of Garnet Structured Ionic Conductors

CROSS-REFERENCES TO RELATED APPLICATIONS

[0001] This application claims priority to U.S. Patent Application No. 62/592,930 filed November 30, 2017.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH

[0002] Not Applicable.

BACKGROUND OF THE INVENTION

1. Field of the Invention

[0003] This invention relates to electrochemical devices, such as lithium ion conducting solid-state electrolytes, solid-state lithium ion batteries, and solid-state lithium metal batteries. In one example embodiment, the lithium ion conducting solid- state electrolyte comprises Li6La3ZrBiOi2 (LLZBO) and is formed using hot-pressing techniques.

2. Description of the Related Art

[0004] Lithium ion (Li-ion) battery technology has advanced significantly and has a market size projected to be $10.5 billion by 2019. Current state of the art lithium ion batteries comprise two electrodes (an anode and a cathode), a separator material that keeps the electrodes from touching but allows Li ⁺ ions through, and an electrolyte (which is an organic liquid with lithium salts). During charge and discharge, Li ⁺ ions are exchanged between the electrodes.

[0005] State-of-the-art (SOA) Li-ion technology is currently used in low volume production plug-in hybrid and niche high performance vehicles; however, widespread adoption of electrified powertrains requires 25% lower cost, 4 times higher performance, and safer batteries without the possibility of fire. One approach is to develop solid-state battery technology. Solid-state batteries offer the promise of 3-4 times the energy density compared to the SOA Li-ion batteries at a reduction in the pack cost of 20%.

[0006] Currently, the liquid electrolyte used in SOA Li-ion batteries is not compatible with advanced battery concepts, such as the use of a lithium metal anode or high voltage cathodes. Furthermore, the liquid utilized in SOA Li-ion batteries is flammable and susceptible to combustion upon thermal runaway. The use of a solid electrolyte to replace the liquid used in the SOA enables advanced cell chemistries while

simultaneously eliminating the risk of combustion. Several solid-electrolytes have been identified including U2PO2N (LiPON) or sulfide based glasses, and companies have been formed to commercialize these types of technologies. While progress has been made towards the performance of cells of these types, large scale manufacturing has not been demonstrated since LiPON must be vapor deposited and sulfide glasses form toxic H2S upon exposure to ambient air. Thus, special manufacturing techniques are required for those systems.

[0007] Super conducting oxides (SCO) have also been proposed for use in a solid- state electrolyte. Although several oxide electrolytes are reported in the literature, selection of a particular material is not trivial since several criteria must be

simultaneously satisfied. The following metrics were identified on a combination of the SOA Li-ion battery technology baseline: (1 ) conductivity >0.2 mS/cm, comparable to SOA Li-ion battery technology, (2) negligible electronic conductivity, (3) electrochemical stability against high voltage cathodes and lithium metal anodes, (4) high temperature stability, (5) reasonable stability in ambient air and moisture, and (6) ability to be manufactured at a thicknesses of < 50 microns. Until recently, no SCO simultaneously met the above criteria.

[0008] In 2007, high Li ion conductivity in the garnet family of super conducting oxides was identified [see, Thangadurai, et al., Adv. Fund. Mater. 2005, 15, 107; and Thangadurai, et at., Ionics 2006, 12, 81 ], maximizing with the SCO garnet based on Li7La3Zr20i2 (LLZO) [see, Murugan, et al., Angew. Chem. Inter. Ed. 2007, 46, 7778] Since then, it has been shown that LLZO can meet all of the criteria necessary for a solid-electrolyte outlined above.

[0009] Several compositions in the garnet family of materials are known to exhibit Li- ion conduction with the general formula Li3+aM2Re30i2 (where a = 0 - 3, M = a metal with +4, +5, or +6 valence, and Re = a rare earth element with a +3 valence) [see, Xu, et al., Phys. Rev. B 2012, 85, 052301] T. Thompson, A. Sharafi, M.D. Johannes, A. Huq, J.L. Allen, J. Wolfenstine, J. Sakamoto, Advanced Energy Materials 2015, 11, 1500096, identified which compositions, based on Li content, exhibit maximal Li-ionic conductivity. LLZO is a particularly promising family of garnet compositions.

[0010] It has been well established that the processing temperatures of LLZO must be above 1000°C to achieve the high densities that are associated with high ionic conductivities. For the purposes of fabrication and incorporating garnet electrolytes into other systems, lower processing temperatures are desirable.

[0011] Therefore, what is needed is an improved method for the fabrication of a solid state electrolyte wherein the method dramatically lowers the densification temperature of garnet-structured solid state electrolytes, while maintaining comparable physical and electrochemical properties of previous garnet-structured solid state electrolytes.

SUMMARY OF THE INVENTION

[0012] The foregoing needs are met by the method and system provided in the present disclosure. The present disclosure provides a method of forming a solid state electrolyte using relatively low processing temperatures. The resulting electrolyte shows unexpectedly high relative densities and ionic conductivities when compared to similar electrolyte compositions formed using alternative methods.

[0013] It is one aspect of the invention to provide a method for the fabrication of a solid state electrolyte. The method includes a first step of combining a solid comprising lithium, a second solid comprising lanthanum, a third solid comprising zirconium, and a fourth solid comprising bismuth to form a mixture. The method includes a second step of applying simultaneous heat and pressure to the mixture to form a ceramic material. The ceramic material can have a stoichiometric chemical formula of Li7-xLa3Zr2-xBi _x Oi2, wherein x has a value between 0.01 and 1 .99. In another embodiment of the invention, x has a value between 0.75 and 1 . In another embodiment of the invention, x has a value of 1 .

[0014] In the method, the step of applying simultaneous heat and pressure to the mixture may comprise using a hot-pressing technique, and the hot-pressing technique may use at least one of induction heating, indirect resistance heating, or direct hot- pressing. The temperature applied may be below at least one of 1000, 950, 900, 850, 800, 750, 700, or 650 degrees Celsius. In one embodiment of the invention, the temperature applied is below 900 degrees Celsius. The applied pressure may be between 5 and 80 MPa. In one embodiment of the invention, the pressure applied is between 40 and 60 MPa.

