Description

A METALLIC NANOPARTICLE DISPERSION Field of the Invention

[001] The present invention relates to metallic nanoparticle dispersions, for example

nanosilver dispersions, and to conductive inks and pastes prepared therefrom. The invention also relates to a method of preparing the metallic nanoparticle dispersion and to conductive layers or patterns formed from the metallic nanoparticle dispersion at moderate curing conditions.

Background of the Invention

[002] The interest in metallic printing or coating fluids comprising metallic nanoparticles has increased during the last decades due to their unique properties when compared to the bulk properties of a given metal. For example, the melting point of metallic nanoparticles decreases with decreasing particle size making them of interest for printed electronics, electrochemical, optical, magnetic and biological applications.

[003] The production of stable and concentrated metallic printing or coating fluids, which can be printed, for example by inkjet printing, or coated at high speed is of great interest as it enables the preparation of electronic devices at low costs.

[004] Metallic printing or coating fluids are typically metallic nanoparticle dispersions

comprising metallic nanoparticles and a dispersion medium. Such metallic nanoparticle dispersions can be directly used as a printing or coating fluid. However, additional ingredients are often added to the metallic nanoparticle dispersion to optimize the properties of the resulting metallic printing or coating fluids.

[005] The preparation of metallic nanoparticles may be carried out in water or organic solvents by the so-called polyol synthesis as disclosed in for example ^' Approaches to the synthesis and Characterization of Spherical and Anisotropic Silver

Nanomaterials ^' , Metallic Nanomaterials Vol. 1., Edited by Challa S. S.R.Kumar, Wiley-VCH Verlag GmbH&Co.KGaA, Weinheim, by a derivative of the po!yol synthesis methodology or by an in-situ reduction of metallic salts in the presence of various reducing agents. Such methods are disclosed in for example

US2010143591 , US2009142482, US20060264518, EP-A 2147733, EP-A 2139007, EP-A 803551 , EP-A 2012952, EP-A 2030706, EP-A 1683592, EP-A 166617, EP-A 2119747, EP-A 2087490, EP-A 2010314, WO2008/151066, WO2006/076603, WO2009/152388, WO2009/157393.

[006] A polymeric dispersant is often used in the preparation of the metallic nanoparticles to obtain stable metallic printing or coating fluids. The polyol synthesis to prepare silver nanoparticles referred to above is typically carried out in the presence of polyvinylpyrrolidone (PVP). Non-stable metallic nanoparticle dispersions may lead to irreversible phase separation causing among others clogging of coating or print heads. Agglomeration of the metallic nanoparticles may also result in a decrease of the conductivity.

[007] Polymeric dispersants are typically homo- or copolymers prepared from acrylic acid, methacrylic acid, vinyl pyrrolidinone, vinyl butyral, vinyl acetate or vinyl alcohol monomers.

[008] Typically, after applying the metallic printing or coating fluids on a substrate, a

sintering step, also referred to as curing step, at elevated temperatures is carried out to induce/enhance the conductivity of the applied patterns of layers. The organic components of the metallic printing or coating fluids, for example the polymeric dispersants, may reduce the sintering efficiency and thus the conductivity of the applied patterns of layers. For this reason, higher sintering temperatures and longer sintering times are often required to decompose the organic components.

[009] Typical polymeric dispersants, such as those described above, are characterized by a full decomposition temperature of at least 350°C. Therefore, the layers or patterns coated or printed with metallic printing or coating fluids comprising such polymeric dispersants typically require a sintering step at elevated temperatures to be sure that most of the polymeric dispersants are decomposed.

[010] Such high sintering temperatures are not compatible with common polymer foils, such as polyethylene terephthalate (PET) or polycarbonate, which have relatively low glass transition temperatures. This restricts the choice to more expensive polymers such as polyimide.

[01 1] There is thus an interest in lowering the sintering temperatures needed to obtain conductive layers or patterns.

[012] EP-A 2468827 discloses polymeric dispersants having 95 wt% decomposition at a temperature below 300°C, as measured by Thermal Gravimetric Analysis. By using metallic printing or coating fluids comprising such polymeric dispersants, the sintering temperature and time could be reduced. In EP-A2608218 and

EP-A 2608217 a so called sintering additive is used in combination with a polymeric dispersant of EP-A 2468827 to further lower the sintering temperature. [013] EP-A 2671927 discloses a metallic nanoparticle dispersion comprising a specific dispersion medium, for example 2-pyrrolidone, resulting in a more stable dispersion without using a polymeric dispersant.

[014] EP-A 2781562 discloses a method of preparing metallic nanoparticle dispersions in the presence of a specific dispersion medium, for example 2-pyrrolidone, and a carboxylic acid.

[015] A problem associated with conductive inks is often their poor adhesion.

[016] EP1860163 discloses an electrically conductive ink comprising an electrically

conductive material and a vinyl chloride/vinylacetate/hydroxyalkyl(meth)acrylate copolymer resin. The ink has good adhesion to various base materials such as paper and various plastic films.

[017] WO2004/069941 discloses a conductive ink composition for deposition onto a

substrate comprising a mixture of (a) a reactive organic medium, (b) metal flake of powder, and (c) an adhesion promoting additive. The adhesion promoting additive may be a polymer selected from polyvinylidene chloride, polyvinylchloride, polyethylene vinyl chloride, polyester, copolymers thereof, or a primary diamine.

[018] WO2015/023370 discloses a composition comprising stabilized submicron silver particles, a thermoplastic resin and optionally an organic diluent. The thermoplastic resin may be vinyl copolymer comprising among others vinylidene chloride, vinyl chloride, acrylonitrile or alkyl acrylate.

[019] As nanosilver ink is typically used in combination with different substrates, there is still a need to further improve the adhesion of nanosilver inks towards various substrates.

[020] It has also been observed that during screen printing the nanosilver ink may cause, after some time, a change in surface roughness by swelling of the screen stencil on the screen printing seeve used. This may result in a poor printing quality.

[021] It has also been observed that during screen printing the nanosilver ink may cause sticking of the screen emulsion or screen capillary film on the screen printing seeve used to the substrate being printed on. This may also result in a poor printing quality due to difficult seperation of substrate and screen stencil.

Summary of the invention

[022] It is an object of the present invention to provide a stable metallic nanoparticle

dispersion wherewith highly conductive coatings or patterns can be obtained having an improved adhesion towards various substrates. This object is realized by the metallic nanoparticle dispersion as defined in claim 1.

[023] Further advantages and embodiments of the present invention will become apparent from the following description and the dependent claims.

Detailed description of the invention

Definitions

[024] The terms polymeric support and foil, as used herein, mean a self-supporting

polymer-based sheet, which may be associated with one or more adhesion layers, e.g. subbing layers. Supports and foils are usually manufactured through extrusion.

