Title:
A METHOD FOR EXTRACTING RARE-EARTH METALS
Document Type and Number:
WIPO Patent Application WO/2014/137239
Kind Code:
A1
Abstract:
The present invention relates to a method for complex processing of apatite concentrate resulting in producing concentrate of rare earth metals (REM) and plaster from phosphogypsum, a waste of sulphuric acid technology for producing phosphoric acid from apatite. The method comprises recrystallization of hemihydrate or anhydrite of calcium sulphate into dihydrate of calcium sulphate in the presence of a soluble calcium salt at concentrations of 0.075-3.75 M (in terms of Ca2+) at subacidic conditions (pH>1), and dissolution with strong acid (pKa<0) at a concentration of 0.2-8.0 M (in terms of H+). Recovery of REM into solution is up to 95%, the residual content of impurities of phosphorus, fluorine and alkali metals in dihydrate of calcium sulphate does not exceed 0.3 wt.%, 0.1 wt.%, 0.05 wt.%, respectively.

Inventors:
GENKIN MIKHAIL VLADIMIROVICH (RU)
EVTUSHENKO ALEKSEY VLADIMIROVICH (RU)
KOMKOV ALEKSEY ALEKSANDROVICH (RU)
SAFIULINA ALFIYA MINEROVNA (RU)
SPIRIDONOV VASILIY SERGEEVICH (RU)
SHVETSOV SERGEY VLADIMIROVICH (RU)
Application Number:
PCT/RU2013/000991
Publication Date:
September 12, 2014
Filing Date:
November 08, 2013
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
OPENED JOINT STOCK COMPANY UNITED CHEMICAL COMPANY URALCHEM (DE)
International Classes:
C22B59/00; C22B3/06
Foreign References:
RU2293781C12007-02-20
RU2225892C12004-03-20
PL272533A21989-02-20
EP0522234A11993-01-13
Other References:
See also references of EP 2971197A4
Attorney, Agent or Firm:
PYLNEV, Yuri Aleksandrovich (Limited,White Gardens, 10th Floor,9 Lesnaya Stree, Moscow 7, RU)
Download PDF:
Claims:
What is claimed:

1. A method for extracting rare earth metals (REM) from phosphogypsum comprising successive steps of recrystallization of phosphogypsum and dissolution of REM, wherein recrystallization of hemihydrate or anhydrite of calcium sulphate into dihydrate of calcium sulphate is carried out in the presence of soluble calcium salt at concentration of 0.075-3.75 M (in terms of Ca2+) at subacidic conditions (pH>l), and dissolution is carried out with strong acid (pKa <0) at concentration of 0.2-8.0 M (in terms of H+).

2. The method of claim 1 , wherein the calcium nitrate or calcium chloride, or a mixture thereof is used as the calcium salt, and nitric acid or hydrochloric acid or sulphuric acid or a mixture thereof is used as the acid.

3. The method of claim 1 , wherein recrystallization is carried out at 10-50 °C during 0.25-4.0 hours, preferable at 20-30 °C during 2.0-3.0 hours.

Description:
A METHOD FOR EXTRACTING RARE-EARTH METALS

Field of the invention

The present invention relates to technologies for complex processing of apatite, in particular, technologies for obtaining a concentrate of rare-earth metals (REM) and gypsum plaster from phosphogypsum, a waste of sulphuric acid technology for producing phosphoric acid from apatite.

Background of the invention

Tens of millions of tons of phosphorus-containing minerals, such as apatite, rock phosphate, etc., are processed for producing phosphorus-containing fertilizers. Typically, the processing is carried out by treating these natural materials with concentrated nitric or sulphuric acid. During the treatment with sulphuric acid, apatite is decomposed with precipitation of calcium sulphate and formation of phosphoric acid solution. In this case, the main waste product is phosphogypsum (calcium sulphate contaminated with impurities of P2O5, F, Fe, Al, Sr, REM) which comprises most of the rare-earth metals contained in apatite. For example, apatite of the Kola Peninsula contains up to 1 % of rare-earth metals, the 70 to 100 % of which are precipitated with calcium sulphate at apatite processing with sulphuric acid. Phosphogypsum constitutes whole mountains around the plants for processing of apatite. Every year millions of tons of phosphogypsum containing about 0.5 % REM in terms of oxides, which currently can not be extracted from it, are sent to dumps. Furthermore, the presence of such dumps containing toxic compounds including fluorine is an environmental problem. In this regard, numerous research projects have been conducted to develop processing technology to extract REM and remove toxic components.