[0015] In the method, the first solid may comprise a lithium oxide or a lithium salt. In one embodiment of the invention, the first solid comprises lithium carbonate. The second solid may comprise a lanthanum oxide or a lanthanum salt. In one embodiment of the invention, the second solid comprises lanthanum hydroxide. The third solid may comprise a zirconium oxide or a zirconium salt. In one embodiment of the invention, the third solid comprises zirconium dioxide. The fourth solid may comprises a bismuth oxide or a bismuth salt. In one embodiment of the invention, the fourth solid comprises bismuth oxide.

[0016] In the method, the ceramic material can have a relative density above 90%.

In one embodiment of the invention, the ceramic material has a relative density above 94%. The ceramic material can have a total ionic conductivity above 0.1 mS/cm. The ceramic material can have an ionic transference number of above 0.99990 when measured with chronoamperometry voltages between 2 and 10 Volts. The ceramic material can have a garnet-type or garnet-like crystal structure.

[0017] In the method, combining the solids may involve mixing dry powders. In one embodiment of the invention, the combining of the solids comprises cold-pressing and calcining the mixed dry powders. The calcining process may occur at temperatures between 500-1000 degrees Celsius for 2-8 hours. The simultaneous heat and pressure can be applied for less than 2 hours. The solids can be hot-pressed into a rectangular prism or cylindrical shape.

[0018] It is another aspect of the invention to provide an electrochemical device comprising a cathode, an anode, and the solid state electrolyte formed using the method described herein. The cathode may comprise a lithium host material selected from the group consisting of lithium metal oxides wherein the metal is one or more aluminum, cobalt, iron, manganese, nickel and vanadium, and lithium-containing phosphates having a general formula UMPO4 wherein M is one or more of cobalt, iron, manganese, and nickel. The anode may comprise a lithium host material selected from the group consisting of graphite, lithium titanium oxides, hard carbon, tin/cobalt alloy, and silicon/carbon. The anode may comprise lithium metal. The electrochemical device may include a lithium metal anode and a cathode comprising sulfur. The electrochemical device may include a lithium metal anode and a cathode comprising an air electrode.

[0019] These and other features, aspects, and advantages of the present invention will become better understood upon consideration of the following detailed description, drawings, and appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] Figure 1 is a schematic of a lithium ion battery.

[0021] Figure 2 is a schematic of a lithium metal battery.

[0022] Figure 3 depicts experimental X-ray diffraction spectra of pre-hot pressed powder and pellets hot-pressed at 750°C, 850°C, and 950°C. Markers indicate peaks belonging to the Li-deficient pyrochlore phase.

[0023] Figure 4 shows scanning electron microscope (SEM) images of fractured surfaces of LLZBO pellets hot-pressed at 750°C, 850°C, and 950°C.

[0024] Figure 5 shows experimental energy dispersive x-ray spectroscopy maps showing the distribution of Bi and Zr on the polished surface of LLZBO pellets hot- pressed at 750°C, 850°C, and 950°C.

[0025] Figure 6 is a graph depicting Raman Spectra for a phase pure LLZBO pellet hot-pressed at 850°C. The spectra for an Al-stabilized LLZO pellet is shown as a reference.

[0026] Figure 7 is a graph depicting the relative change in pellet height as a function of temperature. The arrows depict the thermal history.

[0027] Figure 8A depicts a schematic of the equivalent circuit used for fitting of the impedance spectra.

[0028] Figure 8B depicts impedance spectra for LLZBO hot-pressed at 850°C and 950°C.

[0029] Figure 8C depicts impedance spectra for LLZBO hot-pressed at 750°C.

[0030] Figure 8D shows example chronoamperometry measurement for LLZBO hot- pressed at 850°C.

[0031] Figure 9 is a graph depicting the experimental ionic transference number of LLZBO hot-pressed at 850°C as a function of the applied potential. DETAILED DESCRIPTION OF THE INVENTION

[0032] Before the present invention is described in further detail, it is to be

understood that the invention is not limited to the particular embodiments described. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting. The scope of the present invention will be limited only by the claims. As used herein, the singular forms "a", "an", and "the" include plural embodiments unless the context clearly dictates otherwise.

[0033] It should be apparent to those skilled in the art that many additional modifications beside those already described are possible without departing from the inventive concepts. In interpreting this disclosure, all terms should be interpreted in the broadest possible manner consistent with the context. Variations of the term

"comprising", "including", or "having" should be interpreted as referring to elements, components, or steps in a non-exclusive manner, so the referenced elements, components, or steps may be combined with other elements, components, or steps that are not expressly referenced. Embodiments referenced as "comprising", "including", or "having" certain elements are also contemplated as "consisting essentially of" and "consisting of" those elements, unless the context clearly dictates otherwise. It should be appreciated that aspects of the disclosure that are described with respect to a system are applicable to the methods, and vice versa, unless the context explicitly dictates otherwise.

[0034] Numeric ranges disclosed herein are inclusive of their endpoints. For example, a numeric range of between 1 and 10 includes the values 1 and 10. When a series of numeric ranges are disclosed for a given value, the present disclosure expressly contemplates ranges including all combinations of the upper and lower bounds of those ranges. For example, a numeric range of between 1 and 10 or between 2 and 9 is intended to include the numeric ranges of between 1 and 9 and between 2 and 10.

[0035] The present invention provides a method for forming a ceramic garnet based ionically conducting material that can be used as a solid state electrolyte for an electrochemical device such as a battery or supercapacitor. [0036] In an aspect, the present disclosure provides a method for forming a solid state electrolyte. The method includes a first step of combining a first solid comprising lithium, a second solid comprising lanthanum; a third solid comprising zirconium, and a fourth solid comprising bismuth to form a mixture. The method includes a second step of applying simultaneous heat and pressure to the mixture to form a ceramic material.

