CROSS-REFERENCE TO RELATED APPLICATIONS [0001] This application claims the benefit of U.S. Provisional Patent Application No.

61/348,996, filed on May 27, 2010, and fully incorporated herein by reference.

FIELD OF THE INVENTION

[0002] Embodiments of the invention relate to methods of producing crosslinkable silyl group-containing polyoxyalkylene polymers.

BACKGROUND OF THE INVENTION

[0003] Crosslinkable silyl group-containing polyoxyalkylene polymers are widely used as raw material polymers in sealing materials, adhesives, coating materials and the like for architectural or industrial use. Such crosslinkable silyl group-containing polyoxyalkylene polymers may be produced according to various methods, such as the methods mentioned in U.S. Pat. No 6,503,995. For example, first a polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule may be obtained by subjecting an epoxy compound to ring opening polymerization using an unsaturated group- and active hydrogen-containing compound as a polymerization initiator and a double metal cyanide complex as a catalyst. The polyoxyalkylene polymer may then be reacted with a compound having a hydrogen- silicon bond and a crosslinkable silyl group in each molecule in the presence of a hydrosilylation catalyst to thereby carry out a hydrosilylation reaction. However, according to U.S. Pat. No 6,503,995, in order for the hydrosilylation yield to be acceptable, the

polyoxyalkylene polymer must first either have the double metal cyanide complex catalyst removed or be treated with a metal-coordinating compound before the hydrosilylation reaction.

[0004] Therefore there is a need for method for producing crosslinkable silyl group- containing polyoxyalkylene polymers without the need to remove or otherwise treat the double metal cyanide catalyst. ¾ U MM K Ϊ Ut I tit, 11 V £1 I 1U1

[0005] Embodiments of the invention provide for methods of producing highly hydrosilylated polyoxyalkylene polymers without the need to remove or otherwise treat double metal cyanide (DMC) catalysts complex present in the hydrosilylation reactants.

[0006] In one embodiment a method of producing a hydrosilylated polyoxyalkylene polymer having at least one crosslinkable silyl group and at least one hydroxyl group in each molecule is provided, The method includes providing a polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule. The polyoxyalkylene polymer includes an impurity double metal cyanide complex mixed therein, and the polyoxyalkylene polymer has not been treated with a metal-coordinating compound and has not been purified to significantly remove the impurity double metal cyanide complex. The method further provides adding to the polyoxyalkylene polymer a compound having a hydrogen- silicon bond and a crosslinkable silyl group in each molecule and a hydrosilylation catalyst to thereby carry out a hydrosilylation reaction. The hydrosilyation reaction is performed in an absence of a metal-coordinating compound and the hydrosilyation reaction has a hydrosilylation efficiency of at least about 70% as determined by ^-NMR.

[0007] In another embodiment a method of producing a crosslinkable silyl group- containing polyoxyalkylene polymer is provided, The method includes (a) providing a polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule, wherein the polyoxyalkylene polymer includes an impurity double metal cyanide complex mixed therein, and wherein the polyoxyalkylene polymer has not been treated with a metal-coordinating compound and has not been purified to significantly remove the impurity double metal cyanide complex, then adding to the polyoxyalkylene polymer a compound having a hydrogen-silicon bond and a crosslinkable silyl group in each molecule and a hydrosilylation catalyst to thereby carry out a hydrosilylation reaction, wherein the

hydrosilyation reaction is performed in an absence of a metal-coordinating compound and the hydrosilyation reaction has a hydrosilylation efficiency of at least about 70% as determined by ^-NMR; and (b) carrying out a coupling reaction in which the hydroxyl group occurring in the polymer is involved.

DESCRIPTION OF EMBODIMENTS OF THE INVENTION

[0008] Embodiments of the invention provide for methods of producing highly hydrosilylated polyoxyalkylene polymers without the need to remove or otherwise treat double metal cyanide (DMC) catalysts complex present in the hydrosilylation reactants. Luuuyj i ne nyarosiiyiation reactants inciuae at least one poiyoxyaiKyiene polymer naving at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule and at least one compound having a hydrogen-silicon bond and a crosslinkable silyl group in each molecule.

[0010] The at least one polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule (hereinafter referred to as

"polyoxyalkylene polymer") may be made by subjecting an epoxy compound to ring opening polymerization using an unsaturated group- and active hydrogen-containing compound as a polymerization initiator and a double metal cyanide catalyst complex as a catalyst.

[0011] The active hydrogen-containing compound that may be used as a polymerization initiator is not restricted but may be any of those compounds which are applicable in association with double metal cyanide complexes, such as, for example, compounds including an alcoholic hydroxyl, phenolic hydroxyl or carboxyl group.

[0012] The alcoholic hydroxyl-containing compound may include allyl alcohol, methallyl alcohol, trimethylolpropane monoallyl ether, trimethylolpropane diallyl ether, glycerol monoallyl ether, glycerol diallyl ether; ethylene oxide adducts or propylene oxide adducts thereof and like compounds containing at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule; hydroxyl-terminated hydrocarbon compounds such as hydroxyl-terminated polybutadiene; and the like. Such active hydrogen-containing compounds serving as

polymerization initiators may be used singly or a plurality thereof may be used in combination.

[0013] The monoepoxide which may be used in the ring opening polymerization may include, among others, monoepoxides having no unsaturated group such as ethylene oxide, propylene oxide, butene oxide, isobutene oxide, epichlorohydrin and styrene oxide; and unsaturated group-containing monoepoxides such as allyl glycidyl ether, methallyl glycidyl ether, glycidyl acrylate, glycidyl methacrylate, butadiene monoxide and cyclopentadiene monoxide.. These may be used singly or a plurality thereof may be used in combination.

[0014] According to the embodiments of the invention, the DMC catalyst complex may comprise a metal selected from potassium, zinc, cobalt, iron, chromium, platinum, and/or iridium. For example, a DMC catalyst complex may include zinc hexacyanocobaltate

Zn ₂ [Co(CN)6]2 prepared, in part, from potassium hexacyanocobaltate K ₃ [Co(CN)6] . Some methods of catalyst preparation have been reported: Such DMC catalysts and methods of preparation are well known in the art, see for example, U.S. Patents 3,427,334; 3,941,849;

4,477,589; 5,158,922; 5,470,813 and 5,482,908.

