Field of the Invention

The field of art to which the invention relates comprises the art of corrosion protection for structures being used or to be used in marine environments.

Background of the Invention

Installation of various type metal structures in corrosive liquids such as sea water are confronted with a major problem in avoiding the adverse effects of corrosion and erosion. Either can severely reduce the life expectancy of the structure. Exemplifying the situation are structures such as off-shore rigs and/or production platforms for recovering oil in the many oceans and seas of the world. Briefly, such structures include not only supports for the rig itself, but also risers comprising conduits through which transmission of recovered oil is conducted. Typically, the various structural items and/or risers are pre- coated, encased or otherwise provided with cathodic protection or the like in order to ward off or deter the deleterious corrosive effects of the sea water. Little had been known however, how to restore such risers on site after the onset of corrosion when the original protective coating, etc., had begun to wear or generally deteriorate. Temporary repair or replacing

the affected structures had been customary although undesirable because of the associated high costs and less than satisfactory results.

Background of the Prior Art

There have been many attempts to passivate the adverse effects of impact/abrasion and corrosion to structural members of offshore platforms, drilling rigs, pipelines, risers, pilings, wharfs, or any edifice that is located in the splash or tidal zones of a marine environment. There are several known techniques for applying pre-installation protection to metallic structures for protecting them from the ultimate effects of corrosion and erosion that attack the supports of the structure located in the splash zone. By way of example, steel pilings and/or production piping are usually covered with a rust- resistant inorganic zinc silicate primer and organic top coats as a coating system during the fabrication phase of new construction. Exemplifying such coatings are the disclosures of U.S. Patents 3,370,998; 4,619,557; and 4,743,142.

Once a structure such as a production platform is emplaced offshore and subjected to prolonged exposure of the marine environment during normal operating procedures, previously coated steel surfaces tend to become slowly penetrated and eroded to a point whereby the existing steel substrate is ultimately exposed. The corrosion rate of steel in the splash zone is typically about

100 mils per year. Normally these steel support members, without good repair procedures, will lose their structural integrity after about seven to ten years of exposure. The replacement cost of risers and other steel supports in situ offshore are considered extremely expensive such that replacement is preferred to be avoided.

Over the last couple decades, coating manufactures have formulated epoxy resins that will cure under water. These materials were primarily developed for spot repair usage and have enjoyed some limited success on small projects. Historically, these formulations are based on polyamide cured epoxy resins that are heavily filled with inert inorganic compounds, i.e., silica flour or mica, to produce increased viscosity, thixotropy and solids by weight. These properties are essential in order to reduce the possibility of the material being "washed off" by encounted wave action.

Despite existence of such conventional underwater epoxy formulations, a problem has been a lack of sufficient adhesion of the epoxy with the applied surfaces. The end result has been a more or less "envelope" effect, whereby the coating does not bond tenaciously to the substrate surface particularly in repair situations where an onset of corrosion or erosion has already been encountered. Under those circumstances, indiscriminate delamination or spalling usually occurs within the first year after application.

In my prior U.S. patent 5,087,154 there is disclosed a coating composition and method of applying the coating to items being used or to be used in a marine environment. The coating tenaciously adheres to the recipient surface and is comprised of a plurality of layers of epoxy composition sequentially applied about the affected surface area. A vitrified cloth wrap is disposed between each layer of epoxy.

Objects of the Invention

It is therefore an object of the invention to provide an improved system for effecting protection against corrosion and erosion of support structures in a marine environment.

It is a further object of the invention to achieve the previous object with a coating and encapsulating cladding structure that can be applied on site and underwater more quickly and with less labor intensity than previously possible.

It is a still further object of the invention to achieve the previous objects with an adhesion type barrier coating continuously maintained in a compressing relation by the encapsulating cladding.

Summary of the Invention:

This invention relates to a novel system and method of application for effecting corrosion protection of marine

structures. More specifically, the invention relates to a novel such system and method of applying the protection to afford superior corrosion and erosion protection to a support structure to be used or being used in a marine environment. The installation can be either pre-applied during initial fabrication or post-applied on site to existing support structures in need of repair or restoration. In either situation, the life expectancy of the structure upon which the protection hereof has been installed can typically be increased by at least about five years over the otherwise current life expectancy of such structures. At the same time, the protection can be installed more quickly and with less labor intensity than disclosed, for example, in my prior U.S. patent 5,087,154 incorporated herein by reference. The system hereof for achieving the foregoing enables a continuous application of a uniform uninterrupted epoxy coating over the surface area to be protected. A rigid cladding surrounds and encapsulates the coating so as to place the coating in compression. Prior to placement of the cladding the uncured epoxy is concomitantly applied both to the surface area and to the interior surface of the cladding. Preferably, for an item of circular cross-section, the cladding is in the form of half shells comprised of arcuate sections of impervious reinforced thermosetting resin pipe (RTRP) or fiberglass resin pipe (FRP) . The coating is comprised of a solvent-free, 100 percent solids by volume epoxy polyamine adhesive that is applied either

