Field

[0001] Embodiments relate to modifiers for use in compositions for forming high clarity-low temperature use containers such as freezer containers.

Background

[0002] Polyolefin based materials for forming freezer containers for use at low temperatures (i.e., below 0 °C), that still have high clarity (i.e., greater than 90% clarity), may be challenging. For example, the use of polypropylene-based

homopolymers, polypropylene-based random copolymers (RCP), or polypropylene- based copolymers that have been impact-modified with elastomers have been proposed. However, polypropylene-based homopolymers and copolymers may provide the desirable toughness and clarity for many applications, but may suffer from relatively poor impact properties at lower temperatures due to polypropylene' s high Tg (glass transition temperature). Further, the impact-modified copolymers may suffer from relatively poor clarity in comparison to the homopolymers and random copolymers. Accordingly, a composition is sought that can provide both toughness and clarity even at low temperatures.

Summary

[0003] Disclosed herein is a composition for forming a sub-ambient temperature use container, the composition including from 10 wt% to 40 wt% of a modifier and from 60 wt% to 90 wt% of a propylene polymer base that has a melt flow rate from 2 g/10 min to 100 g/10 min, according to ASTM D1238 and at 230 °C/2.16 kg. The modifier includes (a) from 10 wt% to 50 wt%, based on a total weight of the modifier, of a block composite, a specified block composite, or a crystalline block composite, (b) from 20 wt% to 90 wt% of a first polyolefin copolymer, based on a total weight of the modifier, the first polyolefin copolymer being derived from ethylene and at least one of a C3 to Cio alpha-olefin, having a melt index from 0.5 g/10 min to 1500 g/10 min, according to ASTM D1238 and at 190 °C/2.16 kg, and having a density from 0.850 g/cc to 0.910 g/cc, and (c) optionally, from 30 wt% to 60 wt% of a second polyolefin copolymer, based on a total weight of the modifier, the second polyolefin copolymer being derived from ethylene and at least one of a C3 to C10 alpha-olefin, having a melt index from 100 g/10 min to 2000 g/10 min, according to ASTM D1238 and at 190 "C/2.16 kg, and having a density from 0.860 g/cc to 0.900 g/cc.

Brief Description of the Drawings

[0004] Features of the embodiments will be apparent to those of ordinary skill in the art with reference to the attached figures, in which:

[0005] FIG. 1 illustrates the TEM morphology of Comparative Ex. A at 1 μιη and 0.2 μιη.

[0006] FIG. 2 illustrates the TEM morphology of Comparative Ex. C at 1 μιη and 0.2 μιη.

[0007] FIG. 3 illustrates the TEM morphology of Working Ex. 2 at 1 μιη and 0.2 μιη.

[0008] FIG. 4 illustrates the TEM morphology of Working Ex. 3 at 1 μιη and 0.2 μιη.

[0009] FIG. 5 illustrates the TEM morphology of Working Ex. 4 at 1 μιη and 0.2 μιη.

[0010] FIG. 6 illustrates the TEM morphology of Working Ex. 5 at 1 μιη and 0.2 μιη.

Detailed Description

[0011] Clear optics may be challenging when blending ethylene-based elastomers in polypropylene. For example, certain elastomers significantly lower the modulus and clarity of polypropylene. As such, to obtain clear compositions, refractive index matching of the materials has been proposed. However, an approach that relies only on refractive index matching of elastomers with polypropylene has the disadvantage of being restricted to the use of plastomers (such as plastomers having a density greater than 0.900 g/cm ³ ), which may provide lower impact properties especially at lower temperatures. Accordingly, a new compatibilization approach is proposed that relies on particle sizing via compatibilization of non-refractive index matched elastomers with polypropylene; this allows for the expanded use of elastomers having a density from 0.850 g/cm ³ to 0.910 cm ³ (e.g., 0.850 g/cm ³ to 0.890 cm ³ , 0.850 g/cm ³ to 0.885 g/cm ³ , and/or 0.850 g/cm ³ to 0.875 g/cm ³ ) that have relatively better impact properties at lower temperatures (i.e., have a relatively lower glass transition temperature).

[0012] According to embodiments, a modifier for use with a propylene polymer base to form compositions for forming high clarity-low temperature use containers, such as freezer containers, has been proposed. The modifier is able to enhance toughness at low temperatures (i.e., below 0 °C) while still forming a high clarity (i.e., greater than 90% clarity) container. With respect to the modifier, impact efficiency of an elastomeric modifier is directly related to crystallinity of the modifier and dispersion of the individual elastomer domains into a polypropylene matrix. Further,

conventionally, the dispersion of an elastomer into polypropylene may be challenged in view of, e.g., the melt-mixing process and compatibility. Accordingly, embodiments relate to a modifier that combines an impact resistance provider for enhancing toughness at low temperatures, a high melt flow provider for enabling good melt- mixing, and a non-refractive index matched elastomer. For example, the modifier may be provided in pre-blended form as a single component (e.g., in pellet form) and added into an existing process that uses at least a propylene polymer base for forming a container, such as a freezer container. As would be understood by a person of ordinary skill in the art, the modifiers may be added as separate components to the propylene polymer base.

Terms

[0013] The numerical ranges in this disclosure are approximate, and thus may include values outside of the range unless otherwise indicated. Numerical ranges include all values from and including the lower and the upper values, in increments of one unit, provided that there is a separation of at least two units between any lower value and any higher value. As used with respect to a chemical compound, unless specifically indicated otherwise, the singular includes all isomeric forms and vice versa.

[0014] All references to the Periodic Table of the Elements herein shall refer to the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 2003. Also, any references to a Group or Groups shall be to the Group or Groups reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Unless stated to the contrary, implicit from the context, or customary in the art, all parts and percents are based on weight. For purposes of United States patent practice, the contents of any patent, patent application, or publication referenced herein are hereby incorporated by reference in their entirety (or the equivalent US version thereof is so incorporated by reference) especially with respect to the disclosure of synthetic techniques, definitions (to the extent not inconsistent with any definitions provided herein) and general knowledge in the art.

[0015] "Composition" and like terms mean a mixture or blend of two or more components. For example, one composition is the combination of a propylene based polymer and a block composite.

[0016] "Blend," "polymer blend," and like terms mean a blend of two or more polymers. Such a blend may or may not be miscible. Such a blend may or may not be phase separated. Such a blend may or may not contain one or more domain

configurations, as determined from transmission electron spectroscopy, light scattering, x-ray scattering, and any other method known in the art.

[0017] "Polymer" means a compound prepared by polymerizing monomers, whether of the same or a different type. The generic term polymer, thus, embraces the term homopolymer, usually employed to refer to polymers prepared from only one type of monomer, and the terms interpolymer and copolymer as defined below. The term polymer also embraces all forms of interpolymers, e.g., random, block, homogeneous, heterogeneous, etc.

[0018] "Interpolymer" and "copolymer" mean a polymer prepared by the polymerization of at least two different types of monomers. These generic terms include both classical copolymers, i.e., polymers prepared from two different types of monomers, and polymers prepared from more than two different types of monomers, e.g., terpolymers, tetrapolymers, etc. The terms "ethylene/alpha-olefin copolymer" and "propylene/alpha-olefin copolymer" are indicative of interpolymers as described below.

[0019] "Units derived from ethylene," "ethylene content," and like terms mean the units of a polymer that formed from the polymerization of ethylene monomers. "Units derived from a-olefin," "alpha-olefin content," "a-olefin content," and like terms mean the units of a polymer that formed from the polymerization of specific a-olefin monomers, in particular at least one of a C3-10 a-olefin. "Units derived from

propylene," "propylene content," and like terms mean the units of a polymer that formed from the polymerization of propylene monomers.

[0020] "Propylene based polymer," and like terms mean a polymer that comprises a majority weight percent polymerized propylene monomer, also referred to as units derived from propylene (based on the total amount of polymerizable monomers), and optionally comprises at least one polymerized comonomer different from propylene (such as at least one selected from a C2 and C4-10 a olefin) so as to form a propylene- based interpolymer. For example, when the propylene -based polymer is a copolymer, the propylene content is greater than 50 wt%, based on the total weight of the copolymer.

[0021] "Ethylene based polymer" and like terms mean a polymer that comprises a majority weight percent polymerized ethylene monomer, also referred to as units derived from ethylene (based on the total weight of polymerizable monomers), and optionally may comprise at least one polymerized comonomer different from ethylene (such as at least one selected from a C3-10 a olefin) so as to form an ethylene-based interpolymer. For example, when the ethylene-based polymer is a copolymer, the amount of ethylene is greater than 50 wt%, based on the total weight to the copolymer.

[0022] The term "polyethylene" includes homopolymers of ethylene and copolymers of ethylene and one or more C3-8 a-olefins in which ethylene comprises at least 50 mole percent. The term "polypropylene" includes homopolymers of propylene such as isotactic polypropylene, syndiotactic polypropylene, and copolymers of propylene and one or more C ₂ , _4-8 a-olefins in which propylene comprises at least 50 mole percent. Preferably, a plurality of the polymerized monomer units of at least one block or segment in the polymer (a crystalline block) comprise propylene, preferably at least 90 mole percent, more preferably at least 93 mole percent, and most preferably at least 95 mole percent. A polymer made primarily from a different a-olefin, such as 4- methyl-l-pentene would be named similarly.

[0023] "Random copolymer polypropylene" (RCP) and like terms mean a propylene/alpha-olefin interpolymer in which the units derived from the alpha-olefin monomer are randomly distributed across the polymer chain, as opposed to distributed across the polymer chain in an alternating, periodic, or block pattern. In contrast, "homogenous propylene -based interpolymer" and like terms mean a propylene/alpha- olefin interpolymer in which the units derived from the alpha-olefin monomer are approximately evenly distributed across the polymer chains of the bulk polymer.

[0024] "Impact modified propylene-based copolymer" and the like terms mean a propylene-based polymer composition that has been impact-modified such that the composition's impact strength at room temperature or below is maintained or increased as compared to said given composition's impact strength at the same temperature without the added impact modifier.

[0025] The term "block composite" (BC) refers to polymers comprising an ethylene based polymer (EP) having an ethylene content of from 10 mol% to 90 mol%, an alpha- olefin based polymer (AOP) having an alpha-olefin content of greater than 90 mol%, and a block copolymer having an ethylene block (EB) and an alpha-olefin block (AOB), wherein the ethylene block of the block copolymer is the same composition as the ethylene based polymer of the block composite and the alpha-olefin block of the block copolymer is the same composition as the alpha-olefin based polymer of the block composite. The compositional split between the amount of ethylene based polymer and alpha-olefin based polymer will be essentially the same as that between the corresponding blocks in the block copolymer. In certain embodiments, the alpha- olefin is propylene. In further embodiments, the AOB and EB may be an iPP-EP diblock copolymer.

[0026] The term "specified block composite" (SBC) refers to polymers comprising an ethylene based polymer (EP) having an ethylene content of from 69 mol% to 90 mol%, an alpha-olefin based polymer (AOP) having an alpha-olefin content of from 61 mol% to 90 mol%, and a block copolymer having an ethylene block (EB) and an alpha- olefin block (AOB), wherein the ethylene block of the block copolymer is the same composition as the ethylene based polymer of the specified block composite and the alpha-olefin block of the block copolymer is the same composition as the alpha-olefin based polymer of the specified block composite. The compositional split between the amount of ethylene based polymer and alpha-olefin based polymer will be essentially the same as that between the corresponding blocks in the block copolymer. In certain embodiments, the alpha-olefin is propylene. In certain embodiments, the AOB and EB may be an iPP-EP diblock copolymer. In further embodiments, the AOB and EB may be a PE/EP (propylene-ethylene and ethylene-propylene) diblock copolymer.

[0027] The term "crystalline block composite" (CBC) refers to polymers comprising a crystalline ethylene based polymer (CEP) having an ethylene content of greater than 90 mol%, a crystalline alpha-olefin based polymer (CAOP) having an alpha-olefin content of greater than 90 mol%, and a block copolymer having a crystalline ethylene block (CEB) and a crystalline alpha-olefin block (CAOB), wherein the CEB of the block copolymer is the same composition as the CEP of the crystalline block composite and the CAOB of the block copolymer is the same composition as the CAOP of the crystalline block composite. The compositional split between the amount of CEP and CAOP will be essentially the same as that between the corresponding blocks in the block copolymer. In exemplary embodiments, the alpha-olefin is propylene. In further embodiments, the CAOB and the CEB may be an iPP-EP (isotactic polypropylene and ethylene-propylene) diblock copolymer.

