COMPOSITION

Related Applications

[0001] The present application claims priority to U.S. Provisional

Applications Serial Nos. 61/559,851 , filed on November 15, 2011 , and 61/641 ,397, filed on May 2, 2012, which are incorporated herein in their entirety by reference thereto.

Background of the Invention

[0002] Electrical components often contain molded parts that are formed from a liquid crystalline, thermoplastic resin. Recent demands on the electronic industry have dictated a decreased size of such components to achieve the desired performance and space savings. Unfortunately, however, it is often difficult to adequately fill a mold cavity of a small dimension (e.g., width or thickness) with a liquid crystalline polymer. Even when filling is accomplished, the mechanical strength of the resulting part is sometimes poor. In response to such problems, milled glass powder has been mixed with the liquid crystalline polymer in an effort to improve its strength properties. However, this considerably raises the price of the electrical component and is generally undesirable. As such, a need exists for a liquid crystalline thermoplastic composition that can readily fill mold cavities of a small dimension, and yet still attain good mechanical properties.

Summary of the Invention

[0003] In accordance with one embodiment of the present invention, a method for forming a liquid crystalline thermoplastic composition within an extruder is disclosed. The extruder contains at least one rotatable screw within a barrel, wherein the screw has a total length and diameter and wherein a feed section and melt section located downstream from the feed section are defined along the length of the screw. The method comprises supplying at least one thermotropic liquid crystalline polymer to the feed section of the extruder; supplying a plurality of fibers to the feed section of the extruder at a location downstream from the thermotropic liquid crystalline polymer, wherein the fibers have a volume average length of from about 1 ,000 micrometers to about 5,000 micrometers; and blending the fibers and the liquid crystalline polymer within the extruder to form the liquid crystalline thermoplastic composition. The volume average length of the fibers in the composition is from about 40% to about 95% less than the volume average length of the fibers supplied to the feed section of the extruder.

[0004] In accordance with another embodiment of the present invention, a molded part is disclosed that comprises a liquid crystalline thermoplastic

composition. The composition comprises from about 20 wt.% to about 90 wt.% of at least one thermotropic liquid crystalline polymer and from about 2 wt.% to about 40 wt.% of relatively short fibers having a volume average length of from about 50 to about 400 micrometers and wherein at least about 70% by volume of the relatively short fibers have a length of from about 50 to about 400 micrometers. The composition is formed by a method that comprises supplying at least one thermotropic liquid crystalline polymer to a feed section of an extruder, the extruder containing at least one rotatable screw within a barrel; supplying a plurality of relatively long fibers to the feed section of the extruder at a location downstream from the thermotropic liquid crystalline polymer; and blending the relatively long fibers and the liquid crystalline polymer within the extruder to form the composition that contains the relatively short fibers.

[0005] Other features and aspects of the present invention are set forth in greater detail below.

Brief Description of the Figures

[0006] A full and enabling disclosure of the present invention, including the best mode thereof to one skilled in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures, in which:

[0007] Fig. 1 is an exploded perspective view of one embodiment of a fine pitch electrical connector that may be formed according to the present invention;

[0008] Fig. 2 is a front view of opposing walls of the fine pitch electrical connector of Fig. 1 ;

[0009] Fig. 3 is a schematic illustration of one embodiment of an extruder screw that may be used to form the thermoplastic composition of the present invention; [0010] Figs. 4-5 are graphs of the fiber length distribution for Samples 1 -3 of Example 1 ;

[0011] Figs. 6-12 are graphs of the fiber length distribution for Samples 4-9 of Example 2;

[0012] Figs. 3-20 are graphs of the fiber length distribution for Samples 10- 17 of Example 3;

[0013] Figs. 21-22 are respective front and rear perspective views of an electronic component that can employ an antenna structure formed in accordance with one embodiment of the present invention; and

[0014] Figs. 23-24 are perspective and front views of a compact camera module ("CCM") that may be formed in accordance with one embodiment of the present invention.

Detailed Description

[0015] It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention.

[0016] Generally speaking, the present invention is directed to a method for forming a liquid crystalline thermoplastic composition that comprises blending at least one thermotropic liquid crystalline polymer and a plurality of fibers within an extruder. The extruder contains at least one rotatable screw received within a barrel (e.g., cylindrical barrel) and defines a feed section and a melting section located downstream from the feed section along the length of the screw.

Relatively long fibers are initially supplied to the feed section of the extruder, but at a location downstream from the liquid crystalline polymer so that the polymer is still in a solid state when it initially contacts the fibers. In this manner, the present inventors have discovered that the polymer can act as an abrasive agent for reducing the length of the fibers. For example, the fibers in the composition may be relatively short, such as about 40% to about 95%, in some embodiments from about 45% to about 90%, and in some embodiments, by about 50% to about 80% less In volume average length than the fibers supplied to the extruder. The present inventors have discovered that such an in situ fiber length reduction is efficient and economical, and can result in a thermoplastic composition having a desirable combination of strength and flowability. [0017] The extruder may be a single screw or twin screw extruder.

Referring to Fig. 3, for example, one embodiment of a single screw extruder 80 is shown that contains a housing or barrel 114 and a screw 120 rotatably driven on one end by a suitable drive 124 (typically including a motor and gearbox). If desired, a twin-screw extruder may be employed that contains two separate screws. The configuration of the screw is not particularly critical to the present invention and it may contain any number and/or orientation of threads and channels as is known in the art. As shown in Fig. 3, for example, the screw 120 contains a thread that forms a generally helical channel radially extending around a core of the screw 120. A hopper 40 is located adjacent to the drive 124 for supplying the liquid crystalline polymer and/or other materials through an opening in the barrel 114 to the feed section 132. Opposite the drive 124 is the output end

144 of the extruder 80, where extruded plastic is output for further processing.

[0018] A feed section 132 and melt section 134 are defined along the length of the screw 120. The feed section 32 is the input portion of the barrel 114 where the liquid crystalline polymer and fibers are added. The melt section 134 is the phase change section in which the liquid crystalline polymer is changed from a solid to a liquid. While there is no precisely defined delineation of these sections when the extruder is manufactured, it is well within the ordinary skill of those in this art to reliably identify the feed section 132 and the melt section 34 in which phase change from solid to liquid is occurring. Although not necessarily required, the extruder 80 may also have a mixing section 136 that is located adjacent to the output end of the barrel 114 and downstream from the melting section 134. If desired, one or more distributive and/or dispersive mixing elements may be employed within the mixing and/or melting sections of the extruder. Suitable distributive mixers for single screw extruders may include, for instance, Saxon,

Dulmage, Cavity Transfer mixers, etc. Likewise, suitable dispersive mixers may include Blister ring, Leroy/ addock, CRD mixers, etc. As is well known in the art, the mixing may be further improved by using pins in the barrel that create a folding and reorientation of the polymer melt, such as those used in Buss Kneader extruders, Cavity Transfer mixers, and Vortex Intermeshing Pin mixers.

[0019] Regardless of their particular configuration, one or more of the sections of the extruder are typically heated, such as within a temperature range of from about 200°C to about 450°C, in some embodiments, from about 220°C to about 400°C, and in some embodiments, from about 250°C to about 350°C to form the thermoplastic composition.

