TECHNICAL FIELD

[0001] The present disclosure relates to liners for bulk containers such as drums and rigid intermediate bu!k containers (!BC) that are abuse-resistant, i.e., show excellent flex-crack resistance, and are barrier-providing. The liners are multi-plied and the plies are rnuSti-Sayered. The !iners comprise multi-layered plies comprising an ethySene-vinyl aicohoi (EVOH) copolymer film layer with a thermoplastic eiasiomer (TPE) centered between linear low density polyethylene (LLDPE) or very Sow density polyethylene (VLDPE) iayers.

BACKGROUND

[0002] Industrial packaging of liquid products needs to meet many kinds of requirements to ensure the product remains protected during shipping. Some requirements include providing oxygen barrier protection and providing abuse resistance such thai the packaging resists cracking and pinholes. Historically, metal-containing polymer films have been used for oxygen barrier purposes as an outer ply of a bulk container liner. The presence of metal in the films, however, makes recycling of the liner complex and expensive. Also historically, mono-layered polymer films of linear low density polyethylene (LLDPE) have been used for abuse resistance as inner plies of the bulk container liners.

[0003] There is an on-going need to provide bulk container liners that provide excellent protection to the products being shipped, while at ihe same time are economical to both make and recycle.

SUMMARY

[0004] In order to minimize the use of metals in bulk container liners, it has been found that multi-layered plies comprising an ethylene-vinyl alcohol

("EVOH") copolymer film with a thermoplastic elastomer (TPE) centered between linear low density polyethylene (LLDPE) or very low density polyethylene

(VLDPE) Iayers provide both oxygen barrier protection and flex crack resistance. Configuration of ihe plies and the layers may be tailored depending on the nature of the liquid products to be packaged.

[0005] Sn an aspect, provided are liners for a bulk container, the liners comprising: at feast one sidewali comprising at ieast first and second plies, each ply independently comprising at least three layers that comprise: a first layer and a third layer each comprising a linear bw density polyethylene {LLDPE) or a very Sow density polyethyiene (VLPDE): and a second layer between the first and third iayers and comprising a thermopiastic oxygen barrier of ethylene-vinyl alcohol copolymer (EVOH) and a thermoplastic elastomer (TPE); and a fitment attached to the at ieast one sidewali.

[0006] Other features that may be used individually or in combination with respect to any aspect of the invention are as follows.

[0007] The liner may be metal-free.

[0008] The TPE may com rise a polyester TPE, a polyamide TPE or a polyurethane TPE. Further, the TPE may be a block copolymer that comprises rigid and fiexibie segments whereby those segments comprise poiyamides, copolyamides, polyesters, copoiyesters, polycarbonates, poiyurethanes, polyethers or copolyethers. The TPE may comprise both aliphatic and aromatic components. The TPE may comprise block copolymers including polyamide- esters, poSyamide-ethers, polyamide-ester-ethers, polyester-esters, polyester- ethers, polyester-ester-ethers, poSyurethane-esters, polyureihane-ethers, polyurethane carbonates and poSyurethane-ester-ethers.

[0009] The first ply may further comprise a fourth layer and a fifth layer, each comprising a polyamide, the fourth Iayer being located between the first and second layers and the fifth layer being located between the second and third iayers. The polyamide may comprise nylon 66, nylon 610, nylon 66/610, nylon 6/66, nylon 1 1 , nylon 6, nylon 66T, nylon 612, nylon 12, nylon 6/12, ny!on 6/69, nylon 46, nylon 6-3-T, nyion MXD-6, nylon MXDt, nylon 12T and nylon 8I/8T or blends thereof.

[0010] The liner may further comprise a third ply adjacent to and having the same composition as the first ply and a fourth ply adjacent to and having the same composition as the second ply. Or, the liner may further comprise a third p!y as an outer ply, the third ply comprising at least three layers that comprise a first iayer and a third layer each comprising a linear low density polyethylene (LLDPE) or a very low density polyethylene (VLDPE), a second iayer between the first and third layers and comprising meta!ized oriented polyethylene terephtha!ate (OPET).

[0011] The first ply may be an outer ply and the second ply may be an inner ply. Or, the first ply may be an inner ply and the second ply may be an outer ply.

