[001] The invention relates to the field of detection of structural monitoring. More specifically, the invention relates to monitoring Sulfate Reducing Bacteria (SRB) that cause degradation and corrosion damage of infrastructural metal structures used in the oil industry. BACKGROUND OF THE INVENTION

[002] In the petroleum industry, colonies of microbes can grow on infrastructural equipment. In particular, the growth of sulfate-reducing bacteria (SRB) is problematic to the petroleum industry due to the ability of SRBs to reduce sulfates to sulfides. Sulfides are found to contribute to corrosion, plugging of injection wells, souring of gas and/or oil and to the increase of toxic hydrogen sulfide. These problems raise production costs significantly due to equipment failure, the additional equipment needed to remove sulfides, the remedial use of biocides to control microbial growth, and the additional chemicals employed to remove or prevent iron sulfide deposits.

[003] Traditionally, the petroleum industry has used the Most Probable Number (MPN) method to detect the growth of SRB from field samples. The MPN method is slow and can take up to 28 days to report the final reading. Another drawback of this method is that it cannot detect low densities of viable SRB cells. Therefore, SRBs can be present in samples without being detected because their concentration is under the detection limit of the MPN method.

[004] Direct microscopy is an alternative method that is rapid, but it does not distinguish live from dead bacteria. Other SRB test kits are also available; however, these kits have their own associated disadvantages in terms of inordinate test length times and lack of sensitivity. There is therefore a need for an SRB detection method which easily adapts to the rigors of the oil field and has enhanced sensitivity would improve detection of Sulfate Reducing Bacteria and their growth.

[005] It is with respect to these and other considerations that the disclosure made herein is presented. SUMMARY OF THE INVENTION

[006] According to the present invention a method of determining a concentration of sulfate reducing bacteria (SRB) comprising is provided. The method comprises preparing a standard growth medium in a group of test vials, adding ferrous chloride tetrahydrate (FCTH) to the each of the test vials, adding a sample portion to a first of the group of test vials, sequentially diluting the sample portion by injecting succeeding vials in the test group with fluid from sequentially previous vials and incubating the group of test vials, wherein blackening of fluid in an incubated test vial indicates a presence of a threshold number of SRB.

[007] In some embodiments, the method of determining a concentration of SRB according to the present invention includes adding an iron source to the standard growth media in the group of test vials prior to adding the FCTH. In some embodiments, the FCTH is added at a dosage of 0.01 grams per 9 milliliters of standard growth media. In some implementation, the FCTH is added as 0.5 to 1 milliliter of solution to 8 milliliters of standard growth media and 1 ml of tested sample.

[008] In other embodiments, the method of determining a concentration of SRB according to the present invention includes adjusting the pH of the standard growth media to compensate for addition of FCTH which is approximately 7.6. In further embodiments, the step of sequential diluting is performed by drawing one milliliter from a vial already containing mixed tested sample and injecting the drawn milliliter it to a next sequential vial. In some implementations, that group of test vials is incubated for 5 to 7 days. In some implementations, the test vials can be incubated at 37 degrees Celsius.

[009] The present invention also provides a test kit for determining a concentration of sulfate reducing bacteria (SRB) in a test sample. Embodiments of the test kit comprise a group of test vials containing a standard growth media and an iron additive comprising ferrous chloride tetrahydrate (FCTH) for adding to the test vials. During a determination, a test sample is added to a first of the group of test vials, and the test sample is sequentially diluted in remaining vials of the group. Upon incubation of the test vials with diluted sample and iron additive, a blackening of fluid in any of the test vials in the group indicates SRB concentration above a threshold level.