[0020] As noted above, the fibers are added a location downstream from the point at which the liquid crystalline polymer is supplied (e.g., hopper 40), but yet prior to the melting section. In Fig. 3, for instance, a hopper 42 is shown that is located within a zone of the feed section 132 of the extruder 80. The fibers supplied to the hopper 42 are initially relatively long, such as having a volume average length of from about 1 ,000 to about 5,000 micrometers, in some embodiments from about 2,000 to about 4,500 micrometers, and in some embodiments, from about 3,000 to about 4,000 micrometers. Nevertheless, by supplying these long fibers at a location where the liquid crystalline polymer is still in a solid state, the present inventors have discovered that the polymer can act as an abrasive agent for reducing the volume average length of the fibers within the extruder to a certain size. For instance, the fibers may be reduced to a volume average length of from about 50 to about 400 micrometers, in some embodiments from about 80 to about 250 micrometers, in some embodiments from about 100 to about 200 micrometers, and in some embodiments, from about 110 to about 180 micrometers.

[0021] Regardless of the actual size to which the fibers are reduced, the present inventors have found that the length reduction is consistent throughout the composition, which can result in a narrow length distribution. That is, at least about 70% by volume of the fibers, in some embodiments at least about 80% by volume of the fibers, and in some embodiments, at least about 90% by volume of the fibers have a length within the range of from about 50 to about 400

micrometers, in some embodiments from about 80 to about 250 micrometers, in some embodiments from about 00 to about 200 micrometers, and in some embodiments, from about 110 to about 180 micrometers. Without intending to be limited by theory, the present inventors believe that the combination of a reduced length and narrow length distribution can improve the strength of the resulting part and the uniformity of its properties, which can result in improved dimensional stability. [0022] To help control the degree to which the length of the fibers are reduced during extrusion, a variety of different parameters may be selectively controlled. For example, the ratio of the total length ("L") of the screw to its diameter ("D") may be selected to achieve an optimum balance between

throughput and fiber length reduction. The L/D value may, for instance, range from about 15 to about 50, in some embodiments from about 20 to about 45, and in some embodiments from about 25 to about 40. The length of the screw may, for instance, range from about 0.1 to about 5 meters, in some embodiments from about 0.4 to about 4 meters, and in some embodiments, from about 0.5 to about 2 meters. The diameter of the screw may likewise be from about 5 to about 150 millimeters, in some embodiments from about 10 to about 120 millimeters, and in some embodiments, from about 20 to about 80 millimeters. Perhaps even more important than the total L/D ratio of the screw is the ratio of the length of the screw after the point at which the fibers are supplied to the diameter. More particularly, the screw has a blending length ("L _B ") that is defined from the point at which the fibers are supplied to the extruder to the end of the screw, the blending length being less than the total length of the screw. As noted above, it is desirable to add the fibers before the liquid crystalline polymer is melted, which means that the LB/D ratio would be relatively high. However, too high of a L _B /D ratio could result in degradation of the polymer. Therefore, the LB/D ratio of the screw after the point at which the fibers are supplied is typically from about 4 to about 20, in some embodiments from about 5 to about 15, and in some embodiments, from about 6 to about 10.

[0023] In addition to the length and diameter, other aspects of the extruder may also be selected to achieve the desired fiber length. For example, the speed of the screw may be selected to achieve the desired residence time, shear rate, melt processing temperature, etc. Generally, an increase in frictional energy results from the shear exerted by the turning screw on the materials within the extruder and results in the fracturing of the fibers. The degree of fracturing may depend, at least in part, on the screw speed. For example, the screw speed may range from about 50 to about 200 revolutions per minute ("rpm"), in some embodiments from about 70 to about 150 rpm, and in some embodiments, from about 80 to about 20 rpm. The apparent shear rate during melt blending may also range from about 100 seconds ^"1 to about 10,000 seconds ^"1 , in some embodiments from about 500 seconds ^"1 to about 5000 seconds ^"1 , and in some embodiments, from about 800 seconds ^"1 to about 1200 seconds ^"1 . The apparent shear rate is equal to 4Q/ R ³ , where Q is the volumetric flow rate ("m ³ /s") of the polymer melt and R is the radius ("m") of the capillary (e.g., extruder die) through which the melted polymer flows.

[0024] The fibers used in the thermoplastic composition generally have a high degree of tensile strength relative to their mass. For example, the ultimate tensile strength of the fibers (determined in accordance with ASTM D2 01 ) is typically from about 1 ,000 to about 15,000 Megapascals ("MPa"), in some embodiments from about 2,000 MPa to about 10,000 MPa, and in some embodiments, from about 3,000 MPa to about 6,000 MPa. To help maintain an insulative property, which is often desirable for use in electronic components, the high strength fibers may be formed from materials that are also generally insulative in nature, such as glass, ceramics (e.g., alumina or silica), aramids (e.g., Kevlar® marketed by E. I. DuPont de Nemours, Wilmington, Delaware), polyolefins, polyesters, etc., as well as mixtures thereof. Glass fibers are particularly suitable, such as E-glass, A-glass, C-glass, D-glass, AR-glass, R- glass, S1 -glass, S2-glass, etc., and mixtures thereof. In addition to possessing the length characteristics noted above, the fibers may also have a relatively high aspect ratio (average length divided by nominal diameter) to help improve the mechanical properties of the resulting thermoplastic composition. For example, the fibers may have an aspect ratio of from about 2 to about 50, in some embodiments from about 4 to about 40, and in some embodiments, from about 5 to about 20 are particularly beneficial. The fibers may, for example, have a nominal diameter of about 0 to about 35 micrometers, and in some

embodiments, from about 15 to about 30 micrometers.

[0025] The relative amount of the fibers in the thermoplastic composition is also selectively controlled to help achieve the desired mechanical properties without adversely impacting other properties of the composition, such as its flowability. For example, the fibers typically constitute from about 2 wt.% to about 40 wt.%, in some embodiments from about 5 wt.% to about 35 wt.%, and in some embodiments, from about 6 wt.% to about 30 wt.% of the thermoplastic

composition. Although the fibers may be employed within the ranges noted above, one particularly beneficial and surprising aspect of the present invention is that small fiber contents may be employed while still achieving the desired mechanical properties. Without intending to be limited by theory, it is believed that the narrow length distribution of the fibers can help achieve excellent mechanical properties, thus allowing for the use of a smaller amount of fibers. For example, the fibers can be employed in small amounts such as from about 2 wt.% to about 20 wt.%, in some embodiments, from about 5 wt.% to about 16 wt.%, and in some

embodiments, from about 6 wt.% to about 12 wt.%.

[0026] The thermotropic liquid crystalline polymer that is blended with the fibers generally has a high degree of crystallinity that enables it to effectively fill the small spaces of a mold. The amount of such liquid crystalline polymers is typically from about 20 wt.% to about 90 wt.%, in some embodiments from about 30 wt.% to about 80 wt.%, and in some embodiments, from about 40 wt.% to about 75 wt.% of the thermoplastic composition. Suitable thermotropic liquid crystalline polymers may include aromatic polyesters, aromatic poly(esteramides), aromatic

poly(estercarbonates), aromatic polyamides, etc., and may likewise contain repeating units formed from one or more aromatic hydroxycarboxylic acids, aromatic dicarboxylic acids, aromatic diols, aromatic aminocarboxylic acids, aromatic amines, aromatic diamines, etc., as well as combinations thereof.

