COVER APPLICATION

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit of priority under 35 U.S.C. § 119 of U.S.

Provisional Application Serial No. 62/444,470 filed on January 10, 2017 and US Provisional Application Serial No. 62/355,542 filed on June 28, 2016, the content of which is relied upon and incorporated herein by reference in its entirety.

BACKGROUND

[0002] The present disclosure relates to curved cold-formed glass substrates, articles including such glass substrates, and related processes.

[0003] Curved glass substrates are desirable in many contexts. One such context is for use as a cover glass for a curved display, which may be incorporated into an appliance, an architectural element (e.g., wall, window, modular furniture, shower door, mirrors etc.), a vehicle (e.g., automobiles, aircraft, sea craft and the like), or other applications. Existing methods of forming such curved glass substrates, such as thermal forming, have drawbacks including optical distortion and surface marking. Accordingly, there is a need for curved glass substrates that do not exhibit the optical distortion and surface marking typically found in thermally-formed curved glass substrates, while maintaining superior display quality.

BRIEF SUMMARY

[0004] The present disclosure is directed to articles comprising cold-formed glass substrates bonded to a non-planar rigid support structure, and methods of making such articles.

[0005] A first aspect of this disclosure pertains to a process for forming an article described herein. In one or more embodiments, the process includes cold-forming a substantially flat glass substrate into a non-planar shape using a die.

[0006] In one or more embodiments, the process includes coupling the cold-formed glass substrate to a non-planar rigid support structure. In one or more embodiments, coupling the cold-formed glass substrate to a non-planar rigid support structure includes bonding the cold-formed glass to the non-planar rigid support structure. In some instances, the cold- formed glass may be coupled or bonded to the non-planar rigid support structure at a plurality of non-planar points. Such coupling or bonding may be achieved using the die. In one or more embodiments, the process may include simultaneously cold-forming the substantially flat glass substrate and coupling the cold-formed glass substrate to the non-planar rigid support structure.

[0007] In some embodiments, a process comprises cold-forming a flat glass substrate into a non-planar shape using an injection-molding die. In some embodiments, bonding is accomplished by injection molding the non-planar rigid support structure onto the cold- formed glass substrate while the die holds the cold-formed glass substrate in the non-planar shape.

[0008] In some embodiments, the cold-formed glass substrate has opposing major surfaces, and the non-planar rigid support structure is bonded to only one of the major surfaces.

[0009] In some embodiments, the process further comprises, after bonding, applying an adhesive to at least a portion of an interface between the cold-formed glass substrate and the non-planar rigid support structure. In some embodiments, the interface is between an edge (or minor surfaces orthogonal to the maj or surfaces) of the cold-formed glass substrate and the non-planar rigid support structure. In one or more embodiments, the process includes applying adhesive to at least a portion of the edge or the non-planar rigid support structure at the interface.

[0010] In some embodiments, a process comprises cold-forming a glass substrate into a non-planar shape. In some embodiments, the process includes using the die to directly bond the cold-formed glass substrate onto a non-planar rigid support structure. In one or more embodiments, the non-planar rigid support structure is formed prior to the bonding.

[0011] In some embodiments, die includes a recess and the non-planar rigid support structure is placed into the recess prior to bonding.

[0012] In some embodiments, the process further comprises applying one of or both a coating and a surface treatment to a surface of the substantially flat glass substrate prior to cold-forming. In one or more embodiments, the process further comprises applying one of or both a coating and a surface treatment to a surface of the substantially flat glass substrate after cold-forming. In either instance, the surface may include any one or more of the opposing major surfaces and minor surface(s) orthogonal to the major surfaces (forming an edge). In one or more embodiments, the coating may be an ink coating, an antireflective coating, an antiglare coating and/or any other suitable coating. In one or more embodiments, the surface treatment may include an antiglare surface, a haptic surface that provides tactile feedback, recessed and/or raised portions providing indicia and the like.

[0013] In some embodiments, the cold-formed glass substrate includes an open region. When the cold-formed glass substrate is coupled to the non-planar rigid support structure, the open region is not in direct contact with the non-planar rigid support structure. In one or more embodiments, the open region having a curved shape maintained by the non- planar rigid support structure. A display may be attached to at least one of the cold-formed glass substrate and the non-planar rigid support structure, such that the display is at least partially visible through the open region of the cold-formed glass substrate.

[0014] In some embodiments, during and after cold-forming, the temperature of the glass substrate does not exceed its glass transition temperature. In one or more embodiments, the temperature of the glass substrate does not exceed 800 °F (or about 427 °C).

[0015] In some embodiments, the process includes strengthening the substantially flat glass substrate. In one or more embodiments, the process includes chemically strengthening the substantially flat glass substrate, thermally strengthening the substantially flat glass substrate, mechanically strengthening the substantially flat glass substrate or strengthening the substantially flat glass substrate using any one or more of chemical strengthening, thermal strengthening and mechanical strengthening.

[0016] In some embodiments, an article is formed by any of the processes described herein.

[0017] A second aspect of this disclosure pertains to an article including a cold- formed glass substrate having opposing major surfaces and a curved or non-planar shape, the opposing major surfaces each comprising a surface stress that differs from one another. In one or more embodiments, the cold-formed glass substrate is coupled to a rigid support structure having the curved or non-planar shape (i.e., the same curved or non-planar shape as the cold-formed glass substrate). In one or more embodiments, the cold-formed glass substrate is bonded to the non-planar rigid support structure. In some embodiments, the rigid support structure is bonded to only one of the major surfaces.

[0018] In one or more embodiments, the cold-formed glass substrate includes an open region not in direct contact with the rigid support structure, and the open region has a curved shape maintained by the rigid support structure.

[0019] In some embodiments, the rigid support structure has a developable surface. In one or more embodiments, the cold-formed glass substrate has a developable surface. In some embodiments, both the rigid support structure and the cold-formed glass substrate have a developable surface.

[0020] In some embodiments, a display is attached to at least one of the cold-formed glass substrate and the non-planar rigid support structure. In one or more embodiments, the display is at least partially or completely visible through the open region of the cold-formed glass substrate. In one or more embodiments, the cold-formed glass substrate may be free of open regions (i.e., the glass substrate may be a continuous sheet) and the display may be visible through the cold-formed glass substrate.

[0021] In some embodiments, the cold-formed glass substrate comprises either one of or both a coating and a surface treatment on at least one major surface thereof. The coating may be an ink coating, an antireflective coating, an antiglare coating and/or any other suitable coating. The surface treatment may include an antiglare surface, a haptic surface that provides tactile feedback, raised and/or recess portions providing indicia, and the like.

[0022] In some embodiments, the cold-formed glass substrate is a strengthened glass substrate. The strengthened glass may include a chemically strengthened glass, a thermally strengthened glass, a mechanically strengthened glass or a glass that has been strengthened using any one or more of chemical strengthening, thermal strengthening and mechanical strengthening.

[0023] The embodiments of the preceding paragraphs may be combined in any permutation.

BRIEF DESCRIPTION OF THE DRA WINGS

[0024] The accompanying figures, which are incorporated herein, form part of the specification and illustrate embodiments of the present disclosure. Together with the description, the figures further serve to explain the principles of and to enable a person skilled in the relevant art(s) to make and use the disclosed embodiments. These figures are intended to be illustrative, not limiting. Although the disclosure is generally described in the context of these embodiments, it should be understood that it is not intended to limit the scope of the disclosure to these particular embodiments. In the drawings, like reference numbers indicate identical or functionally similar elements.

[0025] FIG. 1 illustrates an injection mold die designed with an exemplary curved shape, and a substantially flat glass substrate, according to one or more embodiments. [0026] FIG. 2 illustrates the die of FIG. 1 cold-forming the glass substrate into a non- planar shape.

[0027] FIG. 3 illustrates the die of FIG. 2 after material has been injection-molded into recesses in the die to form a non-planar rigid support structure bonded to the back of the cold-formed glass substrate.

[0028] FIG. 4 illustrates the die of FIG. 3 and the resultant article after the die retracts. The resultant article is a cold-formed glass substrate bonded to a non-planar rigid support structure. The cold-formed cover glass substrate retains design curvature because of the rigidity of the non-planar rigid support structure coupled to a major surface of the cold- formed glass substrate.

