FIELD OF THE INVENTION

[0001] The invention relates to the field of chemical synthesis. More particularly, this invention relates to a method of synthesising a hollow silica vesicle, the silica vesicle thereby produced and its use in drug delivery and as part of an immunogenic composition.

BACKGROUND TO THE INVENTION

[0002] Any reference to background art herein is not to be construed as an admission that such art constitutes common general knowledge in Australia or elsewhere.

[0003] Inorganic hollow spheres have attracted considerable attention due to their unique morphology and potential use in a wide range of applications. They show good stability in solvents and body fluids, have excellent thermal properties and also high mechanical strength by comparison with their organic counterparts. These properties have seen them used in applications as varied as catalysis, drug/gene delivery, bio-imaging, as nanoreactors, low-dielectric constant materials and in separation technologies.

[0004] Methods have been developed to synthesize inorganic hollow spheres utilizing preformed templates to produce the desired characteristics. Some techniques involve a soft template approach, including micelles, emulsions, microemulsions etc. This approach has a number of drawbacks including the need for a significant amount of chemical based organic solvents or organic additives. A hard template approach, including single crystals and colloid spheres, has also been utilized to produce spheres with the required pore size followed by an etching step to remove the hard template. Such an approach is expensive, time-intensive and environmentally-unfriendly and has been shown to give relatively low yields of product. [0005] Silica vesicles are a type of hollow sphere constructed by supramolecular assembly in the absence of preformed templates. Silica vesicles with small particle sizes (generally smaller than 200 nm in diameter) have potential cell-based and/or animal appltcations due to their low toxicity and biodegradability. The void space inside the hollow morphology ca be used as a reservoir for high-capacity storage of cargo molecules and subsequent controlled release. The wall structure (including wall thicknes and porous nature) is crucial for both the immobilisation and release of cargo molecules. However, fine control over the pore size and entrance size within the walls of silica vesicles has proven to be a difficult challenge.

[0006] It would be useful to provide silica vesicles (SV) with controlled structures for the delivery of small molecules and larger biomolecul.es alike which overcomes or circumvents one or more of these problems.

SUMMARY OF INVENTION

[0007] According to a first aspect of the invention, there is provided a method of forming a silica vesicle including, the steps of:

(a) producing a silica formulation by adding a hydrolysab!e silica source to an aqueous solution comprising a block copolymer, the silica formulation being maintained at a temperature of less than 20°C, and agitating the formulation until silica-polymer composite vesicles form, followed by step (b) or step (c);

(b) raising the temperature of the silica formulation containing the silica-polymer composite vesicles to be between 25°C to 100°C and agitating the mixture to form silica-polymer composite vesicles having spherical structures within the vesicle walls;

(c) exposing the vesicles to a hydrothermal treatment; and

(d) calcining the vesicles, to thereby produce the silica vesicles. [0008] According to a second aspect of the invention there is provided a silica vesicle having;

(a) a particle diameter of between 30 to 70 nrn;

(b) a wall structure perforated by spherical pores; and

(c) an average pore entrance size of between 4 to 40 nm formed in the wall.

[0009] Preferably, the particle diameter is between 40 to 60 nm, more preferably about 45 to 55 nm, even more preferably about 50 nm,

[0010] A third aspect of the invention resides in a silica vesicle when produced by the method of the first aspect.

[0011] According to a fourth aspect of the invention there is provided a drug or chemical deliver system comprising a silica vesicle of the second or third aspects and a drug or chemical agent encapsulated within the vesicle or bound to an outer surface thereof.

[0012] Preferably, the drug is an organic drug molecule and the chemical agent is a pesticide,

[0013] A fifth aspect of the invention resides in an immunogenic composition comprising one or a plurality of silica vesicles of the second or third aspects and one or a plurality of immunogens and/or antigens.

[0014] Preferably, the immunogen is an immunogenic fragment of the bovine viral diarrhoea virus (BVDV). More preferably, the immunogen and/or antigen is the E2 protein, or a fragment thereof, of the BVDV.

[0015] A sixth aspect of the invention resides in a method of eliciting an immune response in a subject including the step of administering a therapeutically effective amount of the immunogenic composition of the fifth aspect [0016] A seventh aspect of the invention resides in a method of preventing o treating a disease or condition including the step of administering a therapeutically effective amount of the immunogenic composition of the fifth aspect to a subject in need thereof.

[0017] In one embodiment, the disease or condition is bovine viral diarrhoea.

[0018] An eighth aspect of the invention resides in the use of a silica vesicle of the second or third aspects and an immunogen in the manufacture of a medicament for the treatment of a disease or condition.

[0019] A ninth aspect of the invention resides in the use of a silica vesicle of the second or third aspects as an adjuvant.

[0020] The various features and embodiments of the present invention, referred to in individual aspects above apply, as appropriate, to other aspects, mutatis mutandis. Consequently features specified in one aspect may be combined with features specified in other aspects, as appropriate.

[0021] Further features and advantages of the present invention will become apparent from the following detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS

[0022] In order that the invention may be readily understood and put into practical effect, preferred embodiments wilf now be described by way of example with reference to the accompanying figures wherein:

[0023] FIG 1 is a series of FE-SE images of novel silica vesicles (A) SV-10-50 and (B) SV-10-50-140 after calcinations;

[0024] FIG 2 A-B shows a series of TEM images of as-synthesized SV-10-x-100 before calcinations;

[0025] FIG 3 is a proposed scheme showing the formation of the silica vesicles throughout three synthetic steps; [0026] FIG 4 A-D shows a series of TEM images of (A, B) SV-10-50 and (C, D) SV-10-50-140 after calcinations;

[0027] FIG 5 shows nitrogen sorption isotherm plots of SV-10-T2 (A), and SV-10-X-T3 (B) after calcinations, pore size distribution plots calculated from N ₂ sorption isotherms (C) BdB pore size distribution curves of SV-1 -T2 from adsorption branch in the range of 1 -30 nm, (D) BJH pore size distribution curves of SV-1.0-X-T3 from desorption branch;

[0028] FIG 6 is BdB pore size distribution from adsorption branch in the range of 1 -1 80 nm of SV-10-T2 (A) and SV-10-X-T3 (B) after calcinations;

[0029] FIG 7 is a series of TEM images of (A) SV-10-70, (B) SV-1 O-x-100, (C) SV-10-X-130, (D) SV-10-X-1-80 after calcinations, respectively;

[0030] FIG 8 is a series of TEM images of (A) 5V-10.-X-1 G0-I (aqueous layer), (B) SV-1 O-x-100-u (TEOS layer) and (E) SV-20-X-100 after calcinations and (C, 0} are images of the reaction mixture after step 1 with continuous stirring (C) or with only 10 min stirring and 24 h of static conditions (D);

[0031] FIG 9 is a series of cryo-TEM images of reaction solution at 10 °C (A) before adding TEOS and (B-D) after adding TEOS and after 12, 15 and 24 h, respectively;

[0032] FIG 10A is an ATR-FTIR spectra of the reaction mixture at 10 °C after adding TEOS in step (a) and FIG 10B is an ATR-FTIR spectra of the precipitate in the subsequent 70 °C treatment in step (b), in the SV-10-70 reaction system as a function of time;

[0033] FIG 1 1 is a graphical representation of the amount of adsorption of cytochrome c in the silica vesicles after calcination as a function of time (T = 25 °C);

[0034] FIG 1 is a series of TEM images of (A) pure SV-10-50-140 after calcination and (B-D) SV-10-50-140 loading of cytochrome c without tilting B), with single tilting angle in x axis of +50° (C) and -50° (D), respectively; [0035] FIG 13 is a TEM image of SV-10-50 loading of cytochrome c;

[0036] FIG 14 is FT!R spectra of (A) pure liquid n-ODMS, (B and C) SV-10-50 and (D and E) SV-10-50-140 after calcinations (B and D) or after hydrophobic modification (C and E), respectively;

[0037] FIG 15 is a series of TEM images of pure SV-10-50 after hydrophobic modification, before (A) and after (B) loading of ribonuclease A;

[0038] FIG 16 is a series of confocal microscopy images of SCC25 cells which are either in a control group (A-D), have been treated with FITC labelled SV-10-50 (E-H) or with SV-10-50-140 (l-L) with 25 ug/ml in 24 h;

[0039] FIG 17 is a g aphical representation of cell viability in an SCG25 cell line with a ribonuclease A dosage of 16 pg at 24 h and 72 h;

[0040] FIG 18 is a series of images showing the results of a semi-quantitative assay to determine the cytotoxicity of hollow silica vesicles using trypan blue Staining (0.2%) of MDBK cells; (a) 0.5 mg/ml SV-1 Q-X-100-A; (b) 0.1 mg/m! SV-1 -X-100-A; (c) 0.01 mg/ml SV-tQ-x-1 G0-A; (d) 0.5 mg/ml SV- O-x-140; (e) 0.1 mg/ml SV-10-X-140; (f) 0.01 mg/ml SV-10-X-140; (g) G.5mg/ml MCM-41 as synthesised vesicles (h) MDBK cells alone without silica vesicles;

[0041] FIG 19 is a gel analysis of the adsorption and desorption characteristics of the silica vesicles;

[0042] FIG 20 is a graphical representation of the results of a serie of ELISA assays indicating response of mice to injections of potential immunogenic compositions;

[0043] FIG 21 is a graphical representation of the results of an EL!SPOT assay of antigen specific IF -y secretion of murine sp!enocytes from immunised mice; [0044] FIG 22 is an image of an SDS-PAGE gel showing adsorption of oE2 on SV-140; Lane 1 - marker, lane 2 - oE2 protein, lane 3 - oE2/SV-140 supernatant, lane 4 - oE2/SV-140 pellet;

[0045] FIG 23 is a graphical representation showing end point titer data of test sera bleeds for the eight animals after the first and second immunisation. All the mice were administered 100 pL dose at 3 week intervals to the tail base. Sera of individual animals were diluted from 1 :100 to 1 :6400. The individual graph line in the chart represents individual animals (Ml to M8) in each group;

[0046] FIG 24 is a graphical representation showing end point titer data of test sera bleeds for the four animals maintained for long-term antibody responses after the second immunisation. Sera of individual animals were diluted from :100 to 1 :6400. The graph line in the chart represents the four individual animals (M5 to M8) in each group;

[0047] FIG 25 is a graphical representation showing detection of antigen specific IFN-γ secretion by ELISPOT assay of murine spienocytes from immunised mice. M1 to M4 are the individual mice in each treatment group. The bars in the figure indicate the number of cells producing IFN-γ in response to the oE2 antigen;

[0048] FIG 26 is a graphical representation showing detection of antigen specific IFN-y secretion by ELISPOT assay of murine spienocytes from immunised mice. M5 to 8 are the individual mice in each treatment group. The bars in the figure indicate the number of cells producing iFN-γ in response to the oE2 antigen;

[0049] FIG 27 is a series of images showing immunohistochemistry analyses to determine the induction of total IgG in the spleen sections of the immunised animals; oE2 plus Quil A positive treatment group a) 3 weeks post the final immunisation, b) 25 weeks post the final immunisation; 0E2/SV-140 nanovaccine treatment group c) 3 weeks post the final immunisation, d) 25 weeks post the final immunisation; unimmnised group e) 3 weeks post the final immunisation, f) 25 weeks post the final immunisation;

[0050] FIG 28 is a series of images showing the results of a istopatho!ogy assay to determine the effects of nanovaccine immunisations; i) Heart, ii) Kidney, iii) Injection sites, iv) Liver samples collected 3 weeks post the final immunisation a) oE2 plus Quil A, c) OE2/SV-140, e) unimmnised and samples collected 25 weeks post the final immunisation b) oE2 plus Quil A, d) OE2/SV-140, f) unimmunised;

[0051] FIG 29 is a gel image showing VirB9.2 adsorbed onto the 4 types of SV particles. The supernatants after adsorption show little protein remaining, indicating complete adsorption. The particle lanes show protein adsorbed. M SeeBlue 2 marker. 1 ; VirB9.2 protein. 2; SV100 adsorption supernatant. 3; SV10Q particles. 4; SV100NH ₂ adsorption supernatant. 5; SVI OONH ₂ particles. 6; SV140 adsorption supernatant. 7; SV140 particles. 8; SVI 4O H ₂ adsorption supernatant. 9; SV140NH ₂ particles;

[0052] FIG 30 is a graphical representation showing desorption of VlrB9.2 from SV particles in 0.1 % SLS, overnight at 37°C. SV100 and SV-140 show the best desorption. SV1 Q0 and SV140 show 100% desorption ;

[0053] FIG 31 is a graphical representation showing the humoral immune response against VirB9.1 protein 2 weeks after second immunisation at a dilution of 1 :4000. Good response is seen from animals immunised with VirB9.1 with Quil-A as well as SV100. Mixed injection of two proteins with Quil A as well as mixed nanoformulation also gives a similar high antibody response specific to VirB9.1. No cross reaction seen from animals only immunised with VirB9.2 protein;

[0054] FIG 32 is a graphical representation showing the humoral immune response against VirB9.2 protein after second immunisation. Good response is seen from animals immunised with VirB9.2 with Quil-A as well as SV100. Mixed injection of two proteins with Quil A as well as mixed nanoformulation also gives a similar high antibody response specific to VirB9.2, No cross reaction seen from animals only immunised with VirB9.1 protein;

[0055] FIG 33 is a graphical representation showing the humoral response against VirB9.1 protein, 1 :4000 dilution. Average response from 5 mice over the course of the experiment, showing relative immune response for the test groups. Pre-immune test bleed was negative and the antibody response shows increasing trend with injections. The trend was observed for both single and mixed nano -formulation;

[0056] FIG 34 is a graphical representation showing the cell mediated immune response against VirB9.1 protein. The antigen specific IFN-γ secretion by ELISPOT assay of murine splenocytes from 5 individual mice, (A) Mice injected with VirB9.1 + Qui!-A show comparable results to VirB9.1 +SV100 and also to the multivalent injections VirB9.1/9.2+Guil-A and VirB9.1 /9.2 + SV100. ConA is the internal control. (B) There was minimal response of animals injected with VirB9.2+QuilA and VirB9.2+SV1 00 and (C) SV100 alone and unimmunised responses;

[0057] FIG 35 is a graphical representation showing the cell mediated immune response against VirB9.2 protein. The antigen specific IFN-γ secretion by ELISPOT assay of murine splenocytes from 5 individual mice. (A) Mice injected with VirB9.2 + Guil-A show comparable results to VirB9.2 + SV100 and also to the multivalent injections VirB9.1/9.2+Quil-A and VirB9.1/9,2 + SV100. ConA is the internal control. (B) There was minimal response of animals injected with VfrB9.1 +Gui!A and VirB9.1 +SV1 00 and (C) SV100 alone and unimmunised responses;

[0058] FIG 36 is a graphical representation showing correlations of the wall thickness of calcined silica vesicles (circle), entrance size before (diamond) and after (square) hydrophobic modification, the cytochrome c adsorption capacity (upside down triangle) on unmodified silica vesicles and ribonuclease a (lower line, triangle) on modified silica vesicles, as a function of T. T is the temperature of the last synthetic step;

[0059] FIG 37 is a graphical representation showing differential scanning calorimetry curves of free RNase A and RNase A loaded in hydrophobic modified silica vesicles dissolved or dispersed in 10 m PBS solution (RNase A 0.5 mg/ml), the heating rate is 60 ^c C/h ;

[0060] FIG 38 is a graphical representation showing circular dichroism spectra of RNase A/silica vesicles treated with 0.01 M HCI (pH 2} at 65 °C for 40 min and neutralized to pH 7 with 0.01 NaOH. Final RNase A concentration is mg/ml;

[0061] FIG 39 is a graphical representation showing cell viability of (A) SCC25 and (B) HCT1 6 cells treated with RNase A at a dosage of 6 pg/rol after 24, 48 and 72 h. The free R ase A and RNase A loaded in silica vesicles were treated with 0.01 M HCI (pH 2) at 65 °C for 40 min and neutralized to pH 7 with 0.01 NaOH before adding to the cells; and

[0062] FIG 40 is a graphical representation showing mass spectrometry of RNase A loaded in (A) SV-10-120 without modification and (B) SV-10-120-C ₁₈ with hydrophobic modification after the treatment of trypsin digestion.

DETAILED DESCRIPTION

[0063] The present invention is predicated, at least in part, on the finding that precise control over the formation of relatively large pore hollow silica vesicles with high purity (>98%) and yield, unique pore wall structure and controllable pore entrance si2e is achieved by an approach which includes; a first step of cooperative self-assembly at low temperature to form unilamellar vesicles of silica-polymer composites; a second step involving a secondary controlled self-assembly process within the composite walls at a moderate/intermediate temperature to form and shape pore wall structures; and an optional third step being a hydrothermal treatment process at high temperature which allows for further adjustment of the pore entrance sizes, when required. The novel silica vesicles provided have been found to have a number of desirable properties including high protein loading capacity, excellent cell uptake and efficacy as a drug/chemical agent delivery system and as part of an immunogenic composition for vaccine purposes.

[0064] In this patent specification, adjectives such as first and second, left and right, front and back, to and bottom, etc., are used solely to define one element or method step from another element or method step without necessarily requiring a specific relative position or sequence that is described by the adjectives unless such is clear from the context.

[0065] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as would be commonly understood by those of ordinary skill in the art to which this invention belongs.

[0066] As used herein, the terms "silica vesicle ⁵ ' (SV) or "hollow silica vesicle" (HSV) refer generally to a vesicle comprising a silica based wall surrounding an internal cavity. Particularly, the SV's described herein have a cavity in the mesoporous range (i.e. between 2 to 50 nm) and have a unilamellar silica- void-silica wall and can be classified as small unilamellar vesicles (SUVs) as they have a diameter of less than 100 nm. Porosity in the walls of the vesicles is provide by spherical perforations in the vesicle walls. These spherical pores may be interconnected so as to form a continuous pore pathway bridging the inner and outer surfaces of the vesicle walls. In cases where the spherical pores have a diameter similar to the thickness of the wall of the vesicle, a single spherical pore can bridge the inner and outer surfaces of the wall, providing a large pore entrance to the internal cavity of the vesicle.

[0067] As used herein, the word "agitation" may refer to any means of causing mixing, perturbation or other dynamic movement of the reagents during the respective reaction. Stirring is a preferred means of agitating the reaction mixture although, sonication, shaking and other means may be acceptable.

