MATERIALS PREPARED BY METAL EXTRACTION

BACKGROUND OF THE INVENTION

[1] The present invention is in the field of battery technology and, more particularly, in the area of improved active materials for use in electrodes in electrochemical cells. [2] Research into active materials for cathodes for secondary batteries has yielded several classes of active materials. One class of active materials is a type of "over-lithiated" layered oxide (OLO) represented as: χϋ ₂ ΜηΟ ₃ ·(1 -x)Li[MniNijCOk]O ₂ (i) where 0≤x<1 , i+j+k=1 , and i is non-zero. Such OLO materials are promising candidates for next generation batteries because of their high specific capacity.

[3] However, OLO materials suffer from a large irreversible capacity loss during the first cycle of use in an electrochemical cell. Batteries fabricated with OLO materials are assembled using a non-activated form of the OLO material. On first cycle, the non-activated material is electrochemically activated by simultaneous extraction of lithium in the form of Li ⁺ and oxygen in the form of O ₂ or other oxygen- containing gasses. This activation process has several drawbacks. First, gas is generated, which can lead to problems in cell manufacture. Second, defects may be generated in the surface and bulk, which can reduce rate capability, increase the rate of metal dissolution, and increase the rate of electrolyte oxidation. Third, the extracted lithium may form unstable lithium species on the anode that interfere with typical anode stabilization.

[4] OLO has been chemically activated by reaction with aqueous acids, such as hydrochloric acid (HCI). Such an activation process has several drawbacks. First, this activation process requires an excess of acid, which can make it difficult to control the extent of lithium extraction such that an insufficient amount or excess amount of lithium is extracted. Second, water and/or protons can become incorporated into any vacancies generated by the activation and this can lead to poor cycle life and rate performance. Third, the disposal of the wastewater from this process can be costly due to the chemical contaminants in it, making the process difficult to scale up. [5] Some research has been conducted into the use of organo-fluorides, such as polyvinylidenefluoride (PVdF) and polytetrafluoroethylene (PTFE), to remove alkali- ions from metal oxides. In some research, the organo-fluoride was used to remove both alkali ions and oxygen. See, e.g., T. Ozawa et al., Inorg. Chem, 49, (2010) 3044 and T. Ozawa et al., Inorg. Chem, 51 (1 1 ), (2012). The reaction was used to remove all of the alkali-ion from the material.

[6] Further, there has been some work on the use of aluminum fluoride (AIF ₃ ) coatings to improve the electrochemical performance of lithium-rich layered oxides. See, e.g., Scrosati, B. et al., Adv. Mater. 2012, 24, 1 192-1 196 and Zheng, J.M. et al., J. Electrochem. Soc. 2008, 155 (10), A775-A782. [7] Some research has been conducted on delithiating LiNiO2 for rechargeable batteries. See, e.g., Arai, H. et al., Electrochem. Acta 2002, 47, 2697 (for use of sulfuric acid) and Arai, H. et al., J. Power Sources 1999, 81 -82, 401 (for use of NOPF ₆ ). In the work using NOPF ₆ , the PF ₆ reacts with the LiNiO2 and generates an LIPF ₆ salt and NO gas. In this reaction, all the fluorine atoms remain bonded to the phosphorous. Further, the degree of delithiation was low in spite of the excess amount of NOPF ₆ (NOPF ₆ / LiNiO ₂ = 2).

[8] There remains a need for an efficient, scalable means of pre-activating OLO active materials through controlled lithium extraction for the fabrication of full cells for use as primary and secondary batteries. BRIEF SUMMARY OF THE INVENTION

[9] According to some embodiments of the invention, a method for reducing the irreversible capacity loss of lithium-rich layered oxide materials is presented herein.

[10] According to some embodiments of the invention, a method for extracting ions from an active material for use in a battery electrode includes mixing the active material and an activating compound to form a mixture. The mixture is annealed such that an amount of ions is extracted from the active material, an amount of oxygen is liberated from the active material, and an activated active material is formed. The reaction products are optionally separated from the activated active material and the battery electrode is formed. Embodiments of the invention include the activated active material, the electrode, and the primary and secondary batteries formed from such activated active materials.

