Abstract:
A method of densifying porous substrates, such as brake performs, using a liquid precursor, in which the rate at which "fresh" or "new" liquid precursor is consumed is reduced by maintaining the liquid precursor being used for the densification at a purity level that is less that pure but still chemically suitable for obtaining the desired densification product.

Inventors:
CHANG KENNY (US)
ZIMMERMAN BRUCE (US)
FILLION ARNAUD (US)
Application Number:
PCT/EP2007/058193
Publication Date:
February 14, 2008
Filing Date:
August 07, 2007
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
MESSIER BUGATTI (FR)
CHANG KENNY (US)
ZIMMERMAN BRUCE (US)
FILLION ARNAUD (US)
International Classes:
C04B35/83; C23C16/04; F16D69/02; C04B35/80
Domestic Patent References:
WO1999040042A11999-08-12
WO1998040327A11998-09-17
Foreign References:
EP0592239A21994-04-13
Other References:
None
Attorney, Agent or Firm:
JOLY, Jean-Jacques et al. (158 Rue de l'Université, Paris Cedex 07, FR)
Download PDF:
Claims:
We claim:

1. A method of densifying a porous substrate comprising:

in a reaction chamber, submerging the porous substrate in a liquid precursor

so that the liquid precursor infiltrates pores in the porous substrate; and

inductively heating the submerged porous substrate to a temperature

sufficient to cause liquid precursor to pyrolize and deposit a decomposition product

within the pores of the substrate so as to densify the porous substrate,

wherein a chemical purity level of the liquid precursor is controlled to be less

than chemically pure and sufficiently chemically pure to obtain a decomposition

product having desired physical characteristics.

2. The method of claim 1, wherein the liquid precursor comprises a

hydrocarbon.

3. The method of claim 1, wherein the decomposition product comprises

carbon.

4. The method according to claim 2, wherein the hydrocarbon is selected

from the group consisting of cyclopentane, cyclohexene, 1-hexene, gasoline, toluene,

methylcyclohexane, n-hexane, kerosene, hydrodesulfurized kerosene, benzene, and

combinations thereof.

5. The method according to claim i, wherein the chemical purity level of

the liquid precursor is controlled to be between about 80% and about 99.9%.

6. The method according to claim 5, wherein impurities are present in the

liquid precursor, the impurities comprising one or more of cyclopentadiene, hexane,

methylclopentane, benzene, cyclohexene, hepane, methylcyclohexane, toluene,

ethylbenzene, phenylacetylene, styrene, nonane, indene, naphthalene,

methylnaphthalene, acenaphtalene, and fluorine.

7. The method according to claims 1-6, wherein the chemical purity of the

liquid precursor is controlled using an in-line distillation process.

8. The method according to claim 7, wherein the chemical purity of the

liquid precursor is controlled within a range of about 95% ± 5%.

9. The method according to claim 7, wherein the chemical purity of the

liquid precursor is controlled within a range of about 90% ± 5% by mixing a quantity

of a chemically pure liquid precursor with a quantity of aged liquid precursor

containing one or more impurities reflecting use in one or more prior densification

cycles.

10. The method according to claim 1, wherein the liquid precursor contains

an organosilane.

11. The method according to claim 10, wherein the organosilane is selected

from the group consisting of methyltrichlorosilane, dimethyldichlorosilane,

methydichlorosilane, and tris-n-methyl amino silane.

12. The method according to claim 10, wherein the decomposition product

comprises silicon carbide and silicon nitride.

13. The method according to claim 1, wherein the liquid precursor is a

mixture of an organosilane and a hydrocarbon.

14. The method according to claim 12, wherein the decomposition product

one of carbon/silicon carbide or carbon/silicon nitride.

