Title:
MEMBRANES WITH COATINGS COMPRISING POLYMERIZED GLYCI DYLMETHACRYLATE FOR IMPROVED FLUX AND METHOD OF PREPARATION
Document Type and Number:
WIPO Patent Application WO/2014/095751
Kind Code:
A1
Abstract:
Membrane comprising a coating, wherein said coating comprises glycidylmethacrylate in polymerized form.

Inventors:
KONRADI RUPERT (DE)
MARCZEWSKI DAWID (DE)
STAUDT CLAUDIA (DE)
Application Number:
PCT/EP2013/076747
Publication Date:
June 26, 2014
Filing Date:
December 16, 2013
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BASF SE (DE)
International Classes:
B01D67/00; B01D69/02; B01D71/48
Domestic Patent References:
WO2005032701A22005-04-14
WO2005026224A12005-03-24
WO2006034575A12006-04-06
Foreign References:
US20120123002A12012-05-17
EP1842582A12007-10-10
Other References:
KIM M ET AL: "Ring-opening reaction of poly-GMA chain grafted onto a porous membrane", JOURNAL OF MEMBRANE SCIENCE, ELSEVIER SCIENTIFIC PUBL.COMPANY. AMSTERDAM, NL, vol. 117, no. 1, 21 August 1996 (1996-08-21), pages 33 - 38, XP004041613, ISSN: 0376-7388, DOI: 10.1016/0376-7388(96)00026-9
Download PDF:
Claims:
Claims

1 . Membrane comprising a coating, wherein said coating comprises glycidylmethacrylate in polymerized form, wherein said coating further comprises at least one flux enhancing monomer in polymerized form,

wherein said at least one flux enhancing monomer is an antiadhesive monomer selected from

a) esters of (meth)acrylic acid polyols, wherein (meth)acrylic esters with polyalkylene- oxides are excluded;

b) vinyl ethers of polyols;

c) hydrophilic macromonomers different from monomers a) and b);

d) N-vinyl compounds;

e) Low molecular weight hydrophilic (meth)acrylamides;

f) (meth)acrylates or (meth)acrylamides bearing epoxy groups;

g) monomers having a betain structure;

h) hydrophilic monomers selected from hydroxyethyl-(meth)acrylate, vinyl alcohol, (Meth)acryloyl and (meth)acrylamide-modified mono- and oligosaccharides,

with R1 = H, Methyl; X=0, NH;

i) Ion pair comonomers; and/or a biocidal monomer selected from

j) vinyl-imidazolium compounds;

k) ethylenically unsaturated monomers bearing quarternary ammonium or phosphoni- um groups;

I) diallyldialkylammoniumchlorides;

m) alkylaminoalkyl (meth)acrylates and alkylaminoalkyl (meth)acrylamides;

n) Polylysine (meth)acrylamides or (meth)acrylates;

o) alkyl-4-vinylpridinium and alkyl-2-vinyl-pyridinium salts, in particular bromides and iodides;

p) ethylenically unsaturated monomers bearing guanide and biguanide groups;

q) Halamines.

Membrane according to claim 1 , in which said membrane is suitable as a reverse osmosis membrane or forward osmosis membrane.

Membrane according to claim 1 or 2, wherein said coating is bound to the surface of base membrane through reaction of the epoxy group of glycidylmethacrylate with functional groups present on the surface of said base membrane.

4. Membrane according to any of claims 1 to 3, wherein said coating comprises at least one monomer according to formula (I)

10

(I) wherein

R7 is H or CH3,

Rs is Ci-Cs alkyI bi-radical,

Rg and Rio are independently H or d-Cs alkyl radical which can be linear or branched, and X is a divalent radical of -O-, -NH- or -NRn, wherein Rn is Ci-C6 alkyl.

5. Membrane according to any of claims 1 to 4, wherein said coating comprises 2-tert- butylaminoethyl (meth)acrylate or a combination of 2-Hydroxyethyl methacrylate and [2- (methacryloyloxy)ethyl] trimethylammonium chloride.

6. Membrane, obtained by a process comprising the following steps:

A. optionally oxidizing the surface of a base membrane,

B. treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C. curing said composition to form a coating,

wherein said at least one flux enhancing monomer is an antiadhesive monomer selected from

a) esters of (meth)acrylic acid polyols, wherein (meth)acrylic esters with polyalkylene- oxides are excluded;

b) vinyl ethers of polyols;

c) hydrophilic macromonomers different from monomers a) and b);

d) N-vinyl compounds;

e) Low molecular weight hydrophilic (meth)acrylamides;

f) (meth)acrylates or (meth)acrylamides bearing epoxy groups;

g) monomers having a betain structure;

h) hydrophilic monomers selected from hydroxyethyl-(meth)acrylate, vinyl alcohol, (Meth)acryloyl and (meth)acrylamide-modified mono- and oligosaccharides,

with R1 = H, Methyl; X=0, NH;

i) Ion pair comonomers; and/or a biocidal monomer selected from

j) vinyl-imidazolium compounds;

k) ethylenically unsaturated monomers bearing quarternary ammonium or phosphoni- um groups;

I) diallyldialkylammoniumchlorides;

m) alkylaminoalkyl (meth)acrylates and alkylaminoalkyl (meth)acrylamides;

n) Polylysine (meth)acrylamides or (meth)acrylates;

o) alkyl-4-vinylpridinium and alkyl-2-vinyl-pyridinium salts, in particular bromides and iodides;

p) ethylenically unsaturated monomers bearing guanide and biguanide groups;

q) Halamines.

7. Membrane according to claim 6, wherein said composition comprises at least one monomer according to formula (I)

(I) wherein

R7 is H or CHs,

Rs is Ci-Cs alkyI bi-radical,

Rg and Rio are independently H or d-Cs alkyl radical which can be linear or branched, and X is a divalent radical of -O-, -NH- or -NRn, wherein Rn is Ci-C6 alkyl.

8. Membrane according to any of 5 to 7, wherein said composition comprises 2-tert- butylaminoethyl (meth)acrylate or a combination of 2-Hydroxyethyl methacrylate and [2- (methacryloyloxy)ethyl] trimethylammonium chloride.

Membrane according to claims 5 to 8, wherein said composition comprises at least antiadhesive monomer and at least one biocidal monomer.

10. Membrane according to at least one of the preceding claims, wherein the membrane or the separating layer of the membrane comprises as main component a polymer selected from polyarylene ether, polysulfone, polyethersulfones (PES), polyphenylensulfone, pol- yamides (PA), polyvinylalcohol (PVA), Cellulose Acetate (CA), Cellulose Triacetate (CTA), CA-triacetate blend, Cellulose ester, Cellulose Nitrate, regenerated Cellulose, aromatic , aromatic/aliphatic or aliphatic Polyamide, aromatic, aromatic/aliphatic or aliphatic Polyimide, Polybenzimidazole (PBI), Polybenzimidazolone (PBIL), Polyacrylonitrile (PAN), PAN-poly(vinyl chloride) copolymer (PAN-PVC), PAN-methallyl sulfonate copolymer, Polysulfone, Poly(dimethylphenylene oxide) (PPO), Polycarbonate, Polyester, Polytetrafluroethylene PTFE, Poly(vinylidene fluoride) (PVDF), Polypropylene (PP), Polyelectrolyte complexes, Poly(methyl methacrylate) PMMA, Polydimethylsiloxane (PDMS), aromatic, aromatic/aliphatic or aliphatic polyimide urethanes, aromatic, aromatic/aliphatic or aliphatic polyamidimides, crosslinked polyimides or mixtures thereof.

1 1 . Membrane according to at least one of the preceding claims, in which said membrane is suitable as a reverse osmosis membrane, forward osmosis membrane, nanofiltration membrane, ultrafiltration membrane and/or microfiltration membrane.

12. Process for making a membrane according to at least one of the preceding claims, comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

13. Process for making a membrane according to at least one of the preceding claims, comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising glycidylmethacrylate, with the proviso that the composition does not comprise flux enhancing monomers

C) treatment with a composition comprising

i) optionally glycidylmethacrylate at least one flux enhancing monomer

D) curing said composition to form a coating.

14. Use of membranes according to at least one of the preceding claims or of membranes made according to at least one of the preceding claims for the treatment of water, used for the treatment of seawater or brackish water, for the desalination of sea water or brackish water, for the treatment of industrial or municipal wastewater, for food processing or for medical applications like dialysis.

15. Composition comprising

i) glycidylmethacrylate

ϋ) at least one flux enhancing monomer,

wherein said at least one flux enhancing monomer is an antiadhesive monomer selected from

a) esters of (meth)acrylic acid polyols, wherein (meth)acrylic esters with polyalkylene- oxides are excluded;

b) vinyl ethers of polyols;

c) hydrophilic macromonomers different from monomers a) and b);

d) N-vinyl compounds;

e) Low molecular weight hydrophilic (meth)acrylamides;

f) (meth)acrylates or (meth)acrylamides bearing epoxy groups;

g) monomers having a betain structure;

h) hydrophilic monomers selected from hydroxyethyl-(meth)acrylate, vinyl alcohol, (Meth)acryloyl and (meth)acrylamide-modified mono- and oligosaccharides,

with R1 = H, Methyl; X=0, NH;

i) Ion pair comonomers; and/or a biocidal monomer selected from

j) vinyl-imidazolium compounds;

k) ethylenically unsaturated monomers bearing quarternary ammonium or phosphoni- um groups;

I) diallyldialkylammoniumchlorides;

m) alkylaminoalkyl (meth)acrylates and alkylaminoalkyl (meth)acrylamides;

n) Polylysine (meth)acrylamides or (meth)acrylates;

o) alkyl-4-vinylpridinium and alkyl-2-vinyl-pyridinium salts, in particular bromides and iodides;

p) ethylenically unsaturated monomers bearing guanide and biguanide groups;

q) Halamines.

16. Composition according to claim 15, wherein said composition comprises at least one monomer according to formula (I)

(I) wherein

R7 is H or CHs,

Rs is Ci-Cs alkyI bi-radical,

Rg and Rio are independently H or d-Cs alkyl radical which can be linear or branched, and X is a divalent radical of -O-, -NH- or -NRn, wherein Rn is Ci-C6 alkyl.

17. Composition according to any of claims 15 to 16, wherein said composition comprises 2- tert-butylaminoethyl (meth)acrylate or a combination of 2-Hydroxyethyl methacrylate and [2-(methacryloyloxy)ethyl] trimethylammonium chloride.

18. Use of a composition according any of claims 15 to 17 for improving the flux through membranes.

19. Filtration system comprising at least one membrane, wherein at least one component or at least one part of a component of the filtration system has been obtained by a process comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

Description:
MEMBRANES WITH COATINGS COMPRISING POLYMERIZED GLYCI

DYLMETHACRYLATE FOR IMPROVED FLUX AND METHOD OF PREPARATION The invention is related to novel membranes comprising a coating, wherein said coating comprises glycidylmethacrylate in polymerized form.

The invention is further related to processes for making such membranes, the use of such membranes and to a method of increasing the flux through a membrane.

Different types of membranes play an increasingly important role in many fields of technology. In particular, methods for treating water rely more and more on membrane technology. An important issue with the application of membranes is fouling. The problem of biofouling is pronounced in semipermeable membranes used for separation purposes like reverse osmosis, forward osmosis, nanofiltration and/or ultra and micro filtration. Membranes may be classified according to their separation mechanism and/or pore sizes. For example, in water filtration applications ultrafiltration and microfiltration membranes (approximate pore diameter: 5 - 1000 nm) are used for wastewater treatment retaining organic and bioorganic material. In reverse osmosis and forward osmosis membranes, where monovalent ions and all components with larger diameter are rejected, the separation mechanism is based mainly on solution-diffusion mechanism.

In all applications where the ambient medium is an aqueous phase, potential blockage may oc- cur by adhesion of microorganisms and biofilm formation. As a consequence, a membrane is desired, which reduces biofilm formation and thus requires fewer cleaning cycles. This can for example be achieved through membranes with anti-adhesive or antifouling properties.

Thus, fouling is currently one of the major remaining problems for filtration membranes. Fouling causes deterioration of the membrane performance and shortens membrane lifetime, limiting further application of membrane technology. It is thus desirable to improve antifouling and antibacterial properties to membranes without impairing their separation characteristics in order to enhance their resistance.

Several approaches have been tried to solve the problem of fouling and biofouling and to pre- vent the formation and deposition of organic materials from organisms.

Recent research has focused on three strategies to prevent biofouling of membranes: 1 ) blending of hydrophilic or amphiphilic copolymers for the manufacture of membranes; 2) surface modification of membranes and 3) bulk modification of membrane materials.