[0015] In the embodiments of the invention, the DMC catalyst complex includes an organic complexing agent. Suitable complexing agents may include water-soluble aliphatic aiconois, sucn as etnanoi, isopropanoi, n-Dutanoi, isoDutanoi, z-Dutanoi, tert-Dutanoi, ana trimethylolpropane. In another embodiment, the catalyst may also include a polyol complexing agent, see for example U.S. Patents 5,482,908, 5,545,601 ; 5,637,673 and 5,789,626. In one embodiment the complexing agent is tert-butanol. In yet another embodiment the complexing agent may be a combination of water-soluble aliphatic alcohols, such as for example tert-butanol, and polyols, such as for example polypropylene glycol.

[0016] The DMC catalyst complex, in some embodiments, may be activated. For example, the catalyst may be activated prior to introduction to a reactor (e.g. , before arriving at a catalyst inlet). The catalyst may be activated, for example, upon introduction to a reactor (e.g. , in a catalyst inlet). The catalyst may be activated, for example, after introduction to a reactor (e.g. , in a reaction chamber within a reactor).

[0017] The DMC catalyst complex, in some embodiments, may be present in at a concentration of from about 10 ppm to about 1000 ppm, from about 10 ppm to about 100 ppm, from about 10 ppm to about 50 ppm, or from about 20 ppm to about 30 ppm based on the weight the resulting polyoxyalkylene polymer.

[0018] The ring opening polymerization reaction may be performed as is commonly known in the art. The ring opening polymerization reaction may be performed continuously or batchwise.

[0019] In a continuous processes, the polymerization initiator and catalyst mixture is continuously fed into a continuous reactor such as a continuously stirred tank reactor (CSTR) or a tubular reactor. A feed of monoepoxide is introduced into the reactor and the product continuously removed. Examples of such continuous processes are described in, for example, EP912625.

[0020] In a batch processes, the polymerization may be performed by first mixing the polymerization initiator and the DMC catalyst complex. The dispersion of solid catalyst may be homogenized with a commercially available homogenizer, such as an IKA Ultra Turrax T25 high speed mixer. In one embodiment the dispersion is homogenized at about 20000 rpm for about 1 minute. The catalyst may alternatively be dispersed in a solvent and then mixed with the polymerization initiator. The solvent may be a non-protic polar solvent such as acetone, DMSO or THF. Alternatively the solvent may be a non-protic non-polar solvent such as benzene, toluene or xylene. While stirring, the mixture may be flushed several times with an inert gas, such as nitrogen or argon. The inert gas may be introduced such that the internal pressure of the reaction vessel is between about 1 bar and about 10 bar, or between about 2 bar and about 5 bar. Stirring may be performed at between about 10 rpm and about 1000 rpm, preferably between about 100 rpm and about 700 rpm. In one embodiment the stirring is performed at about 500 rpm. Alternatively, wnne continuing to stir tne mixture, a vacuum may De applied to reduce tne pressure in the reaction vessel to about 0.01-0.5 bar.

[0021] The mixture of catalyst and the polymerization initiator are then heated to between about 90°C and about 160°C, or between about 120°C and about 140°C, and then adding to the reactor with an initial quantity of monoepoxide, until a pressure is reached in the reaction vessel of between about 1 bar and about 10 bar, preferably between about 2 bar and about 5 bar. In one embodiment, the mixture is heated to about 120 °C, and the reaction vessel pressurized with alkylene oxide to about 3 bars. The monoepoxide may be metered into the reaction vessel. For example, the monoepoxide may be added to the reaction vessel over a time of between about 0.5 hours and about 30 hours, or between about 10 hours and about 20 hours. Upon all the monoepoxide being added the reaction vessel contents may continue to be stirred at the reaction temperature to complete the reaction of the monoepoxide over a time of between about 0.5 hours and about 5 hours. Subsequent amounts of monoepoxide may be metered into the reaction vessel, or to fractions of the reaction vessel contents, to further polymerize and increase the molecular weight of the reaction product. The further monoepoxide reactions may be performed at similar reaction conditions as in when the initial quantity of monoepoxide is reacted, or at different reaction conditions, such as different reaction temperature and/or reaction stirring rate.

[0022] The molecular weight of the resulting unsaturated polyoxyalkylene polymer may, in terms of number average molecular weight, be between about 1,000 and about 30,000, or between about 5000 and 12,000. The number average molecular weight can be determined by measuring the terminal groups. Specifically, when the polyoxyalkylene polymer is linear type polymer, the molecular weight can be determined by obtaining a hydroxyl value (OHV; meq/g) per a unit weight and an unsaturated value (IV; meq/g) from a known method, followed by calculating it with the formula: 2000/(1 V+OHV). Alternatively, the number average molecular weight can be determined by gel permeation chromatograpy using PEG standards.

[0023] The resulting polyoxyalkylene polymers may have low concentrations of free zinc ions. The concentration of free zinc ions in the polyoxyalkylene polymers may, for example, be below 0.2, 0.15, 0.10, 0.075, 0.05, 0.025, 0.01, 0.0075, 0.005, 0.0025, or 0.001 parts per hundred of polyoxyalkylene polymers.

[0024] Surprisingly, and contrary to the teachings of U.S. Pat. No 6,503,995, the unsaturated polyoxyalkylene polymers according to the embodiments of the invention may undergo a hydrosilylation reaction without the need to remove or otherwise treat (such as adding a metal-coordinating compound to the polyoxyalkylene polymer) the DMC catalysts complex present in the unsaturated polyoxyalkylene polymers. Even without the removal or treatment of the DMC catalysts complex, the unsaturated polyoxyalkylene polymers according to the embodiments or tne invention may oe nyarosiiyiatea witn a nign nyarosiiyiation emciency. in some embodiments, the unsaturated polyoxyalkylene polymers are hydrosilylated with a hydrosilylation efficiency of at least about 70%, such as between about 70 % and 95%. This includes unsaturated polyalkylene oxide polymers hydrosilylated with a hydrosilylation efficiency of 80 to 95% and further includes hydrosilylated polymers capped with a

hydrosilylation efficiency of 85 to 92%. As used herein, the "hydrosilylation efficiency" = [100 x ((number of unsaturation groups on the polyol hydrosilylated)/( total number of unsaturation groups on the polyol that were initially available for hydrosilylation)], and may be measured using ^-NMR.

[0025] The unsaturated polyoxyalkylene polymers may be hydrosilylated by reacting the polyoxyalkylene polymers with a compound having a hydrogen-silicon bond and a crosslinkable silyl group in the presence of a hydrosilylation catalyst.