15. A reactor for densifying porous preforms using a liquid matrix precursor

comprising:

a reaction chamber;

at least one inductive coil heating assembly disposed in the reaction chamber;

a fluid level indicator for monitoring liquid precursor consumption;

means for adding liquid precursor during a densification process;

means for purging the reaction chamber with inert gas;

a vapor recovery system connected to the reaction chamber and constructed

and arranged to condense precursor vapor in the reaction chamber and to return the

condensed precursor to the reactor vessel;

an exhaust system connecting the vapor recovery system and the means for

purging to a thermal oxidizer; and

pressurizing means for maintaining a reactor pressure between about 760 Torr

and about 780 Torr during densification.

16. The method according to claim 1, wherein inductively heating the

submerged porous substrate comprises:

setting an initial frequency and power level for inductive heating, the initial

frequency and power level being effective to accumulate sufficient heat at a

geometric center region of the porous substrate to cause pyrolysis of liquid precursor

vapor and preferentially in the pores located in the geometric center region of the

porous substrate;

supplying an initial power level for inductive heating at the initial frequency

sufficient to densify the geometric center region of the porous substrate without

simultaneously densifying other parts of the porous substrate;

after densifying the geometric center region of the porous substrate, further

adjusting the supplied power level and frequency so as to progressively densify the

interior regions of the porous substrate in a radial direction outwards from the

geometric center region of the porous substrate, and

ramping down the power level to zero at the end of the densification process.

17. The method according to claim 1, further comprising a heat treatment

performed after densification, the heat treatment comprising:

draining the liquid precursor completely from the reaction chamber;

purging the reaction chamber with an inert gas;

inductively heating the densified porous substrate in the inert gas atmosphere

at a temperature between about 1600 0 C to about 2400 0 C while maintaining a

pressure of about 760 Torr to about 780 Torr; and

ramping down the inductive heating to zero to conclude heat treatment.

Description:

METHOD FOR DENSIFICATION OF POROUS ARTICLES

Cross-reference to related applications:

This application claims priority from U.S. Provisional Application No. 60/821 ,596, filed on August 7, 2006, the entire content of which is incorporated herein by reference.

Field of the invention:

The present invention relates to a method and apparatus for densifying porous articles with a desirably high rate of production, particularly, but not necessarily only, with respect to the field of friction braking articles, such as aircraft brakes.

Background of the invention:

In the field of friction materials, it is generally known to use porous materials to manufacture friction members, such as friction brake disks.

The manufacture of such friction members generally begins with the construction of a porous preform. For example, in many friction brake applications, annular preforms are used.

The annular preforms can be constructed using several different known methods. For example, carbon fiber fabric plies can be needled together and annular preforms can be cut from the stacked material.

Also, near net shape preforms can be formed, for example, by weaving carbon fibers, or by braiding the carbon fiber into a desired shape. Certain carbon fiber fabrics are known having a weave that facilitates laying the fabric in a spiral form. In this context, "near-net" refers to forming structures having a form close to a desired shape of the final article, such as an annular brake disk.

Oxidized polyacrylonitride ("PAN") fibers or pitch-based fibers are common examples of starting fibers used in this type of application. Subsequently, these fibers may be carbonized in a high temperature treatment step. In another conventional approach, the starting fibers are formed using a resin or pitch, and the resultant mass is later cured with a reactive gas, such as nitrogen gas. The thusly cured mass is then carbonized to obtain a semi-rigid preform.

In any event, it is desirable to further densify the resulting porous preform (especially, but not necessarily only, with a carbonaceous material) so as to obtain desired friction and mechanical properties.

Chemical vapor infiltration ("CVI") is a widely used conventional technique in this regard for obtaining carbon/carbon composite materials. CVI uses a hydrocarbon-containing gas to infiltrate a porous preform. The CVI gas is then cracked under high temperatures so as to leave a carbon coating on the fiber structure of the preform.

Conventional CVI typically requires several hundred hours of processing in

order to obtain a carbon/carbon ("C/C") structure having a desired density and mechanical properties. By way of example, a typical conventional CVI process includes a first infiltration cycle performed, for example, over approximately 300-500 hours or more.