The following documents describe approaches undertaken in recent years: H. Yamamura, K. Kimmura, Y. Watanabe, Mechanism involved in the evolution of physically irreversible fouling in microfiltration and ultrafiltration membranes used for drinking water treatment, Environ. Sci. Technol. 41 (2007) 6789-6794.

V. Kochkodan, S. Tsarenko, N. Potapchenko, V. Kosinova, V. Goncharuk, Adhesion of micro- organisms to polymer membranes: a photobactericidal effect of surface treatment with ΤΊ02, Desalination 220 (2008) 380-385.

J. Mansouri, S. Harrisson, Vivki Chen, Strategies for controlling biofouling in membrane filtration systems: challenges and opportunities. J. Mater. Chem., 20 (2010) US 4,277,344 discloses antifouling approaches on RO layers, formed by interfacial reaction.

Desalination 275 (201 1 ) 252-259, describes the grafting of PEG on a polyamide layer.

US 6,280,853 and US 2010/043,733 disclose coatings of composite membranes with various polymers including polyalkylene oxide compounds or polyacrylamide compounds.

A. V.R. Reddy, D. J. Mohan, A. Bhattacharya, V. J. Shah, P. K. Ghosh, Surface modification of ultrafiltration membranes by preadsorption of a negatively charged polymer: I. Permeation of water soluble polymers and inorganic salt solutions and fouling resistance properties, J. Membr. Sci. 214 (2003) 21 1-221 .

K. C. Khulbe, C. Feng, T. Matsuura, The art of surface modification of synthetic polymeric membranes, J. Appl. Polym. Sci. 1 15 (2010) 855-895.

B. Van der Bruggen, Chemical modification of polyethersulfone nanofiltration membranes: A review, J. Appl. Polym. Sci. 1 14 (2009) 630-642.

US 2007/0251883 discloses RO membranes with a branched polyalkyleneoxide modified antifouling surface.

WO 2005/32701 discloses the use of copolymers containing N-vinyl lactam for producing func- tionalized membranes.

WO 2005/26224 discloses a separating material obtained grafting of polymeric layers onto ami- no functional groups on a membrane surface.

Kim et al, Journal of Membrane Science, Elsevier, vol. 1 17, no.1 , 1996, p. 33-38 discloses ring opening reactions of poly-GMA chain grafted onto a porous membrane.

US 2012/123002 discloses a "method for the purification of antibody using porous membrane having amino groups and alkyl groups both bound to graft chain immobilized on porous sub- strate".

EP 1 842 582 discloses charged membranes obtained by grafting with epoxides and positively charged monomers.

WO 2006/34575 discloses composite materials comprising a support member having pores, a first polymer layer having hydrophobic and hydrophilic properties and a second polymer layer being more hydrophilic than the first polymer layer. It was an object of the invention to provide membranes that are less prone to fouling.

This objective has been solved by membrane comprising a coating, wherein said coating comprises glycidylmethacrylate (GMA) in polymerized form.

The concept of a membrane is generally known in the art. In the context of this application a membrane shall be understood to be a thin, semipermeable structure capable of separating two fluids or separating molecular and/or ionic components or particles from a liquid. A membrane acts as a selective barrier, allowing some particles, substances or chemicals to pass through, while retaining others.

Membranes according to the invention can for example be microporous (average pore diameter smaller than 2 nm), mesoporous (average pore diameter from 2 nm to 50 nm) or macroporous (average pore diameter above 50 nm). Average pore diameters in this context are determined according to DIN 14652:2007-09 through correlation with the molecular weight cutoff of a membrane.

Suitable membranes or the separation layer of suitable membranes can be made of at least one inorganic material like a ceramic or at least one organic polymer.

Examples of inorganic materials are clays, silicates, silicon carbide, aluminium oxide, zirconium oxide or graphite. Such membranes made of inorganic materials are normally made by applying pressure or by sintering of finely ground powder. Membranes made of inorganic materials may be composite membranes comprising two, three or more layers.

In one embodiment, membranes made from inorganic materials comprise a macroporous support layer, optionally an intermediate layer and a separation layer.

In this application the term "membrane" shall, depending on the context, refer to a membrane according to the invention that comprises a coating comprising GMA in polymerized form, or to a membrane that is subjected to a coating or grafting process to obtain a membrane according to the invention, or both.

Optionally, a membrane or the layer of a membrane that is used as starting material for a coating process to obtain a membrane according to the invention is sometimes referred to as a "base membrane".

Thus, in case a membrane comprises more than one layer, the "base membrane" can refer to all layers of said membrane as a whole or to each of the layers of said membrane. The term "base membrane" usually refers to the layer that is subjected to the process steps A), B) and C) as defined above. In one preferred embodiment, the base membrane refers to the separation layer of a membrane.

In another embodiment, the base membrane denotes the support membrane of a membrane, the protective layer or a nonwoven or woven support layer of a membrane.

In a preferred embodiment, suitable membranes and/or the separation layer of a membrane comprise organic polymers, hereinafter referred to as polymers as the main components. A polymer shall be considered the main component of a membrane if it is comprised in said membrane or in the separation layer of said membrane in an amount of at least 50 %by weight, preferably at least 60%, more preferably at least 70%, even more preferably at least 80% and particularly preferably at least 90% by weight.

Examples of suitable polymers are polyarylene ether, polysulfone, polyethersulfones (PES), polyphenylenesulfone (PPSU), polyamides (PA), polyvinylalcohol (PVA), cellulose acetate (CA), cellulose diacetate, cellulose triacetate (CTA), CA-triacetate blend, cellulose ester, cellulose nitrate, regenerated cellulose, aromatic , aromatic/aliphatic or aliphatic polyamide, aromatic, aromatic/aliphatic or aliphatic polyimide, polybenzimidazole (PBI), polybenzimidazolone (PBIL), polyacrylonitrile (PAN), polyetheretherketone (PEEK), sulfonated polyetheretherketone

(SPEEK),PAN-poly(vinyl chloride) copolymer (PAN-PVC), PAN-methallyl sulfonate copolymer, poly(dimethylphenylene oxide) (PPO), polycarbonate, polyester, polytetrafluroethylene PTFE, poly(vinylidene fluoride) (PVDF), polypropylene (PP), polyelectrolyte complexes, poly(methyl methacrylate) PMMA, polydimethylsiloxane (PDMS), aromatic, aromatic/aliphatic or aliphatic polyimide urethanes, aromatic, aromatic/aliphatic or aliphatic polyamidimides, crosslinked poly- imides or mixtures thereof.

Preferably, membranes according to the invention comprise polysulfones, polyethersulfones (PES), polyamides (PA), polyvinylalcohols (PVA), Cellulose Acetate (CA), Cellulose Triacetate (CTA) Poly(vinylidene fluoride) (PVDF) or mixtures thereof as main components.

Suitable polyethersulfones can for example be obtained from BASF SE under the brand name Ultrason< R >.

Preferred polyarylene ether sulfones (A) are composed of units of the general formula I where the definitions of the symbols t, q, Q, T, Y, Ar and Ar 1 are as follows: t, q: independently of one another 0, 1 , 2, or 3, Q, T, Y: independently of one another in each case a chemical bond or group selected from -0-, -S-, -SO2-, S=0, C=0, -N=N-, and -CR a R b -, where R a and R b independently of one another are in each case a hydrogen atom or a Ci-Ci2-alkyl, Ci-Ci2-alkoxy, or C6-Ci8-aryl group, and where at least one of Q, T, and Y is -SO2-, and Ar and Ar 1 : independently of one another an arylene group having from 6 to 18 carbon atoms.

If, within the abovementioned preconditions, Q, T or Y is a chemical bond, this then means that the adjacent group on the left-hand side and the adjacent group on the right-hand side are present with direct linkage to one another via a chemical bond.

However, it is preferable that Q, T, and Y in formula I are selected independently of one another from -O- and -SO2-, with the proviso that at least one of the group consisting of Q, T, and Y

If Q, T, or Y is -CR a R b -, R a and R b independently of one another are in each case a hydrogen atom or a Ci-Ci2-alkyl, Ci-Ci2-alkoxy, or C6-Ci8-aryl group.

Preferred Ci-Ci2-alkyl groups comprise linear and branched, saturated alkyl groups having from 1 to 12 carbon atoms. The following moieties may be mentioned in particular: Ci-C6-alkyl moie- ty, e.g. methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, 2- or 3-methylpentyl, and longer chain moieties, e.g. unbranched heptyl, octyl, nonyl, decyl, undecyl, lauryl, and the singly branched or multibranched analogs thereof.

Alkyl moieties that can be used in the abovementioned Ci-Ci2-alkoxy groups that can be used are the alkyl groups defined at an earlier stage above having from 1 to 12 carbon atoms. Cyclo- alkyl moieties that can be used with preference in particular comprise C3-Ci2-cycloalkyl moieties, e.g. cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclopropylme- thyl, cyclopropylethyl, cyclopropylpropyl, cyclobutylmethyl, cyclobutylethyl, cyclopen- tylethyl, -propyl, -butyl, -pentyl, -hexyl, cyclohexylmethyl, -dimethyl, and -trimethyl.

Ar and Ar 1 are independently of one another a C6-Ci8-arylene group. On the basis of the starting materials described at a later stage below, it is preferable that Ar derives from an electron-rich aromatic substance that is very susceptible to electrophilic attack, preferably selected from the group consisting of hydroquinone, resorcinol, dihydroxynaphthalene, in particular 2,7- dihydroxynaphthalene, and 4,4'-bisphenol. Ar 1 is preferably an unsubstituted C6- or Ci2-arylene group.

Particular C6-Ci8-arylene groups Ar and Ar 1 that can be used are phenylene groups, e.g. 1 ,2-, 1 ,3-, and 1 ,4-phenylene, naphthylene groups, e.g. 1 ,6-, 1 ,7-, 2,6-, and 2,7-naphthylene, and also the arylene groups that derive from anthracene, from phenanthrene, and from naph- thacene. In the preferred embodiment according to formula I, it is preferable that Ar and Ar 1 are selected independently of one another from the group consisting of 1 ,4-phenylene, 1 ,3-phenylene, naph- thylene, in particular 2, 7-dihydroxynaphthylene, and 4,4'-bisphenylene. Preferred polyarylene ether sulfones (A) are those which comprise at least one of the following repeat units la to lo:

Other preferred units, in addition to the units la to lo that are preferably present, are those in which one or more 1 ,4-phenylene units deriving from hydroquinone have been replaced by 1 ,3-phenylene units deriving from resorcinol, or by naphthylene units deriving from dihy- droxynaphthalene. Particularly preferred units of the general formula I are the units la, Ig, and Ik. It is also particularly preferable that the polyarylene ether sulfones of component (A) are in essence composed of one type of unit of the general formula I, in particular of one unit selected from la, Ig, and Ik.

In one particularly preferred embodiment, Ar = 1 ,4-phenylene, t = 1 , q = 0, T is a chemical bond, and Y = SO2. Particularly preferred polyarylene ether sulfones (A) composed of the abovemen- tioned repeat unit are termed polyphenylene sulfone (PPSU) (formula Ig).

In another particularly preferred embodiment, Ar = 1 ,4-phenylene, t = 1 , q = 0, T = C(CH3)2, and Y = SO2. Particularly preferred polyarylene ether sulfones (A) composed of the abovementioned repeat unit are termed polysulfone (PSU) (formula la). In another particularly preferred embodiment, Ar = 1 ,4-phenylene, t = 1 , q = 0, T = Y = SO2. Particularly preferred polyarylene ether sulfones (A) composed of the abovementioned repeat unit are termed polyether sulfone (PESU or PES) (formula Ik). This embodiment is very particularly preferred.

For the purposes of the present invention, abbreviations such as PPSU, PESU, and PSU are in accordance with DIN EN ISO 1043-1 :2001 .

The weight-average molar masses M w of the polyarylene ether sulfones (A) of the present invention are preferably from 10 000 to 150 000 g/mol, in particular from 15 000 to 120 000 g/mol, particularly preferably from 18 000 to 100 000 g/mol, determined by means of gel permeation chromatography in dimethylacetamide as solvent against narrowly-distributed polymethyl meth- acrylate as standard.

In one embodiment of the invention, suitable polyarylene ether sulfones , particularly polysul- fones or polyethersulfones comprise sulfonic acids, carboxylic acid, amino and/or hydroxy groups on some or all of the aromatic rings in the polymer.

Production processes that lead to the abovementioned polyarylene ethers are known to the person skilled in the art and are described by way of example in Herman F. Mark, "Encyclope- dia of Polymer Science and Technology", third edition, volume 4, 2003, chapter "Polysulfones" pages 2 to 8, and also in Hans R. Kricheldorf, "Aromatic Polyethers " in: Handbook of Polymer Synthesis, second edition, 2005, pages 427 to 443.