[11] According to some embodiments of the invention, a method of activating a lithium oxide material, such as a lithium transition metal oxide material, for use in a battery electrode includes mixing the lithium oxide material and an amount of activating compound to form a mixture. The mixture is annealed such that a controlled amount of lithium is extracted by preselecting the amount of activating material in the mixture. A non-gaseous oxygen reaction product may be formed.

[12] According to some embodiments of the invention, a method of extracting alkali ions from a material includes mixing the material and an amount of activating compound to form a mixture wherein the activating compound is a non-fluorinated organo-halide. The mixture is annealed such that a controlled amount of alkali ions is extracted from the active material. The amount is controlled by preselecting the amount of activating material in the mixture. A non-gaseous oxygen reaction product may be formed. BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS

[13] Figure 1 illustrates a voltage trace for a conventional OLO material and depicts the irreversible capacity loss after the first cycle.

[14] Figure 2 illustrates voltage traces comparing a conventional OLO material to a material according to an embodiment of the invention and depicts an improvement in irreversible capacity loss after the first cycle.

[15] Figure 3 illustrates voltage traces comparing a conventional OLO material to a material according to an embodiment of the invention and depicts an improvement in irreversible capacity loss after the first cycle in a full cell with a carbon anode.

[16] Figure 4 is a table of data illustrating improved performance attributable to compounds and methods according to embodiments of the invention as compared to conventional materials in a full cell with a carbon anode.

[17] Figure 5 illustrates voltage traces comparing a conventional OLO material to a material according to an embodiment of the invention and depicts an improvement in irreversible capacity loss after the first cycle. [18] Figure 6 illustrates a graph comparing a conventional OLO material to a material according to an embodiment of the invention and depicts rate performance improvements.

[19] Figures 7A, 7B, and 7C are each scanning electron micrographs depicting the morphology of a conventional material (Figure 7A), a milled material (Figure 7B), and a material mixed using a low-energy process (Figure 7C). The low-energy process substantially preserves the original morphology.

[20] Figure 8 illustrates voltage traces comparing a conventional OLO material to a material according to an embodiment of the invention and depicts an improvement in irreversible capacity loss after the first cycle. [21] Figure 9 illustrates a voltage trace for a primary battery in which the cathode material was delithiated according to an embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

[22] The following definitions apply to some of the aspects described with respect to some embodiments of the invention. These definitions may likewise be expanded upon herein. Each term is further explained and exemplified throughout the description, figures, and examples. Any interpretation of the terms in this description should take into account the full description, figures, and examples presented herein.

[23] The singular terms "a," "an," and "the" include the plural unless the context clearly dictates otherwise. Thus, for example, reference to an object can include multiple objects unless the context clearly dictates otherwise.

[24] The terms "substantially" and "substantial" refer to a considerable degree or extent. When used in conjunction with an event or circumstance, the terms can refer to instances in which the event or circumstance occurs precisely as well as instances in which the event or circumstance occurs to a close approximation, such as accounting for typical tolerance levels or variability of the embodiments described herein.

[25] The term "about" refers to the range of values approximately near the given value in order to account for typical tolerance levels, measurement precision, or other variability of the embodiments described herein.

[26] The term "transition metal" refers to a chemical element in groups 3 through 12 of the periodic table, including scandium (Sc), titanium (Ti), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), cobalt (Co), nickel (Ni), copper (Cu), zinc (Zn), yttrium (Y), zirconium (Zr), niobium (Nb), molybdenum (Mo), technetium (Tc), ruthenium (Ru), rhodium (Rh), palladium (Pd), silver (Ag), cadmium (Cd), hafnium (Hf), tantalum (Ta), tungsten (W), rhenium (Re), osmium (Os), iridium (Ir), platinum (Pt), gold (Au), mercury (Hg), rutherfordium (Rf), dubnium (Db), seaborgium (Sg), bohrium (Bh), hassium (Hs), and meitnerium (Mt).