[0012] Both the first and second plies may further comprise a fourth layer and a fifth Iayer, each comprising a poiyamide, the fourth layer being located between the first and second layers and the fifth Iayer being located between the second and third layers.

[0013] The layers of the first ply, the second ply, or both plies may be coextruded. The first ply, the second ply, or both plies may further independently comprise one or more tie layers between the at least three layers of both the first and second plies,

[0014] In a detailed aspect, provided is a liner for a bulk container, the !iner comprising at ieast one sidewaiS that comprises: first and second plies, each ply comprising five layers that comprise; a first iayer and a third iayer each

comprising a linear low density polyethylene (LLDPE) or a very low density polyethylene (VLDPE); a second layer between the first and third layers and comprising a thermoplastic oxygen barrier of ethylene-vinyl alcohol copolymer (EVOH) and a thermoplastic elastomer (TPE); a fourth layer and a fifth Iayer, each comprising a poiyamide, the fourth iayer being located between the first and second layers and the fifth layer being located between th second and third layers; third and fourth plies, each ply comprising three layers that comprise: a first layer and a third layer each comprising a linear low density polyethylene (LLDPE) or a very low density polyethylene (VLDPE); a second layer between the first and third layers and comprising a thermoplastic oxygen barrier of ethylene-vinyl alcohol copolymer (EVOH) and a thermoplastic elastomer (TPE); and a fitment attached to the at least one sidewall; wherein all of the layers of the plies are coexiruded and are metal-free. The four plies may be positioned in any sequence relative to one another. In some embodiments, the first piy may be an outer ply and the fourth piy may be an inner ply. Or, the first piy may be an inner ply and the fourth piy may be an outer piy.

[001 S] Other aspects provide methods of making a liner for a bulk container, the methods comprising; coextruding a first polymer resin through a die thereby forming a tubular extrudate comprising at least three layers that comprise a first layer and a third layer each comprising a linear low density polyethylene (LLDPE) or a very low density polyethylene (VLDPE), a second layer between the first and third layers and comprising a thermoplastic oxygen barrier of ethylene-vsny! alcohol copolymer (EVOH) and a thermoplastic elastomer (TPE); collapsing the tubular extrudate between rollers to form a fiat sheet, slitting the sheet to form two separate plies, and winding the two plies onto a roil thereby forming a double wound first film; forming two sidewa!is from the double wound first film; adhering the two sidewaISs to each other to create a seam thereby forming a two-plied bag; and attaching a fitment to one of the sidewalls to form a liner.

[0016] The method may further comprise: coextruding a second polymer resin through a die thereby forming a tubular extrudate comprising at least three layers that comprise a first layer and a third layer each comprising a linear low density polyethylene (LLDPE) o a very low density polyethylene (VLDPE), a second layer between the first and third layers and comprising a thermoplastic oxygen barrier of eihyiene-vinyi alcohol copolymer (EVOH) and a thermoplastic elastomer (TPE), a fourth layer and a fifth layer, each comprising a poiyamide, the fourth layer being located between the first and second layers and the fifth layer being located between the second and third layers; collapsing the tubular extrudate between rollers to form a flat sheet, slitting the sheet to form two separate piies, and winding the two plies onto a roil thereby forming a double wound second polymer film having a first piy and a second piy; placing the first double wound polymer film proximate the second double wound polymer film; and forming two sidewails from the first and second double wound polymer films; adhering the two sidewails to each other to create a seam thereby forming a four- pi ied bag.

10017] In another aspect, provided is a method of providing a liquid product in a bulk container, the method comprising: obtaining the liner of any embodiment disclosed herein; and packaging the iiquid product in the liner. The liquid product may comprise a fruit or vegetable.

[0018] These and other aspects of the invention are described in the detailed description below. In no event should the above summary be construed as a limitation on the claimed subject matter.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] The disclosure may be more completely understood in

consideration of the following detailed description of various embodiments of the disclosure in connection with the accompanying drawings, in which:

[0020] FIGS. 1 -3 are schematic cross-section views of exemplary plies of different embodiments of liners; and

[0021] FIG. 4 is a schematic top view of a liner for a bulk container in accordance with an embodiment.