to surface prepared virgin metal as a fabrication coating or, in the case of restoration, over a previously abrasive blasted metallic substrate that is free of scale, oxidation and/or chemical contamination. The utilized polyamine formulations of epoxy adhesive provide characteristics that displaces water and creates a strong molecular attraction or adhesive strength to the substrate. The cladding enables a uniform circumferential compression of the coating squeezing out excess water and trapped air. Being an impervious outer shell encapsulating the coating, it affords superior resistance to impact, abrasion and erosion not adversely affected by salt water. As such, it complies with ASTM F927 "General Marine Services".

The above noted features and advantages of the invention as well as other superior aspects thereof will be further appreciated by those skilled in the art upon reading the detailed description which follows in conjunction with the drawings.

Brief Description of the Drawings

FIGURE 1 is a schematic illustration of a typical offshore platform;

FIGURE 2 is an enlarged fragmentary section of the encircled portion 2 of FIGURE 1;

FIGURE 3 is an enlarged isometric exploded view of the installed protection hereof; and

FIGURE 4 is a fragmentary substantially enlarged section of the completed installation.

Description of the Preferred Embodiment

In the description which follows, like parts are marked throughout the specification and drawings with the same reference numerals respectively. The drawing figures are not necessarily to scale and the proportions of certain parts may have been exaggerated for purposes of clarity.

Referring now to the drawings, there is illustrated in FIGURE 1 an exemplary use of the coating and method hereof as represented by an offshore platform designated 10 secured via a support structure 12 to the sea bottom 14. Above sea level 16, there is provided a working deck 18 from which a pipeline riser 20 dependently extends while secured via clamps 22 to the support structure 12. For inhibiting the adverse effects of corrosion and erosion in the splash or tidal zone there is provided on riser 20, as illustrated in FIGURE 2 and 3, the system of the invention including a coating designated 24 with cladding 26.

As will be understood, the coating 24 with cladding 26 are useful as a preliminary protection applied during initial fabrication prior to installation of riser 20. Alternatively,

they can be applied for restoration purposes during post- installation service on site following some initial deleterious onset of corrosion and/or erosion effects on the riser. During fabrication, the coating and cladding can be applied directly to abrasively blasted virgin metal as a substitute for other inhibitive type coatings of a type which have been applied for many years or can be applied in combination therewith.

For restoration or repair of existing structures, the affected surface is first abrasively blasted above and below water level to a near white finish in accordance with the Steel Structures Painting Council (SSPC-SP10). This has the effect of removing all rust, oxidation, scale and chloride contamination from the riser surface. Depth of anchor profile should be a minimum of at least about 3 mils so as to remove imbedded contaminants consisting of mil scale (new steel) or Fβ2θ ₃ , chlorides, chro ates and nitrates that exist on deteriorated steel .

Comprising coating 24 is a solvent free, 100 percent solids by volume epoxy polyamine adhesive composition formulated for underwater curing. An essential property thereof is the tenacious adhesive characteristics it assumes when applied directly to a properly prepared steel substrate. This has been achieved herein with an epoxy resin (A) and converter (B) mixed together in equal proportions from the following ingredients: (A) (percent by volume)

a) Bisphenol-F epoxy resin (about 80-95%) b) fumed silica (about 5-10%) c) coloring matter such as carbon black (about less than 5%) (B) (percent by volume) a) polyamine compound (about 80-95%)

b) alkyl substituted amino-phenol (about 5-15%) c) barium sulphate (about 5-10%) d) organic acid (less than about 5%)

