Title:
METHOD FOR MANUFACTURING METAL COMPONENTS USING RECYCLED FEEDSTOCK AND ADDITIVE MANUFACTURING
Document Type and Number:
WIPO Patent Application WO/2020/131276
Kind Code:
A1
Abstract:
A method for manufacturing metal components [36] includes the steps of providing a waste feedstock [10] having a selected chemical composition; producing an additive manufacturing (AM) grade alloy powder [12] from the waste feedstock [10] using a cold hearth mixing process; providing an additive manufacturing system [22A]; controlling the producing of the alloy powder [12] such that the properties of the alloy powder [12] optimize building of the components [36] using the additive manufacturing system [22A]; and building the components [36] using the alloy powder [12] and the additive manufacturing system [22A].

Inventors:
LATOUR ANDREW VANOS (US)
EONTA CHRISTOPHER PAUL (US)
CHARLES MATHEW (US)
CLARK ANDREW R (US)
SACKMANN VALENTINE C (US)
Application Number:
PCT/US2019/062111
Publication Date:
June 25, 2020
Filing Date:
November 19, 2019
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
MOLYWORKS MAT CORP (US)
LATOUR ANDREW VANOS (US)
EONTA CHRISTOPHER PAUL (US)
CHARLES MATHEW (US)
CLARK ANDREW R (US)
SACKMANN VALENTINE C (US)
International Classes:
B22F9/06; B33Y10/00; B33Y70/00; C22B9/22; C22B34/12
Foreign References:
US20180133804A12018-05-17
US5224534A1993-07-06
US20190119787A12019-04-25
CN104550960A2015-04-29
US9925591B22018-03-27
US4750542A1988-06-14
US20150020646A12015-01-22
Attorney, Agent or Firm:
GRATTON, Stephen A. (US)
Download PDF:
Claims:
WHAT IS CLAIMED IS:

1. A method for manufacturing metal components comprising:

providing a waste feedstock having a selected chemical composition; producing an additive manufacturing (AM) grade alloy powder from the waste feedstock using a cold hearth mixing process, the alloy powder comprising particles having selected properties;

providing an additive manufacturing system;

controlling the producing of the alloy powder such that the properties of the particles optimize building of the components using the additive manufacturing system; and

building the components using the alloy powder and the additive manufacturing system.

2. The method of claim 1 wherein the selected properties include particle size distribution, morphology, density, phase behavior, elemental composition and surface characteristics.

3. The method of claim 1 wherein the waste feedstock comprises an element selected from the group consisting of failed builds, broken parts, prototype parts, support structures, and used alloy powder.

4. The method of claim 1 wherein the waste feedstock comprises recycled aircraft components.

5. The method of claim 1 further comprising during the producing step correcting a composition of the waste feedstock using additives to achieve a particular composition of metal alloy.

6. The method of claim 1 wherein the alloy powder comprises a titanium-based

powder.

7. The method of claim 1 wherein the additive manufacturing system comprises a laser powder bed fusion (LPBF) system.

8. The method of claim 1 wherein the additive manufacturing system comprises a laser metal deposition (LMD) system.

9. The method of claim 1 wherein the additive manufacturing system comprises an electron beam melting (EBM) system.

10. A method for manufacturing titanium-based alloy components comprising: providing a waste feedstock having a selected chemical composition;

producing an additive manufacturing (AM) grade alloy powder from the waste feedstock using a cold hearth mixing process;

correcting a composition of the waste feedstock using additives during the cold hearth mixing process to achieve a particular composition of metal alloy;

providing an additive manufacturing system comprising a system selected from the group consisting of laser powder bed fusion (LPBF) systems, laser metal deposition (LMD) systems and electron beam melting systems; and

building the components using the alloy powder and the additive manufacturing system.

11. The method of claim 10 wherein the additive manufacturing system comprises a laser powder bed fusion (LPBF) system and the alloy powder comprises a titanium alloy powder.

12. The method of claim 10 wherein the additive manufacturing system comprises a laser metal deposition (LMD) system and the alloy powder comprises a titanium alloy powder.

13. The method of claim 10 wherein the additive manufacturing system comprises an electron beam melting (EBM) system and the alloy powder comprises a titanium alloy powder.