[0068] In the experimental work described herein the silica vesicles synthesised are generally denoted by the treatment temperatur steps they have undergone during synthesis. For example, SV-T1 -T2-T3-n, in which T1 , T2 and T3 indicate the temperature for each of the three synthetic steps employed, respectively. The suffix n stands for the specific samples, for example, 'c ^! stands for after calcination, 'a' stands for am ^' ino-modification having been carried out on the sample and ^! u ^; or T inform as to whether the sample was taken from th upper or lower layer in those particular instances where the reaction mixture comprised more than one phase. The letter 'x' indicates the absence of a specific step depending where in the notation the 'χ' is placed. For example, SV-10-X-140 represents silica vesicles which were synthesised via a first step at 1.0°C, the second step was not carried out but instead the vesicles were subjected to a hydrothermal treatment at 140°C in a third step, as defined herein.

[0069] In a first aspect of the invention, there is provided a method of producing hollow silica vesicles including the steps of:

(a) producing a silica formulatio by adding a hydrolysable silica source to an aqueous solution comprising a block copolymer, the silica formulation being maintained at a temperature of less than 20°C, and agitating the formulation until silica-polymer composite vesicles form, followed by step (b) or step (e);

(b) raising the temperature of the silica formulation containing the silica-polymer composite vesicles to be between 25°G to 100°C and agitating the mixture to form silica-polymer composite vesicles having spherical structures within the vesicle walls;

(c) exposing the vesicles to a hydrothermal treatment; and

(d) calcining the vesicles, to thereby produce the silica vesicles.

[0070] The hydrolysab!e silica source is suitably of the general formula [(X )(X2}Si(X ₃ )(X ₄ }]. Each X group is not particularly restricted except that at least two are hydrolysable. Preferably, three of the four X groups are hydrolysable and, more preferably, all of the X groups are hydrolysable. Each X may be different but is an organic group which is seiected from the group consisting of a CrCio aikoxy substituted or unsubstituted, an ary!oxy substituted or unsubstituted, a C _r Ci ₀ alkyi substituted or unsubstituted or aryl substituted or unsubstituted, a C Cto alkenyl substituted or unsubstituted. Preferably, the aikoxy, alkenyl and alkyl groups referred to are CrC _s groups inclusive of G2-C-8 groups, G3-C8 groups, C-rGs groups, G5-C8 groups, Ce-Ce groups and C7 or Ce groups. More preferably the aikoxy, alkenyl and alkyl groups are d-C ₆ groups inclusive of Ca- e groups, Ca-Ce groups, C4-C6 groups and C ₅ and C ₆ groups. Even more preferably the aikoxy, alkenyl and alkyl groups are C1-C4 groups inclusive of C ₂ -C ₄ groups and C ₃ and C ₄ groups. Still more preferably the aikoxy, alkenyl and alkyi groups may be C1-C3 inclusive of Ci , C2 and G3 groups. Yet still more preferably the aikoxy, alkenyl and alkyl groups may be selected from the group consisting of methyl, ethyl, propyl, isopropyl, butyl, s- and t-butyl groups.

[0071] In one preferred embodiment, the hydrolysable silica source is such that all four X groups are C C ₆ aikoxy groups inclusive of Cz-C _& , C ₃ -C _e , C ₄ -C ₆ and C _s and C ₆ as well as C1-C , C ₂ -C ₄ and C ₃ and C ₄ and Ci and C2 groups. Preferably, the hydrolysable silica source is an alkylorthosilicate which may be optionally substituted. Preferably, the alkylorthosilicate is selected from the group consisting of tetramethylorthosilicate, tetrethylorthosilicate, tetrapropylorthosilicate and tetrabutylorthosiiicate, all of which may be optionally substituted.

[0072] The term "alkyf refers to optionally substituted linear and branched hydrocarbon groups having 1 to 10 carbon atoms. Where appropriate, the alkyl group may have a specified number of carbon atoms, for example, Ci-Gs a!kyl or Ci-Ce alkyl which includes alkyl groups having 1 , 2, 3, 4, 5 or 6 carbon atoms in linear or branched arrangements. Non-limiting examples of alkyl groups include methyl, ethyl, propyl, isopropyl, butyl, s- and t-butyl, pentyl, 2-methylbutyl, 3-methylbutyl, hexyl, heptyi, 2-methyipentyl, 3-methylpentyI, 4-methylpentyl, 2-ethylbutyl, 3-ethytbutyl, octy!, nonyi, deeyl, undecy!, dodecyl, tridecyl, tetradecyl, pentadecyl.

[0073] The term "alkenyl refers to optionally substituted unsaturated linear or branched hydrocarbon groups, having 2 to 10 carbon atoms and having at least one carbon-carbon double bond. Where appropriate, the alkenyl group may have a specified number of carbon atoms, for example, C ₂ -Cs alkenyl or C _z -C _& alkenyl which includes alkenyl groups having 2, 3, 4, 5 or 6 carbon atoms in linear or branched arrangements. Non-limiting examples of alkenyl groups include, etheny!, propeny!, isopropenyl, butenyl, s- and t-butenyl, pentenyl, hexenyl, hept-l,3-diene, hex-i,3-diene, non-l,3,5-triene and the like,

[0074] The term ^iC a!kox as used herein means straight or branched chain alkyl groups linked by an oxygen atom (i.e., -0-aikyl) to the silicon atom, wherein alkyl is as described above. The term "arybxy" as used herein has a similar meaning with an aryl group, as defined below, replacing the alkyl group.

[0075] The term ^a ary as used herein means a stable monocyclic, bicyclic, or tricyclic carbon ring of up to 8 members in each ring, wherein at least one ring is aromatic as defined by the Huckel 4n+2 rule.

[0076] The term "optionally substituted" includes substitution of the group referred to with one or more groups selected from the group consisting of, but not limited to alkyl, alkenyl, aryi, amine, amino, halide, thio, hydroxy and carboxyl groups. Those skilled in the art will appreciate that other groups may be used for substitution. [0077] By way of non-limiting example only, the hydroiysable silica source may be selected from the group consisting of one or more of: methyltrimethoxysilane, methyitriethoxysilane, methyitri-n-propoxysflane, methyltri-iso-propoxysilane, methyitri-n-butoxysilane, methyltri-sec-butoxysilane, methyltri-tert-butoxysilane, ethyltrimethoxysilane, ethyltriethox silane, ethyltri-n-propoxysilane, ethyltn-iso-propoxysiiane, ethyltn-n-butoxysilane, ethyltri-sec-butoxysilane, ethyltri-tert-butoxystiane, n-propyltnmethoxysilane, n-propyltriethoxysilane, n-propyltri-n-propoxysilane, n-propyltri-iso-propoxysilane, n-propyltin-n-butoxysilane, n-propyltri-sec-butoxysilane, n-propyltri-tert-butoxysilane, isoprapyltrimethoxysilane, isopropyltriethoxysilane, isopropyltri-n-propoxysilane, isopropyltriisopropoxysilane, isopropyltri-n-butoxysilane, isopropyitri-sec-butoxysilane, isopropyltri-tert-butoxysilane, n-butyiihmethoxysiiane, n-butyitriethoxysilane, n-butyltri-n-propoxysilane, n-butyltriisopropoxysilane, n-butyltri-n-butoxysilane, n-butyltri-sec-butoxysiiane, n-butyltri-tert-butoxysilane, sec-butyltrimethOxysilane, sec-butyltriethoxysilane, sec-butyltri-n-propoxysilane, sec-butyltriisopropoxysilane, sec-butyltri-n-butoxysilane, sec-butyltri-sec-butox siiane, sec-butyitri-tert-butoxysilane, tert-butyltrimethoxysilane, tert-butyltriethoxysilane, tert-butyltri-n-propoxysilane, tert-butyltriisopropoxysilane, tert-butyltri-n-butoxysilane, tert-butyltri-sec-butoxysilane, tert-butyltri-tert-butoxysifane, isobutyltrimethoxysiiane, isobutyitnethoxysilane, isobutyitri-n-propoxysilane, isobutyltriisopropoxysilane, isobutyltri-n-butoxysilane, isobutyltri-sec-butoxysilane, isobutyltri-tert-butoxysilane, n-pentyltrimethoxysilane, n-pentyltriethoxysilane, n-pentyltri-n-propoxysilane, n-pentyltriisopropoxysilane, n-pentyltri-n-butoxysilane, n-pentyjtri-sec~butoxysilane, n-pentyltri-tert-butoxysilane, sec-pentyltrtmethoxysilane, sec-pentyltriethox silane, sec-pentyltri-n-propoxysilane, sec-peniyltriisopropoxysilane, sec-pen ty!tri -n - butoxysf Ian e , sec-pentyltri-sec-butoxysilane, sec-pentyitri-tert-butoxysilane, tert-pentyltrimethoxysilane, tert-pentyltriethoxysilane, tert-pentyltri-n-propoxysilane, tert-pentyltriisopropoxysilane, tert-pentyltri-n-butoxysilane, te rt - penty It r i-sec- bu toxy si Ian e , tert-pentyltri-tert-butoxysilane, iso pentyltri ethoxysi lane, isopentyltriethoxysilane, isopentyitri-n-propoxysflane, isopentyltriisopropoxysilane, isopentyltri-n-butoxysflane, isopentyitri-sec-butoxysftane, !sopentyltri-tert-butoxysilane, neo-pentyitrimethoxysilane, neo-pentyltriethoxysilane, neo-pentylth-n-propoxysilane, neo-pentyltriisopropoxysilane, neo-pentyltri-n-butoxysilane, neo-pentyltri-sec-butoxysilane, neo-pentyltri-neo-butoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, phenyltri-n-propoxysilane, phenyltriisopropoxysilane, phenyltri-n-butoxysilane, phenyltri-sec-butoxysilane, phenyltri-tert-butoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane. methyldi-n-propoxysifane, dimethyldiisopropoxysilane, methyldi-n-butoxysilane, dimethyldi-sec-butoxysilane, methyidi-tert-butoxysilane, diethy!dimethoxysilane, diethyidiethoxysilane, ethyldi-n-propoxysilane, diethyldiisopropoxysilane, diethyldi-n-butoxysilane. ethyldi-sec-butoxysilane, diethyidi-tert-butoxys!lane _!

-n-propyldimethoxysifane, di-n-propyldimethoxystlane

-n-propyidi-n-propoxysilane, di-n-propyldiisopropoxysilane _;

-n-propyldt-n-butoxysilane, di-n-propyldi-sec-butoxystlane _;

-n-propyidi-tert-butoxysflane, diisopropyldimethoxysilane _; isopropyidiethoxysilane, diisopropyldi-n-propoxys!iane _: isopropyldiisopropoxysilane, diisopropyldi-n-butoxysiiane, isopropy!di-see-butoxysifane, diisopropyidi-tert-butoxysilane _;

-n-butyidimethoxysilane, di-n-butyldiet oxysilane _; -n-butyldi-n-propoxysilane, di-n-butyidiisopropoxysilane,

-n-butyidi-n-butoxysilane, di-n-butyidi-sec-butoxysilane,

-n-butyidi-tert-butoxysiiane, di-sec-butyldtmet oxysilane,

-sec-butyidiethoxysilane, di -sec- bu ty !di - n -p ro poxys i lane ,

-sec-buiyidiisopropoxysilane, di-sec-butyldi-n-butoxysilane,

-sec-butyldi-sec-butoxysilane, di-sec-butyidi-tert-bu toxysi lane ,

-tert-butyidimethoxysilane, d i -te rt-butyidieth oxysi Ian e ,

-tert-butyldi-n-propoxysilane, di-tert-butyldiisopropoxysilane,

-tert-butyidi-n-butoxysiiane, di-iert-butyidi-seo-butoxysflane,

-tert-butyldi-tert-butoxysiiane, diphenyldimethoxysilane, phenyidiethoxysilane, diphenyldi-n-propoxysiiane, phenyldiisopropOxyst!ane, d i ph en y Id i -n - bu toxy si Ian e , phenyldi-sec-butoxysilane, diphenyldi-tert-butoxysilane, methyineopentyidimethoxysilane, methylneopentyldiethoxysilane, methyldimethoxysilane, ethyidimethoxysiiane, n-propyldimethoxysilane, isopropyldimethoxysilane, n-butyldimethoxysilane, sec-butyldimethoxysilane, tert-butyidimethoxysilane, isobutyidimethoxysilane, n-pentyidimethOxysilane, sec-pentyldirnethoxysilane, tert-p ntyidimethoxysilane, isopentyidimethoxysilane, neopentyidimethoxysilane, neohexyldimethoxysilane, cyclohexyldimethoxysilane, phenyldimethoxysilane, methyldieth oxysi la e, ethyidiethoxysilane, n-propyldiethoxysilane, isopropyldiethoxysiiane, n-butyldiethoxysilane, sec-butyidiethoxysilane, tert-butyidiethoxysilane, isobutyldiethoxysilane, n-pentyldiethoxysilane, sec-pentyldiethoxysilane, tert-pentyidiethoxysilane, isopentyldiethoxysilane, neopentyidieth oxysi lane , neohexyldiethoxysilane, cyclohexyldiethoxysilane, phenyidiethoxysflane, trimethoxysilane, triethoxysilane, tri-n-propoxysilane, iriisopropoxysilane, tn-n-butoxysilane, tri-sec-butoxysilane, tri-tert-butoxysiiane. Of the above compounds, the preferred compounds are methyltrimethoxysiiane, methyltriethoxysilane. methyltri-n-propoxysilane, methyltriisopropoxysila- ne, ethyltrtmethGxysilane, ethyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysil ne, diethyldimethoxysilane and diethyidiethoxysilane.

[0078] The hydrolysable silica source may be an oligomer formed by reaction of one or more types of monomer described by the above formula or listed above.

[0079] Preferably, the aqueous solution is an aqueous buffer solution.

[0080] Suitably, the aqueous buffer solution is an acidic buffer solution. In a preferred embodiment the pH of the aqueous buffer solution is between 3 to 6, or between 3 to 5, preferably 4 to 5. in one preferred embodiment the aqueous buffer solution is a sodium acetate/acetic acid buffer solution.

[0081] Preferably, an inorganic salt is also present in the silica formulation. Suitable inorganic salts include sodium and potassium salts. Sodium sulphate and sodium chloride are two examples of preferred salts. It is postulated that a high ionic strength in the formulation improves the stability of larger vesicles and assists in maintaining uniformity. This is based on experimental observations that the vesicles, while still commercially useful, will become relatively small (30 nm) and show reduced uniformity in the absence of salts.

[0082] Preferably, the block copolymer is an olefinic block copolymer. A wide range of olefinic block copolymers are commercially available. More preferably, the block copolymer is a triblock copolymer i.e. of the A-B-A configuration, in one embodiment the triblock copolymer is a poly(aikylene oxide)-poly(alkylene ₂ oxide)~poly(alkytenei oxide) block copolymer wherein the alkylenei and alkylene components may be independently selected from the grou consisting of ethylene, propylene, butylene, pentylene, hexylene and derivatives, e.g. glycol derivatives, thereof.

[0083] Even more preferably, the block copolymer is a poly(ethylene oxide)-poly(alkylene oxide)-poly(ethylene oxide) block copolymer wherein the alkylene group is as described above for the alkylenei and alkylene^ components. In preferred embodiments, the block copolymer is a polyethylene oxide)-poly(propylene oxide)-poiy(ethylene oxide) or a polyiethylene oxide}-poly(butylene oxide)-poiy(ethyiene oxide) block copolymer.

[0084] Preferably, in step (a), the silica formulation is maintained at a temperature of between 0°C to 20°G, preferably between 5°C to 15°C, more preferably at about 10°C. Between 0 ^e C to 20°C may include ranges of between Q°C to 15°C, 0°C to 12°C, 5°C to 20°C, 5°C to 15°C, 7°C to 1 3°C and is inclusive of temperatures of about 0°C _T 1 °C, 2°C, 3°C. 4°C, 5°C, 6°C, 7°C, 8°C, 9°C, 10°C, 1 1 °C, 12°C, 13°C, 14 ^C C, 15°C, 16°C, 17°C, 18°C, 19°C and 20°O or of ranges from any one of those values to another one of those values.

[0085] Suitably, the agitation of the mixture in step (a) is stirring. Preferably, the stirring until formation of the silica-polymer composite vesicle occurs is continuous stirring for a first predetermined period of time. The first predetermined period of time may be determined experimentally by observation of the reaction mixture by known techniques such as TE until formation of the silica-polymer composite vesicles is observed. Failure to continuously stir the formulation may lead to phase separation of the formulation into to layers which disrupts formation of the vesicles.

[0086] Suitably, the silica formulation is stirred for a significant portion of, preferably the majority of, more preferably a substantial portion of and even more preferably for substantially all of the first predetermined period of time.

[0087] By "a significant portion of" it is intended that stirring be continuous for at least the first 20% of the first predetermined period of time. By "the majority of it is intended that stirring be continuous for at least the first 50% of the first predetermined period of time. B "a substantial portion of it is intended that stirring be continuous for at least the first 75% of th first predetermined period of time. By "substantially all of it is intended that stirring be continuous for at least the first 80%, preferably 90% of the first predetermined period of time.

[0088] The inventors have surprisingly found that continuous stirring is a critical aspect of at least the first ste and it is important that continuous stirring be maintained until the majority of the initial silica-polymer composite vesicles have formed. They have shown experimentally that, with other conditions maintained the same, if the reaction is carried out without stirring then the desired vesicles fail to form and amorphous silica results. This is described in the experimental section.

[0089] Preferably, the first predetermined period of time is at least 5 hours, more preferably at least 10 hours, even more preferably at least 15 hours, still more preferably at least 20 hours. In one preferred embodiment, the first predetermined period of time is about 24 hours or more.

[0090] Suitably, in step (b), the temperature is raised to be between 30°C to 9Q°C, preferably between 30°C to 85°C, more preferably between 35°C to 80°C. Between 30°C to 90°G may include ranges of between 30°C to 80*C, 30°C to 75°C, 30°C to 70°C, 40°C to 90°C. 40°C to 85°C, 40°C to 80 ^o C, 40°C to 75°C, 40°C to 70°C and is inclusive of temperatures of about 30°C, 35°C. 40°C, 45°C, 50°G, 55°C, 60°C, 65°C, 70°C, 75°C ₅ 80°C, 85°C and 90°C or of ranges from any one of those values to another of those values.

[0091] Suitably, the agitation of the mixture in step (b) is stirring. Preferably, the stirring is continued until formation of spherical structures are generated inside the walls of the silica-polymer composite vesicles. This formation may occur after continuous stirring for a second predetermined period of time.

[0092] Preferably, the second predetermined period of time is between about 0.1 to about 6.0 hours, preferably between about 0.5 to about 5.0 hours, more preferably between about ,0 to about 4.0 hours, even more preferably between about 2.0 to about 3.0 hours. The second predetermined period of time can also be determined experimentally, as for the first predetermined period of time, and can be taken to be at an end when a suitable percentage of the vesicles with wall spherical structures, for example when greater than 90%, 95% or 98% of said vesicles are formed.