[025] The term layer as used herein, is considered not to be self-supporting and is

manufactured by coating or spraying it on a (polymeric) support or foil.

[026] PET is an abbreviation for polyethylene terephthalate.

[027] The term alkyl means all variants possible for each number of carbon atoms in the alkyl group i.e. methyl, ethyl, for three carbon atoms: n-propyl and isopropyl; for four carbon atoms: n-butyl, isobutyl and tertiary-butyl; for five carbon atoms: n-pentyl, 1 ,1-dimethyl-propyl, 2,2-dimethylpropyl and 2-methyl-butyl etc.

[028] Unless otherwise specified a substituted or unsubstituted alkyl group is preferably a Ci to C6-alkyl group.

[029] Unless otherwise specified a substituted or unsubstituted alkenyl group is preferably a C2 to C6-alkenyl group.

[030] Unless otherwise specified a substituted or unsubstituted alkynyl group is preferably a C2 to C6-alkynyl group.

[031] Unless otherwise specified a substituted or unsubstituted aralkyl group is preferably a phenyl group or a naphthyl group including one, two, three or more Ci to Ce-alkyl groups.

[032] Unless otherwise specified a substituted or unsubstituted alkaryl group is preferably a Ci to C6-alkyl group including an aryl group, preferably a phenyl group or naphthyl group.

[033] Unless otherwise specified a substituted or unsubstituted aryl group is preferably a substituted or unsubstituted phenyl group or naphthyl group.

[034] A cyclic group includes at least one ring structure and may be a monocyclic- or polycyclic group, meaning one or more rings fused together.

[035] A heterocyclic group is a cyclic group that has atoms of at least two different

elements as members of its ring(s).The counterparts of heterocyclic groups are homocyclic groups, the ring structures of which are made of carbon only. Unless otherwise specified a substituted or unsubstituted heterocyclic group is preferably a five- or six-membered ring substituted by one, two, three or four heteroatoms, preferably selected from oxygen atoms, nitrogen atoms, sulphur atoms, selenium atoms or combinations thereof.

[036] An alicyclic group is a non-aromatic homocyclic group wherein the ring atoms

consist of carbon atoms.

[037] The term heteroaryl group means a monocyclic- or polycyclic aromatic ring

comprising carbon atoms and one or more heteroatoms in the ring structure, preferably, 1 to 4 heteroatoms, independently selected from nitrogen, oxygen, selenium and sulphur. Preferred examples of heteroaryl groups include, but are not limited to, pyridinyl, pyridazinyl, pyrimidyl, pyrazyl, triazinyl, pyrrolyl, pyrazolyl, imidazolyl, (1 ,2,3,)- and (1 ,2,4)-triazolyl, pyrazinyl, pyrimidinyl, tetrazolyl, furyl, thienyl, isoxazolyl, thiazolyl, isoxazolyl, and oxazolyl. A heteroaryl group can be unsubstituted or substituted with one, two or more suitable substituents. Preferably, a heteroaryl group is a monocyclic ring, wherein the ring comprises 1 to 5 carbon atoms and 1 to 4 heteroatoms.

[038] The term substituted, in e.g. substituted alkyl group means that the alkyl group may be substituted by other atoms than the atoms normally present in such a group, i.e. carbon and hydrogen. For example, a substituted alkyl group may include a halogen atom or a thiol group. An unsubstituted alkyl group contains only carbon and hydrogen atoms.

[039] Unless otherwise specified a substituted alkyl group, a substituted alkenyl group, a substituted alkynyl group, a substituted aralkyl group, a substituted alkaryl group, a substituted aryl, a substituted heteroaryl and a substituted heterocyclic group are preferably substituted by one or more substituents selected from the group consisting of methyl, ethyl, n-propyl, isopropyl, n-butyl, 1-isobutyl, 2-isobutyl and tertiary-butyl, ester, amide, ether, thioether, ketone, aldehyde, sulfoxide, sulfone, sulfonate ester, sulphonamide, -CI, -Br, -I, -OH, -SH, -CN and -NO2.

The metallic nanoparticle dispersion

[040] The metallic nanoparticle dispersion according to the present invention comprises metallic nanoparticles, a binder and a liquid carrier, characterized in that the binder is a copolymer of vinyl chloride and a hydroxyfunctional monomer.

[041] The metallic nanoparticle dispersion may further comprise a surfactant and other additives to further optimize its properties. Binder

[042] The metallic nanoparticle dispersion comprises metallic nanoparticles, a binder and a liquid carrier, characterized in that the binder is a copolymer of vinyl chloride and a hydroxyfunctional monomer.

[043] The hydroxyl functional monomer is preferably selected from the group consisting of 2-hydroxypropyl acrylate, 1-hydroxy-2-propyl acrylate, 3-methyl-3-buten-1-ol, 2-methyl-2-propenoic acid 2-hydroxypropyl ester, 2-hydroxy-3-chloropropyl methacrylate, N-methylolmethacrylamide, 2-hydroxyethyl methacrylate,

poly(ethylene oxide) monomethacrylate, glycerine monomethacrylate, 1 ,2-propylene glycol methacrylate, 2,3-hydroxypropyl methacrylate, 2-hydroxyethyl acrylate, vinyl alcohol, N-methylolacrylamid, 2-propenoic acid 5-hydroxypentyl ester, 2-methyl-2- propenoic acid, 3-chloro-2-hydroxypropyl ester, 1-hydroxy-2-propenoic acid,

1- methylethyl ester, 2-hydroxyethyl allyl ether, 4-hydroxybutyl acrylate,

1.4- butanediol monovinyl ether, poly(e -caprolactone) hydroxyethyl methacrylate ester, poly(ethylene oxide) monomethacrylate, 2-methyl-2-propenoic acid,

2.5- dihydroxypentyl ester, 2-methyl-2-propenoic acid, 5,6-dihydroxyhexyl ester,

1.6- hexanediol monomethacrylate, 1 ,4-dideoxy-pentitol, 5-(2-methyl-2-propenoate),

2- propenoic acid, 2,4-dihydroxybutyl ester, 2-propenoic acid, 3,4-dihydroxybutyl ester, 2-methyi-2-propenoic acid, 2-hydroxy butyl ester, 3-hydroxypropyl

methacrylate, 2-propenoic acid, 2,4-dihydroxybutyl ester, isopropenyl alcohol.

[044] The hydroxyl functional monomer is most preferably vinyl alcohol, 2-hydroxypropyl acrylate, 1-hydroxy-2-propyl acrylate, 4-hydroxybutyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxyethyl acrylate.