[27] The term "halogen" refers to any of the chemical elements in group 17 of the periodic table, including fluorine (F), chlorine (CI), bromine (Br), iodine (I), and astatine (At).

[28] The term "chalcogen" refers to any of chemical elements in group 16 of the periodic table, including oxygen (O), sulfur (S), selenium (Se), tellurium (Te), and polonium (Po). [29] The term "alkali metal" refers to any of the chemical elements in group 1 of the periodic table, including lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), and francium (Fr).

[30] The term "alkaline earth metals" refers to any of the chemical elements in group 2 of the periodic table, including beryllium (Be), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), and radium (Ra).

[31] The term "rare earth element" refers to scandium (Sc), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), and lutetium (Lu). [32] The term "organic moiety" refers to carbon-containing chemical compounds, as the term "organic" is widely understood in the chemical arts.

[33] The term "specific capacity" refers to the amount (e.g., total or maximum amount) of electrons or lithium ions a material is able to hold (or discharge) per unit mass and can be expressed in units of mAh/g. In certain aspects and embodiments, specific capacity can be measured in a constant current discharge (or charge) analysis, which includes discharge (or charge) at a defined rate over a defined voltage range against a defined counterelectrode. For example, specific capacity can be measured upon discharge at a rate of about 0.05C (e.g., about 7.5 mA g) from 4.95 V to 2.0 V versus a Li/Li+ counterelectrode. Other discharge rates and other voltage ranges also can be used, such as a rate of about 0.1 C (e.g., about 15 mA g), or about 0.5C (e.g., about 75 mA g), or about 1 .0 C (e.g., about 150 mA/g).

[34] A rate "C" refers to either (depending on context) the discharge current as a fraction or multiple relative to a "1 C" current value under which a battery (in a substantially fully charged state) would substantially fully discharge in one hour, or the charge current as a fraction or multiple relative to a "1 C" current value under which the battery (in a substantially fully discharged state) would substantially fully charge in one hour.

[35] The term "NMC" refers to materials of Formulas (I) or (II) in which nickel, manganese, and cobalt are present. Formula (II) depicts lithium-rich NMC materials, also referred to herein at "OLO" materials.

[36] To the extent certain battery characteristics can vary with temperature, such characteristics are specified at room temperature (about 25 degrees C), unless the context clearly dictates otherwise.

[37] Ranges presented herein are inclusive of their endpoints. Thus, for example, the range 1 to 3 includes the values 1 and 3 as well as intermediate values.

[38] The terms "milling" and "mixing" are used interchangeably, except in the instances where low energy mixing processes are specified. In such instances, the materials were predominantly mixed rather than milled.

[39] A component of the OLO active material can be represented as: Lii ₊ a[Mn _b Ni _c COd]O2 (I) where a+b+c+d=1 and b is non-zero. In its activated form, the material represented by Formula (I) has a lithium ion vacancy such that it can be represented as:

Li _a [Mn _b Ni _c COd]O ₂ (II)

The loss of a lithium ion creates a vacancy and it is this vacancy in the active material represented by Formula (II) that facilitates lithium ion transfer in an electrochemical cell. Thus, an active material with lithium vacancies is said to be "activated."

[40] According to certain embodiments of the invention, the active material represented by Formula (II) advantageously can be formed prior to assembly of the electrochemical cell, thereby avoiding significant irreversible capacity losses during the first cycle of use of the electrochemical cell. In such embodiments, formation of the active material represented by Formula (II) occurs via the following generalized reaction:

Lii ₊ a[Mn _b NicCOd]O2+ AB LiB + AO _2-x + Li _a [MnbNicCOd]O ₂ (III) Formula (I) Formula (II) where A is an organic moiety or a metal; B is a halogen or a chalcogen; x= 1 or 0; a, b, c, & d retain the values defined for them in Formulas (I) and (II). The "AB-type" materials of Formula (III) can be referred to as activating compounds when used according to embodiments of the invention. The reaction can extract both an alkali metal, such as lithium, and an anion, such as an oxygen ion.