[0022] The figures are not necessarily to scale. Like numbers used in the figures refer to like components. It will be understood, however, that the use of a number to refer to a component in a given figure is not intended to limit the component in another figure labeled with the same number.

DETAILED DESCRIPTION

[0023] Provided are liners for bulk containers such as drums and rigid intermediate bulk containers. The liners comprise a fitment and at least one sidewa!l having at least two plies that are multi-layered , the plies being sealed together and the fitment being attached to the at least one sidewaSS, The liner fits in a bulk container. [0024] A "ply" as used herein refers to a building block of sldewalls of a liner that may be supplied as a polymer film, A single wound polymer film supplies one ply and a double wound polymer film supplies two plies. Films used to form plies herein may be coextruded.

[002S] A "layer" as used herein refers to a structure of a single polymer- type or a blend of polymers that may be accompanied by additives. Plies used herein are muSti -layered.

[0026] Reference to "outer ply" as used herein refers to the portion of the liner that is subject to wear and tear from the environment during shipping. The outer ply is in contact with an internal surface of a bulk container during use.

[0027] Reference to "inner ply" as used herein refers to the portion of the liner that forms an interio surface of the enclosed liner and directly contacts product that is packaged in the liner.

[0028] As used herein, the term "polymer" refers to the product of a polymerization reaction, and is inclusive of homopo!ymers, copolymers, terpoiymers etc. In general, the layers of a film can consist essentially of a single polymer, or can have still additional polymers together therewith, i.e., blended therewith.

[0029] As used herein, "EVOH" refers to ethylene-vinyi alcohol copolymer. EVOH is otherwise known as saponified or hydrolyzed ethylene-vinyi acetate copolymer, and refers to a vinyl alcohol copolymer having an ethylene

comonomer. EVOH is prepared by the hydrolysis {or saponification) of an ethylene-vinyi acetate copolymer. The degree of hydrolysis is preferably from about 50 to 100 mote percent, more preferably from about 85 to 100 mole percent, and most preferably at least 97%. It is well known that to be a highl effective oxygen barrier, the hydro lysis-sapon if lcation must be nearly complete, i.e., to the extent of at least 97%. EVOH is commercially available in resin form with various percentages of ethylene and there is a direct relationship between ethylene content and melting point. For example, EVOH having a melting point of about 175° C. or lower is characteristic of EVOH materials having an ethylene content of about 38 mole percent or higher. EVOH having an ethylene content of 38 moie percent has a melting point of about 175° C, With increasing ethylene content, the melting point is lowered. A melting point of about 158° C.

corresponds to an ethylene content of 48 mole percent. EVOH copolymers having lower or higher ethylene contents may also be employed. It is expected that processabiiity and orientation would be facilitated at higher ethylene contents; however, gas permeabilities, particularly with respect to oxygen, may become undesirably high for certain packaging applications which are sensitive to microbial growth in the presence of oxygen. Conversely, lower contents may have lower gas permeabilities, but processability and orientation may be more difficult. In some embodiments, ethyiene-vinyS alcohol copoiymers comprise from about 27-38 mole % ethylene, or even 27-29 mole % ethylene.

0030] The term "polyamide" means a high molecular weight polymer having amide linkages (-- CONH— ) _n which occur along the molecular chain, and includes "nylon" resins which are well known polymers having a multitude of uses including utility as packaging films, bags, and casings. See, e.g., Modem Plastics Encyclopedia, 88 VoS. 64, No. 10A, pp 34-37 and 554-555 (McGraw-Hill, Inc., 1987) which is hereby incorporated by reference. PoSyamides are preferabl selected from nylon compounds approved for use in producing articles intended for use in processing, handling, and packaging food.

|0031] The term "nylon" as used herein refers more specifically to synthetic polyamides, either aliphatic or aromatic, either in crystalline, semi- crystalline, or amorphous form characterized by the presence of the amide group -CONH. It is intended to refer to both poiyamides and co-poiyamides.