[0028] "Block copolymer" or "segmented copolymer" refers to a polymer comprising two or more chemically distinct regions or segments (referred to as "blocks") joined in a linear manner, that is, a polymer comprising chemically differentiated units that are joined (covalently bonded) end-to-end with respect to polymerized functionality (e.g., polymerized propylenic functionality), rather than in pendent or grafted fashion. Block copolymers comprise sequences ("blocks") of the same monomer unit, covalently bound to sequences of unlike type. The blocks can be connected in a variety of ways, such as A— B in diblock and A— B— A triblock structures, where A represents one block and B represents a different block. In a multi- block copolymer, A and B can be connected in a number of different ways and be repeated multiply. It may further comprise additional blocks of different type. Multi- block copolymers may be linear multi-block, multi-block star polymers (in which all blocks bond to the same atom or chemical moiety) or comb-like polymers where the B blocks are attached at one end to an A backbone. The block copolymers can be linear or branched. With respect to the block copolymers, the blocks may differ in the amount of comonomer incorporated therein. The blocks may also differ in the type of comonomer, density, the amount of crystallinity, the crystallite size attributable to a polymer of such composition, the type or degree of tacticity (isotactic or syndio tactic), regio-regularity or regio-irregularity, the amount of branching, including long chain branching or hyper-branching, the homogeneity, or any other chemical or physical property. The block copolymers are characterized by unique distributions of polymer polydispersity (PDI or Mw/Mn), block length distribution, and/or block number distribution, e.g., due to the effect of the shuttling agent(s) in combination with the catalyst(s).

[0029] "Crystalline" refers to a polymer or polymer block that possesses a first order transition or crystalline melting point (Tm) as determined by differential scanning calorimetry (DSC) or equivalent technique. The term may be used interchangeably with the term "semicrystalline".

[0001] The term "crystallizable" refers to a monomer that can polymerize such that the resulting polymer is crystalline. Crystalline ethylene polymers typically have, but are not limited to, densities of 0.89 g/cc to 0.97 g/cc and melting points of 75°C to 140°C. Crystalline propylene polymers may have, but are not limited to, densities of 0.88 g/cc to 0.91 g/cc and melting points of 100 °C to 170°C.

[0030] "Amorphous" refers to a polymer lacking a crystalline melting point as determined by differential scanning calorimetry (DSC) or equivalent technique.

[0031] "Isotactic" is defined as polymer repeat units having at least 70 percent isotactic pentads as determined by ¹³ C-NMR analysis. "Highly isotactic" is defined as polymers having at least 90 percent isotactic pentads.

Block Composite

[0032] In certain embodiments, the modifier of the composition includes from 10 wt% to 50 wt% (e.g., from 15 wt% to 50 wt%, from 15 wt% to 40 wt%, etc.), based on a total weight of the modifier, of a block composite. In exemplary embodiments, the block composite may have a total ethylene content that is from 25 wt% to 70 wt% (e.g., from 25 wt% to 60 wt%, from 25 wt% to 55 wt%, and from 30 wt% to 50 wt%) based on the total weight of the block composite. The remainder of the total weight of the block composite may be accounted for by units derived from at least one C3-10 alpha- olefin. For example, the remainder of the total weight of the block composite may be accounted for by units derived from propylene.

[0033] In exemplary embodiments, the block composite refers to polymers comprising an ethylene based polymer (EP) (soft copolymer) having an ethylene content of from 10 mol% to 90 mol%, an alpha-olefin based polymer (AOP) (hard copolymer) having an alpha-olefin content of greater than 90 mol%, and a block copolymer having an ethylene block/segment (EB) and an alpha-olefin block/segment (AOB), wherein the ethylene block of the block copolymer is the same composition as the ethylene based polymer of the block composite and the alpha-olefin block of the block copolymer is the same composition as the alpha-olefin based polymer of the block composite. The compositional split between the amount of ethylene based polymer and alpha-olefin based polymer will be essentially the same as that between the corresponding blocks in the block copolymer.

[0034] In further embodiments, the block composite refers to polymers comprising an EP having an ethylene content that is greater than 10 wt% and less than 95 wt%, an AOP having a propylene content that is greater than 90 wt% and up to 100 wt%, and a block copolymer (e.g., a diblock) having an EB (i.e., soft block) and an AOB (i.e., hard block), wherein the AOB of the block copolymer is the same composition as the AOP of the block composite and the EB of the block copolymer is the same composition as the EP of the block composite. The compositional split between the amount of EP and AOP will be essentially the same as that between the corresponding blocks in the block copolymer.

[0035] In exemplary embodiments, the hard blocks refer to highly crystalline blocks of polymerized alpha-olefin units (e.g., propylene). In the hard blocks, the monomer (i.e., propylene) may be present in an amount greater than 90 wt%. The remainder of the hard block may be the comonomer (e.g., ethylene) in an amount of less than 10 wt%. In exemplary embodiments, the hard blocks comprise all or substantially all propylene units, such as an iPP (isotactic) homopolymer block or an iPP copolymer block with less than 10 wt% of ethylene. In exemplary embodiments, the soft blocks refer to amorphous, substantially amorphous, or elastomeric blocks of polymerized ethylene units. In the soft blocks, the monomer (i.e., ethylene) may be present in an amount of greater than 20 wt% and equal to or less than 100 wt% (e.g., from 40 wt% to 99 wt%, from 45 wt% to 90 wt%, and/or from 50 wt% to 80 wt%). The remainder of the soft block may be the comonomer (e.g., propylene).

[0036] According to an exemplary embodiment, the block composite includes a block copolymer having 30-70 wt% hard block and 30-70 wt% soft block. In other words, the block composite includes a block copolymer having 30-70 wt% hard block and 30-70 wt% soft block based on the weight of the block copolymer.

[0037] According to an exemplary embodiment, the block copolymer of the block composite has the formula (EP)-(iPP), in which EP represents the soft block of polymerized ethylene and propylene monomeric units (e.g., 50-80 wt% of ethylene and remainder propylene) and iPP represents a hard block of isotactic propylene homopolymer or isotactic propylene copolymer (e.g., less than 10 wt% of ethylene and remainder propylene).

[0038] The block composites may include from 0.5 wt% to 95.0 wt% EP, from 0.5 to 95.0 wt% iPP, and from 5.0 wt% to 99.0 wt% of the block copolymer. Weight percents are based on total weight of block composite. The sum of the weight percents of EP, iPP, and the block copolymer equals 100%. An exemplary measurement of the relative amount of the block copolymer is referred to as the Block Composite Index (BCI), as further discussed below. The BCI for the block composite is greater than 0 and less than 1.0.

[0039] In some embodiments, the block composites may have a microstructure index greater than 1 and equal to or less than 20. The microstructure index is an estimation using solvent gradient interaction chromatography (SGIC) separation to differentiate between block copolymers from random copolymers. In particular, microstructure index estimation relies on differentiating between two fractions, i.e., a higher random copolymer content fraction and a higher block copolymer content fraction, of which the random copolymer and the block copolymer have essentially the same chemical composition. The early eluting fraction (i.e., the first fraction) correlates to random copolymers and the late eluting component (i.e., the second fraction) correlates to block copolymers. The calculation of the microstructure index is discussed below.

[0040] The block composites may have a weight average molecular weight (Mw) from 10,000 g/mol to 2,500,00 g/mol, from 35,000 g/mol to 1,000,000 g/mol, from 50,000 g/mol to 300,000 g/mol, and/or from 50,000 g/mol to 200,000 g/mol. For example, the Mw may be from 20 kg/mol to 1,000 kg/mol, from 50 kg/mol to 500 kg/mol, and/or from 80 kg/mol to 200 kg/mol. The molecular weight distribution (Mw/Mn) or polydispersity of the block composites may be less than 5, between 1 and 5, and/or between 1.5 and 4. Weight average molecular weight (Mw) and number average molecular weight (Mn) are well known in polymer art and can be determined by methods known to a person of ordinary skill in the art.

[0041] The melt flow rate (MFR) of the block composites may be from 0.1 g/10 min to 1,000 g/10 min measured in accordance with ASTM D-1238 (230°C; 2.16 kg). For example, the melt flow rate of the block composites may be from 1 g/10 min to 50 g/10 min, from 1 g/10 min to 25 g/10 min, and/or from 1 g/10 min to 10 g/10 min.

[0042] The density of the block composites may be between 0.850 and 0.900 g/cc. In exemplary embodiments, the density of the block composites is from 0.860 to 0.895, from 0.865 to 0.895, and/or from 0.865 to 0.890 g/cc. Density is measured in accordance with ASTM D792.

[0043] The block composites may have a second peak Tm of greater than 90°C ( e.g., greater than 100°C). According to an exemplary embodiment, the block composites exhibit a second peak Tm in a range from 100°C to 150°C).

Specified Block Composite

[0044] In certain embodiments, the modifier of the composition includes from 10 wt% to 50 wt% (e.g., from 15 wt% to 40 wt%,), based on a total weight of the modifier, of a specified block composite. In exemplary embodiments, the specified block composite may have a total ethylene content that is from 30 wt% to 70 wt% based on the total weight of the specified block composite. The remainder of the total weight of the specified block composite may be account for by units derived from at least one C _3- 10 alpha-olefin. For example, the remainder of the total weight of the specified block composite may be accounted for by units derived from propylene.

[0045] The specified block composite (SBC) includes an ethylene based polymer (EP) (soft copolymer), an alpha-olefin based polymer (AOP) (hard copolymer), and a block copolymer having an ethylene block/segment (EB) (soft block) and an alpha- olefin block/segment (AOB) (hard block), where the ethylene block of the block copolymer is the same composition as the ethylene based polymer of the specified block composite and the alpha-olefin block of the block copolymer is the same composition as the alpha-olefin based polymer of the specified block composite. The compositional split between the amount of ethylene based polymer and alpha-olefin based polymer will be essentially the same as that between the corresponding blocks in the block copolymer. In the specified block composite, the alpha-olefin is at least one selected from the group of C3-10 a-olefins (e.g., may be propylene and/or butylene).

[0046] The alpha-olefin based polymer and the alpha-olefin block of the specified block composite may have an alpha-olefin content that is from 61 mol% to 90 mol%. The remainder may be essentially accounted for by at least one selected from the group of C2 - C4-10 a -olefins as comonomers. For example, the remainder may be essentially accounted for by units derived from ethylene, e.g., such that the ethylene content is from 10 mol% to 39 mol%. Said in another way, the alpha-olefin based polymer and the alpha-olefin block may have an alpha-olefin content (such as propylene content) that is from 70 wt% to 93 wt%.

[0047] The ethylene based polymer and ethylene block of the block copolymer of the specified block composite may have an ethylene content from 69 mol% to 90 mol%. The remainder may be essentially accounted for by at least one selected from the group of C3-10 a -olefins as a comonomer, e.g., such that the comonomer content is from 10 mol% to 31 mol%. Said in another way, the ethylene content of ethylene based polymer and ethylene block of the block copolymer may be from 70 wt% to 93 wt%.

[0048] In exemplary embodiments, the alpha-olefin based polymer and the alpha- olefin block of the block copolymer in the specified block composite includes propylene. For example, the propylene content is from 61 mol% to 90 mol%. The alpha-olefin based polymer and the alpha-olefin block of the block copolymer and may additional comprise ethylene as a comonomer. Further, the ethylene based polymer and the ethylene block of the block copolymer may comprise propylene as a comonomer. The compositional split between the amount of ethylene based polymer and the alpha- olefin based polymer will be essentially the same as that between the corresponding blocks in the block copolymer.

[0049] According to an exemplary embodiment, the specified block composite includes a block copolymer having 30-70 wt% hard block and 30-70 wt% soft block. In other words, the specified block composite includes a block copolymer having 30-70 wt% hard block and 30-70 wt% soft block based on the weight of the block copolymer.