[0029] FIG. 5 shows the cold-formed glass substrate bonded to a non-planar rigid support structure of FIG. 4, with an adhesive.

[0030] FIG. 6 shows a perspective view of a cold-formed glass substrate bonded to a non-planar rigid support structure, according to one or more embodiments.

[0031] FIG. 7 shows a top view of a cold-formed glass substrate bonded to a non- planar rigid support structure. The curvature is not visible due to the angle of the view, according to one or more embodiments.

[0032] FIG. 8 illustrates a direct-bonding die designed with a specific desired curved shape, a flat glass substrate, and a non-planar rigid support structure inserted into recesses in the die, according to one or more embodiments..

[0033] FIG. 9 illustrates the die of FIG. 8 cold-forming the glass substrate into a non- planar shape and bonding the non-planar rigid support structure to the cold-formed glass substrate.

[0034] FIG. 10 illustrates the die of FIG. 9 and the resultant article after the die retracts. The resultant article is a cold-formed glass substrate bonded to a non-planar rigid support structure. The cold-formed cover glass substrate retains design curvature because of the rigidity of the non-planar rigid support structure coupled to a major surface of the cold- formed glass substrate.

[0035] FIG. 11 shows the cold-formed glass substrate bonded to a non-planar rigid support structure of FIG. 10, with an adhesive.

[0036] FIG. 12 shows a process flowchart corresponding to the process illustrated in

FIGS l to 5.

[0037] FIG. 13 shows a process flowchart corresponding to the process illustrated in

FIGS 8 to 10. [0038] FIG. 14 illustrates a die having ridges that position a glass substrate within the die, according to one or more embodiments.

[0039] FIG. 15 illustrates an automotive interior display comprising a cold-formed glass substrate bonded to a non-planar rigid support structure, according to one or more embodiments.

[0040] FIG. 16 shows a top view of a cold-formed glass substrate bonded to a non- planar rigid support structure, having a display bonded to the cold-formed glass substrate, according to one or more embodiments. The curvature is not visible due to the angle of the view.

[0041] FIG. 17 shows a side view of a glass substrate being applied to a rigid support structure having a developable surface using a single roller, according to one or more embodiments.

DETAILED DESCRIPTION

[0042] Vehicle manufactures are creating interiors that better connect, protect and safely inform today's drivers and passengers. In addition, as the industry moves towards autonomous driving, there is a need for creating large format appealing displays. There is already a trend towards larger displays including touch functionality in the new models from several OEMs. Such trends are also immerging in appliances, architectural elements (e.g., wall, window, modular furniture, shower door, mirrors etc.), and other vehicles (e.g., aircraft, seacraft and the like). However, most of these displays consist of two dimensional plastic cover lens.

[0043] Due to these emerging trends in the automotive interior industry and related industries, there is a need to develop a low cost technology to make three-dimensional transparent surfaces. Strengthened glass materials, such as chemically strengthened, thermally strengthened and/or mechanically strengthened glass materials are particularly desirable for use as such surfaces, particularly where the glass substrate is used as a curved cover glass for a display.

[0044] However, many methods for forming curved glass surfaces involve subj ecting glass substrates to thermal forming processes (including thermal forming processes that include heating a glass substrate to a temperature above the transition temperature of the glass). Such processes can be energy intensive due to the high temperatures involved and such processes add significant cost to the product. Furthermore, thermal forming processes may cause strength degradation or may damage any coatings present on the glass substrate, such as antireflective (AR) coatings or ink coatings. Moreover, thermal forming processes may impart undesirable characteristics onto the glass itself, such as distortion and marking.

[0045] Various aspects of this disclosure pertain to an article including a cold-formed glass substrate that can exhibit and maintain a curved shape. As used herein, "cold-forming" refers to bending a glass substrate at a temperature below the glass transition temperature of the glass to achieve a curved or non-planar shape. In one or more embodiments, this temperature is less than about 800 °F (or 427 °C). The resulting curved or non-planar glass substrate is a cold-formed glass substrate.

[0046] In some embodiments, a portion of a major surface of the cold-formed glass substrate may include a "developable" surface. A developable surface has a surface with zero Gaussian curvature. In one or more embodiments, the developable surface means that all points of the cold-formed glass substrate surface have a Gaussian curvature (GC) that is equal to zero (wherein GC is equal to Kmax*Kmin, wherein Kmax and Kmin are principal curvatures defined as Kmax = 1/R' and Kmin = 1/R"), and wherein one of Kmax and Kmin is non-zero. R' is the maximum radius of curvature and R" is the minimum radius of curvature. In one or more embodiments, the surface of the cold-formed glass substrate that can be flattened into a plane without stretching or compressing within the plane of the surface.

[0047] Examples of developable surfaces include cones, cylinders, oloids, tangent developable surfaces, and portions thereof. A surface that projects onto a single curved line is a developable surface.

[0048] In one or more embodiments, the article includes the cold-formed glass substrate with a non-planar shape, a first major surface and a second major surface opposing the first major surface, and the cold-formed glass substrate is coupled to a non-planar rigid support structure. In one or more embodiments, the cold-formed glass substrate is coupled to the non-planar rigid support structure by a bond. In one or more embodiments, an adhesive is used to bond the cold-formed glass substrate is coupled to the non-planar rigid support structure. In one or more embodiments, the non-planar rigid support structure is injection molded onto the cold-formed glass substrate.

[0049] In one or more embodiments, the non-planar rigid support structure is coupled to the first major surface of the cold-formed glass substrate at one or more points, which may be non-planar points. In some embodiments, the non-planar rigid support structure is bonded to the first major surface at a plurality of non-planar points. [0050] In one or more embodiments, the first and second opposing major surfaces each exhibit a surface stress that differs from one another. Such difference in stress is generated by cold-forming. The stresses can include surface compressive stresses generated by the cold-forming process in addition to any surface stresses that may be present from strengthening processes imparted to the glass substrate. These stresses are not thermally relaxed because the glass substrate is maintained at temperatures well below the glass transition temperature. In some embodiments, the cold-formed glass substrate exhibits a surface compressive stress on the first and second major surfaces that differ from one another at, near or adj acent the one or more non-planar points. As illustrated in FIG. 4, first and second major surfaces 121 and 122 are in tension or compression depending on the direction of curvature. First major surface 121 at a first position 121 A adjacent the non-planar rigid support structure 130 is in tension, while second major surface 122 at a second position 122 A adjacent the same non-planar rigid support structure 130 is in compression. Accordingly, the second major surface 122 at the second position 122 A exhibits a greater surface compressive stress than first major surface 121 at a first position 121 A. This is asymmetrical surface compressive stress is exhibited even when the glass substrate 120 is strengthened as described herein and exhibits a surface compressive stress prior to being cold-formed. In one or more embodiments, first position 121 A and the second position 122A of the respective first and second major surfaces 121 , 122 are adjacent the same non-planar rigid support such that either one or both the first position and the second positions is located at a distance of 5 centimeters or less from the non-planar rigid support structure 130. In one or more embodiments, either one or both the first position and the second position are located at a distance of 4 centimeters or less, 3 centimeters or less, 3 centimeters or less, 2 centimeters or less, 1 centimeter or less or 0.5 centimeter or less from the non-planar rigid support structure 130. The distances of the first and second positions relative to the non-planar rigid support structure 130 are measured from the center 131 of the non-planar rigid support structure 130 to the respective first and second positions. In some embodiments, the first position 121 A and the second position 122A are located directly opposite from one another and exhibit the asymmetric surface compressive stress described herein, as illustrated in FIG. 5

[0051] In some embodiments, either one of or both the first major surface and the second major surface of the glass substrate may include a coating or surface treatment. In one or more embodiments, the coating may be an ink coating, an antireflective coating, an antiglare coating and/or any other suitable coating. In one or more embodiments, the surface treatment may include an antiglare surface, a haptic surface that provides tactile feedback, recessed and/or raised portions providing indicia and the like.

