Nanocomposite and Method

The present disclosure is related to nanocomposites, and in particular, to nylon nanocomposites.

Reinforcing polymeric composites using nano-sized particles with high aspect ratio have been investigated since the 1980's (see, US-A-4,739,007). Polymer/layered-silicate nanocomposites have extensively been investigated due to the significant improvements in the mechanical strength and stiffness, enhanced gas permeability barrier, good thermal resistance, and flame retardancy. Polymer nanocomposites normally require a low loading concentration of inexpensive silicate clays such as montmorillonite (MMT), vermiculite, saponite, and hectorite. Well-exfoliated nanocomposites can be produced by in situ polymerization and melt-compounding techniques. Nanocomposites have been prepared by a melting process from a wide variety of polymers. US-A-4,739,007 disclosed a method to produce nylon 6 organoclay nanocomposites using in-situ polymerization to produce highly reinforced nylon composites, achieving high flexural modulus, tensile strength and heat distortion. On the other hand, these nylon-based nanocomposites become non-ductile. Typically, impact modifiers are added to improve impact toughness at the expense of flexural modulus. What is desired commercially is an approach for toughening these nylon/organoclay composites to obtain high impact strength while retaining high modulus and strength. Besides, to make high-performance nanocomposite fibers and coating for elastic strings, the improvement in elongation is also important for clay nanocomposites. Some groups have reported improving elongation of clay-based nylon nanocomposites by using a rubber impact modifier while maintaining a relatively high modulus and strength, but none of them achieved a good elongation at break which is comparable to that of pristine nylon (see, A. J. Oshinsko, H. Keskkula, and D. R. Paul, Polymer, 37, 4891, (1996); Young-Cheol Ahn, D. R. Paul, Polymer, 47, 2830 (2006)). Most reports showed that relatively high rubber loadings over 5% were used to toughen nanocomposites with a high impact strength, leading to even lower modulus and strength than neat polymer, however. It is an object of the invention to provide a nanocomposite, in particular a rubber toughened thermalplastic clay nanocomposite, and a method for making the same, whereby the nanocomposite has a high tensile strength and modulus and also a high elongation.

This object is achieved by the method of claimi and the composite of claim 9. Preferred embodiments of the invention are characterized in the sub-claims. In embodiments of the present invention, SEBS /SEBS-MA and ethylene propylene copolymers with various morphologies are used to improve the physical properties of nylon nanocomposites. Instead of employing melt-compounded nylon nanocomposites, the nylon nanocomposites made from an in-situ

polymerization method, which is known to achieve the best exfoliation and the best tensile strength, are melt-compounded with different impact modifiers. It is found that semi-crystalline ethylene propylene random copolymer with medium maleic anhydride content is melt-compounded with the exfoliated clay- Dased nanocomposiie io significantly improve eioπgaϋϋπ of No/day riαπϋcύmposiies at a veiy tow toadiπy of impact modifier less than 4%. However, similar results were not achieved from other groups, although some groups reported elongation can be improved to near 90%. But, the loadings of impact modifier are normally higher than 4%. The semi-crystalline EP impact modifier melt-compounded with exfoliated clay-N6 nanocomposites can produce nano-sized clusters of impact modifier uniformly dispersed in N6-clay matrix. The exfoliated clay platelets do not penetrate into the rubber phase so that more elongated EP particles are produced in clay-N6 matrix, resulting in very effective toughening to caly-N6 nanocomposites.

A lot of applications may be found for this modified nylon nanocomposites if the nanocomposites not only keep high tensile strength and modulus, but have a high elongation, such as making high-strength fibers, packaging, etc.

Figure 1 illustrates a flow diagram configured in accordance with embodiments of the present invention.

To toughen polymer nanocomposites, such as nylon/clay nanocomposites, the nanocomposites are generally melt-compounded with a maleated elastomer wherein the grafted maleic anhydride readily reacts with the amine end groups of polyamide to form a graft copolymer that strengthens the interface between the two phases and controls the morphology. Elastomer particle size is a key parameter in achieving good toughness of polyamides. Many types of impact modifiers are currently available in the market place. For nylon nanocomposites, maleated or non-maleated styrene-hydrogenated butadiene- styrene triblock copolymers (MA-SEBS or SEBS), ethylene propylene random copolymer (EPR or EPR-g-

MA), ethylene-glycidyl methacrylate copolymer (PE-GMA) ₁ etc. have been employed to enhance the physical properties of nylon nanocomposites. To improve the properties of nanocomposites by using impact modifier, the type of impact modifier and melt-compounding process must be carefully chosen.