14. The method of claim 10 wherein the waste feedstock comprises an element selected from the group consisting of failed builds, broken parts, prototype parts, support structures, and used alloy powder.

15. The method of claim 10 wherein the waste feedstock comprises recycled aircraft components.

Description:
METHOD FOR MANUFACTURING METAL COMPONENTS USING RECYCLED FEEDSTOCK AND ADDITIVE MANUFACTURING

Government License Rights

[0001] This invention was made with government support under Contract FA8222-18- P-0005, awarded by the US Air Force. The government has certain rights in the invention.

Cross Reference to Related Application

[0002] This application claims priority from US Provisional No. 62/781,107, filed 12/18/2018, and to US Provisional No. 62/790,103, filed 01/09/2019, both of which are incorporated herein by reference.

Field

[0003] This disclosure relates to a method for manufacturing metal components using high temperature metal alloys fabricated from a variety of waste feedstocks.

Background

[0004] Working metals into alloys has been done throughout human history. High temperature alloys are a very recent discovery. These metals are being utilized in industries that need materials to withstand high temperatures, such as airplane engines, turbine blades, and chemical processing equipment. However, the high heat tolerance of these metals makes recycling difficult to accomplish. Current recycling technologies, while successful, are not efficient enough for today’s industry requirements.

[0005] In addition, the minerals containing the metals needed to make high temperature metal alloys must be imported into the United States due to these mineral deposits not being present on US soil. This makes optimizing the metal recycling process essential for reducing international dependence on obtaining these valuable metals.

[0006] In view of the foregoing, there is a need in the art for improvements in recycling processes for high temperature metal alloys. This disclosure relates to a method for recycling high temperature metals from a variety of waste feedstocks, which are converted into an additive manufacturing (AM) grade powder, and then into metal alloy components, such as aircraft components. Summary

[0007] A method for manufacturing metal components includes the initial step of providing a waste feedstock having a selected chemical composition. Exemplary waste feedstocks include failed builds, broken parts, prototype parts, support structures, and used powder. For manufacturing components out of a titanium based alloy, recycled aircraft components can be used as the waste feedstock.

[0008] The method also includes the step of producing an additive manufacturing (AM) grade alloy powder from the waste feedstock using a cold hearth mixing process. In cold hearth mixing, a heat source, such as a plasma torch or an electron beam is used to heat raw materials into a molten material, which is then atomized into a powder. Composition correction can also be performed using additives. For example, during production of the alloy powder, the composition of the molten waste feedstock can be adjusted to achieve a particular composition of metal alloy. In exemplary embodiments, titanium-based alloy powders are produced.

[0009] The method also includes the steps of providing an additive manufacturing system, and controlling the producing of the alloy powder such that the properties of the alloy powder optimize building of the components using the additive manufacturing system. In exemplary embodiments, the additive manufacturing system can utilize laser powder bed fusion (LPBF) technology, laser metal deposition (LMD) technology or electron beam melting (EBM) technology. With each technology, the properties of the alloy powder produced from the waste feedstock are engineered to satisfy the requirements of the additive manufacturing system.

[0010] The method also includes the step of building the components using the additive manufacturing (AM) grade alloy powder and the additive manufacturing system. In an additive manufacturing system that uses laser powder bed fusion (LPBF), one or more lasers fuse powder particles together layer by layer. After each layer of the part is built, another layer of powder is dispensed over the surface, which is subsequently fused by the laser. The resulting part is cut from a build plate, allowing excess powder to fall away and be recycled. In an additive manufacturing system that uses laser metal deposition (LMD), molten powder is deposited directly onto a substrate. Laser metal deposition (LMD) differs from laser powder bed fusion (LPBF) in the way powder is delivered. In (LPBF), a laser melts powder that is lying stationary in a powder-bed. A hopper dispenses powder across the bed and the part is built in layers. In contrast, (LMD) uses a stream of powder which is melted by a laser as it travels from the nozzle to the substrate. In an additive manufacturing system that uses electron beam melting (EBM), an electron beam and lens system are used to melt and fuse powder particles in layers on a build plate.

[0011] Following the building step, the method can also include the steps of heat treating the components, machining the components and testing the components.

Brief Description of the Drawings

[0012] Exemplary embodiments are illustrated in the referenced figures of the drawings. It is intended that the embodiments and the figures disclosed herein be to be considered illustrative rather than limiting.