[045] Examples of copolymers of vinyl chloride and a hydroxyfunctional monomer are chloroethylene-vinyl acetate-vinyl alcohol copolymer, vinyl alcohol-vinyl chloride copolymer, 2-hydroxypropyl acrylate-vinyl chloride polymer, propanediol

monoacrylate-vinyl chloride copolymer, vinyl acetate-vinyl chloride-2-hydroxypropyl acrylate copolymer, hydroxyethyl acrylate-vinyl chloride copolymer, 2-hydroxyethyl methacrylate-vinyl chloride copolymer.

[046] The a particular preferred copolymer is a copolymer of vinyl chloride, vinyl acetate and a hydroxyfunctional monomer.

[047] The amount of vinyl chloride is preferably more than or equal to 90 wt% relative to the total weight of the copolymer.

[048] The Molecular Weight (MW) of the copolymer of vinyl chloride and a

hydroxyfunctional monomer, measured with Gel Permeation Chromatographt (GPC) usin polystyrene standards and THF as eluent, is preferably more than or equal to 15 000, more preferalby more than or equal to 20 000.

[049] The K value of the copolymer of vinyl chloride and a hydroxyfunctional monomer, measured according to IS01628-2 (1998) is preferably more than or equal to 40, more preferably more than or equal to 45.

[050] Suitable copolymers are for example Solbin® A, which is a copolymer of 92 wt% vinylchloride - 3 wt% vinylacetate - 5 wt% vinylalchohol, Solbin® AL, which is a copolymer of 93 wt% vinylchloride - 2 wt% vinylacetate - 5 wt% vinylalchohol, Solbin® TA2, which is a copolymer of 83 wt% vinylchloride - 4 wt% vinylacetate - 13 wt% hydroxyalkyl acrylate, Solbin® TA3 which is a copolymer of 83 wt% vinylchloride - 4 wt% vinylacetate -13 wt% hydroxyalkylacrylate, Solbin® TAO, which is a copolymer of 91 wt% vinylchloride - 2 wt% vinylacetate - 7 wt% vinyl alcohol, all commercially available from Shin Etsu; Vinnol® E15/40 A, Vinnol® E 15/45 A, Vinnol® E 15/48 A, Vinnol® E 22/48 A, and Vinnol® H 5/50 A, all commercially available from Wacker Chemie; Sunvac® GH, which is a copolymer of 90 wt% vinylchloride - 4 wt% vinylacetate - 6 wt% vinyl alcohol, Sunvac® GF, which is a copolymer of 81 wt% vinylchloride - 4 wt% vinylacetate - 15 wt% hydroxylalkyl acrylate and Sunvac® OH, which is a copolymer of 81 wt% vinylchloride - 4 wt% vinylacetate - 15 wt% hydroxylalkyl acrylate, all commercially available from Yantai Suny Chem International; S-Lec E4-HA commercailly available from Sekisui; and VROH, LPOH and UMOH commercially available from Wuxi Honghui Chemical.

[051] The amount of binder in the metallic nanoparticle dispersion is preferably between 0.1 and 15 wt %, more preferably between 0.2 and 7.5 wt%, most preferably between 0.25 and 5 wt%, particularly preferred between 0.5 and 3.0 wt%, relative to the total weight of the dispersion. When the amount of binder is too high, for example above 15 wt% relative to the total weight of the dispersion, the conductivity of the metallic nanoparticle dispersion tends to decrease. When the amount of binder is too low, for example less than 0.1 wt% relative to the total weight of the dispersion, no improvement in adhesion may be observed.

Metallic nanoparticles

[052] The metallic nanoparticle dispersion of the present invention comprises metallic nanoparticles.

[053] The metallic nanoparticles comprise one or more metals in elemental or alloy form.

The metal is preferably selected from the group consisting of silver, gold, copper, nickel, cobalt, molybdenum, palladium, platinum, tin, zinc, titanium, chromium, tantalum, tungsten, iron, rhodium, iridium, ruthenium, osmium, aluminium and lead. Metallic nanoparticles based on silver, copper, molybdenum, aluminium, gold, copper, or a combination thereof, are particularly preferred. Most preferred are metallic nanoparticles based on silver.

[054] The term "nanoparticles" refers to dispersed particles having an average particle size or average particle diameter of less than 100 nm, preferably less than 50 nm, more preferably less than 30 nm, most preferably less than 20 nm. The average particle diameter referred to is determined with Transmission Electron Microscopy (TEM). A metallic nanoparticle dispersion, such as for example a silver ink, may comprise primary particles, and secondary particles. The latter may be aggregated primary particles. The particle diameter referred to above is the particle diameter of the primary particles.

[055] The metallic nanoparticle dispersion preferably comprises at least 5 wt %, more preferably at least 10 wt %, most preferably at least 15 wt %, particularly preferred at least 20 wt % of metallic nanoparticles, relative to the total weight of the dispersion.

Liquid Carrier

[056] The metallic nanoparticle dispersion comprises a liquid carrier.

[057] The liquid carrier is preferably an organic solvent. The organic solvent may be selected from alcohols, aromatic hydrocarbons, ketones, esters, aliphatic hydrocarbons, dimethylsulfoxide (DMSO), higher fatty acids, carbitols, cellosolves, and higher fatty acid esters.

[058] Suitable alcohols include methanol, ethanol, propanol, 1-butanol, 1-pentanol,

2-butanol, t-butanol.

[059] Suitable aromatic hydrocarbons include toluene and xylene.

[060] Suitable ketones include methyl ethyl ketone, methyl isobutyl ketone,

2,4-pentanedione and hexa-fluoroacetone.

[061] Also glycol, glycolethers, Ν,Ν-dimethyl- acetamide, Ν,Ν-dimethylformamide may be used.

[062] A mixture of organic solvents may be used to optimize the properties of the metallic nanoparticle dispersion.

[063] Preferred organic solvents are high boiling solvents. High boiling organic solvents referred to herein are solvents which have a boiling point that is higher than the boiling point of water (> 100°C).

[064] Preferred high boiling solvents are shown in the following table.

[065] Particularly preferred high boiling solvents used in conductive inkjet inks are

2-phenoxy-ethanol, propyleencarbonate, n-butanol, gamma-butyro-lactone, and mixtures thereof.

[066] Particularly preferred high boiling solvents used in conductive screen printing inks are dimethylsulfoxide, 2-Butoxyethanol, dipropylene glycol methyl ether acetate, and mixtures thereof.

[067] Particularly preferred high boiling solvents used in conductive flexo and gravure printing inks are methyl isobutyl ketone, 2-Butoxy-ethanol, propylene glycol mono methyl ether acetate, and mixtures thereof.

[068] The liquid carrier may also comprise solvents which are used in the preparation method of the nanoparticles, such as those used in the methods disclosed in EP-A 2671927 and EP-A 2781562, for example 2-pyrrolidone.

