Title:
METHOD FOR THE PREPARATION OF POLYANILINE/REDUCED GRAPHENE OXIDE COMPOSITES
Document Type and Number:
WIPO Patent Application WO/2016/067243
Kind Code:
A1
Abstract:
The present invention concerns a method for obtaining polyaniline/reduced graphene oxide composites comprising the steps of dispersing the graphene oxide in an acid aqueous solution containing an emulsifying agent to obtain a graphene oxide dispersion; dissolving one or more aniline oligomers in an organic solvent to obtain an oligomer solution; mixing the oligomer solution with the graphene oxide dispersion, said oligomer being added in a stoichiometric excess compared to the quantity required to complete the graphene oxide reduction; adding to the suspension of the polyaniline/reduced graphene oxide composite an oxidizing agent in a stoichiometric quantity compared to said excess of oligomer so as to oxidize the excess of said oligomer to obtain a suspension of the polyaniline/reduced graphene oxide composite.

Inventors:
BOCCHINI SERGIO (IT)
CHIOLERIO ALESSANDRO (IT)
PORRO SAMUELE (IT)
Application Number:
PCT/IB2015/058356
Publication Date:
May 06, 2016
Filing Date:
October 29, 2015
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
FOND ISTITUTO ITALIANO DI TECNOLOGIA (IT)
International Classes:
C01B31/04; B01J31/06; B01J37/00; C08G73/02; C08L79/02; C09D11/322; C09D11/52; C09D179/02; G01N27/48; H01B1/12; H01G11/30; H01M4/92
Domestic Patent References:
WO2015001534A12015-01-08
Foreign References:
US20140087192A12014-03-27
ITTO20130561A12015-01-05
Other References:
DI WEI ET AL: "Properties of graphene inks stabilized by different functional groups;Properties of graphene inks stabilized by different functional groups", NANOTECHNOLOGY, vol. 22, no. 24, 20 April 2011 (2011-04-20), IOP, BRISTOL, GB, pages 245702, XP020205502, ISSN: 0957-4484, DOI: 10.1088/0957-4484/22/24/245702
HUANG Y F ET AL: "Facile synthesis and morphology control of graphene oxide/polyaniline nanocompositespolymerization process", POLYMER, vol. 53, no. 13, 16 April 2012 (2012-04-16), ELSEVIER SCIENCE PUBLISHERS B.V, GB, pages 2574 - 2582, XP028513640, ISSN: 0032-3861, [retrieved on 20120421], DOI: 10.1016/J.POLYMER.2012.04.022
DATABASE WPI Week 201263, Derwent World Patents Index; AN 2012-C59153, XP002741876
UNSWORTH, J.; LUNN, B. A.; INNIS, P. C.; JIN, Z.; KAYNAK, A.; BOOTH, N. G. J., INTELL. MATER. SYST. STR., vol. 3, 1992, pages 380 - 395
SCHOCH, K. F., IEEE ELECTR. INSUL. MAG., vol. 10, 1994, pages 29 - 32
ANGELOPOULOS, M, IBM J. RES. DEVELOP., vol. 45, 2001, pages 57 - 75
GOSPODINOVA, N.; TERLEMEZYAN, L, PROG. POLYM. SCI., vol. 23, 1998, pages 1443 - 1484
GOSPODINOVA, N.; TERLEMEZYAN, L., PROG. POLYM. SCI., vol. 23, 1998, pages 1443 - 1484
BHADRA, S.; DIPAK, K.; SINGHA, N. K.; LEE, J., PROG. POLYM. SCI., vol. 34, 2009, pages 783 - 810
BOCCHINI, S.; CHIOLERIO, A.; PORRO, S ET AL., J. MATER. CHEM. C, vol. 1, 2013, pages 5101 - 5109
MACDIARMID, A. G., ANGEW. CHEM. INT. ED, vol. 40, 2001, pages 2581 - 2590
KANG, E.; NEOH, K. G.; TAN, K. L., PROG. POLYM. SCI., vol. 23, 1998, pages 277 - 324
CHIOLERIO, A.; BOCCHINI, S; PORRO, S, ADV. FUNCT. MATER., vol. 24, 2014, pages 3375 - 3383
DI VENTRA, M.; PERSHIN, Y.V.; CHUA, L.O., ARXIV:0901.3682VL
BERZINA, T. S.; GORSHKOV, K. V.; EROKHIN, V. V.; NEVOLIN, V. K.; CHAPLYGIN, Y. A, RUSSIAN MICROELECTRONICS, vol. 42, 2013, pages 27 - 32
LU, W, NATURE MATER, vol. 12, 2013, pages 93 - 94
PICKETT, M. D; MEDEIROS-RIBEIRO, G.; WILLIAMS, R. S., NATURE MATER, vol. 12, 2013, pages 114 - 117
NOVOSELOV, K.; GEIM, A.; MOROZOV, S.; JIANG, D.; ZHANG, Y.; DUBONOS, S.; GRIGORIEVA, I.; FIRSOV, A., SCIENCE, vol. 306, 2004, pages 666 - 669
GEIM, A. K.; NOVOSELOV, K. S, NAT. MATER, vol. 6, 2007, pages 183 - 191
KATSNELSON, M.I.; NOVOSELOV, K.S., SOLID STATE COMMUN, vol. 143, 2007, pages 3 - 13
ROURKE, J.P.; PANDEY, P.A.; MOORE, J.J.; BATES, M.; KINLOCH, I.A.; YOUNG, R.J.; WILSON, N.R., ANGEW. CHEM. INT. ED., vol. 50, 2011, pages 3173 - 3177
BOEHM HP; CLAUSS A; FISCHER G; HOFMANN U: "Fifth Conference on Carbon", vol. 1962, PERGAMON PRESS, pages: 73
XU LQ; LIU YL; NEOH KG; KANG ET; FU GD., MACROMOL. RAPID COMM., vol. 32, no. 8, 2011, pages 684 - 688
SHIM, Y. B.; PARK, S. M: "Electrochemistry of conductive polymers VII. Autocatalytic rate constant for polyaniline growth", SYNTH. MET., vol. 29/1, 1989, pages 169 - 174, XP024160658, DOI: doi:10.1016/0379-6779(89)90293-2
XIA, Y.; WIESINGER, J. M.; MACDIARMID, A. G.; EPSTEIN, A. J: "Camphorsulfonic acid fully doped polyaniline emeraldine salt: conformations in different solvents studied by an ultraviolet/visible/near-infrared spectroscopic method", CHEM. MATER., vol. 7, 1995, pages 443 - 445
PERSHIN, Y. V.; DI VENTRA; M. MEMORY EFFECTS IN COMPLEX MATERIALS AND NANOSCALE SYSTEMS, ADV. IN PHYS., vol. 60, 2011, pages 145 - 227
MENG, Y.; WANG, K.; ZHANG, Y.; WEI, Z: "Hierarchical porous graphene/polyaniline composite film with superior rate performance for flexible supercapacitors", ADV. MATER., vol. 25, 2013, pages 6985 - 6990
PLONSKA-BRZEZINSKA, M. E.; BRECZKO, J.; PALYS, B.; ECHEGOYEN, L: "The electrochemical properties of nanocomposite films obtained by chemical in situ polymerization of aniline and carbon nanostructures", CHEM. PHYS. CHEM., vol. 14, 2013, pages 116 - 124
LEE, T. ET AL.: "Hybrid multilayer thin film supercapacitor of graphene nanosheets with polyaniline: importance of establishing intimate electronic contact through nanoscale blending", J. MATER. CHEM, vol. 22, 2012, pages 21092 - 21099
KOCHOWSKI, S.; NITSCH, K.: "Description of the frequency behaviour of metal-Si02-GaAs structure characteristics by electrical equivalent circuit with constant phase element", THIN SOLID FILMS, vol. 415, 2002, pages 133 - 137, XP004380228, DOI: doi:10.1016/S0040-6090(02)00506-0
ZHU, J. ET AL.: "Carbon nanostructure-derived polyaniline metacomposites: electrical, dielectric, and giant magnetoresistive properties", LANGMUIR, vol. 28, 2012, pages 10246 - 10255
HILL, A.; MIKHAILOV, S.; ZIEGLER, K: "Dielectric function and plasmons in graphene", EUROPHYS. LETT., vol. 87, 2009, pages 27005
MONGUZZI; A., TUBINO; R. MEINARDI: "Upconversion-induced delayed fluorescence in multicomponent organic systems: role of Dexter energy transfer", F. PHYS. REV. B, vol. 77, 2008, pages 155122
CHEN, H. C. ET AL.: "White-light emission from an upconverted emission with an organic triplet sensitizer", CHEM. COMM., vol. 27, 2009, pages 4064 - 4066, XP002660710, DOI: doi:10.1039/b905572j
REINEKE, S ET AL.: "White organic light-emitting diodes with fluorescent tube efficiency", NATURE, vol. 459, 2009, pages 234 - 238
MAYO, D. W.; MILLER, F. A.; HANNAH, R. W.: "Course notes on the interpretation of infrared and Raman spectra", 2004, JOHN WILEY & SONS
SILVERSTEIN, R. M.; WEBSTER, F. X: "Spectrometric identification of organic compounds", 1998, JOHN WILEY AND SONS
JAMROZ, D.; MAR6CHAL, Y: "Hydration of sulfonated polyimide membranes. II. Water uptake and hydration mechanisms of protonated homopolymer and block copolymers", J. PHYS. CHEM. B, vol. 109, 2005, pages 19664 - 19675
LEE, H. Y.; RWEI, S. P.; WANG, L.; CHEN, P. H: "Preparation and characterization of core-shell polyaniline-polystyrene sulfonate@Fe 0 nanoparticles", MATER. CHEM. PHYS., vol. 112, 2008, pages 805 - 809, XP025656782, DOI: doi:10.1016/j.matchemphys.2008.06.050
TANG, J.; JING, X.; WANG, B.; WANG, F: "Infrared spectra of soluble polyaniline", SYNT. MET., vol. 24, 1988, pages 231 - 238, XP024158859, DOI: doi:10.1016/0379-6779(88)90261-5
Attorney, Agent or Firm:
CASCIANO, Lidia et al. (Via Viotti 9, Torino, IT)
Download PDF:
Claims:
CLAIMS