[0013] Figure 1 is a flow diagram illustrating steps in a method for manufacturing metal components;

[0014] Figure 2A is a schematic view of a waste feedstock used with the method;

[0015] Figure 2B is a schematic view illustrating a cold hearth mixing system used with the method;

[0016] Figure 2C is a schematic view illustrating an atomization system used with the method during production of an alloy powder;

[0017] Figure 2D is a schematic view illustrating the alloy powder produced by the method;

[0018] Figure 3 is a schematic view illustrating an additive manufacturing system that includes a laser powder bed fusion (LPBF) system for performing a building step of the method;

[0019] Figure 4A is a perspective view of a landing gear coupon component built by the system of Figure 3 using the method;

[0020] Figure 4B is a perspective view of a subscale component built by the system of Figure 3 using the method;

[0021] Figures 5A-5E are schematic views illustrating build plates and support structures for performing a building step of the method;

[0022] Figure 6A is a schematic view illustrating an additive manufacturing system that includes a laser metal deposition (LMD) system for performing a building step of the method; [0023] Figure 6B is an enlarged side elevation view of a laser head of the laser metal deposition (LMD) system shown in Figure 6A;

[0024] Figures 7A and 7B are schematic views illustrating build plates after printing using the laser metal deposition (LMD) system shown in Figure 6A;

[0025] Figures 8A and 8B are schematic views illustrating printed blocks after printing using the laser metal deposition (LMD) system shown in Figure 6A; and

[0026] Figure 9 is a schematic view illustrating an additive manufacturing system that includes an electron beam melting (EBM) system for performing a building step of the method.

Detailed Description

[0027] Referring to Figures 1 and 2A-2D, steps in a method for manufacturing metal components are illustrated. As shown in Figure 2A, an initial step in the method comprises providing a waste feedstock 10. Exemplary waste feedstocks 10 include failed builds, broken parts, prototype parts, support structures, and used powder. Titanium, although relatively rare, can be found in aircraft components. In addition, wherever metal parts are expended, steel, stainless steel, aluminum, and copper can be found. US Patent Application No. 16/135, 191, which is incorporated herein by reference, discloses a deployable manufacturing center (DMC) system for providing the waste feedstock 10.

[0028] By way of example, for providing the waste feedstock 10, large pieces of metal scrap can be collected, analyzed by a handheld XRF, and cut to pieces smaller than 6" in diameter. Small fragments of scrap materials are usually not collected due to lower yield, greater variations in alloy composition, and increased likelihood of contamination. Hazardous components, such as radioactive materials, toxic materials such as asbestos, or metals such as beryllium, cadmium, and mercury pose dangers to personnel and are removed from the feedstock 10 before processing. In addition, chemical analysis of the waste feedstock 10 can be performed to predict elements needed for correction of the final composition to the desired alloy. Ideally, a batch is composed of scrap from a single source material. This makes the composition relatively easy to predict and correct. When the waste feedstock is inconsistent, however, predictive analysis is not sufficient. For inconsistent waste feedstock, a post-melt chemical analysis can be performed to determine the composition of the material. After the mixed-scrap composition is determined, the alloy can be corrected to its desired composition. [0029] As shown in Figures 2B-2D, the method also includes the step of producing an additive manufacturing (AM) grade alloy powder 12 (Figure 2D) from the waste feedstock 10 using a cold hearth mixing process performed using a cold hearth mixing system 11 (Figure 2B). As shown in Figure 2B, the cold hearth mixing system 11 includes a heat source 16, such as a torch, and a mixing cold hearth 14. As shown in Figures 2B and 2C, during the cold hearth mixing process, the heat source 16 and the mixing cold hearth 14 (Figure 2B) are operated to produce a molten metal 20 having a uniform composition, with composition correction performed if necessary.