[41] In embodiments of the invention, lithium oxide materials react with the AB compound such that the lithium reacts with the halogen or chalcogen. In some embodiments, a binary alkali halide salt or a binary alkali chalcogenide salt is formed, and the formation of these salts provides the thermodynamic driving force for substantial chemical delithiation.

[42] More generally, embodiments of the invention relate to metal extraction from ceramic materials by high temperature reaction with an organo-halide or organo- chalcogenide. In such reactions, the halide or chalcogenide component reacts with the ceramic to form a metal-halide or metal-chalcogenide compound or complex. In this manner, the organo-halide or organo-chalcogenide extracts metal from the ceramic. Preferably, the metal is an alkali metal or an alkaline-earth metal.

[43] One of the advantages of the reaction of Formula (III) is that any oxygen liberated during the reaction is easily removed from the system prior to fabrication of the cathode. Another advantage of the reaction of Formula (III) is that the extraction of lithium from the material represented by Formula (I) can be stoichiometric. Control over the reaction is exercised by preselecting the amount of activating compound. In contrast, certain known methods of extracting lithium from the material represented by Formula (I) rely on the first cycle of an assembled cell to extract lithium. Such prior art methods of lithium extraction can release oxygen, which is problematic in an assembled cell, and do not allow for stoichiometric control of the lithium extraction.

[44] Another advantage of certain embodiments is that by pre-activating the active material of the cathode, the cathode is effectively chemically charged rather than electrochemically charged. Using a chemically charged or activated material, such as the material represented by Formula (II), it is possible to fabricate a primary battery from these high energy density OLO materials or similar materials. In contrast, conventional OLO materials are presently used only in secondary batteries where they can be electrochemically activated during a charge/discharge cycle. Thus, embodiments of the invention could be used for activation of battery materials, including full removal of alkali or alkaline-earth metal ions from a cathode material, to enable such a cathode material to be used in a primary battery.

[45] For example, in the case of a lithium nickel oxide cathode material chemically activated using PVdF, at least two different reactions are possible:

LiNiO ₂ + C ₂ H ₂ F ₂ NiO ₂ + LiF (IV) or LiNiO ₂ + C ₂ H ₂ F ₂ NiO _2-x + LiF + xCO (or CO ₂ ) (V)

Formula (V) illustrates the case where oxygen is liberated and reacts with the carbon of the PVdF. Other reaction products, including, but not limited to, CO, CO ₂ , H ₂ O, CO ₂ F, C, and/or C _x H _y , may be formed.

[46] According to embodiments of the invention, the irreversible capacity loss in OLO materials is reduced by pre-activating OLO materials via the reaction represented by Formula (III). Organo-halides, organo-chalcogenides, and metal halides are preferred materials for facilitating this chemical activation of OLO materials. According to certain embodiments, the activation process uses conventional materials for the formation of cathode materials based on lithium-rich layered oxides, such as Li ₂ CO ₃ , LiOH, Ni(OH) ₂ , NiO, NiOOH, NiCO ₃ , MnO ₂ , Mn ₂ O ₃ , MnCO3, CoO, Co ₂ O3, and Co(OH) ₂ , as well as various nitrates, sulfates, halides, and acetates for Li, Ni, Mn, and Co. These starting materials are milled using conventional milling processes or mixing processes with activating compounds represented in Formula (III), such as organo-halides, organo-chalcogenides, metal halides, or combinations thereof. This milled mixture is then annealed.

[47] In embodiments of Formula (III) in which A is a metal, the metal is preferably an alkali or alkaline-earth metal. In some embodiments of Formula (III) in which A is a metal, the metal may be a transition metal. In some embodiments of Formula (III) in which A is a metal, the metal may be an element from group 13, 14 or 15 of the periodic table or a rare earth element.

[48] In embodiments of Formula (III) in which A is an organic moiety, the organic moiety preferably contains a functional group that forms stable complexes with alkali or alkaline earth metals. Examples of preferable classes of organic moieties include fluoro-polymers, chloro-polymers, carbon-halides, alkyl fluorides, aryl fluorides, and combinations thereof. Examples of preferable fluoro-polymers include PVdF and PTFE. Examples of preferable chloro-polymers include polyvinylchloride (PVC). Examples of preferable carbon-halides include carbon monofluoride (CFx). Examples of preferable aryl fluorides include octafluoronapthalene.