[0093] The inventors have found that the heating in step (b) at moderate/intermediate temperature is the period during which pore wall structure formation occurs, i.e. the formation of hollow spherical bodies within the wall structure, and the elevated temperature over that in step (a) is critical to achieve the desired vesicle wail morphology. Without wishing to be limited by theory, the inventors believe that at the completion of step (a) the silica species in the silica-polymer composite vesicle may not be full hydrolysed, still retaining some of their silica precursor organic groups and consequently a degree of hydrophobicity. Under these conditions, the lamellar structure of the block copolymer is favoured. However with step (b), the degree of hydrolysis of the silica precursor is increased such that the surface of the silica becomes more dominated by the hydroxyi terminated groups typical of silica surfaces, and therefore, more hydrophilic. With this decrease in wall hydrophobicity, the surfactant conformation can change to the more curved structures such as spherical micelles favoured under hydrophilic conditions. This results in the formation of vesicle wall pores with a spherical structure. It will be appreciated by those skilled in the art that depending on the selection of the surfactant, temperature, water content, degree of silic precursor hydrolysis and other factors, curved surfactant structures other than spherical micelles may be formed at step (b) and as such, the porosity of the vesicle walls may take on the shape of these curved surfactant structures. Curved surfactant structures that may form as an alternative to spherical micelles include but are not limited to hexagonal rods and cubic phases including bi-continuous cubic phases. The extent of curved surfactant structures that may be formed will be well understood by those skilled in surfactant liquid crystal behaviour. [0094] However, in one embodiment, the method includes step (a) followed by step (c) prior to calcining the vesicles. Here, it is step (c), the hydrothermal step, that is key in forming the larger spherical pores in the walls of the vesicles. In cases where pore sizes only at the larger end of the range provided by the methods of the present invention are desired, step (b) (which without the following hydrothermal step produces smaller pore sizes) may be omitted from the method.

[0095] In one highly preferred embodiment, the method includes step (a) followed by step (b) followed by step (c), prior to calcining the vesicles. That is, the silica formulation of step (a) is exposed to step (b) and it is the silica-polymer composite vesicles having spherical structures within the vesicle walls, as a product of step (b), which are then exposed to step (c).

[0096] Preferably, the hydrothermal treatment of step (c), for all embodiments, is carried out at a temperature which is greater than 90°C and less than 200°C, preferabl greater than 90°C and less than 180°C, more preferably greater than 95°C and less than 160°C, for example about 100°C to about 1 6G°C. In certain embodiments the hydrothermal treatment may be carried out at a temperature which is between 100°C and 2O0°G, preferably between 100°C and tSO^C, more preferably between 100°C and 1 60°C. Temperatures of about 100°C, 105°C, 1 10°C, 1 15°C, 12G°C, 125°C, 130°C, 135°C, 140°C, 145°C, 150°C, 155°C and 160°C are considered useful.

[0097] Preferably, the hydrothermal treatment step is carried out for a third predetermined period of time until formation of the silica-polymer composite vesicles with entrances which are formed throughout the siliceous walls,

[0098] Preferably, the third period of time is generally equivalent to those periods described for the first period of time.

[0099] Suitably, the hydrothermal step (c) is carried out at an elevated pressure. Preferably, the elevated pressure is greater than 0.7 bar and less than 1 5.5 bar inclusive of 1 .1 bar to 15.0 bar, 1.5 bar to 1 .0 bar, 1 .5 bar to 10.0 bar, 1.5 bar to 8,0 bar, 1.5 bar to 6,0 bar and 1.5 ba to 5.0 bar. In one embodiment the elevated pressure is greater than 0.7 bar and less than 10 bar, more preferably greater than 0.8 bar and less than 6 bar, for example about 1 bar to about 6 bar.

[00100] As indicated in FIG 3, carrying out step (b) without the additional hydrothermal step may result in the formation of relatively small pores in the vesicle walls, typically with diameters lower than 4 nm. These pores are largely formed by microcracks in the vesicle walls and the microcracks may be associated with small internal spherical cavities in the wall of the vesicle such that these cavities are connected with the internal cavity of the vesicle and the outside of the vesicle, forming a continuous pore path through the vesicle wall. Carrying out the hydrothermal step, with or without the inclusion of step (b) (that is, following step (a) or step (b)) may result in the formation of larger pores in the walls of the vesicles as shown in FIG 3. Thus, while either step (b) or step (c) may directly follow step (a) and be followed by calcination to produce useful and commercially valuable products it is preferred that step (a) is followed by step (b) which is itself followed by step (c) and then, finally, calcination to produce silica vesicles with fine control over morphology.

[00101] Suitably, the calcination is carried out at any temperature suitable to remove the copolymer template and typically would be carried out at greater than 400°C, preferably greater than 500°C, even more preferably about 550°C.

[00102] Those skilled in the art will understand that references made to the silica formed at the various stages of the processes of the present invention may refer to silicon-oxygen based materials such as partially condensed and hydrated forms of silicon-oxygen based species since silica of the approximate composition StO≥ would not expect to be fully formed until calcination is carried out. The silicon-oxygen based materials formed at the different stages of the processes of the present invention are well known to those knowledgeable of the formation of silica from the silica precursors described herein using known pathways such as hydrolysis and condensation.

[00103] A surface modification of the silica vesicles may be optionally carried out following the calcination step. This typically involves increasing the hydrophobicity of the surface of the silica vesicle which has been found to increase the loadable amount of certain proteins and drug compounds. Surface modification may be applied to the outer or inner surfaces of the silica vesicles, or both. In one highly preferred embodiment, the method includes, after calcination of the silica vesicles, the step of modifying the silica vesicle with appropriate functional groups. Preferably, the surface modification is a hydrophobic modification.

[00104] The .chemical agent used to modif the silica vesicle surface may be a hydrolysable silica source with the general formula [(Xi)(X2)Si( 3)(X4)]. Each X group is not particularly restricted except that at least one is hydrolysable and at least one is a hydrophobic functional group. Each hydrolysable X may be different but is an organic group which is selected f om the group consisting of a d-C* alkoxy, substituted or unsubstituted, and halogen substituent groups. Preferably, the alkoxy groups referred to are methoxyl and ethoxyl groups. More preferably the alkoxy groups are methoxyl groups. Preferably, the halogen groups referred to are chloride and bromide groups. More preferably the halogen groups are chloride groups. Alternatively, each hydrophobic functional X group may be different but is an organic group which is selected from the group consisting of a Gi-C ₂ o alky! substituted or unsubstituted. The hydrolysable silica source used to impart surface modification of the silica vesicles may include, but is not limited to, one or a combination of two or more of the following compounds: methyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, propyltrimethoxysi!ane, propyltriethoxysilane, butyltrimethoxysilane, butyltriethoxysiiane, pentyltrimethoxysilane, pentyitriethoxysilane, hexyltrimethoxysilane, hexyltriethoxystlane, heptanyltrirnethoxysllane, heptanyltriethoxysilane, octyltrimethoxysi lane octyltriethoxysilane, nonanyltrimethoxysilane, nonanyltriethoxysi lane decanyltrimethoxysilane, decanyitriethoxysilane, undecyltrimethoxys lane, undecylttiethoxysilane, dodecyltrimethoxysilane, dodecyltriethoxys lane _; tridecyltrimethoxysilane, tridecyltrtethoxysilane, tetradecyltrimethoxys lane _; tetradecyltnethoxysilane, pentadecyltrimethoxys lane _: pentadecyltriethQxysilane, _. cetyltrimethoxysilane, cetyitriethoxysi lane heptadecyltrimethoxysi!ane, heptadecyltrieihoxys lane, octadecyltrimethoxysiiane, pctadecy!tfiethoxysilane, pfrenyltrimethoxys Iane _: phenyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxys lane _; dieihyldimethoxysilane, diethyldiethoxysilane, dipropyldimethoxys iane _: dipropyldiethoxysilane, dibutyldimet oxysiiane, dibutyldiethoxysi lane dipen.tyldimethoxysilane, dipentyidiethoxysilane, dihexyldtmethoxys lane dihexyidiethoxysilane, diheptanyldimethoxysilane, diheptanyldiethoxys lane. dioctyldimethoxysilane, dioctyidiethoxysilane, dinonanyldimethoxys Iane _; dinonanyldiethoxysilane, didecanyldimethoxysilane, didecanyldiethoxysi iane _: diundecyldimethoxysi!ane, diundecyldiethoxys lane didodecyldimethoxysilane, didodecyldiethoxys lane ditridecy!dimethoxysilane, ditridecyldiethpxys lane _: ditetradecyldimethoxysiiane, ditetradecyldiethoxys lane dipentadecyidimethoxysilane, dipentadecyldiethoxys! iane _! dicetyldimethoxysilane, dicetyldiethoxysiiane, diheptadeeyldimethoxys lane _: diheptadecyldiethoxystlane, dioctadecyldimethoxys lane dioctadecyldiethoxysilane, diphenyldimethoxysilane, diphenyldiethoxys lane _; ethylmethyldimethoxysilane, ethylmethyldiethoxys lane _; propylmethyldimethoxysilane, propylmethyldiethoxys lane _; butylmethyldimethoxysi!ane, butylmethyldiethoxysi lane pentyimethyldimethoxysflane, pentylmethyldiethoxysi lane, hexylmethyldimethoxysilane, hexylmethyldiethoxys lane _; heptanylmethyldimethoxysilane, heptanylmethyldieihoxys lane _; octylmethyldimethoxysllane, octylmethyldiethoxysi ane, nonanylmethyldimethoxysflane, nonanylmethyldiethoxysf a e decanylmethyldimethoxysilane, decanylmethyldiethoxysi ane undecylmethyldimethoxysiiane, undecylmethyldiethoxysi ane dodecylmethyldimethoxysifane, dodecylmethyldiethoxysi ane tridecyimethyldimet oxysltane, tridecylmethyldiethoxysi ane tetradecylmethyldimethoxysiiane, tetradecylmethyldiethoxyst ane pentadecylmethyldimethoxysilane, pentadeeylmethyldiethoxysi ane cetylmethyldimethoxysilane, cetylmethyldiethoxysf ane heptadecylmethyldimethoxysilane, heptadecylmethyldiethoxysi ane octadecylmethyldimethoxysiiane, octadecylmethyldiethoxysf ane phenylmethyldimethoxysilane, phenylmethyldiethoxysi ane trimethyichlorosiiane, ethyidimethylchlorosilane, propyldimethylchlorosi ane butyldimet ylchlofOsilane, pentyidimethy!chlorasi ane hexyldimethyichlorQsilane heptanyidimethylchlorosi ane oetyldimethylchlorosilane, nonanyldimethyichlorosi ane decanyldimethylchlprosiiane, undecyldimethylchlorosi ane dodecyldimet ylchlorosiiane, tndecyldimethy!chlorosi ane tetradecyldimethylehlorosilane, pentadecyidimethy!chlorosi ane cetyldim thylchlorosilan , heptadecyidimethylchlorosi ane octadecyldimethylchlorosi!ane, pheny!dimethyichlorosi ane phenethyldimethylchlorosiiane, dimethyl idichiorosiiane ethylmethyldich lorosi lane, propyimethy!diGhlorosi ane butylmethyldichlorosilane, pentylmethy!dichlorosi ane hexyldimethyldichlorosilan^, hepianyimethyldichlorosi ane octylmethyldichlorosilane, nonanylmethyidichlorasi ane decanylmethyldichlorosilane, undecyimethyidichiorosi ane dodecylmethyldichlorosiiane, tridecyimethyldichiorosi ane tetradecy I m ethyldic hlorosilane, pentadecylmethyldichlorosi ane eetylmethyldichlorosilane, heptadecylmethy!dichlorosi ane octadecylmethyidichlorosilane, phenyimethy!d!cbiorosiiane phenethylmethyldichlorosilane, methyltrichlorosilane, ethyltrichlorosi!-ane propyltrich!orosilane, butyltrich!orosilane, pentyltrichlorosilane hexyltrich!orosilane, heptanyltrichlorosilane, octyltrichlorosilane nonanyltriehlorosilane, deeanyltrichlorosilane, undecyltrichlorosilane, dodecyltrichiorosilane, tridecyltrichiorosiiane, tetradecyitrichiorosiiane, pentadecyltriGhlorosilane, cetyitrichlorosi!ane, heptadecyltrichlorosiiane, octadecyltrichlorosilane, phenyltrichiorosilane, phenethyltrichlorosilane.

[00105] Suitably, surface modification of the silica vesicles is carried out by combining the silica vesicles with the hydrolysable agent used for surface modification in a suitable media to facilitate either a gas phase or liquid phase reaction. In the case where the surface modification is carried out i a liquid phase medium, the silica vesicles are added to an appropriate solvent (for the hydrolysable silica source) and agitation of the mixture containing the silica vesicles may be carried out before and/or after the addition of the hydrolysable agent used for surface modification. Alternatively, the silica vesicles may be added to a solvent already containing the agent to be used to effect the hydrophobic modification. Preferably, the agitation of the mixture in surface modification step is carried out by stirring or ultrasoni cation. More preferably, the agitation of the mixture in the surface modification step is carried out by stirring.

[00106] Suitably, in the surface modification step, the temperature may be raised to be between 80°C and 12Q ^Q C, preferably between 100°C and 120°C, more preferably between 105°C and 11 S°C.

[00107] Suitably, the surface modification step may be carried out in one or a combination of two or more organic solvents. Solvents that may be used include, but are not limited to one or a combination of two or more of the following: pentane, 2-methylbutane, neopentane, n-hexane, 2-methylpentane, 3-methyipentane, 2,2-dimethylbutane, 2,3-dimethyibutane, n-heptane, 2-methylhexane, 3-methylhexane, 2,2-dimethylpentane, 2,3-dimethylpentane, 2,4-dimethyipentane, 3,3-dimethyjpentane, 3-ethy!pentane,

2,2,3-trimethyibutane, octane, 2-methylheptane, 3-methylheptane, 4-methylheptane, 3-ethylhexan, 2,2-dimethyihexane, 2,3-dimethylhexane, 2,4-dirnethylhexane, 2,5-dimethyihexane. 3,3-dimethylhexane,

3,4-dimethyihexane, 3-ethyi-2-methylpentane, 3-ethyl-3-methylpentane,

2.2.3- trimethyipentane, 2,2,4-trimethyipentane, 2,3,3-trimethylpentane,

2.3.4- trimethylpentane, tetramethyibutane, nonane, decane, undecane, dodecane, ethanol, propan-1 -οί, isopropyt alcohol, butyl alcohol, pentanol, hexan-1-o! ,heptan-1 -ol, octan-1 -ol, nonan-1 -ol, decan-1 -ol, undecan-1 -οί, dodecan-1 -ol, benzene, toluene, ethylbenzene, 1 ,2-dimethyIbenzene, 1 ,3-dimethylbenzene, 1 ,4-dimethylbenzene, n-propylbenzene, 1 ,2,3-trimethyibenzene, 1 ,3,5-trimethylbenzene, 1 ,2,4-trimethylbenzene, benzyl alcohol. Preferably, the solvents are C§-Ci _S a kanes substituted or unsubstituted, C C ₂ alcohols or aromatic compounds which are C C ₃ substituted or unsubstituted. More preferably, the solvents are C Ce alcohols or aromatic compounds which are C C ₃ substituted, even more preferably C2-C5 alcohols or C- Cs substituted benzene. The solvent is preferably octane, ethanoi, propan-1 -ol, isopropyl alcohol or toluene or a combination of one or more of these.

[00108] For the formation of the silica vesicles the results presented in the experimental section, and particularly those shown in FIG 8, clearly indicate that continuous stirring, until the silica-polymer vesicles are formed, and low temperature are two key parameters for the formation of vesicular structure and high yield.

[00109] In the self-assembfy of surfactants, the structure of supramoiecular aggregates is predicted mainly by the g factor of organic surfactant molecules. The inventors have demonstrated that in PEO-PBO-PEO type block copolymer tempiating systems, cooperatively self-organized block copolymer/silicate composite structures can be influenced by the hydrophobicity/hydrophilicity of silica precursors. Specifically, the inventors postulate that temperature, in this instance the relatively low temperature of the first step, will influence the hydrolysis rate of TEOS which in turn influences the hydrophobicity/hydrophilicity of the forming silica oligomer and so influences the self-assembly of the vesicular structure. In synthesis step (a) higher temperatures lead to a faster hydrolysis rate of TEOS, which gives rise to hydrophilic silica oligomers and hence undesired generation of tubular and amorphous silica structures whereas lower temperatures, as previously defined, can produced the desired vesicle structure. Although high temperature hydrothermal treatment can alter the pore entrance size, direct hydrothermal treatment after step (a) prohibits the formation of spherical bodies within the pore wall structure thereby producing a still commercially useful but less preferred vesicle structure. At moderate or 'intermediate' temperature, as in step (b), a sandwich-like silica/surfactant composite structure gives direct evidence that TEOS deposits on both sides of the surfactant layer to thereby give the silica-void-silica wall structure upon later removal of the polymer during calcination.

[00110] In order to visualise the SV formation mechanism, Cryo-TEM was used to investigate the forming vesicle structure at different times throughout the process. As indicated in FIG 9A, the block copolymer surfactant is in micelle form with a diameter less than 10 nm, before adding the silica source (TEOS). This shows that the present method does not use a pre-formed vesicular template in the synthesis but rather the formation of silica vesicles is a cooperative self-assembly of surfactant and silica oligomers. 15 h after adding the TEOS, self-assembled silica-surfactant vesicles can be observed (FIG 9C), however, no pore wall structure is observed at the end of step 1 (FIG 9D). It is also clear that the spherical bodies in the pore wall structure are formed only in a post treatment at moderate temperature i.e. step (b) or T2 (as represented in FIG 3).

[00111] According to a second aspect of the invention there is provided a silica vesicle having: (a) a particle diameter of between 30 to 70 nm;

(b) a wall structure perforated by spherical pores; and

(c) an average pore entrance size of between 4 to 40 nm formed in the wall,

[00112] Preferably, the particle diameter is between 40 to 60 nm, more preferably about 45 to 55 nm, even more preferably about 50 nm. This is an idea! size to promote cellular uptake of the vesicle, and accompanying chemical or biological agents, via endocytosis.

[00113] Suitably, the average pore entrance size is between 5 to 38 nm, more preferably between about 6 to about 34 nm. The preferred pore entrance size will depend on the size of the protein or other drug or biornolecule to be accommodated. For example, for cytochrome C and ribonuclease A which both have a size of approximately 3nm, an SV with an average pore entrance size of about 6 nm will be preferred. For applications where larger molecules need to be accommodated then SVs with an average pore entrance size of 8, 12, 16, 24 or 34 nm may be more appropriate.