1. A method for obtaining polyaniline/reduced graphene oxide composites comprising the steps of:

- dispersing the graphene oxide in an acid aqueous solution containing an emulsifying agent to obtain a graphene oxide dispersion;

dissolving one or more aniline oligomers in an organic solvent to obtain an oligomer solution;

mixing the oligomer solution with the graphene oxide dispersion, said oligomer being added in a stoichiometric excess compared to the quantity required to complete the graphene oxide reduction;

- adding to the suspension of the polyaniline/reduced graphene oxide composite an oxidizing agent in a stoichiometric quantity compared to said excess of oligomer so as to oxidize the excess of said oligomer to obtain a suspension of the polyaniline/reduced graphene oxide composite.

2. A method according to the preceding claim, wherein said oligomer is an aniline dimer.

3. A method according to any one of the preceding claims, wherein said oligomer is alternatively substituted in one of the ortho and meta positions to the nitrogen atom or on the nitrogen atom itself with a radical selected from the group consisting of methoxyl, ethoxyl, propyloxyl, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertbutyl, pentyl, phenyl, sulfonyl, vinyl. 4. A method according to any one of the preceding claims, wherein said emulsifying agent is selected from the group consisting of poly(styrene sulfonate), dodecylbenzenesulfonate, methylbenzenesulfonate (MBSA) , 2- aminoethylphosphonate, polyacrylate, adipate, poly (2- acrylamido-3-methyl-l-propane sulfonate) , dodecyldiphenyl oxide disulfonate, N, N' -dimethyl (methacryloylethyl ) ammonium propane sulfonate, 2-acrylamido-2-methyl-l-propane sulfonate, isophthalic 5-sulfonate.