[49] In some embodiments of Formula (III) in which B is a halogen, the halogen is not fluorine. In such embodiments, preferably the AB material of Formula (III) is an organo-halide based on chlorine, such as polyvinyl chloride (PVC). PVC is a comparatively low-cost organo-halide and would allow the activation process to be scaled up efficiently.

[50] In some embodiments of Formula (III) in which B is a chalcogen, the AB compound is preferably cadmium telluride, indium sulfide, zinc telluride, or sodium selenide. [51] Without being bound to any particular theory or mode of action, the annealing process may promote reaction of the "B" materials with the lithium contained in the cathode starting materials. For example, the high temperature may promote fluorine reaction with the lithium contained in a layered oxide material. Further, the "A" materials may react with any oxygen liberated in this process. For example, an organic "A" material such as carbon can react with liberated oxygen to form CO _x . Such a process results in an OLO material that has some amount of lithium pre- discharged or extracted, and provides an improvement in the observed irreversible capacity loss during first cycle. [52] According to certain embodiments, the milling is accomplished via a conventional milling process, such as ball-milling or other substantially equivalent milling processes.

[53] In certain embodiments, low energy mixing processes are preferable for materials where the low energy milling process preserves the morphology of the particles. Milling can deform particles and certain ceramics or cathode materials from which the metal is extracted benefit from a low energy mixing process.

[54] According to certain embodiments, the milled or mixed mixture is annealed at a relatively high temperature for a sufficient time. A suitable temperature range may be from about 150 degrees C to about 800 degrees C, from about 200 degrees C to about 800 degrees C, from about 250 degrees C to about 800 degrees C, from about 300 degrees C to about 800 degrees C, from about 350 degrees C to about 800 degrees C, from about 400 degrees C to about 800 degrees C, from about 450 degrees C to about 800 degrees C, from about 500 degrees C to about 800 degrees C, from about 550 degrees C to about 800 degrees C, from about 600 degrees C to about 800 degrees C, from about 650 degrees C to about 800 degrees C, or from about 700 degrees C to about 800 degrees C. A preferable temperature range may be from about 200 degrees C to about 600 degrees C.

[55] The annealing time may vary from about 0 hours to about 24 hours. More preferably, the annealing time varies from about 1 hours to about 6 hours, from about 1 .5 hours to about 6 hours, from about 2.0 hours to about 6 hours, from about 2.5 hours to about 6 hours, from about 3.0 hours to about 6 hours, from about 3.5 hours to about 6 hours, from about 4.0 hours to about 6 hours, from about 4.5 hours to about 6 hours, or from about 5.0 hours to about 6 hours.

[56] Although embodiments of the invention are described herein as relating to lithium extraction from OLO materials, certain embodiments are related more generally to the extraction of alkali metals from ceramic materials by high temperature reaction with an organo-halide, organo-chalcogenide, metal halide, or other activating materials disclosed herein. Certain embodiments disclosed herein can activate battery materials other than OLO materials and can be used to extract alkali ions, such as lithium, from the active materials of primary batteries. [57] The following examples describe specific aspects of some embodiments of the invention to illustrate and provide a description for those of ordinary skill in the art. The examples should not be construed as limiting the invention, as the examples merely provide specific methodology useful in understanding and practicing some embodiments of the invention. EXAMPLES

Lithium-rich layered oxides for secondary batteries (Half-cell)

[58] Materials and Synthetic Methods. All reactions were prepared in a high purity argon filled glove box (M-Braun, oxygen and humidity contents <0.1 ppm). Unless otherwise specified, materials were obtained from commercial sources (Sigma- Aldrich, Advanced Research Chemicals Inc, Alfa Aesar, etc.) without further purification.