[001 1.4] The silica vesicle is a hollow silica vesicle.

[001 15] Preferably, the hollow silica vesicle has a wall thickness of between 4 to 15 nm, more preferably between 5 to 14 nm, even more preferably between 7 to 13 nm.

[00116] A third aspect of the invention resides in a silica vesicle when produced by the method of the first aspect. The silica vesicles will have the physical characteristics already outlined for those of the second aspect.

[001 17] According to a fourth aspect of the invention there is provided a drug or chemical delivery system comprising a silica vesicle of the second or third aspects and a drug or chemical agent encapsulated within the vesicle or bound to an outer surface thereof. [00118] Preferably, the drug is an organic molecule and may include "biologic" molecules such as proteins and peptides and fragments thereof.

[00119] Preferably, the chemical agent is a pesticide such as a termiticide.

[00120] The drug or chemical agent may be adsorbed or bound onto the outer surface of the hollow silica vesicle, captured within the pores or encapsulated within the vesicle cavity. It may be eovalently bonded but is preferably releasably bound such as by ionic attraction or electrostatic interactions or simply physically entrapped within the pore structure to thereb provide slow release characteristics.

[00121] A fifth aspect of the invention resides in an immunogenic, composition comprising one or a plurality of silica vesicles of the second or third aspects and one or a plurality of immunogens and/or antigens.

[00122] The immunogen may be any molecule, protein, peptide, nucleic acid, carbohydrate, lipid or a fragment of any of these species which can, upon administration to a subject, elicits an immune response in the subject, In some embodiments, the immune response may be a protective immune response. The immunogen may be derived from a pathogen, cell, tissue or organ, may be a purified antigen, cell lysate or culture filtrate, or may be of recombinant or synthetic origin.

[00123] In one embodiment, the immunogen or antigen may be a combination of immunogens or antigens.

[00124] In one embodiment, the immunogenic composition is a vaccine composition.

[00125] In one embodiment, the immunogenic vaccine composition is a muitt-vaient vaccine composition,

[00126] In one embodiment, the immunogen is derived from a pathogenic virus, bacterium or other organism. Suitably, the pathogen from which the immunogen is derived is a single -stranded R A virus. Preferably, the virus is selected from the group consisting of the families FlavMridae, Hepacivirus, Pegivirus, Ephemerovirus, Rhabdoviridae and Pestivirus. In one preferred embodiment the virus is a pestivirus.

[00127] When the virus is a Ephemerovirus or Rhabdoviridae virus then it may be a bovine ephemeral fever-causing virus. Bovine ephemeral fever (BEF) is also known as Three Day Sickness in cattle, it is an arthropod vector-borne disease of cattle. The BEF virus is a negative, single stranded RNA genome with a lipid envelope and 5 structural proteins. The envelope glycoprotein G contains type-specific and neutralizing antigenic sites.

[00128] In certain embodiments, the immunogen may be derived from a species of the genus Babesia. Such a parasitic organism may be, for example, Babesia bovis or Babesi bigemina.

[00129] In certain embodiments, the immunogen may be derived from a species of the order Rickettsiales. The species may be of the genus Anapfasma, for example, Anaplasma marginals. Infection of cattle with Anapiasma marginale leads to a disease generally referred to as anapiasmosis.

[00130] It will be appreciated that the immunogenic composition of the present invention is not limited in the type of immunogen/antigen that it may be used with. Examples of antigens that may be used with the HSV drug delivery system include, but are not limited to, those used in the treatment or prophylaxis of adenovirus Type 4 and Type 7, anthrax, tuberculosis, diphtheria and tetanus, pertussis, Hepatitis B, poliovirus, Haemophilus, meningococcal disease, Hepatitis A, human papillomavirus, influenza, Japanese encephalitis, measles, mumps and rubella, pneumococcal disease, rabies, rotavirus, smallpox, typhoid, varicella, yellow fever, porcine circovirus, classical swine fever virus, equine influenza virus, foot and mouth disease virus, Newcastle disease virus, respirator syncitial virus, parainfluenza virus 3, equine influenza virus, rabies virus, canine distemper virus, porcine contagious pleuropneumonia (caused by Actmobacilius pleuropneumoniae), canine babesiosis and canine visceral leishmaniasis.

[00131] In any one formulation of a product using the silica vesicles of the present invention, or any composition or aspect described herein relating to the use of the silica vesicles, more than one drug molecule or immunogen may be present. Here, combinations of different immunogens, combinations of different drug molecules or combinations of immunogens and drugs may be used in a single formulation. This enables the development of multi-valent vaccines, multi-drug combinations and drug vaccine combinations. Multi-drug combinations, multi-valent vaccines and drug vaccine combinations may be constructed by either mixing the pharmaceutically active molecules (that is, the drug molecules, immunogens or other molecules) together and then loading these into the silica vesicles such that individual vesicles may contain more than one type of active molecule, or alternatively, active molecules of a single type may be separately adsorbed (loaded) into separate lots of the silica vesicles and then the silica vesicles loaded with different active molecules ma be combined into a single formulation. This latter approach allows different silica vesicle designs to be used with the different active molecules such that the release of each active molecule in a formulation may be independently tailored with respect to the release characteristics of the other active molecules in the formulation. For example, in a single formulation, silica vesicles with large pore entrance openings may be used for loading a large molecule such as a protein while small organic drug molecules i the same formulation may be accommodated within silica vesicles with smaller pore entrance openings to better moderate the controlled release of these small molecules, if desired. As another example, multi-valent vaccine formulation may be constructed using hydrophobical!y-modifted silica vesicles to maximise the loading of protein immunogens that have a strong hydrophobic character, while un-modifted vesicles may be used to accommodate more hydrophilic immunogensin the same formulation. As an alternative strategy to constructing combination products, the silica vesicles may be sequentially loaded with different active molecules.

[00132] In one embodiment, the immunogenic composition comprises a plurality of silica vesicles which are of substantially the same character presenting or encapsulating plurality of immunogens which are of a different structural and/or functional character from one another.

[00133] in one embodiment, the immunogenic composition comprises a plurality of silica vesicles of a different structural character which are presenting or encapsulating immunogens which are of substantially the same structural and/or functional character.

[00134] It will be further appreciated by those skilled in the art that the immunogenic composition of the present invention may be formulated using any number or combination of excipient materials. These excipient materials may be included in a formulation for any number of reasons well known to those skilled in the art including, but not limited to, provide a stable formulation, improve flowability, adjust pH, allow easy reconstttution, stabilise antige species, minimise adverse toxicologica! responses, improve manufacturability, increase stability or lifetime or allow easier administration, storage or transportation. Excipients that could be used to formulate a drug product containing the immunogenic composition of the present invention include, but are not limited to, acetone, alcohol, anhydrous lactose, castor oil, cellulose acetate phthalate, dextrose, D-fructose, D-mannose, FD&C Yellow #6 aluminium lake dye, fetal bovine serum, human serum albumin, magnesium stearate, micro-crystalline cellulose, plasdone C, polacrilin potassium, sodium bicarbonate, sucrose, aluminium hydroxide, amino acids, benzethonium chloride, formaldehyde, inorganic salts and sugars, vitamins, asparagine, citric acid, lactose, glycerin, iron ammonium citrate, magnesium sulfate, potassium phosphate, aluminium phosphate, formaldehyde, glutaraldehyde, 2-phenoxyethanol, glutaraldhyde, polysorbate 80. aluminium potassium sulfate, ammonium sulfate, bovine extract, gelatin, peptone, sodium phosphate, thimerosal, caif serum, glutaraldehyde, lactalbumin hydrolysate, neomycin sulfate, polymyxin B, lactalbumin hydrolysate, yeast extract, M C-5 cellular protein, neomycin, polymyxin B sulphate, aluminium hydroxyphosphate sulphate, hemin chloride, mineral salts, nicotinamide adenine dinucleotide, potassium aluminium sulfate, sodium borate, soy peptone, phosphate buffers, polsorbate 20, sodium borate, lipids, sodium dihydrogen phosphate dehydrate, carbohydrates, L-histidine. Beta-propiolactone, calcium chloride, dibasic sodium phosphate, egg protein, monobasic potassium phosphate, monobasic sodium phosphate, polymyxin B, potassium chloride, sodium taurodeoxychoalate, gentamicin sulfate, hydrocortisone, octoxynol-10, a-tocopheryl hydrogen succinate, sodium deoxycholate, ovalbumin, nonylphenol ethoxylate, octylphenol ethoxylate (Triton X-100), arginine, dibasic potassium phosphate, egg protein, ethylene diamine tetraacetic acid, gentamicin sulfate, hydrolyzed porcine gelatin, monobasic potassium phosphate monosodium giutamate, protamine sulfate, sodium metabisulphtte, phenol, casamino acid, sodium citrate, sodium phosphate monobasic monohydrate, sodium hydroxide, calcium carbonate, dextran, sorbitol, trehalose, sugar alcohols, polysaccharides, glucosamine, mannitol, polymers and xanthan.

[00135] Preferably, the immunogen is an immunogenic fragment of the bovine viral diarrhoea virus (BVDV). More preferably, the immunogen is the E2 protein, or a fragment thereof, of the BVDV. The structural envelope glycoprotein, E2, is a major immunogenic determinant, and is an ideal candidate as a subunit vaccine as immunisation with E2 evokes the production of neutralising antibodies. The neutralising antibodies produced by E2 after natural infection or vaccination is considered as the most important protective mediator against subsequent BVDV infection. Preferably, the E2 protein used in the immunogenic composition is a soluble, endotoxin free E2 generated using E.coli expression. The E2 protein expressed in this way has been shown to be immunogenic in mice and sheep and was detectable by several BVDV-E2 specific antibodies. It is referred to herein as OptiE2 protein.

[00136] Bovine viral diarrhoea (BVD) is a prevalent cattle disease that causes serious mucosal lesions and clinical disorders suc as reproductive, congenital defects and persistent infections. BVDV, commonly known as bovine pestivirus, is a single-stranded RNA virus which infects mostly cattle and some sheep. A major concern regarding pestivirus is not only limited to the substantial economic losses incurred but also to the fact that these viruses are not host specific signifying that they can easily spread amongst livestock such as sheep, pigs and goats. It has been well established that sheep and goats can be infected with BVDV and then transmit the virus back to cattle. BVDV has also been found in native bison and water buffalo populations.

[00137] Currently the available live and inactivated BVDV vaccines are relatively effective at preventing the majority of clinical diseases associated with acute infections, however these vaccines fail to completely protect against transmission by persistently infected animals. To date, Pestigard® (Pfizer) is the only BVDV vaccine approved for use in Australia. It is an inactivated viral vaccine with two antigenetically different Type 1 strains of BVDV, which have been isolated in Australia - Trangie and Bega. This vaccine needs to be administered as two doses, 6-8 weeks apart, with an annual booster injection required thereafter. Once opened the vaccine has a short shelflife of only one month and needs refrigeration. BVDV vaccine Bovilis BVD (Merck) is available in the UK and comprises of inactivated BVDV antigen of strain C-86. It protects the foetus against transplacental infection with BVDV and animals require an annual booster dose for protection. It has a shelf life of 18 months at +2°C to +8°C. Once opened the vaccine shelf life is reduced to 10 hours.

[00138] Subunit vaccines are comprised of highly purified recombinant antigens such as proteins and peptides, these vaccines are more stable and have better safety profiles compared to the conventional vaccines. However, subunit vaccines can have poor imm.unogenicity and are often unable to cross intestinal mucosal tissues due to degradation by metabolic enzymes. To improve the immunogenicity of subunit vaccines, adjuvants are often added to the formulation. Adjuvants are defined as compounds that are added to the vaccine formulations in order to enhance the activation of the dendritic cells (DC) and generate strong antigen specific immune responses,

[00139] The silica vesicles of th present invention are also suitable for use with DNA vaccines. While DNA vaccines are capable of eliciting a strong immune response and high specificity, they often suffer from low efficiency of transfection of cell in vivo. Due to their ability to efficiently penetrate cell walls b endocytosis and release a biologically active payload, the immunogenic compositions of the present invention may be used to develop effective DNA vaccines with high transfection efficiency.

[00140] QuilA saponin-based adjuvant is known to stimulate Th1 immune response and production of cytotoxic T-lymphocytes against antigens, making it ideal for use in subunit vaccines for infectious diseases and cancer immunotherapy. However, disadvantages like pain at the site of injection, severe local reactions and toxicity profile of these adjuvants make them unsuitable for human use.

[00141 ] In the experimental section the use of the present hollow silica vesicles SV-1 0-X-140 (being unmodified silica vesicles) and SV-10-X-100-A (being amino-modified silica vesicles} to test in vitro cytotoxicity to MDBK cells is set out as a prelude to testing their use as delivery agents in a nanovaccine formulation. In the cell culture study it was found that the amino functionalised SV-10-X-1 G0-A at a concentration of 0,5 mg/ml was toxic compared to the unfunctionalised SV-1 0-X-140 (Fig. 18). However, at a lower concentration of 0.1 mg/ml and 0.01 mg/ml both SV-I O-x-140 and SV-10-X-1 00-A were found to be of low toxicity. Hence, based on the in vitro cytotoxicity results, both SV-I O-x-140 and SV-10-X-100-A were selected for further investigation. The concentration of the OptiE2 protein loaded SV-1 Q-X-140 and SV-10-X-10G-A was 200 μg protein/mg of silica vesicles after overnight adsorption as determined by protein assay. This represents an excellent level of loading of the antigenic component and is an advantageous feature of the present hollow silica vesicles.

[00142] The in vitro desorption studies on the OptiE2 loaded SVs at 37°C in different buffers indicates that protein once bound to the present SVs does not dissociate easily which is further advantageous. QptiE2 protein did not dissociate when the experiment was performed with 0.1 N HCL and citrate buffer pH 4,0, however, minimal desorption of the protein occurred in 0.1 % SLS.

[00143] To determine the optimal characteristics required of unfunctionalised and amino functionaiised vesicles such as pore size, surface area and functionalisation, both were investigated in an in vivo animal study. The treatment groups injected with OptiE2 {50 pg) loaded SV-10-X-140 (250 pg) and OptiE2 (50 pg) loaded SV-10-X-1.00-A (250 pg) immunogenic composition induced excellent antibody response, which was comparable to the positive control group adm inistered with OptiE2 (50 pg). plus Qui! A (10 pg). However, co-administration of traditional adjuvant Qui! A did not enhance the total IgG titre and the IFN-y response to OptiE2, as treatment groups injected with Quil A plus the HSV nanovaccine looked similar to the positive control group and the OptiE2 protein loaded HSV groups. Adjuvants act like immunostimulators or as antigen delivery vehicles, Qui! A is known to initiate T-cell mediated immune response and the inventors have demonstrated that silica vesicles have the ability to induce both antibody and T-cell mediated responses. The assumption that co-administration of adjuvant and nanoparticles will elicit a strong immune response was based on the immunostimulatory effects and the 'depot effect' slow release of the antigen, where Quil A would potentiate the immune response and antigen loaded nanoparticles would act as delivery vehicles and immunostimulants. However, the results obtained from this experiment indicate that the co-administration of silica HSVs along with traditional adjuvant Qui! A, did not induce a robust immune response.

[00144] This highlights the adjuvancy properties of the present silica vesicles as they act as excellent immunostimulators as well as antigen delivery vehicles, the groups administered protein plus SV nanoformulations induced a better IFN-y response to OptiE2 epitope compared to the positive control group. Both antigen loaded SV-10-X-140 and SV-10-X-1 G0-A elicited good antibody and cell-mediated immune responses. The mice remained healthy throughout the trial and there were no visible focal responses at the injection sites. Addition of traditional adjuvant Qui! A to the protein/nanoparticle formulation did not enhance the immune response. This showed that the SVs themselves act as excellent adjuvants and so present a number of advantages when employed as part of a nanovaccine or immunogenic composition.

[00145] The excellent binding properties, low toxicity, relatively high cellular uptake levels and pore wall structure result in a HSV which has highly advantageous properties as part of an immunogenic composition. These properties, in particular, the pore wail structure in combination with the large internal cavity of the HSVs make this delivery system especially suitable for the development and manufacture of single-dose vaccine products. More specifically, the large internal cavity of the HSVs allows a large amount of drug to be loaded into the HSVs and a larger than normal dose of drug to be delivered to a patient or subject. Since the pore wail structure of the HSVs provides for a limited rate of release of drug from the HSV, this large dose does not become bioavailable all at once, preventing an overdose from occurring. Rather, the drug is released slowly such that an immune response may be elicited over an extended period of time. In this way, drugs that are conventionall delivered using a multiple dose regimen (such as a prime-boost regimen) could, by using the HSVs in a formulation as described herein, be developed to be single-dose drugs. The conversion of a drug's dosing regimen from multiple dose to single dose has a number of advantages including lower administration costs and potentially higher compliance since the real world efficacy of some drugs delivered in multipie doses is limited by poor compliance to multiple dose regimens.

[00146] Further, vaccine immunogens/antigens, and proteins more generally, have long suffered from poor thermal stability, requiring refrigeration from the point of production through to use in the field (the "cold chain") to avoid degradation of the vaccine antigens or proteins and reduction in performance. A major goal in pharmaceutical research has been to improve thermal stability as this would greatly improve the usability and lower the cost of vaccines and protein therapeutics, particularly in remote areas such as on some farms and in developing countries. The present inventors have found that proteins which are contained within the silica vesicles of the present invention have significantly improved thermal stability such that the proteins, housed within the silica vesicles, may be exposed to temperatures well above room temperature without significantly denaturing the protein and affecting its biological activity. Exposure to elevated temperatures may be carried out while the silica vesicle/protein system is in a liquid carrier or in the form of a dried powder. The latter is possible since the protein-containing silica vesicles may be dried out and reconstituted (re-suspended) into a liquid carrier if desired.

[00147] The inventors have also found that encapsulating proteins within the silica vesicles of the present invention improves the resistance of the protein to breakdown by acids. This is a particularly useful feature for situations in which the silica vesicles may be used for the delivery of protein or other acid-sensitive molecules by the oral delivery route. Proteins are difficult to deliver by the oral route as they are typically broken down in the stomach due to the highly acidic environment, rendering them less pharmaceutically effective. The inventors have surprisingly found that protein contained within the silica vesicles is not significantly denatured by exposure to acidic conditions that simulate the environment of the stomach. As such, it may be feasible to use the silica vesicles in the development of oral dosage forms where acid-sensitive molecules such as proteins are desired to be delivered. Similar protection is also offered from trypsin and other digestive agents,

[00148] A sixth aspect of the invention resides in a method of eliciting an immune response in a subject including the step of administering a therapeutically effective amount of the immunogenic composition of the fifth aspect.

