Leather-surface repair-composition and the method for surface repair of leather surfaces

FIELD OF THE INVENTION

The invention refers to a leather surface repair set and a method for surface repair for leather surfaces.

BACKGROUND OF THE INVENTION

For coloring and fosterage of highly utilized leather surfaces, like car seats, steering- wheels, motorcyclist's clothes and equipment and the like various compositions and methods of applying such compositions are known :

EP 0 572 353 A1 describes a method of coloring leather with a polyazo dye with at least two sulphur groups and some alkali halogenide.

EP 0 071 420 B2 describes a method of after tanning of leather of oligomers on acryl basis.

EP 0 492 608 A2 describes a process for producing leather comprising the steps of pre- treatment, tanning and finishing, the finishing steps including treatment with fatting agent and top finish. A fatting agent for leather is also known from DE-C-22 45 077.

JP 2005 264130 A1 describes a preserving cream for leather without using volatile components or vaseline which is stable for a long period without degradation and applicable to all leather products .

EP 0 927 271 B1 describes a leather-treatment agent which is obtained by polymerization of 70 - 100 wt.-% acrylic acid and/or methacrylic acid and/or the acid chlorides and/or anhydrides thereof with 0 - 30 wt.-% of other water-soluble monomers copoly- merizable with the first component and 0 - 20 wt.-% of water insoluble monomers co- polymerisable with the two first components. Said polymer being reacted with amines of formula R ₁ -NH-R ₂ , wherein Ri represents a Ci ₂ - C ₃₀ alkyl or alkenyl residue and R ₂ represents H, _a C ₁ - C ₄ alkyl or C ₁ - C ₂ hydroxyalkyl residue. Such leather treatment agents are used producing low-fogging leathers, i.e. leathers which do not deliver to much material which may condense on the surface of the window panels of a car, i. e. without making the window panel too foggy.

Chinese Publication 2002-68 31 96 (XP 002143103) proposes a polyurethane leather repairing agent consisting amongst others a distilled water and a thickener being used to simplify leather repair processes.

DE 195 10 242 A1 discloses a leather sheet which is covered on its outer side with a polyurethane containing watery dispersion. This cover layer is prefabricated in a mould with a surface comparable to the original leather. This prefabricated cover layer is used to ennoble a leather sheet by giving the characteristic look of natural leather to the leather sheet.

US 4 507 413 discloses an aqueous polyurethane reactive coating composition suitable for coating leather and other materials and also containing thickeners and pigments.

All said compositions are used for treating the leather surface as a whole.

Leather-surface-repair composition which can be used for repairing damaged spots like scratches, cuts, imperfections and damaged or injured surfaces, is known from US-PS- 1 ,506,983. These compositions substantially consists of carnauba wax, bees wax, shellac wax, dry shellac and turpentine and a color base. This composition is applied to the leather surface by means of a heated spatula or knife blade and subjected to pressure and a rubbing action for working it into a homogenous state.

DESCRIPTION OF THE INVENTION

For leather surface repair of car seats and other highly utilized leather surfaces or leather clothes which are sometimes scratched like motorcyclist jackets or trousers when the motorcyclist slips over the ground or the like, a leather surface repair composition must be stable enough to bring back to the leather surface its former abrasion resistance. For these and other leather surface repair applications a leather surface repair set according to claim 1 and a method for surface repair of leather surfaces according to claim 18 is proposed. It was found that a polyurethane in form of an emulsion is easy to be applied to smaller spots of leather surfaces to be repaired and allows to shape the service of the composition after being applied in a way very similar to the surface structure of the rest of the leather surface. After the repair action the composition polymerizes in a way in which sufficient flexibility of the leather surface is maintained, while the repaired surface spot is stable enough to allow a long period of use in the repaired state without losing the good look of the repaired spot. The leather-suface repair set according to the invention consists at least of a degreaser and of a composition comprising an emulsion of polyurethane and at least one pigment component and further comprises at least one further component which allows to relatively increase or decrease the elasticity of the reactive composition, i.e. the elasticity of the repaired leather surface and particularly of the colored layer which is applied to the leather surface to be repaired.

According to another object of the invention, the further component is a plasticizer, like a 2-ethylhexyladipate and/or 2-isodecyladipate, and/or a stabilizer like triisodecylphos- phate. 2-ethylhexyladipate and isodecyladipate are used together as a rule, like in form of 2-ethylhexylipodecyladipate. The triisodecylphosphate, as a rule, is used together with the adipate component and this mixture will make the leather surface flexible once dry and will avoid cracking of the leather surface. The amount of these further components is selected so as to increase or decrease the elasticity of the repaired leather to the appropriate extent, taking into account that especially in cars and for motorcycles leather like on the seats or on the steering wheel is highly bonded by the weight of the driver, friction due to drivers movements and chemical stresses and strains due to the exudation of the drivers hands and sometimes dirt or fat on the hands. Typically, in the pigmented polyurethane emulsion composition, the portion in which the elasticity effecting components are applied, are 0,1 to 20 wt-%. _5 to 10% of the adipate component and 0 to 5% of the phosphate component are preferred.