Suitable membranes are for example membranes suitable as reverse osmosis (RO) membranes, forward osmosis (FO) membranes, nanofiltration (NF) membranes, ultrafiltration (UF) membranes or microfiltration (MF) membranes. These membrane types are generally known in the art.

Suitable membranes are for example those disclosed in US 201 1/0027599 in [0021] to [0169]; US 2008/0237126 in col 4, In 36 to col 6, In 3; US 2010/0224555 in [0147] to [0490]; US

2010/0062156 in [0058] to [0225]; US 201 1/0005997 in [0045] to [0390], US 2009/0272692 in [0019] to [0073], US 2012/0285890 in [0016] to [0043]; these documents are incorporated here- in by reference.

Further suitable membranes are for example those disclosed in US6787216,col. 2, In 54 to col 6, In 19; US 6,454,943, col. 3; In 25 to col. 6, In 12; and WO 2006/012920, p. 3, last paragraph to p. 10, first paragraph.

FO membranes are normally suitable for treatment of seawater, brackish water, sewage or sludge streams. Thereby pure water is removed from those streams through a FO membrane into a so called draw solution on the back side of the membrane having a high osmotic pressure. Typically, FO type membranes, similar as RO membranes are separating liquid mixtures via a solution diffusion mechanism, where only water can pass the membrane whereas monovalent ions and larger components are rejected.

In a preferred embodiment, suitable FO membranes are thin film composite (TFC) FO membranes. Preparation methods and use of thin film composite membranes are principally known and, for example described by R. J. Petersen in Journal of Membrane Science 83 (1993) 81 - 150.

In a further preferred embodiment, suitable FO membranes comprise a support layer, a separation layer and optionally a protective layer. Said protective layer can be considered an additional coating to smoothen and/or hydrophilize the surface. Said fabric layer can for example have a thickness of 10 to 500 μηη. Said fabric layer can for example be a woven or nonwoven, for example a polyester nonwoven.

Said support layer of a TFC FO membrane normally comprises pores with an average pore diameter of for example 0.5 to 100 nm, preferably 1 to 40 nm, more preferably 5 to 20 nm. Said support layer can for example have a thickness of 5 to 1000 μηη, preferably 10 to 200 μηη. Said support layer may for example comprise a main component a polysulfone, polyethersulfone, polyphenylenesulfone (PPSU), PVDF, polyimide, polyimideurethane or cellulose acetate. Nano particles such as zeolites, particularly zeolite LTA, may be comprised in said support membrane. This can for example be achieved by including such nano particles in the dope solution for the preparation of said support layer.

Said separation layer can for example have a thickness of 0.05 to 1 μηη, preferably 0.1 to 0.5 μηη, more preferably 0. 15 to 0.3 μηη. Preferably, said separation layer can for example comprise polyamide or cellulose acetate as the main component.

Optionally, TFC FO membranes can comprise a protective layer with a thickness of 30-500 preferably 100-300 nm. Said protective layer can for example comprise polyvinylalcohol (PVA) as the main component. In one embodiment, the protective layer comprises a halamine like chloramine.

In one preferred embodiment, suitable membranes are TFC FO membranes comprising a support layer comprising polyethersulfone as main component, a separation layer comprising polyamide as main component and optionally a protective layer comprising polyvinylalcohol as the main component.

In a preferred embodiment suitable FO membranes comprise a separation layer obtained from the condensation of a polyamine and a polyfunctional acyl halide. Said separation layer can for example be obtained in an interfacial polymerization process. RO membranes are normally suitable for removing molecules and ions, in particular monovalent ions. Typically, RO membranes are separating mixtures based on a solution/diffusion mechanism.

In a preferred embodiment, suitable membranes are thin film composite (TFC) RO membranes. Preparation methods and use of thin film composite membranes are principally known and, for example described by R. J. Petersen in Journal of Membrane Science 83 (1993) 81 -150.

In a further preferred embodiment, suitable RO membranes comprise a fabric layer, a support layer, a separation layer and optionally a protective layer. Said protective layer can be considered an additional coating to smoothen and/or hydrophilize the surface

Said fabric layer can for example have a thickness of 10 to 500 μηη. Said fabric layer can for example be a woven or nonwoven, for example a polyester nonwoven.

Said support layer of a TFC RO membrane normally comprises pores with an average pore diameter of for example 0.5 to 100 nm, preferably 1 to 40 nm, more preferably 5 to 20 nm. Said support layer can for example have a thickness of 5 to 1000 μηη, preferably 10 to 200 μηη. Said support layer may for example comprise a main component a polysulfone, polyethersulfone, PVDF, polyimide, polyimideurethane or cellulose acetate. Nano particles such as zeolites, particularly zeolite LTA, may be comprised in said support membrane. This can for example be achieved by including such nano particles in the dope solution for the preparation of said sup- port layer.

Said separation layer can for example have a thickness of 0.02 to 1 μηη, preferably 0.03 to 0.5 μηη, more preferably 0.05 to 0.3 μηη. Preferably, said separation layer can for example comprise polyamide or cellulose acetate as the main component.

Optionally, TFC RO membranes can comprise a protective layer with a thickness of 5 to 500 preferable 10 to 300 nm. Said protective layer can for example comprise polyvinylalcohol (PVA) as the main component. In one embodiment, the protective layer comprises a halamine like chloramine.

In one preferred embodiment, suitable membranes are TFC RO membranes comprising a nonwoven polyester fabric, a support layer comprising polyethersulfone as main component, a separation layer comprising polyamide as main component and optionally a protective layer comprising polyvinylalcohol as the main component. In a preferred embodiment suitable RO membranes comprise a separation layer obtained from the condensation of a polyamine and a polyfunctional acyl halide. Said separation layer can for example be obtained in an interfacial polymerization process. Suitable polyamine monomers can have primary or secondary amino groups and can be aromatic (e. g., a diaminobenzene, a triaminobenzene, m-phenylenediamine, p-phenylenediamine, 1 ,3,5-triaminobenzene, 1 ,3,4-triaminobenzene, 3,5-diaminobenzoic acid, 2,4-diaminotoluene, 2,4-diaminoanisole, and xylylenediamine) or aliphatic (e. g. ethylenediamine, propylenediamine, piperazine, and tris(2-diaminoethyl)amine).

Suitable polyfunctional acyl halides include trimesoyl chloride (TMC), trimellitic acid chloride, isophthaloyl chloride, terephthaloyl chloride and similar compounds or blends of suitable acyl halides. As a further example, the second monomer can be a phthaloyl halide.

In one embodiment of the invention, a separation layer of polyamide is made from the reaction of an aqueous solution of meta-phenylene diamine (MPD) with a solution of trimesoyl chloride (TMC) in an apolar solvent. In another embodiment of the invention, the separation layer and optionally other layers of the membrane contain nanoparticles other than of vanadium pentoxide. Suitable nanoparticles normally have an average particle size of 1 to 1000 nm, preferably 2 to 100 nm, determined by dynamic light scattering. Suitable nanoparticles can for example be zeolites, silica, silicates or aluminium oxide. Examples of suitable nanoparticles include Aluminite, Alunite, Ammonia Alum, Altauxite, Apjohnite, Basaluminite, Batavite, Bauxite, Beideilite, Boehmite, Cadwaladerite, Cardenite, Chalcoalumite, Chiolite, Chloraluminite, Cryolite, Dawsonite, Diaspore, Dickite, Gearksutite, Gibbsite, Hailoysite, Hydrobasaluminite, Hydrocalumite, Hydrotalcite, lllite, Kalinite, Kaolinite, Mellite, Montmoriilonite, Natroalunite, Nontronite, Pachnolite, Prehnite, Prosopite, Ralstonite, Ransomite, Saponite, Thomsenolite, Weberite, Woodhouseite, and Zincaluminit, kehoeite, pahasapaite and tiptopite; and the silicates: hsianghualite, lovdarite, viseite, partheite, prehnite, roggianite, apophyllite, gyrolite, maricopaite, okenite, tacharanite and tobermorite.

Nanoparticles may also include a metallic species such as gold, silver, copper, zinc, titanium, iron, aluminum, zirconium, indium, tin, magnesium, or calcium or an alloy thereof or an oxide thereof or a mixture thereof. They can also be a nonmetallic species such as Si3N4, SiC, BN, B4C, or TIC or an alloy thereof or a mixture thereof. They can be a carbon-based species such as graphite, carbon glass, a carbon cluster of at least C~, buckminsterfullerene, a higher fuller- ene, a carbon nanotube, a carbon nanoparticle, or a mixture thereof. In yet another embodiment the separation layer and optionally other layers of the membrane contain zeolites, zeolite precursors, amorphous aluminosilicates or metal organic frame works (MOFs) any preferred MOFs. Preferred zeolites include zeolite LTA, RHO, PAU, and KFI. LTA is especially preferred. Preferably, the nanoparticles other than vanadium pentoxide comprised in the membrane have a polydispersity of less than 3. In another embodiment of the invention the separation layer of the membrane contains a further additive increasing the permeability of the RO membrane. Said further additive can for example be a metal salt of a beta-diketonate compound, in particular an acetoacetonate and/or an at least partially fluorinated beta-diketonate compound.

NF membranes are normally especially suitable for removing separate multivalent ions and large monovalent ions. Typically, NF membranes function through a solution/diffusion or/and filtration-based mechanism.

NF membranes are normally used in cross filtration processes.

NF membranes can for example comprise as the main component polyarylene ether, polysul- fone, polyethersulfones (PES), polyphenylenesulfone (PPSU), polyamides (PA), polyvinylalco- hol (PVA), Cellulose Acetate (CA), Cellulose Triacetate (CTA), CA-triacetate blend, Cellulose ester, Cellulose Nitrate, regenerated Cellulose, aromatic , aromatic/aliphatic or aliphatic Poly- amide, aromatic, aromatic/aliphatic or aliphatic Polyimide, Polybenzimidazole (PBI), Polyben- zimidazolone (PBIL), polyetheretherketone (PEEK), sulfonated polyetheretherketone (SPEEK), Polyacrylonitrile (PAN), PAN-poly(vinyl chloride) copolymer (PAN-PVC), PAN-methallyl sulfonate copolymer, Polysulfone, Poly(dimethylphenylene oxide) (PPO), Polycarbonate, Polyester, Polytetrafluroethylene PTFE, Poly(vinylidene fluoride) (PVDF), Polypropylene (PP), Poly- electrolyte complexes, Poly(methyl methacrylate) PMMA, Polydimethylsiloxane (PDMS), aromatic, aromatic/aliphatic or aliphatic polyimide urethanes, aromatic, aromatic/aliphatic or aliphatic polyamidimides, crosslinked polyimides or mixtures thereof. In a preferred embodiment, said main components of NF membranes are positively or negatively charged.

Nanofiltration membranes often comprise charged polymers comprising sulfonic acid groups, carboxylic acid groups and/or ammonium groups.

Preferably, NF membranes comprise as the main component polyamides, polyimides or polyi- mide urethanes, Polyetheretherketone (PEEK) or sulfonated polyetheretherketone (SPEEK).

UF membranes are normally suitable for removing suspended solid particles and solutes of high molecular weight, for example above 1000 Da. In particular, UF membranes are normally suitable for removing bacteria and viruses. UF membranes normally have an average pore diameter of 0.5 nm to 50 nm, preferably 1 to 40 nm, more preferably 5 to 20 nm.

UF membranes can for example comprise as main component a polyarylene ether, polysulfone, polyethersulfones (PES), polyphenylenesulfone (PPSU), polyamides (PA), polyvinylalcohol (PVA), Cellulose Acetate (CA), Cellulose Triacetate (CTA), CA-triacetate blend, Cellulose ester, Cellulose Nitrate, regenerated Cellulose, aromatic , aromatic/aliphatic or aliphatic Polyamide, aromatic, aromatic/aliphatic or aliphatic Polyimide, Polybenzimidazole (PBI), Polybenzimidazo- lone (PBIL), Polyacrylonitrile (PAN), PAN-poly(vinyl chloride) copolymer (PAN-PVC), PAN- methallyl sulfonate copolymer, Polysulfone, Poly(dimethylphenylene oxide) (PPO), Polycarbonate, Polyester, Polytetrafluroethylene PTFE, Poly(vinylidene fluoride) (PVDF), Polypropylene (PP), Polyelectrolyte complexes, Poly(methyl methacrylate) PMMA, Polydimethylsiloxane (PDMS), aromatic, aromatic/aliphatic or aliphatic polyimide urethanes, aromatic, aromatic/aliphatic or aliphatic polyamidimides, crosslinked polyimides or mixtures thereof.

Preferably, UF membranes comprise as main component polysulfone, polyethersulfone, polyphenylenesulfone (PPSU), PVDF, polyimide, polyamidimide, crosslinked polyimides, polyimide urethanes or mixtures thereof. In one embodiment, UF membranes comprise further additives like block copolymers of polyarylene sulfones and alkyleneoxides like polyethyleneoxide.