[00149] It will be appreciated that the immunogenic composition of the present inventio is not limited in the type of disease that it is used to prevent (in the case of prophylactic vaccines) or treat (in the case of vaccines used for treatment). Examples of diseases that could be treated or prevented using the immunogenic composition of the present invention include, but are not limited to. Adenovirus Type 4 and Type 7, anthrax, tuberculosis, diphtheria and tetanus, pertussis, Hepatitis B, poliovirus, haemophiius, meningococcal disease, hepatitis A, human papillomavirus, influenza, Japanese encephalitis, measles, mumps and rubella, pneumococcal disease, rabies, rotavirus, smallpox, typhoid, varicella and yellow fever.

[00150] The immune response may be a cell-mediated immune response or antibody immune response.

[00151 ] A seventh aspect of the invention resides in a method of preventing or treating a disease or condition in a subject including the step of administering a therapeutically effective amount of the immunogenic composition of the fifth aspect.

[00152] In one embodiment, the disease or condition may be bovine viral diarrhoea, bovine ephemeral fever, anaplasmosis, human papilloma virus (HPV), Hepatitis B virus and influenza and those diseases o conditions listed in relation to the fifth and sixth aspects, above.

[00153] As used herein, the terms "subject" or "individual" or "patient" may refer to any subject, particuiarly a vertebrate subject, and even more particuiarly a mammalian or fish subject, for whom therapy or prophylaxis is desired. Suitable vertebrate animals include, but are not restricted to, primates, avians, livestock animals (e.g., sheep, cows, horses, donkeys, pigs, fish), laboratory test animals (e.g., rabbits, mice, rats, guinea pigs, hamsters), companion animals (e.g., cats, dogs) and captive wild animals (e.g., foxes, deer, dingoes). A preferred subject is a livestock animal selected from the group consisting of a cow, sheep, pig, fish or goat.

[00154] An eighth aspect of the invention resides in the use of a silica vesicle of the second or third aspects and an immunogen in the manufacture of a medicament for the treatment of a disease or condition.

[00155] The disease or condition may be any one or more of those described above in relation to the fifth to seventh aspects of the invention.

[00156] A ninth aspect of the invention resides in the use of a silica vesicle of the second or third aspects as an adjuvant.

[00157] All components of the sixth, seventh, eighth and ninth aspects including the immunogen, silica vesicles, diseases or confitions for treatment and the like may be as previously described in any of the first to the fifth aspects.

[00158] As discussed above, it has been demonstrated experimentally that the silica vesicles synthesised by the method described herein act as excellent immunostimulators as well as antigen delivery vehicles. An improved IFN-γ response to the OptSE2 epitope has been shown in the presence of the SVs.

EXPERIMENTAL Materials

[00159] Block copolymer EO39BO47EO39, commercial name B50-66G0, [EO is polyethylene oxide) and BO is poly(butylene oxide)] was purchased from Dow Company. Tetraethyi orihosilicate (TEOS, 98%), (3-aminopropyl)triethoxysilane (APTES) and fiuorescein-5-isothiocyanate (FITC) were ail purchased from Sigma-Aldrich. The other reagents were of analytical reagent grade.

Analysis.

[00160] The morphologies of the HSVs were observed using a JEOL J.S 7800F field emission scanning electron microscope (FE-SEM) operated at 1.5 kV. For FE-SEM measurements samples were prepared by dispersing powdered samples in ethanol, after which they were dropped onto aluminium foil pieces and attached to conductive carbon film on SEM mounts.

[00161 ] Transmission electron microscopy (TEM) images were obtained with a JEOL 2100 and JEOL 1010 operated at 200 kV and 100 kV, respectively. For TEM measurements samples were prepared by dispersing powdered samples in ethanol on carbon film on a Cu grid and drying.

[00162] Nitrogen adsorption/desorption isotherms were measured at 77 K using a Micromeritics Tristar II system. The samples were degassed at 453 K overnight on a vacuum line. The pore volume and cavity size distribution curves were derived from the adsorption branches of the isotherms using the Broekhoff and de Boer (BdB) model. The Barrett-Joyner-Halanda (BJH) method was utilized to calculate the entrance size from the desorption branch, and the Brunauer-Emmett-Teller (BET) method was utilized to calculate the specific surface areas. The total pore volume was calculated from the amount adsorbed at a maximum relative pressure (P/P _& ) of 0.99.

[00163] Fourier transform infrared (FT!R) spectra were collected on a ThermoNicolet Nexus 6700 FTIR spectrometer equipped with a Diamond ATR (attenuated total reflection) crystal. For each spectrum, 32 scans were collected at a resolution of 4 cm ^"1 over the range 400-4000 cm ^"1 .

[00164] Cryo-TEM and ATR-FTIR of the reaction mixtures were performed at different reaction times to enable real time monitoring of the formation of the silica vesicles. For Cryo-TEM sample preparation, one drop of reaction mixture was dropped onto the carbon film on Cu TE!Vl grids, before and after adding TEOS to the buffer solution containing the block copolymer and subsequently samples were analysed at 15 and 24 hours. The TEM grids were treated with liquid nitrogen for 10 min then freeze dried for at least 2 days.

[00165] For the ATR-FTIR studies, a series of ATR-FTIR spectra were collected at different reaction times (3, 6, 9, 12, 15 and 24 h) after the addition of TEOS into the buffer solution in step 1. Each spectrum was obtained against a background measured using the same buffer solution with an equal amount of Na ₂ S0 ₄ . A further two analyses were carried out for reaction mixture in step 2 which was being performed at 70 C. The analysis was carried out at 3 and 6 h, respectively.

Preparation of hollow silica vesicles

[00166] Step 11 0.5 g of EO39BO47EO3S ^was dissolved in 30 g of pH = 4.7 NaAc-HAc buffer solution ([NaAc] = [HAc] = 0.40 M) with the addition of 0.852 g of Na2SO ₄ (0.20 M) to form a homogenous solution under stirring at 10 °C. To this solution 3.33 g of TEOS was added with continuous stirring for 24 h.

[00167] In order to investigate the influence of temperature in step 1 , a second experiment was carried out at 20 C with all other parameters kept the same.

[00 68] Yet a further experiment was carried out to investigate the influence of stirring in step 1 with all other parameters kept the same but only 10 min of stirring followed by 24 h of the reaction mixture sitting under static conditions. The different phases of reaction mixture which appear without stirring will be separated into different containers to take forward to the next steps.

[00169] Step 2: In step 2, the reaction mixtures from step 1 were taken up to a moderate temperature (40, 50, 60 or 70 C were all triailed in separate experiments) with continuous stirring for a further 24 h.

[00170] Step 3; Reaction mixtures from step 2 were separately exposed to a hydrotherrnal treatment (HT) at different temperatures. To achieve this the appropriate samples were removed from their reaction vessels and placed into autoclaves and hydrothermally treated at one of 100, 120, 130, 140, 150, 170 or 180 C for a further 24 h, at a pressure of 1 , 2, 2.5, 3.5, 5, 8 and 10 bar, respectively. After this treatment step the precipitates were filtered off, repeatedly washed with water to remove the added salts, and the dried in air (referred to herein as the 'as-synthesized sample'). The final product was obtained by calcination of the as-synthesized sample at 550 C in ai for 5 h. To indicate the viabilit of the hollo silica vesicles after step 2 a number of those samples had the precipitate filtered off, washed and ealcined ready for analysis without having being subjected to step 3.

Amino- and FITC modification of HSVs

[00171 ] In the HSV amino-modification process, 1 .5 g of calcined SV-10-50 and SV-10-50-140 were added into separate flasks. 60 ml toluene was added into each flask and the reaction was stirred for 6 h before adding 1 .0 ml APTES. After stirring at 1 10 °C for 12 h, the HSVs were washed extensively with toluene and ethanol before being dried in a fume-hood at room temperature. The ammo-modified samples were denoted SV-10-50-A or SV-10-50-140-A, accordingly.

[00172] To modify the HSVs with FITC, free - H ₂ moieties were utilized for labelling with FITC. The functional group of FITC, thioeyanate, is highly ami oreactive. 20 mg of powdered SV-As i.e. arnino-modified silica vesicles, were dispersed in 3 ml deionized water and mixed with 5 ml of an FITC ethano! solution (0.3 mg/ml). After stirring in the dark at room temperature for 8 h, the SVs were centrifuged and washed with ethanoi three times until the supernatant became colorless. The FITC labelled SVs were used for confocal microscopy observations after use in SCC25 cell uptake experiments.

Hydrophobic modification of HSVs

[00173] To achieve hydrophobic modification of the SVs, 48 mg calcined SV-10-50 and SV-10-50-140 were added separately to two 50 ml three-neck flasks. Each sample was taken up in 6 ml of toluene and the reactant mixtures were stirred for 6 h before adding 0.12 ml (2 %v/v) of n-octadecyltrimethoxylsilane (n-ODMS). After stirring at 110 °C for 12 h, the hydrophobically modified SVs were extensively washed with toluene and ethanoi before being dried in a fume-hood at room temperature. The hydrophobically modified SV products were denoted SV-10-50-C18 or SV-10-50-140-C18, accordingly.

Cell cul tyre and uptake

[00174] SCC25 cells were maintained in Dulbecco's Modified Eagle Medium (DMEM) and supplemented with fetal calf serum (10%, Sigma, MO), L-giutamine (1 %), penicillin (1%) and streptomycin (1%) in 5% COg at 37 C. The medium was routinely changed on alternate days and the cells were separated by trypsinisation before reaching confluency. SCC25 cells were seeded on glass cover slip in a 6-well plate (5 x 10 ⁵ cells per well) and incubated for 24 h. After washing twice with PBS, the cells were incubated with 1 ug/mi FITC labelled SV-10-50 or SV-10-50-140 in 2 ml of the serum supplemented DMEM medium for 24 h. Subsequently, the cells were washed twice with PBS to remove the remaining SVs and dead cells. The cells were then fixed with 2 ml of 4% PFA solution for 30 min at 4 °C, and their nuclei were stained with DAPI and mounted on glass slide. Finally, the cells were viewed under a confocal microscope (LSM Zeiss 710) and images were captured. Loading of cytochrome C and staining

[00175] 0,5 ml PBS solution containing 1 mg SV-10-50 or SV-10-50-140 after calcination or following amino-modification was mixed with 0.5 ml cytochrome c-PBS solution (2 mg/mi). After incubation at 25 °C for a range of different times (5 _S 15, 30 min, 1 , 2, 3, 8 and 12 h), the mixtures were centrifuged. To evaluate the cytochrome c loading efficiency, the supernatant was collected and the residual cytochrome c content measured using a UV-2450 (UV-Vis spectrophotometer, Shimadzu) at a wavelength of 480 nm. The loading amount of cytochrome c can be calculated based on the original and residual cytochrome c concentrations and volumes. The cytochrome c loaded SVs were re-dispersed into 1 ml. One drop of this suspension can be dropped onto the carbon film on Cu TEM grids and dried in air. The TEM grids were then treated with the staining agent 5 % uranyl acetate (UAT) in 50 % ethanoi solution at 60 °C for 6 min. The stained TEM grids were washed with deionized water and dried in air.

Loading of Ribonuclease A and staining

[00176] 0.5 ml of phosphate buffered saline (PBS) solution containing 1 mg of either SV-10-50-C18 or SV-10-50-140-C18 was prepared as a suspension using an ultrasonic bath. Each suspension was mixed with 0.5 ml of ribonuclease A (RNase A)-PBS solution (2 mg/mi). After shaking at 200 rpm in a 25 °C incubator for 18 h, the mixtures were centrifuged. To evaluate the RNase A loading efficiency, the supernatant was collected through a 200 nm filter and the residual RNase A content was measured using a UV-2450 (UV-Vis spectrophotometer, Shimadzu) at a wavelength of 277.5 nm. The loading amount of RNase A can be calculated based on the original and residual RNase A concentrations and volumes. The RNase A loaded SVs were re-dispersed into 1 ml. One drop of this suspension was dropped onto the carbon film on Cu TEM grids and dried in air. The TEM grids were then treated with the staining agent 5 % uranyl acetate (UAT) in 50 % ethanoi solution at 60 °C for 6 min. The stained JEM grids were washed with deionized water and dried in air.

Cell toxicity and RNase A denaturation

[00177] SCG25 cells were seeded in a 96-well plate at a density of 2 x 10 ⁴ cells per well and cultured in 5% C0 ₂ at 37 C for 24 h. Then, free RNase A, SVs, RNase A loaded SVs and corresponding denatured samples were added to the cells in DM EM medium at an RNase A dosage of 4-16 pg/ml, and the cells were incubated in 5% COa at 37 °C for 24 and 72 h. Subsequently, MTT reagent (10pl/wel[ volume from 5mg/ml solution in PBS) was added to each well, shaken for 10 seconds and then incubated at 37 °C for 4 h. The precipitants were collected following cent ilugation for the above cell toxicity experiments after the removal of the supernatant. Then DMSO (100μΙ) was added to each well to dissolve the formazan crystals and the optical density (OD) was recorded at 570 nm using a micropfate reader (SpectraMax M5, Bio-Strategy, Ltd). Cells incubated in the absence of SVs and RNase A were used as the control. All the experiments were performed in triplicate for each group.

[00178] Another series of controf groups was prepared after heat and acid denaturation of RNase A, including both free RNase A and RNase A loaded SVs. In the denaturation process, 50 μ! of HCl (0.01 M, pH 2.0) solution was added in to 1 mg of free RNase A or 6-9 mg of SVs (loaded with 1 mg RNase A). The mixtures were incubated at 65 ^; C for 40 min, cooled and centrifuged. NaOH (0.01 M) solution was added dropwise into the mixtures until the pH reached -7, indicated by precise pH paper and used as a denatured RNase A group in the present experiment.

HOLLOW SILICA VESICLES AS VACCINE DELIVERY SYSTEMS

HSV Characteristics [00179] The SVs used in the 'nanovaccine' experiments were both unmodified 'SV-I O-x-140' and amino-modified 'SV-10-x-IOO-A' versions with the characteristics as shown in table 1 below.

Trypan blue staining for in vitro cytotoxicity assay

[00180] Madin-Darby bovine kidney (MDB ) cells (ATCC) were seeded at 80-90% confluency onto glass coverslips in a 24 well plate and allowed to adhere overnight in a 37°C, 5% C02 incubator. To investigate th effect of nanoparticle concentration on the ceils a dilution range (0.5 rng/mi, 0.1 mg/ml and 0.01 mg/ml) of SV-I O-x-140 and SV-10-X-100-A particles in Earle's Minimum Essential Media (containing 5% foetal bovine serum (Life Technologies) were prepared and gently added drop wise to the adherent cells. The cells were incubated in the presence of unfunctionalised SV-I O-x-140, SV-10-X-100-A and MCM-41 (commercially available mesoporous silica) as synthesised nanoparticles at 37°C, 5% CD ₂ for 20 . Media was carefully removed and the wells were gentiy washed three times with PBS to remove the SVs/nanoparticies. To determine cell viability 0.2% trypan blue stain (Life Technologies) was added for 2 minutes. Trypan blue stain was carefully removed and the weils were washed onc with PBS. Cells were fixed in 4% paraformaldehyde (PFA) pH 7.4 for 15 minutes, and then washed three times with PBS. Coversltps were mounted with 5μΙ of MOWiOL (Sigma). Cell viability was determined by imaging on a Zeiss HAL100 microscope under bright field.

QptiE2 Adsorption to SV and SV-A nanoparticies

[00181] Adsorption reactions used 1.5 mg of SV-IO-x-140 and SV-10-X-100-A particles with 300 Mg of OptiE2 in sterile Tris buffer at 2,5 mg/ml in a 2ml final volume. This particle-protein slurry was placed in a shaker at room temperature (RT), after 24h a sample of particle-protein slurry (50 μΐ) was removed and centrifuged at 16.2 gfor 1 minute. The amount of unbound OptiE2 protein was assessed by electrophoresis of the supernatants on SDS-PAGE gels.

Desorption studies

[00182] The OptiE2 loaded SV-10-x-140 and SV-10-x-100-A nanoparticle pellets were resuspended in 1000 μΙ of PBS plus 0.1 % SLS (sodium laureth sulfate), or 0.1 N HCL or citrate buffer with pH 4.0 and the samples were left on shaker at room temperature for 120 min at 200 rpm. The supernatant was assessed for desorbed protein by electrophoresis on SDS-PAGE gels.

Protein Assay

[00183] The supernatant of the adsorbed samples were quantified by protein assay (BioRad DC kit) following the manufacturer's instructions.

Polvacrvaiamide gel electrophoresis (PAGE)

[00184] Silica vesicle/nanopartic!e samples were resuspended in 15 μΙ of PBS and 5 μΙ SRB (SDS Reducing Buffer consisting of 62.5 mM Tris-HCI (pH 6.8), 117 mM DTT, 10 % Glycerol, 2 % SDS, 0.02 % Bromophenol blue), incubated at 85 °C for 2 min then subjected to electrophoresis on 10 % Tris-Giycine gels (Invitrogen). Th ge!s were visuaiised by staining in 50% methanol, 10% acetic acid, 0.25% Coomassie Blue R250 for 30 min, followed by destaining in 30% methanol, 10% acetic acid for three 30 min washes.