[0052] In some instances, the article may include an adhesive applied to an interface between the cold-formed glass substrate and the non-planar rigid support structure. In one or more embodiments, the interface is between one or more minor surface(s) of the cold-formed glass substrate and the non-planar rigid support structure. In one or more embodiments, the interface may be substantially free of an adhesive or other material such that one or more minor surfaces are exposed.

[0053] In some instances, the cold-formed glass substrate includes an open region not in direct contact with the non-planar rigid support structure, and the open region has a curved shape maintained by the non-planar rigid support structure. In some instances, the article includes a display disposed on at least one of the glass substrate and the non-planar rigid support structure, wherein the display is at least partially or completely visible through the cold-formed glass substrate. In some instances, the display is disposed between the glass substrate and the non-planar rigid support structure. In some instances, the display may be attached to at least one of the glass substrate and the non-planar rigid support structure.

[0054] In some embodiments, a cold-formed glass substrate has a developable surface, as described herein. In some instances, the cold-formed glass substrate may include a complex developable surface, which is a combination of two or more developable surfaces such as cones, cylinders, oloids, planes and tangent developable surfaces. For instance, a complex developable surface may be a combination of at least a planar and at least a concave surface, or at least a planar and at least a convex surface, or at least a concave and at least a convex surface.

[0055] In some embodiments, a complex developable surface may also be formed by a combination of planar, conical, cylindrical, and other developable surfaces and involve both inward and outward bending. In some embodiments, the combination of planar, conical, cylindrical, and other developable surfaces may be in such a way that no sharp edges form while going from one developable surface to another.

[0056] In some embodiments, a complex developable surface or a complex developable surface may include one or more planar portions, one or more conical portions, one or more cylindrical portions, and/or one or more other developable surface portions.

[0057] In the embodiment shown, the cold-formed glass substrate has a thickness (t) that is substantially constant and is defined as a distance between the opposing major surfaces. The thickness (t) as used herein refers to the maximum thickness of the glass substrate. In one or more embodiments, the cold-formed glass substrate has a thickness (t) that is about 1.5 mm or less. For example, the thickness may be in a range from about 0.1 mm to about 1.5 mm, from about 0.15 mm to about 1.5 mm, from about 0.2 mm to about 1.5 mm, from about 0.25 mm to about 1.5 mm, from about 0.3 mm to about 1.5 mm, from about 0.35 mm to about 1.5 mm, from about 0.4 mm to about 1.5 mm, from about 0.45 mm to about 1.5 mm, from about 0.5 mm to about 1.5 mm, from about 0.55 mm to about 1.5 mm, from about 0.6 mm to about 1.5 mm, from about 0.65 mm to about 1.5 mm, from about 0.7 mm to about 1.5 mm, from about 0.1 mm to about 1.4 mm, from about 0.1 mm to about 1.3 mm, from about 0.1 mm to about 1.2 mm, from about 0.1 mm to about 1.1 mm, from about 0.1 mm to about 1.05 mm, from about 0.1 mm to about 1 mm, from about 0.1 mm to about 0.95 mm, from about 0.1 mm to about 0.9 mm, from about 0.1 mm to about 0.85 mm, from about 0.1 mm to about 0.8 mm, from about 0.1 mm to about 0.75 mm, from about 0.1 mm to about 0.7 mm, from about 0.1 mm to about 0.65 mm, from about 0.1 mm to about 0.6 mm, from about 0.1 mm to about 0.55 mm, from about 0.1 mm to about 0.5 mm, from about 0.1 mm to about 0.4 mm, or from about 0.3 mm to about 0.7 mm.

[0058] In one or more embodiments, the cold-formed glass substrate has a width in a range from about 5 cm to about 250 cm, from about 10 cm to about 250 cm, from about 15 cm to about 250 cm, from about 20 cm to about 250 cm, from about 25 cm to about 250 cm, from about 30 cm to about 250 cm, from about 35 cm to about 250 cm, from about 40 cm to about 250 cm, from about 45 cm to about 250 cm, from about 50 cm to about 250 cm, from about 55 cm to about 250 cm, from about 60 cm to about 250 cm, from about 65 cm to about 250 cm, from about 70 cm to about 250 cm, from about 75 cm to about 250 cm, from about 80 cm to about 250 cm, from about 85 cm to about 250 cm, from about 90 cm to about 250 cm, from about 95cm to about 250 cm, from about 100 cm to about 250 cm, from about 110 cm to about 250 cm, from about 120 cm to about 250 cm, from about 130 cm to about 250 cm, from about 140 cm to about 250 cm, from about 150 cm to about 250 cm, from about 5 cm to about 240 cm, from about 5 cm to about 230 cm, from about 5 cm to about 220 cm, from about 5 cm to about 210 cm, from about 5 cm to about 200 cm, from about 5 cm to about 190 cm, from about 5 cm to about 180 cm, from about 5 cm to about 170 cm, from about 5 cm to about 160 cm, from about 5 cm to about 150 cm, from about 5 cm to about 140 cm, from about 5 cm to about 130 cm, from about 5 cm to about 120 cm, from about 5 cm to about 110 cm, from about 5 cm to about 110 cm, from about 5 cm to about 100 cm, from about 5 cm to about 90 cm, from about 5 cm to about 80 cm, or from about 5 cm to about 75 cm. [0059] In one or more embodiments, the cold-formed glass substrate has a length in a range from about 5 cm to about 250 cm, from about 10 cm to about 250 cm, from about 15 cm to about 250 cm, from about 20 cm to about 250 cm, from about 25 cm to about 250 cm, from about 30 cm to about 250 cm, from about 35 cm to about 250 cm, from about 40 cm to about 250 cm, from about 45 cm to about 250 cm, from about 50 cm to about 250 cm, from about 55 cm to about 250 cm, from about 60 cm to about 250 cm, from about 65 cm to about 250 cm, from about 70 cm to about 250 cm, from about 75 cm to about 250 cm, from about 80 cm to about 250 cm, from about 85 cm to about 250 cm, from about 90 cm to about 250 cm, from about 95cm to about 250 cm, from about 100 cm to about 250 cm, from about 110 cm to about 250 cm, from about 120 cm to about 250 cm, from about 130 cm to about 250 cm, from about 140 cm to about 250 cm, from about 150 cm to about 250 cm, from about 5 cm to about 240 cm, from about 5 cm to about 230 cm, from about 5 cm to about 220 cm, from about 5 cm to about 210 cm, from about 5 cm to about 200 cm, from about 5 cm to about 190 cm, from about 5 cm to about 180 cm, from about 5 cm to about 170 cm, from about 5 cm to about 160 cm, from about 5 cm to about 150 cm, from about 5 cm to about 140 cm, from about 5 cm to about 130 cm, from about 5 cm to about 120 cm, from about 5 cm to about 110 cm, from about 5 cm to about 110 cm, from about 5 cm to about 100 cm, from about 5 cm to about 90 cm, from about 5 cm to about 80 cm, or from about 5 cm to about 75 cm.

[0060] In one or more embodiments, a portion of one or both major surfaces comprises a convex shape and an R' of the convex shape is in a range from about 37.5 mm to about 500 mm. In some embodiments with a convex surface, the thickness of the substrate may be 0.4 mm and the R' may be in a range from about 100 mm to about 200 mm, from about 125 mm to about 200 mm, from about 150 mm to about 200 mm, form about 175 mm to about 200 mm, from about 100 mm to about 175 mm, from about 100 mm to about 150 mm, or from about 100 mm to about 125 mm. In some embodiments with a convex surface, the thickness of the substrate may be 0.55 mm and the R' may be in a range from about 150 mm to about 250 mm, from about 175 mm to about 250 mm, from about 200 mm to about 250 mm, form about 225 mm to about 250 mm, from about 150 mm to about 225 mm, from about 150 mm to about 200 mm, or from about 150 mm to about 175 mm. In some embodiments with a convex surface, the thickness of the substrate may be 0.7 mm and the R' may be in a range from about 200 mm to about 300 mm, from about 225 mm to about 300 mm, from about 250 mm to about 300 mm, form about 275 mm to about 300 mm, from about 200 mm to about 275 mm, from about 200 mm to about 250 mm, or from about 200 mm to about 225 mm. In some embodiments with a convex surface, the thickness of the substrate may be 1.1 mm and the R' may be in a range from about 350 mm to about 450 mm, from about 375 mm to about 450 mm, from about 300 mm to about 450 mm, form about 325 mm to about 450 mm, from about 350 mm to about 425 mm, from about 350 mm to about 400 mm, or from about 350 mm to about 375 mm. In some embodiments with a convex surface, the thickness of the substrate may be 1.3 mm and the R' may be in a range from about 450 mm to about 550 mm, from about 475 mm to about 550 mm, from about 400 mm to about 550 mm, form about 425 mm to about 550 mm, from about 450 mm to about 525 mm, from about 450 mm to about 500 mm, or from about 450 mm to about 475 mm.