[0030] US Patent No. 9,925,591 B2, which is incorporated herein by reference, discloses exemplary cold hearth mixing systems. For example, the mixing cold hearth 14 (Figure 2B) can include fluid cooled walls, a melting cavity configured to hold the waste feedstock 10 (Figure 2B) and the molten metal 20 (Figure 2C), and an induction coil (not shown) configured to generate an electromagnetic field for stirring and heating the molten metal 20 (Figure 2C). The mixing cold hearth 14 (Figure 2C) can also include a mechanical drive (not shown) configured to mount and move the mixing cold hearth 14 (Figure 2C) for mixing the molten metal 20 (Figure 2C) in the melting cavity and to rotate the mixing cold hearth 14 (Figure 2C) for pouring the molten metal from the melting cavity. Movement of the mixing cold hearth (Figure 2C) 14 by the mechanical drive can include both oscillatory motion and rotational motion or a combination thereof. The mixing cold hearth 14 (Figure 2C) can also include a skull (not shown) at least partially lining the melting cavity and configured to provide a heat transfer boundary for the molten metal 20 (Figure 2C). In addition, the mixing cold hearth 14 (Figure 2C) can comprise a removal element of an assembly of interchangeable mixing cold hearths, with each mixing cold hearth 14 of the assembly configured for melting a specific category of raw material to produce a specific product. In the mixing cold hearth 14 (Figure 2C) composition correction can optionally be performed by adding additives to a known material of undesirable composition to create a new material of a desired composition. The cold hearth mixing process is thus controlled to provide the material for making the alloy powder 12 with an exact chemical composition.

[0031] Following processing in the mixing cold hearth 14 (Figure 2B), an atomization process can be performed using a gas atomization system 18 (Figure 2C) to form the alloy powder 12 (Figure 2D). Previously cited US Patent No. 9,925,591 B2 discloses exemplary gas atomization systems. For example, atomization can be performed by pouring the molten metal 20 (Figure 2C) across a die that produces turbulent high-velocity gas in a sharp stream. The stream of turbulent high-velocity gas disintegrates the molten stream and produces spherical metal particles that are cooled rapidly in flight as they travel through an atomization chamber. As it is cooling in flight, the metal powder solidifies and is transferred into a cyclone (not shown) where it is collected as the alloy powder 12 (Figure 2D). As other examples, atomization can be performed with plasma gas, a spinning disk, a vibratory plate, or another method that disintegrates the molten metal into fine particles. Preferably, the atomization process is controlled such that the resulting particle size of the alloy powder 12 (Figure 2D) can be between 0-350 um. In one embodiment, the alloy powder 12 (Figure 2D) has a particle size of 10-160 um. In another embodiment, a particle size of 25-50 um is produced.

[0032] Following the atomization process, the alloy powder 12 (Figure 2D) can be analyzed by the SEM analysis apparatus to confirm particle size, microstructure, and elemental composition. Characterization of the alloy powder 12 (Figure 2D) can include analysis of particle size, size distribution, morphology, density, phase behavior, elemental composition and surface characteristics. Purity, morphology, and defect-free microstructure can also be confirmed upon characterization, as well as avalanche angle and surface fractal. All of these characteristics can be selected to satisfy the requirements of the additive manufacturing system 22A (Figure 3) or 22B(Figure 6A).

[0033] Referring again to Figure 1, the method also includes the step of building the components using the additive manufacturing (AM) grade alloy powder 12 (Figure 2D) and an additive manufacturing system 22A (Figure 3) or 22B (Figure 6A). In a first embodiment, the additive manufacturing system 22A (Figure 3) employs laser powder bed fusion (LPBF) technology. As shown in Figure 3, the additive manufacturing system 22A can include a laser 24, a scanner 26, and a build chamber 28. Within the build chamber 28 are a powder bed 34 and for containing the alloy powder 12 and a roller rake 30 for conveying the alloy powder 12 into the powder bed 34 for building the components 32.

[0034] In a second embodiment, the additive manufacturing system 22B (Figure 6A) employs laser metal deposition (LMD) technology. Laser Metal Deposition (LMD) is a type of additive manufacturing which deposits molten powder directly onto a substrate. It is different from powder-bed fusion in the way powder is delivered. In LPBF, a laser melts powder which is lying stationary in a powder-bed. A hopper dispenses powder across the bed and the part is built in layers. In contrast, LMD uses a stream of powder which is melted by a laser as it travels from the nozzle to the substrate. LMD can be used for building new parts and part repairs. The powder used in LMD has a particle size range of 75-150pm, which is too large for LPBF. As shown in Figure 6A, the additive manufacturing system 22B includes a deposition nozzle 46 in flow communication with a quantity of the alloy powder 12 and configured for movement in a direction of travel 54. The deposition nozzle 46 produces moving powder particles 56 that are melted by a laser beam 48 emanated from a laser head 58 (Figure 6B) to form a melt pool 50 and a deposited track 52.