Immunization studies conducted in mice [00185] C57BL/6J mice were purchased from and housed in the Biological Resource Facility, The University of Queensland, Brisbane, Australia under specific pathogen-free conditions. Eight week old female mice were housed in HEPA-filtered cages with 4 animals per group in an environmentally controlled area with a cycle of 12 hours of fight and 1 hours of darkness. Food and water were given ad libitum. All procedures were approved by The University of Queensland Ethics Committee. Animals were closely monitored throughout the study. All the animals remained in good health for the duration of the study with no visible deleterious health effects. Pre-immunisation b!ood samples were collected by retro-orbital bleeds using heparin coated hematocrit tubes (Hirsehmann Laborgerate, Heilbronn, Germany). Pre-immunisation blood samples collected prior to the first immunisation were referred to as the preimmune (PI) samples. Table 2 below shows the different treatment groups in the study. Adsorption reactions were prepared aseptically as described above. QuilA (Superfos Bioseotor, Vedback, Denmark) was resuspended at 2 mg/ml in sterile injectable water (Pfizer, Brooklyn, USA). The injectable doses were administered into the tail base by four subcutaneous injection to investigate the difference between the immune responses produced b the OptiE2 loaded SV-I O-x-140, OptiE2 loaded SV-I O-x-140 plus QuilA, QptiE2 loaded SV-10-X-1 GO-A, and OptiE2 loaded SV-10-X-1 Q0-A plus QuilA. The positive control group of mice received 5Gpg QptiE2 protein and 10pg QuilA. The negative control group received injections of SV-I O-x-140 and SV-10-x-1 GO-A (25Qpg) vesicles plus Quil A (10pg). Dose volumes of 100μΙ (in 0.9% saline, Pfizer) were administered by subcutaneous injection at the tail base using a sterile 27 gauge needle (Terumo, Tokyo, Japan). Three injections were administered at 2 week intervals to all the treatment groups except for the unimmunised group and mice were sacrificed 14 days after the final immunisation. The OptiE2-specific antibody responses were studied using the Enzyme-Linked Immunosorbent Assay (ELISA) assay and the cell-mediated response was studies using ELISOPT assay. Group Prototype Vaccine Injection Dose

1 OptiE2 + Qui!A OptiE2 {50pg) + QuilA ftOpg)

Positive control

2 OpiiE2 (SOpg) bound OptiE2 (SOpg) + SV-tO-x-140

SV-10-X-140 (250 M9)

3 OptiE2 (SOpg) bound OptiE2 (50pg) + SV-10-X-1 0

SV-10-x-14G + GuiiA (250 Mg) + Quil A. {10M9)

4 OptiE2 (50pg) bound OptiE2 (50pg) + SV-10-X-100-A

SV-10-X-100-A (250 M9)

5 QptiE2 (5Gpg) bound OpiiE2 (SOpg) + SV-10-x-100-A

SV-10-X-100-A + Qui! (250 pg) + Quil A (10jjg)

6 SV-10-X-100-A + Qui! SV-10-x-100-A (250 g) + Quil

A (10pg) A (10pg)

7 SV-10-X-140 + Qui! A SV-10-X-140 {250 Mg) + Quil A

<1-0ng) (10pg)

8 Unimmunised -

Immunization groups in mice trial. All doses were administered at the

EL ISA protocol

[00186] Detection of OptiE2-specific antibod responses: Enzyme-Linked Immunosorbent Assay (ELISA) for the detection of OptiE2-specific antibodies were performed by coating microtitre plates (96 well. Nunc, Maxisorb, Roskilde, Denmark) with OptiE2 antigen solution (2 ng pL-1 , 50 pL) i PBS overnight at 4 °C. The coating solution was removed and the plates were washed once with PBS-T (PBS (1 x), Tween-20 (0.1 %), Sigma-Aldrich) and blocked with Bovine Serum Albumin (BSA, 5%, Sigma-Aldrich) and skim milk (5%, Fonterra, Auckland, New Zealand) in PBS (200 pL) for 1 h with gentle shaking at RT. Plates were washed three times with PBS-T. Mouse sera samples were diluted from 1 :100 to 1 :6400 in PBS {50 pL) and each dilution was added to the wells of the blocked plates followed by incubation for 2 h at RT. To detect mouse antibodies HRP conjugated polyclonal sheep anti-mouse IgG antibodies (Chemicon Australia, Melbourne, VIC, Australia) diluted in PBS to 1 :1000 were added to each well and incubated for 1 h at room temperature with gentle shaking. Plates were washed three times in PBS-T. T S substrate (100 pL, Sigma-Aldrich) was added to each well and incubated for 15 min at room temperature; HC! (1 N, 100 pL) was added to wells to stop the chromogenic reaction. The plates were read at 450nm on a Labsystems Multiskan RC plate scanner.

Isolation of murine splenocvtes and ELISPOT Assay

[00187] Spleens were aseptically removed following euthanasia and placed into ice cold DMEM media (5 mL) supplemented with fetal bovine serum (FBS, 10%), Hepes (20 mM, pH 7.3), sodium pyruvate (1 ), Glutamax (1 M), penicillin G, streptomycin, Fungizone (calculate final amounts of each). Spleens were gently disrupted and passed through a nylon mesh (100 mm, Becton Dickinson, Franklin Lakes, NJ) using a syringe plunger. Cells were washed with DMEM (5 mL) and centrifuged (800 g, 5 min, 4 °C) and then resuspended in lysis buffer (NH ₄ CI (0.15 M), KHCO ₃ (10 mM), Na ₂ -EDTA (0.1 mM), 1 mL) for 5 min at room temperature. Repeat wash steps twice with DMEM (9 mL and 5 mL) each time. Cell pellets were resuspended in DMEM (2 mL) and cell numbers determined by staining with trypan blue (0.2%). Cells from each mouse spleen were seeded at 1 .0 - 1 .5 x 10 ⁵ cells/well in triplicate into Polyvinylidene fluoride (PVDF) ELISPOT plates precoated with monoclonal interferon-g (IFN-y) (Mabtech) capture antibody. Cells were incubated in complete DMEM medium at 37 "C and 5% CO ₂ for 40 h in the presence or absence of OptiE2 antigen (1 mg/mL, SIINFEKL, Auspep, Parkvi!le, VIC, Australia) or the polyclonal activator concavalin A (Con A, 1 mg/mL, Sigma Aldheh) as a positive control. IFN-γ ELISPOT assays were performed according to the manufacturer's specifications. The ELISPOT plates were read on an ELISPOT reader (Autoimmun Diagnostika, Strassburg, Germany). RESULTS

Characteristics of SVs

[00188] FIG 1 shows two field emission SEM images (A and B) showing that both SV-10-50 (image A) and SV-10-50-140 (image B) possess a spherical morphology with a uniform particle size under 100 nm. Looking to FIG 2 the TEM images of as-synthesized SV-10-x-I GO show unilamellar vesicles with a diameter of approximately 50 nm and a wall thickness of about 5nm (FIG 2A). From the higher magnification TEM image (FIG 2B), it can be seen that a sandwich-like unilamellar structure of silica-void-silica is formed in the vesicle walls, indicating the existence of a silica-surfactant composite as represented in FIG 3. After calcination, SV-10-50 maintains a unilamellar vesicle structure, as seen in FIG 4A, and the spherical bodies can be clearly observed inside the vesicle walls indicating that the silica vesicles possess a porous wall structure which is made up of these spherical bodies, being bubble-like voids within the siliceous wall, which may be separate from one another or may be interconnected to form a pathway from the exterior to the interior cavity of the SV. This is best seen in FIG 4B. SV-10-50-140 also maintains a unilamellar vesicle structure (FIG 4G), and an entrance size of ~ 15 nm can be observed on the wall as shown in FiG 4D.

[00189] The existence of a void in the silica vesicle walls is further confirmed by N ₂ sorption analysis. FIG 5A illustrates the nitrogen adsorption-desorption isotherms of SV samples at 40-70 °C heat treatment in step (b), which all show type IV isotherms with a type H2 hysteresis loop, indicating these four samples , having been exposed to an 'intermediate ¹ temperature treatment in the second step, show similar pore structures. More structural information from the N ₂ sorption results are shown in Table 1. FIG 5B shows the nitrogen adsorption isotherms of S samples which had been exposed to hydrothermal treatment temperatures of 120, 130, 140, 150, 170 and 180 ^e C, at pressures of 2, 2.5, 3.5, 5, 8 and 10 bar, and these are seen to be typical type IV isotherms with desorption branch shifting to higher relative pressure as the hydrothermal treatment temperature increases. A BdB method is used to calculate the cavit size from the adsorption branc of nitrogen adsorption isotherms, and the entrance size is calculated using a BJH method from the desorption branch. The BdB pore size distribution curves in FIG 5C show a peak centred at approximately 2 and 15 nm in SV samples with step (b) performed at 40-70 °C, and for SV samples subjected to a hydrothermal treatment temperature of 100-180 °C, at pressures of 1 -10 bar, the BJH pore size distribution curves calculated from desorption branch, as seen in FIG 5D, show peaks shifting to the right with increasing temperature, indicating increasing entrance sizes.

[00190] It is noted that all SV samples show a BdB calculated inner cavity size of 40-50 nm (FIG 6), which indicates that all SV samples have similar cavity sizes within this range. As summarized in Table 3, below, the pore entrance size of the SVs could be adjusted in the range of 6-16 nm.

Table 3: Structural information from N ₂ sorption results

x: samples with direct hydrothermal treatment after continuous stirring at 10 °C. V _R; : total pore volume; SQ _EJ - BET surface area. [00191 ] TEM images of SV-10-70 after calcination (FIG 7A) show similar vesicular structure with a pore wall structure in line with that already observed for SV-10-50. In contrast, no pore wall structure can be observed in the TEM images of SV-10-X-100, SV-I O-x-130 and SV-x-180 after calcination (FIG 7B-D) indicating the second step of treatment at moderate or intermediate temperature is essential for proper pore wall structure formation. Pore entrances with sizes of approximately 10 and 30 nm can also be observed (FIG 7C and D), respectively, which is in accordance with the N ₂ sorption results.

[00192] In comparison, the TEM images of SV samples which were generated with onl 10 min of stirring followed by 24 h static treatment show no vesicular structure. Instead short tubular structures and amorphous silica structures are observed as shown in FIG 8A and B, respectively. Compared to the uniform white reaction mixture achieved with continuous stirring, shown in FIG 8C, the reaction mixture without continuous stirring separates into a transparent lower phase and white gel-like upper phase, shown in FIG 8D. The TEM image of SV-20-x-IOO shows a mixture of vesicular and tubular structures, FIG 8E. It is clear from this result that some form of agitation is crucial for formation of the desired vesicular morphology.

Cryo-TEM and ATR-FTIR Observations

[00193] In order to understand the SV formation mechanism, Cryo-TEM was utilized to investigate the developing vesicle structure at different time points during step (a) (T1 in FIG 3). As indicated in FIG 9A, block copolymer B50-6600 surfactant is in micelle form with a diameter less than 20 nm, before addition of the silica source (TEOS). This shows no pre-formed vesicular template is used in the synthesis at 12 h (FIG 9B), and the formation of SVs is a cooperative self-assembly of surfactant and silica oligomers. 15 h later after adding TEOS, self-assembled silica-surfactant vesicles can be observed (FIG 9C), however, no pore wall structure can be observed at the end of step 1 (FIG 9D), it is therefore apparent that the pore wall structure is formed only in a post treatment at moderate temperature.

[00194] ATR-FTIR spectroscopy, in addition to the Cryo-TEM. discussed above, was used to monitor the chemical species forming in the reaction mixtures. The ATR-FTIR spectra of reaction mixtures at different reaction times (3, 6, 9, 12, 15 and 24 h) in step (a) or T1 , as denoted in FIG 3, were measured. FIG 10A shows three characteristic peaks appearing at 877, 1045 and 1272 cm ^"1 which can be attributed to EtOH (v(C-0)+ v(C-C)} and (p'(CH ₃ }+ p(CH ₂ )}, respectively. The weak and broad band observed at 964 cm is associated with the Si-0 stretching of Si-OH groups. The vibration of Si-O-Si in condensed silica exhibits a broad peak in the region of 1050-1200 cm ^"1 , the assignment of which is complex. All the spectra from step one show the same characteristic bands at 783, 960 (p(CH ₃ )}, 1084 (v(C-0)/(G-0)+(C-C)), 1105 (p'(CH ₃ )), 1167 (p(CH ₃ )), 1272 (τ(ΟΗ ₂ )}, 1396 (5s(CH ₃ )) cm ^"1 , which can be assigned to the -Si-OChbCHs groups.

[00195] The presence of -Si-OCHaCh groups throughout the 24 h reaction period in step (a) or T1 , as denoted i FIG 3, shows that the hydrolysis rate of TEOS is slow, which can be attributed to the steric effect of the alkoxy groups. The intensity of the bands at 878 and 1045 cm ^"1 (both attributed to ethanol) increases slowly with the reaction time, indicating that the hydrolysis rate of TEOS is slow and the hydroiysis reaction of ethoxy groups continues in the time window in step (a) or T1. It is noted that the siianol groups derived from the hydrolysis of ethxoy groups should also exhibit a characteristic band at around 960 cm ^"1 (Si-0 stretching). However, considering the limited amount of ethanols released and thus a small amount of silanois generated, the peak for silanois can be overlapped with the band associated with SiOCH ₂ CH ₃ and so may not be observed. Moreover, by comparing the characteristic peaks in the range of 1050-1200 cm ^'1 , no obvious broadening of bands in this region (which indicates the formation of -Si-O-Si) is observed in the TEOS system, i.e. the condensation rate of TEOS is also slow. As a result, the dominant siliceous species In step (a) or T1 are both partially hydrolyzed silanols and unreacted hydrophobic ethoxy groups. The hydrophobic silica oligomer in step

(a) or T1 leads to a high g factor of silica/surfactant composite. The formation of vesicles is assumed to be from the bending and closure of a composite layer, which is similar to the formation of surfactant vesicles.

[00196] The ATR-FTIR spectra of the reaction products at 3 and 6 h in step

(b) or T2, as denoted in FiG 3, were also measured and are shown in FIG 10B. Ail characteristic peaks (876, 1045, 1086, 1277, 1348, 1413 and 1452 cm ¹ } can be attributed to EtOH (v(C-0)+ v(C-C)} and (p' CH ₃ }+ p(CH ₂ )), respectively. No peak can be assigned to the -5ί-ΟΟΗ ₂ 0Η ₃ groups, indicating TEOS has a much faster hydrolysis rate in this step and a low condensation rate at a moderate temperature from -Si-OCH ₂ CH ₃ groups to silanol in step (b) within the silica vesicle-surfactant composites. This hydrophiiic silica oligomer in step (b) leads to a lower g factor of silica surfactant composite, which gives rise to high curvation change of the silica surfactant composite without changing the vesicular skeleton to form a pore wail structure within the siliceous walls. The proposed formation mechanism of these silica vesicles is described in FIG 3.

Loading of cytochrome C and staining

[00197] FIG 11 shows high adsorption amounts of cytochrome c at 5 min in the hollow silica vesicles tested which indicates very fast adsorption for both SV-10-50 and SV-10-50-140 after calcinations. The adsorption level remains relativel steady after 5 min indicating the maximum adsorption amount has already been reached in this short space of time. The amount of loaded cytochrome c was 620, 642 mg/g for SV-10-50, SV-10-50-140, respectively.

[001 8] 5% UAT in 50% ethanol solution was utilized as the staining agent for cytochrome c loaded in HSVs. The same staining method was applied to pure SV-10-50-140-C, i.e. after calcination, as a control, and the TE image shown in FIG 12A is similar to that of a HSV which has not been stained, indicating that the siliceous materials will not be stained by UAT, Figure 12B shows several silica vesicles having a cavity with higher contrast (darker cavity, indicated by white arrows), which is stained cytochrome c. The high contrast of the cavity remains average with high tilting angles, as seen in FIG 12C and D, which indicate cytochrome c is uniformly adsorbed by the HSVs. This staining method has also been applied to SV-10-50 vesicles (FIG 13).

Loading of Ribonuclease A and staining

[00199] The FTIR spectra seen in FIG 14 show the characteristic peaks of octadecyl groups on the vesicles after hydrophobic modification, indicating successful grafting of the hydrophobic groups onto the silica vesicles. The adsorption amount of RNase A for SV-10-50 and SV-10-50-140 after hydrophobic modification at 18 h is 206+6 and 276±8 mg/g, respectively, 5% UAT in 50% ethanol solution was utilized as the staining agent toward cytochrome c loaded in the SVs. The same method was applied to pure SV-10-50 after hydrophobic modification, and the TEM image (FIG 1.5) is similar to that of the SV without staining, indicating the siliceous materials will not be stained by UAT. FIG 15B shows a single silica vesicle possessing a cavity with higher contrast (darker cavity), which is considered to represent stained RNase A. RNase A has been shown to be uniformly adsorbed by the SVs.

Oeil culture and u ptake

[00200] Silica vesicles which had been labelled with FITC, as described above, were studied by confocal microscopy to visualize the cellular uptake. As shown in FIG 16, when the cells are incubated with FITC labelled SV-10-50 and SV-10-50-140, strong green fluorescent signals originating from FITG are detected inside the cells, indicating that the HSVs are readily taken up by SCC25 cancer cells (FIG 16H and L). FITC labelled SV-10-50-140 shows a stronger signal suggesting an increased amount of SV-10-50-140 internalized by SCC25 ceils. Cell toxicity

[00201 J RNase A is regarded as a strong protein synthesis disrupter which can degrade mRNA and tRNA to influence cell viability. It has been reported that heat-denatu ration of RNase A reduced cell toxicity in MCF-7 cell lines where RNase A was conjugated on the outer surface of the dense silica nanoparticles. The anti-cancer effects of free RNase A, RNase A loaded SVs, SVs and corresponding denatured samples were investigated in human skin cancer SGC25 cells. Cells were treated with free RNase A, RNase A-SVs, denatured RNase A or denatured RNase A-SVs with the same concentration of RNase A, The SV concentrations were calculated from the adsorption amount of RNase A in SVs.

[00202] The results in FIG 17 reveal that both SV-10-50 and SV-10-50-140 showed almost no toxicity to SCC25 ceils at 24 h at the concentration of 78 and 58 pg/ml, respectively. SV-10-50-140 shows low toxicity at 72 h ( 7% inhibition), indicating both SV species are biocompatible nano-carriers. Fre RNase A and free RNase A after denaturation exhibit no cytotoxicity to SCC25 cells. Compared to free RNase A, RNase A loaded SV-10-50 and SV-10-50-140 after hydrophobic modification showed the highest cytotoxicity over a long time range (inhibition of 17%, 26% at 24 h and 54%, 43% at 72 h, respectively). Interestingly, RNase A loaded SVs after heat and strong acid denaturation showed high cytotoxicity to SCC25 cells compared to free RNase A with an inhibition of 14%, 22% at 24 h and 48%, 38% at 72 h for SV-10-50 and SV-1 0-140, respectively. RNase A-SVs after denaturation show slightly lower cell toxicity than RNase A-SVs without denaturation. These results demonstrate that the present SVs can provide protection to RNase A, whic is proved to be adsorbed within the silica vesicles, from harsh conditions. RNase A loaded in SV-10-50-140 showed higher cytotoxicity due to its higher efficiency of cell internalization.

VACCINE DELIVERY SYSTEM RELATED RESULTS In vitro cytotoxicity studies

[00203] The in vitro cytotoxicity of the SV-10-x-i 0 and SV-10-x-100-A vesicles was determined by trypan blue dye exclusion staining of MDBK cells. The cells were treated with different concentrations (0.5, 0.1 and 0.01 mg/ml) of SV-I O-x-140 and SV-10-X-10Q-A vesicles. Dead cells exhibited a blue colour due to the uptake of the dye via permeabilised cell membranes whereas viable cells remain intact and do not take up the stain. SV-I O-x-140 and SV-10-x-100-A at 0.1 mg/ml and 0.01 mg/ml did not show any toxic effect on cell viability (FIG 18, b, c, e and f). However, the SV-10-x-100-A at 0.5mg/ml had a toxic effect on the MDBK cells (FIG 18a) after 20 hours incubation. The cells incubated with lower concentrations of SV-I O-x-140 and SV-10-x-100-A vesicles looked comparable to the cells incubated alone without vesicles, hence all further experimental investigations were carried out using both SV-I O-x-140 and SV-10-X-100-A vesicles.