5. A method according to any one of the preceding claims, wherein said organic solvent is selected from the group consisting of 1,2- butanediol, 1, 3-butanediol, 1, 3-propanediol, 1, 4-butanediol, 1,4- dioxane, 1, 5-pentanediol, 1-propanol, 2-butoxyethanol, 2-propanol, acetaldehyde, acetic acid, acetone, acetonitrile, butyric acid, diethanolamine, diethylenetriamine, dimethoxyethane, di- methylsulfoxide, N,N-dimethylformamide, ethanol, ethylamine, ethylene glycol, formic acid, furfuryl acid, glycerol, methanol, methyldiethanolamine, methyl isocyanide, propanoic acid, propylene glycol, pyridine, tetrahydrofuran, triethylene glycol, N- methylpirrolidone, N, N-dimethylacetamide .

6. A method according to claim 1, characterized in that said oxidizing agent is selected from the group consisting of ammonium persulfate, Cu2+, Cu+, Fe3+, Pd2+, Mn04~, Sb+5, Ag+, Au3+, Au+, Pt2+, Cr2072~, Rh+, Ce+, Mn3+, Co3+, Cr042_, S20,f2 salts, hydrogen peroxide and gaseous oxygen.

7. A method according to claim 6, characterized in that said oxidant is ammonium persulfate.

8. A method according to claim 1, characterized in that it includes a heating step after said step of mixing said oligomer solution with said graphene oxide dispersion.

9. A method according to the preceding claim, wherein said heating is carried out over a temperature interval between 40 and 90°C.

10. A method according to any one of the claims from 8 to 9, wherein said heating is carried out for a time interval between 20 minutes and 6 hours . 11. A method according to any one of the preceding claims, wherein said aqueous acid solution is an aqueous solution of an acid selected from the group consisting of hydrochloric, nitric, sulfuric and phosphoric acid.

12. A use of the composite obtained according to the method of any one of the preceding claims as an ink for electromagnetic applications.

13. A use of the composite obtained according to the method of any one of the claims from 1 to 11 for the realization of elements selected from the group consisting of capacitors and super-capacitors with an adaptive capacity in sign and absolute value, having a positive or negative capacity and/or overcapacity.

Description:
"ME THOD FOR THE PREPARATION OF POLYAN I LINE /REDUCED GRAPHENE

OXIDE COMPOSI TES"

TECHNICAL FIELD

The present invention concerns a method for obtaining polyaniline/reduced graphene oxide composites. In particular, said composites are used as conductive inks and in other electrical and electronic applications such as: thermoelectrical , electrochemical, electromagnetic, electromechanical, electro-luminescent, electro-rheological and chemical applications, and for the production of membranes and sensors.

BACKGROUND ART

The intrinsically conductive polymers (ICPs) owe their electrical conductivity to the presence of a π electronic system of conjugated type in their structure 1-3 . Polyaniline (PANI) is an ICP which shows relatively low conductivity values compared to other ICPs such as doped polyacetylene or polyphenylene, but has the advantage of presenting high stability and workability 4 . Due to its easy preparation, good ambient stability, interesting redox properties and potential for applications in electronic and optical devices 5 , polyaniline has become one of the most important conductive polymers and has been intensely studied over the last two decades 6-7 . In a recent study 8 it was demonstrated that polyaniline can be used for the synthesis of functional inks which can be used for digital printing and deposited as thin films on flexible polymer substrates; polyaniline also shows particular electronic properties, such as negative overcapacity in the low frequency range. The particular trend of the charge vs. DC voltage diagram, in a "butterfly" form, is clear evidence of the underlying memristive, or better "memcapacitive" properties, as suggested in Di Ventra et al. 9 . Promising memristive properties have been found in devices produced with nanocomposites of PANI-graphene , which provide the base for future application in neuromorphic systems 11-12 .

Although ten years have elapsed since its discovery 13 , two- dimensional graphene with honeycomb lattice continues to arouse great interest due to the non-conventional phenomena associated with this material, mainly originating from the fact that the electrons belonging to the carbon atoms are obliged to move in the plane defined by the graphene sheet according to paths with hexagonal symmetry, a fact which makes them similar to massless particles 14 . The introduction of graphene in PANI matrices to form nanocomposite structures of PANI/graphene has led to an improvement in the electronic characteristics of the ICP and also to interesting new electronic effects. In particular, in accordance with the quanto-relativistic effects in the scattering of electrons due to short-radius disturbance potentials such as those introduced by charged groups into the ad acent ICP matrix, the massless Dirac fermions which interfere with small scattering centres make a negligible contribution to the overall resistivity. Only in the case of resonant scattering can it be found that the contribution to the resistivity is equal to that of a non-relativistic electron gas 15 . Due to the presence of oxygen functions on the basal planes and on the edges, which make them very hydrophilic, graphene oxide sheets (GO) are often preferred to graphene in the formulation of polymer composites, since in water they swell up and are easily dispersed 16 .

Furthermore, it has been recognised for some time that GO has strong oxidising properties 17 and it has therefore been used in the one-pot synthesis of PANI/graphene composites, coupling the GO reduction process with the oxidative polymerisation process of the aniline precursor 18 . However, this process has a limiting phase consisting in dimerization of the aniline precursor .

A known method of synthesising PANI/reduced graphene oxide composites uses a process in which a dispersion of graphene oxide in the presence of an anionic emulsifying agent is mixed with a solution of an aniline oligomer in an organic solvent.

However, the composite obtained has the drawback of resulting only in a well-defined and limited quantity of PANI formed in a stoichiometric ratio with respect to the reduction of graphene oxide.

The need is therefore felt in the art for an alternative method for the preparation of polyaniline and reduced graphene oxide composites starting from low toxicity reagents, which is conducted in an aqueous medium, which is quicker and simpler than the known methods, which provides a highly regular product and allows the preparation of stable reduced graphene polyaniline solutions with polyaniline/reduced graphene oxide ratio that can be varied as required for applications such as flexible electronics obtained by inkjet printing, and improved properties for application in electronic devices.

DISCLOSURE OF INVENTION

The object of the present invention is therefore to provide a new preparation method which is free from the drawbacks of the methods described above.