[0035] In the examples to follow, landing gear coupon components 36 (Figure 4A) and subscale components 38 (Figure 4B) were made by additive manufacturing (AM) using the alloy powder 12 (Figure 2D). Using the previously described method, Titanium 10-2-3 alloy powder was produced by MolyWorks Materials Corporation at its R&D facility in Cloverdale, CA. Alloy powder production was performed via a cold hearth mixing process as previously described using certified scrap feedstock. In the examples to follow, the alloy powder 12 had particle sizes up to 75 pm and the additive manufacturing system included an Ml 00 printer. Ti 10-2-3 alloy powder was tested in-house for oxygen and hydrogen, and sent out for analysis to Anamet Inc., a third-party laboratory specializing in materials analysis (located in Hayward, CA). Oxygen content of the alloy powder ranged from 0.14% to 0.22%. The average oxygen content of the alloy powder 12 was 0.18% with a CV of 14.1%. The oxygen added by the foundry was in the range of 400-800 ppm, with final oxygen content of the alloy powder 12 typically between 0.16% and 0.2%. For one lot of alloy powder 12, an analysis from Anamet showed that oxygen content was 0.12%, meeting industry specifications for Titanium.

[0036] Manufacturing process parameters were developed for Titanium 10-2-3 and Ti 6-4. Destructive and nondestructive tests were used to generate mechanical properties, microstructure, and chemical composition data. Results indicate that coupon components 36 and subscale components 38 fabricated using the alloy powder 12 and an additive manufacturing (AM) process have substantially lower high-cycle fatigue strength compared to wrought material (40 vs 90 ksi at runout, respectively). Low-cycle fatigue strength of the coupon components 36 (Figure 4A) and subscale components 38 was also lower than for equivalent wrought components (1000 cycles to failure at 0.75% strain for coupon components vs 1% strain for equivalent wrought components). However, there was significant overlap in the data for the components formed by the present method using recycled feedstock used to produce the alloy powder 12. Failure analysis and optical microscopy revealed that the coupon components 36 and subscale components 38 showed microstructural differences when compared to equivalent wrought components, such as larger grains and smaller dimples in the fracture surfaces. Subscale part manufacturing tests indicate that the present method is capable of producing at least seven unique landing gear parts whose production has become obsolete.

[0037] Example 1. In this example, the additive manufacturing system included a 3-D printer in the form of a modified EOS M100 3D-Printer manufactured by EOS GmbH Electro Optical Systems. Fatigue coupons were designed to fit the usable build platform of the M100 and meet ASTM standards. Work was performed with 3DXpert to design build plates and support structures. Files were designed in CAD and converted to 3DXpert, where support structures and tolerances were added. Before printing, 3DXpert files were exported (as .stl files) to EOS Print for positioning on the build platform.

[0038] Coupons were prepared in both vertical and horizontal orientations to test the capabilities of the EOS M100. The EOS100 required extensive modifications to function as an additive manufacturing system for performing the present method. For example, prior to modifications the usable build volume was found to be approximately 25% of the actual build volume, and the powder hopper was found to be too small to feed a full build plate. Horizontal builds were limited in size due to problems with the powder dispensing system - powder was not dispensed evenly from the hopper. The typical oxygen added to titanium parts by the Ml 00 during the reporting period was 400-600 ppm. Further oxidation of powder was observed due to overheating of overhangs when no support structures were present. Oxidation problems may be attributed to the inert gas purge system which allows 1000 ppm of oxygen to remain in the build chamber during printing. A vacuum system could reduce the oxygen added to as low as 25 ppm.

[0039] The average production rate of the M100 was around 3 coupons per day. Round samples presented challenges when printed in the horizontal orientation. Problems arose from the overhang of the rounded sides, requiring addition of support material. When not firmly supported, parts printed in the horizontal orientation curled away from the build plate due to vertical residual stresses. When support structures were added to compensate for residual stress, the support structures created difficulties in subsequent machining. Closely spaced support material compounded the difficulties of removal in machining.