In order to optimize the color of the polyurethane emulsion composition, six colors are preferred for mixing: white, black, yellow, blue, red, ocher. To mix the desired color, polyurethane emulsion compositions which are colored with said six primary colors each are mixed together at the necessary quantities.

To make an emulsion of polyurethane, water is preferred, which avoids the need of using experts to the repair job and accelerates the polymerization step.

!n some cases, the composition may also include a biocide and/or anti foaming agent and/or pigments.

According to another embodiment a thickening agent, particularly an acrylic thickening agent, ammonia and/or propylene glycol and/or matting agents may be comprised in the composition to improve the repair result.

The composition may be applied manually and may be used in one or more layers according to the adsorption of the leather and/or the deepness of scratches or the like which are to be repaired. Also excellent rub resistance is a factor for good repair results. Before applying, the composition is a viscose fluid having a dry content preferably between 20 and 40 % and particularly around 30 %. The pH-value is preferred to be between 6 and 10 and most preferred between 7,0 and 9,0.

While a degreaser and the colored repair composition is sufficient in many cases, the leather surface repair set should also include a repairing paste of repairing leather which is stronger damaged and even may have deep scratches or holes. This repairing paste is used after degreasing and before applying the colored composition. If a repairing paste is used, this can be applied with a spatula spreading a sufficient quantity of repairing paste on the leather surface to be repaired. When the repairing paste has dried sufficiently, for instance for two minutes, and it doesn't stick any more to the fingers, a metal imprint tool may be pressed on the past to print the range of the leather before coloring the repair spot. The repairing paste preferably comprises an aqueous dispersion of polyurethanic and/or acrylic polymers and one or more inert substances. The inert substances preferably comprise an expanded polyurethane and kaolin. The polyurethanic and acryl polymers preferably are use together. Repairing paste may also comprise pigments. However, as a standard, it is not necessary to give the final color to the repairing paste. It is normally sufficient to have the repairing paste color light, i.e. with white pigments, if the final color is a light one or to add dark, like black pigments, if the final color will be a dark one. Of course, the closer coloration of the repairing paste will be to the final color, the less effort will be necessary to recoloring the leather with the pigmented polyurethane emulsion composition.

According to another object of the invention the leather surface repair set further consists of a fixer for fixing the composition on the decreased leather or on the repairing paste being applied on the decreased leather. It was found that a fixer will improve the durability of the repaired leather surface. Aqueous anionic polyurethane dispersions were found to be most favorable for the purpose of the fixer which are known as such

for instance from US patent 5 236 995. In combination with the aqueous an ionic poly- urethane dispersion, a water miscible organic solvent may be comprised in the fixer. Particularly favorable as a water-miscible organic solvent are N-methyl-2-pyrrolidone. The fixer most favorably will be applied with the paint brush on the clean and decreased surface - eventually after a repairing paste has been applied. After drying of fixer the colored polyurethane emulsion composition is applied and this application is, preferably, also performed by using a paint brush and thereafter shaped by a sponge. Thanks to the fixer, it is possible to apply the colored polyurethane emulsion composition even on plastic surfaces which are sometime used as imitation of leather. _Preferably, the fixer comprises 90 to 95 wt-% of an anionic polyurethane and 5 to 10 wt-% of n-methyl-2- pyrrolidone.

The leather surface repair composition according to the invention is particularly suitable inside motor vehicles like for seats, steering-wheels, door panels and the like made of leather and for motorcyclist's clothes and equipment like jackets, trousers, boots, bags and the like. It can be colored in a wide range of known colors and is used to repair the grazed, spotted or worn leather. Is an enables to restore the colored layer of the leather. The composition is applied as an liquid or a cream. For preparing the leather surface the spot to be repaired should be treated with a degreaser like "WaterfloW". The composition may be applied with a paint-brush for liquid composition, or with a cotton rag or applying the composition as a cream. A suitable surface appearance can be received when the applied composition is dabbed with a dry synthetic sponge. This treatment may be repeated of several like two or three times.

Attached hereto, two examples which each show a leather surface before and after repair action.

Fig. 1 A/B showing a seat of a car

Fig. 2A/B showing a motor cyclist jacket

Fig. 3A/B/C/D showing a steering wheel (3B = after first treatment; 3C = after second treatment; 3D = after final treatment)