In one embodiment, UF membranes comprise further additives like polyvinyl pyrrolidones.

In a preferred embodiment, UF membranes comprise as major components polysulfones or polyethersulfone in combination with further additives like polyvinylpyrrolidone.

In one preferred embodiment, UF membranes comprise 80 to 50% by weight of polyethersul- fone and 20 to 50 %by weight of polyvinylpyrrolidone.

In another embodiment UF membranes comprise 95 to 80% by weight of polyethersulfone and 5 to 15 %by weight of polyvinylpyrrolidone.

In another embodiment UF membranes comprise 99.9 to 80% by weight of polyethersulfone and 0.1 to 15 %by weight of polyvinylpyrrolidone.

In one embodiment of the invention, UF membranes are present as spiral wound membranes. In another embodiment of the invention, UF membranes are present as tubular membranes. In another embodiment of the invention, UF membranes are present as flat sheet membranes. In another embodiment of the invention, UF membranes are present as hollow fiber membranes. In yet another embodiment of the invention, UF membranes are present as single bore hollow fiber membranes.

In yet another embodiment of the invention, UF membranes are present as multi bore hollow fiber membranes.

MF membranes are normally suitable for removing particles with a particle size of 0.1 μηη and above. MF membranes normally have an average pore diameter of 0.1 μηη to 10 nm, preferably 1.0 μηη to 5 μηη.

Microfiltration can use a pressurized system but it does not need to include pressure. MF membranes can be hollow fibers, flat sheet, tubular, spiral wound, hollow fine fiber or track etched. They are porous and allow water, monovalent species (Na + , Ch), dissolved organic matter, small colloids and viruses through while retaining particles, sediment, algae or large bacteria.

Microfiltration systems are designed to remove suspended solids down to 0.1 micrometres in size, in a feed solution with up to 2-3% in concentration.

MF membranes can for example comprise as main component polyarylene ether, polysulfone, polyethersulfones (PES), polyphenylenesulfone (PPSU), polyamides (PA), polyvinylalcohol (PVA), Cellulose Acetate (CA), Cellulose Triacetate (CTA), CA-triacetate blend, Cellulose ester, Cellulose Nitrate, regenerated Cellulose, aromatic , aromatic/aliphatic or aliphatic Polyamide, aromatic, aromatic/aliphatic or aliphatic Polyimide, Polybenzimidazole (PBI), Polybenzimidazo- lone (PBIL), Polyacrylonitrile (PAN), PAN-poly(vinyl chloride) copolymer (PAN-PVC), PAN- methallyl sulfonate copolymer, Polysulfone, Poly(dimethylphenylene oxide) (PPO), Polycarbonate, Polyester, Polytetrafluroethylene PTFE, Poly(vinylidene fluoride) (PVDF), Polypropyl- ene (PP), Polyelectrolyte complexes, Poly(methyl methacrylate) PMMA, Polydimethylsiloxane (PDMS), aromatic, aromatic/aliphatic or aliphatic polyimide urethanes, aromatic, aromatic/aliphatic or aliphatic polyamidimides, crosslinked polyimides or mixtures thereof.

In one preferred embodiment of the invention, membrane according to the invention comprise a coating, wherein said coating comprises GMA and further comprises at least one flux enhancing monomer in polymerized form.

A "monomer", for example "biocidal monomers", "antiadhesive monomers" or specifically GMA in this application shall, depending on the context, refer to such monomer in unpolymerized (monomeric) form or in polymerized form. When the term "monomer" is for example used in the context of a formulation, it normally refers to the unpolymerized form. When the term "monomer" is for example used in the context of a polymer or a coating, it normally refers to the polymerized form, in which said monomer is comprised in the polymer or coating.

Monomers that impart flux enhancing properties to the membrane are herein also referred to as "flux enhancing monomers" or "flux improving monomers". The term "flux" shall denote the flux of the medium that is subjected to a separation operation. In many cases, "flux" means the flux of water through the membrane. For example in the case of water treatment applications, "flux" means the amount of water that permeates through the specified membrane area in a certain period of time.

In the context of this application, "improving the flux" or "enhancing the flux" shall also be understood to mean "reducing the decrease of flux through a membrane over time".

Flux enhancing properties in the context of this invention refer in particular to the long term properties of membranes. While it is possible that through the application of a coating the flux may decrease over a short term, the flux over the long term will be improved (meaning that the decrease of flux is reduced) relative to a membrane to that no such coating has been applied. The duration of a "short term" or "long term" may vary depending on the membrane or the application or the material subjected to that application, that is for example from the type of water treated. Thus, enhancing of flux in the context of this application shall mean that after at least one certain period of time and under at least one set of application conditions, the flux through a membrane according to the invention shall be improved or the decrease of flux be reduced over the flux through a membrane comprising no coating according to this invention or over membranes known from the art For example, membranes according to the invention may show improved flux over prior art membranes after a period of 1 hour, 1 day, 3 days, 5 days, 1 week, 2 weeks, three weeks, one month, two months, three months, six months and/or one year. Some- times the enhanced flux of membranes according to the invention only becomes observable after one or a certain number of cleaning cycles have been applied to the membrane.

It is also possible the membranes according to the invention show improved properties with respect to their ability to restore the flux after cleaning. Also membranes according to the invention can be easier to clean. Furthermore less cleaning agents may be requires for cleaning membranes according to the invention.

In particular, suitable flux enhancing monomers reduce fouling and in particular biofouling of the membrane.

In the context of this application, an effect of a polymer or the coating comprising a flux enhancing monomer is also sometimes referred to as the effect of the flux enhancing monomer. Monomers bearing a charge, for example from ammonium groups or carboxylate groups, are accompanied by one or more counterions. If, in this application, a monomer bearing a charge is depicted or named without corresponding counterion, such monomers are to be understood to be accompanied by a suitable counterion (with the exception of betaines). Such counterions are for example chloride, bromide, iodide or carboxylates for monomers bearing a positive charge. For monomers bearing negative charge, suitable counterions are for example sodium, potassium, magnesium, calcium or ammonium.

In a preferred embodiment, suitable flux enhancing monomers are antiadhesive or biocidal monomers that impart biocidal and/or antiadhesive properties to the membrane.

An antiadhesive monomer in the context of this application shall mean a monomer that imparts antiadhesive properties to the coating, be it by itself or in combination with other components. Antiadhesive properties or antiadhesive coating means that for example particles or biological material or biological organisms or degradation products of biological material or biological organisms have a lower tendency to adhere to the surface of a membrane having such antiadhesive properties. The degree of fouling and in particular biofouling of a membrane is thus reduced.

Antiadhesive coatings are sometimes also referred to as anti-sticking coatings, 'stealth' coatings or biopassive coatings.

The concept of antiadhesive polymers and coatings is for example disclosed in the following pieces of literature, which are incorporated herein by reference:

R. Konradi et al. Macromol. Rapid Commun. 2012, 33, 1663-1676;

R. G. Chapman , E. Ostuni , M. N. Liang , G. Meluleni , E. Kim, L. Yan , G. Pier , H. S. Warren , G. M. Whitesides , Langmuir 2001 , 17 , 1225;

R. G. Chapman , E. Ostuni , S. Takayama , R. E. Holmlin , L. Yan, G. M. Whitesides,

J.Am.Chem.Soc. 2000 , 122 , 8303;

E. Ostuni , R. G. Chapman , R. E. Holmlin , S. Takayama, G. M. Whitesides , Langmuir 2001 , 17 , 5605;

E. Ostuni , R. G. Chapman , M. N. Liang , G. Meluleni , G. Pier, D. E. Ingber , G. M. Whitesides, Langmuir 2001 , 17 , 6336. In one embodiment of the invention, suitable antiadhesive monomers are those, whose polymerization leads to the formation of antiadhesive coatings that are characterized by the presence of hydrophilic groups and preferentially the presence of hydrogen-bond-accepting groups, preferentially the absence of hydrogen-bond donating groups and preferentially the absence of net charge.

Suitable antiadhesive monomers are for example selected from

a) esters of (meth)acrylic acid with polyols

b) vinyl ethers of polyols c) hydrophilic macromonomers different from monomers a) and b)

d) N-vinyl compounds

e) Low molecular weight hydrophilic (meth)acrylamides

f) (meth)acrylates or (meth)acrylamides bearing epoxy groups

9) monomers having a betain structure

h) hydrophilic monomers different from those mentioned under a) to g).

i) Ion pair comonomers

Suitable esters of (meth)acrylic acid with polyols a) are preferably esters with polyols that are hydrophilic and with which coatings can be prepared that show antiadhesive properties as described above.

In one embodiment, suitable esters of (meth)acrylic acid with polyols are polyols, in which each OH group is esterified with (meth)acrylic acid.

In one embodiment, suitable esters of (meth)acrylic acid with polyols are polyols, in which at least one OH group is esterified with (meth)acrylic acid and at least one OH group is not esterified.

In one embodiment, suitable esters of (meth)acrylic acid with polyols are polyols , in which at least one OH group is esterified with (meth)acrylic acid and at least one OH group is etherified with an alcohol like methanol, ethanol, propanol or a polyol like ethyleneglycol, neopentylglycol, trimethylolpropane, glycerol, trimethylolethane ,pentaerythritol or dipentaerythritol,

(poly)saccharide, in particular sorbitol. Examples of suitable esters of (meth)acrylic acid with polyols are for example (meth)acrylates of alkoxylated polyols like ethyleneglycol, neopentylglycol, trimethylolpropane, glycerol, trimethylolethane, pentaerythritol, dipentaerythritol, or (poly)saccharide, in particular sorbitol bearing 1 to 100, preferably 1 to 50 ethoxy, propoxy, mixed ethoxy and propoxy, more preferably exclusively ethoxy groups per OH-group of the polyol .

More Preferably, suitable esters of (meth)acrylic acid with polyols are (meth)acrylates of, with respect to each OH group of the polyol, singly to hundred-fold, more preferably triply to 50-fold, in particular triply to vigintuply (20-fold) ethoxylated, propoxylated or mixedly ethoxylated and propoxylated, and more particularly exclusively ethoxylated, neopentylglycol,

trimethylolpropane, glycerol, trimethylolethane , pentaerythritol, dipentaerythritol, or

(poly)saccharide, in particular sorbitol.

Particularly preferred esters of (meth)acrylic acid with polyols are

- ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, oligoethylene glycol di(meth)acrylate, polyethylene glycol

di(meth)acrylate,

ethylene glycol mono(meth)acrylate, diethylene glycol mono(meth)acrylate, triethylene glycol mono(meth)acrylate, oligoethylene glycol mono(meth)acrylate, polyethylene glycol mono(meth)acrylate,

Ethylene glycol methyl ether (meth)acrylate, di(ethylene glycol) methyl ether

(meth)acrylate, tri(ethylene glycol) methyl ether (meth)acrylate, oligo(ethylene glycol) methyl ether (meth)acrylate, poly(ethylene glycol) methyl ether (meth)acrylate,

- glycerol tri(meth)acrylate, glycerol alkoxylate tri(meth)acrylate, preferentially glycerol ethoxylate tri(meth)acrylate

trimethylolpropane tri(meth)acrylate, trimethylolpropane alkoxylate tri(meth)acrylate, preferentially trimethylolpropane ethoxylate tri(meth)acrylate

pentaerythritol tetra(meth)acrylate, pentaerythritol alkoxylate tetra(meth)acrylate, preferentially pentaerythritol ethoxylate tetra(meth)acrylate

pentaerythritol tri(meth)acrylate, pentaerythritol alkoxylate tri(meth)acrylate, preferentially pentaerythritol ethoxylate tri(meth)acrylate

dipentaerythritol penta(meth)acrylate, dipentaerythritol alkoxylate penta(meth)acrylate, preferentially dipentaerythritol ethoxylate penta(meth)acrylate

- sorbitol hexa(meth)acrylate, sorbitol alkoxylate hexa(meth)acrylate, preferentially sorbitol ethoxylate hexa(meth)acrylate; sorbitol penta(meth)acrylate, sorbitol alkoxylate penta(meth)acrylate, preferentially sorbitol ethoxylate penta(meth)acrylate; sorbitol tetra(meth)acrylate, sorbitol alkoxylate tetra(meth)acrylate, preferentially sorbitol ethoxylate tetra(meth)acrylate; sorbitol tri(meth)acrylate, sorbitol alkoxylate

tri(meth)acrylate, preferentially sorbitol ethoxylate tri(meth)acrylate

In one embodiment, suitable esters of (meth)acrylic acid with polyols do not include

(meth)acrylic esters with polyalkyleneoxides like polyethyleneoxides.

In another embodiment, suitable esters of (meth)acrylic acid with polyols do not include esters of (meth)acrylic aid with polyvalent alcohols or phenols.