[0040] Figures 5A-5E illustrate exemplary build plates 40A-40E, build areas 42A-40E and support structures 44A-44E for performing the building step. In Figures 5A-5B the build plates 40A-40E are represented by the checkered patterns, the build areas 42A-42E are represented by the honeycomb patterns (or plus minus patterns) and the support structures 44A- 44E by solid lines. In Figure 5 A, solid supports 44A that are slightly wider than the base of the component were used. The supports 44A were extruded down 4mm from the bottom of the part to enable the build plate 40A to be removed from the component. This method was used for all parts which utilized solid supports. Honeycomb build areas 42A and solid supports 44A were used for the bottom. The honeycomb had a distance of 2mm and an external wall. Texture 2-S was used. The solid supports 44A used were mated against flat surfaces on the component (e.g. coupon component 36 - Figure 4A) or subscale part component 38 (Figure 4B) to facilitate removal. In Figure 5B, a plus minus build area 42B and solid supports 44B on a build plate 40B were employed. All of the build areas 42B beneath and between the supports used a plus- sign pattern with a distance of 3mm and an external wall. The bottom supports 44B used texture 1-S. In Figure 5C, honeycomb build areas 42C and supports 44C on a build plate 40C were utilized. External walls were removed from several areas to ease removal of support structures after printing. The center solid support 44C required removal by drilling. Honeycomb build areas 42C surrounding the circle had a distance of 2mm. Honeycomb dimensions of the external walls were 2.5mm. The remaining honeycomb build areas 42C were set at 3mm. The four supports 44C on the comers were solid, with a small latticed center to provide rigidity. The build areas 42C on the two outside holes were honeycomb, with a distance of 3mm. External walls were utilized on some supports and omitted from others for ease of removal and surface finish. The support material for the cross-holes (from each side hole to the center hole) was plus signs with a distance of 4mm, with external walls eliminated for ease of removal. No textures were utilized for the walls of the supports. In Figure 5C, the supports 44C were square grid and solid. The square grid had a distance of 3mm and an external wall with Texture 2-S. In Figure 5D, solid supports 44D and honeycomb build areas 42D on a build plate 40D were used. All honeycombs for this part had a distance of 3mm. In Figure 5E, cylindrical solid supports 44E, square grid build area 42E and build plate 40E were used. The square grid had a distance of 3mm, an external wall with Texture 2-S, and selected cell properties.

[0041] Example 2. In Example 2, the additive manufacturing system 22B (Figures 6A- 6B) included laser metal deposition technology. Figures 7A and 7B are schematic views illustrating a build plate 60 after printing of block components 62 A, 62B using the laser metal deposition (LMD) system shown in Figure 6A. Figures 8A and 8B are schematic views illustrating printed block components 62A , 62B after printing using the laser metal deposition (LMD) system shown in Figure 6A.

[0042] Alloy powder production was performed via a cold hearth mixing process as previously described using certified scrap feedstock. In this example, Ti 10-2-3 alloy powder 12 was produced in a size range of 75-150pm. Alloy powder 12 with particle sizes in the 75- 150pm range was sent to Formalloy (Spring Valley, CA) for printing of a landing gear part on an L-series LMD system. Although prior art parts are typically made from Ti 6-4, in this example the part was built using Ti 10-2-3.

[0043] Oxygen and hydrogen were measured at each step in the process. The data was collected using an Eltra Elementrac ONH-p. The alloy powder 12 was analyzed, printed into pins, and analyzed again. The results indicate that the oxygen added to titanium parts was approximately 400-600 ppm.

[0044] Ti 10-2-3 printing of high and low cycle fatigue coupons was conducted by MolyWorks Materials Corporation at its Cloverdale facility. Fifteen E466 high cycle fatigue coupons and sixteen E606 low cycle fatigue coupons were produced. Horizontal build orientation was used for all samples. Blanks were printed, cut from build plates via band saw, and shipped to Quintus (Lewis Center, Ohio) for HIP and heat treatment. After heat treatment, coupons were machined to geometric specifications and sent to TRL for testing.