[0010] In some embodiments, the vials are filled with 8 milliliters of standard growth media and 0.5 to 1 milliliter of FCTH. In some implementations, the first of test vials is injected with 1 milliliter of a test sample. Additionally, the pH of the standard growth media can be adjusted to compensate for the FCTH iron additive to approximately 7.6. [0011] These and other aspects, features, and advantages can be appreciated from the following description of certain embodiments of the invention and the accompanying drawing figures and claims. BRIEF DESCRIPTION OF THE DRAWINGS

[0012] FIG. 1 is a flow chart of a method for preparing a test group and a control group for determining the presence and amount of sulfate-reducing bacteria in field samples using an FCTH additive according to an embodiment of the present invention;

[0013] FIG. 2 is a flow chart of a method for applying the FCTH iron additive to the test group to prepare a test for SRB concentration according to an embodiment of the present invention;

[0014] FIG. 3 is a schematic illustration of the process of sequential dilution of a test sample with addition of FCTH according to an embodiment of the present invention; and

[0015] FIG. 4 is a schematic illustration of the results of three exemplary tests for SRB using the methods of the present invention.

[0016] FIG. 5 is a table used for calibrating dilution test results to an estimate of SRB concentration according to the prior art.

DETAILED DESCRIPTION OF CERTAIN EMBODIMENTS OF THE INVENTION

[0017] To more quickly and accurately test for the number of SRB present in a sample, a test protocol is disclosed in which an iron compound, ferrous chloride tetrahydrate

(FeS04-7H20) ("FCTH"), is used as an additive to a standard bacterial growth media. As described herein, this additive acts as a supplemental media to the standard media and not only increases SRB detection sensitivity but also provides for rapid detection of SRB growth. In particular, as described herein, the present method of detection of SRB relies upon a visual cue to alert the tester that SRB is present and more particularly, the presence of SRB will be clearly revealed by the growth medium having turned black due to a suspension of iron sulfides.

[0018] The protocol starts by employing a standard media, such as API RP 386, for supporting the growth of SRB and then adds the FCTH in a serially dilutive manner. Upon incubation, the FCTH boosts the production of iron sulfides by the SRB, which darken the media and provide a marker for the presence of SRB. Using vials having different degrees of dilution, the number of SRB present can be estimated according to the degree of dilution at which iron sulfide darkening is visually detected in the sample (i.e., the growth medium turns black). The addition of FCTH improves the lower limit of detection to approximately 10 ⁴ to 10 ^s cells per milliliter.

[0019] FIG. 1 is a flow chart of an embodiment of a method for preparing a test group and a control group for determining the presence and amount of sulfate-reducing bacteria in field samples according to the present invention. In step 101, the method begins. In step 102, samples are collected from field equipment (e.g., oil pipelines, well holes, storage vessels) to determine whether the samples contain SRB, and if so, the amount of SRB that they contain. In a second step 104, an iron additive is prepared. In some implementations, this step involves dissolving 1 gram of FCTH in 100 ml of distilled water, purging the solution with argon gas, and then sealing and autoclaving the solution for approximately 15 minutes (which yields an iron additive solution of concentration 10 mg/ml).

[0020] In step 106, a standard SRB growth media ("standard media") is prepared. In some implementations, the standard media is prepared using water and the components shown below in Table 1.

TABLE 1

COMPONENT Weight (g/l.OL)

Ammonium Chloride (NH4CI) 1

Calcium Sulfate (CaS04.2H ₂ 0) 1

Magnesium Sulfate (MgS04.7H ₂ 0) 2

Sodium Lactate (C3Hs03Na) 3.5 mL

Yeast Extract 1

Ascorbic Acid 0.1

Resazurin solution (25 mg/100 H2O) 4.0mL

Sodium Thiogly collate (CH ₂ SHCOONa) 0.1

Ferrous Sulfate (FeS04.7H ₂ 0) 0.5

Potassium Hydrogen Phosphate (K2HPO4) 0.5

[0021] During preparation of the standard media, the salinity of the water used to create the media can be adjusted to match the salinity of the samples (e.g., water (synthetic or filtered original water) with similar salinity can be used). In addition, the pH of the standard media can be adjusted for the presence of iron. For example, the pH of the prepared media without an iron supplement can be compared to the pH of the standard media including a supplement of 1 ml of iron. If the pH of the two media is significantly different, the pH of the standard media that includes the iron supplement can be adjusted to match the pH of the standard media without the iron supplement. In general, the components listed in Table 1 can be prepared separately to avoid precipitation and to maintain anaerobic conditions.