[0027] Aromatic polyesters, for instance, may be obtained by polymerizing

(1 ) two or more aromatic hydroxycarboxylic acids; (2) at least one aromatic hydroxycarboxylic acid, at least one aromatic dicarboxylic acid, and at least one aromatic diol; and/or (3) at least one aromatic dicarboxylic acid and at least one aromatic diol. Examples of suitable aromatic hydroxycarboxylic acids include, 4- hydroxybenzoic acid; 4-hydroxy-4'-biphenylcarboxylic acid; 2-hydroxy-6-naphthoic acid; 2-hydroxy-5-naphthoic acid; 3-hydroxy-2-naphthoic acid; 2-hydroxy-3- naphthoic acid; 4'-hydroxyphenyl-4-benzoic acid; 3'-hydroxyphenyl-4-benzoic acid;

4'-hydroxyphenyl-3-benzoic acid, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. Examples of suitable aromatic dicarboxylic acids include terephthalic acid; isophthalic acid; 2,6-naphthalenedicarboxylic acid; diphenyl ether-4,4'-dicarboxylic acid; 1 ,6-naphthalenedicarboxylic acid; 2,7- naphthalenedicarboxylic acid; 4,4'-dicarboxybiphenyl; bis(4-carboxyphenyl)ether; bis(4-carboxyphenyl)butane; bis(4-carboxyphenyl)ethane; bis(3- carboxyphenyl)ether; bis(3-carboxypheny[)ethane, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. Examples of suitable aromatic diols include hydroquinone; resorcinol; 2,6-dihydroxynaphthalene; 2,7-dihydroxynaphthalene;

1 ,6-dihydroxynaphthalene; 4,4'-dihydroxybiphenyl; 3,3'-dihydroxybiphenyl; 3,4'- dihydroxybiphenyl; 4,4'-dihydroxybiphenyl ether; bis(4-hydroxyphenyi)ethane, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof.

[0028] In one particular embodiment, the aromatic polyester contains monomer repeat units derived from 4-hydroxybenzoic acid ("HBA") and 2,6- hydroxynaphthoic acid ("HNA") and/or 2, 6-naphthalenedicarboxylic acid (" DA"), as well as other optional repeat units, such as terephthalic acid ("TA") and/or isophthalic acid ("IA"); hydroquinone ("HQ"), 4,4-biphenol ("BP"), and/or acetaminophen ("APAP"); etc., as well as a combination thereof. The monomer units derived from HBA may constitute from about 40% to about 75% of the polymer on a mole basis and the monomer units derived from HNA and/or NDA may constitute from about 1 % to about 25% of the polymer on a mole basis. The monomer units derived from TA and/or IA may constitute from about 2% to about

25% of the polymer on a mole basis. Likewise, the monomer units derived from

HQ, BP, and/or APAP may constitute from about 10% to about 35% of the polymer on a mole basis. Suitable aromatic polyesters are commercially available from Ticona, LLC under the trade designation VECTRA® A. The synthesis and structure of these and other aromatic polyesters may be described in more detail in

U.S. Patent Nos. 4,161 ,470; 4,473,682; 4,522,974; 4,375,530; 4,318,841 ;

4,256,624; 4,219,461 ; 4,083,829; 4,184,996; 4,279,803; 4,337,190; 4,355,134;

4,429,105; 4,393,191 ; 4,42 ,908; 4,434,262; and 5,541 ,240.

[0029] Liquid crystalline polyesteramides may likewise be obtained by polymerizing (1 ) at least one aromatic hydroxycarboxylic acid and at least one aromatic aminocarboxylic acid; (2) at least one aromatic hydroxycarboxylic acid, at least one aromatic dicarboxylic acid, and at least one aromatic amine and/or diamine optionally having phenolic hydroxy groups; and (3) at !east one aromatic dicarboxylic acid and at least one aromatic amine and/or diamine optionally having phenolic hydroxy groups. Suitable aromatic amines and diamines may include, for instance, 3-aminophenol; 4-aminophenol; 1 ,4-phenyienecliamine; 1 ,3- phenylenediamine, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. In one particular embodiment, the aromatic polyesteramide contains monomer units derived from 2,6-hydroxynaphthoic acid, terephthalic acid, and 4- aminophenol. The monomer units derived from 2,6-hydroxynaphthoic acid may constitute from about 35% to about 85% of the polymer on a mole basis (e.g., 60%), the monomer units derived from terephthalic acid may constitute from about 5% to about 50% (e.g., 20%) of the polymer on a mole basis, and the monomer units derived from 4-aminophenol may constitute from about 5% to about 50% (e.g., 20%) of the polymer on a mole basis. Such aromatic polyesters are commercially available from Ticona, LLC under the trade designation

VECTRA® B. In another embodiment, the aromatic polyesteramide contains monomer units derived from 2,6-hydroxynaphthoic acid, and 4-hydroxybenzoic acid, and 4-aminophenol, as well as other optional monomers (e.g., 4,4'- dihydroxybiphenyl and/or terephthalic acid). The synthesis and structure of these and other aromatic poly(esteramides) may be described in more detail in U.S.

Patent Nos. 4,339,375; 4,355,132; 4,351 ,917; 4,330,457; 4,351 ,918; and

5,204,443.

[0030] The liquid crystalline polymers may be prepared by introducing the appropriate monomer(s) (e.g., aromatic hydroxycarboxylic acid, aromatic

dicarboxylic acid, aromatic diol, aromatic amine, aromatic diamine, etc.) into a reactor vessel to initiate a polycondensation reaction. The particular conditions and steps employed in such reactions are well known, and may be described in more detail in U.S. Patent No. 4,161 ,470 to Calundann; U.S. Patent No. 5,616,680 to Linstid, III, et al.; U.S. Patent No. 6,114,492 to Linstid, Ill, et al.: U.S. Patent No. 6,514,611 to Shepherd, et al.: and WO 2004/058851 to Waggoner, which are incorporated herein in their entirety by reference thereto for all relevant purposes. The vessel employed for the reaction is not especially limited, although it is typically desired to employ one that is commonly used in reactions of high viscosity fluids. Examples of such a reaction vessel may include a stirring tank- type apparatus that has an agitator with a variably-shaped stirring blade, such as an anchor type, multistage type, spiral-ribbon type, screw shaft type, etc., or a modified shape thereof. Further examples of such a reaction vessel may include a mixing apparatus commonly used in resin kneading, such as a kneader, a roll mill, a Banbury mixer, etc.

[0031] If desired, the reaction may proceed through the acetylation of the monomers as referenced above and known the art. This may be accomplished by adding an acetylating agent (e.g., acetic anhydride) to the monomers. Acetylation is generally initiated at temperatures of about 90°C. During the initial stage of the acetylation, reflux may be employed to maintain vapor phase temperature below the point at which acetic acid byproduct and anhydride begin to distill.

Temperatures during acetylation typically range from between 90°C to 150°C, and in some embodiments, from about 110°C to about 150°C. If reflux is used, the vapor phase temperature typically exceeds the boiling point of acetic acid, but remains low enough to retain residual acetic anhydride, For example, acetic anhydride vaporizes at temperatures of about 140°C. Thus, providing the reactor with a vapor phase reflux at a temperature of from about 1 10°C to about 130°C is particularly desirable. To ensure substantially complete reaction, an excess amount of acetic anhydride may be employed. The amount of excess anhydride will vary depending upon the particular acetylation conditions employed, including the presence or absence of reflux. The use of an excess of from about 1 to about 10 mole percent of acetic anhydride, based on the totai moles of reactant hydroxyl groups present is not uncommon.