[0026] The compound having a hydrogen-silicon bond and a crosslinkable silyl group in each molecule, may be represented by the general formula (I) shown below:

H-(Si(R ¹ ₂ _ _b )(X _b )O _m Si(R ² 3-a)Xa (I) where R ¹ and R ² are the same or different and each represents an alkyl group containing 1 to 20 carbon atoms, an aryl group containing 6 to 20 carbon atoms or an aralkyl group containing 7 to 20 carbon atoms or a triorganosiloxy group represented by R^SiO- and, when there are a plurality of R ¹ or R ² groups, they may be the same or different; R ³ is a univalent hydrocarbon group containing 1 to 20 carbon atoms and the three R ³ groups may be the same or different with one another; X represents a hydroxyl group or a hydrolyzable group and, when there are two or more X groups, they may be the same or different with each other or one another; a represents 0, 1, 2 or 3 and b represents 0, 1 or 2; b's in the m of -Si R ¹ ₂ - _b )(X _b )0-groups may be the same or different with each other or one another; and m represents an integer from 0 to 19 provided that the relation a+∑b>l should be satisfied.

[0027] The hydrolyzable group represented by X may be any of those hydrolyzable groups known in the art, for example halogen atoms and alkoxy, acyloxy, ketoximato, amino, amido, acid amide, aminoxy, mercapto and alkenyloxy groups. Among them, alkoxy groups such as methoxy, ethoxy, propoxy and isopropoxy are preferred in view of their mild hydrolyzability and the ease of handling. One to three such hydrolyzable groups may be bonded to one silicon atom and the sum (a+∑b) is preferably 1 to 5. When there are two or more hydrolyzable groups, they may be the same or different with each other or one another. The number of silicon atoms in the crosslinkable silyl group may be about 1 to 30. Luuzej in some embodiments, tnecompouna naving a nyarogen-sincon Dona ana a crosslinkable silyl group in each molecule represented by the above general formula (I) may include the compounds represented by the general formula (II):

H-Si(RVcXXc)

wherein R ⁴ represents an alkyl containing 1 to 20 carbon atoms, an aryl group containing 6 to 20 carbon atoms or an aralkyl group containing 7 to 20 carbon atoms or a triorganosiloxy group represented by R ³ ₃ SiO- and, when there are a plurality of R ⁴ groups, they may be the same or different; R ³ is a univalent hydrocarbon group containing 1 to 20 carbon atoms and the three R ³ groups may be the same or different with one another; X represents a hydroxyl group or a hydrolyzable group and, when there are two or more X groups, they may be the same or different with each other or one another; and c represents 1, 2 or 3.

[0029] As specific examples of the compound having a hydrogen- silicon bond and a crosslinkable silyl group in each molecule, there may be mentioned halosilanes such as trichlorosilane, methyldichlorosilane, dimethylchlorosilane, phenyldichlorosilane,

trimethylsiloxymethylchlorosilane and 1,1,3,3-tetramethyl-l-bromodisiloxane; alkoxysilanes such as trimethoxysilane, triethoxysilane, methyldiethoxysilane, methyldimethoxysilane, phenyldimethoxysilane, trimethylsiloxymethylmethoxysilane and trimethylsiloxydiethoxysilane; acyloxysilanes such as methyldiacetoxysilane, phenyldiacetoxysilane, triacetoxysilane, trimethylsiloxymethylacetoxysilane and trimethylsiloxydiacetoxysilane; ketoximatosilanes such as bis(dimethyl ketoximato)methylsilane, bis(cyclohexyl ketoximato)methylsilane, bis(diethyl ketoximato)trimethylsiloxysilane, bis(methyl ethyl ketoximato)methylsilane and

tris(acetoximato)silane; alkenyloxysilanes such as methylisopropenyloxysilane; and the like. Preferred among them from the mild reactivity and ease of handling viewpoint are alkoxysilanes such as methyldimethoxysilane, trimethoxysilane, methyldiethoxysilane and triethoxysilane; and halosilanes such as trichlorosilane and methyldichlorosilane.

[0030] After reaction with an unsaturated group in the manner of hydrosilylation, the halogen atom(s) in the halosilanes may be converted to some other hydrolyzable group(s) by reacting with an active hydrogen-containing compound such as a carboxylic acid, oxime, amide or hydroxylamine or a ketone-derived alkali metal enolate by an appropriate method known in the art.

[0031] The hydrosilylation catalyst may be any of those metal complexes the metal of which is selected from among the group VIII transition metals such as platinum, rhodium, cobalt, palladium and nickel. From the hydrosilylation reactivity viewpoint, H2PtCl6.6H ₂ 0, platinum- divinylsiloxane complexes, platinum-olefin complexes, Pt metal, RhCl(PPh ₃ ) ₃ , Rh(¾, RI1/AI2O ₃ , RuCl ₃ , IrCl ₃ , FeCl ₃ , A1C1 ₃ , PdCl ₂ .2H ₂ O, NiCl ₂ , T1CI4 and the like are preferred, H ₂ PtCl ₆ .6H ₂ 0, piatinum-vinyisiioxane complexes ana piatinum-oietin complexes are more preterrea ana platinum-vinylsiloxane complexes and platinum-olefin complexes are particularly preferred. The platinum-vinylsiloxane complexes collectively refer to compounds resulting from coordination of an intramolecular vinyl-containing siloxane, polysiloxane or cyclic siloxane, as a ligand, to a platinum atom. As typical examples of the ligand, there may be mentioned 1,1,3,3-tetramethyl- 1,3-divinylsiloxane and the like. As specific examples of the olefin ligand in the platinum-olefin complex, there may be mentioned 1,5-hexadiene, 1,7-octadiene, 1,9-decadiene, 1,11-dodecadiene and 1,5-cyclooctadiene. Among the ligands specifically mentioned above, 1, 1,3,3 -tetramethyl- 1,3-divinylsiloxane and 1,9-decadiene are preferred from the hydrosilylation reactivity viewpoint. The hydrosilylation catalyst to be used in the practice of the invention may be used singly or a combination of a plurality of species may be used.

[0032] The amount of the hydrosilylation catalyst to be used is not particularly restricted but generally is 0.00001 to 1 part by weight, preferably 0.00005 to 0.05 part by weight, more preferably 0.0001 to 0.01 part by weight, based on the weight of the metal in the catalyst, per 100 parts by weight of the polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule. When the amount is less than 0.00001 part by weight, any sufficient reaction activity may not be obtained in some instances and an amount exceeding 1 part by weight may be economically disadvantageous or cause discoloration of the polymer in certain instances.