Suitable antiadhesive monomers b) are vinyl ethers of polyols or vinyl ethers of alkoxylated polyols. Suitable vinyl ethers of polyols are preferably ethers with that are hydrophilic and with which coatings can be prepared that show antiadhesive properties as described above.

In one embodiment, suitable vinyl ethers of polyols are polyols, in which each OH group is etherified vinyl alcohol.

In one embodiment, suitable vinyl ethers of polyols are polyols, in which at least one OH group is etherified with vinyl alcohol and at least one OH group is not etherified.

In one embodiment, suitable vinyl ethers of polyols are polyols , in which at least one OH group is etherified vinylalcohol and at least one OH group is etherified with a saturated alcohol like methanol, ethanol, propanol or a polyol like ethyleneglycol, neopentylglycol, trimethylolpropane, glycerol, trimethylolethane, pentaerythritol, dipentaerythritol, (poly)saccharide like sorbitol.

Examples of suitable vinyl ethers of polyols are for example vinyl ethers of alkoxylated polyols like ethyleneglycol, neopentylglycol, trimethylolpropane, glycerol, trimethylolethane, pentaerythritol or dipentaerythritol bearing 1 to 100, preferably 1 to 50 ethoxy, propoxy, mixed ethoxy and propoxy, more preferably exclusively ethoxy groups per OH-group of the polyol.

Preferred vinyl ethers of polyols are ethylene glycol divinylether, diethylene glycol divinylether, triethylene glycol divinylether, oligoethylene glycol divinylether, polyethylene glycol divinyl ether, methoxyethylene glycol monovinylether, methoxy diethylene glycol monovinylether, methoxy triethylene glycol monovinylether, methoxy oligoethylene glycol monovinylether, methoxy polyethylene glycol monovinyl ether.

Suitable antiadhesive monomers c) are for example hydrophilic macromonomers such as (meth)acryloyl-, (meth)acrylamide- and vinylether-modified hydrophilic polymers, preferentially (meth)acryloyl-modified polyvinyl alcohol, (meth)acryloyl-modified partially hydrolyzed polyvinyl acetate, (meth)acryloyl-modified poly(2-alkyl-2-oxazoline), (meth)acrylamide-modified poly(2- alkyl-2-oxazoline), in particular (meth)acryloyl and (meth)acrylamide-modified poly(2-methyl-2- oxazoline) and (meth)acryloyl- and (meth)acrylamide-modified poly(2-ethyl-2-oxazoline), (meth)acryloyl- and (meth)acrylamide-modified polyvinyl pyrrolidone), (meth)acryloyl- and (meth)acrylamide-modified hydrophilic polypeptoids, (meth)acryloyl- and (meth)acrylamide- modified polyphosphorylcholine, (meth)acryloyl- and (meth)acrylamide-modified polysulfobetain, (meth)acryloyl- and (meth)acrylamide-modified polycarbobetain, (meth)acryloyl- and

(meth)acrylamide-modified polyampholyte.

Suitable antiadhesive monomers d) are N-vinyl compounds such as N-vinyl pyrrolidone, N-vinyl- Caprolactam, N-vinylcaprolactone or N-vinyl-2-piperidone.

In one embodiment, monomers d) do not include N-vinyl pyrrolidone.

Suitable antiadhesive monomers e) are low molecular weight (meth)acrylamides with a molecu- lar weight below 200, preferably below 150.

Preferred low molecular weight (meth)acrylamides are those according to formula with or CH3, R2, 3 = independently from each other H, methyl, ethyl, 1 -propyl, 2-propyl, 1 -butyl, 2-butyl.

Preferred alkylated (meth)acrylamides are: (=(meth)acrylamide), R2=R3=methyl (=N,N-dimethyl (meth)acrylamide), R2=R3=ethyl (=N,N-diethyl (meth)acrylamide), R2=H, R3=2- propyl (=N-isopropyl(meth)acrylamide). Suitable (meth)acrylates or (meth)acrylamides bearing epoxy groups f) are for example glycidyl (meth)acrylate.

Suitable monomers having a betain structure g) are for example sulfobetaines or carbobetaines of (meth)acrylates or (meth)acrylamides, sulfonyl- or carboxy-modified vinylimidazolium betains, sulfonyl- or carboxy-modified vinylpyridinium betains, sulfobetain- or carbobetain-modified styrenyls, phosphobetain(meth)acrylates or Phosphobetain(meth)acrylamides.

Suitable sulfobetaines or carbobetaines of (meth)acrylates or (meth)acrylamides are for example Sulfobetain(meth)acrylates, Sulfobetain(meth)acrylamides, Carbobetain(meth)acrylates, Carbobetain(meth)acrylamides of general formula , wherein

Ri = H, Methyl;

R2, R3 = alkyl, aryl, aralkyl, preferentially R2 = R3 = Methyl;

X = O, NH;

L = alkyl, aryl, aralkyl. L may contain heteroatoms in particular one or several groups of (CH2)nO, (CH2)nNH, n is preferentially 2-3; preferably L is methylene, ethylene or propylene; in particular ethylene or propylene.

Z = alkyl, aryl, aralkyl. Z may contain heteroatoms in one or several groups of (CH2) n O, (CH2)nNH, n is preferentially 2-3; preferably Z is methylene, ethylene, propylene, bu- tylene

Y = sulfonate or carboxylate

Examples of suitable sulfobetaines or carbobetaines of (meth)acrylates or (meth)acrylamides a

Further suitable sulfobetaines or carbobetaines of (meth)acrylates or (meth)acrylamides are sulfobetain di(meth)acrylates, sulfobetain di(meth)acrylamides, carbobetain di(meth)acrylates and carbobetain di(meth)acrylamides. Preferred sulfobetaines or carbobetaines of

(meth)acrylates or (meth)acrylamides are of the general formula

, wherein

Ri, R 2 = H, Methyl

R3 = alkyl, aryl, aralkyl, preferably R3 = Methyl

X = O, NH

Li, l_2 = independently from each other alkyl, aryl, aralkyl. L may contain heteroatoms in particular one or several groups of (CH2) n O, (CH2) n NH, n is preferentially 2-3; preferably L = methylene, ethylene, propylene; in particular ethylene and propylene; L3 = alkyl, aryl, aralkyl. Ls may contain heteroatoms in particular one or several groups of (CH2)nO, (CH2)nNH, n is preferably 2-3; preferably L3 = methylene, ethylene, propylene, butylene;

Y = sulfonate or carboxylate.

Further examples of suitable sulfobetaines or carbobetaines of (meth)acrylates or

(meth)acrylamides are

Suitable sulfonyl- or carboxy-modified vinylimidazolium betains are for example sulfonyl- or carboxy-modified vinylimidazolium betains of general formula

, wherein

R a , R b and R c independently of one another are an H atom or an organic radical having up to 22 C atoms, preferably R a = R b = R c = H,

L = alkyl, aryl, aralkyl. L may contain heteroatoms in particular one or several groups of

(CH2)nO, (CH2)nNH, n is preferentially 2-3; preferably L = methylene, ethylene, propylene, butylene,

Y = sulfonate or carboxylate. Examples of sulfonyl- or carboxy-modified vinylimidazolium betains are:

Suitable sulfonyl- or carboxy-modified vinylpyridinium betains are for example those according to the general formula

Y

V // N~L'

, wherein

L = alkyl, aryl, aralkyl; L may contain heteroatoms in particular one or several groups of (CH 2 ) n O, (CH 2 ) n NH, n is preferably 2-3;

preferably L = methylene, ethylene, propylene, butylene;

Y = sulfonate or carboxylate. xamples of sulfonyl- or carboxy-modified vinylpyridinium betains include

Suitable Sulfobetain- or Carbobetain-modified styrenyls are for example those according to the general formula , wherein

i, R2 = alkyl, aryl, aralkyi, preferably Ri = R2 = Methyl,

Li, l_2 = independently from each other alkyl, aryl, aralkyi; L may contain heteroatoms in particular one or several groups of (CH2) n O, (CH2) n NH , n is preferentially 2-3; preferably L = methylene, ethylene, propylene, butylene; in particular ethylene and propylene,

Y = sulfonate or carboxylate. rbobetain-modified styrenyls include:

Suitable phosphobetain(meth)acrylates or phosphobetain(meth)acrylamides are those of the general formula

0 0 , wherein

Ri = H, Methyl,

R2, R3, R 4 = alkyl, aryl, aralkyi, preferentially R2 = R3 = R3 = Methyl,

X = O, NH,

Li, l_2 = independently from each other alkyl, aryl, aralkyi. Li, L2 may independently from each other contain heteroatoms in particular one or several groups of (CH2) n O, (CH2)nNH, n is preferably 2-3; preferably Li, L2 are independently from each other methylene, ethylene, propylene, butylene; in particular and independently from each other ethylene and propylene. Examples of phosphobetain(meth)acrylates or phosphobetain(meth)acrylamides include

Suitable Ion pair comonomers are in particular ion pairs of ammonium-modified (meth)acrylates or (meth)acrylamides and sulfo-, carboxy-, phosphonyl or phosphoryl -modified (meth)acrylates or (meth)acrylamides. A preferred example is the combination

Suitable hydrophilic monomers h) different from those mentioned above are hydroxyethyl- (meth)acrylate, Vinyl alcohol, (Meth)acryloyl and (meth)acrylamide-modified mono- and oligosaccharides.

Suitable Ion pair comonomers i) are in particular ion pairs of ammonium-modified

(meth)acrylates or (meth)acrylamides and sulfo-, carboxy-, phosphonyl or phosphoryl -modified (meth)acrylates or (meth)acrylamides. A preferred example is the combination

In one embodiment of the invention the coating comprises only one antiadhesive monomer. In one embodiment of the invention the coating comprises two or more antiadhesive monomers.

A biocidal monomer in the context of this application shall mean a monomer that imparts biocidal properties to the coating, be it by itself or in combination with other components. Biocidal properties or biocidal coating means that living biological organisms like plants, algae, bacteria, cyanobacteria, fungi, yeasts, molds, protozoa, viruses, mycoplasma, other microorganisms or higher organisms such as barnacles are deterred, controlled and/or inactivated by said coating. The degree of fouling and in particular biofouling of a membrane is thus reduced. The mechanisms of such biocidal effects are not entirely understood. It is assumed the biocidal effect of biocidal monomers or coatings can for example be due to the interfering with the production of the bacterial plasma wall, interfering with protein synthesis, nucleic acid synthesis, or plasma membrane integrity, or to inhibiting critical biosynthetic pathways in the bacteria.

Suitable biocidal monomers are for example selected from

j) vinyl-imidazolium compounds

k) ethylenically unsaturated monomers bearing quarternary ammonium or phosphonium groups

I) diallyldialkylammoniumchlorides

m) alkylaminoalkyl (meth)acrylates and alkylaminoalkyl (meth)acrylamides

n) Polylysine (meth)acrylamides or (meth)acrylates

o) alkyl-4-vinylpridinium and alkyl-2-vinyl-pyridinium salts, in particular bromides and iodides

p) ethylenically unsaturated monomers bearing guanide and biguanide groups

q) halamines

Further biocidal monomers and corresponding polymers can be found for example in Tatsuo Tashiro Macromol. Mater. Eng. 2001 , 286, 63-87.

Suitable vinyl-imidazolium compounds j) are in particular 3-vinyl-imidazol-1 -ium compounds . These are preferably selected from a 3-vinyl-imidazol-1 -ium compounds having the formula (III)

in which R a is an organic radical having 1 to 22 C atoms,

R b , R c and R d independently of one another are an H atom or an organic radical having up to 22 C atoms and An- is an anion.

R a is an organic radical having 1 to 22 C atoms. The organic radical may also comprise further heteroatoms, more particularly oxygen atoms, nitrogen, sulfur or phosphorus atoms, or function- nal groups, as for example hydroxyl groups, ether groups, ester groups, or carbonyl groups. More particularly R a is a hydrocarbon radical which apart from carbon and hydrogen may further comprise at most hydroxyl groups, ether groups, ester groups or carbonyl groups. R a with particular preference is a hydrocarbon radical having 1 to 22 C atoms, more particularly having 4 to 20 C atoms, which comprises no other heteroatoms, e.g., oxygen or nitrogen. The hydrocarbon radical may be aliphatic (in which case unsaturated aliphatic groups are also included, but less preferred) or aromatic, or may comprise both aromatic and aliphatic groups. Preferably R a is an aliphatic hydrocarbon radical.

Examples of hydrocarbon radicals include the phenyl group, benzyl group, a benzyl group or phenyl group substituted by one or more Ci to C 4 alkyl groups, or the mesityl group, alkyl groups and alkenyl groups, more particularly the alkyl group. With very particular preference R a is a C 4 to C22 alkyl group, preferably a C 4 to C18.

