Title:
MATERIAL PROCESSING SYSTEM AND METHOD
Document Type and Number:
WIPO Patent Application WO/2019/092407
Kind Code:
A1
Abstract:
The present invention presents a system for and method of processing a particulate material, for example carbonaceous materials, food products or minerals, to produce a processed material having more desirable properties. The method comprises the steps of: introducing the particulate material into a chamber; providing a flow of fluid into said chamber for entraining the particulate material via inlets at a lower end of the chamber; and providing an exhaust of fluid out of the chamber via an outlet at an upper end of the chamber. The chamber comprises a processing zone having a substantially circular transverse cross-section, the fluid flow being introduced into the processing zone at a non- perpendicular angle with respect to a tangent of the substantially circular transverse cross- section of the processing zone to establish a fluid flow following a substantially helical path in the processing chamber. Said processing zone is provided in a central region of said chamber. Individual particulate material during processing in the processing zone is entrained by the fluid flow exceeding the terminal velocity of the particulate material, exits the processing zone in a radially outward direction, circulates to a base of the chamber and then returns to the processing zone in a repeated cycle. Individual particulate material can increase in mass or aggregate to form a mass of particulate material with larger mass during processing until its terminal velocity exceeds the fluid flow and thereby exits the processing zone by descending through an opening at the base of the chamber under gravity. A toroidal bed reactor is also provided.

Inventors:
DODSON CHRISTOPHER (GB)
Application Number:
PCT/GB2018/053207
Publication Date:
May 16, 2019
Filing Date:
November 05, 2018
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
MORTIMER TECH HOLDINGS LTD (GB)
International Classes:
B01J8/14; B01J8/18; B01J8/38; B01J19/24
Domestic Patent References:
WO2006003454A12006-01-12
WO2016042289A12016-03-24
Foreign References:
US7998421B22011-08-16
EP0068853A21983-01-05
US7998421B22011-08-16
Attorney, Agent or Firm:
BOULT WADE TENNANT LLP (GB)
Download PDF:
Claims:
CLAIMS:

1 . A method of processing particulate material to produce processed particulate material, the method comprising the steps of:

introducing the particulate material into a chamber;

providing a flow of fluid into said chamber for entraining the particulate material via inlets at a lower end of the chamber; and

providing an exhaust of fluid out of the chamber via an outlet at an upper end of the chamber,

wherein the chamber comprises a processing zone having a substantially circular transverse cross-section, the fluid flow being introduced into the processing zone at a non- perpendicular angle with respect to a tangent of the substantially circular transverse cross- section of the processing zone to establish a fluid flow following a substantially helical path in the processing chamber,

wherein:

said processing zone is provided in a central region of said chamber; and individual particulate material during processing in the processing zone is entrained by the fluid flow exceeding the terminal velocity of the particulate material, exits the processing zone in a radially outward direction, circulates to a base of the chamber and then returns to the processing zone in a repeated cycle; and

individual particulate material can increase in mass or aggregate to form a mass of particulate material with larger mass during processing until its terminal velocity exceeds the fluid flow and thereby exits the processing zone by descending through an opening at the base of the chamber under gravity.

2. The method of claim 1 , wherein individual particulate material can decrease in mass during processing until it is entrained in the exhaust fluid leaving the chamber.

3. The method of claim 1 or claim 2, wherein the fluid flow is introduced at a velocity selected so as to achieve a predefined residence time of the supplied particulate material within the chamber prior to egress from the chamber.

4. The method of any preceding claim, wherein the fluid flow is introduced at a temperature of at least 600°C, preferably 800°C, preferably no more than 1 100°C.

5. The method of any preceding claim, further comprising the pre-processing of carbonaceous material to achieve a moisture content of less than 30%, preferably less than 10%. 6. The method of any preceding claim, wherein the method is used to process particulate carbonaceous material to produce activated carbon.

7. The method of any one of claims 1 to 5, wherein the method is used to process particulate mineral, the mineral preferably being clay, to produce a processed product.

8. The method of claim 6 or claim 7, wherein the residence time is at least 10 seconds, preferably no more than 500 seconds.

