 ' -tetramethyl-4,4 ' -methylene dianiline; poly(3 ,3 ' ,4,4 ' -benzophenone tetracarboxylic dianhydride -3,3'-dihydroxy-4,4'-diamino-biphenyl -2,4,6-trimethyl-m-phenylenediamine) polyimide derived from the polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 3,3'-dihydroxy-4,4'-diamino-biphenyl and 2,4,6-trimethyl- m-phenylenediamine; poly(3, 3 ',4,4 '-benzophenone tetracarboxylic dianhydride -3,3'- dihydroxy-4,4'-diamino-biphenyl -3,3 ',5,5 '-tetramethyl-4,4 '-methylene dianiline) polyimide derived from the polycondensation reaction of 3,3',4,4'-benzophenone tetracarboxylic dianhydride with 3,3'-dihydroxy-4,4'-diamino-biphenyl and 3,3 ',5,5 ' -tetramethyl-4,4 '- methylene dianiline; poly(3, 3 ',4,4 '-benzophenone tetracarboxylic dianhydride -2,2-bis(3- amino-4-hydroxyphenyl)-hexafluoropropane-3 ,3 ' ,5 ,5 ' -tetramethyl-4,4 '-methylene dianiline) polyimide derived from the polycondensation reaction of 3,3 ',4,4 '-benzophenone tetracarboxylic dianhydride with 2,2-bis(3-amino-4-hydroxyphenyl)-hexafluoropropane and 3,3 ',5,5 '-tetramethyl-4,4'-methylene dianiline.
[0048] A fourth embodiment of the invention is a process for separating at least one gas from a mixture of gases comprising a. providing a chemically cross-linked aromatic polyimide membrane comprising a formula (I)
wherein R is selected from the group consisting of -H, -COCH 3 ,
and mixtures thereof; XI, X2, X3, and X4 are selected from the group consisting of
and mixtures thereof, and -R'- is selected from the group consisting of
and mixtures thereof; Yl is selected from the group consisting of
and mixtures thereof ; Y3 is selected from the group consisting of
and mixtures thereof, and -R"- is selected from the group consisting of-H, COCH 3 , and mixtures thereof; n, m, n' and m' are independent integers from 2 to 500; n/m is in a range of 1 : 100 to 100: 1; and n'/m' is also in a range of 1 : 100 to 100: 1; contacting the mixture of gases to one side of the chemically cross-linked aromatic polyimide membrane to cause at least one gas to permeate the membrane; and removing from an opposite side of the chemically cross-linked aromatic polyimide membrane a permeate gas composition comprising a portion of the at least one gas that permeated the membrane. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the at least two gases are a mixture of volatile organic compounds and atmospheric gas. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the at least two gases are a mixture of helium, nitrogen, carbon dioxide or hydrogen sulfide, or mixtures thereof in a natural gas stream. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the mixture of gases are a pair of gases selected from the group consisting of nitrogen and oxygen, carbon dioxide and methane, hydrogen and methane, nitrogen and methane, or a mixture of carbon monoxide, helium and methane. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the mixture of gases are selected from the group consisting of a mixture of iso and normal paraffins, and a mixture of xylenes. An
embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the mixture of gases are a hydrocarbon vapor and hydrogen. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the mixture of gases is a mixture of propylene and propane. An embodiment of the invention is one, any or all of prior embodiments in this paragraph up through the fourth embodiment in this paragraph wherein the mixture of gases comprises methane, carbon dioxide, oxygen, nitrogen, water vapor, hydrogen sulfide, and helium.
[0049] Without further elaboration, it is believed that using the preceding description that one skilled in the art can utilize the present invention to its fullest extent and easily ascertain the essential characteristics of this invention, without departing from the spirit and scope thereof, to make various changes and modifications of the invention and to adapt it to various usages and conditions. The preceding preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limiting the remainder of the disclosure in any way whatsoever, and that it is intended to cover various modifications and equivalent
arrangements included within the scope of the appended claims.
[0050] In the foregoing, all temperatures are set forth in degrees Celsius and, all parts and percentages are by weight, unless otherwise indicated.