[0050] The specified block composite may include from 0.5 wt% to 95.0 wt% EP, from 0.5 wt% to 95.0 wt% AOP, and from 5.0 wt% to 99.0 wt% of the block copolymer. For example, the specified block composite may include from 5.0 wt% to 80.0 wt% EP, from 5.0 wt% to 80.0 wt% AOP, and from 20.0 wt% to 90.0 wt% of the block copolymer. Weight percents are based on total weight of block composite. The sum of the weight percents of EP, AOP, and the block copolymer equals 100%. An exemplary measurement of the relative amount of the block copolymer is referred to as the Modifier Block Composite Index (MBCI). The MBCI is based on HTLC separation (e.g., not xylene separation) to isolate unbounded polypropylene in the block composite, and the methodology and assumptions are similar to the CBCI calculation, as discussed below. The MBCI for the specified block composite is greater than 0 and less than 1.0.

[0051] The specified block composites may have a weight average molecular weight (Mw) from 10,000 g/mol to 2,500,00 g/mol, from 35,000 g/mol to 1,000,000 g/mol, from 50,000 g/mol to 300,000 g/mol, and/or from 50,000 g/mol to 200,000 g/mol. For example, the Mw may be from 20 kg/mol to 1 ,000 kg/mol, from 50 kg/mol to 500 kg/mol, and/or from 80 kg/mol to 200 kg/mol. The molecular weight distribution (Mw/Mn) or polydispersity of the specified block composites may be less than 5, between 1 and 5, and/or between 1.5 and 4. Weight average molecular weight (Mw) and number average molecular weight (Mn) are well known in polymer art and can be determined by methods known to a person of ordinary skill in the art. [0052] The MFR (melt flow rate) of the specified block composites may be from 0.1 to 1000 g/10 min (230°C/2.16 kg), from 1 to 500 g/10 min (230°C/2.16 kg), from 1 to 100 g/10 min (230°C/2.16 kg), from 3 to 50 g/10 min (230°C/2.16 kg), and/or from 5 to 20 g/10 min (230°C/2.16 kg).

[0053] In accordance with ASTM D792, the density of the specified block composite may be between 0.850 and 0.900 g/cc. In exemplary embodiments, the density of the specified block composite may be from 0.860 to 0.900, from 0.865 to 0.890, and/or from 0.870 to 0.890 g/cc.

[0054] The specified block composite may have a second peak Tm of greater than 60°C, greater than 70°C, and/or greater than 80°C.

Crystalline Block Composites

[0055] In certain embodiments, the modifier of the composition includes from 10 wt% to 50 wt% (e.g., from 15 wt% to 40 wt%), based on a total weight of the modifier, of a crystalline block composite. In exemplary embodiments, the crystalline block composite may have a total ethylene content that is from 40 wt% to 70 wt% based on the total weight of the crystalline block composite. The remainder of the total weight of the crystalline block composite may be accounted for by units derived from at least one C3-10 alpha-olefin. For example, the remainder of the total weight of the crystalline block composite may be accounted for by units derived from propylene.

[0056] The crystalline block composite (CBC) refers to polymers having a crystalline ethylene based polymer (CEP), a crystalline alpha-olefin based polymer (CAOP), and a block copolymer comprising a crystalline ethylene block/segment (CEB) and a crystalline alpha-olefin block/segment (CAOB), wherein the CEB of the block copolymer is the same composition as the CEP of the crystalline block composite and the CAOB of the block copolymer is the same composition as the CAOP of the crystalline block composite. Additionally, the compositional split between the amount of CEP and CAOP will be essentially the same as that between the corresponding blocks in the block copolymer.

[0057] The crystalline block composite (CBC) includes the crystalline ethylene based polymer (CEP), the crystalline alpha-olefin based polymer (CAOP), and the block copolymer having the crystalline ethylene block (CEB) and the crystalline alpha- olefin block (CAOB), where the CEB is the same composition as the CEP and the CAOB is the same composition as the CAOP. In the crystalline block composite, the alpha-olefin is at least one selected from the group of C3-10 a -olefins (e.g., may be propylene and/or butylene). The CAOP and the CAOB may have an alpha-olefin content that is greater than 90 mol%. The CEP and CEB comprise greater than 90 mol% of units derived from ethylene (i.e., ethylene content), and any remainder may be at least one of selected from the group of C3-10 a -olefins as a comonomer (in an amount less than 10 mol%, less than 7 mol%, less than 5 mol%, less than 3 mol%, etc.).

[0058] In exemplary embodiments, the CAOP and CAOB include propylene, e.g., greater than 90 mol% units derived from propylene and any remainder may be ethylene and/or at least one of selected from the group of C4-10 a -olefins as a comonomer (in an amount less than 10 mol%, less than 7 mol%, less than 5 mol%, less than 4 mol%, less than 4 mol%, etc.). The CEP and CEB include ethylene, e.g., greater than 90 mol% units derived from ethylene and any remainder may be propylene and/or at least one of selected from the group of C4-10 a -olefins as a comonomer (in an amount less than 10 mol%, less than 7 mol%, less than 5 mol%, less than 4 mol%, less than 4 mol%, etc.). The compositional split between the amount of CEP and CAOP will be essentially the same as that between the corresponding blocks in the block copolymer. The CEB and the CAOB may be referred to as hard (crystalline) segments/blocks.

[0059] In exemplary embodiments, the CAOB refers to highly crystalline blocks of polymerized alpha olefin units in which units derived from the monomer that is one of C3-10 a-olefins are present in an amount greater than 90 mol%, greater than 93 mol%, greater than 95 mol%, and/or greater than 96 mol%. In other words, the comonomer content in the CAOB is less than 10 mol%, less than 7 mol%, less than 5 mol%, and/or less than 4 mol%. A CAOB with propylene crystallinity may have corresponding melting points that are 80°C and above, 100°C and above, 115°C and above, and/or 120°C and above. In some embodiments, the CAOB comprises all or substantially all propylene units. CEB refers to blocks of polymerized ethylene units in which the comonomer content (such as propylene) is 10 mol% or less, between 0 mol% and 10 mol%, between 0 mol% and 7 mol%, and/or between 0 mol% and 5 mol%. Said in another way, the CEB is derived from at least 90 mol% ethylene, greater than 90 mol% ethylene, greater than 93 mol% ethylene, and/or greater than 95 mol% ethylene. Such CEBs have corresponding melting points that may be 75°C and above, 90°C and above, and/or 100°C and above.

[0060] In an exemplary embodiment, the CAOB may refer to highly crystalline blocks of polymerized alpha olefin units in which the monomer that is one of C3-10 a-olefins is present in an amount of at least 88 wt% and/or at least 90 wt%. In other words, the comonomer content in the CAOBs is less than 10 wt%. CEB may refer to blocks of polymerized ethylene units in which the comonomer content (such as propylene) is 10 wt% or less.

[0061] The crystalline block composite may include from 0.5 wt% to 95.0 wt% CEP, from 0.5 wt% to 95.0 wt% CAOP, and from 5.0 wt% to 99.0 wt% of the crystalline block copolymer. For example, the crystalline block composite may include from 5.0 wt% to 80.0 wt% CEP, from 5.0 wt% to 80.0 wt% CAOP, and from 20.0 wt% to 90.0 wt% of the crystalline block copolymer. Weight percents are based on total weight of crystalline block composite. The sum of the weight percents of CEP, CAOP, and the crystalline block copolymer equals 100%. An exemplary measurement of the relative amount of the crystalline block copolymer is referred to as the Crystalline Block Composite Index (CBCI). The CBCI for the crystalline block composite is greater than 0 and less than 1.0. For example, the CBCI is from 0.20 to 0.99, from 0.30 to 0.99, from 0.40 to 0.99, from 0.40 to 0.90, from 0.40 to 0.85, and/or from 0.50 to 0.80.

[0062] The crystalline block composite may have, a Tm greater than 90°C (e.g., for both a first peak and a second peak), a Tm greater than 100 °C (e.g., for both a first peak and a second peak), and/or greater than 120 °C (e.g., for at least one of a first peak and a second peak). For example, the Tm is in the range of from 100 °C to 250 °C, from 110 °C to 220 °C, and/or from 115 °C to 220 °C. According to an exemplary embodiment, the crystalline block composite exhibits a second peak Tm in a range from 100 °C to 130 °C (e.g., 100 °C to 120 °C, 100 °C to 110 °C, etc.) and a first peak Tm in a range from 110 °C to 150 °C (e.g., 110 °C to 140 °C, 115 °C to 130 °C, 115 °C to 125 °C, etc.), in which the second peak Tm is less than the first peak Tm. [0063] The crystalline block composite may have a weight average molecular weight (Mw) from 10,000 g/mol to 2,500,000 g/mol, from 35000 g/mol to 1,000,000 g/mol, from 50,000 g/mol to 300,000 g/mol, and/or from 50,000 g/mol to 200,000 g/mol. For example, the Mw may be from 20 kg/mol to 1000 kg/mol, from 50 kg/mol to 500 kg/mol, and/or from 80 kg/mol to 125 kg/mol. The molecular weight distribution (Mw/Mn) or polydispersity of the crystalline block composites may be less than 5, between 1 and 5, and/or between 1.5 and 4. Weight average molecular weight (Mw) and number average molecular weight (Mn) are well known in polymer art and can be determined by methods known to a person of ordinary skill in the art.

[0064] The MFR (melt flow rate) of the crystalline block composites may be from 0.1 to 1000 dg/min (230°C/2.16 kg), from 1 to 500 g/10 min (230°C/2.16 kg), from 3 to 30 g/10 min (230°C/2.16 kg), and/or from 5 to 11 g/10 min (230°C/2.16 kg).

[0065] In accordance with ASTM D792, the density of the crystalline block composite may be between 0.850 and 0.920 g/cc (e.g., from 0.875 to 0.920 g/cc and/or from 0.890 to 0.910 g/cc).

Polymerization of BC, SBC, and CBC

[0066] The block composite, specified block composite, and crystalline block composite ("the composites") may be differentiated from conventional, random copolymers, physical blends of polymers, and block copolymers prepared via sequential monomer addition. The composites may be differentiated from random copolymers by characteristics such as higher melting temperatures for a comparable amount of comonomer, BCI, MBCI, CBCI, and microstructure index; from a physical blend by characteristics such as BCI, MBCI, CBCI, microstructure index, better tensile strength, improved fracture strength, finer morphology, improved optics, and/or greater impact strength at lower temperature; and from block copolymers prepared by sequential monomer addition by molecular weight distribution, rheology, shear thinning, rheology ratio, and in that there is block polydispersity. For example, the composites include block copolymers having distinct regions or segments (referred to as "blocks") joined in a linear manner. The blocks differ, e.g., in the type of crystallinity such as polyethylene (PE) versus polypropylene (PP). The block copolymers can be linear or branched. When produced in a continuous process, the composites may possess PDI from 1.7 to 15 (e.g., from 1.8 to 10, from 1.8 to 5, and/or from 1.8 to 3.5). When produced in a batch or semi-batch process, the composites may possess PDI from 1.0 to 2.9 (e.g., from 1.3 to 2.5, from 1.4 to 2.0, and/or from 1.4 to 1.8). Exemplary composites are described in, e.g., U.S. Patent Noa. 8,716,400, 8,802,774, and 8,822,598, which incorporated herein by reference with respect to, for example, processes to make them and methods of analyzing them.

[0002] The composites include the block copolymers possessing a most probable distribution of block lengths. The block copolymers may contain 2 or 3 blocks or segments. In a process for making the polymers of the composites, chain shuttling is used as a way to prolong the lifetime of a polymer chain such that a substantial fraction of the polymer chains exit at least the first reactor of a multiple reactor series or the first reactor zone in a multiple zoned reactor operating substantially under plug flow conditions in the form of polymer terminated with a chain shuttling agent, and the polymer chain experiences different polymerization conditions in the next reactor or polymerization zone. Different polymerization conditions in the respective reactors or zones include the use of different monomers, comonomers, or monomer/comonomer(s) ratio, different polymerization temperatures, pressures or partial pressures of various monomers, different catalysts, differing monomer gradients, or any other difference leading to formation of a distinguishable polymer segment. Thus, at least a portion of the polymer comprises two, three, or more, preferably two or three, differentiated polymer segments arranged intramolecularly.