[0061] In one or more embodiments, a portion of one or both major surfaces comprises a concave shape and an R' (maximum radius of curvature) of the concave shape is in a range from about 20 mm to about 500 mm. In some embodiments with a concave surface, the thickness of the substrate may be 0.4 mm and the R' may be in a range from about 15 mm to about 100 mm, from about 30 mm to about 100 mm, from about 50 mm to about 100 mm, form about 75 mm to about 100 mm, from about 15 mm to about 75 mm, from about 15 mm to about 50 mm, or from about 15 mm to about 30 mm. In some embodiments with a concave surface, the thickness of the substrate may be 0.55 mm and the R' may be in a range from about 20 mm to about 150 mm, from about 40 mm to about 150 mm, from about 50 mm to about 150 mm, form about 75 mm to about 150 mm, from about 20 mm to about 125 mm, from about 20 mm to about 100 mm, or from about 20 mm to about 75 mm. In some embodiments with a concave surface, the thickness of the substrate may be 0.7 mm and the R' may be in a range from about 25 mm to about 175 mm, from about 50 mm to about 175 mm, from about 75 mm to about 175 mm, form about 100 mm to about 175 mm, from about 150 mm to about 175 mm, from about 25 mm to about 150 mm, from about 25 mm to about 125 mm, from about 25 mm to about 100 mm or from about 25 mm to about 75 mm. In some embodiments with a concave surface, the thickness of the substrate may be 1.1 mm and the R' may be in a range from about 40 mm to about 225 mm, from about 50 mm to about 225 mm, from about 75 mm to about 225 mm, form about 100 mm to about 225 mm, from about 150 mm to about 225 mm, from about 40 mm to about 200 mm, from about 40 mm to about 175 mm, from about 40 mm to about 150 mm or from about 40 mm to about 100 mm. In some embodiments with a concave surface, the thickness of the substrate may be 1.3 mm and the R' may be in a range from about 150 mm to about 250 mm, from about 175 mm to about 250 mm, from about 200 mm to about 250 mm, form about 225 mm to about 250 mm, from about 150 mm to about 225 mm, from about 150 mm to about 200 mm, or from about 150 mm to about 175 mm.

[0062] In some embodiments, the cold-formed glass substrate is strengthened (prior to being cold-formed). For example, the glass substrate may be strengthened by any one or more of thermal strengthening, chemical strengthening, mechanical strengthening or by a combination thereof. In some embodiments, strengthened glass substrate have a compressive stress (CS) layer extending from a surface of the substrate thereof to a compressive stress depth (or depth of compressive stress layer or DOL). The depth of compression is the depth at which compressive stress switches to tensile stress. The region within the glass substrate exhibiting a tensile stress is often referred to as a central tension or CT layer.

[0063] As used herein, "thermally strengthened" refers to glass substrates that are heat treated to improve the strength of the substrate. In thermally- strengthened glass substrates, the CS layer is formed by heating the substrate to an elevated temperature above the glass transition temperature (i.e., near or approaching the glass softening point), and then cooling the glass surface regions more rapidly than the inner regions of the glass. The differential cooling rates between the surface regions and the inner regions generates a residual CS layer at the surfaces.

[0064] Factors that impact the degree of surface compression generated by thermal strengthening processes include the air-quench temperature, volume, and other variables that create a surface compression of at least 10,000 pounds per square inch (psi). In chemically strengthened glass substrates, the replacement of smaller ions by larger ions at a temperature below that at which the glass network can relax produces a distribution of ions across the surface of the glass that results in a stress profile. The larger volume of the incoming ion produces the CS layer extending from a surface and the CT layer in the center of the glass.

[0065] Chemical strengthening may be achieved by an ion exchange process which includes immersion of a glass substrate into a molten salt bath for a predetermined period of time to allow ions at or near the surface(s) of the glass substrate to be exchanged for larger metal ions from the salt bath. In some embodiments, the temperature of the molten salt bath is from about 375 °C to about 450 °C and the predetermined time period is in the range from about four to about eight hours. In one example, sodium ions in a glass substrate are replaced by potassium ions from the molten bath, such as a potassium nitrate salt bath, though other alkali metal ions having larger atomic radii, such as rubidium or cesium, can replace smaller alkali metal ions in the glass. In another example, lithium ions in a glass substrate are replaced by potassium and/or sodium ions from the molten bath that may include potassium nitrate, sodium nitrate or a combination thereof, although other alkali metal ions having larger atomic radii, such as rubidium or cesium, can replace smaller alkali metal ions in the glass. In some embodiments, smaller alkali metal ions in the glass substrate can be replaced by Ag+ ions. Similarly, other alkali metal salts such as, but not limited to, sulfates, phosphates, halides, and the like may be used in the ion exchange process. The glass substrate may be immersed in a single bath or in multiple and successive baths which may have the same or different composition and/or temperature from one another. In some embodiments, the immersion in such multiple baths may be for different periods of time from one another.

[0066] In mechanically- strengthened glass substrates, the CS layer is generated by a mismatch of the coefficient of thermal expansion between portions of the glass substrate.

[0067] In strengthened glass substrates, the DOL is related to the CT value by the following approximate relationship (Equation 1):

CT « (CS X DOL)/(thickness - (2 X DOL)) (1) where thickness is the total thickness of the strengthened glass substrate. Unless otherwise specified, CT and CS are expressed herein in megaPascals (MPa), whereas thickness and DOL are expressed in millimeters or microns. Unless otherwise described, the CS value is the value measured at the surface and the CT value is the tensile stress value (as determined by Equation 1). CS values and CT values provided herein are provided as absolute values.

[0068] In some embodiments, a strengthened cold-formed glass substrate can have a surface CS of 300 MPa or greater, e.g., 400 MPa or greater, 450 MPa or greater, 500 MPa or greater, 550 MPa or greater, 600 MPa or greater, 650 MPa or greater, 700 MPa or greater, 750 MPa or greater or 800 MPa or greater. In some embodiments, the surface CS is the maximum CS in the cold-formed glass substrate. The strengthened cold-formed glass substrate may have a DOL of 15 micrometers or greater, 20 micrometers or greater (e.g., 25, 30, 35, 40, 45, 50 micrometers or greater). In one or more embodiments, the strengthened cold-formed glass substrate may include a maximum CT value of 10 MPa or greater, 20 MPa or greater, 30 MPa or greater, 40 MPa or greater (e.g., 42 MPa, 45 MPa, or 50 MPa or greater) but less than 100 MPa (e.g., 95, 90, 85, 80, 75, 70, 65, 60, 55 MPa or less). In one or more specific embodiments, the strengthened cold-formed glass substrate has one or more of the following: a surface CS greater than 500 MPa, a DOL greater than 15 micrometers, and a maximum CT of greater than 18 MPa.

[0069] The CS and DOL may be determined by surface stress meter such as the commercially available FSM-6000 instrument, manufactured by Orihara Industrial, Co., Ltd. (Tokyo, Japan). Surface stress measurements rely upon the accurate measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass. SOC in turn is measured by those methods that are known in the art, such as fiber and four point bend methods, both of which are described in ASTM standard C770-98 (2013), entitled "Standard Test Method for Measurement of Glass Stress-Optical Coefficient," the contents of which are incorporated herein by reference in their entirety, and a bulk cylinder method.