[0022] After the standard media has been prepared and the salinity adjusted, in step 108, a test control group is created by distributing a quantity of the standard media into a group of vials, into each of which an iron source, such as an iron nail, is also added. The vials are then sealed. In a particular implementation, 9 ml of the standard media is distributed to eight or more vials. In step 110, a test group is prepared similarly by distributing a smaller amount of standard media into a second group of vials ("test group"), into each of which an iron source, such as a nail, as well as FCTH is also added. The test group vials are then sealed as well. In a particular implementation, 8 ml of standard media is distrusted to the vials of the test group. Afterwards 0.5 ml of stack solution including FCTH (1 g/ml of solution) is then added to test group.

[0023] FIG. 2 is a flow chart of a method for applying the FCTH iron additive to the test group to prepare a test for SRB concentration. In step 201, the method begins. In step 202, the test vials are sterilized for one hour in an autoclave or similar sterilization device. After sterilization, in step 204 the first vial of the test group is injected with 1.0 ml of the sample to be tested and the solution is then mixed thoroughly. In step 206, one ml of the mixture is extracted from the first vial which is then added to the next vial of the test group. In this manner the successive vial receives a diluted portion (i.e., one tenth concentration) of the sample. The process of sequential addition and extraction is repeated until it is determined in step 208 that all eight or more of the vials in the test group have been inoculated with a portion of sample. This process is schematically illustrated in FIG. 3. As shown, a test group includes six vials 302, 304, 306, 308, 310 and 312. Although six vials are shown, this is merely for ease of illustration, and a smaller, or preferably larger, number of vials can be used. A syringe 315 is shown which is able to both inject fluid into and draw fluid out of the vials 302-312. The first vial 302 includes 9 ml of fluid and is injected with one ml of sample, yielding a 1 : 10 sample/fluid ratio, or one tenth of the original sample concentration. When 1 ml of the fluid is drawn from vial 302 and injected into vial 304, vial 304 then effectively contains one-tenth of one-tenth of the original sample concentration, or a 1 :100 sample/fluid ratio. During the process of sequentially drawing 1 ml of fluid from a vial and injecting the drawn fluid into the next sequential vial, the sample/fluid ratio decreases geometrically: vial 306 has a 1 : 1000 ratio, vial 308 has a 1 :10,000, vial 310 has a 1: 100,000 ratio, and vial 312 has a 1 :1,000,000 ratio. [0024] After inoculation of the test group, in step 210, an amount of FCTH, such as 0.5 ml, is added (e.g., by injection) to all of the vials (that contain the diluted sample) and the resulting solution is thoroughly mixed. In step 212, the sequentially diluted test group vials are incubated for a period at 37 degrees Celsius. The preferred period of incubation is five (5) to seven (7) days, a reduction of at least 75 percent over the prevailing method which requires 28 days. After incubation, in step 214 the presence of SRB is revealed, and their magnitude is determined, when the medium in the test group vials turns black due to a suspension of iron sulfides.