[0033] In the above reaction, the use of a solvent is essentially unnecessary. For uniformly dissolving the catalyst and/or substrate, for controlling the reaction system temperature and/or for facilitating the addition of the substrate and/or catalyst components, however, a solvent can be used. Solvents suited for these purposes include, but are not limited to, hydrocarbon compounds such as hexane, cyclohexane, ethylcyclohexane, heptane, octane, dodecane, benzene, toluene, xylene and dodecylbenzene; haogenated hydrocarbon compounds such as chloroform, methylene chloride, chlorobenzene and o-dichlorobenzene; and ethers such as ethyl ether, tetrahydrofuran and ethylene glycoldimethyl ether, among others. Those plasticizers which can be used as plasticizers for the polyoxyalkylene polymer, such as phthalate esters and polyethers, can also be used as the reaction solvents. These may be used singly or a plurality of them may be used in combination.

[0034] The hydrosilylation reaction temperature is not particularly restricted but may for example be within the range of 0°C to 150°C, or between the range of 20°C to 100°C. At below 0°C, the rate of reaction may be low in some instances and, at above 150°C, side reactions involving the hydroxyl group, hydrogen-silicon bond and/or crosslinkable silyl group may proceed in certain instances, in one embodiment, tne nydrosiiyiation reaction temperature is about 60°C.

[0035] The hydrosilylated polyoxyalkylene polymer having at least one crosslinkable silyl group and at least one hydroxyl group in each molecule (hereinafter referred to as

"hydrosilylated polyoxyalkylene polymer") as produced by the above described process can react with water or atmospheric moisture to give crosslinked cured products and therefore is useful as a raw material or raw material intermediate for sealing, adhesive, coating and like materials or compositions for architectural or industrial use. The high remaining hydroxyl group percentage of this polyoxyalkylene polymer having at least one crosslinkable silyl group and at least one hydroxyl group in each molecule is favorable for the functional group introduction thereinto by urethane bond formation or esterification, for instance, or for the coupling thereof.

[0036] In subjecting the hydrosilylated polyoxyalkylene polymer to coupling reactions utilizing the hydroxyl group thereof in accordance with the embodiments of the invention, a coupling agent is used. The coupling agent to be utilized is not particularly restricted provided that it has two or more functional groups capable of reacting with the hydroxyl group but includes, among others, polyisocyanate compounds, polybasic carboxylic acid compounds, polybasic carboxylic acid anhydrides and polybasic carboxylic acid derivatives. Further, compounds having only one functional group but capable of reacting with and binding to two or more hydroxyl groups can also be used. Such compounds include, but are not limited to, aldehyde compounds and carbonate compounds, for instance.

[0037] For the cured products to acquire satisfactory physical characteristics, it is preferred that the yield of the coupling reaction which utilizes the hydroxyl group is as high as possible. In accordance with the present invention, a yield of not less than 80% is preferably for the coupling reaction, more preferably not less than 85%, based on the area ratio of the values as obtained from the gel permeation chromatography analysis. Here, the following formula is used in the calculation method of obtaining the yield of the coupling reaction from the gel permeation chromatography analysis: (1-X)xl00 (%), where X is the ratio of the peak area showing the uncoupled polymer relative to the peak area showing total polymer.

[0038] Among the coupling agents usable in the practice of the embodiments of the invention, the polyisocyanate compounds, namely compounds having two or more isocyanato groups in each molecule, include, but are not limited to, aliphatic, cycloaliphatic, arylaliphatic and aromatic isocyanates.

[0039] Examples of suitable aromatic isocyanates include the 4,4'-, 2,4' and 2,2'-isomers of diphenylmethane diisocyante (MDI), blends thereof and polymeric and monomeric MDI blends, toluene-2,4- and 2,6-diisocyanates (TDI), m- and p-phenylenediisocyanate, cmoropnenyiene-z,4-aiisocyanate, aipnenyiene-4,4 -ansocyanate, 4,4 -ansocyanate- ό, ό - dimehtyldiphenyl, 3-methyldiphenyl-methane-4,4'-diisocyanate and diphenyletherdiisocyanate and 2,4,6-triisocyanatotoluene and 2,4,4'-triisocyanatodiphenylether.

[0040] Mixtures of isocyanates may be used, such as the commercially available mixtures of 2,4- and 2,6-isomers of toluene diisocyantes. A crude polyisocyanate may also be used in the practice of the embodiments of the invention, such as crude toluene diisocyanate obtained by the phosgenation of a mixture of toluene diamine or the crude diphenylmethane diisocyanate obtained by the phosgenation of crude methylene diphenylamine. TDI/MDI blends may also be used.

[0041] Examples of aliphatic polyisocyanates include ethylene diisocyanate, 1,6- hexamethylene diisocyanate, isophorone diisocyanate, cyclohexane 1,4-diisocyanate, 4,4'- dicyclohexylmethane diisocyanate, l,3-bis(isocyanatomethyl)cyclohexane, 1,4- bis(isocyanatomethyl)cyclohexane, saturated analogues of the above mentioned aromatic isocyanates, and mixtures thereof.

[0042] Among the coupling agents usable in the practice of the embodiments of the invention, the polybasic carboxylic acid compounds include, but are not limited to, adipic acid, itaconic acid, iminodiacetic acid, ethylenediaminetetraacetic acid, glutaric acid, citraconic acid, oxalic acid, tartaric acid, diparatoluoyltartaric acid, dibenzoyltartaric acid, sebacic acid, 3,3'- thiodipropionic acid, thiomaleic acid, dodecanedioic acid, 1 ,2-cyclohexanediaminetetraacetic acid, brasilic acid, malonic acid, isophthalic acid, terephthalic acid, naphthalenedicarboxylic acid, 5-hydroxyisophthalic acid, l-cyanoethyl-2-methylimidazole trimellitate, l-cyanoethyl-2- phenylimidazole trimellitate, l-cyanoethyl-2-ethyl-4-methylimidazole trimellitate, 1-cyanoethyl- 2-undecylimidazole trimellitate, imidazole-4,5-dicarboxylic acid, chelidamic acid, 2,3- pyrazinedicarboxylic acid, folic acid, citric acid, succinic acid, fumaric acid, malic acid, glutamic acid, aspartic acid and cystine, among others.