[069] It has been observed that silverinks wherein the liquid carrier comprises methyl-5- (dimethylamino)-2-methyl-5-oxopentanoate (commercially available as Rhodasolv Polarclean from Rhodia) or methylbutyrolactone have improved sticking behavior and improved varnish stability.

[070] The amount of the liquid carrier depends on the desired viscosity of the printing or coating fluid. The amount of the liquid carrier is preferably less than 95 wt%, more preferably less than 90 wt%, most preferably less than 85 wt% relative to the total weight of the metallic nanoparticle dispersion.

Surfactants

[071] The metallic nanoparticle dispersion preferably comprises a surfactant. Various surfactants may be used. However, it has been observed that the addition to the metallic nanoparticle dispersion of a surfactant selected from the group consisting of Disperbyk 2151 , Disperbyk 2025, and Diserbyk 2155 results in a further

improvement of the adhesion of the dispersion, especially on ITO (Indium Tin Oxide) substrates. Particularly good results are obtained with Disperbyk-2151.

[072] The amount of the surfactants is preferably between 0.01 and 10 wt%, more

preferably between 0.05 and 5 wt%, most preferably between 0.1 and 1.0 wt %, relative to the total amount of the metallic nanoparticle dispersion. Adhesion promoting compound

[073] It has been observed that the addition of adhesion promotoring compounds may further improve the adhesion towards various substrates.

[074] For example the commercially available adhesion promoting compound Byk-4511 may improve the adhesion, especially towards ITO (Indium Thin Oxide) substrates.

[075] Particularly preferred adhesion promoting compounds are acidic polyesters. It has been observed that metallic nanoparticle dispersions comprising an acidic polyester are characterized by a substantial improved adhesion on ITO (Indium Thin Oxide) substrates.

[076] The amount of the acidic polyester is preferably between 0.01 and 10 wt%, more preferably between 0.05 and 5 wt%, most preferably between 0.1 and 1.0 wt %, relative to the total amount of the metallic nanoparticle dispersion.

[077] The acidic polyester is typically a copolymer with acidic groups having an acid value from 15 up to 100 mg KOH/g. Examples of commercially available acidic polyesters include BYK-4510 (commercially available from Byk Altana), PLUSOLIT H-PD (commercially available from Mader) or BORCHI GEN HMP-F (commercially available from OMG Borchers).

[078] The acidic polyester is typically a polycondensate of a polyol and a polycarboxylic acid. The polyol and polycarboxylic acid are combined in desired proportions and chemically reacted using standard esterification (condensation) procedures to provide a polyester having both hydroxyl and carboxylic acid groups in the polyester resin. A triol is typically used to provide a branched polyester.

[079] Examples of suitable polycarboxylic acids or anhydrides include, but are not limited to, maleic anhydride, maleic acid, fumaric acid, itaconic acid, phthalic acid, phthalic anhydride, isophthalic acid, trimellitic anhydride, terephthalic acid, naphthalene dicarboxylic acid, adipic acid, azelaic acid, succinic acid, sebacic acid and various mixtures thereof.

[080] Examples of suitable diols, triols and polyols include, but are not limited to,

ethylene glycol, propylene glycol, 1 ,3-propanediol, glycerol, diethylene glycol, dipropylene glycol, triethylene glycol, trimethylolpropane, trimethylolethane, tri propylene glycol, neopentyl glycol, pentaerythritol, 1 ,4- butanediol, trimethylol propane, hexylene glycol, cyclohexane dimethanol, and polyethylene or polypropylene glycol. [081] A preferred polyol is trimethylolpropane, a preferred polycarboxylic acid is adipic acid.

[082] Other preferred acidic polyesters are the reaction product of

(a) a polyester having a Molecular Weight (Mn) of 2000 to 10 000, a hydroxyl number of 20 to 75, and an acid value of 15 to 25, the polyester being a condensate of:

(i) a polyol component comprising a mixture of diols and triols,

(ii) a polyacid component comprising an alpha, beta-ethylenically unsaturated polycarboxylic acid, and

(b) a phosphorus acid.

[083] Further examples of phosphatised polyesters are disclosed in WO2012/162301.

Dispersion-stabilizing compound (DSC)

[084] The metallic nanoparticle dispersion according to the present invention may

comprise a dispersion-stabilizing compound (DSC) according to Formulae VII, VIII, IX or X,

Formula VII Formula VIII Formula IX Formula X wherein

Q represents the necessary atoms to form a substituted or unsubstituted five or six membered heteroaromatic ring;

M is selected from the group consisting of a proton, a monovalent cationic group, an alkyl group, a heteroalkylgroup and an acyl group;

R9 and R 0 are independently selected from the group consisting of a hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted alkynyl group, a substitued or unsubstituted alkaryl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted aryl or heteroaryl group, a hydroxyl group, a thioether, an ether, an ester, an amide, an amine, a halogen, a ketone and an aldehyde;

R9 and R10 may represent the necessary atoms to form a five to seven membered ring; R11 to R13 are independently selected from the group consisting of a hydrogen, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted alkynyl group, a substituted or unsubstituted alkaryl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted aryl or heteroaryl group, a hydroxyl group, a thiol, a thioether, a sulfone, a sulfoxide, an ether, an ester, an amide, an amine, a halogen, a ketone, an aldehyde, a nitrile and a nitro group;

R12 and R13 may represent the necessary atoms to form a five to seven membered ring.

[085] The dispersion-stabilizing compound is preferably a compound according to

Formula VII.

[086] The dispersion-stabilizing compound is more preferably a compound according to Formula VII, wherein Q represents the necessary atoms to form a five membered heteroaromatic ring.

[087] A particular preferred dispersion-stabilizing compound is a compound according Formula VII, wherein Q is a five membered heteroaromatic ring selected from the group consisting of an imidazole, a benzimidazole, a thiazole, a benzothiazole, an oxazole, a benzoxazole, a 1 ,2,3-triazole, a 1 ,2,4-triazole, an oxadiazole, a thiadiazole and a tetrazole.

[088] Some examples of dispersion-stabilizing compounds are shown in the following table.

[089] The dispersion-stabilizing compound is preferably selected from the group

consisting of N,N-dibutyl-(2,5-dihydro-5-thioxo-1 H-tetrazol-1-yl-acetamide, 5-heptyl- 2-mercapto-1 ,3,4-oxadiazole, 1-phenyl-5-mercaptotetrazol, 5-methyl-1 ,2,4-triazolo- (1 ,5-a) primidine-7-ol, and S-[5-[(ethoxycarbonyl)amino]-1 ,3,4-thiadiazol-2-yl] O- ethyl thiocarbonate.