[0003] The composites are prepared, e.g., by a process comprising contacting an addition polymerizable monomer or mixture of monomers under addition

polymerization conditions with a composition comprising at least one addition polymerization catalyst, a cocatalyst, and a chain shuttling agent. The process is characterized by formation of at least some of the growing polymer chains under differentiated process conditions in two or more reactors operating under steady state polymerization conditions or in two or more zones of a reactor operating under plug flow polymerization conditions.

[0004] Suitable processes useful in producing the composites may be found in, e.g. example, U.S. Patent Nos. 8,053,529, 8,686,087, and 8,716,400. The polymerization may be carried out as a continuous polymerization, e.g., a continuous-solution polymerization, in which catalyst components, monomers, and optionally solvent, adjuvants, scavengers, and/or polymerization aids are continuously supplied to one or more reactors or zones and polymer product continuously removed therefrom. Within the scope of the terms "continuous" and "continuously" as used in this context are those processes in which there are intermittent additions of reactants and removal of products at small regular or irregular intervals, so that, over time, the overall process is substantially continuous. Further, a chain shuttling agent(s) may be added at any point during the polymerization including in a first reactor or zone, at the exit or slightly before the exit of the first reactor, between the first reactor or zone and a second or any subsequent reactor or zone, or even solely to the second or any subsequent reactor or zone. Exemplary chain shuttling agents, catalysts, and cocatalysts are those disclosed in, e.g., U.S. Patent No. 7,951,882. For example, chain shuttling agents that are dialkyl zinc compounds may be used.

[0005] The catalyst may be prepared as a homogeneous composition by addition of the requisite metal complex or multiple complexes to a solvent in which the polymerization will be conducted or in a diluent compatible with the ultimate reaction mixture. The desired cocatalyst or activator and, optionally, the shuttling agent may be combined with the catalyst composition either prior to, simultaneously with, or after combination of the catalyst with the monomers to be polymerized and any additional reaction diluent.

[0006] Due to the difference in monomers, temperatures, pressures, or other differences in polymerization conditions between at least two of the reactors or zones connected in series, polymer segments of differing composition such as comonomer content, crystallinity, density, tacticity, regio-regularity, or other chemical or physical difference, within the same molecule are formed in the different reactors or zones. The size of each segment or block is determined by continuous polymer reaction conditions, and preferably is a most probable distribution of polymer sizes. Each reactor in the series can be operated under high pressure, solution, slurry, or gas phase

polymerization conditions.

[0007] In the following exemplary processes, continuous or substantially continuous polymerization conditions may be employed. In a multiple zone polymerization, all zones operate under the same type of polymerization, such as solution, slurry, or gas phase, but at different process conditions. For a solution polymerization process, it is desirable to employ homogeneous dispersions of the catalyst components in a liquid diluent in which the polymer is soluble under the polymerization conditions employed. A high pressure process may be carried out at temperatures from 100°C to 400°C and at pressures above 500 bar (50 MPa). A slurry process may use an inert hydrocarbon diluent and temperatures of from 0°C up to a temperature just below the temperature at which the resulting polymer becomes substantially soluble in the inert polymerization medium. Exemplary temperatures in a slurry polymerization are from 30°C and pressures may range from atmospheric (100 kPa) to 500 psi (3.4 MPa).

[0008] Without limiting in any way the scope of the embodiments, one means for carrying out such a polymerization process is as follows. In one or more well stirred tank or loop reactors operating under solution polymerization conditions, the monomers to be polymerized are introduced continuously together with any solvent or diluent at one part of the reactor. The reactor contains a relatively homogeneous liquid phase composed substantially of monomers together with any solvent or diluent and dissolved polymer. Exemplary solvents include C4-10 hydrocarbons or mixtures thereof, especially alkanes such as hexane or mixtures of alkanes, as well as one or more of the monomers employed in the polymerization. Catalyst along with cocatalyst and optionally chain shuttling agent are continuously or intermittently introduced in the reactor liquid phase or any recycled portion thereof at a minimum of one location.

[0009] The reactor temperature and pressure may be controlled by adjusting the solvent/monomer ratio, the catalyst addition rate, as well as by use of cooling or heating coils, jackets or both. The polymerization rate is controlled by the rate of catalyst addition. The content of a given monomer in the polymer product is influenced by the ratio of monomers in the reactor, which is controlled by manipulating the respective feed rates of these components to the reactor. The polymer product molecular weight is controlled, optionally, by controlling other polymerization variables such as the temperature, monomer concentration, or by the previously mentioned chain shuttling agent, or a chain terminating agent such as hydrogen. Connected to the discharge of the reactor, optionally by means of a conduit or other transfer means, is a second reactor, such that the reaction mixture prepared in the first reactor is discharged to the second reactor without substantially termination of polymer growth. Between the first and second reactors, a differential in at least one process condition is established. For example, use in formation of a copolymer of two or more monomers, the difference is the presence or absence of one or more comonomers or a difference in comonomer concentration. Additional reactors, each arranged in a manner similar to the second reactor in the series may be provided as well. Upon exiting the last reactor of the series, the effluent is contacted with a catalyst kill agent such as water, steam or an alcohol or with a coupling agent. The resulting polymer product is recovered by flashing off volatile components of the reaction mixture such as residual monomers or diluent at reduced pressure, and, if necessary, conducting further devolatilization in equipment such as a devolatilizing extruder.

[0010] Alternatively, the foregoing polymerization may be carried out in a plug flow reactor with a monomer, catalyst, shuttling agent, temperature or other gradient established between differing zones or regions thereof, optionally accompanied by separated addition of catalysts and/or chain shuttling agent, and operating under adiabatic or non-adiabatic polymerization conditions.

First Polyolefin Copolymer

[0067] In certain embodiments, the composition of the present disclosure includes from 20 wt% to 90 wt% (e.g., from 25 wt% to 85 wt%) of a first polyolefin copolymer. In embodiments, the first polyolefin copolymer is derived from ethylene and at least one of a C3 to C10 alpha-olefin or is derived from propylene and at least one of a C2 and C ₄ to Cio alpha-olefin. For example, the polyolefin copolymer may be an

ethylene-propylene copolymer, an ethylene-butylene copolymer, an ethylene-hexene copolymer, and/or an ethylene-octene copolymer. In embodiments, the first polyolefin copolymer has a melt index from 0.5 g/10 min to 1500 g/10 min (e.g., from 0.5 g/10 min to 100 g/10 min, from 1.0 g/10 min to 50 g/10 min, from 1.0 g/10 min to 25 g/10 min, and/or from 1.0 g/10 min to 15 g/10 min), according to ASTM D1238 and at 190 "C/2.16 kg. The first polyolefin copolymer has a relatively low density, according to ASTM D792, such that the density is from 0.850 g/cc to 0.910 g/cc, preferably from 0.850 g/cc to 0.885 g/cc, and more preferably from 0.850 g/cc to 0.875 g/cc. [0068] The first polyolefin copolymer may have a low glass transition temperature, e.g., less than -30 °C, less than -40 °C, and/or less than -50 °C.

[0069] The first polyolefin copolymer may have a weight average molecular weight (Mw), e.g., less than or equal to 150,000 g/mole, less than or equal to 80,000 g/mole, and/or less than or equal to 50,000 g/mole. The weight average molecular weight (Mw) may be greater than or equal to 30,000 g/mole, greater than or equal to 50,000 g/mole, and/or greater than or equal to 100,000 g/mole.

[0070] The first polyolefin copolymer may have an Mw/Mn of less than 5, preferably less than 4, and more preferably less than 3.

Second Polyolefin Copolymer

[0071] In certain embodiments, the composition of the present disclosure includes from 30 wt% to 60 wt% (e.g., from 35 wt% to 50 wt% and/or from 40 wt% to 50 wt%) of a second polyolefin copolymer. In embodiments, the second polyolefin copolymer is a high melt flow copolymer derived from ethylene and at least one of a C3 to C10 alpha- olefin or is derived from propylene and at least one of a C2 and C ₄ to C10 alpha-olefin. For example, the second polyolefin copolymer may be an ethylene-propylene copolymer, an ethylene-butylene copolymer, an ethylene-hexene copolymer, and/or an ethylene-octene copolymer. The second polyolefin copolymer has a relatively high melt index such that the melt index is from 100 g/10 min to 2000 g/10 min, according to ASTM D1238 and at 190 "C/2.16 kg. For example, the melt index may be from 100 g/10 min to 1500 g/10 min, 200 g/10 min to 1200 g/10 min, 300 g/10 min to 700 g/10 min, and/or 400 g/10 min to 600 g/10 min. The second polyolefin copolymer has a relatively low density, according to ASTM D792, such that the density is from 0.860 g/cc to 0.900 g/c, preferably from 0.860 g/cc to 0.885 g/cc, and more preferably from 0.860 g/cc to 0.875 g/cc.

[0072] The second polyolefin copolymer may have a low glass transition temperature, e.g., less than -30 °C, less than -40 °C, and/or less than -50 °C. The glass transition temperature (T _g ) may be greater than -80 °C. The Brookfield viscosity (@ 350°F/177°C) may be from 1,000 cP to 25,000 cP (e.g., from 3000 cP to 20,000 cP, from 5000 cP to 20,000 cP, from 10,000 cP to 20,000 cP, and/or from 15,000 cP to 20,000 cP).

[0073] The second polyolefin copolymer may have a low weight average molecular weight (Mw), e.g., less than or equal to 40,000 g/mole, less than or equal to 30,000 g/mole, and/or less than or equal to 25,000 g/mole. The weight average molecular weight (Mw) may be greater than or equal to 5000 g/mole, greater than or equal to 7000 g/mole, and/or greater than or equal to 10,000 g/mole.

[0074] The second polyolefin copolymer may have an Mw/Mn of less than 5, preferably less than 4, preferably less than 3.

Propylene Polymer Base

[0075] The composition includes from 60 wt% to 90 wt% of the propylene polymer base that has a melt flow rate from 2 g/10 min to 100 g/10 min (e.g., from 10 g/10 min to 80 g/10 min, from 20 g/10 min to 60 g/10 min, from 30 g/10 min to 50 g/10 min, and/or from 35 g/10 min to 45 g/10 min), according to ASTM D 1238 and at 230 "C/2.16 kg. The propylene polymer base may include one or more polypropylene based polymers that have a melt flow rate from 2 g/10 min to 100 g/10 min, according to ASTM D 1238 and at 230 "C/2.16 kg. In exemplary embodiments, the composition may consist essentially of the modifier and the propylene polymer base. The propylene polymer base may include a random copolymer polypropylene that has an ethylene content from 0.5 wt% to 5.0 wt%, based on the total weight of the random copolymer polypropylene. The propylene polymer base may include 95 wt% to 100 wt% of the random copolymer polypropylene based on the total weight of the propylene polymer base.

[0076] The propylene polymer base may have a density, in accordance with ASTM D792-00, Method 13, from 0.870 g/cm ³ to 0.910 g/cm ³ (e.g., from 0.880 g/cm ³ to 0.905 g/cm ³ , from 0.885 g/cm ³ to 0.905 g/cm ³ , and/or from 0.890 g/cm ³ to 0.905 g/cm ³ ). The propylene polymer base may consist of heterogeneous polypropylene or homogeneous polypropylene.

[0077] The propylene polymer base may be a propylene homopolymer, propylene based interpolymers, a random copolymer polypropylene (RCPP), an impact copolymer polypropylene (e.g., homopolymer propylene modified with at least one elastomeric impact modifier) (ICPP), a high impact polypropylene (HIPP), a high melt strength polypropylene (HMS-PP), an isotactic polypropylene (iPP), a syndiotactic

polypropylene (sPP), or a combination thereof. In exemplary embodiments, the propylene polymer base may be in the isotactic form of homopolymer polypropylene, although other forms of polypropylene may be used (e.g., syndiotactic or atactic).

[0078] The propylene polymer base is formed without the use of a chain shuttling agent, as discussed above with respect to the composites. Exemplary comonomers for polymerizing with propylene include ethylene, 1-butene, 1 pentene, 1-hexene, 1- heptene, 1-octene, 1-nonene, 1-decene, 1-unidecene, 1 dodecene, as well as 4-methyl-l- pentene, 4-methyl- 1-hexene, 5 -methyl- 1-hexene, vinylcyclohexane, and styrene.

Exemplary comonomers include ethylene, 1-butene, 1-hexene, and 1-octene.