[0070] The materials for the glass substrates may be varied. The glass substrates used to form the articles described herein can be amorphous or crystalline. In this regard, the use of the term "glass" is general and is intended to encompass more than strictly amorphous materials. Amorphous glass substrates according to some embodiments can be selected from soda lime glass, alkali aluminosilicate glass, alkali containing borosilicate glass and alkali aluminoborosilicate glass. Examples of crystalline glass substrates can include glass- ceramics, sapphire or spinel. Examples of glass-ceramics include Li ₂ 0-Al ₂ 0 ₃ -Si0 ₂ system (i.e. LAS-System) glass ceramics, MgO-Al ₂ 0 ₃ -Si0 ₂ System (i.e. MAS-System) glass ceramics, glass ceramics including crystalline phases of any one or more of mullite, spinel, ex- quartz, β-quartz solid solution, petalite, lithium disilicate, β-spodumene, nepheline, and alumina.

[0071] Glass substrates may be provided using a variety of different processes. For example, exemplary glass substrate forming methods include float glass processes and down- draw processes such as fusion draw and slot draw. A glass substrate prepared by a float glass process may be characterized by smooth surfaces and uniform thickness is made by floating molten glass on a bed of molten metal, typically tin. In an example process, molten glass that is fed onto the surface of the molten tin bed forms a floating glass ribbon. As the glass ribbon flows along the tin bath, the temperature is gradually decreased until the glass ribbon solidifies into a solid glass substrate that can be lifted from the tin onto rollers. Once off the bath, the glass substrate can be cooled further and annealed to reduce internal stress.

[0072] Down-draw processes produce glass substrate having a uniform thickness that possess relatively pristine surfaces. Because the average flexural strength of the glass substrate is controlled by the amount and size of surface flaws, a pristine surface that has had minimal contact has a higher initial strength. Down-drawn glass substrate may be drawn into a sheet having a thickness of less than about 2 millimeters. In addition, down drawn glass substrate have a very flat, smooth surface that can be used in its final application without costly grinding and polishing. [0073] The fusion draw process, for example, uses a drawing tank that has a channel for accepting molten glass raw material. The channel has weirs that are open at the top along the length of the channel on both sides of the channel. When the channel fills with molten material, the molten glass overflows the weirs. Due to gravity, the molten glass flows down the outside surfaces of the drawing tank as two flowing glass films. These outside surfaces of the drawing tank extend down and inwardly so that they join at an edge below the drawing tank. The two flowing glass films join at this edge to fuse and form a single flowing sheet of glass. The fusion draw method offers the advantage that, because the two glass films flowing over the channel fuse together, neither of the outside surfaces of the resulting sheet of glass comes in contact with any part of the apparatus. Thus, the surface properties of the fusion drawn sheet of glass are not affected by such contact.

[0074] The slot draw process is distinct from the fusion draw method. In slow draw processes, the molten raw material glass is provided to a drawing tank. The bottom of the drawing tank has an open slot with a nozzle that extends the length of the slot. The molten glass flows through the slot/nozzle and is drawn downward as a continuous sheet and into an annealing region.

[0075] In one or more embodiments, the article includes a single glass substrate. In one or more embodiments, the article may include a second glass substrate. In such embodiments, the second glass substrate forms a laminate with the cold-formed glass substrate. In one or more embodiments, the second glass substrate is cold-formed to have the same curve or non-planar shape as the cold-formed glass substrate. In some embodiments, the glass substrates may be separated by an interlayer, thus laminates according to some embodiments comprise at least two glass substrates bonded together by an interlayer. In such embodiments, one major surface of the cold-formed glass substrate is coupled to the non- planar rigid support structure, the opposing major surface of the cold-formed glass substrate is in contact with the interlayer, which will be disposed between the cold-formed glass substrate and the second glass substrate. Examples of suitable interlayers include poly(vinyl butyral) (PVB) , ethylenevinylacetate (EVA), polyvinyl chloride (PVC), ionomers, and thermoplastic polyurethane (TPU). The second glass substrate may be strengthened

(chemically, thermally, and/or mechanically) as described above.

[0076] The second glass substrate may face a user, while the cold-formed glass substrate may face the opposite direction. For example, when the article is used as in the interior of a vehicle, in an appliance or an architectural element, the second glass substrate may form the user interface. In vehicle applications such as automotive glazings, the cold- formed glass substrate may be exposed to a vehicle or automobile interior and the second glass substrate may face an outside environment of the automobile, and vice versa. In automotive interiors, the cold-formed glass substrate is unexposed and faces (and the rigid non-planar support structure) an underlying support (e.g., a display, dashboard, center console, instrument panel, seat back, seat front, floor board, door panel, pillar, arm rest etc.), and the second glass substrate is exposed to the vehicle or automobile interior and thus the user. In architectural applications, the second glass substrate is exposed to a building, room, or furniture interior and the first ply faces an outside environment of the building, room or furniture.

[0077] Some embodiments of the articles disclosed herein are useful in automobile interiors because such articles provide a curved cover compatible with curved displays. To be compatible with a curved display, a cover should match the shape of the curved display closely to insure optimal fit and enable a high quality viewing. It is also desirable to provide a cover that is high optical quality and cost effective. Thermal forming a cover to the precise shape presents challenges in attaining that desired shape. In addition, when glass is used, it is a challenge to minimize the downside effects of heating the cover to its softening point (e.g., distortion, and marking). The concept of cold-forming addresses these issues and permits the use of glass but creates new challenges in providing a sufficient support to maintain the cold- form shape and provide rigidity. The ability to cold-form a thin glass substrate to the prescribed shape presents the opportunity for a high quality, cost effective solution.

[0078] The embodiments of the article described herein include a cold-formed glass substrate that is supported by the non-planar rigid support structure so the cold-formed glass substrate maintains a curved shape, while the stresses generated by cold-forming are minimize. In embodiments where a display is incorporated into the article, the cold-formed glass substrate surface conforms to the display shape.

[0079] With respect to high quality, the articles described herein enable superior fit to curved displays and exhibit high optical quality. Cold-formed glass substrates may possess a flexible characteristic able to accommodate the curved display. Cold-forming maintains the high quality of the flat glass substrate that could be diminished in a thermal forming process. This concept also allows excellent stress management, minimizing the cold-form stress by providing support over a large area.

[0080] Moreover, the articles described herein are also compatible with coatings and surface treatments that are often desirable. More specifically, the articles described herein can easily integrate high quality coatings and surface treatments on a curved substrate surface, where such coatings are typically limited to flat parts. For example, AR and AG coatings and AG surfaces may improve display visibility in a variety of challenging ambient lighting conditions; however, high-quality multi-layer AR coating processes are typically applied utilizing vapor deposition or sputter coating techniques. These techniques are usually limited to deposition on flat surfaces due to the nature of the process. Providing these coatings on a curved three dimensional surface is challenging and further adds to the cost of the process. In accordance with one or more embodiments, coatings and/or surface treatments may be applied to a glass substrate prior to cold-forming, and cold-forming the coated and/or treated glass substrate in turn avoids the issues associated with thermal forming (i.e., damage to the coating and/or surface treatment from handling and/or high processing temperature). In one or more embodiments, the coating may be an ink coating, an antireflective coating, an antiglare coating and/or any other suitable coating. In one or more embodiments, the surface treatment may include an antiglare surface, a haptic surface that provides tactile feedback, recessed and/or raised portions providing indicia and the like. Decorative ink coatings can be applied to a variety of shaped/curved surfaces, however the process to apply these coating to flat surfaces are simpler, better established, and more cost effective. Further, surface treatments (typically formed by etching treatments) are also typically applied to flat surfaces. Accordingly, the articles described herein permit application of coatings and/or surface treatments on substantially flat glass substrates, which are then cold-formed into curved shapes. The cold-forming process does not degrade the coating or surface treatment in the same manner as some thermal processes.

[0081] Another aspect of this disclosure pertains to a process of forming the articles described herein. In one or more embodiments, the process transforms a substantially flat glass substrate (such as the glass substrates described herein), which can optionally include the above-described coatings or surface treatments, into a cold-formed glass substrate that is sufficiently support to exhibit and maintain a desired shape. In one or more embodiments, the process includes cold-forming a substantially flat glass substrate to a shape that matches or approximates the shape of a curved display.