[090] The dispersion-stabilizing compounds according to Formula VII to X are preferably non-polymeric compounds. Non-polymeric compounds as used herein means compounds having a Molecular Weight which is less preferably than 1000, more preferably less than 500, most preferably less than 350. [091] The amount of the dispersion-stabilizing compounds (DSC) expressed as wt % relative to the total weight of silver (Ag) in the metallic nanoparticles is preferably between 0.005 and 10.0, more preferably between 0.0075 and 5.0, most preferably between 0.01 and 2.5. When the amount of the dispersion-stabilizing compound relative to the total weight of silver in the metallic nanoparticles is too low, the stabilizing effect may be too low, while a too high amount of the dispersion- stabilizing compound may adversely affect the conductivity of the coating or patterns obtained with the metallic nanoparticle dispersion.

Additives

[092] To optimize the coating or printing properties, and also depending on the application for which it is used, additives such as reducing agents, wetting/levelling agents, dewettting agents, rheology modifiers, adhesion agents, tackifiers, humectants, jetting agents, curing agents, biocides or antioxidants may be added to the metallic nanoparticle dispersion described above.

[093] It may be advantageous to add to the metallic nanoparticle dispersion a small

amount of an inorganic acid or a compound capable of generating such an acid during curing of a metallic layer or pattern formed from the metallic nanoparticle dispersion such as disclosed in EP-A 2821164. Higher conductivities and/or lower curing temperatures were observed of layers or patterns formed from such metallic nanoparticle dispersions.

[094] Higher conductivities and/or lower curing temperatures may also be obtained when using metallic nanoparticles dispersions containing a compound according to Formula XI, as disclosed in WO2015/000937.

Formula XI wherein

X represents the necessary atoms to form a a substituted or unsubstituted ring.

[095] A particularly preferred compound according to Formula XI is an ascorbic or

erythorbic acid derivative compound. [096] A thickening agent may be added to increase the viscosity of the printing or coating fluid. Preferred thickening agents may be selected from amorphous silica, polyvinylpyrrolidones having different Molecular Weights, and cellulose based thickening agents. A particular preferred thickening agent is hydroxypropylcellulose.

Preparation of the metallic nanoparticle dispersion

[097] The preparation of the metallic nanoparticle dispersion according to the present invention typically comprises the addition of the liquid carrier, the copolymer of vinyl chloride and a hydroxyfunctional monomer and optional additives to the metallic nanoparticles by using a homogenization technique such as stirring, high shear mixing, ultra-sonication, or a combination thereof.

[098] The metallic nanoparticles from which the metallic nanoparticle dispersion is made is typically a paste or a highly concentrated dispersion of metallic nanoparticles. A preferred preparation method of the metallic nanoparticles is described below.

[099] The homogenization step can be carried out at elevated temperature up to 100°C. In a preferred embodiment, the homogenization step is carried out at temperature equal or below 60°C.

[0100] In a preferred embodiment, the metallic nanoparticle dispersion is used in an inkjet printing method. Such a metallic nanoparticle dispersion, also referred to as metallic inkjet fluid or ink or conductive inkjet fluid or ink, preferably has a viscosity lower than 35 mPa.s, preferably lower than 28 mPa.s, and most preferably between 2 and 25 mPa.s at 25°C and measured at a shear rate of 90 s ^_1 .

[0101] When using so-called throughflow printheads, the viscosity of the metallic inkjet fluid may be higher, preferably below 60 mPa.s at 25°C and at a shear rate of 90 s ¹ . A higher viscosity limit for the metallic inkjet fluid opens up more compositional variations of the fluid which may be advantageous towards more concentrated and/or more stable metallic inkjet fluids

[0102] In another preferred embodiment, the metallic nanoparticle dispersion is used in a flexographic printing process. Such a metallic nanoparticle dispersion, also referred to as metallic flexo ink or conductive flexo ink, preferably has a viscosity between 10 and 200 mPa.s, more preferably between 25 and 150 mPa.s, most preferably between 50 and 100 mPa.s measured at 25°C and at a shear rate of 90 S ^"1 .

[0103] In another preferred embodiment, the metallic nanoparticle dispersion is used in a screen printing process. Such a metallic nanoparticle dispersion, also referred to as metallic screen ink or conductive screen ink, preferably has a viscosity between 3000 and 1000000 mPa.s, most preferably between 5000 and 750000 mPa.s, most preferably between 10000 and 500000, measured at 25°C and at a shear rate of 1 s- ¹ .

Metallic layers or patterns

[0104] Thin layers or patterns printed or coated from the metallic nanoparticle dispersion can be rendered conductive at lower sintering temperatures compared to those obtained with conventional metallic printing or coating fluids. Therefore, conductive thin layers or patterns made from the metallic printing or coating fluids of the present invention can be coated or printed on flexible supports that can not withstand thermal treatment at high temperature, such as for example PET.

[0105] The metallic layers or patterns are prepared by a method comprising the steps of applying a metallic nanoparticle dispersion as defined above on a support followed by a sintering step.

[0106] The support may a glass, a paper or a polymeric support.

[0107] Preferred polymeric supports are polycarbonate, polyethylene terephthalate (PET) or polyvinylchloride (PVC) based supports. A preferred PET support is for example an AUTOSTAT™ heat stabilized polyester from MacDermid.

[0108] The above mentioned supports may be provided with one or more layers to improve the adhesion, absorption or spreading of the applied conductive inkjet, screen or flexo inks.

[0109] Polymeric supports are preferably provided with so-called subbing layers to improve the adhesion of the applied conductive inkjet, screen or flexo inks. Such subbing layers are typically based on vinylidene copolymers, polyesters, or (meth)acrylates.

[0110] Useful subbing layers for this purpose are well known in the art and include, for example, polymers of vinylidene chloride such as vinylidene chloride/acrylonitrile/ acrylic acid terpolymers or vinylidene chloride/methyl acrylate/itaconic acid terpolymers.

[01 11] Other preferred subbing layers include a binder based on a polyester-urethane

copolymer. In a more preferred embodiment, the polyester-urethane copolymer is an ionomer type polyester urethane, preferably using polyester segments based on terephthalic acid and ethylene glycol and hexamethylene diisocyanate. A suitable polyester-urethane copolymer is Hydran™ APX101 H from DIC Europe GmbH.

[0112] The application of subbing layers is well-known in the art of manufacturing polyester supports for silver halide photographic films. For example, the preparation of such subbing layers is disclosed in US 3649336 and GB 1441591. [0113] An acid generating compound may be incorporated in a primer layer on a support as disclosed in WO2015/000932. A preferred primer comprises a copolymer of vinylidene chloride, an acrylic ester and itaconic acid.