Examples for R a are methyl, ethyl, 1 -propyl, 2-propyl, 1 -butyl, 2-butyl, 2-methyl-1 -propyl (isobu- tyl), 2-methyl-2-propyl (tert-butyl), 1 -pentyl, 2-pentyl, 3-pentyl, 2-methyl-1 -butyl, 3-methyl-1 -butyl, 2-methyl-2-butyl, 3-methyl-2-butyl, 2,2-dimethyl-1 -propyl, 1 -hexyl, 2-hexyl, 3-hexyl, 2-methyl- 1 -pentyl, 3-methyl-1 -pentyl, 4-methyl-1 -pentyl, 2-methyl-2-pentyl, 3-methyl-2-pentyl, 4-methyl-2- pentyl, 2-methyl-3-pentyl, 3-methyl-3-pentyl, 2,2-dimethyl-1 -butyl, 2,3-dimethyl-1 -butyl, 3,3- dimethyl-1 -butyl, 2-ethyl-1 -butyl, 2,3-dimethyl-2-butyl, 3,3-dimethyl-2-butyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, icosyl, phenylmethyl (benzyl), diphenylmethyl, triphenylmethyl, 2-phenylethyl, 3-phenyl- propyl, cyclopentylmethyl, 2-cyclopentylethyl, 3-cyclopentylpropyl, cyclohexylmethyl, 2-cyclo- hexylethyl, and 3-cyclohexylpropyl.

With very particular preference R a is a 1 -butyl, 2-butyl, 2-methyl-1 -propyl (isobutyl), 2-methyl-2- propyl (tert-butyl), 1 -pentyl, 2-pentyl, 3-pentyl, 1 -hexyl, 2-hexyl, 3-hexyl, 2-methyl-1 -pentyl, 3-methyl-1 -pentyl, 4-methyl-1 -pentyl, 2-methyl-2-pentyl, 3-methyl-2-pentyl, 4-methyl-2-pentyl, 2-methyl-3-pentyl, 3-methyl-3-pentyl, 2,2-dimethyl-1 -butyl, 2,3-dimethyl-1 -butyl, 3,3-dimethyl-1 - butyl, 2-ethyl-1 -butyl, 2,3-dimethyl-2-butyl, 3,3-dimethyl-2-butyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, or icosyl group, with the butyl, pentyl, hexyl, octyl, decyl, dodecyl, tetradecyl, hexadecyl, and octa- decyl groups having particular importance.

In one preferred embodiment R b is an H atom.

In another preferred embodiment R b is an alkyl group, as for example a Ci to C18 alkyl group, preferably a Ci to C16, more preferably a Ci to Ci 4 , very preferably Ci to C12, and more particu- larly Ci to C10 alkyl group. For the radical R b , a Ci to C6 alkyl group represents one particular embodiment, and in a very particular embodiment the alkyl group is a Ci to C 4 alkyl group.

R c and R d are preferably independently of one another a hydrogen atom or an organic radical having 1 to 10 C atoms. The organic radical may also comprise further heteroatoms, more par- ticularly oxygen atoms, nitrogen, sulfur or phosphorus atoms, or functional groups, as for example hydroxyl groups, ether groups, ester groups, or carbonyl groups.

More particularly R c and R d are a hydrocarbon radical which apart from carbon and hydrogen may further comprise at most hydroxyl groups, ether groups, ester groups or carbonyl groups.

R c and R d with particular preference are independently of one another a hydrocarbon radical having 1 to 20 C atoms, more particularly having 1 to 10 C atoms, which comprises no other heteroatoms, e.g., oxygen or nitrogen. The hydrocarbon radical may be aliphatic (in which case unsaturated aliphatic groups are also included) or aromatic, or may comprise both aromatic and aliphatic groups.

Examples of hydrocarbon radicals include the phenyl group, benzyl group, a benzyl group or phenyl group substituted by one or more Ci to C 4 alkyl groups, or the mesityl group, alkyl groups and alkenyl groups, more particularly the alkyl group.

With very particular preference R c and R d are a hydrogen atom or a Ci to Cio alkyl group. A particularly preferred alkyl group is a Ci to C6 alkyl group, and in one particular embodiment the alkyl group is a Ci to C 4 alkyl group.

With very particular preference R c and R d are independently of one another a methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl or tert-butyl group, with the methyl, ethyl n-propyl, and n-butyl groups having particular importance. In one particular embodiment R c and R d are each H atoms.

In a very particular embodiment R b , R c , and R d are each H atoms.

Examples of imidazolium ions are

1 -butyl-3-vinyl-imidazol-1 -ium, 1 -pentyl-3-vinyl-imidazol-1 -ium, 1 -hexyl-3-vinyl-imidazol-1 -ium, 1 -octyl-3-vinyl-imidazol-1 -ium, 1 -decyl-3-vinyl-imidazol-1 -ium, 1 -dodecyl-3-vinyl-imidazol-1 -ium, 1 -tetradecyl-3-vinyl-imidazol-1 -ium, 1 -hexadecyl-3-vinyl-imidazol-1 -ium, 1 -octadecyl-3-vinyl- imidazol-1 -ium, 1 -hexyl-2-methyl-3-vinyl-imidazol-1 -ium, 1 -octyl-2-methyl -3-vinyl-imidazol-1 - ium, 1 -decyl-2-methyl -3-vinyl-imidazol-1 -ium, 1 -dodecyl-2-methyl -3-vinyl-imidazol-1 -ium, 1 - tetradecyl-2-methyl -3-vinyl-imidazol-1 -ium, 1 -hexadecyl-2-methyl -3-vinyl-imidazol-1 -ium, and 1 -octadecyl-2-methyl -3-vinyl-imidazol-1 -ium.

Preferred imidazolium ions are 1 -butyl-3-vinyl-imidazol-1 -ium, 1 -hexyl-3-vinyl-imidazol-1 -ium, 1 -octyl-3-vinyl-imidazol-1 -ium, 1 -decyl-3-vinyl-imidazol-1 -ium, 1 -dodecyl-3-vinyl-imidazol-1 -ium, 1 -tetradecyl-3-vinyl-imidazol-1 -ium, 1 -hexadecyl-3-vinyl-imidazol-1 -ium, and 1 -octadecyl-3-vinyl- imidazol-1 -ium.

The anion An- is any desired anion, preferably a halide or carboxylate anion, preferably a halide anion. Anions other than carboxylate anion are described, for example, in WO 2007/090755, particularly from page 20 line 36 to page 24 line 37 therein, which is hereby made part of the present disclosure content by reference. Suitable anions are more particularly those from the group of the halides and halogen-containing compounds of the following formulae:

F-, CI-, Br, I-, BF 4 -, PF 6 -, AlCk, AI2CI7-, A Cho " , AIBr 4 _ , FeCk, BCk, SbF 6 " , AsF 6 " , ZnC " , SnC " ,

CuCI 2 -, CF3SO3-, (CF 3 S0 3 ) 2 N-, CF3CO2-, CCI3CO2-, CN-, SCN-, OCN-, NO 2" , NO 3" , N(CN)- , 1%; the group of the sulfates, sulfites, and sulfonates, of the following general formulae:

S0 4 2 -, HS0 4 -, SO3 2 -, HSO3-, R e OS0 3 -, R e S0 3 -; the group of the phosphates, of the following general formulae:

P0 4 3 -, ΗΡ0 4 2 -, Η 2 Ρ0 4 -, R e P0 4 2 " , HR e P0 4 " , R e R f P0 4 -; the group of the phosphonates and phosphinates, of the following general formula:

R e HP0 3 -,R e R f P0 2 -, R e R f P0 3 -; the group of the phosphites, of the following general formulae:

P0 3 3 -, HP0 3 2 -, H2PO3-, R e POs 2 -, R e HP0 3 -, R e R f P0 3 -; the group of the phosphonites and phosphinites, of the following general formula:

R e R f P0 2 " , R e HP0 2 -, R e R f PO-, R e HPO " ; the group of the borates, of the following general formulae:

BO3 3 -, HBO3 2 -, H2BO3-, R e R f B0 3 -, R e HB0 3 -, R e B0 3 2" , B(OR e )(OR f )(OR 9 )(OR h )-, B(HS0 4 )-, B(R e S04)- ; the group of the boronates, of the following general formulae:

R e B0 2 2 -, R e R f BO-; the group of the carbonates and carbonic esters, of the following general formulae:

the group of the silicates and silicic acid esters, of the following general formulae:

Si0 4 4 -, HSi0 4 3 -, H 2 Si0 4 2 -, H 3 Si0 4 -, R e Si0 4 3 -, R e R f Si0 4 2 -, R e R f R9Si0 4 -, HR e Si0 4 2 -, H 2 R e Si0 4 -,

HR e R f Si0 4 -; the group of the alkyl silane and aryl silane salts, of the following general formulae:

R e Si0 3 3 -, R e R f Si0 2 2 -, R e R f R 9 SiO " , R e R f R 9 Si0 3 -, R e R f R 9 Si0 2 -, R e R f Si0 3 2 -; the group of the carboximides, bis(sulfonyl)imides, and sulfonylimides, of the following general formulae:

R- R-

O

O O the group of the methides, of the following general formula:

S0 2 -R e

R9-02S S0 2 -R f

the group of the alkoxides and aryl oxides, of the following general formulae:

R e O-; the group of the halometallates, of the following general formula:

[M r Hal t ] s -,

where M is a metal and Hal is fluorine, chlorine, bromine or iodine, r and t are positive integers, and indicate the stoichiometry of the complex, and s is a positive integer and indicates the charge of the complex; the group of the sulfides, hydrogen sulfides, polysulfides, hydrogenpolysulfides, and thiolates, of the following general formulae:

S 2 -, HS-, [Sv] 2 -, [HSv]-, [R e S]-,

where v is a positive integer from 2 to 10; and the group of the complex metal ions such as Fe(CN)6 3" , Fe(CN)6 4" , MnCv, Fe(CO)4 ~

In the above anions, R e , R f , Rs, and R h independently of one another are in each case hydrogen;

C1-C30 alkyl and its aryl-, heteroaryl-, cycloalkyl-, halogen-, hydroxyl-, amino-, carboxyl-, formyl-, -0-, -CO-, -CO-O- or -CO-N< substituted components, such as, for example, methyl, ethyl, 1 -propyl, 2-propyl, 1 -butyl, 2-butyl, 2-methyl-1 -propyl (isobutyl), 2-methyl-2-propyl (tert-butyl), 1 -pentyl, 2-pentyl, 3-pentyl, 2-methyl-1 -butyl, 3-methyl-1 -butyl, 2-methyl-2-butyl, 3-methyl-2-bu- tyl, 2, 2-dimethyl-1 -propyl, 1 -hexyl, 2-hexyl, 3-hexyl, 2-methyl-1 -pentyl, 3-methyl-1 -pentyl, 4-me- thyl-1 -pentyl, 2-methyl-2-pentyl, 3-methyl-2-pentyl, 4-methyl-2-pentyl, 2-methyl-3-pentyl, 3-me- thyl-3-pentyl, 2,2-dimethyl-1 -butyl, 2,3-dimethyl-1 -butyl, 3,3-dimethyl-1 -butyl, 2-ethyl-1 -butyl, 2,3-dimethyl-2-butyl, 3,3-dimethyl-2-butyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, icosyl, henicosyl, docosyl, tricosyl, tetracosyl, pentacosyl, hexacosyl, heptacosyl, octacosyl, nonacosyl, triacontyl, phenyl- methyl (benzyl), diphenylmethyl, triphenylmethyl, 2-phenylethyl, 3-phenylpropyl, cyclopentyl- methyl, 2-cyclopentylethyl, 3-cyclopentylpropyl, cyclohexylmethyl, 2-cyclohexylethyl, 3-cyclo- hexylpropyl, methoxy, ethoxy, formyl, acetyl or C q F2( q - a )+(i-b)H2a+b with q < 30, 0 < a < q and b = 0 or 1 (for example, CF 3 , C 2 F 5 , CH 2 CH2-C( q -2)F2( q -2) + i, C 6 Fi 3 , C 8 Fi 7 , C10F21 , C12F25);

C3-C12 cycloalkyl and its aryl-, heteroaryl-, cycloalkyl-, halogen-, hydroxyl-, amino-, carboxyl-, formyl-, -0-, -CO- or -CO-O-substituted components, such as, for example, cyclopentyl, 2-me- thyl-1 -cyclopentyl, 3-methyl-1 -cyclopentyl, cyclohexyl, 2-methyl-1 -cyclohexyl, 3-methyl-1 -cyclo- hexyl, 4-methyl-1 -cyclohexyl or C q F2( q -a)-(i-b)H2a-b with q < 30, 0 < a < q and b = 0 or 1 ;