[0082] In some embodiments, a die is used to cold-form the glass substrate into the desired shape. As used herein, a die includes a structure used to impart a desired shape to a glass substrate, and to attach a non-planar rigid support structure to the glass substrate. The die itself is not a part of the finished article, but rather may be used repeatedly to create many finished articles. In one or more embodiments, the term "die" refers to a tool used to impart a desired shape upon an object. In such embodiments, "die" has at least two parts, a first part and a second part, that may be pressed together to impart a desired shape on a flexible object disposed between the first and second parts. In one or more embodiments, the die is also used to bond a non-planar rigid support structure to the cold-formed substrate while the die is imparting the desired shape. Once the non-planar rigid support structure is bonded to the cold-formed glass substrate, the die may be removed, and the non-planar rigid support structure maintains the desired shape of the cold-formed glass substrate. A die may be reused many times to reproducibly and precisely create the same shape for multiple articles comprising a non-planar rigid support structure bonded to a cold-formed glass substrate.

[0083] In some embodiments, an injection molding process is used to transform the substantially flat glass substrate described herein to a cold-formed glass substrate having a curved shape. In one or more embodiments, a support structure is injection molded on a major surface of the glass substrate. In one or more embodiments, the glass substrate may be cold-formed prior to injection molding the support structure. The inj ection molded support structure forms a non-planar rigid support structure that holds the cold-formed glass substrate to the prescribed shape. In some embodiments, injection molding is used to form a non-planar rigid support structure bonded to a surface of a cold-formed glass substrate. Any suitable injection molding process and material(s) may be used. For example, polyvinyl chloride (PVC) and thermoplastic polyurethane (TPU) are two common materials used to injection mold the non-planar rigid support structure. Reaction injection molding (RIM) may be used in some embodiments. Common materials used in RIM include polyurethane polyureas, polyisocyanurates, polyesters, polyphenols, polyepoxides, and nylon 6. Different materials may have different operating parameters. The machines, operating parameters (e.g. , pressure, flow rate, temperature), and mold design may be different for different materials. Typical injection molding temperatures range from 300°F to 450°F, and typical process pressures can range from the 200psi to higher than lOOOpsi; however, any suitable process parameters may be used.

[0084] In some embodiments, a direct bonding process is used to cold-form and bond a substantially flat glass substrate to a non-planar rigid support structure, with the non-planar rigid support structure providing rigidity to the cold-formed glass substrate and holding the cold-formed glass substrate into a desired curved or non-planar shape.

[0085] Various techniques other than direct bonding or injection molding may be used to achieve the articles described herein. [0086] Embodiments of the processes are illustrated in the Figures, which are not necessarily drawn to scale. The different parts of various figures may have some parts not drawn to scale relative to other parts in order to better illustrate concepts.

[0087] FIG. 1 illustrates an injection mold die 110 designed with a specific desired curved shape, and a flat glass substrate 120 with opposing major surfaces 121 and 122.

Injection mold die 110 includes two parts, a first die part 111 and a second die part 112. First and second die parts 111 and 112 have a curved shape corresponding to that desired for a cold-formed glass substrate. First die part 111 includes recesses 113 adapted to receive molten material as a part of an injection-molding process. Flat glass substrate 120 is disposed between first and second die parts 111 and 112, but is not yet cold-formed.

[0088] FIG. 2 illustrates the die 110 of FIG. 1 cold-forming a substantially flat glass substrate 120 into a non-planar shape. The cold-forming is accomplished by pressing together first and second die parts 111 and 112 while glass substrate 120 is disposed in between. In FIG. 2, recesses 113 remain empty.

[0089] FIG. 3 illustrates the die of FIG. 2 after material has been injection-molded into recesses 1 13 to form a non-planar rigid support structure 130 bonded to the back of the cold-formed glass substrate 120.

[0090] FIG. 4 illustrates the die of FIG. 3 and the resultant article after first and second die parts 111 and 112 retract. The resultant article is a cold-formed glass substrate 120 bonded to a non-planar rigid support structure 130. Cold- formed glass substrate 120 retains the curvature imparted by first and second die parts 111 and 112 because of the rigidity of non-planar rigid support structure 130. Each of the opposing major surfaces (first major surface 121 and second major surface 122) are in tension or compression depending on the direction of curvature. In FIG. 4, first major surface 121 at a first position 121 A that is adjacent the non-planar rigid support structure 130 is in tension while the second major surface 122 at a second position 122A adjacent the non-planar rigid support structure 130 is in compression. Accordingly, the second major surface 122 at a second position 122 A exhibits a greater surface compressive stress than the first major surface 121 at a first position 121 A. This is exhibited even when substrate 120 is strengthened as described herein and exhibits a surface compressive stress prior to being cold-formed.

[0091] FIG. 5 illustrates cold-formed glass substrate 120 bonded to non-planar rigid support structure 130 of FIG. 4, with additional adhesive 140 added along the interface where cold-formed glass substrate 120 is bonded to non-planar rigid support structure 130.

Additional adhesive 140 is optional, and may help improve bonding between cold-formed glass substrate 120 and non-planar rigid support structure 130. Although additional adhesive 140 may be applied without using a mold, the overall structure still benefits from the precision obtained by using a mold to bond cold-formed glass substrate 120 to non-planar rigid support structure 130.

[0092] FIG. 6 illustrates a perspective view of cold-formed glass substrate 120 bonded to a non-planar rigid support structure 130.

[0093] FIG. 7 illustrates a top view of a cold-formed glass substrate 120 bonded to a non-planar rigid support structure 130. The curvature is not visible due to the angle of the view. Line 7-7' shows a cross section illustrated by FIGS. 1-5. FIGS. 8-11 illustrate a similar cross section.

[0094] FIG. 8 illustrates a direct-bonding die 810 designed with a specific desired curved shape, and a flat glass substrate 820. Direct-bonding die 810 includes two parts, a first die part 811 and a second die part 812. First and second die parts 811 and 812 have a curved shape corresponding to that desired for a cold-formed glass substrate. First die part 811 includes recesses 813 adapted to receive a non-planar rigid support structure 830 formed by a separate process. Non-planar rigid support structure 830 may be formed by any suitable process, such as injection molding. Non-planar rigid support structure 830 has been inserted into recesses 831 in first die part 811. Optionally, adhesive layer 831 may be applied to non- planar rigid support structure 830 by any suitable process, before or after non-planar rigid support structure 830 is inserted into recesses 831. Flat glass substrate 820 is disposed between first and second die parts 811 and 812, but is not yet cold-formed.

[0095] FIG. 9 illustrates die 810 of FIG. 8 cold-forming glass substrate 820 into a non-planar shape and bonding the non-planar rigid support structure to the cold-formed glass substrate. The cold-forming is accomplished by pressing together first and second die parts 811 and 812 while glass substrate 820 is disposed in between. This pressing together of first and second die parts 811 and 812 also brings non-planar rigid support structure 830 into contact with glass substrate 820, and direct-bonds non-planar rigid support structure 830 to glass substrate 820. Recesses 813 ensure precise positioning of non-planar rigid support structure 830 relative to glass substrate 820.

[0096] FIG. 10 illustrates die 810 of FIG. 9 and the resultant article after die 810 retracts. The resultant article is a cold-formed glass substrate 820 bonded to non-planar rigid support structure 820. Optionally, adhesive layer 831 may assist with such bonding. Cold- formed glass substrate 820 retains the curvature imparted by first and second die parts 811 and 812 because of the rigidity of non-planar rigid support structure 830. [0097] FIG. 11 illustrates cold-formed glass substrate 820 bonded to non-planar rigid support structure 830 of FIG. 10, with additional adhesive 840 added along the interface where cold-formed glass substrate 820 is bonded to non-planar rigid support structure 830. Additional adhesive 840 is optional, and may help improve bonding between cold-formed glass substrate 820 and non-planar rigid support structure 830. Although additional adhesive 840 may be applied without using a mold, the overall structure still benefits from the precision obtained by using a mold to bond cold-formed glass substrate 820 to non-planar rigid support structure 830.