The method for extracting rare-earth elements from phosphogypsum by treatment with nitric acid and subsequent extraction of rare earth elements (REE) by phosphine oxide is known (Martynova I.N. et al. Research of distribution of REE in the course of extraction from acidic nitrate-phosphate solutions. Collected articles "Processing and physico-chemical properties of compounds of rare elements. Apatity, 1984, pp. 6-8 (Rus)). The disadvantage of this method is the need for expensive trialkyl phosphine oxide and the impossibility of complete liquid-phase removal of REE from the organic phase. Furthermore, because of the high loss of trialkyl phosphine oxide with the aqueous phase, this method is uneconomical and requires additional facilities for trialkyl phosphine oxide utilization.

Nitric acid extraction technology for isolation of rare earth elements from apatite, giving up to 85% release in a solution also containing phosphorus and fluorine is known (Kosynkin V.D. et al. "Condition and perspective of rare earth industry in Russia", "Metals" (rus), No. 1 , 2001 ). The disadvantage of this method is the impossibility of using process solutions in a closed loop and the subsequent low recovery of REM in the process in closed loop.

The method for extracting rare earth elements from phosphogypsum (PCT publication WO201 1008137) is known. The method involves the acid extraction of rare earth element compounds from phosphogypsum using a solution consisting of a mixture of sulphuric acid and nitric acid in a ratio of 3.2: 1.2 with a concentration of 1 -3 wt.% and a liquid to solid ratio of 4:5 over a period of 8-12 minutes, while the extraction suspension is agitated and subjected to a hydroacoustic effect. The insoluble gypsum residue is then separated from the extraction suspension and the rare earth element compounds are recovered from the extraction solution by cation exchange sorption with the extraction solution being passed through a cation exchange filter. The main disadvantages of this method are not sufficiently high enough degree of extraction of rare earth metals (up to 85%) with the high cost ion exchanger, long duration of the process and large material flows.

The method of recovering rare-earth elements from phosphogypsum disclosed in RU patent No. 2293781 seems to be the closest analog of the present invention. The method comprises treatment of phosphogypsum with sulphuric acid solution to recover rare-earth elements into solution, separation of gypsum precipitate, increasing of oversaturation rate of the solution in terms of rare-earth elements to crystalize rare-earth metal concentrate, and separation of the concentrate from mother liquor followed by concentrate processing. Phosphogypsum is treated with 22-30% sulphuric acid solution at liquids-to-solids ratio 1.8-2.2 during 20-30 min to prevent spontaneous crystallization of rare-earth element concentrate in solution before insoluble precipitate is separated. An increase of the oversaturation rate of the solution is achieved by means of providing sodium concentration 0.4-1.2 g/L. The disadvantage of this method is the use of additional reagents, high acid concentrations and significant amounts thereof, a large number of basic technological operations with incomplete extraction of rare earth elements (up to 71.4%) and the overall complexity of the process.

The present invention addresses the problem of highly efficient extraction of REM from phosphogypsum followed by obtaining REM concentrate, and simultaneous purification of calcium sulphate from phosphorus and fluorine impurities. In the present invention, the term "REM" is used to indicate lanthanides and yttrium. Also, the symbol "Ln" is used for these elements.

The problem is solved by the method of the present invention. The first step of the method comprises recrystallization of phosphogypsum from hemihydrate CaS0 4 * 0,5 H 2 0 or anhydride CaS0 4 into dihydrate CaS0 4 » 2H 2 0 in neutral or subacidic solution of calcium salts, at the same time REM are extracted from solid solution of calcium sulphate into separate solid phase. At the second step of the method, compounds of REM, fluorine, phosphorus and alkali metals are dissolved with an acid. Yield of REM extraction is 88-95 %, the residual content of phosphorus, fluorine and alkali metals in calcium sulphate dihydrate is no more than 0.3 wt.%, 0.1 wt.%, 0.05 wt.%, respectively. Isolation of REM concentrate from the aqueous solution can be effected by any suitable method described in the literature.