[0032] Acetylation may occur in a separate reactor vessel, or it may occur in situ within the polymerization reactor vessel. When separate reactor vessels are employed, one or more of the monomers may be introduced to the acetylation reactor and subsequently transferred to the polymerization reactor. Likewise, one or more of the monomers may also be directly introduced to the reactor vessel without undergoing pre-acetylation.

[0033] In addition to the monomers and optional acetylating agents, other components may also be included within the reaction mixture to help facilitate polymerization. For instance, a catalyst may be optionally employed, such as metal salt catalysts (e.g., magnesium acetate, tin(l) acetate, tetrabutyl titanate, lead acetate, sodium acetate, potassium acetate, etc.) and organic compound catalysts (e.g., N-methylimidazole). Such catalysts are typically used in amounts of from about 50 to about 500 parts per million based on the total weight of the recurring unit precursors. When separate reactors are employed, it is typically desired to apply the catalyst to the acetylation reactor rather than the

polymerization reactor, although this is by no means a requirement.

[0034] The reaction mixture is generally heated to an elevated temperature within the polymerization reactor vessel to initiate melt polycondensation of the reactants. Polycondensation may occur, for instance, within a temperature range of from about 210°C to about 400°C, and in some embodiments, from about 250°C to about 350°C. For instance, one suitable technique for forming an aromatic polyester may include charging precursor monomers (e.g., 4- hydroxybenzoic acid and 2,6-hydroxynaphthoic acid) and acetic anhydride into the reactor, heating the mixture to a temperature of from about 90°C to about 50°C to acetylize a hydroxyl group of the monomers (e.g., forming acetoxy), and then increasing the temperature to a temperature of from about 210°C to about 400°C to carry out melt polycondensation. As the final polymerization temperatures are approached, volatile byproducts of the reaction (e.g., acetic acid) may also be removed so that the desired molecular weight may be readily achieved. The reaction mixture is generally subjected to agitation during polymerization to ensure good heat and mass transfer, and in turn, good material homogeneity. The rotational velocity of the agitator may vary during the course of the reaction, but typically ranges from about 10 to about 100 revolutions per minute ("rpm"), and in some embodiments, from about 20 to about 80 rpm. To build molecular weight in the melt, the polymerization reaction may also be conducted under vacuum, the application of which facilitates the removal of volatiles formed during the final stages of polycondensation. The vacuum may be created by the application of a suctional pressure, such as within the range of from about 5 to about 30 pounds per square inch ("psi"), and in some embodiments, from about 10 to about 20 psi.

[0035] Following melt polymerization, the molten polymer may be discharged from the reactor, typically through an extrusion orifice fitted with a die of desired configuration, cooled, and collected. Commonly, the melt is

discharged through a perforated die to form strands that are taken up in a water bath, pelletized and dried. The resin may also be in the form of a strand, granule, or powder. While unnecessary, it should also be understood that a subsequent solid phase polymerization may be conducted to further increase molecular weight. When carrying out solid-phase polymerization on a polymer obtained by melt polymerization, it is typically desired to select a method in which the polymer obtained by melt polymerization is solidified and then pulverized to form a powdery or flake-like polymer, followed by performing solid polymerization method, such as a heat treatment in a temperature range of 200°C to 350°C under an inert atmosphere (e.g., nitrogen).

[0036] Regardless of the particular method employed, the resulting liquid crystalline polymer typically may have a high number average molecular weight (Mn) of about 2,000 grams per mole or more, in some embodiments from about 4,000 grams per mole or more, and in some embodiments, from about 5,000 to about 30,000 grams per mole. Of course, it is also possible to form polymers having a lower molecular weight, such as less than about 2,000 grams per mole, using the method of the present invention. The intrinsic viscosity of the polymer, which is generally proportional to molecular weight, may also be relatively high. For example, the intrinsic viscosity may be about about 4 deciliters per gram ("dL/g") or more, in some embodiments about 5 dL/g or more, in some

embodiments from about 6 to about 20 dL/g, and in some embodiments from about 7 to about 15 dL/g. Intrinsic viscosity may be determined in accordance with ISO-1628-5 using a 50/50 (v/v) mixture of pentafluorophenol and

hexafluoroisopropanol.

[0037] In addition to the components noted above, still other additives that can be included in the composition may include, for instance, antimicrobials, fillers, pigments, antioxidants, stabilizers, surfactants, waxes, flow promoters, solid solvents, and other materials added to enhance properties and

processability. For example, mineral fillers may be employed in the thermoplastic composition to help achieve the desired mechanical properties and/or appearance.

When employed, such mineral fillers typically constitute from about 1 wt.% to about

40 wt.%, in some embodiments from about 2 wt.% to about 35 wt.%, and in some embodiments, from about 5 wt.% to about 30 wt.% of the thermoplastic

composition. Clay minerals may be particularly suitable for use in the present invention. Examples of such clay minerals include, for instance, talc

(Mg ₃ Si ₄ Oio(OH) ₂ ), halloysite (AI ₂ Si ₂ O ₅ {OH)4), kaolinite (AI ₂ Si ₂ O ₅ (OH) ₄ ), illite ({K,H ₃ 0)(AI,Mg,Fe) ₂ (Si,AI)40io[(OH) _2> (H ₂ 0)]) ₁ montmorillonite

(Na,Ca)o.33(AI,Mg) ₂ Si ₄ 0 ₁ o(OH)2 iH ₂ 0) _l vermicuiite ((MgFe,AI) ₃ (AI,Si) ₄ Oi ₀ (OH) ₂ - 4H ₂ 0), palygorskite ((Mg,AI) ₂ Si ₄ O ₁₀ (OH)-4{H ₂ O)), pyrophyllite (AI ₂ Si ₄ Oi ₀ (OH) ₂ ), etc., as well as combinations thereof. In lieu of, or in addition to, clay minerals, stiil other mineral fillers may also be employed. For example, other suitable silicate fillers may also be employed, such as calcium silicate, aluminum silicate, mica, diatomaceous earth, wollastonite, and so forth. Mica, for instance, may be particularly suitable. There are several chemically distinct mica species with considerable variance in geologic occurrence, but all have essentially the same crystal structure. As used herein, the term "mica" is meant to generically include any of these species, such as muscovite (KAI ₂ (AISi ₃ )Oio(OH) ₂ ), biotite

(K(Mg,Fe)3(AISi ₃ )O ₁₀ (OH) ₂ ), phlogopite (KMg ₃ (AISi ₃ )0 ₁ o(OH) ₂ ) _l lepidolite (K(Li,AI) _{2- 3} {AiSi3)O ₀ {OH)2), glauconite (K,Na)(AI,Mg,Fe}2(Si,AI) ₄ O ₁₀ (OH) ₂ ), etc., as well as combinations thereof.