Exemplary propylene based interpolymers include propylene/ethylene, propylene/1- butene, propylene/ 1-hexene, propylene/4-methyl- 1 -pentene, propylene/1 -octene, propylene/ethylene/ 1 -butene, propylene/ethylene/ENB , propylene/ethylene/ 1 -hexene, propylene/ethylene/ 1-octene, propylene/styrene, and propylene/ethylene/styrene.

Optionally, the propylene polymer base includes a monomer having at least two double bonds such as dienes or trienes.

[0079] An exemplary discussion of various polypropylene polymers is contained in Modern Plastics Encyclopedia/89, mid October 1988 Issue, Volume 65, Number 11, pp. 86-92, the entire disclosure of which is incorporated herein by reference. Examples of such propylene based polymers include VERSIFY™ (available from The Dow Chemical Company), Vistamaxx™ (available from Exxon Mobil), INSPIRE™

(available from Braskem), and Pro-Fax (available from LyondellBasell).

[0080] In exemplary embodiments, the propylene polymer base may be a propylene-alpha-olefin copolymer, which is characterized as having substantially isotactic propylene sequences. "Substantially isotactic propylene sequences" means that the sequences have an isotactic triad (mm) measured by ¹³ C NMR of greater than 0.85; in the alternative, greater than 0.90; in another alternative, greater than 0.92; and in another alternative, greater than 0.93. [0081] The propylene polymer base may contain LCB. For example, the propylene polymer base may contain an average of at least 0.001, an average of at least 0.005 and/or an average of at least 0.01, long chain branches/1000 total carbons. The term long chain branch, as used herein, refers to a chain length of at least one (1) carbon more than a short chain branch, and short chain branch, as used herein with regard to propylene/alpha-olefin copolymers, refers to a chain length of two (2) carbons less than the number of carbons in the comonomer. For example, a propylene/l-octene interpolymer has backbones with long chain branches of at least seven (7) carbons in length, but these backbones also have short chain branches of only six (6) carbons in length.

[0082] The propylene polymer base may include clarifying and/or nucleating agents therewithin. For example, clarifying and/or nucleating agents may alter the way polypropylene chains crystallize and agglomerate in a molten state. These agents may increase the onset of crystallization temperature. Clarifying agents (or clarifiers) are usually organic, non-polymeric molecules. The clarifying generally also may act as nucleating agents, but nucleating agents are not necessarily clarifying agents.

Exemplary clarifiers are chemical derivatives of dibenzylidene sorbitol and have melting temperatures within the processing window of polypropylene resins.

Nucleating agents generally are inorganic materials with a small average particle size and a high melting point. When a nucleated resin is melted in an extruder, the nucleating agent may typically remain solid and provide a site around which polypropylene spherulites can form. Exemplary nucleating agents are chemical derivatives of benzoic acid. For example, the nucleating agent may be sodium benzoate, kaolin, and/or talc.

[0083] The composition may be used in the manufacture of durable containers for applications requiring low temperature (such as sub-ambient and/or below 0 °C) mechanical. The containers may be suitable for use in food and beverage consumer markets. Exemplary container based applications that may benefit from the improved balance of impact, clarity, and modulus include food packaging (such as ice cream containers and puncture resistance bags) for low temperature mechanical properties, beverage bottles, and clear heavy duty shipping sacks. Composition

[0084] According to embodiments, the present disclosure is directed to a composition for forming high clarity-low temperature use containers that includes at least a propylene polymer base and a modifier and to containers/films formed using the composition thereof.

[0085] The composition includes from 10 wt% to 40 wt% of the modifier, based on the total weight of the composition. The composites (block composite, specified block composite, or crystalline block composite), the first polyolefin copolymer, and optionally the second polyolefin copolymer of the modifier may be dry blended or pre- blended prior to blending the modifier with propylene polymer base such that the composition includes the modifier finely dispersed in polypropylene. In another exemplary embodiment, the components of the modifier blend may be individually added at the time of preparation of the article, by feeding the propylene polymer base along with the modifier blend components together into an extruder in one-step to form a modified propylene. In another exemplary embodiment, the modified propylene may be prepared by melt blending all of the individual components of the modifier blend along with the propylene polymer base together and then pelletized for a ready-to-feed modified propylene. This pelletized modified propylene may then be fed directly into a process, e.g., to for an article by injection molding.

[0086] The modifier includes from 10 wt% to 50 wt% a block composite, specified block composite, or crystalline block composite. The modifier further includes from 20 wt% to 90 wt% of a first polyolefin copolymer that has a relatively low density. The modifier may optionally include from 30 wt% to 60 wt% of a second polyolefin copolymer that has a high melt flow and a relatively low density.

[0087] With respect to the composition, without intending to be bound by this theory, the blend of the propylene polymer base (e.g., such as a polypropylene homopolymer) and the block copolymer that has a continuous polypropylene phase would result in relatively smaller and discrete rubber domains in comparison to a simple polypropylene/elastomer blend. If the rubber domain sizes are smaller than the wavelengths of visible light (400-700 nm), less scattering of the light would occur, and the polymer/resultant article would maintain clarity. Further, the block copolymer would compatibilize rubber such that the propylene polymer base could be considered impact-modified with improved toughness at low temperatures such as the temperature inside a typical freezer. Accordingly, the resultant composition would have improved impact modification while still providing light transmittance similar to that which is realized with a polypropylene homopolymer. For example, the modifier may have the features of being readily compatible and dispersible in polypropylene, remains clear in polypropylene, and results in a composition adapted to form an article that provides sufficient impact toughness at freezer temperatures.

[0088] The polymer blends may be used to prepare containers with known polymer processes such as extrusion (e.g., sheet extrusion and profile extrusion); molding (e.g., injection molding, rotational molding, and blow molding); and blown film and cast film processes. For example, in general, extrusion is a process by which a polymer is propelled continuously along a screw through regions of high temperature and pressure where it is melted and compacted, and finally forced through a die. The extruder may be a single screw extruder, a multiple screw extruder, a disk extruder or a ram extruder. The die may be a film die, blown film die, sheet die, pipe die, tubing die or profile extrusion die. Injection molding is used for manufacturing a variety of plastic parts for various applications. Typically, injection molding is a process by which a polymer is melted and injected at high pressure into a mold, which is the inverse of the desired shape, to form parts of the desired shape and size. The mold can be made from metal, such as steel and aluminum. Molding is generally a process by which a polymer is melted and led into a mold, which is the inverse of the desired shape, to form parts of the desired shape and size. Molding may be pressureless or pressure-assisted. In exemplary embodiments, the containers are prepared using injection molding.

[0089] The temperature of forming the polymer blend of the modifier with the propylene polymer base may be above the melting temperature of the propylene polymer base. For example, the temperature may be from 150 °C to 250 °C and/or from 200 °C to 225 °C, in order to form a homogeneous melt blend. The temperature for forming the modifier, when pre-blended, may be from 150 °C to 200 °C. For example, the temperature for pre -blending the modifier may be lower than the temperature for form the polymer blend with the modifier and the propylene polymer base. The polymer blend with the modifier and the propylene polymer base may have a relatively low viscosity blend (compared to traditional modifiers in polypropylene), may operate at a lower temperature, may operate at a lower cycle time, may provide improved uniformity in a resultant part, and/or may provide better homogenous blend with improved balance of clarity and impact properties.

[0090] The compositions of the present disclosure can optionally include one or more additives and/or fillers. Non-limiting examples of additives and/or fillers include plasticizers, thermal stabilizers, light stabilizers (e.g., UV light stabilizers and absorbers), antioxidants, slip agents, process aids, optical brighteners, antistats, lubricants, catalysts, rheology modifiers, biocides, corrosion inhibitors, dehydrators, organic solvents, colorants (e.g., pigments and dyes), surfactants, demolding additives, mineral oil, antiblocking agents, nucleating agents, flame retardants, reinforcing fillers (e.g., glass, fibers, anti-scratch additives, talc, calcium carbonate, mica, glass fibers, whisker, etc.), processing aids, metal fibers, boron fibers, ceramic fibers, polymeric fibers, kaolin, glass, ceramic, carbon/polymeric microspheres, silica, mica, carbon fibers, clay, hemp fibers, and combinations thereof.

Examples

Test Methods

[0091] Density is measured in accordance with ASTM D792. The result is reported in gamma (g) per cubic centimeter, or g/cm ³ .

[0092] Melt Index (b) is measured in accordance with ASTM D-1238 (190°C; 2.16 kg). The result is reported in grams/10 minutes.

[0093] Melt flow rate (MFR) is measured in accordance with ASTM D-1238 (230°C; 2.16 kg). The result is reported in grams/10 minutes.

[0094] Tensile Properties, including tensile stress at break and tensile elongation at break, are measured according to ASTM D638.

[0095] Secant Flexural Modulus, including Flex 1% and Flex 2%, is measured according ASTM D790. [0096] Percent Clarity, Percent Haze, and Percent Transmittance are measured using BYK Gardner Haze-gard as specified in ASTM D1746.

[0097] Izod Impact, including at 23 °C, at 0 °C, and -20 °C, are measured according to ASTM D256, at a thickness as indicated in the respective examples. Samples are preparing by injection molding.

[0098] Charpy Impact is based on ISO 170 for Determination of Charpy Impact Properties. It calculates the impact energy absorbed by a specimen after windage and friction loss has automatically been determined. Ten specimens are die cut from a molded plaque. Specimens are approximately 80 mm in length and 10 mm in width.

[0099] Differential Scanning Calorimetry (DSC) is performed on a TA Instruments Q100 DSC V9.8 Build 296 using Universal V3.7A analysis software from TA

Instruments. Samples are rapidly heated to 230° C. and held isothermally for 3 minutes in order to remove any previous heat history. The sample are then cooled to -90° C. at 10° C./minute cooling rate and held at -90° C. for 3 minutes. The first cooling and second heating curves are recorded. The percent crystallinity is calculated by dividing the heat of fusion (H ), determined from the second heat curve, by a theoretical heat of fusion of 292 J/g for PE (165 J/g, for PP), and multiplying this quantity by 100 (for example, % cryst. = (H _f / 292 J/g) x 100 (for PE)).

[00100] Unless otherwise stated, melting point(s) (T _m ) of each polymer is determined from the second heat curve (peak Tm), and the crystallization temperature ( _c ) is determined from the first cooling curve (peak Tc). With respect to DSC, the temperature at the maximum heat flow rate with respect to a linear baseline is used as the melting point. The linear baseline is constructed from the beginning of the melting (above the glass transition temperature) and to the end of the melting peak.

[00101] High Temperature Liquid Chromatography: High Temperature Liquid Chromatography Experimental Method Instrumentation is the HTLC experiment, which is done according to the published method with minor modifications (Lee, D.; Miller, M. D.; Meunier, D. M.; Lyons, J. W.; Bonner, J. M.; Pell, R. J.; Shan, C. L. P.; Huang, T. /. Chromatogr. A 2011, 1218, 7173). Two Shimadzu (Columbia, MD, USA) LC-20AD pumps are used to deliver decane and trichlorobenzene (TCB) respectively. Each pump is connected to a 10: 1 fixed flow splitter (Part #: 620-PO20-HS, Analytical Scientific Instruments Inc., CA, USA). The splitter has a pressure drop of 1500 psi at 0.1 mL/min in ¾0 according to the manufacturer. The flow rates of both pumps are set at 0.115 mL/min. After the splitting, the minor flow is 0.01 mL/min for both decane and TCB, determined by weighing the collected solvents for more than 30min. The volume of the collected eluent is determined by the mass and the densities of the solvents at room temperature. The minor flow is delivered to the HTLC column for separation. The main flow is sent back to the solvent reservoir. A 50-μί mixer (Shimadzu) is connected after the splitters to mix the solvents from Shimadzu pumps. The mixed solvents are then delivered to the injector in the oven of Waters (Milford, MA, USA) GPCV2000. A Hypercarb™ column (2.1 x 100 mm, 5 μιη particle size) is connected between the injector and a 10-port VICI valve (Houston, TX, USA). The valve is equipped with two όθ-μί sample loops. The valve is used to continuously sample eluent from the first dimension (Dl) HTLC column to the second dimension (D2) SEC column. The pump of Waters GPCV2000 and a PLgel Rapid™-M column (10 x 100 mm, 5 μιη particle size) are connected to the VICI valve for D2 size exclusion chromatography (SEC). The symmetric configuration is used for the connections as described in the literature (Brun, Y.; Foster, P. /. Sep. Sci. 2010, 33, 3501). A dual-angle light scattering detector (PD2040, Agilent, Santa Clara, CA, USA) and an IR5 inferred absorbance detector are connected after the SEC column for measurement of concentration, composition, and molecular weight.