[0025] FIG. 4 is a schematic illustration showing three exemplary sample tests, test 1, test 2 and test 3 of different original samples. As shown, in test 1 the fluid in four vials 402, 404, 406 and 408 is shown as having blackened, indicating a threshold concentration of SRB, (while the fluid in two vials 410, 412 is shown as not having blackened, indicating that the SRB concentration is lower than the threshold in vials 410, 412. Vials 402, 404, 406 and 408 represent the 10 ^"1 , 10 ^~2 , 10 ^~3 and 10 ^"4 sample/fluid ratios, respectively, while vials 410 and 412 represent the 10 ^"5 and 10 ^"6 sample/fluid ratios, respectively. This shows that beyond the 1 :10,000 dilution level of the original sample, there is insufficient SRB concentration to cause blackening of the fluid by production of iron sulfide. Similarly, in test 2, the fluid in four vials 422, 424, 426 and 428 is shown as having blackened, again indicating a threshold concentration of SRB, while the fluid in two vials 430, 432 is shown as not having blackened, indicating that the SRB concentration is lower than a threshold in vials 430, 432. Vials 422, 424, 426 and 428 represent the 10 ^"1 , 10 ^~2 , 10 ^~3 and 10 ^"4 sample/fluid ratios, respectively, while vials 430 and 432 represent the 10 ^"5 and 10 ^"6 sample/fluid ratios, respectively. Test 2 similarly shows that beyond the 1 :10,000 dilution level of the original, there is insufficient SRB concentration to cause blackening of the fluid by production of iron sulfide. Thus, in tests 1 and 2, the blackening of the fluid at the 10 ^"4 dilution level gives an indication of the magnitude of SRB in the original samples used in the tests, which can be converted into a measurement of the concentration of SRB present in the original samples used in test 1 and test 2.

[0026] The dilution level at which blackening occurs can be converted with a sufficient degree of accuracy to an estimate of the number of SRB per ml in a sample using the most probable number (MPN) calibration method. The MPN calibration method utilizes a table in which results of standard dilution tests are calibrated with an estimate of organism concentration. As an example, The following example illustrates how this method is used. A sample is taken and used in three serial dilution tests for SRB concentration. The vial results are shown in Table 2 directly below in which "+" indicates blackening and "-" indicates no blackening. From the test results, the fifth, sixth and seventh dilutions are selected to provide an estimate of the concentration of SRB in the sample. As indicated in Table 2, all three tests were positive at the 10 ^"5 level (10 ^"N in the MPN table of FIG. 5), 2 tests were positive at the 10 ^"6 level (10 ^"N+1 in the MPN table) and 1 test was positive at the 10 ^"7 level (10 ^"N+2 in the MPN table). Matching this 3-2-1 pattern in the MPN table to an MPN estimate gives a value of 1.5. Multiplication by the dilution factor yields a value of 1.5 x 10 ^s SRB in the original sample. Table 2: Example calibration with MPN table

[0027] In contrast, in test 3 the fluid in only three of the vials 442, 444, 446 have blackened, indicating a threshold concentration of SRB, while the fluid in two vials 448, 450 and 452 is shown as not having blackened, indicating that the SRB concentration is lower than the threshold in vials 448, 450 and 452. Vials 442, 444, and 446 represent the 10 ¹ , 10 ^"2 and 10 ^~3 sample/fluid ratios, respectively, while vials 448, 450 and 452 represent the 10 ^"4 , 10 ^"5 and 10 ^"6 sample/fluid ratios, respectively. Thus, test 3 differs from tests 1 and 2 in that beyond the 1 :1,000 dilution level of the original (as opposed to the 1 :10,000 level), there is insufficient SRB concentration to cause blackening of the fluid by production of iron sulfide.

[0028] A number of tests were conducted in which various types of water samples with different salinity and SRB cultures were used. SRB cultures were prepared and isolated from different locations, namely, the Abu Ali water supply, Abu Ali disposal water, hard water supply and Uthmaniyah water supply. Different volumes (i.e., 0.1ml and 0.2 ml) of SRB culture were injected in 100 ml of distilled water. After that, 1 ml from the total volume was used as inoculum to conduct the MPN test. This inoculum was conducted with different water salinity. Tables 1-6 set forth different test examples and more specifically: Example 1 : SRB culture (35% of QSW) - a) 0.1 ml SRB/100 distilled water; and b) 0.2 ml SRB/100 distilled water; Example 2: SRB culture (100% of QSW) - a) 0.1 ml SRB/ 100 distilled water; and b) 0.2 ml SRB/100 distilled water; Example 3: Abu Ali water supply well (35% of QSW); Example 4: Abu Ali disposal water (100% of QSW); Example 5: hard water sample (100% of QSW); and Example 6: Uthmaniyah water samples (100% of QSW).