9. The method of any preceding claim, wherein the fluid flow has a temperature in the range 600*C to 1 100*C.

10. A method of processing particulate material having a moisture content of greater than 30% by weight to produce processed particulate material, the method comprising the steps of:

processing particulate material in a toroidal bed reactor in a drying stage to reduce the moisture content to below 30% to produce dried particulate material using a method according to any one of the preceding claims in which the temperature of the fluid flow is below 600°C, preferably below 200*C; and

processing the dried particulate material in a toroidal bed reactor in a final stage using a method according to any one of the preceding claims in which the temperature of the fluid flow is greater than 600°C, preferably greater than 800°C.

1 1 . A method of processing particulate material having a moisture content of greater than 30% by weight to produce processed particulate material, the method comprising the steps of:

processing particulate material in a toroidal bed reactor in a drying stage to reduce the moisture content to below 30% to produce dried particulate material using a method according to any one of the preceding claims in which the temperature of the fluid flow is below 600°C, preferably below 200*C; processing the dried particulate material in a toroidal bed reactor in an intermediate stage to produce an intermediate particulate material using a method according to any one of the preceding claims in which the temperature of the fluid flow is from 600°C to 800°C; and

processing the intermediate particulate material in a toroidal bed reactor in a final stage using a method according to any one of the preceding claims in which the temperature of the fluid flow is greater than 600°C, preferably greater than 800°C.

12. The method of claim 1 1 , wherein the method processes particulate material having a moisture content of greater than 60% by weight.

13. The method of any preceding claim, wherein an amount of oxidising agent in the fluid is controlled to prevent the amount of oxidising agent in the chamber from exceeding 20%, preferably 10%, more preferably 7%.

14. The method of any preceding claim, wherein the fluid is preheated prior to introduction into the chamber.

15. The method of any preceding claim, wherein the fluid is recycled exhaust gas from the chamber.

16. A toroidal bed reactor, comprising:

a chamber;

a fluid supply for supplying a flow of fluid into the chamber; and

an outlet for supplying exhaust of fluid out of the chamber,

characterised by:

sensor means for providing a measurement of the oxidising agent content of the chamber;

a mixer for modulating the amount of oxidising agent in the fluid supply based on the measurement provided by the sensor.

17. A toroidal bed reactor, comprising:

a chamber;

a fluid supply for supplying a flow of fluid into the chamber; and

an outlet for supplying exhaust of fluid out of the chamber, characterised by:

a recirculation device arranged to recirculate exhaust fluid to the fluid supply; and a heater arranged to increase the temperature of the recirculated fluid.

Description:
MATERIAL PROCESSING SYSTEM AND METHOD

FIELD

The present invention presents a system for and method of processing a particulate material, for example carbonaceous materials, food products or minerals, to produce a processed material having more desirable properties.

BACKGROUND ART

The Inventor has previously developed an expanded toroidal bed reactor described in US7998421 , the disclosure of which is incorporated herein by reference.

It has been discovered that this device, or a similar device, can be used to process particulate material to achieve desirable properties. In particular, the device can be used to process particulate carbonaceous material to produce activated carbon, metallurgical coke, charcoal or carbonaceous material. Advantageously, this has been found to produce products with a surprisingly high surface area.

DESCRIPTION OF APPARATUS

The following describes a device that can establish a processing zone which provides for a predictable particle flow path, both circumferentially and helically, in the processing zone to ensure more uniform particle treatment and gas/solid mixing for a given residence time.

The device may be used in a method of processing a particulate material that comprises the steps of:

(a) introducing particulate material into a chamber;

(b) providing a flow of fluid into said chamber for entraining the particulate material; and

(c) removing processed fluid and/or particulate material from the chamber. The chamber comprises a processing zone having a substantially circular transverse cross- section, the fluid flow is introduced into the processing zone at an angle of between 10° and 75° with respect to a tangent of the substantially circular transverse cross-section of the processing zone to establish a fluid flow following a substantially helical path in the processing zone. It has been recognised that the introduction of the fluid flow into the processing zone within the above-referenced parameters is particularly suitable for establishing a uniform particle flow path. Thus, uniform particle treatment and gas/solid mixing may be achieved. The particulate material and fluid are in contact with each other in the processing zone.