[0038] Lubricants may also be employed in the thermoplastic composition that are capable of withstanding the processing conditions of the liquid crystalline polymer without substantial decomposition. Examples of such lubricants include fatty acids esters, the salts thereof, esters, fatty acid amides, organic phosphate esters, and hydrocarbon waxes of the type commonly used as lubricants in the processing of engineering plastic materials, including mixtures thereof. Suitable fatty acids typically have a backbone carbon chain of from about 12 to about 60 carbon atoms, such as myristic acid, palmitic acid, stearic acid, arachic acid, montanic acid, octadecinic acid, parinric acid, and so forth. Suitable esters include fatty acid esters, fatty alcohol esters, wax esters, glycerol esters, glycol esters and complex esters. Fatty acid amides include fatty primary amides, fatty secondary amides, methylene and ethylene bisamides and alkanolamides such as, for example, palmitic acid amide, stearic acid amide, oleic acid amide, ΙΜ,Ν'- ethylenebisstearamide and so forth. Also suitable are the metal salts of fatty acids such as calcium stearate, zinc stearate, magnesium stearate, and so forth;

hydrocarbon waxes, including paraffin waxes, polyolefin and oxidized polyolefin waxes, and microcrystalline waxes. Particularly suitable lubricants are acids, salts, or amides of stearic acid, such as pentaerythritol tetrastearate, calcium stearate, or

Ν,Ν'-ethylenebisstearamide. When employed, the lubricant(s) typically constitute from about 0.05 wt.% to about 1.5 wt.%, and in some embodiments, from about 0.1 wt.% to about 0.5 wt.% (by weight) of the thermoplastic composition.

[0039] The melt viscosity of the resulting thermoplastic composition is generally low enough so that it can readily flow into the cavity of a mold having small dimensions. For example, in one particular embodiment, the thermoplastic composition may have a melt viscosity of from about 0.5 to about 100 Pa-s, in some embodiments from about 1 to about 80 Pa-s, and in some embodiments, from about 5 to about 50 Pa-s, determined at a shear rate of 1000 seconds ^"1 . Melt viscosity may be determined in accordance with ASTM Test No. 1238-70 at a temperature of 350° C.

[0040] To help achieve the desired melt viscosity, one or more functional compounds may be employed as flow modifiers that interact with the liquid crystalline polymer to reduce its melt viscosity. The functional compounds used herein may be mono-, di-, tri-functional, etc., and may contain one or more reactive functional groups, such as hydroxyl, carboxyl, carboxylate, ester, and primary or secondary amines. Hydroxy-functional compounds are particularly suitable flow modifiers as they contain hydroxyl functional groups that can react with the polymer chain to shorten its length and thus reduce melt viscosity. When employed, such hydroxy-functional compounds typically constitute from about 0.05 wt.% to about 4 wt.% of the thermoplastic composition. One example of such a hydroxyl-functional compound is an aromatic diol, such as hydroquinone, resorcinol, 4,4'-bipheno[, etc., as well as combinations thereof. Such aromatic diols may constitute from about 0.01 wt.% to about 1 wt.%, and in some

embodiments, from about 0.05 wt.% to about 0.4 wt.% of the thermoplastic composition. Water is also a suitable hydroxyl-functional compound, and can be used alone or in combination with other hydroxyl-functional compounds. If desired, water can be added in a form that under process conditions generates water. For example, the water can be added as a hydrate that under the process conditions

(e.g., high temperature) effectively "loses" water. Such hydrates include alumina trihydrate, copper sulfate pentahydrate, barium chloride dihydrate, calcium sulfate dehydrate, etc., as well as combinations thereof. When employed, the hydrates may constitute from about 0.02 wt.% to about 2 wt.%, and in some embodiments, from about 0.05 wt.% to about 1 wt.% of the thermoplastic composition. [0041] In addition to those noted above, still other functional compounds may also be employed as flow modifiers in the thermoplastic composition. For instance, aromatic dicarboxyiic acids can be employed that generally act to combine smaller chains of the polymer together after they have been cut by other types of functional compounds. This maintains the mechanical properties of the composition even after its melt viscosity has been reduced. Suitable aromatic dicarboxyiic acids for this purpose may include, for instance, terephthalic acid, 2,6- napthalenedicarboxylic acid, isophthalic acid, 4,4'-bibenzoic acid, 2- methylterephthalic acid, etc., as well as combinations thereof. When employed, such dicarboxyiic acids typically constitute from about 0.001 wt.% to about 0.5 wt.%, and in some embodiments, from about 0.005 wt.% to about 0.1 wt.% of the thermoplastic composition. In one particular embodiment, the thermoplastic composition of the present invention employs a mixture of an aromatic diol, hydrate, and aromatic dicarboxyiic acid. The present inventors have discovered that this specific combination of ingredients can reduce melt viscosity and improve flow, but without having an adverse impact on mechanical properties. Typically, of the flow modifiers employed in the thermoplastic composition, aromatic diols constitute from about 5 wt.% to about 45 wt.%, hydrates constitutes from about 45 wt.% to about 75 wt.%, and aromatic dicarboxyiic acids constitute from about 1 wt.% to about 15 wt.%.

[0042] Conventionally, it was believed that thermoplastic compositions having such the low viscosity noted above would not also possess sufficiently good thermal and mechanical properties to enable their use in certain types of applications. Contrary to conventional thought, however, the thermoplastic composition of the present invention has been found to possess both excellent thermal and mechanical properties. For example, the composition may possess a high impact strength, which is useful when forming small parts. The composition may, for instance, possess a Charpy notched impact strength greater than about 4 kj/m ² , in some embodiments from about 5 to about 40 kJ/m ² , and in some embodiments, from about 6 to about 30 kJ/m ² , measured at 23°C according to ISO

Test No. 179-1 ) (technically equivalent to ASTM D256, Method B). The tensile and flexural mechanical properties of the composition are also good. For example, the thermoplastic composition may exhibit a tensile strength of from about 20 to about 500 MPa, in some embodiments from about 50 to about 400 MPa, and in some embodiments, from about 100 to about 350 MPa; a tensile break strain of about 0.5% or more, in some embodiments from about 0.6% to about 10%, and in some embodiments, from about 0.8% to about 3.5%; and/or a tensile modulus of from about 5,000 MPa to about 20,000 MPa, in some embodiments from about 8,000 MPa to about 20,000 MPa, and in some embodiments, from about 10,000 MPa to about 5,000 MPa. The tensile properties may be determined in

accordance with ISO Test No. 527 (technically equivalent to ASTM D638) at 23°C. The thermoplastic composition may also exhibit a flexural strength of from about 20 to about 500 MPa, in some embodiments from about 50 to about 400 MPa, and in some embodiments, from about 100 to about 350 MPa; a flexural break strain of about 0.5% or more, in some embodiments from about 0.6% to about 10%, and in some embodiments, from about 0.8% to about 3.5%; and/or a flexural modulus of from about 5,000 MPa to about 20,000 MPa, in some embodiments from about 8,000 MPa to about 20,000 MPa, and in some embodiments, from about 10,000 MPa to about 15,000 MPa. The flexural properties may be determined in accordance with ISO Test No. 178 (technically equivalent to ASTM D790) at 23°C.