C2-C30 alkenyl and its aryl-, heteroaryl-, cycloalkyl-, halogen-, hydroxyl-, amino-, carboxyl-, formyl-, -0-, -CO- or -CO-O-substituted components, such as, for example, 2-propenyl, 3-bu- tenyl, cis-2-butenyl, trans-2-butenyl or C q F2( q - a )-(i-b)H2a-b with q < 30, 0 < a < q and b = 0 or 1 ;

C3-C12 cycloalkenyl and its aryl-, heteroaryl-, cycloalkyl-, halogen-, hydroxyl-, amino-, carboxyl-, formyl-, -0-, -CO- or -CO-O-substituted components, such as, for example 3-cyclopentenyl, 2- cyclohexenyl, 3-cyclohexenyl, 2,5-cyclohexadienyl or C q F2( q - a )-3(i-b)H2a-3b with q < 30, 0 < a < q and b = 0 or 1 ;

aryl or heteroaryl having 2 to 30 carbon atoms, and their alkyl-, aryl-, heteroaryl-, cycloalkyl-, halogen-, hydroxy-, amino-, carboxy-, formyl-, -0-, -CO- oder -CO-O-substituted components, such as, for example, phenyl, 2-methylphenyl (2-tolyl), 3-methylphenyl (3-tolyl), 4-methylphenyl, 2-ethylphenyl, 3-ethylphenyl, 4-ethylphenyl, 2,3-dimethylphenyl, 2,4-dimethylphenyl, 2,5-dime- thylphenyl, 2,6-dimethylphenyl, 3,4-dimethylphenyl, 3,5-dimethylphenyl, 4-phenylphenyl, 1 -na- phthyl, 2-naphthyl, 1 -pyrrolyl, 2-pyrrolyl, 3-pyrrolyl, 2-pyridinyl, 3-pyridinyl, 4-pyridinyl or CeF( 5 -

two radicals denote an unsaturated, saturated or aromatic ring which is unsubstituted or substituted by functional groups, aryl, alkyl, aryloxy, alkyloxy, halogen, heteroatoms and/or hetero- cycles, and which is uninterrupted or interrupted by one or more oxygen and/or sulfur atoms and/or by one or more substituted or unsubstituted imino groups.

In the above anions, R e , R f , Rs, and R h are preferably each independently of one another a hydrogen atom or a Ci to C12 alkyl group or a CF3. Examples of anions include chloride; bromide; iodide; thiocyanate; isothiocyanate; azide, hex- afluorophosphate; trifluoromethanesulfonate; methanesulfonate; the carboxylates, especially formate; acetate; mandelate; carbonates, preferably methyl carbonate and n-butyl carbonate, nitrate; nitrite; trifluoroacetate; sulfate; hydrogensulfate; methylsulfate; ethylsulfate; 1 -propyl- sulfate; 1 -butylsulfate; 1 -hexylsulfate; 1 -octylsulfate; phosphate; dihydrogenphosphate; hydro- gen-phosphate; C1-C4 dialkylphosphates; propionate; tetrachloroaluminate; AI2CI7-; chlorozin- cate; chloroferrate; bis(trifluoromethylsulfonyl)imide; bis(pentafluoroethylsulfonyl)imide;

bis(methylsulfonyl)imide; bis(p-tolylsulfonyl)imide; tris(trifluoromethylsulfonyl)methide; bis(penta- fluoroethylsulfonyl)methide; p-tolylsulfonate; tetracarbonylcobaltate; dimethylene glycol mono- methyl ether sulfate; oleate; stearate; acrylate; methacrylate; maleate; hydrogencitrate; vinyl- phosphonate; bis(pentafluoroethyl)phosphinate; borates such as bis[salicylato(2-)]borate, bis[oxalato(2-)]borate, bis[1 ,2-benzenediolato(2-)-0,0']borate, tetracyanoborate, tetrafluorobo- rate; dicyanamide; tris(pentafluoroethyl)trifluorophosphate; tris(heptafluoropropyl)trifluoro- phosphate, cyclic arylphosphates such as pyrrocatechol-phosphate (C6H402)P(0)0-, and chlorocobaltate.

Particularly preferred anions are those from the group of the halides, especially chloride, bromide, iodide, azide, thiocyanate, acetate, methyl carbonate, tetrafluoroborate, trifluorome- thanesulfonate, methanesulfonate, bis(trifluoromethylsulfonyl)imide, ethylsulfate and diethyl phosphate.

Examples of suitable vinyl-imidazolium compounds include:

Suitable flux enhancing monomers bearing quarternary ammonium or phosphonium groups k) are for example selected from compounds of the general formula

An-, wherein

R1 = H, methyl, preferably methyl,

X = O, NH preferably O, Z = alkylene or polyoxyalkylene, preferably ethylene or polyoxyalkylene (polyalkylenglycol, preferably poly(ethylene glycol), poly(propylene glycol); poly(2-alkyl-2-oxazoline), preferably poly(2-methyl-2-oxazoline), poly(2-ethyl-2-oxazoline)):;

L = N, P; preferably N

R 2 , R 3 , R 4 = alkyl; preferably R 2 = R 3 = methyl; R 4 = preferably C 6 - C 22 , more preferably C 8

- Ci8, especially preferably C& - C12, particularly preferably C12;

An-: counterion, preferably bromide or iodide.

Examples of biocidal monomers bearing quarternary ammonium groups are for example

(MAA-TMEA),

Further suitable flux enhancing monomers bearing quarternary ammonium groups are 3- methacryloyl aminopropyl-trimethyl ammoniumchloride, 2-methacryloyl oxyethyltrimethyl am- monium chloride, 2-Methacryloyloxyethyl-trimethylammoniummethosulfate, 3-acrylamidopropyl trimethylammoniumchloride, trimethylvinylbenzyl-ammoniumchlorid, 2-acryloyloxyethyl-4- benzoylbenzyl-dimethyl ammoniumbromide, 2-acryloyloxyethyl- trimethylammoniummethosulfate, Ν,Ν,Ν- Trimethylammonium-ethylenebromide, 2- hydroxy N,N,N-trimethyl-3-[(2-methyl-1 -oxo-2-propenyl)oxy]-ammoniumpropane chloride, Ν,Ν,Ν - Trimethyl-2- [(1 -oxo- 2-propenyl)oxy]-ammoniumethane-methylsulfate, N,N- Diethyl-N-methyl-2- [(1 -oxo-2-propenyl)oxy ]-ammoniumethane-methylsulfate,

N,N,N-trimethyl-2- [(1 -oxo-2-propenyl)oxy]-ammonium ethanechloride, N,N,N-trimethyl-2-[(2- methyl-1 -oxo-2-propenyl)oxy]-ammonium ethanechloride, Ν,Ν,Ν- trimethyl-2-[(2-methyl-1 -oxo-2- propenyl)oxy]-ammoniumethan-methylsulfate, Ν,Ν,Ν- triethyl- 2- [( 1 -oxo- 2- propenyl) amino]-ammoniumethan.

Further suitable biocidal monomers bearing quarternary ammonium or phosphonium groups are for example selected from compounds of the general formula

An-, wherein

X = N, P; preferably N,

Li = alkylene or polyoxyalkylene, preferably ethylene or polyoxyalkylene (polyalkylenglycol, preferably poly(ethylene glycol), poly(propylene glycol); poly(2-alkyl-2-oxazoline), preferably poly(2-methyl-2-oxazoline), poly(2-ethyl-2-oxazoline)),

Ri, R2, 3 = independantly alkyl, aryl or aralkyl;

If X = N: preferably Ri = R2 = methyl; R3 = preferably C6 - C22, more preferably Cs - Cis, especially preferably Cs - C12, particularly preferably C12;

If X = P: preferably Ri = R2 = R3 = octyl, butyl or phenyl;

An-: counterion, preferably halide, most preferably chloride, bromide or iodide.

Examples of further suitable biocidal monomers bearing quarternary ammonium or phosphoni- u

Suitable diallyldialkylammoniumchlorides I) are for example diallyldimethylammoniumchloride (DADMAC).

Suitable alkylaminoalkyi (meth)acrylate and alkylaminoalkyi (meth)acrylamide m) are for example those according to formula (I)

(I) wherein R 7 is H or CH 3 ,

R 8 is CrC 5 alkyl bi-radical,

R 9 and Rio are independently H or CrC 5 alkyl radical which can be linear or branched, and X is a divalent radical of -O-, -NH- or -NR-n, wherein R-n is CrC 6 alkyl.

Preferred flux enhancing monomers according to formula (I) are 2-tert-butylaminoethyl (meth)acrylate (tBAEMA), 2-dimethylaminoethyl (meth)acrylate, 2-diethylaminoethyl

(meth)acrylate, 3-dimethylaminopropyl (meth)acrylate, N-3-dimethylaminopropyl

(meth)acrylamide, and N-3-diethylaminopropyl (meth)acrylamide with the most preferred being 2-tert-butylaminoethyl (meth)acrylate (tBAEMA).

Suitable Polylysine (meth)acrylamides or (meth)acrylates n) are for example epsilon-poly-L- lysine methacrylamide:

Suitable N-alkyl-4-vinylpridinium and alkyl-2-vinyl-pyridinium salts are for example the bromides and iodides of methyl in particular bromides and iodides N-methyl-4-vinylpridinium and N- methyl-2-vinyl-pyridinium.

Suitable biocidal monomers bearing guanide and biguanide groups are for example

(Meth)acryloyl- modified Poly(hexamethylene biguanide)

wherein Ri = H, methyl; Y = H, methyl.

Examples of suitable biocidal monomers bearing guanide and biguanide groups include: and

, wherein

Ri = H, methyl

R2 = alkyl, aryl, aralkyl, preferentially R2 = 2-ethyl-hexyl, hexyl, octyl, decyl, dodecyl, tetradecyl, hexadecyl, octadecyl

Suitable halamines q) are for example chloramine

CI

Flux enhancing monomers can be used in combination with other flux enhancing monomers. In one embodiment of the invention, membranes comprise a coating comprising only antiadhesive monomers as flux enhancing monomers.

In one embodiment of the invention, membranes comprise a coating comprising only biocidal monomers as flux enhancing monomers.

In one embodiment of the invention, membranes comprise a coating comprising antiadhesive and biocidal monomers as flux enhancing monomers.

In one embodiment of the invention, membranes comprise a coating comprising only one antiadhesive monomer and no biocidal monomer as flux enhancing monomer. In one embodiment of the invention, membranes comprise a coating comprising only one biocidal monomer and no antiadhesive monomer as flux enhancing monomer.

In one embodiment of the invention, membranes comprise a coating comprising at least one antiadhesive and at least one biocidal monomer as flux enhancing monomers.

Flux enhancing monomers can also be used in combination with further monomers having no flux enhancing effect. Suitable further monomers are monomers comprising an ethylenically unsaturated double bond that by themselves do not qualify as flux enhancing monomers a) to q) as defined above.

Examples of further monomers include acrylic acid, methacrylic acid, alkyl (meth)acrylate and alkyl (meth)acrylamide, in particular methyl (meth)acrylate, ethyl (meth)acrylate, butyl

(meth)acrylate, lauryl (meth)acrylate, ethylhexyl (meth)acrylate, 4-hydroxy butyl (meth)acrylate, phenoxyethyl (meth)acrylate, styrene, alkyl vinyl ether, in particular, methyl vinyl ether, ethyl vinyl ether, n-butyl vinyl ether, 4-hydroxybutyl vinyl ether, vinyl acetate, acrylic nitrile, maleic anhydride.

When reference is made in this application to embodiments of membranes comprising certain flux enhancing monomers or combinations of flux enhancing monomers, this shall be understood to include membranes or filtration systems that have been obtained using a composition comprising the respective flux enhancing monomers or combinations of flux enhancing monomers.

In one embodiment of the invention, membranes according to the invention comprise a coating comprising at least one antiadhesive and/or biocidal monomer, with the proviso that said at least one antiadhesive and/or biocidal monomer is different from antiadhesive monomers a) as defined above.

In one embodiment of the invention, membranes according to the invention comprise a coating comprising at least one antiadhesive and/or biocidal monomer, with the proviso that said at least one antiadhesive and/or biocidal monomer is not an acrylic ester.

In one embodiment of the invention, membranes according to the invention comprise at least one antiadhesive monomer a) as defined above.

In one embodiment of the invention, membranes according to the invention comprise at least one antiadhesive monomer b)-i) as defined above.

In one embodiment of the invention, membranes according to the invention comprise a coating comprising at least one antiadhesive monomer a) as defined above in combination with at least one antiadhesive and/or biocidal monomer selected from monomers b) to q) as defined above. In one embodiment of the invention, membranes according to the invention comprise at least one antiadhesive monomer b)-i) as defined above in combination with at least one antiadhesive and/or biocidal monomer selected from monomers c) to q) as defined above.