[0037] The ceramic material may have a stoichiometric chemical formula of

Li7-xLa3Zr2-xBixOi2 wherein x has a value between 0.01 and 1.99. The ceramic material may have an x value between 0.75 and 1 , between 0.95 and 1 .05, or of 1 .

[0038] A hot-pressing technique may be used to apply the simultaneous temperature and pressure to the solid mixture. The hot pressing technique may use at least one of induction heating, indirect resistance heating, or direct hot pressing. The applied temperature may be below at least one of 1000, 950, 900, 850, 825, 800, 775, 750, 725, 700, 675, or 650 degrees Celsius. The temperature applied may be specifically below 900 degrees Celsius. The applied pressure may be between 3 and 100 MPa, between 5 and 80 MPa, between 40 and 60 MPa, between 40 and 50 MPa, or specifically 47 MPa.

[0039] The first solid may comprise a lithium oxide or a lithium salt. For example, the first solid may comprise lithium carbonate. The second solid may comprise a lanthanum oxide or a lanthanum salt. For example, the second solid may comprise lanthanum hydroxide. The third solid may comprise a zirconium oxide or a zirconium salt. For example, the third solid may comprise zirconium dioxide. The fourth solid may comprise a bismuth oxide or a bismuth salt. For example, the fourth solid may comprise bismuth oxide.

[0040] The ceramic material may have a relative density above at least one of 75%, 80%, 85%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%. For example, the ceramic material may specifically have a relative density above 94%. The ceramic material may have a total ionic conductivity above at least one of 0.01 , 0.1 , 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1 , 2, 5, or 10 mS/cm. For example, the ceramic material may have a total ionic conductivity above 0.1 mS/cm. The ceramic material may have an ionic transference number above 0.99990 when measured with chronoamperometry voltages between 2 and 10 Volts. The ceramic material may have a garnet-type or garnet-like crystal structure. In one form, the ceramic material has the space group Ia3d.

[0041] The method step of combining the solids may comprise mixing dry powders. The method step of combining the solids may comprise cold-pressing and calcining the mixed dry powders. The calcining process may occur at temperatures between 500 and 1000 degrees Celsius for 2 to 8 hours.

[0042] The solids may be hot-pressed into a rectangular prism or cylindrical shape. The simultaneous heat and pressure may be applied for less than at least one of 0.2,

0.5, 1 , 1.5, 2, 3, 4, 6, 8, 10 , or 12 hours.

[0043] In another aspect, the present disclosure provides for an electrochemical device comprising a cathode, an anode, and a solid-state electrolyte that was formed using the method described herein.

[0044] The cathode of the electrochemical device may comprise a lithium host material selected from the group consisting of lithium metal oxides wherein the metal is one or more aluminum, cobalt, iron, manganese, nickel and vanadium, and lithium- containing phosphates having a general formula UMPO4, wherein M is one or more of cobalt, iron, manganese, and nickel. The anode may comprise a lithium host material is selected from the group consisting of graphite, lithium titanium oxides, hard carbon, tin/cobalt alloy, and silicon/carbon. The anode may comprise a lithium metal. The electrochemical device may include a lithium metal anode and a cathode comprising sulfur. The electrochemical device includes a lithium metal anode and a cathode comprising an air electrode.

[0045] In one non-limiting example application, a solid state electrolyte formed using the methods of the invention is used in a lithium ion battery as depicted in Figure 1. The lithium ion battery 10 of Figure 1 includes a current collector 12 (e.g., aluminum) in contact with a cathode 14. A solid state electrolyte 16 formed using the methods of the invention is arranged between the cathode 14 and an anode 18, which is in contact with a current collector 22 (e.g., aluminum). The current collectors 12 and 22 of the lithium ion battery 10 may be in electrical communication with an electrical component 24. The electrical component 24 could place the lithium ion battery 10 in electrical communication with an electrical load that discharges the battery or a charger that charges the battery.

[0046] A suitable active material for the cathode 14 of the lithium ion battery 10 is a lithium host material capable of storing and subsequently releasing lithium ions. An example cathode active material is a lithium metal oxide wherein the metal is one or more aluminum, cobalt, iron, manganese, nickel and vanadium. Non-limiting example lithium metal oxides are LiCo02 (LCO), LiFe02, LiMn02 (LMO), LiMn204, LiN 1O2 (LNO), LiNixCo _y 02, LiMn _x Coy02, LiMn _x Ni _y 02, LiMn _x Ni _y 04, LiNi _x Co _y Al _z 02, LiNii/3Mm/3Coi/302 and others. Another example of cathode active materials is a lithium-containing phosphate having a general formula UMPO4 wherein M is one or more of cobalt, iron, manganese, and nickel, such as lithium iron phosphate (LFP) and lithium iron fluorophosphates. Many different elements, e.g., Co, Mn, Ni, Cr, Al, or Li, may be substituted or

additionally added into the structure to influence electronic conductivity, ordering of the layer, stability on delithiation and cycling performance of the cathode materials. The cathode active material can be a mixture of any number of these cathode active materials.

[0047] A suitable active material for the anode 18 of the lithium ion battery 10 is a lithium host material capable of incorporating and subsequently releasing the lithium ion such as graphite, lithium titanium oxide, hard carbon, a tin/cobalt alloy, or silicon/carbon. The anode active material can be a mixture of any number of these anode active materials.