The epoxy resin (A) when mixed with the converter reactor (B) develops a very high degree of molecular attraction through exothermic polymerization to the steel substrate. The phenomenon is sometimes termed "good wetting", i.e. the surface of steel contains multiple layers of water molecules and this composition provides molecular attraction by diffusing through those water layers by emulsification (or disperses the water through the adhesive so that contact to the steel is accomplished.) It is an essential step that an adequate degree of adhesion develop during the curing state. Emulsification is attributed to the hydrophobic fatty acid portion of the polyamine molecules, which in combination with the hydrophilic portion of the molecule acts as the emulsifier. Characteristically, the resulting epoxy composition is able to withstand temperatures of down to 45°F and pressures to at

least 1,500 pounds per square inch without adversely affecting its curing capabilities. Whether applied to new riser structures prior to installation or to post installed structures subsequent to abrasive blasting, the two-part epoxy formulation with preferably a black and white pigmentation respectively is first mixed in equal proportions. When properly mixed, the epoxy will appear as a uniform dark gray color with a consistent smooth viscosity free of lumps or undissolved particles having a workable pot life of approximately forty minutes at 80 ^* F. Cladding 26 is comprised of reinforced thermosetting resin pipe (RTRP) or fiberglass resin pipe (FRP) custom sized as to ID and wall thickness. The pipe composition is one having optimum compatibility with the composition of coating 24 and in a preferred composition is comprised of an epoxy amine resin, glass filament wound procedure and then heat cured. Once cured, the pipe is cut into two arcuate clam shell sections and the ID is abrasive blasted to provide an anchor or surface profile.

For centering the cladding pipe and affording a substantially concentric annular space between the OD of riser 20 and the ID of cladding 26, centralizers 28 are initially formed on the ID substrate of cladding 26. The centralizers are comprised of dimensionally controlled segments of coating composition 24 applied and cured on cladding 26 at least 24 hours prior to installation. The centralizers function as stand off projections about 1/8 inches to 1/4 inches in thickness throughout the longitudinal axis of both halves of cladding 26

and are about 2-3 inches in length. When the cladding is installed they are spaced systematically throughout the entire annular space thereby enabling the applied coating 24 to fill any void spacing. Subsequent to preparation of the epoxy mixture, the first step is to apply concomitantly a controlled quantity of still viscous epoxy mixture uniformly about the surface of riser 20 above and below the water line and to the ID surface of cladding halves 26. Application of the mixture to the exterior surface of riser 20 can be by hand or roller. To the cladding, while preferably out of the water, it is generally applied by roller or brush. The combined coating thickness should be at least sufficient to obtain a continuous filling of the annular spacing between the OD of the riser 20 and the ID of the cladding 26. A preferred thickness is about 50-70 mils.

Once both surfaces contain the requisite thickness of epoxy mixture, the cladding halves are disposed about the affected riser area insitu and clamped by annular clamps (not shown). As the clamps are emplaced and tightened, the developed compression forces excessive quantities of the mixture along with water and air from the annulus out the top and bottom and through the two longitudinal seams 30 and 32 between the cladding halves. The volume of the affected annular space will, of course, vary as a diametal relation of the riser and cladding. The clamps are usually of steel and are left to disintegrate in salt water after

several months. Optionally, nylon straps could be utilized instead of clamps.

The coating cure rate will vary with atmospheric and water temperatures. At 80°F the system will cure hard within about two hours. Final cure above and below water normally occur within 24 hours when applied in water temperatures of at least about 55"F. Most installations are performed by a trained and competent painter in the minus (-)3 to (-)5 foot level in the splash zone. When water depth exceeds about five feet, installation usually requires special equipment and the use of divers. It is anticipated that the process hereof can be successfully applied to water depths of at least 100 feet.

When the system hereof has been properly installed, it is anticipated to extend initial life expectancy of the recipient structure for at least five additional years compared to prior coatings initially applied for that purpose. At the same time, the benefit in a restoration situation is anticipated to be far superior to repair methods previously utilized by extending the practical life of the structure for at least five additional years. Even then, should subsequent breakdown of the installation occur, additional restoration can be re-applied over a space of time when required any number of times for so long as the basic structural integrity of the metal structure of riser 20 remains. By the above description, there is disclosed a novel system for effecting corrosion protection of marine structures. By

forming an epoxy coating composition having superior adhesion properties and encapsulating the composition with a firm and rigid cladding of fiber resin pipe, unusually long-lasting barrier protection is achieved. When constructed in this manner, the resultant installation is sufficiently durable to withstand anticipated erosion effects for prolonged time periods, during which it is unpenetratable by sea water. At the same time, it greatly expedites the installation time while being less labor intensive, particularly in the sub sea or rising/falling tidal action as compared to the method and installation described in my prior patent mentioned supra. Moreover, the cladding provides superior resistance to impact, abrasion and erosion than previously attainable.

Since many changes could be made in the above construction and many apparently widely different embodiments of this invention could be made without departing from the scope thereof, it is intended that all matter contained in the drawings and specification shall be interpreted as illustrative and not in a limiting sense.