[59] Layered Oxide Activation: An organo-halide and lithium-rich layered oxide material were mixed using a milling process. In some instances a low energy mixing process was used. Milling vessels were loaded with the organo-halide precursor (5 wt%), the lithium-rich layered oxide, and optionally a solvent, such as acetone. The vessels were then sealed and milled. After milling, solvents were evaporated from the mixture at 60 degrees C and the mixture was subsequently annealed in air, for example at from about 350 degrees C to about 450 degrees C. Reaction products may be optionally removed by rinsing or other methods. [60] Electrode Formulation. Cathodes based on the activated layered oxide material were prepared using a formulation composition of 85 : 7.5 : 7.5 (active material : binder : conductive additive) according to the following formulation method: 198 mg PVdF (Sigma Aldrich) was dissolved in 15 ml_ NMP (Sigma Aldrich) overnight. 198 mg of conductive additive was added to the solution and allowed to stir for several hours. 150 mg of the activated layered oxide material was then added to 1 ml_ of this solution and stirred overnight. Films were cast by dropping about 50 μΙ_ of slurry onto stainless steel current collectors and drying at 150 degrees C for about 1 hour. Dried films were allowed to cool, and were then pressed at 1 ton/cm ² . Electrodes were further dried at 150 degrees C under vacuum for 12 hours before being brought into a glove box for battery assembly.

[61] Electrochemical Characterization. All batteries were assembled in a high purity argon filled glove box (M-Braun, O2 and humidity contents <0.1 ppm), unless otherwise specified. Half cells were made using lithium as an anode, Celgard 2400 separator, and 90 μΙ_ of 1 M LiPF6 in 1 :2 EC:EMC electrolyte. Electrodes and cells were electrochemically characterized at 25 degrees C with a constant current C/10 charge and discharge rate between 4.7 and 2.5V. No constant voltage step was included. Full cells were made with carbon anodes.

Lithium-rich layered oxides for secondary batteries (Full-cell)

[62] Materials and Synthetic Methods. All reactions were prepared in a high purity argon filled glove box (M-Braun, oxygen and humidity contents <0.1 ppm). Unless otherwise specified, materials were obtained from commercial sources (Sigma- Aldrich, Advanced Research Chemicals Inc, Alfa Aesar, etc.) without further purification.

[63] Layered Oxide Activation. An organo-halide and OLO material were mixed using a milling process. Milling vessels were loaded with the organo-halide precursor (5 wt%), the OLO, and optionally a solvent, such as acetone. The vessels were then sealed and milled. After milling, solvents were evaporated from the mixture at 60 degrees C and the mixture was subsequently annealed in air at 450 degrees C. Reaction products may be optionally removed by rinsing or other methods. [64] Electrode Formulation. Cathodes based on the activated layered oxide material were prepared using a formulation composition of 85 : 7.5 : 7.5 (active material : binder : conductive additive) according to the following formulation method: 198 mg PVdF (Sigma Aldrich) was dissolved in 15 ml_ NMP (Sigma Aldrich) overnight. 198 mg of conductive additive was added to the solution and allowed to stir for several hours. 150 mg of the activated layered oxide material was then added to 1 ml_ of this solution and stirred overnight. Films were cast by dropping about 66 μΙ_ of slurry onto stainless steel current collectors and drying at 150 degrees C for about 1 hour. Dried films were allowed to cool, and were then pressed at 1 ton/cm ² . Electrodes were further dried at 150 degrees C under vacuum for 12 hours before being brought into a glove box for battery assembly. [65] Anodes based on MCMB (mesoporous carbon micro beads) were prepared using a formulation composition of 85 : 7 : 8 (active material : binder : conductive additive) according to the following formulation method: 132 mg PVdF (Sigma Aldrich), 1 15 mg of conductive additive, and 1400 mg of MCMB were dissolved in 10 ml_ NMP (Sigma Aldrich) overnight. Films were cast by dropping about 50 μΙ_ of slurry onto stainless steel current collectors and drying at 150 degrees C for about 1 hour. Dried films were allowed to cool, and were then pressed at 1 ton/cm ² . Electrodes were further dried at 150 degrees C under vacuum for 12 hours before being brought into a glove box for battery assembly.