The essence of the present invention is set forth in details below.

The authors of the present invention have found that a significant part of REM in the phosphogypsum hemihydrate is present in the form of compounds MLn (S0 4 ) 2 (wherein M - alkali metal atom, Na or ), forming a solid solution with the main phase of calcium sulphate. Thus, treatment of calcium sulphate which is not accompanied by changes in the crystal structure thereof will not provide a high degree of extraction of rare earth metals in the solution. That is, the best extraction of rare-earth metals is achieved by recrystallization of calcium sulphate hemihydrate CaS0 4 « 0,5 H 2 0 or anhydride CaS0 4 into dihydrate CaS0 4 * 2 H 2 0. It is shown for dihydrate CaS0 4 » 2 H 2 0 that REM form separate phases in the form of sulphates, while REM are not present in detectable amounts in crystals of CaS0 4 * 2 H 2 0 available (Bushuev N.N., Nabiev A.G., Petropavlovskiy I.A., Smirnov I.C. "The nature of inclusion of REE cerium subgroup in the structure of calcium sulphate crystalline hydrates", Journal of Applied Chemistry (rus), 1988, No. 10, V. 61 , pp. 2153-2158; Bobik V.M. Coprecipitation of rare earth elements in a system of three heterovalent ions with sulphates of alkali and alkaline earth elements. Radiochemistry (rus), 1977, No. 5, pp. 606-610).

Thus, behaviour of REM in the course of recrystallization of phosphogypsum hemihydrate can be described by the following equation:

MLn(S0 4 ) 2 . n(2 CaS0 4 * H 2 0) + 3n H 2 0 2n Ca(S0 ) . 2H 2 O so iid + MLn(S0 4 ) 2 solid.

The presence of calcium salts in the solution promotes extraction of REM from solid solution of calcium sulphate and precipitation thereof in form of separate solid phase. Therefore, recrystallization is preferably carried out in the presence of readily soluble calcium salts: Ca(N0 3 ) 2 , CaX 2 (where X is CI, Br, I), Ca(C10 4 ) 2 , CaSiF 6 etc. The concentration of calcium salt is selected to allow: a) proceeding recrystallization of phosphogypsum (increasing calcium concentration makes dihydrate formation thermodynamically less favorable); and b) full recovering of the rare earth metals (as it is shown in the Examples below, increasing calcium concentration increases recovery rate). Use of CaCl 2 and Ca(N03) 2 at concentration of 10-300 g/L and 10-500 g/L, respectively, is especially preferred (0.075 - 3.75 M in terms of Ca 2+ ). The upper limit is determined by item "a" (the possibility of occurrence of recrystallization of hemihydrate), the bottom limit is determined by item "b" (the desired degree of REM extraction from the solid solution).

The duration and temperature of the process is determined by the same demands, such as the possibility of occurrence of recrystallization of hemihydrate into dihydrate and the completeness of recrystallization. The process is preferably carried out at 10-45 °C for 0.5-4.0 hours, most preferably - at 20-30 °C for 1-2 hours.

Conversion of hemihydrate into dihydrate and anhydride into dihydrate is thermodynamically possible, but due to the high stability of the calcium sulphate anhydride, conversion of anhydride into dihydrate takes too much time (under normal conditions the detectable conversion occurs within a few weeks). Conversion of hemihydrate into dihydrate is more preferable, since it occurs quickly.

REM can be precipitated from neutral or subacidic solutions in form of separate phases, such as MLn(S0 4 ) 2 , LnP0 « nH 2 0, LnF3 » nH 2 0, M x Ln y (P0 ) » nH 2 0 etc. Thus, on the second step of the method of the present invention, REM along with calcium phosphates and calcium fluoride is dissolved by strong acid. The term "strong acid" includes HX (where X is CI, Br, I), H 0 3 , H 2 S0 4 etc.

Ca x (P0 4 ) y F z + n H + → x Ca 2+ + y H 3 P0 4 + z HF.

LnP0 4 + 3H + → La 3+ + H 3 P0 4 .

MLn(S0 ) 2 + 4H + → Ln 3+ + M + + 2H 2 S0 .