Said object is achieved by the present invention, since it relates to a method for the preparation of polyaniline and reduced graphene oxide composites according to claim 1 and the use of said composite according to claims 12 and 13.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will now be described in detail with reference to the Figures of the attached drawings, in which:

Figure 1 illustrates the UV-vis absorption spectra of the

PANI-PSS, PPG and CE-PPG composites;

Figure 2 illustrates the weight loss in thermal degradation (TGA) under nitrogen flow of the PANI-PSS composite ;

Figure 3 illustrates the weight loss in thermal degradation (TGA) under nitrogen flow of the PPG composite;

Figure 4 illustrates the weight loss in thermal degradation (TGA) under nitrogen flow of the CE-PPG composite;

Figure 5 illustrates a) the curve IV of a group of PPG samples printed by inkjet (width 1 mm, different number of overprints) which shows the insulating behaviour, b) the curve IV of a group of CE-PPG samples printed by inkjet (width 1 mm, different number of overprints) which shows the ohmic conduction behaviour, c) cyclic IV measurements (10 repetitions) of CE-PPG samples after subtraction of the linear ohmic contribution, d) cyclic IV measurements (10 repetitions) of CE-PPG samples which show the memristive behaviour with a small hysteresis;

Figure 6 illustrates a) the impedance modulus between 20 Hz and 2 MHz for a group of PPG samples printed by inkjet (width 1 mm, 2 and 10 overprints) subjected to sinusoidal excitation with amplitude of 10V, b) the impedance phase between 20 Hz and 2 MHz for a group of PPG samples printed by inkjet (width 1 mm, 2 and 10 overprints) subjected to sinusoidal excitation with amplitude of 10V, c) the Nyquist graph for a PPG sample printed by inkjet with 2 overprints (width 1 mm thickness) subjected to sinusoidal excitation with amplitude of 10V and cyclizing the DC contribution from -40 to +40V, d) the Nyquist graph for a PPG sample printed by inkjet with 10 overprints (1 mm width) subjected to sinusoidal excitation with amplitude of 10V and cyclizing the DC contribution from -40 to +40V, e, f ) Comparison between the real part (e) and imaginary part (f) of the impedance for two CE-PPG devices printed with different number of overprints; Figure 7 illustrates a) series resistance in a device printed in 2 overprints of 1 mm of PPG subjected to a sinusoidal signal of 15 kHz with an overlapped voltage repeated cyclically between -40 and +40V, b) series capacity in a device printed in 2 overprints of 1 mm of PPG subjected to a sinusoidal signal of 15 kHz with an overlapped voltage repeated cyclically between -40 and +40V, c) modulation of the series resistance in a device printed in 2 overprints of 1 mm of PPG subjected to a sinusoidal signal of 15 kHz with an overlapped voltage repeated cyclically between -40 and +40V, d) series capacity on CE-PPG devices analysed in figure 6e and 6f ;

Figure 8 illustrates a) the FT-IR spectrum for the PANI- PSS composite, b) the FT-IR spectrum for the PPG composite, c) the FT-IR spectrum for the CE-PPG composite.

BEST MODE FOR CARRYING OUT THE INVENTION

According to a first aspect of the invention a method is provided for obtaining polyaniline and reduced graphene oxide composites comprising the steps of:

- dispersing the graphene oxide in an acid aqueous solution containing an emulsifying agent to obtain a dispersion of graphene oxide;

dissolving one or more oligomers of the aniline in an organic solvent to obtain an oligomer solution;

mixing the oligomer solution with the dispersion of graphene oxide, said oligomer being added in stoichiometric excess with respect to the quantity required for completing the reduction of the graphene oxide;

- adding to the suspension of the polyaniline and reduced graphene oxide composite an oxidising agent in stoichiometric quantity with respect to said excess of oligomer so as to oxidise said oligomer excess to obtain a polyaniline and reduced graphene oxide composite.

Advantageously, the present method allows a composite to be obtained containing polyaniline chains having greater regularity since starting from the oligomer reduces the statistical probability of ramification in the ortho position of the aniline which is also reduced by the steric effects; the product thus obtained due to the presence of the emulsifier which separates the reduced graphene oxide (rGO) sheets and bonds the polyaniline to the graphene forms stable solutions also in organic solvents such as DMSO thereby simplifying the end use as ink in inkjet printing techniques.

Unlike the methods that make use of aniline as a starting monomer, the polymerisation starting from oligomers, preferably dimers, does not entail the use of toxic reagents, making the reaction easier to perform. Lastly the use of oligomers allows the reduced graphene oxide concentration in the end composite to be modulated, so that the use thereof can be limited to the quantity strictly necessary, thereby permitting variation of the conductivity (which decreases as the quantity of graphene decreases) of the compound according to the type of application required.

The use of an excess of oligomer which is subsequently oxidised by an oxidising agent allows the preparation of a composite containing an even greater quantity of polymer with respect to the composites of the known art, thus significantly improving the resonance scattering effects.

In this text "oligomer" means a compound resulting from the polymerisation of a finite and reduced number of monomer units, preferably from 2 to a maximum of 10 monomer units.

In one embodiment the oligomers of the aniline can if necessary be substituted in the ortho and meta positions to the nitrogen atom or on the nitrogen atom itself with a radical selected from the group consisting of methoxyl, ethoxyl, propyloxyl, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertbutyl, pentyl, phenyl, sulfonyl, vinyl.

The use of an emulsifier overcomes the problem of solubilisation of the oligomers in aqueous solution forming a stable suspension.

In one embodiment, the aniline oligomer used is the dimer (N- phenyl-1, 4-phenylenediamine) (DANI) . The oligomer is dissolved in an organic solvent preferably chosen from the group consisting of 1 , 2-butanediol , 1,3- butanediol, 1 , 3-propanediol , 1 , 4-butanediol , 1,4-dioxane, 1,5- pentanediol, 1-propanol, 2-butoxyethanol , 2-propanol, acetaldehyde, acetic acid, acetone, acetonitrile, butyric acid, diethanolamine, diethylenetriamine, dimethoxyethane, dimethylsulfoxide, N, N-dimethylformamide, ethanol, ethylamine, ethylene glycol, formic acid, furfuryl alcohol, glycerol, methanol, methyl diethanolamine, methyl isocyanide, propanoic acid, propylene glycol, pyridine, tetrahydrofuran, triethylene glycol, N-methylpyrrolidone, N, N-dimethylacetamide .