[00102] Separation for HTLC: Approximately 30 mg are dissolved in 8-mL decane by gently shaking the vial at 160 °C for 2 hours. The decane contains 400 ppm

BHT(2,6-Di-tert-butyl-4-methylphenol) as the radical scavenger. The sample vial is then transferred to the autos ampler of GPCV2000 for injection. The temperatures of the autosampler, the injector, both the Hypercarb and the PLgel columns, the 10-port VICI valve, and both the LS and IR5 detectors are maintained at 140 °C throughout the separation.

[00103] The initial conditions before injection are as follows. The flow rate for the HTLC column is 0.01 mL/min. The solvent composition in the Dl Hypercarb column is 100% decane. The flow rate for the SEC column is 2.51 mL/min at room temperature. The solvent composition in the D2 PLgel column is 100% TCB. The solvent composition in the D2 SEC column does not change throughout the separation.

[00104] A 311-μΕ aliquot of sample solution is injected into the HTLC column. The injection triggers the gradient described below:

From 0 - 10 min, 100% decane/ 0% TCB;

From 10 - 651 min, TCB is increased linearly from 0% TCB to 80% TCB. The injection also triggers the collection of the light scattering signal at 15° angle (LS15) and the "measure" and "methyl" signals from IR5 detector (IRmeasure and

IRmethyi) using EZChrom™ chromatography data system (Agilent). The analog signals from detectors are converted to digital signals through a SS420X analog-to-digital converter. The collection frequency is 10 Hz. The injection also triggers the switch of the 10-port VICI valve. The switch of the valve is controlled by the relay signals from the SS420X converter. The valve is switched every 3 min. The chromatograms are collected from 0 to 651 min. Each chromatogram consist of 651/3 = 217 SEC chromatograms.

[00105] After the gradient separation, 0.2 mL of TCB and 0.3 mL of decane are used to clean and re-equilibrate the HTLC column for next separation. The flow rate of this step is 0.2 mL/min, delivered by a Shimadzu LC-20 AB pump connected to the mixer.

[00106] Data Analysis for HTLC: The 651 min raw chromatogram is first unfolded to give 217 SEC chromatograms. Each chromatogram is from 0 to 7.53 mL in the unit of 2D elution volume. The integration limit is then set and the SEC chromatograms undergo spike removal, baseline correction, and smoothing. The process is similar to batch analysis of multiple SEC chromatograms in conventional SEC. The sum of all the SEC chromatograms is inspected to ensure both left side (upper integration limit) and right side (lower integration limit) of the peak were at the baseline as zero.

Otherwise, the integration limit is adjusted to repeat the process.

[00107] Each SEC chromatogram n from 1 to 217 yields an X-Y pair in the HTLC chromatogram, where n is the fraction number: Xn = elution volume (mL) = Dl flow rate x n x t _SW itch

where iswitch = 3min is the switch time of the 10-port VICI valve.

peak end

Y _n = signal intensity (Voltage) = ∑/R_ _e> „

peak start

[00108] The above equation uses /Rmeasure signal as the example. The obtained HTLC chromatogram shows the concentrations of the separated polymeric components as a function of elution volume. The normalized /Rmeasure HTLC chromatogram is shown in Figure 9 with Y represented by dW/dV, meaning the normalized weight fractions with respect to the elution volume.

[00109] X-Y pairs of data are also obtained from /Rmethyi and LSI 5 signals. The ratio of 7R _m ethyi/ Rmeasure is used to calculate composition after calibration. The ratio of LS15//Rmeasure is used to calculate weight-average molecular weight ( _w ) after calibration.

[00110] Calibration follows the procedures of Lee et al., ibid. High density polyethylene (HDPE), isotactic polypropylene (z ^' PP), and ethylene-propylene copolymer with propylene contents of 20.0, 28.0, 50.0, 86.6, 92.0, and 95.8 wt% P are used as the standards for 7R _m ethyi/ Rmeasure calibration. The composition of the standards are determined by NMR. The standards are run by SEC with IR5 detector. The obtained ZRmethyi//Rmeasure ratios of the standards are plotted as a function of their compositions, yielding the calibration curve.

[00111] The HDPE reference is used for routine LS15 calibration. The M _w of the reference is predetermined by GPC as 104.2 kg/mol with LS and RI (refractive index) detectors. GPC uses NBS 1475 as the standard in GPC. The standard has a certified value of 52.0 kg/mol by NIST. Between 7 to 10 mg of the standard is dissolved in 8- mL decane at 160 °C. The solution is injected to the HTLC column in 100% TCB. The polymer is eluted under constant 100% TCB at 0.01 mL/min. Therefore, the peak of the polymer appears at the HTLC column void volume. A calibration constant, Ω, is determined from the total LS15 signals (ALSIS) and the total /Rmeasure signals

( AlR ₅ measure) · A

Ω = ^L L,S15

A I, R, measure M' w

[00112] The experimental LS 15/IR, measure ratio is then converted to M _w through Ω.

[00113] By way of example, three HTLC chromatograms are shown in FIG. 11. The black chromatogram is for Comparative BCN1 (i.e., CBCN1). The red chromatogram is for the blend of z ^' PP and TAFMER™ P-0280 (an ethylene/alpha-olefin copolymer product available from Mitsui Chemicals). The blue chromatogram is for the blend of VERSIFY™ 2400 (a propylene-ethylene copolymer available from The Dow Chemical Company) and TAFMER™ P-0280. The dashed line is a linear regression fit of the chemical compositions of iPP, VERSIFY™ 2400, and TAFMER™ P-0280 versus their peak elution volumes. Note that VERSIFY™ 2400 has two peaks. The composition and elution volume of the main peak is used for the linear fit. The three polymers all have Mw above 80,000 Daltons.

[00114] Transmission Electron Microscopy (TEM) is for morphology determination. The center location of each injection molded chip was isolated and trimmed so that sections could be collected at the core (slide 4). The trimmed samples were

cryopolished prior to staining by removing sections from the blocks at -60°C to prevent smearing of the elastomer phases. The cryo-polished blocks were stained with the vapor phase of a 2% aqueous ruthenium tetraoxide solution for 3hrs at ambient temperature. The staining solution was prepared by weighing 0.2gm of ruthenium (III) chloride hydrate (RuCb x H2O) into a glass bottle with a screw lid and adding 10ml of 5.25% aqueous sodium hypochlorite to the jar. The samples were adhered to a glass slide having double sided tape and placed in a glass bottle. The slide was placed in the bottle in order to suspend the blocks about 1 inch above the staining solution and tightly closed. Sections of approximately 90 nanometers in thickness were collected at ambient temperature using a diamond knife on a Leica EM UC7 microtome and placed on 400 mesh virgin TEM grids for observation.

[00115] Image Collection - Images were collected on a JEOL JEM- 1230 operated at lOOkV accelerating voltage and collected on a Gatan-791 and 794 digital cameras. The images were post processed using Adobe Photoshop 7.0. [00116] Xylene Soluble Fractionation Analysis: is performed by using a weighed amount of resin is dissolved in 200 ml o-xylene under reflux conditions for 2 hours. The solution is then cooled in a temperature controlled water bath to 25 °C to allow the crystallization of the xylene insoluble (XI) fraction. Once the solution is cooled and the insoluble fraction precipitates from the solution, the separation of the xylene soluble (XS) fraction from the xylene insoluble fraction is done by filtration through a filter paper. The remaining o-xylene solution is evaporated from the filtrate. Both XS and XI fractions are dried in a vacuum oven at 100°C for 60 min and then weighed.

[00117] ¹³ C Nuclear Magnetic Resonance (NMR) involves the following:

[00118] Sample Preparation: The samples are prepared by adding approximately 2.7g of a 50/50 mixture of tetrachloroethane-d2/orthodichlorobenzene that is 0.025M in chromium acetylacetonate (relaxation agent) to 0.21g sample in a 10mm NMR tube. The samples are dissolved and homogenized by heating the tube and its contents to 150°C.

[00119] Data Acquisition Parameters: The data is collected using a Bruker 400 MHz spectrometer equipped with a Bruker Dual DUL high-temperature

CryoProbe. The data is acquired using 320 transients per data file, a 7.3 sec pulse repetition delay (6 sec delay + 1.3 sec acq. time), 90 degree flip angles, and inverse gated decoupling with a sample temperature of 125 °C. All measurements are made on non spinning samples in locked mode. Samples are homogenized immediately prior to insertion into the heated (130°C) NMR Sample changer, and are allowed to thermally equilibrate in the probe for 15 minutes prior to data acquisition.

[00120] Comonomer content in composite polymers may be measured using any suitable technique, with techniques based on nuclear magnetic resonance (NMR) spectroscopy preferred.

[00121] Gel Permeation Chromatography (GPC): The gel permeation

chromatographic system consists of either a Polymer Laboratories Model PL-210 or a Polymer Laboratories Model PL- 220 instrument. The column and carousel compartments are operated at 140 °C. Three Polymer Laboratories 10-micron Mixed-B columns are used. The solvent is 1 ,2,4 trichlorobenzene. The samples are prepared at a concentration of 0.1 grams of polymer in 50 milliliters of solvent containing 200 ppm of butylated hydroxytoluene (BHT). Samples are prepared by agitating lightly for 2 hours at 160°C. The injection volume used is 100 microliters and the flow rate is 1.0 ml/minute.

[00122] Calibration of the GPC column set is performed with 21 narrow molecular weight distribution polystyrene standards with molecular weights ranging from 580 to 8,400,000, arranged in 6 "cocktail" mixtures with at least a decade of separation between individual molecular weights. The standards are purchased from Polymer Laboratories (Shropshire, UK). The polystyrene standards are prepared at 0.025 grams in 50 milliliters of solvent for molecular weights equal to or greater than 1,000,000, and 0.05 grams in 50 milliliters of solvent for molecular weights less than 1,000,000. The polystyrene standards are dissolved at 80°C with gentle agitation for 30 minutes. The narrow standards mixtures are run first and in order of decreasing highest molecular weight component to minimize degradation. The polystyrene standard peak molecular weights are converted to polyethylene molecular weights using the following equation (as described in Williams and Ward, J. Polym. Sci., Polym. Let., 6, 621

(1968)): Mpolypropylene = 0.645(M _po lystyrene).

[00123] Polypropylene equivalent molecular weight calculations are performed using Viscotek TriSEC software Version 3.0.

Preparation of Block Composite, Specified Block Composite, and Crystalline Block Composite

[00124] Block Composite (BC) and Specified Block Composite (SBC) samples are produced using a catalyst fed simultaneously into two reactors.

[00125] Each of the BC and SBC samples includes (i) an ethylene-propylene polymer, (ii) an isotactic propylene polymer, and (iii) a block copolymer including an ethylene-propylene soft block that has a same composition as the ethylene-propylene polymer and an isotactic polypropylene hard block that has a same composition as the isotactic propylene polymer. With respect to the block copolymers, the ethylene- propylene soft block is produced in the first reactor and the isotactic propylene hard block is produced in the second reactor. The split between soft and hard block in the block copolymer of the BC is approximately 50/50. The split between soft and hard block in the block copolymer of the SBC is approximately 50/50.