[0032] Linear low density polyethySenes (LLDPE) are copoiymers of ethylene with aSpha-olefins having densities from 0.915 to 0,940 g/cm ³ . The aipha-olefin utilized Is usually 1-butene, 1-hexene, or 1-octene and Ziegler-type catalysts are usually employed (although Phillips catalysts are also used to produce LLDPE having densities at the higher end of the range, and metailocene and other types of catalysts are also employed to produce other known variations of LLDPE). [0033] Very Sow density poiyethylenes (VLDPE) which may also be cailed "ultra low density poiyethylenes" (ULDPE) comprise copolymers of ethylene with alpha-olefins, usually l-butene, 1~hexena or 1 -octane and are recognized by those skilled in the art as having a high degree of linearity of structure with short branching rather than the long side branches characteristic of LDPE. However, VLDPEs have lower densities than LLDPEs. The densities of VLDPEs are recognized by those skilled in the art to range between 0.860 and 0.915 g/cm ³ . An exemplary VLDPE is Attane™ Ultra Low Density Polyethylene 4701 G available from Dow Chemical Company having a density of 0.912 g/cm ³ ,

[0034] Preferably, polymers are selected from compositions approved as safe for producing articles intended for use in processing, handling and

packaging of food, such as nylon resins approved by the U.S. Food and Drug Administration provided at 21 CFR § 77.1500 ("Nylon resins"), which is incorporated herein by reference.

[0035] The term "adhesive layer," or "tie layer," refers to a layer or material placed on one or more layers to promote the adhesion of that layer to another surface. Preferably, adhesive layers are positioned between two layers of a multilayer film to maintain the two layers in position relative to each other and prevent undesirable delamination. Unless otherwise indicated, an adhesive layer can have any suitable composition that provides a desired level of adhesion with the one or more surfaces in contact with the adhesive layer material. Optionally, an adhesive layer placed between a first layer and a second layer in a multilayer film may comprise components of both the first layer and the second layer to promote simultaneous adhesion of the adhesive layer to both the first layer and the second layer to opposite sides of the adhesive layer,

[0036] A "sidewa!S" is a discrete piece of polymer film that is sealed to itself or another sidewa!l by, for example, welding or an adhesive, to form a bag. A "fitment" is a structure that provides an inlet/outlet for product-filling and/or product-dispensing from the bag.

[0037] The term "oxygen transmission rate" (OTR) is defined herein as the amount of oxygen in cubic centimeters (cm ³ ) that will pass through 100 in ² of film in 24 hr. at 80% relative humidity (R.H.) and 23°C. (or cm ³ /100 In ² over 24 hr. at 80% R.H, and 23°C). Packaging films which are useful as an oxygen barrier in this application are required to have an OTR value of from about 0-0,20 cm ³ /100 in ² over 24 hr.at 80% R.H. and 23°C, Oxygen transmission may be measured according to ASTI D-3985-81 which is incorporated herein by reference.

MATERIALS

[0038] A layer having an ethylene/vinyl alcohol ("EVOH") copolymer film provides oxygen barrier protection, A TPE is added to an EVOH film to provide enhanced flex-crack resistance. An exemplary TPE is HytreS® Thermoplastic Elastomer 4G53FG NC010, available from DuPont Company.

0039] Linear low density polyethylene (LLDPE) or very low density polyethylene (VLDPE) films provide abuse resistance layers to the liner as a whole and they are used on either side of the EVOH film to provide further protection to that layer, in some embodiments, a combination (i.e., LLDPE in one layer and VLDPE in another layer) or mixture (i.e., LLDPE and VLDPE combined in a single layer) of LLDPE and VLDPE are used.

[0040] Nylon or poSyamide-based films may be interleaved with other layers as desired to provide further strength and protection to a ply. Examples of nylon polymeric resins for use in food packaging and processing include; nylon 66, nylon 610, nylon 66/610, nylon 6/66, nylon 1 , nyion 6, nylon 66T, nylon 612, nylon 2, nylon 6/12, nyion 6/69, nylon 46, nylon 6-3-T, nylon MXD-6, nylon

XDI, nylon 12T and nyion 6I/6T disclosed at 21 CFR § 177.1500. Examples of polyamides include nyion homopoSymers and copolymers such as those selected form the group consisting of nyion 4,6 (poly{tetra methylene adipamsde)), nylon 6 (poiycaprolactam), nylon 6,6 (poly{hexamethySene adipamide)}, nylon 6,9