The graphene oxide is suspended in an acid aqueous solution containing the anionic emulsifier, for example chosen from the group consisting of sulfonates, phosphorylates and carboxylates , preferably chosen from the group consisting of poly(sodium 4-styrene sulfonate) (PSS), dodecylbenzenesulfonate (DBSA) , methylbenzenesulfonate (MBSA) , 2-amino-ethyl-phosphonate, polyacrylate, adipate, poly (2- acrylamido-3-methyl-l-propane sulfonate) , dodecyl diphenyloxide disulfonate, N, N' -dimethyl (methacryloyl ethyl) ammonium propane sulfonate, 2-acrylamido-2-methyl-l-propane sulfonate, isophthalic 5-sulfonate. The acid aqueous solution is an aqueous solution of an acid selected from the group consisting of hydrochloric acid, nitric acid, sulphuric acid and phosphoric acid. The method of the invention, despite the use of the aniline dimer, notoriously non-soluble in water, can be carried out in an aqueous environment due to the formation of a stable emulsion following the action of the emulsifier present in the graphene oxide solution.

During the polymerisation reaction, the graphene oxide acts as an oxidiser of the oligomer which polymerises to polyaniline, while the graphene oxide is reduced by the oligomer forming the reduced graphene.

The oligomer solution is added to the graphene oxide suspension in a quantity such that the oligomer contained in it is in stoichiometric excess with respect to the quantity required to complete the reduction of the graphene oxide.

Advantageously, the dimer proved to be a more effective reducing agent for the graphene oxide than the monomer aniline and therefore the reaction speed is higher, determining a complete reaction in the space of 1 hour at 80°C against a reaction time of 24 hours at 70°C in the case of use of the monomer aniline 21 .

In one embodiment, after mixing the graphene oxide suspension with the oligomer solution, the reaction mixture was heated to a temperature between 40 and 90°C, preferably between 60 and 80°C, in particular for a time interval between 20 minutes and 6 hours, to promote and accelerate the polymerisation. If a reduction in the reduced graphene oxide load is desired, the dianiline can be substituted with an oligomer with higher molecular weight.

The excess of oligomer, not oxidised by the graphene oxide, is subsequently oxidised with an oxidising agent, preferably an oxidising agent having an oxidisation potential greater than 0.1 volt, more preferably an oxidising agent selected from the group consisting of ammonium persulfate, salts of Cu 2+ , Cu + , Fe 3+ , Pd 2+ , Mn0 4 ~ , Sb +5 , Ag + , Au 3+ , Au + , Pt 2+ , Cr 2 0 7 2~ , Rh + , Ce + , Mn 3+ , Co 3+ , Cr0 2_ , S 2 0,T 2 , hydrogen peroxide and gaseous oxygen.

In one embodiment, the oxidising agent is ammonium persulfate.

Further characteristics of the present invention will become clear from the following description of some merely illustrative non-limiting examples.

The following abbreviations are used in the examples below: min (minutes), h (hours), με (microseconds), g (grams), mg (milligrams), ml (millilitres ) , nm (nanometres), Da (Dalton) , mmol (millimoles ) , M (molar), W (Watt), °C (degrees centigrade), Hz (Hertz), V (Volt), PANI (polyaniline) , ICPs (intrinsically conductive polymers), DANI (dimer of aniline, N-phenyl-1, 4-phenylenediamine) , GO (graphene oxide), rGO (reduced graphene oxide), PSS (poly(sodium 4-styrene sulfonate) ) , DMSO (dimethylsulfoxide) , STM (scanning tunnelling microscope) , APS (ammonium persulfate) , HC1 (hydrochloric acid) .

Example 1

Synthesis of the polyaniline and reduced graphene oxide composite according to the present invention (CE-PPG)

The single layer graphene oxide in 300-800 nm sheets with thickness of 0.7-1.2 nm was purchased from CheapTubes (Brattleboro, VT, USA) and used in the state in which it was received. The aniline dimer (N-phenyl-1 , 4-phenylenediamine 98%), the poly(sodium 4-styrene sulfonate) (PSS, PM = 70000 Da) , the hydrochloric acid (HC1, 37% by weight) , the dimethylsulfoxide (DMSO, 99.9%) and the ammonium persulfate (APS, 98%) were obtained from Sigma Aldrich (Milan, Italy) and used in the state in which they were received. 0.050 g of GO were added to 100 ml of a solution of PSS (0.500 g) in HC1 0.1 M. The dispersion was treated with an ultrasound probe for 1 h (50 W) so as to obtain a stable dispersion of GO. This was then diluted to 300 ml with a 0.1M solution of HC1.

0.411 g of PSS were then added.

A solution of DANI (4mmol, 0.921 g) in 10 ml DMSO was prepared separately.

10 ml of this solution were added dropwise to the oligomer dispersion to obtain an emulsion of DANI. The solution was heated to 80°C for 1 h to obtain complete reduction of the graphene oxide. During the heating a green precipitate formed. The solution was cooled to 25°C and an excess of APS was added slowly (5 mmol, 1.141 g) previously dissolved in 100 ml of HC1 0.1 M to oxidise the excess of DA I. After 4 hours, the precipitate was filtered and washed several times with distilled water until discolouration, then with methanol and lastly dried at 60°C until a constant weight was obtained . Example 2

Synthesis of the polyaniline and reduced graphene oxide composite according to the known art (PPG)

As reference material, a polyaniline and reduced graphene oxide composite was prepared as illustrated in TO2013A000561.

0.100 g of GO were added to 100 ml of a PSS solution (1.000 g) in HC1 0.1 M. The dispersion was treated with an ultrasound probe for 1 h (50 W) so as to obtain a stable dispersion of GO.