The fluid flow upon entry into the processing zone may define an angle of between 20° and 60°; or between 30° and 45° with respect to said tangent. The fluid flow upon entry into the processing zone is preferably inclined upwardly at an angle between 5° and 45°; between 10° and 40°; between 15° and 35°; or between 20° and 30° with respect to a horizontal plane.

The particulate material may be removed at predetermined time intervals in a batch process. Alternatively, the particulate material may be fed continually into the device with egress of the processed particulates occurring automatically owing to their changed mass resulting from processing. It has been discovered that by intentional calibration of the fluid flow, the mass distribution of the processed material leaving the chamber can be predetermined.

The velocity of the fluid flow is preferably controlled so as to be greater than the terminal velocity of particulate material in the chamber that has not yet been sufficiently processed.

The direction of the fluid flow may be developed by at least one nozzle or tube.

Alternatively, the direction of the fluid flow is developed by at least one vane or deflector. Preferably, however, a plurality of vanes, deflectors or tubes are employed.

The fluid flow in the chamber preferably can cause the particulate material to undergo both vertical and horizontal displacement. Thus, the mixing of the particulate material with the fluid may be maximised within the chamber.

Although the processing zone may be defined by the walls of the chamber, it is preferably formed by fluid flow in a central region of the chamber to allow particulate material to exit the processing zone and be deposited radially outwardly of the processing zone. The deposited particulate material preferably forms a flowing bed. The chamber preferably has a base inclined downwardly towards the centre of the chamber to bias particulate material in the flowing bed back towards the processing zone.

The processing zone is preferably annular or toroidal in shape. This may be achieved by providing a central conduit or pillar in the chamber, but is preferably implemented by the helical movement of the fluid flow inside the chamber.

Although the fluid may be introduced into the side or the top of the processing zone, it is preferably introduced at the base thereof. Although in certain arrangements it may be desirable for the fluid to be a liquid, it is more usually a gas. The helical fluid flow is preferably either conical or cylindrical. The apparatus further comprises a flow controller suitable for controlling the velocity of the fluid introduced into the chamber.

For a better understanding of the invention, and to show how the same may be put into effect, reference will now be made, by way of example only, to the accompanying drawings, in which:

FIG. 1 is a transverse cross-sectional view of a particulate material reactor which may be used in the invention;

FIG. 2 is a longitudinal cross-sectional view a lower portion of the reactor shown in FIG. 1 ;

FIG. 3 illustrates the flow path of fluid and particles in a contrasting reactor not used in the invention;

FIG. 4 illustrates the flow path of fluid and particles in a reactor which may be used in the invention;

FIGS. 5A, 5B and 5C show bottom, front and end views respectively of angled vanes provided at the base of the processing zone to direct the flow of fluid as it enters the processing zone; and

FIGS. 6A and 6B are top and side views respectively of an assembly of the vanes shown in FIG. 5. A cross-sectional view of a toroidal bed reactor (1 ) in accordance with a preferred embodiment of the present invention is shown in FIG. 1 . The reactor (1 ) comprises a cylindrical housing (3) that defines a chamber inside of which a processing zone (5) is formed. The processing zone (5) is annular in shape and extends co-axially with the housing (3).

A cross-sectional view of the lower portion of the reactor (1 ) is shown in FIG. 2. A tapered section (7) is provided at the base of the housing (3). The tapered section (7) is inclined downwardly towards the centre of the reactor (1 ). Gas is introduced into the reactor (1 ) through a series of vanes (9) provided at the base of the tapered section (7). The vanes (9) establish a desired fluid flow path (A) within the housing (3).

A hole (8a) for the egress of processed particulates is provided in the base of the housing (3). The hole 8a is preferably annular and centred around the longitudinal axis of the housing (3).

A hole (8b) for the egress of processed particulates is provided in the side of the housing (3), distal from the base of the housing (3). This hole 8b is preferably the exhaust path of the fluid exiting the chamber. In this way, the exhaust fluid may entrain some of the processed particulates.