[0043] Among the coupling agents usable in the practice of the embodiments of the invention, the polybasic carboxylic acid anhydrides include, but are not limited to, itaconic anhydride, citraconic anhydride, maleic anhydride, 3,3',4,4'-benzophenonetetracarboxylic acid dianhydride, trimellitic anhydride, pyromellitic anhydride, phthalic anhydride, maleated methylcyclohexene tetrabasic acid anhydride, endomethylenetetrahydrophthalic anhydride, chlorendic anhydride, methylendomethylenetetrahydrophthalic anhydride and

methyltetrahydrophthalic anhydride, among others.

[0044] Among the coupling agents usable in the practice of the embodiments of the invention, the polybasic carboxylic acid derivatives include, but are not limited to, diethyl ethoxymethylenemalonate, diethyl succinate, diethyl oxalate, fumaroyl chloride, diallyl nexanyaropntnaiate, aietnyi maionate, aiaiiyi isopntnaiate, aimetnyi isopntnaiate, aimetnyi terephthalate, diallyl terephthalate, triallyl trimellitate, dimethyl naphthalenedicarboxylate, bis(2- hydroxyethyl)terephthalate, o-phthaloyl chloride, diallyl phthalate, butylphthalyl butyl glycolate, dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diheptyl phthalate, di-2-ethylhexyl phthalate, butyl benzyl phthalate, dicyclohexyl phthalate, dioctyl adipate, diisononyl adipate, bis(2-ethylhexyl)azelate, dibutyl sebacate, triethyl acetylcitrate, dibutyl maleate, dibutyl fumarate, dilauryl 3,3'-thiodipropionate, ethylene dodecanedioate, ethylene brasilate, aspartame, succinyl dichloride, oxalyl dichloride, o-phthaloyl dichloride and adipoyl dichloride, among others.

[0045] Among the coupling agents usable in the practice of the embodiments of the invention, the aldehyde compounds include, but are not limited to, acrolein, acetaldehyde, octylaldehyde, glyoxal, glyoxylic acid, crotonaldehyde, butyraldehyde, formaldehyde, methacrolein, methylglyoxal, p-aminobenzaldehyde, 3,4,5-trimethoxybenzaldehyde,

hydroxybenzaldehyde, benzaldehyde, 3-aldehydopyridine, furfural, chlorobenzaldehyde, dichlorobenzaldehyde, monochloroacetaldehyde, trifluoromethylbenzaldehyde, anisaldehyde, amylcinnamic aldehyde, undecylenic aldehyde, cuminaldehyde, cinnamaldehyde, cyclamen aldehyde, 3,4-dimethoxybenzaldehyde, decylaldehyde, vanillin, hydoxycitronellal,

phenylacetaldehyde, heliotropin and p-methylphenylacetaldehyde, among others.

[0046] Among the coupling agents usable in the practice of the embodiments of the invention, the carbonate compounds include, but are not limited to, ethylene carbonate, diethyleneglycolbis(allyl carbonate), di-tert-butyl carbonate, dimethyl carbonate, propylene carbonate, diethyl carbonate, diallyl carbonate, allyl ethyl carbonate and diphenyl carbonate, among others.

[0047] In the practice of the embodiments of the invention, the coupling agent is used preferably in an amount of 0.5 to 3 moles, more preferably 0.8 to 2 moles, most preferably 0.95 to 1.5 moles, as expressed in terms of such a functional group as an isocyanate or carboxyl group, per mole of the hydroxyl group in the polyoxyalkylene polymer containing at least one crosslinkable silyl group and at least one hydroxyl group.

[0048] Those coupling agents which can be used in the practice of the embodiments of the invention may be used singly or a plurality thereof may be used in combination.

[0049] When a compound having two or more isocyanato groups in each molecule is used as the coupling agent, up to about 5 moles of the isocyanato group can be reacted with the hydroxyl groups in each mole of the hydrosilylated polyoxyalkylene polymer. In such a case, it is possible to effect the coupling by reacting a compound having two or more active hydrogen atoms in each molecule with the excess isocyanato group. Thus, the polyoxyalkylene polymer naving at least one crossiinKaoie siiyi group ana at least one nyaroxyi group in eacn molecule is reacted with a compound having two or more isocyanato groups in each molecule in relative amounts such that the isocyanato group is excess relative to the hydroxyl group and then the unreacted isocyanato group is reacted with a compound having two or more active hydrogen atoms in each molecule, whereby the coupling reaction can be effected.

[0050] Such compound having two or more active hydrogen atoms in each molecule includes, but is not limited to, compounds having, in each molecule, two or more groups selected from the group consisting of hydroxyl, mercapto, carboxyl and nitrogen-bound hydrogen- containing amino groups.