However, conventional CVI frequently causes rapid blockage of the surface porosity of the preform before interior portions of the preform are adequately densified. In order to "reopen" the surface porosity to permit further densification, an intermediate machining step becomes necessary. In general, this intermediate machining (using a known method, such as milling) removes surface layers of the preform having carbon-blocked pores to expose open pores of the preform so that

the hydrocarbon gas can again infiltrate the preform structure. Taking into account that several hundred preforms are densified in a typical densification process, the intermediate machining step can add as much as 48 hours to the overall conventional CVI densification process.

Once the intermediate machining of the partially densified articles is completed, a second CVI process is performed to make use of the reopened surface porosity of the preforms. This second CVI process step can last, for example, another 300-500 hours or more. This generally completes the conventional densification process using CVI.

Another approach to densifying porous preforms uses a liquid instead of gaseous hydrocarbon precursor. This method of densification is sometimes referred to in the art as "film boiling" or "rapid densification."

Film boiling densification generally involves immersing a porous preform in a liquid hydrocarbon so that the liquid substantially completely infiltrates the pores and interstices of the preform. Thereafter, the immersed preform is inductively heated by appropriately placed electrical elements, such as induction coils, to a temperature above the decomposition temperature of liquid hydrocarbon (typically 1000 0 C or more). More particularly, the liquid hydrocarbon adjacent to the inductively heated preform structure dissociates into various gas phase species within the preform porosity. Further thermal decomposition of the gas phase species results in the formation of pyrolitic carbon on interior surfaces in the open regions of the porous material. The use of liquid precursors for densification is discussed in, for example, US Patent Nos. 4 472 454, 5 389 152, 5 397 595, 5 733 611 , 5 547 717, 5 981 002, and 6 726 962. Each and every one of these documents is incorporated herein by reference in its entirety.

The concept of inductive heating in this field is generally known, including as described in the aforementioned references. However, heating a preform to high temperatures (at least 1000 0 C and as much as 1400 0 C) while it is literally immersed in highly volatile hydrocarbon liquids (such as, for example, cyclohexane) raises very important safety issues. Summary of the invention:

The present invention relates to a process of densifying porous substrates using a liquid precursor, in which the volume of "new" or "fresh" liquid precursor used is usefully reduced by maintaining the liquid precursor used for densification at a level of purity that is less than pure, but still chemically suitable for the densification process. In effect, the present invention uses an artificially "aged" (in terms of the impurities present therein) liquid precursor.

Brief description of the drawings:

The present invention will be even more clearly understood with reference to the drawings appended hereto, of which:

FIG. 1 is a schematic representation of a facility for performing densification using a liquid precursor according to the present invention;

FIG. 2 and FIG. 3 are partially cutaway side and top view of a reaction chamber for densifying porous articles according to the present invention;

FIG. 4 illustrates an experimentally derived relationship between densification run cycles and liquid precursor purity, quantified as concentration of a principal precursor component;

FIG. 5 illustrates an experimentally obtained progression of impurity levels in a liquid precursor over several cycles;

FIG. 6 illustrates calculated versus experimental data over several cycles where precursor purity is periodically restored; and

FIGS. 7 and 8 illustrate calculated versus experimental data over several cycles where precursor purity is periodically partly restored.

Detailed description of the invention:

The feature and details of the method and apparatus of the invention with the reference to the accompanying drawings are shown by way of illustration and not as limitations of the invention.

Solely by way of example and/or illustration, mention is made hereinbelow of porous preforms, such as preforms for manufacturing friction brake disks. It is expressly noted, however, that the present invention is more generally applicable to densifying other kinds of porous substrates in the manner described.