[0114] In a preferred embodiment, the subbing layer has a dry thickness of no more than 0.2 μιτι or preferably no more than 200 mg/m ² .

[0115] Another preferred support is a support based on transparent conductive oxides.

Such a support is typically a glass or polymer support whereupon a layer or pattern of a transparent conductive oxide (TCO) is provided. Examples of such conductive oxides are ITO (Indium Tin Oxide), ZnO, Sn02 or doped oxides such as ZnO:AI.

A particularly preferred TCO is ITO.

[0116] A preferred paper based support is the Powercoat® paper substrate, a substrate designed for printed electronics by Arjowiggins Creative Papers.

[0117] Multiple metallic layers or patterns, i.e. a stack of patterned or unpatterned layers, may be applied on a substrate. The support referred to in the method of preparing the metallic layers or patterns thus also encompass a previously applied metallic layer or pattern.

[0118] Metallic layers may be provided onto a support by co-extrusion or any conventional coating technique, such as dip coating, knife coating, extrusion coating, spin coating, spray coating, blade coating, slot die coating, slide hopper coating and curtain coating.

[0119] Metallic layers and in particular metallic patterns may be provided onto a support by a printing method such as intaglio printing, screen printing, flexographic printing, offset printing, inkjet printing, gravure offset printing, etc.

[0120] Preferred printing methods are an inkjet, screen printing and flexographic printing method.

[0121] Another method to provide a metallic layer or pattern on a support is aerosol jet printing. Aerosol Jet Printing, which has been developed by Optomec, preserves most of the advantages of inkjet printing, while reducing many of its limitations. The technique is developed for use in the field of printed electronics. The technique is disclosed in for example US2003/0048314, US2003/0020768, US2003/0228124 and WO2009/049072. An Aerosol Jet Print Engine is commercially available from Optomec, for example the Aerosol Jet Printer OPTOMEC AJ 300 CE.

[0122] Virtually any liquid having a viscosity less than 5000 mPa.s can be deposited using the Aerosol Jet Printing technique. Using higher viscous fluids may be

advantageous with respect to the stability of the metallic inks Curing Step

[0123] After the layers or patterns are applied on the support, a sintering step, also referred to as curing step, is carried out. During this sintering step, solvents evaporate and the metallic particles sinter together. Once a continuous percolating network is formed between the metallic particles, the layers or patterns become conductive. Conventional sintering is typically carried out by applying heat. The sintering temperature and time are dependent on the support used and on the composition of the metallic layer or pattern. The sintering step for curing the metallic layers may be performed at a temperature below 250°C, preferably below 200°C, more preferably below i80°C, most preferably below 160°C.

[0124] The sintering time may be less than 60 minutes, preferably between 2 and 30

minutes and more preferably between 3 and 20 minutes, depending on the selected temperature, support and composition of the metallic layers.

[0125] However, instead of or in addition to the conventional sintering by applying heat, alternative sintering methods such as exposure to an Argon laser, to microwave radiation, to IR radiation, to UV radiation or to low pressure Argon plasma, photonic curing, plasma or plasma enhanced, electron beam, laser beam or pulse electric current sintering may be used. When using pulse electric current sintering, the electric current may be directly applied to the conductive ink or indirectly via induction.

[0126] Another curing method uses the so-called Near InfraRed (NIR) curing technology.

The metal of the coating or the pattern, for example silver, may act as absorber for the NIR radiation.

[0127] Still another curing method uses heated steam instead of hot air temperature curing which also efficiently heats up and sinters the metal of the coating or the pattern.

[0128] The metallic layers of the present invention allow to use lower curing temperatures than the prior art processes. In consequence it is possible to use polymeric substrates that can not withstand thermal treatment at high temperature, such as for example PET. The curing time may also be substantially reduced leading to the possibility of having higher production per hour than the prior art processes. The conductivity of the metallic layers are maintained or even improved in certain cases.

[0129] To further increase the conductivity or to lower the curing temperature it may be advantageous to contact the metallic layer or pattern with a solution containing an acid or an acid precursor capable or releasing the acid during curing of the metallic layer or pattern, as disclosed in WO2015/000932. [0130] The metallic layers or patterns may be used in various electronic devices or parts of such electronic devices as for example organic photo-voltaics (OPV's), inorganic photo-voltaics (c-Si, a-Si, CdTe, CIGS), OLED displays, OLED lighting, inorganic lighting, RFID's, organic transistors, thin film batteries, touch-screens, e-paper, LCD's, plasma, sensors, membrane switches or electromagnetic shielding.

Preparation of the metallic nanoparticles

[0131] The metallic nanoparticle according to the present invention may be prepared by any known preparation method.

[0132] A particularly preferred method to prepare the metallic nanoparticles is disclosed in

EP-A 2781562.

[0133] The metallic nanoparticle dispersion obtained by the method disclosed in

EP-A 2781562 typically contains at least 15 wt %, more preferably at least 30 wt%, most preferably at least 50 wt % of metallic nanoparticles, relative to the total weight of the dispersion. This highly concentrated dispersion is then used to prepare the metallic nanoparticle dispersion according to the present invention as described above.

EXAMPLES

Materials

[0134] All materials used in the following examples were readily available from standard sources such as ALDRICH CHEMICAL Co. (Belgium) and ACROS (Belgium) unless otherwise specified. The water used was deionized water.

[0135] Silver oxide (Ag ₂ 0) was prepared by the precipitation of silver nitrate in an alkaline aqueous solution of sodium hydroxide (33 wt%) followed by filtration and drying.

[0136] Solbin® A, a copolymer of 92 wt% vinylchloride, 3 wt% vinylacetate, and 5 wt% vinylalchohol commercially available from SHIN ETSU.

[0137] Solbin® AL, a copolymer of 93 wt% vinylchloride, 2 wt% vinylacetate, and 5 wt% vinylalchohol commercially available from SHIN ETSU.

[0138] Solbin® MFK, a copolymer of 90 wt% vinylchloride, 7 wt% vinylacetate, and 3 wt% acrylic acid commercially available from SHIN ETSU.

[0139] Solbin® TAO, a copolymer of 91 wt% vinylchloride, 2 wt% vinylacetate, and 7 wt% vinyl alcohol commercially available from SHIN ETSU. [0140] Solbin® TA2, a copolymer of 83 wt% vinylchloride, 4 wt% vinylacetate, and 13 wt% hydroxyalkyl acrylate commercially available from SHIN ETSU,

[0141] Solbin® CNL, a copolymer of 90 wt% vinylchloride and10 wt% vinylacetate

commercially available from SHIN ETSU.

[0142] Laroflex MP15, a copolymer of vinylchloride and vinylisobutylether commercially available from BASF.