[0048] In another non-limiting example application, a solid state electrolyte formed using the methods of the invention is used in a lithium metal battery as depicted in Figure 2. The lithium metal battery 1 10 of Figure 2 includes a current collector 1 12 in contact with a cathode 1 14. A solid state electrolyte 1 16 formed using the methods of the invention is arranged between the cathode 1 14 and an anode 1 18, which is in contact with a current collector 122. The current collectors 1 12 and 122 of the lithium metal battery 1 10 may be in electrical communication with an electrical component 124. The electrical component 124 could place the lithium metal battery 1 10 in electrical communication with an electrical load that discharges the battery or a charger that charges the battery. A suitable active material for the cathode 1 14 of the lithium metal battery 1 10 is one or more of the lithium host materials listed above, or porous carbon (for a lithium air battery), or a sulfur containing material (for a lithium sulfur battery). A suitable active material for the anode 1 18 of the lithium metal battery 1 10 is lithium metal.

[0049] Certain garnet based ceramic materials are useful for forming solid state electrolytes. The garnet phase of the ceramic material exhibits fast ion conduction similar to prior LLZO phases. The room temperature total Li ionic conductivity of the ceramic material can be 0.1 mS/cm or higher. This is close to the reported values for conventional Al doped LLZO (0.3-0.4 mS/cm).

Example

[0050] The following example is provided in order to demonstrate and further illustrate certain embodiments and aspects of the present invention and is not to be construed as limiting the scope of the invention.

Overview

[0051] In recent years, there has been a growing interest in the garnet structured Li7La3Zr20i2 (LLZO) solid electrolyte due to its unprecedented combination of high ionic conductivity, stability against Li metal, and moderate stability in air [Ref. 1-3] These properties make LLZO a suitable material for Li-ion solid state and Li-S batteries to meet the high energy density requirements that future energy storage applications demand [Ref. 4, 5] As only the cubic polymorph of LLZO exhibits superionic conductivity, there has been significant effort in studying the effects of various dopants, like Al, Ta, and Nb in the garnet structure [Ref. 6-9] It has been shown by Xia et al. that a partial substitution of Bi ⁵⁺ on the Zr ⁴⁺ octahedral site can also stabilize the cubic phase [Ref. 10] The Bi garnet, LisLa3Bi20i2 (LLBO), has been characterized as well and is shown to exhibit relatively low ionic conductivities compared to LLZO [Ref. 1 1- 13] Although the conductivity is lower, Bi garnets have exhibited significantly lower calcination and sintering temperatures, in the range of 600°C-900°C [Ref. 12-15] In comparison, traditional LLZO requires processing temperatures above 1000°C for the cubic garnet structure to form, and even higher to achieve the high densities required for high ionic conductivity. In more recent studies, it has been observed that garnets of the composition Li7-xLa3Zr2-xBi _x Oi2 (LLZBO) also exhibit these low processing temperatures [Ref. 10, 16-18] Not only does the Bi substitution stabilize the cubic phase, but also significantly lowers the densification temperature.

[0052] Currently there are few studies that focus on the properties and behavior of this system. Existing studies have looked at the properties of sintered LLZBO, however, it is known that the processing methods of LLZO have a significant impact on the ionic conductivity of the material, due to grain boundary resistance [Ref. 19, 20] It has been seen with LLZO that high density pellets fabricated by hot-pressing exhibit significantly higher ionic conductivity and critical current densities compared to pressure-less sintering approaches [Ref. 19-21 ]

[0053] We suspected that the simultaneous application of temperature and pressure of LLZBO would improve grain boundary contact and adhesion, which results in significantly lower grain boundary impedance. Therefore, we believed that using such manufacturing methods may not only improve the total conductivity, but also reduce the sintering time, create a more uniform microstructure, and improve the mechanical properties.

[0054] The focus of this experiment was to demonstrate the synthesis of phase pure LLZBO with high (>90 %) relative densities than can be achieved by pressure-assisted densification. A Bi concentration of above 0.2 may stabilize the cubic phase, and fast Li-ion transport may be seen with Bi concentrations between 0.75 and 1.0 [Ref. 16]

[0055] LLZBO of the nominal composition Li6La3ZrBiOi2 was the focus of this work. The effect of hot-pressing temperature and pressure on the relative density and phase purity was investigated. A potential mechanism for the low densification temperatures was also investigated. Using a combination of AC and DC methods, the ionic and electronic impedance/resistance of high density LLZBO were measured. Overall, using a variety of materials characterization techniques, including x-ray diffraction, scanning electron microscopy, and Raman spectroscopy, this study presents the first

investigation of LLZBO fabricated by a hot-pressing approach and that Zr-based LLZO can be densified to >90% relative density below 900°C.

[0056] In the study of this Example, Li6La3ZrBiOi2 (LLZBO) was prepared by a rapid-induction hot-pressing technique and characterized using a variety of techniques, including x-ray diffraction, scanning electron microscopy, and Raman spectroscopy. We demonstrated in this Example the ability to synthesize phase pure LLZBO with higher relative densities (~94%) than can be achieved by pressure-less sintering methods, at pressing temperatures of only 850°C. The ionic conductivity was measured to be 0.1 mS/cm, which is comparable to the best reported conductivities of high density LLZO. This demonstrates the ability to fabricate dense, phase pure, and high conductivity LLZBO at temperatures significantly lower than other garnet compositions, which will prove useful for scalability and reducing reactivity with cathodes during densifi cation.

Experimental

Materials Synthesis And Processing

[0057] LLZBO with the composition Li6La3ZrBiOi2 was synthesized by a solid state synthesis technique. U2CO3 (1 pm, Alfa Aesar, Ward Hill, Massachusetts, USA), La(OH)3 (1 pm, Alfa Aesar, Ward Hill, Massachusetts, USA), Zr02 (30-60 nm, Inframat, Advanced Materials, Manchester, Connecticut, USA), and B12O3 (80-200 nm, Alfa Aesar, Ward Hill, Massachusetts, USA) were used as starting precursors. The precursors were weighed in the stoichiometric amounts and dry-milled in a planetary ball mill (PM 100; Retsch, Haan, Germany). An excess 30 wt% of L12CO3 was added to account for Li volatilization during calcination. The resulting mixture was cold-pressed and calcined in air at 800°C for 4 hours. The calcined pellets were reground, cold pressed, and calcined again at 800°C for 4 hours. This process was repeated twice and a 20 wt% excess of L12CO3 was added each time to account for Li volatilization. The final LLZBO powder was formed into pellets by a rapid induction hot-pressing technique as described by Rangasamy et al [Ref. 21] The powder was pressed in a graphite die at 47 MPa and at temperatures between 750°C and 950°C. The resulting pellets were cut into 1.5 ± 0.2 mm disks on a diamond saw and polished with various sandpapers and diamond pastes to a final polish using 0.1 pm diamond paste.