(po!y(hexamethy!eme nonanediamide)), nylon 6,10 {poiy(hexamethyiene sebacarnide)), nylon 6,12 (poly(hexamethy!ene dodecanediamide)), nylon 6/12 (poly(caproiactam-co-dodecanediamide)) _; nylon 6,6/6 (poly(hexamethylene adipamide-co-caprolactam)), nylon 66/610 (e.g., manufactured by the

condensation of mixtures of nylon 66 salts and nylon 610 salts), nyion 6/69 resins (e.g., manufactured by the condensation of epsilon-caprolactam, hexamethySenediamine and azelaic acid), nylon 11 (poiyundecanoiactam), nylon 12 (poiylauryllactam) and copolymers or mixtures thereof.

10041] Between any of the layers, a tie or adhesive layer may be provided to provide adhesion and continuity between the layers. Adhesive compositions invention may include, but are not limited to: modified and unmodified poiyoiefins, preferably polyethylene, most preferably, ethylene-ct-olefin copolymer, modified and unmodified acrylate resin, preferably selected from the group consisting of ethylene-methyt acrylate copolymer, eihylene-ethyS acrylate copolymer, ethylene-butyS acrylate copolymer, or blends thereof. EVA is an ethylene-vinyl acetate co-polymer, which may be used in particular to form a layer to facilitate bonding of polym erica !Sy dissimilar layers.

FEATURES

[0042] The liner sidewal!s may be configured as needed to fit into the desired bulk container. For example, a piilow bag has seals around four edges of two plies. An exemplary bag has inner dimensions of about 81 inches (205 cm) wide by about 85" (216 cm) long.

[0043] Regarding fitments, one or more of them may be affixed through a ply for filling and dispensing from the liners. They may be any structure suitable for sealing the liquid within the liner, for example a threaded tube may be affixed through a ply and a cap threads onto the tube.

FABRICATION

[0044] In general terms, to form films for liners disclosed herein, the following steps are used. Films may be fabricated by any coextrusion method known to a person of ordinary skill in the art. Films described in the Examples herein were manufactured by the following steps: (a) adding to extruders thermoplastic resins that are suitable to result in a multi-layered film; (b) heating the thermoplastic resins to form streams of melt-ptasticized polymers; (c) forcing the streams of me!t-plasticized polymers through a multi-orifice annular die to form a tubular extrudate having a diameter and a hollow interior; (d) expanding the diameter of the tubular extrudate by a volume of fluid entering the hollow interior via the central orifice; (e) and collapsing the tubular extrudate onto itself to form a continuous sheet having two plies joined at their edges. An optional additional ste includes: (f) slitting the edges of the two ply sheets and rolling the resulting sheets to form a double wound film.

[0045] Upon formation of double wound films of desired designs, films are cut to desired sizes and at least one sidewall is formed from a section of film. A fitment is attached to the sidewall. The sidewa!J may be sealed to itself to another sidewall to form a liner. Seals between the sidewail(s) may be achieved by methods known in the art, for example, by heat welding or by use of an adhesive.

[0046] Before describing several exemplary embodiments of the invention, it is to be understood that the invention is not limited to the details of construction or process steps set forth in the following description. The invention is capable of other embodiments and of being practiced or being carried out in various ways.

[0047] Turning to the figures, FIGS. 1-3 are schematic cross-section views of exemplary plies of different embodiments of liners. In FIG. 1 , the liner 100 comprises a first ply 102 and a second ply 110. The first ply 102 comprises a first layer 104, a second layer 106, and a third layer 108. In this embodiment, the first layer 104 and the third layer 08 comprise the same material and the second layer 108, located between the first and third layers, is a different material. The second ply 110 comprises a first layer 112, a second layer 114, and a third layer 116. In this embodiment, the first layer 112 and the third layer 116 comprise the same material and the second layer 1 14, located between the first and third layers, is a different material. The plies 102 and 110 of the embodiment of FIG. 1 may be the same or different design. For example, plies 102 and 110 may independently further comprise a fourth layer (not shown) between the f irst and second layers and a fifth layer (not shown) between the second and third layers.