The vanes (9) direct the gas flow so that it enters the processing zone (5) at an angle a with respect to a tangent (B) of the substantially circular transverse cross-section of the processing zone, as shown in FIG. 1 . The angle a is approximately 30° in this embodiment.

The advantage of directing the gas flow inwardly at an angle a is that there is an increased mixing of the gas flow. This provides for a uniform distribution of particulate matter as will be described below. A gas flow which is introduced along a tangent of the processing zone (angle a=0°) will produce less mixing of the gas flow, and so will provide a less uniform distribution of particulate matter.

Furthermore, the vanes (9) cause the gas to enter the processing zone at an angle β inclined upwardly with respect to a horizontal plane (C), as shown in FIG. 2. The angle β is approximately 15° in this embodiment. The path followed by particulate material (1 1 ) introduced into the reactor (1 ) will now be described for different gas flow paths with reference to FIGS. 3 and 4.

FIG. 3 shows a gas flow path (D) inside the reactor (1 ) when the gas enters the base of the housing (3) in a radial direction (i.e. a is 90°, and β is 0°). The gas tends to travel up the inside of the tapered section (7) and causes the particulate material (1 1 ) to collect in an annular region (9) around the inside wall of the housing (3). The gas travels towards the centre of the housing (3), around the base of the annular region (9), and up towards the top of the housing (3). Thus, the particulate material (1 1 ) comes into limited contact with the gas as it travels through the reactor (1 ).

In contrast, when the gas is introduced into the reactor (1 ) in accordance with the invention (e.g. a is 30° and β is 15°), it follows a helical flow path (E), as shown in FIG. 4. The processing zone (5) is defined by the helical flow of the gas in the housing (3). The particulate material is entrained in the vortex formed by the gas in the processing zone (5) and is transported vertically before being progressively separated from the fluid stream due to centrifugal force. By this means, the processing zone (5) utilising the present invention contains a rapidly and uniformly circulating mass of particulate material evenly distributed in the processing zone (5). A path (F) followed by the particulate material (1 1 ) introduced into the reactor (1 ) is shown in FIG. 4.

The even distribution of particles in the fluid flow is important to help prevent undesirable effects that may occur when the gas follows the flow path (D) shown in FIG. 3. As shown in FIG. 4, the particulate material (1 1 ) is displaced upwardly by the fluid flow in the processing zone (5) and then expelled radially outwardly. The particulate material (1 1 ) then falls to the base of the housing (3) and a moving bed of particulate material is formed by the tapered portion (7) of the reactor (1 ). The moving bed returns the particulate material to the processing zone (5) under the action of gravity. The cycle is thereby repeated. This cyclical motion of the particulate material allows the reaction in the reactor (1 ) to be carefully controlled.

The velocity of the gas entering into the processing zone (5) is advantageously controlled to ensure that it is greater than the terminal velocity of the particulate material. This control of the fluid flow helps to reduce or prevent the collection of particulate material at the base of the reactor (1 ).

It has been found that if the angle β of entry of the gas into the processing zone is 10° or more above a horizontal plane, and it is inclined at an angle a of 10° or more relative to a tangent to a radial line at the point of entry, the fluid and particulate material follow the fluid path illustrated in FIG. 4. The mass of particulate material is suspended in a coherent rotating mass with particles aggregated without incipient fluidisation. The arrangement of the vanes (9) at the base of the reactor (1 ) will now be described in greater detail. A single vane (9) is shown in FIGS. 5A, 5B and 5C. The vanes (9) each have a leading edge (13), a trailing edge (14) and three slots (15) formed in the surface thereof. As shown in FIG. 5B, the vanes (9) are tapered towards the leading edge (13) to form a tapered region (17) which serves to align the vanes (9) relative to each other. The slots (15) each extend from the leading edge (13) in a transverse direction across the tapered region (17). A chamfered region (19) is provided at the trailing edge of each vane (9), diametrically opposed from the tapered region (17). A front view of a vane (9) is shown in FIG. 5C. The slots (15) extend at an angle β relative to a reference axis perpendicular to the leading edge (13) of the vane (9), as shown in FIGS. 5A and 5C. The angular offset of the slots (15) causes the gas to be introduced into the reactor (1 ) upwardly, at said angle β, relative to a horizontal plane, as described above. A top view of the vanes (9) arranged in an assembly (21 ) ready for use is shown in FIG. 6A. A side view of the assembly (21 ) is shown in FIG. 6B. The tapered region (17) of each of the vanes (9) determines the angular orientation of the vanes relative to each other and, thereby, the angular orientation of the slots (15). Thus, the taper angle of the tapered region (17) defines the angle a at which the gas is introduced into the processing zone (5).