[0029] The experiments were conducted under the following conditions: for each test sample, two triplicate 16-dilution series of MPN were tested. One MPN set used the standard SRB media (9 ml of media in each vial), while the other MPN set was prepared by adding 1 ml of iron additive to the standard media resulting in 9 ml of media in each vial after addition of the iron additive. A water sample of 1 ml was inoculated for the 16 dilution series in triplicate. The samples were incubated for 28 days at 35°C. Growth was checked daily and the day in which the sample (culture) turned black was recorded in order to confirm whether the iron additive (IC) expedites SRB growth. After 28 days, the final MPN reading and data conversion was conducted and this indicates whether the iron additive improves SRB detection sensitivity.

[0030] Table 2, set forth below, shows SRB growth that results using the standard MPN method (described herein) with and without the addition of 0.1 ml and 0.5 ml of iron compound at the 0.1 ml SRB culture in 35% of Qurayyah seawater (QSW). The below data indicates that in the absence of the iron compound (IC) which is represented by the original sample column, low growth of 2.3 SRB/ml was detected after one day (i.e., day 1) of incubation. After two days, SRB growth increased to 230 SRB/ml but then remained at this level up to the end of the incubation period of 28 days. However, with the addition of 0.1 ml of iron compound (IC), the results show that 2.3 SRB/ml was detected after one day (day 1) of incubation. After two days, SRB growth increased to 2.3X10 ⁴ SRB/ml and remained at this level up to the end of the incubation period of 28 days. Similar results were detected with the addition of 0.5 ml of iron compound (IC). The results thus show that 2.3 SRB/ml was detected after one day of incubation. After two days, SRB growth was increased to 2.3X10 ⁵ SRB/ml and remained up to the end of the incubation period of 28 days. The test results thus indicate that the iron compound (IC) not only expedites SRB growth but also improves SRB detection sensitivity. Table 3: Results of 0.1 ml SRB culture (35 % of QSW) /100 Distilled Water

mm Original l( -O. l n.l I ( -0.5ml

Sample

1 2.3 2.3 2.3

2 230 2.3X10 ⁴ 2.3X10 ⁵

3 230 2.3X10 ⁴ 2.3X10 ⁵

[0031] Table 3 shows the SRB growth results with and without the addition of 0.1 ml and 0.5 ml of iron compound to the 0.2 ml SRB culture in 35% of Qurayyah seawater (QSW). The data indicates that in the absence of the iron compound low growth of 2.3 SRB/ml was detected after one day of incubation. After two days, SRB growth was increased to 230 SRB/ml and remained at this level up to the end of the incubation period of 28 days.

However, with the addition of 0.1 ml of iron compound, the result show that 2.3 SRB/ml was detected after one day of incubation. After two days, SRB growth was increased to 2.3X10 ³ SRB/ml and remained up to the end of the incubation period of 28 days. Comparable results were detected with the addition of 0.5 ml of iron compound. The results show that 230 SRB/ml was detected after one day incubation. Later, SRB growth was increased to 2.3X10 ⁴ SRB/ml and remained up to the end of the incubation period of 28 days. The test results thus indicate that the iron compound (IC) not only expedites SRB growth but also improves SRB detection sensitivity.