[66] Electrochemical Characterization. All batteries were assembled in a high purity argon filled glove box (M-Braun, O2 and humidity contents <0.1 ppm), unless otherwise specified. Full cells were made using MCMB as an anode, Celgard 2400 separator, and 90 μΙ_ of 1 M LiPF6 in 1 :1 EC:EMC electrolyte. Electrodes and cells were electrochemicaNy characterized at 30 degrees C with a constant current C/20 charge and discharge rate between 4.6V and 2.0V. Delithiated lithium nickel oxide for primary batteries

[67] Materials and Synthetic Methods. All reactions were prepared in a high purity argon filled glove box (M-Braun, O2 and humidity contents <0.1 ppm). Unless otherwise specified, materials were obtained from commercial sources (Duracell) without further purification. [68] Lithium Nickel Oxide Delithiation. The organo-halide and lithium nickel oxide material were mixed using a low energy mixing process. Mixing vessels were loaded with the organo-halide precursor (70 molar ration) and the lithium nickel oxide. The mixture was then annealed at about 450 degrees C for about 6 hours in an inert atmosphere.

[69] Electrode Formulation. Cathodes based on the lithium nickel oxide material were prepared using a formulation composition of 79:21 (delithiated materials: carbon) according to the following formulation method: 1 g of delithiated materials was mixed with 267mg of carbon followed by adding 66.7μΙ_ of KOH (9M). 450mg of well-mixed materials were transferred into a cathode can and pressed by hand. 2.4g of Zn slurry was added to the anode can and enclosed by insulator ring. The separator was wetted using KOH (9M) and placed into the cathode can with cellophane tape facing the cathode film. The cathode can and the anode can were crimped together by hand.

[70] Electrochemical Characterization. All batteries were assembled in a high purity argon filled glove box (M-Braun, O2 and humidity contents <0.1 ppm), unless otherwise specified. Electrodes and cells were electrochemically characterized at 25 degrees C with a constant current C/40 discharge rate between about 2.5V and about 0.2V. No constant voltage step was included.

RESULTS

[71] Figure 1 is a voltage trace illustrating the irreversible capacity loss after the first cycle in a conventional OLO material. The coulombic efficiency (labeled "CE" in the graph) of this conventional, unmodified material was measured to be 78%. There was a 71 mAh/g irreversible capacity loss in the first charge-discharge cycle. Figure 1 demonstrates the irreversible capacity loss in prior art OLO materials.

[72] Figure 2 is a voltage trace illustrating an improvement in irreversible capacity loss using compounds and methods according to embodiments of the invention as compared to conventional materials. An OLO material was chemically delitiathed using PVdF as the "AB" material (an organo-fluoride) in the process described above. Figure 2 demonstrates an improvement in irreversible capacity loss - 24 mAh/g for the chemically delithiated material (labeled "PVdF treated") versus 71 mAh/g for the conventional material. The coulombic efficiency of the chemically delithiated material was measured to be 91 %. [73] Figure 3 is a voltage trace illustrating an improvement in irreversible capacity loss using compounds and methods according to embodiments of the invention as compared to conventional materials. The chemically delitiathed material shows an improved irreversible capacity loss. The materials were measured in a full cell using a carbon anode. The irreversible capacity loss improved from 76 mAh/g for the conventional OLO material to 49 mAh/g for the OLO material chemically delithiated with PVdF. The coulombic efficiency improved from 77.2% for the conventional OLO material to 82.0% for the OLO material chemically delithiated with PVdF.

[74] Figure 4 is a table of data illustrating improved performance attributable to compounds and methods according to embodiments of the invention as compared to conventional materials in a full cell with a carbon anode. The top row compares the actual irreversible capacity loss on the first cycle for conventional OLO materials and an OLO material chemically delithiated with PVdF. The OLO material has an irreversible capacity loss between about 80 mAh/g and about 75 mAh/g while the chemically delithiated material has an irreversible capacity loss of about 55 mAh/g. The middle row compares the percent irreversible capacity loss on the first cycle for conventional OLO materials and an OLO material chemically delithiated with PVdF. The OLO material has an irreversible capacity loss between about 31 % and about 29% while the chemically delithiated material has an irreversible capacity loss between about 25% and about 24%. The bottom row compares the coulombic efficiency for conventional OLO materials and an OLO material chemically delithiated with PVdF. The OLO material has a coulombic efficiency around about 77% while the chemically delithiated material has a coulombic efficiency around about 81 %.