[0098] FIG. 12 shows a process flowchart corresponding to the process illustrated in

FIGS 1 to 5. The following steps are performed, in order:

[0099] Step 1210 - Die 110 is used to cold-form glass substrate 120 into a desired shape.

[0100] Step 1220 - Rigid support structure 130 is formed in recesses 113 and bonded to cold-formed glass substrate 120 by injection molding.

[0101] Step 1230 - Die 110 is removed.

[0102] Step 1240 - Optionally, additional adhesive 140 is applied.

[0103] FIG. 13 shows a process flowchart corresponding to the process illustrated in

FIGS 8 to 10. The following steps are performed, in order:

[0104] Step 1310 - Rigid support structure 830 is placed in recesses 813.

[0105] Step 1320 - Die 810 is used to cold-form glass substrate 820 into a desired shape while direct bonding rigid support structure 830 to cold-formed glass substrate 820.

[0106] Step 1330 - Die 810 is removed.

[0107] Step 1340 - Optionally, additional adhesive 840 is applied.

[0108] FIG. 14 illustrates a die 1410 having first die part 1411 and second die part

1412. First die part 1413 includes recesses 1413. As illustrated, both first die part 1411 and second die part 1412 include ridges 1414 useful for precisely positioning glass substrate 1420 relative to first and second die parts 1411 and 1412. This allows a rigid support structure to be precisely placed relative to glass substrate 1420, whether by injection molding, direct bonding, or other die-based process. In some embodiments, ridges may be present on only one of first die part 1411 and second die part 1412. In some embodiments, ridges 1414 may be absent.

[0109] FIG. 15 shows an example of a part, a section of an automotive interior display, including but not limited to an instrument cluster, a console display, or a center stack display, having a monitor, that may be made in some embodiments. A cold-formed glass substrate is bonded to a rigid support structure 1530. Cold-formed glass substrate 1510 includes an open region 1550 that is not in direct contact with non-planar rigid support structure 1530. Open region 1550 has a curved shape maintained by the non-planar rigid support structure 1530. A monitor or display may be laminated to open region 1550. Rigid support structure 1530 may be designed to be attached to other parts of an automobile (such as a dashboard, center console, instrument panel, seat back, seat front, floor board, door panel, pillar, arm rest etc.) or an architectural application (such as a wall, window, wall panel, furniture, appliance, door, etc.). The embodiment of FIG. 15 may be formed by any of various processes disclosed herein, including the embodiment of FIG. 12 and the embodiment of FIG. 13.

[0110] FIG. 16 illustrates a top view of a cold-formed glass substrate 120 bonded to a non-planar rigid support structure 130. The curvature is not visible due to the angle of the view. The interior of non-planar rigid support structure 130 defines an open region 1610 of the cold- formed glass substrate that is not in direct contact with the non-planar rigid support structure. Open region 1610 has a curved shape maintained by the non-planar rigid support structure. Display 1620 is attached to cold-formed glass substrate 120. Display 1620 is visible through open region 1610 of cold-formed glass substrate 120.

[0111] In some embodiments, glass substrate is cold-formed into a curved shape, which may include a developable surface or a complex developable surface. A force holding the cold-formed glass substrate in such shapes is applied and maintained across different portions or the entirety of a major surface of the cold-formed glass that is coupled to a non- planar rigid support structure. In one or more embodiments, the force is applied and maintained at a plurality of non-planar points until the coupling is sufficient to maintain the shape. For example, in the embodiment of FIGS. 1-5, injection mold die 110 may be maintained in the position shown in FIG. 3 until the material of non-planar rigid support structure 130 is sufficiently solidified and bonded to glass substrate 120 to maintain the cold formed shape of glass substrate 120 in the absence injection mold die 110. Similarly, in the embodiment of FIGS. 8-10, direct-bonding die 810 may be maintained in the position shown in FIG. 9 until the adhesive layer 831 is sufficiently cured, and glass substrate 820 is sufficiently bonded to rigid support structure 830 to maintain the cold formed shape of glass substrate 820 in the absence direct bonding die 810.

[0112] Force may be "maintained" in an area by application of force in spaced or periodic parts of the area. For example, direct bonding die 810 may contact glass substrate 820 everywhere except where rigid support structure 830 is present, as shown in FIG. 9. Or, there may be gaps in such contact, where contact is maintained at enough points to hold glass substrate 820 in place until adhesive layer 830 can cure.

[0113] If force is not applied and maintained across different regions of a complex developable surface, complications may arise. For example, if, instead of using a die process or other process that applies and maintains force, a single roller is used, it may be difficult to bond a glass substrate to a rigid support structure having a complex developable surface. At the very least, yield is expected to suffer. Without being bound by theory, internal stress exists in cold-formed glass. In the absence of external constraints, this stress will move the glass towards its initial shape.

[0114] For example, as shown in FIG. 17, a single roller 1790 is used to press an initially planar glass substrate 1720 against a rigid support structure 1730 having a complex developable surface - three adjacent cylindrical surfaces, where the middle surface has a concavity opposite the outer two. An adhesive layer 1731 is present on rigid support structure 1730. As roller 1790 passes from left to right, stresses in the cold-formed glass substrate 1720 to the left of roller 1790 will tend to return glass substrate 1720 to a planar shape, as illustrated by arrows 1780. These stresses may lead to delamination, or low yield. For simple shapes, this phenomena may not be present (for example in a plane), or may be addressed in other ways (for example, when adhering glass with adhesive to the inside of a cylinder, a slight compressive force across the plane of the glass may push the glass against the adhesive everywhere as the adhesive cures). But, for complex developable surfaces, particularly those with different regions having different concavity, application and maintenance of force is preferred.

[0115] Another aspect pertains to a vehicle interior system that includes a base including a non-planar support structure, and a cold-formed glass substrate (or laminate including a cold-formed substrate, as described herein) disposed on the non-planar support structure. In one or more embodiments, the base includes a display disposed between the non- planar support structure and the cold-formed substrate (or laminate including a cold-formed substrate). The display may be curved. In one or more embodiments, a cold-formed glass substrate comprises a thickness of 1.5 mm or less (or from about 0.4 mm to about 1.3 mm).

[0116] In one or more embodiments, the cold-formed glass substrate used in such vehicle interior systems comprises a glass surface, and wherein at all point of the glass surface have a Gaussian curvature (GC) that is equal to zero (GC=Kmax*Kmin, wherein Kmax and Kmin are principal curvatures defined as Kmax = 1/R' and Kmin = 1/R"), and wherein one of Kmax and Kmin is non-zero, R' is the maximum radius of curvature and R" is the minimum radius of curvature. The glass surface may be one or both the opposing major surfaces of the cold-formed glass substrate

[0117] In one or more embodiments, the base comprises any one of a center console, a dashboard, an arm rest, a pillar, a seat back, a floor board, a headrest, a door panel, and a steering wheel. The vehicle may be any one of an automobile, a seacraft, and an aircraft.

[0118] Embodiments of the present disclosure are described in detail herein with reference to embodiments thereof as illustrated in the accompanying drawings, in which like reference numerals are used to indicate identical or functionally similar elements. References to "one embodiment," "an embodiment," "some embodiments," "in certain embodiments," etc. , indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.

[0119] As used herein, "comprising" is an open-ended transitional phrase. A list of elements following the transitional phrase "comprising" is a non-exclusive list, such that elements in addition to those specifically recited in the list may also be present.

[0120] The following examples are illustrative, but not limiting, of the present disclosure. Other suitable modifications and adaptations of the variety of conditions and parameters normally encountered in the field, and which would be apparent to those skilled in the art, are within the spirit and scope of the disclosure.

[0121] Aspect (1 ) of this disclosure pertains to a process comprising: cold-forming a flat glass substrate into a non-planar shape using a die; and bonding the cold-formed glass substrate to a non-planar rigid support structure at a plurality of non-planar points using the die.

[0122] Aspect (2) of this disclosure pertains to the process of Aspect (1), wherein the die is an injection- molding die, and the bonding is accomplished by injection molding the non-planar rigid support structure onto the cold-formed glass substrate while the die holds the cold-formed glass substrate in the non-planar shape.