A solution of DANI (4.34 mmol, 1.000 g) in 10 ml DMSO was prepared separately.

10 ml of this solution were added dropwise to the oligomer dispersion to obtain an emulsion of DA I . The solution was heated to 80°C for 1 h to obtain complete reduction of the graphene oxide. During the heating a green precipitate formed following oxidisation of the DANI to form PA I . The precipitate was separated by centrifugation and washed several times with distilled water and ethanol. The final product (PPG), a green powder, was dried at 60°C until obtaining a constant weight.

Example 3

Physical-chemical characterisation of the composite obtained according to the invention (CE-PPG) and comparison with the composite of the known art (PPG)

The structure of the composites obtained in examples 1 and 2 was characterised to evaluate the reduction of GO and the concomitant oxidisation of DA I.

UV-vis spectrum

The UV-Vis absorption spectra were recorded in the wavelength range from 250 to 1100 nm at ambient temperature on solutions in DMSO using a UV-vis-NIR Cary 5000 spectrometer.

THe UV-visible spectra of the composites in a DMSO solution are shown in figure 1, in which the acronym PANI-PSS indicates a polyaniline composite containing PSS as doping agent, PPG is a polyaniline and reduced graphene composite, doped with PSS, prepared as illustrated in example 2, and CE-PPG is the composite of the invention. As in many other solvents, the PANI-PSS composite adopts in DMSO a compact spiral conformation. In this case, the main bands observed are: the transition n-n* at approximately 314 nm partially overlapped with absorption of the PSS; the polaron-n* band at 443 nm for the protonated conductive PANI-PSS, which gives the solution its green colour; the absorption band at approximately 600-650 nm for the np transition, observed for the base emeraldine 21 . This latter band reveals that the PANI-PSS composite is not completely protonated, as scheduled for the PANI doped with a macromolecular agent without secondary doping.

The presence of relatively high quantities of graphene modifies the UV-vis spectra in the samples of PPG composite, in which the transition n-n* at 292 nm is still recognisable, but the absorbance of the graphene which overlaps the band shifts the maximum towards lower wave numbers. For the same reason, it is difficult to identify the polaron-n* band (approximately 440 nm) , while the np transition derived from the emeraldine in the base form is only just recognisable.

On the other hand, the samples of the CE-PPG composite, which contain a higher quantity of PANI, show bands more similar to PANI-PSS, even if the presence of the graphene shifts the peak maximums. The n-n* transition is observed at 284 nm, the polaron-n* band around 437 nm and the np transition around 600-650 nm.

Infrared spectrum

The spectra of the Fourier transform infrared spectroscopy ( FT- IR) were collected with an FT- IR Nicolet 5700 (ThermoFisher) spectrometer.

The samples were prepared by deposition of a solution in DMSO on a silicon wafer. The measurement was taken from the mean of 64 spectra collected at a resolution of 2 cnf 1 from 4000 to 400 cnf 1 .

The complete FT-IR spectra are shown in figure 8. The assignment of the peaks is shown in the following tables 1, 2 and 3. Table 1

Table 2 Assignment Assignment cm 1 v H 2 0

3450 v NH 3305 v CH v CH 3052 v CH v CH 3025 v as CH 2 2924 v s CH 2 2850 vArom 1600 v quinone ring 1568 vArom 1502 v benzenoid ring 1488 vCN 1309 asSC 1226

Absorption peak

1151 NdQdN*

Bending vibration on plane

1122 of benzene ring

sSC 1031

Bending vibration on plane

1004 of benzene ring

Bending outside the plane

for the para-disubstituted 824 benzene

Bending outside the plane of the quinone 750 CH

v C-S of the benzenoid ring 668

Table 3

PPG

PSS PANI

Assignment Assignment cm 1 v H 2 0

3450

The FT-IR spectrum of the PPG composite is very similar to that of the PANI-PSS composite, since the main peaks of the PSS and the PANI are present. The PSS shows the characteristic peaks of the polystyrene and of the sulfonic group. The area between 3100 and 3000 cnf 1 shows the vibration of the bonds between the hydrogen and the aromatic carbon, while the area between 3000-2800 cnf 1 shows the elongation of the bonds between hydrogen and carbon of the aliphatic chain 32 . The carbon-carbon stretching of the benzene ring 33 is present at 1600 and 1503 cnf 1 . The peaks at 1120 and 1004 cnf can be assigned to the vibration of the skeleton in the plane of the benzene ring and to the vibration outside the plane of the benzene ring 33 . The antisymmetric and symmetric vibrational absorption peaks of the SC>3 ~ group can be assigned, respectively 33 , to the peaks at 1222 and 1030 cnf 1 . The characteristic band centred at 622 cnf 1 corresponds to the C-S elongation of the benzene ring 34,35 . The presence of PANI was confirmed by the peak at 3227 cnf 1 due to the elongation of the nitrogen hydrogen bond of the secondary aromatic amine 33 and by the carbon hydrogen elongation of the aromatic ring between 3100 and 3000 cnf 1 .

In the regions of the aromatic rings, the PANI presents a band at 1566 cnf 1 attributed to the C=N stretching of the quinone diimino unit (the oxidised form of the PANI) 36 . The C-C stretching of the aromatic ring of the benzonoid diamine unit (the reduced form of PANI) 36 appears at 1489 cnf 1 and, lastly, the band at 746 cnf 1 is due to the band of the CH outside the plane of the quinone ring 33 .

The FT-IR spectra of the PPG and CE-PPG samples are very similar to those of the PANI-PSS, thus confirming the formation of PANI also in the case of PPG samples. Thermogravimetric analyses

The thermogravimetric analyses (TGA) were conducted on 10 mg samples using a TG 209 Fl Libra ® (NETZSCH GmbH) thermogravimetric analyser, heating speed 10°C min -1 , from 25°C to 800°C under nitrogen flow (60 cm 3 min -1 ) . The thermal degradation temperatures reported refer to the maximum weight loss rate (T max ) . The residual percentage by weight was evaluated at 800°C. The experimental error was estimated to be generally below 0.05 mg (approximately ± 0.5%) . As can be seen in figure 2, the PANI-PSS composite shows three main weight losses: the first at 204°C, resulting from evaporation of the humidity and degassing of small molecules (for example HC1) from the starting solution; the second and third peak, at 324°C and 394°C respectively, correspond to the thermal degradation of PA I .