[75] Figure 5 is a voltage trace comparison for conventional lithium-rich materials and materials chemically delithiated using PVdF. Figure 5 demonstrates that the irreversible capacity has been reduced from 18.7% to 3.9% by chemically delithiating the OLO material without any decrease in specific capacity. Further, Figure 5 shows that coulombic efficiency on first charge increases from 81 .3% to 96.1 % for the chemically delithiated material. [76] Figure 6 is a rate performance comparison between a conventional OLO material that has been chemically delithiated (circles) and one that has not been chemically delithiated (squares). The OLO material activated (that is, chemically delithiated) according to embodiments disclosed herein demonstrated improved rate performance. Figure 6 shows that the chemical activation process improves the rate performance for the OLO material from 64.5% to 76.1 %. [77] Figures 7A, 7B, and 7C are each scanning electron microscopy images of various materials according to embodiments of the invention. Figure 7A is an image of an unprocessed, as-received OLO material. Figure 7B is an image of the OLO material processed using a ball-milling mixing process. Figure 7C is an image of the OLO material processed using a lower energy mixing process and Figure 7C demonstrates that the low energy mixing process preserves the initial morphology. Importantly, the performance improvements shown in Figures 5 and 6 are accomplished without modifying the original particle morphology (Figure 7A), as shown in Figure 7C. Using a low energy mixing process, the as-received particle morphology is maintained while still improving irreversible capacity and rate performance.

[78] Figure 8 is a voltage trace comparison between a conventional OLO material (solid line) and the same material that has been chemically delithiated using PTFE (dashed line). Figure 8 demonstrates that the irreversible capacity has been reduced from 18.7% to 5.5% while also maintaining similar specific capacity between the materials.

[79] Table 1 provides a summary of data for a conventional OLO compared to the same material that has been chemically delithiated using PVdF. Table 1 shows that capacity, coulombic efficiency, rate performance, and cycle life are similar or better for the chemically delithiated material.

Table 1 . Cathode performance data with and without activation

Metric Activated Control

Specific Capacity at Cycle 1 (mAh/g) 254 260

Coulombic Efficiency at Cycle 1 (%) 96.1 81 .3

Rate Performance (2C/0.2C) 76.1 64.5

Cycle Life 25th cycle / 5th cycle (%) 93.0 91 .4

[80] Figure 9 is a voltage trace for a primary battery cell with a LiNiO ₂ cathode material delithiated using PVdF. Figure 9 demonstrates an extraction efficiency of approximately 70% for a solid state lithium extraction process using PVdF. From these results, it is understood that a ratio of PVdF to the nickel oxide starting material in excess of 100% is required to fully delithiate LiNi02-

[81] According to embodiments disclosed herein, conventional OLO materials can be improved using a chemical delithiation process such that the rate performance improves and the irreversible capacity loss at first cycle is less than 5%. These and other performance gains are achieved without diminishing other properties such as specific capacity. Particle morphology can be preserved as well.

[82] While the invention has been described with reference to the specific embodiments thereof, it should be understood by those skilled in the art that various changes may be made and equivalents may be substituted without departing from the true spirit and scope of the invention as defined by the appended claims. In addition, many modifications may be made to adapt a particular situation, material, composition of matter, method, or process to the objective, spirit and scope of the invention. All such modifications are intended to be within the scope of the claims appended hereto. In particular, while the methods disclosed herein have been described with reference to particular operations performed in a particular order, it will be understood that these operations may be combined, sub-divided, or reordered to form an equivalent method without departing from the teachings of the invention. Accordingly, unless specifically indicated herein, the order and grouping of the operations are not limitations of the invention.