The processing zone (5) is generally annular in shape because of the helical fluid flow inside the housing (3).

By controlling the angle of entry of the fluid into the processing zone to maintain it larger than 10° but less than 75° relative to the tangent to the radial line at the point of entry; and to be greater than 5° but less than 45° relative to said horizontal plane, as shown in FIGS. 1 and 2 respectively, the fluid and particulate flows can be made to circulate along a helical path, as shown in FIG. 4. The circulating particles are accelerated by the gas flow in the processing zone (5) in both horizontal and vertical directions to travel tangentially of said circumferential flow until such accelerated particles lose their energy and settle into the flowing bed arranged

circumferentially of the processing zone (5). By displacement in the flowing bed, the circulating particles are returned to the base of the processing zone (5) thereby ensuring that all of the particles in the bed are exposed to the processing gases to provide for uniform and rapid processing of said particles.

The device can be used in a process for processing particulate material with a stream of fluid in an annular processing zone. The process includes the steps of supplying the particulate material for processing into the processing zone, discharging processed material from the zone and generating in the processing zone a circumferentially directed flow of fluid to develop a circulating turbulent band of particles. The device advantageously provides a predictable particle flow path both circumferentially and helically, within the processing zone. The process preferably comprises directing the flow of fluid to develop a circulating bed, a flow of fluid directed at an angle relative to the tangent to the radial line to the point of fluid and to the horizontal plane at entry into the processing zone base.

The process may also comprise controlling fluid velocity so that it is greater than the terminal velocity of particles that have not been sufficiently processed at their point of impact on the bed base and less than the terminal velocity of particles that have been processed a desired amount in the superficial space above the bed upper surface.

DESCRIPTION OF METHOD

A method of processing particulate material to produce processed particulate material, the method comprising the steps of: introducing the particulate material into the chamber of a toroidal bed reactor; and providing a flow of fluid into said chamber for entraining the particulate material via inlets at a lower end of the chamber.

In the following example, the particulate material is carbonaceous material. However, other materials may be used, such as minerals or clay. Although not always the case, the carbonaceous material may be provided in a form that is undesirably wet. For example, it may have in excess of 30% moisture by weight. In fact, it may have more than 60% moisture by weight. Accordingly, an optional pre-processing step of drying the carbonaceous material to below 30% moisture is provided. This may be carried out in a toroidal bed reactor (e.g., of the type described above). The drying step is carried out at a temperature of no more than 600 ° C. Preferably, the drying is carried out at a temperature of no more than 200 ° C. As described above, the chamber comprises a processing zone having a substantially circular transverse cross-section. The fluid flow is introduced into the processing zone at a non-perpendicular angle with respect to a tangent of the substantially circular transverse cross-section of the processing zone to establish a fluid flow following a substantially helical path in the processing chamber.

This fluid flow entrains and transports individual particulate material in a cyclical path during processing. Specifically, as may be seen in Figure 4, the unprocessed particulate material in the processing zone is entrained or lifted by the fluid flow in the inner vortex E, the velocity of which exceeds the terminal velocity of the particulate material. Owing to the cyclonic circulation of fluid, the particulate material will exit the inner processing zone E in a radially outward direction F due to centrifugal forces, and circulate under the force of gravity or by entrainment in a downward flow fluid flow to a base of the chamber where it will return to the inner vortex E processing zone to complete a cycle. This process is then repeated during which time the particle is processed.

The processing may alter the terminal velocity of the particles. Firstly, the heat of the processing fluid may alter the particles. For example, the particles will be dried.