Materials Characterization

[0058] X-ray diffraction was performed using a Rigaku Miniflex 600 X-ray

diffractometer, using Cu Ka radiation over a 2Q range of 15° to 65° with a 0.02° step size. [0059] Microstructural and energy dispersive x-ray spectroscopy (EDS) analysis was performed on a Tescan MIRA3 GMU FEG scanning electron microscope.

[0060] The conductivity of the material was measured using electrochemical impedance spectroscopy (EIS) and DC polarization methods, on a Biologic VMP-300 galvanostat/potentiostat. EIS was performed from 1 Hz to 7 MHz with a perturbation of 100 mV at room temperature and sputtered Au blocking electrodes. The DC

polarization method used was staircase potentiometry (Mott-Schottky), with 1 0V steps over a range from 3.5 V to 8.5 V vs Li/Li ⁺ .

[0061] Raman spectroscopy was performed on a Horiba Micro Raman Spectrometer using a 532 nm laser, 1800 lines per mm holographic grating, and 50x magnification at room temperature.

[0062] Thermomechanical analysis (TMA) was performed using a TA Instruments Q400 Thermomechanical Analyzer. For performing TMA, calcined powders were cold pressed into a pellet under 150 kPa of pressure. The pellet was loaded under 0.8 N and heated to 850°C at a rate of 57m in in an Ar atmosphere. Due to the fact that the LLZBO is likely to react with most available crucibles used for thermal analysis, a “pseudo-dilatometry” experiment was used to estimate the melting temperature. A cold pressed pellet of LLZBO powder was loaded into a graphite die and heated while under pressure. A constant pressure of 16 MPa was applied while heating from room temperature to 1300°C at a rate of 120°C-min ¹ . Extrusion of molten powder was observed to correlate to a drastic increase in the strain and the corresponding

temperature was estimated to be the melting temperature.

Results

X-Ray Diffraction

[0063] X-ray diffraction was conducted for three different hot-pressing temperatures and is shown in Figure 3. The samples for each hot pressing temperature exhibit a clear display of the cubic garnet structure, shown as a reference in Figure 3. The partial substitution of Bi stabilizes the cubic phase as no tetragonal garnet is evident [see Ref. 16] The lattice parameter was calculated based on the XRD spectra of the phase pure 850°C sample. The calculated lattice parameter of 13.036 A shows an increase from the lattice parameter of cubic LLZO, 12.980 A. This is to be expected considering the relative size of Bi ⁵⁺ compared to Zr ⁴⁺ . Trace impurities can be observed for the calcined powder as well as the lower temperature samples. The 950°C hot pressed sample exhibits a significant amount of impurities, primarily the Li deficient pyrochlore phase indicated by the markers in Figure 3. As seen with other garnet systems, Li volatilizes more easily at higher temperatures resulting in the significant fraction of pyrochlore in the 950°C hot-pressed sample. Although slightly higher densities may be achieved, the faster Li volatilization rates make it more difficult to achieve good phase purity.

Additionally, the most attractive feature of this composition of LLZBO is its low densification temperature and so there is little interest in studying temperatures above 950°C in this work. From the XRD spectra and density calculations presented here, it is clear that both good phase purity and relatively high densities can be achieved at 850°C.

Density Analysis

[0064] Previous reports on compositions of LLZBO have reported up to 90% relative densities by pure pressure-less sintering, as measured by the Archimedes method or by gas pycnometry. However, it was observed that high densities could not be achieved by pressure-less sintering alone, as measured by geometric density calculations. SEM analysis suggests that at lower densities, there is a percolated network of pores throughout the material ending at the surfaces, which may be accessible to the fluids used for these methods. For these reasons, we believe the geometric density may provide a more accurate value for the relative densities. From the geometric

dimensions of the hot-pressed pellets, it was calculated that the relative densities for the 750°C, 850°C, and 950°C samples are 90%, 94%, and 98% respectively. Even at the lowest hot-pressing temperature, the relative density reported here is higher than any reported in the literature. For the more common dopants such as Al, Ta, or Nb, to achieve similar densities requires hot-pressing temperatures above 1000°C [Ref. 6, 8, 19, 20]

[0065] Figure 4 shows SEM images of fracture surfaces of each sample and the observed microstructures seem consistent with the calculated relative densities. It was observed that there is increasing grain boundary adhesion and decreasing porosity with increasing hot-pressing temperatures. Although intergranular fracture was observed for all three temperatures, there was increasing evidence of intragranular fracture with increasing temperature. Even at the lowest temperature there was still evidence of intragranular fracture, which is a good example of the strong grain boundary adhesion that can be achieved by a technique such as hot-pressing, as observed by Kim et al [Ref. 20]

Energy Dispersive X-Ray Spectroscopy

[0066] Energy dispersive x-ray spectroscopy (EDS) was conducted on a polished surface of a hot-pressed pellet. The secondary electron images of each sample also seem consistent with the reported trend in the relative density as a function of temperature. Figure 5 shows the elemental maps for Zr and Bi. On all imaged samples, both the Zr and Bi maps are homogeneous and no major phase separation was observed. The uniform distribution of both Zr and Bi suggests that the Bi is indeed substituting into the LLZO structural framework, as opposed to forming separate regions of LLZO and LLBO. This is also consistent with the increase in lattice parameter observed in XRD analysis and the Raman spectroscopy analysis discussed in the next section.