For the PPG composite (figure 3), the complete absence of the peak at 220°C, due to the loss of oxygen, confirms the reduction of the initial GO (approximately 50% by weight) due to the interaction with DANI . The TGA curve of the weight loss is very similar to that of the PA I-PSS composite, showing a first weight loss below 200°C due to degassing of small molecules. The second and third phases of the weight loss are in the same thermal interval as those observed for PANI-PSS, confirming that the polymerisation has taken place.

Lastly, the TGA of CE-PPG (figure 4) is substantially identical to that of the PANI-PSS. However, as scheduled, the final weight at 800°C is lower than approximately 43.6% with respect to the initial weight as against 41.5% of the PANI-PSS composite, confirming the presence of the graphene, which is non volatile.

DC characteristics

The synthesised materials as described in examples 1 and 2 were dispersed in DMSO to prepare the printable ink formulation. To increase the solubility of the inks, mechanical mixing and an ultrasound bath were used. The solutions are stable for 1-2 days prior to gelation. Therefore, just before printing, the solutions were treated in an ultrasound bath for one hour in order to re-disperse the ink, and then placed in a 3 ml tank and loaded in the inkjet printing system. The jet parameters fixed, using an asymmetric impulse, are the following: first rise time 12 με, hold time 15 με, fall time 5 με, echo time 20 με, second rise time 2 με, waiting voltage 0 V, maintenance voltage 35 V, echo voltage - 13 V. The analysis of the DC characteristics of the composites PPG and CE-PPG (figure 5) show that the percolation conduction paths are favoured in the CE-PPG samples, in which the PANI is present in a larger quantity than in the PPG samples, thus improving the conductance from an insulating behaviour of the PPG (figure 5a) to an ohmic dissipative behaviour of the CE- PPG (figure 5b) . The current that crosses the CE-PPG is five orders of magnitude greater than the one measured for the PPG, in the same potential interval applied. A confirmation of the reduction of the GO to graphene derives from the direct comparison with the pure PANI which has a conductivity three orders of magnitude greater than the CE-PPG. Another important characteristic is the extremely clear signal, as shown by the error bar in figure 5b.

Furthermore, by cycling IV measurements, it is possible to exploit also the memristive properties 22 (figure 5c), whose characteristic "butterfly" diagram can be seen better after subtracting the linear ohmic contribution (figure 5d) .

A particular behaviour can be observed by applying a combination of DC and AC stimuli. In particular, in figure 6, the evidence of a persistent negative capacity in the entire frequency range is proved for PPG printed with a low number of overprints: the phase is saturating at +90° from values below 10kHz up to 1MHz (Figure 6a and 6b) . On the other hand, the PPG printed with a high number of overprints shows an impedance phase which grows statistically up to +90° only below 500 Hz, while at higher frequencies it behaves like an ohmic conductor. Seemingly, the impedance does not depend on the DC polarisation, as shown for the PPG samples (figures 6c and 6d) . The most promising results were obtained in samples with high conductivity (CE-PPG) , in which the resistive and reactive parts of the impedance show a resonant diffusion, which occurs in the kHz regime and depends on the thickness of the sample (figures 6e and 6f) . In some PPG samples this resonance produces a stable signal, which leads to perfectly voltage-controlled impedance variations which are visible both in the resistive component and in the reactive component of the impedance (figures 7a, 7b and 7c) . This property is extremely interesting because this material can be immediately used as a voltage-controlled phase shifter element.

Many experimental examples have been based on hierarchical structures consisting of graphene or other carbon-based nanomaterials in combination with the PANI for applications in supercapacitors ' ' , but so far a clear definition of the phenomena that occur at nanometric level has not been provided . The impedance spectra are normally adapted to models that include ideal elements, like the Constant Phase Element 26 or other diffusion circuit elements, well known in electronics, such as the Warburg impedance element, which are used simply to improve the adaptability.

An attempt to describe the negative permittivity values in PANI/graphene nanocomposites was made in a recent study 27 which evokes the surface plasmonic resonance and the tunability of the graphene Fermi level voltage. Although the graphene can show a controlled voltage switching from the relativistic state of the Dirac fermion to a conventional state similar to metal , the plasmonic frequencies are generally much higher (10-100 THz) than the phenomena described in this patent (typical frequencies in the order of kHz) 22 .

Therefore, the printed inkjet devices produced according to this example have practical applications in the electronics sector as adaptable supercapacitors, provided with positive or negative overcapacity according to the operating frequency. Considering the resistive component of the impedance, the enormous contribution found in the CE-PPG sample in the interval between 500 Hz and 5 kHz (particularly evident for the sample printed with high number of overprints, fig. 6e) can be explained by a resonance scattering, once again, in which the quanto-relativistic nature of the graphene is such that the scattering potentials make a non-negligible contribution to the resistivity 15 .

A system has therefore been described in which the quanto- relativistic properties of the graphene emerge, inducing a transfer of resonant energy between Dirac fermions and small scattering centres adjacent to the PANI chains. These events show the occurrence of extremely interesting physical phenomena, so far never reported in one single material, such as negative capacity at high frequency (MHz), voltage- controlled phase shift and negative/positive diverging capacities at the characteristic resonance frequency (kHz) . These properties can be exploited in advanced electronic devices, taking advantage of the possibility of use in solution and direct inkjet printing.

References

I. Unsworth, J., Lunn, B. A., Innis, P. C, Jin, Z., Kaynak, A., Booth, N . G. J. Intell. Mater. Syst. Str. 3, 380-395

(1992) .

2. Schoch, K. F . IEEE Electr. Insul . Mag. 10, 29-32 (1994); Angelopoulos, M. IBM J. Res. Develop., 45, 57-75 (2001);

Gospodinova, N., Terlemezyan, L. Prog. Polym. Sci. 23, 1443- 1484 (1998) .