Figure 1 illustrates a flow diagram of a process to make N6 nanocomposites. Nylon 6 nanocomposites 10 and rubber impact modifiers 11 are dried 101 separately in an oven at 7O ⁰ C for at least 8 hours. 4% clay nylon 6 composites 10 made by in-situ polymerization are melt-compounded with impact modifiers 11 of EXXELOR EP 1840, EXXELOR EP 1801, and SEBS/SEBS-MA, to improve impact strength and elongation. The difference between EXXELOR EP 1840 and EXXELOR EP 1801 are that EXXELOR EP 1840 (Exxelor is a brand name from ExxonMobil Chemical) has medium maleic anhydride content and

EXXELOR EP 1801 has a high maieic anhydride content. The mixture of SEBS and SEBS-MA is also used to melt-compound with 4% clay nylon 6 nanocomposites. In step 102, to mix the pellets of in-situ N6/clay nanocomposite and impact modifier evenly, the two types of pellets are put into a bottle or a plastic bag. Shake and rotate the bottle or the bag to make the impact modifier pellets ovεrsly distributed in the mixture. A HAAKE Rheomex CTW 100 twin screw extruder is used to blend nylon/clay nanocomposites with impact modifiers 13. Following are the parameters used in this process:

Screw zone 1 temperature: 240 ⁰ C;

Screw zone 2 temperature: 230 ⁰ C; Screw zone 3 temperature: 230°C;

Die temperature: 240 ⁰ C;

Sped of screw 103: 50 (maximum speed designed for this extruder is 200 rpm).

The nanocomposite fiber is quenched in water and pelletized 14 using a Haake PP1 Pelletizer POSTEX after extrusion process. The nanocomposite pellets are dried 104 at 70 ⁰ C prior to the injection molding process 15 to make specimens of dog-bones for tensile tests and Izod bars for modulus and impact tests.

Following are the parameters used:

Injection pressure: 70 bar;

Holding pressure. 35 bar;

Holding time. 20 seconds;

Heating zone 1 temperature. 245°C;

Heating zone 2 temperature: 250 ⁰ C;

Heating zone 3 temperature: 255°C;

Nozzle temperature: 260 ⁰ C;

Mold temperature: 60 - 80 ⁰ C.

The specimens after injection molding are kept in dry desiccators 105 or in vacuum and ready for tests. The molded samples with specific dimensions follow ASTM-standards 16 (ASTM D628 for tensile strength testing, ASTM D256 for impact strength testing, ASTM D790 for flexural modulus testing).

To choose proper impact modifier for the highest impact strength, nylon 6 nanocomposites with 4%

clay loading are melt compounded with different rubber impact modifiers at a loading of 20%, 10%, and 5%, respectively. Table I shows the results.

EXXELOR EP 1840 of ethylene propylene copolymer with medium maleic anhydride content has the best performance in terms of impact strength and elongation. SEBS-MA has the worst effect on nanocomposites for blended nanocomposites. Table Il shows that the mixture of 80% SEBS and 20%

SEBS-MA has a better performance than SEBS-MA or SEBS only, indicating that the proper MA content is required to toughen nanocomposites.

Table II. Properties of N6 nanocomposites from SEBS & Maleic Anhydride grafted SEBS(SEBS- MA) Impact modifier.

As indicated in Table III, by adding 3% EXXON 1840 achieved was a tensile strength of 93

MPa while retaining the elongation over 100% and modulus over 4 GPa, although impact strength still needs to be improved to the level of pristine nylon 6.

Table III. Properties of N6 nanocomposites from EP EXXELOR 1840.

However, 4% rubber loading shows a better impact strength than neat nylon 6. Important is that a

very low loading of impact modifier only decreases the tensile strength and modulus a little comparing clay nylon 6 nanocomposites, but tremendously improves the elongation at beak. This property may lead to a high performance fiber for the textile industry because without impact modifier it is impossible to directly fabricate fibers by using brittle nylcn naπcccrripcεitεs. Another important application is using the modified nylon nanocomposites as coating materials for strings to improve wear-resistance and durability of polymer strings. To make nylon packaging materials stronger and have better enhanced gas permeability barrier, the elongation is also required if nylon nanocomposites would be applied. These applications will benefit from the rubber modified nanocomposites with very low loading of impact modifier less than 4%.

2% and 3% 1840 impact modifier, however, show some unexpected results. The reason, is due to the extrusion process and blending quality of N6 and impact modifier pellets because the pellet size is so big so that the difference between 2% and 3% may not be so much different if mixing is not very even. Tuning the extrusion process and getting better mixing may allow for better control of the melt- compounding process.