A highly schematic representation of a facility for performing densification using liquid precursors is illustrated in Figure 1. The system can include a remote liquid precursor storage site 100 (including, for example, a fluid transfer system) for managing the transport of new and used precursor liquid. One example of a precursor liquid used according to the present system is a liquid hydrocarbon, such as cyclohexane (CeHi 2 ). For example, a tank "farm" of one or more remote storage tanks (collectively indicated at 100) for the liquid precursor may be provided. The tank farm could also include one or more tanks for at least initially storing used liquid precursor. It may be desirable or even required (depending on applicable industrial requirements) to keep at least the tank farm 100 at some distance from the rest of the facility for safety reasons. For example, some local and/or national ordinances require separation on the order of hundreds of feet.

The facility may optionally include a relatively smaller local storage tank 105 for keeping a relatively small quantity of new precursor liquid close to the processing equipment, if desired.

The piping system (including pumps and the like) used to interconnect various parts of the facility is conventional and may be of any construction and arrangement appropriate for the transport of liquid precursor being used, particularly, but not necessarily only, liquid hydrocarbons. The fluid transfer system is preferably but not necessarily computer-controlled. Commercially available computer-controlled systems (for example and without limitation, those commercially available from the company OPTO 22) can be used for monitoring and controlling this type of fluid transfer system, including loading of new liquid precursor from an outside supplier.

The liquid precursor is supplied to one or more reaction chambers (collectively indicated at 110) from the local precursor storage tank 105. Preferably, sufficient liquid precursor is provided to substantially immerse the one or more preforms being densified therein, as well as the induction heating coils associated therewith.

As mentioned before, the film boiling process creates gaseous species that in part causes the formation of pyrolitic carbon on interior surfaces of the preform porosity. Precursor vapor is captured to the extent possible and condensed at the conventional condenser unit 115 for possible recycling in the process. A commercial cooling tower 140 is available to maintain an adequate water temperature for the cooling of the condenser unit 115.

Effluent gas that is still left over is preferably conveyed to a thermal oxidizer 120 of a known configuration to burn off residual hydrocarbons in the effluent gas.

The power from the power supply 125 is transferred to the induction coils 25 by metal bus bars 30 constructed according to a given arrangement of elements in a

facility and according to appropriate desired dimensional considerations. The bus bars may be made from copper, for example, and are preferably but not necessarily water-cooled by water cooling networks 50. (See Figure 2.)

Each power supply 125 may have remote PID loop control capability and can be monitored and controlled from a computer control terminal. Power density control, voltage control, current control, frequency control, and/or temperature control of the densification process by known methods is also within the scope of the contemplated arrangement.

Figure 2 illustrates a reaction chamber 110 constructed and arranged to process two (for example) porous preforms therein. The reaction chamber 110 has two induction heating coil sets 25 corresponding to each preform 35 that is to be processed. The induction coils sets 25 are preferably mounted in position using non- reactive thermally stable supports made from, for example, an electrically non- conductive glass composite material 45 (such as that known in the art as "G-10") that can withstand, for example, a liquid hydrocarbon environment. The induction heating coils 25 are preferably water-cooled pancake spiral coils, and may be made from copper metal. For this reason, it is desirable to provide a heat exchanger 135 (see Figure 1 ) dedicated to the water-cooling system for the induction coils 25. In use, a preform (or worn brake) 35 being densified is heated by direct coupling from the induction coil 25.

In an example of loading and unloading coil/reactor chamber 110, a top cover panel 15 is provided with a conventional locking mechanism for sealing the chamber 1 10. Each reactor chamber 110 (as many as are provided) is provided with a common liquid precursor supply line connection 20, and a common exhaust line 10 operably connected to the condenser 115 and thermal oxidizer 120.

Each reactor chamber 110 can be desirably filled, drained, and monitored from the computer control system. The exhaust liquid precursor vapor from the densification process is condensed and fed back to the reactor chambers 110, whereas residual effluent gas is then taken to the thermal oxidizer 120 and burned.