[00126] The BC and SBC samples are prepared using two continuous stirred tank reactors (CSTR) connected in series and using a catalyst fed simultaneously into both reactors. The soft blocks are produced in the first reactor and the hard block are produced in the second reactor. Each reactor is hydraulically full and set to operate at steady state conditions. In particular, the BC and SBC are prepared by flowing monomers, Catalyst, Cocatalyst-1, Cocatalyst-2, and SA (as a chain shuttling agent) according to the process conditions outlined in Table 1, below. Two port injectors are used to feed the Catalyst, Cocatalyst-1, Cocatalyst-2, and SA (shuttling agent) -1, separately into the reactors. For preparation of the BC and SBC, the Catalyst is ([[rel- 2',2"'-[(lR,2R)-l,2-cylcohexanediylbis(methyleneoxy-KO)] bis[3-(9H-carbazol-9-yl)-5- methyl[l,l'-biphenyl]-2-olato-KO]](2-)]dimethyl-hafnium). The Cocatalyst-1 is a mixture of methyldi(Ci4-i8 alkyl)ammonium salts of tetrakis(pentafluorophenyl)borate, prepared by reaction of a long chain trialkylamine (Armeen™ M2HT, available from Akzo-Nobel, Inc.) are used. The Cocatalyst-2 is mixed C14-18 alkyldimethylammonium salt of bis(tris(pentafluorophenyl)-alumane)-2-undecylimidazolide, prepared according to U.S. Patent No. 6,395,671, Ex. 16. The SA is a solution of diethylzinc (DEZ) that may contain 1-3 mol% of modified methylalumoxane (MMAO-3A) from Akzo Nobel Chemicals. Upon exiting the reactor, water and/or additives may be injected into the polymer solution.

[00127] The process conditions for producing the BC and SBC samples are as follows:

Table 1

[00128] The characteristics of the BC and SBC samples are shown below in Table 2.

Table 2

[00129] The CBC sample is synthesized in dual reactors in series, using a similar method as described above with the BC and SBC samples. The CBC sample includes (i) an ethylene-propylene polymer, (ii) an isotactic polypropylene polymer, and (iii) a block copolymer including an ethylene-propylene block that has a same composition as the ethylene-propylene polymer and an isotactic polypropylene block that has a same composition as the isotactic polypropylene polymer. The split between the EP and iPP blocks in the block copolymer of the CBC is approximately 50/50. The measured properties of the CBC samples are provided below in Table 3.

Table 3

Block Composite Index Calculations

[0011] The term Block Composite Index (BCI) is herein defined to equal the weight percentage of the block copolymer divided by 100% (i.e., weight fraction). The value of the BCI can range from 0 up to 1.0, where 1.0 would be equal to 100% of the block copolymer and zero would be for material such as a traditional blend or random copolymer. Said in another way, for an insoluble fraction, the BCI is 1.0, and for a soluble fraction, the BCI is assigned a value of zero. The following is a description for estimating the block composite index.

[0012] Estimation of Block Composite Index is based on showing that the insoluble fractions contain an appreciable amount of ethylene that would not otherwise be present if the polymer was simply a blend of iPP homopolymer and EP copolymer. To account for this "extra ethylene", a mass balance calculation can be performed to estimate a block composite index from the amount of xylene insoluble and soluble fractions and the weight % ethylene present in each of the fractions.

[0013] A summation of the weight % ethylene from each fraction according to equation 1 results in an overall weight % ethylene (in the polymer). This mass balance equation can also be used to quantify the amount of each component in a binary blend or extended to a ternary, or n-component blend.

^{Wt %} C2overall = ^W In _S oluble(^ ^%C2 / _nS0 lub _te ) + ^W soluble ( ^Wt%C2 soluMe ) _Pn Wt % C2 _0verall - W _WPHlai (wt%C2 _ipp ) + W _{EP soft} ( Vi%C2 _£fto/i ) _E ^ ₂

[0014] Applying equations 2 through 4, the amount of the soft block (providing the source of the extra ethylene) present in the insoluble fraction is calculated. By substituting the weight % C2 of the insoluble fraction in the left hand side of equation 2, the weight % iPP hard and weight % EP soft can be calculated using equations 3 and 4. Note that the weight % of ethylene in the EP soft is set to be equal to the weight % ethylene in the xylene soluble fraction. The weight % ethylene in the iPP block is set to zero or if otherwise known from its DSC melting point or other composition measurement, the value can be put into its place.

_ ^{Wt % C 2} xylenein _S o lMe - ^{Wt % C l} EPsoft

Wt% C2 _ipphard - Wt%Cl _{EPsoft 3}

[0015] After accounting for the 'additional' ethylene present in the insoluble fraction, the only way to have an EP copolymer present in the insoluble fraction, the EP polymer chain must be connected to an iPP polymer block (or else it would have been extracted into the xylene soluble fraction). Thus, when the iPP block crystallizes, it prevents the EP block from solubilizing.

[0016] To estimate the block composite index, the relative amount of each block must be taken into account. To approximate this, the ratio between the EP soft and iPP hard is used. The ratio of the EP soft polymer and iPP hard polymer can be calculated using Equation 2 from the mass balance of the total ethylene measured in the polymer. Alternatively it could also be estimated from a mass balance of the monomer and comonomer consumption during the polymerization. The weight fraction of iPP hard and weight fraction of EP soft is calculated using Equation 2 and assumes the iPP hard contains no ethylene. The weight % ethylene of the EP soft is the amount of ethylene present in the xylene soluble fraction.

[0017] The corresponding BCI calculations for BC are provided in Table 4, below.

Table 4 2 wt C2 in PP block/polymer Measured 0.5

3 wt C2 in EP block/polymer Measured 65

4 wt fraction iPP (in block or polymer) Calc. 0.457

5 wt fraction EP (in block or polymer) Calc. 0.543

6 Analysis of HTLC Separation

7 wt fraction xylene soluble Measured 0.281 *

8 wt fraction xylene insoluble Measured 0.719*

9 wt C2 in xylene insoluble Measured 24.0**

10 wt fraction PP in insoluble Calc. 0.636

11 wt fraction EP in insoluble fraction 1-Line 10 0.364

12 wt fraction Diblock in insoluble fraction Line 11 Line 5 0.671

13 Block Composite Index (BCI) Calc 0.482

*Estimated from CEF

** Estimated mass balance

Modified Block Composite Index and Crystalline Block Composite Indexes

[00130] CBCI and MBCI provide an estimate of the quantity of block copolymer within the crystalline and specified block composites under the assumption that the ratio of CEB/EB to CAOB/AOB within the diblock is the same as the ratio of ethylene to alpha-olefin in the overall block composite. This assumption is valid for these statistical olefin block copolymers based on the understanding of the individual catalyst kinetics and the polymerization mechanism for the formation of the diblocks via chain shuttling catalysis as described in the specification. This CBCI and MBCI analysis shows that the amount of isolated PP is less than if the polymer was a simple blend of a propylene homopolymer (in this example the CAOP/AOP) and polyethylene (in this example the CEP/EP). Consequently, the polyethylene fraction contains an appreciable amount of propylene that would not otherwise be present if the polymer was simply a blend of polypropylene and polyethylene. To account for this "extra propylene", a mass balance calculation can be performed to estimate the CBCI/MBCI from the amount of the polypropylene and polyethylene fractions and the weight % propylene present in each of the fractions that are separated by HTLC.

[00131] The corresponding calculations for CBC and SBC are provided in Table 5, below. Table 5

[00132] Referring to Table 5, above, the CBCI/MBCI is measured by first determining a summation of the weight % propylene from each component in the polymer according to Equation 1 , below, which results in the overall weight % propylene/C3 (of the whole polymer). This mass balance equation can be used to quantify the amount of the PP and PE present in the block copolymer. This mass balance equation can also be used to quantify the amount of PP and PE in a binary blend or extended to a ternary, or n-component blend. For the CBCs and SBCs, the overall amount of PP or PE is contained within the blocks present in the block copolymer and the unbound PP and PE polymers. Wt% C3, Overall = w _pp (wt%C3 _PP ) + w _PE (wt%C3 _PE ) Eq. l where

Wpp = weight fraction of PP in the polymer

= weight fraction of PE in the polymer

wt C3pp = weight percent of propylene in PP component or block

wt C3p _E = weight percent of propylene in PE component or block

[00133] Note that the overall weight % of propylene (C3) is measured from C ¹³ NMR or some other composition measurement that represents the total amount of C3 present in the whole polymer. The weight % propylene in the PP block (wt%C3pp) is set to 100 (if applicable) or if otherwise known from its DSC melting point, NMR measurement, or other composition estimate, that value can be put into its place.

Similarly, the weight % propylene in the PE block (wt%C3pE) is set to 100 (if applicable) or if otherwise known from its DSC melting point, NMR measurement, or other composition estimate, that value can be put into its place.

[00134] Calculating the Ratio of PP to PE in the crystalline block composite and/or the specified block composite: Based on Equation 1, the overall weight fraction of PP present in the polymer can be calculated using Equation 2 from the mass balance of the total C3 measured in the polymer. Alternatively, it could also be estimated from a mass balance of the monomer and comonomer consumption during the polymerization. Overall, this represents the amount of PP and PE present in the polymer regardless of whether it is present in the unbound components or in the block copolymer. For a conventional blend, the weight fraction of PP and weight fraction of PE corresponds to the individual amount of PP and PE polymer present. For the crystalline block composite and the specified block composite, it is assumed that the ratio of the weight fraction of PP to PE also corresponds to the average block ratio between PP and PE present in this statistical block copolymer. wt%C Overall - wt%C PE

W P, P Eq. 2 wt% C3 _PP - wt%C PE where wpp = weight fraction of PP present in the whole polymer wt C3pp = weight percent of propylene in PP component or block wt C3p _E = weight percent of propylene in PE component or block

[00135] To estimate the amount of the block copolymer (diblock) in the Crystalline Block Composite and/or the Specified Block Composite, apply Equations 3 through 5, and the amount of the isolated PP that is measured by HTLC analysis is used to determine the amount of polypropylene present in the diblock copolymer. The amount isolated or separated first in the HTLC analysis represents the 'unbound PP' and its composition is representative of the PP block present in the diblock copolymer. By substituting the overall weight % C3 of the whole polymer in the left hand side of Equation 3, and the weight fraction of PP (isolated from HTLC) and the weight fraction of PE (separated by HTLC) into the right hand side of Equation 3, the weight % of C3 in the PE fraction can be calculated using Equations 4 and 5. The PE fraction is described as the fraction separated from the unbound PP and contains the diblock and unbound PE. The composition of the isolated PP is assumed to be the same as the weight % propylene in the PP block as described previously. wt % C3 _0verall = w _Wisolited (wt%C3 _PP ) + ^ _m.faction (wt%C3 _PE _ _fractlon ) Eq. 3

_^tC r r^ ^{Wt %C3} Overall ~ PPtsolated (wt%C3 _pp )

^{Wt % 3} PE- fraction = ^EC I · ⁴

^ PE— fraction

^W PE- fraction ^~ ~ ^W PPisolated Eq. 5 where wppisoiated = weight fraction of isolated PP from HTLC wpE-fraction = weight fraction of PE separated from HTLC, containing the diblock and unbound

PE wt C3pp = weight % of propylene in the PP; which is also the same amount of propylene present in the PP block and in the unbound PP wt C3p _E -fraction— WC1 ght % of propylene in the PE-fraction that was separated by HTLC wt C3overaii = overall weight % propylene in the whole polymer

[00136] The amount of wt% C3 in the polyethylene fraction from HTLC represents the amount of propylene present in the block copolymer fraction that is above the amount present in the 'unbound polyethylene'. To account for the 'additional' propylene present in the polyethylene fraction, the only way to have PP present in this fraction is for the PP polymer chain to be connected to a PE polymer chain (or else it would have been isolated with the PP fraction separated by HTLC). Thus, the PP block remains adsorbed with the PE block until the PE fraction is separated.

[00137] The amount of PP present in the diblock is calculated using Equation 6. wt%C3 _PE _ _fractlon - wt%C3 _PE

Eq. 6 wt% C3 _PP - wt%C3 _PE

Where wt C3pE-fraction = weight % of propylene in the PE-fraction that was separated by HTLC (Equation 4) wt C3pp = weight % of propylene in the PP component or block (defined previously) wt C3pE = weight % of propylene in the PE component or block (defined previously) wpp-dibiock = weight fraction of PP in the diblock separated with PE-fraction by HTLC

[00138] The amount of the diblock present in this PE fraction can be estimated by assuming that the ratio of the PP block to PE block is the same as the overall ratio of PP to PE present in the whole polymer. For example, if the overall ratio of PP to PE is 1 : 1 in the whole polymer, then it assumed that the ratio of PP to PE in the diblock is also 1: 1. Thus, the weight fraction of diblock present in the PE fraction would be weight fraction of PP in the diblock (wpp-dibiock) multiplied by two. Another way to calculate this is by dividing the weight fraction of PP in the diblock (wpp-dibiock) by the weight fraction of PP in the whole polymer (Equation 2).