Furthermore, the particles may collide with one another of surrounding structures and break apart by a process of attrition.

The terminal velocity of an aggregated mass of particles may eventually become greater than the velocity of fluid flow introduced into the chamber at which point the particles will not be entrained by the fluid flow in the processing zone, and will not be forced radially outwardly. At this point, they will descend through the hole 8a under the force of gravity. There may also be provided an outlet 8b at the upper end of the chamber for the exhaust of fluid out of the chamber. Fine processed particulate material may be entrained in the exhaust fluid and exit the chamber via the outlet 8b. In preferred embodiments, the fluid flow is introduced at a velocity selected so as to achieve a predefined amount of processing of the particulate material within the chamber prior to egress from the chamber.

Preferably, this is achieved by introducing the fluid flow at a velocity selected so as to achieve a predefined residence time of the supplied particulate material within the chamber prior to egress from the chamber.

The preferred fluid flow (whether it be expressed as velocity, mass flow rate, volume flow rate, etc.) for the method may be determined by a calibration process using the device prior to the above-described processing. The calibration process comprising the steps of:

introducing a particulate material into a chamber, the particulate material comprising a distribution of masses; providing a flow of fluid at a known velocity into said chamber for entraining the particulate material via inlets at a lower end of the chamber; and monitoring the mass of particulates exiting the chamber.

Alternatively, the preferred fluid flow for the method may be determined by a feedback process during the above-described process. The feedback process comprising the steps of: monitoring the mass of particulates exiting the chamber via hole 8a during processing; increasing the fluid flow in response to the mass of particulates being below a

predetermined lower mass value; and decreasing the fluid flow in response to the mass of particulates being above a predetermined upper mass value.

The preferred fluid flow rate for carbonaceous material particles with a water content of less than 10% will preferably be selected to provide a residence time of at least 10 seconds, preferably no more than 500 seconds.

The fluid flow is introduced at a temperature of at least 600 ° C. However, it has been found that fluid in the range 800 ° C to 1 100 ° C is preferable for producing activated carbon or charcoal material. The fluid flow preferably has a temperature in the range 600 ° C to 1 100 ° C.

The method is preferably used in a staged manner. Firstly, the above-described optional drying step may be used.

An optional intermediate step may be used in which the dried particulate material is processed in a toroidal bed reactor in which the temperature of the fluid flow is from 600 ° C to 800 ° C. This stage produces a product that can be used as a final product in some applications. Preferably, however, this is just an intermediate product that can be used in the final stage.

In the final stage the above described method is applied with a fluid flow temperature greater than 800 * C and preferably, from 800 ° C to 1 100 * C. Each of the stages may be carried out in a single toroidal bed reactor, or may be implemented in separate toroidal bed reactors.

In order to achieve the temperatures of the final stage, additional heating means may be provided, external to the chamber, to increase the temperature of the fluid flow. That is, the fluid is preferably preheated prior to introduction into the chamber. This is the case even when the fluid is recycled exhaust gas taken from the chamber exhaust outlet 8b.

In fact, in some embodiments, the recycled exhaust gas may comprise volatile constituents be taken from the chamber, and this may be combusted to increase the fluid temperature prior to the reintroduction of the fluid back in to the chamber.

With general applicability to other materials, but with particular benefit for the processing of carbonaceous material, the oxygen content of the chamber may be controlled. In preferred embodiments means for measuring the oxidising agent content of the chamber is provided. Such devices are well known and include laser measuring devices. This may, for example, include means for measuring the amount of moisture, CO, C0 2 , or 0 2 , etc. in the chamber. An amount of oxidising agent in the fluid can be modulated in order to prevent the amount of oxidising agent in the chamber from exceeding 20%. More preferably, an amount of oxidising agent in the fluid can be modulated in order to prevent the amount of oxidising agent in the chamber from exceeding 10%. Most preferably, in particular for carbonaceous material, the amount of oxidising agent in the fluid can be modulated in order to prevent the amount of oxidising agent in the chamber from exceeding 7%.

An amount of oxidising agent in the fluid can be modulated, for example, by supplying a mix of oxygen or air with recirculated exhaust gases.