Table 4: Results of 0.2 ml SRB culture (35 % of QSW) /100 Distilled Water

DAY Ori inal IC-O. l ml I ( ^' -0.5ml

Sample

1 2.3 2.3 2.3

2 230 2.3X10 ³ 2.3X10 ⁴

3 230 2.3X10 ³ 2.3X10 ⁴

[0032] Table 4 shows SRB growth results with and without the addition of 0.5ml of iron compound to the 0.1 ml SRB culture in 100% of Qurayyah seawater (QSW). The result shows that in the absence of the iron compound, low growth of 2.3 SRB/ml was detected after one day of incubation. After two days, SRB growth was increased to 2.3X10 ² SRB/ml. Later, SRB growth was increased to 2.3X10 ⁴ SRB/ml in the third day. Subsequently, SRB growth continued to increase significantly to 2.3X10 ¹² SRB/ml in the fifth day and remained at this level to the end of the incubation period. Similar results were detected with the addition of 0.5 ml of iron compound. SRB growth was detected at 2.3 SRB/ml after one day of incubation. Two days later, SRB growth increased to 2.3X10 ² SRB/ml then to 2.3X10 ⁴ SRB/ml after two days, respectively. On the fifth day, the SRB growth increased to 2.3X10 ¹⁷ SRB/ml, and remained at this level to the end of the incubation period of 28 days. The test results thus indicate that the iron compound (IC) not only expedites SRB growth but also improves SRB detection sensitivity.

Table 5: Results of 0.1ml SRB culture (100 % of QSW) /100 Distilled Water

l ) \Y Oriuiiii.il Sample l( -0.5ml

1 2.3 2.3

2 2.3X10 ² 2.3X10 ²

3 2.3X10 ⁴ 2.3X10 ⁴

[0033] The results in Table 5 shows SRB growth results with and without the addition of 0.5ml of iron compound to the 0.2 ml SRB culture in 100% of Qurayyah seawater (QSW). The results indicate that in the original sample without iron compound addition, the SRB growth was below the detection limit, for the first two days of incubation. A very slight increase to 23 SRB/ml was detected on the fourth day, and continued at this level to the end of the incubation period. Identical results were detected with the addition of 0.1 ml of the iron compound. SRB growth was below the detection limit, for the first two days of incubation. But, very minor increase to 23 SRB/ml was detected on the fourth day, and continued at this level to the end of the incubation period. However, with the addition of 0.5 ml of Iron compound, SRB growth was below the detection limit after one day of incubation. But after two days, the result show that the SRB growth was slightly increased to 2.3 SRB/ml. After that, SRB growth was increased to 2.3X102 SRB/ml in the third day, and again increased to 2.3X104 SRB/ml after four days, and stayed at this level up to the end of the incubation period of 28 days. The test results thus indicate that the iron compound (IC) not only expedites SRB growth but also improves SRB detection sensitivity.

Table 6: Results of 0.1ml SRB culture (100 % of QSW) /100 Distilled Water

DAY Original l( ^' -0.1 ml K ^' -0.5ml

Sample

1 <0.4 <0.4 <0.4

2 <0.4 <0.4 2.3

3 2.3 2.3 2.3X10 ²

[0034] SRB results for Abu Ali water supply well- 840 (35% of QSW) are shown in Table 6. The test was designed to detect SRB growth without and with the addition of 0.5ml of iron compound at the 0.5 ml. The result indicated that in original sample without iron compound addition, SRB growth was below the detection limit, during the 28 days of incubation period. Identical result was detected with the addition of 0.5 ml of the iron compound. SRB growth was below the detection limit up to the fifth day. However, the SRB growth was increased gradually to 2.3 SRB/ml, then to 2.3X10 ² SRB/ml after five and ten days, respectively, and stayed at this level up to the end of the incubation period of 28 days. The test results thus indicate that the iron compound (IC) not only expedites SRB growth but also improves SRB detection sensitivity.

Table 7: SRB Results for Abu Ali water supply well- 840 (35% of QSW)

2 <0.4 <0.4

3 <0.4 <0.4

4 <0.4 <0.4

[0035] SRB results for a hard water sample are presented in Table 7. The result shows that in the absence of the iron compound addition (original sample), the SRB growth was below the detection limit during the 28 days. In addition, identical results were detected with the addition of 0.2 ml of iron compound. SRB growth was below the detection limit for 28 days. However, with the addition of 0.5 ml of iron compound, SRB growth was below detection limit for the first five days. But after six days, SRB growth was slightly increased to 2.3 SRB/ml, and remained at this level to the end of the incubation period of 28 days.