[0048] FIG. 2 shows a liner 200 comprising a first ply 202, a second ply 210, and a third ply 218. The first ply 202 comprises a first layer 204, a second iayer 206, and a Ihird layer 208, In this embodiment, the first iayer 204 and the third iayer 208 comprise the same materia! and the second iayer 206, located between the first and third layers, is a different material. The second ply 210 comprises a first Iayer 212, a second layer 214, and a third layer 216, In this embodiment, the first iayer 212 and the third Iayer 216 comprise the same materia! and the second layer 214, located between the first and third layers, is a different materia!. The third ply 218 comprises a first layer 220, a second Iayer 222, and a third Iayer 224. In this embodiment, the first iayer 220 and the third iayer 224 comprise the same materia! and the second Iayer 222, located between the first and third layers, is a different materia!. Plies 202 and 210 of the embodiment of FIG. 2 are the same design and p!y 218 has a different design and may further comprise a metal-containing iayer located between either the first and second layers or the second and third layers.

[0049] FIG, 3 shows a liner 300 comprising a first ply 302, a second ply 310, a third piy 318, and a fourth ply 326. The first ply 302 comprises a first layer 304, a second iayer 306, and a third layer 308. In this embodiment, the first iayer 304 and the third Iayer 308 comprise the same material and the second layer 306, located between the first and third layers, is a different material. The second ply 310 comprises a first layer 312, a second layer 314, and a third layer 316, In this embodiment, the first layer 312 and the third layer 316 comprise the same material and the second layer 314, located between the first and third iayers, is a different material. The third ply 318 comprises a first iayer 320, a second !ayer 322, and a third layer 324, !n this embodiment, the first layer 320 and the third iayer 324 comprise the same materia! and the second layer 322, located between the first and third layers, is a different material. The fourth ply 326 comprises a first layer 328, a second layer 330, and a third layer 332. In this embodiment, the first layer 328 and the third layer 332 comprise the same materia! and the second layer 330, located between the first and third layers, is a different material. Piies 302 and 318 of the embodiment of FIG. 3 are the same design and plies 310 and 326 are the same design that may be the same or different from piles 302 and 318. For example, both plies 302 and 318 and/or both plies 310 and 328 may independently further comprise a fourth layer (not shown) between the first and second layers and a fifih layer (not shown) between the second and third layers.

[0050] FIG. 4 is a schematic top view of a liner for a bulk container in accordance with an embodiment. The liner 400 comprises a sidewail 440 that has seams 442 to seal the sidewail 440 to another sidewail (not shown). Fitment 444 is attached to sidewail 440.

EXAMPLES

[0051] In the following examples, reference is made to "oxygen

transmission rate" (OTR), and to one-hour Gelbo Flex Test results.

Measurement of OTR was done in accordance with ASTJV1 D-3985 81. The Gelbo Flex Test was done in accordance with ASTIVl F392 At best, there would be zero pinholes. A target range for pinholes is less than 10, or less than 5, or even less than 2.

COMPARATIVE EXAMPLE 1

[0052] A two ply barrier film was formed from a collapsed bubble. The structure and weight percents of a single ply were:

[0053] LLDPE 40,2%/tie 6.8%/EVOH 17.4%/tie 6.8%/LLDPE 15.4%/EVA 13.4%.

[0054] The EVOH layer had a 29 mole percent content of ethylene.

[0055] Due to the nature of the collapsed bubble forming process, the plies were orientated as a mirror image to one another (i.e. , the EVA layers of each ply were in contact, and the outer LLDPE layers were both outward facing in the two ply combination),

[0056] The resulting two ply film was a total of 0.0045 inches (114 pm) thick. The film had an oxygen barrier measurement of 0.06 cc 100in ² /day at 23° C and 80% relative humidity and a one hour Gelbo Flex Test result of 45 pinholes. Although the oxygen barrier measurement was acceptable, the number of pinholes was undesirable. COMPARATIVE EXAMPLE 2

[0057] A n-ionomer resin was included as an additive at 10% and 20% by weight amounts into a 29 mole percent EVOH iayer in a single p!y blown film having the structure and weight percents:

10058] i) VLDPE+LLDPE 39.4%/tie 6.7%/EVOH + 10% n-ionomer

17.3%/tie 6.7% VLDPE+LLDPE 15.4%/LLDPE 14,6%.