The concentration of acid is selected to allow complete dissolution of REM along with phosphorus, fluoride, alkali metal impurities (as it is shown in the Examples below, increase of acid concentration increases recovery rate). Use of HC1 and HNO3 at concentration of 5-250 g/L and 5-300 g/L, respectively, (0,2-8 M in terms of H + ) is especially preferred. If all the above conditions are fulfilled, the degree of extraction of REM in the solution is up to 95%, a residual content of phosphorus, fluorine and alkali metal impurities in calcium sulphate dihydrate does not exceed 0.3 wt.%, 0.1 wt.%, and 0.05 wt.%, respectively.

Isolation of REM concentrate from an aqueous solution is described in the literature (e.g. Chemistry and technology of rare and trace elements. Part 2. Ed. Bolshakov .A., Moscow, High School, 1976, p. 360 (rus)) and is not the subject of the present invention. As an example, the process comprising precipitation of REM from sulphuric acid solution with sodium sulphate (RU patent 2293781) or the process comprising acid neutralization followed by precipitation of REM in form of phosphate-fluorine salt (RU patent 2109686) can be used.

Thus, the overall recovery of REM from phosphogypsum into the concentrate according to the present invention is up to 95%.

The present invention is explained in more detail below using exemplary embodiments, serving solely for illustrative purposes and not intended to limit the scope of the present invention defined by the appended claims.

Examples 1-3.

Recrystallization CaSO 4 » 0,5 H2O + 1 ,5 H2O→ CaS0 4 * 2 Η 2 0 was carried out under the following conditions: temperature - 20-45 °C, total time of crystallization - 3 hours, the weight ratio of the solution (L, liquid) and loaded hemihydrate (S, solid), L/S = 3/1. Recrystallization was carried out by continuously stirring the suspension.

At the end of the recrystallization process, precipitate of dihydrate of calcium sulphate was filtered and washed out.

Then, resulted precipitate was treated with nitric acid solution for 1 hour at temperature 20-45 °C, the weight ratio of the solution (L, liquid) and loaded dihydrate (S, solid), L/S = 3/1. The treatment was carried out by continuously stirring the suspension.

Table 1 shows the composition of the initial hemihydrate and the resulting recrystallized dihydrate after acidic treatment.

Examples 4-5.

Recrystallization CaSO . 0,5H 2 O + 1 ,5 H 2 0→ CaS0 4 .2 H 2 0 in y% CaCl 2 solutions was carried out under the following conditions: temperature - 20-45 °C, total time of crystallization - 3 hours, the weight ratio of the solution (L, liquid) and loaded hemihydrate (S, solid), L/S = 3/1. Recrystallization was carried out by continuously stirring the suspension.

At the end of the recrystallization process, precipitate of dihydrate of calcium sulphate was filtered and washed out.

Then, resulted precipitate was treated with 4% nitric acid solution for 1 hour at temperature 20-45 °C, the weight ratio of the solution (L, liquid) and loaded dihydrate (S, solid), L/S = 3/1. The treatment was carried out by continuously stirring the suspension.

Table 2 shows the composition of the initial hemihydrate and the resulting recrystallized dihydrate after acidic treatment.

Examples 6-7.

Recrystallization CaS0 4 » 0,5 H 2 0 + 1,5 H 2 0→ CaS0 4 » 2 H 2 0 in solutions of nitric and hydrochloric acids without additional salts was carried out under the following conditions: temperature - 20-22 °C, total time of crystallization - 3 hours, the weight ratio of the solution (L, liquid) and loaded hemihydrate (S, solid), L/S = 3/1. Recrystallization was carried out by continuously stirring the suspension.

At the end of the recrystallization process, precipitate of dihydrate of calcium sulphate was filtered and washed out.

Table 3 shows the composition of the initial hemihydrate and the resulting recrystallized dihydrate after acidic treatment.

As can be seen from the data in Tables 1 -3, recrystallization in the presence of calcium salts yields much higher extraction of REM into solution (up to 95%), then recrystallization without calcium salts (up to 50%).

While the present invention is described in detail above, one skilled in the art will recognize that modifications and equivalent substitutions can be made, and such modifications and substitutions are within the scope of the present invention defined by the appended claims. Table!.

Table 2

Table 3