Table 8: SRB Results for Hardh water sample

2 <0.4 <0.4 <0.4

3 <0.4 <0.4 <0.4

4 <0.4 <0.4 <0.4

5 <0.4 <0.4 <0.4

6 <0.4 <0.4 <0.4

[0036] Table 8 shows the SRB results for hard water sample, with and without the addition of 0.2ml and 0.5ml of iron compound. The results show that in the absence of the iron compound addition, SRB growth was below the detection limit during the all incubation period. Identical result was detected with the addition of 0.2 ml of iron compound. SRB growth was below the detection limit for 28 days. However, with the addition of 0.5 ml of iron compound, SRB growth rate was below the detection limit for the first two days. But after four days, the SRB growth was slightly increased to 2.3 SRB/ml, and remained at this level to the end of the incubation period of 28 days. Table 9: SRB Results for UTHM water sample

DAY Original IC- 1 ( ^' -0.5ml

Sample 0.2ml

1 <0.4 <0.4 <0.4

2 <0.4 <0.4 <0.4

[0037] The methods of determining SRB concentration according to the present invention provide several advantages over the current art. The methods enable detection of very low concentrations of viable SRB cells, typically below the detection limit of any known bacterial growth culture. Furthermore, the methods provide for the rapid re-activation of dormant SRB, particularly SRB that cannot be regrown using standard procedures and are typically wrongly perceived to be no longer alive. Significantly, the methods enable rapid growth an detection of SRB, generally within 5-7 days, which is at least 75% less time than required for the growth of SRB from oilfield samples using standard media (i.e., up to 28 days).

[0038] Applicant has discovered that the additional of the FCTH enhances and boosts the activity of SRBs and activates dormant SRBs as supported by the present disclosure and the examples contained herein.

[0039] As discussed herein, the present invention is directed to a media supplement in the form of an iron compound (IC) is ferrous chloride tetra-hydrate (FeC12.4H20) that was added to SRB standard media that is used for most probable number-MPN method. The following observations were made:

1. Iron compound acts as a supplement media to increase the SRB detection sensitivity and promote the detection of SRB growth.

2. Rapid growth and detection of SRB (usually within 5-7 days) after the addition of iron compound.

3. In the absence of the iron compound, the MPN method cannot detect very low densities of viable SRB cells.

4. In the absence of the iron compound, the MPN method very slow re-activation of the dormant SRB.

5. The addition of the iron compound with different volume were effective. However, 0.5 ml from the IC stock Iron salutation (1 g FeCk.4H20 in 100 ml distilled water) was one preferred effective volume.

6. The amount of IC will can range from 50 to 55 mg/L.

[0040] The rapid detection of SRB provided by the methods of the present invention can be applied in design of microbial control kits, tools and treatment programs (e.g., biocide treatment). The methods enable rapid evaluation and adjustments of treatments, maximizing SRB control and reducing operating costs significantly. Moreover, the methods of the present invention help in minimizing the environmental impact from application of chemicals used in the procedures, and aid in optimizing such application.

[0041] It is to be understood that any structural and functional details disclosed herein are not to be interpreted as limiting the systems and methods, but rather are provided as a representative embodiment and/or arrangement for teaching one skilled in the art one or more ways to implement the methods.

[0042] It is to be further understood that like numerals in the drawings represent like elements through the several figures, and that not all components and/or steps described and illustrated with reference to the figures are required for all embodiments or arrangements.

[0043] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms "a", "an" and "the" are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms "comprises" and/or

"comprising", when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.

[0044] The method steps discussed above can be performed in different orders without departing from the scope of the invention. For instance, the iron additive can be prepared after preparation of the standard growth medium.

[0045] Also, the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. The use of "including," "comprising," or "having," "containing," "involving," and variations thereof herein, is meant to encompass the items listed thereafter and equivalents thereof as well as additional items.

[0046] While the invention has been described with reference to exemplary embodiments, it will be understood by those skilled in the art that various changes can be made and equivalents can be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications will be appreciated by those skilled in the art to adapt a particular instrument, situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.