[045] In both Example 1 and Example 2, heat treatments were selected to produce the highest-strength condition. A Hot Isostatic Press (HIP) was performed by Quintus at 1650F and 15,000 psi for 2 hours, immediately followed by a solution treatment at 1410F for lh followed by a rapid argon quench. Some warping and surface oxidation was observed in the coupon blanks. The oxide layer was removed by subsequent machining. Warping was not significant enough to create problems during machining. A stress relief anneal performed while the parts are still attached to the build plate may be used in future tests to prevent warping.

[0046] In Example 1, after heat treatment, coupons were machined to final geometry and polished. In Example 2, control samples were also machined from Ti 10-2-3 ingot. Controls were cut from a Ti 10-2-3 round forged bar and blanked with an industrial saw. The ASTM E606 samples were rough turned on a large manual lathe and finish turned on a CNC lathe. The ASTM E466 samples were CNC milled to rough dimensions, finish ground, and polished. Once machining was completed, density testing was performed, and all coupons were sent to Touchstone Research Laboratory in Triadelphia, WV for testing. [0047] With respect to testing, the density of components was measured in-house using an Archimedes apparatus and an analytical balance. Samples were weighed in air and weighed again in distilled water. The temperature of the water was measured and recorded to correct for changes in water density. The samples were carefully inspected during weighing in water to ensure no bubbles were trapped underneath.

[0048] With respect to testing, fatigue tests were performed using test conditions that allow the results to be compared to literature data for conventional manufacturing processes. Load type was tension-tension using type-1 round bar with parallel gage length and R=0.1. Grips were wedge style. Results from both tests were used to generate stress-life and strain-life curves. Ti 10-2-3 fatigue data is not available from MMPDS; however, literature data is available which may be used for comparison.

[0049] Fatigue coupon fracture surfaces were viewed in a scanning electron microscope to assess the failure mode. While the surfaces of control samples contained dimples surfaces, the dimple morphology in the printed samples were smaller. The difference between the control samples and printed samples are evident in the morphology of the dimples, which can be attributed to the internal grain structure of the materials. Control samples have very small grain size, while with other printed samples the grain structure appears to be coarse. Typically, smaller grains and smaller feature sizes are associated with better fatigue performance.

[0050] Corrosion resistance testing was performed in a salt-spray cabinet conforming to ASTM B117. Testing temperatures were 95° F in chamber, and 117° F in the bubble tower (containing salt solution). Hot air bubbles were generated which passed through the bubble tower at 12 psi. A 5% salt solution (ASTM D1193, ACS grade salt) was atomized to produce fog in the chamber. Graduated cylinders were used to measure the amount of fog, with a 1- 2mL per hour target. pH was held within the range of 6.5-7.2. Samples were placed on wooden blocks during testing. No corrosion was visible in the Ti 10-2-3 samples upon completion of testing.

[0051] Samples were initially prepared for optical microscopy by sectioning using a circular table saw and mounting in resins for further preparation. Next, samples were ground and polished by standard metallographic specimen preparation procedures and etched with Kroil’s reagent to reveal microstructure. Wrought material is typical beta with woven microstructure of alpha plates. The images reveal typical heat-treated titanium alloy with an average grain size of 20 pm. Further internal structure of the grains consists of Widman Staten structure of alpha laths in a matrix of beta phase grain. The as-printed material showed larger elongated grains which contained fine precipitates (these may be V-Al or Ti-Al). Compared to the control material, the additively manufactured samples had very coarse grains.

[0052] Example 3. In Example 3, the additive manufacturing system 22C (Figure 9) can includ electron beam melting (EBM) technology with the alloy powder 12 (Figure 2D) produced to satisfy the requirements of this technology. As shown in Figure 9, the additive manufacturing system 22C can include a filament 64 and a lens system 66 configured to produce an electron beam 68. The additive manufacturing system 22C can also include a build plate 72 on a build platform 74 in a vacuum chamber 76 wherein layers of melting powder can be formed into components. One suitable additive manufacturing system 22C that uses electron beam melting (EBM) is commercially available from Arcam EBM of Sweden.

[0053] While a number of exemplary aspects and embodiments have been discussed above, those of skill in the art will recognize certain modifications, permutations, additions and subcombinations thereof. It is therefore intended that the following appended claims and claims hereafter introduced are interpreted to include all such modifications, permutations, additions and sub-combinations as are within their true spirit and scope.