[0143] Laroflex MP60, a copolymer of vinylchloride and vinylisobutylether commercially available from BASF.

[0144] DEG (CASRN 1 1 1-46-6) is diethyleneglycol commericially available from Sigma- Aldrich.

[0145] Dowanol DPMA (CASRN 88917-22-0) is Dipropylene Glycol Methyl Ether Acetate commercially available from DOW CHEMICALS.

[0146] Butyl Cellosolve (CASRN 11 1 -76-2) is etylene glycol monobutylether commerically available from Merck.

[0147] Efka FL3277 (CASRN 849624-75-5) is a wetting agent commercially available from BASF.

[0148] Disperbyk 2151 is a wetting agent commercially available from BYK CHEMIE.

[0149] Byk 4510 is an adhesion promoting compound commercially available from Altana.

[0150] Rhodiasolv® PolarClean is methyl-5-(dimethylamino) 2-methyl 5-oxopentanoate commercially available from SOLVAY.

[0151] Rhodiasolv® Iris is dimethyl 2-methylpentanedionate commercially available from

SOLVAY.

[0152] Agnique AMD-3 is lactic acid dimethylamide commercially available from BASF.

Measurements Methods

Conductivity of the silver coatings

[0153] The surface resistance (SER) of the silver coatings was measured using a four-point collinear probe. The surface or sheet resistance was calculated by the following formula:

SER = (π /ln2)*(V/l)

wherein

SER is the surface resistance of the layer expressed in Ω/Π;

Π is a mathematical constant, approximately equal to 3.14; In2 is a mathematical constant equal to the natural logarithmic of value 2, approximately equal to 0.693;

V is voltage measured by voltmeter of the four-point probe measurement device;

I is the source current measured by the four-point probe measurement device.

[0154] For each sample, three measurements were performed at different positions of the coating and the average value was calculated.

[0155] The silver content M _Ag (g/m ² ) of the coatings was determined by WD-XRF.

[0156] The conductivity of the coated layers was then determined by calculating the

conductivity as a percentage of the bulk conductivity of silver using the following formula:

Ag * ^CT Ag

% Ag _(bulk) = * 10-5 * 100%

M _Ag * SER

0.1663

% Ag _(bulk) = * 100%

A _g * SER

wherein

p Ag is the density of silver (10.49 g/cm ³ ) and σ _Ag the specific conductivity of silver (equal to 6.3 10 ⁵ S/cm).

Adhesion

[0157] The adhesion of the silver coatings on different substrates has been evaluated by a tape test according to ASTM D3359. The evaluation results in a score from 0 (very good adhesion) to 5 (very bad adhesion).

Varnish Clarity

[0158] The term varnish of a silver ink means the composition of the silver inks containing all ingredients except the silver sediment that is typically added at the end of the preparation process. The Varnish Clarity was visually evaluated by letting the Varnish stand for at least 24 hours at room temperature. If no visual cloudiness or haziness of the varnish was observed, it was evaluated as "OK". If cloudiness was observed in the varnish, it was evaluated as "Cloudy". If gel formation was observed, the varnish clarity was evaluated as "gel". Sticking behaviour

[0159] The sticking behaviour of the silver inks towards the sieve used for screen printing the inks has been evaluated. Therefore at least 50 g of silver ink was deposited on a non-printing area of a screen with a Plus 8000 emulsion stencil, available from MacDerrmid, applied at the bottom of the sieve. After at least waiting for at least 4 hours a change of stickness was evaluated by softly touching the stencil at the opposite position of the sieve below the deposited ink and comparing a change in roughness and/or stickness of the stencil compared to a stencil position at the bottom of the sieve where no ink deposited at the opposite. If no change was felt it was noted as "OK", otherwise "NOK" was noted.

Example 1

Preparation of the silver nanoparticle dispersion NPD-01

[0160] 78.0 g of silver oxide was slowly added, while stirring, to a 1 I reactor containing 275.0 g of pentanoic acid and 401.0 g of 2-pyrrolidone. The temperature of the mixture was kept at 25°C.

[0161] After complete addition of the silver oxide, the suspension was stirred overnight at 25°C.

[0162] Then, 300.0 g of Ν,Ν-diethylhydroxylamine was added in a time span of 1.5 hours to the suspension. The temperature of the reaction mixture was kept at 25 °C. When all reducing agent was added, the reaction mixture was kept at 25 °C while stirring for another hour.

[0163] The reaction mixture is then fed to a sedimentation vessel, where it was kept

overnight, without stirring. The supernatant was carefully removed from the sediment.

[0164] The obtained sediment was washed four times, two times with Dowanol PM™ (547 g) and two times with butylcellosolve™ (547 g). In each washing step, the solvent was added to the sediment and the resulting suspension stirred for 0.5 hour at 300 rpm. Then, the unstirred suspension was kept for another hour, and the supernatant carefully removed.

[0165] After the last washing step with butylcellosolve™, the sediment was centrifuged, in a centrifugal decanter from Rousselet Robatel (France) at 3000 rpm during 0.5 hour.

[0166] The obtained silver nanoparticle dispersion NPD-01 had ± 75 wt % of silver, relative to the total weight of the dispersion. Preparation of the silver inks SI-01 to SI-14

[0167] The Silver inks SI-01 to SI-14 were prepared by mixing together while stirring the non-silver ingredients of Table 1 until a clear solution is obtained. The silver nanoparticle dispersion NPD-01 is then added to the clear solution, followed by high shear homogenization.

Table 1

Ingredients SI-08 SI-09 SI-10 SI-11 SI-12 SI-13 SI-14 (wt %) (INV) (INV) (COMP) (COMP) (COMP) (COMP) (COMP)

Solbin A 2.01 - - - - - -

Solbin AL - 2.01 - - - - -

Laroflex MP15 - - 1.86 - 1.57 1.71 1.86

Laroflex MP60 - - - 1.86 - - -

2-pyrrolidone 11.00 1 1.00 - - - - -

DowanolDPMA - - 21.30 21.30 - - -

Butyl cellosolve 6.50 6.50 - - - - -

Byk 4510 0.20 0.20 - - - - - Disperbyk 2151 0.80 0.80 0.70 0.70 0.70 0.70 0.70

Efka FL3277 0.40 0.40 0.30 0.30 0.30 0.30 0.30

Acetic Acid ^* 0.50 0.50 - - - - -

NPD-01 78.60 78.60 75.80 75.80 75.80 75.80 75.80

^* 20 wt% in Butyl Cellosolve

[0168] The Silver inks SI-01 to SI-014 were screen printed on different substrates using a polyester P180 ULANO sieve (Ulano CDF Matrix UV film) thereby forming a pattern with a dimension of approximately 6.0 x 4.5 cm. The printed silver was then dried in a belt oven during 3 minutes at 130°C, followed by a curing step during 15 minutes at 150°C in a box oven.