[0051] Such compounds include, but are not limited to, polyhydric alcohols such as 3,6- dimethyl-4-octyne-3,6-diol, 2,4,7, 9-tetramethyl-5-decyne-4,7-diol, 2,5-dimethyl-3-hexyne-2,5- diol, 2,5-dimethyl-3-hexane-2,5-diol, N-methyldiethanolamine, triisopropanolamine, triethanolamine, ethylene glycol, diethylene glycol, triethylene glycol, octanediol, sorbitol polyglycidyl ether, gluconic acid, glycerol .alpha.-monochlorohydrin, 1 ,4-cyclohexanediol, 1,3- dihydroxyacetone, disodium l,4-dihydroxy-l,4-butanedisulfonate, diisopropyl tartrate, thiodiglycol, trimethylolethane, trimethylolpropane, neopentyl glycol, butanediol, 2-butyl-2- ethyl- 1,3-propanediol, propylene glycol, dipropylene glycol, tripropylene glycol, 1 ,6-hexanediol, 1,2,6-hexanetriol, hexylene glycol, pentaerythritol, 1,5-pentanediol, polyethylene glycol, polytetramethylene ether glycol, polypropylene glycol, 3-methyl- 1,5-pentanediol, catechol, 1,4- dihydroxyanthraquinone, 1 ,4-dihydroxynaphthalene, hydrogenated bisphenol A, 2,3,4- trihydroxybenzophenone, 2,3,5-trimethylhydroquinone, hydroquinone, bis(2-hydroxyethyl) terephthalate, bis(4-hydroxyphenyl)sulfone, bisphenol A, p-hydroxyphenethyl alcohol, 4-tert- butylcatechol, 2-tert-butylhydroquinone, protocatechuic acid, phloroglucinol, gallic acid, lauryl gallate, resorcinol, leuco-l,4-dihydroxyanthraquinone, l,l'-bi-2-naphthol, 2-phenyl-4,5- bis(hydroxymethyl)imidazole, kojic acid, citrazinic acid, spiroglycol, tris(2- hydroxyethyl)isocyanurate, 5-fluorouracil, 2-(2-hydroxyethoxy)ethyl 2-hydroxypropyl tetrabromophthalate, 2,2-bis(4-hydroxyphenyl)hexafluoropropane, polysiloxanes hydroxyl- terminated at both termini, polyparavinylphenol, polyvinyl alcohol, .beta.-l,4-glucose, 2,2'- methylenebis(4-methyl-6-tert-butylphenol), 4,4'-thiobis(3-methyl-6-tert-butylphenol), poly(oxyethylene)alkylamines, poly(oxyethylene)alkylamides, sorbitan fatty acid esters, erysorbic acid, nordihydroguaiaretic acid, propyl gallate, riboflavin, pyridoxine, pantothenicacid, ascorbicacid, glycerophosphate, gluconic acid, gluconodeltalactone, erythritol, xylitol, xylose, sorbitol, inosine and arabinosylcytosine; polythiol compounds such as trimethylolpropane tris(thioglycolate), triglycol dimercaptan, pentaerythritol tetrakisthioglycolate, pentaerythritol tetrakisthiopropionate, trimethylolpropane tris(.beta.-thiopropionate) and 2,5-dimercapto- 1,3,4- tniaaiazoie; poiyoasic carooxyiic acia compounas sucn as aaipic acia, azoDiscyanovaieric acia, itaconic acid, imidiacetic acid, ethylenediaminetetraacetic acid, glutaric acid, succinic acid, citraconic acid, oxalic acid, tartaric acid, diparatoluoyltartaric acid, dibenzoyltartaric acid, sebacic acid, 3,3'-thiodipropionic acid, thiomaleic acid, dodecanedioic acid, trans-1,2- cyclohexanediaminetetraacetic acid, brasilic acid, hexahydrophthalic acid, polyacrylic acid, poly(4-hydroxybutyl acrylate), poly (2-hydroxy ethyl acrylate), poly(2-hydroxypropyl acrylate), poly(2-hydroxyethyl methacrylate), poly(2-hydroxypropyl methacrylate), malonic acid, isophthalic acid, terephthalic acid, 1,4-naphthalenedicarboxylic acid, 2,6- naphthalenedicarboxylic acid, 5-hydroxyisophthalic acid, trimellitic acid, pyromellitic acid, phthalic acid, l-cyanoethyl-2-methylimidazole trimellitate, l-cyanoethyl-2-phenylimidazole trimellitate, l-cyanoethyl-2-ethyl-4-methylimidazole trimellitate, imidazole-4,5-dicarboxylic acid, chelidamic acid, 2,3-pyrazinedicarboxylic acid, chlorendic acid, folic acid, aspartic acid, glutamic acid, citric acid, fumaric acid, malic acid and glycyrrhetic acid; polyamine compounds such as adipic dihydrazide, primary amine-modified acrylic polymers, 3,3'- iminobis(propylamine), 3-(methylamino)propylamine, N-methyl-3,3'-iminobis(propylamine), ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine,

pentaethylenehexamine, carbohydrazide, guanidine, guanylthiourea, 1,4-diaminobutane, diaminopropane, diaminomaleonitrile, dicyandiamide, 3,9-bis(3-aminopropyl)-2,4,8,10- tetraoxaspiro[5.5]undecane, thiocarbohydrazide, thiosemicarbazide, thiourea,

dodecanedioicdihydrazide, hexamethylenediamine, formamidine, m-xylylenediamine, dianisidine, 4,4'-diaminostilbene-2,2'-disulfonic acid, 1,4-diamnoanthraquinone, 4,4'-diamino- 3,3'-diethyldiphenylmethane, 4,4'-diaminobenzanilide, diaminodiphenyl ether, 3,3'-dimethyl-4,4'- diaminodiphenylmethane, tolidine base, m-toluylenediamine, phenylenediamine, amidol, paramine, acetoguanamine, l-(2-aminoethyl)piperazine, 2,4-diamino-6-(2-methyl-l-imidazolyl)- ethyl-l,3,5-triazine, l,3-bis(hydrazinocarboethyl)-5-isopropylhydantoin, piperazine,

benzoguanamine, melamine, 3,3'-dichloro-4,4'-diaminodiphenylmethane, 3,3'-dichloro-4,4'- diaminobiphenyl, aminopolyacrylamide, polyallylamine and bisbentiamine; compounds having different kinds of active hydrogen, such as N-(2-aminoethyl)ethanolamine, N- methylethanolamine, 12-aminododecanoic acid, 3-amino-l-propanol, monoisopropanolamine, diisopropanolamine, monoethanolamine, diethanolamine, N-carboxy-4,4'- methylenebiscyclohexylamine, glyoxylic acid, glycylglycine, cysteamine, thioglycolic acid, 1- thioglycerol, lactic acid, . alpha. -hydroxyisobutyric acid, 2-hydroxyethylaminopropylamine, formamidoxime, 2-mercaptoethanol, .beta.-mercaptopropionic acid, p-aminobenzoic acid, 2- amino-4-chlorophenol, 2-aminothiophenol, aminophenol, anthranilic acid, .beta.- hydroxynaphthoic acid, salicylic acid, 2-amino-5-naphthol-7-sulfonic acid, thiosalicylic acid, p- nyaroxyoenzoic acia, o-nyaroxy-z-napntnoic acia, p-nyaroxypnenyiacetic acia, p- hydroxyphenylacetamide, p-hydroxyphenylpropionic acid, benzilic acid, mandelic acid, leuco- 1,4-diaminoanthraquinone, p-hydroxyphenylglycine, 3-carbamoylpyrazinecarboxylic acid, (hydroxyethyl)piperazine, 2-amino-4-chlorobenzoic acid, isoleucine, threonine, tryptophan, valine, histidine, phenylalanine, methionine, lysine, aspartame, alanine, glycine and theanine; water; ammonia; and so forth. These may be used singly or a plurality thereof may be used in combination.

[0052] Among these, hydroxyl-containing compounds and amino-containing compounds are preferred from the reactivity viewpoint and compounds having three or more hydroxyl groups or amino groups in each molecule, such as trimethylolpropane, trimethylolethane, pentaerythritol, 1,2,6-hexanetriol and melamine, are more preferred since product polymers showing increased strength can be obtained with them.