[0043] The melting temperature of the composition may likewise be from about 250°C to about 400°C, in some embodiments from about 270°C to about 380°C, and in some embodiments, from about 300°C to about 360°C. The melting temperature may be determined as is well known in the art using differential scanning calorimetry ("DSC"), such as determined by (SO Test No. 11357. Even at such melting temperatures, the ratio of the deflection temperature under load ("DTUL"), a measure of short term heat resistance, to the melting temperature may still remain relatively high. For example, the ratio may range from about 0.65 to about 1 .00, in some embodiments from about 0.66 to about 0.95, and in some embodiments, from about 0.67 to about 0.85. The specific DTUL values may, for instance, range from about 200°C to about 300°C, in some embodiments from about 210°C to about 280°C, and in some embodiments, from about 215°C to about 260°C. Such high DTUL values can, among other things, allow the use of high speed processes often employed during the manufacture of components having a small dimensional tolerance. [0044] The thermoplastic composition may be molded into any of a variety of different shaped parts using techniques as is known in the art. For example, the shaped parts may be molded using a one-component injection molding process in which dried and preheated plastic granules are injected into the mold. Regardless of the molding technique employed, it has been discovered that the thermoplastic composition of the present invention, which possesses the unique combination of high flowabiiity and good mechanical properties, is particularly well suited for parts having a small dimensional tolerance.

[0045] One such part is a fine pitch electrical connector. More particularly, such electrical connectors are often employed to detachably mount a centra! processing unit ("CPU") to a printed circuit board. The connector may contain insertion passageways that are configured to receive contact pins. These passageways are defined by opposing walls, which may be formed from a thermoplastic resin. To help accomplish the desired electrical performance, the pitch of these pins is generally small to accommodate a large number of contact pins required within a given space. This, in turn, requires that the pitch of the pin insertion passageways and the width of opposing walls that partition those passageways are also small. For example, the walls may have a width of from about 500 micrometers or less, in some embodiments from about 100 to about 450 micrometers, and in some embodiments, from about 200 to about 400 micrometers. In the past, it has often been difficult to adequately fill a mold of such a thin width with a thermoplastic resin. Due to its unique properties, however, the thermoplastic composition of the present invention is particularly well suited to form the walls of a fine pitch connector.

[0046] One particularly suitable fine pitch electrical connector is shown in Fig. 1. An electrical connector 200 is shown that a board-side portion C2 that can be mounted onto the surface of a circuit board P. The connector 200 may also include a wiring material-side portion C1 structured to connect discrete wires 3 to the circuit board P by being coupled to the board-side connector C2. The board- side portion C2 may include a first housing 10 that has a fitting recess 10a into which the wiring material-side connector C1 is fitted and a configuration that is slim and long in the widthwise direction of the housing 10. The wiring material-side portion C1 may likewise include a second housing 20 that is slim and long in the widthwise direction of the housing 20. In the second housing 20, a plurality of terminal-receiving cavities 22 may be provided in parallel in the widthwise direction so as to create a two-tier array including upper and lower terminal- receiving cavities 22. A terminal 5, which is mounted to the distal end of a discrete wire 3, may be received within each of the terminal-receiving cavities 22. If desired, locking portions 28 (engaging portions) may also be provided on the housing 20 that correspond to a connection member (not shown) on the board- side connector C2.

[0047] As discussed above, the interior walls of the first housing 10 and/or second housing 20 may have a relatively small width dimension, and can be formed from the thermoplastic composition of the present invention. The walls are, for example, shown in more detail in Fig. 2. As illustrated, insertion passageways or spaces 225 are defined between opposing walls 224 that can accommodate contact pins. The walls 224 have a width "w" that is within the ranges noted above. When the walls 224 are formed from a thermoplastic composition containing fibers (e.g., element 400), such fibers may have a volume average length and narrow length distribution within a certain range to best match the width of the walls. For example, the ratio of the width of at least one of the walls to the volume average length of the fibers is from about 0.8 to about 3.2, in some embodiments from about 1 ,0 to about 3.0, and in some

embodiments, from about 1.2 to about 2.9.

[0048] In addition to or in lieu of the walls, it should also be understood that any other portion of the housing may also be formed from the thermoplastic composition of the present invention. For example, the connector may also include a shield that encloses the housing. Some or ail of the shield may be formed from the thermoplastic composition of the present invention. For example, the housing and the shield can each be a one-piece structure unitarily molded from the thermoplastic composition. Likewise, the shield can be a two- piece structure that includes a first shell and a second shell, each of which may be formed from the thermoplastic composition of the present invention.

[0049] Of course, the thermoplastic composition may also be used in a wide variety of other components having a small dimensional tolerance. For example, the thermoplastic composition may be molded into a planar substrate for use in an electronic component. The substrate may be thin, such as having a thickness of about 500 micrometers or less, in some embodiments from about 100 to about 450 micrometers, and in some embodiments, from about 200 to about 400 micrometers. Examples of electronic components that may employ such a substrate include, for instance, cellular telephones, laptop computers, small portable computers (e.g., ultraportable computers, netbook computers, and tablet computers), wrist-watch devices, pendant devices, headphone and earpiece devices, media players with wireless communications capabilities, handheld computers (also sometimes called personal digital assistants), remote controllers, global positioning system (GPS) devices, handheld gaming devices, battery covers, speakers, integrated circuits (e.g., SIM cards), etc.

[0050] In one embodiment, for example, the planar substrate may be applied with one or more conductive elements using a variety of known

techniques (e.g., laser direct structuring, electroplating, etc.). The conductive elements may serve a variety of different purposes. In one embodiment, for example, the conductive elements form an integrated circuit, such as those used in SIM cards. In another embodiment, the conductive elements form antennas of a variety of different types, such as antennae with resonating elements that are formed from patch antenna structures, inverted-F antenna structures, closed and open slot antenna structures, loop antenna structures, monopoles, dipoles, planar inverted-F antenna structures, hybrids of these designs, etc. The resulting antenna structures may be incorporated into the housing of a relatively compact portable electronic component, such as described above, in which the available interior space is relatively small.

[0051] One particularly suitable electronic component that includes an antenna structure is shown in Figs. 21 -22 is a handheld device 410 with cellular telephone capabilities. As shown in Fig. 21 , the device 410 may have a housing

412 formed from plastic, metal, other suitable dielectric materials, other suitable conductive materials, or combinations of such materials. A display 414 may be provided on a front surface of the device 4 0, such as a touch screen display. The device 410 may also have a speaker port 440 and other input-output ports. One or more buttons 438 and other user input devices may be used to gather user input.

As shown in Fig. 22, an antenna structure 426 is also provided on a rear surface 442 of device 410, although it should be understood that the antenna structure can generally be positioned at any desired location of the device. As indicated above, the antenna structure 426 may contain a planar substrate that is formed from the thermoplastic composition of the present invention. The antenna structure may be electrically connected to other components within the electronic device using any of a variety of known techniques. For example, the housing 412 or a part of housing 412 may serve as a conductive ground plane for the antenna structure 426.