In one embodiment of the invention, membranes according to the invention comprise at least one antiadhesive monomer a) as defined above in combination with at least one antiadhesive and/or biocidal monomer selected from monomers b) to q) as defined above.

In one embodiment of the invention, membranes according to the invention comprise at least one antiadhesive monomer b) to i) as defined above.

In one embodiment of the invention, membranes according to the invention comprise a coating comprising at least one antiadhesive and/or biocidal monomer, with the proviso that said at least one antiadhesive and/or biocidal monomer is different from hydroxyethyl-methacrylate, ethyleneglycol-methacrylate, ethyleneglycol-dimethacrylate or compounds of formulae

MA-DMP, o MA-EDMAPS.

In one embodiment of the invention, membranes according to the invention comprise a coating comprising at least one antiadhesive and/or biocidal monomer selected from hydroxyethyl- methacrylate, ethyleneglycol-methacrylate, ethyleneglycol-dimethacrylate or compounds of for- mulae

MA-EDMAPS, in combination with at least one antiadhesive and/or biocidal monomer selected from monomers a) to q) as defined above that are different from the above monomers. In one embodiment, coatings comprise 5 to 95 % by weight of flux enhancing monomers and 95 to 5 % by weight of further monomers relative to the overall mass of the coating.

In one embodiment, membranes according to the invention comprise tBAEMA in combination with at least one flux enhancing monomer comprising at least one quaternary ammonium group. In another embodiment, membranes according to the invention comprise tBAEMA in combination with at least one halamine.

In another embodiment, membranes according to the invention comprise at least one flux enhancing monomer comprising at least one quaternary ammonium group in combination with at least one halamine.

In one embodiment, membranes according to the invention comprise tBAEMA in combination with at least one flux enhancing monomer comprising at least one quaternary ammonium group and with at least one halamine. In one embodiment, membranes according to the invention comprise HEMA (2-Hydroxyethyl methacrylate) and QAEMA ([2-(methacryloyloxy)ethyl] trimethylammonium chloride).

In another embodiment membranes according to the invention comprise HEMA (2-Hydroxyethyl methacrylate), QAEMA ([2-(methacryloyloxy)ethyl] trimethylammonium chloride) and acrylic acid.

In a preferred embodiment, membranes according to the invention comprise vinyl pyrrolidone in combination with at least one biocidal monomer j), k), I), m), n), o), p) or q). The flux enhancing monomer can be applied on the base membrane neat or in solution with a solvent. Depending on the nature of the flux enhancing monomers and the further monomers used, different solvents can be used. Examples of suitable solvents are water, THF, dioxane, alcohols. A preferred solvent is water. In a preferred embodiment of the present invention, flux enhancing monomers and the further monomers are applied in solution at a concentration in the range of from 0.01 to 70 % by weight, more preferably in the range of from 0.5 to 60 % by weight, based on the overall content of flux enhancing and further monomers.

In one embodiment, the composition comprising the at least one flux enhancing monomer optionally comprises further additives like dispersants. Further additives that can be comprised generally are known in the art.

The coating normally has a thickness of 1 nm to 100 μηη, preferably 2 nm to 1 μηη, more preferably 5 nm to 0.1 μηη. Another aspect of the invention is a membrane, obtained by a process comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

Some types of membranes by themselves comprise anchor groups on the surface of the membrane. Examples of such membranes include polyamide membranes like RO membranes with a separation layer based on polyamide.

Anchor groups in this context means a functional group that is capable of reacting with epoxy groups of GMA, thus binding the polymer to the surface of the base membrane. Suitable anchor groups include for example carboxylic groups, sulfonic acid groups, phosphonic acid, phosphoric acid and thiols.

These types of membranes comprising by themselves anchor groups can bind to the polymer comprising GMA in a reaction between said acidic groups on the surface of the membrane and epoxy groups of GMA comprised in the coating.

Some types of membranes do not by themselves comprise anchor groups on the surface of the membrane. Examples of such membranes include membranes based on polysulfones, polyeth- ersulfones, cellulose acetate or PVDF.

In one embodiment of the invention, particularly if the base membrane does not by itself comprise anchor groups on the surface of the membrane, the surface of said membrane can be subjected to additional process steps to obtain anchor groups on the surface of the base membrane.

In one embodiment of the invention the surface of the base membrane is subjected to an oxidative process like flame treatment, corona discharge, plasma treatment, in particular oxygen- containing plasma, actinic irradiation such as ultraviolet, x-ray or gamma irradiation and electron beam treatment, treatment with oxidative immersion baths such as baths containing chromium sulfuric acid, sulfuric acid, hydrogen peroxide ammonium hydroxide, persulfuric acid, peroxo disulfuric acid, phosphoric acid, hypophosphorous acid, phosphorous acid, pyrophosphoric acid, triphosphoric acid, perphosphoric acid, permonophosphoric acid and mixtures thereof .

Corona discharges can be electrical discharges characterized by a corona and occurring when one of two electrodes in a gas has a shape causing the electric field at its surface to be signifi- cantly greater than that between the electrodes. Air is usually used as gas. The substrate is usually located at ambient pressure in the discharge field between the two electrodes, for example by passing a film as substrate between two electrodes. Plasma can be a gas where electrons and ions are present. Plasma can be generated by the treatment of gases with high temperatures or high electric fields. Plasma treatment is usually carried out in vacuum chambers at 10 to 100 Pa with a nonthermal plasma in a gas atmosphere consisting of an inert gas or reactive gas, for example oxygen.

Flame can be flames that are formed when a flammable gas and an oxygen containing gas, for example atmospheric air, are combined and combusted. Examples of flammable gases are propane, butane or town gas. Flame treatment is usually carried out at ambient pressure. Ozone can be generated from atmospheric oxygen in a corona discharge or by ultraviolet radiation.

Electron beam can be generated by electron beam accelerators, for example by cathode ray tubes.

X-rays can be generated by X-ray generators, for example by X-ray-tubes.

Preferably, the oxidation of the surface is performed by treatment with corona discharge, plasma or flame. More preferably, it is performed by corona discharge treatment or plasma treat- ment.

After the optional oxidation step of the surface, said surface is treated with a composition comprising

i) glycidylmethacrylate, and

ii) at least one flux enhancing monomer.

Said at least one flux enhancing monomer has been defined above.

In another embodiment, the surface of a base membrane is after the optional oxidation step treated with a composition comprising GMA but not comprising flux enhancing monomers. Said composition id brought to reaction with the surface. This can for example be done by heating, for example to 40, 60 80, or 100 °C. The surface of the base membrane is then treated with a second composition comprising at least one flux enhancing monomer and optionally GMA..

Said composition is then cured.

In one embodiment, said composition does not comprise a radical initiator.

In one embodiment, said composition comprises one or more radical initiators. The one or more radical initiators can be thermal initiators such as 2,2-azobisisobutyronitrile or photoinitiators. Preferably, the one or more radical initiators are photoinitiators as they are for example disclosed in WO 08/132037A2 on p. 13, In 5 to p.19, In 13. Preferred radical initiators are azo and peroxo-type initiators, in particular azo initiators.

In another embodiment of the invention, said composition is cured in a radiation induced radical polymerization, for example using UV light.

In another embodiment of the invention, said composition is cured thermally.

The coating normally has a thickness of 1 nm to 100 μηη, preferably 2 nm to 1 μηη, more preferably 5 nm to 0.1 μηη.

In one preferred embodiment of the invention, membranes according to the invention comprise a coating, wherein said coating is bound to the surface of base membrane through reaction of the epoxy group of glycidylmethacrylate with functional groups present on the surface of said base membrane.

Another aspect of the invention is a process for making a membrane, comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

Another aspect of the invention is a process for making a membrane, which comprises the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising glycidylmethacrylate, with the proviso that the composition does not comprise flux enhancing monomers C) treatment with a composition comprising

i) optionally glycidylmethacrylate

ii) at least one flux enhancing monomer

D) curing said composition to form a coating.

After step B), it is preferred to induce reaction of GMA with the surface of the membrane, for example by heating, for example to 40, 60, 80 or 100°C. Another aspect of the invention is a method of improving the flux through membranes, which comprises the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

Another aspect of the invention is the use of a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer for the preparation of membranes.

For compositions according to the invention the same embodiments and preferred embodiments with respect to the choice of flux enhancing monomers apply as for membranes according to the invention.

Another aspect of the invention is the use of a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer for improving the flux through membranes and/or for imparting biocidal and/or antiadhesive properties to a membrane.

Optionally, such compositions may further comprise at least one solvent.

Optionally, such compositions may comprise further additives such as dispersants.

Another aspect of the invention is a filtration system comprising at least one membrane, where- in at least one component or at least one part of a component of the filtration system has been obtained by a process comprising the following steps:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

iii) glycidylmethacrylate

iv) at least one flux enhancing monomer

C) curing said composition to form a coating.

In different embodiments of the invention, the component or part of the component in filtration systems according to the invention that is subjected to the above process steps is selected from a membrane, the separating layer of a membrane, a support layer of a membrane, a fabric layer of a membrane, the feed spacer of a membrane, the permeate spacer of a membrane, the casing of the filtration system, the piping of the filtration system, the joints of the filtration system, manifolds of the filtration system.

Normally the components suitable for the above process comprise an organic polymer as the main component.

In another aspect of the invention pertains to a process for making filtration systems, preferably comprising a membrane, comprising:

A) optionally oxidizing the surface of a base membrane,

B) treatment with a composition comprising

i) glycidylmethacrylate

ii) at least one flux enhancing monomer

C) curing said composition to form a coating.

It is an advantage of this process that it is not limited to certain parts or components of a filtration system. Rather, it can be applied to any component or part of a component of such filtration systems, if it comprises an organic polymer. Examples of suitable components or part s of components include a membrane, the separating layer of a membrane, a support layer of a membrane, a fabric layer of a membrane, the feed spacer of a membrane, the permeate spacer of a membrane, the casing of the filtration system, the piping of the filtration system, the joints of the filtration system, manifolds of the filtration system.

Membranes according to invention show improved properties with respect to the decrease of flux through a membrane over time and their fouling and particularly biofouling properties.

Membranes according to the invention are easy and economical to make.

Filtration systems and membranes according to invention can be made using aqueous or alco- holic systems and are thus environmentally friendly. Furthermore, leaching of toxic substances is not problematic with membranes according to the invention.

Membranes according to the invention have a long lifetime and allow for the treatment of water. Membranes according to the invention can be cleaned more easily and with lower amounts of cleaning agents.

Membranes according to the invention have longer cleaning cycles meaning that they need to be cleaned less often than membranes known from the art.

In a preferred embodiment, membranes according to the invention are used for the treatment of sea water or brackish water.

In one preferred embodiment of the invention, membranes according to the invention, particularly RO, FO or NF membranes are used for the desalination of sea water or brackish water. Membranes according to the invention, particularly RO, FO or NF membranes are used for the desalination of water with a particularly high salt content of for example 3 to 8 % by weight For example membranes according to the invention are suitable for the desalination of water from mining and oil/gas production and fracking processes, to obtain a higher yield in these applica- tions.

Different types of membrane according to the invention can also be used together in hybrid systems combining for example RO and FO membranes, RO and UF membranes, RO and NF membranes, RO and NF and UF membranes, NF and UF membranes.

In another preferred embodiment, membranes according to the invention, particularly NF, UF or MF membranes are used in a water treatment step prior to the desalination of sea water or brackish water. In another preferred embodiment membranes according to the invention, particularly NF, UF or MF membranes are used for the treatment of industrial or municipal waste water.

Membranes according to the invention, particularly RO and/or FO membranes can be used in food processing, for example for concentrating, desalting or dewatering food liquids (such as fruit juices), for the production of whey protein powders and for the concentration of milk, the UF permeate from making of whey powder, which contains lactose, can be concentrated by RO, wine processing, providing water for car washing, making maple syrup, during electrochemical production of hydrogen to prevent formation of minerals on electrode surface, for supplying water to reef aquaria

Membranes according to the invention, particularly UF membranes can be used in medical applications like in dialysis and other blood treatments, food processing, concentration for making cheese, processing of proteins, desalting and solvent-exchange of proteins,

fractionation of proteins, clarification of fruit juice, recovery of vaccines and antibiotics from fermentation broth, laboratory grade water purification, drinking water disinfection (including removal of viruses), removal of endocrines and pesticides combined with suspended activated carbon pretreatment. Membranes according to the invention, particularly RO, FO, NF membranes can be used for rehabilitation of mines, homogeneous catalyst recovery, desalting reaction processes.

Membranes according to the invention, particularly NF membranes, can be used for separating divalent ions or heavy and/or radioactive metal ions, for example in mining applications, homogeneous catalyst recovery, desalting reaction processes.