Raman Spectroscopy

[0067] The Raman spectra shown in Figure 6 was collected for the phase pure 850°C hot-pressed sample, as well as Al-stabilized LLZO pellet for reference. Previous investigations of the Raman spectra for LLZO and LLBO have been reported [Ref. 9,

16] These studies report that the band at 650 cm ¹ is related to the stretching of Zr-0 bonds while the band at 590 cm ¹ is related to the stretching of Bi-0 bonds. This is also consistent with the calculated lattice parameter from the XRD spectra of the phase pure 850°C sample. The increase in the lattice parameter, the presence of both the Bi-0 and Zr-0 Raman bands, and the homogeneous distribution of both Zr and Bi are strong indications that the Bi is substituting on the Zr octahedral site (see Figures 6 and 7).

Thermomechanical analysis

[0068] This Example reports the investigation of LLZBO synthesized by a pressure- assisted densification method. The low densification temperature in

Bi-containing garnets may be due to the presence of a“pseudo-liquid” phase that forms, due to the fact that Bi tends to form low melting point oxides [Ref. 18] This liquid phase would not only allow for improved grain boundary sliding, but may also improve diffusive transport during the densification process.

[0069] Thermomechanical analysis was conducted to further elucidate the presence of a liquid phase. The results can be seen in the graph of Figure 7. Drastic dilation was observed beginning around 650°C and it is evident that the majority of the densification for this system occurs between 600°C - 800°C, which is more than 200°C lower than the densification temperatures for LLZO and other similar garnets. It can be seen that even with a negligible load applied, there is a dramatic onset of densification at significantly lower temperatures.

[0070] Due to the reactivity of the LLZBO with common crucible materials for thermal analysis, a“pseudo-dilatometry” experiment was used to estimate the melting

temperature, which was estimated to be within the range of 1050°C-1100°C. This melting temperature is significantly lower than other garnet systems, such as yttrium aluminum garnets (YAG) and gadolinium gallium garnets (GGG), which have melting temperatures of 1940°C and 1750°C, respectively [Ref. 22, 23] Considering the pseudo-phase diagram of the garnet system consisting of the U2O, I_a203, and Zr02 binary phases, the melting temperature should correlate with the melting temperature of each component. In the LLZBO system, since the melting temperatures of bismuth oxides are significantly lower than L12O, La203, and Zr02, it is reasonable that the overall melting temperature of the LLZBO system will also be significantly lower than that of the LLZO system. We hypothesize that the densification temperature

appropriately scales with the melting temperature of the overall system, and therefore since the addition of the Bi substitution lowers the melting temperature, it also lowers the densification temperature.

Ionic Transference Number

[0071] Electrochemical impedance spectroscopy was conducted on each hot- pressed sample. To determine the ionic conductivity, the impedance spectra were modeled using a modified version of the equivalent circuit proposed by Huggins [Ref.

24] As in the Huggins model, a resistive element was used to represent the impedance of the bulk material, the grain boundary, and the interface. The capacitive elements that are used in the Huggins model were replaced by constant phase elements (CPEs) to accommodate variations in the time constants. The resulting equivalent circuit is depicted in Fig. 8A. The EIS spectra were fit to this equivalent circuit and each component of the spectra was assigned a physical phenomenon based off of the calculated capacitance value, with capacitance values of 10 ¹² F and 10 ⁸ F indicating the bulk component and grain boundary component, respectively [Ref. 25]

[0072] Figures 8B-8C show the impedance spectra for LLZBO hot-pressed at 750°C, 850°C, and 950°C; Figure 8D shows chronoamperometry measurement for LLZBO hot- pressed at 850°C; and a summary of the physical properties and the ionic resistances of LLZBO hot-pressed at 750°C, 850°C, and 950°C is provided in Table 1.

Table 1

For the phase pure 850°C sample, the total resistance (Rtotai) was measured to be 9.33 kQ-cm, which corresponds to a conductivity (o) of 0.107 mS crrr ¹ . This ionic

conductivity is comparable to the conductivities reported for LLZO samples of similar densities, and higher than conductivities reported for LLBO samples [Ref. 12, 13] The resistance of the lowest density 750°C sample was the highest for both the bulk

(Rbuik)and grain boundary (RGB) components. The high bulk resistance is likely due to the low relative density while the high grain boundary resistance is likely due to the poor grain boundary adhesion seen under SEM. The bulk resistance of the 850°C sample was the lowest, which can be attributed to the combination of high relative density and high phase purity. On the contrary, the 950°C sample had a slightly higher bulk resistance. Although the higher relative density correlates to a lower bulk resistance, the larger amount of impurities likely increased the resistance. However, it was also observed that the grain boundary resistance of the 950°C sample was significantly lower than both the 750°C and 850°C samples, which is consistent with the trend of increasing intergranular fracture with increasing temperature that was observed under SEM. Intragranular fracture, as opposed to intergranular fracture, is an indication of strong grain boundary adhesion and a high degree of contact area, which enhances ionic transport between grains. This results in a correlation between a high degree of intragranular fracture and high grain boundary conductivity which has also been observed in other garnet systems [Refs. 20, 26]

[0073] The electronic conductivity was determined by chronoamperometry from 3.5 V to 8.5 V vs Li/Li ⁺ and was used to measure the ionic transference number for the phase pure 850°C sample. For the blocking electrode set-up used, the initial transient region of the current response represents the combined current contributions of both ionic and electronic transport. As the supply of mobile ions is depleted, the current becomes dominated by the electronic current and therefore the steady state is representative of solely the electronic current. Using these steady state values, the average electronic conductivity was measured to be 8.2x1 O ¹⁰ S/cm, which is

approximately the same as reported values for LLZO [Ref. 27] The ionic transference number as a function of potential is shown in Figure 9. It was observed that the transference number is nearly equal to 1 in the entire potential window, which indicates that the majority of the conductance is caused by ionic transport rather than electron transport. A small dip in the transference number was observed near 5.5 V vs Li/Li ⁺ , which was also observed in similar studies for Ta-stabilized LLZO [Ref. 27] The dip at this potential may be an indication of hole injection into the LLZO valence band maximum.