[0052] A planar substrate that is formed form the thermoplastic

composition of the present invention may also be employed in other applications. For example, in one embodiment, the planar substrate may be used to form a base of a compact camera module ("CCM"), which is commonly employed in wireless communication devices (e.g., cellular phone). Referring to Figs. 23-24, for example, one particular embodiment of a compact camera module 500 is shown in more detail. As shown, the compact camera module 500 contains a lens assembly 504 that overlies a base 506. The base 506, in turn, overlies an optional main board 508. Due to their relatively thin nature, the base 506 and/or main board 508 are particularly suited to be formed from the thermoplastic composition of the present invention as described above. The lens assembly 504 may have any of a variety of configurations as is known in the art, and may include fixed focus-type lenses and/or auto focus-type lenses. In one

embodiment for example, the lens assembly 504 is in the form of a hollow barrel that houses lenses 604, which are in communication with an image sensor 602 positioned on the main board 508 and controlled by a circuit 601. The barrel may have any of a variety of shapes, such as rectangular, cylindrical, etc. In certain embodiments, the barrel may also be formed from the thermoplastic composition of the present invention and have a wall thickness within the ranges noted above. It should be understood that other parts of the cameral module may also be formed from the thermoplastic composition of the present invention. For example, as shown, a polymer film 510 (e.g., polyester film) and/or thermal insulating cap 502 may cover the lens assembly 504. In some embodiments, the film 510 and/or cap 502 may also be formed from the thermoplastic composition of the present invention. [0053] The present invention may be better understood with reference to the following examples.

Test Methods

[0054] Melt Viscosity: The melt viscosity (Pa-s) was determined in accordance with ISO Test No. 1 1443 at 350°C and at a shear rate of 1000 s ^" using a Dynisco LCR7001 capillary rheometer. The rheometer orifice (die) had a diameter of 1 mm, length of 20 mm, L/D ratio of 20.1 , and an entrance angle of 180°. The diameter of the barrel was 9.55 mm + 0.005 mm and the length of the rod was 233.4 mm.

[0055] Melting Temperature: The melting temperature ("Tm") was determined by differential scanning calorimetry ("DSC") as is known in the art. The melting temperature is the differentia! scanning calorimetry (DSC) peak melt temperature as determined by ISO Test No. 11357. Under the DSC procedure, samples were heated and cooled at 20°C per minute as stated in ISO Standard 10350 using DSC measurements conducted on a TA Q2000 Instrument.

[0056] Deflection Temperature Under Load ("DTUL"): The deflection under load temperature was determined in accordance with ISO Test No. 75-2

(technically equivalent to ASTM D648-07). More particularly, a test strip sample having a length of 80 mm, thickness of 10 mm, and width of 4 mm was subjected to an edgewise three-point bending test in which the specified load (maximum outer fibers stress) was 1 .8 Megapascals. The specimen was lowered into a silicone oil bath where the temperature is raised at 2°C per minute until it deflects 0.25 mm (0.32 mm for ISO Test No. 75-2).

[0057] Tensile Modulus, Tensile Stress, and Tensile Elongation: Tensile properties are tested according to ISO Test No. 527 (technically equivalent to

ASTM D638). Modulus and strength measurements are made on the same test strip sample having a length of 80 mm, thickness of 10 mm, and width of 4 mm.

The testing temperature is 23°C, and the testing speeds are 1 or 5 mm/min.

[0058] Flexural Modulus, Flexural Stress, and Flexural Strain: Flexural properties are tested according to ISO Test No. 178 (technically equivalent to

ASTM D790). This test is performed on a 64 mm support span. Tests are run on the center portions of uncut ISO 3167 multi-purpose bars. The testing temperature is 23°C and the testing speed is 2 mm/min. [0059] Notched Charpy impact Strength: Notched Charpy properties are tested according to ISO Test No. ISO 1 79-1 ) (technically equivalent to ASTM D256, Method B). This test is run using a Type A notch (0.25 mm base radius) and Type 1 specimen size (length of 80 mm, width of 10 mm, and thickness of 4 mm). Specimens are cut from the center of a multi-purpose bar using a single tooth milling machine. The testing temperature is 23°C.

[0060] Fiber Length: The volume average fiber length is determined by initially placing several pellet samples (e.g., 7 or 8) in a muffle furnace at 420°C overnight. The resulting ash is immersed in an aqueous solution containing a glycerol surfactant to disperse the glass fibers. The aqueous solution is then placed on a glass slide and images are collected via image analysis system.

Glass fibers are selectively chosen from the images by ImagePro™ software, and the software automatically measures the length of the selected glass fiber based on calibrated length. Measurement continues until at least 500 glass fibers are counted. Then, the volume average fiber length and distribution are calculated.

[0061] Weldline Strength: The weldline strength is determined by first forming an injection molded line grid array ("LGA") connector (size of 49 mm x 39 mm x 1 mm) from a thermoplastic composition sample as is well known in the art. Once formed, the LGA connector is placed on a sample holder. The center of the connector is then subjected to a tensile force by a rod moving at a speed of 5.08 millimeters per minute. The peak stress is recorded as an estimate of the weldline strength.

EXAMPLE 1

[0062] Three (3) samples of a thermoplastic composition are formed from

67.375 wt.% of a liquid crystalline polymer, 10 wt.% glass fibers, 22 wt.% talc, 0.3 wt.% Glycolube™ P, 0.2 wt.% alumina trihydrate, 0.1 wt.% 4-biphenol, and 0.025 wt.% 2,6-napthalene dicarboxylic acid ("NDA"). The liquid crystalline polymer is formed from 4-hydroxybenzoic acid ("HBA"), 2,6-hydroxynaphthoic acid ("HNA"), terephthalic acid ("TA"), 4,4'-biphenol ("BP"), and acetaminophen ("APAP"), such as described in U.S. Patent No. 5,508,374 to Lee, et al. The glass fibers are obtained from Owens Corning and had an initial length of 4 millimeters.

[0063] To form the thermoplastic composition, pellets of the liquid crystalline polymer are dried at 150°C overnight. Thereafter, the polymer and Glycolube™ P are supplied to the feed throat of a ZSK-25 WLE co-rotating, fully intermeshing twin screw extruder in which the length of the screw is 750 millimeters, the diameter of the screw is 25 millimeters, and the L/D ratio is 30. The extruder has Temperature Zones 1-9, which may be set to the following temperatures: 330°C, 330°C, 310°C, 310°C, 310°C, 310°C, 320°C, 320°C, and 320°C, respectively. For Samples 1-2, the screw design is selected so that melting occurs after Zone 4. For Sample 3, the screw design is selected so that melting begins prior to Zone 4. The polymer is supplied to the feed throat by means of a volumetric feeder. The glass fibers and talc are fed to Zones 4 and/or 6 as indicated in the table below. Once melt blended, the samples are extruded through a single-hole strand die, cooled through a water bath, and pelletized.

[0064] The samples are then tested for fiber length in the manner indicated above. The results are set forth in Table 1 below.

Table 1

[0065] The length distribution of the fibers of Samples 1-3 is also shown in Figs. 4-6, respectively. As indicated in Table 1 and Figs. 4-6, when the glass fibers are fed at Zone #4 (Sample 1 , L/D after glass fiber feeding = 7.75), the fiber length becomes effectively shorter and its distribution is narrower. When fed at Zone #6 (Sample 2, L/D after glass fiber feeding = 3.90) or at Zone #4 but after melting of the polymer (Sample 3, L/D after glass fiber feeding = 4.80), however, no significant change in length is observed.