Because volatile liquid hydrocarbons are a particular example of the liquid precursor used in the present invention, it is desirable (but not obligatory) to provide a nitrogen (N2) gas supply system (not shown) to, for example, flush out the piping systems and generally fill voids in the system with an inert gas (instead of oxygen- containing air) so as to decrease the risk of combustion. In a particular example, empty spaces in both the remote and local liquid precursor storage tanks are maintained at a slight, continuously supplied, overpressure of nitrogen (or other conventionally known inert) gas so as to prevent potentially dangerous accumulations of volatile vapors. Hydrocarbon species mixed with the exhausted nitrogen gas are sent to the thermal oxidizer 120 so that the hydrocarbons can be burned off before the gas is exhausted to the exterior.

Also, because the system uses a "wet" process, it is useful to provide a drying oven 130 in the system to dry off densified preforms following densification. The exhaust from such a drying oven 130 is preferably also connected to the thermal oxidizer 120 in order to process heavy and light aromatics entrained in the resultant effluent gas. With respect to safety considerations, it is useful to use an oven structure that is structurally resistant to failure in the event of an explosion therein, given the presence of volatile gases in the oven during drying. The drying process can be, for example, computer controlled in order to simplify process control.

TABLE 1

Total 3999 X 8ι 9988 °-9 7c 99 77 99 hi 9965 99 V 995 c ι 9948 9 C W 9945 °949 9944 99 -ii' 9a 31

Table 1 provides the analysis of aged CeH 12 and the major impurities produced from the densification process. In this study, eight densification cycles in three reactors were performed with carbonized preforms using a dedicated power curve. In particular, an objective was to reduce the usage of new or "fresh" liquid precursor (which can be relatively costly) to replenish the precursor being used during production.

Sixteen aged CβHi 2 samples from eight consecutive runs were collected and sent for analysis. The goal was to correlate individual contaminant peak value to the aged C 6 Hi 2 . Samples were collected before and after each densification cycle and identified as A and B.

The CβHi2% concentration at the end of 8th cycle was still above 94%. The major resulting impurity peaks were Benzene, Naphthalene, Toluene, Styrene, Cyclohexene, Cyclopentadiene, and Indene. Six out of the seven measured impurities followed a steady, generally increasing trend throughout the eight cycles. A gas chromatography (GC) analysis made from the aging study indicates all major contaminants and Cyclohexane concentrations are very predictable. All impurity peaks are consistently repeated from one cycle to the next cycle.

Simulation of aged liquid precursors by doping a liquid precursor with various impurities is also contemplated. In this manner, it may be possible to beneficially extend the usable life of a liquid precursor and/or reduce the need for highly pure (and, therefore, relatively expensive) liquid precursors. In other words, on the one hand, a "minimum" level of precursor purity can be identified, such that the precursor can be used at purity levels above that minimum (before replacement with highly pure precursor). On the other hand, a lower acceptable level of precursor purity can be identified such that the contemplated densification process would use that lower purity precursor on an ongoing basis. Either way, the usage of high purity precursor liquid is desirably reduced.

Aged liquid precursors were simulated by doping a liquid precursor with various impurities mentioned above in order to approximate the gradual "deterioration" of a highly pure liquid precursor after several process cycles. A model was developed to predict Cyclohexane concentrations at various cycles. Extrapolation was performed based on experimental data from the eight consecutive runs previously described. Figure 4 illustrates the predicted Cyclohexane concentrations versus number of consecutive process runs. It is noted that the calculated Cyclohexane concentration substantially reaches steady state after about

io

40 runs, mainly because new Cyclohexane is added to the process tank prior to the densification cycle.

500 Gallon Batch Calculations

' otrtt 99 08 0 /00 474 If.

Note: Calculated density for the mixture is: 0.790 g/cc. Allowable tank capacity is 480 gallons 480 gallon batch weight: 0.790 x 480 x 3.785 = 1435 (kg)

TABLE 2

Nine chemicals were purchased from Alfa Aesar to dope the cyclohexane precursor. Table 2 provides the information about the chemicals used for the doping. The purity of the purchased chemicals ranged from 99.6% to 80%.