[0123] Aspect (3) of this disclosure pertains to the process of Aspect (1), wherein the non-planar rigid support structure is formed prior to the bonding, and the bonding comprises using the die to directly bond the cold-formed glass substrate onto the non-planar rigid support structure.

[0124] Aspect (4) of this disclosure pertains to the process of Aspect (3), further comprising placing the non-planar rigid support structure into a recess in the die prior to bonding.

[0125] Aspect (5) of this disclosure pertains to the process of Aspect (3) or Aspect

(4), further comprising applying an adhesive to at least one of the non-planar rigid support structure and the flat glass substrate prior to bonding.

[0126] Aspect (6) of this disclosure pertains to the process of any one of Aspects (1) through (5), further comprising, after bonding, applying an adhesive to an edge of an interface between the cold-formed glass substrate and the non-planar rigid support structure.

[0127] Aspect (7) of this disclosure pertains to the process of any one of Aspects (1) through (6), further comprising applying a coating to the flat glass substrate prior to cold- forming.

[0128] Aspect (8) of this disclosure pertains to the process of Aspect (7), wherein the coating is an ink coating.

[0129] Aspect (9) of this disclosure pertains to the process of Aspect (7), wherein the coating is an antireflective coating.

[0130] Aspect (10) of this disclosure pertains to the process of any one of Aspects (7) through (9), wherein the cold-formed glass substrate, after bonding to the non-planar rigid support structure, includes an open region not in direct contact with the non-planar rigid support structure, the open region having a curved shape maintained by the non-planar rigid support structure.

[0131] Aspect (11) of this disclosure pertains to the process of Aspect (10), further comprising attaching a display to at least one of the cold formed glass substrate and the non- planar rigid support structure, such that the display is visible through the open region of the cold-formed glass substrate.

[0132] Aspect (12) of this disclosure pertains to the process of any one of Aspects (1) through (11), wherein, during and after cold-forming, the temperature of the glass substrate does not exceed 800 °F.

[0133] Aspect (13) of this disclosure pertains to the process of any one of Aspects (1) through (12), wherein the glass substrate comprises a strengthened glass. [0134] Aspect (14) of this disclosure pertains to the process of any one of Aspects (1) through (13), wherein the cold-formed glass substrate has opposing major surfaces, and wherein one major surface is free of the non-planar rigid support structure.

[0135] Aspect (15) pertains to an article comprising: a cold-formed glass substrate comprising a non-planar shape and a first major surface and an opposing second major surface, the first and second major surfaces comprising a surface compressive stress that differ from one another; a non-planar rigid support structure bonded to the first major surface at a plurality of non-planar points.

[0136] Aspect (16) pertains to the article of Aspect (15), wherein: the non-planar rigid support structure is injection molded onto the cold-formed glass substrate while the cold- formed glass comprises the non-planar shape.

[0137] Aspect (17) pertains to the article of Aspect (15), wherein the cold-formed glass substrate comprises a second major surface opposite the first major surface, the second major surface comprising a coating or surface treatment.

[0138] Aspect (18) of this disclosure pertains to the process of any one of Aspects

(15) through (17), further comprising an edge adhesive applied to an edge of an interface between the cold-formed glass substrate and the non-planar rigid support structure.

[0139] Aspect (19) of this disclosure pertains to the process of any one of Aspects

(15) through (18), wherein the cold-formed glass substrate includes an open region not in direct contact with the non-planar rigid support structure, and the open region has a curved shape maintained by the non-planar rigid support structure.

[0140] Aspect (20) pertains to the article of Aspect (19), further comprising a display attached to at least one of the cold formed glass substrate and the non-planar rigid support structure, wherein the display is visible through the cold-formed glass substrate.

[0141] Aspect (21) of this disclosure pertains to the process of any one of Aspects

(15) through (20), further comprising a coating disposed on the cold- formed glass substrate.

[0142] Aspect (22) of this disclosure pertains to the process of Aspect (21), wherein the coating is an ink coating.

[0143] Aspect (23) of this disclosure pertains to the process of Aspect (21), wherein the coating is an antireflective coating.

[0144] Aspect (24) of this disclosure pertains to an article comprising: a glass substrate having opposing major surfaces and a curved shape, the opposing major surfaces comprising a surface stress that differ from one another, wherein the glass substrate is attached to a rigid support structure having the curved shape, wherein the glass substrate includes an open region not in direct contact with the non-planar rigid support structure, and the open region has a curved shape maintained by the non-planar rigid support structure.

[0145] Aspect (25) of this disclosure pertains to an article comprising: a non-planar rigid support structure having a complex developable surface; a cold-formed glass substrate bonded to the non-planar rigid support structure, the cold formed glass substrate having the complex developable surface.

[0146] Aspect (26) of this disclosure pertains to the article of Aspect (25) or Aspect

(24), further comprising a display attached to at least one of the glass substrate and the non- planar rigid support structure, wherein the display is visible through the open region of the glass substrate.

[0147] Aspect (27) of this disclosure pertains to an article of any one of Aspects (24) through (26), further comprising a coating disposed on the glass substrate.

[0148] Aspect (28) of this disclosure pertains to an article of Aspect (27), wherein the coating is an ink coating.

[0149] Aspect (29) of this disclosure pertains to an article of Aspect (27), wherein the coating is an antireflective coating.

[0150] Aspect (30) of this disclosure pertains to an article of any one of Aspects (24) through (29), wherein the glass substrate is a chemically strengthened glass substrate.

[0151] Aspect (31) of this disclosure pertains to an article of any one of Aspects (24) through (30), wherein one major surface is free of the non-planar rigid support structure.

[0152] Aspect (32) of this disclosure pertains to an article of any one of Aspects (24) through (31), wherein the cold formed glass substrate has a complex developable surface.

[0153] Aspect (33) of this disclosure pertains to vehicle interior system comprising: a base having a curved surface; an article comprising a cold-formed glass substrate disposed on the curved surface, wherein the glass substrate comprises a surface, and wherein at all point of the surface have a Gaussian curvature (GC) that is equal to zero (GC=Kmax*Kmin, wherein Kmax and Kmin are principal curvatures defined as Kmax = 1/R' and Kmin = 1/R"), and wherein one of Kmax and Kmin is non-zero, R' is the maximum radius of curvature and R" is the minimum radius of curvature.

[0154] Aspect (34) pertains to the vehicle interior system of Aspect (33), wherein the glass substrate has a thickness of about 1.5 mm or less.

[0155] Aspect (35) pertains to the vehicle interior system of Aspect (33) or Aspect

(34), wherein a portion of the surface comprises a concave shape and R' of the concave shape is in a range from about 37.5 mm to about 500 mm. [0156] Aspect (36) pertains to the vehicle interior system of Aspect (33) or Aspect

(34), wherein a portion of the surface comprises a convex shape and R' of the convex shape is in a range from about 20 mm to about 500 mm.

[0157] Aspect (37) pertains to the vehicle interior system of any one of Aspects (33) through (36), further comprising a display.

[0158] Aspect (38) pertains to the vehicle interior system of Aspect (37), wherein the display is disposed between the base and the article.

[0159] Aspect (39) pertains to the vehicle interior system of Aspect (37) or Aspect

(38), wherein the display is curved.

[0160] Aspect (40) pertains to the vehicle interior system of any one of Aspects (33) through (39), wherein the glass substrate is strengthened.

[0161] While various embodiments have been described herein, they have been presented by way of example only, and not limitation. It should be apparent that adaptations and modifications are intended to be within the meaning and range of equivalents of the disclosed embodiments, based on the teaching and guidance presented herein. It therefore will be apparent to one skilled in the art that various changes in form and detail can be made to the embodiments disclosed herein without departing from the spirit and scope of the present disclosure. The elements of the embodiments presented herein are not necessarily mutually exclusive, but may be interchanged to meet various needs as would be appreciated by one of skill in the art.

[0162] Embodiments described herein may be combined in any permutation.

[0163] It is to be understood that the phraseology or terminology used herein is for the purpose of description and not of limitation. The breadth and scope of the present disclosure should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.