[0066] Parts are injection molded from Samples 1-3 and tested for their thermal and mechanical properties. The results are set forth below in Table 2. Table 2

EXAMPLE 2

[0067] Six (6) samples of a thermoplastic composition are formed from 67.375 wt.% of a liquid crystalline polymer, 30 wt.% glass fibers, 20 wt.% talc, 0.3 wt.% Glycolube™ P, 0.2 wt.% alumina trihydrate, 0.1 wt.% 4-biphenol, and 0.025 wt.% 2,6-napthalene dicarboxylic acid ("NDA"). The liquid crystalline polymer and glass fibers are the same as employed in Example 1. To form the thermoplastic composition, pellets of the liquid crystalline polymer are dried at 150°C overnight. Thereafter, the polymer and Glycolube™ P are supplied to the feed throat of a ZSK-25 WLE co-rotating, fully intermeshing twin screw extruder in which the length of the screw is 750 millimeters, the diameter of the screw is 25 millimeters, and the L/D ratio is 30. The extruder has Temperature Zones 1-9, which may be set to the following temperatures: 330°C, 330°C, 310°C, 310°C, 310°C, 310°C, 320°C, 320°C, and 320°C, respectively. The screw design is selected so that melting begins at Zone 4. The polymer is supplied to the feed throat by means of a volumetric feeder. The glass fibers and talc are fed to Zones 4 and/or 6 as indicated in the table below. Once melt blended, the samples are extruded through a single-hole strand die, cooled through a water bath, and pelletized.

[0068] The samples are then tested for fiber length in the manner indicated above. The results are set forth in the table below in Table 3. Table 3

[0069] The length distribution of the fibers of Samples 4-9 is also shown in Figs. 7-12, respectively. As indicated in Table 3 and Figs. 7-12, when the glass fibers are fed at Zone #4 (Samples 4-7, L/D after glass fiber feeding = 7.75), the fiber length becomes effectively shorter and its distribution is narrower. When fed at Zone #6 (Samples 8-9, L/D after glass fiber feeding = 3.90), however, no significant change in length is observed.

[0070] Parts are injection molded from Samples 4-9 and tested for their thermal and mechanical properties. The results are set forth below in Table 4,

Table 4

EXAMPLE 3

[0071] Six (6) samples of a thermoplastic composition are formed from 49.375 wt.% of a liquid crystalline polymer, 0.3 wt.% Glycolube™ P, 0.2 wt.% alumina trihydrate, 0.1 wt.% 4-biphenol, 0.025 wt.% 2,6-naphthalene dicarboxylic acid ("NDA"), and varying percentages of glass fibers and mineral filler (talc or mica). The liquid crystalline polymer of Samples 10-15 is the same as employed in Example 1. The liquid crystalline polymer of Samples 16-17 is formed from 4- hydroxybenzoic acid ("HBA"), NDA, terephthalic acid ("TA"), isophthalic acid ("IA"), hydroquinone ("HQ"), and acetaminophen ("APAP").

[0072] To form the thermoplastic composition, pellets of the liquid crystalline polymer are dried at 150°C overnight. Thereafter, the polymer and Glycolube™ P are supplied to the feed throat of a ZSK-25 WLE co-rotating, fully intermeshing twin screw extruder in which the length of the screw is 750 millimeters, the diameter of the screw is 25 millimeters, and the L/D ratio is 30. The extruder has Temperature Zones 1 -9, which may be set to the following temperatures: 330°C, 330°C, 310°C, 310°C, 310°C, 3 0°C, 320°C, 320°C, and 320°C, respectively. The screw design is selected so that melting begins at Zone 4. The polymer is supplied to the feed throat by means of a volumetric feeder. The glass fibers and talc are fed to Zone 4. Once melt blended, the samples are extruded through a single-hole strand die, cooled through a water bath, and pelletized.

[0073] The samples are then tested for fiber length in the manner indicated above. The results are set forth in the table below in Table 5. Table 5

[0074] The length distribution of the fibers of Samples 10-17 is also shown in Figs. 13-20, respectively. As indicated, no significant change in fiber length and distribution is observed by changing filler ratio and filler content.

[0075] Parts are injection molded from Samples 10- 7 and tested for their thermal and mechanical properties. The results are set forth below.

EXAMPLE 4

[0076] Two (2) samples of a thermoplastic composition are formed from 64.375 wt.% of a liquid crystalline polymer, 18 wt.% glass fibers, 18 wt.% talc, 0.3 wt.% Glycoiube™ P, 0.2 wt.% alumina trihydrate, 0.1 wt.% 4-biphenol, and 0.025 wt.% 2,6-napthalene dicarboxylic acid ("NDA"). The liquid crystalline polymer and the glass fibers are the same as employed in Example 1. To form the

thermoplastic composition, pellets of the liquid crystalline polymer are dried at 150°C overnight. Thereafter, the polymer and Glycoiube™ P are supplied to the feed throat of a ZSK-25 WLE co-rotating, fully intermeshing twin screw extruder in which the length of the screw is 750 millimeters, the diameter of the screw is 32 millimeters, and the L/D ratio is 30. The extruder has Temperature Zones 1 -9, which may be set to the following temperatures: 330°C, 330°C, 310°C, 310°C, 310°C, 310°C, 320°C, 320°C, and 320°C, respectively. The screw design is selected so that melting occurs after Zone 4. The polymer is supplied to the feed throat by means of a volumetric feeder. The glass fibers and talc are fed to Zones 4 and 6, respectively. Once melt blended, the sample is extruded through a single-hole strand die, cooled through a water bath, and pelletized.

[0077] The sample is then tested for fiber length in the manner indicated above. The results are set forth in Table 6 below.

Table 6

[0078] A part is injection molded from Sample 8 and tested for its thermal and mechanical properties. The results are set forth below in Table 7.

Table 7

EXAMPLE 5

[0079] A sample of a thermoplastic composition (Sample 19) is formed from 64.375 wt.% of a liquid crystalline polymer, 18 wt.% glass fibers, 18 wt.% talc, 0.3 wt.% Glycolube™ P, 0.2 wt.% alumina trihydrate, 0.1 wt.% 4-biphenol, and 0.025 wt.% 2,6-napthalene dicarboxylic acid ("NDA"). The liquid crystalline polymer and the glass fibers are the same as employed in Example 1. To form the

thermoplastic composition, pellets of the liquid crystalline polymer are dried at 150°C overnight. Thereafter, the polymer and Glycolube™ P are supplied to the feed throat of a ZSK-25 WLE co-rotating, fully intermeshing twin screw extruder in which the length of the screw is 750 millimeters, the diameter of the screw is 32 millimeters, and the L/D ratio is 30. The extruder has Temperature Zones 1-9, which may be set to the following temperatures: 330°C, 330°C, 310°C, 3 0°C, 310°C, 310°C, 320°C, 320°C, and 320°C, respectively. The screw design is selected so that melting occurs after Zone 4. The polymer is supplied to the feed throat by means of a volumetric feeder. The glass fibers and talc are fed to Zones 4 and 6, respectively. Once melt blended, the sample is extruded through a single-hole strand die, cooled through a water bath, and pelletized.

[0080] The sample is then tested for fiber length in the manner indicated above. The results are set forth in Table 8 below.

Table 8

Sample 19

L/D after GF feeding 8.75

L/D before GF feeding 1.75

Vol. Average Length of Fibers (μπι) 110 Vol. Standard Deviation of Fibers 60

Max 480

Count 1477

Coefficient of Variance (%) 51

[0081] A part is injection molded from the sample and tested for its thermal and mechanical properties. The results are set forth below in Table 9.

Table 9

[0082] These and other modifications and variations of the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whoie or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.