Adsorptio n and Desorptio n an alysi s

[00204] OptiE2 protein was loaded onto the SV-I O-x-140 and SV-10-X-100-A vesicles, as described above. The molecular weight of OptiE2 is 42 kDa. SDS-PAGE analysis was used to determine whether there was adsorption to the particles. Protein assays of the binding supematants and application of a mass balance equation were used to determine the amount of OptiE2 adsorption to SV-IO-x-140 and SV-10-x-100-A vesicles. 200 pg of OptiE2 bound to 1 mg of SV-I O-x-140 and SV- 0-x-100-A vesicles as determined by protein assay. Desorptian studies were performed on the OptiE2 loaded SV-I O-x-140 and SV-10-x-100-A.

[00205] To investigate the desorption the OptiE2 loaded vesicles pellets were resuspended in different buffers which included 0.1 N HCL 0.1 % SLS and citrate buffer at pH 4.0. The samples were incubated at 37°C on a shaker for 120 minutes. Gel analysis on the desorbed supernatant and particle fractions showed that in the presence of 0.1 N HCL and citrate buffer pH 4.0, the protein remained strongly bound to the vesicles and it did not desorb from both SV-I O-x-140 and SV-10-X-1 G0-A (FIG 19).

[00206] The details of the analytical results presented in FIG 19 are as follows: (a) Evaluation of OptiE2 loaded nanopartfCleB, lane 1 : OptiE2 protein; lane 2: OptiE2 loaded SV-10-x-I OO-A supernatant; lane 3: OptiE2 loaded SV-10-X-100-A nanoparticle pellet; lane 4: OptiE2 loaded SV-tO-x-140 supernatant; lane 5: OpttE2 loaded SV-I O-x-140 nanoparticle pellet (b) Desorption studies of OptiE2 loaded nanoparticles, lane 1 : QptiE2 loaded SV-10-X-100-A supernatant desorbed in 0.1 N HCL; lane 2: OptiE2 loaded SV-10-X-100-A nanoparticle pellet desorbed in 0.1 N HCL; lan 3: OptiE2 loaded SV-10-X-100-A supernatant desorbed Q.1 % SLS; lane 4: OptiE2 loaded SV-10-X-1 G0-A nanoparticle pellet desorbed in 0.1% SLS; lane 5: OptiE2 loaded SV-1 Q-X-1 G0-A supernatant desorbed in citrate buffer (pH - 4.0); lane 6: OptiE2 loaded SV-10-x-I OO-A nanoparticle pellet desorbed in citrate buffer (pH - 4.0); lane 7: OptiE2 loaded SV-IO-x-140 supernatant desorbed in 0.1 N HCL; lane 8: OpttE2 loaded SV-IO-x-140 nanoparticle pellet desorbed in 0.1 N HCL; lane 9: OptiE2 loaded SV-tO-x-140 supernatant desorbed 0.1% SLS; lane 10: OptiE2 loaded SV-I O-x-140 nanoparticle pellet desorbed in 0.1% SLS; lane 11 : OptiE2 loaded SV-IO-x-140 supernatant desorbed in citrate buffer (pH - 4,0); lane 12: OptiE2 loaded SV-10-x~140 nanoparticle pellet desorbed in citrate buffer (pH - 4.0).

[00207] A very low amount of protein desorption from the vesicles was observed in the presence 0.1 % SLS. The SV-I O-x-140 and SV-10-X-100-A showcased similar adsorption and desorption characteristics. The SV-I O-x-140 and SV-10-X-100- have different pore sizes, therefore in order to investigate if the OptiE2 protein binds differently to these particles (internally or externally) and can have an effect on elicitation of immune responses when co-administered with a traditional adjuvant. Qui! A, in vivo experiments were carried out with SV-10-x-1 0 and SV-10-x-100-A vesicles.

ELISA data [00208] Mice were Immunised with vaccine formulations as described in Table 2. The total IgG responses of the immunised mice were analysed by anti-OptiE2- specific ELISA assays post three subcutaneous vaccine injections. The OptiE2 loaded HSV vaccine formulations were freshly prepared before the injection. PI sera samples from mice were collected at the start of the trial, and the subsequent sera samples were collected at two-week intervals following each injection over a 6 week period. Aii the mice remained in the normal weight range throughout the experiment. The ELISA result (FIG 20} from the terminal bleeds suggest that the immunogenic composition treatment groups (OptiE2 + SV-IO-x-140. OptiE2 + SV-I O-x-140 + Quil A, OptiE2 + SV-10-x-10Ό-Α, GptiE2 + SV- G-X-100-A + Quil A) and the positive control group (OptiE2 + Quil A) showed an excellent antibody titre up to a dilution of 1 ;6400 with an average OD450nm of 1 ,20. The treatment group administered with OptiE2 plus HSV (SV) without any traditional adjuvant elicited an antibod response comparable to that seen for the positive control group. The group of mice injected with BVDV OptiE2 Ioaded unmodified or functionalised HSVs plus Quil A, showed almost simitar responses, The co-administration of HSVs and traditional adjuvant did not result in a robust immune response, as the presence of Quil A in the vaccine formulation did not dramatically increase the response. Variation in the antibody respons was observed between the four mice receiving OptiE2 plus SV-10-X-100-A nanoformulation. The negative control groups receiving SV-I O-x-140 and SV-1O-X-1C0-A HSVs plus Quil A, showed a low background antibody response to OptiE2 epitope.

ELISPOT Assay

[00209] To determine the T cell mediated IFN-γ response to OptiE2 antigen an ELISPOT assay was used. Two weeks after the final immunisation, spleens from sacrificed mice were collected and harvested to obtain splenocyte cell populations. The mice receiving nanovaccine formulations OptiE2 + SV-10-X-140, OptiE2 + SV-I O-x-140 + Quil A, OptiE2 + SV-10-X-1 G0-A, and OptiE2 + SV-10-X-100-A + Qui! A showed excellent cell-mediated immune response to OptiE2 epitope. The results from the ELISPOT assay (FIG 21 wherein M1 to M4 are the individual mice in each group and the black bars indicate the number of cells producing IFN-y in response to the OptiE2 antigen) indicate that groups receiving antigen plus hollow silica vesicles looked more or less similar to the groups administered with antigen loaded HSVs plus traditional adjuvant. However, the groups receiving the nanovaccine formulations showed a better !FN-γ response compared to the positive control group (OptiE2 + ^■ Quil A), highlighting the eff iciency of silica vesicles as excellent adjuvants in their own right. In addition, the groups treated with antigen loaded HSVs elicited better T cell mediated response compared to the groups treated with antigen loaded HSVs plus traditional adjuvant. Co-administration of SVs plus traditional adjuvant did not increase the antibody response as well as the IFN-γ response significantly. The negative control groups, SV-10-X-140 plus Qui! A, SV-1 O-X-1O0-A plus Quil A and the immunised group produced an IFN-γ response. However, the response was not specific to the OptiE2 antigen as the unimmunised group too produced an IFN-γ response to the OptiE2 epitope.

FURTHER NANOVACCiNE EXPERIMENTS

[00210] The preceding experiments indicated clearly that the silica vesicles of the present invention with thin shell wail, large cavity and entrance size, improved OptiE2 protein adsorption and release. In addition, the OptiE2 (50 pg)/SV-140 (250 pg) formulation induced higher anti-OptiE2 IgG as well as IFN-y responses compared to the positive control group OptiE2 (50 pg) plus Quil A (10 pg) and acted as se!f-adjuvants. While indicating commercially useful efficacy it was noted that to obtain a good level of antibody and cell-mediated immune responses the animals received administration of three nanovaccine injections. This success led the present inventors to develop an effective nanovaccine that could generate long-term immune responses using BVDV E2 as a model virus antigen. General Discussion

[00211 J Generally, the long term in vivo functionality of OptiE2 loaded silica vesicles (SV)- 40 was tested in mice models by administering the positive control group with Opt!E2 plus Quil A (100 pg of OptiE2 plus 10 pg of Quil A) and the nanovaccine treatment group with QptiE2/SV-140 (100 pg of OptiE2 adsorbed to 500 pg of SV-140). The mice were vaccinated with two injections and blood samples were collected at eight different time points for a period of six months to analyse the antibody responses. Spleens from the sacrificed mice, at two different time points post the final immunisation at 3 weeks (four mice) and 25 weeks (four mice), were collected to determine the IFN-γ response. The nanovaccine treatment group OptiE2/SV-140 generated BVDV specific antibody responses comparable to the conventional adjuvant Quil A at all the eight time points. In addition, at 25 weeks the cell-mediated response, which is essential to recognise and eliminate the invading pathogens, was higher [1500 spot forming units (SFU)/millipn cells] in all four mice immunised with OptiE2/SV-140 in comparison to OptiE2 plus Quil A (473-1500 SFU/million cells). These experiments demonstrate the ability of SVs to induce long term humoral as well as cell mediated immune responses. Immunohistochemistry studies also showed higher response in mice injected with BVDV E2 SV formulation as compared to BVDV E2 Qui! A, In addition, histopathology analyses was done on ail the major organs of the animals at both 3 weeks and 25 weeks to make sure that the SV did not have a detrimental effect. All the animals used in the study remained healthy throughout the experimental period.

Experimental

Adsorption of QptiE2 on SV-140

[00212] Adsorption reactions used 2 rng of SV-140 with 500 pg of GptiE2 in sterile 50mM T is buffer (pH7.0) containing 0.2% Igepa! CA630, in a 2 ml final volume. This particle-protein slurry was placed on a shaker at room temperature (RT) at 200 rpm. After 24 h a sample of particle-protein slurry (50 μ|_) was removed and centrifuged at 16.2 g for 1 minute. The amount of unbound OptiE2 protein was assessed by electrophoresis of the supernatants and the particles on SDS-PAGE gels.

Immunization Studies Conducted In Mice

[00213] C57BL/6J mice were purchased from and housed in the Biological Resource Facility, The University of Queensland, Brisbane, Australia under specific pathogen-free conditions. Eight week old female mice were housed in HEPA-filtered cages with eight animals per group in an environmentall controlled area with a cycle of 12 h of light and 12 h of darkness. Food and water were given ad libitum. Animals were closely monitored throughout the study. All the animals remained in good health for the duration of the study with no visible deleterious health effects.

[00214] Pre-immunisation blood samples were collected by retro-orbital bleeds using heparin coated hematocrit tubes (Hirschmann Laborgerate, Heilbronn, Germany). Pre-immunisation blood samples collected prior to the first immunisation were referred to as the pre-immune (PI) samples. Adsorption reactions were prepared aseptieally as described above and the adsorbed OptiE2/SV pellet was washed in 1 mL of saline before preparing the final injectable doses. Qui! A (Superfos Biosector, Vedbaek, Denmark) was resuspended at 2 mg/mL in sterile injectable water (Pfizer, Brooklyn, USA). The injectable doses were administered to investigate the difference between the immune responses produced by the OptiE2 plus Quil A, OptiE2/SV-140 and the unimmunised group. The positive control group of mice received 100 pg OptiE2 protein and 10 pg Quil A. The treatment group received injections of OptiE2 (100 pg) loaded SV-140 (500 pg) (Table 3 below). Dose volumes of 100 pL (in 0.9% saline, Pfizer) were administered b subcutaneous injection at the tail base using a sterile 27 gauge needle (Terumo. Tokyo, Japan). Two injections were administered at 3 week intervals to all the treatment groups except for the unimmunised group. Four mice from each group were sacrificed 21 days after the final immunisation. Blood samples from the remaining four mice were collected every 4 weeks for up to 25 weeks and at the end of the trial period animals were sacrificed. The animals were weighed and monitored for their health once a week. In addition, they were also observed for clinical signs and any signs of illness were converted to a numerical score as follows: 0 = normal, 1 -4 = Moderate changes, animals need to be monitored daily, 5-10 - Significant changes: monitor twice daily with the consultant the chief veterinary officer at the animal facility and 10 - Euthanize.

Table 3: immunisation groups in the further mice trial. All doses were administered at the tail base.

Enzyme-Linked Immunosorbent Assay f ELISA) protocol

[00215] Detection of OptiE2-specific antibody responses: ELJSA for the detection of OptiE2-specific antibodies were performed by coating microtitre plates (96 well, Nunc, Maxisorb, Roskilde, Denmark) with OptiE2 antigen solution (2 ng/μΐ., 50 μ!_) in PBS overnight at 4°C. The coating solution was removed and the plates were washed once with PBS-T (1 PBS, 0.1 % Tween-20, Sigma-Aldrich) and blocked with Bovine Serum Albumin (5%, Sigma-Aldrich) and skim milk (5%, Fonterra, Auckland, New Zealand) in 200 pL PBS for 1 h with gentle shaking at RT. Plates were washed three times with PBS-T.

[00216] Mouse sera samples were diluted from 1 :100 to 1 :6400 in 50 pL PBS and each dilution was added to the wells of the blocked plates followed by incubation for 2 h at RT. To detect mouse antibodies HRP conjugated polyclonal sheep anti-mouse IgG antibodies (Chemicon Australia, Melbourne, VIC, Australia) diluted in PBS to 1 :50000 were added to each well and incubated for 1 h at RT with gentle shaking. Plates were washed three times in PBS-T, TMB substrate (100 xL, Life Technologies) was added to each well and incubated for 10 min at RT; 100 μΐ. of 1 HCi was added to the wells to stop the chromogenic reaction. The plates were read at 450 nm on the BloTek microplate reader (Winooski, US).

Isolation of murine splenocytes and enzyme-iinked immunosorbent spot (ELISPOT) Assay

[00217] Spleens were aseptically removed following euthanasia from the four animals sacrificed at 3 weeks and the other four at 25 weeks after the final immunisation, the collected spleens were placed into 5 ml ice cold DMEM media (Life Technologies) supplemented with 10% foetal bovine serum (FBS, Life Technologies), 20 m Hepes (pH 7.3), 1 sodium pyruvate, 1 M Giutamax, 100 units/mL penicillin G, 00 g/mL streptomycin, 0.25 pg/mL Fungizone. Spleens were gently disrupted and passed through a 100 μί ^η nylon mesh (Becton Dickinson) using a syringe plunger. Ceils were washed with 5 mL DMEM and centrifuged at 800 g for 5 min at 4°C and then resuspended in 1 mL lysis buffer (0.15 M NH ₄ CI, 10 mM KHC0 ₃ , 0.1 mM Na ₂ -EDT ) for 5 min at RT. Repeat wash steps twice with DMEM (9 mL and 5 mL) each time. Cell pellets were resuspended in 2 mL DMEM and cell numbers determined by staining with 0.2 % trypan blue. Cells from each mouse spleen were seeded at 1.0 - 1.5 x 10 ^b cells/well in triplicate into Polyvinylidene fluoride (PVDF) ELISPOT plates precoated with monoclonal interferon- γ (IFN-γ) (Mabtech, Sweden) capture antibody. Ceils were incubated in complete DMEM medium at 37°C and 5% C0 ₂ for 40 h In the presence or absence of 1 ^gfml OptiE2 antigen or the polyclonai activator concavaiin A (Con A, 1 pg/mL, Sigma Aldrich) as a positive control. IF ^' N-y ELISPOT assays were performed according to the manufacturer's specifications. The ELISPOT plates were read on an ELISPOT reader (Autoimmun Diagnostika, Strassburg, Germany).

Immunohistochemistrv [00218] Spleen sections were collected from the sacrificed mice at the time points 3 weeks and 25 weeks. A part of the spleen was dissected and frozen in OCT and 5 prn sections were cut using Hyrax C60 cryostat. The slides with cryosections were fixed in cold ethanol on ice for 8 min and then dried at RT for 20 min. The slides were then washed 3 x 5 min in PBS, left to dry at RT for 20 min and using a Dako pen circles were marked around the sections. The sections were then incubated overnight with the blocking buffer (1 % BSA + 5% FBS + PBS) at 4°G. Next day, to remove the block the slides were washed 3 x 5 min in PBS. The sections were then incubated with Aiexa Fluor 488 Goat Anti-Mouse IgG at 1 :500 for 1 h at RT in dark, the slides were then washed 3 x 5 min in PBS. To stain the nucleus the sections were then incubated with DAP I for 5 min and quickly washed in PBS. The sections were mounted with ProLong® Gold Antifade mounting medium and examined under microscope.

Histopatho!oav

[00219] Heart, kidney, liver and injection sites from the sacrificed mice were collected and fixed in 10% formalin for 48 h. The organs were further processed and embedded in paraffin and 8 m sections were cut using the Leica RM 2245 Rotary Microtome. The sections were then stained using the following haematoxylin and eosin staining procedure. Sections were first Dewaxed in xylene (3 changes of 2 min each), and then rehydrated ir absolute alcohol (2 changes of 2 min each), in 90% for 2 min, in 70% for 2 min. Then washed in running tap water for 2 min and stained in haematoxylin for 3 min and again washed in running tap water for 2 min. Sections were then washed in 70% alcohol for 2 min and stained in eosin for 3 min. Sections were then washed in 95% alcohol for 2 min, then in absolute alcohol (3 changes of 2 min each). Finally, the sections were rapidly dehydrated and fixed in xylene (3 changes of 2 min each) and mounted in DePeX. The sections were then observed under microscope.

RESULTS

Adsorption [00220] Adsorption tests were conducted by incubating 500 pg of OptiE2 protein with 2 mg of SV-140 for 24 h. The molecular weight of the expressed OptiE2 {referred to hereinafter as OptiE2 or oE2 which terms are used interchangeably) is 42 kDa. The protein and particle slurry was collected and separated into supernatant and particle samples and analysed by SDS-PAGE to determine the adsorption of protein. The gel analysis indicates that after 24 h of binding no protein was detected in the supernatant (FIG 22-lane 3) and complete binding of OptiE2 to SV-140 was observed in the particle pellet (FIG 22-lane 4).

EL ISA data

[00221] The mice were immunised with oE2 plus Qui! A and OE2/SV-140 vaccine formulations (as set out in table 3) with two subcutaneous vaccine injections and sera samples were collected at three-week intervals after each injection over a 25-week period. The animals in all the treatment groups remained healthy and in the normal weight range throughout the trial period. The total IgG responses of the immunised mice were analysed b anti-oE2-specific EL ISA assays. The ELISA result from the terminal bleeds at two time points 3 weeks and 25 weeks (show in FIGs 23 and 24), showed that both the nanovaccine treatment group injected with oE2/SV-140 and the positive control group oE2 plus Qui! A showed a similar trend in reduction as expected with the antibody response. The negative control group receiving no vaccination showed no antibody response specific to oE2 epitope.