[0074] In this Example, it has been demonstrated that through a hot-pressing approach, high density, phase pure LLZBO can be fabricated at temperatures significantly lower than possible for other garnet systems. The high density and high phase purity have shown to contribute to a relatively high ionic conductivity compared to previous reports for Bi garnets. Furthermore, the conductivities measured here are comparable to the conductivities reported for other compositions of cubic LLZO, sintered at temperatures above 1000°C. The study presented here focuses on one example composition of the LLZBO garnet family, but other hot-pressing conditions or Bi content may maximize the conductivity and minimize the densification temperature. Conclusions

[0075] In this Example, we demonstrated the synthesis of Li6La3ZrBiOi2 by a hot- pressing method. We achieved surprisingly good phase purity and higher relative densities compared to pressure-less sintering methods at similar processing

temperatures. Analysis under EDS and Raman spectroscopy shows good incorporation of the Bi dopant into the garnet structure. SEM of both the polished surfaces and fracture surfaces are consistent with geometric density calculations and show strong grain boundary adhesion, as evidenced by the domination of intragranular fracture. Without intending to be bound by theory, the high total ionic conductivity (0.1 mS/cm) reported may be caused by the improved density and grain boundary adhesion. The reported electronic conductivity of 8 ^c 10 ¹⁰ S/cm in this Example also suggests that the ionic transference number is near unity. Furthermore, thermomechanical analysis was conducted to provide insight into the low temperature densification properties. It was observed that rapid densification begins to occur around 650°C, which is hypothesized without intending to be bound by theory to be a consequence of the low melting temperature of the LLZBO system. Improving the density of ion conducting ceramic oxides at lower temperatures is an important requirement for the scalability of solid state electrolytes. We have demonstrated in this Example the capability of Bi-containing garnets to achieve similar conductivities and densities of typical LLZO at significantly lower densification temperatures in a continued effort to successfully integrate garnet solid electrolytes into all solid state Li-ion batteries and lithium metal batteries.

References

[1 ] R. Murugan, V. Thangadurai, W. Weppner, Fast Lithium Ion Conduction in Garnet-Type Li7La3Zr20i2, Angew. Chem. Int. Ed. 46 (2007) 7778-7781.

doi: 10.1002/anie.200701144.

[2] V. Thangadurai, S. Narayanan, D. Pinzaru, Garnet-type solid-state fast Li ion conductors for Li batteries: critical review, Chem. Soc. Rev. 43 (2014) 4714-4727.

doi: 10.1039/C4CS00020J.

[3] T. Thompson, A. Sharafi, M.D. Johannes, A. Huq, J.L. Allen, J. Wolfenstine,

J. Sakamoto, A Tale of Two Sites: On Defining the Carrier Concentration in Garnet- Based Ionic Conductors for Advanced Li Batteries, Adv. Energy Mater. 5 (2015)

1500096. doi: 10.1002/aenm.201500096.

[4] J.-M. Tarascon, M. Armand, Issues and challenges facing rechargeable lithium batteries, Nature. 414 (2001 ) 359-367. doi: 10.1038/35104644.

[5] J.B. Goodenough, Y. Kim, Challenges for Rechargeable Li Batteries ^† , Chem. Mater. 22 (2010) 587-603. doi: 10.1021 /cm901452z.

[6] J.L. Allen, J. Wolfenstine, E. Rangasamy, J. Sakamoto, Effect of substitution (Ta, Al, Ga) on the conductivity of Li7La3Zr20i2, J. Power Sources. 206 (2012) 315-319. doi:10.1016/j.jpowsour.2012.01.131.

[7] L.J. Miara, S.P. Ong, Y. Mo, W.D. Richards, Y. Park, J.-M. Lee, H.S. Lee, G. Ceder, Effect of Rb and Ta Doping on the Ionic Conductivity and Stability of the Garnet

Li7+2x-y(La3-xRbx)(Zr2- _y Ta _y )012 (0 < x < 0.375, 0 < y < 1 ) Superionic Conductor: A First Principles Investigation, Chem. Mater. 25 (2013) 3048-3055. doi: 10.1021 /cm401232r.

[8] E. Rangasamy, J. Wolfenstine, J. Allen, J. Sakamoto, The effect of 24c-site (A) cation substitution on the tetragonal-cubic phase transition in Li7-xLa3-xA _x Zr20i2 garnet-based ceramic electrolyte, J. Power Sources. 230 (2013) 261-266.

doi: 10.1016/j.jpowsour.2012.12.076.

[9] T. Thompson, J. Wolfenstine, J.L. Allen, M. Johannes, A. Huq, I.N. David, J. Sakamoto, Tetragonal vs. cubic phase stability in Al - free Ta doped Li7La3Zr20i2 (LLZO), J. Mater. Chem. A. 2 (2014) 13431-13436. doi:10.1039/C4TA02099E. [10] Y. Xia, L. Ma, H. Lu, X.-P. Wang, Y.-X. Gao, W. Liu, Z. Zhuang, L.-J. Guo, Q.-F. Fang, Preparation and enhancement of ionic conductivity in Al-added garnet-like Li6.8La3Zn.8Bio.2O12 lithium ionic electrolyte, Front. Mater. Sci. 9 (2015) 366-372.

doi: 10.1007/s11706-015-0308-6.

[11] S. Teng, J. Tan, A. Tiwari, Recent developments in garnet based solid state electrolytes for thin film batteries, Curr. Opin. Solid State Mater. Sci. 18 (2014) 29-38. doi:10.1016/j.cossms.2013.10.002.