[0059] ii) VLDPE+LLDPE 39,5%/tie 6.7%/EVOH + 20% n-ionomer

17.0%Aie 6.7%/VLDPE+LLDPE 15,4%/LLDPE 14.7%.

[0060] The oxygen barrier for the 10% n-ionomer example was 0.043 cc/100in ² /day at 23° C and 80%. The oxygen barrier for the 20% n-ionomer example was 0.09 cc/100in2/day ai 23° C and 80%.

[0061] The addition of n-ionomer did not reduce the Geibo Flex Test pinhole count as compared to Comparative Example 1.

EXAMPLE 3

[0062] TPE resin (Hytrel 4053FG) was included as an additive at 10% by weight amount into a 29 mole percent EVOH Iayer into a collapsed blown film having the structure and weight percents;

[0063] VLDPE 19.9%/tie 3,4%/EVOH + 10% TPE 8, 7%/tie 3.4% VLD 7.7%/EVA 13.8%/VLDPE 7.7%/tie 3.4%/ EVOH + 10% TPE 8.7%7 ie

3.4% VLDPE 19.9%.

[0064] The resulting film was a total of 0.0045 inches (1 14 pm) thick. The oxygen barrier was 0.08 cc/100in ² /day at 23° C and 80%. The Geibo Flex Test pinhole count was 2 to 5 pinholes in one hour.

EXAMPLE 4

[0065] A collapsed bubble film was prepared in the same manner as Example 3, except that the EVA Iayer was replaced with a VLDPE layer. The VLDPE Iayer allowed the collapsed bubble to be separated into two plies and double wound. The structure and weight percents of a single ply were: [0066] VLDPE 39,7%/tie 6,8%/EVOH + 10% TPE 17,4%/fie 6.8%/VLDPE 29,3%.

[0067] The resulting film had a two~p!y thickness of 0.0045 inches (1 14 μπι}. The oxygen barrier was 0.055 cc/100in ² /day at 23° C and 80% for a two piy sample. The GeSbo Fiex Test pinhole count was 0 to 2 pin holes in one hour for a two~piy sample.

EXAMPLE 5

[0068] A collapsed bubble film was prepared in the same manner as Example 4 _; except that two !ayers comprising a 80:20 biend of Nylon 8 and Nylon 6/66 were added. The structure and weight percenis of a single ply were:

[0069] VLDPE 33.0%/tie 6.8%/Nylon biend 6,8%/EVOH + 10% TPE 17.4%/Nylon blend 8.8%/tie 15.5%/VLDPE 13.8%.

[0070] The resulting film had a iwo-piy thickness of 0.0045 inches (1 14 pm). The oxygen barrier was 0.09 cc/100in ² /day at 23° C and 80% for a two p!y sample. The GeSbo Flex Test pinhoie count was 0 to 2 pinholes in one hour for a two-ply sample.

[0071] Unless otherwise indicated, all numbers expressing quantities of ingredients, properties such as molecuiar weight, reaction conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term "about." Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present disclosure. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

[0072] Reference throughout this specification to "one embodiment," "certain embodiments," "one or more embodiments" or "an embodiment" means that a particular feature, structure, materia!, or characteristic described in connection with the embodiment is inc!uded in at ieast one embodiment of the invention. Thus, the appearances of the phrases such as "in one or more embodiments," "in certain embodiments," "in one embodiment" or "in an embodiment" in various places throughout this specification are not necessarily referring to the same embodiment of the invention. Furthermore, the particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments,

[0073] Although the invention herein has been described with reference to particular embodiments, it is to be understood thai these embodiments are merely illustrative of the principles and applications of the present invention. It will be apparent to those skilled in the art that various modifications and variations can be made to the method and apparatus of the present invention without departing from the spirit and scope of the invention. Thus, it is intended that the present invention include modifications and variations that are within the scope of the appended claims and their equivalents.