[00139] To further estimate the amount of diblock present in the whole polymer, the estimated amount of diblock in the PE fraction is multiplied by the weight fraction of the PE fraction measured from HTLC. To estimate the crystalline block composite index or the modified block composite index, the amount of diblock copolymer is determined by Equation 7.1 or 7.2, respectively. To estimate the CBCI and the MBCI, the weight fraction of diblock in the PE fraction calculated using Equation 6 is divided by the overall weight fraction of PP (as calculated in Equation 2) and then multiplied by the weight fraction of the PE fraction. The value of the CBCI and/or MBCI can range from 0 to 1.0, wherein 1.0 would be equal to 100% diblock and zero would be for a material such as a traditional blend or random copolymer.

CBCI = ^Wpp - ^dM - ^k · W _PE _ _fraclwn Eq. 7.1 (CBCI)

MBCI = ^W? r-" . _WpE _ _fraction Eq. 7.2 (M BCI)

Where wpp = weight fraction of PP in the diblock separated with the PE-fraction by HTLC (Equation 6) wpp = weight fraction of PP in the polymer wpE = weight fraction of PE separated from HTLC, containing the diblock and unbound PE (Equation 5)

Preparation of Modifiers

[00140] The modifiers are blends of the Block Composite, Specified Block

Composite, Crystalline Block Composite, a first polyolefin copolymer, and/or a second polyolefin copolymer. In particular, the materials principally used are the following: Block Composite The Block Composite discussed above that

includes block copolymers having 50 wt% of EP soft blocks (with 65 wt% of ethylene, based on the total weight of the soft blocks) and 50 wt% of iPP hard blocks (with 1 wt% of ethylene, based on the total weight of the hard blocks), and a melt flow rate of 6.5 g/10 min at 230 °C/2.16 kg.

Specified Block Composite The Specified Block Composite discussed above that includes block copolymers having 50 wt% of EP soft blocks (with 88 wt% of ethylene, based on the total weight of the soft blocks) and 50 wt% of iPP hard blocks (with 15 wt% of ethylene, based on the total weight of the hard blocks), and a melt flow rate of 12.4 g/10 min at 230 °C/2.16 kg.

Crystalline Block Composite The Crystalline Block Composite discussed above that includes block copolymers having 50 wt% of EP soft blocks (with 90 wt% of ethylene, based on the total weight of the soft blocks) and 50 wt% of iPP hard blocks (with 1 wt% of ethylene, based on the total weight of the hard blocks), and a melt flow rate of 9.8 g/10 min at 230 °C/2.16 kg.

First Polyolefin Copolymer A An ethylene-octene copolymer having a melt index of 5.0 g/10 min (according to ASTM D1238 and at 190 °C/2.16 kg), a density of 0.870 g/cc (according to ASTM D792), and a Mooney Viscosity of 8 MU (according to ASTM D1646 and at ML 1+4, 121 °C) (available as ENGAGE™ 8200 from The Dow Chemical Company).

First Polyolefin Copolymer B An ethylene-octene copolymer having a melt index of 13.0 g/10 min (according to ASTM D1238 and at 190 °C/2.16 kg), a density of 0.864 g/cc (according to ASTM D792), and a Mooney Viscosity of 4 MU (according to ASTM D1646 and at ML 1+4, 121 °C) (available as ENGAGE™ 8137 from The Dow Chemical Company).

First Polyolefin Copolymer C An ethylene-octene copolymer having a melt index of 1.0 g/10 min (according to ASTM D1238 and at 190 °C/2.16 kg), a density of 0.857 g/cc (according to ASTM D792), and a Mooney Viscosity of 25 MU (according to ASTM D1646 and at ML 1+4, 121 °C) (available as ENGAGE™ 8842 from The Dow Chemical Company).

First Polyolefin Copolymer D An ethylene-butene copolymer having a melt index of 5.0 g/10 min (according to ASTM D1238 and at 190 °C/2.16 kg), a density of 0.865 g/cc (according to ASTM D792), and a Mooney Viscosity of 7 MU (according to ASTM D1646 and at ML 1+4, 121 °C) (available as ENGAGE™ 7447 from The Dow Chemical Company).

Second Polyolefin Copolymer A high melt flow ethylene-octene polyolefin elastomer having a melt index of 500 g/10 min (according to ASTM D1238 and at 190 °C/2.16 kg), a density of 0.874 g/cm ³ (according to ASTM D792), a Brookfield Viscosity at 177 °C of 17,000 cps, a DSC melting point of 70 °C, and glass transition temperature of -56 °C (available as AFFINITY™ GA 1950 from The Dow Chemical Company).

AO An antioxidant available from BASF as Irganox®

B 225. Preparation of Working Examples and Comparative Examples

[00141] The materials principally used are the following:

RCP A clarified polypropylene random copolymer that is marketed as offering very good see-through and contact clarity, but is observed as having a relatively low toughness at lower temperatures, having a melt flow rate of 40 g/10 min (according to ASTM D1238 and at 230 °C/2.16 kg), a density of 0.90 g/cc (according to ASTM D792), and a haze of 8% (available as Pro-fax RP448S from Ly ondellB asell) .

Modifier 1 A modifier as discussed above that includes 40 wt% of the Block Composite and 60 wt% of the First Polyolefin Copolymer A. AO in the amount of 0.2 wt% may be included.

Modifier 2 A modifier as discussed above that includes 40 wt% of the Specified Block Composite and 60 wt% of the First Polyolefin Copolymer A. AO in the amount of 0.2 wt% may be included.

Modifier 3 A modifier as discussed above that includes 30 wt% of the Specified Block Composite, 25 wt% of the First Polyolefin Copolymer A, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 4 A modifier as discussed above that includes 40 wt% of the Crystalline Block Composite and 60 wt% of the First Polyolefin Copolymer A. AO in the amount of 0.2 wt% may be included.

Modifier 5 A modifier as discussed above that includes 30 wt% of the Crystalline Block Composite, 25 wt% of the First Polyolefin Copolymer A, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 6 A modifier as discussed above that includes 15 wt% of the Specified Block Composite and 85 wt% of the First Polyolefin Copolymer A. AO in the amount of 0.2 wt% may be included.

Modifier 7 A modifier as discussed above that includes 15 wt% of the Crystalline Block Composite and 85 wt% of the First Polyolefin Copolymer A. AO in the amount of 0.2 wt% may be included.

Modifier 8 A modifier as discussed above that includes 15 wt% of the Specified Block Composite and 85 wt% of the First Polyolefin Copolymer B. AO in the amount of 0.2 wt% may be included.

Modifier 9 A modifier as discussed above that includes 30 wt% of the Specified Block Composite, 25 wt% of the First Polyolefin Copolymer B, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 10 A modifier as discussed above that includes 15 wt% of the Crystalline Block Composite and 85 wt% of the First Polyolefin Copolymer B. AO in the amount of 0.2 wt% may be included.

Modifier 11 A modifier as discussed above that includes 30 wt% of the Crystalline Block Composite, 25 wt% of the First Polyolefin Copolymer B, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included. Modifier 12 A modifier as discussed above that includes 15 wt% of the Specified Block Composite and 85 wt% of the First Polyolefin Copolymer C. AO in the amount of 0.2 wt% may be included.

Modifier 13 A modifier as discussed above that includes 30 wt% of the Specified Block Composite, 25 wt% of the First Polyolefin Copolymer C, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 14 A modifier as discussed above that includes 15 wt% of the Crystalline Block Composite and 85 wt% of the First Polyolefin Copolymer C. AO in the amount of 0.2 wt% may be included.

Modifier 15 A modifier as discussed above that includes 30 wt% of the Crystalline Block Composite, 25 wt% of the First Polyolefin Copolymer C, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 16 A modifier as discussed above that includes 15 wt% of the Specified Block Composite and 85 wt% of the First Polyolefin Copolymer D. AO in the amount of 0.2 wt% may be included.

Modifier 17 A modifier as discussed above that includes 30 wt% of the Specified Block Composite, 25 wt% of the First Polyolefin Copolymer D, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

Modifier 18 A modifier as discussed above that includes 15 wt% of the Crystalline Block Composite and 85 wt% of the First Polyolefin Copolymer D. AO in the amount of 0.2 wt% may be included.

Modifier 19 A modifier as discussed above that includes 30 wt% of the Crystalline Block Composite, 25 wt% of the First Polyolefin Copolymer D, and 45 wt% of the Second Polyolefin Copolymer. AO in the amount of 0.2 wt% may be included.

EC140R A clarified polyolefinic resin that is marketed as offering high impact resistance at room and subzero temperatures, good transparency, good resistance to stress whitening, and high fluidity and has a density of 0.902 g/cc (according to ASTM D792) and melt flow rate of 30 g/10 min (according to ASTM D 1238 at 230 °C/2.16 kg) (available as Clyrell EC140R from

Ly ondellB asell) .

Copolymer 1 An ethylene-octene copolymer having a melt index of 30 g/10 min (according to ASTM D1238 at 190C/2.16 kg), a density of 0.902 g/cc (according to ASTM D792), and a Mooney Viscosity of 2 MU (available as ENGAGE™ 8402 from The Dow Chemical Company).

[00142] Working Examples 1 to 5 and Comparative Examples A to C are prepared according to the formulations in Table 6, below:

Table 6

[00143] In particular, the working examples and comparative examples are prepared by dry blending and injection molding on a KraussMaffei KMl 10-390 injection molding machine. Dual butterfly molds are used to make the samples (7.4 mm X 7.4 mm squares) to which specimens used for Izod impact, Charpy Impact, and tensile testing were die cut into plaques of 1.6 mm and 0.75 mm thickness.

[00144] The properties of Working Examples 1 to 5 and Comparative Examples A to C, at a plaque specimen thickness of 1.60 mm, are evaluated as shown below in Table 7.

Table 7

[00145] The properties of Working Examples 1 to 5 and Comparative Examples A to C, at a specimen thickness of 0.75 mm, are evaluated as shown below in Table 8. In this regard, it is noted that the specimen thickness of 0.75 mm is too thin for Izod and Charpy impact data.

Table 8

[00146] As seen in at least Table 7, the inventive formulations of the working examples are surprisingly clear. Furthermore, as shown in the figures, TEM micrographs show the dispersion and break-up of the polyolefin elastomer is best for the compatibilized blends with block composite, specified block composite, or crystalline block composite. Indeed, the micrographs shown at 0.2 μιη show domains with the size of the shortest dimension of the compatibilized blends to be in the range of 200-300nm; these blends are visibly clear and have low haze, especially for containing non-refractive index matched elastomer. In comparison, the comparative examples show much larger domains with the size of the shortest dimension greater than 500 nm. Comparative Examples A and C, for example, are less clear and have higher haze compared to some of the working examples, which is expected for blends containing a partially or non-refractive index matched elastomer alone.

[00147] Furthermore, as seen in at least Table 7, the inventive formulations of a number of the working examples that are compatibilized with block composite, specified block composite, or crystalline block composite surprisingly show high impact strength (including at low temperatures). [00148] Further working examples are prepared with regard to Modifiers 6-11, 13 and 15. In particular, Working Examples 6 to 13 and Comparative Example D are prepared according to the formulations in Table 9, below:

Table 9

[00149] In particular, the working examples and comparative examples are prepared by dry blending and injection molding on a KraussMaffei KMl 10-390 injection molding machine. Dual butterfly molds are used to make the samples (7.4 mm X 7.4 mm squares) to which specimens used for Izod impact, Charpy Impact, and tensile testing were die cut into plaques of 1.6 mm and 0.75 mm thickness.

[00150] The properties of Working Examples 6 to 13 and Comparative Example D, at a plaque specimen thickness of 1.60 mm, are evaluated as shown below in Table 10.

Table 10

00151] The properties of Working Examples 6 to 13 and Comparative Example D, at a specimen thickness of 0.75 mm, are evaluated as shown below in Table 11. In this regard, it is noted that the specimen thickness of 0.75 mm is too thin for Izod and Charpy impact data. Table 11

[00152] As seen in at least Tables 10 and 11, the inventive formulations of the working examples are surprisingly clear and surprisingly show high impact strength (including t low temperatures). Accordingly, the novel formulations of the present disclosure that are compatibilized with a block composite, specified block composite, or crystalline block composite surprisingly provide for high clarity-low temperature use containers that have not been seen in the state of the art.