[12] R. Murugan, W. Weppner, P. Schmid-Beurmann, V. Thangadurai, Structure and lithium ion conductivity of bismuth containing lithium garnets Li5La3Bi2012 and Li6SrLa ₂ Bi ₂ 0i2, Mater. Sci. Eng. B. 143 (2007) 14-20. doi:10.1016/j.mseb.2007.07.009.

[13] Y.X. Gao, X.P. Wang, W.G. Wang, Z. Zhuang, D.M. Zhang, Q.F. Fang, Synthesis, ionic conductivity, and chemical compatibility of garnet-like lithium ionic conductor Li5La3Bi20i2, Solid State Ion. 181 (2010) 1415-1419.

doi: 10.1016/j .ssi.2010.08.012.

[14] H. Peng, L. Xiao, Y. Cao, X. Luan, Synthesis and ionic conductivity of

Li6La3BiSnOi2 with cubic garnet-type structure via solid-state reaction, J. Cent. South Univ. 22 (2015) 2883-2886. doi: 10.1007/s11771 -015-2821 -2.

[15] H. Peng, Y. Zhang, L. Li, L. Feng, Effect of quenching method on Li ion conductivity of LisLa3Bi20i2 solid state electrolyte, Solid State Ion. 304 (2017) 71-74. doi: 10.1016/j. ssi.2017.03.030.

[16] R. Wagner, D. Rettenwander, G.J. Redhammer, G. Tippelt, G. Sabathi,

M.E. Musso, B. Stanje, M. Wilkening, E. Suard, G. Amthauer, Synthesis, Crystal Structure, and Stability of Cubic Li7-xLa3Zr2-xBi _x Oi2, Inorg. Chem. 55 (2016) 12211- 12219. doi: 10.1021 /acs. inorgchem.6b01825.

[17] D.K. Schwanz, E. Marinero, Low Temperature Synthesis of Cubic-phase

Fast-ionic Conducting Bi-doped Garnet Solid State Electrolytes, in: 2016.

http://adsabs.harvard.edu/abs/2016APS..MARH5401 OS.

[18] D.K. Schwanz, E.E. Marinero-Caceres, Solid-state electrolytes and batteries made therefrom, and methods of making solid-state electrolytes, US20160133990 A1 , [19] I.N. David, T. Thompson, J. Wolfenstine, J.L. Allen, J. Sakamoto, Microstructure and Li-Ion Conductivity of Hot-Pressed Cubic Li7La3Zr20i2, J. Am.

Ceram. Soc. 98 (2015) 1209-1214. doi:10.1111 /jace.13455.

[20] Y. Kim, H. Jo, J.L. Allen, H. Choe, J. Wolfenstine, J. Sakamoto, The Effect of Relative Density on the Mechanical Properties of Hot-Pressed Cubic Li7La3Zr20i2,

J. Am. Ceram. Soc. 99 (2016) 1367-1374. doi:10.1111 /jace.14084.

[21 ] E. Rangasamy, J. Wolfenstine, J. Sakamoto, The role of Al and Li concentration on the formation of cubic garnet solid electrolyte of nominal composition Li7La ₃ Zr ₂ 0i2, Solid State Ion. 206 (2012) 28-32. doi:10.1016/j.ssi.2011.10.022.

[22] J.L. Caslavsky, D.J. Viechnicki, Melting behaviour and metastability of yttrium aluminium garnet (YAG) and YAIO3 determined by optical differential thermal analysis, J. Mater. Sci. 15 (1980) 1709-1718. doi:10.1007/BF00550589.

[23] Q. Xiao, J. J. Derby, Heat transfer and interface inversion during the

Czochralski growth of yttrium aluminum garnet and gadolinium gallium garnet, J. Cryst. Growth. 139 (1994) 147-157. doi: 10.1016/0022-0248(94)90039-6.

[24] R.A. Huggins, Simple method to determine electronic and ionic components of the conductivity in mixed conductors a review, Ionics. 8 (2002) 300-313.

[25] Irvine JTS, Sinclair DC, West AR (1990) Electroceramics: characterization by impedance spectroscopy. Adv Mater 2(3): 132-138. https://doi.org/10.1002/ adma.19900020304

[26] Wolfenstine J, Ratchford J, Rangasamy E et al (2012) Synthesis and high Li-ion conductivity of Ga-stabilized cubic Li7La3Zr20i2. Mater Chem Phys 134(2-3):571- 575. https://doi.Org/10.1016/j. matchemphys.2012.03.054

[27] T. Thompson, S. Yu, L. Williams, R.D. Schmidt, R. Garcia-Mendez, J.

Wolfenstine, J.L. Allen, E. Kioupakis, D.J. Siegel, J. Sakamoto, Electrochemical Window of the Li-Ion Solid Electrolyte Li7La3Zr20i2, ACS Energy Lett. 2 (2017) 462-468.

doi: 10.1021 /acsenergylett.6b00593.

The citation of any document or reference is not to be construed as an admission that it is prior art with respect to the present invention. [0076] Thus, the present invention provides a ceramic garnet based ionically conducting material that can be used as a solid state electrolyte for an electrochemical device such as a battery or supercapacitor. Cubic garnet Li7La3Zr20i2 (LLZO) and similar compositions of fast ion-conducting solid-state electrolytes have shown great potential for the development of high-energy-density solid-state Li-ion batteries.

Although these materials have shown unprecedented ionic conductivities and chemical stability, these materials require high processing temperatures for synthesis. For many of the common compositions of LLZO, temperatures above 1000°C are required to form the cubic garnet phase and to achieve high conductivities. Therefore, lowering the processing temperatures of these materials as described herein is of great interest for the purposes of scalability and fabrication. A Bi co-dopant not only stabilizes the cubic garnet phase but also lowers the densification temperature.

[0077] Although the invention has been described in considerable detail with reference to certain embodiments, one skilled in the art will appreciate that the present invention can be practiced by other than the described embodiments, which have been presented for purposes of illustration and not of limitation. Therefore, the scope of the appended claims should not be limited to the description of the embodiments contained herein.