Generation of Cell-mediated immune responses

[00222] ELISPOT assays were used to determine the T-helper type 1 (Th 1 ) cell mediated interferon- γ (IFN-γ) responses to oE2 antigen. Three weeks and twenty-five weeks post the final immunisation spleens from the sacrificed mice from each group were collected and harvested to obtain splenocyte cell populations. The mice receiving nanovaccine formulations oE2/SV-14G showed excellent cell-mediated immune responses to oE2 antigen even after twenty-five weeks post the final immunisation as indicated by the number of cells producing Spot Forming Units (SFU). At 3 weeks, spleen samples were collected from the four sacrificed mice (from the three treatment groups). The 6-week data shows that the cell-mediated response induced by oE2/SV-14Q (599-1500 SFU/million cells) was comparable to the oE2 plus Quit A (551-1500 SFU/million cells) as the two mice in each treatment group showed low response and the other two displayed high response (FIG 25),

[00223] The four mice sacrificed at twenty-five weeks showed that the OE2/SV-140 induced a stronger cell mediated responses (1500 SFU/million cells) in comparison to the positive control group (473-1500 SFU/million cells) (FIG 26). The ability of SV-140 vesicles to induce both antibody and cell mediated responses after 3 weeks as well as 25 weeks, highlights their potential as excellent self-adjuvants and vaccine delivery vehicles.

ImmunohistQchemistry data

[00224] ImmunohistQchemistry studies were conducted on the mice spleen sections. The sections were stained with Alexa Fluor 488 Goat Anti-Mouse IgG and the nucleus with DAPI. The green color in the spleen section represents the presence of antibody response. The oE2/SV-140 (FIG 27 c and d) not only produced antibody responses 3 weeks after the final immunisation but also after 25 weeks post the final immunisation. The IgG response appeared stronger at both the time points (3 weeks and 25 weeks) with oE2/SV~14Q compared to the positive control oE2 plus Qu i I A. The absence of the green color in the sections of the unimmunised treatment group confirms that the mice in the negative control group did not generate antibody responses.

Histopathology data

[00225] Heart, kidney, fiver and injection sites from the sacrificed mice were collected and fixed in 10% formalin; they were further processed and stained with hematoxylin and eosin stain. The histopathology results demonstrate that administration of oE2/SV-140 nanovaceine did not have a detrimental effect on the heart, kidney, liver and injection sites at both the time points 3 weeks and 25 weeks post the final immunisation as the sections of mice injected with the OE2/SV-14Q looked similar to the negative treatment group (unimmunised) (FIG. 28 i, ii, iii (compare c and d to e and f}). The sections of the animals treated with oE2 plus Quil A also looked similar to the unimmunised group. This shows that administration of 500 μg of 50 nm SV-140 was very well tolerated in the animals and it did not have any adverse effects on the major organs of the animals.

Conclusion on Nanovaccibe Experiments Using BVDV E2

[00226] The oE2 adsorbed on the rationally designed SV-140 induced both anti-oE2 IgG as well as IFN-y responses even after 25 weeks post the final immunisation, demonstrating the potential of SV as both efficient vaccine delivery vehicles and potent adjuvants. The animals were administered with two vaccine doses at three week intervals, th oE2 (100 pg) plus Qui! A (10 μg) and the oE2 (100 pg) /S V-140 (500 μg) showed a similar trend of reduction for antibody responses. The oE2/SV~140 produced robust long-term cell-mediated responses in comparison to the positive control oE2 plus Quit A. The immunohistochemistry results confirmed that the animals treated with OE2/SV-140 produced strong total IgG responses and the histopathology study revealed that injecting a higher dose of nanovaceine (500 pg) did not have a debilitating effect on the major organs of the animals. These results indicate the usefulness of SVs towards the development of a new platform technoiogy for safer and more effective subunit vaccines with an ability to induce long-term humoral as well as cell mediated responses.

NANO VACCINE EXPERIMENTS ON ANAPLASMA

[00227] Following on from the experiments relating to adsorbing BVDV-E2 onto silica vesicles (SV), specifically with SV-140, with a high adsorption rate of 200 pg/mg particle, it was decided to use the same approach with 2 different proteins, VirB9.l (56KDa) and VirB9.2 (44kDa), from Anaplasma margm ^' &le, the causal organism of cattle tick fever. The proteins were expressed in an Escherichia coli system. VirB9.1 was expressed using a GST tag in Rosetta (DE3) pLysS cells, induced by 0.2 mM IPTG for 17 hours at 15°C The resultant soluble protein was purified from bacterial cell lysate by chromatography using a GST affinity column and Superdex 200 10/300 GL size exclusion column, respectively. After purification, VirB9.1 fractions were collected, concentrated and dialysed into PBS for further work. VirB9.2 was expressed using pET-SUMO in BL21 (DE3) cells, induced by 1 mM IPTG for 5 hours at 37°C. The resultant protein was purified from the insoluble inclusion body fraction. After solubilisation, VirB9.2 was dialysed into PBS for further work.

[00228] Adsorption of VirB9.1 and VirB9.2 was conducted in 1 xPBS buffer at 4 °C and room temperature, respectively. The adsorptions rates onto SV100 particles were 200 μα,/mg for VirB9.1 and 400 g mg for VirB9.2. The adsorption ratios of VirBg.1 onto SV100-NH ₂ , SV140 andSV140~MH ₂ were also approximately 200 pg/mg. VirB9.2 shows similar adsorption onto SV100-NH ₂ , SV140 & SV140-NH ₂ (FIG 29).This data confirms th ability of SV particles to act as carriers of antigenically important proteins other than BVD V E2. Desorption of VirB9.2 from SV100 and SV140 was found to be better as compared to the amino-functiona!ised particles (FIG 30). Based on these observations, SV100 loaded with VirS proteins were used in mice trial experiments. Both VirB9.1 and VirB9.2 were adsorbed onto SV100 particles for use in a mice trial to check their ability to induce immune responses. The proteins were adsorbed separately onto the particles and nano-formulations were prepared containing each individual protein and both proteins in combination (Table 4).

Group Prototype Vaccine

1 VirB9.1 (50 pg) + Quil-A {10 pg) 2 VirB9.2 (50 pg) + Quil-A (10 pg)

3 VirB9.1 {50 pg) + VirB9.2 (50 pg) + Quii-A (1 Gpg)

4 VirB9.1 (50 pg) + SV100 (250 pg)

5 VirS9.2 (50 pg) + SV100 (125 pg)

6 VirB9.1 (50 pg + SV10Q {250 pg)

VirB9.2 (50 pg) + SV1Q0 (125 pg)

7 Control SV100 alone (375 pg)

8 Control Unimmunised

Table 4: Mouse trial experimental groups.

Time-!ine for Nanovaccine Anaplasma Mice Trial 2014

DAY 55

DAY O Terminal

Pre-immune DAY 21 Bleeds

Test bleeds DAY 42

bleeds DAY 35 Third injection - ELISA

Primary Second

Spleens for injection injection Test bleeds: _{tf re} q _U j _reC f based

ELISA _0i1 EUSA results ELISPOT

0 3 4 5

Time (weeks)

[00229] VirB9.1 and VirB9.2 have been shown to be linked proteins and immunisation of linked proteins can increase T-cell-dependant IgG responses (linked recognition), as well as presenting more than one immunogenic protein (Morse et a!. 2012). The preliminary data for this experiment shows VirB9.1 and VirB9.2 adsorbed onto SV100 particles successfully induced humoral immunity (FIGs 31 and 32),

[00230] The ELISA results from the Terminal sera (3 weeks after the last injection) for VirB9.1 also show a good antibody response (FIG 33), The ELISA results for Terminal sera for VirB9.2 follow similar trends as for VirB9.1. Excellent ceil mediated immune responses (FIGs 34 and 35) obtained after three injections also showed that VirB9.1 and ViRB9. injected with SV 100 gave consistent responses comparable to Guil- as the traditional adjuvant.

[00231] In the trial, 2 groups of mice were also injected with a combination of both VirB9.1 and VirB9.2 (Table 4). Group 3 (Table 4) uses the traditional adjuvant Quil-A, while Group 6 comprised injecting formulation containing separately adsorbed VirB9.1/9.2 combined after adsorption as a mixed nano-formulation. Animals immunised with the combined VirB9,1 and VirB9.2 nano-formulations showed good humoral (FIGs 31 to 33) and cei! mediated (FIGs 34 and 35) immune responses comparable to the immune response of mice injected with the individual VirB/SV formulations. More importantly animals vaccinated individually with Vi.rB9.1/SV showed little reactivity with VirB9.2 protein and vice versa in both ELISA (humoral responses, FIGs 31 to 33) and ELISPOT assay (cell mediated responses, FIGs 34b and 35b).

[00232] In addition to confirming the ability of SVs to act as an adjuvant and protein carrier in vivo, the immune responses from the combined immunisation showed that the individual proteins are processed independently by the immune system, indicating that SVs can be used to produce multivalent vaccines, which may be able to target multiple diseases in a single dose.

ADSORPTION CAPACITY OF MODEL THERAPEUTICAL PROTEINS BY SILICA VESICLES AND PROTEIN STABILITY TESTS

Correlation of Protein Loading Amount and Entrance Size of Silica Vesicles

[00233] The inventors have found the entrance size of the present silica vesicles (SVs) can be adjusted from < 3.9 to 34 nm (diamond in FIG 36) while the wall thickness is maintained at - 6 nm (circle in FIG 36). After hydrophobic modification with -Cis chains, the entrance size of SVs decreases 1 -2 nm in all cases (square in FIG 36). The relationship between loading amount of therapeutical proteins and entrance size of SVs has bee investigated using both these series of SV. Cytochrome c (the upside down triangle in FIG 36) and Ribonuclease A (RNase A indicated by the triangle) have been used as model therapeutical proteins and results have been discussed previously. [00234] As shown in FIG 36, both series of SV show a similar trend of adsorption capacity towards two model proteins as entrance size increases: when the entrance size of SV is equal to the wall thickness, the loading capacity reaches a maximum {563 mg/g for RNase A on hydrophobic modified SV and 840 mg/g for Cyto C on unmodified SV).

[00235] To further predict the positions of RNase A adsorbed on functionalized SV samples, the RNase A adsorption capacity per unit surface area (mg/m ² ) was calculated (Table 5), dividing the adsorption capacity by BET surface area excluding the unusable micropore area for protein adsorption. Solid Stober spheres with the same hydrophobic modification and -50 nm particles size have also been used for RNase A adsorption in comparison with SV, which showed 89 mg/g loading amount of RNase A after 18 h. For modified Stober spheres, it is clear that the adsorption of RNase A occurs on the external surface with a single layer adsorption behavior. Compared to 50 nm solid Stober spheres, SV-1 Q-5Q-Ci ₈ has a same size but weaker adsorption capacity of 0.64 mg/m ² , half of that of Stober spheres (1 ,13 mg/m ² }. Like in the case of solid Stober spheres, RNase A can only be adsorbed on the outer surface of SV-1Q-5G-Cig because its entrance size is smaller than the protein size. However, its BET surface area excluding the micropore area consists of both the internal and external surface area of hollow SV-10-50-G-I8 measured by nitrogen sorption, which is double of that of solid Stober spheres, causing a lower adsorption capacity. SV-10-100-Ci _a shows a capacity of 1.51 mg/m ² , which is slightly higher than that in solid Stober spheres. The entrance size of SV-10-10Q-Ci ₈ is < 3.9 nm after hydrophobic modification. Although the exact entrance size cannot be determined from the nitrogen adsorption technique, it can be deduced that the entrance size is close to 3.9 nm considering that SV-10-100 has an entrance size of 6 nm and the entrance size decrease after modification is in the range of 1 -2 nm. This entrance size is close to the protein size, thus RNase A can be loaded into the cavity, leading to a relatively high adsorption capacity. SV-10-120-Cig and SV-10-140-Cis with entrance sizes much larger than the size of RNase A show an adsorption capacity per unit area twice of that in Stober spheres, indicating that RNase A is adsorbed not only on the surface of silica shell, but also inside the cavity through multi-layer adsorption.

capacity; C'RNase A: RNase A adsorption capacity per m (CRNase A /SBer-Micro) .

Thermal stability of RNase ..A loaded in hydrophobic modified

[00236] The thermal unfolding of RNase A was measured by differential scanning calorimetry (DSC) in the range of 10-130 °C. The DSC was carried out using a VP DSC microcaiorimeter ( icroCal Company, USA) with a heating rate of 60 °C/h. In a typical procedure, the RNase A/SV was suspended in 10 mM PBS solution with the RNase A concentration of 0.5 mg/ml. reference suspension was also prepared using only SV the same concentration. The reference and sample suspension were injected in the corresponding cells for DSC measurements. The DSC curve of free RNase A was also obtained. FIG 37 shows a series of DSC curves with the temperature of RNase A/SV suspension as the x axis and the apparent molar heat capacity (Cp) as the y axis which is baseline-substrated and normalized by the concentration of RNase A. The DSC curve of free RNase A shows an endothermic peak which indicates thermal unfolding of RNase A. The midpoint temperature for the RNase A thermal unfolding (T _m ) was also measured to be centred at 83.6 °C, in accordance with literature reports. The T _m of RNase A loaded in SV-10-120-C ₈ increases to - 119 °C, much higher than that of RNase A/SV-10-50-C ₁₈ (71.9 °C) and RNase A/SV-1G-140-C ₁₈ (74.9, 118 ^e C). The DSC results show that RNase A loaded in the hydrophobic modified SV with the entrance s ze of - 6 nm shows the highest thermal stability in PBS compared to SV-10-50-Ci ₃ that adsorbs RNase A on the outer surface and RNase A/SV-l 0-140-Ci ₈ that possesses large entrance size.

Activity of RNase A loaded in hydrophobic modified SV after acid and heat treatment

[00237] The stability and activity of RNase A loaded in hydrophobic modified SV was further investigated with acid and heat treatment. In a treatment procedure, 50 μ! 0.01 M HCI (pH 2) was added to ~ Img RNase A loaded in SV. The mixture was kept in 65 °C for 40 min, then neutralized with 0.01 NaOH solution (pH 12} until the pH reached 7. The final RNase A concentration was then diluted to 0.5 mg/ml. Free RNase A was also treated accordingly as a control group. In order tor investigate the secondary structure change of RNase A after the treatments, circular dichroism (CD) spectra of RNase A SV suspension was measure with SV suspensions as the reference. FIG 38 shows that the intensity in CD spectra in the wavelength range of 200-230 nm is RNase A/SV-10-120-C ₁₈ > RNase A/SV-10-140-Ci ₈ > RNase A/SV-10~50-C _1S > RNase A/SV-10-1 0. The higher intensity indicates more secondary structure is maintained after the treatment, Thus, RNase A loaded in SV-10-120-Ci8 show the highest content of secondary structure after the acid and heat treatment.

[00238] The RNase A/SV-10-120-Ci _a after acid and heat treatment was then used for cellular delivery to further test the activity of RNase A. The procedure described previously was employed. As displayed in FIG 39, SV-10-120-C18 shows minimised cellular toxicity to both SCC25 and HCT116 cells even after 72 h, indicating the excellent biocompatibility of the functionalized SV samples. When SCC25 and HCT1 16 cel!s are treated with free RNase A, no inhibition can be seen, because the naked protein cannot enter into cells. RNase A delivered by SV-10-120-Ci _B exhibits time-dependent cell toxicity, where the cell inhibition ability increases with the exposure time increasing from at the RNase A concentration of 16 pg/ml (FIG 39A). The same trend can be observed in HCT116 cells with the ceil inhibition of 33% at 24 h to 48% at 48 h and finally 69% at 72 h. The cell inhibition ability of RNase A/SV-I O-I 2O-C 8 confirms the stability and retained activity of RNase A after acid and heat treatment.

100239] Most therapeutical proteins possess fragile structures that easily undergo denaturation or digestion by proteases. For example, proteins need to survive pepsin or trypsin digestion during oral delivery and plasm in in intravenous injections. In the present experiments, the RNase A/SV-l O-120-Ci8 was digested with trypsin and the amount of intact RNase remaining was quantitatively detected by mass spectromatry (MS). Firstly 1 mg of RNase A loaded in SV was treated with dithiothreitol at 60 °C for 30 mins. This process is to break the disulfide bonds in free RNase A. Secondly, the RNase A/SV was added to 1 mg/mi trypsin in PBS solutions (1 :50) at 37 °C with shaking for -12 h. The mixture was then centrifugated, and the supernatant was removed from the precipitate. The precipitate was spotted onto a ALDI. MPT 384 plate and mixed with 1 μί GHGA solution before the test- The samples were analyzed on a Brisker Autoflex TOF TOF III Smart beam. The mass spectra were obtained in the LP-Pep!V!i mode via an accumulation of 200 laser shots at 10 different sites under a laser intensity of 39% for data collectio and calibrated. Three standard peptides, Angiotensin y ( _w « 1046.5 Da), ACTH-CIrp (Mw « 2485,2 Da) and Somatostatin 28 (Mw 3147.5 Da) were used for calibration purposes to reduce variability, FIG 40A shows the MS 0! RNase A/SV- 0- 20 which shows a series of peaks ranging from 1000-5000 in the ass- o-charge ratios. These peaks can all be attributed to the peptides digested from intact RNase A by trypsin, in comparison, the MS of RNase A/SV-10-12Q-C _Tg shows a small peak at the mass- to -charge ratio of 13.7k which- is the mass of intact RNase A. As a result, an amount of RNase A remains after the trypsin digestion process when adsorbed by hydrophobic modified SV, white without the modification RNase A loaded. Is completely digested.

[00240 The results presented herein show that SVs with the entrance size close to the protein size show the highest loading amount of the model therapeutical proteins. Using RNase A as an example, it is predicted that the location of RNase A loaded in SV-10-120-Cie is not only on the outer surface but also in the SV cavity. Furthermore, these experiments suggest that SV-10-120-018 with an entrance size of ~ 6 nm and hydrophobic modifications shows protection toward RNase A from harsh conditions of heat or potential acid or tryspin digestion. The RNase A loaded in SV-10-1 2G-Gi ₈ still shows successful inhibition to cancer cells even after treatment with heating and strong acid. This finding is surprising and provides an important understanding not previously found in the art whic will be crucial for designing effective protective nano-carriers for therapeutical protein delivery.

[00241 ] In the claims which follow and in the preceding description of the invention, except where the context clearly requires otherwise due to express language or necessary implication, the word "comprise", or variations thereof including "comprises" or "comprising", is used in an inclusive sense, that is, to specify the presence of the stated integers but without precluding the presence or addition of further integers in one or more embodiments of the invention.