[0053] It is also possible to subject the excess isocyanato group to coupling by the isocyanurate ring formation reaction.

[0054] When, in the practice of the embodiments of the invention, the hydrosilylated polyoxyalkylene polymer is reacted with a coupling agent such as a compound having two or more isocyanato groups in each molecule, it is not always necessary to use a catalyst. For increasing the rate of reaction or improving the degree of conversion, however, a catalyst may be used. The catalyst to be used in carrying out the coupling reaction using a polyisocyanate compound includes, but is not limited to, those catalysts mentioned in Polyurethanes: Chemistry and Technology, Part I, Table 30, Chapter 4, Saunders and Frisch, Interscience Publishers, New York, 1963, for instance.

[0055] Preferred as the urethane formation reaction catalysts usable in effecting the coupling reaction using a polyisocyanate compound because of their high activity are tin catalysts such as stannous octylate, stannous stearate, dibutyltin dioctoate, dibutyltin

dioleylmaleate, dibutyltin dibutylmaleate, dibutyltin dilaurate, l,l,3,3-tetrabutyl-l,3- dilauryloxycarbonyldistannoxane, dibutyltin diacetate, dibutyltin diacetylacetonate, dibutyltin bis(o-phenylphenoxide), dibutyltin oxide, dibutyltin bis(triethoxysilicate), dibutyltin distearate, dibutyltin bis(isononyl 3-mercaptopropionate), dibutyltinbis(isooctyl thioglycolate), dioctyltin oxide, dioctyltin dilaurate, dioctyltin diacetate and dioctyltin diversatate. Further, it is preferable to use catalysts low in activity against crosslinkable silyl groups and, thus, for example, sulfur atom-containing tin catalysts such as dibutyltin bis(isononyl 3-mercaptopropionate) and dibutyltin bis(isooctyl thioglycolate) are particularly preferred.

[0056] In cases where the coupling reaction is carried out using a polybasic carboxylic acid, polybasic carboxylic acid anhydride, polybasic carboxylic acid derivative, aldehyde compound, caroonate compound or tne lute, too, tnose catalysts Known in tne art tor tne respective reactions can be used.

[0057] The addition amount of such a catalyst is not particularly restricted but preferably is 0.0001 to 3 parts by weight, more preferably 0.001 to 0.5 part by weight, most preferably 0.003 to 0.1 part by weight, per 100 parts by weight of the silylated polyoxyalkylene polymer. At an amount below 0.0001 part by weight, a sufficient reaction activity may not be obtained while, at an amount exceeding 3 parts by weight, the heat resistance, weathering resistance, hydrolysis resistance and/or like physical properties of the crosslinkable silyl group-containing

polyoxyalkylene obtained may be impaired as the case may be.

[0058] While the use of a solvent is not necessary in the above coupling reaction, a solvent may be used for uniformly dissolving the catalyst and/or substrate, or for controlling the reaction system temperature or for facilitating the addition of the catalyst components. Solvents suited for such purposes include, but are not limited to, hydrocarbon compounds such as hexane, cyclohexane, ethylcyclohexane, heptane, octane, dodecane, benzene, toluene, xylene and dodecylbenzene; halogenated hydrocarbon compounds such as chloroform, methylene chloride, chlorobenzene and o-dichlorobenzene; and ethers such as ethyl ether, tetrahydrofuran and ethylene glycol dimethyl ether, among others.

[0059] The methods of the embodiements of the invention do not require any treatment step or any purification step either before or after the hydrosilylation reaction or either before or after the coupling reaction which utilizes the hydroxyl group. The application of some or other treatment step or purification step for a particular reason is not excluded, however.

[0060] Since the production method of the invention does not require any purification step, the series of reaction steps from the polyoxyalkylene polymer production by polymerization to the coupling reaction can be carried out in succession in one and the same reactor.

[0061] The silylated polyoxyalkylene polymers obtained by the production method according to the embodiments of the invention can give crosslinked cured products upon reaction with water or the moisture in the atmosphere and are useful as raw materials or raw material intermediates for use in sealing compositions, adhesive compositions, coating compositions and the like for architectural or industrial use.

[0062] The embodiments of the invention, which have the constitution mentioned above, makes it possible to expediently obtain, from a polyoxyalkylene polymer having at least one unsaturated group and at least one alcoholic hydroxyl group in each molecule, a silylated polyoxyalkylene polymer having at least one crosslinkable silyl group and at least one hydroxyl group in each molecule or a crosslinkable silyl group-containing polyoxyalkylene polymer, without the necessity of removing the process-derived double metal cyanide complex catalyst or otnerwise treat tne aouoie metal cyaniae catalyst, AS a result, tne relevant puntication or treating step can be omitted and the production process can be markedly simplified. The thus-obtainable silyleated polyoxyalkylene polymer shows a high crosslinkable silyl group introduction rate and a high remaining hydroxyl group percentage and therefore is suited for use in further functional group introduction or coupling utilizing the crosslinkable silyl group and/or hydroxyl group. The crosslinkable polyoxyalkylene polymer obtained provides satisfactory physical properties when used as a raw material in sealing compositions or adhesives compositions. In addition, the polymer can be stored stably for a long period. Furthermore, since any step of purifying or further treating the raw material is not necessary, the reactions from polymerization to coupling can be carried out continuously in a single reaction vessel.

EXAMPLES

[0063] The following examples are provided to illustrate the embodiments of the invention, but are not intended to limit the scope thereof. All parts and percentages are by weight unless otherwise indicated.

[0064] The following materials were used:

PGME A propylene glycol monoallyl ether. The PGME had an allylic content of 13.1% (0.998 mol of unsat/mol monol) and an OH number of 266.2 or 8.067%OH.

DMC catalyst A zinc hexacyanocobaltate based catalyst prepared as

described in U.S. Pat. No. 5,482,908. The complexing agent is a combination of tert-butanol and polypropyleneglycol

Propylene oxide 99.9% purity, available from The Dow Chemical Company. Karstedt' s catalyst Platinum-divinyltetramethyldisiloxane and xylene as carrier solvent, the Pt loading in the catalyst is 2 wt%. available from Gelest, Inc.

Methyldiethoxysilane Available from Gelest, Inc.

Methyldimethoxysilane Available from Gelest, Inc.

ISONATE ^* 50-OP A 50 percent 4,4'-methylene diphenyl isocyanate, 50 percent

2,4'-methylene diphenyl isocyanate mixture having a functionality of 2.0 and an equivalent weight of 125 g/equivalent available from The Dow Chemical Company.