3. Gospodinova, N., Terlemezyan, L. Prog. Polym. Sci. 23, 1443-1484 (1998) .

4. Bhadra, S., Dipak, K., Singha, N. K., Lee, J. Prog.

Polym. Sci. 34, 783-810 (2009) .

5. Bocchini, S., Chiolerio, A., Porro, S. et al . J. Mater. Chem. C 1, 5101-5109 (2013) .

6. MacDiarmid, A. G. Angew. Chem. Int. Ed. 40, 2581-2590 (2001) .

7. Kang, E., Neoh, K. G., Tan, K. L. Prog. Polym. Sci. 23,

277-324 (1998) .

8. Chiolerio, A., Bocchini, S. and Porro, S. Adv. Funct . Mater. 24, 3375-3383 (2014) .

9. Di Ventra, M., Pershin, Y.V., Chua, L.O.,

arXiv: 0901.3682vl

10. Berzina, T. S., Gorshkov, K. V., Erokhin, V. V., Nevolin, V. K., Chaplygin, Y. A. Russian Microelectronics 42, 27-32 (2013) .

II. Lu, W. Nature Mater. 12, 93-94 (2013) .

12. Pickett, M. D., Medeiros-Ribeiro, G. & Williams, R. S. Nature Mater. 12, 114-117 (2013) .

13. Novoselov, K., Geim, A., Morozov, S., Jiang, D., Zhang, Y., Dubonos, S., Grigorieva, I., Firsov, A. Science 306, 666-

669 (2004) .

14. Geim, A. K., Novoselov, K. S. Nat. Mater. 6, 183-191 (2007) .

15. Katsnelson, M.I., Novoselov, K.S., Solid State Commun 143, 3-13 (2007) .

16. Rourke, J. P., Pandey, P.A., Moore, J. J., Bates, M., Kinloch, I.A., Young, R.J., Wilson, N.R. Angew. Chem. Int. Ed.

50, 3173-3177 (2011)

17. Boehm HP, Clauss A, Fischer G, Hofmann U. Fifth

Conference on Carbon, Pergamon Press, Oxford 1962, p. 73.

18. Xu LQ, Liu YL, Neoh KG, Rang ET, Fu GD . Macromol. Rapid Comm. 2011; 32(8) : 684-8.

19. Shim, Y. B., Park, S. M. Electrochemistry of conductive polymers VII. Autocatalytic rate constant for polyaniline growth. Synth. Met. 29/1, 169-174 (1989) .

20. Bocchini, S., Chiolerio, A., Porro, S. Metodo per la preparazione di compositi di polianilina e ossido di grafene ridotto. Italian Patent Application n. TO2013A000561, 4th July 2013.

21. Xia, Y., Wiesinger, J. M., MacDiarmid, A. G., Epstein, A. J. Camphorsulfonic acid fully doped polyaniline emeraldine salt: conformations in different solvents studied by an ultraviolet/visible/near-infrared spectroscopic method. Chem. Mater. 7, 443-445 (1995) .

22. Pershin, Y. V., Di Ventra, M. Memory effects in complex materials and nanoscale systems. Adv. in Phys . 60, 145-227

(2011) .

23. Meng, Y., Wang, K., Zhang, Y., Wei, Z. Hierarchical porous graphene/polyaniline composite film with superior rate performance for flexible supercapacitors . Adv. Mater. 25, 6985-6990 (2013) .

24. Plonska-Brzezinska, M. E., Breczko, J., Palys, B.,

Echegoyen, L. The electrochemical properties of nanocomposite films obtained by chemical in situ polymerization of aniline and carbon nanostructures . Chem. Phys. Chem. 14, 116-124

(2013) .

25. Lee, T. et al . Hybrid multilayer thin film supercapacitor of graphene nanosheets with polyaniline: importance of

establishing intimate electronic contact through nanoscale blending. J. Mater. Chem. 22, 21092-21099 (2012) .

26. Kochowski, S., Nitsch, K. Description of the frequency behaviour of metal-Si02-GaAs structure characteristics by electrical equivalent circuit with constant phase element. Thin Solid Films 415, 133-137 (2002) .

27. Zhu, J. et al . Carbon nanostructure-derived polyaniline metacomposites : electrical, dielectric, and giant

magnetoresistive properties. Langmuir 28, 10246-10255 (2012) .

28. Hill, A., Mikhailov, S., Ziegler, K. Dielectric function and plasmons in graphene . Europhys . Lett. 87, 27005 (2009) .

29. Monguzzi, A., Tubino, R. Meinardi, Upconversion-induced delayed fluorescence in multicomponent organic systems: role of Dexter energy transfer. F. Phys . Rev. B 77, 155122 (2008) .

30. Chen, H. C. et al . White-light emission from an

upconverted emission with an organic triplet sensitizer. Chem. Comm. 27, 4064-4066 (2009) .

31. Reineke, S. et al . White organic light-emitting diodes with fluorescent tube efficiency. Nature 459, 234-238 (2009) .

32. Mayo, D. W., Miller, F. A., Hannah, R. W. Course notes on the interpretation of infrared and Raman spectra (Hoboken, John Wiley & Sons, NJ, USA, 2004) .

33. Silverstein, R. M., Webster, F. X. Spectrometric

identification of organic compounds 6th ed Ch. 3 (John Wiley and Sons, New York, 1998) .

34. Jamroz, D., Marechal, Y. Hydration of sulfonated

polyimide membranes. II. Water uptake and hydration mechanisms of protonated homopolymer and block copolymers. J. Phys. Chem. B 109, 19664-19675 (2005) .

35. Lee, H. Y., Rwei, S. P., Wang, L., Chen, P. H.

Preparation and characterization of core-shell polyaniline- polystyrene sulfonate@Fe 3 C> nanoparticles . Mater. Chem. Phys. 112, 805-809 (2008) .

36. Tang, J., Jing, X., Wang, B., Wang, F. Infrared spectra of soluble polyaniline. Synt. Met. 24, 231-238 (1988) .