[0169] The conductivity (Cond. expressed as % Ag-bulk) and the adhesion (Adh.) of the printed silver patterns were evaluated as described above. The results are shown in Table 2.

[0170] A conductivity that is greater than 25 and an adhesion that is lower than 2 are

considered to be acceptable.

Table 2

* 175 m heat stabilized polyester support from MacDermid [0171] It is clear from the results of Table 2 that the inventive silver inks comprising a copolymer comprising vinyl chloride and a hydroxyfunctional monomer have a very good adhesion on all substrates tested while its conductivity remains acceptable.

Example 2

Preparation of the silver inks SI-15 to SI-24

[0172] The Silver Inks SI-15 to SI-24 were prepared by mixing together while stirring the non-silver ingredients of Table 3 until a clear solution is obtained. The silver nanoparticle dispersion NPD-01 is then added to the clear solution, followed by high shear homogenization.

Table 3

Ingredients (wt %) SI-20 SI-21 SI-22 SI-23 SI-24

Solbin A 2.07 2.32 2.40 2.55 2.55

2-pyrrolidone 11.00 11.00 6.00 9.00 6.00

Butyl Cellosolve 4.20 4.00 6.30 3.10 6.10

Byk 4510 0.20 0.20 0.20 0.20 0.20

Disperbyk 2151 0.80 0.80 0.80 0.80 0.80

Efka FL3277 0.40 0.40 0.40 0.40 0.40

Methylnonylketone - - - - -

NPD-01 83.90 81.30 83.90 83.90 83.90 [0173] The Silver inks SI-15 to SI-24 were screen printed on different substrates using a polyester P180 ULANO sieve (Ulano CDF Matrix UV film) thereby forming a pattern with a dimension of approximately 6.0 x 4.5 cm. The printed silver was then dried in a belt oven during 3 minutes at 130°C, followed by a curing step during 15 minutes at 150°C in a box oven.

[0174] The conductivity (Cond. expressed as % Ag-bulk) and the adhesion (Adh.) of the printed silver patterns were evaluated as described above. The results are shown in Table 2.

[0175] A conductivity that is greater than 25 and an adhesion that is lower than 2 are

considered to be acceptable.

Table 4

The results of Table 4 illustrate that all silver inks containing a copolymer comprising vinyl chloride and a hydroxyfu notional monomer have a very good adhesion on all substrates tested while its conductivity remains acceptable.

Example 3

Preparation of the silver inks SI-25 to SI-42

[0177] The Silver Inks SI-25 to SI-42 were prepared by mixing together while stirring the non-silver ingredients of Table 5 until a clear solution is obtained. The silver nanoparticle dispersion NPD-01 is then added to the clear solution, followed by high shear homogenization.

Table 5

Ingredients (wt %) SI-39 SI-40 SI-41 SI-42

Solbin A 2.55 2.55 2.55 2.55

Rhodiasolv Iris 10.00 - - - Rhodiasolv Polarclean - 9.00 - -

Dowanol DPMA - - 9.00 -

Dowanol PGMA - - - 9.00

Butyl Cellosolve 2.50 3.00 3.00 3.00

Byk 4510 0.20 0.20 0.20 0.20

Disperbyk 2151 0.80 0.80 0.80 0.80

Efka FL3277 0.40 0.40 0.40 0.40

NPD-01 83.20 83.80 83.80 83.80

[0178] The Silver inks SI-25 to SI-42 were screen printed on different substrates using a polyester P180 ULANO sieve (Ulano CDF Matrix UV film) thereby forming a pattern with a dimension of approximately 6.0 x 4.5 cm. The printed silver was then dried in a belt oven during 3 minutes at 130°C, followed by a curing step during 15 minutes at 150°C in a box oven.

[0179] The conductivity (Cond. expressed as % Ag-bulk) and the adhesion (Adh.) of the printed silver patterns were evaluated as described above. The results are shown in Table 6.

[0180] A conductivity that is greater than 25 and an adhesion that is lower than 2 are

considered to be acceptable.

Table 6

Cond Adh Cond Adh Cond Adh Cond Adh

SI-25 42.4 0.5 36.1 0.5 42.4 0.5 37.7 0.6

SI-26 40.0 0.5 41.3 0.5 40.7 0.5 39.0 0.5

SI-27 37.5 0.5 40.8 0.5 40.0 0.5 38.0 0.5

SI-28 40.5 0.5 39.9 0.5 39.4 0.5 39.6 0.5

SI-29 38.3 0.5 40.4 0.5 39.0 0.5 38.8 0.5

SI-30 - - - - - - - -

SI-31 40.1 0.5 40.9 0.5 40.9 0.5 36.9 0.5

SI-32 41.5 0.5 43.2 0.5 42.3 0.5 37.6 0.6

SI-33 53.9 0.5 - - 41.2 0.5 36.6 0.5

SI-34 37.2 0.5 - - 32.8 0.5 34.1 0.5

SI-35 41.1 0.5 40.3 0.5 41.7 0.5 38.5 0.9

SI-36 42.7 0.5 39.7 0.5 42.9 0.5 37.5 1.2 SI-37 42.1 0.5 45.0 0.5 41.8 0.5 43.1 0.6

SI-38 32.5 0.7 43.8 0.5 44.0 0.5 41.5 0.5

SI-39 46.4 0.5 47.6 0.5 43.8 0.5 44.1 0.8

SI-40 54.4 0.5 57.0 0.5 40.4 0.5 54.5 0.5

SI-41 54.5 0.5 50.6 0.5 51.7 0.5 55.7 0.5

SI-42 44.7 0.5 56.6 0.6 53.5 0.6 48.7 0.5

[0181] The results of Table 6 illustrate that all silver inks containing a copolymer comprising vinyl chloride and a hydroxyfunctionai monomer have a very good adhesion on all substrates tested while its conductivity remains acceptable.

[0182] The Varnish Clarity and the Sticking behaviour were evaluated as described above.

The results are shown in Table 7.

Table 7

Varnish Sticking

SI-25 OK NOK

SI-26 OK OK

SI-27 gel OK

SI-28 OK NOK

SI-29 OK OK

SI-30 cloudy -

SI-31 gel OK

SI-32 gel OK

SI-33 OK OK

SI-34 OK OK

SI-35 OK OK

SI-36 OK OK

SI-37 OK OK

SI-38 gel OK

SI-39 OK OK

SI-40 OK OK

SI-41 gel OK

SI-42 gel OK The results of Table 7 illustrate that the silverinks wherein the liquid carrier comprises Rhodasolv Polarclean or methylbutyrolactone have improved sticking behavior and improved varnish stability.