PAPI 27 A polymeric MDI (polymethylene polyphenylisocyanate) available from The Dow Chemcial Company having a functionality of approximately 2.7, an iscyante equivalent weignt or approimateiy i ana an r uu content Dy weignt of about 31.4 %.

DABCO T-12 A tin catalyst available from Air Products.

Anhydrous ZnCl ₂ powder Available from Alfa Aesar.

* IS ON ATE and PAPI are trademarks of The Dow Chemical Company

Test Methods

[0065] Tensile strength was measured according to ASTM standard test D1708.

Elongation at break was measured according to ASTM standard test D1708. 100% Secant Modulus was measured according to ASTM standard test D1708.

Alkoxylation of propylene glycol monoallyl ether

[0066] DMC catalyst (0.3207 g) was added to PGME (235.68 g). The mixture was dispersed for one minute with an Ultra Turrax high speed mixer, then charged into a previously nitrogen purged 9 L pressure reactor. The reactor contents were heated with agitation at 135°C, then propylene oxide monomer (5390 g) was metered at 5-7 gram/min into the reactor at 135 °C. After propylene oxide feed was complete, the reactor was agitated at reaction temperature for an additional 1 hr to digest unreacted oxide. Approximately 1 kg of the alkoxylated propylene glycol monoallyl ether (APGME-1) was dispensed from the pressure reactor and saved for later use. APGME-1 has a number average molecular weight of about 5000.

[0067] The remaining content of the reactor contents (4688 g) was further reacted with a second feed of propylene oxide (455 g) at 135°C, followed by a digest to consume unreacted propylene oxide. Approximately 1 kg of the further alkoxylated propylene glycol monoallyl ether (APGME-2) was dispensed from the pressure reactor and saved for later use. APGME-2 has a number average molecular weight of 5500.

[0068] The remaining content of the reactor (4256 g) was then further reacted with a third feed of propylene oxide (385 g) at 135°C, followed by a digest to consume unreacted propylene oxide. The further alkoxylated propylene glycol monoallyl ether (APGME-3) was dispensed from the reactor. The final DMC concentration in APGME-3 was experimentally determined to be 41ppm according to Atomic Absorption spectroscopy. APGME-3 has a number average molecular weight of about 6000.

[0069] Another batch of polyalkylene oxide alkoxylated propylene glycol monoallyl ether (APGME-4) was synthesized following the same preparation method described above for APGME-1. DMC catalyst (0.875 g) was added to PGME (1003.62 g). The mixture was dispersed for one minute with an Ultra Turrax high speed mixer, then charged into a previously nitrogen purged y L pressure reactor, ine reactor contents were neatea witn agitation at i 03 u, men propylene oxide monomer (1060 g) was metered at 5-7 gram/min into the reactor at 135 °C. After propylene oxide feed was complete, the reactor was agitated at reaction temperature for an additional 1 hr to digest unreacted oxide. DMC concentration in APGME-4 was experimentally determined to be 28 lppm. 6000 OH

Hydrosilylation of alkoxylated propylene glycol monoallyl ethers

Example 1

[0070] APGME-3 (102.28 g) was charged into a 250-ml glass reactor equipped with continuous nitrogen purge, a heating mantle and a thermocouple. The reactor was then warmed to 68 °C, and Karstedt' s catalyst (0.112 g) was added. Methyldiethoxysilane (2.15 g) was added and the hydrosilylation reaction was allowed to take place at 70-75 °C for 15 min. ^] H-NMR results showed a hydrosilylation efficiency of 80.2%. Hydrosilylation efficiency was calculated by integrating the ^] H-NMR peaks corresponding to reacted and unreacted methyl group that is covalently bonded to a Si atom.

Example 2

[0071] APGME-3 (58.63 g) was charged into a 250 ml glass reactor equipped with continuous nitrogen purge, a heating mantle and a thermocouple. The reactor was heated to 50°C and the reactor temperature was carefully controlled. Methyldimethoxysilane (0.96 g) and

Karstedt' s catalyst (0.06 g) were subsequently added. Reaction conversion was followed using ^] H-NMR over a period of 30 minutes. The conversion at 15 minutes was 95.4%.

Examples 3-15

[0072] Alkoxylated propylene glycol monoallyl ether (100 g) was charged into a 250 mL glass reactor equipped with continuous nitrogen purge, a heating mantle and a thermocouple. The alkoxylated propylene glycol monoallyl ether used is given in Table 1. The reactor was heated to the temperature specified in Table 1. The hydrosilylation reaction is initiated by injecting methyldimethoxysilane (1.8 g) and calculated amount of Karstedt' s catalyst, see Table 1 for details. The reaction was allowed to proceed for 1 hr. The reaction mixture was analyzed using ^] H NMR. laoie i

[0073] As seen in Table 1, allyl monol containing 41, 140 and 281 ppm DMC catalyst resulted in similar hydrosilylation conversions. Thus, hydrosilylation of a terminally unsaturated polyalkylene oxide polymer is not dependent upon DMC concentration.

Isocyanate reaction of hydrosilylated alkoxylated propylene glycol monoallyl ethers

Example 16

[0074] ISONATE 50-OP (1.08 g) was added to the reactor containing the hydrosilylated product of Example 2 along with DABCO T-12 catalyst (0.05 g) to carry out the coupling reaction: the reaction of hydroxyl with isocyanate. The reactor was heated to 60°C for 1 hour and complete conversion of isocyanate was confirmed by FTIR. The final product was cured at ambient conditions for 10 days. Physical properties were measured on samples having a width of 0.187 inches, a length of 1.500 inches, and a thickness of 0.014 inches. The tensile strength was 35.5 psi, the elongation at break was 679.7%, and the 100% Secant Modulus was 4.278 psi. Example i /

[0075] PAPI (0.78 g) was added to a reactor containing the hydrosilylated product of

Example 1 (53.8 g) along with DABCO T-12 catalyst (0.02 g) to carry out the coupling reaction. The reactor was heated to 60°C for 1 hour and complete conversion of isocyanate was confirmed by FTIR. The final product was cured at ambient conditions for 10 days. Physical properties were measured on samples having a width of 0.187 inches, a length of 1.500 inches, and a thickness of 0.014 inches. The tensile strength was 55.2 psi, the elongation at break was 368%, and the 100% Secant Modulus was 22 psi.

While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.