Table 2 provides the quantity used for the individual chemicals to obtain a 90% Cyclohexane concentration. A 90% Cyclohexane concentration was used for the initial mix in order to simulate the model, although cyclopentadiene was not used in the mix for safety reasons because this gel-like material is extremely flammable in air. The effect on the test is believed however to be minimal. Six consecutive densification cycles were performed using the initial 90% mix. Samples of the liquid precursor were collected before and after each cycle and sent for GC analysis.

99 87 789

TABLE 3

A total of twelve aged precursors from six consecutive cycles were sent to a laboratory for gas chromatography analysis. Aged precursor samples were collected before and after the densification cycle from the 500 gallon tank. Table 3 provides the GC analysis for the simulated 90% mix precursor. It was observed in Table 3 that the reported concentrations from all chemicals closely followed the mass % used in the 90% mixture with the exception of Cyclopentadiene, which was not actually used due to its high flammability in air. It is however believed that the omission of cyclopentadiene from the actual samples has a minimal overall effect on the test.

Doping Study- six consecutive runs

Total klUO WX ) WO.) 1 QQOO 1(X)(X) 10000 - 1 OQOu W)(X) IQJW 100X 1 Q)U) 10,00

TABLE 4

Table 4 illustrates a progression of the major contaminants from the six consecutive cycles, or twelve precursor samples. The purity generally started at 90.3% and ended at 88.4% after six densification cycles. In most of the cases,

contaminants reached steady state or slowly declined with the exception of Benzene. (See, for example, Cyclopentadiene, Cyclohexene, Toluene, Ethylbenzene, Phenylacetylene, Styrene, lndene, Naphthalene, Methylnaphthalene, Acenaphthalene, and Fluorene in Table 4.) This indicates that continuation of chemical breakdown from Cyclohexane (CeHi 2 ) to Benzene (CeH 6 ) is most likely to continue at lower C 6 Hi 2 concentration levels. (See, for example, the benzene concentration in Figure 5.)

In practice, several methods can be used to manage the precursor. Some of them are described hereafter.

Several consecutive cycles could be run with the same liquid precursor bath, followed by periodically replacing the whole storage tank with new cyclohexane. In that manner, the cyclohexane concentration will vary between fresh cyclohexane

concentration and a low concentration depending on the number of consecutive cycles run. Figure 6 is shown a case where the storage tank is drained every 8 cycles.

Another way to manage the precursor is to periodically replace only a part of liquid precursor in the storage tank. This approach reduces the variations in concentrations and therefore permits better control of the pyrocarbon deposited from this precursor (microstructure, thermal-mechanical or friction properties). In this regard, Figure 7 illustrates how cyclohexane concentration is theoretically affected by replacing half the storage tank with fresh cyclohexane every 4 runs.

According to these two methods, the storage tank is never totally drained. Multiple runs were performed according to the approaches corresponding with Figures 6 and 7, respectively, and the used cyclohexane samples were analyzed by gas chromatography. Tables 5a and 5b, respectively, provide the results of these analyses.

TABLE 5A

TABLE 5 B

The experimental data confirm the calculation is an accurate method to forecast the cyclohexane concentration versus the runs number (see Figure 8.) It is noted that Figures 7 and 8 also illustrate 8-cycle experimental data that further confirms the expected rate of cyclohexane degradation in terms of its general curvature.

Moreover, the analyses show that the concentration of every chemical component remains substantially steady after several runs.

Although the present invention has been described above with reference to

certain particular examples for the purpose of illustrating and explaining the

invention, it is to be understood that the invention is not limited solely by reference

to the specific details of those examples. More specifically, a person skilled in the art

will readily appreciate that modifications and developments can be made in the

preferred embodiments without departing from the scope of the invention as defined

in the accompanying claims.